Search Documents

By A. A. Scheil, S. I. Hoyt

In technological studies on steel considerable emphasis has been placed on the identification of the foreign inclusions, testimony of which is adequately given in the metallographic literature covering methods for their identification. The outstanding accomplishment in this field is the scheme devised by Campbell, Comstock and Wohrman for identifying various oxides, sulfides, silicates and other constituents by systematic etching tests and microscopic examination.' The time involved in carrying out this procedure has led to attempts to secure quicker methods, or at least to shorten the time required to secure essential information. An example of this is the use of dark field illuminatin,2 but when this was tried out by the authors it was found that cavities and pits on the polished surface appeared bright on a dark field and could not be distinguished from small glassy inclusions. Still another means is the Leitz Ultropak, an instrument equipped with optical units for the illumination of the specimen by reflected light to secure an effect similar to dark field illumination. The structures are made visible in exceedingly sharp details by utilizing the inherent properties of the samples, such as refractive index, absorption coefficients and reflection powers. We have had no experience with the Ultropak, but a recent paper by Benedicks and Löfquist3 describes methods for determining the refractive index of (Fe, Mn) O and MnS by the use of this equipment. Presumably this method would be subject to about the same limitations as dark field illumination, though the, feature added by Benedicks and Löfquist appears to offer great promise in inclusion identification.

Jan 1, 1935

By A. A. Scheil, S. I. Hoyt

In technological studies on steel considerable emphasis has been placed on the identification of the foreign inclusions, testimony of which is adequately given in the metallographic literature covering methods for their identification. The outstanding accomplishment in this field is the scheme devised by Campbell, Comstock and Wohrman for identifying various oxides, sulfides, silicates and other constituents by systematic etching tests and microscopic examination.' The time involved in carrying out this procedure has led to attempts to secure quicker methods, or at least to shorten the time required to secure essential information. An example of this is the use of dark field illuminatin,2 but when this was tried out by the authors it was found that cavities and pits on the polished surface appeared bright on a dark field and could not be distinguished from small glassy inclusions. Still another means is the Leitz Ultropak, an instrument equipped with optical units for the illumination of the specimen by reflected light to secure an effect similar to dark field illumination. The structures are made visible in exceedingly sharp details by utilizing the inherent properties of the samples, such as refractive index, absorption coefficients and reflection powers. We have had no experience with the Ultropak, but a recent paper by Benedicks and Löfquist3 describes methods for determining the refractive index of (Fe, Mn) O and MnS by the use of this equipment. Presumably this method would be subject to about the same limitations as dark field illumination, though the, feature added by Benedicks and Löfquist appears to offer great promise in inclusion identification.

Jan 1, 1935

By Frank H. Macpherson

Few people realize the tremendously important part that Saline and Pulaski Counties in central Arkansas have played in the winning of the war The present favorable war situation might have been very different if we had not had the bauxite produced during the past two years from these two small areas, a total Of about 15 square miles. As a general statement, it can be said that the Arkansas bauxite deposits are, individually, relatively small, irregular in thickness, somewhat scattered and, therefore, compared with coal or iron-ore or open-pit copper deposits, relatively ill adapted to a rapid and drastic expansion in output. A few years ago it would have seemed an impossibility for these two counties to produce over six million long dry tons of bauxite in one year. However, with the cooperation of the operators, that is what happened in 1943, when the state of Arkansas achieved the seemingly impossible with a production of 6,020,684 1 long tons (dried equivalent) of bauxite ore during the calendar year, compared with an average annual production of 323,7252 tons in the period 1931 to 1941. It became apparent early in the year '94' that the united States soon might be drawn into the war, and, therefore, that an immediate study of the domestic metal situation was necessary. Aluminum is by far the most important metal used in the manufacture of aircraft and many other implements of war and it was evident that there would have to be a tremendous increase in the domestic production of bauxite, which is practically the only present source of this metal. AS more than 95 per cent of the known bauxite reserves of the United states was in Arkansas, careful preliminary studies were made in that state by representatives of the united States Bureau of Mines, the United States Geological survey and the War Production Board in the summer of 1941 Reserves in other states also were studied. The result of these studies was a recommendation by the War Production Board that mining in the bauxite.producing areas of Arkansas be geared for maximum production, in order to supply sufficient ore for this country's war requirements and, if necessary, to supply the war needs of Canada as well. The annual goal of eight million long tons (dry weight) set for Arkansas by the war Production Board was exceeded in 1943, when in August the output reached a rate equivalent to more than 8,300,000 long tons, dry basis. Because of the comparatively small tonnage of bauxite reserves, Congress appropriated funds for an extensive drilling program to be carried out by the Bureau of Mines in cooperation with the Geological Survey. Drilling began in May 1942 but owing to delay in delivery of drills, and trucks upon which the drills were mounted the program did not get into peak operation until early in 1943. By the end of July 1944, the Bureau of Mines records indicated an addition to the Arkansas reserves of 10,000,000 long tons (wet basis) in place,

Jan 1, 1946

AARONS, J. BOYD, Major. AGNEW, FRANK VANS. ALLEN, HERMAN H., Private, D Co., 8th -Reserve Engineers. BAINS, THOMAS M., Major, Engineer Officers' Reserve Corps. BANKS, H. R., Lieutenant, Canadian Engineers, B. E. F. BARBOUR, PERCY E., Deputy Supt. (Captain), New York State Troopers; Captain, 22d Regiment, N. Y. N. G. BARLING, H. B., Ist Lieutenant', Engineer Officers' Reserve Corps. BIGELOW, BRAXTON. BLOOMFIELD, E. C., Lieutenant. , BORROW, F. K. BROCK, R. W., Major, 19th Reserve Battalion of Canadians. BROOKS, ALFRED H., Captain, Engineer Officers' Reserve Corps. BROWNE, DE COURCY, 1st Lieutenant, Ordnance Dept., Fortress Monroe, Va.

Jan 9, 1917

By Frederick L. Knouse

THE south border of Espirito Santo begins about 400 km. north of Rio de Janeiro and extends along the Atlantic Coast northward some 325 km. and inland 100 to 150 km. The area under consideration, where quartz crystal of strategic grades has been mined, extends from 19° to 21° and 30" south latitude; and from 40° to 41° and 30" west longitude. This includes the central part of Espirito Santo, chiefly south of the Rio Doce from the Atlantic ocean, and west across the border into Minas Gerais near the town of Aimores, in the municipalities of Aimores, Minas Gerais; Baixo Guandu, Santa Teresa, Santa Leopoldina, Colatina, Joao Neiva, Fundao and Domingo Martines, Espirito Santo (Fig. 1). During 1943 and the first half of 1944, this region accounted for approximately 3 to 5 per cent of the quartz crystal produced in Brazil. Shipments of crystal have been made chiefly by rail to Rio de Janeiro. This region is serviced by the E. F. Minas-Vitoria and E. F. Leopoldina to Rio de Janeiro through Vitoria; and by the E. F. Minas-Vitoria and E. F. Central do Brasil through Bello Horizonte, Minas Gerais to Rio de Janeiro. The major deposits are accessible from the railheads by dirt roads, some being 5 to 30 km. off the road, reached by trail. In 1943 and the first half of 1944, the bulk of the production was from inter mountain marshes and adjoining hillside alluvial placer deposits in the zone surrounding the town of Santa Teresa. Most of these deposits were formed from the erosion of pegmatites, quartz veins and pockets in the gneiss, with minor quantities produced from miarolitic cavity fillings in the granitic rock. EARLY OPERATIONS Mining of quartz crystal in this region began in 1928, and has been stimulated by the market demand for military uses. Before 1936 little attention was given to it, either in Espirito Santo or eastern Minas Gerais. From 1936 to 1941 the Japanese sent agents to various points of production or potential production to acquire quartz through purchase. They bought crystal as small as 10 grams. Since 1941 only the United States and Great Britain have received quartz from Brazil. The United States purchases crystals of loo grams and larger for strategic purposes. The first known discoveries were made either in the municipalities of Aimores, Minas Gerais, or in Baixo Guandu, or Domingos Martines, Espirito Santo. Marketable quartz crystal was first found either in the massive quartz replacement veins of the Victor Hugo mine in the municipality of Domingo Martines, or in the large cores of quartz in the pegmatites near Baixo Guandu, extending into Minas Gerais. PRODUCTION The production of quartz in Espirito Santo from 1936 through 1941 as recorded

Jan 1, 1946

The Honor Roll includes the names of all members of the Institute Whom we know to have been on active military duty it the date of compilation, Mar. 5, 1919. Despite our efforts to have this list accurate and complete, some of our members who have been rendering military service are probably left off because of the fact that we have not been informed of their military connection. The list of men in military service has been compiled with great difficulty owing to the modesty of the members, who in their patriotism began their service but neglected to send us notice. In 1918, We published a separate Honor Roll of the Institute in which we included a list entitled "On active duty in other departments of the service" which contained the names of members who were rendering important emergency service to the Government other than in the Army. This list is entirely omitted this year because any list We might compile for this purpose would be entirely inadequate and must inevitably do injustice to a large number of our members who have been devoting great time and making many sacrifices for the benefit of the government along lines not within our ken. It is not too much to say that almost all our membership in this country has been, more or less directly, doing its uttermost for the successful prosecu¬tion of the war. The active work of many of these members we are Well aware of, as is also the rest of the civilized world. Faithful and wholehearted efforts on the part of many other members we have not been informed of, so that any list would be both incomplete and unsatisfactory.

Jan 1, 1923

By W. D. Sylwestrowicz

In tests on polycrystalline copper and aluminum, the ratio of the yield stress to modulus of elasticity was found to be strongly dependent on tempemture. Also, it was shown that the change of the yield stress with temperature of a material at a given temperature and deformed to a given yield stress, but not necessarily to the same strain, does not depend on previous mechanical thermal history. Likewise, for a material at a given temperature and deformed to a given yield stress, the rate of work hardening is independent of the temperature of prior stressing. It has been shown by Los and Orowan1 and by Dorn, Goldberg, and Tietz2 that the temperature dependence of the yield stress-strain curves of crystalline materials reflects two effects: not only does the yield stress of a material in a given structural state depend on the temperature, but the structural state (and the corresponding strain hardening) after a given amount of plastic straining also depends on the temperature at which the pre-straining has been carried out. Thus, for instance, if a specimen of a ductile metal has been strained along the stress-strain curve 1 at room temperature to point A, Fig. 1, and then the straining continued in liquid nitrogen along curve NR, the yield stress A' immediately after lowering the temperature is lower than the yield stress A" of a specimen that has been strained by the same amount in liquid nitrogen (along curve 3). AA' represents the effect of the temperature change upon the yield stress of the specimen pre-strained at room temperature; A' A" is the excess strain hardening acquired if the pre-straining has been carried out in liquid nitrogen instead of at room temperature. The dependence of the yield stress (i.e., of the structural state acquired during preceding straining) upon the conditions (speed, temperature) of a pre-straining is the reason for the nonexistence of a so-called "mechanical equation of state" for plastic deformation. A 'mechanical equation of state" is a relationship of the form F(s,E, e, T) = 0, or s = f(E, E, T) [1] It was first suggested by Ludwik3 that plastic deformation might obey such an equation; this, however, was conclusively disproved by experiments of Kochendorfer.4 Additional disproofs were given in

Jan 1, 1959

By E. C. Harder, D. F. Hewitt

Since early in 1916, when it became apparent that the steel industry of the United States could not depend for the duration of the war on several important foreign sources of manganese and might have to depend entirely on domestic ores, the U. S. Geological Survey, with the assistance of several cooperating organizations, has made a comprehensive investigation of domestic manganese resources. The work has included field studies in a number of states well as annual, quarterly, and monthly canvasses among operators concerning current and future production. In order that the interested public might have access to the important results of the studies, preliminary reports concerning the field work as well as periodic summaries of production were issued as promptly as possible. Although numerous summaries of production l2, l3, l4 have been prepared from time to time for the use of the several boards and committees responsible for the conduct of the war, it has been thought for some months that those engaged in the industry, as well as others, might be interested in a preliminary summary of the accumulated geologic and production data. The cessation of hostilities, in November, 1918, probably detracts from the usefulness of much of the material that is here presented, but apart from the historic interest in the performance of an important industry in war time, there is a possibility that some of the conclusions may be helpful to those who continue to exploit domestic deposits, as well as to those who wish to measure the country's independence in mineral supplies. Appropriate final geologic reports are being prepared by the geologists who did the field work. The present authors, having done but a small part of the recent field work, acknowledge with great appreciation the use of preliminary and unpublished reports and the cordial informal cooperation of the following geologists in the preparation of this paper: F. L. Ransome, G. W. Stose, F. C. Schrader, J. T. Pardee, E. L. Jones, Jr., H. D. Miser, Laurence LaForge, J. B. Umpleby, Arthur Keith, F. J. Katz, and E. S. Larsen, of the U. S. Geological Survey. Field work in Virginia was carried out in cooperation with the Virginia Geological Survey, T. L. Watson, State Geologist; in Georgia, with the Georgia

Jan 1, 1920

By Hsun Hu, R. S. Cline

The effect of rate of deformation on texture formatiotz has been studied with cube-oriented single crystals of 3 pct Si-Fe, compressed 80 pct at two widely different rates. Compression at a low rate (crosshead speed, 0.1 ipm) produces large orienta-tional changes and coarse deformation bands, whereas little change in orientation is observed, particularly at the surface of the crystal, when compressed at a high rate (impact velocity, -500 ips). Thin plates of mechanical twins are produced at the high rate, but their contribution to the deformation texture is practically negligible. The crystal deformed at a high rate has a lower hardness and a more uniform dislocation structure and is morc resistant to recrystallization. There is also a dilference in the recrystallization texture between the slowly and rapidly compressed crystals. These results indicate that plastic flow is less "turbulent" at high strain rates than at low strain ratcs. THE behavior of metals under high-speed deformation has been the subject of wide study in the past decade. Most of these works were concerned with mechanical properties during testing at high rates of loading, the resulting structures, and the theoretical aspects of the observed phenomena. The present status of knowledge and research activities in this field has been documented in recent publications.17' There is, however, very little information available in the literature concerning the effect of high-speed deformation on the texture formation in metals. The possibility of an effect of rate of deformation on texture is suggested by the microstructural differences observed between normally and very rapidly deformed samples. Aside from the strong tendency for twinning (and phase transformation in certain metals) in high-speed deformation, the slip-line patterns and the dislocation configurations show marked differences as a result of large differences in the strain rates. For instance, in mild steel in static and dynamic compression, Campbell and co-worker3,4 observed that coarse slip occurred on several systems in specimens deformed at normal strain rates, whereas specimens deformed rapidly showed only fine slip on fewer systems, the slip-line pattern being very similar to that in specimens deformed at low temperatures and at normal strain rates. The absence of multiple slip was also noticed by Dieter5 in shock-loaded nickel. The dislocation configuration in an iron shock loaded at 70 kbar pressure was shown by Leslie et al.6 to be similar to that produced by light rolling at low temperature—the dislocation lines were mostly straight and uniformly distributed. These observations suggest that the mode of deformation at high strain rates is notably different from that at low strain rates. Consequently, the nature and the extent of lattice reori-entation during deformation should also be different. This investigation was undertaken to test this idea. MATERIAL AND METHOD The remaining part of a single-crystal ingot of a 3 pct Si-Fe alloy,* prepared for an earlier investi- gation,1 was used in the present studies. Specimens 9/16 in. square and 0.365 in. thick were cut from this ingot with (001) planes parallel to the square surfaces, and the [loo] and 1010] directions parallel to the edges of the specimen, within ±1 deg. These machined crystals were etched to remove distorted metal, and annealed at 1300°C for 24 hr in a purified helium atmosphere. The annealed crystals had a hardness of 161 Dph. The crystal orientation was rechecked with X-ray back-reflection techniques. In high-strain rate experiments the crystal was compressed in a Dynapak machine to approximately 80 pct reduction in thickness (from 0.360 to 0.070 in. with an impact velocity of -500 ips). Thus, the duration of loading was approximately 6x 10-4 sec, and the average strain rate was about 103 sec-1. As a result of this rapid, severe deformation, the specimen became a roughly circular thin disc. The original shape of the crystal, however, could still be recognized by a diffusely outlined square area in the center of the disc. For compression at a low speed, the crystal was deformed in a universal testing machine at a rate of crosshead movement of 0.1 ipm. Compared with

Jan 1, 1965

By Warren B. Davis

Introduction If a subject this broad were to be covered in even moderate detail, it would require a set of books about the size of an encyclopedia. Since an acceptable length for this paper is a small fraction of one book, it will have to consist of a few samples of the subjects that I think are the most pertinent to World Fossil Fuel Economics. I plan to discuss the trends in world energy demand, particularly in the U. S. and Europe; the consumption patterns and cost patterns of oil, gas and coal; the prospects of synthetics; and some of the effects of government regulation of fuel economics. World Energy Demands Fig. 1 shows Free World energy consumption by principal areas for the period from 1950 to 1970 and a forecast for the period from 1970 to 1985. These figures include only the measurable forms of energy. An example of energy consumption that is not measured is the wood a peasant might cut in the forest and bum in a fireplace to heat his home. This omission probably is a very small part of the total. This forecast is not identical with that of Wayne E. Glenn (see Page 22), but the differences in total energy consumption are not significant. The U. S. consumption, which was 55 percent of the world total in 1950, had declined to 45 percent by 1970, and is expected to decline further to 38 percent by 1985. Western Europe has consumed 28 percent of the total from 1950 to 1970 and is expected to lose share slightly between 1970 and 1985. The most spectacular gainer is Japan, which increased consumption from 2.5 percent in 1950 to 7.5 percent in 1970, and is expected to reach nearly 17 percent by 1985. The over-all Free World total has grown from 62 quadrillion Btu (equivalent to 29 million B/D of crude oil) in 1950 to 151 quadrillion by 1970, an average growth rate of 4.5 percent/year. This total is expected to grow at a rate of 5 percent/year between now and 1985, reaching 315 quadrillion Btu (equivalent to nearly 150 million B/D). Fig. 2 shows which fuels supplied this energy between 1950 and 1970, and gives an estimate of how it will be supplied between 1970 and 1985.

Jan 1, 1971

By G. Howell Clevenger

FORMERLY great divergence of opinion existed in regard to the influence of copper in steel, as affecting its various physical properties. More recently the investigations of Stead,1 Breuil,2 Wigham,3 Burgess and Aston,4 Ball and Wingham,5 Miiller,6 Dillner,7 and others have shown fairly good agreement in the major points. Copper steel has been shown by these investigators to possess special properties which make it valuable for certain uses. The general range of composition of the useful alloys of copper and iron, and of copper, iron, and carbon, has been quite definitely established, for the former by Burgess and Aston,8 and for the latter by Breuil 9 and Stead.10 Stead 11 has removed one difficulty in reconciling certain of the earlier data by calling particular attention to the influence of carbon in copper steels. Another point which caused confusion in the earlier investigations, particularly in regard to " red-shortness," was the presence of sulphur. Failure to note the presence of sulphur often led to attributing " red-shortness " to the presence of small amounts of copper. Turner 12 has called attention to the fact that where copper exists in an iron ore it often occurs as the sulphide, so that the presence of copper in steel made from such ores might also, necessarily, mean the presence of sulphur. It is evident that the effect in this case might be quite different than where pure copper was added.

Jan 10, 1913

By C. Norman Cochran, James L. Brandt

ALTHOUGH gas in aluminum and its effect on aluminum products have been the subject of a number of papers, not many quantitative determinations of the hydrogen content of solid aluminum and its alloys have been recorded in the literature. For solid aluminum samples, four investigators have reported hydrogen contents which appear reasonable compared with the hydrogen solubility of 0.7 ml per 100 g, STP, in molten aluminum at 660°C established by Ransley and Neufeld' and verified by Opie and Grant' and Ransley and Talbot. Sloman," who used a vacuum fusion procedure, reported the hydrogen content of some high purity aluminum as 0.66 ml per 100 g, STP. Griffith and Mallett, employing the tin fusion method, reported the internal hydrogen content of six different aluminum alloys as ranging from less than 0.1 ml per 100 g, STP, for 1100 alloy to 0.7 ml per 100 g, STP, for 4043 alloy (previously 43S, a 5 pct Si alloy). Eborall and Ransley," using a solid extraction of the gases at 600°C, reported hydrogen contents ranging from 0.1 ml per 100 g, STP, to 1 ml per 100 g, STP. Ransley and Talbot reported that several thousand analyses on 99.2 pct and higher purity aluminum as well as Duralumin type alloys indicated hydrogen contents ranging from 0.1 ml per 100 g, STP, to 0.5 ml per 100 g, STP.

Jan 1, 1957

By R. M. Caves

High-purity dense tungsten coating is obtained by means of a modified de Boer-van Arkel iodide process using tungsten bromides. The all-glass reaction system is pumped, baked, and sealed (pinched-off) at about 10-7 mm Hg pressure. The bromides then formed in situ are decomposed, depositing tungsten on heated tungsten surfaces. Heating of the specimen is done inductively in a novel arrangement that avoids electrodes of glass-to-metal seals. The tungsten, deposited at specimen temperatures from 2000° to 2800°F and bulb (halide) temperatures of 225" to 725°F, was adherent and uniform, and ranged in thickness to 1/8-in. REFRACTORY metals are of interest at NASA for use in hypersonic aircraft, in rocket engines, and in other thrust devices where very high temperatures are encountered. Tungsten, with a melting point about 6100° F, is potentially very useful for some of these applications. Considerable research on tungsten and its alloys is currently being conducted at the NASA Lewis Research Center. In this tungsten research program, there is need for a method of depositing high-purity, nonporous tungsten coatirlgs. Metallurgical bonding of the coating both to itself and to the substrate is required. In addition, it is necessary to be able to deposit thin, uniform coatings on substrates of a variety of shapes and sizes for laboratory test purposes. A survey of the methods previously used for depositing tungsten coatings indicated that none would likely meet these requirements for high purity, good uniformity, and high density except thermal decomposition of the halides. The method for coating that was selected for investigation was the thermal decomposition of tungsten bromide. This is a variation of the van Arkel and de Boer iodide process established years ago and recently reviewed.1,2 This process is applicable to the transition metals in general. More recently, the application and techniques were extended with chlorine3 and fluorine,4 and included the coating of tungsten. This is believed to be the first report on the use of the bromide for tungsten coating. Bromine was chosen over the other halogens because it promised a lower temperature for tungsten

Jan 1, 1962

By George Lehman

THE Inspiration Consolidated Copper Co. had an orebody at Miami, Ariz., of close to 100,000,000 tons of low-grade copper ore, and the method of mining this ore most profitably was of great importance. The selection of a method was practically limited to a "top-slicing," a "shrinkage-stope" or a "caving" method. The "top-slicing" method would give a high extraction of the developed ore, at a high mining cost, and the ?shrinkage-stope" or "caving" methods ) a lower extraction of, the developed ore, at a lower mining cost. ORE-DRAWING TESTS To decide on the method to be used it was necessary to know about what extraction of the ore could be obtained by the "shrinkage-stope" or "caving" methods. As no definite information regarding the question was available at the time, C. E. Mills, the general manager, thought that some information could be obtained by experimenting in drawing ore, covered with capping, from an experimental box. Some work had already been done along these lines by W. C. Browning for the Inspiration Copper Co. and by myself for the Live Oak Development Co. The idea was to represent as nearly as possible, in the experimental box, the conditions within an area of caved stopes of caved ore all ready for drawing. That is, the area was supposed to represent a semibroken mass with the capping above it in the same condition and ready to follow the ore downward as it was drawn out of the chutes under the ore. To represent the above condition, in the experimental box, crushed ore from the mine was placed in it to a given height, and red barren capping from the mine was placed on top of the ore.

Jan 9, 1916

J. M. Wadsworth,' Okmulgee, Okla. (written discussion).—It seems to me that thc young man must first be absolutely sure that the work he has taken up is to his liking and then I would advise that he get into the practical end of it and learn as much about it as he can as fast as he can. For instance, in the refinery business the college man, graduated in chemical engineering, should ground himself by going through the various departments in a refinery and working in them until he is thoroughly familiar with the operating problems. In a short time he would be able to apply many things which appear in the abstract form in his college work and this would opcn up an opportunity for him to capitalize on them, promoting his own interest. I do not criticize the present-day college men as a class, but I have found that many of them come into your plant with the idea that mere possession of a diploma should insure rapid promotion; in a short time they are impatient and usually leave. We have found in employing men that the single attribute most difficult to find in them is a lot of energy and whole-hearted interest in the work at hand, and it seems to me that if a man combines these with a careful technical training he should be fairly well equipped to gamble on his future. They must learn that the biggest satisfaction to be gained in life is in their work. Procedure for Attaining Objective of Young Petroleum Engineer H. B. Fell,+ Ardmore, Okla. (written discussion).—Of course, the first thing to be ronsidered in any proposition is the ultimate objective that is desired to be attained. 1 presume that the desired objective of most of the young men graduating in petroleum engineering will be that of chief executive of one of the companies in the petroleum industry, or one of the allied industries, or to become an independent oil producer, or oil refiner, or possibly an oil distributor. The next phase then to be considered is the procedure which should most logically be followed to attain the objeckive of the indivitlual, since in these cases these young men will have been trained in a course in petroleum engineering and it would logically be presumed that the attainment of their objective should be through the operating end of the branch of the business with which they are connected. The operating end is, of course, the department of each branch of the business that develops the resources, or refines the products, or distributes the products, from which the profits are derived, and is a part of any business which is filled with enough interesting work to appease the desires of the most ambitious young men. In order to get the best possible training it would appear to me that the place for a young man to start after graduation would be at the bottom of that branch of the industry which he expects to follow. For example, if he is going in the producing end he can gct no better training than is secured by starting as a roustabout in the ficltl, where he romes in constant rontact with the character of work that is necessary

Jan 1, 1928

T. L. Joseph (University of Minnesota, Minneapolis, Minn.)—Mr. Killian is to be commended for his inquiry as to why a decrease of 15.3 pct in coke consumption was accompanied by a decrease of only 1.9 pct in the CO/CO, ratio of the top gas. Although I encouraged him in his efforts to find a more significant and meaningful carbon-gas ratio, the method, calculations, and conclusions originated entirely with the author. Whether we agree entirely with the assumptions underlying his corrected ratio, I think we can all agree that a better ratio is needed, and that he deserves credit for recognizing the need and for doing something about it. To be most useful, the CO/CO, ratio for the top gas should reflect the way in which the carbon is gasified in the furnace, particularly the degree of oxidation and the extent of heat release. The effect of CO, from the decomposition of the limestone and the effect of the reaction of CO and water vapor in the upper part of the furnace on the quality of top gas should be isolated from the effect of more basic reactions such as ore reduction and solution loss. The reduction of sufficient iron oxide to produce a ton of pig iron and the accompanying changes in the proportions of the carbon gases can be expressed on a mol basis as follows: 16.5FeA + 16.5CO - 33FeO + 16.5CO, [1] 33FeO + 33.0CO = 33Fe + 33CO. [2] The CO, from eq 1 normally escapes from the furnace because it does not react with coke at the temperature of its release. However, as much as 50 pct of the CO, from eq 2 may react with coke because it is released at temperatures above 1000°C: 16.5CO. + 16.5CO2 = 33CO [3] Thus we see that the gasification of 16.5 mols or about 200 lb of C in solution loss will regenerate as much CO as is required for the last stage of reduction. The pronounced effect of reaction 3 on the final proportions of CO and CO, in the gas stream is obvious. It also follows that reaction 3 materially alters the heat release but it cannot be entirely eliminated in Lake ore practice. A previous study indicates that 100 lb of solution loss may be necessary to maintain the reducing power of the gas. A reduction of 100 lb from the normal level of 200 lb would mean that over 1,-000,000 additional Btu are released in the process. The 100 lb of additional carbon which will be burned at the tuyeres will release 437,000 Btu and the absorption of 583,000 Btu by eq 3 would be prevented. One of the chief objectives of sized ore burdens and more uniform distribution of the gas stream is to minimize solution loss by completing reduction higher in the furnace and in turn to release the maximum amount of heat from the carbon charged. It was odd, indeed, to find that the use of sized ore and sinter in the careful tests reported by Dobscha had changed the CO/CO2 ratio very little. The author has stressed the close correlation between his corrected CO/CO, ratio and production. A correlation of fuel consumption and the CO/CO, might be more logical. Fuel consumption on the prepared ore burden decreased 15.3 pct whereas the corrected CO/CO2 ratio decreased 19.0 pct. Although this agreement between the reduction in fuel and the reduction in corrected CO/CO2 ratio is not as close as the correlation with tonnage, it indicates the corrected ratio is superior to the normal ratio which decreased less than 4 pct. Some adjustment should be made for the reaction: CO + H2O = CO2 + H2 —700Btu [41 because there is evidence to indicate that about one half of the hydrogen is formed in the upper 21 ft of

Jan 1, 1953

By J. L. Bruce, N. B. Braly, F. A. Linforth, Wm. B. Daly, Paul A. Gow, C. L. Berrien, R. H. Sales, P. F. Beaudin, John Gillie, G. W. Roddewig

Butte mining district is situated in Silver Bow County, in the southwestern part of Montana. Butte originated as a placer mining camp, gold having been discovered in 1864, on Silver Bow Creek, near the southerly end of what is now Main Street. The Butte placer gold was heavily alloyed with silver, and only commanded $13 an ounce. Placer mining was vigorously prosecuted along Silver Bow Creek and its tributary gulches for about 5 years, at the end of which time, in 1870, the Butte camp was practically deserted. In the meantime, the quartz veins prominently traceable over the hillsides were located, the first location, July 12, 1864, being made by the Missoula Mining Co. and called the Missoula Lode Claim, and later relocated by G. 0. Humphreys. Reasoning from the presence of the gold placers, free milling gold and silver ores were eagerly looked for by the early prospectors. Claims covering the great Rainbow and other silver lodes were located in the 60's. The presence of valuable silver ores in these veins caused the staking of many claims, believed to be valuable only for silver, but which later, at depth, proved to be enormous copper producers.

Jan 1, 1925

By Ernst F. Eurich

Alexander Parkes patented in England in 1851-52-53 a process for desilvering lead by means of zinc, making use of the greater affinity of silver for zinc than for lead, discovered by Karsten in 1842. The efforts in England to develop it commercially were not particularly successful, nor was the attempted introduction into the United States. This last was not surprising, as it was about the beginning of our Civil War, and at that period there was very little lead-bullion produced in the United States and there was no field for the process here. There was at that time on Staten Island an establishment that pattisonized lead, probably from Rossie, N. Y., and Chester, Pa., and possibly some Spanish lead, but the production of lead-bullion in the Far West had not yet begun. In 1864, Edward Balbach, of Newark, N. J., patented in this country a process for desilvering lead by means of zinc, and in 1867 Edward Balbach, Jr., patented a " movable black-lead retort with a neck, placed in a furnace," for the purpose of distilling the alloy of zinc, lead, and the precious metals. A brief comparison of the Parkes and the Balbach processes is interesting. The Parkes process as practiced in England consisted in stirring into silver-bearing lead, melted in a kettle, from 1 to 2 per cent. of zinc, cooling, skimming the alloy of lead, zinc, and silver that rose to the surface, liquating it in an iron retort, distilling the residual rich alloy in fire-clay retorts, thus regaining the zinc, and refining the desilvered lead at a low heat in a shallow cast-iron pan that formed the hearth of a reverbera-tory furnace. If the lead was too impure, it was first softened

Jan 1, 1913

By B. Egeberg, H. B. Smith

Britannia metal is a white alloy consisting primarily of tin and antimony, the tin greatly predominating. The alloy usually contains a small amount of copper and occasionally very small amounts of one or two other metals, such as bismuth, zinc, and lead. It is capable of being cold-rolled, it takes a high polish, and it is fairly noncorrosive; properties which make it a popular metal for many household and traveling utensils. Britannia metal is similar in many respects to pewter and has largely replaced pewter in the arts, but it should not be confused with that alloy, because pewter is essentially a tin-lead alloy, while Britannia is a tin-antimony alloy. In view of the fact that so little has been published concerning Britannia metal, the authors feel justified in presenting the results of their investigation, particularly since the behavior of this alloy under cold rolling and heat treatment differs so greatly from that of other metals and alloys. The old craftsman, engaged in the making of ornaments or tableware, heated the cold-rolled sheet metal or his finished product to a straw color corresponding to about 375" I?., claiming to produce thereby a harder and more rigid article. The fact that possibly led him to this heating was that a reheated article or sheet made from Britannia metal has a distinct metallic ring when struck a sharp blow, whereas an unheated article or sheet has a leady, dead note. No doubt he has associated the metallic ring with a greater rigidity and strength, and justly so, as will be seen later. The approximate analysis of the metal we investigated was 91 Sn, 7 Sb, 2 Cu, and the molten metal was bottom-poured into an iron mold yielding an ingot 7 3/4 in. wide by 11 in. long and % in. thick, the casting temperature being 800" F. The ingot was cold-rolled to a sheet 0.032 in. thick, sufficiently large samples for experimental purposes being cut from the sheet at intermediate stages. The samples were all tested for hardness with scleroscope and Brine11 machine, then heated to 212" F. for 30 min., and again tested after cooling to room temperature. The same samples were heated successively at 300°, 400°, and 440" F., followed

Jan 1, 1929

By H. B. Smith, B. Egeberg

Britannia metal is a white alloy consisting primarily of tin and antimony, the tin greatly predominating. The alloy usually contains a small amount of copper and occasionally very small amounts of one or two other metals, such as bismuth, zinc, and lead. It is capable of being cold-rolled, it takes a high polish, and it is fairly noncorrosive; properties which make it a popular metal for many household and traveling utensils. Britannia metal is similar in many respects to pewter and has largely replaced pewter in the arts, but it should not be confused with that alloy, because pewter is essentially a tin-lead alloy, while Britannia is a tin-antimony alloy. In view of the fact that so little has been published concerning Britannia metal, the authors feel justified in presenting the results of their investigation, particularly since the behavior of this alloy under cold rolling and heat treatment differs so greatly from that of other metals and alloys. The old craftsman, engaged in the making of ornaments or tableware, heated the cold-rolled sheet metal or his finished product to a straw color corresponding to about 375" I?., claiming to produce thereby a harder and more rigid article. The fact that possibly led him to this heating was that a reheated article or sheet made from Britannia metal has a distinct metallic ring when struck a sharp blow, whereas an unheated article or sheet has a leady, dead note. No doubt he has associated the metallic ring with a greater rigidity and strength, and justly so, as will be seen later. The approximate analysis of the metal we investigated was 91 Sn, 7 Sb, 2 Cu, and the molten metal was bottom-poured into an iron mold yielding an ingot 7 3/4 in. wide by 11 in. long and % in. thick, the casting temperature being 800" F. The ingot was cold-rolled to a sheet 0.032 in. thick, sufficiently large samples for experimental purposes being cut from the sheet at intermediate stages. The samples were all tested for hardness with scleroscope and Brine11 machine, then heated to 212" F. for 30 min., and again tested after cooling to room temperature. The same samples were heated successively at 300°, 400°, and 440" F., followed

Jan 1, 1929