By L. D. Hall, S. J. Rothman

DIFFUSION coefficients of RaD (PD) and RaE (Bi) in a Bi-0.255 atomic pct Pb alloy have been measured by the methods outlined in a previous paper.' The following changes were made in the experimental procedures: the bath was made up of about 400 to 500 g Bi; and no correction was made for the volume change of bismuth on melting. The data are presented in Table I and Fig. 1. A least-squares analysis of the data yielded D = (0.120 t 0.09) exp ( -9680 + 1070/RT) D- (0.0465 0.001) exp (-8100 + 466/RT). Statistical analysis of the data indicated that the activation energies are significantly different at the 50 pct level, but not at the 75 pct level, while the D values are significantly different at the 97.5 pct level, but not at the 99 pct level. The differences are thus not as clear-cut as they were for lead. However, bismuth diffuses faster than lead in high bismuth alloys as well as in lead. The high activation energies, more than twice the value calculated from viscosities, are in good agreement with the results of Grace and Derge.' No data were obtained at higher temperatures because of gas bubble formation in the capillary. Acknowledgments This work was supported by the Office of Ordinance Research under contract DA-04-200-ORD-178. The authors thank 0. P. Vieria and M. Volpe for help in the experimental work.

Jan 1, 1957

By R. W. Smith, M. E. Brookes

The temperature at which th: quenched 0' (ordered bcc) phase transfo.rms to the ( (complex hexagonal) phase on heating has been examined for certain Ag-Zn and Ag-Au-Zn alloys using an electrical resistivity method. The transition temperature decreases by approxinzately 7°C as the zinc content is reduced by 1 at. pct. The critical temperature, Tc, for long-range order has also been measured for a number of Ag-Au-Zn alloys. Extrapolation to zero gold content suggests that Tc decreases by approximately 5°C per 1 at. pct reduction in zinc content. The 0 phase of the Ag-Zn system exists over a narrow range near the composition Ag zn,' Fig. 1, and has a bcc structure which is disordered above 272°C. Slow cooling to temperatures below the range 274"/258"C allows the complex hexagonal phase, r° to form.2 This is the stable structure at room temperature.3 Upon quenching 0 -phase alloys from high temperatures, it is found that the 0 — (' transformation is suppressed; but ordering takes place (i.e., 0 -0'). This ordered structure can also be obtained by the room-temperature aging of cold-worked (0.4 Deformation of the 0' phase gives rise to a fur- ther hexagonal phase ( (of nearly ideal axial ratio) which reverts to b' within a few hours.= In view of this, it has been suggested that the equilibrium struc-

Jan 1, 1969

By Ralph Sweetser

THE present state of iron blast-furnace practice is metallurgical rather than mechanical; the tend-ency is toward intensity rather than toward ex-tension. The engineers have built blast furnaces big enough and strong enough, and have furnished accessory equipment ample and accurate enough for the present state of the art, but the metallurgical side has been too much neglected; the metallurgist, rather than the engi-neer, is now the man on whom the present and future progress in iron blast-furnace practice depends. The mining engineer has produced great tonnages of iron ores, and has kept ahead of the demands for quantity; now the metallurgist is improving the chemical and physical qualities of this product by ore-dressing and other forms of beneficiation. For a generation or more, the principles of mechanics have had most influence in the advancement of iron blast-furnace practice; atten-tion now is given more to the principles of metallurgy, chemistry, and ore-dressing. This metallurgical progress is taking place inside and outside the blast furnace. The two great determining factors of the inside operation are the slag, and the rate of combustibility of the coke. Outside the fur-nace, the progress is, and will be, along the lines of more careful mixing of ores and iron-bearing materials, in the sizing and washing of limestone, and in the char-acter and structure of byproduct coke.

Jan 3, 1922

By W. L. Chen

The Batac jig was first introduced in the US for fine coal cleaning in 1973 (Tackett, 1977; Hake, 1976). Since then, a total of six such jigs of various sizes have been installed in five US plants for a total capacity of 2346 t/h. The raw coal size ranges from 19 mm x 0 to 9.5 mm x 0-fraction sizes previously fed to heavy medium cyclones, Deister tables, or water only cyclones. Growing interest in the Batac jig as a replacement for the above equipment is due to the following reasons: • Unlike heavy medium cyclones, no magnetite is required. As a result, the operating cost of the plant is reduced. • The compactness of equipment is unique on a unit ton per hour basis as compared to other equipment. • Solid state electronic control of jig stroke length, frequency, and jig bed depth makes the equipment highly efficient. Installations of Batac jigs in the US as of June 1980 are shown in [Table 1]. Use of the Batac jig is even greater outside the US (Anonymous, 1980; Chen, 1980). Its use is not limited to fine coal but is applied to coarse coal as well, with 102 mm size in the feed (Zimmerman, 1975). In countries where consumption of magnetite associated with the heavy medium system of coal cleaning is considered a waste of iron ore resource, the Batac jig is regarded as the primary choice in the selection of cleaning equipment (Chen, 1980).

Jan 1, 1981

By Fred Van Covern

Before getting into a discussion of the subject of my paper, I want first to make it clear to everyone that I am speaking as an individual; and that any expressions of opinion that are contained herein, or may be expressed in any oral discussion that may follow its presentation, are entirely my own, and must not be construed to be the official opinion of the American Petroleum Institute. Demand fob Motor Fuel, 1936 During the year just closed the domestic demand for gasoline exceeded 481 million barrels. This compares with 434,810,000 bbl. consumed during 1935 and indicates an increase of 10.46 per cent. Export shipments amounted to 27,831,000 bbl. while in 1935 they totaled 30,613,000 bbl. Total demand, therefore, was 509,422,000 bbl., or 9.16 per cent above the 465,423,000 bbl. of 1935. Following are the figures for several years: Already we are supplying gasoline domestically and as foreign shipments at a rate almost 25 per cent greater than our low level of 1933. Before giving figures for 1937, I should like to spend a moment or two in discussion of gasoline inventories, from the point of view of minimum working stocks and other requirements and of probable actual levels. Inventories of Gasoline The year 1936 closed with about 62,900,000 bbl. of finished and unfinished gasoline in storage—about 6 million barrels more than was on hand

Jan 1, 1937

By W. A. Tiller, W. C. Johnston

A theoretical analysis of alloy solidification in which the effective partition coefficient, k, of the solute is allowed to vary as a function of interface position is performed. A variety of solute distm'butions in the solid is predicted depending upon the functional dependence of k with interface position. Conversely, the variation of k with interface position required to produce a particular solute distributzon in the solid can be calculated. These preciictions have been tested by controlling the width of the momentum boundary layer in the liquid as a function of interface position with a rotating mugnetic field. One of the objects of controlled solidification is to utilize the freezing process for the preparation of crystals of specific materials containing a predetermined distribution of solutes. For example, a thermoelectric power generation material may exhibit a figure of merit, 2,' as a function of temperature, T, and solute concentration, C, as illustrated in Fig. 1. If we wish to use this material in a device between the temperature limits T1 to T2 a significantly greater efficiency will result from the device if the thermoelectric element illustrated in Fig. 1 consists of a range of solute concentrations appropriately located with respect to the temperature distribution rather than using a sample of constant solute concentration. For this reason and many others2 we are interested in programming and controlling the solute distribution in a single crystal

Jan 1, 1962

It has been stated, by Sir James M. Barrie, that "the man of science appears to be the only man who has something to say, just now-and the only man who does not know how to say it ". The friendly jibe of the novelist contains enough exaggeration to make it humorous to the followers of Huxley and Spencer; but could any litterateur poke similar fun at the exponents of the avowedly utilitarian branches of science-the men of technology-without suggesting an unpleasant truth? Indeed the engineer does bungle language deplorably. He makes a fetish of efficiency, yet he shows no regard for the effective use of one of his most important tools-the pen; he believes devoutly in accuracy, yet he employs an instrument of precision as carelessly as a small boy handles a gun. This inconsistency may be due to causes such as were indicated by the Academic Senate when it undertook to explain the defective writing of the students in this university.* The Senate suggested that the student is "constantly subjected by his environment to the unedifying influence of myriad examples of poor English", and that he is also affected by "a certain public prejudice against correctness of expression". With these statements most of us will agree. Our local newspapers, for instance, tend to spoil the student's taste for good English; later in life, as an engineer, his daily contact with illiterate men inclines him to careless speech and slovenly writing. As

Jan 1, 1931

By William Blauvelt

Tun technical and engineering problems in the manufacture of coke are today the problems of the byproduct oven. Except in a few special localities, practically no beehive ovens have been built in the United States for the last 5 or 6 years except as renewals of old plants, and during these years the total number of beehive ovens in existence has been steadily falling. On the other hand, the number of byproduct ovens has increased from 4624 in 1911 to a total of about 7660 in operation at the end of 1917; with 2800 building, this makes a total of about 10,460 which will be in operation in 1918, or shortly thereafter. Preliminary Government estimates place the total production of coke for 1917 at 56,600,000 tons, the largest tonnage in the history of the industry. Of this 34,000,000 tons or 60 per cent. was beehive, and 22,-600,000 tons, or 40 per cent. was byproduct coke. Some time in 1918 the production of byproduct coke should pass the beehive output, and when the byproduct ovens now building are completed the total byproduct capacity will be about 40,000,000 tons of coke per. annum, which is over 70 per cent. of the record-breaking total coke production of 1917. The reasons for these changes in the coking industry are familiar to all of us, and need not be discussed here.

Jan 3, 1918

By R. J. C. Tait

INTRODUCTION Process Control at the Ecstall Concentrator begins in the open pit at the Kidd Creek Mine. While this paper, naturally, emphasizes the instrumental and technical features of the Process Control system within the concentrator itself, it would not be complete without some mention of the selective mining methods and grade control practices at the mine, and of certain features of plant design, which are simple, but highly effective, elements of the Process Control system. The success of the entire Process Control system, from pit to concentrate load-out, owes much to the high degree of cooperation and mutual understanding among all the operating departments at Ecstall Mining Limited and to the willingness of management to accept, from the start, an overall control philosophy based upon the inter-dependence of mining and metallurgical operations. INFLUENCES OF MINERALOGY AND METALLURGY ON MINE PLANNING AND PLANT DESIGN Mineralogically, the Kidd Creek ores are fine grained and mostly very complex. Because of complex mineral associations and extensive inter-locking, very fine grinding and regrinding of middling fractions are necessary and selective flotation requires a very delicate touch. Four separate concentrates are made for shipment to copper, lead and zinc smelters. The Process Control system is tailored to the metallurgical objectives of maximum recoveries of copper, lead, zinc and silver into concentrates of optimum quality, for maximum economic returns. For example, zinc and lead in copper con-

Jan 1, 1970

By Elmer R. Kaiser

COMBUSTION of coal and transfer of heat from flames and gases to boiler surfaces continue to be of great interest to engineers here and abroad. Numerous investigations have been in progress to improve furnace and boiler performance and economy. The importance of better understanding of the processes and opportunities for improvement is apparent when it is remembered that heat from at least 500 million tons of coal a year the world over is being transferred to boiler water at efficiencies ranging mostly between 50 and 90 pct. Even slight gains in efficiency, economy, and labor saving become very significant when multiplied by the enormous quantity of fuel consumed. Also the competitive position of the large coal, oil, and gas industries in satisfying the fuel consumers is greatly affected by the achievements made through technical progress with each fuel. This paper is part of a continuing activity of Bituminous Coal Research, Inc., to extend the knowledge of coal utilization for steam generation and to seek promising directions for future research and development in cooperation with others. Particularly in the latter regard, numerous interviews were held during the last three years to seek the experience and advice of boiler and combustion- equipment manufacturers, electric-utility executives, and fuel engineers. A wealth of published information was also reviewed, which together with the interviews pointed to the advisability of further work on ash and sulphur control.

Jan 3, 1954

By Dorsey A. Lyon, Robert M. Keeney

Page I. Introduction..........234 I1. Chemistry oF Copper Smelting...235 1. Native Copper Ores.......235 2. Oxide and Carbonate Ores....235 3. Sulphide Ores.......236 (a) Elimination of sulphur ...236 III. Reverberatory Copper Smelting...237 IV. Substitution of the Electric Furnace for the Reverberatory Furnace..................... 238 V. Smelting of Fine Michigan Native-copper Concentrates in the Electric Furnace.................. 239 1. Conclusions.................240 VI. Proposed Process for Electric melting of Fine Native-copper Concentrates.................. 241 VII. OrdINary Copper Blast Furnace 'Smelting......... 245 1. Prerequisites.................. 245 2. Losses .................... 247 VIII. Experimental Data on the Electric Smelting of Raw Sulphide. Oxidized and Carbonate Ores............. 248 1. Vattier's experiment................ 248 2. Wolkoff's experiments................ 249 3. Experiments of Stephan.............. 250 (a) Conclusions of Stephan ............ 251 IX. Smelting of Sulphide Ores in the Electric Furnace...... 251 1. Ores Treated.................. 252 2. Conclusions................... 253 X. ELectric Furnace vs. the Reverberatory Furnace and Blast Furnace as a Melting Agent.............. 253 XI. Smelting of Sulphide Ores without Roasting or Partial Pyritic Smelting............254 XII. The Electric Blast Furnace vs. the Copper Blast Furnace for Partial Pyritic Smelting.......259 1. Metallurgical conditions......259 2. Mechanical considerations......259 3. Comparison of costs.......260 (a) General considerations .....260 (b) Cost of plant........260 (c) Amount of electrical energy...260 (d) Cost of smelting.......261 (e) Cost of electrodes........262 XIII. The Use of the Electric Furnace in the Smelting of PyRITIc ORES : 262 XIV. Summary...................... 264

Jan 1, 1914

By A. W. Gray

Page CRUSHING STRENGTH...................... 659 The Black Dynamometer....................659 A Standardized Procedure for Crushing Strength Tests...... 660 Influence of Height of Test-piece upon Apparent Strength ..... 662 Influence of Packing Pressure and of Packing Time........ 662 Application of the Logarithmic Law...............665 Influence of Amalgamation Variables.............. 665 Influence of Temperature................... 669 The Transition Region Near 70" C............... 671 Influence of Packing Pressure at Various Temperatures ...... 673 Influence of Age upon Alloy and Amalgam........... 676 DIMENSIONAL CHANGES DURING THE HARDENING OF AN AMALGAM .......................... 678 The Black Amalgam Micrometer............... 678 Thermostated Dilatometer Designed by the Author........ 681 Graphical Representation of Reaction Expansions......... 683 The Typical Reaction Expansion Curve ............. 684 Influence of Packing Pressure................. 686 Influence of Trituration Time................. 687 Influence of Temperature................... 688 Influence of Mercury-alloy Ratio................ 689 Influence of Packing Time................... 689 Influence of Annealing the Alloy................ 691 Influence of Size of Alloy Particles...............691 Extension of the Typical Expansion Curve........... 693 Influence of Thermal Softening and of Reamalgamating a Hardened Amalgam.......................... 634 Curves Obtained with a Variety of Dental Alloys ........ 694 Copper Amalgam ...................... 694 PRACTICAL APPLICATIONS OF THE RESULTS.......... 695 Phenomena which reveal chemical and physical processes that probably go on in many alloys at temperatures not far removed from their melting ranges are observable in dental amalgams. These amalgams should. therefore. be of even more interest to the metallographer, the metallurgistl the chemist. and the physicist than to the dentist who uses them for saving decaying teeth. For this reason I am here de-

Jan 1, 1919

By B. F. Oliver, C. W. Haworth

Pure tin and Sn-0.5pct Pb ingots have been frozen unidirectionally from the base. For quiescent melts that were initially undercooled, a transition from lower eqlciaxed structure to an upper columnar structure is found in the alloy ingots. Columnar to equi-axed back to columnar transitions are observed in superheated alloy ingots, but no such equiaxed band is observed impure tin. The reproducible equiaxed band is associated with a thermal undercooling followed by a recalescence. This undercooling is <5"C, whereas the critical (maximum obtainable) under-cooling for both the pure tin and the alloys used is -20°C. A similar undercooling is observed at the same position in the pure tin ingots, although in this case no clear transition in structure can be seen. The structure of the pure tin ingots is either entirely columnar or mixed columnar-equiaxed. A consideration of the detailed thermal history of the ingots indicates that the ingot macrostructures are determined by the occurrence of a local therlnal undercooling in conjunction with nuclei multiplication and transport mechanisrris. GENERALLY it is found that a pure metal ingot solidifies so as to produce an entirely columnar structure. Frequently an alloy ingot is found to have a columnar outer zone and an equiaxed central portion. Early systematic work to examine the factors controlling the formation of the equiaxed structure was reported by Northcott&apos; who showed that, for copper alloys frozen unidirectionally with a given ingot practice, the alloying element influenced the length of columnar crystals and the extent of the equiaxed structure. Northcott showed that alloys with a wider freezing range more readily produced the equiaxed structure. The nucleation process can be important in producing equiaxed structures; frequently an alloy which readily solidifies with an entirely columnar structure will produce an entirely equiaxed structure when a nucleating agent is added to the melt.&apos; The formation of the equiaxed structure was attributed by Winegard and chalmers3 to the presence of constitutional supercooling; that is, a region of liquid in front of the growing solid could have a temperature below its equilibrium liquidus temperature. Thus, with a small enough temperature gradient in the liquid, it was suggested that the presence of constitutional supercooling may be sufficient to bring about the nuclea-tion necessary for the formation of an equiaxed structure. Although this explanation is plausible, and may be relevant in many ingots, Walker has described an experiment&apos; for which constitutional supercooling seems to be an unlikely cause of nucleation. A Ni-20 pct Cu alloy, repeatedly undercooled more than 50"C, was crystallized and found to show the typical colum-nar-equiaxed structure. The separation between the liquidus and the solidus for the alloy is 40°C. Thus, in this experiment the nucleation required for the formation of the equiaxed structure must have come about in some other way than by the nucleation catalysis constitutional supercooling hypothesis. Chalmers has suggested more recently5 that nuclei (in a typical ingot) are present immediately after pouring and are prevented from redissolving by the constitutional supercooling effect. More recently Uhlman, Seward, Jackson, and ~unt&apos; have shown direct evidence using ice and organic materials that freeze dendritically that the "remelt mechanism" may be an extremely effective crystal multiplication process during the freezing of ingots under conditions involving dendritic growth. JSlia" experimentally demonstrated the detachment of dendrite arms. chernov14 has analyzed the dendrite arm detachment process as a coarsening phenomena driven by the minimization of interphase area. Katta-mis and ~lemings" working with undercooled steel melts give evidence supporting this mechanism. Mechanisms of dendrite arm detachment such as those assisted by convection are believed to be the origin of the macrostructures obtained in this study. This study makes no attempt to distinguish the relative contributions of these mechanisms. The object of the present work was to obtain accurate temperature measurements during the solidification of an ingot and to correlate these measurements with the formation of equiaxed grains in the resulting ingot structures. Similar previous work is very limited. The measurements carried out by Northcott are neither sufficiently extensive nor sufficiently accurate for any interpretation. Plaskett and winegard7 carried out experiments on A1-Mg alloys in which they observed values of the temperature gradient, G, in the liquid and rate of freezing, R (for a given alloy solute content Co), at the transition from a columnar to an equiaxed structure. They reported that equiaxed crystals were produced at values of G/G approximately proportional to the solidus composition. Similar experiments using Pb-Sn alloys carried out by £111011" showed a linear relation between G/R and the solidus composition. However, the thermocouples were in the mold wall rather than in the melt and, in one case, ingot surfaces were examined. There is ambiguity in the meaning of the values of G and R measured in all these experiments. APPARATUS AND EXPERIMENTAL PROCEDURE Alloys were prepared by induction melting 99.999 pct Sn and 99.999 pct Pb to form a Sn-0.5 wt pct Pb alloy in air in a graphite crucible and casting into a cylindrical graphite mold 6 in. long, 1 in. in diarn , and with a & in. wall thickness. This mold was mounted on a copper base through which cooling water could be

Jan 1, 1968

By G. Derge, Ling Yang, G. M. Pound

The specific conductance and its temperature dependence were measured over the entire composition range of the molten Cu2S-CuCI system. At a typical temperature of 1200°C, 10 rnol pet of the ionically conducting CuCl reduced the specific conductance from about 77 ohm-lcm-l for pure Cu2S to about 32 ohm -1cm -1, and 50 mol pet CuCl reduced the conductance to that for pure CuCI—about 5 ohm 1cm1. The nature of electrical conduction in molten Cu2S, FeS, CuCI, and mixtures was studied by measuring the current efficiency of electrolysis at about 1100°C. The Cu2S, FeS, and mattes were found to conduct exclusively by electrons, but addition of 1 5 wt pet CUS to Cu2S produces a small amount of electrolysis. Addition of CuCl to Cu2S suppresses electronic conduction, and ionic conduction reaches almost 100 pet at a CuCl concentration of about 50 mol pet. These facts are interpreted in terms of electron energy level diagrams by analogy to the situation in solids. RESULTS of electrical conductivity studies on molten Cu-FeS mattes as a function of composition and temperature have been reported.&apos; The specific conductances ranged from about 100 ohm-&apos; cm-&apos; for pure Cu2S to 1500 ohm-&apos; cm-1 for pure FeS. This is in sharp contrast with the low specific conductance of molten ionic salts for which the transfer of electricity is by migration of ions in the field. In general, these ionically conducting molten salts, such as NaC1, KC1, CuC1, etc., have a specific conductance of the order of magnitude of 5 ohm-&apos; cm-&apos;. It was concluded on the basis of this evidence that molten FeS and Cu,S exhibit electronic conduction. Pure molten FeS has a small negative temperature coefficient of specific conductance, resembling metallic conduction, while pure molten Cu2S has a small positive temperature coefficient, resembling semi-conduction. The molten Cu2S-FeS mattes follow a roughly additive rule of mixtures, both with respect to specific conductance and temperature coefficient. Savelsberg2 has studied the electrolysis of molten Cu2S and Cu2S + FeS. He concluded that while molten Cu2S is an electronic conductor, there is some ionic conduction in molten Cu2S + FeS3 owing to the formation of the molecular compound 2Cu2S.FeS and its dissociation into Cu1 and FeS2-1 ions. The present work does not verify his results. Chipman, Inouye, and Tomlinson" have studied the specific conductance of molten FeO and report a high specific conductance, about 200 ohm-1 cm-1 of the same order of magnitude as that found for molten mattes, and a positive temperature coefficient. They interpret these results in terms of p-type semiconduction in the ionic liquid by analogy to the situation in solid FeO.1 imnad and Derne&apos; detected appreciable ionization in molten FeO by means of electrolytic cell efficiency measurements. In order to verify the conclusion that electrical conduction in molten Cu2S and mattes is electronic, and to gain further insight into the structure of molten sulfides, the following investigations were carried out in the present work: 1) The specific conductance, s of the molten system Cu2S-CuC1 was measured as a function of temperature over the entire composition range. As discussed later, molten CuCl is an ionic substance. It was thought that if molten Cu2S were simply ionic in nature, addition of small amounts of CuCl might not have a catastrophic effect in lowering the high conductance of the Cu2S. On the other hand, if much electronic conduction occurs, addition of the ionic CuCl should have a large effect in destroying the electronic conduction. 2) The electrolytic cell efficiency of the following molten systems was measured at about 1100°C in specially designed cells: Cu3; Cu2S + FeS, 50:50 by wt; FeS; Cu2S + CuS, 15 wt pet; Cu2S + CuC1, 5.9 to 46.4 mol pet; and CuC1. This gives a direct measure of the fraction of current carried by ions in these melts. Further, the cell efficiency, extrapolated to zero ionic current, is given by cell efficiency = (s leasile + s elexstronic). [1] s lucile for molten CulS would be expected to be no greater than that for molten CuC1, whose s lonle is about 5 ohm-&apos; cm-1, as will be seen in the following. u,.,,.,.,.......for molten Cu,S is of the order of 100 ohm-&apos; cm-&apos;.&apos; Thus, a large increase in cell efficiency from 0 to values of 10 to 100 pet upon addition of CuCl to Cu2S would indicate destruction of the electronic conductance. Conductance Measurements Experimental Procedure—The apparatus and experimental method were the same as those described in detail in connection with the study of electrical conduction in molten Cu,S-FeS mattes.&apos; A four terminal conductivity cell and an ac poten-

Jan 1, 1957

By C. H. Li, S. H. Bendel, J. A. Sartell

Small additions of Mg to a 62 Cu-38 Ni alloy reduce the oxidation yates drastically between 500° and 850°C. Metallographic examination of the oxide scale disclosed a continuous network, identified by X-ray diffraction as (Ni, Mg)O solid solutions, located along the former alloy grain boundaries. This network acts as a barrier to diffusion. It is thought to result from the segregation of mg to the alloy grain boundaries. Oxidation occurs preferentially in these regions because of the presence of this more active element. To substantiate these ideas, homogenized alloys ulere oxidized. No oxide network was produced and oxidation rates were the same as for the parent 62 Cu-38 Ni alloy. An interesting aspect of the oxidation of the 62 Cu-38 Ni alloy previously described by the present authors, is the relationship between oxidation kinetics and changes in the microstructure of the oxide.&apos; The oxide scale on these alloys consists of two layers: a thin layer of CuO outside a much thicker layer of Cu20 in which particles of NiO are dispersed. In addition, immediately beneath the oxide-metal interface there is an internally oxidized zone in which NiO particles are dispersed in a copper-rich alloy matrix. Experimental observations on the growth of the individual layers under isothermal conditions have led to the conclusion that the rate-determining step in the oxidation of this alloy is the diffusion of anions through the Cu20 layer. It has been found that this diffusion rate is increased by the recrystallization of the outer CuO layer. Willardson and Gorton have reported that the addition of magnesium to the 62 Cu-38 Ni alloy causes a decrease in the oxidation rate.2 The present investigation was undertaken in order to determine the mechanism by which magnesium additions improve the oxidation resistance of the 62 Cu-38 Ni alloy. EXPERIMENTAL PROCEDURE Fifty-gram ingots of Cu-Ni alloys were prepared by vacuum melting materials of 99.999+ pct purity. These ingots were then remelted in a He atmos- phere and magnesium added in the form of a previously prepared and analyzed Cu-Mg master alloy. This procedure was necessitated by the high reactivity of pure magnesium at high temperatures. The proportion of the alloying elements was adjusted so as to obtain alloys with the desired magnesium content while maintaining a Cu-Ni ratio of 62 :38 by weight. (All alloy compositions will be given in weight percent.) Since it was considered desirable to study the oxidation of only single-phase, solid-solution alloys, it was necessary first to determine the approximate limit of solid solubility of magnesium in the 62 Cu-38 Ni alloy. A series of melts with various magnesium contents was made, homogenized by annealing for 48 hr at 975OC, then cooled in the furnace. Metallographic samples were prepared, etched in a potassium dichromate solution and examined at XI500 for the presence of a second phase. The alloys were then chemically analyzed and it was found that the approximate limit of solid solubility of magnesium in the 62 Cu-38 Ni alloy was 1 pct Mg. The ingots containing less than 1 pct Mg (0.19, 0.29, 0.58, and 0.87 pct Mg) were cold-rolled down to thicknesses suitable for oxidation experiments and specimens for gravimetric studies were cut to dimensions of 3.0 by 1.5 by 0.05 cm, specimens for inert marker studies, 0.6 by 0.6 by 0.17 cm. These were heat-treated in a protective atmosphere at a temperature (975" C) well above the oxidation temperatures and furnace-cooled to insure structural stability of the alloy during oxidation. Immediately prior to oxidation, the specimens were chemically cleaned by immersion for 1 min in a solution of 2 parts nitric acid, 1 part acetic

Jan 1, 1961

By M. Hansen, C. C. Wang

THE 6 phase of the Cu-Sn system (Cu,Sn, = 32.53 pct Sn) was considered to be stable down to room temperature until Owen and Iball showed by X-ray analysis that it undergoes a eutectoid decomposition into the a and e phases at a temperature near 300°C. Their findings have been confirmed by other investigators,2-5 a11 of whom used X-ray diffraction studies of powdered specimens. The transformation temperature has been reported by various authors as lying between 300" and 380°C. To our knowledge, no microscopic evidence of the eutectoid reaction has been published, as yet. It was in connection with other work that longtime annealings at 300°C were conducted with alloys containing 22, 32.6, and 35 pct Sn (nominal compositions) prepared from electrolytic copper and electrolytic tin and cast in a small iron mold. The specimens were first annealed at 700°C for 5½ hr and quenched from 400 °C after cooling to, and annealing at, that temperature for 9½ hr. After this treatment the sample with 22 pct Sn was cold worked for 15 pct reduction in thickness; the 32.6 and 35 pct alloys were too brittle to be cold worked. The final anneal at 300°C was done in a sealed pyrex glass bulb for 63 days. Fig. 1 represents the microstructure of the annealed alloy with 22 pct Sn. It shows primary a solid-solution crystals in a matrix of the (a + 8)-eutectoid formed at 520 °C. The a crystals contain 8 inclusions which precipitated from a due to the decrease in the solubility of tin in copper with fall in temperature. The decomposition of the 8 phase into a (light) and E (dark) can clearly be seen in some areas of the (a + 8)-eutectoid matrix. However, the decomposition is far from being completed, even after the long-time anneal used. Figs. 2 and 3 depict the microstructures of the annealed 32.6 pct alloy, which was intended to consist entirely of 6 phase. Due to some loss in copper on melting, the composition is slightly higher in tin. Accordingly, the sample after quenching from 400 "C consisted of grains of the 8 phase with the e phase arranged along the grain boundaries and as a Wid-manstatten precipitate within the 6 grains. After an annealing time of 63 days, the eutectoid decomposition, 6 + a + e, is still in its early, initial state. The pearlitic type of eutectoid is nucleated at the c crystals, preferably those surrounding the grain boundaries of the 8 phase. The appearance of the (a + €)-eutectoid in the 35 pct Sn alloy was very similar to that shown in Figs. 2 and 3. Again, the eutectoid decomposition nucleated at the 6 phase and proceeded from there into the 8 areas. As is evident from Fig. 2, the rate of decomposition of the 6 phase at 300°C is extremely sluggish: In the representative area shown only about 5 pct of the 8 phase has undergone the eutectoid trans- formation after annealing for 63 days. On the other hand, Owen and Williams2 have reported that X-ray photographs of powdered samples with between 17.5 and 34 pct Sn did not show 8 lines after annealing for only five to seven days at 300°C. This is in accordance with the fact that the rate of reaction in powdered samples is higher than in massive specimens, as a result of the excess free energy of the powder (due to its greater surface area). The authors wish to express their thanks to C. A. Johnson for preparation of the micrographs.

Jan 1, 1952

By Dwight H. Seely, Louis R. Records

A process for low-temperature dehydration of natural gas utilizing Joule-Thomson effect in expansion through a throttling orifice has been tested in a full-scale field installation. The results of these tests are presented in the form of performance curves from which the process may be easily evaluated. The effect of separation temperature on condensate recovery from the process is also shown. INTRODUCTION The transportation of natural gas from producing well to the consumer has always encountered the problem of hydrate prevention. This problem has become increasingly important in the past ten years due to the rapid increase in produced gas volumes, production pressures, transportation pressures and distance from producing wells to consumer. Natural gas, as normally produced from gas or gas-condensate wells, is saturated with water vapor at well-head conditions of temuerature and pressure. The solution of the hydrate problem require; but one basic process — dehydration of the gas to a water content which will result in a water dew-point below the minimum temperature to be encountered from the producing well to the point of consumption. Much of the recent development of gas and gas-condensate reserves in the Gulf Coast Area has been in locations which are accessible only by water. High well-head pressures, pipeline construction and maintenance costs and the desirability of final central gas-condensate separation facilities have stimulated the development of dehydration equipment which can be installed at each well and which will permit hydrate-free transportation of both gas and condensate in the same line to central facilities. There are four types of natural gas dehydration processes now used: 1. Adsorptive processes. 2. Absorptive processes. 3. Chemical reaction processes. 4. Refrigeration processes. The first three of these processes are indirect in that they require use of adsorbents, absorbents or reactive chemicals. These materials require regeneration and part of the total gas stream is consumed in the regenerative process. Indirect processes have a wide range of flexibility as defined by allowable operating pressure and temperature, but most are not easily adapted to automatic operation. The refrigeration process described in this paper was designed for installation at the producing well-head. It requires no regenerative cycle and with normal well-head temperatures no external source of heat. The flexibility of this process is limited only by the pressure drop which may be allowed between well-head and transportation line. THEORY There are three basic physical concepts involved in the low temperature dehydration process. These are: 1. Formation of hydrocarbon hydrates. 2. Joule-Thompson effect resulting from the expansion of gaseous mixtures through a throttling orifice. 3. The equilibrium composition characteristics of water vapor and gaseous hydrocarbon mixture.. The chemical composition and physical structure of hydrate; have been described by several investigators.3,4,5,10 Specific conditions of temperature, pressure and composition as well as the requirements for turbulence and presence of free water necessary for hydrate formation have been described by Katz.6 Natural gas hydrates, as they are found in plugged gas pipe lines, have the appearance of packed snow. The mass of these hydrates has low continuous porosity and permeability. Joule-Thomson effect. or the reduction in temperature which occurs when natural gas is throttled throusll a restrictive orifice, is the basic phenomenon which permits efficient use of refrigeration for the purpose of dehydrating natural gas. Joule-Thomson coefficients for gafeous mixture; of methane with ethane and with butane have been reported by Buder.-I~olzer, Sage and Lacey.2 Brown1 predicted temperature drops for pressure drops from enthalpy-entropy calculations. Aside from this work there were no fundamental data found which would be applicable to natural gas mixtures of varying spe-

Jan 1, 1951

By Dwight H. Seely, Louis R. Records

A process for low-temperature dehydration of natural gas utilizing Joule-Thomson effect in expansion through a throttling orifice has been tested in a full-scale field installation. The results of these tests are presented in the form of performance curves from which the process may be easily evaluated. The effect of separation temperature on condensate recovery from the process is also shown. INTRODUCTION The transportation of natural gas from producing well to the consumer has always encountered the problem of hydrate prevention. This problem has become increasingly important in the past ten years due to the rapid increase in produced gas volumes, production pressures, transportation pressures and distance from producing wells to consumer. Natural gas, as normally produced from gas or gas-condensate wells, is saturated with water vapor at well-head conditions of temuerature and pressure. The solution of the hydrate problem require; but one basic process — dehydration of the gas to a water content which will result in a water dew-point below the minimum temperature to be encountered from the producing well to the point of consumption. Much of the recent development of gas and gas-condensate reserves in the Gulf Coast Area has been in locations which are accessible only by water. High well-head pressures, pipeline construction and maintenance costs and the desirability of final central gas-condensate separation facilities have stimulated the development of dehydration equipment which can be installed at each well and which will permit hydrate-free transportation of both gas and condensate in the same line to central facilities. There are four types of natural gas dehydration processes now used: 1. Adsorptive processes. 2. Absorptive processes. 3. Chemical reaction processes. 4. Refrigeration processes. The first three of these processes are indirect in that they require use of adsorbents, absorbents or reactive chemicals. These materials require regeneration and part of the total gas stream is consumed in the regenerative process. Indirect processes have a wide range of flexibility as defined by allowable operating pressure and temperature, but most are not easily adapted to automatic operation. The refrigeration process described in this paper was designed for installation at the producing well-head. It requires no regenerative cycle and with normal well-head temperatures no external source of heat. The flexibility of this process is limited only by the pressure drop which may be allowed between well-head and transportation line. THEORY There are three basic physical concepts involved in the low temperature dehydration process. These are: 1. Formation of hydrocarbon hydrates. 2. Joule-Thompson effect resulting from the expansion of gaseous mixtures through a throttling orifice. 3. The equilibrium composition characteristics of water vapor and gaseous hydrocarbon mixture.. The chemical composition and physical structure of hydrate; have been described by several investigators.3,4,5,10 Specific conditions of temperature, pressure and composition as well as the requirements for turbulence and presence of free water necessary for hydrate formation have been described by Katz.6 Natural gas hydrates, as they are found in plugged gas pipe lines, have the appearance of packed snow. The mass of these hydrates has low continuous porosity and permeability. Joule-Thomson effect. or the reduction in temperature which occurs when natural gas is throttled throusll a restrictive orifice, is the basic phenomenon which permits efficient use of refrigeration for the purpose of dehydrating natural gas. Joule-Thomson coefficients for gafeous mixture; of methane with ethane and with butane have been reported by Buder.-I~olzer, Sage and Lacey.2 Brown1 predicted temperature drops for pressure drops from enthalpy-entropy calculations. Aside from this work there were no fundamental data found which would be applicable to natural gas mixtures of varying spe-

Jan 1, 1951

By H. Biloni, B. Chalmers

Metallographic studies of the segregation of solute in and near the surfaces of chill-cast alloys have shown that, under sufficiently severe conditions, nucleation on the cold mold surface is followed by the formation of a disc of solid of the same composition as the liquid. This disc is surrounded by two concentric rings in which the concentration first decreases and then increases. The discs and rings are surrounded by a region in which arms of low solute concentration separate regions of high concentration. These arms start at the periphery of the outer ring and are initially radial; they make a gradual curved transition from the radial direction to a crystallographic direction. A normal dendritic substrcture is established beyond the position at which the arms have become crystallographically aligned. When the cooling is less severe, the disc becomes less irregular in shape and has a concentration minimum at the center. The term "Predendritic" is proposed for these transitions. A qualitative explanation is outlined for the phenomena observed at the surface and in the equiaxed region of the ingots. It is well-established1-&apos; that the normal mode of solidification for alloys under most conditions is dendritic. A characteristic of dendritic solidification is the growth of rods or plates in specific crys-tallographic directions. The remaining liquid solidifies later, usually with a higher concentration of solute than the original liquid. Very little is known, however, about the transition from a crystal nucleus until the dendritic pattern is established. It is clear that there must be a transition because the nucleus is much smaller than the characteristic spacings found in the "steady-state" structure. And it also seems clear that the initial conditions must be important since the undercooling existing during the nucleation of the grains has a remarkable influence upon the grain size4 and the segregation pattern. The present paper reports a study of the micro-segregation in regions where crystals have nucleated, and the conclusions that can be drawn regarding the early stages of growth, in connection with the details of the solidification process. Aluminum of 99.993 purity, A1-Cu alloys containing 0.5 to 20 wt pct Cu, and Pb-Sn alloys with 5 wt pct Sn were cast and examined metallographically at the as-cast surface, close to the surface, and in the interior after casting. The alloys were cast from controlled temperatures against surfaces at different temperatures ranging from room temperature to approximately the liquidus temperature of the alloy. The surfaces were, in various experiments, graphite, stainless steel, copper, and aluminum. The methods used for metallographic examination were as follows. 1) The Nomarski phase contrast interferometer6 was used to obtain information on the topography of the as-cast surface. 2) The distribution of any solute present in A1 99.993 pct and copper in the A1-Cu alloys was studied by the anodic film technique originated by Lacombe and Mouflard7 and previously applied in the study of the solidification of aluminum by Biloni.8 The electropolished surface of the specimen is anodized under controlled conditions so that the thickness of the oxide film and therefore the interference colors under white light are sensitive to the local composition. This technique was applied to the as-cast surfaces and to metallographically prepared surfaces from the interior. 3) If in Al-Cu alloys, the surface is anodically oxidized for several minutes, instead of seconds as in the color-film technique, the copper segregation is outlined by a different level with respect to the matrix. This method is less sensitive but complementary to that for the color films. 4) The distribution of copper revealed and mapped by the metallographic techniques was confirmed by electron probe. 5) In samples with high concentration of copper, evidence for the copper distribution could be seen optically after electropolishing.

Jan 1, 1965

By Attilio Ligasacchi

The production of magnetite in copper smelting has been the subject of wide investigation in the past.1-9 It is accepted that most of the magnetite is produced in the converters and returned to the re-verberatory furnace with the converter slag. Part of this magnetite is circulated back to the converters in the matte. As a result, if proper fluxing practice is not followed, and temperatures in the converting process are not strictly controlled, an undesirable circulating load of magnetite may occur. This might ultimately lead to saturation in the reverberatory bath with consequent settling of the magnetite at the furnace bottom. This paper contains the cumulative results of a series of investigations on the formation and control of magnetite presently being conducted by the metallurgical department of the Chino Mines Division of Kennecott Copper Corp. THE METHOD USED FOR THE DETERMINATION OF MAGNETITE AND OTHER MAGNETIC MATERIALS Conventional wet chemical magnetite analyses are neither reproducible nor theoretically sound. These analyses are sensitive to time, temperature, and heating rate-all factors which tend to decrease their accuracy and reproducibility. To overcome the unreliability of the above method, H. W. Mossman1 developed an inductance bridge magnetite "meter" which completely replaces the wet chemical analysis with the advantage of quicker and reproducible results. Fig. 1 is a schematic diagram of the meter in use in the Chino metallurgical laboratory. When a pulverized specimen with magnetic properties is placed in coil A of the inductance bridge circuit, the permeability of the core is increased, causing a voltage drop across the coil. The unbalance is amplified to operate the balancing motor which adjusts the movable iron core in coils C and D to bring the bridge back to balance. An indicator arm connected to the movable iron core indicates directly the percent, or weight, of the magnetic material in the specimen. Coil B acts as a reference coil and a zero adjustment. The meter is standardized with a set of various amounts of -100 mesh pure magnetite crystals (99.8 pet Fe3O4) thoroughly mixed in a test tube with -100 mesh quartz sand. These mixtures are combined with inert transoptic powder and heated to 140° to 160°C (melting point of the powder) and subsequently cooled to room temperature, solidifying the whole mixture, in this manner eliminating any possible preferential orientation of the magnetite grains. In order to determine the effect of the particle size" of the magnetite and other magnetic materials on the meter determinations, five size fractions were obtained by wet screening of the 99.8 pet pure magnetite and several reverberatory matte and slag samples. The following size fractions were investigated: -80 + 100; -100 + 150; -150 + 180; -200 + 250; -250 + 300 and -100 mesh. The deviation of the meter readings for the various sizes of each sample never exceeded ±0.3 pet. This deviation is considered well within the accuracy needed for common smelter operation procedures. Further investigation proved also that grinding slag and matte samples in our laboratory disc grinder normally produced a powder constituted of 95 pet -200 + 300 mesh. For practical purposes a - 100 mesh size was used as standard for our studies. It was also found that for rapid determinations tamping of the sample in the test tube was sufficient and gave comparable results with those samples solidified with transoptic powder. For the purpose of this study we define the magnetite content in copper smelter slags and matte as the equilibrium amount of crystalline Fe3O4 existent in the specimen at a given reference temperature, excluding any secondary magnetite precipitated in the specimen during nonequilibrium conditions. MAGNETITE DETERMINATION IN SLAGS Since it is impossible to ascertain the status of equilibrium of a conventional slag sample, due to

Jan 1, 1965