(1) Introduction: The purpose of this paper is to call attention to certain methods which will shorten and simplify the calculation of plane tri-angulation. These methods, though not new,',2 do not appear to have been properly publicized in the United States. The cotangent (or tangent) solution of a triangle permits calculation of coordinates in a smooth series of operations of the calculating machine with a minimum of notation. The semigraphical solution permits the simultaneous solution of a number of intersections, at one station, without the added burden of solving additional triangles. This in turn encourages more numerous field checks and more complete office computation than would normally be undertaken. RICHARD HAMBURGER, Junior Member AIME, is Junior Engineer, Inspiration Consolidated Copper Co., Inspiration, Arizona. TP 2798 A. Discussion (2 copies) may be sent to Transactions AIME before March 31, 1950. Tables I and I1 show the distinct advantage which the combined use of the cotangent and the semi-graphical solutions hold over, what might well be called, the standard solution. It will be shown that the positions for the entire net in fig. 1 may be calculated without computing any distances, thus saving much computation. (2) Comparison of Cotangent and Standard Solutions: To compare the cotangent method with the standard method, the notation involved in the solution of triangle 1-X-4, fig. 1, by both methods is shown. Fig. 2 shows the given information, that is, the coordinates and azimuths of Stations 1 and 4, and angles of the triangle or the azimuths from Stations 1 and 4 to Station X. (Azimuths are used here because the author feels that they are easier to handle, but bearings may be used by those who prefer them). It will be seen from the above comparison that the advantages of the cotangent solution of a triangle are: (a) rapidity, (b) full use of the calculating machine, (c) the small number of

Jan 1, 1951

By R. C. Ruder, C. E. Birchenall

The method of decrease in surface activity was used to determine the rates of diffusion of Co" into cobalt and into nickel. Since the absorption curves for cobalt radiation were quite complex under the conditions of these experiments, the effects of geometry and surface preparation on the diffusion results were investigated. The cobalt self-diffusion coefficients obey the equation DCoco = e-61100/RT cm2 per sec. For dilute cobalt diffusing in nickel, DConi, == 1.46 e-/R' cm2 er sec. AS part of the general program to measure the self-diffusion and dilute-solution diffusion rates of the iron-group metals, the diffusion coefficients of cobalt into cobalt and nickel have been measured using the radioactive isotope Co"'. Self-diffusion studies in iron have been previously reported by Birchenall and Mehl.' The technique of measurement used was the decrease in surface activity method described by Steigman, Shockley, and Nix.' It has been determined that scattering of the measured beta radiation by the specimen matrix is significantly influenced by the condition of the surface and the counting geometry. Accurate diffusion coefficients can be calculated from the activity data provided that the specimens have plane diffusion surfaces and that the absorption properties of the emitted radiation are determined under geometrical conditions duplicating with external absorbers the absorption and scattering in a thin film at the specimen surface as nearly as possible. The cobalt used in this research was originally in the form of hydrogen reduced rondels 99.9+ pct pure. The nickel had been prepared by the carbonyl process and was found by spectrographic analysis to contain 0.03 pct Fe, 0.04 pct Co and smaller traces of other metallic elements for a balance purity of 99.9+ pet Ni. Both materials were vacuum melted and cast in rectangular ingots. Specimens 7/8x7/8x1/4 in. were machined from these ingots. The specimens were then ground to 4-0 emery paper and annealed in hydrogen for at least a day at 1200°C. Some of the specimens were used in preliminary experimentation after which their diffusion faces were machined to remove the radioactive material from the previous diffusion experiments. After grinding, the specimens were polished using an electrolytic lapping technique described by Mazia." This lapping was continued until at least 0.005 in. was removed from the diffusion surface. The final surfaces were metallographically smooth except for a few fine scratches caused by the glass cloth. A large percentage of the area was undisturbed as determined by microscopic examination. The grain diameters of the diffusion specimens varied from 0.1 to 5 mm. There were no effects due to grain boundary diffusion in the experiments

Jan 1, 1952

By Paul Giesecke

SINCE most modem metallurgical plants are operated continuously and on a large scale, successful operation at maximum efficiency demands that an accurate knowledge of the performance at each stage of the process be available at all times. Quantitative analyses provide the most practical process guides, and it is essential to have analytical procedures that combine accuracy and speed. In continuous plant operations, large losses may occur if the time interval between the development of trouble at any stage and its recognition and correction is great. Many metallurgical plants are using rapid colorimetric and spectrochemical methods of analyses for control purposes. So-called "color coppers" may be cited as an example of the colorimetric methods, in contrast with the routine use of the ultraviolet spectrograph for the analysis of steels.42 By means of this more refined spectrochemical procedure, a complete quantitative analysis of the molten metal is obtained every few minutes. During the past two years the Physics Division and the Ore Dressing Laboratory of the American Cyanamid Company's Stamford Research Laboratories have collaborated in a study of the use of spectrochemical methods for the analysis of various metallurgical products. New methods have been developed, which have proved of practical value in plant operation. The following pages give a general review of the principles of spectrochemical methods and also the details of several specific analyses. PRINCIPLES OF SPECTROCHEMICAL ANALYSIS In general, it can be said that a visible light spectrochemical analysis can be performed for any ion or molecule that is naturally colored, or that can be made to react with another to produce a colored salt or complex. Whereas transmission measurements in the ultraviolet and infrared portions of the spectrum are most useful for the analysis of organic molecules, visible light measurements are of particular value for metal salts. Such elements as copper, manganese, cobalt, nickel, iron, molybdenum, vanadium, chromium, phosphorus, mercury, zinc, lead, and a great many others, can now be determined with a high degree of sensitivity, accuracy and dispatch. From the simplest of qualitative determinations, color analyses have been improved to such an extent that, at the present time, through the use of recording spectrophotometers, hundreds of accurate quantitative analyses can be performed by a single analyst during an 8-hr. day after the standardization curves have been established for the ions to be determined.

Jan 1, 1944

[For the year ending February, 1936 PRESIDENT AND DIRECTOR HENBY A. BUEHLER3 ROLLA, Mo. PAST PRESIDENTS AND DIRECTORS FREDERICK M. BECKET1 NEW YORK, N. Y. HOWARD N. EAVENSON2 PITTSBURGH, PA.]

Jan 1, 1936

By Leonard Austin

WHAT Colonel Dwight says regarding the treat-ment of oxidized ores1 holds true also of the silver-lead smelting operations in Utah. The ore sought for was such as would, with appropriate fluxes, yield slag, and "lead bullion," as the lead reduced from the ore and carrying its gold and silver, was called. No matte, and probably little or no speiss, was yielded, and hence there was nothing to roast, either of ore or matte. But, by 1880, when I first took hold in smelting, there was quite a production of matte at the works of the Ger-mania Smelting and Refining Co., Utah, because, by that time, ores containing some pyrite and galena were being smelted. This was due, as at the Grant Works, Denver, to the more attractive price paid for the treatment of such ores. The matte, containing about 5 per cent. copper, was accordingly heap-roasted and returned to the blast furnace for the recovery of its contained metals. By this time there had been built a long-bedded, hand-rabbled reverber-atory roaster with a hearth of about 40 by 10 ft. in size, and in this matte and ore, crushed at the sampling mill, was treated. When, in 1892, I took control of this works, called& now the Germania Lead Works, three other roasters had been added, but the prac-tice of heap-roasting continued. This had the merit of needing no equipment, and of doing good work, because the pieces that were imperfectly roasted went back upon the next roast heap. At this time, when some suitable lump ore was obtainable, I roasted in heaps, in a satisfactory way. By 1892, the Bruckner cylinder roaster had been installed, which, compared with the reverberatory roaster, reduced labor. As such a cylinder revolves, a talus of ore is formed within it and at the same time fresh surfaces are exposed to the air, but the trouble was that the air did not reach to the bottom of the cylinder. This we corrected by placing a steam jet at the fire-box end, to project the air down-ward upon this stagnant ore, thus increasing the speed and completeness of roasting without at the same time increasing dust formation. The firing, if skilfully done, gave a somewhat sintered product, but with certain ores a slight access of heat over the normal would cause accretions to form within the cylinder near the fire end. These could be cut off by running back the fire box and barring off the crusts. It was in 1895 that the Bruckner cylinders at the Arkansas Valley plant, Leadville, were giving unsatis-factory service and I was called in to investigate. The steam jet was put in use as at the Germania Lead Works, but we found that, due to the altitude (10,500 ft.), combustion was feebler than at sea level or even at 4000 to 5000 ft. Later it appears, as Colonel Dwight states, that R. D. Rhodes and Mots sought to increase the air supply by admission through perforated tiles, but the trouble was due to the air itself.

Jan 8, 1922

By C. C. Bailey

THE vendor seeking outside capital for his project has the following potential sources which may be approached; 1--private sources, 2-institutional funds, 3--government agencies, 4--established mining concerns, and 5-public financing.

Jan 7, 1953

By P. W. Bridgman

Flow and fracture are admittedly complicated phenomena of which we are yet only partially masters. There is not even nni-.persal agreement as to the details of the language best adapted merely to describe the phenomena, to say nothing of any theory. Certain points of view, however, are widely held, and there are certain general expectations as to what sort of procedures will prove permissible. A complete description of any situation involving fracture would demand a complete history of all the variables in the control of the experimenter. The experimenter endeavors so to choose his independent variables that they are adequate to determine completely the situation in the sense that when an experiment is repeated on the same initial material and with the independent variables running through the same sequence, all the other measurable properties of the system will also run through the same course. It is, I think, the universal conviction that when we are dealing with phenomena of flow and fracture, the most important of the necessary variables are the external forces acting on the various parts of the body; when the force history repeats, with certain obvious restrictions such as that temperature must be constant and non-mechanical forces, such as magnetic field, must be small enough to be ineffective, then the history of all measurable properties will repeat; in particular the alteration of geometrical shape due to flow will run through the same course, and when fracture comes, the character of the fracture will be reproduced. Complete mastery of merely the descriptive aspects of flow and fracture would demand the ability to predict the entire course of flow and complete characterization of the final fracture for every possible combination of forces, varying in time in all possible ways, when applied to bodies of all possible shapes. This full situation is obviously of prohibitive complexity. The first stage in reduction to manageable simplicity is to resolve the total situation into the sum of contributions made by small elements. Our thesis is that if each of the elements is adequately characterized, the behavior of the whole system is fixed. The element is usually taken of a simple geometrical shape, suggested by the mathematics best adapted to the particular situation. The forces acting across the faces of the elements are ultimately determined by the forces acting across the free faces of the whole system. The detailed process of finding the precise forces on the faces of all the elements in terms of the external forces involves the use of a special mathematical invention, the stress, a constructional quantity consisting of six components. The stress at any point in the body is determined by both the external force system and by the physical properties of the body at all points; quite different stresses prevail at the interior of bodies of the same shape under the same external forces in the elastic and plastic ranges. The forces on the faces of any element are, however, uniquely determined by the stress system at the element. Our fundamental thesis

Jan 1, 1945

By Kyle Wightman

INTRODUCTION CRA Limited is the largest mining group in Australia by value of sales and the second largest company in Australia in terms of share market capitalisation. In the past 25 years, CRA, its predecessors and affiliates have been involved in a number of mining and further processing developments in Australia and elsewhere. Many of these have been financed using project financing techniques. These include Comalco's development of the Weipa bauxite deposits in Northern Queensland in the late 1950's, the Hamersley iron ore developments in the Pilbara region of Western Australia in the mid 1960's, the Queensland Alumina Limited alumina refinery in Gladstone, Queensland, at about the same time, and the Bougainville copper project in 1969/70. In the past three years CRA has again utilised project financing techniques to fund its Tarong steaming coal project in Queensland, the Blair Athol steaming coal project also in that State and CRA's interest in the Argyle diamond project in the Kimberley region of Western Austrlia. PROJECT FINANCE DEFINED Nevitt Definition Nevitt's is the most frequently quoted definition - "A financing of a particular economic unit in which a lender is satisfied to look initially to the cash flows and earnings of the economic unit as the source of funds from which a loan will be repaid and to the assets of the economic unit as collateral for the loan." Risk and Balance Sheet Treatment It is important to focus in more detail on two aspects of project financing, risk and balance sheet treatment. The assessment of the various elements of risk in a project and the sharing of that risk between sponsors and lenders is the most critical feature. At one end of the spectrum is full absorption of risk by the sponsor(s). This can be described as "on risk" or "on credit" or "full recourse" to the sponsor(s) and is effectively a corporate financing. At the other end of the spectrum the lenders absorb the whole risk in a non-recourse financing which is "off risk" or "off credit" for the sponsor. The other aspect is the sponsor's balance sheet treatment. If the balance sheet of the economic unit undertaking the project and the financing need not be consolidated into the balance sheet of the sponsor (because ownership does not exceed 50%) then the financing may be described as off-¬balance sheet. If consolidation is required then the financing is described as on-balance sheet. Most project financings involve some recourse to the sponsor, i.e. they are limited recourse. Very few are non-recourse or off credit to the sponsor. Limited recourse financings may be on-balance sheet although many may also be off-balance sheet insofar as consolidation is concerned. However, sponsor support may very well be a contingent liability to the sponsor and require disclosure by way of note to the balance sheet should consolidation not be required. CORPORATE FINANCE CONTRASTED A financing which is on credit or full recourse to the sponsor, whether it is directly borrowed or guaranteed by that sponsor, is a corporate financing. Lenders will tend to base their credit assessment on a historical assessment of the sponsor's activities and its financial results rather than an assessment of the project or a detailed assessment of the future activities and prospects of the sponsor. PROJECT FINANCE - A BORROWER'S PERCEPTION Although CRA could choose to arrange all finance on a corporate basis (except perhaps for the very largest projects or acquisitions), project financing techniques provide a number of specific advantages which CRA has noted and which should be carefully considered by a project sponsor. Advantages

Jan 1, 1985

By C. W. Covington, H. C. Cook, J. F. Libsch

Sputtered aluminum thin films were prepared in each of two conventional bell-jar vacuum systems. One system utilized an inner "getter sputtering" enclosure; the second system was a standard diode sputterirlg arrangement. Consistent and repeatable film properties were obtained in both systems provided sufficient cleanup and presputter time was allowed. The various problems associated with aluminum sputtering are discussed, with pavticular attention to the vzinimization of film contamination by outgassing and oxidation. The growth and structure of the aluminum thin films were studied with the aid of electron wzicroscopy and related to deposition rate, substrate temperature, and film thickness. The resistivity of the films was correlated to film structure and surface roughness. Resistiuities as low as 3.5 microhm-cm (2.3 x bulk resistiuity) were measured for relatively thick films (20,000). THIS investigation was undertaken to explore the problems and film characteristics associated with the sputtering of aluminum. Earlier work reported on aluminum sputtering has stressed the contamination of both the cathode and film as well as abnormally low deposition rates.' Data on sputtering yields,3 however, indicate that aluminum sputtering could be practical. Recently, it was shown by Theuerer and Hauser3 that aluminum sputtering was feasible in a conventional oil-diffusion pumped vacuum system provided an inner "getter sputtering" enclosure was employed to minimize gaseous contamination. This technique employs the getter action of aluminum to produce extremely low reactive gas partial pressures in the deposition zone. Aluminum films have already found use in solid-state electronic devices such as transistors and integrated microcircuits. To the present time, most aluminum films have been prepared by evaporation due to the ease with which this metal can be evaporated. Controlled sputtering of aluminum offers a number of advantages over evaporation, however, such as 1) manufacturing compatibility with other metals which must be sputtered, 2) better control of process variables resulting in more repeatable and uniform films, 3) generally better adhesion resulting from higher-energy metal atoms, 4) built-in material supply for continuous operation, and 5) the ability to deposit alloys. The data presented in this paper are the result of two separate studies. One study utilized a small "getter sputtering" enclosure (System A) and was concerned with the structure and properties of thin aluminum films up to about 1600A thick. In this thickness range, study of the film structure was possible with transmission electron microscopy. The second study was conducted with a conventional diode sputtering apparatus (System B) and covered $ much wider range of film thickness up to about 34,000A. Emphasis was placed on developing techniques which would extend aluminum sputtering to an existing in-line continuous deposition process.4 I) EQUIPMENT AND PROCEDURE System A. Fig. 1 shows a schematic of the "getter sputtering" inner chamber used and Fig. 2 is a photograph of this chamber mounted on an 18-in. access ring of a standard liquid-nitrogen trapped bell-jar vacuum system. This chamber was designed after a similar system used by Theuerer and auser.3 The configuration allowed the glow to emanate in all directions from the cathode. Argon (99.99') was allowed to enter only at the top of the chamber such that most of the reactive gases entering with the argon were reacted with the aluminum vapor and deposited on the chilled walls of the chamber before reaching the deposition zone. Provision was also made as shown, Fig. 1, for heating and cooling the substrate from about 20" to 400°C. Two substrate materials were used: Corning 7059 glass (12 by 12 by 0.048 in.) and carbon films about

Jan 1, 1967

By Wayne L. Worrell

Thermodynamic data for the stable carbides and oxides of chromium, molybdenum, and tungsten have been critically eualuuted and are used to determine the stable condensed phases at 1 atm total pressure in each metal-carbon-oxygen system. Pourbaix-Ellingham diagrams have been constructed and are used to estimate the minimum temperatures neces.see)*y to oblain these metals by corbolhermic redlrction under reduced pressures. USING recently reported data for the carbides and oxides of chromium, molybdenum, and tungsten, the stable phases in the Group VI metal-carbon-oxygen systems at specific temperatures and pressures can be determined. The thermodynamically stable regions in each metal-carbon-oxygen system can be completely pictured using a Pourbaix-Ellingham diagram in which the two coordinates are oxygen potential (-RT In Po2) and temperature. Worrell and chipman' have described and constructed such diagrams for the metal-carbon-oxygen systems of vanadium, columbium, and tantalum. Downing2 has used similar diagrams to provide a description of the reactions in submerged arc furnaces. One of the examples which he cited was the Cr-C-O system; however, an improved diagram is presented in this paper using recently obtained data for the carbides of chromium. Although some of the oxides and carbides of the Group VI metals exist over slight ranges of composition,3 all solid phases are represented as stoi-chiometric compounds in the subsequent diagrams. Any error introduced into the calculated equilibria by neglecting the compositional variation of these phases is less than the uncertainty in the thermodynamic data. In a Pourbaix-Ellingham diagram for a three-component system, the phase rule requires that at equilibrium four condensed phases specify a point, three condensed phases determine a line, and two condensed phases define an area. To obtain a well-defined area at high oxygen potentials and teniperatures, the initial carbon to oxygen mole ratio is specified to be more than sufficient to reduce the oxide but not enough to convert all the metal to carbide. Thus, the lowest regions in the subse- quent Pourbaix-Ellingham diagrams represent areas in which the metal and its carbide are the stable condensed phases. Cr-C-O SYSTEM A) Thermodynamic Data. To simplify the subsequent calculations, all thermodynamic data are presented in the form of linear Gibbs-energy-of-formation* equations which were derived for the temperature range 505° to 2000°K and are reasonably accurate over the entire temperature ranges of the diagrams. The thermodynamic data for the compounds occurring in the Cr-C-O system are summarized in Table I. Several volatile chromium oxides have been reported,4 but their influence is negligible in the Cr-C-O system. Thermodynamic data for CO and CO2 were taken from the compilation of Coughlin.5 The only solid chromium oxide sufficiently stable to exist below 1800°K in the Cr-C-O system is Cr2Os.11 The Gibbs-energy-of-formation equation for Cr2O3 was obtained by revising the data tabulated in Coughlin,5 using the heat of formation of ah' and the high-temperature thermal data for chromium.7 In 1953 Richardson8 re-evaluated the original work of Kelley and coworkers,9 who measured the thermodynamic properties of the chromium carbides. However, the high-temperature equilibrium results of Boericke9 yield values for ?G°f of Cr2O3 which are 2 kcal more positive than the accepted data. His results for the chromium carbides are based on the same questionable equilibria. Gleiser10 recently determined the Gibbs energy of formation of Cr3C2 and the equation in Table I was calculated from her data and the thermal data of Kelley and coworkers.9 Thermodynamic data for the Cr7C3 and Cr23C6 carbides were obtained by combining the Cr3C2 data

Jan 1, 1965

By Franklin J. Hill, Theodore D. Tiemann

Sized fractions of Wisconsin Gogebic taconite were reduced with hydrogen over the temperature range from 600° to 1000°C. In general, the degree and rate of reduction increase with temperature. Particle size has no observable effect except in the smaller fractions at 900°C and above, where reduction is impeded, possibly due to the siliceous nature of the ore. Gaseous diffusion appears to be significant as a rate controlling factor at certain stages. THE depletion of high grade iron ore reserves in the United States has established the need to utilize all available iron ore deposits, both in long range planning and from the viewpoint of national emergency. This has led to extensive research and development in this field. The beneficiation of Wisconsin Gogebic taconite ore has been previously studied by investigators at the University of Wiscconsin, 1 the United States Bureau of Mines,, Battelle Memorial Institute, 3 and others. Methods investigated have included concentration by flotation processes, magnetic and gravity separation, magnetic roasting and various combinations of them. The foregoing studies have been concerned with the production of an enriched ore suitable for blast furnace use. If the ore could first be reduced to metallic iron and then beneficiated, the product could be used directly in the open hearth or electric steel-making furnace. The by-passing of the blast furnace should enhance the economic feasibility of the beneficiating process. The work reported here,4 was undertaken to establish data on the hydrogen reduction of Wisconsin taconite that would eventually lead to the development of an economic direct reduction process for this and perhaps other low grade siliceous ores. The volume of work on direct reduction can be judged by the fact that 240 direct reduction processes were patented in the United States alone up to 1951, 5 and numerous additional processes have since been developed. Some of the factors contributing to direct reduction development are: 1) The increasing capital cost of the blast furnace and its accessory equipment. 2) The decreasing availability of high grade domestic ore. 3) The high cost of steel scrap for use in the open hearth and electric furnaces. In general, direct reduction processes can be divided into two types; those using a solid reductant (coal, peat, lignite) usually carried out in a kiln, and those using a gaseous reductant (H2, CO) in a shaft furnace or a fluidized bed retort. As there is no low cost coal readily available in northern Wisconsin but natural gas could be quite easily obtained, it is believed a gaseous reductant process would offer the greater feasibility for use on Wisconsin taconite. It is hoped that this preliminary work will beof interest to other investigators in this increasingly important field. TACONITE ORE The ore used in the investigation was obtained originally from the U. S. Bureau of Mines, and consisted of a representative composite made up from trench samples of the Norrie, Pabst, Plymouth, Pence, and Yale members of the Wisconsin Gogebic range iron formation. Chemically, the ore contains approximately 52 pct SiO, and 30 pct Fe. X-ray diffraction and other studies indicate the principal minerals to be quartz (SiO2), hematite (Fe2O3), and goethite (Fe2O3. H2O). Minor amounts of iron containing silicates, siderite (FecO3), and magnetite (FeO-Fe2O3) are present. The iron minerals and quartz are so finely disseminated that the ore requires grinding to less than 200 mesh (74 µ) for essential liberation.l,2 The iron content of each of the several size fractions studied is shown in Table I. EXPERIMENTAL METHOD The method used throughout the investigation was based on that developed by the U. S. Bureau of Mines in Minneaopolis6,7 in which the course of reduction is followed by the loss in weight of the ore sample. More specifically, a 100-g sample of the size frac-

Jan 1, 1962

By A. Rosen, P. Wynblatt, J. E. Dorn

The temperature, strain rate, and structure dependence of the flow stress in a poly crystalline Fe-2 pct Mn alloy was investigated between 77" and 370°K. It was possible to identify the low-temperature data from 77° to 160°K with Dorn and Rajnak's theory of the Peierls mechanism of plastic deformation. Above 160°K one or more thermally activated mechanisms must he operative; however, these were not identified in this investigation. The mechanistic basis for the rapid decrease in the flow stress of bcc metals with an increase in temperature over the low-temperature range is yet being debated. Various dislocation mechanisms have been suggested in the past but the agreement between the various proposed theories and the experimental results have not been definitive. In the present paper, the authors will demonstrate that the plastic behavior of polycrystalline iron containing 2 wt pct Mn plus interstitials agrees excellently with predictions based on the Peierls mechanism from 77" to 160°K whereas from 160" to about 370°K other as yet unidentified thermally activated mechanisms take over. Undoubtedly, the overlap of these mechanisms with the Peierls mechanism contributed to the difficulties of rationalizing the low-temperature behavior of iron and its alloys. I) EXPERIMENTAL TECHNIQUES AND RESULTS Although extensive data are now available on the effect of temperature and strain rate on the flow stress of various bcc metals and alloys, it was, nevertheless, deemed necessary for the objectives of the present study to obtain highly accurate data of the type most pertinent for checking the theories on a series of well-documented work-hardened states. Iron containing 2 wt pct Mn was used in this investigation in order to obtain a lower ductile to brittle transition temperature than that for iron.' The additional elements present were 0.004 pct C, 0.05 pct 0, 0.004 pct S, 0.003 pct P, 0.006 pct N, and 0.001 pct Si. The as-received 3/8 by 3/4 in. bars were cold-rolled to 0.100-in. thickness, recrystallized under argon for 30 min at 1073"~, further cold-rolled to 0.063-in. thickness, and finally recrystallized under argon for 30 min at 1000°K. This treatment gave a stable reproducible equiaxed grain structure having an average grain diameter of about 90 p. Prior to the final recrystallization treatment, the sheet was machined into tensile specimens 1/4 in. wide having a 1.625-in.-long gage section. All specimens were tested in controlled-temperature baths on an Instron Testing Machine. For convenience in the theoretical analyses the data will be given in terms of the shear stress for flow, 7, the shear strain rate, f, and the shear strain, y. A series of three standard strain-hardened states were obtained by prestraining specimens at 300°K and at a shear strain rate of 7.68 x lo-' per sec to three stress levels of 6.89 X l08, 10.3 X lo8, and 14.5 x 10' dynes per sq cm, respectively. Immediately following this prestrain the temperature bath was changed and each specimen was pulled in tension at either f = 7.68 X lo-' or f = 3.06 X 10"3 per sec. In terms of the accuracy that was achieved, the values obtained did not deviate more than *0.1 X 10' dynes per sq cm and * 1°K from the reported values of stress and temperature and not more than *5 pct in the reported values of the strain rate. The tensile stresses were converted to shear stresses using a factor of 1/2. The shear stress for the initiation of flow at the test temperature was determined by taking a y = 6.16 x 10'3 offset. from the modulus line at which point good accuracy could be achieved in determining y and the associated flow stress 7, with only a negligible increase in the pre-

Jan 1, 1965

By John C. Sawyer

A brief review is given to show that catastrophic oxidation of stainless steel in the presence of lead oxide is similar in many respects to catastrophic oxidation as caused by MoO3 and V2O5, Experimental data are presented to show that lead oxide accelerates the normal oxidation process of stainless steel by chemically altering the normally protective oxide film formed on the base metal. Data are given to show that similar reactions occur during oxidation of stainless steel in the presence of MOO3,and V2O5. THE mechanism by which pure metals oxidize at high temperatures has been the subject of intensive research for many years and much has been accomplished towards understanding the processes involved. The mechanisms by which alloys oxidize have also been investigated, but due partly to the fewer number of investigations and partly to the complexity of the oxide systems present, available knowledge is not as extensive as with pure metals. When oxidation processes are further complicated by atmospheres contaminated with sulfide, halide, or oxide vapors, the knowledge of fundamentals becomes meager or altogether lacking. Thus, it is not surprising to find that the catastrophic oxidation of stainless steels in metal oxide vapors of MOO, and V2O5 is not a well understood phenomenon despite the fact that a number of investigations have been undertaken. The literature in dealing with the subject of catastrophic oxidation is primarily concerned with the effects of MOO3 and V2O5, but does mention that other metal oxide vapors, one of which is lead oxide, appear to promote a similar type of accelerated oxidation. While this latter effect is virtually unknown, the deleterious effect of lead oxide is of considerable commercial importance, as it is believed to be one of the fundamental reasons for exhaust-valve failure in gasoline engines. For this reason studies have been in progress for many years attempting to better understand the mechanism involved. Modern exhaust-valve alloys"2containing 20 to 25 pct Cr plus nickel and/or manganese are in effect high-grade austenitic stainless steels exhibiting ex- cellent oxidation resistance in air at exhaust valve operating temperatures of 1100° to 1700°F; yet these same alloys are prone to corrode during engine service because of the conditions attending their operation. These conditions are such that the valves become coated with deposits of complex lead compounds mainly derived from gasoline additives of tetraethyllead, ethylene dibromide, and ethylene dichloride. Literature searches3-7 and discussions with various investigators show that considerable difference of opinion exists as to the nature of the lead-bearing deposits found on the surface of exhaust valves and the atmospheres to which they are subjected; yet, all seem to generally agree that corrosion, a gradual transformation of alloy to nonmetallic products of corrosion, is a consequence of the presence of lead compounds. This majority opinion seems to be substantiated by laboratory engine tests which show that corrosion does not occur to any appreciable extent when lead-free fuels are used. The first observations of catastrophic oxidation reported in the literature were probably made by pfeil,8 but it was Leslie and Fontana9 who undertook the first detailed study of the phenomenon. Their work was chiefly centered on the acceleration of oxidation which took place when stainless steels containing more than 3 pct Mo were heated in air with restricted circulation. These investigators reported that the presence of other oxides near the surface would further accelerate the rapid oxidation which occurred. While they recognized that the effect was attributable to the presence of molybdenum, it was Rathenau and Meijering" who emphasized the fact that the presence of molybdenum in the alloy was incidental to the presence of MOO3 vapor in the atmosphere surrounding the specimens. Evans,11 as well as Cunningham and Brasunas 12 studied similar

Jan 1, 1962

By M. J. Hordon

Measurements of the 103 yield stress of ordered and disordered poly crystalline Cu ,Au were related to the ordered antiphase domain size determined by resistivity measurements. For undeformed material, a yield stress maximum wa obtained at a critical domain diameter of about 40A. Plastic deformation resulted in a marked increase in the yield stress and electrical resistivity of the ordered alloy compared to the disordered, the strain hardening rate increasing regularly with initial antiphase domain size. Order hardening was accompanied by a sharp reduction in size of the initially large domains. It has been observed that the yield stress of ordered and partially ordered Cu3Au alloy varies sensitively with antiphase domain size aid degree of order.ly2 In addition, ordering of the lattice leads to a marked increase in the strain hardening rate (order hardening) as compared to the rate for the disordered alloy. In the present investigation, changes in the electrical resistivity and yield stress of ordered polycrystalline Cudu with varying initial domain diameters were measured after tensile plastic deformation in order to examine the effect of cold work on the antiphase domain size. EXPERIMENTAL PROCEDURE Au-Cu alloy of 99.99 pct purity analyzing 50.85 wt pct Au-balance copper was obtained from the Handy-Harmon Co., N. Y., in the form of 0.061 in. diam drawn wire. Wire specimens 3 in. in length were given the following annealing treatment in nitrogen: 500" for 72 hr, 820" for 15 hr, and 450" for 5 hr, followed by a water quench. The annealing sequence resulted in a completely disordered structure with a grain size of about 0.2 mm. The disordered specimens were then reannealed at 360' in nitrogen for periods varying from 10 min to 150 hr followed by quenching to produce ordered structures with varying domain sizes. The degree of ordering and variation of domain size was followed by electrical resistivity measurements made at room temperature using a low resistance precision Kelvin double bridge apparatus. The specimen resistance was determined over a length of 4.0 cm between two brass knife-edge contacts while the specimen was immersed in an oil bath to minimize temperature variations. In addition, the current flow in the circuit was minimized by a current pulse technique in balancing the bridge in order to avoid heating the specimen. Using a sensitive galvanometer to detect the bridge null, the accuracy of the resistance measurement Wire specimens were plastically strained in tension with an Instron tensile unit at strain rates in the range 5 x 10"5 sec-' to 2 x 10"4 sec-'. Stress and extension data were fed into the Instron chart drive amplifier to obtain the actual stress-elongation curve from which the yield stress at 10"3 strain was determined. The maximum resolution of the apparatus was approximately 50 psi stress and 3 x 104 strain. At various plastic strain levels, deformation was interrupted and the electrical resistivity determined after removing the stress. RESULTS AND DISCUSSION 1) Yield Strength of Ordered Cudu. In order to determine the effect of the ordered antiphase domains on the initial yield stress, specimens were prepared with varying domain sizes ranging from zero for 5 completely disordered structure to about lo5A for a completely ordered structure by suitable annealing treatment. Domain sizes were estimated by comparing room temperature electrical resistivity data with the original data of Jones and sykes3 as modified by rdle.' In agreement with previous work, the resistivity varied sensitively with domain diameter and degree of order, decreasing from approximately 11.6 x l0- ohm-cm for the disordered structure to about 5.9 x l0- ohm-cm for ordered domains above 10"3 cm in diameter. Fig. 1 shows the change of the 103 yield stress with ordered domain size. It is evident that the maximum

Jan 1, 1963

By R. Grierson, R. N. Parkins

The m.echanica1 properties, at high lzomologous temperatures, of the intermetallic compounds InzBi and Mg17A112 were measured as a .function of temperature, applied strain rate, previous thermal and mechanical history, and composition. Mgl,Al12 was investigated ilz compression, whereas Zn,Bi was investigated in tension. A decrease inflow stress with increasing strain was observed jor both alloys. The results obtained are discussed in terms of the dislocation-multiplication processes in these materials. MANY intermetallic compounds are reported to undergo a brittle-ductile transition at high homologous temperatures.' There is evidence in the literature that some of these compounds exhibit a large yield drop when plastically deformed.'j3 Both of these forms of behavior are shown by the covalent elements germanium and silicon4,5 and also by certain ionic compounds.8 The present work is a study of the deformation, at high homologous temperatures (>2/3 Tm), of two intermetallic compounds, In2Bi and Mg17Al12. InzBi has a disordered hexagonal structure7 (c/a = 0.598) and a solubility range of 32.3 — 33.2 at. pct Bi.8 It has a melting range from 72° to 89°C. Mg17Al12 has an ordered bcc (A12 type)7 structure and exists over the range 50 to 60 at. pct Mg8 with a melting range from 437° to 462°C. We have been unable to find any reference to previous investigations of the mechanical properties of BiIn,. Novikovg has reported that cast samples of Mg17A112 show ductility, when bend-tested, at temperatures above 380°C. EXPERIMENTAL Ingots of In2Bi and Mg17Al12 were melted under an argon atmosphere and cast, in situ, in a graphite crucible. The materials used were of 99.99 pct purity. The alloys prepared contained 66.9 at. pct In in the case of In2Bi and 58.4 at. pct Mg in the case of m17A112. The ingots were homogenized and then extruded. Two-in.-diam Mg17Al12 ingots were extruded at 375°C to give 3/8-in.-diam rod. The rate of formation of this rod was 0.25 in. per min. One-in.-diam InzBi ingots were extruded at 20°C, using a rate of 1 in. per min, to give 1/8-in.-diam rod. In both cases the extruded rod had a recrystal- lized, fine-grain, structure. (For Mg17Al12, d = 11.2 µ; for BiIn2, d = 22 µ.) Mechanical-property determinations were made in a hard-beam machine, in tension in the case of In2Bi and in compression with Mgl7Al12. The tensile tests were on specimens having a gage length of 1.1/2 in. and a diameter of 1/8 in. The compression tests on Ml7A112 were on specimens of 3/8 in. diam by 3/8 in. high and the ends were coated with poly-tetrafluorethylene to minimize friction. RESULTS In2Bi. Fig. 1 shows, particularly at the higher applied strain rates, that In2Bi exhibits a marked yield drop as the deformation increases to about 2 pct, after which the material shows neither hardening nor softening up to 15 pct strain. The magnitude of the yield drop, the stress in the region of flow under constant stress (the stress plateau), and the 0.5 pct proof stress were all dependent upon the applied strain rate according to an expression of the form

Jan 1, 1965

By J. B. Clemmer, P. E. Churchward, C. Rampacek

A cyclic method for processing manganese ores using sodium sulphate as the basic reagent is described. Sodium sulphate is electrolyzed in a diaphragm cell to give an anolyte-containing agentisdescribed.Sodiumsulphuric acid and a catholyte-containing iselectrolyzedincaustic soda, a part of which is carbonated in a cyclic manner to form soda ash. The reduced ore is leached with the anolyte to dissolve the manganese and the impurities are precipitated by addition of catholyte. Manganese in the pregnant todissolvethemanganeseandtheimpuritiessolution is precipitated as synthetic rhodochrosite with a carbonated catholyte, and sodium sulphate is regenerated. Calcining the manganese carbonate gives a high grade product and the carbon dioxide is returned to the carbonation step. The results of laboratory tests using cells equipped with synthetic-fiber diaphragms and permselective membranes, which permit transfer of anions or cations during electrolysis, are described. A METHOD which has been considered for pro-cessing manganese ores under emergency conditions to recover a product suitable for smelting to ferromanganese involves reductive roasting of the ore for leaching with dilute sulphuric acid followed by precipitation of the manganese from the purified pregnant solution with sodium carbonate. Although the process is operable and involves no novel or untried steps, it is noncyclic in regard to reagents. Research seemed warranted to determine if a cyclic process could be developed by electrolyzing the sodium sulphate formed during precipitation of the manganese with soda ash to regenerate sulphuric acid and sodium hydroxide. Reduced ore would be leached with acid anolyte to dissolve the manganese. The iron, alumina, and other dissolved impurities would be precipitated with the caustic catholyte, and the manganese in the purified pregnant solution would be precipitated as artificial rhodochrosite with carbonated catholyte to regenerate simultaneously sodium sulphate for electrolysis. Waste boiler gas and CO, from calcining the manganese precipitate would be recycled for carbonation of the caustic catholyte. There is a surprising lack of data in the technical literature on diaphragm electrolysis of sodium sulphate. One of the more comprehensive papers, by Atwell and Fuwa, describes the problem involved in electrolyzing byproduct sodium sulphate from the viscose process with particular regard to the design and operation of asbestos diaphragm cells. Frisk' also investigated electrolysis of sodium sulphate from viscose-spinning baths to recover caustic soda and sulphuric acid. The objective in these investigations was to produce, by electrolysis and evaporation, a concentrated caustic-soda solution and a sulphuric-acid solution low in sodium sulphate. Because of these requirements, the process was not too attractive despite a favorable yield of caustic and acid with a reasonable power consumption. Because strong acid and base are not required for processing manganese ores and nonelectrolyzed sodium sulphate is not objectionable in either reagent, the present problem was somewhat simpler than that of these investigators. The purpose of this report is to summarize briefly the results of laboratory electrolysis of commercial sodium sulphate in diaphragm cells of different types and the application of the acid and caustic for processing manganese ores in a cyclic manner. Electrolysis in Permeable Diaphragm Cells The principal problem in electrolyzing sodium sulphate in a permeable diaphragm cell is to prevent mixing of the acid and base formed in the anode and cathode compartments. It is not enough to separate the anolyte and catholyte by a single diaphragm. A three-compartment cell in which the sodium-sulphate solution is fed to the center compartment and flows through the permeable diaphragms to the anode and cathode compartments is more efficient electrically. Diaphragms should be porous enough to allow flow of solution to outer compartments but tight enough to prevent gross mixing of the anolyte and catholyte. In addition to being resistant to acid and alkali, the diaphragms should offer minimum resistance to the flow of current. It is also important that the electrolyte contain a high concentration of sodium sulphate to furnish an abundance of sodium and sulphate ions and thereby decrease the current carried by hydrogen and hydroxyl ions. A practical limitation of sodium-sulphate concentration is imposed by the decreased solubility of sodium sulphate with decreasing temperature. At 20°C, a concentration of 200 g per liter sodium sulphate can be maintained. Little is gained in conductivity by using a concentration greater than 200 g per liter. The small-scale continuous electrolysis tests were made in a 12x12 in. open-top bakelite cell equipped

Jan 1, 1956

By A. U. Seybolt, R. A. Oriani

The pressure and composition of the solid solution of nitrogen in chromium has been investigated as a function of temperature. The partial molal heat of solution, the activity of nitrogen in solid solution, and the partial molal free energy have been computed. The enthalpy of three reactions is summarized: N + 2Cr(3) = Cr2N(4), H° = —28,500 cal per mol 1/2N2(p) + 2Cr(8) = Cr2N(3)1 ?HO = —23,500 cal per mol 1/2N2(p) = N, ?H° = 5,000 cal per mol. WORKERS who have investigated the problem of the preparation of ductile chromium have been concerned with the effects of minor amounts of impurities upon this refractory metal. In particular, gaseous impurities such as oxygen and nitrogen have been suspected of causing trouble because of many known cases where brittleness in transition elements has been definitely traced to these elements. In order to evaluate the possible effects of the nitrogen impurity in chromium, it appeared desirable to learn something of the dependence of the nitrogen solubility upon temperature and pressure. Previous Work Maier3 in 1942 in his treatise on sponge chromium reviewed the thermodynamics of the chromium nitrides Cr2N and CrN, both of which are well-estab- lished compounds, but which apparently have not been studied in much detail. Maier presented some free energy-temperature expressions for the reactions 2 Cr,N = 4 Cr + N2 [1] and 4 CrN = 2Cr2N + N2 PI based mainly on the work of Satoh2 and Sano." Pearson and Ende3 in 1953 briefly reviewed the thermodynamics of Cr-N using the same data available to Maier, and also derived a free energy-temperature expression for reaction 1. Of the two nitrides mentioned previously, the present investigation was only concerned with Cr,N, since this nitride is in equilibrium with the metal phase, at least over most of the temperature range, Blix4 in 1929 established the structure of Cr2N (close-packed-hexagonal) by X-ray diffraction methods, and indicated that its homogeneity limits extend from 11.2 pet to 15.1 wt pet N. At a temperature of 1200°C, 38 mm Hg from the Maier expression and 43 mm Hg from the Pearson

Jan 1, 1957

By W. J. Skewes, C. T. Holland

Properly constructed stopes are necessary underground for proper ventilation and safe, healthful working conditions. Mining companies are concerned with providing the best possible stoppings at an economic cost. It is important to consider 1) proper materials, 2) construction that ensures maximum performance from the material used, and 3) keeping costs within reasonable limits for the unit operation—stopping—involved. The authors investigated all aspects of the problem and have attempted to layout a study program to provide information on all phases. Mining companies every year purchase huge amounts of material for the construction of ventilation stoppings. This material by the time it is in place in the stoppings will cost the company many thousands of dollars. In addition and more importantly these stoppings are supposed to confine air travel along certain well defined paths into areas where it is needed to provide safe and healthful atmospheres for workmen. The cost of forcing this air through the mine is large and in general increases as the total quantity increases. Consequently, if the stoppings leak, increased cost results and in addition unsatisfactory ventilation may prevail in the mine. Therefore, it is essentia1 to provide the best possible stoppings at an economic cost. When attempting to provide the best stoppings possible at an economic cost, three aspects of the problem must be considered. These are 1) getting the most suitable material for stopping constructions, 2) constructing the stopping so as to get the best performance from the material used, and 3) keeping the cost of stopping construction to a minimum for a suitable stopping. This investigation is concerned with all phases of the problem and has attempted to lay out a study to provide information on all of them. In order to develop information on the best stopping material available it seemed wise, after con- sidering the job a stopping must do, to investigate the following aspects of material used for stoppings: 1) strength in compression, 2) compressibility or yield under load, 3) porosity, and 4) permeability. To provide information on the best manner of construction the following aspects of air leakage through the stopping were investigated: 1) when the stopping is built of dry stacked materials—i.e., the joints are not mortar-laid (See Fig. 1); 2) when the stopping is built of dry stacked material and then plastered on one side (see Fig. 2); 3) when the

Jan 1, 1961

By J. A. Ede

The object of the writer is to call attention to a rather unique aggregation of economic products distributed over a line of succeeding formations about 3 mi. long, to be seen within a few miles of La Salle, Ill. Fig. 1 is an ideal section of the stratification exposed and exploited along a distance of 3 1/5 mi. in a southwesterly direction from the quarry of the Utica Hydraulic Cement Co. located near the historic site of Kaskaskia village to the Oglesby shaft at Oglesby. No attempt has been made to cover the whole field, special mention only being made (with the exception of two places) of the operations found along the course or parallel to the direction assumed in the ideal section. I have used Fig. 2, after J. R. Bent and De Witt Kelly, to locate the relation of the La Salle anticline to the coal mines of this district and to show the operation of No. 1 and 3 mincs of the Illinois Zinc Co. Anticline and the Rock Formations Owing to the structural deformation between La Salle and Utica, the older rocks of the state are exposed to the surface along the northern embankment and the bottoms of the Illinois River valley near the latter place. At; the Illinois Zinc Co. works, Sec. 16, Tp. 33, R 1, a well for water mas sunk 1828 ft. and samples taken every 10 ft. of the ground penetrated; duplicates were sent to Mr. Cady of the Illinois Geological Survey. A general compilation or synopsis study of this section is here presented. As the well is over 1 mi. west of the Western limb of the anticline, the section affords some reliable data. These samples were studied and interpreted by H. M. DuBois as Lower Magnesian, and by G. H. Cady as the Lower Magnesian. The results are given in Fig. 3. The most interesting geological feature of this district is the La Salle anticline. In 1865, Leo les Quereux, looking at Split Rock, asked how it happened that the upper coal measures overlie strata of the Lower Silurian and what has become of the formations which are generally found intermediate—the Upper Silurian, the Devonian and sub-carboniferous, and the lower member of the coal measures?

Jan 1, 1920

By C. D. Dolman

Since the outbreak of the war we have discovered in the united States minerals of which there was no general knowledge, and which compared very favorably with anything that could be found in any foreign country. One of these was magnesite, or the carbonate of magnesium as it occurs in nature. This mineral crystallizes in the rhombohedra1 form, has a specific gravity of 3.00, molecular weight of 84.4, molecular volume of 28.1, and a hardness of 3.5 to 4.5.1 Had it not been for the development of the California deposits of this mineral and the discovery of immense new deposits in Stevens County, Wash., the production of steel during the war would have been more seriously handicapped than it was. Now that the war is over, we face the possibility of competition with the cheap Austro-Hungarian magnesite; and while that may not be so cheap as it was before the war, adequate protection should be given the producers in this country to insure the full development of our own resources. The consumption of magnesite in the United States in 1913, the year preceding the war, was 172,591 tons of calcined and 22,872 tons of crude magnesite. Less than 3 per cent. of this amount was produced at home. At the present time, practically all of the magnesite used in the United States is produced at home. Expensive plants have been constructed, extensive exploration work done, and production pushed to the utmost to supply the necessary requirements of the war. Thus a considerable industry has been built up within our borders. Some magnesite has been imported from Canada and Mexico, but the Canadian ore was of an inferior grade and could not be used satisfactorily. During the year 1918, production decreased in both the United States and Canada; the production in the United States was 225,000 tons in 1918 as against 315,000 in 1917, and in Canada 39,365 tons in 1918 as against 58,090 in 1917. This decrease was mainly due to over-production during 1917, the domestic demand being only 300,000 tons. The material produced and sold in the United States must contain, in the crude form, not more than 3.5 per cent. silica and 2 per cent. lime;

Jan 1, 1920