By Murray Johnston

New measurements have been made on the equilibrium distribution of selenium and tellurium between molten slag and metal phases. Distribution coefficients of Se and Te between magnesia-saturated calcium ferrite slag and copper or silver alloys were measured over the temperature range 1473 and 1673 K under controlled oxygen patrial pressures of 10-11 to 10-0.68atm. The results demonstrate that the minor elements are present in the calcium ferrite slag as the selenide (Se2-) and telluride (Te2-) respectively, up to a PO2 of 10-6 atm. As conditions become more oxidising, Te undergoes a transition to the divalent oxide whereas Se does not. Increasing the temperature was found to enhance partitioning of the minor elements to the slag. In terms of activities, at 1573 K, Se showed strong negative deviation from the ideal behaviour in the slag, while Te showed only slight positive deviation.

Jan 1, 2006

By Kan Song, Lin Liu, Hengzhi Fu, Jun Zhang, Haijun Su, Xiaojiao Jia

"Al2O3/YAG/ZrO2 eutectic in situ composite has been regarded as new generation of high temperature structural material due to its excellent performance even close to its melting point. The directionally solidified Al2O3/YAG/ZrO2 eutectic ceramics are prepared by recently developed Laser Floating Zone Melting (LFZM) apparatus in which a splitter mirror is used to obtain two beams with the same quality from one CO2 laser. With the two laser beams irradiate the sample from opposite directions, the sample is zone melted. The apparatus configuration and the solidification processing are described in detail. The solid/liquid interface morphology is studied and the mechanism of microstructure formation especially the characteristic of eutectic cellular is discussed. It is shown that YAG and ZrO2 phases play a leading role during the ternary eutectic growth. Meanwhile, the relationship between the solidification microstructure and the processing parameters are investigated.IntroductionAl2O3/YAG/ZrO2 ternary eutectic in situ composite, due to its excellent high temperature mechanical properties, is now considered to be a promising candidate material as a replacement of nickel based super alloy for new generation aero space engine turbine blade [1]. They exhibit flexural strength of 360-500 MPa from room temperature to 2073K in air atmosphere [2]. The compression creep strength at 1873K is 433MPa with the strain rate of 104/s [3]. However, because of the high melting point and complex physical properties, there remain still many difficulties for its application. One of the bottlenecks is the poor understanding of the relationship between microstructure and solidification conditions."

Jan 1, 2012

By I. D. Reznik

The flowsheets of converter matte production from sulphide copper - nickel and oxide nickel ores on Severonickel and Yuzhuralnickel integrated ,;corks are given. The cobalt behaviour in electrosmelting and autogenous ore smelting, converting and converter slag cleaning is observed. A list of acticles published in the 80 th is given.

Jan 1, 1993

By Upali Siriwardane, Tushar V. Kudale, Naidu V. Seetala

"Cellulose acetate (CA) membranes with 25% triethyl citrate (TEC) as plasticizer were prepared with varying thickness for CO2 gas separation from water-gas-shift (WGS) reaction products. The AFM analysis of the CA membrane showed that the uniform coating had fewer and smaller pores as the film thickness increased, and corroborated by gas permeability studies. The CO2 permeability has decreased faster than CO permeability with the CA/TEC membrane thickness, and findings support that the CA membrane could be used to entrap CO2. Several CA/TEC membranes were also staked to increase the separation efficiency. Positron Annihilation Lifetime Spectroscopy (PALS) was used to estimate the nano-porosity (pore size and concentration) changes of CA/TEC films. PALS results show a decrease in pore size with increasing CA-TEC concentration in acetone, while the pore concentration increases. The PALS results are correlated with the CO2/CO permeability variations as the CA-TEC concentration change.IntroductionHydrogen is one of the main energy sources available for the future advancement of clean fuel technologies especially for fuel cells. Generation of hydrogen and CO2 from Water Gas Shift (WGS) reaction mixtures of CO and H2O is of interest to many researchers since it allows a large scale production of hydrogen [1, 2]. Once hydrogen is produced using the WGS reaction, the output products contain mixture of CO, CO2, H2, and water vapor. Metallic membranes have been used as hydrogen separation membranes [3-6]. As H2 is separated from the mixture using the metal membranes, we need to separate CO2, and find ways of sequestration of CO2 to avoid environmental problems by greenhouse gasses. Polymeric Membranes have been used for CO2 separation [7]. Plasticizer can control the micro-structural properties such as pore size and concentration of polymer membranes [8], which influence the size/molecular weight dependent diffusion rates of the gas molecules. We have used cellulose acetate with triethyl citrate as plasticizer to separate CO2 from the WGS reaction products. Positron annihilation lifetime spectroscopy (PALS) is very sensitive and able to identify different kinds of defects and their agglomerates such as vacancies, vacancy loops, and voids [9, 10]. PALS has been successful in determining the free volume in polymers that influence the properties of the polymers [11, 12]. Microscopic properties of the free volume obtained from PALS have been correlated to macroscopic properties [13, 14]. We used PALS to study the nanoporosity (pore size and concentration) and fractional free volume changes of CA/TEC films, and used to understand the variations observed in the CO2/CO permeability as the CA-TEC concentration in the membranes change."

Jan 1, 2014

By Richard D. Hagni

The United States is dependent upon foreign sources for more than 93% of its bauxite and alumina supply. Domestic production of bauxite, which comes from Alabama, Georgia and Arkansas, is limited to those bauxite ores containing less than about l ½ % iron. Bauxites with higher iron contents are generally not utilized because they cause problems in bauxite calcining and especially because they produce undesirable brick discoloration and cracking. In order to improve beneficiation and expand the utilization of high-iron or ferruginous bauxites, a mineralogical and textural study has been conducted on selected samples from the Eufaula, Alabama, bauxite district. Reflected light microscopic, petrographic, and X-ray techniques have shown that a variety of iron minerals are present, including hematite, goethite, lepidocrosite, siderite, pyrite, marcasite, and ilmenite. Although the iron minerals may be locally concentrated into concretions and pisolites, most occur as very fine grains that are disseminated and show a variety of intergrowths. Mineralogical and textural observations indicate that the fine-grained iron mineral grains may be amenable to high gradient magnetic separation.

Jan 1, 1981

By Stanko Nikolic

The Top Submerged Lance (TSL) technology, developed in the 1970s, is now widely used for the processing of a range of materials. TSL technology for continuous converting was first patented in the 1990s. The process is based on the use of calcium ferrite slag. Although this slag system had been applied elsewhere the phase equilibria had not been thoroughly investigated. This lead to a collaboration between the Process Technology group of Mount Isa Mines, now part of Glencore, and the Pyrometallurgy Innovation Centre (PYROSEARCH) at The University of Queensland. Through multiple research programs this complex system was successfully investigated. The results were then implemented within thermodynamic modelling tools. This combined new knowledge was then applied to the design and industrial implementation of the TSL continuous converting technology, ISACONVERT™. This paper describes the key findings of the research and how this was applied to the industrial implementation of the technology.

By I. M. Richardson, M. Janssen, W. Geerstma, I. J. Bennett, V. A. Popovich

Avoiding wafer breakage is a big challenge in the photovoltaic silicon industry, limiting production yield and further price reduction. Special fracture strength tests suitable for thin silicon solar wafers and solar cells, to be used in combination with Weibull statistics, finiteelement (FE) modelling and digital image correlation have been developed in order to study the mechanical stability of solar wafers. The results show that removal of the saw damage significantly increases the strength of crystalline silicon wafers. Furthermore, it was found that silicon crystallinity and the location where the wafer is extracted from the cast Si ingot have a significant effect on the strength, namely samples taken from the bottom of the ingot are 30% stronger than those taken from the top. The study also showed that there is a decrease in fracture strength when an anti-reflective SiNx coating is applied, which is caused by high thermal stresses.

Jan 1, 2015

By Shadia J. Ikhmayies

"Tin oxide (SnU2) thin films of thicknesses in the range 100-600 nm were prepared on glass substrates by vacuum evaporation at ambient temperature. The films were characterized by transmittance measurements, X-ray diffraction (XRD), scanning electron microscope (SEM) observations and energy dispersion X-ray analysis (EDAX). It is found that the films have high transmittance and non sharp absorption edges. XRD diffractograms showed that the films are amorphous and the SEM micrographs showed that the surfaces are smooth, uniform and well covered with the material. The EDAX analysis showed that the films are deficient in oxygen. Indirect optical bandgap energy and Urbach tailing in the bandgap was observed, and the width of the tail, which is related with disorder and localized states, was estimated.IntroductionTin oxide is an n-type wide bandgap semiconducting material with a direct bandgap energy of 4 eV and an indirect bandgap of 2.6 eV [1], where inherent oxygen vacancies act as an n-type dopant [2], Tin oxide thin films have been used for transparent electrodes in photoelectric conversion devices namely amorphous silicon solar cells, liquid crystal displays, gas discharge displays, etc. [3]. Perfectly amorphous thin SnO2 films show good electrical response to reducing gases in air and could, hence, be applied to construct semiconductor gas sensors where the metal oxide films function as a monograin-eqivalent active layer [4]. Amorphous SnU2 can also be used in extended gate field-effect transistors (EGFET) as a pH sensor, where the sensitive part is made of the SnO2/Al structure. This device can be used to detect and to quantify any kind of substance that can produce or consume protons, like an enzymatic reaction, therefore showing a large range of applications as biosensors [5].There are different methods to prepare SnO2 films, such as atomic layer deposition (ALD) [6], reactive magnetron sputtering [7], chemical vapor deposition [8, 9], dip coating [10], spray pyrolysis (SP) [3, 11-14], and evaporation [8], The thermal evaporation method was chosen to produce SnO2 thin films in this work because deposition by this technique does not present any compositional problems. In addition, it is a low temperature technique, which increases the probability of producing amorphous films. To increase this probability, the films were deposited at ambient temperature."

Jan 1, 2012

By J. T. I. Poijärvi

Outokumpu Harjavalta Metals Oy operates copper and nickel smelters, three sulphuric acid plants and nickel refinery at Harjavalta and copper refinery and precious metal plant at Pori. The by-products of these plants are presented in this paper. The by-products of the smelters include products from slag cleaning of flash smelting furnaces and converters, flue dusts and smelter off-gases. Weak acid and sludges from cleaning of smelter off-gases and acids are the by-products of the acid plants. The by-products out of the copper refinery are crystallized metal sulphates and sludges from electrolyte purification, on which a co-production process of the copper tankhouse is based. The main by-products of the precious metals plant are products from anode slime treatment and platinum metal group concentrates in the recovery of precious metals. Sludges from nickel matte leaching and precipitates from solution purification are the by-products of the nickel refinery. The formation, treatment and processing as well as the research work done for the utilization instead of dumping of the by-products in the production of copper and nickel will also be discussed in this paper.

Jan 1, 1995

By Juan Patricio Ibáñez

Separation of arsenic and copper from Cu-As-H2S04 electrolytes by electrodialysis has been investigated at room temperature. The effects of current density and pH were studied. An arsenic-free copper solution was obtained for all the tested conditions. The transport efficiency for copper ions was found to be higher than 98% after 3 hours' test. Transport of arsenic and copper through the ion exchange membranes was increased by increasing pH and current density. Solution pH was found to be a key parameter for the separation process, since it controls the speciation of the ions to be transported and the formation of unwanted precipitates which reduce the global efficiency of the electrodialysis process. The main conclusion is that electrodialysis is a promising technique to be used in separating and/or concentrating ions of interest in copper electrometallurgy.

Jan 1, 2003

By Jyri Talja, Shaolong Chen, Hannu Mansikkaviita

"Drying (water removal) prior to smelting is always economically feasible. Unnecessary heating of vapour can thus be eliminated resulting in savings of5-15 MUSD every year.Thermodynamically removal of one ton of water out of copper concentrate at 100 °C (with 10 % moisture) requires approximately 3150 MJ/tH2o, consisting of heating of the water (377 MJ), heating of the concentrate (509 MJ) and water evaporation (2260 MJ). This is quite independent of the selected drying technology. In reality some more heat is needed as higher temperature is practiced to enhance the drying performance and to reduce the equipment size.Major nominator in drying energy efficiency is amount of gases, which depends greatly on the drying technology. Dryers based on direct heating with fossil fuels have high gas flow rates, and thus they require additional energy of about 1400-1600 MJ/tH2o, compared to indirect modemsteam drying at 250-400 MJ/tH2o.Significant benefits in energy consumption (900-1300 MJ/tH2o) with additional potential for a bonus profit of 2-4 MUSD/y year, together with full elimination of some 40 000 tpy CO2 per mid-size dryer is available by selecting sustainable, energy efficient steam drying.IntroductionRemoval of water from the concentrate is very energy intensive thus having a significant environmental impact. However, drying prior to smelting is always economically feasible and very often viable also from the perspective of process operations. This environmental impact of drying can, however, be decreased or even fully eliminated with proper selection of the drying technology.Energy incorporated in drying consists always of a number of phases like liquid (water), solids (concentrate) and gases (water vapour, purging I dilution air, combustion gases). Each phase is heated to a specific temperature during the drying process.Heating of water, heating of the concentrate and water evaporation consumes more or less the same amount of energy despite of the drying technology (3150 MJ per ton of water). In conventional drying this amount of energy is achieved by combustion of fossil fuels wirg subsequent CO2 emission. Alternatively, chemical energy derived from sulphide smelting can be utilized in a form of steam thus generating zero emission ofCO2, in modem steam drying."

Jan 1, 2012

By Beate Ina Jenssen

Ferric iron removal from the nickel electrolyte at Glencore Nikkelverk AS in Kristiansand, Norway, is achieved by precipitation of iron hydroxide followed by filtration, and it is desirable to improve filtration properties of the precipitated iron hydroxide in order to decrease the filtration time. The effect of increasing the residence time from the current 45 min to 75 min and temperature from 65 °C to 90 °C on the filtration properties of the precipitated iron hydroxide (akaganéite) was studied by simulating the industrial process conditions in a continuous reactor setup operating at steady state, using ferrous-containing process solution as feed material. It was possible to decrease the filter cake resistance by both increasing residence time and temperature, but temperature gave the most pronounced effect and reduced the filter cake resistance by one order of magnitude.

By O. A. Bascur

Applying the latest information technologies in mining and metallurgical complexes has become a serious challenge to management and technical teams. Emerging component design is changing the way the user relates to the desktop. Connectivity between mining and metallurgical process operations and their business systems has become a reality. Expanded use of plant information on the desktop is a standard tool for revenue improvement, cost reduction and adherence to production constraints. The industrial component desktop support access to information for continuous improvement and innovation by staff personnel and engineers. Collaboration between groups enables the implementation of an overall process effectiveness index based on losses due to equipment availability, production recovery and quality rate. The integration of information from mining, mineral processing and metallurgical performance monitoring increases production efficiency, even when many elements cannot be measured directly. Three case studies of large mining/metallurgical complexes are highlighted.

Jan 1, 1999

By Petrus Christiaan Pistorius, Farzin Fatollahi-Fard

The production of synthetic rutile—a common starting material for most titanium production processes—from iron-rich titanium minerals such as pseudorutile and ilmenite is described. The process for “upgrading” the mineral to synthetic rutile is by carbothermal reduction of the mineral while immersed in a molten salt at high temperature, followed by magnetic separation of the reduced iron. A variety of factors are also investigated, such as particle size of the mineral, the type of mineral, and the molten salt used. The solubility of iron(III) oxide in different molten salts is also experimentally determined.

Jan 1, 2016

By P. G. Comba

Many gold producing states are requiring rinsing of spent heaps to render the leached ore compatible with the environment and are placing restrictions on effluent pa, cyanide, and metals concentrations. Parameters which may affect efficient rinsing of heaps have been investigated by the U.S. Bureau of Mines in laboratory column studies. Rinse profiles for cyanide, metals, and pH as a function of the volume of water passed through the spent ore are presented. Fresh water rinsing of spent ore in columns showed that rinsing of cyanide was not affected by the rinse solution application rate. Interrupted rinsing with a rest period between applications reduced the volume of water required to meet effluent cyanide concentrations. chemical oxidation of the effluent with recycle of the rinse solutions reduced effluent cyanide concentrations and the volume of waste solution generated. Water rinsing was not successful in reducing the alkalinity of the cement agglomerated ore. A dilute acid solution had to be applied after cyanide removal to reduce effluent pa levels to specified limits.

Jan 1, 1992

By Qingyu Deng, Shiwei Ma, Wang Hua, Guibao Qiu

"The flow properties of the blast furnace slag bearing high TiO2 at high temperature like the viscocity may change a lot due to the formation of the carbonitride inside, causing serious problems on the separation between the metal and the slag. Therefore, the critical condition of the formation of Ti(C,N) in blast furnace is vital importance for the ironmaking process with iron ore bearing titania. In this study, the formation of Ti(C,N) in blast furnace and the influences of various factors on the Ti(C,N) formation are investigated by FactSage. It is found that the mass of Ti(C,N) would reach the maximum at 1480 oC, and the product is mainly TiN below 1620 oC, while it is mainly TiC above 1620oC. The order of the factors by the importance from strong to weak was: temperature, the content of TiO2 in slag, basicity of slag, the content of MgO and Al2O3.IntroductionThe titanium dioxide (TiO2) in iron ore bearing titania will be partly reduced by carbon to titanium carbonitride (Ti(C,N)) in blast furnace, causing serious problems on the separation between the metal and the slag because of the change of flow property. Therefore, the critical condition of the formation of Ti(C,N) in blast furnace is vital importance for the ironmaking process, especially for the smelting of iron ore bearing titania. Extensive experimental data in regard to the formation of Ti(C,N) has been reported in numerous papers[1-6]. However, only some discrete data can be obtained by experiment, and it is difficult to detect the mass of Ti(C,N) in slag. In addition, the experiment is difficult to be proceeded when the temperature is above 1600oC. Therefore, it is very difficult to make clear the critical condition of the formation of Ti(C,N) by experiment."

Jan 1, 2012

By Dong Hoon Han

The sulfation rates of magnesium oxide and calcium oxide (molar ratio 7:3) contained in calcined CMA ( calcium magnesium acetate) by SO2 were measured. The experiments were carried out in the temperature range 700 to 1100 °C and under the SO2 concentrations of 0.3 to I mol % (5 % 02). In the low-temperature range below 830 °C the reaction produced CaSO4.3MgSO4 and unreacted MgO, but no MgSO4 phase. The formation of CaSO4.3MgSO4 phase has a significant implication in that it allows the utilization of MgO for SO2 removal whereas the sulfation of MgO from conventional sources is so slow that it is of no practical interest. Thus, the calcined CMA can remove SO2 at lower temperatures than conventional SO2 absorbents and at a greater capacity. Above 950 °C only CaO reacts with SO2, but at a much greater rate than the calcined Ca(OH)2, which is one of the most reactive SO2 absorbents.

Jan 1, 1998

By Andreas Orth

Outokumpu Lurgi Metallurgie has developed a process for the calcination and reduction of laterite nickel ore tines where the reduction of iron and nickel to the wustite/metallic states respectively, is performed in a fluidized bed reactor using reduction gas generated very cost effectively from natural gas in an autothermal catalytic reactor. As an option coal can be used as reductant as well as additional fuel. The process of reduction and calcination is very energy optimized. It uses the off gas from the fluidized bed reduction reactor, which still contains energy, to dry and calcine the nickel ore fines in a primary stage circulating fluidized bed (CFB) reactor. The product shows high metallisation of nickel and iron oxides reduced to the wustite stage. This results in considerable energy savings in smelting the prereduced product to ferro-nickel. Alternatively the product can be leached to produce nickel. Laboratory tests showed very high recovery of nickel and cobalt. Keywords: Fluidized Bed, Prereduction, Calcination, Ferro-Nickel

Jan 1, 2004

By Guy Xueyi

The environmental impact assessment of the Imperial Smelting Process for metallic zinc and lead production in Shaoguan Smelter, China, was carried out by the life cycle assessment method. The detailed inventory analysis of the Input/Output in the process during 1998-2000 was conducted and the allocation was done among the main products of zinc, lead and sulfuric acid, according to the system expansion and substitution principle, The environmental impacts were assessed by using the following five Eco-indicators: Gross Energy Requirement (GER), Global Warming Potential (GWP), Acidification Potential (AP), Heavy Metal Toxicity' (HMT) and Solid Waste Burden (SWB). The results from this study are useful to address the environmental situation of the technology practice in this smelter, and provide a scientific basis for the further improvement.

Jan 1, 2003

By Li Ma, Shaoguo Chen, Gele Qing, Qihang Liu, Keng Wu

Olivine contains higher MgO element, which can be added into blast furnace burden to improve slag stability and fluidity. Effect of calcined olivine and untreated olivine on low silicon pellet production process and quality was studied in this paper. The results shows, calcined olivine has no effect on bursting temperature of green pellet, however the bursting temperature of green pellet will decrease with increase of untreated olivine ratio. Untreated olivine has slight effect on green pellet strength than calcined olivine while the ratio is higher than 2%. The compressive strength of low silicon pellet will increase first and decrease afterwards with increases of calcined olivine ratio under firing temperature of 1250°C, whereas, the changing sequence is reverse fired under 1280°C. The result of untreated olivine pellet compressive strength is same as calcined olivine pellet. However, the compressive strength and metallurgical property of calcined olivine pellet is slightly higher than that of untreated olivine pellet under same condition.

Jan 1, 2015