By Dirk Verhulst

The Altair process employs digestion of ilmenite ore in concentrated hydrochloric acid, solvent extraction to concentrate Ti in a purified stream and spray hydrolysis to produce a TiO2 hydrate, followed by final calcining and milling. HCl gas is regenerated by pressure-swing distillation and reinjected in the leaching solution. All chloride streams are recycled. Chromium compounds generally remain in the residue. Solvent extraction provides flexibility for the removal of naturally occurring radioactive elements (NORMs) present in some ilmenites. The process was previously tested at a 5 t/day feed scale. Recent work at pilot scale (40 liter reactor) led to further improvements. Recovery of Ti in solution is now at least 90% with ilmenite ores, while crystallization at lower temperature lowers the amount of Fe in solution to about 5 g/l and improves solvent extraction, which is now conducted in columns. Higher Ti and lower Fe concentrations in the SX eluate improve the economics. A new formula for pigment production via spray hydrolysis produces a pigmentary base with a narrow particle size distribution.

Jan 1, 2003

By Rafael Padilla

In the production of copper from chalcopyrite (CuFeS2) concentrates by the smelting and converting technology, the ambient pollution with gaseous S02 and toxic metals such as arsenic compounds is still a serious problem, especial1y in the converting step due to the batch nature of the conventional Peirce Smith process. Non-SO2 emitting alternatives are leaching processes. However, few of them have had a limited industrial application and they are not very effective in discarding safely the toxic impurities. A combination of pyro-hydrometal1urgical methods: the sulfidation of chalcopyrite and subsequent leaching of the sulfidized material is a non-polluting alternative to treat not only clean chalcopyrite concentrates but also complex chalcopyrite-enargite concentrates. In this article, this alternative is discussed concerning the thermodynamics and kinetics of the sulfidation of chalcopyrite with gaseous sulfur. The kinetics of the leaching of the sulfidized concentrate in an H2SO4-NaCI-O2 system is also discussed.

Jan 1, 2003

By Yuri Gelfgat

"This paper presents some results of the investigation of the steady magnetic field influence on hydrodynamics and heat/mass transfer in processes of semiconductor single crystal growth (Si, Ge, InSn). The investigation employed mathematical and physical simulation techniques of relevant processes and full-scale experiments on growth facilities. A number of additional MHD phenomena have been found generated in the melt due to the rearrangement of flow pattern, the formation of specific convective cells, and the origin of MHD boundary and shift layer.IntroductionMagnetohydrodynamic (MHD) means of creating forces by contact-free methods in liquid conducting media have been widely used in the production of volume semiconducting single crystals. The goal of this method is to control convective transfer processes in the melt volume and on the crystallization front [1-3]. This is due to the sufficiently high conductivity of semiconductor melts (s = 104 /106 O1m-1 ) and an obvious relationship between the hydrodynamics in the melt and at interfaces and the conditions of formation of single crystals and their quality [ 1].All types of MHD effects rest upon the generation of volume electromagnetic forces in the melt by various means as well as on the possibility to direct them arbitrary in space and to adjust easily their absolute values. Fig. l presents different means how to implement MHD phenomena during single crystal growth. It should be emphasized that in all the modifications given in Fig. l additional energy introduced into the melt cannot influence directly the crystallization process since it is incomparable to the energy of molecular forces. Both the influence and efficiency of MHD means are determined solely by the change of motion, heat and mass transfer characteristics."

Jan 1, 1998

By E. Gutierrez-Miravete

A computational method for the simulation of mold filling processes is described. The method is based on the representation of the flowing or deforming medium as a collection of mutually interacting parcels of material. Instantaneous positions of individual material parcels are calculated by numerical integration of the dynamic equations, subject to appropriate initial and boundary conditions. So far, the method has been used to produce qualitative simulations of some flowing and deforming systems encountered in mold filling technology, and our findings are summarized herein. In all cases, individual material particle motions can be followed in detail, allowing critical examination of potentially problematic mold design features.

Jan 1, 1992

By Jin Liu

To improve value metals recovery, a new operating concept for the Inco flash furnace was investigated, in which the flash furnace coke addition practice would aim at establishing a reducing barrier on the surface of the molten bath. The descending partially oxidized sulfide mineral particles would reach the supernatant coke layer prior to the formation of slag. The key for success depends on the effectiveness of the coke layer to produce a sulfur deficient matte while maintaining furnace production capacity. The mechanism and rate of carbon reduction of the phases formed in the flash flame, i.e. sulfide (matte) and oxysulfide was investigated by means of crucible graphite reduction test work. The objective of these tests was to measure the rate of solid graphite reduction of matte, oxysulfide, slag, and matte+slag mixture at different temperatures. These tests were expected to permit understanding and explaining the reduction mechanism of each material by comparing the respective reaction rates, product reaction gas compositions, reduced material assays, and other relevant parameters. Direct visual inspection of the test crucibles would provide additional information.

Jan 1, 2006

By W. G. Davenport

H20 is present in many flash furnace inputs. Examples are: (a) moisture in concentrate and flux (b) humidity in blast (c) moisture in hydrocarbon fuel, particularly coal, Appendix IV. H20 may also leak into the furnace from damaged water-cooling jackets. H2O, especially that it be included H2O, exerts a strong cooling effect on the flash furnace. It is important our calculations. As will be seen from the calculations, gaseous and liquid H2O both increase flash furnace industrial oxygen and oil requirements. This is because gaseous H2O (humidity in blast) must be heated from its input temperature to the flash furnace off gas temperature. Liquid H2O must be evaporated and heated.

Jan 1, 2001

By Alexandre Chagnes

The extraction properties of two synthesized cationic exchangers, i.e. bis (1,3-dibutoxypropan-2-yl) phosphoric acid (BiDiBoPP) and bis(1,3-diisobutoxypropan- 2-yl) phosphoric acid (IPA), have been studied for the liquid-liquid extraction of Co(II), Ni(II) and Mn(II) contained in 1 M HCl. A comparison of the extraction properties of these extractants diluted in kerosene with Cyanex® 272 shows BiDiBoPP and IPA extract advantageously at lower pH than Cyanex® 272 and a better Co(II)-Mn(II) separation is achieved using BiDiBoPP or IPA than with Cyanex® 272.

By William Bourcier

Geothermal Brines are a significant potential source of valuable minerals and metals. These brines are water that is heated by the natural heat flow from the depths of the earth. Hotter brines, typically with temperatures greater than 120°C, are used to generate electricity. Lower temperature brines are directly used to supply thermal energy to applications such as agriculture, aquaculture and process/domestic heat. The geothermal waters have had intimate and lengthy contact with the layers of the earth?s crust that they flow through, resulting in dissolution of minerals and metals from the rocks, and solution into the hot water. These aqueous solutions can be processed to recover minerals and metals. Some potential products include silica, zinc and lithium, along with other materials. Recovery of minerals and metals from geothermal brines can be viewed as ?solution mining by nature?, followed by application of known or new hydrometallurgical techniques for isolation and purification. This paper discusses the opportunities, the processes, the challenges, the current status, the economics and the potential for recovery of minerals and metals from geothermal brines.

Jan 1, 2006

By Larry G. Stolarczyk

The development of geosteering technology for geothermal reservoirs is challenged by the integration of electrically small antennas in small-diameter metallic drill rods. To be useful, the antenna pattern must achieve sufficient back-lobe suppression, preferably with a forward-looking pattern. Forward-looking capability requires an antenna array with phase control. The phase-controlled antenna pattern enables imaging of geologic structures ahead of and surrounding the well bore. This paper describes the development of electric and magnetic dipole arrays for small-diameter drilling pipe.

Jan 1, 2006

By Bekir Karasu

Boron raw materials are amongst the most important natural sources for many industrial branches and their values become increasingly raised with the discovery of boron usage in many new technological fields. All the countries in the world are unfortunately not as lucky as Turkiye and USA where major boron deposits are mainly located. It is widely known fact that on one side, boron is very precious component with its technological importance, on the other; only its limited sources are available. Therefore, even its wastes have to be evaluated and regained. In the present work wastes of Etibor Kirka Borax Company of Turkiye were used in the production of opaque frits which was suitable for floor tile glazes. Standard and newly produced frit based glazes were applied on the pre-engobed floor tile bodies and single firing was employed. Final products were examined according to the certain standard tests and their microstructures were also investigated. All the results confirmed the evaluation of boron wastes in opaque floor tile glazes.

Jan 1, 2006

By S. S. Chabot, S. E. James

A recent survey of major steel companies worldwide revealed the importance of recycling zinc units from electric arc furnace (EAF) dust, mill scale, blast furnace dust and other zinc containing streams within the steel industry. Many processes have been developed and installed in response to this challenge. The most successful approach involves the production of a crude zinc oxide and its sale to primary zinc producers to recover the metal values. The problem with this process is the high concentration of halides in the crude oxide. This type of material cannot be processed directly in an electrolytic zinc plant because of the corrosion problems it will cause in electrolysis. In 1999, Big River Zinc installed a zinc oxide receiving and washing plant to minimize the impact of halides in its electrolysis circuit. A description of the washing plant and the initial operating results are presented in this paper.

Jan 1, 2000

By Nobuyuki Higashiyama, Ikuo Yonezu

"Hydrogen-absorbing alloys containing rare-earth elements are used in high capacity nickel-metal hydride secondary batteries,' hydrogen storage systems for portable fuel cells, and refrigeration systems. New hydrogen-absorbing alloys containing rare-earth elements have also been developed and introduced into these applications. High performance in nickel-metal hydride secondary batteries is strongly demanded because of the remarkable advancements in portable electric appliances. A large hydrogen absorption capacity, high electrochemical reactivity and superior corrosion resistance in an alkaline solution are required for hydrogen-absorbing alloys used in nickel-metal hydride batteries. The aim of this investigation is to improve the performance of conventional LaNi5 type hydrogen-absorbing alloys. For example, Mm(Ni-Co-Al-Mn)„ type hydrogen-absorbing alloys with various non-stoichiometric compositions were developed. In addition, a new process of rapid quenching process was applied for preparing these hydrogen-absorbing alloys in order to improve their performance.IntroductionRecently, the trend in electronic appliances toward portability has increased the demand for high capacity of secondary batteries as power sources. Since nickel-metal hydride batteries were first commercialized in 1990 in Japan, they have become increasingly popular as power sources for cellular phones, portable computers, electric shavers, and other, products.The performance of a nickel-metal hydride battery, such as its discharge capacity, high rate capability, and charge-discharge cycle life, strongly depends on the characteristics of the hydrogen-absorbing alloy negative electrode. Many types of hydrogen-absorbing alloys have been developed so far. For a hydrogen absorbing alloy to be used as the negative electrode material, (1) it must allow a large amount of hydrogen to be absorbed and desorbed in an alkaline solution, (2) its reaction rate should be high, and. (3) it must have long term durability under repeated charge-discharge cycling. However, LaNi5, a typical rare earth-nickel type alloy, shows significant capacity deterioration during repeated charge-discharge cycling. Therefore the first step in its development was to obtain sufficient corrosion resistance of the LaNi5 alloy for its use as an electrode material. A partial replacement of nickel with cobalt and a substitution of the lanthanum- content with misch metal (Mm), a mixture of rare earth elements such as lanthanum, cerium, praseodymium and neodymium, were very useful in improving the charge-discharge cycle life. However, the discharge capacity of the alloy was still not sufficient for a practical battery. A study of the effect of the partial substitution of aluminum and manganese showed that the best alloy composition was Mm(Ni-Co-Al-Mn)x, as follows.The stoichiometry x of Mm(Ni-Co-Al-Mn)x largely affects the discharge capacity and cycle life. Theose alloys with non-stoichiometric alloys with the compositions of [Mm(Ni-Co-AMn)x: 4.7<x<4.8] have a large capacity and a long cycle life. Nogami' et al. reported that 'a non-stoichiometric alloy with a Mm(Ni-Co-Al-Mn)x (x=4.76) composition showed approximately 10% higher discharge capacity than the stoichiometric alloy (x=5) [1] and greater influence of x on the electrochemical properties of multi-component AB„ type hydrogen-absorbing alloys for batteries."

Jan 1, 2000

By A. F. Otero

During the electrowinning (EW) of copper significant quantities of highly toxic vapors (acid mist) are produced due to the liberation of oxygen at the cathodes. Acid mist affects the health of operators, the environment and plant infrastructure. Acid mist can be decreased to acceptable levels by a combination of physical means (e.g. ventilation, plastic spheres over electrolyte) and chemical surfactants that decrease the surface tension of the electrolyte, modifying the way oxygen bubbles burst at the surface of the electrolyte. However, only few chemical surfactants are compatible with electrolytic applications, and they are not always used due to their high costs. This paper describes the application of a novel surfactant of natural origin (commercial name Mistop®) to suppress acid mist in copper EW process. Mistop® contains triterpenic saponins derived from the Chilean quillaja tree Quillaja saponaria Molina. The product is non-toxic, and poses no risks to the environment or to EW operators. Mistop® was tested at a laboratory, pilot plant and industrial scale in the world?s largest copper EW production plant at Radomiro Tomic (RT), CODELCO, Chile. At a Mistop® dosage of 8-9 ppm, acid mist decreased below the value accepted by Chilean regulations (< 0.5 mg/m3). At this dosage, Mistop® represents and economical alternative to chemical surfactants, and it is currently industrially used at RT.

Jan 1, 2003

By George Kachaniwsky

Until mid-1982 the Mines Gaspe copper smelter consisted of a fluid bed roaster, a reverberatory furnace, two Peirce-Smith converters of which only one was blowing at any one time, anode casting facilities, and a single contact sulphuric acid plant treating both roaster and converter gases. Reduced concentrate supplies have led to the shutdown of the roaster and, as a result, it was necessary to adapt the converter and acid plant operation to the new operating mode: green concentrate smelting with resulting lower matte grades and acid plant treatment of off-gases from only one blowing converter. Therefore, modifications were carried out to existing equipment and methods of operation and control. This paper describes the result of work done to obtain steady, maximum strength, converter off-gas flow and an efficient acid plant operation. Topics covered include: optimization of converter operation, tightness of hood and off-gas ducting, improvements in acid plant/converter communications and modifications of acid plant operation and control to cope with the fluctuations in converter gas flowrates and strengths.

Jan 1, 1983

By R. K. F. Lam

Unacceptable levels of impurity were noted in high purity chromium melting. Analysis of recent melting data determined that oxygen content in chromium is the critical parameter. Thermodynamics studies identify zirconia to be the most stable oxide in the presence of liquid chromium, followed by alumina and silica. Iron oxide reacts readily with liquid Cr. A certain degree of chemical reaction between liquid chromium and oxides does occur, contamination by the crucible is therefore unavoidable. Equilibrium constants indicate that a chromium oxide addition decreases &apos;ceramic dissolution and reduces impurity contamination. Safe operating conditions with oxygen content between 1190 ppm and 2500 ppm were identified. Additions of chromium oxide (Cr2O3) of 161 grams and 264 grams to liquid chromium yielded acceptable levels of impurity, and oxygen content was respectively increased to 1624 ppm and 2 179 ppm. A new process of melting high purity chromium with chromium oxide addition for controlling the activity of Cr2O3 is recommended.

Jan 1, 1997

By H. Hirayama, T. Okura, O. Kato

"Saganoseki Smelter & Refinery, one of the largest copper smelters in the world, has the annual capacity of 300,000 metric tons in copper content with two flash furnaces, six Pierce-Smith type converters, two anode furnaces, four acid plants, three tank houses and perfect pollution control system.Coping with the many severe conditions surrounding the copper industry in the last decade, Saganoseki Smelter has kept performing the stable operation, while enhancing the smelting capacity and developing new technologies such as the hydrometallurgical treating of converter dust recovered at electric precipitators. Especially in the operation of flash furnaces, which are of Nippon Mining's conversion type using hot air in a temperature of l,000ºC some technological improvements and complete operation control factors have approved the concentrate feed rate to reach to 2,200 tons a day for a flash furnace.Reported in this paper are the production control design for copper smelting process, and the operation control scheme of the flash furnace following the brief review of the characteristic of Saganoseki Smelter's process and some improvements. Copper Smelting ProcessDescriptions of major unit operations and general specifications of the copper smelting facilities are summarized in Table 1, and the present flowsheet of the copper smelting is described in Figure 1 (1,2).Outputs and raw materials treated in the last five years are shown in Table 2, in which concentrate includes powder copper scrap which amounts to 3 to 4% of concentrate.A full operation was performed for a period of one month, for both one flash furnace operation and for two flash furnace operation. With one furnace operation, 19,200 tons of copper were produced. With the two furnace operation, 84,000 tons of concentrates were charged and 33,500 tons of anode (net 28,600 tons of copper) were produced.The actual production level, however, has been kept at 80 to 90% of the full capacity because of low copper price, tight market of copper concentrate or fall of net demand in Japan."

Jan 1, 1989

By Chen Yongming

In order to eliminate the serious environmental pollution caused by low concentration of sulfur dioxide smoke in antimony smelters, a new smelting process, named as reducing-matting smelting, is proposed in this paper. The effects of technical conditions such as smelting temperature, smelting time, Pyrite cinder addition and the amount of additive on the smelting of stibnite concentrate have been investigated by the method of single-factor experiment. The results show that the optimum conditions are as follow: The amount of pyrite cinder is 1.2 times of its theoretical amount. The addition of soda and sodium sulfate is 15% and 72.6%, respectively, to the amount of stibnite concentrate when the total amount of sodium is 30%. The reducing-matting smelting is conducted at 1100°C for 2h then the smelting temperature is raised to 1200°C for 50min. Under the optimum conditions, the direct and total recovery ratio of antimony can gain 90.99% and 98.87%, respectively, and the fixed ratio of sulfur is higher than 99%.

Jan 1, 2006

By Adolfo Pillihuaman, Alberto Nogueira, Cyro Takano, Marcelo Mourão

The organic household waste has a growing disposal problem, requiring costly disposal systems. It is necessary to find new applications for these materials; one could be the steelmaking raw material production. In this paper is studied the development of self-reducing pellets from the organic waste pyrolysis, where is generated carbon and condensable and non-condensable volatiles. Non-condensable volatiles were burned and condensable volatiles were recovered. The resulting tar was mixed with iron ore, coal powder and flux (CaO), to then be pelletized together. Compression, falls and tumbler tests were conducted to characterize the pellets before and after heat treatment and reduction processes. The reduction curve and their physical and morphological characterization were measured. The results were as was expected, the fluidized coal create sufficient adhesion that pellets earned resistance with an equivalent resistance of common pellets, showing a good feasibility of this process.

Jan 1, 2015

By B. C. Blakey

The economic feasibility of the sulphuric acid pressure leaching route for the extraction of nickel and cobalt values from limonitic ores is highly dependent upon the behavior of aqueous aluminium. This is primarily due to its precipitation as hydronium alunite ((H30)A13(S04)2(OH)6), which is one of the major scale-forming compounds found in autoclaves used for pressure leaching. As a result of renewed interest in the pressure leaching process, an investigation of the aqueous-solid eqilibria in the aluminium-sulphate-water system under acidic (< pH l), high temperature (230 to 270°C) conditions has been conducted. Pure hydronium alunite was synthesized in an autoclave by leaching boehmite (A100H) at elevated temperatures in sulphuric acid solutions initially 0.25 to 0.75 m H2S04 in concentration. Spontaneous, in situ precipitation of hydronium alunite followed. A high temperature solution speciation model was used for the analysis of the resulting solubility data in order to calculate equilibrium constants for the precipitation reaction.

Jan 1, 1994

Most of the world's zinc metal is produced via the roast- leach-electrowinning (RLE) process. The process is well established, but most of the sulphur in the sphalerite concentrates reports in the acid, which has to be stored and/or sold. There are significant incentives to develop a simpler process with much reduced acid generation. Ferric ion is a well known oxidant for most sulphides, in particular sphalerite, and it converts the sulphide to elemental sulphur. Based on stoichiometry, however, the amount of ferric ion needed to achieve acceptable zinc extractions is prohibitive for downstream zinc recovery from the leach solutions. The process suggested here makes use of less-than-stoichiometric ferric sulphate additions because the ferric ion is regenerated by sparging SO2/O2 mixtures. This regeneration can be effected in-situ in the leach vessel or outside the leach vessel. An example of the application of this new process is presented for a Canadian sphalerite concentrate assaying 60% Zn. The effects of temperature, ferric concentration and ferric ion regeneration are presented. Options to recover zinc from the leach solution are also briefly discussed.

Jan 1, 2000