By CLAYTON C. BALL

In the year 1948, more than ever before, the coal industry established itself on the threshold of a new and exciting future expansion. While production did not equal the wartime and peacetime peaks of 1944 and 1947, it was, in review, a good coal year. During the latter part of the year a combination of mild weather, record stock piling, and general business slackening reduced coal demand to the extent that marginal mines suspended operations, while mines remaining active found it necessary to renew their attention to producing better products at lower operating costs.

Jan 1, 1949

Organization Place Date 1919 National Drainage Congress St. Louis, Mo. Nov. 11-13 American Mining Congress St. Louis, Mo. Nov. 1.7-21 Canadian Mining Institute Vancouver, B. C. Nov.. 26-28 American Society of Mechanical Engineers:.... New York, N. Y. Dec. 2-5 American Institute of Chemical Engineers Savannah, Ga. Dec. 3-6 Geological Society of America...; Boston, Mass. Dec. 29-31. American Society of Heating and Ventilating 1920 Engineers New York, N. Y. Jan. Mining and Metallurgical Society of America ... New York, N. Y. Jan. 13. American Institute of Min. and Met. Engineers... New York, N. Y. Feb. 16-19 American Ceramic Society Philadelphia, Pa. Feb. 23-26

Jan 11, 1919

By H. D. Mellom

The direction of the optic or "C" axis of a uniaxial metal crystal can be found with the metallurgical polarizing microscope by examining two planes of section on the crystal. Complete orientation of the crystal can be determined if a twin crystal is common to both surfaces of section. Examination of Uniaxial Metals in Polarized Light-Rotation of a uniaxial crystal surface, properly prepared,' shows four extinction positions 90 deg apart, provided that the surface is not close to a basal section. One of these two extinction directions corresponds with the projection of the optic axis on the surface of section. This direction can be found if the 'sign of the rotationr2 for the metal is known. To find the direction of the optic axis, the crystal is rotated on the stage 45 deg from an extinction position. With a crystal of negative sign, to produce extinction the analyser must be rotated towards the optic axial direction and vice versa. All sections, other than basal, of a uniaxial crystal have the same sign of rotation and, since there is no change in sign with wave length, white light can be used for these measurements. U the sign of the rotation is not known the presumed direction of the optic axis can be determined assuming a positive sign. A third section cut normal to the presumed optic axis will show basal extinction if the assumption is correct. It is convenient to use the edge between the two planes of section as a fiducial direction common to both surfaces. The optic axis can be related to this direction. If the above measurements are repeated on the other plane of section and the angle between the two section planes measured, stereographic projection can be used to determine the orientation of the crystal optic axis. Determination of Complete Orientation—The complete orientation of a uniaxial crystal can be determined provided that a twin crystal is common to both surfaces of section, and the twin law is known. The orientation of the twin crystal optic axis can be determined in the same way as for the main crystal

Jan 1, 1962

By Herbert H. Kellogg

The chemistry of sulfide roasting is analyzed to show those aspects of performance which Thecan be predicted from considerations of thermodynamic equilibrium. It is concluded that equilibrium calculations can serve as a yardstick for prediction of roaster-gas composition and sulfate formation in the calcine for fluid-bed roasting practice. A method of calculation which combines the equilibrium and stoichiometric factors is outlined, and illustrated by an example from the roasting of Cu-Fe sulfides. ON first examination the roasting of sulfides would not seem to be a process to which equilibrium calculations could be applied to yield results of practical value. The burning of sulfides is an ex-tremely spontaneous reaction, excess air is always used to obtain rapid reaction, and in most traditional roaster designs (hearth roasting) the temperature and gas composition vary widely from point to point in the roaster. These are all conditions which promote a non-equilibrium state in the roasting process. However, the introduction of the fluid-bed roaster1 has brought to roasting practice new conditions of operation, so that equilibrium calculations can be used to predict certain limited aspects of practical operation. The fluid bed is characterized by uniformity of temperature, gas composition, and calcine composition from point to point throughout the bed. These relatively uniform properties of the bed make the meaningful calculation of the equilibrium state of certain reactions in roasting possible. It is the purpose of this paper to analyze roasting from an equilibrium viewpoint, to show where the method may be expected to yield valuable information, where it fails, and to outline methods of calculation. Main Roasting Reaction The reaction MS (s) + 3/2 0, = MO (s) + SO, [I] might well be called the main roasting reaction. It adequately accounts for the well known facts that metal sulfide and air are the main reactants, and metal oxide and SO, the main products. Deviations from this simple stoichiometry will be discussed under side reactions. For all metal sulfides, Reaction 1 is strongly exothermic and the equilibrium position is far to the right. Since the reaction is exothermic, the equilibrium shifts in the right-to-left direction as the temperature is raised. However, at all practical roaster temperatures (between 500" and 1200°C), the amount of this shift is small, and the equilibrium position remains far to the right. The main roasting reaction is essentially irreversible, and the application of equilibrium considerations to this reaction will not be! a fruitful field of investigation. A knowledge of the rate of this reaction. although not the proper subject of this paper, is of great importance to the roasting process. Analysis of the factors which influence this rate shows that: 1) The rate will increase rapidly with increased temperature. 2) The rate will be proportional to the partial pressure of oxygen at the surface of the reacting particle. Because of diffusion effects, the partial pressure of oxygen at the particle surface may be considerably less than in the bulk of the roaster gas. For this reason, intimate contact between gas and solid and high relative velocity between gas and solid, such as can be obtained in a fluid bed or flash roaster, will markedly increase the rate of reaction. 3) The rate will be proportional to the surface area of metal sulfide. Therefore, smaller particle size will permit a more rapid rate per unit of weight. To achieve practical rates of roasting the partial pressure of oxygen in the roaster gases must be maintained at a finite level at all times. Even where the gas-solid contact is very good, as in the fluid-bed roaster, the oxygen content of the gas must not be allowed to drop below some limiting value (perhaps 1 pct), or the rate of the main roasting reaction will become too small for practical operation. Side Reactions in the Gas Phase The gas phase during roasting of metallic sulfides contains the elements oxygen, sulfur, nitrogen, by-

Jan 1, 1957

Organization Place Date 1918 American Society of Mechanical Engineers...:.. Worcester, Mass. June 4-7 American Institute of Chemical Engineers Berlin, N. H. June 19-22 American Concrete Institute Atlantic City, N. J. June 24-26 American Society for Testing Materials Atlantic City, N. J. June 25 28 American Institute of Electrical Engineers Atlantic City, N. J. June 26-28 New York Electrical Society, Annual Meeting... New York, N. Y. June American Institute of Mining Engineers Colorado Sept. 2-7 National Association of Stationary Engineers.... Cincinnati, 0. Sept. 9-13 British Iron and Steel Institute, Autumn Meeting London, Eng. Sept. 12-13 National Exposition of Chemical Industries New York, N. Y. Sept. 23-28 American Chemical Society Cleveland, 0. Sept. National Petroleum Association.: Atlantic City, N. J. Sept.

Jan 6, 1918

By R. S. French, W. R. Hibbard

FOR tensile deformation, if the stress value is defined by the ratio of the load to the actual area, and the strain value by the natural logarithm of the ratio of the immediate length to the original gauge length of the sample, the resulting data when plotted with logarithmic coordinates result in a linear relation extending from the initial plastic yielding through the maximum load and in some cases, such as for copper and brass, to fracture'.'. The normal form of the curve, therefore, is a parabola, satisfying the following equation: S = Kem [1] where S and e represent true stress and strain, K is a constant, and m is a coefficient evaluating the slope of the curve and designated therefore as the strain hardening coefficient. Hollomon² has reported that this coefficient is a function of the yield strength as effected by grain size in alpha brass, and the carbon content and heat treatment of steel. In the case of steel, the value of the proportionality constant is a function of the carbon content. It was further shown in that paper2 and also by Low and Prater -hat, if the power relation between stress and strain remains valid, the strain hardening coefficient m, is equal to the strain at the maximum or necking load. Thus, an added significant feature is that this coefficient may serve as an index of the capacity for deformation prior to localized necking and subsequent fracture, e.g. drawability. The constant K may be defined as the strength of the material at unit strain. Together the K constant and the m coefficient describe an alloy's physical properties as far as strength and ductility are concerned for a particular yield strength and, in the case of steel, a particular carbon content. The work of Lacy and Gensamer4 gives data on alloy ferrites from which very close estimates of the strength of ternary and higher iron alloys have been made. It was the purpose of this investigation to develop similar data for commercial copper base alpha solid solution alloys. Preparation of Specimens Commercial binary alloys of copper with aluminum, beryllium, cadmium, nickel, silicon, tin and zinc were investigated. In addition, laboratory castings were made of a 1 pct silicon alloy and a 2 pct aluminum alloy to complete these particular series. Two types of copper were used, oxygen free OFHC and tough pitch FC. The analyses of these alloys are shown in table I. Standard ASTM sheet tensile specimens were used to determine the usual physical properties of each alloy and to obtain stress data at strains from 0.0005 to 0.01. Small (1/4 in. x 3 in. x tk.) samples

Jan 1, 1951

By George A. Laird

I. INTRODUCTION. THIS old and once famous district played, through its enormous production of silver and gold, an important part in the history of the State of San Luis Potosi. According to a pamphlet prepared under the direction of the Governor of the State, Sr. Don Blas Escontria, and presented to the visiting members of the Institute during the Mexican meeting of 1901, this district is situated 20 km. east of the city of San Luis Potosi, in a range of mountains of moderate height, extending 135 km. N. and S., and 16 km. E. and W.; and the mineralized area hitherto developed is about 600,000 sq. m. The history of the district,. as given by the record dated 1778, and formerly kept in the San Francisco convent, says that it was discovered in 1575 by Sr. Don Pedro Irarte, and adds that the city of San Luis Rey de Francisco del Potosi received its name (in allusion to the famous Potosi mines in Bolivia) by reason of the remarkable productiveness of its gold- and silver-mines in the first period of their exploration, during which they paid to the Crown, as " quintos " (the fifth part of the product), $97,000,000, as appears from the accounts of the royal treasury. The amount of the quientos paid during the " bonanza period " of 80 years was $72,000,000. The larger sum first mentioned probably represents a longer series of years. But either will suffice to indicate the great wealth of the mines. In 1663, the decadence of the industry began with the caving¬ in of several mines, concerning which the record of 1778, al¬ready cited, says, in substance, that on Good Friday one of the owners in the enterprise, in view of the unfavorable prospect of a lawsuit in which he was engaged, set fire to the timbers supporting the underground galleries and workings of the San

Jan 1, 1905

By E. T. Turkdogan

Jan 1, 1962

By C. H. Mathewson

MY treatment of the subject of "Metals of the Future" is imaginative rather than statistical or scientific, because reliable information concerning useful concentrations in the form of ore deposits of by far the majority of the elements does not exist and the chemical, physical, and mechanical properties of the unfamiliar metals are recorded only in fragmentary and uncertain form or not at all.

Jan 1, 1944

By C. C. Miller, A. R. Belyea, C. H. Herty, E. B. Burkart

The removal of sulfur from steel has been studied by many investigators, but the quantitative relationships between the factors involved have not been determined. This is undoubtedly due to the number of variables encountered in practice, an attempt to study any one reaction or relation being affected by other reactions the relative importance of which cannot be estimated. The factors that affect the extent of removal of sulfur in the basic open-hearth process are generally considered to be: 1. Basicity of the slag: (a) Iron oxides in the slag; (b) carbon in the metal or carbide in the slag; (c) temperature. These factors affect the reactions: FeS + CaO = CaS + FeO FeS + CaO + C = CaS + CO + Fe. 2. Amount of sulfur in the gas. 3. Amount of manganese in the metal. The factors which affect the rate of removal of sulfur include, in addition to these: 4. Fluidity of the slag: (a) Normal changes in fluidity with temperature; (b) changes in fluidity because of the addition of special reagents such as fluorspar. 5. Agitation of the bath. Within the past two years, two papers have been presented dealing with the influence of sulfur in the gas on slag and metal. Nead' has shown that if a gas high in sulfur be used for heating, the metal and slag will absorb sulfur. Whitely2 concluded from his experiments that if a

Jan 1, 1925

By E. H. Herron, J. H. Perry

Mathematical simulation of reservoir behavior may be used to help understand reservoir processes and to predict reservoir behavior, thereby leading to the most economically desirable form of exploitation. In addition, simulation can be used as a tool for reservoir description to learn more about the physical nature of the reservoir and the mode of primary recovery. This use is essential in most reservoir studies and represents one of the more significant applications of simulation. Prediction of reservoir behavior provides information concerning displacement efficiency, optimum well locations, and the comparison of alternative producing processes. Since oil, water and gas all commonly occur in many reservoirs, a simulation that takes into account the simultaneous flow of three immiscible phases is a prerequisite for obtaining such information. Furthermore, a simulation that describes this flow in two dimensions provides the capability of evaluating combination gas- and water-drive reservoirs with either an areal or a cross-sectional description. Many reservoir problems require such a simulation. The objective of the research described here was to develop a mathematical model and associated computer program for accurate, efficient, and economical prediction of the reservoir flow of three phases in two-dimensional geometry. Several authors have discussed multidimensional reservoir simulation of two phases.l-3 Gottfried et al.' presented an analy- sis of three-phase simulation in one dimension. Fagin and Stewart" and Garrett6 have discussed the simulation of three-phase flow in two dimensions, but their solution techniques were different from the method discussed in this paper. In particular, previous models and computer programs have usually involved either fewer capabilities or inefficient and less rigorous descriptions resulting in limited applicability. In the following sections, we present a description of the model, an evaluation of the method, and the application to reservoir problems. Additional and supporting material is presented in the Appendix. The Three-Phase Model General Description The three-phase model consists of the mathematical description of the flow of oil, water and gas in a reservoir. Conceptually this description considers flow in all three space dimensions, but in the subject simulator it is assumed that no flow occurs in the third dimension. The model includes the effects on reservoir behavior of fluid and rock compressibility, viscosity, gravity, capillary pressure, relative permeability and gas solubility. Within the two-dimensional restriction, the reservoir considered may be completely heterogeneous and anisotropic. The differential equations governing multiphase, multidimensional flow in a reservoir are too complex to be solved analytically, so they are approximated by a system of finite difference equations and solved

Jan 1, 1970

By C. S. Samis, D. P. Seraphim

In the presence of oxygen, galena is oxidized in an aqueous medium containing ammonium acetate in accordance with the following reaction: PbS + 1/2 0, + 2 NH~Ac -» PbAc, + So + 2 NH: + H2O. This reaction was studied in an autoclave under oxygen pressure by polarographic measurement of the concentration of lead ion in solution. Oxidation rate is parabolic. The reaction products are lead acetote and elemental sulfur, the latter forming a film on the galena crystal. Reaction kinetics appear to be determined by the diffusion of lead from the galena phase to the solution interface through the film of sulfur. RECENT applications of pressure leaching on a commercial scale have emphasized the metallurgical importance of the oxidation of sulfide minerals in aqueous media by oxygen under pressure. Research experience has shown that sulfates, thio-nates, and metal oxides are the products of humid oxidation of sulfide minerals in basic solutions. The metal oxides may be solubilized in the presence of a complexing ion.' Certain oxide minerals are also amenable to treatment by this type of oxidation.' Several kinetic studies have been made of reactions of this type. Stenhouse' found that pyrite (FeS?) oxidized in a sodium hydroxide solution to produce a soluble sulfate and an insoluble layer of iron oxide and that the kinetics of the reaction were controlled by oxygen diffusion through the oxide layer. Andersen' studied the oxidation of galena (PbS) in a sodium hydroxide solution under oxygen pressure. He found the lead and sulfur to be simultaneously oxidized to produce plum bite ions and sulfate ions, and that the reaction rate was proportional to the surface area of the galena. The kinetics appeared to be determined by the reaction of oxygen and water with the galena surface. In each of the above reactions the metal and sulfur components of the mineral were oxidized simultaneously and at equal rates. In the present study the alkaline medium has been replaced by an approximately neutral solution of ammonium acetate in which lead sulfate is soluble. Under the conditions no sulfate was produced and no sulfur could be detected in the solution. The metal component of the mineral was solubilized and the liberated sulfur remained as a film of elemental sulfur on the surface of the galena crystal. A kinetic study of this reaction was undertaken to establish the kinetic mechanism and to determine the rate controlling step. Specific reaction rates were determined by oxidizing crystals of galena of measured surface areas in an autoclave maintained at the desired temperature and oxygen pressure. The rate of reaction was followed by measuring the concentration of lead in the ammonium acetate solution with a cathode ray polarograph, employing stationary platinum electrodes incorporated in the autoclave. Experimental Materials and Equipment Crystals of galena obtained from Violamac Mines, Retallack, B. C., were selected for oxidation because

Jan 1, 1957

By R. F. Shurtz

The problem of estimating the precision of systematic samples from a mineral deposit is attacked by interpolating the quality, or other attribute measured, by using Fourier approximation. Such approximation using trigonometric functions yields a particularly simple expression for the variance of the mean value of the attribute sampled. The increasing volume of publication in which the science of statistics has been applied to the problem of predicting the quality of an ore deposit from sets of samples taken from it might lead one to believe that engineering judgment can be replaced by statistics. There is, in fact, an implicit application of the principle of indifference or of "no advance knowledge" which has been discredited in modern statistical theory and practice. These pages will show that it is not always advantageous, efficient, or safe to apply this principle. This problem will be dealt with by using series of orthonormal functions to describe the distribution of the quality of ore in space as contrasted with the more commonly used distribution of quality as a frequency function. Mining engineers are rarely well acquainted with the use of such series or of the functions comprising them. These uses are commonplace in the fields of communication and information theory and it is not surprising that applications taken from these fields should be found appropriate for the analysis of the information contained in a set of samples from an ore deposit. It is hoped that presentation of the following basic, but incomplete, results will generate wider interest in this method and a fuller development of it as well as of the necessary computational techniques. FUNDAMENTAL PREMISES Random variables in the strictest sense are not very common in mine sampling. The sets of samples are almost always taken systematically and are, hence, not subject to all the laws governing random events. Therefore, unless there is indeed random experimental error in the determinations of quality, the treatment of systematic samples of n members as though they were random samples of n members often leads to calculation of confidence limits for the mean quality which are larger than they should be with the result that unnecessary additional sampling is done. The reason for this will emerge in the following discussion leading to Eq. 24 and its generalization. In order to inquire into such questions on a rigorous basis and at the same time avoid arithmetic complications that would obscure the concepts involved, a one dimensional distribution of quality will be assumed. The quality, Q, in suitable units is expressed as a function of the distance, x, along some straight traverse of the deposit. Such a function

Jan 1, 1967

THREE regional meetings are planned for this summer and fall following the spring meeting held under the auspices of the Iron and Steel Committee and the Ohio Section at Cleveland in April and in lieu of a general fall meeting of the Institute. Plans for all of them are maturing rapidly. Excellent programs and. interesting visits to points of local tech¬nical interest are already assured. THE SALT LAKE CITY MEETING This meeting will be under the auspices of the Milling Committee and the Utah Section. It will be one of the features of the joint convention held the week of August 22 to 26 with the Western Division of the American Mining Congress. The Congress will be responsible for the general arrangements and for the program on the first day. The following general committees have been appointed:

Jan 7, 1927

By Myron Read

DURING the past 25 years, mining engineers have seen the development of a multitude of specialized engineering curricula in the mineral industry field. Bachelor degrees are now !ranted in the fields of mineral dressing petroleum engineering, geological engineering, fuel technology, and many others. These fields were all, previously considered to be part of a mining enginieer's work and elementary phases of them were included in mining engineering curricula. Their emergence has left some mining engineers with the fear that nothing will he left for a purely mining engineer to teach, or that mining engineering graduates will be unable to complete in any of these fields with the more specialized students and thus will have neatly restricted employment opportunies. A secondary reaction has been that if students who began to say that the pining engineering curriculum taught everything but mining, since so many of :he subjects that had always been udedAuded in the mining engineering curriculum now were fields in their own right.

Jan 1, 1946

By A. W. Ruff

The seismic wave produced by an explosive is very important in blasting. A true understanding of the wave is only important when considering possible structural damage to buildings located near the blast, but it is also of primary importance when considering rock fragmentation. Because of the importance of the seismic wave to fragmentation, a finda-mental study of the seismic wave and its effect was made at the Cananea Consolidated Copper Co.'s mine at Cananea, Sonora, Mexico. Strain gages were used to measure the strain in the rock when nearby explosive charges were detonated. The variance in the circuit voltage caused by changes in the resistance of the strain gage was measured with an oscilloscope and recorded with a Polaroid camera. CONFINED DRILLHOLE CHARGES To record the seismic wave from a confined drillhole explosive charge, a gage was cemented to the bottom of a 4-in diam drillhole. The horizontal gage hole and nine horizontal charge holes were drilled perpendicular to the center line of the 2-39 drift and 4 ft above the floor. The gage hole was 29 in. deep, and the charge holes were drilled so that each bottomed 1 in. deeper than the gage hole. The gage was installed with its axis horizontal and parallel to the 2-39 drift. The charge holes had the following horizontal distances from the gage: hole 3, 3 ft; hole 4, 4 ft; hole 5, 5 ft; hole 9, 9 ft; hole 10, 10 ft; hole 14, 14 ft; and hole 15, 15 ft. Figs. 1 and 2 show the relationships of the gage and the charge holes. Charges of 80 pct special gelatin, which weighed 50, 100, and 150 g were exploded in the charge holes and the seismic waves were recorded. All charges were stemmed with 200 g of mud and detonated with an electric blasting cap. Fig. 3 shows the recorded seismic waves. The reflected components of the waves were too weak to be objectional on these records. Table I shows the data taken from the wave forms. The approximate average velocity of a wave with a 9-ft travel distance was 12,900 fps. Since different charge weights were used, it was necessary to scale the data. The scaled maximum compress ion-strain data and the scaled maximum tens ion-strain data are shown in Figs. 4 and 5, respectively. Figs. 6 and 7 show the strain-distance data from Figs. 4 and 5 converted to a 1-lb charge. The results showed that the wave consisted of an initial compression pulse followed by a tension pulse. The amplitude of the tension pulse approached the amplitude of the compression pulse as the distance between the gage and the shot increased. The decay rate of the seismic wave is very important in the evaluation of the blasting characteristics of a rock. When high-amplitude stresses are produced, as in rock fragmentation, the rate of decay is much more rapid than when small amplitude stresses are produced. In underground mine blasting, the burdens are usually not greater than 6 ft and the decay is very rapid. The rapid seismic-wave decay rate in the fragmentation range means that in practice, if the minimum weight of powder is used to break a specified burden, only a very

Jan 1, 1961

By L. E. Fish, G. S. Wyman

CHUQUICAMATA open-pit mine is capable of producing a total of 105,000 tons daily. When the sulphide plant is operating to capacity the distribution of this quantity will be approximately 30,000 tons sulphide ore, 30,000 tons oxide ore and 45,000 tons of waste. At that time the combined capacity of the oxide and sulphide plants will be about 540 million lb of copper per year. Twenty one benches have been opened to date and all are still active except the three top ones at the northeastern limit of the pit. These have been pushed back to final slope line. The pit is 8850 ft long, 3540 ft wide and 980 ft deep. Benches are not all developed to a standard height as the large development shovels used in cutting new benches have been of different size and range. At this time new benches 521 ft high are being developed with an' 11-yd shovel. Ore haulage through the greater part of the pit operation has been on down grades to the crushing plant. With the opening of bench F-4 in April 1944 the first adverse-grade ore haul was encountered. Of the total tonnage now being mined, 35 pct comes from the four benches that are below the level of the crushing plant yard. Waste had been dumped on the same or nearly the same level as the bench from which it was removed up to the opening of bench F-4. Waste from this and lower levels is hauled to the level of the crusher, yard where it must cross the flow of ore traffic to reach the only available dumping space to the east of the mine. The average ore haul is 3.13 miles one way shovel to crusher, and the average waste haul from that portion handled by railroad is 3.32 miles one way from shovel to waste dump. Waste that is being removed by truck haulage from the upper part of the -mine is hauled an average of 1 mile. Ore loaded by trucks is hauled 3/4 mile to a car loading ramp and then by rail to the crushing plant. Drilling and Blasting There are two types of development for blasting being used: One for opening new benches and the other for bank shooting. The former consists of 9a in. diam churn-drill holes drilled 11.8 ft center to center in rows 10.2 ft apart with the holes staggered in the rows thus giving an equilateral-triangle pattern of 11.8 ft on a side. After the first block, 492 ft long by 71.5 ft wide, is shot in the pattern described above, the cut is advanced by smaller shots consisting of four rows of holes spaced 23 ft center to center with the rows 23 ft apart. These shots are fired in conjunction with side shots in which the holes are drilled 33 ft center to center and 29.5 ft back from the toe, thus squaring up the bank for subsequent shooting. An average bank shot consists of about 60 holes drilled in two rows parallel to the face, 30 holes to

Jan 1, 1952

By K. J. Gill, P. Chiotti

Thermal, metallographic, and vapor pressure data were obtained to establish the phase diagram for the thorium-zinc system. Four compounds corresponding to the stoichiometric formulas Th2Zn, ThZn2, ThZn4, and Th2Zn17 were observed. The melting points of these compounds under constrained vapor conditions were found to be 1055°, 1105°, 1095°, and 1015°C respectively. Four eutectics exist in this system with the following eutectic temperatures and thorium contents in wt pct: 1040°C, 89 Th; 945°C, 79 Th; 1045°C, 55 Th; and 995°C, 35 Th. The standard free energy, enthalpy, and entropy of formation for the compounds were determined from zinc vapor pressure data. ALTHOUGH the thorium-zinc system has been of technical importance in the commercial production of thorium and more recently of interest to some proposed pyrometallurgical separations processes for reactor fuels or blanket materials no detailed investigation of this system has been made in the past. Some previous work has been reviewed by Hanssen.1 The existence of four compounds, Th2Zn17, ThZn4, ThZn2, and Th2Zn has been established and their crystal structures have been studied by X-ray diffraction techniques.2-4 Smirnov et al.,5 determined the solubility of thorium in zinc and investigated the two-phase region between Th2Zn17 and zinc. They calculated some of the thermodynamic properties for these alloys from emf measurements on the cells Th/ThCl4(fused)/Cl2, C and Th2Zn17(s)+ Zn (l)/ThCl4(fused)/Cl2, C. The possibility of reaction between the anode materials and fused thorium tetrachloride to produce a lower valent thorium salt would have to be resolved in order to evaluate the results obtained. The purpose of the present investigation is to establish the phase diagram for the thorium-zinc system and to determine the standard free energy, enthalpy, and entropy of formation for the compounds formed. MATERIALS AND EXPERIMENTAL PROCEDURES The metals employed in the preparation of alloys were Bunker Hill slab zinc, 99.99 pct pure and Ames Lalboratory thorium. The major impurities in the thorium in parts per million were oxygen—1250, carbon—350, iron—100, nitrogen-75, and silicon—70. The metals in the form of several small massive pieces, total weight about 30 g, were cleaned with acid, washed with water and acetone, and dried just prior to their use for alloy preparation. Tantalum containers were found to be suitable for all the alloys studied and were used throughout this investigation. The metals were sealed inside of small 1-in.-diam tantalum crucibles by welding on preformed tantalum covers. A small thermocouple well made from 1/8-in.-diam tantalum tubing was welded in the bottom of each crucible. These crucibles were enclosed in

Jan 1, 1962

By Gorr W. W., Wyche E. H, R. Smith

The combination of high strength and corrosion resistance of cold-worked 18 Cr, 8 Ni steel has been advantageously utilized for some time, particularly in aircraft and rail car structures. There are, however, certain limitations on the use of such materials because the high strengths can be obtained only by cold-working, limiting the available products to sheets, strip, wire and tubes. The authors sought to overcome these limitations by resorting to precipitation-hardening, which has been used so successfully in nonferrous metallurgy but only to a limited extent in iron-base alloys. Accomplishment of this objective not only overcame the limitations, but also effected certain improvements in mechanical and other properties. This paper is an account of the development by Carnegie-Illinois Steel Corporation of a precipitation-hardening 18-8 stainless steel (called Stainless W‡ and tentatively identified as type 322). A description is given of its composition and metallurgical characteristics, heat-treatment, physical and mechanical properties and corrosion resistance. Development of the New Steel For a considerable length of time the authors were unable to determine the mechanism of the precipitation-hardening process that had been noted by Ffield18,19 in 18-8 Ti or 18-8 Cb after cold-working and reheating to moderately elevated temperatures. All known variables were exhaustively studied, but with little success. However, results began to indicate that chemical composition was the most important variable, particularly the ratio of austenite-forming to ferrite-forming elements. The investigators then focused their attention upon the composition, and, in particular, upon the element titanium and its mode of alloying in the presence of other elements. A heat was obtained that could not be brought to the softness level of annealed 18-8. The response to cold-straining and aging* was very marked by previous standards, and, more important, cold-straining was found to be entirely unnecessary to produce the precipitation-hardening effect. The chemical composition of this heat was: C, 0.06 per cent; Mn, 0.54; P, 0.016; S, 0.016; Si, 0.58; Ni, 7.28; Cr, 17.60; Ti, 0.90; Al, 0.17. For some time the development work, particularly on composition, was carried

Jan 1, 1947

By Gorr W. W., R. Smith, Wyche E. H

The combination of high strength and corrosion resistance of cold-worked 18 Cr, 8 Ni steel has been advantageously utilized for some time, particularly in aircraft and rail car structures. There are, however, certain limitations on the use of such materials because the high strengths can be obtained only by cold-working, limiting the available products to sheets, strip, wire and tubes. The authors sought to overcome these limitations by resorting to precipitation-hardening, which has been used so successfully in nonferrous metallurgy but only to a limited extent in iron-base alloys. Accomplishment of this objective not only overcame the limitations, but also effected certain improvements in mechanical and other properties. This paper is an account of the development by Carnegie-Illinois Steel Corporation of a precipitation-hardening 18-8 stainless steel (called Stainless W‡ and tentatively identified as type 322). A description is given of its composition and metallurgical characteristics, heat-treatment, physical and mechanical properties and corrosion resistance. Development of the New Steel For a considerable length of time the authors were unable to determine the mechanism of the precipitation-hardening process that had been noted by Ffield18,19 in 18-8 Ti or 18-8 Cb after cold-working and reheating to moderately elevated temperatures. All known variables were exhaustively studied, but with little success. However, results began to indicate that chemical composition was the most important variable, particularly the ratio of austenite-forming to ferrite-forming elements. The investigators then focused their attention upon the composition, and, in particular, upon the element titanium and its mode of alloying in the presence of other elements. A heat was obtained that could not be brought to the softness level of annealed 18-8. The response to cold-straining and aging* was very marked by previous standards, and, more important, cold-straining was found to be entirely unnecessary to produce the precipitation-hardening effect. The chemical composition of this heat was: C, 0.06 per cent; Mn, 0.54; P, 0.016; S, 0.016; Si, 0.58; Ni, 7.28; Cr, 17.60; Ti, 0.90; Al, 0.17. For some time the development work, particularly on composition, was carried

Jan 1, 1947