By S. Korman, S. B. Tuwiner

THE purpose of this study is to investigate the effect of agitation upon the flotation of chal-cocite. It is believed that the concentration of collector which is required to produce a water-repellent surface upon the mineral is determined among other things by the rate of collector diffusion through an impeding film of more or less stagnant fluid. Its thickness depends upon the intensity of agitation. In the first part of this study a method is developed for determining the thickness of the fluid film upon a polished surface of synthetic chalcocite. The film thickness is then determined as precisely as possible under three readily reproducible condi-tions of agitation intensity. These determinations serve as a quantitative evaluation of agitation. In Part 2 it is demonstrated that in solutions of lime at PH 10.5 and in the absence of air or dissolved oxygen the concentration of collector required to develop water-repellency upon the surface in any given time is a function of the fluid film thickness, and that after about 10 min the relation becomes linear. This points to the possibility that the collector ions may be involved in a diffusional process through the fluid film. In Part 3 it is shown that where air is present more collector is required to produce water-repellency than for the case in which air is excluded. Next, it is shown that for the latter case the most minute amount of sodium sulphide suffices to preclude development of water-repellency. Both oxygen and sulphide are in a sense, therefore, depres- sants for chalcocite in a lime solution at PH 10.5. When oxygen and sulphide are present simultaneously there is a region of minimum critical collector concentration for water-repellency which is very markedly lower than the concentration where oxygen alone or where sulphide alone is present. Moreover, this minimum appears to be identical with the collector concentration which is required where sulphide and oxygen are both excluded. This would appear to indicate that in certain ranges of concentration of oxygen and sulphide, each cancels the effect of the other. The range of concentration of solution for this effect in solutions saturated with oxygen is a function of the agitation intensity. Thus we are led to believe that a chemical reaction involving sulphide and oxygen occurs at the surface of the chalcocite. Part 4 of this study is a further development of this idea and some of its consequences from an electrochemical standpoint, while in Part 5 the disappearance of sulphide from pulps of several minerals is noted with an indication that both dissolved oxygen and the mineral are necessary, the reaction being catalytic or pseudocatalytic. Part 1. Determination of Fluid Film Thickness The Fluid Film Concept: The hindrance to the diffusion of collector to the surface of the chalcocite is a barrier of stagnant fluid in the vicinity of the surface. It is the same barrier that limits the rate of transfer of heat, the rate of solution of dissolving crystals, or any of the other rates pertaining to chemical engineering unit operations in which the film resistance to diffusion plays a principal role.' Fluid films are present upon the surface to an extent which varies with the geometry and intensity of agitation. They result from the fact that in the region within the fluid near a surface, motion is entirely parallel to it. From the standpoint of transfer to or away from the interface the effect is as though the fluid were stagnant. Outside of the film, movement of the fluid may be streamline or turbu-

Jan 1, 1951

By S. Korman, S. B. Tuwiner

THE purpose of this study is to investigate the effect of agitation upon the flotation of chal-cocite. It is believed that the concentration of collector which is required to produce a water-repellent surface upon the mineral is determined among other things by the rate of collector diffusion through an impeding film of more or less stagnant fluid. Its thickness depends upon the intensity of agitation. In the first part of this study a method is developed for determining the thickness of the fluid film upon a polished surface of synthetic chalcocite. The film thickness is then determined as precisely as possible under three readily reproducible condi-tions of agitation intensity. These determinations serve as a quantitative evaluation of agitation. In Part 2 it is demonstrated that in solutions of lime at PH 10.5 and in the absence of air or dissolved oxygen the concentration of collector required to develop water-repellency upon the surface in any given time is a function of the fluid film thickness, and that after about 10 min the relation becomes linear. This points to the possibility that the collector ions may be involved in a diffusional process through the fluid film. In Part 3 it is shown that where air is present more collector is required to produce water-repellency than for the case in which air is excluded. Next, it is shown that for the latter case the most minute amount of sodium sulphide suffices to preclude development of water-repellency. Both oxygen and sulphide are in a sense, therefore, depres- sants for chalcocite in a lime solution at PH 10.5. When oxygen and sulphide are present simultaneously there is a region of minimum critical collector concentration for water-repellency which is very markedly lower than the concentration where oxygen alone or where sulphide alone is present. Moreover, this minimum appears to be identical with the collector concentration which is required where sulphide and oxygen are both excluded. This would appear to indicate that in certain ranges of concentration of oxygen and sulphide, each cancels the effect of the other. The range of concentration of solution for this effect in solutions saturated with oxygen is a function of the agitation intensity. Thus we are led to believe that a chemical reaction involving sulphide and oxygen occurs at the surface of the chalcocite. Part 4 of this study is a further development of this idea and some of its consequences from an electrochemical standpoint, while in Part 5 the disappearance of sulphide from pulps of several minerals is noted with an indication that both dissolved oxygen and the mineral are necessary, the reaction being catalytic or pseudocatalytic. Part 1. Determination of Fluid Film Thickness The Fluid Film Concept: The hindrance to the diffusion of collector to the surface of the chalcocite is a barrier of stagnant fluid in the vicinity of the surface. It is the same barrier that limits the rate of transfer of heat, the rate of solution of dissolving crystals, or any of the other rates pertaining to chemical engineering unit operations in which the film resistance to diffusion plays a principal role.' Fluid films are present upon the surface to an extent which varies with the geometry and intensity of agitation. They result from the fact that in the region within the fluid near a surface, motion is entirely parallel to it. From the standpoint of transfer to or away from the interface the effect is as though the fluid were stagnant. Outside of the film, movement of the fluid may be streamline or turbu-

Jan 1, 1951

By P. K. Koh

Isothermal salt bath annealing of 0.014-in. thick 3 pct Si-Fe sheet was conducted at temperatures ranging from 927" to 1260°C in order to investigate the grain-growth behavior. Within the temperature range studied normal grain growth did not take place; instead nucleated grain growth prevailed. The nucleation frequency was found to increase with the annealing temperature, with corresponding decrease in grain diameter of ultimate secondaries after long-time annealing. Large secondaries grown by low-temperature isothermal annealing are essentially of (110)[001] orientation, and the (110)[001] texture is strong. The relatively small secondaries grown by high-temperature isothermal annealing also have orientations near (110)[001] as an average but widely scattered; thus the amount of (110)[001] texture is found to decxease with isothermal annealing temperature. Grain growth and texture development at various annealing temperatures can be described by families of sigmoidal curves with the time axis. ThE cube-on-edge (110)[001] texture and predominating large secondaries in fully annealed 3 pct Si-Fe are customarily produced by a 1100°C annealing of a primary recrystallized sheet. On annealing the primary recrystallized sheet above the temperature at which secondary recrystalliza-tion starts May and turnbull' have demonstrated that secondary grains decrease in size as the temperature is increased. The phenomenon was attributed to a decrease in the (G/N) ratio where G is the growth rate of secondary grains and N is their nucleation frequency. In addition, the growth of grains in orientations rather far from (110) [0011 occurred. The present investigation is devoted to detailed rate studies of the same phenomenon. Mi-crostructure, magnetic anisotropy, and texture data were obtained on strips of 3 pct Si-Fe isothermally annealed for various lengths of time in a BaC12 salt bath at temperatures ranging from 927' to 1260°C. The texture results are reported elsewhere.2 EXPERIMENTAL PROCEDURE Commercial 0.014-in. cold-rolled silicon-iron strip (3.16 pct Si), prepared by two stages of cold rolling with an intermediate short anneal, was given a decarburizing 3-min anneal at 800°C. Metallo- graphic studies indicated complete recrystallization. In order to provide a protective atmosphere and to obtain a rapid rise to an elevated temperature, a BaC12 and NaCl fused salt bath was used to heat samples isothermally at temperatures from 927" to 1260°C for various lengths of time. Torque magnetometer measurements were made on 1-in.-diam disc specimens before and after annealing, since magnetic torque curves supply information on textures and texture changes. Surface layers of the strip samples were polished and etched to reveal the grain structure. The diameters of grains were measured from micrographs at X100. The average value of diameters of matrix grains was established. Individual grains in the micrograph were cut out separately along grain boundaries. These grains were classified either as matrix grains or growth grains. The percent weight of growth grains in the cut-out patterns was reported as percent growth. Manv of the individual grains in the annealed samples were large enough to be X-rayed with a 5-mil beam for Lauegrams. Complete (110) pole figures were obtained for the primary recrystallized structure and short-time annealed structure with CoKa radiation at 30 kv in the back-reflection range, such as (220) for (110) poles, as described recently by Newkirk and ~ruce.~ Both the X-ray optics and the technique for pole figure differed slightly from those adapted previously.4

Jan 1, 1960

By C. A. Siebert, S. H. Bush

Isothermal temper-embrittlement studies were conducted on a 5140 steel at various temperatures for times as long as 3000 hr. Specimens from the embrittled steel were subjected to impact tests, metallographic examination, microhardness, and lattice-parameter measurements. SEVERAL of the steels in the low alloy group are subject to a pronounced decrease in impact energy if held within, or cooled slowly through, a range of temperatures below the lower critical. This phenomenon, known as temper embrittlement, is quite pronounced in the chromium steels of which AISI 5140 is typical. This study considered the response of one heat of 5140 steel when embrittled isothermally at various temperatures for times as long as 3000 hr. Excellent reviews of the work done in the field of temper embrittlement have been written by Hollomonl and Woodfine.' Both authors list the various theories which have been advanced to explain temper embrittlement. Some of the mechanisms considered were: 1—a transformation below 700°C; 2—an allotropic modification of iron; 3—precipitation from the ferrite of such compounds as carbides, nitrides, phosphides, or chromium oxides; 4—decomposition of retained austenite; 5—modification of special carbides; 6—grain-boundary segregation; and 7—selective distribution of carbides. The present study investigated the changes in hardness, Meyer's number, impact properties, micro-structure, and lattice parameter which occurred on embrittlement. Previous studies considered the influence of microstructure and of prior austenitic grain size3 on the response of 5140 steel to temper embrittlement. Equipment and Procedure All samples were taken from one heat of 5140 steel; the chemical composition of this steel was: 0.43 pct C, 0.86 pct Mn, 0.020 pct P, 0.019 pct S, 0.27 pct Si, 0.84 pct Cr, 0.10 pct Ni, 0.06 pct Mo, 0.10 pct Cu, and the remainder Fe. The material was received as % in. rounds. This stock was cut down to blanks measuring approximately 0.425~0.425~2.196 in. Heat Treatment: The rough blanks were normalized at 1600°F (870°C) for 1 hr, then austenitized at 1600°F (870°C) for 1 1/2 hr, and quenched into an agitated oil bath. The specimens were tempered at 1275°F (690°C) for 5 hr and water quenched. These tempered specimens were designated as the toughened state. Embrittling Treatments: The tempered bars were divided into sets and subjected to the various embrittling treatments listed in Table I. Temperatures from 750" to 1050°F were investigated for times of 1 to 3000 hr. Special tests to determine the effect of heating a short time at a higher temperature after long-time embrittlement at some lower temperature were also conducted. All specimens were water quenched at the end of the embrittling cycle, then ground and notched to obtain standard Charpy V-notch specimens. Impact Tests: The bars were fractured in a 260 ft-lb Charpy impact unit; specimens were fractured at temperatures ranging from —315°F to room temperature. Fixed temperatures used consisted of —315°F with liquid nitrogen, —115°F with dry ice and acetone, and 32°F with ice and water. Intermediate temperatures were obtained by suspending the bars in a jig over the liquid nitrogen, dry ice and acetone, or ice and water.

Jan 1, 1955

By Richard B. Reese, George R. St. Pierre, Robert A. Rapp

The vapor pressures of pure iron and pure chromium have been measured using a Knudsen cell coupled with a mass spectrometer. The experimental results agree well with some previously reported data; heats of sublimation and vaporization have been calculated. From vapor pressure rr~easurernents, the activities of iron and chromium in their binary alloys have been determined for NcY = 0.10 to 0.65 over a 1400" to 1700~ temperature range. The activity of chromium in the liquid alloys was found to exhibit positive deviation from ideal behavior when referred to solid chromium as the standard state; however, for the activity of chromium referred to nonequilibrium undercooled liquid chromium as standard state, the activity behavior is almost ideal. ALTHOUGH the Fe-Cr system is important as the basic system of alloy steels, the thermodynamic properties of this system have not been thoroughly investigated at elevated temperatures. In view of the potential practical applications of such data as well as their contribution to alloy theory, further study of the Fe-Cr system was undertaken. In addition, further development of experimental techniques for equilibrium measurements at high temperature is required. The present research involved an application of the Knudsen effusion method in conjunction with a time-of-flight mass spectrometer. Belton and ~ruehan' have measured the activities in Fe-Ni and Fe-Co alloys by a similar method. Speiser, Johnston, and lackbburn' have determined the vapor pressure of pure solid chromium between 1283" and 1561°K by a Langmuir free evaporation technique. The vapor pressure of chromium was described by the expression: over the temperature range 1283" to 1561°K. McCabe, Hudson, and paxton3 have measured the vapor pressures of pure iron and pure chromium by the Knudsen cell technique around 1500°K. The vapor pressure and heat of sublimation at O°K, AH,", for pure chromium agreed within experimental error with the measurements of Speiser et al. at 1200°C. Kubaschewski and HeYmer~ determined the vapor pressure of pure solid chromium in the temperature range 1170" to 1400°C by the Knudsen effusion technique combined with a radioactive tracer analysis of crS1. Their results agreed with the work of previous investigators. Edwards, Johnston, and Ditmars5 have measured the vapor pressure of pure solid iron by the Langmuir technique between 1356" and 1519°K. The vapor pressure of solid iron in the temperature range studied was given by: The data of McCabe, Hudson, and paxton3 on the vapor pressure of pure iron around 1500°K by the Knudsen effusion technique were in good agreement with those obtained by Edwards et a~.~ Hultgren, Orr, Anderson, and Kelley give the selected values for the AH: of pure iron and pure chromium as 98,990 *200 and 94,340 * 500 cal per mole, respectively. These values are the average values determined in the several investigations by different methods. The Fe-Cr phase diagram7 is shown in Fig. 1. Previous determinations of activities in this system have been carried out by several investigators, but most of the work has been done on solid alloys. Using a Knudsen effusion method with cr5', Kubaschewski and Heymer4 reported that the Fe-Cr system exhibits positive deviation from the ideal behavior for compositions ranging from NCr = 0.0398 to 0.699 at 1170"

Jan 1, 1969

By M. P. E. Desvaux, P. Charsley

OLIP-line observations on copper alloys, using the electron microscope, have been made by a number of workers,13 but this work has been confined to a brass. In a CuAl alloys Koppenaal4 and Koppenaal and Fine5 have made observations with the optical microscope and by the use of interferometry. They found that the observed slip step heights inside the Liiders bands accounted for only 42 pet of the total macroscopic strain. The suggestion was put forward that optically unresolvable slip in other parts of the specimen accounted for a major part of the macroscopic strain. This is surprising since it is known from other workers that slip in a brass is inhomogeneous; i.e., large amounts of slip occur on individual {lll) closelys paced than being shared by a large number of closely spaced planes. Furthermore, a brass and a CuAl alloys with high concentration of aluminum exhibit similar deformation characteristics and slip-line patterns. Prior to investigations into the behavior of copper and a CuAl alloys under reversed stresses in tension and compression, some preliminary experiments have yielded results which the authors think resolve this discrepancy, and throw some further light on the behavior of a CuAl in tension. An experiment was carried out on a 10 at. pet CuAl single crystal, of gage length 7.5 cm, diameter 3.1 mm, and orientation shown in Fig. 3 (inset), for the purpose of resolving the above discrepancy. The specimen gage length was electropolished for 10 min in a 50:50 orthophosphoric acid (SG=1.75)-distilled water system, with 2 v across the cell and a current density of 0.5 amp per sq cm. The cathode was made of copper. After a tensile strain of 0.067 ± 0.001, intense slip was observed over a length 2 cm of the gage length whilst the rest of the specimen was relatively undeformed. In the lightly deformed region, slip bands of mean width 20 /x were spaced about 1 mm apart on average. The transition from the heavily slipped region (usually called a Liiders band) to the lightly deformed region was gradual, the slip-band density increasing as the "Liiders band" was approached. In the latter, the slip bands became so close together that, to the naked eye, the specimen appeared to be continously slipped, and the typical microtopography of this region is shown in Fig. 1. Twelve electron micrographs were taken at random from replicas of the Liiders-band region, and the widths of the slip lines were measured. The slip lines account for an over-all tensile deformation of 7.0 ± 0.7 pet, after allowing for the lengths of the un-slipped regions, which is in good agreement with the macroscopic strain. The distribution of slip-line widths was also measured and is shown in Fig. 3. Since Koppenaal could not resolve slip lines with height less than 540A (limit of resolution represented by dashed line), then it was deduced that he could have measured only about 50 pet of the deformation within the 'Liiders Band'. It is concluded, contrary to the suggestion of Koppenaal,5 that virtually all the macroscopic strain is accommodated within the "Luders band" and that there is no need to invoke fine slip distributed uniformly over the gage length.

Jan 1, 1967

By E. L. Dougherty

A phenomenological theory for a one-dimensional unstable miscible displacement similar in type to the Buckley-Leverett model but including the effects of mixing is proposed An equation giving the fractional flow of pure solvent through an oil phase containing dissolved solvent is derived including the effects of gravity and nonbomogeneities. Numer ical integration of the resulting pair of nonlinear hyperbolic partial differential equations gives volumes of dissolved and undissolved solvent as functions of space and time. Parameters in the model which characterize mixing due to dispersion were determined from experimental data; the parmeters correlated with viscosity ratio. The results indicate that the rate of dispersive mixing is proportional to volumetric flow rate Incorporated into our equations were Koval's heterogeneity factor H. which characterizes mixing due to channeling. This allowed satisfactory predictions of displacement behavior observed in horizontal floods in nonhomo-geneous cores; but in most cases the values of H which we used were considerably larger than those used by Koval. INTRODUCTION It has been shownl,2,3 that for favorable viscosity ratios, the diffusion equation with convection satisfactorily describes the behavior of a miscible displacement in a porous media. Numerous attempts to develop a satisfactory mathematical description for the case of unfavorable viscosity ratio have been reported, but they have met with only partial success. These attempts, which are reviewed by oval! have taken two approaches: (1) development of a flow model akin to the Buckley-Leverett approach for immiscible displacement neglecting the effects of mixing5,6 and (2) simultaneous application of Darcy's Law for flow and the diffusion equation with a convection term for mass transfer.7,8,9 We set out to construct a mathematical model of Type 1 including, though, the effects of mixing. Based upon a set of hypotheses, we derived a pair of nonlinear hyperbolic partial differential equations which describe in a one-dimensional system the combined effects of flow and mixing. To work with these equations it was necessary to develop a fractional flow formula. The combined system was integrated numerically using the method of characteristics. In our equations the mixing process is characterized by four parameters. Three of these, labeled ß, P1 and P2, account for dispersive type mixing. The fourth is the heterogeneity factor H, proposed by Koval to account for channeling due to nonhomogeneities in the porous media. Values of the parameters which would cause agreement between theory and experiment were determined by trial-and-error for miscible floods conducted in horizontal cores of both homogeneous and heterogeneous materials. Calculations were also performed for vertical floods in homogeneous cores. The purpose of this paper is (1) to present the details of the mathematical analysis, (2) to present the results of the calculations, (3) to consider what light the results shed on the mixing process in an unstable miscible displacement, and (4) to provide a firmer foundation for the correlation technique developed by Koval for predicting the behavior of unstable miscible floods. STATEMENT OF PROBLEM The problem is to construct a mathematical model which describes in one dimension the observed behavior in an unstable miscible displacement. The approach is phenomenological in that the equations are based on assumptions which violate certain physical precepts known to apply to the displacement phenomenon. However, the assumptions do allow us to account mathematically for the more essential phenomena. The work is of value if we can quantitatively predict experimental results which heretofore could not be predicted, even though the synthetic nature of the model belies complete explanation of the observations. We assume that the system is comprised of two contiguous flowing phases. One phase, which we call free solvent, has the properties of pure solvent. We call the fraction of the pore volume occupied by this phase the solvent saturation, designated s. The oil phase consists of oil containing dissolved

By A. E. Powers, J. F. Libsch

THE simultaneous influence of time and temperature upon the tempering process in steel is well known. Hollomon and Jaffe¹ have expressed the effect of time and temperature upon the progress of tempering by a single parameter, T (c + log t); where T is the absolute temperature; t, the tempering time; and c, a constant characteristic of the steel and treatment. It was found that when hardness data for plain carbon and low alloy steels were plotted vs. this parameter, a master tempering curve was obtained which satisfied all the data for a given steel and a given hardening treatment. Roberts, Grobe, and Moersch² successfully applied the tempering parameter to various tool steels, including high speed steel for tempering times ranging from 6 min to 100 hr. The influence of tempering time and temperature upon the physical properties of high speed steel has also been extensively investigated.'" Recently, the use of induction heating for very rapid tempering treatments has received attention. The authors% have shown that tempering treatments of only a few seconds duration may be successfully applied to plain carbon and low alloy steel. However, the influence of such short tempering treatments in high speed steel has not been explored. Since high speed steel is a highly alloyed steel exhibiting physical reactions during tempering that are often relatively slow and large in magnitude, it is an interesting steel for the study of tempering reactions. It was the purpose of the present investigation, therefore, to study the early progress of reactions leading to secondary hardness in high speed steel, type 6-5-4-2, and to determine if induction-tempering treatments of a few seconds duration are able to produce results equal to those of more conventional long-time tempering cycles. Experimental Details The chemical compositions for two different heats of W-Mo high speed steel used in this study are given in Table I. Table II summarizes the heat treatment given various groups of specimens cut 21/2 in. long and centerless ground to ¼ in. diam. Hardening treatments consisted of preheating to 1600°F (870°C) for V2 hr and then oil quenching from 2250°F (1230°C). Heat I was subjected to the high temperature in a salt bath for 3 min, while specimens of heat II were austenitized in a carbon-block muffle furnace for 10 min. Specimens of series E were immediately refrigerated to — 318°F (— 195°C) in liquid nitrogen following the hardening treatment to transform the major portion of the retained aus-tenite. Specimens of series F and G were subzero cooled to — 100°F (-75°C) in a dry ice-alcohol mixture. Induction tempering was performed with a Lepel high frequency converter operating at a frequency of approximately 300,000 cycles per sec. Heating cycles were controlled and recorded for each specimen using a chromel-alumel thermocouple, percussion welded to the surface of the specimen, and a modified high speed instrument with a timer previously used and described.' Temperature oscillation of the specimens, while being held at the tempering temperature, was ± 15°F (8°C). Tempering Treatments: After hardening, specimens were tempered between 900" and 1500°F (480" and 815°C) to study the progress of retained austenite decomposition and secondary hardening. The specimens tempered in salt for 1 hr (series C, G, and I) were considered to represent conventional treatment and are used for comparison with rapid tempering treatments. Several induction-tempering cycles were employed: 1—flash tempering, i.e., induction heating to the tempering temperature and immediately cooling (series A, E, and F); 2—induction heating for 60 sec at temperature (series B); and 3—double-induction tempering by two successive heating and cooling cycles (series D). All specimens tempered by induction were heated at an initial rate of 450°F (250°C) per sec except those of series E, which were heated at an initial rate of 1300 °F

Jan 1, 1952

By A. L. Lee, M. H. Gonzalez, R. F. Bukacek

Experimental viscosity data for methane are presented for temperatures from 100 to 340F and pressures from 200 to 8,000 psia. A summary is given of the available data for methane, and a comparison is presented for that data common to the experimental range reported in this paper. Correlation of the data is presented, and predicted values are given for temperatures up to 460F and pressures up to 10,000 psia. INTRODUCTION The increasing ranges of temperature and pressure at which fluids are produced, transferred and processed in the petroleum and chemical industries stress the need for accurate information on physical properties, both for engineering calculation and for improving the methods used to estimate physical properties. A survey of the literature reveals that disagreements between published data on the viscosity of methane are common and that most investigations have been conducted over restricted temperature and pressure ranges. This situation made it desirable to undertake an investigation with a scope common to most of the literature data available. APPARATUS AND MATERIALS The apparatus used in this investigation was the capillary tube viscometer'described by Dolan,10 with modifications introduced in the general design and operation of the instrument. It has an effective pressure range from 14.7 to 10,000 psia and a temperature range from room temperature to 400F. The design of the viscometer is based on the establishment of a manometric head between two vessels containing the test fluid and a volume of mercury. The reservoirs are connected by a capillary tube through which the test fluid flows and a tube through which mercury flows. A pressure gradient is established by elevating one of the vessels above the other, the resulting flow of mercury displacing the test fluid through the capillary. The schematic diagram of the system (Fig. 1) shows the arrangement of the equipment auxiliary to the viscometer. The density cells assembly (E, Fig. 1) was not used in this investigation since reliable data are available on methane. 23 The assembly consists of a bank of eight 316 stainless steel pycnometers. Experimental values of the density of a natural gas19 and i-butane14 samples have been obtained for pressures up to 8,000 psia and temperatures up to 340F. The methane used was obtained from the Southern California Gas Co. Mass spectrometric analysis showed a composition of 99.8 percent CH4, 0.1 percent C2H6 and 0.1 percent C3H8. EXPERIMENTAL VALUES AND ACCURACY OF DATA Determinations were carried out at several temperatures. With the temperature in the cabinet controlled at a given level, a series of runs were made at various pressures. To establish pressures lower than that obtained from the methane cylinder, it was necessary to vent the gas slowly to the atmosphere until the desired pressure was reached. The consistency of the test run time for a particular condition can be used as a criterion for the accuracy of the data. A further check is obtained by comparison of the viscosity values obtained using different driving heads. To establish the instrument's reproducibility, a large number of runs were made at three completely different conditions of temperature and pressure. Data obtained were analyzed statistically to determine the most reliable value for the variance of the experimental data. It was found that the variances of the data taken at different experimental conditions were not statistically equivalent, but they were small. The largest variance was found at 8,000 psia and 100F, where the standard deviation was 0.385 micropoise. Therefore, 99.9 percent of the data can be expected to fall within 1.15 micropoises of the population mean, except for the intervention of systematic errors in operation.

By J. A. Musselman, P. F. Gnirk

A study was made of indexed penetrations by a single dull bit tooth under statically applied loads into rock subjected to confining pressures from atmospheric to 5,000 p.si and atmospheric pore pressure. Experimental results obtained with a 45" wedge tooth over the above range of pressures are presented for two limestones and a sandstone, a variely of indexing distances and two degrees of tooth dullness. The optimum distance between successive bit-tooth penetrations required for maximum rock damage and chip formation decreases substantially with increa.sing confining pressure above the brittle-to-ductile transition pressure of a particular rock. However, the distance remains approximately constant for a variation in confining pressure below the transition pressure. At a given confining pressure, the bit-tooth force required lor chip formation is constant for indexing distances greater than optimum, but generally decreases linearly with decreasing indexing distance for distances less than optimum. The chip-formation force data obtained at confining pressures for which the chip-generation mechanism is macroscopic-ally of a pseudoplastic nature compare favorably with previous theoretical results for indexed dull hit-tooth penetrntion into an idealized, rigid, perfectly plastic rock. INTRODUCTION To study the cutting action of a roller-cone bit, the interaction of a penetrating bit tooth with craters formed in a rock surfacc by the passage of previous bit teeth must be considered. Current knowledge of the basic mechanics of bit tooth-rock intcract:on under simulated borehole environmental conditions has been extensively reviewed.',' Particularly of current interest are the effects of bit-tooth shape, distance between successive penetrations and differential pressure at the rock surface on the extent of the interaction. Pertinent to this paper are results of an experimental investigationb f the interaction between successive penetrations by sharp, wedge-shaped bit teeth. It was demonstrated that both bit-tooth angle and differential pressure influence the extent of rock damage between successive bit-tooth penetrations. Specifically, the optimum or minimum distance between successive penetrations required for maximum interact'on or chip generation tends to decrease with decreasing bit-tooth angle and increasing differential pressure. In addition, at differential pressures on the order of 2,000 psi for four va- rieties of limestones and sandstones, the macroscopic mechanism of chip formation exhibits a transition from brittle to ductile. In this paper, experimental consideration is given to successive or indexed penetrat ons by wedge-shaped bit teeth. Since pore pressure in a rock sample is maintained at atmospheric pressure, the differential pressure at the fluid-rock interface is equal to the confining pressure. The degrees of bit-tooth dullness include teeth with flat and round apexes (Fig. 1). Of primary concern in this paper are the bit-tooth forces required for chip formation, the macroscopic mechanism of chip formation and the minimum distance between successive penetrations, i.e., optimum indexing distance required for maximum rock damage, as functions of differential pressure. Of further interest is a comparison of actual bit-tooth chip formation forces at elevated differential pressures with calculated forces from previous theoretical results4 for indexed dull bit tooth penetration into a rigid-plastic rock. EXPERIMENTAL APPARATUS AND PROCEDURE The experimental apparatus consists of a pressure vessel equipped with a piston through the side of the vessel (Fig. 2). A single bit tooth inserted in the lower end of the piston is forced at a desired rate into the rock when the ram pressure chamber is pressurized. Electrical instrumentation incorporated into the apparatus yields a graphical plot of force on the piston as a function of bit-tooth penetration or displacement into the rock. Since the piston and ram assembly are in force equilibrium for a constant confining pressure in the main vessel, the fluid volume in the vessel remains constant during bit-tooth penetration. Hence, the force resisting penetration of the tooth is independent of the force exerted on either end of the as-

By P. E. Schauer

During the initial nine-year deple-tion of the McKamie-Patton pool gas-condensate reservoir, the pressure behavior and fluid analyses indicated pressure maintenance by gas injection would be attractive relative to continued pressure depletion. As a result, a gas cycling program was inaugurated in Aug., 1949, which has since maintained reservoir pressure. In order to evaluate the benefits of this program, the recoveries for natural depletion and for cycling followed by blowdown were determined by calculating the fractional balance of the molar quantities of vapor and liquid remaining in the reservoir and produced at the surface for various stages of depletion. The results of the investigation show theoretical ultimate recovery due to the cycling program will be 42 per cent greater than would be realized under pressure depletion type operation. INTRODUCTION The benefits of gas injection pressure maintenance programs in condensate reservoirs have been recognized and qualitatively described in several papers1-8 during the past 15 years. Some of these papers also describe methods for calculating the increased recovery realized from cycling; however, as a rule, hypothetical reservoirs were used as examples".'.. This paper presents an evaluation of the pressure maintenance program for the McKamie-Patton condensate reservoir and includes a description of the fractional balance method employed to determine the benefits. Reservoir Development and Characteristics The McKamie-Patton pool, Lafayette County, Ark., was opened in June, 1940, with production obtained from the oolitic Smackover lime at a depth of approximately 9,300 ft. The structure is an anticline 8 miles long by 1 to 2 miles wide, and is one of many productive Smackover structures in Southern Arkansas. Of predominant importance is the condensate-bearing gas cap portion of the reservoir, which covers approximately 4,000 acres, attains a maximum thickness of some 200 ft, and has an average thickness of 90 ft. Development of the cap was accomplished with 21 wells drilled on 160 acre spacing. An isopach map of the cap is shown in Fig. 1. In addition, an oil rim is present along most of the periphery of the pool. Production practice includes field separation of black oil, and a high pressure gathering system which carries total well stream from gas cap wells to a plant where condensate is separated and the gas is processed for recovery of natural gasoline, butane, and propane. Since the gas contains appreciable hydrogen sulfide, it is removed by amine contact, after which free sulfur is produced by the Claus process. Core analyses from 1,767 gas cap formation samples averaged 14.2 per cent porosity and 379 md dry air permeability. Connate water was restored on seven samples of gas cap rock by air-brine capillary techniques, from which the interpreted water saturation averaged 28.17 per cent. During the early life of the field, it was believed the recovery mechanism, based on several of the other regional Smackover reservoirs, might be a natural water drive. However, subsequent production and pressure history revealed that the gas cap would not be produced by water drive, but would behave as a closed reservoir. In this respect, during the nine-year period of natural depletion from initial production to Aug., 1949, the cap production of 84.3 billion

Jan 1, 1958

By W. W. Gerberich

SINCE the original formulation of fracture mechanics concepts,&apos;y2 relatively little work has related the fracture mechanics description of metal behavior on a gross, structural component scale to the behavior of its microstructural constituents. The purpose of this note is to suggest the utilization of fracture mechanics to describe material behavior on a microscopic scale. A Fracture Concept for Two-Phase Structures. A critical displacement concept considering the tough unidirectional phase in a relatively brittle matrix is first examined. It is assumed that a flaw exists at position 1 as depicted in Fig. 1. As the crack moves from position 1 to 2 the plastic zone could be of the shape described with the size approximated by the Dugdale3 model: where c is the half-crack length, OO is the applied stress, and oyS is the yield strength. Hahn and Rosen-field4 have presented a simple fracture criterion for homogeneous materials based upon the displacement at the crack tip. They also have shown the equivalence of the critical displacement, v*, to fracture toughness by Kc = (2v*oysE)1/2 [2] The displacement at the crack tip is given by and the displacement at any distance in front of the crack tip may be determined knowing the plastic zone size and utilizing the development of Goodier and Field.5 Recalling Fig. 1, the value of v* for fracture in material M1 may be calculated from Eq. [2] providing the critical stress intensity factor is known. As the material is loaded, when vc > vM1 the crack moves from position 1 to position 2 where it encounters the tough second phase. If vc2 < vm2, then the crack will be arrested providing the width of the M2 phase is sufficiently large. This condition is necessary since the displacement at position 2 has increased due to the longer crack length. Thus, the displacement at the distance X (representing the dimension of the second phase) in front of the crack may be larger than the critical displacement for failure in the brittle material. If v, > vm, then failure will proceed in the brittle material. The value of v, may be calculated as indicated above. This latter consideration is the same as predicting fracture of a brittle second phase at some distance in front of a crack located in a ductile matrix. Experimental Evidence. On a macrostructural scale, tungsten wires in a ductile Be-Cu matrix are seen to fracture well ahead of the main crack front in Fig. 2. Utilizing a Kc value of 14.2 ksi-in.1/2 obtained by Schroder et al.6 for as-received tungsten, the critical displacement 2v*, for fracture is calculated from Eq. [2] to be about 6.5 X 10-5 in. The crack tip displacement, 2vc, is calculated from Eq. [3] to be 0.0028 in. indicating that fracture would occur at a considerable distance in front of the crack tip. From the ratio of v*/vc and the plastic zone estimate of Eq. [I], the distance in front of the crack tip at which a tungsten wire should fracture is calculated to be about 0.195 in. As shown in Fig. 2, a fractured wire occurs at a distance of 0.140 in. (fractured in three places), not at 0.250

Jan 1, 1968

By E. J. Harris

Mathematical solutions to complex mine ventilation problems are possible, but often the airway network is so complex that the mathematical solution becomes tedious and impractical. A fluid network analyzer, designed and built for analyzing mine ventilation problems has been in service at the Bureau of Mines&apos; Pittsburgh station for approximately nine years. Using this analogue as a model, the mine ventilation network is simulated electrically by a combination of series and parallel circruits laid out to conform with actual mine airways. A tungsten filament lamp, referred to as a Fluistor, is used to simulate mine airway resistance. With the analogue ventilation model established, voltages of the proper amplitude to represent ventilating pressures are impressed across the circuit at points where mine fans and airshafts are located. Comparison of mathematical solutions of complex systems against analogue results showed a maximum variance of 3% for pressures and 2% for quantities. An electrical fluid network analyzer, designed and built especially for analyzing mine ventilation distribution problems, has been in service at the Bureau of Mines, Pittsburgh, for approximately nine years. It is a nonlinear, low voltage, fluid network analyzer of the type developed by the late Malcolm S. McIlroy, Professor of Electrical Engineering, Cornell University, who cooperated with G. E. McElroy, of the Bureau of Mines, in adapting the instrument to mine ventilation systems. Several modifications have been made since the original installation, but a considerable part of this paper is drawn from G. E. McElroy&apos;s original description of the analogue.&apos; The analysis of water or gas distribution systems2,3 led to the development of this type of network analyzer. Several similar units are now employed by utility companies for this purpose; however, the Bureau of Mines unit is the only one designed specifically for mine airflow problems. Other airflow analogues employing a similar principle have been used at the Central Research Station of the Netherlands State Mines,4 in England,5 and in South Africa.6 Information on these devices indicated they were somewhat inflexible because commercial lamps with a sufficient range of resistance are difficult to obtain. Computers for mine ventilation analysis have been developed in Germany which instead of lamps use a variable resistance to adjust for turbulent flow laws. These units are expensive, but excellent results have been reported in their application. THE ANALYZER Theory of Application: As airflow generally follows the law of turbulent fluid flow, resistance to flow is nonlinear; consequently, the problem has been to find a nonlinear resistance element of suitable range that can be used for electrically simulated airflow. Tungsten filament lamps operated on alternating or direct current approximate the square-law resistance characteristics of mine airflow over a large range below maximum or rated voltage; that is, the voltage drop varies approximately as the square of the current. Consequently, the heart of the network analyzer is a nonlinear resistor known as a Fluistor, which is simply a custom-made low voltage, tungsten filament lamp that is available in a progressive series of relative resistance values ranging from 0.05 to 500 in nominal 5% steps. However, variations in manufacturing large groups result in differences of 1 to 3%, but series arrangements required for high-loss branches can be matched within about 1%. Utilizing a combination of Fluistors and load circuits, the mine ventilation system is duplicated electrically. Intake load circuits are connected from power intake to primary points of the circuit network; segments of unregulated flow along intakes and returns are represented by Fluistors, regulated splits and leakage paths are represented by load circuits and Fluistors of proper capacity; and mine exhausts are connected to ground from the last point of the network to complete the circuit. For the special purpose of representing booster fans or natural draft conditions, boosters or separate source circuits are provided that can be inserted between any two points of a network to increase voltage to the required value. Physical Layout: The analyzer consists of three 42

Jan 1, 1963

By Smith, George Otis

THE matter that I have on my mind this evening is engineering&apos;s need of an open forum. Our fathers of three centuries ago were pro-testanta for freedom of speech and thought in matters religious; later, our fathers were revolutionists for freedom of speech in matters political; until today freedom of speech has become so universal throughout the land that even in the sanctuary of our homes, at times, we have to turn off the loud-speaker. Talk is not always a condition of progress, but light is everywhere necessary to growth, whether the growing thing is a blade of grass, a baby chick, or a young idea, and we must regret anything that tends to shut out the light from the operations of business and industry. Of course, I realize there is little that is novel in what I am saying. Indeed, I have found that Dr. James Douglas-a name we love to honor in our Institute-as long ago as 1907, gave an address at the Toronto meeting that any of us would be proud to be author of twenty-one years after. Dr. Douglas at that time spoke on secrecy in the arts and the text then taken by this leader in metallurgical technique and in the constructive management of big business was "the dangerous temptation to adopt secretive methods by very large corporations." In both thought and language Dr. Douglas was direct and vigorous and he needs no internreter. He advocated the wide open door for ideas on two counts: advancement of technical knowledge and education of public opinion. A few sentences will serve not only to prove the vision of James Douglas, but also, I hope, tempt you to hunt up his address in the Institute&apos;s TRANSACTIONS, and thus get his whole thought first hand.

Jan 1, 1928

By William R. Patterson

ACCORDING to the phase diagram for the Mn-Ni system,&apos; the high-temperature, fcc y-manganese solid solution is stabilized to below room temperature, in the range approximately 22 to 28 wt pct Ni. However, pearson2 cites evidence in the literature showing that for manganese contents greater than about 75 wt pct the quenched phase in Mn-Ni alloys is fct. This is in keeping with zener&apos;s3 suggestion that in manganese-rich alloys the fcc high-temperature phase undergoes a diffusionless or martensitic transformation to a fct structure upon quenching. Work by Basinski and christian4 on manganese-rich compositions in the similar alloy system Mn-Cu established that in alloys of greater than about 82 wt pct Mn the y-manganese phase underwent a fee fct martensitic transformation upon quenching to room temperature. Striking evidence for this martensitic transformation was the highly twinned or banded microstructure, an example of which is shown in Fig. 1. Similar microstructures have also been found in quenched Mn-Cr5 and Mn-Au6 alloys. In the present investigation, we attempted to obtain similar evidence of a fcc — fct martensitic transformation in manganese-rich Mn-Ni alloys. Manganese alloys in the range 10 to 30 wt pct Ni were prepared by arc-melting, under argon, at atmospheric pressure. The alloys all were 50 g in size, and negligible weight loss occurred during melting. The starting materials were electrolytic manganese and nickel, both of 99.9+ pct purity. The alloys were subsequently homogenized 48 hr at 1750°F, hot-rolled 50 pct at 1700°F, annealed 2 hr at 1700°F, and water-quenched to room temperature. All heat treatment was done in purified argon. Both X-ray and metallographic techniques were used to examine the structures of the quenched alloys. X-ray diffractometer studies were conducted on powder specimens obtained from filings rean-nealed 2 hr at 1700°F in argon and water-quenched. Identification of the intensity peaks from the diffractometer counter traces showed that below about 10 to 12 pct Ni the y phase decomposed partially upon quenching to give an a- + ?-manganese structure. In the range approximately 12 to 25 pct Ni, the structure was found to be fct ? manganese with a c/a ratio approaching 1.0 at 25 pct Ni. Beyond approximately 25 pct Ni, the structure remained fcc. These results, including lattice-parameter determinations, are given in Table I. Metallographic examination. was carried out on specimens polished and etched after quenching, and also on polished specimens reannealed and quenched. In the first case, the distinctive twinning or banding so prevalent in Mn-Cu alloys was sought, while in the second, the surface relief effect generally regarded as being truly characteristic of a martensitic transformation was sought. The microstructure of representative alloys in the range 12 to 25 pct Ni is shown in Fig. 2. The structure of the Mn-15 pct Ni

Jan 1, 1965

By Richard M. Foose

Five miles southwest of Mt. Holly Springs, Cumberland County, Pennsylvania, the Philadelphia Clay Co. has been mining and milling a white clay since 1896; for use in white cement, as a filler in rubber, pigment and paper, in the manufacture of insecticides, and for other minor purposes. Until late in 1942, when the mine was abandoned because of labor shortage, combined underground mining and surface stripping produced approximately 30,000 tons of clay a year, of which 10,000 tons were refined in the mill. Geology Lower Cambrian Antietam quartzite and the Rilontalto quartzite, stratigraphi-cally older, trend N.55°E. and make a sharp 1600-ft. anticlinal ridge of the South Mountains. The Tomstown dolomite overlies the Antietam quartzite on the southeast flank of the anticline, which is displaced near its crest by a steeply dipping oblique fault. Erosion of the less resistant Tomstown formation has resulted in a narrow valley at an elevation of 700 ft. Directly on top of the Antietam quartzite and at the base of the Tomstown formation is a zone of sandy white clay, lenticular along the strike of the formations, ranging in thickness from 10 to 300 ft. within a mile. All of the formations dip steeply to the southeast, from 65" to vertical. The clay crops out at an elevation of about 1000 feet. Origin and Character The uppermost part of the Antietam formation is sericitic and schistose at many places, and at all these places weathering is in an advanced stage. The clay is the residual product of weathering of this sericitic quartzite or sandy schist. The crude clay has the physical aspect of a sandy kaolin, but there Are large areas in the clay formation that are low in free silica, and commonly the 30 ft. adjacent to the Antietam quartzite is notably free of silica. The overlying Tomstown dolomite has been weathered almost completely to a mixed yellow and brown clay, which carries a zone of nodular and chunky limonite and manganese ore, 4 to 12 ft. thick, about loo ft. from the contact with the white clay. In mining, this zone is an important "marker," indicating where the white clay may be expected in an advancing tunnel. The contact of the white clay formation with the yellow and brown clay of the Tomstown formation is relatively sharp, although the line of contact is irregular and therefore responsible for the lenticular character of the white clay formation. Following is an analysis of the refined clay containing less than one per cent of moisture when dried at 212°F.: SiO2, 67.05 per cent; Al2O3, 22.27; Fe2O3, 0.40; CaO, 0.00; TiO2, 1.05; MgO, 0.52; Na20, 0.04; K2O, 0.88; ignition loss, 7.65; total, 99.86.

Jan 1, 1948

By Richard M. Foose

Five miles southwest of Mt. Holly Springs, Cumberland County, Pennsylvania, the Philadelphia Clay Co. has been mining and milling a white clay since 1896; for use in white cement, as a filler in rubber, pigment and paper, in the manufacture of insecticides, and for other minor purposes. Until late in 1942, when the mine was abandoned because of labor shortage, combined underground mining and surface stripping produced approximately 30,000 tons of clay a year, of which 10,000 tons were refined in the mill. Geology Lower Cambrian Antietam quartzite and the Rilontalto quartzite, stratigraphi-cally older, trend N.55°E. and make a sharp 1600-ft. anticlinal ridge of the South Mountains. The Tomstown dolomite overlies the Antietam quartzite on the southeast flank of the anticline, which is displaced near its crest by a steeply dipping oblique fault. Erosion of the less resistant Tomstown formation has resulted in a narrow valley at an elevation of 700 ft. Directly on top of the Antietam quartzite and at the base of the Tomstown formation is a zone of sandy white clay, lenticular along the strike of the formations, ranging in thickness from 10 to 300 ft. within a mile. All of the formations dip steeply to the southeast, from 65" to vertical. The clay crops out at an elevation of about 1000 feet. Origin and Character The uppermost part of the Antietam formation is sericitic and schistose at many places, and at all these places weathering is in an advanced stage. The clay is the residual product of weathering of this sericitic quartzite or sandy schist. The crude clay has the physical aspect of a sandy kaolin, but there Are large areas in the clay formation that are low in free silica, and commonly the 30 ft. adjacent to the Antietam quartzite is notably free of silica. The overlying Tomstown dolomite has been weathered almost completely to a mixed yellow and brown clay, which carries a zone of nodular and chunky limonite and manganese ore, 4 to 12 ft. thick, about loo ft. from the contact with the white clay. In mining, this zone is an important "marker," indicating where the white clay may be expected in an advancing tunnel. The contact of the white clay formation with the yellow and brown clay of the Tomstown formation is relatively sharp, although the line of contact is irregular and therefore responsible for the lenticular character of the white clay formation. Following is an analysis of the refined clay containing less than one per cent of moisture when dried at 212°F.: SiO2, 67.05 per cent; Al2O3, 22.27; Fe2O3, 0.40; CaO, 0.00; TiO2, 1.05; MgO, 0.52; Na20, 0.04; K2O, 0.88; ignition loss, 7.65; total, 99.86.

Jan 1, 1948

By J. H. Frye, J. W. Caum

ONE of the most important methods of increasing the hardness of metals is alloying. In spite of the widespread use of alloys, the fundamental mechanism of alloy hardening is little understood. This is true even of the simplest form of alloy, the primary substitutional solid solution in which solute atoms substitute for solvent atoms at random in the crystal lattice of the latter. A fundamental understanding of the mechanism of solid-solution hardening would be important, both because of the widespread use of alloys of this type and because of the light that might be thrown on the mechanism of hardening in more complicated alloys. The present investigation covers the hardness of primary substitutional solid solutions of zinc, gallium,, germanium; and arsenic in copper. All of these are B subgroup elements from the third period of the periodic table. Cu, Zn, Ga, Ge, and As are in groups I, II, III, IV, and V, respectively and lie just to the right of the transition elements. Because of their cost, it is unlikely that Ga-Cu and Ge-Cu solutions will ever be of commercial importance, but the intent of this study has been to discover some of the fundamentals of solid-solution hardening and it has been demonstrated that such a study is far more likely to be fruitful if alloys are made up on the basis of position of the constituent elements in the periodic table than if commercially important alloys are used. Many investigations have. been made of the hardness of substitutional solid solutions, but lack of attention to purity of the metals, infrequent grain-size control, and the use of varying testing techniques have virtually invalidated any comparisons. The purpose of most investigations has been to solve immediate problems and not to solve the primary problem: Why do solid solutions usually have a greater hardness than pure metals? PREVIOUS WORK Theories have been advanced to account for the hardness of solid solutions,, but relatively little experimental work has been done. Perhaps the first experimental work of merit was that of Norbury1 on copper alloys. He showed that for several alloys there was a correspondence between the hardness of one atomic per cent solutions and atomic volume of the solutions. More recently Brick, Martin, and Angier2 have investigated the effect of various solute elements on the hardness of copper. They concluded that the hardening effect of these solutes depended "primarily on the difference in atomic volume of solute and solvent or, relatedly, upon the parameter, change of the solvent or the extent of solid solubility." They also observed the effect of these elements on hardness and texture developed by rolling and by annealing of rolled material. Austin3 examined the hardness and response to heat-treatment of various iron solid solutions. Frye and Hume-Rothery4 measured the hardness of a number of silver solid solutions containing approximately

Jan 1, 1943

By F. C. Holden, R. D. Buchheit

In the course of studies made on the Ti-Cu alloy system,&apos; particles identified visually as TiH were encountered unexpectedly in a specimen of high-purity Ti-0.8Cu alloy. The particles did not appear immediately after preparation, but following-storage in a dessicator for several days. Since the alloy had been vacuum annealed to a low hydrogen concentration (19 ppm by vacuum-fusion analysis), the appearance of the TiH particles was suspected as a surface contamination effect. A specimen of a Ti-0.8Cu alloy had been annealed 2 hr at 790°C and water quenched, to produce the single-phase equiaxed a structure. The metallo-graphic sample was ground through 600X paper, rough-polished on a high-speed wheel with a mixture of alumina and chromic acid, awLhish-polished on a slow-speed wheel. Disturbed metal layers were removed from the final surface by alternately etching with a 1 1/2 HF-3 1/2 HNO3-95 H2O solution and polishing on the slow-speed wheel with fine alumina. The final surface was swab-etched with a 1 1/2 HF-3 1/2 HNO3-95 H2O solution, rinsed in tap water, and dried in a stream of filtered air. The micro-structure, shown in Fig. 1, was composed of equiaxed a grains without any trace of second phase. After storage in a dessicator for 3 days, the appearance of small particles in the structure became evident (see Fig. 2). After 7 days of storage, the particles were more distinct, and in some grains, began to appear as elongated particles. The specimen then was etched a second time (without repolishing) to produce the structure shown in Fig. 4. On the basis of micro- structural observation, the line markings were identified as TiH; attempts to obtain diffraction patterns from the surface for positive identification were not successful. That the structure is a surface effect was demonstrated by grinding with 240X paper to remove the surface layer. The surface then was ground, polished, and etched using the procedures described previously. The same observations were made: the freshly prepared surface was devoid of any second phase, whereas the particles again appeared after several days storage. The same effect has been observed in other a-stabilized titanium alloys, including a high-purity Ti-0.20 alloy containing only 16 ppm H by analysis. The effect has not yet been observed in unalloyed titanium, nor does its appearance appear to be consistent with any particular alloy system. From these observations, it is concluded that certain a-titanium alloys are susceptible to the formation of titanium hydride at the surface of metallo-graphic specimens. The hydrogen probably is diffused into the surface from a residual film of etchant decomposition products. Estimates of the hydrogen

Jan 1, 1961

By J. A. Younkins, J. A. Brooke

In 1931 the Philadelphia Company acquired by lease several coal mines in southern Greene County, Pennsylvania. These mines were known as the "Dora," "Seventh Pool" and "Rosedale" mines in the Sewickley seam, and the "Rosemary," "Seventh Pool" and "Warwick" mines in the Pittsburgh seam. All these mines are in the immediate vicinity of Greensboro, Pa., with considerable river frontage on both sides of that village. The mines in each seam are contiguous and to some extent the properties in the two seams lie one above the other. In 1938 the property known as the "Sandy Run mine," in the Sewickley seam, adjoining the Dora mine, was purchased from the Fredericktown Coal and Coke Co. Altogether, by purchase and lease, the company gained control of approximately 3400 acres of coal land in Greene County, from which it was estimated that some 20,000,000 tons of coal could be extracted. Geology of Warwick Properties Both seams of coal outcrop along or near the river on both sides of the town of Greensbgro. They lie on the eastern slope of the Lambert syncline, near the southern end of the axis, consequently the predominant dip of the seams is away from the river, so that development for river handling has the unavoidable disadvantage of adverse grades for haulage to the outside. Predominant grades away from the river at right angles to the "butt" cleat of the coal average about 2.25 per cent dipping in a westerly direction, but local dips occur, which are considerably greater. Predominant grades parallel to the river and at right angles to the "face" cleat of the coal average about one per cent dipping in a northerly direction. Both seams of coal lie in the Monongahela formation, the Pittsburgh bed being the bottom measure of the formation and the Sewickley bed lying about 90 it. above. Approximately midway between the two lies the Redstone coal bed, which is generally thin and of erratic occurrence and therefore of little commercial value. It is mined only locally where it attains sufficient thickness. Sewickley Bed The Sewickley bed is commonly called the "five-foot" or Mapletown" seam, because in Pennsylvania it reaches its greatest thickness and has been mined most extensively in the vicinity of the village of illapletown, approximately one mile west of Greensboro. In the early development of the Warwick properties, which occurred near the river, the seam had an average of 5 it. 2 in. in height. As development proceeded away from the river, however, the height gradually decreased until the average height of the present workings is about 4 ft. 6 in. Present development is encountering lower coal

Jan 1, 1947