Search Documents

By T. S. Plaskett

A striated structure perpendicular to the growth axis was observed by the copper-decoration tech-nique in dislocation-free, .float-zoned silicon crystals. The striations, which were spaced about 100 p apart, fitted the relationship d = f/u , where d is the spacing, f is the growth rate, and u is the crystal rotation rate. Each stria was resolved into an UNDOPED silicon crystals pulled from quartz crucibles by the Czochralski technique usually exhibit a striated structure perpendicular to the growth axis.'-' This structure has been attributed to oxygen segregation, with the oxygen being introduced from the quartz crucible. If the crucible is rotated, the level of oxygen contamination has been reported as high as 10° atoms per cu cm.10 These striations are similar to solute striations commonly observed in doped Czochralski-grown crystals. The periodic nature of the striations is caused by a periodic variation in the growth rate",12 which is attributed mainly to thermal gradients in the melt.13 A finer striated structure14 attributed to constitutional supercooling is sometimes observed between the coarse striae. The oxygen striations have been observed by infrared transmission techniques,' by the copper-decoration technique,' by X-ray diffraction microscopy,6-8 and by 9 p absorption measurements3 on crystals pulled from the melt both with and without dislocations. In this investigation float-zoned dislocation-free crystals were examined by the copper-decoration technique. The level of oxygen for float-zone material is less than 1016 atoms per cu cm the lower limit of detection by 9 p absorption measurement. EXPERIMENTAL TECHNIQUE The crystals were grown by the float-zone process with the rf heating coil outside of the quartz envelope containing the silicon. All float zoning was done under an atmosphere of purified helium. The Dash technique15 was used to grow the crystal dislocation-free. This involves growing the crystal initially with a diameter between 2 and 3 mm and at array of starlike precipitates of copper. The strucLure was not .found at the surface tor a depth of about 1.5 mm, or in a region of similar width ahead of a dislocation network. The structure is postulated to consist of vacancy clusterings or dislocation loops. very rapid rates, about 20 mm per min, for a distance of about 3 cm. The diameter of the crystal is then increased to the diameter of the source of silicon, which in this case was about 19 mm. Because of the arrangement of the apparatus, the zone was passed downward rather than upward, contrary to the standard float-zoning practice. Also, the source was rotated rather than the seed. ziegler17 has made dislocation-free crystals by a similar technique but has passed the zone upwards. The starting material was zone-refined and had a p-type resistivity of 150 ohm-cm. The major impurity was boron; the total impurity excluding the boron was reported by the supplier (Dow-Corning) to be typically less than 2 x 1013 atoms per cu cm. The crystals were examined by the Dash copper-decoration technique18'19—a method in which about 10" atoms per cu cm of copper are diffused at a temperature between 900" and 1000°C into silicon which is then quenched to room temperature. On quenching, the copper precipitates on crystalline defects which are then visible when viewed by transmission infrared microscopy. The photomicrographs shown were taken either of the infrared image tube screen or directly on infrared film. All sections prior to decorating were chemically polished and, for some sections, given a sirtlZ0 dislocation etch-pit examination. After decorating, the samples were mechanically polished. RESULTS A photomicrograph, taken in transmission of a decorated cross section, is shown in Fig. 1. The portion of the section shown is near the surface of the crystal. The entire cross section showed no dislocation etch pits after being given a Sirtl etch treatment. It is seen that the copper precipitated randomly. Each precipitate, as has been reported by others, was found to have a starlike structure.

Jan 1, 1965

By N. J. Grant, R. Nordheim

An extensive study was made of the aging characteristics of alloys based on the 80 pct Ni-20 pct Cr composition hardened with aluminum and/or titanium, each up to 4 pct. Aging was followed by means of hardness and hot electrical resistance measurements as well as by X-ray and microscopy. Stress rupture tests at 1500°F were utilized as a check on the predicted behavior. THE titanium and aluminum hardened Ni-Cr alloys, exemplified by Nimonic 80 and Inconel X, constitute one of the more important groups of alloys developed to meet the demand for materials retaining their strength at elevated temperatures. For service in the temperature range 1200" to 1500°F, these alloys offer high creep resistance. With increasing service temperature, however, the strength of the simpler Ni-Cr base alloys falls off rapidly so that above 1500°F there is a significant loss of strength. The present investigation was undertaken with the hope that a better understanding of the factors controlling the precipitation hardening of these alloys would make it possible to increase the useful service temperature range. Primarily this investigation involved the study of the effects of titanium and aluminum on the hardening and the subsequent softening at elevated temperatures. The titanium and aluminum contents were each varied between 0 and 4 pct by weight at a constant nickel to chromium weight ratio of about 4:1. (Except when otherwise stated, all compositions are expressed on a weight basis.) The major part of the investigation was confined to alloys with less than 0.06 pct C. Recently several papers dealing with the identity of the microconstituents in the titanium and aluminum hardened Ni-Cr alloys have been published. Using X-ray analysis of the residues from anodic dissolution, Rosenbauml was only able to identify carbides and nitrides in Nimonic 80 and Inconel X. However, since Rosenbaum worked with alloys in the hot rolled rather than in the aged condition, his results are inconclusive. Recently Hignett' reported that the hardening of Nimonic 80 was due to the controlled precipitation of Ni,(TiAl) having the cubic Ni3A1 structure. Taylor and Floydv-" published the results of an investigation of the nickel-rich corner of the Ni-Cr-Ti, Ni-Cr-Al, and Ni-Ti-A1 systems. In the Ni-Ti and the Ni-A1 systems the hexagonal Ni,Ti phase, 7, and the cubic Ni3A1 phase, -y', respectively, exist in equilibrium with the nickel-rich solid solution. The interatomic distances in the basal plane of Ni,Ti and the octahedral planes of the matrix are almost equal, thus explaining the Wid-manstaetten type structure formed when Ni,Ti precipitates from solid solution. When Ni:,Al precipitates from solid solution, it appears usually in globular form, often dispersed along rows corresponding to definite crystallographic directions. The 7 and phases are also the only intermetallic compounds which occur in the nickel ternary alloys with up to 25 pct Cr and 10 pct Ti or Al. Taylor and Floyd found that Ni,Ti takes practically no nickel, chromium, or aluminum into solution. Nial, on the other hand, dissolves a considerable amount of chromium and titanium and some nickel. Up to three out of every five aluminum atoms could be replaced by titanium in Ni,Al. This substitution caused a slight increase (less than 1 pct) in the lattice parameter. With respect to the effect of variation in the titanium and aluminum contents on the high temperature strength of Nimonic 80 type alloys, Pfeil, Allen, and Conway" reported that an 80 pct Ni-20 pct Cr alloy containing 0.20 to 0.30 pct A1 had the highest creep resistance when the titanium content was kept between 1.65 and 2.75 pct. Experimental Procedure The materials used for this investigation were electrolytic nickel, electrolytic or low carbon chromium, sponge titanium and 2s aluminum. The alloys were melted in an indirect carbon arc furnace under

Jan 1, 1955

Discussion of the paper of DR. L. EDELEANU, presented at the Pittsburgh meeting, October, 1914, and printed in Bulletin No. 93, September, 1914, pp. 2313 to 2332. F. W. BUSHONG,* Pittsburgh, Pa.-This process of extraction is particularly advantageous in the case of Roumanian oil, on account of its high aromatic content. I have prepared a paper, which will appear probably next month in the Journal of Industrial and Engineering Chemistry, describing a series of two-degree fractions of oil from the Nowata field in Oklahoma. I have made extractions with liquid sulphur dioxide in accordance with Dr. Edeleanu's method, and found that the Oklahoma oils, for instance the kerosene fractions, are purified in this way, although the quantity taken out does not at all compare with that taken out of the Roumanian oil. I have made careful analyses of separate fractions, before and after extraction, and they show a very distinct fractional separation-. I like the distinction, brought out by Dr. Day in previous discussions, in regard to oils, rather than oil, and his beautiful illustration of fractionation. Just as fuller's earth, and other clays, will enable us to obtain lower-boiling fractional portions of the oils, and eventually retain a residuum which is hard to get rid of, or to remove, so there is an advantage to be gained by the use of a reagent which begins at the other end by taking out these last constituents first, namely, ozone. I have also analyzed the ozonides and they are derivatives of hydrocarbons very much poorer. in hydrogen than we have heretofore supposed. Similar results have been obtained with Roumanian, Russian, and Italian petroleums. Furthermore, I have prepared ozonides from a fraction of Oklahoma oils, both before and after ex-' traction with liquid sulphur dioxide, and found that the ozonide obtained from the extract is the same as that precipitated out of the original oils. In other words, the residual substance, which the fuller's earth retains, is the one first thrown down by the use of ozone, but it may also be extracted by liquid sulphur dioxide- and be thus separated in apparently unaltered condition. The analysis of this extract corresponds to the formula C15H20, which is surprising, since it is lower in hydrogen content than we have been in the habit of considering among the constituents of our oils. The extract was probably contaminated with other hydro-carbons, but I think it is unquestionable that we must look for hydro-carbons in petroleum which correspond to a formula at least -as low in hydrogen as C15H2o, and possibly even as low as C15H16.

Jan 4, 1915

By Paul Hunt

UP TO June, 1923, the Park-Utah mine had shipped about 94,000 tons of a direct-smelting ore of a gross value of $4,200,000, or about $45. a ton. These values were in gold and silver only, although the ore carried small amounts of lead, copper and zinc. Freight, treatment and deductions had averaged $15.40 a ton. At the expiration of the Pittman Silver Act there was in sight about 30,000 tons of a similar ore with a gross value of about $15 a ton in gold and silver, and a large body of partly developed lead-zinc ore of a gross value of about $20 a ton, 40 per cent. of which was represented by the lead-zinc content and the balance by the silver and gold. Mine costs had been high during the life of the Pittman Act, but as a large part of the profits had gone into equipment of the mine and the orebodies were large and had good walls, we knew that mine costs could be greatly reduced. We were therefore faced by the necessity of getting lower freight and smelter rates or of concentrating the ore. We did obtain better freight rates on lower grade ore, and a favorable smelting rate on the small tonnage of siliceous silver-gold ore, but this smelter rate could not be applied to the lead-zinc ore with any profit to ourselves. The Judge mill of the Park City Mining & Smelting Co., with which we were affiliated, was running to capacity; if we built our own mill it meant a 5-mile freight haul to a satisfactory millsite and a year's delay. Fortunately, the International Smelting Co. had just inherited a mill at Tooele which, with some changes, was about double the capacity required for its own ores. Flotation tests were run on Park-Utah ore and a contract entered into with a low base treatment charge per ton, the tariff being largely fixed by the metallurgical deductions. This contract has been admirably calculated so that the miner can follow a lean orebody to its limit. Such a procedure has no doubt made it difficult for the smelting company at times, but it has resulted in finding ore extensions that otherwise might have been missed, so in the long run it has profited too. A flat rate per ton would have been like mining up to the claim endlines in a great many of the stopes. In order to offer such a contract it can be inferred that the smelting company must have been able to make high recoveries and high-grade products on a very lean ore.

Jan 1, 1928

By Tracy C. Jarrett

In 14-karat gold alloys, as in 10-karat gold alloys,3 the addition of such metals as zinc, nickel, copper and silver produces a wide range of physical and chemical properties such as color, hardness, corrosion resistance and melting points. These important factors made gold alloys desirable in the optical work and for jewelry. In 14-karat gold alloys, as well as in 10-karat or 12-karat, it is possible to have two golds of the same color, one of which will corrode more than the other, although it may be harder. Some of these alloys have been investigated by F. E. Carter,' E. M. Wise,= and L. Sterner Rainer.4 In this group of alloys the gold content of 58.3 per cent (14-karat) was held constant, while the copper varied from 36 to 24 per cent. The balance of the alloy consisted of one, two, or three of the metals silver, zinc, and nickel. All the alloys were melted in an induction furnace and cast into an ingot that measured 3 by 1/4 by 3/4 in. The method of determining the melting points, color determinations and acid test have been discussed in previous papers by the author.2, 3 It is necessary to use small test bars (Fig. I). The tensile bars were annealed at 1300oF. for 20 min. and then air-cooled. There being a very marked drop when the yield point was reached, "the drop of the beam" method was used in determining the yield point. Alloys Gold-copper.zilzc A~loys.—Gold-copper-zinc alloys melt, cast, and labricate easily. The low melting points, however, limit their use to some extent. The physical properties of these alloys are not entirely satisfactory. When the ultimate strength is satisfactory, the elongation and reduction of area are too low (Table I). Gold-copper-sinr-nickel A lloys.—In this group of alloys, in which zinc and nickel replace copper in approximately equal parts (Table I), the yield point, hardness, and ultimate strength increase with the increase of zinc and nickel content, while the reduction of area and elongation decrease. The physical properties are desirable, particularly of the white gold alloys. The alloys of this group are not difficult to cast and fabricate, and most of these colors could be used commercially. Gold-copper-nickel A lloys.—Gold-copper-nickel alloys are similar to the gold-copper-zinc and the gold-copper-zinc-nickel alloys. They do, however, possess high yield point, ultimate strength and hardness, somewhat higher than those of the other two groups mentioned (Table I). The difficulty with these alloys is that they fire-crack readily and heavy rolling is necessary between annealings. Being hard to fabricate, many

Jan 1, 1941

By Tracy C. Jarrett

In 14-karat gold alloys, as in 10-karat gold alloys,3 the addition of such metals as zinc, nickel, copper and silver produces a wide range of physical and chemical properties such as color, hardness, corrosion resistance and melting points. These important factors made gold alloys desirable in the optical work and for jewelry. In 14-karat gold alloys, as well as in 10-karat or 12-karat, it is possible to have two golds of the same color, one of which will corrode more than the other, although it may be harder. Some of these alloys have been investigated by F. E. Carter,' E. M. Wise,= and L. Sterner Rainer.4 In this group of alloys the gold content of 58.3 per cent (14-karat) was held constant, while the copper varied from 36 to 24 per cent. The balance of the alloy consisted of one, two, or three of the metals silver, zinc, and nickel. All the alloys were melted in an induction furnace and cast into an ingot that measured 3 by 1/4 by 3/4 in. The method of determining the melting points, color determinations and acid test have been discussed in previous papers by the author.2, 3 It is necessary to use small test bars (Fig. I). The tensile bars were annealed at 1300oF. for 20 min. and then air-cooled. There being a very marked drop when the yield point was reached, "the drop of the beam" method was used in determining the yield point. Alloys Gold-copper.zilzc A~loys.—Gold-copper-zinc alloys melt, cast, and labricate easily. The low melting points, however, limit their use to some extent. The physical properties of these alloys are not entirely satisfactory. When the ultimate strength is satisfactory, the elongation and reduction of area are too low (Table I). Gold-copper-sinr-nickel A lloys.—In this group of alloys, in which zinc and nickel replace copper in approximately equal parts (Table I), the yield point, hardness, and ultimate strength increase with the increase of zinc and nickel content, while the reduction of area and elongation decrease. The physical properties are desirable, particularly of the white gold alloys. The alloys of this group are not difficult to cast and fabricate, and most of these colors could be used commercially. Gold-copper-nickel A lloys.—Gold-copper-nickel alloys are similar to the gold-copper-zinc and the gold-copper-zinc-nickel alloys. They do, however, possess high yield point, ultimate strength and hardness, somewhat higher than those of the other two groups mentioned (Table I). The difficulty with these alloys is that they fire-crack readily and heavy rolling is necessary between annealings. Being hard to fabricate, many

Jan 1, 1941

By George Packard

THE shaft of the Raven. mine, at Butte, Mont., is an incline 1,700 ft. in length and dipping at various angles. At the top the dip is 70° from the horizontal, but this is gradually flattened until at the 300-ft. level the inclination is only 47°. This angle continues to the 1,100-ft. level, below which it, curves with a 125-ft. radius to 78°. In addition to these variations in dip, the shaft does not lie in the same vertical plane, with the result that the hoisting rope not only rubs at intervals on both the hanging- and foot-walls, but presses strongly against the west, dividers near the collar, while 300 ft. below it runs close to the east end plates. The early operators used no idlers, and wall plates cut 6 in. deep y the rope resulted. Later operators first attempted to overcome the excessive friction, and the wear of rope and wall plates, by introducing solid cast-iron idlers, 3 in. in diameter. To allow for the travel of the rope from side to side some of these had to be 3 ft. long and were very heavy. Judging from the appearance of the old idlers of this type found at the mine, they often failed to turn in the bearings, which is not surprising when it is considered that they would have to make 1,000 rev.. a minute under ordinary hoisting conditions. The next rolls were made of wood, 6 in. in diameter, with an iron band about each end, and a pintle of 1-in. round steel driven in at the ends to serve as a shaft. These wore rapidly, and were soon replaced by rolls made from water pipe, 5 or 6 in. in diameter, cut to the desired length and fitted with a wooden cylinder into which the pintle was driven. Where the idlers were used on the hanging-wall of the shaft the original bearing was simply a piece of 2 by 1-1 in. strap iron, 10 in. long, turned up at the end in a circle of 18 in. in diameter to receive the shaft. A small hole served for oiling, and common black oil was generally used, although filtered oil from engine bearings and compressor bearings was also used. When the rolls were to be placed on the foot-wall the bearings were made from two pieces of 1 by 3 in. steel, 6 in. long. A half circle was cut on the flat side of each piece and the two half circles together formed a bearing. Oil holes were provided, and in some cases holes were bored through the two pieces so that they could be screwed or spiked to the wall plates.

Jan 8, 1914

By H. L. Washburn, G. L. Judy

DURING recent years thermal drying of fine coal has increased at a tremendous rate, but very little discussion of the several excellent units has found its way into print. This is particularly true for operating and maintenance costs, and the operator who is faced with his first fine coal drying installation must depend chiefly on hearsay when trying to determine what his drying costs will be. This article presents the maintenance and operating costs for the seven drying units now installed in preparation plants of Pittsburgh Consolidation Coal Co. and lists other cost information that should be obtained before any particular drying unit is selected. Plant Description: The fine coal drying section of Plant A consists of four Flash driers operating on two furnaces equipped with spreader stokers. Plant B has one Flash drier operating (together with a screen-type coarse coal drier) on one furnace equipped with a spreader stoker. Plant C has two Cascade-type driers operating on a single furnace with a spreader stoker. Plant Costs: Tables I, 11, and III present the cost of operating these units as reported by the individ- ual plants. As can be seen, the labor rates vary, depending on the amount of overtime paid and the time interval the cost figures cover. There is considerable variation in thermal units used and in the value given to the thermal units at the particular mine. There is some difference in power costs at a given location and, finally, the power costs of conveyors leading to the drying plants were included in some cases. Maintenance supply costs are simply a tabulation of the cost of all supplies used on the driers, furnaces, and stokers. Depreciation is not included, and the tables omit items such as supervision, plant cleanup, oiling, general maintenance, taxes, and insurance. These tables in themselves do not offer a true comparison of costs. This information must be reduced to some common basis. But what is this common basis to be? A mine operator must calculate his overall mine and preparation plant costs in terms of tons of clean coal sold. Unit costs on pieces of equipment within a given plant are correctly calculated on the same basis. However, when unit costs are compared between one plant and another, some thought must be given to unit design. This reasoning is similar to the old argument concerning i solid bowl vs basket-type centrifuges—the units themselves are not directly comparable without their supporting equipment. So it is with thermal driers. Except in rare cases of low entering moisture i content, driers are sized on the basis of water that must be evaporated, while the wear each unit gets de-

Jan 1, 1958

By Charles H. Morgan

THE process of wire drawing depends upon the property which certain metals possess, termed ductility, 'which is defined in Brande's Dictionary of Science as a property in consequence of which metals may be drawn out at length without interrupting the continuity of their constituent parts. As defined by M. Tresca, it is the property of flowing when subjected to pressure, and is termed by him the "flow of solids," in his paper, read before the Academy of Sciences in Paris, November, 1865 * In the simple language of the wire shop, it is that quality in certain metals that permit, them to be drawn (or stretched) out through a tapering, hole in a metal block or die, the die being more dense and harder than the metal to be reduced. It is a fact well known to those skilled in the art, that to succeed in drawing iron or steel wire, it is of the utmost importance to have thorough lubrication, as a lack of it would caws abrasion of the wire, or of the walls of the tapering hole in the die or plate, and quickly put an end to the operation. In drawing coarse or large sizes of wire, say 2/10 inch diameter, the pressure upon the sides of the tapering hole, where the wire comes in contact with the die, is so great that an ordinary lubricant is squeezed out when the usual reductions in size are made, and abrasion takes place. In order to meet this difficulty, and secure proper lubrication, it has been' a common practice for years to apply a paste made of rye or wheaten flour, or lime, to the surface of the wire to be drawn, and when the paste is dry, to smear the wire with tallow or grease; the wire is then ready to be drawn, the dried paste serving to prevent the lubricant from being pressed out in the. process. Some years since, when Bessemer metal came largely into use as material for wire, "the writer found that its drawing required so much more power than iron wire, that he was led to institute a series of trials to ascertain the difference in power required. It was found that Bessemer wire required from 100 to 200 per cent. more power to make the same reduction in sizes than soft iron wire, the difference depending upon the amount of carbon and other chemical constitu- * Interesting experiments in the flow of metals have been made, by Messrs. Hoopes Townsend, of Philadelphia, in cold-punching iron, published and illustrated in the Journal of the Franklin Institute, of March, 1878, by Mr. David Townsend.

Jan 1, 1881

By R. W. Gurry

THERMODYNAMIC calculations indicate that boron is a better deoxidizer than silicon but probably is not quite as effective as aluminum. Boron should, therefore, be readily oxidized out of the open-hearth bath, which implies that it is not recovered in significant concentration from any scrap charged; also that, if added in the ladle, it tends to oxidize out during teeming unless protected by the presence of a. better deoxidizing agent. These conclusions do not apply to liquid cast iron, in which the oxygen content is much lower than in liquid steel. The possibility of conserving certain strategic alloying elements widely used in steelmaking, notably manganeie, chromium and molybdenum, by the use of boron, which in small concentration appears to be extraordinarily effective in promoting hardenability, raises a question as to what extent any boron present in the scrap charged into the open hearth is oxidized out during melting and subsequent refining. This question is significant because the optimum concentration of boron in the finished steel, which is fairly critical, would be very difficult to attain if the boron in the charge were largely retained in the metal. Moreover, unless boron is substantially eliminated in the open-hearth process its use on a large scale would eventually make it impossible to produce boron-free steel except by restricting the charge to virgin material. There is at present, unfortunately, virtually no satisfactory direct evidence to provide an answer to this question; but there are indications from practice that boron is oxidized out in the open hearth in the production of medium or low-carbon steel, although it may be retained if the carbon content remains fairly high; that is, if the oxygen is kept fairly low. In the absence of direct data, it is necessary to rely upon the indications of indirect evidence, the best approach now available being a thermodynamic calculation of the deoxidizing power of boron in liquid steel by the general method used so successfully by Chipman1 in his study of the reactions in the open-hearth process. The thermal data for boron, upon which such a calculation must be based, are reasonably satisfactory; the only quantities not directly determined are the entropy of melting of boron, the activity coefficient of boron in liquid steel, and the activity coefficient of B203 in an open-hearth slag; but these values may be estimated with ample accuracy. The results of this calculation, which is presented later, are given in Table I, together with corresponding data for other deoxidizing elements. This table shows the calculated residual content of oxygen in equilibrium with different residual concentrations of the deoxidizer in the metal;

Jan 1, 1943

By Walter Crafts, C. M. Offenhauer

In a previous study of the carbide phase of chromium steels, it was shown that chromium carbide (Cr7C3) is 2 more stable carbide than cementite (Fe3C) at tempering temperatures above about 500°C. in quenched steels containing from about I to 7.5 per cent chromium. Below this temperature the carbide phase was found to consist of cementite in all of the steels examined. In the present investigation it was found that a similar change in the carbide phase takes place in molybdenum and in chromium-molybdenum steels at approximately the same tempering temperatures. The approximate ranges of occurrence of the alloy carbides Cr7C3, Cr4C, and Mo2C have been determined in steels containing up to 5 per cent chromium, I per cent molybdenum and 0.60 per cent carbon. The experimental steels were made in small high-frequency furnaces from Armco ingot iron, low-carbon ferrochromium and calcium molybdate and were poured into 2-in. ingots, which were forged to I-in. round bars. Sections of the bars were heated to the carbide-solution temperature and cooled rapidly to induce austenite transformation at relatively low temperatures. The steels were subject to some segregation, therefore comparatively high temperatures were necessary to dissolve all of the carbides. The microstructure of the quenched specimens was examined to verify the belief that the carbides had been dissolved, and also to determine the nature of the nonmartensitic structure of incompletely hardened steels. Ferrite and pseudo-martensite were present in some of the specimens, but all specimens were quenched at such a rate that pearlite was not formed, in order to ensure the formation of the carbides at temperatures lower than about 500°C. It had been found previously1 that in chromium steels the chromium carbide could be produced by transformation of austenite in the pearlite range above 500°C., and, in order to start the tempering treatment with the carbide present as cementite, the absence of pearlite was considered to be essential. The specimens were tempered for 64 hr. to permit the formation of the stable carbide. After tempering, the specimens were submitted to microscopic and X-ray examination. The carbides were separated either electrolytically in a 5 per cent HCl electrolyte or with an acidified copper-potassium chloride solution. The crystal structure of the carbide phases was determined by the Debye-Scherrer type of X-ray patterns. The X-ray patterns obtained from specimens near the boundaries between two types of carbides were generally weak and diffuse as compared with the other patterns. For this reason, and because the more soluble components may be masked, the boundaries between the phases could not be determined precisely. However, the X-ray analysis of electrolytically separated carbides has given consistently reproducible results

Jan 1, 1943

By F. C. von der Weid

The mining district of Sao Fidelis, in the northern part of the State of Rio de Janeiro, is situated on the Paraiba River, where it crosses the Serra do Mar (Mountain of the Sea), in the center of a mountainous country having numerous graphitic outcrops. For a long time, these outcrops were irregularly explored by local people, who had little means and no technical advice. A few years ago, the Cia. Brasileira de Minerasgo de Grafite took over the control of some of the more important outcrops and entrusted to me the task of studying the ores and establishing a flowsheet for a pilot plant to be situated in São Fidelis—the ore to be concentrated being mostly of a very high grade. Mineralization and Ores The rocks of the district are mostly gneiss and crystalline schists, with occasional interstratification of dolomitic limestone belonging to the Archean Brazilian Fundamental Complex. The general direction of the beds is roughly between 60" and 80°E., with variable dip, generally nearly vertical. Mostly, direction and dip of the graphitic outcrops is concordant with the embanking gneisses or schists. These outcrops seem to be aligned in two or three parallel zones (Pádua, São Fidelis, Mac- abu), the Sao Fidelis zone being the best known and the most important to date. Two outcrops of the São Fidelis zone, Saudade and Sao Benedito, are now being exploited. Mining has been carried out, so far, on a small scale. The mineralization consists of a vein of nearly massive graphite in a very compact, partially granitized gneiss, with vertical dip. The vein is most irregular, with nests and lenses irregularly distributed along the fracture plane. The ore consists chiefly (particularly in Sao Benedito) of massive graphite appearing and disappearing along the main direction of the vein, forming a succession of irregular lenses in a sort of rosary design. The average width is more or less one foot, with variations from zero to 6 feet. The lode minerals are quartz, a little feldspar and garnet (the latter having its origin perhaps in the embedding gneisses), with rare ferruginous clays on the outcrops. In Saudade a little pyrite, pyrrhotite and chalcopyrite is found occasionally, as well as a carbonaceous mineral, very light, black and shiny, with conchoidal fracture, looking like a sort of jet. The composition of this mineral has not yet been established, but it seems to be very complex. The mineralization seems to be hydro-thermal at a rather low temperature, perhaps mesothermal. The paragenesis, according to samples from Saudade, seems to be as follows, the earlier minerals being listed first: pyrrhotite, pyrite, chalcopyrite, with quartz concomitant to the three and graphite formed later. Age of the mineralization is still uncertain, owing to the very in-

Jan 1, 1948

By E. H. Rose

THE question is often pondered whether the flotation process is still an art or has become a science. The fact is that flotation is a science in so many variables that only art can blend them. It is demonstrable that no less than one hundred variables are involved in any flotation operation, most of them immeasurable on a routine basis. The behavior of every one of them is always governed by orderly and unchanging law, as no man can doubt. There is nothing truly indefinite about that behavior; the only indefiniteness is in our knowledge of it, either in general or from hour to hour in the circuit. In dealing with a simultaneous equation in, say, one hundred variables, all not only affecting the outcome to some degree but many influencing each other as well, it is small wonder that the mineral-dressing profession presents a case history of debate and controversial opinion. The statement of the subject of this symposium-a symposium on flotation machines-seems to delimit and define the matters to be considered and at least the general nature of the conclusions sought. Nevertheless, in such a meeting it is not possible to meditate upon all the variables that do in one way or another affect performance of flotation machines. To attempt it would be much like trying to operate a hundred-ring circus. Perverse variables being what they are, one could expect the elephant in ring 36 to squirt a trunkful of water at the tightrope performer in ring 37 to ruin that artist's act, just as our learning to depress pyrite in the early 1920's ruined the act of the formerly faithful old Callows. HONEST DISAGREEMENTS Selective flotation dates from 1922 or 1923, when several plants established their regular flotation operations on a selective basis. Since then, two decades of efforr have gone into the development of better and better flotation machines. Many have come and gone. The competition has simmered down to perhaps a dozen machines, each one of which is staunchly defended by some operators as being the best for their particular jobs, and as scornfully dismissed by at least a few others elsewhere as being positively the poorest for theirs. These disagreements are honest disagreements, honestly arrived at after plenty of sweat. In many a flotation plant, one machine has been tried out against another under conditions as fair as they could possibly be made. Sometimes the results are on a par but more often one machine shows a consistent and unmistakable margin of superiority over the other. In equally honest and enlightened tests, machine A may win over machine B in one place, and machine B over machine A by as great a margin in another. This paper purposes to identify some of the more prominent reasons why this is so,

Jan 1, 1944

By P. Raffinot, M. Rey, V. Formanek, G. Sitia

Six years of laboratory study, followed by three years of mill operation treating more than 10,000 tons of ore, have established the flotation of oxidized zinc ores with fatty amines as an efficient process. Recently the method has been applied with success to partially oxidized sulphide ores. In this paper the authors give an account of their research and the milling results obtained in Sardinia since 1951. CONCENTRATION of oxidized copper and lead ores by flotation has been practiced for 30 years, but flotation of oxidized zinc ores has remained unsolved until a few years ago. This problem is, however, of great importance in mining districts where large tonnages of oxidized zinc ores exist in underground mines or in dumps. Some sulphide ores also possess a degree of oxidation high enough to justify recovery of oxide zinc minerals. Various attempts have been made to float the zinc carbonate, smithsonite. It is well known' that smithsonite can be collected with fatty acids, but as the predominant gangue constituents, limestone and dolomite. are floatable with the same reagents, fatty acids are difficult to use. Gaudin has shown,' on mixture of pure minerals, that smithsonite can be floated with higher xanthates, or better, with higher mercaptans. Another procedure, briefly mentioned by Davis," consists in sulphidizing the ore, activating the zinc carbonate with copper sulphate, and floating with ordinary xanthates. This process was attempted in the writers' laboratory in 1946, but results were erratic. It has since been taken up by Italian engineers and is in operation on certain types of ores. Two other research projects should be mentioned. In 1942 Erlenmeyer and others' floated synthetic mixtures of smithsonite and gangue minerals with hydroxyquinoline, an analytical reagent for zinc. On the other hand, Bunge, Fine, and Legsdin published in 19465 Some interesting results obtained on Missouri oxidized zinc ores. With sodium oleate as a collector and a combination of sodium hydroxide, sodium silicate, and citric acid as a limestone depressor, they secured, after four cleaning operations, a good grade of concentrate. With many ores this reagent combination lacks adequate selectivity. In 1939 M. Rey initiated a program of research on this important problem. Work was pursued first at the School of Mines in Liége, Belgium"' and later in Paris in the laboratories of Société Miniére et Mbtallurgique de Penarroya and Société Minerais et Métaux. Reagents used in the beginning were higher xanthates and mercaptans, later fatty amines. Sulphidization with sodium sulphide was found necessary. These conditions make possible the flotation of zinc carbonate and zinc silicate. Two milling plants were put in operation in Sardinia in 1950 and several others are now contemplated." ' It should be mentioned that unknown to the present writers McKenna, Lessels, and Peterson were

Jan 1, 1955

By F. C. von der Weid

The mining district of Sao Fidelis, in the northern part of the State of Rio de Janeiro, is situated on the Paraiba River, where it crosses the Serra do Mar (Mountain of the Sea), in the center of a mountainous country having numerous graphitic outcrops. For a long time, these outcrops were irregularly explored by local people, who had little means and no technical advice. A few years ago, the Cia. Brasileira de Minerasgo de Grafite took over the control of some of the more important outcrops and entrusted to me the task of studying the ores and establishing a flowsheet for a pilot plant to be situated in São Fidelis—the ore to be concentrated being mostly of a very high grade. Mineralization and Ores The rocks of the district are mostly gneiss and crystalline schists, with occasional interstratification of dolomitic limestone belonging to the Archean Brazilian Fundamental Complex. The general direction of the beds is roughly between 60" and 80°E., with variable dip, generally nearly vertical. Mostly, direction and dip of the graphitic outcrops is concordant with the embanking gneisses or schists. These outcrops seem to be aligned in two or three parallel zones (Pádua, São Fidelis, Mac- abu), the Sao Fidelis zone being the best known and the most important to date. Two outcrops of the São Fidelis zone, Saudade and Sao Benedito, are now being exploited. Mining has been carried out, so far, on a small scale. The mineralization consists of a vein of nearly massive graphite in a very compact, partially granitized gneiss, with vertical dip. The vein is most irregular, with nests and lenses irregularly distributed along the fracture plane. The ore consists chiefly (particularly in Sao Benedito) of massive graphite appearing and disappearing along the main direction of the vein, forming a succession of irregular lenses in a sort of rosary design. The average width is more or less one foot, with variations from zero to 6 feet. The lode minerals are quartz, a little feldspar and garnet (the latter having its origin perhaps in the embedding gneisses), with rare ferruginous clays on the outcrops. In Saudade a little pyrite, pyrrhotite and chalcopyrite is found occasionally, as well as a carbonaceous mineral, very light, black and shiny, with conchoidal fracture, looking like a sort of jet. The composition of this mineral has not yet been established, but it seems to be very complex. The mineralization seems to be hydro-thermal at a rather low temperature, perhaps mesothermal. The paragenesis, according to samples from Saudade, seems to be as follows, the earlier minerals being listed first: pyrrhotite, pyrite, chalcopyrite, with quartz concomitant to the three and graphite formed later. Age of the mineralization is still uncertain, owing to the very in-

Jan 1, 1948

By Walter Crafts, C. M. Offenhauer

In a previous study of the carbide phase of chromium steels, it was shown that chromium carbide (Cr7C3) is 2 more stable carbide than cementite (Fe3C) at tempering temperatures above about 500°C. in quenched steels containing from about I to 7.5 per cent chromium. Below this temperature the carbide phase was found to consist of cementite in all of the steels examined. In the present investigation it was found that a similar change in the carbide phase takes place in molybdenum and in chromium-molybdenum steels at approximately the same tempering temperatures. The approximate ranges of occurrence of the alloy carbides Cr7C3, Cr4C, and Mo2C have been determined in steels containing up to 5 per cent chromium, I per cent molybdenum and 0.60 per cent carbon. The experimental steels were made in small high-frequency furnaces from Armco ingot iron, low-carbon ferrochromium and calcium molybdate and were poured into 2-in. ingots, which were forged to I-in. round bars. Sections of the bars were heated to the carbide-solution temperature and cooled rapidly to induce austenite transformation at relatively low temperatures. The steels were subject to some segregation, therefore comparatively high temperatures were necessary to dissolve all of the carbides. The microstructure of the quenched specimens was examined to verify the belief that the carbides had been dissolved, and also to determine the nature of the nonmartensitic structure of incompletely hardened steels. Ferrite and pseudo-martensite were present in some of the specimens, but all specimens were quenched at such a rate that pearlite was not formed, in order to ensure the formation of the carbides at temperatures lower than about 500°C. It had been found previously1 that in chromium steels the chromium carbide could be produced by transformation of austenite in the pearlite range above 500°C., and, in order to start the tempering treatment with the carbide present as cementite, the absence of pearlite was considered to be essential. The specimens were tempered for 64 hr. to permit the formation of the stable carbide. After tempering, the specimens were submitted to microscopic and X-ray examination. The carbides were separated either electrolytically in a 5 per cent HCl electrolyte or with an acidified copper-potassium chloride solution. The crystal structure of the carbide phases was determined by the Debye-Scherrer type of X-ray patterns. The X-ray patterns obtained from specimens near the boundaries between two types of carbides were generally weak and diffuse as compared with the other patterns. For this reason, and because the more soluble components may be masked, the boundaries between the phases could not be determined precisely. However, the X-ray analysis of electrolytically separated carbides has given consistently reproducible results

Jan 1, 1943

By Kenneth C. Vincent, A. M. Gaudin

IN a study1of the action of amyl xanthate on chalcocite in water suspension, it was found that if the xanthate is added in relatively large quantity the xanthate group can be accounted for in three forms: (1) as xanthate ion remaining in water, (2) as benzene-soluble cuprous xanthate on the chalcocite, (3) as a benzene-insoluble coating on the chalcocite. Reduction in the amount of xanthate added leads to disappearance of form 1 then of form 2. With minute quantities of added xanthate, substantially all the reagent is of the "unleachable" kind. Yet this unleachable xanthate can be dissolved by pyridine to form a soluble cuprous xanthate complex, and it is sufficient in effectiveness to make chalcocite flotable even if insufficient in quantity to form a complete monomolecular film on the mineral. In that study it was also found that chalcocite abstracts cuprous xanthate from benzene solution, in what may (or may not) be a case of molecular adsorption. It seemed desirable, therefore, to study further the "unleachable" xanthate on the chalcocite, and particularly to ascertain whether it is formed as a result of the benzene leach or is actually formed during the conditioning of chalcocite in aqueous xanthate solution. A splendid tool to make such studies has recently been perfected; that is, the use of radioactive spies or tracer atoms. With this tool, it was thought possible to answer the problem stated above, but, unfortunately, this did not prove to be true. Answer to the flotation question was clouded by the existence of rapid and selective diffusion of copper atoms in the solid mineral-a phenomenon that was totally unexpected yet remains interesting and perhaps important. METHOD OF RADIOACTIVE SPIES The method of radioactive spies is discussed in many places. Two convenient references are the article by Evans2 and the book by Pollard and Davidson.3 The method was first developed by Von Hevesy and Paneth in 1913, when only natural radioactive isotopes were available. These isotopes are few in number, and so the method remained limited in scope. Recently the synthesis of over 350 active isotopes of all the known stable chemical elements4 has opened widely expanded possibilities for the method. A fundamental tenet of the method is that a radioactive atom and a nonradioactive atom are exactly alike until disintegration of the radioactive atom. Then, by its sudden death, the spy reveals its location. The relative abundance of spies at various locations makes it possible to ascertain the relative abundance of the corresponding nonradioactive atoms at the same times and locations. A second fundamental tenet of the method of radioactive tracers is that the radioactivity lies in the nucleus of the atom: transfer of radioactivity from one

Jan 1, 1944

By Charles A. Bohn

WHEN the need for war work was ended, the late Mrs. Sidney J. Jennings felt that the members of the Woman's Auxiliary, who had worked together so successfully, would profit by having a common permanent aim through scholarship work, financed by annual contributions from the Sections. Under her leadership the Sections responded generously and the educational fund was started. Mrs. Jennings became the first chairman of the executive committee and so remained until her death. It was planned to begin with an award of $500 each year, and to pot aside 25 per cent of all moneys re¬ceived from the Sections to establish an endowed fund. In 1921 the first scholarship of a value of $500 per annum was granted, and an award of the same value has been made regularly every year since. It is called the Subscription Scholarship. The 25 per cent, which is set aside each year and carefully invested, is called the Engineering Education Endowment Fund. Three years ago this fund began to yield around $300 annually and this income has been used each year since to finance a scholarship under that name.

Jan 1, 1937

By W. M. Raynor

LARGE quantities of "midnight oil" have been consumed by researchers in attempting to develop a process to produce cold ductile zirconium at low cost. The tantalizing facts that zirconium is a bright, silvery, tarnish-proof metal and is 2 1/2 times as abundant in the earth's crust as copper, and thirteen times as plentiful as lead have resulted in much speculation on uses, ranging from automobile radiator grills to kitchen sinks. but unfortunately no low-cost process of producing it has so far been found. In the case of zirconium, we cannot say that "virtue is its own reward" for the principal virtues of the metal, namely, corrosion resistance at ordinary temperatures and ability to absorb gases at high temperature, are the very characteristics that defeat all of the usual recovery methods such as sintering, plating, or direct chemical reduction. The only method giving a pure metal sufficiently low in oxides, nitrides, etc. to be truly cold-malleable is the one developed by Van Arkel and DeBoer in 1925. This process involves decomposition of zirconium tetraiodide in contact with a hot filament and pre

Jan 1, 1947

H. 0. Hofman, Boston, Mass. (communication to the Secretary*) :—The experimental demonstration by Professor H. Ries, of the fact that a mixture of clay and finely-ground flux will melt more readily than one in which the flux is less fine and therefore less intimately mixed, is very striking, and will be appreciated especially by those who have to discuss, before classes of students, fusions on a small or a large scale. The statement, that I " rather disputed" the influence of size of flux-particles on the ease with which fire-clay mixtures fused, is an erroneous inference from the paper written by Mr. B. Stoughton and myself in 1898.' We did not undertake to study the influence upon fusibility of the sizes of the particles, either of clay or flux. What we did try to find out was, whether the common practice of finely grinding raw or burnt clay, or a mixture of the two, before testing with Seger cones for resistance to heat and to fluxes, xould give the same results as if the materials were tested just as they were going to be

Jan 1, 1904