By Robert E. Goodwin

There are four main requirements to be considered in selecting a wire rope that will provide the best service. A proper choice is made by correctly estimating the relative importance of each of these requirements and choosing a rope with qualities that will best enable it to withstand the combination of destructive forces expected under continued service. A Good Rope Choice Matches Strength with Stress A wire rope should be (1) strong enough to sup- port the maximum load anticipated with a proper safety factor, (2) able to withstand bending and to resist bending fatigue without failure of the wires, (3) able to withstand surface abuse such as abrasion, pounding, and wire scrubbing, and (4) able to take abuse such as crushing and distortion.

Jan 5, 1969

By S. Roath, F. Paul, D. Melville

Several attempts have been made over the past 40 years to separate red blood cells from whole blood using a magnet. This has been achieved by the authors by using a high gradient magnetic field and " carrying " the red cells in a suitable reducing agent - the deoxyhaemoglobin so produced has 4 unpaired electrons per atom giving appreciable paramagnetic moment as opposed to the usual oxygenated form which is diamagnetic. Red blood cells so separated appear to be undamaged and can be reinjected into a donor animal where their survival is shown to be normal using an isotope tagging technique. Studies on function of the white blood cells and blood platelets also indicate that they are functionally unchanged by separation process.

Jan 1, 1980

By Peretti, E. A.

Since its development about forty years ago by J. V. N. Dorr (Cyanidation and Concentration of Gold and Silver Ores, McGraw Hill Book Co., 1936, 1-5), and others, continuous countercurrent decantation has not only become one of the standard methods for extracting gold and silver from their ores, but has also found wide application in other metallurgical and chemical industries. In 1917 L. B. Eames published an excellent paper (Countercurrent Decantation, Trans AIME, 1917, 57, 143- 158), in which he determined the effects of grade of ore, ratio of solution precipitated to ore treated, variations in the density of the thickener spigot discharge and variations in the value of the barren solution upon the gold assay of the solutions discharged from the thickeners in the system. Eames showed that, other things being equal, the dissolved gold lost in the tailing varies directly as the value of the ore and as the value of the barren solution. The tailing loss de- creases rapidly as the ratio of solution precipitated to ore treated is increased to about three or four to one. Beyond this point the improvement is negligible.

Jan 1, 1949

By Eckley B. Coxe

The plummet lamp, to which I called the attention of the Institute, at the Bethlehem meeting, in August, 1871, with the improvement of the compensating ring, suggested by Mr. Heller, having come into general use for mine surveying in this country, and my attention having been called to the fact that it could not be employed in mines in which there was danger of meeting with fire-damp, I have so modified it that it can be used in all cases with safety. Mining engineers, who are in active practice in those districts where fire-damp is met with in the mines (and I am sorry to say it is becoming much more common in the anthracite regions), know how dangerous their work is when they are called upon to survey such mines, particularly when they are obliged to run lines in those parts of a mine which have been unworked, since by opening of doors, brattice, etc., to get the sights, they are liable to disarrange the currents of air, and cause any fire-damp that may have accumulated in the old workings to find its way into the levels, etc., where the party is at work. It is, therefore, very dangerous to leave an open light (such as the original form of plummet lamp) in an old breast or gangway, even when the safety lamp has shown that no fire-damp is present, for the opening of the doors, etc., may drive the fire-damp to the light, and thus endanger the lives of the engineers. The improved form of plummet lamp, now shown to you, can be used either with or without the safety apparatus. Upon the top of the plumb-bob portion of the old lamp a screw is cut, upon which a ring A is screwed. (See Plate 11.) On the external cylindrical part of this ring two small conical holes are drilled, 180' apart. The compensating ring, by which the plumb-bob part of the lamp is suspended, passes over the ring A, and is fastened to it by two small screws having conical points, which fit into the conical holes in the ring A. The safety apparatus resembles, to a certain extent, that of the Mueseler lamp. It consists of a ring B and plate C, which are united by four rods. The plate C has a cylindrical hole in the middle, and four apertures distributed radially around it. In the central cylindrical hole is fitted a conical brass chimney, which projects below the plate C, and is fastened to the latter, being kept ver-

By H. W. Mead, C. E. Birchenall

SELF-DIFFUSION in pure gold has been studied by Sagrubsky,1 McKay,2 Gatos and coworkers,3,4 and Okkerse.5 Sagrubsky used a sectioning technique but reported results far lower than any of the others. The work seems to be carefully done, and it appears that a factor of 60 must have been omitted in his calculations or the units misstated by an equivalent amount. McKay used a surface activity method, and Gatos and Kurtz, following Gatos and Azzam, applied autoradiography to the measurement of activity on an oblique section through the diffusion zone. These two investigations agree well with each other but give results below those reported here. Okkerse employed a very careful sectioning technique. Chemical interdiffusion in Au-Ag alloys has been measured under several concentration conditions. Average values of the diffusion coefficient for the range of 0 to 18 atomic pct Au were obtained by Braune.6 since the diffusion coefficient probably varies markedly over this range, the values may not be too useful. Also, a plot of these data suggests that grain boundary contributions may have been appreciable at the lowest temperature employed. Ebert and Trommsdorf7 give average values for 0 to 9 atomic pct Ag, and Johnson8 reports average values for 45 to 55 atomic pct Au. Johnson also measured silver and gold self-diffusion coefficients in 49.2 atomic pct Au alloys, and self-diffusion in pure silver. The self-diffusion of gold in pure silver has been determined by Jaumot and Sawatsky.10 Other measurements which do not cover a range of temperature or are of low precision are not mentioned in this account since a review by Kubaschewski is available." This contribution reports diffusion coefficients for self-diffusion in gold, self-diffusion of gold in Au-Ag alloys, and chemical diffusion in Au-Ag alloys. Although it had been intended to obtain silver self-diffusion data in the alloys it now appears unlikely that these measurements can be done soon, so a table has been worked out for a self-consistent scheme of diffusion coefficients which should not be too far from the true values. Experimental Details Experiments on pure metals were conducted using fine gold of 99.99+ pct Au and silver of the same purity. Alloys were prepared by melting the two metals together in a graphite crucible in vacuo and allowing the slug to solidify in the crucible. After machining to a cylinder about 0.85 in. diam each slug formed one half of a diffusion couple. Compositions were determined later by analyzing chips taken from the extremities of the diffusion zones. The gold used in the preparation of alloys was sometimes pure gold but was normally either in the form of clean pickled alloy from previous experiments or gold recovered by oxalic acid precipitation from warm aqueous solution. Chips from the various stages of experimentation were dissolved in aqua regia and the solution taken to low bulk, diluted with water, and again taken to low bulk before diluting for the precipitation. This precipitated gold contained a small amount of silver as the only impurity detectable by spectrographic analysis. Disks for use in diffusion couples had opposite plane faces abraded on emery paper as far as zero grit, were annealed for 12 hr at 900°C in argon, and had one face of each disk polished to 000 emery paper. Radioactive gold was plated at about 2 ma per sq cm from a small volume of cyanide solution containing 1 mg of inactive gold as a carrier. Specimens , were freshly abraded on 4/0 emery paper immediately prior to plating. In the case of the active couples disks of a similarly prepared but unplated alloy or pure metal were placed on top and welded to the active disk. With the concentration couples disks of different compositions were welded. Welding was performed after a pressure of 5,000 lb had been applied at

Jan 1, 1958

By G. T. Smith, R. C. Moyer

Cadmium, along with other impurities such as lead, gallium, germanium and indium, is characteristically found associated with zinc ores, the average ratio of zinc to cadmium being about 200 to 1. The increasing demand for cadmium has led most zinc producers to develop a means for its recovery. The separation and recovery of this byproduct constitutes an important development in the metallurgical field. Zinc sulphide concentrates, principally from domestic sources, are processed at Donora Zinc Works and they assay approximately 60 pct zinc, 30 pct sulphur, 0.37 pct cadmium, and 0.8 pct lead. Concentrates are roasted to convert zinc sulphide to zinc oxide. Sulphur evolved as sulphur dioxide is used to manufacture 60º Baume sulphuric acid by the lead chamber process. The roasted calcine is sintered to remove the remaining sulphur and volatile impurities. Fume from the sintering machines is collected by Cottrell pre-cipitators and sent to the Cadmium Department for cadmium removal. The sintered product, a crude zinc oxide, is then mixed with coke and salt and charged into horizontal retorts for reduction to zinc metal. Furnace residues are then passed through a Waelz kiln which recovers practically all of the remaining zinc as an oxide. This oxide is collected by Cottrell precipi-tators and returned to the sintering plant for further processing. The following discussion covers operating procedure, and equipment used in the Cadmium Department for the manufacture of cadmium and its byproducts. (See attached Flow Sheet, Fig 1.) The production of cadmium may be divided into several steps, each of which will be discussed separately. These steps are as follows: 1. Raw Materials—Sinter Plant Cottrell dust, acid sludge and sulphuric acid. 2. Sulphating—Separation of lead. 3. Purification—Separation of impurities other than zinc. 4. Precipitation—Separation of cadmium from zinc. 5. Briquetting—Preparation of sponge for charging to furnace. 6. Smelting—Distillation of cadmium metal. 7. Remelting—Casting into commercial shapes. 8. Recovery of Rare Metals—Separation of germanium, gallium and indium. Raw Materials The raw material, or Sinter Plant Cottrell dust, from which the cadmium is manufactured, is recovered by Cottrell units collecting fume from two Dwight-Lloyd sintering machines. An average analysis of this dust is 36 pct zinc, 1.5 pct sulphur, 17 pct lead, and 5.5 pct cadmium, with associated elements in smaller amounts. A lesser tonnage of material removed from the sintering machine fans, and called fan cleanings, is also treated for cadmium. It is lower grade material and analyzes approximately 41 pct zinc, 1.2 pct sulphur, 14 pct lead, and 4 pct cadmium. Cottrell dust and fan cleanings are delivered to the Cadmium Department by monorail crane in bell-bottomed dump buckets. Acid sludge and 60" Bauine sulphuric acid are received from the Acid Department. The acid sludge is a mixture of lead sulphate, sulphuric acid and zinc sulphate, and is recovered mainly from the floors of the acid chambers or storage tanks. The acid sludge is delivered to the Cadmium Plant in a lead lined bucket. The 60º Baume sulphuric acid is delivered through a lead pipe to a lead lined storage tank. Sulphating Four well ventilated lead lined sulphating tanks, 8 1/2 ft in diam by 12 ft deep, are used. These are steel tanks lined with 20 lb lead on the bottom and 16 lb lead on the ides, equipped with Hastelloy side agitators. 15 hp motors drive 24 in. propellers at 450 rpm. There are water connections to stuffing boxes to keep sludge from entering the bearings. The tanks are covered with removable wooden lids and are connected to marine plywood

Jan 1, 1950

By Andrew Hodge

ISSUES IN MINING LABOR The examination of mining labor issues is often confined to health, and safety. There are other issues, including the present state of mining manpower availability and utilization, and the nature of mineral industries' industrial relations, which are worthy of consideration. The state of the labor market for mining skills, the availability and utilization of mining engineers and related disciplines, the state of research and its employment of scientists and engineers, and the condition of mining industrial relations with all these groups, all have an important effect on the viability and economic health of the minerals production sector. PRODUCTION LABOR Why examine an industry's production labor market? People involved in an industry should be aware of what labor supplies will be relative to industry requirements. This advance information allows industry and government to plan ahead to alleviate problems by moving to affect labor supplies or to accommodate production to expected labor supplies. This is less costly and less painful than responding after the fact to labor market changes. Any industry requires some form of labor. Labor is especially important to the mining industry. Mining labor is well paid. Average annual earnings are higher than in manufacturing. Average hourly wages are also higher. Payroll costs form a high percentage of total cost in coal mining and nonmetallic minerals mining. In metal mining the percentage is comparable to the average for manufacturing. Payroll cost in oil and gas extraction is quite low, but a major proportion of cost is in the form of income to proprietors, i.e., unincorporated businesses. Mining labor is worthy of specific attention. The minerals extraction labor is unique in many ways. Mining labor and especially underground miners are differentiated from other "unskilled" labor. Miners cannot be considered as part of a larger labor pool. The mining labor market has exhibited a unique combination of characteristics. Mining is the only large sector of United States employment in which hourly wages are high and continuing to rise, yet employment declines. Although industry has introduced new labor-saving investments, and labor requirements continue to decline, there is evidence of a mining labor shortage. Specific problems have arisen in the mining labor market such as a present labor shortage in nonfuels mining. Understanding the causes and remedies for these specific problems is also important. These various problems and questions may be handled in a unified manner by examining the relationships of certain economic variables. The relationship that exists between changes in output, employment, labor productivity, and hours worked per week may be stated explicitly:

Jan 1, 1976

By C. W. Hamilton

In the production of crude petroleum for the year 1930 Venezuela again maintained its world rank of second only to the United States. During the latter months of the year Russia forged ahead of Venezuela in daily rate of production, and from the present outlook will probably rank second among the oil-producing countries of the world in 1931. It is now believed Venezuelan production has passed its peak. The producing fields of the Bolivar coastal district, along the east side of Lake Maracaibo, continue to be the principal source of supply. Such fields as Lagunillas, Mene Grande and La Pas were not produced to capacity throughout 1930. During the year, three new fields entered into commercial development: The Rio Tarra field in the District of Colon, State of Zulia; the El Mene de Salto field in the District of Acosta, State of Falcon and the Quiriquire field, District of Piar, State of Monagas. For 1930 the total crude production of Venezuela was approximately 137,424,000 bbl. as compared to 137,739,000 bbl. during 1929, or a decrease of 315,000 bbl. During the past year exports of crude from Venezuela amounted to 137,8.50,000 bbl. as against 130,044,000 bbl. exported during 1929. Crude oil in field storage decreased from 14,138,-000 bbl. at the beginning of 1930 to 9,600,000 bbl. as of Jan. 1, 1931— present crude stocks fill about one half the field tankage available. Drilling operations in the producing fields declined sharply but throughout the year there was maintained a satisfactory potential reserve in the shape of proven territory and closed-in producers. Of the 2555 wells which have been completed in Venezuela, 1571 wells were in production on Jan. 1, 1931. The status of these present producing wells may be classified as follows: flowing 652, pumping 170, gas-air lift 193 and closed-in 556. The ratio of closed-in wells to producing wells declined in 1930, while the number of wells produced by artificial means increased materially. In the Bolivar coastal fields there is now observed a marked decline in gas volume and well-head pressure. Lago Petroleum Corpn. and Venezuela Gulf Oil Co. each have under construction electric plants designed to generate power for pumping wells by electricity. The first units of these plants will be placed in conlmission in the early spring of 1931. Venezuela Oil Concessions, Ltd. has installed a number of stenrn-

Jan 1, 1931

By Ellis Clark

These mines were discovered by George W. Lufkin in August, 1878, and mere worked almost continuously until August, 1893, a period of fifteen years. The ore-deposits in this locality lie close to the surface, and it is strange that the Spaniards, passing and repassing for nearly three centuries, did not discover them, particularly as they are marked in several places by large outcrops of black flint and iron, which would lead even a casual observer in a mineral country to suspect the proximity of ore. The mines are situated about six miles from the old Santa Fé trail, and fifteen miles from the Rio Grande. The geology is such that a skilled geologist passing over the ground would probably suspect, from the peculiar arrangement of the formations, the occurrence of ore. The formations in the district, eruptive and sedimentary, are nine in number; and of these eight are to be found within one thousand feet of the Grande workings. Topography. The topography of the Lake Valley district shows its dependence on the surface and underground geology, in a degree more marked

Jan 1, 1895

By W. Crafts, J. L. Lamont

Electrolytic extraction of carbides from quenched and tempered steel and their examination under the electron microscope were found to be helpful in understanding the mechanism of secondary hardening in alloy steels1 and the same technique has been applied to isothermally transformed steels. A preliminary survey of the utility of the method has indicated that it has promising possibilities for investigating the characteristics of pearlite and bainite. The examination of a few carbon and chromium steels has suggested that pearlite is formed with carbides of two varieties representing the lamellar and nonlamellar forms and that bainite appears to form with a structure analogous to, but significantly different from, martensite. Procedure The method used for examining the carbides was similar to that described previously.1 The chromium steels used in the investigation were made from an Armco iron base in an induction furnace and were not treated with grain-refining deoxidizers. The composition of the steels is given in Table 1. Three-inch square ingots were forged and rolled to 1/8-in. thick sheet for use in the isothermal studies. After rolling, the sheets were sandblasted to remove the rolling scale. Specimens approximately 3/4-in. wide and l1/2-in. long were prepared from the 1/8-in. sheet. They were heated in a salt "bath at 2100°F (1150°C) for 1/2 hour, transferred to other salt baths at 1300°F (704°C), 1000°F (538°C), 800°F (426°C), or 600°F (315°C), held for various periods up to 100 hr and finally quenched in water. After quenching, the specimens were cut in half, one half being submitted to microscopic examination and the other half being used for the electrolytic extraction. The isothermally transformed specimens were submitted to examination under the light microscope to determine the degree of transformation and type of structure and were photographed at 2000 X. Carbide residues were obtained by electrolyzing in 10 pet hydrochloric acid and collecting the residue in glycerine to minimize attack by the acid. As pointed out in the earlier paper, the carbides are attacked to some degree during electrolysis. This attack is relatively minor on the coarser carbides but may be quite severe on the fine bainitic carbides. The residues were washed free of the glycerine with water and alcohol. The alcohol was removed by repeated washings of amyl acetate, and the amyl acetate suspensions were transferred to stoppered vials. Debye-Sherrer X ray diffraction patterns of the residues were prepared using a chromium target. A selection based on the microstructure and X ray data was then made of samples considered most illustrative of the progress of transformation. Electrolytically extracted residues from these samples were submitted to examination by W. D. Forgeng and A. C. Jenkins on the electron microscope at the Research Laboratories of The Linde Air Products Co. and electron micrographs were made at X 5000 and enlarged to 25,000 X. The micrographs obtained with both the light and the electron microscopes are mounted side by side in the accompanying figures. Although no effort was made to establish the T-T-T diagram for the chromium steels, the times for holding in the salt bath were adjusted with the intention of making the samples represent different stages in the transformation at temperatures of 600, 800, 1000, and 1300°F. The degrees of transformation and results of X ray examination are shown in Tables 2—4. The carbide designations refer to orthorhombic or trigonal carbide types and are not meant to imply that the compositions are exactly as indicated. X ray Diffraction Data The occurrence of Fe3C and Cr7C3 in these steels was found to be consistent with published data on comparable chromium steels. Steels A and B with relatively low ratios of carbon to chromium contained Cr7C3 in the pearlitic structures and FeuC in the

Jan 1, 1950

By Percival Roberts

It may seem necessary to offer an apology for presenting for consideration a process which is conspicuous by its absence in the literature of the Institute, and which may be thought by some to belong to the past in metallurgy, and to have been already superseded. But the large capital invested in puddling calls for a careful consideration of the question whether the time has certainly arrived when the puddling furnace must be replaced by the converter and open-hearth furnace. May there not still be a place for puddled iron alongside of molten iron and steel, and is not the improvement of the puddling process itself worthy the attention of engineers equally with the Bessemer and open-hearth processes? The changes involved in the conversion of pig iron into wrought iron are well understood and need only be briefly alluded to. The patent of Henry Cort bears the date of 1784. Since that time * the improvements in the process have mainly consisted in the replacement of sand by iron bottoms by Samuel Baldwyn Rogers in 1818, and the still more recent substitution of iron oxide for the refractory materials used for the rides and bridge of the hearth, which distinguishes the wet or boiling process from the dry or pnddling process. Chemically, the process consists in the removal of the metalloids from the pig iron, a result effected mainly by the iron oxide. Silicon is first oxidized, then the phosphorus, and finally the carbon. The silicic and phosphoric acids produced pass into the cinder and the carbonic oxide burns as it escapes from the bath of metal. It is interesting in this connection to note the effect of temperature on the removal of the phosphorus from the iron. As is well known, no phosphorus is eliminated under the oxidizing influences prevailing in the Bessemer converter, while from 70 to 80 per cent. is removed in puddling. But we find, if in working cold short irons

Jan 1, 1880

IF you do not make the disc at the same time as the core and as part of it, it is necessary to make it by itself. This is done by spreading on a board or other flat surface a layer of clay as thick and wide as [88] the disc that you made at the feeding head of the first pattern of the gun. When it is dry, mark it exactly with compasses and then, cutting with a chisel or rasp, make it fit exactly into the empty space at the head. Likewise, make a hole just as wide as the thickness of the core exactly in the middle of this clay disc. When you have put the disc in its place in the mould and then pass the core through this hole, it passes exactly through the center of the mould in such a way that it meets the iron ring that you put at the foot of the mould for this purpose. As I said above, if' you do not make it as part of the core, it is necessary to proceed in the aforesaid way. But if' you wish to make it attached to the core (which I like better because it can be done more accurately) make a

Jan 1, 1942

By L. D. Anderson

WHEN, after years of troublous experiences in roasting sulfide ores with heavy dust and fume losses resulting from the equipment and methods first available, there appeared on the scene of metallurgy that revolutionary process known as sintering, it was felt that at last there had been found the ideal method for preparing sulfide ores for blastfurnace reduction. Not only were the sulfides roasted but also the fine oxidized ores were bound together with them in strong porous cellular masses which were in the best possible condition for reduction. With the experiences gained in the manipulation of the Huntington-Heberlein, Carmichael-Bradford, and Dwight & Lloyd processes there developed a refinement of detail which brought the whole plan of roasting by sintering to a high plane of perfection. But that metallurgy is never stationary is revealed by the fact that changes in milling practice, particularly the development of flotation, have introduced a new set of problems in sintering itself. Inasmuch as it is felt that these problems have not yet been solved in an entirely satisfactory manner this paper is written to record the present practice of the Salt Lake Valley smelters with the hope that there will be brought forth such discussios as may perhaps lead to still better practice. By far the greater proportion of the sulfides smelted today are flotation concentrates. Usually they are high grade, sometimes as high as 70 per cent. and more in lead. They are extremely fine, many mills grinding the ore so that from 60 to 80 per cent. will pass through screens of 200 mesh. The physical condition in which many of these concentrates reach the smelters is disconcerting to the metallurgists. Some are of about the consistency of putty. Others are of a sticky, slimy nature. Others again, dried to the limit, are veritable powders. Remembering that the down-draft sintering charge for the best results must be porous enough to let air be drawn through it reasonably well, must be thoroughly mixed, and must have some coarse material in it to segregate out and form a layer on the grates, it will be understood that the advent of this extremely fine material has made necessary still further elaboration in the equipment and processes of preparing sulfides for the blast furnaces,

Jan 1, 1929

The work of the Committee on Industrial Preparedness* is well summed up in the following letter written by Thomas A. Edison, Chair-man of the Naval Consulting Board, after President Wilson and signed the army appropriation and army reorganization bills: "The Committee on Industrial Preparedness of the Naval Consulting Board, of which committee Howard E. Coffin is chairman, after a five months' campaign in many ways unique in vigor and vision has played a very definite part in the measures for the national defense which have just become law. It is responsible for having laid the foundation for a true industrial preparedness in this nation. "Five months ago the committee, wholly non-partisan in make-up, acting with the civil, mechanical, mining and electrical engineers and the chemists of the country, members of five great scientific bodies, began its work in' every nook and cranny of the land. The purpose was to prepare American industry efficiently to support the armed forces of America in the event of war. "The public, the business men and the legislators at Washington knew little regarding the demands on industry in connection with modern war. No department at Washington was charged with the duty of coordinating the needs of the army and navy with transportation, industry, and kindred functions. The purchasing, quartermaster's and ordnance departments of the army and navy were unable to buy military supplies except by competitive offering in the open market. No one had considered the need, and no legislative machinery was in existence, for preventing the presence of skilled workers on the fighting front when they would in time of war be needed in the factories, mills and mines of the country. Neither at Washington or elsewhere was there even a list of the industrial resources of the nation in such shape as could be used for practical purposes in case war should come. "The three things, then, that the committee headed by Mr. Coffin set out to do and that now have been brought about were as follows: First, to mobilize concretely the business men of America and their output against a day of need. This meant chiefly to discover in fullest detail just what equipment our manufacturers possessed that might be swung over to supply the army and navy swiftly and bountifully from the hour the colors were raised. In a few weeks this initial task, which has been a truly colossal one, will be at an end. A complete report of the equipment of practically every concern of substantial size in the country is now in the hands of the - committee. Directly in charge of the great inventory has been W. S. Gifford, Supervising Director of the Committee. The second step was to procure legislation making possible the placing by the war and navy departments of annual orders for munitions in small quantities to American manufacturers now not producing such things, so that quietly, efficiently and thoroughly they could learn in time of peace how to supply the government in time of war. The new laws make all this possible. It should be said here that this practice will bring about a geographical diffusion of munition plants all over our country, instead of affording us only a few such concerns for the most part near the exposed seaboards, as at present. It is obvious that this system will also throttle all talk of a munitions trust.

Jan 10, 1916

Joseph LeConte, Berkeley, Gal.: I have read with some care and with extreme interest the work of Dr. Don, and have 110 hesitancy in expressing my high estimate of its value. We have here an example of laborious work undertaken in the true scientific spirit and by right methods. Loose statements and rash conjectures are here brought to the test of chemical analyses. By such work only may we hope to reach reliable conclusions and finally to solve the complex problems presented by the occurrence of ore-deposits. Such work as this is not only scientific but Is in the highest degree practical; for while a crude and imperfect science, by interfering with the results of approved empirical methods, may be positively hurtful, a more perfect science must eventually become the only sure guide to practice. Such a more perfeet science can only be reached by such work as Dr. Don's. I am sure every member of the Institute will unite with me in the hope that Dr. Don will continue his work, and that his example will incite others to similar work. S. F. Emmons, Washington, D. C.: I desire to bear my humble testimony to the great value of Dr. Don's paper to the science of ore-deposits, the thoroughness and accuracy of his work, and the immense amount of care-taking and tedious labor which it represents. The only regret with regard to it is that it could not have been published in full. No more important paper in its line has ever appeared in the Transactions. Indeed,

Jan 1, 1898

By Oswald J. Heinrich

(Read at the Amenia Meeting, October, 1877.) THE deposit of rock salt along the shores of Lake Huron, in Canada, has been brought before the public during the last six months, in consequence of the developments made by the diamond drill at Goderich. It is likely to be of more than common interest in the future, since now actual operations have been commenced to exploit the deposit and work it by regular mining. The methods of mining rock salt being but little known in this country, it may be of interest to make a few general remarks in regard to them before entering, upon the description of this new mining enterprise. According to the conditions under which salt is found in nature, various methods have been resorted to, in course of time, to make it available for the human race. They consist in : A. Natural or solar evaporation. B. Artificial evaporation, either exclusively or in connection with the former. C. Mining the rock salt in its natural state, and converting it to a marketable product, if need be, by simply pulverizing it. Without going into the details of the various methods of making salt available in an economical point of view, dependent on its degree of purity, or on various local influences, we cannot refrain from. alluding to the general principles which influence the mining and manufacturing of salt in countries where they have been carried on for hundreds of years. ECONOMICAL CONDITIONS FOR SUCCESS. Salt being one of the articles of prime necessity, and one universally distributed throughout nature, it must always be sold at a comparatively low price. It would even be quoted in the market at prices far below those now ruling, if it were not for the high duties generally imposed upon it, for purposes of state revenues. But looking closer into the subject, it will be found that this duty is probably one of the least oppressive, although in some countries it exceeds sixfold the cost of profitable production. To produce the article at the lowest possible cost requires, therefore, a

Jan 1, 1878

By J. F. Kemp

PAGE I. Introduction,.......269 11. Topogmphical Features,.....270 III. Geological Relations of the Mineralized Area,.272 1. Structural Features,.....272 2. Occurrence of the Copper,....274 3. Granite-Contacts,.......274 IV. Descriptions of the Rocks,.....274 1. Granite,........274 2. Limestone,.......276 3. Porphyritic Eruptions,.....278 (a) Quartz-Porphyry,.....278 (b) Trachyte-Porphyry,.....280 V. Contact Phenomena,......285 1. Comparative Immunity of the Limestone, . 285 2. Contact Phenomena in the Quartz-Porphyry,.... 285 3. The Form and Distribution of the Ore-Bodies,290 VI. Method of Deposition,......293 I. Introduction. The White Knob copper-deposits are situated about three miles south of Mackay, on the Salmon River branch of the Oregon Short Line Railroad, in Custer county, Idaho. An outline-map of this district is given in Fig. 1. The deposits have been known and spasmodically worked for many years, and a total of over 3.5 miles of tunnels, shafts and other workings has been driven with a view to their development. These extensive excavations have exposed the deposits sufficiently to permit a careful geological examination. The peculiar features which give special interest to this paper are the branching, tree-like form of the ore-bodies; the absence of zones of secondary enrichment in the partly oxidized pyritic deposits, and the fact that while the deposits are associated in a general way with the contact of an eruptive rock with limeetone, which it penetrates, the garnetization has taken place not in the limestone, as is the usual case, but in the igneous

Jan 1, 1908

By R. E. Cech, J. H. Hollomon

KURDJUMOV and Maksimova reported experiments with manganese steels and high carbon steels' and with an Fe-Ni-Mn alloy' in which mar-tensite was formed isothermally over a range of temperatures. They found in some cases that mar-tensite formation could be suppressed by rapid quenching to liquid nitrogen temperature. From their microstructural observations of martensite formed isothermally, they concluded that the rate controlling step is nucleation rather than growth. Kulin and Cohen,3 in an attempt to reproduce these experiments, found that with a steel having the same composition as that reported by Kurd-jumov and Maksimova, the transformation to martensite was essentially complete above the temperature range of Kurdjumov and Maksimova's isotherms. The possible reasons for this disagreement were not considered. Recent papers by Das Gupta and Lement4 and Kulin and Speich5 report the formation of isothermal martensite in a high chromium steel and in an Fe-Cr-Ni alloy, but neither paper can be considered a verification of the original Kurdjumov and Maksimova results. Further, in neither case were the authors able to suppress the formation of martensite entirely. Because of the important bearing the Kurdjumov and Maksimova results have to an understanding of the mechanism of martensite reactions it was felt that an experimental investigation directly concerned with checking the validity of their results was in order. This paper describes the results obtained on the isothermal transformation over the temperature range from —79" to —196°C of an alloy of iron, nickel, and manganese. Experimental Apparatus A 15 lb heat of an alloy containing 73.3 pct Fe, 23.0 pct Ni, and 3.7 pct Mn was melted by induction and cast under argon. The ingot was forged to 1-in. bar and a portion rolled to 1/16x1 1/2-in. strip. This strip was pack-homogenized 300 hr at 1100" in a helium-filled sealed iron tube. The composition after homogenization was 73.2 pct Fe, 22.94 pct Ni, 3.73 pct Mn, 0.05 pct C, and 0.015 pct N. The strips were cut to 1/2-in. width for dilatometer and metal-lographic specimens. Only the center portion of the 11/2-in. strip was used in the present investigation. The dilatometer employed was similar in design to one described by Flinn, Cook, and Fellows." A concentric fused auartz rod and tube assembly with hooks for holding the specimen was mounted so as to transmit the specimen dilation to a 1/10,000 in., 1/10 in. travel dial gage. The dilatometer proper was mounted by means of extension arms to a counterweighted sliding member on a vertical standard. This method of mounting permitted rapid transfer of the dilatometer from the austenitizing furnace to the quenching bath and low temperature chamber. A small electrical vibrator on the dilatometer kept frictional effects of the quartz members at a minimum. The austenitizing unit was a vertical, molybdenum-wound, hydrogen atmosphere furnace maintained at a constant temperature ±3°C by means of constant power input. A 12-in. stainless steel jacketed copper liner having 1/2-in wall thickness acted to equalize the temperature in the hot zone of the furnace. This liner, closed at the bottom end and open at the top to permit entrance of the dilatometer and specimen, was kept filled with dry nitrogen gas. A chromel-alumel thermocouple was placed inside the tube to determine the temperature. The 4-in. dilatometer specimens in the chamber varied less than 1/2° across the specimen length except for a 1 1/20 drop at the end nearest the open end of the furnace. The low temperature isothermal holding bath was a double Dewar arrangement similar to one described by Turnbull7. The outer bath was filled with a refrigerant at a temperature lower than the desired holding temperature. The inner bath was filled with Freon "11" or "12" or a mixture of both, depending upon the holding temperature. This inner bath which tended to be cooled by the outer bath was kept at a constant temperature by introducing a small amount of heat with a manually controlled electric heater. Stirring was accomplished by bubbling dry air through the bath. A Leeds and North-rup type K potentiometer was used to measure the inner bath temperature as indicated by a five element copper-constantan thermopile. The bath temperature was maintained within ±0.2°C of the desired temperature by occasionally adjusting the heater current so as to keep the Leeds and Northrup galvanometer at zero deflection with a constant setting of the potentiometer. Isothermal tests were usually continued for 300 to 400 min and another reading made at approximately 1000 min if the bath, unattended overnight, had not deviated in temperature more than 5°C. Transformation curves are drawn dashed (Fig. 1) through the time region where temperature was not controlled precisely. Experimental Procedure Dilatometer specimens of 1/2x1/16-in. strip were cut to 41/2-in. length and holes were drilled for the quartz hooks with proper spacing to give a 4-in. measured length. A thermocouple consisting of 0.012-in. diameter chrome1 and alumel wires was spot welded to the specimen and threaded between the dilatometer rods to binding posts near the dial

Jan 1, 1954

By Charles A. Anderson

The Bagdad copper deposit is of the disseminated type (porphyry copper) occurring in a quartz monzonite stock of late Cretaceous or early Tertiary age. This stock, located essentially at the intersection of two dike swarms, is the only one of several stocks cropping out in the area which is appreciably fractured and mineralized. Most of the rocks in the area are of pre-Cambrian age, but their structures have had no discernible influence on the copper mineralization. Hypogene alteration of the quartz monzonite includes the addition of quartz, orthoclase, and sericite and recrystalli-zation of biotite. The hypogene sulphides are pyrite, chalcopyrite, and molybdenite, the latter younger than the chalcopyrite. The late Cretaceous or early Tertiary igneous rocks, veins, and faults were controlled by northeast and northwest shear zones, the intersection of which marks the zone of appreciable copper mineralization. The minor mineralized fractures carrying the bulk of the copper have a preferred orientation parallel to the intersecting shears, and it is concluded that they are of tectonic origin rather than the result of shrinkage on cooling, crystallization, or mineralization. Supergene enrichment during late Tertiary or early Pleistocene time formed a chalcocite zone providing the minable copper ore. The enrichment was controlled in large part by northeast and northwest faults, prticularly at their intersection or where the faults are closely spaced. Introduction A major objective in a regional geologic study of a mining district is to determine whether any structural pattern can be found that has a bearing on the control of mineralization. The Bagdad copper deposit is of the disseminated type (porphyry copper) occurring in a.quartz monzonite stock which is located essentially at the intersection of two dike swarms (Fig 2). Of several quartz monzonite stocks in the area only this One is appreciably fractured and mineralized. The origin of the minute mineralized fractures in disseminated copper deposits has long been a challenging problem to the mining geologist, and evidence has been obtained to suggest that the mineralized fractures at Bagdad are related to a regional pattern of conjugate shears which also controlled the location of the dike swarms. The purpose of this paper is to Present this evidence and to emphasize the structural control of the supergene enrichment in forming a chalcocite zone that has provided the ore for the Bagdad mine. The field work on which these conclusions are based was done between October 1943 and August 1945, as a part of the copper investigations of the Goelogical Survey, U. S. Department of the Interior. The writer and his associates, E. A. Scholz and J. D. Strobell, Jr., have prepared a comprehensive report on the geology and ore deposits of the Bagdad area which will be published subsequently by the Geological Survey. Bagdad is located in west-central Arizona in Yavapai County. Ransome' divided the State of Arizona into three provinces: I? the plateau to the northeast; 111, the desert region to the southwest and 11, the moun-

Jan 1, 1949

By Charles A. Anderson

The Bagdad copper deposit is of the disseminated type (porphyry copper) occurring in a quartz monzonite stock of late Cretaceous or early Tertiary age. This stock, located essentially at the intersection of two dike swarms, is the only one of several stocks cropping out in the area which is appreciably fractured and mineralized. Most of the rocks in the area are of pre-Cambrian age, but their structures have had no discernible influence on the copper mineralization. Hypogene alteration of the quartz monzonite includes the addition of quartz, orthoclase, and sericite and recrystalli-zation of biotite. The hypogene sulphides are pyrite, chalcopyrite, and molybdenite, the latter younger than the chalcopyrite. The late Cretaceous or early Tertiary igneous rocks, veins, and faults were controlled by northeast and northwest shear zones, the intersection of which marks the zone of appreciable copper mineralization. The minor mineralized fractures carrying the bulk of the copper have a preferred orientation parallel to the intersecting shears, and it is concluded that they are of tectonic origin rather than the result of shrinkage on cooling, crystallization, or mineralization. Supergene enrichment during late Tertiary or early Pleistocene time formed a chalcocite zone providing the minable copper ore. The enrichment was controlled in large part by northeast and northwest faults, prticularly at their intersection or where the faults are closely spaced. Introduction A major objective in a regional geologic study of a mining district is to determine whether any structural pattern can be found that has a bearing on the control of mineralization. The Bagdad copper deposit is of the disseminated type (porphyry copper) occurring in a.quartz monzonite stock which is located essentially at the intersection of two dike swarms (Fig 2). Of several quartz monzonite stocks in the area only this One is appreciably fractured and mineralized. The origin of the minute mineralized fractures in disseminated copper deposits has long been a challenging problem to the mining geologist, and evidence has been obtained to suggest that the mineralized fractures at Bagdad are related to a regional pattern of conjugate shears which also controlled the location of the dike swarms. The purpose of this paper is to Present this evidence and to emphasize the structural control of the supergene enrichment in forming a chalcocite zone that has provided the ore for the Bagdad mine. The field work on which these conclusions are based was done between October 1943 and August 1945, as a part of the copper investigations of the Goelogical Survey, U. S. Department of the Interior. The writer and his associates, E. A. Scholz and J. D. Strobell, Jr., have prepared a comprehensive report on the geology and ore deposits of the Bagdad area which will be published subsequently by the Geological Survey. Bagdad is located in west-central Arizona in Yavapai County. Ransome' divided the State of Arizona into three provinces: I? the plateau to the northeast; 111, the desert region to the southwest and 11, the moun-

Jan 1, 1949