By P. Marier, T. R. Ingraham

When anhydrous cupric sulfate is heated in a stream of nonreactive gas, cupric oxysulfate is formed. When this reaction is complete, the cupric oxysulfate then decomposes to cupric oxide, which is the normal end product of reaction. The kinetics of each of these reactions has been studied using pellets prepared from finely divided cupric sulfate and from finely divided cupric oxysulfate. In each case, the reactant-product interface within the pellet is well-defined, and by normalizing the decrease in inter facial area with the weight fraction of the pellet decomposed it has been shown that the interface migrates into the pellet at a uniform rate at constant temperature. The activation energy estirnated for the decomposition of cupric sulfate is 57 ± 7 kcal per mole and that for cupric oxysulfate is 67 ± 8 kcal per mole. The rate of interfacial reaction is flow-sensitive, increasing with increasing flow of a sweep gas in the range from 50 to 2000 cu cm per min. The rate of decomposition is retarded by sulphur trioxide in the sweep gas. The relationship between sulfur trioxide Partial pressure and rate is consistent with the Langmuir Adsorption Isotherm governing the retention of sulfur trioxide in the interfacial layer. MOST of the work reported on the thermal decomposition of cupric sulfate and of cupric oxysulfate is related to the thermodynamics of the individual decompositions.'-4 No information is available on the rates of the individual reactions, on their activation energies, or on the effects of gas flow or of partial pressure of sulfur trioxide on the reaction rates. Some dubious conclusions based on relative reaction rates have been drawn from studies on the oxidation of sulfides. For example, on the basis of the products observed in a quenched system, it has been suggested5" that, when copper sulfide is roasted, the cupric oxide which is formed arises from the decomposition of either cupric sulfate or cupric oxysulfate. This is very difficult to reconcile with the thermodynamics of the C-S-O System,3 which support the probability that both cuprous oxide and cupric oxide precede cupric oxysulfate and cupric sulfate in the sequence of products formed during the oxidation of cuprous sulfide. In this paper the individual sulfate decomposition reactions will be examined and suggestions will be advanced for the mechanism of reaction. This will be based on the effects on reaction rate of changes in interfacial area, flow rate, and back-pressure of sulfur trioxide. EXPERIMENTAL Materials. The copper source material used in all experiments was Fisher Certified Reagent Grade anhydrous cupric sulfate, for which the following analysis was supplied by the manufacturer: chloride, 0.002 pct; alkalies and earths, 0.2 pct; insoluble, 0.002 pct; iron, 0.020 pct. Cupric oxysulfate was prepared by roasting cupric sulfate for 48 hr, with frequent rabbling, in an open tray in a muffle furnace maintained at 725°C. At this temperature, cupric sulfate develops about 0.16 atm pressure of combined sulfur trioxide, sulfur dioxide, and oxygen. Cupric oxysulfate develops only about 0.05 atm pressure, and is stable until

Jan 1, 1965

By F. W. Glaser, W. Ivanick

A pressure-sintering method was used to produce binder-free and very dense TiC specimens. Some physical properties of these TIC bodies were determined and found to compare favorably with those of certain cemented Tic grades. It was also observed that the hot transverse rupture strength of TiC bodies remained substantially the same regardless of the amount or type of binder material used. STUDIES of the structure and physical properties of refractory materials have been intensified recently because of the urgent need for nonstrategic materials that retain their strength at high temperatures. Research aimed at determining and improving the physical properties of cemented carbides and borides has been accelerated with a view toward possible use of such materials in connection with turbine blades, rocket nozzles, and other high temperature applications. On the hypothesis that the strength requirements in connection with some of the above applications could be met only by proper choice of cementing agents for such refractory materials, the literature describing the physical properties of borides or carbides was reviewed. However, with a few exceptions,'-" references were found only to compositions containing at least one or more auxiliary binder metals. Cobalt and nickel are among the most frequently employed cementing agents. The melting point of Tic (approximately 3250°C) and therefore the sintering temperature, at which notable densification of a cold pressed Tic powder compact could be expected in the absence of a liquid binder phase, is relatively high. The present study makes use of a high temperature, pressure-sintering procedure, recently described by one of the authors in connection with the sintering of binder-free ZrB,," to produce dense bodies of sintered Tic—free of any cementing agent. During the course of this sintering study, some physical properties of dense Tic bodies produced by this method will be discussed. Materials, Preparation of Samples, Testing Methods The procedure for the forming of Tic powder consisted of mixing graphite and TiH, powders in stoi-chiometric proportions, and heating this mixture in a H, atmosphere and carbon crucible by high frequency, to temperatures ranging between 1900° and 2100°C (3452" and 3812°F). The powdered carbide was then comminuted and screened to the desired particle size. Table I shows the chemical analysis of the two grades that were employed for the production of samples during this work. Bodies of Tic, approximately 2.5xlx0.5 cm were produced in graphite molds that were heated by direct conduction. Sintering was carried out at temperatures for time intervals ranging from approximately 0 to 30 sec under a constant pressure of about 1.3 tons per sq in. An alternate method for the production of samples consisted in cold pressing the individual Tic grades at pressures ranging from 4 to 10 tons per sq in. and sintering in a hydrogen atmosphere in graphite crucibles heated by high frequency induction. Sintering temperatures ranged from 2600° to 2900°C (4715° to 5255°F). Electrical testing was done by measuring potentiometrically the voltage drop over a length of 1.5 cm for a current of 10 amp at room temperature. Cross-sectional areas as well as densi-

Jan 1, 1953

By Howard N. Eavenson

Waste of coal, or perhaps more properly the percentage of its recovery in mining, has keenly interested me during an experience of over a half century in coal mining. In the early part of that time and until a few years after World War I the use of better mining plans and supervision resulted in an increased recovery. Since then, and particularly since controlled prices have been effective and mechanized mining has been extensively practiced, the tendency has all been toward lesser recovery in mining. The purpose of this paper is not to criticize the methods being used, which after all are the result of economic forces, nor to point to any particular mining method or to any locality where the best recovery is obtained, but to call attention to the tremendous waste of our national coal resources that is constantly continuing. A possible method of reducing this loss will be suggested, but without any illusions that it will be followed or that such attention will be paid to it. Average Recovery The actual average percentage of recovery of coal in the ground is not known. Many papers giving figures of recovery have been published but no definite base of measurement has been agreed upon by those presenting the data. As an example, the Pittsburgh bed can be considered—it has produced a greater output than any other and has been sold or leased at higher prices in place than any other coal bed. Over a large part of its area where high prices have prevailed it has been customary for many years to draw pillars. In these mines it has been usually assumed that the average recovery was higher than in other beds and percentages of recovery of 85 to 95 per cent are usually said to be realized. In all of these mines, however, it has been customary to leave from 4 to 8 in. in the bottom, and 10 to 16 in. in the roof; thus from 14 to 24 in. of coal has been left in the mines out of a total seam thickness of about 96 in., or 15 to 25 per cent of the total coal. No attempt is made to mine this coal for metallurgical purposes, owing to its impurities, although this unmined coal is of excellent quality and better than much of the coal used for steam purposes. If we add to this discard the coal usually lost in mining and those parts of the bed 'that must be left because of bad seam conditions, barrier pillars, reservations for buildings, gas and oil wells, one can easily see that the actual recovery from this bed cannot be more than 65 to 75 per cent. In addition, the rooster or rider or wild coal over the mining bed—often 3 to 4 ft. of coal, high in ash and sulphur but still good steam coal—is hardly ever mined, nor is any attempt made to mine it. It is safe to say that from a broad economic viewpoint not more than 50 to 60 per cent of the fuel value of this great seam is actually being recovered.

Jan 1, 1947

By Howard N. Eavenson

Waste of coal, or perhaps more properly the percentage of its recovery in mining, has keenly interested me during an experience of over a half century in coal mining. In the early part of that time and until a few years after World War I the use of better mining plans and supervision resulted in an increased recovery. Since then, and particularly since controlled prices have been effective and mechanized mining has been extensively practiced, the tendency has all been toward lesser recovery in mining. The purpose of this paper is not to criticize the methods being used, which after all are the result of economic forces, nor to point to any particular mining method or to any locality where the best recovery is obtained, but to call attention to the tremendous waste of our national coal resources that is constantly continuing. A possible method of reducing this loss will be suggested, but without any illusions that it will be followed or that such attention will be paid to it. Average Recovery The actual average percentage of recovery of coal in the ground is not known. Many papers giving figures of recovery have been published but no definite base of measurement has been agreed upon by those presenting the data. As an example, the Pittsburgh bed can be considered—it has produced a greater output than any other and has been sold or leased at higher prices in place than any other coal bed. Over a large part of its area where high prices have prevailed it has been customary for many years to draw pillars. In these mines it has been usually assumed that the average recovery was higher than in other beds and percentages of recovery of 85 to 95 per cent are usually said to be realized. In all of these mines, however, it has been customary to leave from 4 to 8 in. in the bottom, and 10 to 16 in. in the roof; thus from 14 to 24 in. of coal has been left in the mines out of a total seam thickness of about 96 in., or 15 to 25 per cent of the total coal. No attempt is made to mine this coal for metallurgical purposes, owing to its impurities, although this unmined coal is of excellent quality and better than much of the coal used for steam purposes. If we add to this discard the coal usually lost in mining and those parts of the bed 'that must be left because of bad seam conditions, barrier pillars, reservations for buildings, gas and oil wells, one can easily see that the actual recovery from this bed cannot be more than 65 to 75 per cent. In addition, the rooster or rider or wild coal over the mining bed—often 3 to 4 ft. of coal, high in ash and sulphur but still good steam coal—is hardly ever mined, nor is any attempt made to mine it. It is safe to say that from a broad economic viewpoint not more than 50 to 60 per cent of the fuel value of this great seam is actually being recovered.

Jan 1, 1947

By Walter Rose

It is the purpose of this note to call attention to the circumstance complicating the attainment of uniform gas-liquid distributions in multi-phase flow systems, and especially in those of the so-called Hassler type.' Although the complication arises directly as a consequence of gas compressibility and the dependence of fluid distributions on interfacial curvature phenomena, little reference to the problem has yet appeared in the literature.' In fact, it is only the paper of Geffen et al.3 which gives any experimental evidence that a problem exists. On the other hand, previous authorsl,4,5 have made the tacit, albeit fallaceous assumption that uniform gas-liquid distributions automatically are established in linear flow systems by the expedient of maintaining the pressure gradients equal in the flowing gas and liquid phases. Such a device, it can be shown, will succeed only if the immiscible fluids are both equally compressible or both essentially non-compressible. Another necessary condition required before uniform fluid-fluid distributions can be achieved is that the porous matrix is isotropic. Uniform fluid saturation distribution conditions obtain in isotropic media only when the curvature of each interface of contact between wetting and non-wetting fluids is everywhere the same throughout the interspaces. This is a necessary condition which follows from the consideration that variation in interfacial curvature gives rise to finite capillary pressure gradients and therefore to variation in the saturation distribution. That this is not a sufficient condition follows from the consideration that hysteric possibilities allow for different saturations even though the capillary pressure gradient is zero. In any event, it will- be recalled that it is the intent in the Hassler scheme of relative permeability determination' to obtain initially (by the capillary pressure drainage or imhibition process) uniform conditions of fluid distribution in the core sample, and then to maintain this uniformity during mixture flow so that the resultant fluid mobilities which are calculated will refer to steady-state transfer under fixed conditions of uniform saturation. If the flowing fluids are incompressible, it is recognized that employment of the same value of the pressure gradient in each fluid will result in maintenance of the initially obtained condition of zero capillary pressure gradient. On the other hand, the consequence of gas compressibility is that the gradient in the gas pressure varies from point to point in the flowing stream. and since the pressure gradient in an incompressible liquid is constant it is thus impossible to maintain zero capillary pressure gradient during the simultaneous flow of gas-liquid mixtures. Therefore, one would expect to observe a variation in the gas-liquid saturation in the directions of the capillary pressure gradients, depending in magnitude on the particular way saturation changed with capillary pressure. In order to formulate the manner gas compressibility effects prevent the attainment of uniform gas-liquid distributions during mixture flow, consider a linear flow system of unit length. As noted, it is necessary to assume an isotropic medium (viz. one where permeability is independent of position and direction). One then can arbitrarily set the pressure

Jan 1, 1951

By P. Niessen, S. J. Bercovici

RECENTLY Aust et al.&apos; proposed a model of non-equilibrium grain boundary segregation based on a vacancy gradient induced uphill diffusion process of solute to grain boundaries. According to their proposal, solute atoms which are attracted to vacancies would, during the cooling of a sample, migrate with vacancies toward grain boundaries (vacancy sinks) and thereby enhance the solute concentration in boundary regions. For solute atoms which are not attracted to vacancies no such boundary solute enrichment would be expected. These concepts were given experimental support by boundary and bulk mi-crohardness measurements of various thermally treated dilute zinc and lead alloys and also doped aluminum oxide. The underlying assumption in their work was that solute enrichment in boundary regions is indicated by higher microhardness values. From thermodynamic considerations1&apos;2 it appears that the solid-liquid solute distribution coefficient (K), defined as the concentration of solute in the solid to the concentration of solute in the liquid at equilibrium, indicates whether attractive or repulsive forces exist between vacancies and solute atoms. K < 1 indicates a solute-vacancy attractions, K > 1 indicates no, or a repulsive, vacancy-solute interaction. This note is to report on observations of different grain boundary etching phenomena in high purity zinc alloys. These phenomena appear to depend on whether a K < 1 or K > 1 solute is present. In experiments designed to measure directly the solute enrichment in grain boundary regions, samples of zone refined zinc with 0.1 at. pct solute additions were cooled from 380°C at a rate of 3°C per min. A surface layer of approximately 50 was then removed from the samples by chemical polishing. The samples&apos; surfaces were then protected by a chromating treatment such that in a subsequent etch only grain boundary regions were dissolved. The dissolved regions were approximately semicircular troughs, 10 µ in width. The grain boundaries were usually in the middle, i.e., at the bottom, of this trough. For zinc containing the K < 1 solutes cadmium and aluminum, the grain boundary was always indicated by a ridge as shown in Fig. 1. For pure zinc, and zinc containing the K > 1 solutes copper and gold, a groove at the bottom of the trough indicated the boundary position, Fig. 2., To test if these different grain boundary etching behaviors were possibly connected with the segregation process discussed above, the Zn-Cd alloy was again heated to 380°C and quenched into brine. After surface protection and etching it was found that this specimen no longer exhibited the grain boundary ridges but rather grain boundary grooves as shown in Fig. 2. It would appear, therefore, that the boundary ridge is a consequence of a process occurring during the slow cooling of the samples. From absorption spectrophotometric analysis it was found that for slowly cooled samples containing K < 1 solutes, the solute/zinc ratios of the material from the boundary trough were consistently considerably higher than the solute/zinc ratios of the bulk alloys. This boundary region solute enrichment was not observed in quenched samples. It is concluded therefore, that the boundary ridge shown in Fig. 1 is directly or indirectly connected with nonequilibrium solute segregation.

Jan 1, 1970

By William Romanoff

As you are no doubt aware, virgin copper, tin and zinc are strategic metals today and little, if any, is available in the manufacture of brass and bronze ingots. The source of alloys used in the manufacture of implements of war are, therefore, from ingots made almost exclusively from the refining of available scrap. It is amusing to hear of the unusual physical properties of various alloys because they mean nothing unless the foundryman is able to produce good sound castings. A discussion therefore means little unless something is said about the relative foundry practice of the various brass and bronze alloys. Among the factors that influence the quality of castings produced are: (I) improper gating, (2) wrong pouring temperatures, (3) poor sand conditions, (4) bad melting practice, (5) faulty pattern equipment, (6) metal. It seems to be the consensus of opinion that about 95 per cent of defective castings can be attributed to the first three causes. Metal while a source of trouble at times, is probably the least responsible for foundry difficulties. As you all know, a molder never makes a bad mold. His first thought is to blame the "damn" metal as this is the path of least resistance. Let&apos;s consider the "damn" metal and how it is made. In the manufacture of ingot, scrap is collected at various sources and is shipped to the refiner either directly or through the scrap dealer or broker. It is usually sorted, although not always. In working toward a specified chemical analysis, weighed amounts of various grades of scrap metals are melted, and then oxidized by blowing air through the molten bath to rid the metal of detrimental impurities or reduce them to within specification limits after which they are skimmed off with the aid of some added fluxes. The bath of metal is then poled with wood, chemically tested before and after additions are made to bring it up to required specifications, and finally poured into ingots, after which a final chemical and physical examination is made. As mentioned above, the impurities have either been eliminated or reduced to the point where they meet the specifications of all Government Agencies or Technical Societies. Therefore, why worry as to whether castings are to be made from strategic virgin metals or secondary ingots from available scrap. Tests have continuously been made and it is a proven fact that physical properties are no better from virgin metals than from secondary ingots of the same composition. It is definitely more fool-proof to make castings from secondary ingot than from virgin metals because if an error is made in weighing the copper, tin, lead or zinc of the latter, the analysis is off balance. If an error is made in weighing secondary ingots, you merely have more or less metal but the analysis remains constant. Furthermore, when pure copper is melted. it is susceptible to reducing gases as well as oxides. Secondary ingot is already alloyed with natural deoxidizers such as zinc, etc., and the volatilization of the latter also tends to eliminate reducing gases mechanically.

Jan 1, 1943

By Walter Rose

It is the purpose of this note to call attention to the circumstance complicating the attainment of uniform gas-liquid distributions in multi-phase flow systems, and especially in those of the so-called Hassler type.&apos; Although the complication arises directly as a consequence of gas compressibility and the dependence of fluid distributions on interfacial curvature phenomena, little reference to the problem has yet appeared in the literature.&apos; In fact, it is only the paper of Geffen et al.3 which gives any experimental evidence that a problem exists. On the other hand, previous authorsl,4,5 have made the tacit, albeit fallaceous assumption that uniform gas-liquid distributions automatically are established in linear flow systems by the expedient of maintaining the pressure gradients equal in the flowing gas and liquid phases. Such a device, it can be shown, will succeed only if the immiscible fluids are both equally compressible or both essentially non-compressible. Another necessary condition required before uniform fluid-fluid distributions can be achieved is that the porous matrix is isotropic. Uniform fluid saturation distribution conditions obtain in isotropic media only when the curvature of each interface of contact between wetting and non-wetting fluids is everywhere the same throughout the interspaces. This is a necessary condition which follows from the consideration that variation in interfacial curvature gives rise to finite capillary pressure gradients and therefore to variation in the saturation distribution. That this is not a sufficient condition follows from the consideration that hysteric possibilities allow for different saturations even though the capillary pressure gradient is zero. In any event, it will- be recalled that it is the intent in the Hassler scheme of relative permeability determination&apos; to obtain initially (by the capillary pressure drainage or imhibition process) uniform conditions of fluid distribution in the core sample, and then to maintain this uniformity during mixture flow so that the resultant fluid mobilities which are calculated will refer to steady-state transfer under fixed conditions of uniform saturation. If the flowing fluids are incompressible, it is recognized that employment of the same value of the pressure gradient in each fluid will result in maintenance of the initially obtained condition of zero capillary pressure gradient. On the other hand, the consequence of gas compressibility is that the gradient in the gas pressure varies from point to point in the flowing stream. and since the pressure gradient in an incompressible liquid is constant it is thus impossible to maintain zero capillary pressure gradient during the simultaneous flow of gas-liquid mixtures. Therefore, one would expect to observe a variation in the gas-liquid saturation in the directions of the capillary pressure gradients, depending in magnitude on the particular way saturation changed with capillary pressure. In order to formulate the manner gas compressibility effects prevent the attainment of uniform gas-liquid distributions during mixture flow, consider a linear flow system of unit length. As noted, it is necessary to assume an isotropic medium (viz. one where permeability is independent of position and direction). One then can arbitrarily set the pressure

Jan 1, 1951

By E. Maxwell, C. J. Bechtoldt, H. C. Vacher

IN the course of an investigation of the properties of metals at low temperature there was occasion to determine the constitution of four iridium-osmium alloys. There is very little information in the literature1 on the constitution of synthetic Ir-0s alloys. Zvyagintzev&apos; s has made a comprehensive study of different natural Ir-0s alloys and concludes that alloys containing more than 32 pct 0s have the close-packed hexagonal structure of osmium, whereas those containing less than 32 pct 0s have the face-centered cubic structure of iridium. The alloys studied in this work were prepared by the American Platinum Works, Newark, N. J., and were received in the form of fragments approximately 1.5 mm average diameter. The fragments had been obtained by crushing ingots made by fusing charges of iridium and osmium under an arc and air cooling. The ingots were not given a homogenizing heat treatment. Sample fragments Table I. Results of X-Roy Diffraction and Microscopic Examinations Phases Present as Determined by X-ray Diffraction Osmium Alloy Close- Iridium Face- Packed Centered Osmium, Iridium, Hexagonal Cubic Mlcro- WtPot Wt Pct Structure Structure scope 0 99.9 None Present 1 23.6 76.4 None Present 1 38.7 61.3 Present Present 2 59.4 40.6 Present Present 2 79.0 21.0 Present Not detected 2 99.9 0 Present None 1 Note: Chemical analyses of the iridium, osmium, and alloys were furnished by the American Platinum Works. of the iridium and osmium used in making the alloys also were included. Several fragments of each metal and alloy were examined microscopically and by X-ray diffraction. For the X-ray method the fragments were crushed further to pass a 270-mesh screen, then sealed in evacuated fused-silica tubes, heated to 1100°C for 18 hr, and allowed to cool in the furnace. Powder X-ray diffraction patterns were obtained from the annealed fragments by means of a Norelco camera having a diameter of 114 mm, and unfiltered cobaIt radiation. For the microscopic examination several fragments in the as-received condition were mounted in Melmac, (American Cyanamid Co.) and ground using the conventional series of abrasive papers. The polishing was done with 0-2 diamond abrasive on a Microcloth (Buehler Ltd.) lap, wet with xylene. After polishing, the surface was etched electrolytically in a 10 pct solution of chromic acid or in a 10 pct solution of potassium cyanide. Both reagents attacked the osmium-rich constituent, whereas the iridium constituent was attacked slightly by the chromic acid reagent and not noticeably by the potassium cyanide reagent. The results of the X-ray diffraction and microscopic examinations are summarized in Table I. Fig. 1 shows the microstructure of a 21 pct Ir-79 pct 0s alloy. The results indicate an appreciable solid-solu-bility range of osmium in iridium as was reported by Zvyagintzev.&apos; The solid-solubility range of iridium in osmium is more restricted, apparently less than 21 pct Ir. This implies a large range of composition in which two phases can coexist that was not reported by Zvyagintzev.

Jan 1, 1955

By C. E. Sims

In some experimental work conducted several years ago, it was noted that sulphur seemed to have a distinct influence on grain size of carbon steels. 111 order to check this observation, a series of S..A.E. 1040 steels was made with the normal composition held as nearly constant as possible. The steels were made with three sulphur levels, which were 0.012, 0.024 and 0.038 per cent sulphur, respectively. For each of the sulphur levels, steels were made with only silicon deoxidization and with aluminum additions of 0.1015, 0.025, 0.050 and 0.10 per cent. The melting medium was an acid-lined high-frequency induction furnace. These steels were forged and rolled and differentiall!. quenched from temperaturcs in the range of 1500O to 1800°F. After this, the A.S.T.M. grain size was determined and plotted as in Fig. I. It will be noted, first of all, that the aluminum-free steels had filler grain size with higher sulphur when heated to 1500, but that this condition was reversed at 1700°. When aluminum was added to produce fine grain size, the steels in the lowest sulphur level were fine-grained only to 1600°. and then only with an addition of one pound of aluminum per ton. The medium sulphur steels werc fine-grained to 1600&apos; with a wider range of aluminum addition. The steels in the highest sulphur level were fine-grained at 1600° over a still wider range of aluminum additions and fine- grained at 1700° with an addition of one pound per ton. Fig. 2 shows curves of the grain-coarsening temperature for these steels and illustrates how sulphur and aluminum combine to give greater inhibition to grain growth than aluminum alone. Only the highest sulphur steels have a grain-coarsening temperaturc above 1700°.. At 1650°, the low sulphur steel is fine-grained only at its peak, while the highest sulphur steel is fine-grained over a wide range. In these tests, one pound of aluminum per ton gave the best results; this is equivalent to about 1 1/2 lb. per ton for commercial condition. IllcQuaid-Ehn tests made on these steels showed the same trend but to a lesser degree. The tests were repeated on a series of S.A.E:. 1015 steels with sulphur levels of 0.02 and 0.03j per cent. Aluminum additions were made in the range from 0.025 to 0.15 per cent. These steels were forged and rolled, normalized at 2000°F. to put them all in the same starting condition, then reheated to various temperatures from 1600" to 1800" and cooled at rates that would allow ferrite precipitation in the austenitic grain boundaries. The results of these tests arc shown in Fig. 3. It will be noted that. up to the temperature of 1650°, there is very little difference in the grain size obtained from the two levels of sulphur. .At temperatures of 1700° and 1750°, however, the lower sulphur steel was fine-grained only with an aluminum addition of 1 1/2 lb, per ton;

Jan 1, 1945

By M. T. Hepworth, A. K. Stewart

Iron containing 0.1 pct A1 and -0.9 pct P by weight was internally oxidized in the temperature range 900° to 1300° C, where the bcc structure is stabilized by phosphorous. By measuring the depth of penetration of oxygen with time in an internally oxidized zone for an imposed surface oxygen potential, oxygen permeability was determined. The dgfusion coefficient of oxygen in iron was then calculated using known solubility data, yielding the expression: where Do is the diffusion coefficient of oxygen in bcc iron in sq cm per sec and T is temperature in OK. RECENTLY Hepworth, Smith, and Turkdoganl measured the diffusivity of oxygen in bcc iron and reported the temperature dependence of diffusivity from data determined in the a, and 6 temperature ranges. Subsequently Swisher and Turkdogan&apos; have measured the diffusivity of oxygen in fcc iron. Internal oxidation techniques were employed by these investigators and in this current study. The analysis of this technique is developed by wagner3 (presented in English by Hauffe4 and Rapp 5). In this present study bcc iron stabilized by phosphorous was used to determine oxygen diffusivity in the temperature range 900° to 1300°C. Meijerin 6 has studied oxygen permeability in this temperature range using bcc iron stabilized with 5 pct Sn. Other inves- tigators who have studied oxygen permeability in bcc iron at other temperatures are Schenck et al., 7 Bohen-kamp and Engell, 8 and Bradford. EXPERIMENTAL Electrolytic iron of 99.99 pct purity was alloyed to contain 0.897 pct P and 0.093 pct Al. The maximum weight percent phosphorous required to stabilize bcc iron between 910" and 1392°C is 0.51 pct as determined by Haughton,10 0.42 pct by Roquet and jegaden," and 0.58 pct by vogel,12 with the latter value preferred by Hansen.13 Microprobe analysis indicated that there was no segregation of the phosphorous either before or after permeability studies; therefore, the quantity of phosphorous added was assumed to be sufficient to stabilize the bcc structure. Furthermore, the permeability results of studies on this alloy agreed substantially with interpolated values from previous data on bcc iron.&apos; An ingot of the Fe-P-A1 alloy was hot-rolled to a l-in.-thick slab. Specimens were machined to dimensions: 13/8 by $ by 1/4 in. The experimental apparatus and procedure used have been described before.&apos; A constant oxygen potential was established by passing argon and hydrogen through a column of oxalic acid dihydrate, which has a water vapor pressure which is well-known as a function of temperature. Slab specimens were exposed to a gas mixture sufficiently lean in oxygen to prevent the formation of a surface oxide for predetermined temperature for selected times. The specimens were then quenched, sectioned, and examined metallo-graphically. All quenched specimens were iron-plated to provide protection from the outside sample edge during polishing. Fig. 1 shows a typical microstruc-ture for a specimen oxidized at 953°C for 48.00 hr at a water vapor-to-hydrogen pressure ratio of 0.20. DISCUSSION AND RESULTS The following equation was derived by Hepworth et al.&apos; from Wagner&apos;s kinetic expressions for internal oxidation:

Jan 1, 1969

By R. W. Fenn, H. A. Lepper, W. R. Hibbard

A. J. Shaler—I should like to congratulate the authors on the presentation of this paper, which we have been awaiting a long time. The view they have taken of the sintering process, namely that voids are comparable to particles of a second phase capable of dissolving to a slight extent in the metal phase, is an interesting but dangerous one. Pines has given a first-order solution of the problem and Has predicted a decrease in the concentration of pores near the surface. The authors of the present paper have experimentally demonstrated the second-order effects, that is, the diffusion of the space phase between voids of different sizes, and also the movement of atoms from highly curved parts of a void to less curved regions of the same void. I have recently calculated the rate of vapor-phase transport within odd-shaped pores in copper at 850 °C and found that probably at that temperature volume flow is the more rapid shape-changing mechanism. The authors of the present paper have found that at 1000°C, vapor-phase transport is dominant. There is no disagreement here, I think. The dominant phenomenon can easily be different in different temperature ranges and with different pore shapes: I used a cylinder going to a sphere, not a tricuspid going to a "triple cuspidor." But there is some danger in the other art of the explanation, that is, in the study of the diffusion of vacancies from a pore to its neighbors and to the outside. A vacancy is very different in dimension from an atom. When it moves, it carries a field of elastic strain. This has to be taken into account. A concentration gradient of vacancies can cause them to diffuse. But in the absence of such a gradient, they can be made to diffuse by a field of stress. What happens in some of our experiments, and it is most noticeable in the shrinkage of synthetic cylindrical pores, like the tubes we have been working with, may be broken down into the following steps. (1) The presence of a surface establishes a vacancy concentration gradient, as Dr. Kuczynski and the present authors have shown. (2) Vacancies then diffuse in order to decrease this gradient. (3) In so doing, they cause an elastic field to be built up in such a direction as to oppose the diffusion, so that it slows down until it reaches a steady-state rate. (4) The steady-state flow is due to the fact that the surface tension acting on curved surfaces applies a stress to the system which itself mechanically causes vacancy diffusion. What I have said is that the diffusive types of flow of the authors and of Dr. Kuczynski are transient phenomena which soon stop if the pores are large. We are then left with a mechanical problem only, and our researches have not yet disclosed just what the mechanism of flow is; it may be a slip process, or it may take place by a vacancy diffusion of the type Nabarro has de-

Jan 1, 1951

By T. D. Tiemann

The caustic extraction of silica from Wisconsin and Minnesota taconite was investigated by bomb digestion over the temperature range from 312 to 40S°F at caustic concentrations from 25 to 500 gpl. Residual concentrates containing as much as 65 pct iron were obtained. The high rate of silica extraction is related to a microcrystalline variety of quartz, since it is shown that the rate of extraction of silica from quartz is directly proportional to its surface area. Increasing dependence on foreign ore reserves makes the need for developing the technology necessary for treatment of our low grade ores even greater than it was at the time of World War 11, when much research was conducted on the extraction of alumina from clays. Representative of these were the studies carried on at the University of Illinois.&apos; More recently, the U. S. Bureau of Mines investigated the production of alumina from anorthosite, and currently the aluminum industry is showing renewed research interest in this field. The studies reported here are part of a continuing research program based on the above concepts and aimed at the eventual development of processes for the treatment of low grade ores, particularly those of iron. The fact that large reserves 3 of low grade nonmagnetic taconite are contained in the iron formation of the Wisconsin Gogebic range have made this ore an important and attractive target for investigation. The idea of removing silica by caustic extraction is not new.495 The digestion in caustic solution of ground flint, diatomite, and other forms of chalcedonic silica is the basis for the production of soluble sodium silicates by the wet-process. Upgrading bauxites by the caustic extraction of silica has been investigated6 and is the subject of a German patent.7 Although mention is made by Roe&apos; of the caustic extraction of silica from low grade Michigan and Wisconsin iron ores, and he lists a number of patents and references on the subject, recent work in the field does not appear to be extensive. As far as the author knows, there has been no work in this field on these particular ores. It is hoped that this paper will stimulate further investigation which will eventually lead to an econclmic means of processing these large low grade reserbes. TACONITES The taconites investigated in this study were from Minnesota and Wisconsin. That from Minnesota, a semi-taconite, Nas obtained from the Oliver Iron Mining Division, U. S. Steel Corporation, and represents a sample of an oxidized iron formation from their King Mine on the Mesabi range. The Wisconsin taconite came originally from the trench sampling of the U. S. Bureau of Mines, and represents a composite of the Norrie, Pabst, Yale, Plymouth, and Pence members of the Gogebic iron formation. Assays on these samples are given in Table I. A typical calcu1atr:d average analysis of the Wisconsin taconite is given in Table 11. Chemically, the Minnesota semi-taconite sample contains about 39 pct iron and 39 pct silica, while the Wisconsin taconite contains 30 pct iron and 53 pct silica, both on the dry basis.

Jan 1, 1962

By A. T. Robinson, J. E. Dorn

The electrical resistivities of aluminum alloys containing CU, Ge, Zn, Ag, Cd, and Mg were found to increase linearly with the atomic percentage of the solute atoms. Application of Linde&apos;s rule to these data suggests that each aluminum atom contributes 2.5 electrons to the metallic bond. ALTHOUGH aluminum invariably exhibits a Jt\. valence of three in ionic solids, it does not follow necessarily that its valence in the metallic state is also three. As a matter of record, many properties suggest that the number of bonding electrons in metallic aluminum is less than three. For example, as shown in Fig. 1, the atomic radii1 of the metallic elements in the solid state decrease with increasing atomic number at the beginning of any one period. The atomic radius of aluminum, however, is greater than that which would result from a regular decrease in atomic radius with increasing atomic number, suggesting that the number of bonding electrons in aluminum is somewhat less than three. Correlated with the anomalously large atomic radius of aluminum is its abnormally low melting temperature. As the atomic numbers increase in any one period, the melting temperatures of the metallic elements increase.&apos; As shown in Fig. 2, however, the melting temperature of aluminum (13) is only slightly greater than that of magnesium (12). Again the number of bonding electrons in metallic aluminum appears to be nearer two than the expected value of three. In addition Ageev and Ageeva3 alculated the electron density distribution in the aluminum lattice. A comparison of such electron density curves for various assumed valence states of aluminum with experimentally determined curves suggests that the actual number of bonding electrons in metallic aluminum is between two and three. Hume-Rothery and Raynor&apos;, " have suggested that the above-mentioned abnormalities are associated with the overlapping of the Brillouin zones of metallic aluminum when it is in the usual face-centered cubic structure. The importance of the number of bonding electrons in metals has been extended recently into the field of mechanical properties. While formerly it was thought that the plastic properties of alpha solid solutions were primarily dependent upon the lattice strain induced in the solvent by the solute, it is now known that the difference in the number of bonding electrons of the solute and solvent also has its influence on the plastic properties."1&apos; In order to achieve a satisfactory correlation of the effect of alloying elements on the plastic properties of aluminum alloys,"&apos;T however, it was necessary to assume that the number of bonding electrons contributed by aluminum was about two rather than the expected value of three. It appeared to be desirable, therefore, to seek other criteria for evaluating the number of bonding electrons contributed by aluminum to its alpha solid solutions, especially in view of the practical as well as the theoretical importance of the effect of valency on the plastic properties. Norbury&apos; was perhaps the first to illustrate that the increase in resistance of alpha solid solutions is associated with the differences in valence of the solute and solvent metals. In a series of illuminating investigations Linden-&apos;&apos; has shown that the electrical

Jan 1, 1952

By James Terry Duce

In order to facilitate interpretation of the data in this chapter, we print the following excerpts from circulars to authors, compiled by Mr. Frank A. Herald when he was Vice Chairman for Production of the Petroleurn Division: Generally in Table 1 the unit for presentation of data is a field. For our purposes a field is defined as the whole of a surface area wherein productive, locations are continuous. Such unit commonly includes and surrounds nonproductive areas. Such unit commonly includes a great variety of geologic conditions-—several units of continuous productive reservoirs of distinctly different structure and of distinctly different stratigraphy. Therefore it is hoped that our authors will subdivide "field" so as to enable students to make analyses that may have scientific and/or commercial value. As to each space in the tabulation, it is either (1) not applicable, (2) the proper entry is not determinable, (3) the proper entry is determinable, but not determinable from data available to the author, (4) the proper entry is determinable by the author. In spaces not applicable, the author will please draw horizontal lines; in spaces where the proper entries are not determinable, the author will please insert 2; in spaces where the proper entries are determinable but not determinable from data available to the author, the author will please insert y; in spaces where the proper entries are deter-minable by the author he will, of course, make such entries. Generally, y implies a hope that in some future year a definite figure will be available. Inability to determine precisely the correct entry for a particular space should not lead the author to insert merely y. Contributions of great value may be made by the author in many cases where entries are not subject to precise determination. In such cases the author should use his good judgment and make the best entry possible under the circumstances. For many spaces, the correct entries represent the opinion of the author (for example, "Area Proved") and in such cases the entries need not be hedged to such extent as in cases where the quantities are definite yet can be ascertained only approximately by the author. In cases under definite headings but where figures are only approximate, the author may use 2. For example, if the total production of a field is known to be between 1,800,000 and 1,850,000, the author may report 1,8xx,xxx; or if the production is between 1,850,000 and 1,900,000, the author may report 1,9xx,xxx. Where a numeral is immediately to the left of x or y, such numeral represents the nearest known number in that position. As to quantity of gas produced from many fields the question will arise as to whether the figures should include merely the gas marketed or should include also estimates of gas used in operations and gas wasted. Although rough approximations may be involved, our figures should represent as nearly as possible the total quantity of gas removed from the reservoir.

Jan 1, 1936

By L. E. Shiffman

This paper describes the operation of two kerosine flotation plants in Alabama for cleaning —10 mesh bituminous coal. One plant treats washer sludge, the other raw coal. Data on capacity efficiency and capital and operating costs is given. Methods for increasing cell capacity are discussed. IN cleaning coal it has long been recognized that methods which give excellent results for the coarser sizes may give poor or even no cleaning for the finer sizes. Effective cleaning of the fines, therefore, is usually a separate and distinct problem. For many years the problem of fines was considered of relatively minor importance. Now there is growing interest in methods of cleaning the fine sizes of coal because: 1. There are more fines. Increasing mechanization and the adoption of full seam mining methods have resulted in the production of a greater percentage of smaller particles than were produced by hand loading methods. 2. The fines have deteriorated in quality. The same causes that have led to increased quantity have also operated to decrease quality through greater contamination with slate, rock, and other diluents. 3. The fines have become more valuable. When coal was comparatively cheap, loss of the finer sizes was tolerated but, with the rapid increase in the cost of mining coal, it has become imperative that the maximum amount of clean coal be recovered from the mixture of coal and rock delivered to the tipple. 4. In many cases, the fines have become a stream pollution problem. Increasing governmental activity and legislation to prevent stream pollution often have made it necessary to retain the fine material which formerly was permitted to escape with the washer effluent into flowing streams. The Sloss-Sheffield Steel and Iron Co. operates four coal mines, all within a 20-mile radius of Birmingham, Ala., with a total annual production of 1,-250,000 tons of washed coal. Three of these mines are in the Mary Lee seam and one in the Jefferson seam. Although some steam and domestic coals are produced, the major portion of the coal is used to make coke for blast furnace operation. Fine coal is desirable for coking, and all the coal so used by Sloss is crushed to 1/4 in. Therefore, there is no problem of an outlet for even the finest sizes of coal. Since the coal is used for metallurgical purposes, low ash is of greater importance than would be the case if it were used for steam generation or domestic heating. Based on present blast furnace practice at Sloss, it is calculated that each percentage of ash in the coal carries a penalty of $0.22 per ton of coal. Thus there is a considerable margin for operating costs in a fine coal cleaning method that will result in materially lowering the ash content of the cleaned coal. Development of Fine Coal Cleaning Problem In 1942 Sloss reopened its Bessie mine and constructed at this location a new preparation plant to clean 11/4 in. x 0 coal from the Mary Lee seam.

Jan 1, 1951

By L. E. Shiffman

This paper describes the operation of two kerosine flotation plants in Alabama for cleaning —10 mesh bituminous coal. One plant treats washer sludge, the other raw coal. Data on capacity efficiency and capital and operating costs is given. Methods for increasing cell capacity are discussed. IN cleaning coal it has long been recognized that methods which give excellent results for the coarser sizes may give poor or even no cleaning for the finer sizes. Effective cleaning of the fines, therefore, is usually a separate and distinct problem. For many years the problem of fines was considered of relatively minor importance. Now there is growing interest in methods of cleaning the fine sizes of coal because: 1. There are more fines. Increasing mechanization and the adoption of full seam mining methods have resulted in the production of a greater percentage of smaller particles than were produced by hand loading methods. 2. The fines have deteriorated in quality. The same causes that have led to increased quantity have also operated to decrease quality through greater contamination with slate, rock, and other diluents. 3. The fines have become more valuable. When coal was comparatively cheap, loss of the finer sizes was tolerated but, with the rapid increase in the cost of mining coal, it has become imperative that the maximum amount of clean coal be recovered from the mixture of coal and rock delivered to the tipple. 4. In many cases, the fines have become a stream pollution problem. Increasing governmental activity and legislation to prevent stream pollution often have made it necessary to retain the fine material which formerly was permitted to escape with the washer effluent into flowing streams. The Sloss-Sheffield Steel and Iron Co. operates four coal mines, all within a 20-mile radius of Birmingham, Ala., with a total annual production of 1,-250,000 tons of washed coal. Three of these mines are in the Mary Lee seam and one in the Jefferson seam. Although some steam and domestic coals are produced, the major portion of the coal is used to make coke for blast furnace operation. Fine coal is desirable for coking, and all the coal so used by Sloss is crushed to 1/4 in. Therefore, there is no problem of an outlet for even the finest sizes of coal. Since the coal is used for metallurgical purposes, low ash is of greater importance than would be the case if it were used for steam generation or domestic heating. Based on present blast furnace practice at Sloss, it is calculated that each percentage of ash in the coal carries a penalty of $0.22 per ton of coal. Thus there is a considerable margin for operating costs in a fine coal cleaning method that will result in materially lowering the ash content of the cleaned coal. Development of Fine Coal Cleaning Problem In 1942 Sloss reopened its Bessie mine and constructed at this location a new preparation plant to clean 11/4 in. x 0 coal from the Mary Lee seam.

Jan 1, 1951

By John T. Galey

A combination of two factors in addition to the current Federal drilling and price regulations reduced by 120 from I942 the number of new wells completed in southwestern Pennsylvania during the year. No new prospective area was found comparable to the Armbrust gas pool, Westmoreland Co., which accounted for a seventh of the last year&apos;s drilling, and it is considered doubtful whether, even if such a field had been discovered, the drilling contractors, who have been seriously affected by the manpower shortage, could have drilled many more wells than they did during the year. New wells totaling 445 were completed for a combined footage of over 1,250,000 Dry holes numbered 131 and had a footage of nearly 400,000. Old wells drilled deeper total 55, of which 17 were found nonproductive. Shallow Development Oil Oil completions yielded an initial of only slightly over one hundred barrels from 21 wells for about the same per well average as that of a year ago. However, 65 bbl. of this total came from two wells in two new strikes. The footage drilled of nearly 33,000 gives an average of nearly I00 ft. less per well than a year ago. Two old wells drilled deeper had a combined initial of only 4 bbl. The largest oil well of the year, 40 bbl., was found in the Speechley (U. Dev.) sand at a depth of 3492 ft. in German township, Fayette County. The location is several miles east of the nearest oil production hut as the area that could be occupied by a pool is fairly well delimited by drilling, the extent of this production would not appear to be large. The other notable oil production was found in the Dunkard (Penna.) sand, Cumberland township, Greene County, at a depth of 1065 ft. Here the first well had an initial of g bbl. and the second 25 bbl. However, a third proved dry, and as this area is also delimited by drilling, the pool doubtless will be of small area. Gas Gas completions yielded an initial of slightly over one hundred million cubic feet per day and new wells, totaling 303, account for all but four million of this volume. Old wells drilled deeper, numbering 35, found gas. The per well average in new drilling of approximately 320 M cu. ft. is nearly 165 M cu. ft. less than a year ago and the total footage is slightly over 830,000, which is about a quarter of a million feet less than in 1942. Average rock pressure of new completions is approximately 365 lb. per sq. in. The entire volume of new production is from the Upper Devonian or higher stratigraphic horizons. In Allegheny County, the grestest activity was in Forward and Plum townships. Wells there account for more than one half the completions. One large well was drilled in Forward township and an open flow of 3.623 million cubic feet was found in an old Gantz (U. Dev.) sand area. The top of the sand was encountered

Jan 1, 1944

MORE than 5000 miners and suppliers descended upon Denver to make the American Mining Congress&apos; four-day metal mining show one of the most extravagant equipment displays ever assembled in one place at one time. The most recent developments in equipment for mining, milling, and processing ore were shown by the 146 exhibitors at Denver&apos;s new City Auditorium which covers 57,000 sq ft of floor space. Other displays were placed in the open air opposite the auditorium site. Registration desks were opened Sunday, Sept. 21. A field trip to the Colorado School of Mines at Golden was the featured activity of the day. Official opening of the show took place on Monday, and presided over by Howard I. Young, president of American Zinc, Lead & Smelting Co.; Otto Herres, vice president, Combined Metals Reduction Co.; William J. Coulter, vice president, Climax Molybdenum Co.; Charles B. Stainback, Westinghouse Electric Corp.; and Merrill E. Shoup, president, Golden Cycle Corp. Convention welcoming addresses were delivered by a representative of Mayor James Q. Newton, of Denver, and Gov. Daniel V. Thorton of Colorado. Following the formal opening ceremonies a round table discussion dealt with the "Paley Commission Report" formally called Resources for Freedom. Participating in the panel were: Arthur H. Bunker and George R. Brown, members of the Paley commission; H. I. Young, president of the American Mining Congress; Horace M. Albright, president of U. S. Potash Co.; Evan Just, vice president, Cyprus Mines Corp.; Donald H. McLaughlin, president, Homestake Mining Co.; E. H. Snyder, president Combined Metals Reduction Co.; Simon D. Strauss, vice president, American Smelting & Refining Co.; Sen. H. C. Dworshak (R.-Idaho) ; Ira B. Joralemon, consulting engineer; Jess Larson, De fense Materials Procurement Agency; and Andrew Fletcher, president of St. Joseph Lead Co. The panel discussed the report for six hours, adding a great deal of information to the already voluminous amount which has been gathered concerning it. Three objections to the report frequently mentioned were: 1-the multilateral contract; 2-international buffer stocks; 3-international buffer stocks combined with limited quota arrangements. Points on which the panel commended the report were its recommendations for acceleration of topographic and geologic mapping of the United States and Alaska; recognition of the principle of percentage depletion for metals and minerals; and advocation of removal of the present limitations on the expensing of exploration costs applicable to minerals. Technical sessions were held throughout the four days of the meeting. Included in the program were: Progress in Mechanication; Small Mines; Public Lands; Open Pit Mining; Manpower-Labor Relations; Shaft Sinking; Roof Support; Taxation, Gold, Silver and Monetary Policy; Advances in Mill Practices; Special Conference on Strategic Materials; Uranium Mining-Atomic Energy; Prospecting and Exploration; New Metallurgical Processes; and Rock Breaking. About 45 papers and several panels were presented during technical sessions. Formal and informal social functions consumed the remaining time of the convention. Three locations were needed to handle the huge throng attending the Mining Jamboree Monday evening. The only other sponsored social function took place Thursday evening. A great many informal gatherings, chiefly convivial, were held in manufacturers&apos; courtesy rooms-called wet stopes. Field trips included Cripple Creek, Pueblo, Climax -Leadville-Gilman, Colorado Plateau-Grand

Jan 1, 1952

By James Terry Duce

In order to facilitate interpretation of the data in this chapter, we print the following excerpts from circulars to authors, compiled by Mr. Frank A. Herald when he was Vice Chairman for Production of the Petroleurn Division: Generally in Table 1 the unit for presentation of data is a field. For our purposes a field is defined as the whole of a surface area wherein productive, locations are continuous. Such unit commonly includes and surrounds nonproductive areas. Such unit commonly includes a great variety of geologic conditions-—several units of continuous productive reservoirs of distinctly different structure and of distinctly different stratigraphy. Therefore it is hoped that our authors will subdivide "field" so as to enable students to make analyses that may have scientific and/or commercial value. As to each space in the tabulation, it is either (1) not applicable, (2) the proper entry is not determinable, (3) the proper entry is determinable, but not determinable from data available to the author, (4) the proper entry is determinable by the author. In spaces not applicable, the author will please draw horizontal lines; in spaces where the proper entries are not determinable, the author will please insert 2; in spaces where the proper entries are determinable but not determinable from data available to the author, the author will please insert y; in spaces where the proper entries are deter-minable by the author he will, of course, make such entries. Generally, y implies a hope that in some future year a definite figure will be available. Inability to determine precisely the correct entry for a particular space should not lead the author to insert merely y. Contributions of great value may be made by the author in many cases where entries are not subject to precise determination. In such cases the author should use his good judgment and make the best entry possible under the circumstances. For many spaces, the correct entries represent the opinion of the author (for example, "Area Proved") and in such cases the entries need not be hedged to such extent as in cases where the quantities are definite yet can be ascertained only approximately by the author. In cases under definite headings but where figures are only approximate, the author may use 2. For example, if the total production of a field is known to be between 1,800,000 and 1,850,000, the author may report 1,8xx,xxx; or if the production is between 1,850,000 and 1,900,000, the author may report 1,9xx,xxx. Where a numeral is immediately to the left of x or y, such numeral represents the nearest known number in that position. As to quantity of gas produced from many fields the question will arise as to whether the figures should include merely the gas marketed or should include also estimates of gas used in operations and gas wasted. Although rough approximations may be involved, our figures should represent as nearly as possible the total quantity of gas removed from the reservoir.

Jan 1, 1936