By William Mikulas Lars Thomassen, Clair Upthegrove

Little work has been done in the field of the nickel-tin binary system. The complete diagram has been investigated on two occasions, but the results are in very poor agreement. The structure of a compound NiSn and the solubility of tin in nickel have been determined by X-ray methods. Several investigations have been made of the liquidus curve, and the compositions of the eutectics have been determined. A study of the literature, however, shows that there is no satisfactory agreement between the data presented in the various papers. The present investigation was undertaken in an attempt to determine the equilibrium conditions, and to correlate X-ray with metallographic data. The equilibrium diagram was determined by thermal and metallographic means, and the solubility of tin in nickel further investigated with X-rays. Powder diagrams were made of the intermetallic compounds, and three of the structures were partly determined. NO attempt was made to determine the range of homogeneity of the intermetallic compounds. Review of the Literature Vigorouxl prepared alloys of tin and nickel containing 74 and 92 per cent of tin. By treating these alloys with very dilute nitric acid or with sodium hydroxide he was able to separate residues, both of which analyzed 66.7 per cent tin. This corresponds to the compound NiSn and was reported as such. Guillet2 made the first investigation of the complete binary diagram Fig 1) The maximum point of the liquidus is at 43.5 per cent nickel. Several solid solution areas were found, and the compound NiSn was included on the strength of Vigoroux's work. The investigation was

Jan 1, 1937

By Richard McCaffery

CONTENTS PAGE 1. Research on Blast-furnace Slags (A Progress Report). By Richard S. McCaffery 5 2. Determination of Viscosity of Iron Blast-furnace Slags. By Richard S. McCaffery, Clarence H. Lorig, Ira N. Goff, Joseph F. Oesterle and Oscar O. Fritsche 27 3. Effect of Magnesia on Slag Viscosity. By Richard S. McCaffery, Joseph F. Oesterle and Oscar O. Fritsche 55

Jan 1, 1931

By Robert Keeney

THE electric smelting of manganese ore and the production of ferro- manganese did not exist as an industry, in the United States or elsewhere, previous to the outbreak of war in 1914. Ferromanganese had been produced, electrically, during times of high prices by two companies at Niagara Falls and by several European companies, but the production. was spasmodic, and none was electrically produced when ferromanganese sold at from $35 to $40 per ton. Thus the electric smelting of manganese ore must be considered as a development caused by the high prices prevailing during the years 1916, 1917 and 1918, and the necessity of smelting domestic ore in order to fill the ferromanganese requirements of the steel industry of the United States, which increased from 189,088 tons in 1914 to 356,356 tons in 1918. The electric furnace is well adapted to smelting domestic-ore because it can be located in small units near the source of ore supply. In 1918, the ferromanganese production of the United States was 333,027 tons, of which about 7 per cent., or 23,000 tons, was produced in the electric furnace. The electric furnace not only assisted materially in the development of a domestic-ore supply but made a considerable saving of coke, as it requires about 1,4 tons of bituminous or lignite coal per ton of ferromanganese compared with a blast-furnace consumption of 2.9 tons of coke per ton of ferromanganese. Some of the plants in the United States that smelted manganese ore in the electric furnace during the war and in 1920 are listed in Tabled. From early in 1919 to about February, 1920, little ferromanganese was produced in the electric furnace. During this period the price of ferro-manganese (78 to 82 per cent. manganese) was about $100 per ton. During the first half of 1920, several plants resumed operation when the, price of. ferromanganese (76 to 80 per cent. grade) gradually increased to $200 per ton, delivered.

Jan 2, 1921

By T. E. Leonitis, F. N. Rhines

The oxide scale that forms upon magnesium at elevated temperatures is non-protective in the sense that the rate of oxidation is constant and thus does not decrease with the growth of the scale as it does with other common metals. This generality was first stated by Pilling and Bedworth' and has been verified by Suzuki2 and by ScheiL3 Pilling and Bcdworth argued that the nonprotective characteristic could be predicted from the fact that magnesium oxide occupies less space than does the metal from which it springs, wherefore the scale is not expected to cover the metal so completely as to exclude all direct access to the atmosphere. Linear oxidation is thought by Scheil to be common to all cases where the reaction occurs at the oxide-metal interface. According to Suzuki," he product of high-temperature oxidation in the air is MgO contaminated with no more than traces of a nitride. When the metal is allowed to burn freely a fume composed of cubic crystals of Mg04 is given off. Delavaults observed that excrescences form upon liquid magnesium and alloys in thc course of oxidation. Beyond this it is known that the use of atmospheres containing small quantities of sulphur dioxide6 or carbon dioxide serve to retard the oxidation of solid magnesium and that beryllium' and calciums minimize the oxidation of molten magnesium exposed to the air. Many studies have been devoted to the nature and rates of "protective" oxidation, as exemplified by the cases of copper and iron, wherein the rate is characteristically parabolic. The theory of parabolic oxidation is well developed.~ Linear oxidation, on the other hand, has received but little attention and the theories proposed by Pilling and Bedworth and by Schcil have yet to withstand careful examination. There exists no comprehensive survey of the high-temperature oxidation of magnesium (or of any other metal that exhibits linear oxidation) over a broad range of temperature, under a variety of atmospheric conditions and covering a large group of alloys. It has been the purpose of the present investigation to provide such a survey, with the object of gaining a fuller understanding of linear oxidation, especially as applied to magnesium. Experimental Procedure and Results The experimental studies undertaken were of two kinds: (I) measurement of the rate of oxidation as influenced by the 6c

Jan 1, 1946

By H. D. Kynor

By the term mechanical mining is meant that operation, or series of operations, that replace the hand methods of mining. The first undercutting machine to operate in anthracite was placed in the Butler mine of the Hillside Coal and Iron Co., Dec. 23, 1910, by the Sullivan Machinery Co. The first Jackhamer used in the anthracite field was installed at the Wadesville colliery of the Philadelphia & Reading Coal and Iron Co. in Oct., 1912, by the Ingersoll-Rand Co. The first longwall conveyor was installed at the Dodge mines of the Delaware, Lackawanna, & Western Coal Co. in March, 1912. The first mechanical scraper equipment was installed in the Seneca mines of the Lehigh Valley Coal Co. in January, 1914. The amount of anthracite mechanically mined since the first mining machine was installed in 1910" is as follows: Penna. Coal Co. D. L. & W.. ScRanton Temple Hudson YeaR and Hill- Tons Coal Co., Coal Co., Coal Co., Total, side Coal Tons Tons Tons Tons and Iron. Tons 1920................ 372,737b 367,000d 322,892 74,127 371,878 1,508,634 1919................ 950,786 no record 306,616 81,575 319,356 1,658,333 1918................ 917,778 744,966 24,880 44,756 288,781 2,021,161 1917................ 757,940 838,800 5,050 57,279 164,180 1,823,249 1916................ 286,780 860,663 13,960 114,173 101,475 1,377,051 1915................ 428,819 592,169 8,253 1,029,241 1914................ 219,188 153,896 373,084 1913................ 171,505 1912................ 124,267 124,267 1911................ 40,319 40,319 1910................ 1,184 1,184 a A slightly greater production was obtained than here indicated, as the tonnage from individual operations is not shown. b Decrease due to strike conditions in 1920. c Does not include tonnage of D., L., & W. d D., L., & W. decrease in 1920 due to having fewer mining machines in operation. There are about 150 undercutters in use in the anthracite region, 80 mechanical loaders, and 10 longwall conveyors.

Jan 1, 1922

By Oren C. Baptist, Carlon S. Land

Laboratory research has been conducted to evaluute the effect of clay hydration on the permeability to gas of water-sensitive reservoir sands. Samples of a .sandstone containing trace amounts of montmorillonite and a sample of montmorillonite were .studied in the laboratory to detertnine whether swelling or dispersion was the cause of permeability reduction in these samples. Heliuin, containing various amounts of water vapor, was used to hydrate the clay minerals and to determine the gas permeability at various stages of clay hydration. The amount of water adsorbed by the samples using this method is small. The nonwetting-phase permeability at higher water saturations war investigated by saturating the with water and measuring the permeability to humid helium while decreasing the water saturation, Relative-permeability curves obtained from results of these procedures were used to estimate the effect of the swelling of trace amounts of mont/tlorillonite on the permeability of the .samples. Most of the damage to the permeability when reservoir sands containing trace amounts of montmorillonite are exposed to fresh water is due to dispersion and movement of clays. Blockage of pores by the increased volume of expanded montmorillonite is believed to result in permeability damage that is small in comparison to the observed damage to the samples tested. INTRODUCTION Studies have shown that permeability is severely damaged when sands containing only small amounts of montmorillonite are contacted by fresh water.15 When samples of sands containing large amounts of montmorillonite are placed in fresh water in the laboratory, these samples may completely disintegrate, forming an unconsolidated mass of larger volume than that occupied by the dry sample." In this case, it is apparent that the swelling of montmoril-lonite has destroyed the pore structure of the sand. If only a trace of montmorillonite is present in a sand. samples may remain intact when saturated with water, although the permeability to water is a small fraction of the gas permeability of the dry sample. Many workers in the field of water sensitivity have attributed this reduction in permeability to the blocking of pores and reduction of pore size by the increased volume occupied by expanded mont- niorillonite. if the sand contains a detectable amount of montmorill'onite or mixed-layer clay containing rnontmorillonite. Logically3 the smaller amount of montmorillonite present in a sand, the smaller should he the effect of montnlorillonite swelling on permeability; however, the quantity of montmorillonite sufficient to cause severe damage by swelling is not known. Although hundreds of samples have been tested in our laboratory, no correlation has been established between the amount of montmorillonite in samples and the permeability reduction caused by fresh water. To many petroleum engineers, the phrase "clay swelling" is synonymous with "water sensitivity", or "permeability reduction" implying that any formation damage due to the hydration of clays is caused by swelling. Although all clays adsorb water on their surfaces, montmorillonite is the only clay mineral commonly found in reservoir rocks which adsorbs water between intercrystalline layers, resulting in expansion of the clay particle. As montmoril-lonite swells, the first few layers of water adsorbed between platelets are strongly held and well oriented, and the montmorillonite retains its crystalline structure, although expanded. As swelling of sodium montmorillonite continues, the platelets become farther apart and the forces orienting the platelets in the crystalline structure become weaker, resulting in a less orderly orientation of platelets. In an abundance of water, small groups of platelets may become detached from the original monl-rnorillonite particle and may be dispersed throughout the water phase. Because of its swelling properties, sodium montmorillonite is very easily dispersed in water. Particles of other clay minerals. such as illite and kaolinite may also be dispersed in water. causing water sensitivity of sands not containing montmorillonite. The presence of an immobile layer of water adsorbed on the surface of clays has been considered a possible cause of the low permeability to water of dirty sands. Grim states that the thickness of the layer of immobile water held by sodium montrnorillonite is three nlolecular layers or 7.5 A (angstroms), with some orientation of water extending to 100 A. Assuming a very thick, immobile water layer adsorbed on the surface of a pore represented by a capillary tube, the maximum effect of the water layer on permeability can be calculated. Using a pore radius of 10 ' cm and an immobile water layer of 50 A. the calculation shows the permeability to be reduced only 2 per cent. Similar calculations can be used to show that the effect of electro-osmotic counterflow is of the same order of magnitude as that of bound water. The reduction of the permeability to water by either an immobile water layer

Jan 1, 1966

By Gilbert Soler

Producers of alloy steels recognize the importance of chemical composition in relation to the hot-working properties and the typical surface defects found in their product. Each analysis of steel has its own peculiar characteristics. Under conditions of standard mill practice each analysis is susceptible to certain types of defects. Mill practice must be varied to obtain the best combination of surface and internal quality in the product. Chemical composition influences the cast structure and crystallization characteristics of the ingot. It also determines the rate of heating and cooling, the plastic hot-working range, and the phase structure of the steel at various temperatures. as well as the tendency toward scale formation and decarburization. This paper endeavors to emphasize the manner in which chemical composition affects the various properties of steel, and to indicate the relative importance of these factors in relation to the hot-working properties and surface characteristics of killed steel. The influence of chemical composition may be outlined as follows: I. Effect on the cast structure of steel, including: A. State of deoxidation, and type of inclusions. B. Gas content of steel. C. Freezing point and melting point of steel. D. Crystallization characteristics and segregation. 11. Effect on the hot-working properties and surface characteristics of steel, including: A. Plastic hot-working range. B. Phase structures at hot-working temperatures. C. Rate of heating. D. Cooling characteristics. E. Scale formation. F. Surface decarburization. EFferect of Chemical Composition on Cast Structure of Steel State of Deoxidation and Type of Inclu-sions.—The state of deoxidation is limited by the final chemical analysis desired in the finished product, and is controlled primarily by carbon, manganese, silicon, and aluminum, and to a lesser degree by chromium, titanium, vanadium, or other deoxidizing elements. The degree of deoxidation affects the density of the cast structure and broadly classifies the steel as killed, semikilled, or rimming. This in turn manifests itself in surface characteristics. The manner and extent of deoxidation also controls the amount, type, and distribution of nonmetallic inclusions formed. The equilibrium of manganese, silicon and aluminum with the slags and pouring refractories with which the metal comes in contact is important, especially in regard to inclusions of fire-clay origin. Some surface Seams and hot-working difficulties can be traced to nonmetallic inclusions.

Jan 1, 1941

By Gilbert Soler

Producers of alloy steels recognize the importance of chemical composition in relation to the hot-working properties and the typical surface defects found in their product. Each analysis of steel has its own peculiar characteristics. Under conditions of standard mill practice each analysis is susceptible to certain types of defects. Mill practice must be varied to obtain the best combination of surface and internal quality in the product. Chemical composition influences the cast structure and crystallization characteristics of the ingot. It also determines the rate of heating and cooling, the plastic hot-working range, and the phase structure of the steel at various temperatures. as well as the tendency toward scale formation and decarburization. This paper endeavors to emphasize the manner in which chemical composition affects the various properties of steel, and to indicate the relative importance of these factors in relation to the hot-working properties and surface characteristics of killed steel. The influence of chemical composition may be outlined as follows: I. Effect on the cast structure of steel, including: A. State of deoxidation, and type of inclusions. B. Gas content of steel. C. Freezing point and melting point of steel. D. Crystallization characteristics and segregation. 11. Effect on the hot-working properties and surface characteristics of steel, including: A. Plastic hot-working range. B. Phase structures at hot-working temperatures. C. Rate of heating. D. Cooling characteristics. E. Scale formation. F. Surface decarburization. EFferect of Chemical Composition on Cast Structure of Steel State of Deoxidation and Type of Inclu-sions.—The state of deoxidation is limited by the final chemical analysis desired in the finished product, and is controlled primarily by carbon, manganese, silicon, and aluminum, and to a lesser degree by chromium, titanium, vanadium, or other deoxidizing elements. The degree of deoxidation affects the density of the cast structure and broadly classifies the steel as killed, semikilled, or rimming. This in turn manifests itself in surface characteristics. The manner and extent of deoxidation also controls the amount, type, and distribution of nonmetallic inclusions formed. The equilibrium of manganese, silicon and aluminum with the slags and pouring refractories with which the metal comes in contact is important, especially in regard to inclusions of fire-clay origin. Some surface Seams and hot-working difficulties can be traced to nonmetallic inclusions.

Jan 1, 1941

By A. F. Taggart

This paper describes the result of a series of experiments run in the laboratory of the School of Mines, Columbia University, during the winter of 1927-28. It shows that the several operating adjustments of a pneumatic table produce effects in the action of a given coal that may be grouped into two classes, viz.: stroke length, speed and rocker-arm angle, which affect longitudinal travel; air supply and table slope (transverse and longitudinal), which determine transverse travel. The magnitude of the effect of the different adjustments varies. Some of the adjustments affect stratification of the bed, both as respects size and specific gravity of the bed components, as well as direction of travel. Operation of a pneumatic table is fundamentally different from that of a wet table in that the former exerts, through the air supplied, a force on the particles upward away from the deck which is lacking on the wet table while, on the other hand, it lacks the positive control over cross travel that is supplied by the wash and feed water. Apparatus The pneumatic table used is shown in Fig. 1. Deck A is 20 by 12 in. and consists of nainsook supported on slats that register with the riffles. Fig. 2 is a photomicrograph of the nainsook used. It shows that the cotton threads average about 0.13 mm. dia. and the apertures about 0.17 mm. The deck carries 12 riffles consisting of wooden strips, 3/16 in. wide and 1/4 in. high, laid parallel to the feed side of the table. The riffles terminate along a line starting on the feed side at a point 11 in, from the mechanism end and running to the corner formed by the coal side and slate end. Taper starts from a line that runs parallel to their terminal line through the junction of the upper riffle with the mechanism end. The height at the terminal line is about 1/32 in. The deck with its supporting slats is carried on a framework consisting of rails A, sloping end rails B, and adjustable metal strips C, which latter permit variation in transverse slope. This frame is enclosed at the edges by means of heavy canvas, indicated in the sketch by wavy lines, which makes a flexible conduit between the deck and the stationary air chamber,

Jan 1, 1930

Meeting of April 24, 1914.-President Thayer announced the appointment of the Committee on Safety and Sanitation. The Committee on Nominations for officers for 1915 was appointed, as follows: William J. Cox, Chairman; H. Poster Bain, Joseph Daniels, Charles E. Mills, R. V. Norris, E. Gybbon Spilsbury, and Herbert A. Wheeler. The request of twenty residents of Salt Lake City and vicinity for permission to establish the Utah-Nevada Local Section was granted and R. C. Gemmell was appointed Chairman of the Committee on Organization. The following resolution was adopted: Resolved: That under authority of Article V, Section 7, of the Constitution, a special Committee be and hereby is appointed, to consist of the President and six other members of the Institute, to be named by him, Who shall be authorized to appear before the proper authorities at Washington and urge that Mining Engineers be appointed upon the proposed Commission for revision of the Federal Mining Laws. Further Resolved: That the activities of this special Committee be restricted to the authority given in this resolution.

Jan 6, 1914

By Robert R. French

Beneficiation of low-grade nonmetalliferous mineral deposits by electronic color sorting is currently undergoing a period of rapid development. For those deposits in which the specific gravity, strength, soundness, and electric and magnetic properties of the ore and gangue are similar, the possibility of separation by color, reflectivity, or fluorescence offers hope for the utilization of much poorer quality ore than previously thought possible. For those ores in which consistency of color is required or for which a dry process is preferred, the electronic color sorter is particularly adaptable. Tests performed late in 1966 and reported herein are the result of the continued interest in the dry beneficiation of gypsum and the development of higher capacity color sorting machines. The ore used was a discarded fraction that consisted of – 1 ¼ -in, to + 3/8 -in. ore containing 63.1 to 71.4% (average 67.7%) gypsum. This material was contaminated by various amounts of both carbonate rock and shale, but no pretreatment was performed other than screening to closer size limits before electronic color sorting.

Jan 4, 1969

By R. Maddin, R. Pond

THERE have been many recent studies of nonequi-librium alloy structures using specimens which have been formed by rapid solidification.' The general methods for achieving nonequilibrium structure utilize high velocity impingement of a liquid metallic droplet(s) and one or more substrates of relatively high heat conductivity. Specimens formed by current popular techniques are small and have various forms of irregular geometry which severely limit their use for many measurements of physical or mechanical properties. As a result of geometric limitations most research has been restricted to X-ray diffraction, electron microscopy, and to a small degree, electrical resistivity. Recently several attempts in mechanical property evaluation have been reported.2,3 A technique for casting large quantities of regular, rectilinear, continuous metallic fibers has existed for a number of years.4 We have utilized this technique with some slight modifications to produce nonequi- librium alloy structures. The apparatus is composed of a small open tube furnace, a pneumatic cage which raises and lowers a graphite ejection mold, and a

Jan 1, 1970

By Lyall Zickrick

EXPERIMENTS of previous investigations have indicated that calcium-copper alloy, when used as a deoxidizer for molten copper, results in a sound copper casting of good physical and electrical properties. Bradenberg and Wiens1 have obtained successful results in casting sound copper using calcium for deoxidizing. Masing2 has obtained deoxidized copper of high density and high conductivity by use of calcium. Pratt,3 in 1907, patented the use of calcium for the deoxidation and degasification of, copper. Schumacher, Ellis and Eckel 4 in 1929, conducted a series of experiments on deoxidizing copper with calcium. They concluded that so long as there is only a small percentage of residual calcium the mechanical and electrical properties of the copper deoxidized are not impaired; and the deoxidation is thorough. For this investigation, a, copper-calcium alloy high in calcium and 10 variously deoxidized copper ingots were prepared. The investigation concerns itself with the casting properties and structure of these variously deoxidized ingots, their working and annealing characteristics, and the resulting physical and electrical properties of the worked materials.

Jan 1, 1932

By W. J. Houk, F. C. Hull

To clarify interpretations of grain structures and to assist in calculations of spatial grain size distributions, plane distribution curves have been determined for random sections through four regular polyhedrons approximating the shapes of metal grains. The characteristics of the distribution curve for the average metal grain are predicted. IT was realized early in the history of metallurgy that metals are polycrystalline aggregates and that the size and shape of crystals affects the properties of the material. Reaumur1 in 1722 employed the microscope to examine the fractured surfaces of steel and of white and gray cast iron and suggested a polyhedral arrangement of the crystals. The first extensive investigation of the form of crystal grains was carried out by Desch.2 He examined the disintegrated grains from a ß brass sample and noted that the number of faces per grain ranged from eleven to twenty and that the number of edges per face varied from three to eight and the maximum occurred at five. While it has been found practical to examine isolated grains only in exceptional cases, it is always possible to make a plane section through the metal and examine the shape of the grain sections on the plane of polish. Desch2 tried to determine the relation between the form of a polyhedron and that of its plane sections for comparison with distribution curves of numbers of sides per grain section of actual metal samples. The polyhedrons investigated were the rhombic and pentagonal dodecahedrons and the orthic tetrakaidecahedron. However, the frequency distributions of the number of sides of plane intersections were not sufficiently characteristic to decide which polyhedron most closely approximated the average grain in a metal. Determination of Statistical Shape of Grain in Space Scheil3 was interested in the problem of calculating the distribution of grain sizes in space from the easily measured distribution of grain section sizes on the plane of polish. Assuming that the grains were spheres and using the plane distribution curve for a sphere shown in Fig. 1, he employed a successive subtraction method to calculate the spatial distribution. In order to evaluate the accuracy of these calculations, Scheil and Wurst4 determined the actual distribution of grain sizes in space in their sample of ingot iron by polishing off successive layers and following every individual grain in a series of micrographs. From curves of mean radius of intersection of a given grain vs thickness of metal removed in polishing, Scheil and Wurst attempted to derive the statistical shape of a grain in space. Their calculated plane distribution curve for this shape is compared with the distribution curve for a sphere in Fig. 1. A table of values based on this curve was prepared for calculating spatial distributions of grains. The calculated and measured spatial distributions of their sample then agreed much better than when a spherical shape had been assumed. In the present paper, an attempt has been made to learn something about the average metal grain by studying in detail the effect of the shape of regular polyhedrons on the plane distribution of areas and shapes of areas produced by random sections through them. From the data presented below, it can be concluded that the plane distribution curve for the average metal grain differs in three fundamental respects from the curve derived by Scheil and Wurst. Polyhedrons Selected for Study The polyhedrons selected for the statistical study are illustrated in Fig. 2 and consisted of a cube, a figure formed by cutting off the corners of a cube at the midpoints of the original edges, a tetrakaidecahedron, and a pentagonal dodecahedron. The length of edge on any one figure is a constant. For the above models the edge lengths were 3.50, 4.00, 2.00, and 2.08 in., respectively. A cube was selected for one of the polyhedrons because of its simple geometry, because it is a form that by repetition can completely fill space, and because it represents a convenient degree of departure from compactness beyond which the shape of

Jan 1, 1954

By D. G. Oss, S. E. Erickson

An automatic control method for the ferrosilicon heavy media process maintains media density within 0.01 specific gravity points. Continued demands for higher grade, competitive products from the Mesabi Range have resulted in experimental work such as that detailed for one concentrator. Various methods, step by step procedures and instruments used at an iron ore beneficiation plant in the development of an automatic control system are described. Work continues and it is hoped that further applications of control instrumentation can be made in the next operating season. The need for instrumentation and automatic control of the various parameters in the heavy media process of iron ore beneficiation has been apparent for some time. Continued demands for higher grade, competitive products from the Mesabi Range have made it necessary to increase the efficiency of the process in every possible way. In a typical heavy media flow scheme for iron ore beneficiation (Fig. 1) a sized, prepared feed (generally about —1% in. to +% in.) is fed to a heavy media separatory vessel, along with a ferrosilicon slurry. A separation of the feed is made on the basis of specific gravity. Low density particles overflow a tailings discharge weir, while high density ore particles sink to the bottom of the high density pool and are moved away to the concentrate discharge chute. Both products are passed over drainage screens and then are cleaned thoroughly of attached ferrosilicon on wash screens. Float material is generally stockpiled, while the sink product is shipped as a final concentrate. Undersize from the drain screens is returned directly to the circulating media sump. Wash screen undersize is cleaned of contaminating ore particles and slimes by passing through magnetic separators. Provision is also made for splitting a portion of the tailings drain undersize into the cleaning circuit if necessary for control of depth of tailings overflow, or for additional cleaning as required. Cleaned ferrosilicon is stored in a densifier and returned to the Circulating media sump as make-up material. Dilution water is also added to this sump to maintain a desired specific gravity of the circulating media. As in any process, operational intelligence is secured only by keeping records of the process variables. Generally apeaking, plant operators have neither the inclination nor the time to keep complete and detailed records of these variables over the course of their shift. Before instrumentation was added to aid the operator, specific gravity was measured by weighing a given volume of pulp at intervals of from 30 to 60 min. Scale readings were made at the beginning and end of each shift. No records were kept of operating conditions, such as rpm of the separatory ves-sel, media level in the machine, tons per hour of the products, and so forth. These items were recorded only when spot checks were made by the metallurgical staff. CONTlNlJOUS DENSITY RECORDING The first process instrument used, other than the usual ammeter on the drive motor of the separatory vessel, was a nuclear density gauge and its associated circular chart recorder. These instruments were used to indicate and record specific gravity of the circulating media. This was a tremendous aid to the operator in that tie was able to observe and correct the specific gravity at any time. There was also added incentive to make frequent corrections because of the permanent record made by the recorder of the densities. The addition of the nuclear density gauge was influential in securing optimum quality and recovery of the heavy media product. Manual control was improved, and it became possible for a good operator to main control within f.05 specific gravity units. This compares with an unknown quantity, estimated at f0.15 gravity units, when manual measurement and control was used. An example of the improvement in manual control over the course of one season's operations is shown in Fig. 2. Chart A is typical of the records made shortly after the gauge was installed. Needless to say, it was difficult for operators and foremen alike

Jan 1, 1962

By A. M. Gaudin, D. W. Fuerstenau

By streaming potential techniques, the zeta potential of quartz has been measured as a function of the concentration of dodecylammonium salts at different pH values. These experiments indicate that adsorption of dodecylammonium ions takes place as individual aminium ions until a certain critical concentration is reached in the double layer, at which point the adsorbed collector ions begin to associate into patches of ions, called hemimicelles. Because of its effect on the surface potential of quartz, pH controls the adsorption of dodecylummonium ions. The value of cooperating agents and nonionized constituents of flotation systems is discussed. Previous investigation of the role of pH in the flotation of quartz with anionic collectors is here extended to an inquiry of how the cationic collector, dodecylammonium acetate, is adsorbed at the quartz-solution interface. The equilibrium amount of this collector adsorbed by quartz has already been measured as a function of concentration and pH. The weight of prior evidence has suggested that two mechanisms are involved in the adsorption of this collector by quartz, but with existing adsorption measurements alone it is not

Oct 1, 1955

Jan 1, 1957

By S. F. Emmons

In a report upon the geology of Ledville and vicinity, which is till in the hands of the Public Printer, I hare given, at some length, my conclusions as to the genesis of the remarkable silver-lead deposits of that region, and the data, gathered during a long and careful consideration, upon which my views were founded. In the brief abstract of this report, published in 1881, the bare conclusions are given, with but few of the facts upon which they were founded. Since that time, these conclusions have been variously criticized, and it has even beer] assumed that the views I expressed with regard to these deposits were intended as a theory of ore-deposits in general.

Jan 1, 1887

By Henry Turner

THE following notes were taken on a trip through northern Korea in the fall of 1910. We started with about 19 Korean ponies, and as many Koreans, from Shin Anju, on the railway from Seoul to Antung. We passed through the ancient walled city of Anju, and thence up the valley of the Anju river. We then crossed over to the north into the Kalsan drainage, thence over another divide to the Chasung river, and finally reached the old Korean copper-smelting camp of Tong Jom-in all a distance by trail of about 200 miles. The return trip was made with ponies to Mampochin on the Yalu river, and thence down the river in a junk to Antung. The route of travel is shown on the sketch map, Fig. 1.

Jan 4, 1913

By R. E. Hoffman, R. A. Ward

The self-diffusion coefficient in high purity nickel has been measured over the temperature range 870' to 1248°C. The results are described by the relation D = 1.27 exp[—-66,800/RT 1cm2ec-1. The measured activation energy correlates satisfactorily with absolute melting point, heat of fusion, and heat of sublimation. KNOWING the rates of self-diffusion is important in the understanding of many metallurgical reactions. However, in spite of the rather widespread interest in nickel, both commercially and in fundamental investigations, no measurement of the self-diffusion in solid nickel has previously been re- ported." In connection with a program of measuring rates of diffusion in some nickel alloys, self-diffusion in pure nickel has been investigated over a rather wide temperature range by combining a sectioning technique and a surface counting technique.

Jan 1, 1957