By Aichun Dou

Au-Sb alloy sample in which the total amount of Cu and Ni is below 25% (wt. %). In practice, Cu and Ni were difficult to be dissolved in sulphuric acid solution by oxidative leaching under the atmospheric pressure conditions, because of the lower concentration of Cu and Ni in the sample. In this paper, pressure oxidation leaching in sulphuric acid system (POLS) followed by hydrochloric acid leaching (HAL) was employed to remove impurities in the Au-Sb alloy. The effects of variables in POLS on leaching ratios of different metals were investigated in detail. Under the optimal conditions: the concentration of H2SO4 is 1.5 mol/L, liquid-solid ratio is 7:1, the amount of oxidizer is 1.2 times of the theoretical amount, leaching time is 4h and leaching temperature is 427K, the leaching ratios of copper and nickel reached up to 99%, antimony, lead and silver were not dissolved in dilute sulphuric acid solution. The residue from POLS was then treated with hydrochloric acid solution in fixed conditions, the leaching ratio of antimony reached over 92%, the grade of gold in the ultima residue was enriched up to 66%.

Jan 1, 2016

By Robin M. Forbes. Jones, Suhas V. Patankar, Ramesh S. Minisandram, Jr. Carter, Kanchan M. Kelkar

"The nucleated casting process currently under development has the potential for production of Ni-base superalloy preforms that possess superior microstructure to product made by conventional casting processes, primarily for gas turbine applications. In this process, electroslag remelted (ESR) clean (i.e., free of ceramic inclusions) molten metal is conveyed via a watercooled copper Cold-walled Induction Guide (CIG) to a gas atomizer. The spray of clean metal droplets is then directly cast into a water-cooled crucible for ingot production. The microstructure of the resulting ingot preform evolves within the length scale of the individual droplets and is a function of the thermal state of the incoming metal droplets. This, in turn, depends on particle size, flight time and heat exchange with the gas phase.In the present study, computational models is developed for the analysis of the flow and heat transfer in the gas-metal spray system under axisymmetric and steady-state conditions. The gasphase flow is analyzed using an Eulerian framework and turbulent mixing within the gas phase is modeled using the two-equation k-e model. The dynamics of the metal particles is analyzed using a Lagrangian framework that involves calculation of the trajectories of the metal droplets. A two-way coupling is considered whereby the transport and heat transfer in the gas and the metal phases influence each other.The analysis is developed at two levels. The spray model performs a detailed calculation of the spray dynamics in the vicinity of the spray and is intended for predicting the temperature and mass flux distributions of the metal spray depositing into the mold. The chamber model enables prediction of gas flow and motion of metal particles in the entire spray chamber."

Jan 1, 2004

By Shoji Taniguchi, Lifeng Zhang, Kaike Cai

"In the present paper, based on the two-phase (Eulerian-Eulerian) model, the 3D fluid flows in gas-stirred systems, i.e., air-stirred water vessel and argon-stirred liquid steel ladle, are simulated. In the Eulerian-Eulerian two-phase model, gas and liquid are considered to be two different continuous fields. The phases are assumed to share space in proportion to their volume fractions. The exchange between the phases is represented by source terms in conversation equations. Turbulence simulated by the k- e model is assumed to be the property of the liquid phase. The following effects of mathematical treatments and operational factors on the fluid flow are discussed, such as interphase drag force, turbulent model, the size of bubble, and gas injection mode.Some interesting results are derived. Except the interphase drag force, the interphase lift force should be taken into accounted in order to exactly simulate the fluid flow in gas-stirred systems. Suitable turbulent model and drag coefficient have effect on the mathematical simulation. Injecting small bubbles can realize a well mixing flow condition. The distance between the two gas-injection nozzles has effect on the fluid flow."

Jan 1, 2000

By B. C. Tripathy

The effects of alkali metal ions Li+, Na+, K+and transition metal ions Cr3+ and Mo6+ on the cathodic current efficiency, deposit quality, crystallographic orientations, deposit morphology and polarisation behaviour of the cathode during nickel electrocrystallisation on stainless steel substrate from aqueous sulphate solutions containing boric acid were investigated. The alkali metal ions had virtually no effect on the cathodic current efficiency, deposit quality, crystallographic orientations, deposit morphology and cathodic polarisation. On the other hand, there were significant variations in the current efficiency and deposit characteristics when Cr3+or Mo6+ were present in the electrolyte. Current efficiency decreased by more than 10% even at lower concentrations (> 100 mg/L). Similarly purity of the deposits was affected by the presence of either of the metal ions. In the presence of Cr3+, there was progressive shifting of the nucleation potential of nickel towards more negative values, whereas, in the case of Mo6+the nucleation potential shifted initially towards positive values in the concentration range 2-40 mg/L, but then towards negative values when its concentration exceeded 40 mg/L.

Jan 1, 2003

By M. Kawakami

In the blast furnace, the reduction of iron oxide and gasification of coke occur simultaneously. It is well accepted that the gasification reaction controls the simultaneous reaction. Therefore, it is important to develop highly reactive carbonaceous materials. It is also known that the reaction is accelerated catalytically with the addition of some materials. In the present work, the catalytic effect of iron, nickel and CaO on the gasification of graphite and coke was examined. The catalytic effect of iron, nickel and CaO on the reaction rate of graphite was noticed The effect was larger at lower temperature. At 1373 K, the effect almost vanished. The effect was larger in the order of CaO, iron and nickel. The reaction rate of de-ashed coke increased by the addition of iron and nickel. The effect of iron was larger than that of nickel. The effect was larger at higher temperature, which was contrary to the case of graphite. The reactive surface area increased also by the addition. Therefore, the catalytic effect on reaction rate might be attributable to the increase in the reactive surface area.

Jan 1, 2006

By L. Z. Villanueva

An investigation and evaluation has been performed to determine the potential utilization of electron beam irradiation technology for sulfur oxides removal from reduced-S02-strength metallurgical gases from copper smelters. These off-gases, though too weak to be converted to usable, concentrated: sulfuric acid by conventional means, are characterized by SO2 content higher than 2,000 ppm and a complex chemical composition, including high oxygen content and its generation occurring in a cyclical, fluctuating pattern. This work was based on information supplied by principal smelter companies in Chile. A laboratory facility with flow rate of 20 Nm3/h and equipped with an electron accelerator of beam energy 8.00 keV, has been used for testing. Influence on SO2 removal efficiency of operational parameters such as gas temperature, water vapor content, ammonia feed ratio and irradiation dose was established. The main conclusion of this work, from experimental laboratory tests as well as engineering studies, is that the Electron Beam Process (EBDS) is a cost-effective, simple and appropriate chemical process means for emission abatement. EBDS can, on a site-specific basis, adequately augment SO2 removal to upgrade overall abatement as required and in an optimal manner.

Jan 1, 1999

By Steven E. Follin

In-situ leaching is commonly used to recover uranium from low-grade deposits in sandstone formations. Acceptable recovery rates can only be obtained if the formation retains its permeability during leaching. Field experiences indicate that microbial growth, stimulated by the leaching pro- cess, can cause plugging problems. To investigate this hypothesis, leach solution and solid samples from well casings and submersible pumps were obtained from four in-situ mining sites. Chemical and microbiological analyses were performed. Bacillus species, Micrococcus species, pseudomonads, and xanthomonads were isolated from these samples. A mixed culture of these organisms was inoculated into a uranium core that was being leached in the laboratory. The permeability of this ore sample decreased to one-third its original value after 16 days. The addition of hydrogen peroxide (0.2 g L-1) to the leach solution killed the microbes and restored the permeability to its original value. This suggests that periodic injection of hydrogen peroxide into production wells may reduce microbial plugging in these wells and the immediate surrounding formation.

Jan 1, 1985

By Junji Shibata

As one of the effective usages of various wastes discharged in non-ferrous metal industry, the synthesis of hydrotalcite was carried out using aluminum dross as a raw material. Hydrotalcite is one of the inorganic anion exchangers and has layered structure of complex hydroxide. The removal of toxic metal ions such as As(III), As(V), Cr(VI) and Se(IV) with the hydrotalcite was investigated, and the removal properties were compared from the viewpoint of the anion exchange amount and exchange rate. Hydrotalcite can be obtained by a co-precipitation method from the aluminum dross and the waste MgCl2 solution discharged in an aluminum regeneration process. Slight amounts of SiO2, Al2O3, Fe2O3 and so on remain in the reaction product as an impurity component. Interlayer distance of the obtained hydrotalcite is about 0.3nm. Hydrotalcite changes to Mg-Al oxide by the calcination at 773K for 3h, and then hydrotalcite is formed again by a rehydration operation after calcination. The toxic metal ions are removed from aqueous solution by the anion exchange reaction in the pH region where toxic metal ions exist as the anionic species like AsO2-, HAsO42-,CrO42-, and SeO32-. The exchange amount is considerably concerned with the valence of anionic species and the size of anionic species. The removal of toxic metal ions were investigated from the engineering aspects such as the low concentration limit to be removed, the amount of hydrotalcite to be used for the perfect removal of toxic metal ions and so on.

Jan 1, 2006

By L. -C. Lai

A series of LaNi5-based alloys, with partial substitution of Ni by Al, Co, or V, were prepared The gas-phase hydrogen absorption kinetics and pressure-composition-temperature curves were measured The activation became easier and the plateau pressure was reduced as Ni was partially substituted by Al Substitution with Co reduced the hysteresis as well as the hydrogenation capacity, but enhanced the absorption kinetics Vanadium is often considered as a hydride former, but when it was added to LaNi5, it was found that V occupied the B site. A small amount of substitution of Ni with V led to a higher hydrogenation capacity and faster activation rate Based on these properties, an alloys LaNia 25CO0.5V0.1Al0. 15 was fabricated as an electrode. Compared with LaNi4.85Al0.15, it was found to exhibit faster activation, higher discharge capacity, and longer cycle life. The variation of the hydrogenation characteristics is discussed based on the physical and chemical properties of the alloying elements.

Jan 1, 1997

By Robert W. Bartlett

"Economic and other factors, mostly outside of metallurgy, that strongly influence applied research, development and especially successful commercial adoption of new processes for producing primary metals and other commodity materials are reviewed. These factors, which can be both positive and negative in their influence, are often too lightly regarded in the research planning stage. They include continuing imperatives that have long influenced new process development as well as more recent trends. Both are discussed. Nearly all new materials eventually become commodities--products made to standard specifications with no producer control over price. Success requires being a low cost producer on a world wide basis. Composites and other complex material assemblages are unlikely to escape this fate as they mature.INTRODUCTIONThe adoption of new processes, beginning with research and development, for primary metals and other commodity materials is particularly difficult because each new process must supplant an existing process that is already being used commercially. There are many requirements besides technical innovation and cost superiority that must be met by the new process. Consequently, few innovations make it all the way from the research laboratory to commercial success.This paper discusses some of the factors that influence success in developing new processes for primary metals and commodity materials, based on the authors experience as a research metallurgist and industrial research manager. It begins with some of the factors that are always present and constrain successful process research and development, and proceeds to current trends that are expected to continue long enough to influence processes in the year 2000. Many of these trends are contradictory in their effect on new process development, and the future remains uncertain.The prevailing importance of these trends will vary with the material, process concept and other factors intrinsic to each case. Nevertheless, an awareness of these influences can help to avoid some of the R&D pitfalls and dead ends. Such awareness is deemed to be a necessary condition to avoid failure when commercial adoption of a new process is the goal."

Jan 1, 1988

By M. Sahoo

The development of new alloys containing bismuth and selenium for potable water supplies are reviewed. The new alloys are replacements for the leaded red- and semi-red brasses by the low-lead alloys, SeBiLOYS I and II, for sand casting, and SeBiLOY III replaces the lead containing yellow brass, C85800, for permanent mold casting. As the new alloys use bismuth and selenium, the supply and demand of these elements are discussed. The key casting characteristics discussed are: tendency to dross formation, freezing range (liquidus and solidus temperatures), fluidity, resistance to hot tearing, microstructures, mechanical properties, machinability, grain refinement and corrosion behaviour.

Jan 1, 1999

By Tabbetha A. Dobbins

We report studies concerning the time frame for catalytic reactions between NaAlH4 (sodium alanate) and TiCl3 during high energy milling. Spectral features in x-ray absorption spectra were analyzed for samples milled for various times (0 minutes, 1 minute, 5 minutes, 25 minutes, and 125 minutes). A structural transition from Ti3+ to Ti0 is observed within the first 5 minutes of milling. The Ti0 structure persists for samples milled for times longer than 5 minutes?even after those samples underwent a subsequent single hydrogen desorption/absorption cycle. Samples milled for less than 5 minutes retain Ti3+. For samples milled for 1 minute, the Ti-K edge position shifts from Ti3+ to Ti0 after a single desorption/absorption cycle. However, the first coordination sphere around the Ti0 absorber occurs at longer distances for 1 minute milled sample. These results hint at the formation of Ti0 pure metallic clusters upon desorption/adsorption cycling of 1 minute milled sample. Previously reported x-ray absorption spectroscopy studies have demonstrated the structural transition from Ti3+ (in TiCl3) to Ti0(determined to be TiAl3 found at the surface of the alanate powder). Aluminum deficiency on the NaAlH4 lattice is responsible for controlling hydrogen absorption capacity. These time-resolved spectroscopy studies suggest the possibility for controlling aluminum deficiency, while still maintaining titanium activation of the alanate powder, by manipulating the coordination environment of the titanium dopant during the first five minutes of high energy milling. Specifically, a possible approach to mitigating aluminum deficiency during doping would be to introduce an alternative species to which the to Ti3+ catalyst would form a metallic bond after the TiCl3 has attached at the surface of the sodium alanate powder and before the Ti3+ forms the TiAl3 intermetallic species.

Jan 1, 2006

By K. P. Nishad

The origin of many casting defects can be traced at the mold filling stage. Entrapped air/gas pockets and oxide film formation are notable examples. In the present work, the mold-filling process is simulated using a mathematical model, built on a multi-physics based commercial package PHYSICA. The simulation code has the capability to solve multi-phase problems. The numerical model addresses a complicated dynamics of filling operation including free surface flow and subsequent flow behavior and is based on conservation of mass and momentum. The Free surface is modeled using the scalar equation method (SEM). The model is validated with benchmark experimental results from the literature. The role of turbulence and the pouring rate on variables affecting sites prone to oxide film formation are investigated using a simple but novel technique. Key findings of the work are presented.

Jan 1, 2006

By Scott W. Jorgensen

Hydrogen storage research has a long history, with a recent surge of new materials and new concepts. Important progress has occurred in the area of solid phase materials for storage, tank materials and engineering, and new types of materials. More importantly, an understanding of these materials is beginning to allow prediction of hydrides with improved properties. The performance of these new hydrogen storage systems begins to approach that of physical containment methods. The next step is to directly target performance that will permit commercialization.

Jan 1, 2006

"Hematite pellets were electro-deoxidized to iron in molten sodium hydroxide to produce iron containing about 10-wt % oxygen. The anodic reaction was the evolution of oxygen on an inert nickel anode. Before the electrochemical reaction, there is a reaction between sodium hydroxide and ferric oxide to form sodium ferrite and, in order to compensate for the reduction in sodium oxide content, 1 wt % sodium oxide is added to the melt. In a laboratory cell, the cell voltage was 1.7 V with a current density of 5000 A m-2, a current efficiency of 90% and an energy consumption of 2.8 kWh kg-1.Introduction The iron and steel industry contributes about 2.3 bn tonnes/annum of the carbon dioxide to the atmosphere, which is about 10% of the total, and some believe that, in order to prevent a catastrophic rise in the earth’s temperature, carbon dioxide emissions must be reduced by 50% come 2050. However, by 2050, it is likely that the iron and steel industry would have grown significantly so that the production may have risen to 2 or 3 bn tonnes/year so in order to meet the 50 % reduction on today’s figure, the carbon dioxide may have to be reduced to 25% or less, which is a very demanding requirement. There are probably three ways of reducing the carbon dioxide output:1. By capture and sequestration, but this may be technically very demanding.2. Reduction using hydrogen in place of carbon."

Jan 1, 2009

By Jörg Wallner

In order to limit SO2 emissions, the Montanwerke Brixlegg AG has installed a desulphurisation plant with the primary aim of reducing the peak emissions from the copper converter that are of particular ecological concern. The author discusses the process requirements, the desulphurisation process selected and the results achieved.

Jan 1, 1996

By Hao Rang

The article Is specially to Introduce the recovery process of Nb, Mn, P from slags and reutilization techniques of the remaining slags. Nb-Mn-Fe alloys which contain 14-16% Nb, 40-60% Mn can be obtained after using fire refining process of " Blast Furnace-Revolving Furnace-Electric Furnace -Electric Furnace, "meanwhile, phosphorous slags which the content of phosphorus pentoxide Is 29.21%. Further going through wet metallurgical processing and electrowinning technics to recover grading 99°o metallic manganese. Finally, phosphorous slags are grinded finely to be as phosporous fertilizers to be directly used for farmlands. Small particle size (0-8mm) rich slags are mixed with slight solid additions for balling directly, and taken Into blast furnace with blocky slags all together. The remaining tall slags are fully used as constructional materials, slags cement as well as a serial of wall materials, road materials, ground ornamental materials without burning operation and steam curing. The compressive strength range of those materials is up to 15-30 MPa. There is no more solid waste slags effluent In the full technical process.

Jan 1, 1994

By Anne C. Chinellato, Alejandra T. Soria, Nelida L. del Mastro, Amanda C. S. Pereiral, Esperidiana A. B. Moura, Anibal V. Abreu

"This work presents a comparative study of the thermo-mechanical and morphological properties of sugarcane bagasse fiber/HDPE composite treated with electron-beam and gamma radiation. The composite samples obtained by extrusion and injection molding processes were irradiated at 50 and 90 kGy using either a 1.5 MeV electron beam accelerator or gamma irradiator EMI-9, at room temperature in presence of air. The irradiated and non-irradiated samples were submitted to mechanical and MPI tests, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), scanning electron microscopy (SEM), sol-gel analysis and X-Rays Diffraction (XRD) and the correlation between their properties was discussed. Improvement of the bagasse fiber/HDPE composite properties, using electron-beam or gamma radiation, was found.IntroductionResidues of sugarcane bagasse fiber are widely produced in Latin America and other countries: in Southern Africa, Egypt, South-Eastern Asia, India, China, Australia, Cuba, among other producers, as by-products of the sugar and bioethanol industry. The sugarcane industry in Brazil and Uruguay is well established and expanding with large potential to increase the production of sugarcane bagasse in the next years [1-3]. Although the major portion of the bagasse is currently burnt for energy supply in the sugarcane industry, the disposal of this byproduct is still inefficient and, consequently, it is critical for agricu1ture profitability and environmental protection. Sugarcane bagasse is a lignocellu1ose fiber mainly constituted by around 46 % cellu1ose, containing hemicellu1ose, lignin, fat and waxes, silica and other elements [3, 4]. Studies have reported that sugarcane bagasse can be used to produce thermoplastic polymeric composites with excellent properties for many applications. [5-8]. Based on this survey, the transformation of bagasse into high quality industrial products, such as bagasse-polymer composites, can provide its more effective utilization."

Jan 1, 2012

By Takamasa Ishigaki, Gervais Soucy, Mohamed Rahmane

"The induction plasma jets employed for the in-flight nitridation of molybdenum disilicide (MoSi2) powders were investigated in terms of their flow characteristics. The present study shows the effect of the operating parameters of the plasma torch, as used for this process, on the plasma jet properties. The enthalpy probe techniques, along with mass spectrometry, were employed for the measurement of the jet temperature, velocity and concentration fields. The measured values were compared to the results of a numerical simulation performed on the plasma flowing inside the torch-reactor system. The process operating conditions studied were the plasma plate power, chamber pressure and sheath gas composition. The optimal conditions for effecting the nitridation process using thermal plasma are obtained at moderate plasma plate power, at around atmospheric pressure and by using a mixture of argon and nitrogen as the plasma torch sheath gas.IntroductionMolybdenum disilicide (MoSi2) based composites are considered to be one of the most promising candidates for high temperature structural material applications [!], especially because of their high melting points, good oxidation resistance and relatively low cost. However, the wide application of these composite materials is still limited by some factors such as their brittleness at room temperature and lower strength at high temperature (> 1500 K). To overcome such limitations, a number of researchers [2-4] have earlier studied various kinds of reinforcements for MoSi2, e.g. oxides, silicides and nitrides. More recently, Fan and coworkers [5-9] have demonstrated the possibility of in-flight nitridation and carburization of MoSi2, using a thermal plasma process. This work has confirmed the plasma synthesis route as one of the most promising methods for creating an in-situ second phase structure. Properties of the plasma flow, such as its temperature, flow velocity and composition, are of crucial importance for the nitridation of MoSi2 powders during their flight in the plasma. Therefore, the optimization of such a process involving plasma· generated reactive species necessitates a thorough understanding of the plasma flow characteristics."

Jan 1, 2000

By Deepu Philip, Pratik Agarwal, Ajay Kumar Shukla, Ishani Shukla, G Rajesh

Steel plants generally employ static BOF end point control models to arrive at a given temperature and chemistry at the end of blow. These end point models have now been supplemented with chaos control models to steer the blowing process in the right direction while the blow is in progress. Merely arriving at the correct end point temperature is however not adequate because in the subsequent stages as well the temperature variations can be large and unpredictable. The present paper deals with an integrated model to take into account the effect of all parameters affecting temperature and composition from tapping to the start of casting to minimize the use of LF or aluminum heating, and also minimize grade mixing. The application of lean operations strategy is explained in which the previous “Push System’ is changed to a “Pull System”, minimizing the use of ladle furnace or aluminum heating during steelmaking.

Jan 1, 2014