Jan 1, 1955

By R. W. Heckel

It has been shown previously that the effect of applied pressure on the density of a metal powder may be expressed by a relationship of the form:

Jan 1, 1962

By Suzanne T. Mathis, J. C. Ferm, J. T. Berger, W. Horger

A system of core logging and computerized entry and retrieval is described which permits accurate and rapid logging of core, cuttings and geophysical records derived from exploration and development bore holes. The system is so constructed that older drilling records can also be utilized. Output consists of conventional computer print out and graphic logs with a variety of scales, symbols and formats. Such logs can be used in constructing rock profiles which are necessary in property assessment and mine development.

Jan 1, 1983

By William Glenn

That basic slag will rapidly destroy ordinary (i.e., siliceous) fire-bricks is known to every smelter; and the smelter of copper-ores in particular knows that any kind of slag occurring in his practice is destructive. From this fact arises the chief distress of those who attempt to smelt copper-ores in any manner of furnace constructed of bricks or stone, or other similar material. We have passed the fire-brick stage of our experience; and now, having entered upon the period of the water-jacketed cupola, we will employ no furnace other than that having steel walls, kept cool by water. But,, unfortunately, the bottom of a water-jacketed cupola, kept cool by another water-jacket, fails of its purpose, being thereby made so cold as to chill both slag and regulus to a degree not bearable. The situation is more or less ameliorated when the upper surface of the water-jacketed bottom is covered with fire-bricks, since, so long as they last, they prevent the molten material from contact with the cold bottom. My own observation leads me to suppose that most smelters construct cupola-bottoms of iron slabs, which are covered, to a greater or less depth, with fire-bricks. There are cupola-bottoms which

Jan 1, 1902

By AIME

TURMOIL has been rampant in the lead producing industry during 1946. The chronic labor shortage was aggravated by various work stoppages in mines, smelters, and refineries, while shortage of materials was widespread. Price uncertainties helped to confuse the situation in many countries and particularly in the United States until the removal of price control in the latter part of the year. At the end of the first year of peace, lead, which had been comparatively plentiful during the war years, was a scarce and high-priced metal throughout the world. It is the hope of the industry that the law of supply and demand, if allowed to operate without interference, will bring about a satisfactory balance between production and consumption. Under these circumstances it is not surprising that there have been few important developments in the metallurgy of lead, though a number of items of general interest to the industry have been reported. An ore body which may prove to be of considerable importance has been discovered at Mpanda, Tanganyika. The scarcity of lead ore is illustrated by the announced reopening of the La Manche lead mine in Newfoundland, idle for 56 years. A new lead producer came into production when Rhodesia Broken Hill started up its new smelter. Lead concentrate of 75 per cent grade is smelted in Scotch hearths and the lead is refined to market grade by the Harris process without desilverizing. Production is about 1000 tons per month. One Australian lead producer, Mount Isa, has returned to lead production after having operated its lead plant for the production of copper during the war. The East Chicago plant of the International Smelting and Refining Co. has been sold to the Eagle-Picher Co.

Jan 1, 1947

By Ernest R. Dickie

IN 1945 the Bagdad Copper Corp. decided to change from block caving to open-pit mining. By early 1948 the conversion was completed and production was increased from 1500 tons per day to 4000 tons per day. Open-pit mining costs decreased approximately 40 pet from the cost of producing ore by the underground method. At present one P & H model 1400 all-electric 4 1/2-yd shovel and one P & H model 1055 Diesel 3-yd shovel are used continuously for stripping. One 21/2yd North- west shovel handles the ore. Delivery of a new P & H 1055 electric shovel for stripping is expected this month. Blasthole drilling is performed with two Bucyrus model 22 and two Bucyrus model 27 churn drills.

Jan 9, 1951

By John L. Walte

Consolidation Coal Co.'s Renton mine, a 680 000-t/y (750,000-stpy) underground operation located in western Pennsylvania, has reduced the time required for overcast construction in its advancing operations by adopting a prebolting technique followed by multiple blasting. In the past, the mine's overcasts had been excavated by the continuous mining machines used to advance the section. More recently, the overcasts were blasted down and then rebolted with a stoper drill. The new system, using a two-part combination bolt, has proven very successful in speeding up overall construction time and providing more positive horizontal control in blasting. The prebolting approach allows the roof to be blasted down and loaded out without the need for rebolting the shot-out area.

Jan 6, 1978

By Martin J. Gungl, J. Lyman MacInnis

None of the industry submissions could persuade the Canadian Tax Reform draftsmen that the rate of return has had as much bearing on investors' decisions to invest in Canada as the success records of Canadian ore findings. The goverment opted for the position that mining capital goes where the ore can be found. Many tax incentives which were available until the end of 1971 have been greatly reduced. However, it is still recognized that new ventures in exploration and development of natural resources deserve a break even if there is reduced recognition of the established and highly successful members of the industry unless they continue to search and develop. The latter will also get some breaks for processing beyond the prime metal stage.

Jan 7, 1972

By G. R. Speich

A cellular precipitation reaction in which cells consisting of an Ni3Ti (DO24) phase and austenite are formed has been studied in an austenitic Fe-30 Ni-6 Ti alloy. The variation of the growth rate and interlamellar spacing of the Ni3Ti cells with temperature has been determined m the range 400" to 975°C; the interlamellar spacing is proportional to the degree of undercooling; the growth rate can be expressed by an equation of the form G = K?T)2 exp(-Q/RT). The habit of the Ni3Ti lamellae is (001)Ni3Ti (111)y;[010]Ni3T2 [010]y. An almost perfectly coherent interface is formed between Ni3Ti lamellae with this orientation rela -tionship and the intervening austenite. This first Ni3Ti cellular product is subsequently consumed by a second cellular reaction of much coarser spacing. CELLULAR precipitation reactions have been studied in copper-base,1,2 Au-Ni,3 pb-sn,4 and iron-base ferritic5,6 solid solutions, and this mode of precipitation has been treated theoretically by smith," Turnbull,8,9 cahn,10 and more recently by bohm.11 In the case of substitutional austenitic iron-base alloys little or no data are available, Cellular precipitation reactions are well known in austenitic nickel-base alloys12,13 but usually these reactions do not proceed to completion because of general precipitation occurring in the matrix, and they have not been studied in detail. Precipitation from an austenitic Fe-30 Ni-6 Ti alloy was studied as part of a larger investigation of the mechanisms of precipitation from substitutional iron-base alloys. This alloy, austenitic at high temperatures, decomposes at lower temperatures by a double cellular precipitation reaction. The first decomposition product consists of alternate lamellae of an Ni3Ti(DO24) phase and austenite. The reaction proceeds to completion, consuming all of the original austenite. This first cellular product is subsequently consumed by a second cellular reaction of much coarser spacing. The first cellular reaction was studied in detail by light and electron microscopy, hardness measurements, and by X-ray and electron diffraction. Interlamellar spacings and growth rates were measured during isothermal aging in the range 400" to 975°C. The orientation relationship between the Ni3Ti and austenite lamellae was determined and indicates that an almost perfectly coherent interface exists between the two phases. This first Ni3Ti cellular reaction is of particular interest because it occurs over such a wide temperature interval. This allows cellular growth rates and interlamellar spacing data to be obtained for much larger degrees of undercooling than reported hitherto. MATERIALS AND EXPERIMENTAL PROCEDURE The Fe-30 Ni-6 Ti alloy was prepared from electrolytic iron, Mond nickel shot, and sponge-purity titanium* by vacuum melting in a zirconia crucible

Jan 1, 1963

By J. Phillip Neal, Kefton H. Teague, Carroll P. Rogers

Feldspars, the most abundant minerals of the igneous rocks, occur in numerous forms and mixtures. The feldspars of commercial significance are found in widely distributed pegmatites as large crystals usually free of iron-bearing impurities and thus suitable for hand-cobbing, and also in larger bodies where the ore contains various types of feldspar intermingled with quartz and relatively free of iron-bearing impurities, or at least readily unlocked from impurities present at relatively coarse mesh. The latter type of ore includes some pegmatites, and the "alaskite" bodies so common in the Spruce Pine district of North Carolina. On the west coast of the US and in Oklahoma there is-or has been-commercial recovery of natural feldspathic sand as a source of alumina in glass and ceramics. "Aplite" in commercial terminology is a light-colored igneous rock with a granitic composition and a fine sugary texture, often banded with readily removable iron impurities. Only one area in Virginia produces aplite for the glass industry; it is located near Montpelier in Hanover County. According to Deer et al. (1966) the word feldspar derives from the Swedish feldt or jolt (field) and "spath:" chunks of rock appearing in tilled ground overlying granite. Castle and Gillson (1960) indicate a Germanic origin, citing "spat," which is said to refer to any transparent or translucent material which is readily cleavable. The term "spar" has in the past been applied to minerals other than feldspar, such as barite, calcite, and fluorite. It is correct to call the latter "fluorspar." There is a true barium feldspar, but it is rare and of no present economic importance. What is recognized as feldspar or "spar" by present producers and consumers consists of three silicate minerals which, if pure, would have the formulas KA1Si3O8 (microcline or orthoclase), NaAlSi3O8 (albite), and CaAl2Si2O8 (anorthite). These are almost never found in pure form in nature, but occur together in great abundance in a three-component system. A considerable number of different combined ratios of these three exists, with the exception that isomorphism between potassium spar and calcium spar is very limited. User specifications for feldspar products are largely built around the prevalent naturally occurring ratios. Passages following will refer to "K-spar," "Naspar," or "Ca-spar." Nomenclature and Descriptive Terms Relating to both the mineralogy and the economics of feldspar are certain terms whose coverage it is useful to specify. Commercially, aplite is a feldspathic rock mined and beneficiated in one location in Virginia, in which both titanium and feldspar minerals are present-the latter now being the major, if not the only, economic product. Technically, the term aplite when applied to this rock is of questionable accuracy. But, in light of accepted commercial usage, the term will be here used to designate it. Regarding the Virginia rock, Ross (1941) is cited. Alaskite is another term requiring understanding if not precise use. A distinctive rock type customarily called by this name is found near Spruce Pine, Mitchell County, North Carolina. An important major feldspar source, it contains somewhat higher levels of plagioclase feldspar and quartz than alaskite as defined in the Glossary of Geology and Related Sciences, which states that `orthoclase, microcline, and subordinate quartz are the principal

Jan 1, 1983

By R. A. Swalin, L. A. Neimark

The research work presented in this paper had initially a two-fold goal. First, further data concerning the low-temperature recovery of cold work was desired. Recovery phenomena have been extensively studied in face-centered-cubic metals but at the time of initiation of this research, no investigation concerning the low-temperature recovery in body-centered-cubic metals had been made. During the course of the investigation a paper by Martin on the recovery of point defects in molybdenum appeared.&apos; Comparison of our results on tungsten with Martin&apos;s results on molybdenum will be made. Secondly, knowledge concerning the influence of a particular type of impurity addition on the recovery kinetics was desired. It has been known for a long time that extremely small amounts of certain impurity additions exert a profound influence on the recrystallization behavior and the resulting microstructure of tungsten. Small amounts of potassium silicate and aluminum chloride added prior to the reduction of tungsten oxide to the metal have been found by Smithells to raise the recrystallization temperature markedly,2 and yield an ultimate microstructure in which grains several millimeters long are produced in fine wires of say 10 mil diam. If the impurities are added singly, ordinary secondary recrystallization results with none of the spectacular properties of the wire to which special additions were made. Swalin and Geisler3 and Rieck4 have studied the recrystallization behavior of such doped wire in some detail. The former workers found that small amounts of these impurities raised the recrystallization temperature over 400°C and electron microscopic examination revealed no obvious inclusions in the microstructures. In fact. chemical analysis showed that there was <0.001 pct K, <0.002 pct Al, trace of Si, and <0.0003 pct 0 in the wire studied. The possibility that the role of the special impurities is to keep the structure open by void formation and that submicroscopic porosity acts as the inhibiting agent has been discussed.2&apos;3 Meijering and Rieck5 have suggested that the impurities are strung out as second-phase particles in a direction parallel to the drawing direction. It was thought that a kinetic study of recovery could perhaps elucidate the role of the impurities to some extent. When a metal is deformed by cold work three basic types of defects are thought to be introduced into the crystal lattice, namely, interstitials, vacancies, and dislocations. Van Bueren6 has proposed that recovery of cold-worked metal is a four-stage process, each step being the result of the annealing of a primary defect or a combination of defects and having a unique activation energy. The steps in order of increasing activation energy are attributed to a) the diffusion of interstitials recombining with vacancies, b) diffusion of vacancy pairs, c) the diffusion of single vacancies, and d) climb of dislocations. In metals with relatively low- or medium-range melting points the temperatures for recovery are low enough so that the first three steps may occur during room-temperature deformation. For tungsten, because of the high melting point and subsequently high recovery temperature, it was calculated, using Nowick&apos;s approach7 that this recovery would occur in the temperature range 200" to 600°C. It is also known that recovery of X-ray line broadening, presumably due to dislocation climb, occurs at about 600°C.8 EXPERIMENTAL METHOD Two types of cold-rolled 10-mil-diam tungsten wire were used in the investigation; a) pure tungsten, (called undoped) and b) G. E. No. 218 wire (called

Jan 1, 1961

By F. H. McDowell

The electro-magnetic separator of Mr. G. Conkling, Glens Falls, N. Y., described by Mr. Birkinbine* in a paper at the New York meeting of the Institute, in February, 1889, has been in successful operation at the Tilly Foster &apos;mine for a considerable period, under the disadvantages which seem to be the inevitable attendants of pioneer enterprises in new technical fields. The results of a run of several months, which the Superintendent, Mr. S. P. Tomkins, has taken pains to collate, are here presented by his courteous permission, and that of Mr. E. S. Moffat, the energetic and skilful General Manager of the Lackawanna Iron and Coal Company, to whom our profession is already indebted for examples of bold and ingenious practice in mine-engineering. It is believed that these figures will assist those who are planning similar operations to decide intelligently what they may, and, more important still, what they may not, expect to accomplish. The local difficulties in the way of this experiment at the Tilly Foster mine were many and great. Only about two-thirds of the waste-dump, resulting from the assorting of previous years, is ore; and this varies in content of iron from 20 to 28 per cent. The remainder is rock, some (from horses in the vein) showing particles of adhering mineral, some (from the foot- and hanging-walls) entirely barren. The expense of overhauling the dump and removing this rock is by no means the least of the numerous items which must be charged against the concentration. Associated with the lean ore are hornblende and other minerals, carrying iron in the non-magnetic state, which must necessarily be washed away with the tailings. The waste-dump was originally located without reference to future treatment, and now can only be handled by means of a locomotive,

Jan 1, 1891

By R. C. Gifkins

R. C. Gifkins (CSIRO)—In this paper evidence is put forward to support the idea of grain boundary shearing in aluminum at 4.2°K and the phenomenon is explained in terms of a low-temperature "equicohesive temperature". It is stated that these findings show that grain boundary shear cannot be ruled out in any situation by temperature arguments alone. We believe, from our own recent study of "apparent grain boundary sliding&apos;&apos; at temperatures below 0.45 Tm, that it can be ruled out on temperature arguments alone.45 Our experiments were made principally with magnesium and a Ms-A1 alloy ("Magnox A12"). Careful examination of offsets of marker lines or steps at grain boundaries produced by deformation at room temperature (-0.3 Tm) showed many of these to result from curvature over narrow zones along the grain boundaries. A significant residuum did, however, appear as a sharp offset or step. It was found that the mean value of this step rose to a small value during the first 0.5 to 1 pct strain and then remained at this level with further strain. Moreover, exactly the same values were obtained (at the same stress) at 75°C instead of 21°C. That is, in this range of temperature the "apparent sliding" was not temperature-sensitive. At 125°C and above there was sliding which increased with strain and which was temperature-dependent. When this temperature-dependent sliding was used to calculate the sliding to be expected at room temperature, this underestimated the "apparent sliding" by a factor of 104. The conclusion drawn is that the "apparent sliding" consists of shear localized in a zone of a width measured perhaps in microns, whereas it seems that true sliding occurs on the boundary surface.46 A model for such localized shear has been developed in general terms, following a similar model of Urie and Wain.47 Other strong evidence for low-temper- ature sliding has been based on the offsets of marker lines consisting of a substructure seen using the electron microscope to resolve these.48 We have repeated this work and found that the effects can be accounted for in terms of cracks in an oxide film which is produced when the substructure is etched up; these cracks form over zones of shear rather than at actual interfaces. However, in aluminum at room temperature (-0.3 Tm) there is no "apparent sliding" which is optically detectable. We suggest that, when the temperature is much lower (and possibly the rate of strain higher, too), as in the experiments of Chin et al., then aluminum behaves like magnesium at room temperature, and a narrow zone of shear develops to accommodate differences in strain across the grain boundary. Such a zone could well give rise to triple-point cracks. It is hoped to investigate these suggestions further. B. Y. Chin, W. F. Hosford, Jr., and W. A. Backofen (authors&apos; reply)—It is interesting to have Dr. Gif-kin&apos;s comments, although it is somewhat difficult to reply in detail without the reference containing the work that he describes. Apparently though, he does find a low-temperature temperature-independent sliding that would seem to be related to the observations reported here. Perhaps some of the difficulty has semantic origins, growing out of the distinction between (&apos;true sliding" and "apparent sliding".

Jan 1, 1965

By S. S. Shen, M. J. Pool, P. J. Spencer, J. R. Guadagno

VERY few thermodynamic data are available for rare-earth alloys, partly because of the difficulties of obtaining the metals in sufficiently pure form and also because of their comparative scarcity up to the present time. The rare earths form a very interesting series in the periodic table in view of the progressive filling of their 4f subvalence electron shell and would be expected to provide useful information with regard to alloying characteristics of transition elements. It has been found in recent calorimetric investigations that the heats of solution of a number of the rare-earth metals in liquid tin are highly exothermic.1-4 Exceptionally strong bonding between rare-earth and tin atoms is clearly indicated in the liquid solutions. Continued thermodynamic studies of the behavior of rare earths in solution could thus contribute a great deal to present theoretical knowledge of alloying behavior and would yield an insight into bonding of a strength hitherto unencountered in liquid alloys. The determination of the heats of solution of the pure components in liquid tin is an essential preliminary to calorimetric work of this nature. Heats of solution of praseodymium, neodymium, and samarium in liquid tin at 750" &apos; and the heats of mixing of Pr-Nd solid solutions&apos; have already been determined in this laboratory. The present investigations with lanthanum continue the study of rare-earth elements. Details of the construction and operation of the liquid metal solution calorimeter used in this work have been published previously by Pool and Peluso and no further description will be given here. The lanthanum used in heat of solution determinations was supplied by Lunex who quoted the purity as 99.9 pct. Their detailed analysis of the material is given in Table I. Samples of 0.0003 to 0.0005 g-atom were used for each run and great care was taken to remove all surface oxide prior to weighing. The samples were stored at all other times in a beaker of oil to prevent their otherwise rapid oxidation. The compounds LaSn (Cudu, L1P type structure) and La&, (structure not classified) were prepared from the appropriate quantities of the two pure components by arc melting under a purified argon atmosphere and once again great precautions were taken to avoid any subsequent oxidation of the specimens. Although no structural examination of the compounds was made, the consistency of thermodynarnic measurements carried out on twenty or so individual samples of each indicates that the compounds were in fact homogeneous, single phase alloys. Samples of the compounds consisting of 0.0003 to 0.002 moles were used in the calorimetric measurements. A solvent bath consisting of approximately 80 g of 99.9 pct pure Sn was used for each series of runs and its heat capacity was determined at regular intervals throughout the experiments using pure tin or tungsten calibration samples. Measurements were made of the heat of solution of lanthanum in liquid tin at 725", 750C, and 775°K and at compositions up to 2.21, 4.76, and 5.25 at. pct La at the three temperatures respectively. In every case, the heat of solution of lanthanum remained constant at its limiting value, within experimental limits, up to the highest lanthanum concentration investigated. Since no change in was observed, it was concluded that the liquid/liquid + LaSn, phase boundary had not been

Jan 1, 1969

By Charles R. Keyes, D. F. Riddell

For a period of several years, and in a large number of oases, the Metallurgical Laboratories of the New Mexico School of Mines were employed in umpire work. During this time many important local problems mere solved. Against the results of careful chemical analyses of ores, assay-returns mere often checked. In many cases the assay-methods of mine and custom-smelter were compared, and both often found faulty for the ore concerned. A wide range of ores was covered. Many of the chemical analyses and assays were made by Dr. F. C. Lincoln, Professor of Metallurgy, now of the Montana State School of Mines. A varied series of instructive assays was prepared by Prof. R. B. Brinsmade, now of the West Virginia State University. Single assays and given series of tests were undertaken by H. T. Goodjohn, now chief chemist to the Cia. Metalurgica de Torreon, Coahuila, Mexico; by H. J. Hub-bard, now superintendent of the Butters Divisadero Mines, Jocoro, San Salvador, C. A.; by E. D. Morton, now superintendent of the Arizona & Nevada Copper Mining Co., at Lunning, Nev.; and by A. W. Edelen, now superintendent of the Angangueo Unit of the American Smelting & Refining Co., in Michoacan, Mexico. A critical comparison of assay-methods that were found to be followed in the case of certain gouge-ores mined in the Mimbres range in New Mexico, and about which there had been much controversy, was made by D. F. Riddell, then Acting Professor of Assaying, and now superintendent of the Providentia Mines Co. of Parral, in Chihuahua, Mexico. To him is due the credit of much that is contained in the following notes, which he has generously permitted to be used in advance of the publication of the complete results.

Jan 1, 1912

By Philip R. Strand, O. F. Stewart

Vermiculite is the name generally applied to the group of hydrated ferromagnesian aluminum silicates that are characterized by the ability to expand when heated. This process, called exfoliation, results in a lightweight product of commercial value. Most uses of vermiculite are for the expanded material. The chief markets are in construction, agriculture, and horticulture, with lesser uses in general industry. Composition and Properties Vermiculite, in its natural state, has the characteristic micaceous habit, a perfect basal cleavage which causes splitting into thin laminae that are soft, pliable, and inelastic. The structure of vermiculite is basically that of a talc. The prominent monoclinic crystal faces are often marked by lines at 60° and 120°. Hardness varies from 1.5 to 2 or more; specific gravities are between 2.1 and 2.8; color varies from almost clear to amber, bronze, brown, green, or black. Vermiculite feels like talc, especially when wet. Although much research has been performed on the chemical and structural composition, there is not yet complete agreement on the exact formula. This is to be expected when different workers have examined the many different varieties. Vermiculite is not considered to be a single mineral species but a family of related minerals. The structural formula for a trioctahedral vermiculite may be written: (H20)-(Mg,Ca,K)-(A12,Fe,Mg)-(Si,A1,Fe)4O10 (OH) 2 Hydrobiotite also occurs with vermiculite and is usually considered a vermiculite for commercial uses. When heated quickly to elevated temperatures, vermiculite expands by exfoliating at right angles to the cleavage into wormlike particles. The name vermiculite is derived from the Latin vermiculare, to breed worms. This characteristic of expansion is the result of the mechanical separation of the layers by the rapid conversion of contained water to steam. The decrease in bulk density of commercial grades is usually approximately 10 times, from 50 to 5 lb/ft3, but varies depending on the quality, size, and furnace efficiency. Individual flakes may expand up to 30 times. Vermiculite may also be expanded by soaking in chemicals such as hydrogen peroxide, weak acids, and other electrolytes. Color change during expansion is dependent upon the type of vermiculite and furnace conditions. Heating in an oxidizing atmosphere produces a dull gray or tan color, whereas a reducing atmosphere can produce a bronze or gold color. The expansion of the vermiculite crystal results in large pores being formed between the platelets. Thus, exfoliation makes available a large increase in void volume which is important in the application of vermiculite as a chemical carrier. Mathieson and Walker (1954) state vermiculite must be regarded as a true clay mineral. The characteristic properties of the mineral, such as high cation exchange capacity, organic complexing ability, and variable interlamellar distance are very similar to those of montmorillonite. The cation exchange capacity of vermiculite is one of the highest of all the clay minerals. The interplatelet space is accessible to penetration by some electrostatically neutral molecules. Water and glycerine are two common substances whose molecules may be so imbibed. In the natural state and under normal atmospheric conditions, water occupies the spaces between the silicate layers. The crystal d-spacing is near 14.2A. By differential thermal analysis, it has been determined that the water

Jan 1, 1983

By W. L. Worrell

R. C. Gifkins (CSIRO)—In this paper evidence is put forward to support the idea of grain boundary shearing in aluminum at 4.2°K and the phenomenon is explained in terms of a low-temperature "equicohesive temperature". It is stated that these findings show that grain boundary shear cannot be ruled out in any situation by temperature arguments alone. We believe, from our own recent study of "apparent grain boundary sliding&apos;&apos; at temperatures below 0.45 Tm, that it can be ruled out on temperature arguments alone.45 Our experiments were made principally with magnesium and a Ms-A1 alloy ("Magnox A12"). Careful examination of offsets of marker lines or steps at grain boundaries produced by deformation at room temperature (-0.3 Tm) showed many of these to result from curvature over narrow zones along the grain boundaries. A significant residuum did, however, appear as a sharp offset or step. It was found that the mean value of this step rose to a small value during the first 0.5 to 1 pct strain and then remained at this level with further strain. Moreover, exactly the same values were obtained (at the same stress) at 75°C instead of 21°C. That is, in this range of temperature the "apparent sliding" was not temperature-sensitive. At 125°C and above there was sliding which increased with strain and which was temperature-dependent. When this temperature-dependent sliding was used to calculate the sliding to be expected at room temperature, this underestimated the "apparent sliding" by a factor of 104. The conclusion drawn is that the "apparent sliding" consists of shear localized in a zone of a width measured perhaps in microns, whereas it seems that true sliding occurs on the boundary surface.46 A model for such localized shear has been developed in general terms, following a similar model of Urie and Wain.47 Other strong evidence for low-temper- ature sliding has been based on the offsets of marker lines consisting of a substructure seen using the electron microscope to resolve these.48 We have repeated this work and found that the effects can be accounted for in terms of cracks in an oxide film which is produced when the substructure is etched up; these cracks form over zones of shear rather than at actual interfaces. However, in aluminum at room temperature (-0.3 Tm) there is no "apparent sliding" which is optically detectable. We suggest that, when the temperature is much lower (and possibly the rate of strain higher, too), as in the experiments of Chin et al., then aluminum behaves like magnesium at room temperature, and a narrow zone of shear develops to accommodate differences in strain across the grain boundary. Such a zone could well give rise to triple-point cracks. It is hoped to investigate these suggestions further. B. Y. Chin, W. F. Hosford, Jr., and W. A. Backofen (authors&apos; reply)—It is interesting to have Dr. Gif-kin&apos;s comments, although it is somewhat difficult to reply in detail without the reference containing the work that he describes. Apparently though, he does find a low-temperature temperature-independent sliding that would seem to be related to the observations reported here. Perhaps some of the difficulty has semantic origins, growing out of the distinction between (&apos;true sliding" and "apparent sliding".

Jan 1, 1965

By W. A. Stickney, J. W. Town

Tests demonstrated that aqueous solutions of sodiu~n sulfide would dissolve over 95 pct of the cinnabal- in 5 pct Hg flrotation concentrates and 60 to 90 pct of the cinnabav in low-grade ol-es. Double-leach tests showed that potassiutn sulfide would dissolve 90 pct of the avsenic sulfide in Hg-As satnples and only 1 to 10 pct of the Hg; the sodium sulfide would then dissolve 80 to 90 pct of the rernaining Hg and 30 to 70 pct of the vemaining As. 1 HIS paper describes the extraction, by alkaline sulfide solutions, of mercury from cinnabar-bear ing ores and flotation concentrates. Leaching time and solution temperature had minor effects on mercury extraction when compared to the effects of reagent quantity and ore type and grade. Cinnabar, although readily soluble in sodium sulfide, was only partially soluble in potassium sulfide and essentially insoluble in ammonium sulfide. A double leach process was developed to extract selectively the arsenic from Hg-As products with K2S and to treat the residue with sodium sulfide-hydroxide solutions to extract the mercury.&apos; Mercury was then recovered from the pregnant solutions either by precipitation with metallic aluminum or by electrodeposition. The solubility of HgS in alkaline sulfide solutions was first reported by Volhard in 1878.&apos; The first reported commercial application was made in 1915 when Thornhill applied the method to the treatment of an amalgamation tailing.3 Mullhollen, in 1911. described the chemical reaction of HgS with Na,S and alkaline hydrate to be:4 Most investigators have reported using a 4-pct sodium sulfide and a 1-pct sodium hydroxide soluti~n.3-4 An increase in temperature or excessive dilution of the solution causes the reaction to be reversed. Church Holmes described a similar process used for the extraction of antimony from silver concentrates at the Sunshine Mining Company&apos;s mill at Kellogg. Idaho.5 More recently. Erspamer and Wells reported the results of leaching studies on a Hg-Sb ore from Alaska.6 EXPERIMENTAL PROCEDURE Leaching tests were made on samples of mercury ore from eight deposits in Oregon, Washington, and Idaho. In addition. tests were made on flotation concentrates from seven of the samples as well as a flotation concentrate from an operating mill. Since previous investigators reported reagent requirements greatly in excess of that required by the equation HgS + Na2S = HgS . Na2S, initial studies were made on chemically pure HgS. Results showed that the reaction actually required about 1 g of Na,S per g of HgS in an aqueous solution rather than 0.338 g of Na,S as indicated by the equation. To check further the matter of reagent requirements, Na2S and HgS were mixed together in equal mole ratios. Water was then added, a drop at a time, until the components reacted; X-ray diffraction analyses showed no HgS nor Na,S present. The yellow hydrate compound which formed would not redissolve until about three additional mole equivalents of Na,S were added to the solution. This indicated that a stable solution would require at least 4 moles of Na2S for each mole of HgS. While these implications may be valid for pure HgS, the possibility of entirely different results caused by the existence of other elements present in ores and concentrates was recognized. Consequently, experiments of the same order were made on samples of a flotation concentrate from a producing mill. The concentrate, containing about 18 pct

Jan 1, 1962

By E. S. Bardwell, R. J. Lapee

Twenty years ago, W. T. Burns, in his paper presented at the Butte Meeting of the Institute,&apos; discussed the general scheme then in use in the electrolytic copper refinery of the Anaconda Copper Mining Co. at Great Falls, Mont., for removing impurities from tank-room electrolyte and controlling its acid content. Since then marked changes have taken place in copper-refinery practice at Great Falls. The electrolytic copper refinery in use in 1913 has been replaced by a new and entirely modern plant capable of producing up to 27,000,000 Ib. of cathode copper per month. With the building of the new plant in 1916, the treatment of converter anodes was discontinued. At first the substitution of refined anodes for converter anodes resulted in a decrease in the impurity content of the anodes, but as time went on, changes in metallurgical practices at the smelter resulted in substantial increases in the impurity content of the anodes. The leaching of the silver slime to remove copper before shipment to Raritan for treatment further added to the purification problem. The fact that the scheme of purifying electrolyte which Mr. Burns described in his paper has proved adequate for our needs under a wide variation of conditions speaks well for its essential soundness. Method of Purification Briefly, the method adopted for purifying tank-room electrolyte at Great Falls has been as follows: Each day a certain volume of tank-room electrolyte is run off and sent to the purification plant, where it is boiled down to approximately 46&apos; 136. The concentrated electrolyte is then sent to crystallizing tanks where the bulk of the copper is crystallized out as copper sulfate. The mother liquor is then passed through insoluble anode tanks to remove the last of the copper and most of the arsenic and antimony. It is then either returned to the tank room direct or boiled down to 55&apos; Bé, the iron and nickel salts crystallized out and the mother liquor returned to the tank-room circuit as restored acid. Prior to 1930 all of the evaporating was done in lead-lined tanks 13 ft. in diameter by 4.5 ft. deep, provided with lead heating coils through which steam at 30 lb. gage pressure was circulated.

Jan 1, 1934

By M. E. Glicksman, G. S. Ansel

It has been shown by Walton and Chalmers,&apos; that the mechanism of the development of solidification textures in castings involves the preferential growth of dendrites along certain crystallographic directions as determined by the influence of prevailing heat-transfer conditions. Specifically, this growth is parallel to the direction of heat flow. The purpose of the present investigation was to determine the applicability of this mechanism to: 1) commercially pure aluminum (99.75 pct) solidified to coarse columnar crystals, 2) an aluminum-silicon casting alloy (5.25 Si, 0.38 Fe, 0.02 Cu, 0.10 Ti, 0.002 S) cast to a fine-grained structure under complex and reproducible heat transfer conditions. PROCEDURE AND RESULTS 1) Specimen Preparation—Using a technique similar to that employed by Northcott and Thomas,2 samples were melted in the directional solidification mold, Fig. 1, by heating the entire assembly to 670° C. The mold was then end cooled using a water jet. From considerations of harmonic analysis, the likely distribution of isotherm normals encountered by the growing crystals is shown in Fig. 1. 2) Orientation Analysis—The pure aluminum sample froze to large columnar crystals, nucleated close to the metal diaphragm, with the growth direction parallel to the mold axis. Using the back-reflection Laue technique, the growth direction of these crystals was determined to be a <100>, which coincided within 53 deg to the mold axis. Metallographic examination of the relatively fine-grained aluminum-silicon sample revealed a dendritic mode of growth having its primary dendrite arms along isotherm normals. Back-reflection Debye-Scherrer patterns, taken with the specimen rotating about its cylinder axis, yielded rings displaying symmetrical arcing, thus proving that the sample did, indeed, possess the solidification texture inferred from the preliminary metallographic examination. To determine the extent and orientation of the texture in the aluminum-silicon alloy, a density distribution of the (111) poles of the sample was plotted using the transmission Debge-Scherrer

Jan 1, 1960