By E. T. Turkdogan, Klaus Schwerdtfeger

OelSEN and Maetz1 detected some 20 years ago the existence of a miscibility gap in iron oxide-CaO-P2O5 slags melted in iron crucibles at about 1400°C. Because of the importance of this system for the dephos-phorization of steel in the basic Bessemer process, equilibria between liquid iron and selected iron oxide-CaO-P2Q slags have been measured since by numerous investigators.2-5 When in equilibrium with metallic iron, the iron oxide of the slag is present mainly as FeO. In connection with oxygen-blowing steelmaking processes, it is useful to know the phase relations in the slag system at higher oxygen pressure, when major parts of the iron oxide are present as Fe2O3. This problem was investigated by Turkdogan and Bills7 by equilibrating the oxide mixtures contained in platinum crucibles with CO2-CO mixtures at 1550°C. It was found that increasing the Fe2O3 content decreases the composition range of the miscibility gap strongly so that the miscibility gap has almost disappeared at pco2/pco = 75. This result was refuted by the careful work of Olette et a1.,''' who equilibrated their slags with controlled Ha-H2-Ar gas mixtures. Their equilibrium measurements, at 1600°C and at oxygen pressures of 5 x 10"* and 10"5 atm, showed that the oxidation state of the iron has almost no influence on the formation of the miscibility gap. The present experiments were undertaken to check the previous results of Turkdogan and Bills. The experiments were performed at 1625°C in the strongly oxidizing atmosphere of air (PO2 = 0.20 atm) for which no experimental data are available. About 10 g of slag were melted in platinum crucibles and held at constant temperature for 1 hr. After equilibration, the crucible was rapidly pulled out of the furnace and cooled in air. The platinum crucible was removed from the sample. The two slag layers were carefully separated with a small diamond disc, and the surface of the top layer, which may have changed its oxidation state during cooling, was removed. The slags were crushed and analyzed chemically for CaO, P2O5, Fe2+, and Fetotal. The starting mixtures were prepared by sintering the desired amounts of reagent-grade 2CaO . P2O5 - H2O, CaCO3, and Fe2O3. Sintering and subsequent crushing were done three times to ensure homogenization. Molybdenum wire resistance heating was used. The furnace was provided with a recrystallized alumina reaction tube which was left open to air at the top. The temperature was controlled electronically. The reported temperature was measured with a Pt/Pt-10 pct Rh thermocouple and is estimated to be accurate within +5°C. The composition of the equilibrated melts is given in Table I. For the graphical illustration of these quaternary slags the type of projection suggested by Trömel and Fritze10 was used. In this representation, Fig. 1, the composition point of a mixture within the tetrahedron Fe2O3-CaO-P2O5-FeO is projected into the Fe2O3-CaO-P2O5, triangle (triangle I) so that the direction of projection is parallel to the side FeO-Fe2O3, and into the triangle Fe2O3-P2O,-Fe0 (triangle 11) so that the direction of projection is parallel to the side CaO-P2O5, of the tetrahedron. The projected point has the coordinates wt pct CaO, wt pct P205, and wt pct (FeO + Fe2O3) in triangle I and wt pct FeO, wt pct Fe2O3, and wt pct (CaO + PzO5) in triangle 11. Both triangles are turned into the same plane around the Fe203-P20, side of the tetrahedron. An illustration of the projection of a quaternary point in the present system is shown in Fig. 1. The advantage of this type of projection is that all four components for an equilibrium curve can be read directly from the diagram. The present results are shown graphically in Fig. 2. The curves depicting the miscibility gap are dashed in parts where no experimental points were obtained. The composition range covered by the miscibility gap

Jan 1, 1968

By J. H. Swisher

The solubility of graphite in CaO-S2O2-Al,O3 slags was measured by equilibrating slag samples with graphite crucibles and CO gas. Carbon contents as high as 2 ut pct were obtained in CaO-saturated, CaO-A1,O3 slags, and 1.3 wt pct in slags of the composition CaO.Si0,. Although the observed conditions for Sic formation were in agreement with those predicted from thermodynamic data, CaC, was found to form at a lower temperature than predicted frotn thermodynamic data. From measurements of the equilibrium carbon content as a function of CO Partial pressure, it was found that carbide ions dissolve in CaO-A12O3 melts with a valence of minus two. The carbon content increased with CaO concentration in Ca0-Al,O3 melts and increased with SiO, content along the CaO'AlO3-CaOSi0 join in the ternary system. When solid CaC2 was added to CaO-A12O3 and CaO-SiO2-A12O3 slags, it was found that one of the oxides in the slag was reduced by the carbide (Al2O3 in the forrner and SiOz in the latter). In electric furnace steelmaking, a double-slag practice is frequently used to meet alloy specifications. Initially a flush slag, which is oxidizing in nature, is used to remove phosphorus and carbon from the steel bath. Later in the refining period, the flush slag is replaced by a highly reducing carbidic slag. When calcium carbide is formed in or added to a finishing slag, the slag is effective as a desulfurizing agent and also permits alloying elements such as chromium, vanadium, and tungsten to be added to the slag in the form of oxides. The oxides are readily reduced by calcium carbide, thereby minimizing the use of expensive ferroalloys. More work has been done on the thermodynamics of silicon carbide in slags than on calcium carbide. Baird and alor' and Kay and alor' determined the free energy of formation of Sic by measuring the partial pressure of CO in equilibrium with solid silica, silicon carbide, and graphite. Using a similar technique, they determined SiOz activities in CaO-SiOz and Ca0-Si0,-A1203 slags. Rein and chipman3 also determined the free energy of formation of Sic using slag-metal equilibrium measurements. A literature survey has uncovered only one experimental study of the behavior of CaC, in slag systems. Shanahan and cooke4 report the results of some preliminary experiments on the solubility and stability of CaC, in a CaO-A1,03 and a Ca0-Si0-A1,03 slag at a temperature of about 1500". The carbon solubility as CaC, in a slag containing 50 pct CaO and 50 pct A1203 was reported to be 0.6 pct. They also review earlier work on the binary CaO-CaC, system. A eutectic exists in this system, but various investigators disagree on the eutectic temperature and composition. eal has given an explanation for carbide furnace erruptions in terms of the thermodynamic properties of CaC,; his analysis is not based on experimental data, but on compiled data for the free energies of formation of CaC, and CO.' , These data for steel-making temperatures are all extrapolated from the results of low-temperature measurements. In the experiments described in this paper, slag samples were equilibrated with graphite crucibles and with mixtures of CO and argon or with CO gas at 1 atm total pressure for measurement of the carbon solubility. Most of the work was done on Ca0-A1203 binary slags, although in some experiments CaO-SiO, and Ca0-Si0,-A1,03 slags were used. EXPERIMENTAL Slag samples of the desired composition for the solubility measurements were obtained by blending pre-fused master slags. The master slags were prepared by fusing mixtures of reagent-grade CaC03 with either A1,03 or Si0, in a graphite crucible. The master slags were crushed, then decarburized in air in a muffle furnace at 1200O C. A schematic diagram of the apparatus is shown in Fig. 1. The source of carbon for the solubility meas-

Jan 1, 1969

By J. Stuart Warner

The reaction COSO4(c)?CoO(c) + So3(g)was investigated from 950° to 1170OK by two different methods. The sulfate was decomposed in a previously evacuated space and Pso3 calculated from the measured total pressure on the assumption that Pso2 = 2P02. The sulfate was also decomposed under conditions of controlled oxygen pressure. The difference in the results obtained by these experimental techniques is attributed to the effects of thermal diffusion. The standard free energy change for the reaction is given by ?F° = 66,292 + 17.273T log T — 102.57 T (±300 cal/mole). It was found by DTA and X-ray diffraction studies that CoS04 undergoes a transformation at 617°± 4°C. THE metal sulfates may decompose directly to the oxide or pass through one or more intermediate basic sulfates. Provided the oxidation state of the cation does not change in the course of the reaction, the decompositions may be described in general as follows: One of the major objectives of this work was to determine the validity of Eq. [3] as much of the existing sulfate data has been calculated from decomposition pressures by Eq. [5]. The type of apparatus generally used for these measurements consists of a reaction vessel at high temperature which communicates with a manometer at room temperature. A temperature gradient is thus imposed on the gas phase causing thermal diffusion which brings about a partial separation of the different gaseous species present in an initially uniform mixture. The basic theory and experimental facts associated with this phenomenon are summarized elsewhere1 and it will suffice to state here that the heavier gaseous species diffuses down the temperature gradient. Since thermal diffusion destroys the homogeneity of the gas phase, it is not necessarily true that Pso2 = 2Po2 in any particular volume element of the gas phase even though there are twice as many molecules of SO, as of 0, in the gas phase considered as a whole. Under these conditions, the decomposing sulfate gives off SO, which dissociates to SO, and 0, and all three species are distributed throughout the system by thermal diffusion. However, the sulfate will continue to dissociate until the equilibrium value of PSo3 is established on the hot zone. Thermal diffusion may distribute SO2 and O2 throughout the gas phase in any way so long as Eq. [2b] is satisfied in the hot zone; i.e. Pso2(Po2)1/2=K3pso3. When a steady state is reached, we can characterize Pso2 in that

Jan 1, 1962

By A. Cochardt, D. H. Feisel

HE success of the sintered aluminum powder material (SAP)' in raising the maximum useful temperature of aluminum alloys has stimulated effort in investigating similar systems in which the metallic matrixes have higher melting points. Examples of such systems which have been studied are nickel-alumina,2, 3copper-silica,4 copper-alumina,4 titanium-cerium oxide,5 and 80/20 nickel-chromium,8 cobalt,= and molybdenum7 matrixes with various hardeners. Conventional precipitation-hardened high-temperature alloys are often thermally unstable in service. The original fine particles that are responsible for good strength properties grow in size at elevated operating temperatures, a process termed "over-aging." This growth of precipitated particles causes a gradual loss in strength properties. A previous paperb describes the factors that govern the process of overaging, and estimates the time required for overaging of a nickel-alloy matrix dispersion-hardened by various precipitates such as are found in current high-temperature alloys, and by alumina. These calculations indicate that nickel-base alloys hardened with Ni3Al, Tic, or TiN are quite unstable at 1340" F (727°F). Such alloys should overage within a few hours at that temperature. A nickel-base alloy hardened with alumina, on the other hand, should behave differently. It should not overage appreciably within a thousand years. It was further shown8 that the thermal stability of the oxide-hardened alloy is mainly due to the low solubility of oxygen in equilibrium with alumina in the nickel-base matrix. Since the oxygen solubility is small, little oxygen can diffuse, and structural changes require very long times. This paper illustrates the effects of time and temperature on the structural stability of nickel alloy matrixes hardened by dispersions of Ni3A1, Ni3Ti, Tic, and alumina, and of nickel-chromium matrixes hardened by alumina. Hardness measurements and metallography have been used as a measure of structural stability. EXPERIMENTAL PROCEDURE Using the best information from published phase diagrams,'-l4 compositions of the Ni-Al, Ni-Ti, and Ni-Ti-C alloys were determined so as to have 5 vol pct of precipitate at 1350° F(732°C), the temperature selected to illustrate the effect of time on structural stability. Table I lists the chemical compositions of these alloys. Standard laboratory melting and alloying techniques were used in preparing ingots of the F-Series of alloys. The cast ingots, 1 3/4 in. in diam, were forged to 3/8-in. diam rods.

Jan 1, 1960

By M. G. Benz

The superconducting performmce of diffusion-processed Nb3Sn is influenced by its micro structure. High isotropic transverse current density may be achieved in this material by a process which forms a precipitate of ZrO, within the Nb3Sn. FOR an ideal type-I1 superconductor, little or no transport current can be carried in the mixed state; i.e., little or no transport current can be carried above the lower critical field H,,, where the field penetrates abruptly in the form of current vortices or fluxoids, even though full transition to the normal state does not occur until the upper critical field H,,.' Fortunately, nonideal type-I1 superconductors can be readily obtained and these carry large transport currents up to the upper critical field H. Both theoretical and experimental investigations have attributed this current-carrying capability for nonideal type-I1 superconductors to pinning of the fluxoid lattice by heterogeneities in the microstructure of the superconducting material. These heterogeneities may take the form of dislocations or dislocation clusters,2"5 grain boundaries: structural imperfections introduced by phase transformations; radiation damage,8"10 or precipitates.11"15 Nb3Sn formed by diffusion processing is a type-I1 superconductor. Heterogeneities are needed for high superconducting critical currents above H,,. This paper will cover: a) what the microstructure of diffusion-processed NbSn looks like; b) what changes in the microstructure take place when the system is doped with precipitates, and c) how these changes in microstructure influence the superconducting critical currents. EXPERIMENTAL Preparation of Samples. Diffusion processing was used to form the Nb3Sn. The procedure used was as follows: a) coat the surface of a niobium tape with tin; b) heat-treat this tape at a temperature above 930°C to form a layer of Nb3Sn at the Sn-Nb interface. Such a layer of NbsSn is shown in Fig. 1 The thickness of the NbsSn layer formed was controlled by the time and temperature of the heat treatment. The same general procedure was used for preparation of both undoped samples and samples doped with a precipitate. An additional step was included in the preparation of the doped samples which consisted of internal oxidation of zirconium to form ZrOn. The details of the doping process will be reported in a later paper. Sample Testing. The Nb3Sn tape samples were soldered to a copper or brass shunt. Current and voltage leads were then attached to the sample in the usual four-probe resistance measurement configuration. The sample was cooled to 42°K. In some cases it was cooled in the presence of a high magnetic field and in other cases with the field turned off. The results were the same for both cases. The samples were oriented in a configuration with field transverse to current but could be rotated such that the angle between the field vector and the wide side of the tape sample could be changed. Measurements up to 100 kG were done in a superconducting solenoid and measurements above 100 kG in a water-cooled copper magnet at the MIT National Magnet Laboratory. Once the test field was reached, the current in the sample was increased until voltage was detected across the sample. The critical current was taken as the current at which voltage was first detected in excess of background noise. In most cases this was 1 to 2 x 10~6 v for a— in.-wide sample carrying several hundred amperes with a in. separation between voltage leads and with a 10 "-ohm shunt resistance. RESULTS AND DISCUSSION Microstructure. Examination of the microstructure of the undoped Nb3Sn shows rather large-diameter (1 to 2 columnar grains growing outward from the niobium surface toward the tin surface. As the layer is made thicker by longer diffusion times, these grains grow longer. Few new grains are started. Transmission electron microscopy shows little or no second-phase material within the bulk of the Nb3Sn layer. The microstructure of a diffusion-processed NbsSn layer changes quite drastically when the system is doped so as to form a precipitate within the NbsSn layer. Instead of large-diameter columnar grains of NbaSn forming, smaller-diameter (0.5 to 1 ) equiaxed grains of Nb3Sn decorated with the precipitate form. Fig. 2 shows a transmission electron micrograph of a Nb3Sn layer doped with zirconium oxide. This layer has been etched so that one may look between the grains

Jan 1, 1969

By J. F. Kemp

PAGE I. Introduction,.......269 11. Topogmphical Features,.....270 III. Geological Relations of the Mineralized Area,.272 1. Structural Features,.....272 2. Occurrence of the Copper,....274 3. Granite-Contacts,.......274 IV. Descriptions of the Rocks,.....274 1. Granite,........274 2. Limestone,.......276 3. Porphyritic Eruptions,.....278 (a) Quartz-Porphyry,.....278 (b) Trachyte-Porphyry,.....280 V. Contact Phenomena,......285 1. Comparative Immunity of the Limestone, . 285 2. Contact Phenomena in the Quartz-Porphyry,.... 285 3. The Form and Distribution of the Ore-Bodies,290 VI. Method of Deposition,......293 I. Introduction. The White Knob copper-deposits are situated about three miles south of Mackay, on the Salmon River branch of the Oregon Short Line Railroad, in Custer county, Idaho. An outline-map of this district is given in Fig. 1. The deposits have been known and spasmodically worked for many years, and a total of over 3.5 miles of tunnels, shafts and other workings has been driven with a view to their development. These extensive excavations have exposed the deposits sufficiently to permit a careful geological examination. The peculiar features which give special interest to this paper are the branching, tree-like form of the ore-bodies; the absence of zones of secondary enrichment in the partly oxidized pyritic deposits, and the fact that while the deposits are associated in a general way with the contact of an eruptive rock with limeetone, which it penetrates, the garnetization has taken place not in the limestone, as is the usual case, but in the igneous

Jan 1, 1908

By Alden Greninger

TWINNED metal crystals are usually designated as either deformation twins or annealing twins. If twins are to be classified according to the treatment the metal has undergone just prior to the obser vation of the twins, there are two other possible groups: (1) solidification twins,? when observed in the as-solidified or as-cast condition, and (2) transformation twins, ? when observed in a metal which has been cooled from above an allotropic transformation temperature. McKeehan has demonstrated that ferrite does, occasionally at least, contain twinned structures2. The twins, which he studied by optical methods, were obtained during the preparation of iron single crystals by very slow cooling through A3. He proved that the twin relation was actually that which previous investigators had predicted; namely, twinning along three planes of the form {112}. Since McKeehan's discovery, little or no attention has-been given to this transformation twinning of alpha iron, or to the possibility that it might occur at all speeds of cooling from above A3 instead of merely during the prepara-tion of single crystals. McKeehan's twins were evidently regarded as interesting only in proving that a body-centered cubic metal could form twinned structures-at least under certain conditions. It is generally believed that iron seldom if ever forms annealing twins. Certainly the straight-line banding which is so abundant in annealed face-centered cubic metals is characteristically absent in iron annealed below A3. However, O'Neill3. has studied "twin-like" crystals in annealed alpha iron and concludes that the specimen he studied actually

Jan 1, 1936

By William M. Barret

In order properly to evaluate the data related to geomagnetic surveys, it is highly desirable to have all the available information concerning the magnetic properties of the involved media. This is true of surface as well as subsurface formations and becomes of increasing importance as advancement in instrumental and interpretative technique permits the analysis of relatively slight magnetic reflections of buried masses. Since the magnitude and areal distribution of the usually complex resultant magnetic field at the surface of the earth is a function of the susceptibility1 of the involved matter, it necessarily follows that susceptibility determinations will afford valuable data for geophysical correlation. The present method was developed to meet the need for routine analysis of specimens in the geomagnetic laboratory where it was felt that general utility, ruggedness, ease of manipulation and reproducibility of results were of greater importance than extreme sensitivity. Electric Circuits The electric circuits are illustrated diagrammatically in Fig. 1. Current from the battery, B, passes through the variable resistance R1, reversing switch S1, double-break key K1 to switches S2 and S3. From S2 it flows through variable resistance R2, ammeter A2, to the primary coils of the fixed mutual inductance Mf and variable mutual inductance M,. . From S3 it passes through variable resistance R3, ammeter As, to the primary winding of the fixed mutual inductance MI, which is designed to receive the test sample. The ballistic galvanometer2 or fluxmeter3 G is connected in the circuit containing the double-break key

Jan 1, 1932

By G. A. Crowe, W. T. Bishop

WHILE the literature in the United States on general polarographic technique is extensive, very little appears to be directly applicable to the analysis of flotation tailings. For this reason, it seemed worth while to present a few polarographic methods of ore analysis that have been in constant use in the laboratories of the Hercules Experiment Station for the past few years. At the time of our initial investigation of the polarographic method, there was little or no mention of its specific application to flotation tailings. It was therefore necessary for us to establish suitable conditions for the analysis of our flotation tailings and to consider possible interfering constituents. The polarograph, or dropping mercury electrode, method was discovered in 1925 by J. Heyrovsky and M. Shikata,1 of the Charles University, Prague. This method has since received extensive development and the literature contains many articles on the use of the polarograph for the quantitative determination of metals as well as anions, oxygen in solution, and reducible organic compounds. Kolthoff and Lingane,2 by the publication of their book, "Polarography," in 1941 did much to advance the knowledge and use of the polarograph. In chapter 25 of that book, methods for the polarographic analysis of brass, steel and iron products, alloys, and zinc ore are given. Aluminum,3 cadmium,3.4 cobalt,4 copper,3-9 gold,10 iron,3,11 lead, 3,12,13 molybdenum," nickel,4.8,9 tin,15 and zinc3,4,5,7 in ores have been analyzed by the polarograph. However, most of the work on tailing samples has been published in Russian journals and translations are not yet readily available. In this paper we will describe the method that was developed and used in our laboratory for the determination of copper, zinc, and lead in flotation tailings. PRINCIPLE OF THE METHOD The polarograph is an instrument for applying a potential to a mercury pool and a dropping mercury electrode separated by a solution, and for measuring the resultant electrical current. The procedure is essentially a small-scale electrolysis, in which the voltage required to reduce or oxidize the material identifies it qualitatively and the current measures the concentration quantitatively. Different constituents in a sample may often be determined simultaneously provided they reduce at sufficiently different voltages. An example is the determination of copper and zinc in the same solution. The reduction potentials are quite far apart, as shown in Fig. I. The polarographic method is particularly useful in the range of concentration between those normally determined by spectographic and chemical methods. In

Jan 1, 1946

By Enid C. Plante

INTRODUCTION To extend our knowledge of the flotation behavior of sulphide minerals, the response of the following minerals to ethyl xanthate as collector was studied by captive bubble and cylinder flotation tests: antimonite (Sb2S3), arsenopyrite (FeAsS), covellite (CuS), marcasite (FeS2), orpiment (As2S3), pyrrhotite (FeS) and tetrahedrite (4CU2S, Sb2S3). Lollingite (FeAs2) was also examined to determine if its behavior could be correlated with that of pyrite or marcasite (FeS2). EXPERIMENTAL METHOD Mineral for Flotation and Contact Tests Mineral was prepared in the manner already described' and its behavior both freshly ground and "oxidized" was studied. Tests in which the mineral was allowed to oxidize for various periods showed that a uniform response to xanthate was reached in two days or less. Oxidation Products The soluble oxidation products from most of the above minerals were measured and their effect on the flotation of the mineral studied. The mineral samples were wet ground to minus-52 mesh and deslimed, and 20 g of this material placed in 200 ml of distilled water of a measured pH value, and C02 free air bubbled through each suspension at a constant rate (about 1 bubble/sec) for 5 days. It has been shown1 that the size of the mineral is unimportant in the rate of formation of oxidation products and that probably the supply of oxygen to the mineral is the rate-determining step. At the end of 5 days the pH value of the supernatant liquid was measured again, the mineral filtered off and the soluble products determined. Methods for estimation of sulphur acids, ferrous and ferric iron and copper have already been described.1 No satisfactory method was found for antimony. Arsenic was estimated as the arsenate.2 FLOTATION OF "UNOXIDIZED" MINERALS WITH ETHYL XANTHATE AS COLLECTOR Fig I to 3, 4, 6, show the effect of alkali and cyanide as depressants for the minerals with 25 mg potassium ethyl xanthate per liter as collector at 35°C. Wark and Cox3 have shown that with ethyl xanthate as collector, galena, pyrite and chalcopyrite show a greater tolerance to cyanide and hydroxyl ions at room temperature than at 35°C. Covellite (Fig I), marcasite (Fig 2) and pyrrhotite (Fig 3) behave similarly. The independence of the curves for pyrrhotite at 35°C with respect to cyanide

Jan 1, 1947

By J. A. Ede

THE object of the writer is to call attention to a rather unique aggregation of economic products distributed over a line of succeeding formations about 3 mi. long, to be seen within a few miles of La Salle, Ill. Fig. 1 is an ideal section of the stratification exposed and exploited along a distance of 3 1/5 mi. in a southwesterly direction from the quarry of the Utica Hydraulic Cement Co. located near the historic site of Kaskaskia village to the Oglesby, shaft at Oglesby. No attempt has been made to cover the whole field, special mention only being made (with the exception of two places) of the operations found along the course or parallel to the direction assumed in the ideal section. I have used Fig. 2, after J. H. Bent and De Witt Kelly, to locate the relation of the La Salle anticline to the coal mines of this district and to show the operation of No. 1 and 3 mines of the Illinois Zinc Co.

Jan 9, 1919

By B. G. Bunting, D. L. Abata, J. Robb, J. H. Johnson

Toxic gases produced by the detonation of six explosives were measured in an underground hardrock metal mine during mining operations. The explosives included two semi-gelatin dynamites, three slurry explosives, and an ammonium nitrate, fuel-oil/ammonia dynamite combination. Explosives were detonated at the face of a drift and toxic gases produced by the detonation were trapped at the end of the drift by a bulkhead located a short distance away from the face. Toxic gas concentrations were then measured with direct readout instruments and together with the containment volume, the toxic gas volumes per mass of explosive were calculated. Toxic gas measurements were found in the following ranges (ft3/1bm): NO, 0.0100-0.035; N02, 0.003-0.019; CO, 0.08-0.30; SO2, 0.00-0.05; and CO2, 0.7-1.8. Results showed that toxic gas production (ft3/lbm) correlated with the densities (kg/m3) and energy densities (kJ/kg) of the explosives tested.

Jan 1, 1983

The Hurghada field is still the major producing field in Egypt. There was almost no activity in the Abu Durba field during 1936 and no new evidence is available. The following table summarizes the information on the Hurghada field for the year 1936. Hurghada Field Age of field to end of 1936, years.................... 23 Producing area for gas and oil, acres................. 1,050 Barbels Total oil production to end of 1936.................. 29,046,572 Total oil production during 1935.................... 1,212,182 Total oil production during 1936.................... 1,218,708 Daily average during November, 1936............... 3,249 MillionB CU. Ft. Total gas production (Aug. 1925 to end of 1936)...... 3,966 Total gas production during 1935................... 278 Total gas production during 1936................... 280 Maximum daily in 1936............................ 0.9 Number of producing wells completed to end of 1936... 94 Number of producing wells completed during 1936. ... 3 Number of wells abandoned during 1936............. 3 Producing wells at end of 1936...................... 768 Average depth of bottom of producing wells, ft....... 1,720 Average depth of top of producing horizon, ft......... 1,598 Character of oil, approx. average during 1936: Gravity at 60' F., 0.900; base mixed. Character of gas, approx. average during 1936: gallons gasoline per 1,000 CU. ft., 6.2. Producing rock (main): Nubian sands, Cretaceous; character, sand rock and sandy shales. 1 The figures given by the author were in tons. A conversion factor of 6.98. based on 0.900 sp. gr., was used to obtain the number of barrels.—Ed. 2 All pumping.

Jan 1, 1937

By S. Nenno, T. Saburi, Y. Mizutani, M. Yomarnoto, K. Komatsu

In the equilibrium phase diagram of the Ni-Mo sys-tem1,2 available at present, intermetallic compounds (or ordered phases)ß(Ni4Mo) and ?(Ni3Mo) are known to exist to the nickel rich side. In our recent investigations on Ni-Mo alloys, however, it has been found that the quenched alloys from the high temperature region containing more molybdenum than the Ni4Mo do not decompose directly into 0 and when annealed isothermally below the peritectoid temperature, i.e., 865°C. This note is to report the existence of Pt2Mo type superlattice (possibly ordered Ni2Mo) as a metastable phase in the early stage of decomposition. Alloys containing 20.1, 22.7, and 24.4 at. pct Mo were prepared by vacuum-melting electrolytic nickel of 99.9 pct purity and molybdenum powder of 99.9 pct purity in an alumina crucible. From the resulting ingots, sheets 0.3 mm thick were obtained by forging, hot-, and cold-rolling. The sheet specimens were water-quenched from ! region and subsequently annealed for various periods of time at temperatures below the peritectoid temperature. On these specimens were made optical-microscopic and transmis-sion-electron-microscopic observations. Fig. 1- Optical micrograph of the 22.7 at. pct Mo specimen annealed for 100 hr at 700°C after quenching. (ß + ?) region, B, nucleated along a grain boundaries are invading the preexisting (ß + Ni2Mo) region, A. Details of A are observable only by electron microscopy. Etchant: 60 pct HNO3-40 pct CH3COOH.

Jan 1, 1970

By G. Gutierrez, D. A. Elgillani, M. C. Fuerstenau

The zero-points-of-charge of apatite, calcite, and fluorite are pH 6.4, 10.8, and 10.0, respectively. Scheelite is negatively charged above at least pH 3. In this article, the flotation responses of these minerals in the presence of potassium oleate and sodium silicate are described and compared with electrokinetic data. Colloidal silica appears to be the species principally responsible for calcite depression, while silicate anion is the species responsible for fluorite depression. Additions as high as 1 x 10-3 mole/liter silicate have no effect on the flotation responses of apatite and scheelite. Selective flotation of nonmetallic minerals is difficult to achieve with fatty acids or soaps by themselves. As a result, specific reagents are added to aid these separations, and one of the reagents commonly employed for this purpose is sodium silicate. Flotation separations of various calcium-bearing minerals such as fluorite from calcite1-3 and scheelite from calcite2,4 and apatite,2,5 for example, almost always involve the use of sodium silicate. The mechanisms by which sodium silicate functions as a depressant are still not understood, probably for a number of reasons. For one thing, the dissolution process of sodium silicate is complex, giving rise to a number of ionic and colloidal species.' Moreover, the type and concentration of these species depend on the ratio of Na2O to SiO2, the concentration of sodium silicate, and the pH of the system.' At the present time, it is not known which species, colloidal silica or silicate anion, is responsible for depression. If colloidal silica is the species that is adsorbing, then adsorption must occur by electrostatic attraction between the colloid and the mineral surface. Silicate anion, on the other hand, may adsorb either physically or chemically. The objective of this paper is to determine first the active species of sodium silicate and then the conditions under which this species will adsorb and function as a depressant. EXPERIMENTAL MATERIALS AND METHODS Pure samples of apatite (Durango), calcite (Iceland-spar), fluorite, and scheelite were used in this investigation. Pure potassium oleate was used as collector, while reagent-grade HC1 and KOH were employed for pH adjustment. The sodium silicates used were samples obtained from the Philadelphia Quartz Co. In one series of experiments, various sodium silicates containing different ratios of SiO2 to Na2O were added to calcite systems. These sodium silicates contained SiO2-to-Na2O ratios of 3.75 to 1, 3.22 to 1, 2.40 to 1, and 1.60 to 1. All other experiments were conducted with the sodium silicate containing the ratio of 3.22 to 1, which is the one that is normally used in industry. Flotation experiments were conducted with 21/2-g charges of 48 x 150-mesh material in conductivity water with an apparatus and technique described previously. Electrokinetic experiments were conducted with both a Zeta Meter and streaming potential apparatus. Particle size was 48 x 65 mesh for the streaming potential experiments. EXPERIMENTAL RESULTS The first series of experiments involved flotation of scheelite in the absence and presence of sodium silicate. As shown in Fig. 1, flotation response was not affected with even the relatively high addition of 1 x 10-3 mole per liter sodium silicate. Interestingly though, no flotation was effected below pH 6 with this collector addition. The responses of apatite to flotation under these same conditions are given in Fig. 2. Similarly, no depression was obtained in basic media under these conditions. Similar experiments were conducted with fluorite, and in this case, depression was noted above about pH 11 with 1 x 10-3 mole per liter sodium silicate (Fig. 3). When calcite was floated with these same levels of addition of sodium silicate, essentially no flotation was possible above pH 7 (Fig. 4). The effect of collector addition with a constant addition of sodium

Jan 1, 1969

By J. P. Hirth, A. H. Clauer

A simple graphical method is presented for the determination of climb forces on dislocations exerted by uniaxial stresses. In conjunction with standard stereographic projections, the technique is applicable for any crystal system. Climb forces on glide dislocations in bcc crystals are determined as an application. In connection with a study1 of elevated temperature creep of molybdenum single crystals, a detailed analysis of the climb force on a dislocation was necessary. In general, such forces can be calculated for an arbitrary dislocation segment from the Peach-Koehler equation2 (or one of its variants3"6) where Fk are the components of the force per unit length of dislocation line, ?i of the unit sense vector tangent to the line, ojl of the stress tensor, bl of the dislocation Burgers vector, and is the Einstein permutation operator with components ?123 = ?231 = ?321 = —?132 = — ?321 = —?—213 = unity, and all other components zero. It is understood in the suffix notation of Eq. [I.] that repeated indices are to be summed over 1, 2, and 3. For the most general coordinate system, the matrix manipulations required to solve Eq. [I] are fairly complex. However, a simplification can be achieved by specifying a coordinate system based on the dislocation in question. The pertinent system involves cartesian coordinates xi, x;, xi, with attendant unit vectors e'i; ei being parallel to the Burgers vector b, and e'3; being parallel to the climb directions (b x ?), i.e., normal to the slip plane. In this coordnate system b = (bi, 0, 0) and ? = (?'1,?'2, 0). Hence, Eq. [I] yields for the climb force per unit length F3 = ?'2s'11b'1—?'1s'12b'1 [2] The first term on the right side of Eq. [2] is the climb force on the edge component of the dislocation, while the second is the (cross-slip) force normal to the glide plane acting on the screw component. Thus, the problem of determining the climb force reduces to that of resolving the stress components —il and s'12 in the xi coordinate system. Several authors7- l0 have shown, for the glide case, that such stress resolution can be performed most readily by graphical methods. Therefore, we present a similar method for the climb case. Of the suggested methods, we follow that of Hartley and Hirth,9 which can be performed directly with a standard stereographic projection for the crystal system in question. We treat the case of simple tension, or compression, this being the most common creep test in which climb is important. A set of cartesian coordinates (x1, x2, x3) is fixed with x3 parallel to the specimen axis. This set is connected to the x'i set by the factors defined in Table I. A perspective view of the coordinate systems relating them to the glide ellipse, is given in Fig. 1, while a stereographic projection of the coordinate systems is presented in Fig. 2. The transformation matrix connecting the xi and xi coordinates is x'i =aijXj [3] where an a11 a13 aij = a21 a22 a23 a31 a23 [4] s The corresponding transformation for the stresses is i [5] The only nonzero component of okl for the simple tension case is s33,. Hence, using Eqs. [4] and 151, we find that Eq. [2] becomes F3 = b'1s33 sin2 cos ?[cos ? sin a - sin ? cos a] [6] = m1b'1s033 sin a- rn2b's33 cos a where sin a = 5: and cos a = ?i, with a the angle measured from b to ?, i.e., a polar angle in the x1, x2 plane. The same equation with a sign change applies for compression. A graphical plot of the "Schmid" factor m1, relating to the climb force on the edge component, is presented in the stereographic projection of Fig. 3. In this projection the glide plane normal points toward the top of the page and the glide direction points normal to the plane of the page. To use the graph, one

Jan 1, 1970

By W. O. Philbrook, H. E. Burner, F. S. Manning

The equation of continuity for the hydrogen reduction of hematite in a fixed bed of closely-sized particles is solved assuming a flat velocity profile, negligible temperature gradients, md negligible axial diffusion. A kinetic expression from the literature is used which assumes the reduction process is controlled at the oxide-metal interface. The integral fractional conversion is computed, and the importance of particle diameter, flow mte, temperature, bulk axial diffusion, and inter- and intra-particle mass trarnsfer is predicted. Comparison with experimental data suggests one or more additional undefined variable(s) is significant. Equipment modifications are suggested for fidture experimentcll work. WITH the increasing desire to "design" the ore feed of a blast furnace, it has become necessary to define more quantitatively the process variables and to evaluate the extent of their control upon the reduction process. The bulk of the work reported in the literature has centered about the reduction of single particles; however, the blast furnace process more closely resembles reduction of a fixed bed than that of single particles. To simplify this analysis, the isothermal reduction by hydrogen of a natural hematite in a fixed bed of closely-sized particles is examined. With appropriate modifications in the kinetic and flow rate expressions, the approach employed should be extensible to mixtures of carbon monoxide, hydrogen, and inert nitrogen, and to adi-abatic conditions, thus approaching the blast furnace process more closely. The fixed bed variables which are investigated in this study are particle diameter, flow rate, temperature, and bulk axial diffusion, as well as inter-and intra-particle mass transfer. Of particular interest is the effect of particle size upon fractional conversion for a bed operating under constant pressure drop. The constant pressure drop concept bears a close resemblance to the blast furnace process, where regions of larger particles may provide a greater permeability to divert most of the reducing gas flow from the regions of smaller ore particles. Under such conditions one would expect qualitatively that, for sufficiently small particle sizes where the flow rate is small and the total surface area is large, the reduction rate would be limited by the gas flow rate. Initially the gas entering the bed reacts very rapidly and the composition approaches the equilibrium conversion value a short distance from the reactor inlet. This concentration "wave-front" then moves up the bed as the flow of reducing gas is continued, leaving in its wake an ever increasing layer of reduced particles. Providing that the reducing gas leaves the bed at equilibrium concentrations, conversion is expected to increase with an increase in flow rate, and hence with an increase in particle diemater. Conversely, for sufficiently large particles the flow rate will be high but the surface area available for reaction will limit the reduction rate. Since the total surface area decreases with an increase in particle size, conversion, in this case, is expected to decrease as the particle diameter is increased. It is clear then that between these two extremes an optimum particle diameter must exist. THEORETICAL DEVELOPMENT Above the temperature where wiistite is stable (about 560°C) the reduction of hematite proceeds through the series Fe2O3/Fe3O4/FeO/Fe. On the basis of microstructural studies and earlier work, Edström1 has postulated a mechanism for the reduction of an ideal hematite lattice: 1) Iron phase formation at the boundary between wiistite, iron, and gas (for sufficiently porous iron). 2) Diffusion of iron across a wustite layer. 3) Phase boundary reaction of Fe3O4 to FeO. 4) Diffusion across a dense magnetite layer. 5) Phase-boundary reaction of Fe2O3 to Fe3O4. According to the mechanism postulated, gaseous reaction product has to be removed only at the boundaries between wüstite and iron or gas, the only possible exception being enveloped Fe3O4 specks. On this basis McKewan2,3 has proposed that one may consider the hematite reduction process as a simple two-phase system of oxide/metal. If, for FeO and Fe3O4 layers of negligible thickness, the hypothesis is made that the rate of formation of a

Jan 1, 1963

By Robert F. Calman

OUTLINE FIVE EXAMPLES OF GOLD-LINKED FINANCINGS 1. Financing the Lupin Mine • Sale of Cdn $40.0 million of 12% preferred shares and Cdn $40.0 million of Gold Purchase Warrants @ $595 per ounce. 2. Financing the Copper Range acquisition • Borrowing 100,000 ounces from a Canadian chartered bank @ US$307 for five years. 3. Financing the Round Mountain expansion • Borrowing up to US $80.0 million in dollars, convertible into gold, repayable over five years from a group of North American banks. 4. Financing the Tenneco Precious Metals Division acquisition •Sale of SFr 110.0 million of ten year 3-718% bonds with warrants to buy 132,000 ounces of gold at US $560. 5. On Forward Sales, Puts and Calls • Gold, Silver, Canadian Dollars, Swiss Francs THE FINANCIAL RULES AT ECHO BAY 1. Never bet the company 2. Equity is the primary form of capital for a gold mining company 3. On debt 4. The Yardsticks for Corporate Decisions 5. Financial Community Relationships 6. Dividend Policy No Text Available Tables Follow

Jan 1, 1990

By Walter Kauenhowen

The crude-oil production of Germany without Austria during 1938 amounted to 3,864,518 bbl., representing an increase of 21.7 per cent over the 3,173,373 bbl. produced in 1937. Adding the Austrian production, the crude-oil production of the new German Reich totaled 4,259,717 bbl. during 1938, representing an increase of 25.3 per cent compared with the respective figures of the previous year. According to published official data, and using a conversion factor of 1 metric ton equaling 7 bbl., the oil production of Germany in 1938 was as shown in Table 1. A semiofficial publication1 states that the program of the crude-oil industry for the second year (1938) of the four-year plan was successfully accomplished. According to the same source, new drilling developments at the following localities were promising: Reitbrook near Hamburg, Heide in Holstein, Eicklingen-Sandlingen near Celle, Steimbke near Nienburg, Worms in the Rhine Valley, Gifhorn near Braunschweig, Mölme near Oberg, and at other places. The drilling activity for oil is illustrated by the figures in Table 2.

Jan 1, 1939

By Walter Kauenhowen

The crude-oil production of Germany without Austria during 1938 amounted to 3,864,518 bbl., representing an increase of 21.7 per cent over the 3,173,373 bbl. produced in 1937. Adding the Austrian production, the crude-oil production of the new German Reich totaled 4,259,717 bbl. during 1938, representing an increase of 25.3 per cent compared with the respective figures of the previous year. According to published official data, and using a conversion factor of 1 metric ton equaling 7 bbl., the oil production of Germany in 1938 was as shown in Table 1. A semiofficial publication1 states that the program of the crude-oil industry for the second year (1938) of the four-year plan was successfully accomplished. According to the same source, new drilling developments at the following localities were promising: Reitbrook near Hamburg, Heide in Holstein, Eicklingen-Sandlingen near Celle, Steimbke near Nienburg, Worms in the Rhine Valley, Gifhorn near Braunschweig, Mölme near Oberg, and at other places. The drilling activity for oil is illustrated by the figures in Table 2.

Jan 1, 1939