By Arnt Solbu, Jomar Thonstad

The reaction between CO, and aluminum in cryolite-alumina melts in contact with aluminum has been studied by passing CO2 over the melt. In unstirred melts a homogeneous reaction between dissolved metal and dissolved CO2 was observed. In stirred melts in which convection was induced by bubbling argon through the melt, the dissolved metal apparently reacted mainly with gaseous CO2. The rate of formation of CO increased slightly with increasing depth of the melt, and it did not depend on whether CO2 was passed over or bubbled through the melt. The rate of formation of CO increased with increasing area of the metal/melt interface and with the application of anodic current to the metal. It is concluded that the dissolution of metal into the melt is the rate-determining reaction. THE current efficiency in aluminum electrolysis is determined by the rate of the recombination reaction between the anode gas and the metal: 2A1 + 3CO2—A12O3 + 3CO [1] as originally stated by Pearson and waddington.1 The occurrence of this reaction in cryolite-alumina melts in contact with aluminum was first verified experimentally by Schadinger.2 Thonstad3 has shown that the reaction may proceed further to give free carbon: 2A1 + 3CO— A12O3 + 3C [2] Normally only a few percent of the CO formed undergoes such reduction. The mechanism of these reactions has not yet been clarified. Aluminum, as well as CO,, is soluble in the melt. The solubility of aluminum in cryolite-alumina melts at around 1000°C corresponds to 75 x 10- 6 mole A1 per cu cm,4 while that of CO2 is only 3 x 10-6 mole CO, per cu cm.5 Taking into account the stoichiometry of Reaction [I], the ratio between dissolved aluminum and dissolved CO2 available for the reaction in a saturated melt is about 40. Therefore, as will be shown in the following, the reaction probably mainly occurs between gaseous COa and dissolved aluminum. The dissolved aluminum presumably consists of subvalent ions of aluminum and sodium.4'6 Since the interpretation of the present results is not dependent upon the nature of this solution, the dissolved metal will be designated solely as Al+ in the following. The reaction can then be divided into four steps: A) dissolution of metal, e.g., 2A1 + Al3 — 3A1+ [3] B) diffusion of dissolved metal through a boundary layer; C) transport of dissolved metal through the bulk of the melt; D) Reaction [1]. If dissolved CO, takes part in the reaction, three additional steps embodying the dissolution and transport of CO2 must be added. schadinger2 observed, when bubbling CO2 through the melt, that the rate of formation of CO (in the following designated rfco) did not depend on the distance from the metal surface. The results also indicate that the rate of bubbling did not affect the rfco. When passing CO, over the melt, Revazyan7 found that the loss of metal did not depend on the depth of the melt above the metal or on the flow rate of CO2, and concluded that Step A is rate-determining. In an unstirred melt, however, Gjerstad and welch8 found that the rfCo decreased with increasing depth of the melt, indicating that step C was rate-determining. It thus appears that the rate control of the process depends on the experimental conditions, particularly on the convection. In the present measurements the reaction has been studied in unstirred as well as in stirred melts. EXPERIMENTAL AND RESULTS The experiments were carried out at 1000°C in a Kanthal furnace with a 10-cm uniform temperature zone (±0.l°C). The melts were made up of "super purity" aluminum (99.998 pct), hand-picked natural cryolite, and reagent-grade alumina. In experiments where alumina crucibles were used, the alumina content in the melt was close to saturation (13.5 wt pct9); otherwise it was 4 wt pct. Pure Co2 (99.85 pct) was passed over the melt, and the exit gas was analyzed for CO2 and CO by the conventional absorption method.3 From the weighed amount of CO (as CO2) the rfco was calculated as the number of moles of CO formed per min per sq cm of the surface area of the melt. The amount of carbon formed by Reaction [2] was not determined. As already indicated the rfco is much higher than the rfC, by Reaction [2]. Since the rfC probably is proportional to the rfco, the measured rfco should then the proportional to, but slightly lower than, the total rate of Reactions [I] and 121. In general the scatter of results obtained in duplicate measurements was ±5 to 10 pct, while within a given run a precision of ±3 to 5 pct was obtained. The various crucible assemblies that were used will be described below. Measurements in Unstirred Melts. When carrying out aluminum electrolysis in small alumina crucibles. Tuset10 observed that after solidification the lower part of the electrolyte was gray and contained free metal, while the upper part near the anode was white and contained no metal. One may test for the presence of free metal by treating with dilute hydrochlorid acid.

Jan 1, 1969

By David J. Dunn

At a time when mill availability is at a premium, production costs are rising, and lead time for mill liner casting is a year or more, mill liner design is an important factor in ore grinding. Testing and selection of the optimum liner profile for a given set of mill operating conditions can improve mill capacity, reduce liner wear rate, and lengthen liner life. The mill liner that grinds best, lasts the longest, and costs the least is a necessity for economic mill operation. After testing four mill liner profiles for 3.96 X 3.65-m (13 x 12-ft) overflow ball mills, Climax Molybdenum Co. found that an improved design increased mill tonnage by 2.72 t/h (3 stph) while reducing finish grind by 1.7% minus 100-mesh, reduced liner wear rate, and almost doubled liner life.

Jan 12, 1976

By G. H. F. Gardner

The boundary conditions F = 1.0 and 4 = 1.0 (100 per cent) are dictated by the definition of F in the equation 1/F = aFp. These conditions have physical significance as the "limiting conditions" for the observed behavior in systems of dispersed particles. The other boundary conditions, cited by Gardner in his Eq. 3 as applying to this system, have no significance in the systems we studied. Maxwell's equation (Eq. 2) cited in Gardner's comments was developed for and limited to a regular, rather than random, dispersion of spheres which are sufficiently removed from each other so that they do not interfere with current flow about their neighbors. These restrictions also apply to Rayleigh's analysis. The title of Rayleigh's paper cited by Gardner is "On the Influence of Obstacles Arrayed in Rectangular Order upon the Properties of a Medium". He is not discussing randomly dispersed spheres. It might be inferred from Gardner's comments that Rayleigh specifically considered the differential equation (Gardner's Eq. 3). This is not the case. Mathematically, Gardner's Eq. 3 is exactly true for the system to which it applies, however, as both Rayleigh and Maxwell note that their equation for F in terms of F is not for randomly dispersed spheres. At the time we wrote our paper, we were aware of the work of Wyllie and Gregory as cited by Gardner. We cited their work in Ref. 5 of our paper. Our comment on page 287 of the paper about the validity of an m value of 1.3 for spheres with a porosity of 38 per cent remains as our answer to Gardner's question on this point. Our data, at 38 per cent porosity, show that the condition a = 1 and m = 1.3 holds for spheres near 40 per cent porosity.

By L. C. Brown, S. K. Behera

The diffusion rate in Ag-Sb couples is sensitive to con~pressive load with the width of Ag3Sb, the only phase present in the diffusion zone, increasing with stress up to 800 psi and remaining constant above this. Kirkendall marker experiments show silver to diffuse much faster than antimony in Ag3Sb and incipient porosity may therefore develop at the Ag/Ag3Sb interfnce restricting the transfer of atoms from the silver into the diflusion zone. Application of compressive stress reduces the tendency for porosity to develop and so increases the growth rate. In a recent paper Brown et al.1 observed a significant increase in the thickness of Cu2Te in Cu-Te diffusion couples on application of a compressive stress as low as 20 psi. Similar stress effects have also been observed in the Fe-A1,2 Al-u,3 arid cu-sb4,5 systems. It has been suggested that the increase in growth rates of intermetallic phases in these systems is due to a decrease in the amount of Kirkendall porosity with applied stress. In the present paper, results are presented of the effect of compressive stress on diffusion in Ag-Sb, together with a detailed examination of the Kirkendall effect. The Ag-Sb phase diagram6 shows that antimony has a moderate degree of solid solubility in silver, 5.7 at. pct at 350°C, but that there is essentially no solubility of silver in antimony. There are two intermediate phases— (hcp7) from 8.8 to 15.7 at. pct Sb and Ag3Sb (orthorhombic8) from 21.8 to 25.9 at. pct Sb. EXPERIMENTAL Diffusion couples were prepared from fine silver of 99.95 pct purity and from antimony of 99.7 pct purity. Both the silver and antimony were produced in the form of discs 1/2 in. in diam by approximately $ in. thick, with surfaces ground flat to 3/0 emery paper. Diffusion anneals were carried out in the apparatus previously described.1 A compressive load was applied to the diffusion couple through a lever arm system, with a reproducibility estimated to be ±10 psi. All runs were carried out in a protective hydrogen atmosphere. Following the diffusion anneal specimens were sectioned and polished and the width of the diffusion zone was measured metallographically. Composition profiles were measured using an electrostatically focused electron probe with a spot size of 10 , counting on Sb L radiation. Corrections for matrix absorptiori and fluorescent enhancement9 were not required. S. K. BEHERA, formerly Graducate Student, Department of Metallurgy, University of British Columbia, is now Postdoctoral Fellow, Whiteshell Nuclear Laboratories, Atomic Energy of Canada Ltd., Pinawa, Manitoba. L. C. BROWN, Junior Member AIME, is Associate Professor, Department of Metallurgy, University of British Columbia, Vancouver, B.C., Canada. Manuscript submitted June 14, 1968. IMD RESULTS Fig. 1 shows an electron probe traverse of a typical diffusion zone. In all couples examined only one intermediate phase was observed and the composition of this phase, 23 wt pct Sb, was in good agreement with the composition of Ag3Sb, 23 to 28 wt pct Sb. The presence of this phase was confirmed by X-ray diffraction of filings taken from the diffusion zone. The probe traverses showed no detectable solid solubility in either the silver or the antimony although the phase diagram indicates that some antimony, up to 6.5 wt pct pct Sb, should be in solid solution in the silver. However the width of this portion of the diffusion zone would be expected to be very small in view of the low diffusion coefficient in the silver, 4 x 10-l6 sq cm per sec at 350°C, 10 compared with that in the Ag,Sb, estimated as 3 x 10-8 sq cm per sec in the present work, and this region would therefore not be expected to be seen in the probe traverse. Application of stress resulted in a significant increase in the width of the diffusion zone, Fig. 2. At 350°C, the thickness of Ag3Sb increased from 250 at 0 psi to 400 p at the limiting stress of 800 psi, indicating an apparent 150 pct increase in the diffusion coefficient. Similar behavior was also observed at 400°C, indicating that the stress effect is not characteristic of just one temperature. The growth of Ag3Sb at 350°C and at various stresses is shown in Fig. 3. In every case the growth rate was parabolic indicating diffusion control. The kinetic curves all passed through the origin showing that delayed nucleation of Ag3Sb was not responsible for the stress effect and that it was a real growth effect. A series of tests were carried out in which diffusion was allowed to take place at a lower stress following an initial high stress diffusion anneal. Speci-

Jan 1, 1969

By M. A. Schimmelpfennig, A. D. S. Gillies

Loss of visibility due to the occurrence of atmospheric fogging in underground mine airways can lead to longer travel times and loss of production efficiency, an increase in the frequency of vehicular and foot traffic accidents and difficulty in checking rock surfaces for instability and loose material. Where hot and humid surface air meets colder underground air, conditions for fog formation may be present. Further, suspended particulate matter from diesel exhausts or stoping operations together with slow movement of air along passageways may contribute to formation. This study describes an investigation being undertaken with the cooperation of Kennecott's Ozark Lead Co. to identify causes of the problem.

Jan 1, 1984

By AIME AIME

S ULFURIC acid made in the United States during the last four years has averaged approximately 7,000,000 tons of 50" B6 acid a year. This is double the production of the year 1913. About 66 per cent of the acid is made from sulfur, 16 per cent from pyrite, 13 per cent at copper, lead, and zinc smelters, and the remainder from miscellaneous sources it her the chamber process or the contact process, (at some plants both) is used. In 1923, the contact process accounted for nearly 30 per cent of all the sulfuric acid made in this country and since then it has been increasingly employed. It was first introduced here in 1898, and has always .proved less expensive than the chamber process for the manufacture of .acid of high concentration and purity, but the latter produces acid of low strength suitable for many industries.

Jan 1, 1929

I;. D. Godshall, Everett, Wash. (communication to the Secretary) : In Mr. Morse's interesting paper several statements occur which seem to require correction and comment. This is the more appropriate, since Mr. Morse has mentioned me by name, and has cited my "Review of the Russell Process,"* so that silence on my part might be taken as indicating an assent which I cannot give. On the first page of his paper Mr. Morse says that the " goingback " of chlorination was " the only difficulty encountered at Aspen," and adds that he has " never seen any explanation " of the cause. The plain inference is that he now fills this complete

Jan 1, 1896

By D. R. Irving

Prior to this time, ample supplies of high grade mineral fillers, such as clay, have been available close to consuming centers. Now depletion of these accessible deposits, coupled with other factors such as increasing demand due to population expansion and standard of living rise, has made development of upgrading techniques attractive to producers. Various investigations being carried out by the U.S. Bureau of Mines are described. Factors making the development of improved methods for upgrading clays attractive to producers include: depletion of accessible deposits of high-grade clays, rising transportation and labor costs, more exacting specifications, and increased demand resulting from an expanding population and a constantly rising standard of living. Industry recognizes the need for upgrading presently unusable materials and has cooperated with the U.S. Bureau of Mines by providing samples from submarginal deposits and by evaluating the products that USBM upgrades. Following are some examples of recent clay beneficiation work by the Bureau. FIRE CLAY BENEFICIATION At the Rolla Metallurgical Center, Rolla, Mo., the Bureau is conducting research to develop technically and economically feasible mineral-dressing methods to remove quartz, pyrite, and other impurities from submarginal fire clays. The research has been spurred by the growing shortage of high-grade bur-ley, flint, and plastic clays in the Missouri fire-clay district resulting from increased consumption and the low rate of discovery of new deposits of adequate quality. There apparently is ample tonnage of submarginal flint and plastic clays to maintain the industry for many years if such material can be upgraded to commercial quality. Samples have been submitted to USBM by several major producers of refractories, including A. P. Green Fire Brick Co.; Harbison-Walker Refractories Co.; Mexico Refractories Div., Kaiser Aluminum and Chemical Corp.; and Wellsville Fire Brick Co. Research on some samples has been completed and still is in progress on others. The Bureau has found that specimens containing quartz or pyrite in grains coarser than the accompanying clay generally can be upgraded either with a gravity table or hydraulic cyclone. The improvement in quality is notable not only in chemical analysis but in an increase in pyrometric cone equivalent (PCE) of one or more cones. As an example, consider the results attained on a sandy flint—a fine-grained mixture of kaolin and halloysite with quartz and minor quantities of iron and manganese oxides. Chemical analysis was: 35.4 pct alumina (A12O3) and 47.8 pct silica (SiO2). The sample contained 9.2 pct free silica as quartz. The PCE was 33. The sample was crushed to -10-mesh, blunged with water, and then stage-ground to -48-mesh. The ground sample was tabled to yield a clay fraction containing 37.6 pct A12O3, and 45.3 pct SiO2 of which 2.4 pct was free silica. The PCE was 34. Recovery of alumina by this process was 73.6 pct. Concentration of the same clay in the hydraulic cyclone was even more effective in respect to quartz removal. The clay fraction analyzed 38.6 pct A12O3, 45.0 pct SiO2 of which 0.5 pct was free silica as quartz, and had a PCE of 34. Recovery of alumina was 71.9 pct. The hydraulic cyclone was also effective in reducing the pyrite content of a plastic clay which likewise was a mixture of kaolin and halloysite, plus some pyrite, quartz, and carbonaceous material. It analyzed 30.6 pct Al2O3, 52.3 pct SiO2, 2.3 pct Fe2O3, and 0.76 pct S. The sample was blunged and screened through 10-mesh to remove some coarse pyrite, then ground to -65-mesh and cycloned to remove most of the remainder. The final product recovered 81.8 pct of the alumina at a grade of 32.3 pct A12O3, 50.9 pct SiO2, 1.4 pct Fe2O3, and 0.1 pct S. The PCE was 32-1/2, compared with a PCE of 31-1/2 for the crude clay. The fine beneficiated clays, of course, must be pelletized and dried or fired to meet commercial acceptance. This operation has already been solved by industry. Little progress has been made on two remaining problems. One is that of fine-grained impurities, not separable by table or cyclone. Flotation is being investigated to solve this. Although fine pyrite is readily rejected, a satisfactory quartz-clay separation has not been attained. The second problem, a stubborn one, is that of alkali. Samples containing as much as 5 pct potas-

Jan 1, 1961

By F. V. Lene, E. J. Westerman

The recrystallization behaviors of two extruded and cold-drawn experimental sintered aluminum powder alloys, containing 1.75 and 3.0 pct Al2O3 by weight, were compared with that of extruded and cold-drawn commercially pure alumirzum. The kinetics of recrystallization of the alloys are described semiquantitatively. For the alloy containing 1.75 pct A l203 the rates of nucleation and of growth were also semiquantitatively determined. THE most striking property of aluminum alloys strengthened by a dispersion of Al2O3, the so-called SAP alloys, is their stability at elevated temperatures. One of the manifestations of this stability is their resistance to recrystallization after they have been cold worked. Most of the commercial grades of either the Swiss SAP or of Alcoa's Aluminum Powder Metallurgy Products have not been recrys-tallized after cold working, even when they are heated for a long time at a temperature near the aluminum melting point. Lenel, however, observed that the dispersion strengthened aluminum alloys with a larger spacing between the oxide particles than that of most commercial grades would recrys-tallize.1 It appeared to be of interest to further investigate the mode and kinetics of recrystallization of these alloys, and to compare their recrystallization behavior with that of commercially pure aluminum. Because homogeneous deformation of these SAP alloys in tension did not provide sufficient cold work to induce recrystallization, they were cold worked by wire drawing; the nonuniformity of this deformation unavoidably complicated the interpretation of the recrystallization studies. EXPERIMENTAL DETAILS Extrusions—Two types of sintered aluminum powder extrusions were used in this study. One type, designated AT-400, was produced from Reynolds atomized aluminum powder consisting of spherical particles averaging 3µ in diam and containing 1.75 wt pct of Al2O3. This powder was very similar to the R3M powder from which extrusions were previously prepared with an average spacing of 0.9µ between oxide particles.2 The second type, designated MD 2100, was produced from Metals Disintegrating Co. flake powder containing 3.0 wt pct of Al2O3, with an average flake thickness of 0.8µ. The average spacing between oxide platelets in MD 2100 extru- sions was 0.45µ.2 Powder compacts of 3/4-in. diam were extruded at 1000°F into 0.097-in. diam (AT-400) and 0.093-in. diam (MD 2100) wires by methods previously described.3 In order to compare the recrystallization behavior of sintered aluminum powder extrusions with that of wrought commercially pure aluminum 3/4 in. rod stock of 1100 F aluminum was extruded at 1000°F into 0.102-in. diam wire. Wire Drawing—Tungsten carbide dies were used for the AT-400 and 1100 F alloys. They had an included angle of about 15 deg and reduced the wire area approximately 7 pct per pass. Steel dies with an included angle of 11 to 13 deg and an average reduction per pass of 10 pct were used for drawing the MD 2100 alloy, because drawing this alloy through the carbide dies produced overdrawing defects. Heat Treatment—The cold-drawn wires were cut into small samples, and the deformed ends were etched off. The samples were each wrapped tightly in a single layer of aluminum foil, and individually isothermally annealed in a lead bath. Metallography—The modes and kinetics of recrystallization were determined by metallography. Mounted and polished specimens were anodized in a solution of 1.8 pct HBF4;4 examination under polarized light clearly revealed their grain structures. The recrystallized grains were generally much larger than those of the unrecrystallized matrix, and could clearly be distinguished because they alternated between maximum and minimum light reflection when the microscope stage was rotated, while the unrecrystallized matrix had a comparatively homogeneous "salt and pepper" structure. The fractional recrystallized volumes of the dispersion hardened alloy wires were determined by cutting and weighing of recrystallized and total transverse areas on photomicrographs. The recrystallized grains in the 1100 F alloy were too small to be cut out individually; therefore a combination of cutting and lineal analysis was used in this case. RESULTS AND DISCUSSION Modes of Recrystallization—The modes of recrystallization of the three alloys varied widely. In the 1100 F alloy nucleation and growth started in the region midway between the center and the surface;

Jan 1, 1961

By H. Stuart, L. Zwell, N. Ridley

specimen that was subjected to 700°C for 250 hr is shown in Fig. 2(c). The precipitates in this foil appear round and exhibit only very faint strain contrast. From this evidence, along with that described above for the symmetry of the strain field, it may be concluded that this coherent precipitate is spherical, which is generally the favored shape for coherent precipitates when the lattice parameter mismatch is small.12 These observations are consistent with the assumption that this precipitate is the y' (Ni3Al, Ti) phase. y' is known to be spherical in the early stages of precipitation. It is fcc and is similar in composition to the matrix and thus would have contrast similar to that of the matrix as do these precipitates. Direct identification of the spherical precipitate did not prove possible because of its low volume fraction and small size. The results of this investigation suggest that the increases in yield strength and the decreases in elongation observed in 45-Fe 30-Ni 20-Cr alloys containing about 0.4 pct A1 and 0.4 pct Ti on prolonged aging at 550" to 700°C are very likely due to the presence of a coherent, spherical precipitate, thought to be y'. Mi-crohardness measurements indicated that the precipitation of semicoherent M23C6 resulted in some matrix hardening. However, this precipitation process occurs much more rapidly than the changes in mechanical properties at these temperatures. 1C. L. Clark, J. J. B. Rutherford, A. B. Wilder, and M. A. Cordovi: J. Eng. Power, 1962, vol. 84, p. 258. 2 F. A. Comprelli and U. E. Wolff: USAEC Report GEAP-4745, General Electric Company November, 1964. 3C. N. Spalaris: A Monograph, USAEC Report GEAP-4633, General Electric Company, July, 1964. THERE have been many X-ray investigations of the room temperature lattice parameters of austenite which has been retained in quenched steels of various carbon contents. The results of these investigations have been collected by Wrazej,1 Wever et al.,2 and by Roberts3 and are included in Fig. 1 due to Pearson.4 The dashed line in Fig. 1 was considered by Roberts3 to most reliably describe the variation with carbon content of the lattice parameter of retained austenite. This line is given by the equation: a (Å) = 3.555 + 0.044 wt % C and recent unpublished measurements by one of the authors (LZ) support this relationship. The object of this communication is to draw attention to a relationship which describes the variation of the room temperature lattice parameter of 'equilibrium' austenite with carbon content, and which is different from that for retained austenite. The relationship a(Å) = 3.573 + 0.033 wt % C has been obtained from lattice parameter measurements made on equilibrium Fe-C austenites at elevated temperatures, which have been extrapolated to room temperature. The room temperature lattice parameter of 3.555Å which the Roberts' relationship gives for pure y-Fe is no: in agreement with the value of 3.573Å obtained when the high temperature lattice parameter data of Basinski et aL.5 and of Goldschmidt6 is extrapolated to room temperature. A linear extrapolation was

Jan 1, 1970

By Nicholas J. Grant, Bill C. Giessen

The phase diagram Ta-Ni has been treated repeatedly; investigations up to 1958 are summed up in Ref. 1. Since then, an equilibrium diagram has been presented by Kornilov and Pylaeva.2 They found the following intermediate phases: Ta2N; (CuA12 type),3 "TaNi" (p phase, Mo8Co7 type), TaNiz, and TaNi3 (Ticus type).5 Of these, the crystal structure of TaNin remained unknown, and no further literature reference was found. According to Kornilov and pylaeva,&apos; TaNil melts peri-tectically at 1420°C. A 5-g alloy of Ta + 66.7 at. pct Ni was prepared by inert-gas arc melting using 99.95 pct Ta rod (NRC-MG) and 99.9 pct Ni shot (Fisher). The weight loss after three melts was <2 mg; a microscopically homogeneous ingot resulted. As shown in Ref. 6, no oxygen or impurity pickup needed to be considered under these conditions. Specimens were annealed for 15 hr at 1350°C, 15 hr at 1205oC, and 15 hr at 875°C with subsequent powdering and stress relief for 10 min at 1350°C, 15 min at 1205oC, and 1 hr at 875oC, respectively. Micrographs and X-ray analysis (114.6 mm Norelco camera, filtered CuK, radiation) showed homogeneous one-phase alloys in the as-cast state and at all three temperatures, all having the same powder pattern except for broad lines in the as-cast state. From this it is concluded that either TaNi, melts congruently or its melting behavior is a transition between the eutectic and peritectic cases. Since it was found that very slight surface contamination on stress relieving can considerably alter the structure of similar phases (e.g.,TaPt3),7 patterns before and after stress relief were also compared; they were identical except for line broadening in the non-stressrelieved condition, and two faint impurity lines in the stress-relieved samples. The powder pattern is presented in Table I. All lines were accounted for by indexing with a tetragonal lattice, 0Yh- I4/mmm , with a, = 3.154 ± 0.001A, co = 7.905 * 0.002i and c/a = 2.506. The atomic positions are: 1000; 1/2, 1/2, 1/2] + 2Ta(a): 000; + 4Ni(e): *(002); z = 0.333 * 0.002 This proves TaNi2 to be a representative of the MoSiz (Cllb) type. The variable parameter was determined by grouping the visually estimated intensi- ties according to their 2 indices, plotting their F values, and varying z for best fit, which was obtained at z = 0.333= 1/3. Since absorption was not considered, only the relative intensities with similar 28 can be expected to agree. The interatomic distances are presented in Table 11; the standard error is *o.o2A, resulting chiefly from the uncertainty in z. These distances indicate a coordination number 10 for both kinds of atoms and show that the pseudohexagonal layers along (110) are rather un-distorted. The mean atomic volume of 13.1A3 is close to the Vegard&apos;s law value of 13.3A3, showing

Jan 1, 1964

By J. B. Conway

RECENT studies of first-stage creep data have led to a special least-squares procedure for use in calculating the Andrade creep-equation constants. This procedure is easy to apply, uses only experimental data, and yields results which do not vary with the individual making the analysis. Taking logarithms of the Andrade equation I = lo(1 +ßl1/3)ekt leads to In l = In lo + In(1 + ßl1/3) + kt A residual can then be defined as the difference between the logarithm of an experimental length value and the logarithm of a calculated length value. Following the usual least-squares approach differentiation with respect to 10 and k of the expression for the sum of the squares of the residuals leads to two equations which cannot be solved directly for the three constants involved. However, values of ß can be assumed and corresponding values of lo and k can then be calculated. Then the sum of the squares of the residuals can be calculated. For a certain value of ß this sum will exhibit a minimum value to identify the least-squares values for ß, lo, and k. An illustration of the application of the above least-squares approach is obtained by employing the creep data for lead originally presented by Andrade&apos; in the development of the one-third creep law. A plot of the sum of the squares of the residuals as a function of ß is shown in Fig. 1 along with the corresponding lo and k values. The minimum is seen to occur at ß = 0.0143 from which lo = 39.149 and k = 7.27 x 10-5. Based on these results the Andrade equation for these lead data is 1 = 39.149(1 + 0.0143 t1/3)e7.27 x 10-5t compared to the equation I = 39.13(1 + 0.01457/l/3)e6.95 X 10-5t developed by Andrade (calculation procedure not given but was probably a graphical solution). Calculating length values using the above equations and comparing with the experimental length values, residuals corresponding to the difference between experimental and calculated length values can be obtained. The sum of the squares of the residuals can then be calculated. For the case of the least-squares approach a value for this sum was found to be 2.37 x 10-3 compared to a value of 3.47 x 10" for the equation originally proposed by Andrade. In other words, while the constants proposed by Andrade provide an excellent fit for the lead data, a still better representation is afforded by applying the least-squares approach discussed above. A similar result was obtained for the lead data at 162oc.l The least-squares approach led to 1 = 9.866(1 + 0.0497 t1/3)el.011 x 10-2t compared to the equation I = 9.94(1 + 0.0433 l1/3)e1.06 X 10-2t given by Andrade. In this case, too, the sum of the squares of the residuals is slightly smaller for the equation based on the least-squares approach. It should be pointed out that a double trial and er-

Jan 1, 1965

[Trans. No. Place Date Vol. Page 1. Wilkes-Barre, Pa May, &apos;71.. 1 3 2. Bethlehem, I&apos;s Aug., &apos;71.. 110 3. Troy, N. Y Nov., &apos;71.. 113 4. Philadelphia, PaFeb., &apos;72.. 117 5. New York, N. YMay, &apos;72120 6. Pittsburgh, Pa Oct., &apos;72.. 125 7. Boston, MassFeb., &apos;73.. 128 8. Philadelphia, Pa.*May, &apos;73.. 23 9. Easton, PaOct., &apos;73.. 27 10. New York, N. Y Feb., &apos;74211] [ ]

Jan 1, 1925

By R. R. Sayers

THE South African Mining and Engineering Journal recently pointed out that no satisfactory solution of the question of compensation for silicosis can be arrived at by placing further liability of an inequitable nature upon the mines. There are at present 35 scheduled mines liable to contribute to the annual levy of $800,000 and provide for the net outstanding liability of $6,400,000. Several of these mines have, as yet, not been able to set aside sufficient funds against their out- standing liability to the Compensation Fund. The gold producers declare that the gold mining industry today is passing its zenith, and that the production of gold will decline, with a consequent lessening of the spending power of the mines, which in about ten years will be reduced to a great extent unless encouragement is given for the opening of new mines. It is during this period of decline that the mines will be required to meet the large burden already created by miners&apos; phthisis. In England the Workmen&apos;s Compensation Act, 1925, was extended to industries involving exposure to asbestos dust.

Jan 1, 1931

By D. I. Bardos, F. X. Spiegel, R. K. Malik, Paul A. Beck

Study of the occurrence of elongated ß-Mn phase fields and of their direction of extension in fifteen ternary systems indicates that the ß-,mn phases formed by manganese with other transition elements and with either silicon, germanium, or tin may be considered as electron phases. In these phases the alloying behavior of silicon on the one hand and of germanium and tin on the other shows a significant difference . Formally all observations can be satisfactorily described by attributing to germanium and tin an apparent electron concentration of nine electrons per atom. This behavior may be interpreted by assuming that germanium and tin exclude itinerant electvons because of a strong repulsive potential arising fromthe requirement that their wave junctions be orthogonal to those of- the closed d shells of these atoms. The absence of a d shell in silicon allows this atom to admit itinerant d electrons. The following new ternary phases of unknown structure were identified by means of their X-vay difjraction patterns: (Mn,Co,Si)I , (Mn,Co ,Si)Y, (Mn.Co,Si)Q , (Mn ,Ni ,Si)W , and (Mn, Ti ,Si)A. The X-ray data suggest that these phases have large unit cells and that to some extent they may he related structurally to the 0 phase. The a phase and certain other phases formed by transition elements are characterized by their preferred occurrence at a constant electron concentration. AS a result, these "electron phases" have relation to electron concentration. The tendency of the B phase to form elongated phase fields in ternary systems along the directions of constant electron concentration has been previously demonstrated. The occurrence of an elongated 0-Mn phase field in the ternary system Mn-Co-Si was schematically indicated by Cherkashin et al.l0 The present study includes fifteen ternary systems, each containing in addition to manganese a second transition element from the group Ti, V, Cr, Fe, Co, Ni and one of the nontransition elements silicon, germanium, or tin. In each system the boundaries of the B-Mn phase were determined in the 900°, 950°, or 1000°C isothermal section, the temperature being dictated on the one hand by the requirement of sufficient rates of diffusion to approach equilibrium conditions in reasonably short annealing periods and on the other hand by the need to avoid as much as possible the partial melting of alloys during annealing.

Jan 1, 1967

By Charles H. Jacoby, Stanley J. LeFond

Salt, or halite, has had a long and most varied history. While we know the Chinese were producing salt as early as 3000 B.C., the first written reference to salt appears in the book of Job recorded about 2250 B.C., which reads: "Can nothing which is unsavory be eaten without salt?" We do not know when man first used or realized that he needed salt. Perhaps one of our early Eolithic ancestors noted a piece of salt shining along the shore of a salt lake or a bay. He may have been attracted by its shining luster and tasted it. He found that it had a tart, zesty, distinctive flavor and perhaps chewing a large piece, became ill. However, by experimentation he soon learned that taken in the proper proportions salt was a very pleasant additive to his food. He may have noticed, too, that it increased his feeling of well-being. Thus, when the curtain of recorded history rises, we find man using salt for his health&apos;s sake, seasoning his food with it, feeding it to his animals, and using it in many superstitious and religious ceremonies. These uses, however, are a far cry from the uses for salt today. The first attempts of white man to make salt in continental United States were reported in the year 1614, while the first commercial production was in 1790. Practically all of this salt was for human consumption, preserving food, and curing hides. Prior to the coming of the "white man" Indians are known to have made salt from such salt springs as those that existed at Avery Island, La., Charleston, W.Va., Saltville, Va., and Onondaga, N.Y. In 1862 the first rock salt was mined in the U.S. from the Avery Island salt dome. Almost immediately thereafter, rock salt was mined at Saltville, Va., and then at Retsof, N.Y., in 1885. Of the more than 40 million tons produced annually in the United States, about 68% or 27 million tons are consumed by the chemical industry in the production of chlorine, caustic soda, hydrochloric acid, sodium metal, and some 30 other basic chemicals. These basic chemicals, in turn, are used in the preparation of approximately 14,000 chemicals which range from soap and detergents, to such chlorinated hydrocarbons as DDT, BHC, carbon tetrachloride, etc.

Jan 1, 1975

By L. L. Swift

.It the present time there are four base metals being used for automo-tive bearing alloys. Of course there are numerous variations in the amounts of alloying elements added to each base metal and nearly all of these alloys have the conventional, if not classical, duplex structure; that is, they are composed of a hard constituent embedded in a soft matrix. The well-known theory is that the former will wear well, while the latter will be plastic enough to allow the bearing to be broken in and conform to the contours of the shaft. The requirements of the modern bearing have been most aptly described by W. M. Corse: In order to meet the engineering demands of today a good bearing metal must be able to carry the weight of the shaft and stand up under steady or suddenly applied loads, or even blows ill sorne types of service. A certain amount of plasticity is desired to compensate for minute irregularities in the shaft or bearing surface, and to permit yielding, thereby avoiding dangerous stresses in bearing and shaft and pre-venting overheating and rapid wear of parts. Less plasticity is required in a bearing tuetal if the surfaces of bearings and journals are machined accurately, aligned, and kept in alignment. It is desirable, of course, that a bearing metal have a low coeffi-cicnt of friction. Under most operating conditions the friction depends on the unit, pressure of the bcaring, the speed, the temperature, and the properties of the lubricant. A good bearing metal must have a low rate of wear to reduce the necessity for frequent replacements, and adjustment of the bearings. It must wear more rapidly, however, than the journal or shaft running on it, because replacement of the journal or shaft is more difficult and costly than replacement of the bearing.&apos; The hardness of the bearing alloy is a property closely related to several of the foregoing. With a duplex microstructure, the measurement of hardness with any of the usual commercial devices means little. The Bierbaum method of measuring the hardness of the individual canstituents was developed to fill this need. MICROCHARACTER The Bierbaum MicroCharacter~,~ measures the scratch-hardness of a solid by pulling a weighted diamond point over the surface. The diamond point is ground so that it is the corner of a cube, and Mounted

Jan 1, 1939

By L. L. Swift

.It the present time there are four base metals being used for automo-tive bearing alloys. Of course there are numerous variations in the amounts of alloying elements added to each base metal and nearly all of these alloys have the conventional, if not classical, duplex structure; that is, they are composed of a hard constituent embedded in a soft matrix. The well-known theory is that the former will wear well, while the latter will be plastic enough to allow the bearing to be broken in and conform to the contours of the shaft. The requirements of the modern bearing have been most aptly described by W. M. Corse: In order to meet the engineering demands of today a good bearing metal must be able to carry the weight of the shaft and stand up under steady or suddenly applied loads, or even blows ill sorne types of service. A certain amount of plasticity is desired to compensate for minute irregularities in the shaft or bearing surface, and to permit yielding, thereby avoiding dangerous stresses in bearing and shaft and pre-venting overheating and rapid wear of parts. Less plasticity is required in a bearing tuetal if the surfaces of bearings and journals are machined accurately, aligned, and kept in alignment. It is desirable, of course, that a bearing metal have a low coeffi-cicnt of friction. Under most operating conditions the friction depends on the unit, pressure of the bcaring, the speed, the temperature, and the properties of the lubricant. A good bearing metal must have a low rate of wear to reduce the necessity for frequent replacements, and adjustment of the bearings. It must wear more rapidly, however, than the journal or shaft running on it, because replacement of the journal or shaft is more difficult and costly than replacement of the bearing.&apos; The hardness of the bearing alloy is a property closely related to several of the foregoing. With a duplex microstructure, the measurement of hardness with any of the usual commercial devices means little. The Bierbaum method of measuring the hardness of the individual canstituents was developed to fill this need. MICROCHARACTER The Bierbaum MicroCharacter~,~ measures the scratch-hardness of a solid by pulling a weighted diamond point over the surface. The diamond point is ground so that it is the corner of a cube, and Mounted

Jan 1, 1939

By Charles R. Keyes

PAGE I. Introductory............ 140 II. Location and History...........140 III. Surface-Relief of the District....... 141 IV. General GeoloGic Features........ 142 1. Main Relationships and Map....... 142 2. Résumé of Geologic History..143 V. Geologic Formations Represented...144 1. Broader Considerations......... 144 2. Geologic Section.......... 145 3. Nomenclature.......... 146 4. El Pasan Limestones..146 5. Santa Rita Limestone.... 146 6. Silver Shales........... 147 7. Bella Shales........... 147 8. Berenda Limestone..147 9. Grande Limestone... 148 10. Lake Valley Limestone........ 148 11. Sierra Limestone.......... 149 VI. Unconformities........... 149 VII. Geologic Structure.......... 150 1. Main Characteristics......... 150 2. Folding........... 1.50 3. Faultings........... 150 4. Relations of the Eruptives...153 VIII. Geologic Relations OF the Ore-Bodies...... 154 1. Governing Factom......... 154 2. Position.......... 154 3. Relations to Foldings...155 4. Relations to Lines of Dislocation... 15.5 5. Relations to Present Surface.Relief..156 6. Relations to Eruptive Rocks...157 7. Relations to Lithologic Nature of the Rocks.... 158 IX. MINERALOGIC CHARACTER OF THE ORES...... 158 X. Origin of the Ore.Deposits..159 1. General Statement......... 159 2. Original Source of the 0re.Materials...160 3. Contact-Metamorphism of the Region... 161 4. Process of 0re.Concentration..162 5. Lowering of Ground-Water Level..162 6. Formation of Cerargyritic Ores...163 XI. Recapitulation........... 168

Jan 1, 1909

By Henry M. Stanley

The methods about to be described have been tested in practice, and are believed to be specially adapted to such extended topographical surveys as mining engineers in particular are sometimes called upon to execute. The assistance of Mr. H. 0. Flipper in the preparation of this paper, and his practical authorship of the second part, is hereby acknowledged. I. Photographic SuRveying. The writer was recently employed; together with Mr. H. O. Flipper, to survey the properties of the Plata-Reina de Sonora Mining and Milling Company, situated in the mining district of Las Planchas, District of Magdalena, State of Sonora, Mexico. These properties, now owned by an American corporation, of which M. W. Evans, of New Orleans, is president, and Richard A. Pomeroy is resident superintendent, are famous in the history of Mexican mining, as the place where planchus, or bolas de plata were foulld about the beginning of the last century. Ward, the English CILargh d7Affaires in Mexico from 1826 to 1828, writing at that epoch, says: "The idea [that the ores in the north of Mexico were richer than those in the south] probably originated in the discovery of the famous bolas de plata [balls of silver] of Arizona [Planchas de Plata de Arizona, a stock-ranch in northern Mexico], in the beginning of the last century, which was, and probably still is, believed in Europe to be one of those fables with which mining countries always abonnd. But the attention of the present government of Mexico having been drawn to the subject, a search was made in the viceregal archives, by order of the president, for the correspondence which was known to have taken place respecting it in the year 1736. This correspondence I have seen, and I have in my possession a certified copy of a decree of Philip the Fifth, dated Aranjuez, 28th May, 1741, the ohject of which was to terminate a prosecution, instituted by the Royal Fiscal, against the discoverers of Arizona, for having defrauded the treasnry of the duties payable upon the masses of pore silver found there. The decree states the weight of the balls, sheets and other pieces of silver discovered (bolas, planchas, y otras piezas de plata), to have amounted to 165 arroba, 8 pounds, in all, 4133 pounds; and mentions particularly one mass of pure silver, which weighed 108 arrobas (2700

Jan 1, 1892