By C. C. Harris

The characteristics of some common size distribution equations are critically discussed. A generalized form of several well-known size distribution equations is obtained from a differential equation describing statistical distributions. The equation contains three parameters and can describe the major features of size distributions in the fine and the coarse size regions. A graphical method for its implementation is provided. The application of this and other equations to sets of data are compared both for the quality of fit and from a comminution kinetics viewpoint. If a narrow size range of a brittle material is broken sufficiently to obliterate the feed sizes, but not so severely that excessive secondary breakage occurs, a plot of cumulative fraction by weight undersize (Y) vs. sieve size (X) on a log log grid (sometimes called the Gates-Gaudin-Schuhmann plot)1-3 gives a straight line of slope ~ 1 over much of its range. On closer inspection, deviations in the extreme coarse range covering perhaps 10 to 30% of the total sample may be apparent (frequently, a change in slope from ~ 1 to a value different from unity) together with over-all slight irregular departures from a smooth line. One model of breakage postulates that the same fracture pattern persists throughout all size ranges.4 The fracture pattern is characterized by the slope of the line on a log log grid. Accordingly, a distribution of sizes broken in the manner specified earlier is expected to produce a size distribution having the same slope as that of a broken narrow size range. Additionally, the slight irregularities mentioned above should even out in the summation process, giving a smooth straight line of slope ~1 on a log log plot. This idealized state of affairs does not, however, describe the distribution of a multi-event process such as that for a tumbling mill product. On the average, these curves (plotted again log log) tend to have a slope in the fine region different from and usually less than unity,5 while the coarse size region curves with increasing slope for cases of mild reduction, and with decreasing slope when moderate or severe size reduction has occurred. In addition, there are usually slight irregular deviations from a smooth curve. Most curves display two distinct regions — fine and coarse — and a few curves show one or more intermediate regions. Feed size studies6,7 show an effect which theory is required to explain. For the same material, mill loading and other operating conditions, and the same time of grinding, plotting the dimensionless ratios Y vs. X/(feed size) does not reduce the size distribution data to the same curve. Y vs. X does not correlate the coarse region, but it can provide a crude correlation of the fine region which improves as size diminishes and as grinding time increases. The size distribution in the coarse region is somewhat more dependent on the feed size than is the distribution in the fine region wherein the degree of dependence diminishes as time proceeds; the distribution of sizes in the fine region are determined largely by the nature of the material and the comminution conditions. A comprehensive model of comminution must recognize that several different patterns or modes of breakage can occur in a mill; 5,8,9 that there can be some selection in that some size ranges are broken more than others; and that, while some particles may be the product of a single fracture event, or may even remain unbroken, others result from multiple rebreak-age. Thus, breakage in a tumbling mill is more complex than the Schuhmann4 model admits in that several different types of comminution micro-events* occur rather than just one type, and these events, though different in size scale, are of the same overall pattern as that which is visualized by the model. The concept of an average comminution micro-event has, therefore, a mathematical rather than a physical connotation, at least for tumbling milling. Equations with which to describe particle size distributions have been sought for over half a century.10-13 No equation presently in general use was first derived from an analysis of the statistical mechanics of breakage; whatever theoretical basis the existing

Jan 1, 1969

By N. J. Grant, A. W. Mullendore

Three aluminum alloys of 0.94, 1.92, and 5.10 pct Mg, prepared from very high purity metals, were tested at 500°, 700°, and 900°F in creep rupture. The degree of strengthening through solid-solu-tion alloying and the effects on the deformation characteristics and fracture were examined. The ductility of the alloys as a function of stress and temperature was closely followed. STUDIES of the creep process in pure metals in recent years have done much to expand the understanding of the fundamental deformation and recovery processes that contribute to overall creep behavior. In order that this knowledge may be applied to commercial alloys, it is necessary to know the principles governing the effect of alloying on the mechanisms of creep. A limited amount of work has been performed in this field, but few investigators have attempted to follow the changes in particular creep mechanisms with alloying. Recently, studies of the effects of solid-solution alloying on the plastic properties of aluminum have been conducted by Dorn, Pietrokowsky, and Tietz,1 Sherby, Anderson, and Dorn,2 and Sherby and Dorn.3 This paper presents the results of an investigation of the effect of solid-solution alloying of high purity aluminum with magnesium on the creep-rupture properties, and correlates these observations with changes in the creep mechanisms. This work is thus an extension of the creep-rupture observations of Servi and Grant4,5 and the deformation studies of Chang and Grant.6,7 Experimental Procedure Three alloys of aluminum containing approximately 1, 2, and 5 pct Mg were tested. These alloying additions are all within the solid-solubility limit at the testing temperatures.' The analysis of the materials is presented in Table I. The tests fall into two categories: l—creep-rup-ture tests at 500°, 700°, and 900°F, and 2—structure study tests performed primarily at 700°F. Speci-mens of 0.160 in. diameter with milled flats for metallographic observations" ' were utilized for the structure studies. All specimens were annealed in one step to give the desired grain size for the tests. Table II presents the annealing data and final grain sizes. The specimens were polished electrolytically before testing with Jacquet solution (2/3 acetic anhydride, 1/3 perchloric acid) at 25" to 30°C, and 15 to 20 v. Creep-rupture testing was performed under constant load with the apparatus previously described." Results and Discussion Creep-Rupture Properties: The log-log plots of creep-rupture data are presented in Figs. 1 and 2. For these very pure single-phase alloys, the minimum creep rate and the rupture life both exhibit straight-line dependence on stress in this method of plotting as they have for commercial alloys0,10 and for pure aluminum." Curve breaks, based on the use of straight-line segments, at 500°F have been found by metallographic study to correspond to a transition from low to high temperature behavior and so represent zones of equicohesion. Specimens on the high creep-rate side of the break showed normal granular deformation processes whereas those on the low creep-rate side showed rapidly increasing grain-boundary sliding and migration with extensive evidence of intercrystalline cracking at 500°F. Two micrographs of the 0.94 pct Mg alloy, Fig. 3, show the increased participation of the grain boundary in the deformation process at 500°F with decreasing stress. In Fig. 3a is shown the structure of a specimen which exhibits little deformation along the grain boundaries and failed transgranularly; in Fig. 3b is shown the increased deformation along the grain boundaries at a lower stress for a specimen which showed appreciable intercrystalline cracking. The severity of intercrystalline cracking increased with increasing magnesium content at 500°F. Intercrystalline cracking disappeared in most of the specimens at 700°F and persisted only in the 5 pct Mg alloy at high creep rates. At 900°F all of the specimens deformed with extensive grain-boundary participation, including extensive grain-boundary migration. None of the alloys at 900°F showed intercrystalline cracking.

Jan 1, 1955

By John K. Kennedy

ThE basic equations describing continuous zone-melting via the zone-void method were reported by Pfann. Using these equations, a theoretical study was undertaken in this laboratory on the effect of the variation of the significant parameters of the zone-void system. These parameters are the zone length, 1, the heater length, h, and the effective distribution coefficient, k. The object of this study was to determine the effect of these parameters on and (where a = Cp/Cf and ß = Cw/Cf, Cp, C,, and Cf being, respectively, the solute concentration in product, waste, and feed) so that, in future application of this technique to the ultrapurification of materials, the effect of 1 and h would be predictable regardless of the value of k. The basic assumptions made by pfannl were, for the purposes of this study, assumed to hold. For k < 1, the steady-state solute distribution in the stripping section and the shift in this distribution brought about by passage of a void is shown in Fig. 7 of Ref. 1. In this section the definition of k and ß precludes the possibility of ß assuming values less than unity when k < 1. In the course of this investigation it was found that computations based on Pfann&apos;s equations gave values of ß less than unity in the region 1 > k > l/h for almost all values of Ls, where Further computations showed that 6 assumes negative values when k > 1 for many values of L,, 1, and h. A check of the derivation of the stripping-section equations showed that an error had been

Jan 1, 1964

William H. BLAUVELT, Anaconda, Mont.: Mr. Stetefeldt&apos;s comparison of the producer-plants at Aspen, Colorado, and Park City, Utah, is of special interest at this time, when the attention of all western metallurgists is so forcibly drawn to the necessity of reducing expenses and losses. The fact that wood was used at Park City before gas was introduced, for firing the Stetefeldt furnace and dryer, offered an excellent opportunity for showing the economies resulting from the adoption of gas in place of wood, as well as a comparison between the two gas-plants. Some time ago Mr. Stetefeldt contributed an article to one of the technical journals, in which the economy obtained by the substitution of gas for wood at this plant was shown quite in detail. I regret not being able to quote from his article at length, but, remember that the total saving effected would pay for the producer-plant in about one month. This is a striking instance of the advantages to be secured by the adoption of the best methods of using fuel in our metallurgical works. In comparing the figures from the Park City and Aspen plants, the difference of over 20 per cent. in the fuel used in the Stetefeldt furnaces, seems remarkable, even considering the larger amount of sulphur in the Aspen ore, and the greater rapidity with which it was roasted. It would be interesting to have Mr. Stetefeldt&apos;s, opinion as to the cause of so great a difference. The inferior economy of the revolving dryers at Park City might be overcome by lengthening them, or so arranging a second one above

Jan 1, 1894

By Bernard E. Fernow

About eight years ago a comprehensive study of American timbers was begun in the U. S. Division of Forestry with a twofold object. On the one hand, it was desired to deternliiie the working-qualities of our numerous economically important timbers, and to furnish reliable standards of strength. 011 the other hand, it was intended to get a clearer insight into the properties and behavior of wood in general, with a view of establishing more rational methods in its use, and to furnish data for physical inspectioil which would permit an intelligent application of the standards of strength, and place upon a rational foundation the so-called " factor of safety," which is at present a mere baseless guess. The first object, namely, the establishment of standards for any given species, requires a very large series of tests, since Wood is an exceedingly variable substance, so much so that in the same tree a variation of 50 per cent. in strength may be found; hence the greater need of rational data of inspection. So far, the insufficient appropriations and facilities at our disposal have permitted us to establish really reliable standards for five species of southern conifers only. These have been deduced from nearly 20,000 tests. Besides these, 10,000 other tests have furnished indicatious regarding some two dozen other species. This work is now entirely abandoned, waiting for more prosperous times. The study of wood in general, however, can be carried on with smaller means, and has this year yielded not only very interesting, but highly important results, which will soon be published in detail. It is the purpose of this paper to make to the Institute the

Jan 1, 1899

By Howard Drullard

To OBTAIN the best results from hammer drills, close attention must be paid to two factors in drill maintenance, which are of equal importance; one is lubrication, the other is the shank. With the exception of stoping drills, most modern rock drills require both oil and grease. The oil ports are in the lubricator, on or behind the hammer cylinder; the grease port for the lubrication of the &apos;chuck sleeve and rotating mechanism is on the chuck end. Ordinary machine oil is not, adapted to rock drills; a heavier more gelatinous oil such as castor machine oil or liquid-grease should be used. The lubricators should be filled-once for every 12 or 14 ft. (3.5 to 4m.), of hole drilled. Grease-guns should be used to fill the port in the chuck end once a shift; a medium ( No. 3) grease is well adapted to this purpose. Hard grease must not be put into- the lubricators, as it will not flow through that part. Contrary to the popular belief, oiling a machine once or twice a shift does not provide sufficient lubrication; the drills should be oiled once for every 12 or 14 ft. of, hole drilled. The rotating handle of a stoping drill -is an oil reservoir and is provided with a port for oiling. The rotating handle is packed with wicking, or similar material, which causes the oil to feed slowly from the handle to the other parts of the machine. Stoping drills require oil at. least twice a shift; lighter oils than castor, such as Arctic Ammonia may be used.

Jan 8, 1920

By C. H. Noren

For some years the Du Pont Company has utilized computer calculations to study the various theoretical properties of explosives. These studies have yielded valuable information on the effects of density changes or formulation changes on detonation rate, detonation pressure, explosion pressure, heat of explosion and numerous other properties, and have aided in evaluating the theoretical potential of explosives. In addition, a multitude of laboratory tests have been utilized for the evaluation of explosives. When comparing the computer data and the voluminous test data it became evident that numerous anomalies existed. Tests in rock were required to study explosives under borehole confinement. This fact was further emphasized after numerous field measurements showed that the borehole velocity of commercial explosives did not match the theoretical value but was dependent on conditions of field use. Since we are interested in the practical aspects of blasting, a program was initiated to evaluate explosives as used in commercial blasting. INSTRUMENTATION Most of you are familiar with the extensive work that has been done by the U. S. Bureau of Mines in their studies of strain measurements in rock. Early in our work we adopted procedures similar to those used by the Bureau of Mines. Strain pulses were measured by gages cemented in boreholes. Since we were primarily interested in the effect of explosives in the zone where fracture might occur, this system offered several disadvantages for Du Pont: 1. Cemented gages were expensive and not reusable. 2. When gage holes were used for several shots, there was considerable question as to the condition of the rock after the first shot.

Jan 1, 1968

By Frederick Laist

IT IS obviously impossible to design a copper smelting plant which could be considered, ideal under all conditions. For example, a plant properly designed to smelt the concentrates resulting from the treatment of porphyry ores by flotation would not be the kind of plant that one would design for the treatment of a coarse pyritous copper ore. The smelting of flotation or other fine concentrates is generally accomplished in a reverberatory plant, although occasionally the concentrates are sintered and then smelted in blast furnaces. On the other hand, coarse self-fluxing ores, whether pyritic or semi-pyritic, are generally smelted in a blast-furnace plant. Even this statement is only- approximately true, since the choice will be influenced by many factors; for example, the kind of fuel available (coal, oil or coke), the value of power (electric or steam), the uses to which waste steam may be put (heating, drying, etc.), the cost of refractories (silica and fire brick), the permanence and continuity of the ore supply and the relative first costs of the two types of plant (the reverberatory plant is generally more expensive to construct and to shut down), the contour of the site on which the plant is to be built (rugged, rolling or flat), the intelligence and character of the labor avail-able, and many other factors. From these remarks, it is evident that no copper smelter can be ideal for all conditions of ore and locality, and inasmuch as most of the copper now being pro-duced comes from fine or flotation concentrates and these are generally smelted in reverberatory furnaces, I shall confine my remarks to this type of smelt-ing plant.

Jan 5, 1923

By Will H. Coghill, Fred D. DeVaney

THE coercimeter, as its name implies, is an instrument for measuring the coercive force[+] of magnetic substances. It was developed by Davis and Hartenheim in the Special Studies Section, Metallurgical Division. A detailed description of this apparatus may be found elsewhere.2 The coercive force determinations of magnetic materials are interesting because of the relationship established by Gottschalk,4 who showed a linear relationship between the magnetization coercive force and the specific surface of comminuted particles. The value of this relationship in determining grinding efficiency has been shown by Dean.3 The determination of the surface contained in the subsieve sizes has always been a difficult problem for investigators. They made approximate measurements of the surface of coarse materials by sizing on screens, but for the determination of the surface of the sub- sieve sizes it was necessary to make detailed grain counts or elutriation tests, or to study dissolution rates. The technical literature contains many references to other methods for determining these surfaces, either by some special apparatus or by mathematical calculations based on distribution lines. Many of the methods are long and tedious, and the results of some, at least, are questionable. The turbidimeter gives quick results on ground cement. By using magnetite as the material to be ground, a simple determination of its coercive force by the coercimeter, requiring 10 minutes or less, can be transposed directly and accurately into units of relative surface. This subject has been pursued further by the U. S. Bureau of Mines in cooperation with the Missouri School of Mines and Metallurgy, Rolla, Mo., and the following is a description of the results.

Jan 1, 1938

By Fred DeVaney

THE coercimeter, as its name implies, is an instrument for measuring the coercive force? of magnetic substances. It was developed by Davis and Hartenheim in the Special Studies Section, Metallurgical Division. A detailed description of this apparatus may be found elsewhere.2 The coercive force determinations of magnetic materials are inter-esting because of the relationship established by Gottschalk,4 who showed a linear relationship between the magnetization coercive force and the specific surface of comminuted particles. The value of this relationship in determining grinding efficiency has been shown by Dean.3 The determination of the surface contained in the subsieve sizes has always been a difficult problem for investigators. They made approximate measurements of the surface of coarse materials by sizing on screens, but for the determination of the surface of the sub-sieve sizes it was necessary to make detailed grain counts or, elutriation tests, or to study dissolution rates. The technical literature contains many references to other methods for determining these surfaces, either by some special apparatus or by mathematical calculations based on distribution lines. Many of the methods are long and tedious, and the results of some, at least, are questionable. The turbidimeter gives quick results on ground cement. By using magnetite as the material to be ground, a simple determina-tion of its coercive force by the coercimeter, requiring 10 minutes or less, can be transposed directly and accurately into units of relative surface. This subject has been pursued further by the U. S. Bureau of Mines in cooperation with the Missouri School of Mines and Metallurgy, Rolla, Mo., and the following is a description of the results.

Jan 1, 1938

By C. D. Hall, F. E. Dollarhide

Fluid Ioss agent.s for crude oil and for water have been studied in dynamic tests. A treatment using a spearhead with a fluid loss agent followed by plain fluid appears feas ible in crude oil, but not in water. An equation for spearhead depletion shows that spurt loss relative to fracture width must be low, if the portion of spearhead fluid in the treatment is to be small. The presence of colloidal matter in crude oils aids the fluid Ioss agent. Unlike in kerosene, where flow limited the agent deposition, in crude oils the filter cake continually formed and leak-off declined. The volume-time relation varied somewhat for different crudes, but was best described by a square root of time function. Spurt loss was inversely proportional to agent concentration. After the fluid loss agent initiated the filter cake, the crude oil colloids built on it effectively. A 2-minute or a 5-minute spearhead with double the normal agent concentration gave the same fluid Ioss curve as the same concentration did for a 30-minute test. The agents tested in water gave fluid Ioss plots on which, for the first few minutes, volume was proportional to the square root of time, but later became proportional to time. For fracture area calculation the customary square root of time function is a satisfactory approximation. Leak-off rates and spurt losses were higher in water systems than in oils. The spurt Ioss tended to be inversely proportional to concentration. In spearhead tests, the filter cakes were not eroded by water flow. However, the rather high spurt loss values make spearhead treatments impractical for water-based fluids. Introduction The effects of dynamic testing conditions on the performance of fluid loss agents in kerosene have been studied previously.&apos; We have extended the work to include crude-oil- and water-based fracturing fluids. An understanding has been gained of the mechanisms of formation and functioning of the filter cakes of fluid loss agents. The practical aspects of evaluating performance of agents in relation to fracture area calculations also are considered. The feasibility of using the fluid loss agent in a spearhead stage of the treatment is examined further for both types of fluids. Experimental Procedure The dynamic fluid loss tests were performed in an apparatus similar to the high-pressure apparatus described in a previous publication.&apos; A fracturing fluid was circulated over a rock surface located in a closed pressurized loop. The fluid flowed axially over the cylindrical surface of a core 2 in. in diameter X 3.5 in. long, mounted (with the flat ends sealed off) in a pipe, with 0.117 in. annular clearance. The filtrate was collected in a central hole in the core and led through valves to graduated cylinders. Provision was made for changing quickly the circulating fluid during the test (spearhead runs) without interrupting the filtration pressure. The only modifications were to add heating tapes and water jackets for the tests with crude oils, all conducted at ISOF, and to change all parts exposed to the test fluid to stainless steel for the tests with water-based fluids. The latter tests were made at room temperature, 80F. Three crude oils were tested. A mixed crude, obtained from a local refinery, contained a considerable amount of light ends. For safety reasons, it was stripped to 250F vapor temperature before use in the fluid loss tests. The other two oils were used as obtained from lease tanks. One was a greenish-brown, 37" API paraffinic crude, and the other was a black, 32" API asphaltic crude. The fluid loss agent for oil, here designated for brevity as Agent A, was Adomite@ Mark II*, a granular solid commercial agent, the same as previously tested in kerosene.&apos; Three different compositions of fluid loss agents were tested in Tulsa tap water. Agent B was adomit& Aqua*, a solid commercial fluid loss agent, comprising clays and hydrophilic gums principally derived from starch. Agent C was a mixture of three parts of Agent B with two parts of silica flour. Agent D was Dowel1 J137, a mixture of guar gum and silica flour. The test cores were cut from contiguous blocks of Berea or Bandera sandstones. For the oil tests, the cores were oven dried, evacuated, saturated with kerosene, and the kerosene permeability was measured. The cores used with the water-based fluids were pretreated by saturating with 3 percent calcium &loride solution to minimize pemeability damage by the fresh water due to clay migration. The

Jan 1, 1969

By A. E. Powers

YEARS of experience and research have shown that molybdenum, tungsten, and vanadium are among the most useful and effective elements in augmenting the high-temperature strength of heat-treatable, ferritic steels. Grün, for example, in conducting an early survey of the strengthening effects of various elements in annealed, low-carbon steel at 750° and 930°F (400° and 500°C), found molybdenum and vanadium to be the most effective.&apos; Holtmann comprehensively studied the strengthening effects of molybdenum and vanadium in quenched and tempered steels at 930°F as a function of microstructure and carbon content.&apos; He found creep strength to be related to the saturation of the austenite at the austenitizing temperature, such that strength is increased by alloying until the y loop is reached—the terminus of complete austenitization. Beyond this degree of alloying, the inability to heat treat will result in lower strength, at least for low and moderate creep temperatures. Tungsten, owing to higher cost than molybdenum, has been little used in ferritic high-temperature steels. As a result, very few investigations have been made of its high-temperature strengthening ability, and reliable data on its effectiveness are not available. Grün rated tungsten far less effective than molybdenum at 930°F (500°C) on a weight-percentage basis.&apos; However, Tammann has found that tungsten is as effective as molybdenum in raising the recrystallization temperature of iron. For this reason Smith, in a review of the subject, has advocated a re-examination of the influence of tungsten on the high-temperature strength of steel.&apos; In any study of the effects of alloying additions on high-temperature properties, recognition must be made of the many variables involved, some of which can be controlled but have been ignored in innumerable investigations of the past, and some of which are difficult or even impossible to control. One cannot, for example, assign a definite strengthening index to any one alloying element, for this will be dependent upon the microstructure (heat treatment and mechanical treatment), testing con- ditions (temperature, time, and stress), and the complete composition of the steel (accompanying alloying elements, impurities, etc.). One ever-appear ing variable, hardness or tensile strength at room temperature, may be eliminated by heat treating all of the alloys to a single hardness level. An attempt may be made to control the variable of primary quenched structure by oil or water quenching the test specimen. The control of such variables may not be possible in cases of widely varying compositions, but at least such deviations should be recognized. Material and Procedure The alloys, made as 30-lb ingots in an induction furnace, all had the same base composition of about 0.18 pct C, 0.85 pct Mn, and 0.48 pct Si. They were grouped as follows: Mo Group—Containing up to 5.2 pct Mo. W Group-Containing up to 6.0 pct W. V Group—Containing up to 3.3 pct V. Mo-V Group—Containing up to 2.7 pct Mo and up to 1.4 pct V. Mo-W Group—Containing up to 2.5 pct Mo and up to 2.5 pct W. The steels, listed in Table I, were forged to ¾ in. sq bars and the material for the high-temperature, rupture-test specimens was further swaged to %-in. round bars.

Jan 1, 1957

EXCEPT for the material, the same method that you used in alloying gold is used in alloying silver, but its alloy is fine copper. Just as the silver does in gold, so copper in silver diminishes and lowers its fineness and increases its quantity. If half the value is surpassed it is no longer called silver but copper containing silver, as I told you of gold. But in my opinion one could also say silver of 5,4, or 3 leghe or even of one. How- ever, these terms are of no importance for our purpose. It is enough that you suppose that the whole quantity of silver that you have is twelve parts. If you put one part of copper in h with the melt, you will say [74] that you have 11-lega silver and that it is in weight thirteen of the first parts† and so on, when you add two to ten and four to eight, always naming the quantity of the fine silver just as you did with the gold, either

Jan 1, 1942

By J. W. Halley

COPPER has frequently been recommended as an alloying element for steel and the precipitation-hardening of steels containing from 1 to 2 per cent copper has been studied by a number of investigators. The straight copper steels, however, have not been used extensively and little advantage has been taken of the precipitation-hardening of complex steels containing appreciable amounts of copper. It is diffi-cult to produce a satisfactory surface on the straight copper steels and undoubtedly this has discouraged their use. During recent years a number of steels containing enough copper to make them susceptible to precipitation-hardening have been put on the market. These steels belong to the group usually referred to as "low-alloy high-tensile" steels. They were designed for use in the "hot-rolled" condition; transportation equipment and large structures that cannot be readily heat-treated have been their chief application. Little emphasis has been placed on the possibility of strengthening those containing substantial amounts of copper by precipitation-hardening. The present investigation was undertaken to determine the precipitation-hardening characteristic of one of the "low-alloy steels."

Jan 1, 1940

Spencer Gulf takes off from the Great Australian Bight cutting a 200 mile deep wedge of water into the South Australia coastline. A pale winter sun shines yellowly on the choppy surface of this body of water which is progressively more salty as it approaches Port Augusta at the head of the Gulf. Once Port Augusta thrived as a grain port and the speedy clipper ships began or ended their legendary races there. On the eastern shores of Spencer Gulf, farm land spreads away from the water&apos;s edge. The western side of the gulf meets marginal grazing land of acacia tree and salt bush. Part way down the gulf, there are two industrial towns facing each other from opposite shores; Port Pirie on the east and Whyalla on the west. These towns are like half brothers, the common parent being the founders of Broken Hill Pty. Ltd., (BHP) who began lead smelting at Port Pirie and discovered iron ore near Whyalla needed for the lead smelting process. The iron deposits later became the inspiration for BHP&apos;s iron and steel business.

Jan 10, 1964

By Zay Jeffries

THE object of the present paper is to enlarge somewhat on the general principles advanced in my discussion 1 of Mathewson and Phillips&apos; article on. The Recrystallization of Cold-Worked Alpha Brass on Annealing.2 It will also serve as an acknowledgment of Prof. Howe&apos;s3 most important remarks on my contribution. In this paper the writer has adopted Prof. Howe&apos;s suggestion to substitute the term "germinative temperature" for "critical temperature for grain growth." Instead of being an exact or certain temperature it should be considered that the germinative temperature phenomenon exists throughout a small temperature range. Factors Influencing Fast Growth Phenomena The development of grains of macroscopic size at the germinative temperature should be considered the extreme condition of a general rule. When considered in this light it is not strange that the development of these large grains should be the exception and not the rule. The principal factors influencing the operation of the laws of fast growth temperature are as follows: 1. Rate of heating.

Jan 10, 1916

By S. K. Ghosh

This paper discusses how the information on ash composition, ash-fusion temperatures, and ash-slag viscosity can be used to predict slagging and fouling potentials of a particular coal. A review of several empirical parameters that are commonly used for determining such potentials is given. Also, some guideline values for interpreting the relative propensity of slagging and fouling of various types of coal are provided.

Jan 1, 1986

By J. J. Pye, J. B. Drew

Mzasurements of the surface diffusion coefficients of metals have been made. Diffusion profiles for the Ag-Ag system were obtained by means of a radioactive point source and a precision auto-radiographic technique. The activation energy for silver self diffusion (=8.1 kcal per mole) is lower than that previously reported (-10 kcal per mole) on poly crystalline wire by Nickerson and Parker. The bresent data indicate an effect due to parasitic volume diffusion at temperatures above 500°C. RELATIVELY few measurements have been made of the surface self-diffusion coefficients of metals. Nickerson and arker&apos; measured the diffusion of silver over the surface of poly crystalline wires and estimated that the activation energy was 10.3 kcal per mole. Winegard and chalmers2 carried out measurements on both polycrystalline and single crystal surfaces but did not report a value of the activation energy. They found, however, that at temperatures between 250" and 400°C the diffusion coefficients were on the order of lo-&apos; sq cm per sec and that there was an acceleration of the migration of silver on the polycrystalline sample when a change of surface shape occurred. Winegard and Chalmers used an autoradiographic technique, hereafter designated ARG, and Nickerson and Parker used a surface scanning geiger counter in order to determine the diffusion profiles. More recently, Hackerman and simpson3 measured the surface self-diffusion coefficient of copper at a single temperature (750°C), and the value of the diffusivity (- 10-5 sq cm per sec) is in agreement with that given by jostein from his thermal grooving measurements. This paper reports the results of an investigation of the surface self-diffusion coefficients of silver over a large temperature range and describes the adaptation of autoradiographic (ARG) techniques for the determination of diffusion profiles obtained from a radioactive point source. EXPERIMENTAL PROCEDURE The experimental procedure is a modification of the method employed by Hackerman and simpson3 in their measurements on copper. A brief description of their technique is as follows: A radioactive needle which sinters to the surface during the diffusion an- neal serves as the source of diffusing atoms. After the diffusion run the needle is removed and the surface is scanned with a shielded counting arrangement. The diffusion profiles reported in this paper were obtained by a modification of the above procedure which employs a precision ARG technique. Previous investigations in this laboratory and elsewhere51B have shown that under carefully controlled developing conditions and by the use of calibration sources a linear relation exists between the concentration of the isotope and the photographic density for values below unity. The use of ARG under these conditions has advantages over the counter scanning method in that cumbersome shielding and requirements for great mechanical precision of the scanner are eliminated. Also the ARG gives a complete picture of the surface which is advantageous in studies of anisotropic diffusion. A recording microdensitometer having a 0.1 p wide slit was employed. At low temperatures the disturbing effects of subsurface radiations are negligible. The diffusion anneals are carried out in the cell shown in Fig. 1. The needle is formed by grinding down a 1.0 mm rod of high-purity silver until a tip of 0.2 mm radius or smaller is formed. This tip is plated withA"&apos; which becomes the source of the diffusing atoms that are detected by ARG. The needle carrier and the crystal holder, Fig. 1 are constructed of quartz and ports are provided in the holder pedestal which allow free vapor circulation ((2.0 oz) and the carrier apron fits snugly over the crystal holder cap, insuring that the needle does not move and scratch the surface. Temperatures are provided by a stabilized tubular furnace which can be quickly positioned around the cell, thus bringing the crystal up to temperature in a time that is short compared to the diffusing times. The diffusion anneals range from 2 hr for the high-temperature samples to about 25 hr for those at the lowest temperature. The possibility of vapor transport of the radioactive metal as a contributing factor in the diffusion profile was investigated in two ways. One method was to suspend the needle directly over a dummy sample, raise the temperature, for periods of time equal to the diffusion times, and then take an auto-radiograph of the surface. Negligible radioactivity appeared. In the second method a thin slot in the crystal face on one side of the source provided a "cong path" for surface diffusion. If evaporation was the primary source of surface atoms the region of radioactivity around the source would be symmetrical. This was not the case. The profile dipped abruptly at the edge of the slot but on the other side of the source the usual diffusion profile appeared.

Jan 1, 1963

By Dan McLachlan

EXPERIMENTS on ionic solids,1 Cu-A1 alloys,2 and Fe-Si alloys3 have suggested that the ability of dislocations to cross-slip is one of the most important factors governing the nucleation and growth of fatigue cracks. These experiments necessarily had to be made on materials of different composition in order to vary the propensity for cross slip. However, re-

Jan 1, 1967

By P. N. Richards, M. K. Ormay

Commercially hot-rolled low-carbon steel strip may have one of two basic types of orientation texture, depending upon the amount of a iron which was present during the finishing passes. The changes in these textures with varying amounts of cold reduction up to 95 pct have been determined for the sheet surface plane and for parallel planes down to the mid-plane. The development of cold reduction textures has been reassessed on the basis of (200), (222). and (110) stereographic pole figures and pole density or inverse pole figure values. In agreement with the literature, it is shown that the textures can be described in terms of partial fiber textures but alternative descriptions are given for one of the fiber textures, in order to more closely correlate with experimental data. One partial fiber texture consists of orientations of the type (hkk)[011] extending from (100)[011] to {322}(011) in agreement with the literature. At moderate amounts of cold reduction, a second partial fiber texture forms with a <331> fiber axis inclined 20 deg to the sheet normal and a range of orientations centered on one close to (1 11)[112] and reaching to (232)[101] or (322)[011]. An alternative description involves a (111) fiber axis parallel to the sheet normal but capable of rotation about the rolling direction with rotation about the fiber axis. ORIENTATIONS developed in low-carbon steel strip after cold reduction are of commercial importance because they control, in part, the final preferred orientations after subsequent annealing. The method of control however is not understood completely. Some preliminary work indicated that the cold-reduced orientations and the subsequent annealing textures of commercial low-carbon steel were dependent on the orientations present in the material before cold reduction, that is, those present in the hot-rolled strip but, to date, the effects of initial orientations have not been extensively investigated. For this reason, much of the information given in the literature on development of preferred orientation is difficult to assess as details of initial texture and processing conditions are often inadequate or are altered by a subsequent heat treatment such as normalizing.&apos; It is known2 that anomalous results for near surface orientations may be obtained if lubrication during cold rolling is not adequate but whether lubricant was used during the experiments has not always been given, nor has the exact depth below the surface at which determinations have been made. A comprehensive review of cold rolling textures has been made recently by Dillamore and Roberts&apos; and more restricted recent reviews are due to stickels4 and Abe.5 Based largely on the experimental work of Bennewitz,1 reviewers have accepted that the preferred orientations produced on cold reducing low-carbon steel can be described in terms of two partial fiber textures as follows: Partial Fiber Texture A which has a (011) direction in the rolling direction and includes orientations within the spread from (211)[011] through (100)[Oll] to (211)[011.]; there is some controversy as to whether it extends as far as the orientation (111)[011]. As Dillamore6 has observed, the extent of this partial fiber texture depends on the intensity levels selected. Partial Fiber -texture B which has a (011) direction located 60 den from the rolling direction in the plane containing the rolling direction and the sheet normal. There are two directions which satisfy these conditions and orientations in this partial fiber texture extend from (21l)[0ll] through (554)[225] to (121)[101]. The orientations {211}(011) are members of both partial fiber textures A and B and it can be noted that a variant of {554)<225> is within 6 deg of a variant of {111}(112). Barrett7 had postulated earlier that, in addition to orientations which would fall into partial fiber texture A, a true fiber texture with a (111) direction in the sheet normal was present after heavy cold reduction. This fiber texture would include orientations such as {111}(011) and {111}(112). Later investigators, notably Bennewitz,&apos; have discounted this, mostly on the ground that the partial fiber textures A and B, as described above, contain all the strong orientations that have been observed. However in other work it has been reported2 that (222) pole density or inverse pole figure values show a continuing increase with increasing reduction by cold rolling and give values considerably greater than for any other low indices plane. Thus it could be inferred that a (111) fiber texture as described by Barrett would be one which becomes more dominant with increasing cold reduction, whereas Bennewitz&apos; concluded that components such as {554)(225) in partial fiber texture B began to decrease in intensity at high reductions. Following Bennewitz, one would expect a decreasing (222) pole density value (parallel to the sheet normal) with increasing cold reduction. Because fiber textures consist of grains with a range of orientations that have one axis in common, it has been inferred that during deformation the crystal orientations rotate about the fiber axis&apos;74 and that the orientations of crystals that at one stage belong to one fiber texture can rotate on further cold reduction into the other fiber texture through an orientation in which the two fiber textures intersect.&apos; For example,

Jan 1, 1970