By T. lkeda, R. S. Montgomery. A. Hara

Actual test specimens used in the previous laboratory wear investigation,' were fully characterized and the data is given in Table 1. Most of the carbides tested could be placed into groups of similar mean grain size. When the wear rates of the members of these groups were plotted as functions of their hardnesses, a family of curves resulted; curves for groups containing data from larger grained composites were at lower wear rates at the same hardnesses. Most specimens tested showed only A-1 porosity (ASTM Standard designa-

Jan 1, 1971

By H. H. Haung, J. D. Miller, E. F. Pereira

The chemistry of copper extraction from ammoniacal solutions by hydroxyoxime extractants was studied Equilibrium measurements were made by shakeout experiments with subsequent analyasis of the aqueous and/or organic phases The kinetic experiments were carried out in a single drop reaction cell in order to establish the details of the intrinsic reaction kinetics for this system. Equilibrium measurements Indicated that the extraction involves complete displacement of ammonia ligands from the coordination sphere of the cupric ion by the extractant molecules The extraction reaction has the following stoichiometry

Jan 1, 1981

By John Mathews

SOMEONE has divided mankind into two groups: (1) those who have the willingness and imagination to weigh the future gain over against a present indulgence, and (2) those who cannot do so. The former have self-control, patience, foresight and a capacity for sustained effort. Those having these homely virtues become the, possessors of capital and hence employers of others. Those lacking these qualities and owning no capital must seek it from those of the first class, and therefore are employed by others. The human qualities, which divide men into two classes-employers and employed-are, however, capable of change by education, training, environment and by all agencies which tend to develop character. These words of the economist have stuck in my mind for many years and the more I see of men in my business contacts the more firmly I am convinced of their truth. The earth in some respects resembles its inhabitants. When we stroll over the fields and hills we are impressed by the unorganized masses of sand and rock which make up the ground beneath our feet. When by chance we come upon a bit of mineral matter in crystalline form we are impressed by its beauty and symmetry and probably have it polished and call it a gem. Gems constitute a minute portion of the earth's crust, and those intellectual gems, worthy of polish, who brilliantly reflect the incident rays of education and experience that have fallen upon them are few among the masses of mankind.

Jan 1, 1931

By D. I. Bardos, Paul A. Beck

A MARK, Boren, and westgrenl in their X-ray diffraction study of manganese alloys with 10 to 25 at. pct Si reported the occurrence of a phase with complex crystal structure in a Mn + 14.5 at. pct Si alloy after annealing at 800° or at 600°C. Recently Kuzma and Gladyshevskii2 identified Mn6Si as an R phase,3,4 the second binary R phase known. (A binary R phase was previously found in the Mn-Ti system by Waterstrat.5) A ternary R phase was reported earlier0 near the Mn-Si binary border of the Ti-Mn-Si system at 1000°C. In the light of the Russian work it now appears that this "ternary" R phase may be in fact an extension of the binary (Mn6Si)R phase. As already found by Amark, Boren, and Westgren, the corresponding binary phase is absent at 1000°C; the effect of titanium is evidently to stabilize it up to higher temperatures. In a recent paper Wieser and Forgeng7 gave the boundaries of this binary phase, which they referred to as 6. In order to re-examine the identity of this phase, an alloy of Mn + 14.5 at. pct Si was prepared by induction melting in helium atmosphere and annealed for 3 days at 800°C. The powder pattern, taken with an asymmetrical focusing camera of large dispersion and shown in Table I, was found to be that of the R phase, in agreement with the results of Kuzma and Gladyshevskii. For comparison, Table I also lists

Jan 1, 1965

By D. T. Novick, M. B. Bever, B. Roessler

Ordered and disordered specimens of the alloy CusAu were cold worked and then annealed at 2880, 310°, and 340°C, together with disordered unworked specimens. me resistivity decreased during annealing mainly as a result of ordering; the resistivity measurements suggest that in cold-worked specimens the growth of antiphase domains is impeded. The strength properties increased during annealing at 288 "C; in cold-worked specimens this increase was lo a level above that for cold-worked specimens which had not been annealed. X-ray diffraction showed that after annealing for a few hours at 288ºC, the long-range order increased to a constant value; additional annealing at 288ºC resulted in the growth of antiphase domains in which the degree of order was constant. Changes in peak breadth and particle size confirmed that in cold-worked specimens the major effects of cold work were not eliminated during annealing at 288 "C, although a slight recovery process occurred. When a specimen of the alloy Cu3Au is heated to a temperature below the critical temperature (388ºC), long-range ordering tends to occur in a specimen containing less than the equilibrium amount of order characteristic of that temperature Ideally, a specimen of Cu3Au contains no long-range order if it has been quenched from above the critical temperature. Long-range order is reduced by cold work. If cold-worked specimens are heated, restoration processes such as recovery and recrystallization may occur,

Jan 1, 1963

By George Hulst

PRIOR to 1914, there was little demand for antimony in this country; its use was limited almost entirely to the manufacture of type and bearing metals. Practically no antimony ore was mined here, the market being supplied principally from China, and the alloy was produced by a direct mixing of lead and antimony. The great world war, with its demand for shrapnel in hitherto undreamed of quantities, precipitated a great boom in the price of antimony. Nominally quoted at 6 c. to 7 c. in 1914, the price increased by leaps and bounds to 45 c. in March, 1916. Under the stimulus of high prices many shall mines were opened, for it became profitable to work ores containing as low as 20 percent. antimony. High-grade sulfide ores (stibnite), containing 55 per cent. to 60 per cent. antimony, were received from Bolivia, China, and Alaska. Low-grade sulfide ores, running from 20 per cent. to 45 per cent., were produced in Nevada, California, Idaho, Utah, and Mexico; much of this ore was fairly rich in silver. The principal oxide ores came from Mexico and Oregon. The following analyses are representative of various types of antimony ore: Se Pn Cu Ao Au SIC), Fe S CAO ZN As Oxide Ore 25.09 46.02 0.95 0.40 10.98 0.30 0.22 Sulfide ore 5.5.20. 15.12 1.05 19.87 ? 0.40 0.25 Sulfide Ore 37.16 11.30 0.10 34.0 7.60 0.50 17.05 7.40 0.36 0.10 Sulfide Ore 41.55 15.00 0.20 76.0 0.04 5.60 0.25 18.17 0.85 0.25 0.10 The International Lead Refining Co. fortunately was equipped to handle these ores through residue and blast furnaces. The charge consisted of a variety of sulfide ores containing Sb 20 to 60 per cent. and Si02 6 to 45 per cent., oxide ores containing Sb 20 to 40 per cent. and SiO2 10 to 45 per cent. Secondary materials, such as battery plates, battery mud, lead oxide, paint, etc., together with refinery skims, softener skims, and other refinery byproducts, were treated along with the antimony ore to furnish the lead required. All silver-bearing antimony ores were treated in the residue furnace, the sulfur, iron, and copper forming matte that carried part of the silver, the balance going into lead bullion. The

Jan 9, 1919

By George P. Hulst

Prior to 1914, there was little demand for antimony in this country; its use was limited almost entirely to the manufacture of type and bearing metals. Practically no antimony ore was mined here, the market being supplied principally from China, and the alloy was produced by a direct mixing of lead and antimony. The great world war, with its demand for shrapnel in hitherto undreamed of quantities, precipitated a great boom in the price of antimony. Nominally quoted at 6 c. to 7 c. in 1914, the price increased by leaps and bounds to 45 c. in March, 1916. Under the stimulus of high prices many small mines were opened, for it became profitable to work ores containing as low as 20 per cent. antimony. High-grade sulfide ores (stibnite), containing 55 per cent. to 60 per cent. antimony, were received from Bolivia, China, and Alaska. Low-grade sulfide ores, running from 20 per cent. to 45 per cent., were produced in Nevada, California, Idaho, Utah, and Mexico; much of this ore was fairly rich in silver. The principal oxide ores came from Mexico and Oregon. The following analyses are representative of various types of antimony ore: Sb Pb Cu AG AU SIO2 Be S CaO Zn As Oxide ore.......... 25.09 46.02 0.95 0.40 10.98 0.30 0.22 Sulfide ore......... 55.20 15.12 1.05 19.87 0.40 0.25 Sulfide ore......... 37.16 11.30 0.10 34.0 7.60 0.50 17.05 7.40 0.36 0.10 Sulfide ore......... 41.55 18.00 0.20 76.0 0.04 5.60 0.25 18.17 0.85 0.25 0.10 The International Lead Refining Co. fortunately was equipped to handle these ores through residue and blast furnaces. The charge consisted of a variety of sulfide ores containing Sb 20 to 60 per cent. and SiO2 6 to 45 per cent., oxide ores containing Sb 20 to 40 per cent. and SiO2 10 to 45 per cent. Secondary materials, such as battery plates, battery mud, lead oxide, paint, etc., together with refinery skims, softener skims, and other refinery byproducts, were treated along with the antimony ore to furnish the lead required. All silver-bearing antimony ores were treated in the residue furnace, the sulfur, iron, and copper forming matte that carried part of the silver, the balance going into lead bullion. The antimony slag produced was sufficiently low in silver to warrant being smelted in the blast furnace to antimonial lead.

Jan 1, 1921

By J. H. Mallery, J. H. Keeler

THE crystal structure of Zral, the compound richest in zirconium (91.03 pct Zr by weight) in the system Zr-Al, has been found to be ordered face-centered-cubic. This compound is of particular interest, since it is encountered as the precipitated phase in potentially useful zirconium-rich alloys. It forms peritectoidally from body-centered-cubic zirconium and Zr,Al at about 975°C. The Zr-A1 constitution diagram has been reported by McPherson and Hansen.' For the primary determination a 100 g ingot was prepared by arc-melting in a water-cooled copper crucible under purified argon. The raw materials were crystal-bar zirconium (a purity of better than 99.7 pct) and spectroscopically pure aluminum. The ingot was double melted, examined metallographi-cally, and found to be quite uniform as shown in Fig. 1. The hardness of the as-cast button was VHN 390 to 445. A 20 mil diam specimen was prepared from annealed (900°C) filings of Zr,Al. The specimen was mounted in a 5 cm radius powder camera and an 8 hr exposure was taken using copper radiation with a nickel filter. The structure of the compound Zral was found to be ordered face-centered-cubic of the Cuau type, with an a,, value of 4.37220.003A. Its calculated density is 5.976e0.013 g per cu cm. The relative intensities for the lines were calculated using the formula 1+cos2 20 I oc----------------- • p • /F7 sin2 0 cos 0 1 + COS' 20 where----------------is the Lorentz polarization fac- sin2 0 cos 0 tor, p is the multiplicity factor, and F is the structure factor. The X-ray data are given in Table I. The compound has exhibited plasticity when present as particles in a matrix of a zirconium. During hot working at about 900°C, the compound has been found to deform plastically to the extent that some of the particles exhibit a length-to-width ratio greater than 4:1 as shown in Fig. 2. In answer to the discussion of ref. 1, McPherson and Hansen pointed out that the compound may be cold rolled and reduced as much as 33 pct. Zr,Al has also been found2 under certain conditions to precipitate in lamellar form at grain boundaries of the a phase of hexagonal-close-packed zirconium. Acknowledgment This work was carried out under Contract W-31-109-Eng 52 for the United States Atomic Energy Commission.

Jan 1, 1956

By David L. Holt, Walter A. Backofen, Anwar-ul Karirn

ANNEALING the binary alloy, Mg-0.5 wt pct Zr in a hydrogen atmosphere results in extensive precipitation of zirconium hydride. The morphology of these precipitates has already been investigated.lm3 Squires, Weiner, and phillips4 found, following creep testing of the hydrided alloy at 450" and 500°C, that hydride denuded zones formed along grain boundaries that were aligned approximately normal to the tensile axis. Zone formation was attributed to diffusional creep by magnesium transport down the prevailing stress gradients.4'5 Recently, electron microprobe analysis by Karim, Holt, and Backofen6 showed the zones indeed to be zirconium-free and furthermore it was shown that in compression, zones formed along boundaries approximately parallel to the stress axis. Thus it was confirmed that the zones are formed by diffusional creep. Typical zone-formation is shown in Fig. 1. Karim, Holt, and Backofen also measured the con- tribution to the total strain, from diffusional flow, slip creep, and grain boundary shear: results showed that diffusional strain tends to saturate with increasing imposed strain, while grain boundary shear eventually becomes the dominant deformation mode. It was suggested in explanation that the precipitate-denuded zones are soft and easily sheared, such deformation contributing to the grain boundary shear measurement. A point to be emphasized is that the Mg-0.5 Zr alloy was not superplastic for the index of strain rate sensitivity of flow stress, m = a log log 6 was only 0.25. It was recognized that diffusional creep in a poly crystalline aggregate must be accompanied by boundary shearing.' The suggestion was that the non Newtonian-viscous character of diffusional creep in the Mg-0.5 wt pct Zr alloy is due to resistance to sliding of boundaries lying approximately parallel to the tensile axis.= The work described in the present note should be seen against the above background for it represents initial efforts to observe in a similar way diffusional creep in a superplastic alloy. Previous work with the ternary-alloy Mg-6 Zn-0.5 Zr, pellet extruded, showed it to be superplastic however it does not contain resolvable precipitates to act as internal markers for diffusional creep. Also the fine grain size of the alloy (0.5 p) made conventional metallography rather difficult. Solubility relationships in the Mg-Zn-Zr system are not well known, however making reasonable guesses about the probable phase diagram of the ternary, Mg-Zn-Zr, various heat treatments were attempted to produce hydride precipitation. Finally a 16-hr anneal at 495' in hydrogen was found to pro-

Jan 1, 1970

By Charles R. L. Oder, Howard W. Miller

Approximately 5000 tons of zinc ore a day was mined during 1943 in the Mascot-Jefferson City district in East Tennessee. This ore came from the Kingsport formation, a part of the Knox dolomite, of Ordovician age. The Kings-port is composed of 350 to 400 ft. of limestone and dolomite. Thin cherts, sandy layers and shales are numerous. Frequently, the limestones are altered to crystalline dolomite. The Kingsport is divisible into four main lithologic zones. These divisions are illustrated in an accompanying table, which gives detailed sections of the ore-bearing beds as found in the mines and shows the exact positions of the various ore zones within the formation. Key beds are described and the practical applications of stratigraphy in mapping, prospecting and mining are discussed. Introduction The Mascot-Jefferson City zinc district is in Knox and Jefferson Counties, in the Great Valley of East Tennessee. It extends from Mascot, I3 miles northeast of Knoxville, to Jefferson City, about 30 miles northeast of that city. The American Zinc Company of Tennessee is producing from five mines in the district, in which it has operated for more than 30 years. The only other important producer is the Universal Exploration Co. The approximate daily production of the district in 1943 was 5000 tons of sulphide ore, grading from 2.5 to 6 per cent zinc. Small amounts of oxidized ore are mined intermittently. The Knox dolomite has been described by various geologists,'-' but no detailed descriptions of the rock sections revealed by mining have been published. Rock units are not conspicuously different and careful study is required to distinguish them. Nevertheless, familiarity with the stratigraphy of the mineralized zones is essential to successful exploration and extraction of the ores; therefore the purpose of this paper is to give detailed stratigraphic sections as measured in the mines, to discuss their important features and to show their relationship to the stratigraphy of the district. Generalized Section Table I gives the most characteristic general features of the major stratigraphic units. The formation names given in parenthesis are locally and widely used terms, the correlations of which are not necessarily established. For this reason they are put in quotation marks and are replaced by more restricted terms. The names "Mascot" and "Kingsport" were adopted from local towns. They were chosen jointly by Josiah Bridge, of the Federal Geological Survey, and the senior author for use in their separate unpublished manuscripts describing the Knox dolomite in East Tennessee. Descriptions of the type sections may soon be published. The name "Longview" was first applied by Butts6 in Alabama.

Jan 1, 1949

By Edward L. Fidler, Thomas E. Finch

Thin seam coal mining in the western US nominally equates to recovery of stray seams associated with thicker, major seams. The thin or stray seams encountered are generally recovered, but not in all cases. The alternative to extraction is, of course, spoiling. The majority of thin seams are encountered somewhere in the overburden above the major seam or in the parting between thick seams. Although some are true strays and appear anywhere in the geologic sequence, others might be classified as thin "rider" seams immediately above or below a thick seam and separated by some equally thin parting. For the purpose of this discussion, stray or thin seams are defined as those which are less than 1.2 m thick or represent less than 10% of the expected extractable coal. [Figure 1] is a graphic representation of typical thin, stray, or rider seams which actually appear in a western operation. Operationally, stray seams create irritating scheduling problems and require special handling techniques which do not always lead to efficient equipment utilization. Additionally, coal recovery from a thin seam is considerably less than the 95% usually recovered from thick seams. Higher recovery in thin seams leads to dilution problems, which depreciates Btu quality, and most western coals are not in a position to lose heating value. Thin western seams also undulate and pinch or swell more than thick seams, and this leads to more difficult recovery. Often they are associated with equally dark carbonaceous shales and visual selectivity is difficult at best during daylight hours. Resource Recovery Regulations Thin seam recovery in western mines is encouraged by both federal and state regulations and by the mining industry's concern for total resource recovery. [Table 1] lists the western coal states and their recovery regulations. The federal regulations are found in the Surface Mining Control and Reclamation Act of 1977. They state, "General performance standards shall . . . require the operation as a minimum to … conduct the surface coal mining operations so as to maximize the utilization and conservation of the solid fuel resource being recovered." Economic stimulation for thin seam recovery appears to be marginal or at the least controversial. Scheduling and operational problems often outweigh the nebulous profits created by engineering analysis. The only alternative to extracting thin seams occurring above major production seams is to strip directly through them and lose the resource to the spoil pile. Although this is not palatable to environmental emotions or resource promoters, it is the most simple expedient to operations people.

Jan 1, 1981

By B. N. Das, H. E. LaBelle, G. A. Wolf

ZnxHg1-xTe and GUPxAS1-x crystals have been grown from solution by a traveling heater method (THM). In a floating zone type fashion a solution zone sandwich of liquidus composition is made to migrate through feed material of solidus composition by a slow-speed movement of <0.25 mm per hr of the total charge through a stationary radiation or rf heater. ZnxHg1-xTe of composition 0 < x < 0.3 and GUPxAS1-x of composition 0.5 < x < 0.7 have thus been grown from their solution in liquid tellurium and gallium, respectively. A simplified analysis of heat and material transport is given. In this method, Proper adjustment of the temperature distribution along the liquid solution zone axis eliminates instability of the crystal growth front and constitutional supercooling. 1) ZnxHg1—xTe: The solid-solution telluride was grown in sealed quartz tubes at a temperature of 500 to 650°C. For first Preparations mechanical mixtures SINGLE crystals of solid solutions of III-V and II-VI compounds have been grown by various techniques from the melt, from the gaseous phase, or from solutions in of ZnTe and HgTe were used. X-ray determinations showed the resulting crystals to be homogeneous throughout their entire length, except for the end sections. The homogeneity is greatly improved by reusing the ingots obtained from first Preparations as feed material in subsequent crystal growth runs. Ingots of up to 4.5 cm have thus been obtained. 2) GaPxAs1-x: Crystals were grown in a EN crucible at a temperature of 1050°C. For first Preparation a mechanical mixture of Gap and GaAs was cemented together by a minimum amount of liquid gallium through "wet" grinding of Gap and GaAs crystals in the liquid metal and subsequent exuding of excess gallium by compacting of the charge in the EN crucible. Electron microprobe measurements using P-Ka and As-Ka radiation showed uniformity over a length of 0.4 cm. Properties of the various Preparations are described. liquid metals.&apos;-&apos; Their growth from the melt by passing a liquid zone of pseudobinary liquidus composition through a solid rod of solidus composition is generally a convenient method of growth of single crystals of solid solutions of homogeneous composition. This method loses much of its usefulness, however, if the melting point or the vapor pressure of the solid solution is high. In the case of a compound having a high melting

Jan 1, 1969

By W. R. Johnson, M. Hansen, John M. Parks

AS part of a research project sponsored by the Signal Corps Engineering Laboratories, which had the objective of obtaining a magnet wire of good conductivity and low temperature coefficient of resistance, a comprehensive literature survey, supplemented by experimental work, revealed that a linear relationship exists for solid-solution alloys between the electrical conductivity, K, and the temperature coefficient, a, as expressed by the equation: k = a/ß where ß is constant for the solvent metal and a - per°C. tR0 It has long been known that the electrical conductivity at a given temperature and the temperature coefficient of resistance of binary alloys are related to their constitution by the LeChatelier-Guertler rules, as illustrated by Figs. 1 and 2: Rule 1—In alloy systems consisting of a heterogeneous mixture of two phases, the electrical conductivity and temperature coefficient vary as a straight line, if the composition of the alloys is given in volume percentage, Fig. 1. Rule 2—In solid solutions, the electrical conductivity and temperature coefficient are always lower than those of the solvent metal, and usually a considerable decrease occurs with the first small percentage additions of the solute metal, Fig. 2b. If the two components form a continuous series of solid solutions, the electrical conductivity and temperature coefficient curves take the form of a U-curve, Fig. 2a. That some kind of proportionality exists between electrical conductivity and temperature coefficient of resistance is implied by the LeChatelier-Guertler rules and by study of data such as those given by Smith and Palmer,&apos; Fig. 3. Dellinger2 in 1910 first recognized this relationship in a number of commercial copper wires, ranging in conductivity from 94 to 100.7 pct I.A.C.S. He gave the ratio of temperature coefficient to the percentage of conductivity as a constant, C = 0.003939. A year later, Lindeck observed that the linear relationship was valid for a wider range of conductivity in "various sorts of copper," and concluded that the product of resistivity and temperature coefficient was 6.78x10-5 1.5 pct. Since then, this relationship seems to have been entirely ignored. Conductivity-Temperature Coefficient Relationship If the electrical conductivity of copper solid-solution alloys with phosphorus, silicon, arsenic, antimony, aluminum, nickel, manganese, and iron is plotted against the temperature coefficient of these alloys, the diagrams in Figs. 4 and 5 are obtained. Similar data were found with copper-rich solid solutions containing magnesium, cobalt, and titanium,&apos;" as shown in Fig. 6. In all cases, a linear relationship exists. The point representing the highest

Jan 1, 1952

By Howard W. Miller, Charles R. L. Oder

Approximately 5000 tons of zinc ore a day was mined during 1943 in the Mascot-Jefferson City district in East Tennessee. This ore came from the Kingsport formation, a part of the Knox dolomite, of Ordovician age. The Kings-port is composed of 350 to 400 ft. of limestone and dolomite. Thin cherts, sandy layers and shales are numerous. Frequently, the limestones are altered to crystalline dolomite. The Kingsport is divisible into four main lithologic zones. These divisions are illustrated in an accompanying table, which gives detailed sections of the ore-bearing beds as found in the mines and shows the exact positions of the various ore zones within the formation. Key beds are described and the practical applications of stratigraphy in mapping, prospecting and mining are discussed. Introduction The Mascot-Jefferson City zinc district is in Knox and Jefferson Counties, in the Great Valley of East Tennessee. It extends from Mascot, I3 miles northeast of Knoxville, to Jefferson City, about 30 miles northeast of that city. The American Zinc Company of Tennessee is producing from five mines in the district, in which it has operated for more than 30 years. The only other important producer is the Universal Exploration Co. The approximate daily production of the district in 1943 was 5000 tons of sulphide ore, grading from 2.5 to 6 per cent zinc. Small amounts of oxidized ore are mined intermittently. The Knox dolomite has been described by various geologists,&apos;-&apos; but no detailed descriptions of the rock sections revealed by mining have been published. Rock units are not conspicuously different and careful study is required to distinguish them. Nevertheless, familiarity with the stratigraphy of the mineralized zones is essential to successful exploration and extraction of the ores; therefore the purpose of this paper is to give detailed stratigraphic sections as measured in the mines, to discuss their important features and to show their relationship to the stratigraphy of the district. Generalized Section Table I gives the most characteristic general features of the major stratigraphic units. The formation names given in parenthesis are locally and widely used terms, the correlations of which are not necessarily established. For this reason they are put in quotation marks and are replaced by more restricted terms. The names "Mascot" and "Kingsport" were adopted from local towns. They were chosen jointly by Josiah Bridge, of the Federal Geological Survey, and the senior author for use in their separate unpublished manuscripts describing the Knox dolomite in East Tennessee. Descriptions of the type sections may soon be published. The name "Longview" was first applied by Butts6 in Alabama.

Jan 1, 1949

By Wallace F. Lovejoy

The conservation of mineral resources as a public policy question has received a great deal of attention in the area of petroleum and practically no attention in other mineral areas, except, of course, soil and water. Some insights into mineral conservation problems and how these problems can be approached in the social decision-making process are significant. THE MEANINGS OF CONSERVATION Conservation means many things to many people .2, 11 Too often it is a label attached to a proposed program or policy to add respectability and to gain public acceptance. It is a term applied to specific resources in some contexts and to resources generally in other contexts. The oft-quoted comment of President William Howard Taft that conservation is something everybody is for, no matter what it means, succinctly illustrates the confusion over both the meaning of the concept and the policies required to implement a conservation program. This confusion goes quite deep and is more than a matter of semantics or emphasis. For example, the efficient exploitation of a mineral deposit which might be applauded as good conservation in terms of that mineral, might well result in destruction of or harm to the environment which might be viewed as bad conservation. Economics provides some tools to help solve this sort of problem, but there may be fundamental differences in value systems among groups in this society, so that ultimately society must collectively make a subjective political choice as to what is good or bad conservation policy.a An Economic Definition of Conservation The economic concepts of conservation have more relevance and are more easily applied to minerals than to many other natural resources. This does not mean that economics goes all the way in understanding mineral conservation, but at least it provides a framework for analysis which later can be altered to include noneconomic variables. Perhaps the greatest confusion in discussing mineral conservation arises in attempting to relate purely physical concepts with economic concepts. An economist is interested in maximizing or conserving values; he is not interested in maximum physical recovery or utilization. He wants to know the costs and benefits of using, or not using, resources. The economic theory of mineral-resource conservation can be labeled variously as the theory of exhaustion, the theory of resource exploitation, the theory of resource utilization, or simply as a special case of the broad theory of capital.4,28 Consideration of these labels illuminates the concerns of the econo-

Jan 1, 1976

R. C. Canby, Wallingford, Conn. (communication to the Secretary*). —Apropos of the experimental reduction of copper from cuprous chloride by fusion with ground limestone and colre, as described by Messrs. Laist and Frick, and also proposed for use at Chuquicamata, it might be of interest to refer bricfly to the experience at Argentine, Kan., in the smelting of the suboxide of copper (as produced in the Hunt and Douglas process) containing appreciable quantities of chlorides. In the Engineering and Mining Journal of June 10, 1911,I gave some account of what had appeared to be crucial difficulties with the Hunt and Douglas process, and how the filter-press difficulty had been so rapidly overcorne after my discovery of the effect of the sodium salts in the leaching solutions. I also described the effect of the cupola-furnace gases upon the lime rock with which I had replaced the coke in the absorption tower, which apparently showed the presence of considerable chlorine, due to the imperfect conversion of the subchloride to suboxide, as well as that due to the difficulties of washing thoroughly the suboxide with the means provided, and also to the presence of chlorides in the cement copper which was smelted with the suboxide. The fumes from the cupola, when issuing direct into the atmosphere, were very dense and white, except when a hot furnace top caused a reddish tinge due to dust. These fumes had a peculiarly suffocating effect, SO that when they were blown over into the town the population suffered the greatest actual distress, not the mere annoyance which would have been due to a disagreeable odor. The absorption tower had been built at the instance of the city authorities to abate this nuisance, and not with the idea of making any additional metal savings. A serious feature in connection with the Argentine experience with the Hunt and Douglas process was, that it had been implicitly assumed that there could be no metal loss in the Hunt and Douglas process itself, and that all attempts to locate the ruinous copper losses which were accumulating in the metallurgical accounts were devoted to the roasting department. It is possibly unfortunate for metallurgical advance along these particular lines that just about the time of this discovery of this previously unsuspected volatilization loss, in the smelting of the suboxide, the Kansas City company made a contract with the Western Union Telegraph Co. for its supply of copper sulphate and the Hunt and Douglas

Jan 1, 1915

By G. K. Engelhart

A multi-stage counterflow process developed in Germany preheats dry pulverized portland cement raw materials held in suspension in rotary kiln waste gases. Capacity of the first kiln installed for this purpose in the United States has been increased from 860 to 1500 bbl per day, with fuel reductions from 1,100,000 Btu to 650,000 or 700,000 Btu per bbl. Sixty percent of total waste gas is used. As full use of the gas stream is approached, additional kiln production and fuel economy may be expected. EFFECTIVE use of rotary kiln waste gases to preheat dry pulverized materials has been demonstrated in full-scale operation at the Allentown Portland Cement Co. plant, Evansville, Pa. Pulverized raw materials are preheated in suspension in the gas stream in a multi-stage counterflow process which draws the gases through a series of cyclone collectors. Upon entering the first cyclone stage the material, continuously delivered and suspended in the gas stream, is successively collected and re-suspended until it discharges through the kiln feed pipe. Gas and material contact time is thus prolonged, providing a high degree of heat recuperation with a very low temperature differential between gas and material at the final stage. The suspension preheater, developed by Klock-ner-Humboldt-Deutz AG of Cologne, Germany, was first installed at the Norddeutsche Huette plant, Oslebshausen, Germany. Similar preheaters are now in operation at three other German cement plants. The first American installation, at the Allentown Portland Cement Co. plant, was designed and manufactured by Fuller Co. of Catasauqua, Pa., Humboldt&apos;s licensee for the United States, Canada, and Mexico. Design of this installation is essentially the same as the German original, but provision was made for varying the method to adapt the process to specific objectives of American portland cement production. Differences between German and American cement clinker production practices are directly related to differences in three primary production cost items: fuel, labor, and power. Because fuel costs are high in Germany and elsewhere in Europe, thermal efficiency has been the first objective of European cement producers and manufacturers of rotary kilns. The Germans have developed such recuperative equipment as the present suspension preheater, the Miag calcinator, and the Lepol kiln, the invention of 0. G. Lellep. In North America labor is the principal cost item, although rising fuel costs are of growing concern. High clinker production is therefore of first importance. Recent installations of longer dry process cement kilns have been disappointing, failing to make satisfactory reductions in exit gas temperatures when production is held at an acceptable level. The Humboldt suspension preheater satisfies both

Jan 1, 1955

By W. A. Griffith

The fundamental principles and modern techniques of experimental planning and data analysis, applicable to any type of research, are particularly important in flotation experimentation. Since they constitute the modern science of experimentation, they should be among the working tools of any scientist, research engineer, or plant operator engaged in flotation investigates. This chapter is a review of these principles and techniques. Equipment and procedures for the actual conduct of experiments will not be discussed here since these subjects are well covered elsewhere in this volume. Neither will any attempt be made to impart a working knowledge of statistical methods of data analysis since this would be impossible in the space allotted, and many excellent texts are available to the diligent inestigator.1-4 The objective here is simply to interest the reader in the application of statistical techniques to flotation experimentation by illustrating their utility in situations frequently encountered, and to point out the principles of experimental planning necessary for their proper use. Any conscientious metallurgist engaged in flotation experimentation or operations is well aware of the inherent complexity of the flotation process, and of the often frustrating difficulties this introduces into experimentation. The raw materials normally treated by the process are complex both physi- cally and chemically, and often highly variable even when from the same source. The flotation process itself is characterized by a very large number of potentially important process variables. Many of these are beyond the con- trol of the metallurgist, and some cannot even be measured quantitatively with available instruments. Those which can be measured and controlled with reasonable precision often produce effects which are intricately interrelated. Not only are the variables many, but the physical and chemical mechanisms by which they function are imperfectly under stood. To compound the difficulty, experimental techniques are relatively crude. Controls are not very precise, and the human factor looms large in most flotation experiments. These situations lead inevitably to experimental data of a relatively low degree of precision or reproducibility. Some are inclined to think that these conditions are unique to flotation experimentation. They are not. The experimental problems met by the agronomist, the biologist, the social scientist, and others are equally complex. Investigators in these fields pioneered in the development of methods for handling just such situations by proper experimental planning and the application of statistical methods in the analysis of data. Their pioneering work has grown into a well established modern science of experimentation which has spread into every field of science. This science is based upon statistical

Jan 1, 1962

By D. E. Etter, J. E. Selle

The Pu-Ce phase diagram was determined by differential thermal analysis, metallography, and elechm-nricroprobe analysis. The dingram is chararterized by a eutectic with extensive solid solubility in the cubic Phases of both cerium and plutonium. No intermediate phases were found. Cerium is soluble in e plutonium to 16.0 at. pet Ce at 626OC nnd in d plcltoniurn to 23.0 at. pet at 613 "C, decreasing to 17.5 at. pet at room temperature. No solubility in the a, ß, or ? phases was jound, and the mininum cerium required to stabilize 5 plutonium to room temperature is 3.2 at. pet. The maximum solubility of plutonium in 6 cerium is 19.5 at. pet at 721OC, and the maximum soluhility of plutonium in ? cerium is 34.5 at. pet. Invariant points in the system are: a) eutectic at 626oC, L16.5 = E Pu16.0 + y Ce65.5; b) peritectoid at613oC, e Pu13.5 -y Ce65.5- d Pu23.0. AS part of a program aimed at the determination of the phase equilibria in the Pu-Ce-Cu ternary system, preliminary investigations were made of the three binary systems. A survey of the Pu-Ce binary system by differential therma1 analysis indi- cated several areas of disagreement with the published diagram,&apos; primarily in the shape of the liquidus surface. Consequently, a thorough investigation of the system was undertaken, and this report presents the results of the study. EXPERIMENTAL PROCEDURE Three methods of investigation were used: differential thermal analysis (DTA), metallography, and analysis with electron-microprobe X-ray analyzer (EMX). The EMX analysis was particularly useful for the determination of solvus lines. The DTA method was most useful for the determination of the liquidus curves. Metallography complemented both of these techniques. Materials. The cerium metal used for most of this work had a freezing point of 805°C. This material showed 15°C premelting, and was found metallographically to contain some unidentified in~lusions.2 The temperature of premelting is defined as the point at which the DTA curve breaks away from the base line, analogous to a curve obtained from a solid-solution alloy. Several compositions were prepared near the cerium end of the diagram with higher-purity material which had a freezing point of 800°C. etallographic analysis showed this material to be relatively free of inclusions and only 8°C premelting was observed. Major impurities were found by spectrographic

Jan 1, 1964

By AIME AIME

ROBERT F. MEHL was born in Lancaster, Pa., March 30, 1898 and graduated from Franklin and Marshall College in 1919. He then went to Princeton and was granted his doctor&apos;s degree in physical chemistry in 1924. Two years as head of the department of chemistry at Juniata College, followed by a like period as National Research fellow at Harvard, working with T. W. Richards and Albert Sauveuir, satisfied Bob&apos;s immediate affections for college and university life and prepared him to turn temporarily to other fields.

Jan 1, 1938