Search Documents

By N. F. Schulz, H. A. Lex

Representative samples of typical manganiferous iron ores from the Cuyuna Range, Minn., were reduced to the metallic iron state at temperatures just short of fusion with an excess of coke in the manner prescribed by the R-N Direct Reduction Process. The magnetic separation characteristics of the reduced ores were determined at several grinds by means of the Davis magnetic tube concentrator. The efficiency of metallic iron concentration by magnetic separation was a direct function of the degree of metallization of the ore sample and of the degree of liberation at-tained in grinding. Some improvement of liberation characteristics was observed if a small amount of sodium chloride was present in the ore during reduction. Despite the extremely fine-grained structure of the crude ores, iron concentrates containing more than 90% Fe at iron unit recoveries of 90% or more were obtained from well-metallized samples of three of the four ores tested. The rejection of manganese to the tailings corresponding to such separations varied from 80% to 95%. The manganiferous iron ores of the Cuyuna Range in Minnesota constitute a major potential source of manganese in the United States provided that a technically and economically feasible process can be devised for its recovery. The iron and manganese of these ores occur chiefly as oxides or carbonates in the form of very small, irregular, discrete grains embedded in a matrix of quartz or other siliceous gangue. The present investigation was undertaken as a sequel to an earlier one conducted jointly by the U.S. Bureau of Mines and the R-N Corp. Those results indicated that the R-N Direct Reduction Process might be a means for recovering both a metallic iron concentrate and a marketable manganese by-product from Cuyuna manganiferous iron ores.' The R-N Process is one of many proposed schemes for the treatment of crude iron ores involving the di- rect reduction of the iron content to metallic iron followed by physical extraction of the iron. In general, it consists of the following stepsz2 1) Iron oxide in crushed natural ores or iron concentrates is about 95% reduced to metallic iron at elevated temperatures but without fusion in a rotary kiln in the presence of a solid carbonaceous fuel (usually coke), limestone, and combustible gases. 2) The kiln product, consisting of metallized ore, excess coke, lime, and coke ash is cooled. The excess coke is recovered and recycled to the kiln feed. 3) The metallized ore is ground for liberation and magnetically separated to yield a metallic iron concentrate. 4) The metallic iron concentrate is agglomerated by a briquetting process. The reduction kiln temperatures must be high enough for the desirable chemical reactions to proceed at practical rates without causing fusion of any of the ore constituents. The time of exposure of the ore to the reducing conditions must be ample for 90% to 95% metallization of the iron oxides present. If more than 95% of the iron is metallized, however, difficulties may arise in the briquetting step, presumably because of accompanying higher carbon content of the metallic iron. Although not always necessary, powdered limestone or dolomite may be added at some time during reduction to aid in eliminating sulfur and phosphorus from the final product.3,4 Other additives, notably sodium chloride, when present during reduction, result in improved liberation characteristics of the metallic iron from certain reduced ores.'v6 Under the reducing conditions normally employed, P(co + H2)= 1 atmosphere, and 1830' to 2150°F (1000° to 1170°C), the R-N Process is claimed to be adaptable to a wide variety of low, medium, and high grade iron and manganiferous iron ores. The manganese oxides and carbonates are reduced mostly to nonmagnetic MnO which is rejected to the nonmagnetic tailings. Manganese-bearing pyroxenes of the original ore, however, may be rejected poorly, if at all, apparently because these minerals occur within the iron lattice or are entrapped in the metal particles.7 The investigation was limited to studies of the Cuyuna ores listed in Table I, which were reduced to the metallic iron state under various conditions

Jan 1, 1969

By W. G. Pfann

The simultaneous segregation of two solutes during the directional solidification of an ingot is treated mathematically on the basis of simplifying assumptions. Expressions are derived for the difference in concentration of two solutes, and for the location and concentration gradient of a pn barrier formed in a semiconductor by the segregation of a donor and an acceptor. THE problem of normal segregation of a single solute during the freezing of an alloy has been treated mathematically by a number of investigators. Gulliver' showed that coring increases the quantity of eutectic above that to be expected at equilibrium, for a system having limited solid solubility and, on the basis of simplifying assumptions, calculated the fraction of eutectic to be expected. Scheuer2 expressed composition of solid solution in terms of a distribution coefficient and the fraction solidified and compared experiment with calculation for the systems A1-Cu, Al-Zn, Cu-Sn, Cu-Zn. Hayes and Chipman,3 in a detailed study of segregation in a low carbon, rimming steel ingot, calculated distribution coefficients for a number of solutes in iron, compared calculated and experimental segregation curves, and discussed the effects of process variables such as rate of solidification and stirring. In the present paper a mathematical analysis is made of the simultaneous segregation of two solutes during the orderly freezing of a solid solution system, with particular emphasis on the difference in solute concentrations. Although the analysis is quite general and can be applied to the segregation of minor elements in alloys, it is directed in particular at the solidification of a semiconductor containing a donor and an acceptor. Normal segregation has unique aspects in a semiconductor, because of the ways in which donors and acceptors affect the electrical properties. The difference between two solute concentrations becomes of importance, as does also the gradient of the difference where the difference goes through zero, this being the concentration gradient of excess carriers at a pn barrier. A primary object of this paper is to extend the mathematical treatment of segregation to include these newer aspects which are of particular significance for semiconductors. One property of interest is the electrical conduc- tivity, which arises from the presence of donors 'or acceptors in solid solution. The conductivity may be either n-type or p-type depending on whether donors or acceptors, respectively, are in atomic excess. For both germanium and silicon, elements of Group V of the Periodic System, such as P, As, and Sb, are donors and elements of Group 111, as B, Al, In, and Ga, are acceptors.4-6 If a donor or acceptor is present alone in solid solution, the conductivity is proportional to its concentration." If both a donor and an acceptor are present, then the conductivity is proportional to the difference in their atomic concentrations. If the donor and acceptor segregate at different rates then a pn barrier in certain circumstances may form at some point in the ingot. Accordingly, equations are derived and illustrated which express the effect of segregation on: 1—the concentration of a single solute with a discussion of the assumptions; 2—the difference between two solute concentrations and means for minimizing its variation in an ingot; and 3—the location and concentration gradient of a pn barrier. The analysis is applicable to processes in which the entire charge is melted and then progressively frozen from one end. The method in which an ingot is solidified in a crucible7 and that in which a solidifying rod is pulled from the melt8 both fall into this category. Segregation of One Solute If a cylinder of molten alloy is caused to freeze slowly from one end, a normal segregation of solutes will usually occur, producing a lengthwise concentration gradient in the ingot. Depending on whether a solute raises or lowers the melting point of the solvent, it will become concentrated in the first or last regions, respectively, to freeze. If it is assumed that freezing is such that there is no diffusion of solute in the solid, complete diffusion in the liquid, and that k, the distribution coefficient, defined as the ratio of solute concentration in the just-freezing solid to that in the liquid, is constant, then the

Jan 1, 1953

By L. B. Harris

Continuous cyclic unloading during tensile work hardening of polycrystalline zinc at room temperature enables specimens to sustain greatly increased extension. Such enhanced ductility is associated with creep-type extension, during which the cyclic component appears to promote relaxation of internal strains. It is possible to trace the transitions from tension, through enhanced cyclic extension, to fatigue and relate the observed behavior to simpler types of deformation. DISTINCTIVE deformation behavior has been shown to occur when loading includes both cyclic and unidirectional components. For aluminum and copper extended by a sequence of progressively biased strain reversals, coffin1 observed greater fracture ductility and lower flow stresses than during monotonic tension. This may be compared with the reduction in hardness obtained from conventional fatigue softening. But fatigue softening is accompanied by enhanced fatigue life,' whereas Benham3 found that fatigue life was reduced when copper continuously extended during axial load cycling. The corresponding specimen elongation, for large cyclic load amplitudes, was greater than during normal tension. Under different conditions, Bendler and wood4 found that torsional fatigue initiated extension in copper under low tensile loads previously in equilibrium with the specimen; fatigue life was again reduced. Thus there is a type of cyclic softening which is associated with reduced fatigue life and which occurs when the cyclic loading is accompanied by a unidirectional strain component. Further, the fracture ductility or extension obtained from the unidirectional component can exceed that obtained in the absence of cyclic load. Specimen extension was not initiated by axial fatigue at small load amplitudes;3 hence Benham's work distinguishes between fatigue at large and small amplitudes, the former often being linked with unidirectional deformation because of similarities in strain Structure. The initiation of tensile extension during torsional fatigue,4 however, occurred with small amplitudes. Comparable changes in behavior have been ob- served during creep. kennedy' found that combined cyclic and creep stresses on lead at 32°C increased the rate of elongation over that for simple creep, the consequence being a reduction in creep life. It was also demonstrated that small cyclic stresses applied after creep deformation initially increased recovery, but that prolonged application produced only normal fatigue hardening. It is clear that physical properties can be changed by interaction between the cyclic and unidirectional deformations, but owing to the number of different ways in which the deformations can be combined and the large number of possible variables for each combination, trends of behavior become easily obscured. One definite conclusion is that enhanced ductility or increased extension can be obtained by cyclic action, and it is this process that has been investigated for the tensile test by measurements of the extra tensile strain produced by the addition of a cyclic tensile component. EXPERIMENTAL PROCEDURE Material. Specimens were 99.99 pct Zn wire of 1.6 and 2.0 mm diam. Mean grain diameter was 0.02 mm, sufficiently small to give a ductile necked-down fracture under all loading conditions. All experiments were conducted at an average temperature of 20°C. Normal Tension. Unidirectional tensile curves at different strain rates were obtained from an In-stron testing machine, on which load-time curves were recorded autographically, using gage lengths of 5 and 10 cm. Straining was at constant cross-head velocity, and quoted strain rates are with reference to initial specimen length. Measurements of total elongation under simple tension were also made on the tensile machine that had been modified to incorporate an added fluctuating load. Combined Tension and Rapid Cyclic Load. An electromagnetic vibrator was coupled to the elastic beam of a Hounsfield ensometer- and driven sinus-oidally from a power amplifier at frequencies from 20 to 360 cps, the flexible connecting links on the tensometer being replaced by rigid fixtures to eliminate lateral vibration in the specimen. One end of the specimen was pulled by the normal extension drive of the tensometer while the other end, fixed to the elastic beam and vibrator, was subjected to rapid oscillations of load. It was thus possible to apply cyclic load to a tensile test without altering the rate of extension of the specimen

Jan 1, 1964

By B. C. Allen

Surface free energy and surface self-diffusion of solid molybdenum were studied in the temperature range 1600" to 2400°C using pressure-sintered bi-crystals. Comparison of groove angles formed in various surfaces perpendicular to the grain boundary indicate a maximum of 1 pct variation in surface free energy with crystallographic mientation. This anisotropy tends to decrease with increasing temperature. The surface diffusion of the bicrystals is equivalent to that of sheet with a mild (100) Preferred orientation. Anomalously low values found for bi-crystals with surface orientations of (OOl), (012), and (011) are rationalized in terms of anisotropy in surface free energy. THE effect of crystallographic orientation on surface free energy1,' and surface self-diffusion3,4 has been primarily studied in fcc metals. The object of this work was to study the effect of orientation on surface diffusion and surface free energy of bcc molybdenum using pressure-sintered bicrystals. EXPERIMENTAL WORK Materials and Crystal Preparation. Arc-melted molybdenum rod was obtained commercially and electron beam zone refined at 50 cm per hr at 10- 5 torr to form single crystals about 8 cm long and 0.65 cm diam. Three crystals were prepared with axial orientations about 1 deg from [001.], [011], and. [111]. To reduce the carbon content, the crystals were annealed 2 hr in 1.4 atm flowing wet hydrogen at 2050°C. Then the oxygen content was reduced by annealing for 2 hr in -30°C dewpoint hydrogen at 2020°C. The resulting impurity analysis is given in Table I. Bicrystal Preparation. The single crystal rods were cut into transverse slices with a thin silicon carbide abrasive wheel to produce specimens about 0.6 cm long. They were mounted in epoxy and surrounded by stainless steel washers. Cutting in half was done longitudinally at various angles to known crystallographic planes containing the cylinder axis according to Fig. 1. To reduce surface deformation resulting from the cutoff wheel and thus reduce parasitic grain boundary formation on subsequent annealing, about 0.003 cm was manually ground off each cut surface with 600 grit paper. Care was taken to keep the surface flat. After removal from the mounts, one half was generally ro-tated 180 deg with respect to the other to give a po- tential symmetrical tilt grain boundary between the two halves. In the other cases when low misorienta-tion angles were desired, the crystals were not rotated. On the basis of symmetry, sufficient bicrystals were prepared to cover the entire range of misorientations for symmetrical tilt boundaries. The misorientations, +, ranged from 0 to 45, 0 to 90, and 0 to 60 deg for [001], [011], and [111] bicrystals, respectively. One [Ill] twist bicrystal was prepared from 2 single crystal discs rotated 17 deg relative to each other. Each specimen consisted of two pieces which were placed in a cylindrical tantalum can. Sharp edges were rounded and the fit was made as snug as possible to reduce subsequent deformation during bonding. The assembly and crystals generally were vicuum outgassed at 900" or 1700°C and then electron beam welded in the can at l x 10-4 torr. After being leak checked, the samples were placed in an autoclave and hydrostatically gas-pressure bonded5 in four batches under helium at 10,000 to 18,000 psi at 1650°C for 3 hr. Satisfactory bonds were obtained in many cases, and most of the crystals bonded after two exposures. The results did not appear to be affected by the various pressures used, preannealing conditions, crystal orientation, or time-pressure-temperature route taken to the final bonding condition. After bonding, the tantalum cans were selectively removed in cold concentrated HF. Measurements indicated overall deformation was under 1 pct. The bicrystals were metallographically ground and polished flat and perpendicular to the axis. Examination showed the boundaries were straight and almost free of parasitic grains caused by extraneous local deformation. Annealing. In preparation for thermal grooving, the bicrystals were cleaned and annealed by outgassing at 10-5 torr at 1900°C and heating at 2300°C under 1 atm 99.996 Ar for 0.5 hr. The crystals were held in a closed 4-deck box made of molybdenum sheet, and were heated in a Ta-1OW resistance furnace. The ar-

Jan 1, 1970

By Klaus Schwerdtfeger

Activities of lead in Pt-Pb and Pd-Pb melts in the temperature range of 800° to 1200°C have been detev-mined from electromotive-. force measurements 202th the cells Both systems display strong negative deviations from Raoult's law. The data obtained with cell [1] were combined with available data on the activity of PbO in silica-satuvaterl PbO-SbO2 melts to calculate the standard free cnergy of formation 01- liquid PbO. FREE energies of formation of oxides and activities of components in metal and oxide melts can be determined with galvanic cells consisting of a metal phase, an electrolyte containing the oxide of one of the components of the metal phase, and an oxygen electrode. This technique has been used previously to measure the standard free energy of formation of solid sio2, 1 and activities in Fe-si, CO-si,2 Ni-Si,2 and CaO-P2O5 3 melts. The present paper reports activities in Pt-Pb and Pd-Pb melts as measured with the same experimental technique. EXPERIMENTAL METHOD General Considerations. The following cells were used: Pbl (PbO-SiO2)liquid, SiO2 Pt-Pb 1 (PbO-SiOz)liquid, SiO2solidO2 [2] Pd-Pb (PbO-SiOz)liquid, SiO2solid O2 [3] Liquid alloy and' oxide melt were contained together in a silica glass crucible of essentially the same design as described previously.1'2 The PbO-SiO2 melts are ionic conductors.' During the experiment, the silica glass crystalizes in a layer adjacent to the electrolyte. The electrolyte equilibrates with solid silica and hence attains the composition of the Si02-liquidus curve in the system PbO-SiO2 at any particular temperature. Molybdenum wires were used to establish contact with the liquid metal. The oxygen electrode, which reaches the surface of the PbO-SiO, electrolyte from above, consists of a platinum wire inserted into a ceramic tube and provided with a 2-mm-diam platinum bead at its end. Gas of known oxygen partial pressure (pure oxygen of 1 atm: air, or N2 with 1.04 pct 0,) is blown through the ceramic tube onto the surface of the electrolyte. The cell reaction is Pb (metal) + 1/2O2 (gas) = PbO (electrolyte) [4] No oxidation of platinum or palladium ("displacement reaction") occurs. This is to be expected from the noble character of platinum and palladium, but was also shown experimentally, as described in the next section. The galvanic electromotive force of the cell is given by where AG is the change in free energy for Reaction [4], E(=2) is the number of electrical equivalents necessary to form 1 mole of PbO, and F is the Faraday constant. Formula [5] is valid only if no junction potential exists within the electrolyte. Junction potentials occur only when the compositions of the electrolyte are markedly different at the electrodes. Such differences are negligible in the PbO-SiO, electrolyte, as shown in the next section. Since molybdenum contact leads are used, appropriate corrections were made on the measured electromotive forces to account for the thermoelectric effect of the Mo-Pt couple. The thermoelec-tromotive forces were measured separately with a Mo-Pt couple, and were found to vary linearly from 19 mv at 740°C to 40 mv at 1310°C with molybdenum being positive and platinum negative (cold junction at 25°C). Extrapolation of these values to higher temperatures yields values which are in satisfactory agreement with those obtained previously in the temperature range 1440° to 1630°c.1,2 The change in free energy for Reaction [4] is expressed as where chemical potentials of the species. The value of constant for a given temperature because the slag composition is fixed. Inserting [6] into [5] and using appropriate expressions for upb and uO2 the relation

Jan 1, 1967

By B. C. Raynes

IN the early part of 1952, under the auspices of the U. S. Atomic Energy Commission, Horizons Inc. undertook an investigation dealing with the preparation of high purity thorium metal in order to develop an economically competitive production process for this metal based on a recovery of the metal by a fused salt electrolysis, since a survey of the literature of thorium chemistry indicated that electrolytic methods had not received much attention, despite the consideration that electrochemical production methods often offer attractive commercial potentialities. Thorium metal has been prepared by methods which fall into four general categories: 1) reduction of halides or double halides; 2) reduction of the oxide; 3) thermal decomposition of halides; and 4) electrolytic methods. Some of the important results obtained by various investigators since about 1900 in recorded attempts to prepare pure thorium metal are summarized in Table I. A bibliography of pertinent literature is included in this paper. Thorium is strongly electropositive and possesses a great affinity for oxygen and nitrogen. As a result the prospects for the production of high purity thorium from aqueous media or oxygen bearing compounds are remote. The most promising and profitable area of investigation for production of thorium metal lies in fused salt electrolysis. Thorium has been produced previously by this technique from halide salts in fused alkali chloride eutectic mixtures. Until recently, however, the lack of known large uses for thorium has inhibited the investigation of these methods. The basic problem in an investigation into fused salt production methods for thorium is to develop a suitable fused salt system for the economic preparation of thorium. The first portion of the work in these laboratories was a small scale investigation of the electrolysis of potassium thorium fluoride, KThF5, under a variety of conditions. High purity thorium was prepared in this manner, but the process did not appear to offer the simplest and most attractive continuous commercial operation. The work reported here relates to an all-chloride system employing thorium chloride as the cell feed. ThCL4 was produced as an anhydrous material stabilized in molten sodium chloride. This product, further diluted in NaCl, was subjected to electrolysis. The electrolytic process has been studied in cells capable of holding up to 50 lb total salt charge. Ductile, pure thorium metal has been reproducibly obtained in this operation. Considerable experimentation was carried out in the preparation of ThCL as a cell feed free from moisture, oxides, and other impurities. Thorium was cathodically deposited as a coarsely crystalline powder interspersed with residual bath salts. Aqueous procedures for separating and recovering the metal were developed. The thorium metal powder obtained has been evaluated with respect to its hardness, chemical purity, and certain other physical properties. Preparation of ThC1,—Thorium chloride, and the chlorides of some other metals (aluminum, beryllium, tantalum, zirconium, etc.) cannot be obtained from aqueous solution by direct heating and evaporation. Evaporation and heating of a solution of thorium chloride yields a hydrated salt or partially hydrated salt, and finally Tho,. Anhydrous thorium chloride is obtained by forming a hydrated ammonium chloride complex salt in acidified water solution, dehydrating this compound, and finally decomposing the double salt and subliming the ammonium chloride component. Various methods for the preparation of anhydrous thorium chloride, in accordance with this concept, were investigated as indicated in Table I1 from hydrated thorium chloride (ThCl, . 3H2O), and from thorium oxycarbonate (ThOCO,). In the method found most satisfactory for this work, thorium oxycarbonate was dissolved in an excess of concentrated HC1 to give a clear yellow solution. At least 2 mol NH,Cl were added to the solution per mol of contained thorium. Ammonium thorium chloride hydrate was crystallized from solution by cooling and saturation with HC1. The resultant complex, (NH,Cl),ThCl;xH,O, was dehydrated by evaporation at 130° to 150°C and thoroughly dried at about 250°C. The dried ammanium thorium chloride was then mixed with sodium chloride in proportions to form NaThCL or to produce a ThCL4-NaCl mixture with a given thorium content. The ammonium chloride was sublimed off at temperatures above 500°C in an inert atmosphere furnace to give an anhydrous chloride source electrolyte, essentially free of Tho, and of NKC1.

Jan 1, 1958

By J. J. Gilman, T. A. Read

S URFACE effects in the cleavage of brittle crystals have been known for some oftime,1, 2 but our knowledge of surface effects in the plastic deformation of crystals is of relatively recent origin. In 1936, Roscoe9 eported his observations comparing oxidized and clean cadmium crystals. He found that cadmium crystals 1/2 mm in diam when covered by an oxide film less than 1200 atoms thick had critical shear stresses about twice those for clean crystals. This effect is anomalous in that it cannot be caused by the inherent shear strength of a normal oxide film. Either an interaction between the film and the crystal causes the large increase in strength, or the oxide film has an abnormal mechanical strength. Several authors since Roscoe have studied surface effects in crystal plasticity. A complete review of the literature will not be presented, but most of the results may be summarized as follows: 1—The critical shear stress for slip is increased markedly by very thin oxide films on zinc4 and cadmium crystals;" ' also, the entire stress-strain curve is raised by an oxide coating;3,4 both effects increase with decreasing specimen radius. 2—Surface active substances such as oleic acid destroy the hardening effect of oxide films.4, 6-8 The time required for the reduction of the hardening effect to begin increases with the viscosity of the solvent4~ 3—There has been dispute in recent years about the effects of surface active substances themselves on plastic deformation. Rehbinder, Lichtmann, and Maslenikov9 state that surface active substances reduce the strength of metal monocrystals markedly and increase the number of slip lines per unit length at a given strain. The effect varies with orientation for tin crystals being smallest for x, = 0, largest for x, = 45", and intermediate as x, + 90°.10 Several workers claim to have disproved the results of Rehbinder')"." but Rehbinder and Lichtmann9 have defended themselves and Masing with his collaborators" has confirmed some of Rehbinder's results. 4—Immersion of metal specimens in electrolytes such as sodium chloride reduces their strength12,13' and subsequent cathodic polarization increases the strength reduction. For noble metals, the strength reduction occurs for both anodic and cathodic polarization," increasing with increasing polarizing voltage. 5—Electroplated copper coatings effect the creep rates of zinc monocrystals. Poly crystals are not affected." 6—Immersion in dilute acid destroys the hardening effect of an hydroxide film. When an acid solution is applied to a steadily creeping crystal, the creep rate jumps to a very high value and then drops gradually to a steady value which is higher than the initial steady rate.*' " If the hydroxide film to be removed is very thin (about 100A thick), the creep rate does not change measurably, but a small rapid strain-increment is observed when dilute acid is applied." 7—Crystal plasticity depends on specimen dimensions. This was observed by Lichtmann and Ven-stroml" for monocrystalline tin and by Andrade and Kennedy" for polycrystalline lead. 8—Immerson of copper crystals in mercury has no effect on their stress-strain curves.'" 9—Bombardment of creeping cadmium crystals with a particles which penetrate the surface to only 0.005 mm may increase their creep rates as much as five times.''' The experiments which will be described in this paper pertain to: (a) the effect of a crystal's shape on its plastic deformation, and (b) the effect of metallic surface films on plastic deformation. For the work pertaining to (a), crystals of zinc, tin, and lead were grown which had various shapes. These were tested in simple tension. Macroscopic rotations about the tension axis which are unpredicted by the classical theory of slip were observed, and serrated edges were observed in tin crystals. For the work pertaining to (b), the effects of evaporated and electrodeposited films of copper, nickel, gold, and zinc on the mechanical properties of zinc, tin, and lead crystals were determined. The films influenced both slip and twinning of the crystals in creep and tensile tests. Experimental Details Chemically pure zinc, tin, and lead were used in this investigation. The zinc was 99.999t pct pure;

Jan 1, 1953

By D. A. Elgillani, S. Atak, D. A. Rice, M. C. Fuerstenau, R. B. Bhappu

Quartz and feldspar cannot be floated with sulfonate at any pH; spodumene floats over a narrow acid pH range, while beryl responds moderately over a broad pH range. After wet-grinding in a steel mill, beryl, quartz, and spodumene float well with sulfonate below about pH 7, whereas the improvement in the response of feldspar is not so marked. A mechanism by which iron can be adsorbed on these minerals is presented. Also, the responses of leached, natural, and wet-ground beryl to amine, sulfonate, and oleate flotation are shown and related to the measured zero-points-of-charge of these materials. Earlier work with leached beryl showed that good flotation could be obtained with alkyl aryl sulfonate over a rather wide pH range using a Fagergren flotation cell.' When a similar response was observed with leached quartz, it was decided that unintentional activation was being obtained from the metallic components of the Fagergren cell. To obviate this difficulty, a microflotation cell was designed, and an experimental technique was devised. These have been described elsewhere. Experiments conducted with the small cell showed that leached quartz could not be floated at any pH with any sulfonate addition,3 which is in agreement with the observations of Kraeber and Boppel.4 Similarly, it was also found that leached beryl responded to sulfonate flotation only over a narrow pH range rather than the broad range reported earlier.1 This early work,1 however, revealed the important effect that wet-grinding in a steel mill has on the flotation response of certain silicates. That is, it was found that quartz and especially beryl floated well over an unusually wide pH range after wet-grinding in a steel mill. Microcline, however, floated poorly below pH 4, even though wet-ground under the same conditions. The work of Eigeles6 on adsorption of oleic acid on leached quartz and iron-contaminated quartz at constant pH is in agreement with these flotation data. Other research has shown that ferric iron, added as a salt to the system, functions as an activator in the narrow pH range in which Fe +++ iron hydrolyzes to its hydroxy complexes.3,5 These phenomena indicate that iron functions differently in flotation systems depending on its method of introduction. The object of this paper is to determine the mechanism by which iron is adsorbed on certain minerals, the mechanism of collector adsorption after iron abstraction, and the role that Fe++ and Fe+++ assume in the selective separation of these minerals. EXPERIMENTAL MATERIALS AND METHODS Sodium alkyl aryl sulfonate, mol wt 450,7 pure potassium oleate, and pure dodecylamine were used as collectors. All other chemicals were reagent grade in quality, i.e., n-amyl alcohol as frother; HC1, H2SO4, and KOH for pH adjustment; and ferric chloride as activator. Conductivity water, made by passing distilled water through an ion exchange column, was used in the experimental work. All minerals used in the investigation were hand-picked specimens. Sample Preparation: Each of the minerals was crushed through 8 mesh, and the product was divided into two groups, one to be ground dry and the other wet. Dry grinding was accomplished with an alumina mortar and pestle. The product was dry-screened to 48 x 150 mesh, cleaned magnetically, deslimed in conductivity water, and dried. Preparation of the samples by wet-grinding involved grinding a 200-g charge of the mineral (-8 mesh) at 60% solids with natural water in a mild steel rod mill for four minutes. This charge was then wet-screened immediately with natural water to 48 x 150 mesh, dried, and cleaned magnetically. Some experiments were also conducted with leached beryl and quartz. These products were prepared by leaching the sized sample (48 x 150 mesh) with concentrated HC1 with a percolation technique until no iron could be detected in the leach liquor. Following this step, the sample was rinsed with conductivity

Jan 1, 1967

By G. L. Tufford, R. L. Bleifuss

Low-grade manganiferous iron ores of Minnesota's Cuyuna Range, in general, do not respond to conventional mineral dressing techniques because of their fine-grained texture. Reducing these ores to magnetite with subsequent magnetic separation and flotation have not given satisfactory results because, in many instances, concentrate grade and manganese recovery are low. Metallization of iron and concurrent reduction of higher manganese oxides to MnO, as in the R-N process, followed by recovery of iron by magnetic separation and manganese by leaching, seems to be a technically feasible process. High-temperature x-ray diffraction studies show that solid-state reactions between iron and manganese, with the formation of intermediate iron-manganese oxides, occur during reduction and affect recovery of both iron and manganese from the final product. Solid state reactions also occur between FeO, MnO, and SiO, at temperatures as low as 900°C. The kinetics of these reactions are such that they become an important factor in the treatment of ores by the R-N process. These investigations suggest a temperature and gas composition cycle that would maximize both iron and manganese recovery. During the past ten years, iron ore shipments from the Cuyuna Range of Minnesota have decreased sharp1y. Because of adverse grade, structure, and cost, many Cuyuna ores are no longer competitive with high-grade foreign ores and domestic pellets. The low-grade manganiferous iron ores from the Cuyuna Range, in general, do not respond to conventional mineral dressing techniques because of their fine-grained texture. Reducing these ores to magnetite for subsequent magnetic separation and flotation has not given satisfactory results because concentrate grade and manganese recovery are often low. However, a technically feasible process appears to be metallization of the iron and concurrent reduction of manganese oxides to MnO with recovery of metallic iron by magnetic separation and extraction of manganese from the tailings by leaching. In 1962 the R-N Corp., with a grant from the Area Redevelopment Administration, conducted an amenability study of the metallization of manganiferous iron ore from the Cuyuna Range. The results of this preliminary investigation were sufficient to interest the Economic Development Administration in sponsoring further studies of the process with emphasis on secondary recovery of manganese from the nonmagnetic tailings. Inasmuch as the metallization process has considerable influence on the final form of the manganese - its texture and distribution between the magnetic concentrate and nonmagnetic tailings-the investigation included a study of metallization of the ore as well. Therefore, the investigation conducted at the Mines Experiment Station covered three interrelated phases: (1) laboratory R-N roasting studies and magnetic separation tests, (2) laboratory chemical extraction experiments of the nonmagnetic tailings, and (3) a mineralogical study of the crude ores and their various roast products. High-temperature x-ray diffraction investigation of the Fe-Mn-Si0,-0, system is the main topic of this paper and an extension of the mineralogical work. GENERAL GEOLOGY The Cuyuna Range is known for its complicated geologic structure, complex orebodies, and generally indifferent response to attempts at conventional beneficiation. Several geologists have made intensive studies of the Cuyuna Range, including Leithl (1907), ~darns' (1910), Zapffe3 (1925), Grout and Wolff4 (1955), and schmidt5 (1963), whose study was the most comprehensive of all. The Range is covered with glacial deposits - till, out-wash, and lake sediments -up to 250 ft thick. Bedrock stratigraphic units of the Cuyuna Range consist of three tightly folded Precambrian sedimentary formations. The lower unit is the Mahnomen formation, composed of 2000 or more feet of argillite, slate, siltstone, and quartzite. The middle unit is the Trommald formation, which varies from 45 to 500 ft in thickness and comprises the major iron-bearing formation. The upper unit is the Rabbit Lake formation, consisting of over 2000 it of argillite, slate, and interbedded lenses of lean iron formation. In the central part of the Cuyuna Range, the units have been folded into a series of

Jan 1, 1969

By Linda Lee, R. E. Reed-Hill, C. R. Smeal

Four fcc metal surfaces, etched to make them responsive to polarized light, have been studied with an electron microscope. Jones'prediction that these surfaces are grooved has been verified. Optical-goniometer measurements made on commercially pure nickel indicate that the groove walls are poorly defined (100) facets. Surface mientations close to either 4001 or {ill).- show no extinctions on the polam'zid-light microscope. An explanation is offered for this orientation dependence. It has also been deduced that polarized-light extinctions on a grooved cubic-metal surface should not be used directly in crystallographic-orientation determinations. The nature of the etching solutions that produce these surfaces is considered. A cubic-metal surface may be made responsive to polarized light in two basic ways."' In one, an anodic film, believed anisotropic, is formed on the surface. A plane-polarized-light beam, at normal incidence, should be reflected from this type of film with an ellipticity that varies with grain orientation. Under crossed polarizers of a polarized-light microscope, each grain may be distinguished from its neighbors by a difference in reflected-light intensity. An alternate treatment,' more generally applicable to cubic metals and of principal concern here, involves etching of grain surfaces. The characteristic features of this surface were first deduced by Jones3 from light-microscope observations. She concluded that, in general, grain surfaces were furrowed so that light was reflected from two parallel sets of etched facets. A grooved surface produces elliptical polarization of a plane-polarized beam because the beam does not strike groove walls at normal incidence. Jones also observed that the furrows must have faces inclined to each other by approximately 90 deg, since the light returns along the incident path, and that a grooved surface should show four maxima and minima of reflected-light intensity during a 360-deg stage rotation of the polarizing microscope. Positions of maximum extinction were predicted to occur when groove axes were parallel to either polarizer or analyzer vibration directions. Because of the limited resolving power of Jones' optical microscope, her deductions were primarily indirect. Proof of the correctness of her conclu-sions, as demonstrated by the electron microscope, will be given as well as evidence concerning the crystallographic nature of the etch furrows and the types of etching solutions that produce them. EXPERIMENTAL PROCEDURE During a comprehensive study of hot plastic deformation in nickel and nickel alloys, an etch was evolved that produced a surface with an excellent polarized-light response on Nickel 200 ("A" Nickel). The etching solution and associated metal-lographic procedures are given in Table I. In evaluating this etch, a study was made of the topological features of the etched surface and their relation to the underlying crystalline structure. As part of this investigation, large crystals (2 mm average diameter) were grown in a 1-cm-sq Nickel 200 specimen. After the surface was etched, the crystallographic orientations of ten grains were determined by the standard back-reflection Laue technique of Gren-inger.4 Maximum extinction positions during a microscope stage rotation were also measured for the ten grains. Groove-wall positions on the surfaces of the ten grains were measured with a two-circle optical goniometer. The technique was essentially that of Barrett and Levenson.5 Several grain surfaces were photographed with a Philips Model 100A electron microscope. All specimens were replicated with collodion, or collodion backed with formvar and chromium shadowed at 18 to 20 deg. The basic material was Nickel 200. However, an electron-micrographic study was also made of surfaces developed by polarized-light etches on other fcc metals (90-10 a brass, Monel 400, and lead). All etching procedures are given in Tables I and 11. EXPERIMENTAL RESULTS Fig. 1 shows typical electron micrographs of three different fcc metal specimens and an optical micrograph of a fourth. All photographs show a grooved structure corresponding closely to Jones'3 predictions. Also, as noted by Jones, extinctions were always observed when groove axes were either parallel or perpendicular to the microscopes' vertical cross hair. The symmetry of the grooves, with respect to the twin boundaries in Fig. 1, implies that furrows have a crystallographic basis. The coarse-grained Nickel 200 specimen was used to study this basis. Facet Orientation. The poles of the ten Nickel 200

Jan 1, 1964

By D. W. Lillie

Property changes produced by irradiation of Al-0.4 wt pet Li alloys at 270°C to a burnup of 0.155 pct of all atoms are described. Metallographic evidence of the formation of internal pores and the concentration of gases at grain boundaries is shown. Some conclusions are drawn concerning desirable property characteristics for resistance to radiation swelling. RADIATION induced gases are of great practical significance in nuclear engineering since they affect the behavior of fissionable fuels and control rod materials. In fuels the gases xenon and krypton are the major offenders, producing serious em-brittlement at low irradiation temperatures and gross swelling at high irradiation temperatures. In control rod materials containing boron, the production of helium from the B 10 (n, 0) Li7 reaction produces similar reactions. Since the trend in reactor design is for operation at increasingly high temperatures, the phenomenon of high-temperature swelling by these induced gases has been the subject of considerable recent study. The objectives of such work have been to obtain engineering information and quantitative data on the effects in specific fuels and control rods and to obtain further understanding of the mechanism of gas damage so that more intelligent corrective steps can be made. Analogue systems are often useful for the latter objective and in this case alloys containing Li are suitable in view of the reaction Li6 + n - He4 + He 4. Both products are gases and no serious radiation problem is produced to complicate post irradiation handling. Considerable caution is, of course, necessary in any operations in which tritium release is possible. The present program was initiated to provide a detailed study of the effects of He + H3 generated by irradiation in Li-bearing alloys. The results on Mg-Li solid solution alloys have been reported elsewhere.' This paper presents information on irradiation of an A1-0.4 pct Li alloy in which the lithium was present as highly enriched Li6 in order to maximize the radiation burnup. PROCEDURE The original intent in the selection of the alloy content was to have Li in solid solution at all temperatures. It became apparent, however, that the solubility of Li in A1 was substantially lower than that reported in the original reference consulted.' This was substantiated by the work of Nowak3 who reported solubility of less than 0.01 pct Li at 100°C. The alloy used (0.4 pct Li) was therefore two phase at room temperature. The irradiation temperature was estimated to be about 270° C, and at that temperature all or almost all of the Li would be soluble under equilibrium conditions. The precise state of the alloy under irradiation is not known. Aluminum used was 99.996 pct purity (max. impurities Si 0.002 pct, Mg 0.001 pct, Fe 0.0005 pct, and Cu 0.0005 pct). The lithium was obtained from Oak Ridge National Laboratory; 96.1 + 0.1 pct of the lithium was ~i~, but chemical impurities were 0.25 pct Ca, 0.05 pct Fe, 0.02 pct Na, 0.02 pct Cu, 0.01 pct Sr, and 0.01 pct Ba. The two metals were melted in an alumina crucible in a resistance heated furnace in an atmosphere of helium. A l-in. ingot was cast in an iron mold, machined to %-in. round, hot swaged (350°C) to 0.080-in. round, cold swaged to 0.060-in. round, and finally cold drawn to 0.040-in. round. Four-inch wire lengths were then cut and annealed at 250°C for 4 hr in helium. Irradiations were carried out in a VT hole in the Argonne CP-5 reactor. The wires were held in an aluminum jig, sixteen wires per capsule, and were maintained in a helium atmosphere for maximum heat transfer. Eight wires of pure aluminum and eight of Al-Li alloy were placed in each capsule. Argome Laboratory statements were accepted as establishing flux and exposure levels. These were based on previous experience and flux map-

Jan 1, 1961

By J. E. Andersen, J. Halpern, C. S. Samis

In the presence of oxygen, galena is oxidized in an aqueous medium containing sodium hydroxide, in accordance with the following reaction: PbS + 2O2 + 3OH ? HPbO2 + SO4 = + H2O A novel method was devised for following this reaction which takes place in an autoclave under oxygen pressure, by measuring the concentration of HPbO2- in the solution with a cathode ray polarograph employing stationary platinum electrodes. Using this procedure a study was made of the kinetics of the reaction, in which the effect of a number of variables, including temperature, oxygen pressure, NaOH concentration, and agitation, on the rate, were determined. The results of this study are described and discussed, in terms of possible mechanisms for the reaction. IT is known that sulphide minerals can be oxidized in aqueous media in the presence of oxygen under pressure. Reactions of this type can be classified in two categories depending upon whether the products of oxidation are insoluble or soluble in the aqueous medium. An example of the first type of reaction is the oxidation of pyrite in alkaline solutions, giving rise to an insoluble iron oxide. The kinetics of this reaction have been investigated and its mechanism established.' It has been applied in the oxidation of iron sulphides present in refractory gold ores to improve the subsequent recovery of gold by cyanida-tion.' The second type of reaction finds application where it is desired to recover the metal by leaching during oxidation. In this case a medium is selected in which the oxidized mineral is soluble. For example, nickel, copper, and cobalt sulphide ores can be treated by oxidation in the presence of a solution of ammonia dissolving the nickel, copper, and cobalt as the metal ammine sulphate salts.:' A similar treatment has also been reported to apply to zinc sulphide ores.' It is known that lead sulphate is soluble in solutions of sodium hydroxide or ammonium acetate. It should therefore be possible to dissolve the lead from galena ores by aqueous oxidation with oxygen under pressure using either of these solutions. The applicability of the ammonium acetate treatment has been investigated and confirmed in a recent study.' The present paper describes the results of a similar study in which the kinetics of the oxidation of galena in sodium hydroxide solutions have been investigated. The object of this investigation was pri- marily to obtain information of a fundamental nature relating to the kinetics and mechanism of this reaction. The use of pulps of comminuted ore in a study of this type is undesirable because of the difficulty in controlling and measuring the surface area. The measurements were therefore made using galena crystals of measured surface area and in this way absolute reaction rates were obtained. The reaction was found to proceed as follows: PbS + 2O2 + 3OH ? HPbO2 + SO4 + H2O [I] The products are sodium plumbite and sodium sulphate salts which dissolve in the aqueous solution. The reaction studies were carried out in an autoclave in which a desired pressure of oxygen was maintained. The reaction was followed by measuring the concentration of lead in the solution with a cathode ray polarograph. The results obtained in this investigation are presented and discussed in the present paper. Experimental Materials: The crystals of galena were obtained from Violamac Mines, Sandon, B. C. The following impurities were indicated by spectrographic analysis carried out by the Provincial Assay Office, Victoria, B. C.: Sn, 0.02 to 0.2 pct; Sb, 0.07 to 0.7; Zn, 0.01 to 0.1; Si, Fe, Mg, As, less than 0.05 pct; Ag, 126 oz per ton, the latter determined by standard fire-assaying procedure. After cutting a specimen measuring approximately 5x7x12 mm, the crystal surfaces were ground parallel to the 100 axes using No. 2 emery, washed with water, and the dimensions were measured with a micrometer. Oxygen gas was of commercial grade and supplied in cylinders by Canadian Liquid Air. Solutions were made up with chemicals of chemically pure grade and distilled water. Equipment: Autoclave: The autoclave used in these studies was constructed of stainless steel and

Jan 1, 1954

By F. E. Jaumot, R. L. Smith

Self-diffusion in zinc at temperatures below 200°C has been studied using both single crystal and polycrystal samples. Anomalous results were obtained for single crystal samples, the data indicating that in some cases grain boundary diffusion predominated. These anomalous results are presumed to be due to low angle lineage boundaries in the single crystals. When volume diffusion occurred in either single or polycrystal samples, the values for the diffusion coefficient were as much as several orders of magnitude larger than would be expected from high temperature data. ONSIDERABLE work has been done on self-^-*diffusion at temperatures in the neighborhood of two thirds of the melting temperature (in OK) and higher, but very little has been done at lower temperatures. This is particularly true of self-diffusion in single crystals. This paper reports work on self-diffusion in zinc at temperatures below 200 °C where both polycrystalline and single crystal samples have been used. The measurements were made using both the sectioning and absorption techniques. The experiments on diffusion at low temperatures were initiated primarily for three reasons: to obtain data from single crystal diffusion covering a wide range of temperatures, to obtain values of the activation energy for grain boundary diffusion, and to obtain, if possible, a lower limit to the temperatures at which the absorption technique may be used. It is possible to determine whether volume or grain boundary diffusion predominates at low temperatures by analyzing the manner in which the concentration of the diffusing atoms varies with the depth of penetration. The analysis is possible only for the sectioning technique. For volume diffusion and for the boundary conditions of the present experiment, the curve of the logarithm of the concentration, C, vs the square of the penetration depth, x, is a straight line with the slope proportional to — 1/D. If grain boundary diffusion predominates, Fisher' has shown that a curve of In C vs the first power of the penetration depth should be a straight line. This linear dependence of concentration on depth has been observed experimentally by several investigators. (See, for example, refs. 3 and 4.) Following Fisher's analysis, the grain boundary diffusion coefficient can be written as where 8 is the grain boundary width, D, is the volume diffusion coefficient at the temperature involved, t is the time of diffusion, C is the concentration of diffusing material, and x is the depth of penetration. A more general analysis employing the same model as Fisher's but with fewer assumptions has been given by Whipple.' In contrast to Fisher's analysis the more general analysis of Whipple does not always yield a straight line relation between In C and x. Recently Turnbull and Hoffman have discussed both analyses and have applied the Fisher-Whipple model to a more refined dislocation model of the grain boundary. They have also discussed the possibility of a large effect of grain boundary direction on diffusion. In the case of the absorption technique, for which results are also given, one simply gets a value for the diffusion coefficient with no indication of the predominating mechanism. Experimental Techniques Single crystals of 99.99+ pct Zn were grown using a modified Bridgman method. Polycrystal samples were prepared in three grain sizes (small, about 4 mm2; medium, about 9 mm'; and large, about 25 mmz) by quenching, air cooling, and furnace cooling. The grains of the polycrystalline samples tended to be columnar, with some preferred texture such that the c-axis was inclined at about 20" to 25" from the normal to the diffusion face, particularly in the medium and large grain size samples. The samples were cut from the rod, polished, and heavily etched, and faces cut accurately parallel using a jeweler's lathe. They were again etched to remove the lathe smear and annealed for 3 hr at 250" to 300°C. After annealing, they were etched, examined, and the orientation determined by Laue back reflection photographs. They were then electroplated with Zn. The plated surfaces were examined for uniformity; nonuniform coatings were removed by etching and the samples replated without additional preparation. For the diffusion anneals, the samples were placed in pairs, with active faces together, in evacuated Pyrex tubes. Constant temperature baths were used, and the variation in temperature did not exceed ±l°C, Diffusion runs were made at l00°,

Jan 1, 1957

By B. R. Hollebone

The chemical action of molten anhydrous pyridinium chloride (pyridine hydrochloride) on oxy salts and ores of some Group IV and V metals are discussed-in particular zirconium, hafnium, niobium (columbium) , and tantalum. Laboratory-scale experiments are described whose results suggest that this reaction might provide a practicable means of converting ores of these metals to the anhydrous metal chlorides. Experimental results are given which provide some insight into the nature of the reactions and some of the compounds which could be present at intermediate stages. The treatment of ores of the more refractory metals is difficult and expensive and often demands the use of gaseous chlorine, hydrogen fluoride, or other reagents which are, if nothing else, expensive and dangerous to use. This situation is, of course, due to the strong metal-oxygen affinity resulting from the high charge and the small size of the metal ion which combine to produce such high lattice energy in the metal oxide as to defeat standard reduction methods. Thus, the characteristic of these metals which leads to one of their most important properties—corrosion resistance—is the main hurdle in obtaining the metal. Many common methods' for treating ores of zirconium and niobium (columbium), for example, proceed as directly as possible to the preparation of anhydrous halides. These halides are purified by now standard processes of solvent extraction, fractional distillation, and so on. This paper reports on preliminary stages in the development of a method of treating these ores—particularly of niobium—so as to prepare the anhydrous, volatile halides by the use of chemical reagents which are much more easily handled than those used at present. CHEMICAL PRINCIPLES The solvent action of aminium halides has been referred to periodically in the literature over several decades. The chemistry of pyridinium chloride has been discussed particularly by Audreith2 and Starke.3 However, since this is not familiar chemistry in its nonaqueous setting, it is perhaps well to point out some general metallurgical principles and applications. One can use, as point of departure, the fact that HC1 dissolved in pyridine is an acid very much the same as aqueous HC1. It thus gives essentially all the reactions of the HC1 with which we are familiar. However, when the ratio of HC1:pyridine reaches 1:l (a ratio far higher than is possible with H2O) the solution becomes solid C5F5NHC1, pyridinium chloride.* Inter- estingly, the acidic properties of HC1 persist in this medium, although they are manifest only in the molten state of the compound. Some typical reactions of divalent metal compounds which we have carried out in our laboratories are the following: 2PyHCl + Zn — (ZnCl2) + H2 + 2Py 2PyHCl + MnO — (MnCl2) + H2O + 2Py 2PyHCl + CuS — (CuCl2) + H2S + 2Py 2PyHCl + CaCO3 — (CaCl2) + H2O + CO2 + 2Py In these equations, the parentheses indicate a solvated compound which in water would be predominantly a hydra ted cation but which in molten PyHCl will more likely be a complex chloro-anion of the type MC14-. Some important physical properties of pyridinium chloride (PyHCl) are given in Table I. One sees from the data in Table I that at the temperature of molten pyridinium chloride both water and pyridine will boil away. Thus the system will be kept anhydrous. For this reason the reaction 2NbCl5 + 5H2O— Nb2O5 + 10HC1 has no counterpart in molten PyHCl. Instead, the chloride is made even more stable by the formation of a hexachloro complex: Nb2O5 + 12PyHC1 — 2PyHNbC16 + 5H2O + 10Py One interesting property of these complexes is their thermal instability which for the case of niobium can be illustrated as PyHNbCl6 — PyHCl + NbCl5 With a view to possible use of this chemistry in ore treatment, we have attempted to dissolve Pyrochlore (essentially FeO - Nb2O5) and recover the NbC15 from it.

Jan 1, 1968

By J. G. Balkestein, J. W. R. Baerts

During an attempt to develop a method for accurate, rapid, continuous analysis of ash content of wal, the Dutch State Mines Laboratory found that the absorption coefficient for X-rays was related to ash content. This relationship was utilized in the development of an apparatus called CendreX, used to measure the absorption and in turn the ash content. The principle, procedure, accuracy, and applications of the CendreX automatic determination of ash in coal are discussed in detail. Until recent years coal preparation research was concentrated on the possibilities and efficiency of preparation equipment. Ever increasing demands for quality in coal, however, have caused researchers to become concerned with quality control. One of the characteristics strongly influencing quality (calorific value) and, consequently, the price of coal is ash content. Both customer and producer require that the ash content be controlled. To make this possible it is necessary for the producer to collect samples from the coal stream in the washery and to determine their ash content. On the strength of the results obtained the production process can then be adjusted, if required. Until recently incineration was the only method for determining ash content. When coal is incinerated with oxygen, it takes at least 15 min to determine the ash content. Even then some time may be lost in passing on the data. Therefore, this discontinuous and time-consuming method does not make a suitable starting point for checking, re-adjusting, or modifying the production process. Since it was not possible to accelerate incineration by mechanization and automation, another type of rapid continuous analysis had to be found. This would have to depend on some coal characteristic closely linked with ash content. At the Central Laboratory of Dutch State Mines, Dijkstra and Sieswerda found that the absorption coefficient for X-rays was suitable for this purpose. An apparatus based on the measurement of this characteristic was developed. Named CendreX,* this patented equip- *A Stamicarbon N. V. registered trademark. ment, used in combination with a sampler and conditioning apparatus, permits continuous determination of ash content with satisfactory exactness to within 3 min.t At the American Mining Congress meeting of May 1961, Log A. Updegraff, surveying aspects of continuous analyaia, reported on the CendreX appartus (Mining Congress Journal, August 1961). Since the first Condition for correct ash determination, whatever the method used, is always a sample taken in the right way, some practical aspects of sampling will be discussed first. SAMPLING In coal handling operations, each grain has its characteristic properties. In both the cross-sectional and longitudinal direction of the product stream the mixture of these grains is imperfectly blended. The elimination of the factor of segregation between the cross-sections from the direction of the stream is the principal aim of continuous analysis. Therefore, the samples to be analyzed are withdrawn in various places from the segregated product stream in such a way that they form a semi-continuous flow. In order to be truly representative of the product stream, the sample flow must fulfil two conditions: 1) The sample flow must be sufficiently large to insure that adventitious differences between the composition of the product stream and sample flow will be as small as possible. 2) All grains through the entire cross section of the product stream must have an equal chance to get into the sample flow. Since there is always a segregation through the cross section the sample flow will have a bias if the sampler collects only part of this section. In order to prevent the volume of the sample flow from becoming too large, the cross sections are taken discontinuously. However, this discontinuity gives rise to the adventitious differences that arise between the composition of product stream and the sample flow, and these differences become greater and are more deranging as the fluctuations follow each other more quickly. Moreover, the intervals between the morrnents of sampling mean a delay in the analysis. The aim will, therefore, be to collect small samples, or in other words thin cross-sectional increments, taken at sufficiently high frequencies. The following points should also be taken into account: 1) The smallest dimension of the openings in the sample collector must be equivalent to at least 3 d in

Jan 1, 1962

By D. C. Seidel, E. F. Fitzhugh

The Colorado School of Mines Research Foundation has developed a hydrometallurgical process for recovering nickel from oxidized ores, including both the iron-rich laterites and magnesium-rich, soft silicates. Known as the HSO-HTCP (Hydrothermal Sulfidization Oxidation-High Temperature Cementation in Pulp) Process, the system consists of feed preparation, sulfidization, oxidation, precipitation (cementation), and calcination and melting. This paper deals primarily with the sulfidization and oxidation phases of the process. Nickel sulfide ores lend themselves readily to concentration before smelting or pressure leaching, but neither of the major oxidized ore types — the iron-rich laterites and magnesium-rich, soft silicates-has been directly concentrated. Upgrading of crude ore in current practice is limited to cobbing lumps of the harder, lower grade rock (protore) from the softer, enriched silicate ore, because only a small percentage of the nickel in these ores occurs in discrete, contrasting mineral particles. There is no apparent mineralogical contrast in the superficial, iron-rich lateritic ores and, in fact, there is no firm assurance that the nickel atoms are within the lattices of the limonite minerals, or else irregularly adsorbed on the limonite. Within underlying, "rotten rock" silicates, occasional veinlets of gamierite and related nickeliferous silicates are found.' The gamierite veinlets, however, are only incidental, and the majority of the nickel atoms occur as erratic replacements of magnesium atoms in the micaceous chlorites of the ore mass. Pyrometallurgical processes account for nearly all the nickel currently being recovered from oxidized ores. Plants in New Caledonia, Oregon, Japan, Brazil and Greece smelt the ores to make ferronickels or a sulfide matte,2 and the ammoniacal leaching3 at Nicaro, Cuba, is preceded by a reducing roasL4 The only fully hydrometallurgical installation has been the politically ill-fated Freeport Nickel Co. enterprise, and this process was limited to lateritic ores.5p6 A hydrometallurgical technique which might handle both laterite and the typically richer silicate ores has been an enticing goal. The technique described here was developed at the Colorado School of Mines Research Foundation, Inc. on behalf of the Republic Steel Corp. It uses sulfur, heat, air and metallic iron to recover nickel from these ores. Inasmuch as the ores are treated as aqueous slurries, the cost of drying a plant feed that normally carried 30% or more moisture is eliminated, and there are no dust problems. Patent applications have been filed by Republic Steel Corp. on the procedures used for getting the metal into solution and on the subsequent recovery without liquids-so l ids separation of the slurry. It is referred to as the HSO-HTCP Process (Hydrothermal Sulfidization Oxidation — High Temperature Cementation in Pulp). THE PROCESS FLOWSHEET The results of various experimental studies have been combined to form the continuous flowsheet illustrated in Fig. 1. This flowsheet serves as a general pattern showing the sequence of the operations which include: (1) feed preparation; (2) sulfidization; (3) oxidation; (4) precipitation (cementation); and (5) calcination and melting. This paper deals primarily with the sulfidization and oxidation phases of the process. Feed preparation: In general, the silicate ores can be considered as earthy rather than hard, and preparation might be carried out before the addition of water in a trommel, or with water in a scrubber or log washer. This breaks up the earthy particles, allowing the hard lumps to be separated by screening. The oversize material from most ores is relatively barren and may be discarded. If there is occasion to control the iron-magnesium ratio in the plant feed, laterite, which normally breaks up readily into fine sized particles, and silicates are mixed in suitable proportions. The fine product slurry from the initial steps is mixed with elemental sulfur and fed to a conventional ball mill, although the amount of actual grinding that takes place is relatively small. The object of milling is to complete the disintegration to natural particle size and to produce an intimate mixture of the ore and elemental sulfur. This pulp, which is almost entirely -200 mesh, has a pH of about 7.0 and normally can

Jan 1, 1969

By H. L. Marcus, C. D. Turk

Titanium was physically vapor-deposited by electron beam high rate evaporation. Rates of 50,000 and 85,000Å per min at deposition temperatures of 480°, 535°, and 595°C were used. Deposited thickness ranged front 0.004 to 0.010 in. The evaporated titanium had a high degree of basal Plane texture. The specimens were tested in tension at temperatures ranging from 78° to 520°K. From the data, the yield stress, thermal component of the yield stress, and work hardening characteristics were found as a function of temperature, deposition rate, and deposition temperature. It was found that Taylor's equation, best fit the work hardening data with m = 1/2. MANY investigations have been made on the tensile deformation characteristics of commercial- and high-purity titanium.1"7 The data obtained from these experiments emphasize the fact that the mechanical properties are generally related to the method of production. The correlation of mechanical properties to production history arises from the dependence of impurity concentration on the extraction and melting technique used. Additional effects are derived from crystallographic texturing which can result from fabrication history. Lee and Backofen8 and other investigators9 have shown that crystallographic texturing in titanium sheet has a significant effect on the deformation characteristics. Bunshah and Juntz10 prepared high-purity titanium by high rate physical evaporation techniques. These authors found the deposited material to have a columnar structure with grain sizes ranging from 12 to 104 µ, depending upon the substrate temperature. The room-temperature strengths of the coarse-grained distillate were similar to arc-melted, rolled. and annealed crystal bar titanium. Commercial-purity titanium was also produced experimentally in our laboratory using high rate physical vapor deposition techniques. The commercially pure material has a finer structure than the high-purity distillate,10 and is highly textured. Since the method of preparation and degree of texturing affect the mechanical properties, a research program was initiated to determine the temperature dependence of the yield stress and work hardening characteristics as a function of high rate deposition parameters. This paper relates the results of the investigation. EXPERIMENTAL A) Material Preparation. The titanium was received in the form of commercial-grade 0.096-in.-diam wire which has a composition of 0.016 pct C, 0.0037 pct N, 0.110 pct 0, 0.011 pct H, 0.05 pct Mn, 0.051 pct Fe. balance Ti. The wire was continuously fed into a vacuum evaporation unit as shown schematically in Fig. 1. The deposition chamber was evacuated, purged with argon, and reevacuated to a pressure of 10-5 Torr which was maintained during deposition. A focused electron beam was used to evaporate the titanium from a water-cooled copper crucible. The titanium vapor was condensed onto a preheated titanium substrate. The temperature of the substrate was controlled within ±5°C for the deposition temperatures of 480°, 535°, and 595°C. Control of the input power enabled the use of two deposition rates. 50,000 and 85,000Å per min. The evaporated titanium had a final analysis similar to that of the input titanium, within experimental limits. B) Testing. The evaporated titanium was physically stripped from the titanium substrate and machined into tensile specimens with 1-in. gage lengths. In addition, tensile specimens of as received annealed 35-A titanium sheet with a 20 µ grain size and 45 pct cold-rolled 35-A were also prepared. All specimens were tested in tension in an Instron at a strain rate of 3.3 x 10"4 in. per in. per sec. Proportional limit has been used as a measure of yield strength. Tests were conducted at 78°, 220°, 300°, and 520°K. Metallography, X-ray diffraction, and electron microscopy were used to correlate structure with the deposition parameters and mechanical properties. Room-temperature X-ray measurements were made to determine the phases present. Pole figures and a scans were made to determine deposition texture. Because the vapor deposition was symmetrical about the normal to the substrate, there was no preferred di-

Jan 1, 1969

By D. T. Peters, J. C. Bisseliches, J. W. Spretnak

The pain boundary relaxation phenomenon in high-purity copper, 0FHC copper, and a precipitation-hardenable alloy o-fCu-2 uit pct Co has been studied by internal ,friction and elastic aftereffect techniques. The data were analyzed by assuming the broad distribution of relaxation times observed obeys a lognormal distribution law which enables calculation of the relaxation strength. Grain size had no effect on relaxation strength, although the peak width increased with increasing grain size and decreasing temperature. A double grain boundary peak was produced in high-purity copper by annealing to produce secondary recrystallization. The activation energy measured for 99.999 pct Cu is 37.5 * 3 kcal per mol and 46.5 kcal per mole for OFHC copper. A small peak in the Cu-Co alloy at about 220°C at 1 cps was deduced to be the grain boundary peak. Its height increased and its activation energy decreased with increasing aging time. Except for erratic peak positions the observations were consistent with the theory of pain boundary sliding. BEFORE the mechanism of the grain boundary internal friction peak in metals can be satisfactorily explained, the detailed characteristics of the relaxation process must be documented. Of interest are the effect of grain size on relaxation strength, the high-temperature background, and peak width and position. The effect on the grain boundary peak of a precipitate at grain boundaries and of the change in distribution of the particles with aging time must also be explained by any existing or forthcoming theory. The model which has received the most attention was proposed by KG' and zener2 and proposes that the anelastic strain results from sliding of adjacent crystals at grain boundaries. The sliding is limited by the interlocking of grain corners. It follows, according to this model, that the relaxation strength is independent of and the relaxation time is proportional to the grain size. The proportionality between grain size, D, and relaxation time, t, has been confirmed by K&' and Bisseliches . In this case, the internal-friction peaks of various specimens can be superimposed by plotting Q-' as a function of the parameter vD exp H/RT where v is the frequency and H the activation energy. However, the data of Starr et 01.' and Leak6 fit better to a parameter containing D to an exponent near two. A meaningful relationship is not always deducible from the shift of peak temperature with grain size. KG7 demonstrated that a twofold variation in grain size obtained by varying the amount of cold work followed by identical recrystallization anneals will cause a peak shift that is too large to be accounted for even by an exponent of two. Since the decreased grain boundary area existing with a larger grain size is exactly compensated for by an increased sliding distance, the relaxation strength should not decrease with increasing grain size. The height of the internal-friction peak has generally been observed to be rather insensitive to grain size as long as the average grain diameter does not approach the specimen diameter. Exceptions have been reported by Koster, Bangert, and Lang8 for copper, and by Leak6 for iron. The observations for copper could well have been confused by the presence df 0.3 pct0. The possibility that the peaks may simply be increasing in width with increasing grain size and that the relaxation strength, which is proportional to the area under the peak, may remain constant was not examined. his point has been checked in this investigation using high-purity copper. Atomic mechanisms to account for damping by sliding at grain boundaries have been proposed by KG7 and Mott. KG predicts the activation energy to be identical to that for self-diffusion. Mott's "island" model suggests the activation energy is nL where n is the number of atoms in an island and L is the latent heat of fusion per atom. Other authors have felt that a value equal to the activa-

Jan 1, 1964

By R. E. Reed-Hill, W. H. Hartt

The second order, {1011}-{1012} twin bands observed in critically deformed magnesium are often accompanied by an unusual form of kinking. These kinks, which lie adjacent to and run more or less parallel to the twin band habit, allow plastic deformation that occurs inside the twins to be accommodated into the matrix. The bend planes of these kinks cannot be explained using slip dislocations with Burgers vectors lying in the basal plane. A mechanism involving a single set of {1012)(1011) dislocations is proposed to account for the kink band habit, in good agreement with the experimental observations. It has been shown that second order, {101l)-{1012} twinning is an important phenomenon for magnesium deformed in the ambient temperature range. A detailed study of these twins has recently led to a better understanding of their irrational habit plane1 and their relation to fracture in magnesium.' This paper is concerned with a third aspect of these twins; this being the kink bands, originally referred to as shear accommodation kinks,3'4 that are often induced in the adjacent matrix. A twin band and its shear accommodation kink usually appear as a single macroscopic deformation, as seen in Fig. 1. The complex nature of these deformed regions is easily revealed, however, with the aid of a suitable microscope. It has been proposed374 that the primary function of these kinks is to accommodate the nonhomogeneous deformation that normally occurs in the second order twins. The twins tend to form as small discrete lamellae lined up approximately one in front of the other.''' Very large plastic deformations varying in magnitude from one twin to the next, may occur inside these lamellae. The kinks serve both to pass this strain into the matrix and to accommodate strain variations between twins. Deformation within the kinks, subsequent to their formation, has also been observed;3,4 and it is thought that this contributes to the strain accommodation process. The bend planes of the kinks have a habit near that of the twin band itself, which lies about 56 deg from the matrix basal plane. This orientation does not bisect the angle formed between the basal plane to either side of the bend plane and therefore differs markedly from the kink structure usually observed in hcp metals.'-' The present paper reports the results of a study of shear accommodation kinks and proposes a possible solution to the problem of the orientation of the bend plane. EXPERIMENTAL PROCEDURE Rectangular cross-section tensile specimens with axes parallel to (1010) and faces to (1210) and (0001) were cut and acid machined from a high-purity magnesium single crystal. After straining on an Instron machine the specimens were examined by both optical and replica electron microscopy. The basic procedures have been previously reported."' EXPERIMENTAL RESULTS AND DISCUSSION Structure of Shear Accommodation Kinks. A typical, large (101l)-{1012) twin band with its associated shear accommodation kink is shown running diagonally from upper left to lower right in Fig. 1. In this optical micrograph the twin band, consisting of a row of small, highly deformed twin lamellae, is visible as a narrow dark band along the left hand edge of the structure in question. The kink lies to the right of the twins, is approximately three times as wide, and is lighter in contrast. The horizontal slip lines visible on the general specimen surface correspond to matrix basal slip and are parallel to the tensile axis. Note that on the right-hand side of the band these slip lines can be followed from the matrix into the kink. At the kink band boundary the slip lines suffer a clockwise rotation of about 25 deg. Rotations of this magnitude are not uncommon. When a surface such as that in Fig. 1 is given an etch1 making it sensitive to polarized light, it has been observed that the slip traces in the kink are parallel to the basal plane trace in this region. This is in excellent agreement with the assumption that these regions are indeed kinks. Fig. 2 is an electron micrograph of this same twin band and kink. Note that a row of small supplimation pits has formed

Jan 1, 1969

By E. F. Johnson, F. H. Brinkman, H. J. Welge, S. P. Ewing

This paper presents a method for predicting the manrler in which oil will be displaced from a porous body by enriched gas. The calculations apply to a gas rich enough to give a partially, but not a completely, misci-ble displacement. The method — a three-component, two-phase analysis — takes into account condensation of some of the intermediate hydrocarbons from the injected gas into the oil, as well as enhanced volatility of heavier hydrocarbons at elevated pressures and temperatures. The condensation swells the oil and decreases its viscosity, thus aiding in its recovery. The calculations have been extended to apply to actual crude oil-natural gas systems by arranging the components into three groups according to their volatility. As an approximation, each group is then treated as a single component in the analysis. The influence of an angle of dip for an inclined displacement is also taken into account. The recovery predictions are corroborated by experiments which used both consolidated sand cores and un-consolidated glass beads. In some of these tests, actual live crude oil was displaced by a multicomponent gas typical of enriched gases used in oil fields. INTRODUCTION This paper presents a method for predicting the amount of oil that can be displaced from a homogeneous, linear, porous body at various stages during the injection of enriched, or "wet", gas. The porous body can be in either a horizontal or an inclined position. 'This type of displacement is sometimes known as condensing gas drive The method is developed especially for the case in which the injected gas is enriched enough to be partially, but not completely, miscible with the reservoir oil. The need for a calcula-tive procedure for this type of operation is emphasized by the number of field projects where completely miscible drives are not practical, but where near-miscible conditions are feasible. The factors taken into account in the predictive calculations include: (1) the condensation of gas components into the oil, with a resulting increase in oil volume; (2) the lowering of oil viscosity by the addition of lighter ends from the gas; (3) the increase in oil volatility at high temperatures and pressures; and (4) the physical displacement of the oil by the gas. The techniques developed in the paper can be extended to other nonequilibrium displacement processes. Other such processes that we have analyzed include a displacement by lean gas which stripped intermediates from the oil, and a water flood in which the water con. tained in solution a substance somewhat soluble in the oil. ANALYSIS OF ENRICHED-GAS DRIVE GENERAL PRINCIPLES Our method for predicting the amount of oil that can be displaced by an enriched gas uses an analogy between a three-component and a multicomponent system.' The predictive method is based on these assumptions: (1) constant, or nearly constant, pressure; (2) complete equilibrium by diffusion perpendicular to the main direction of flow, but no significant mixing along the direction of flow; (3) constant injection velocity; and (4) flow in a linear porous body. The composition of a liquid or a vapor with respect to three components can be plotted on a three-component, or ternary, diagram like that in Fig. 1. Let Point A represent the composition of the oil originally in place. In this case, Oil A is undersaturated with gas. If Point A lay on the equilibrium Curve BF, the oil would be saturated. In the extreme case where the original oil contained no intermediates or dissolved gas, Point A would lie at the lower left-hand corner of the ternary diagram. In a displacement of Oil A by Gas D, there will be a progressive change in the composition of the oil phase as more and more gas is brought into equilibrium with the oil. The end result of this progressive change is an oil having the composition represented by Point F. This oil is richer in intermediate hydrocarbon and methane than the original oil and, therefore, has a greater forma-