By E. O. Bennett

When oil is takcn from a subsurface structure it is generally accompanied by gas. The gas thus produced represents the 1ighter hydrocarbons present in the original petroleurn accurnulation, which arc, insoluble at the reduced pressures created around a well when it is producing. In some cases the gas accompanying the oil may come from a gas-bearing stratum not in immediate contact with the oil. The amount of gas from the formation accompanying each barrel of oil is called the natural gas factor. Energy Causing Well to Flow The force causing the flow of fluid into a well when it is drilled into an oil-bearing structure is the pressure differential between the well bore and the formation. A pressure differential between the formation and the well may be set up in three different ways, as follows: (1) pressure due to gas in solution or in contact with the oil, (2) hydrostatic pressure due to water in contact with the oil (it may be either bottom or edge water); (3) pressure difference due to forcc of gravity. The greatest source of energy for producing oil from most oil fields, and the one over which the greatest control can be exerted, is the poten-tial energy in the gas under pressure in the formation. In any pool there is but a definite amount of gas available. Part of this gas may be in solution and a part in contact with oil. The amount of gas in solution in each bard of oil depends on the pressure and temperature in the formation and the characteristics of the oil. Whether the gas is in solution or in contact with the oil it is necessary to use the energy it, contains as efficiently as possible in order to obtain the greatest ultimate recovery from the pool. Bush1 states: Gas being the most efficient aid in moving the oil, it is important to prevent more of it from escaping than is necessary to remove the maximum amount of oil from the sands. The conservation of this energy is far more important to the producer of oil than his returns from sales of gas to distributing companies. The flowing life of the well is the most profitable period, and keeping the gas-oil ratio low, or keeping the

Jan 1, 1928

By R. P. Carreker

ONE of a series, this report is concerned with the experimental documentation of the deformation behavior of pure metals over a wide range of temperature. Previous reports in the series describe the creep behavior of platinum1 and aluminum2 and the tensile behavior of copper,&apos; silver,& and molybdenum.5 Subsequent reports will describe the creep behavior of copper and silver and the tensile behavior of platinum, thus providing extensive creep and tensile data on four face-centered-cubic metals tested under comparable conditions. Material Two lots of high-purity aluminum were used in this investigation. One lot, designated AC, was obtained direct from the Aluminum Co. of America as high-purity aluminum in notch-bar form. A typical analysis of this type of aluminum is 0.006 pct Si, 0.015 pct Cu, 0.006 pct Fe, and 99.975 pct Al. Lot BS was obtained from J. I. Hoffman of the Bureau of Standards as a portion of the Aluminum A described in his report of the redetermination of the atomic weight of aluminum.6 Lot BS originated with the Aluminum Co. of America also, and was received in the standard notch-bar form. A detailed chemical and spectroscopic analysis of lot BS has been published.6 Principa1 impurities were 0.006 pct Si, 0.003 pct Fe, 0.002 pct Cu, and >99.987 pct Al. Samples were processed identically by room-temperature swaging and drawing to 0.030 in. diam wires from approximately ½ in. diam rods that were machined from the notch-bar pigs. Samples were cut from the cold-drawn wire, placed in a grooved graphite block in groups of thirteen, and annealed in air for 1 hr at each of several temperatures, with the results shown in Table I. The two lots of aluminum responded quite differently to annealing, the behavior of aluminum AC suggesting that its grain growth was controlled by impurities. The recrystallization texture of aluminum of similar purity comparably treated has been reported as predominantly <111> fiber with some <100> fiber present.7 Testing Procedure The testing procedure and method of analyzing the data have been described previously.2,3 Annealed specimens of 5 in. gage length were tested in an Instron tensile testing machine at a constant head motion corresponding to a strain rate of 0.04 min-&apos; at a number of temperatures. Instantaneous tenfold rate changes were employed in some tests to deter-

Jan 1, 1958

By A. D. Mutch

IT has long been known that there are wide variations in the thermo-electric potential of pyrite. In the last few years a study of this variation and other properties of pyrite was carried out at the University of Toronto by F. G. Smith on specimens of pyrite from many loyalities. As a result of these studies the pyrite geothermometer was developed by Professor Smith. The calibration of the pyrite geothermometer is based on the assumption that "crystals of any one electronically conducting mineral species deposited at a high temperature have a more positive thermoelectric potential than crystals deposited at a low temperature, and the thermo-electric potential varies continuously between any given limits of the temperature of deposition." The cause of the variation was postulated to be crystal discontinuities, such as lineage boundaries. As yet this postulated relationship has not been established as fact. On theoretical grounds it is indicated that the thermo-electric potential of pyrite or any other partial conductor is dependent upon a number of factors as well as the temperature of formation. For this and other reasons there is ground for doubt as to the validity of the relationship postulated above. To date a large number of readings have been made with the pyrite geothermometer which have been recorded in terms of the calibration of the instrument in degrees centigrade. So far most of the pyrite tested by this technique has been in association with gold ore. The values for the temperature of formation obtained in these tests appear to be reasonable and, in relation to geological problems, to vary in the right sense. Determinations on some specimens not in association with gold ore have given readings that appear to be much too high, taking into account the probable maximum temperature of the host rock. To sum up, although many determinations made with the pyrite geothermometer appear to give reasonable values for the temperature of formation of the pyrite, there are at the same time other readings which seem anomalous. On the basis of an examination of available results of work with the pyrite geothermometer, two problems must be considered: 1—the validity of the calibration of the pyrite geothermometer; and 2— the nature of the distribution of the thermo-electric potentials of pyrite in relation to the specific problems that have been examined. In this paper the academic problem relating to the validity of the calibration of the pyrite geothermometer will not be discussed. Instead, the variations of thermo-electric potential of pyrite in association with gold veins will be discussed with regard to specific examinations. The first of these two examinations deals with the distribution of thermo-electric potentials of pyrite in association with a gold vein and was carried out in the McIntyre Porcupine Mine, Schumacher, Ont., in the summer of 1949 as part of a study with this technique. The second problem deals with variations of thermo-electric potential of pyrite in gold ore specimens from all over the world. The specimens used in this study were part of the private collection of Frank Ebbutt, geologist for Howe Sound Exploration Co. Results of Detailed and Reconnaissance Studies In discussion of the results of determinations made in these two studies the values of thermo-electric potential in millivolts will be used. It will be noted that in some of the diagrams the determinations are recorded in terms of pyrite geothermometer temperatures. Fig. 1 is a calibration chart relating pyrite geothermometer temperatures and thermoelectric potentials. A full discussion of the technique is given in the original paper by F. G. Smith.&apos; Briefly, the determinations are made by placing two stainless steel probes, one hot and the other cold, against the surface of the pyrite crystal being tested. The thermoelectric potential that is developed is read with a null-point potentiometer that is calibrated in what

Jan 1, 1953

By C. H. Li, J. A. Sarteli, W. Bonfield

The stress to cause a permanent micros train of 2 x 10-6 in. per in. (defined as the microscopic yield stress) in beryllium is found to be very sensitive to surface condition. The initiation of plastic flow in as-machined specimens, which contain a high density of twins and large residual compressive stresses to a depth of about 0.010 in. from the surface, occurs by the nucleation of slip from high stress fields around twin tips in the surface layers. Removal of the damaged surface layers by chemical polishing results in an appreciable increase in the microscopic yield stress, which is attributed to the remoual of stress raising twins rather than to the release of residual stresses. IT is well known that the macroscopic mechanical properties of beryllium are very sensitive to the nature of its surface finish. Matthews and coworkers1 have shown that the tensile strength of rolled beryllium sheet can be considerably enhanced by chemical polishing, presumably due to the removal of the high concentration of notches, twins, and large residual compressive stresses normally found in the surface layers of ground specimens. There was no similar effect of surface condition on the macroscopic yield stress (the stress to produce 0.2 pct strain), a point to which we shall return. To date there have been no extensive studies on the effect of surface condition on the microstrain region of beryllium. Recent measurements2 of the stress to cause a permanent microstrain of the order of 10-6 in. per in. on machined hot pressed QMV beryllium, gave values ranging from about 600 to 3500 psi. Reasons for the considerable scatter in the results were not discussed. In this paper, we wish to show that the microstrain region of polycrystalline beryllium is, in fact, very sensitive to surface condition. The stress to cause a permanent strain of 2 x 10-6 in. per in. which for convenience we will refer to as the microscopic yield stress, can be increased by almost a factor of 2 by minimizing the amount of surface damage. The variation of microscopic yield stress is attributed to the presence of twins in the surface layers, rather than to residual compressive stresses. EXPERIMENTAL PROCEDURE The starting material for this investigation was commercial purity hot pressed QMV beryllium, with an average grain size of about 20 . The effects of surface treatment were assessed by comparing the microstructure with residual stress measurements and microstrain properties. Specimens were prepared for metallographic examination by wet grinding with 240, 400, and 600 papers, followed by polishing with a suspension of fine alumina in warm 20 pct oxalic acid. After this treatment, the surface could be examined, either in the unetched condition with polarized light, or after etching in 2 pct hydrofluoric or boiling 20 pct oxalic acid with normal light. Thin films of beryllium suitable for electron transmission study were prepared from bulk specimens by chemical polishing with hydrofluoric and phosphoric acids, and were examined in an RCA-EMU-3 electron microscope. Residual stress measurements were made by a procedure similar to that of Treuting and Read.3 Specimens 4.0 in. by 0.625 in. by 0.080 in. were prepared by three different machining procedures, namely: turning, grinding, and sawing, in order to introduce different levels of residual stresses. An electrical resistance strain gage was attached to one side of the specimen, and that surface was then protected by an acid-resistant enamel, while the opposite surface was removed by etching approximately one thousandth of an inch at a time. The change in specimen curvature in the longitudinal direction was noted and the residual stress was calculated by the following formula:

Jan 1, 1963

By M. H. Gaskell, D. C. Lindley

Small, steeply inclined reservoirs without natural water drives often are found associated with salt domes or other highly faulted structures. Frequently, only one well may be economically justified in these reservoirs, from which oil is produced by an expanding gas-cap drive or by a dissolved-gas drive. Although a large fraction of the oil upstructure from the well may be recovered during primary depletion, only a small fraction of the downdip oil can be produced because of gravity effects. This downdip oil has been defined as cellar oil991 in contradistinction to "attic oil" which is the oil above the structurally highest well in reservoirs where a natural water drive is present. In this study, two methods of producing cellar oil by water flooding a one-well reservoir were investigated by means of a laboratory model. This model was scaled to represent a prototype reservoir having an area of 30 acres, a permeability of 500 md, and a thickness and dip of 30 ft and 30°, respectively. One method considered, the simultaneous injection of water and production of oil from a single well, would require that the lower portion of the productive interval of a well be completed for water injection and the upper portion for oil production. The other method considered, intermittent injection, would involve alternate injection of water into and production of oil from a single well. Injection of water into the formation would repressure the reservoir, causing gas to go back into solution. Since some of the injected water would flow updip from the well, water injection usually would be followed by a waiting period during which the water could drain from above the wellbore. Production of oil by gravity drainage and gas-cap drive could be initiated when water drainage became sufficiently complete. The amount of water produced along with the oil would naturally depend on how soon after water injection ceased that production was started. This process could be repeated in cycles until oil could no longer be produced economically. Of these two methods, the intermittent injection technique would be simpler to put into operation since it does not require a dual completion. Also, it is probably more generally applicable than the simultaneous injection-production method. It is to be expected that in some reservoirs the rock and fluid properties would be such that practical oil-production rates could not be achieved by the simultaneous technique. However, in reservoirs where the simultaneous method will result in practical rates of oil production, it does have the advantage of permitting immediate, continuous oil production; whereas in the intermittent method, oil production is interrupted by periods of water injection and drainage. It was the objective of this study to determine whether these two methods of cellar oil production are practical for the representative prototype investigated and to evaluate their relative merits. DESIGN OF LABORATORY MODEL SCALING REQUIREMENTS The prototype reservoir and fluids were selected to have the dimensions and physical properties shown in Table 1. The laboratory model was then designed in accordance with well known scaling criteria, as discussed by Croes, et al,2 except for one modification. According to Croes, et al, one requirement of scaling a laboratory model to a reservoir prototype is that both the relative permeabilities and dimensionless capillary pressure be the same functions of water saturation for the model and the prototype. Since unconsolidated sand packs are used in the laboratory model to represent the consolidated porous media of the prototype, it is virtually impossible to satisfy this requirement. Much of the difficulty stems from the fact that unconsolidated sands usually exhibit lower residual oil and connate-water saturations than do reservoir rocks. To satisfy the scaling requirement as nearly as possible, Perkins and Collins&apos; have suggested that the relative permeabilities be re-defined as

By A. D. Mutch

IT has long been known that there are wide variations in the thermo-electric potential of pyrite. In the last few years a study of this variation and other properties of pyrite was carried out at the University of Toronto by F. G. Smith on specimens of pyrite from many loyalities. As a result of these studies the pyrite geothermometer was developed by Professor Smith. The calibration of the pyrite geothermometer is based on the assumption that "crystals of any one electronically conducting mineral species deposited at a high temperature have a more positive thermoelectric potential than crystals deposited at a low temperature, and the thermo-electric potential varies continuously between any given limits of the temperature of deposition." The cause of the variation was postulated to be crystal discontinuities, such as lineage boundaries. As yet this postulated relationship has not been established as fact. On theoretical grounds it is indicated that the thermo-electric potential of pyrite or any other partial conductor is dependent upon a number of factors as well as the temperature of formation. For this and other reasons there is ground for doubt as to the validity of the relationship postulated above. To date a large number of readings have been made with the pyrite geothermometer which have been recorded in terms of the calibration of the instrument in degrees centigrade. So far most of the pyrite tested by this technique has been in association with gold ore. The values for the temperature of formation obtained in these tests appear to be reasonable and, in relation to geological problems, to vary in the right sense. Determinations on some specimens not in association with gold ore have given readings that appear to be much too high, taking into account the probable maximum temperature of the host rock. To sum up, although many determinations made with the pyrite geothermometer appear to give reasonable values for the temperature of formation of the pyrite, there are at the same time other readings which seem anomalous. On the basis of an examination of available results of work with the pyrite geothermometer, two problems must be considered: 1—the validity of the calibration of the pyrite geothermometer; and 2— the nature of the distribution of the thermo-electric potentials of pyrite in relation to the specific problems that have been examined. In this paper the academic problem relating to the validity of the calibration of the pyrite geothermometer will not be discussed. Instead, the variations of thermo-electric potential of pyrite in association with gold veins will be discussed with regard to specific examinations. The first of these two examinations deals with the distribution of thermo-electric potentials of pyrite in association with a gold vein and was carried out in the McIntyre Porcupine Mine, Schumacher, Ont., in the summer of 1949 as part of a study with this technique. The second problem deals with variations of thermo-electric potential of pyrite in gold ore specimens from all over the world. The specimens used in this study were part of the private collection of Frank Ebbutt, geologist for Howe Sound Exploration Co. Results of Detailed and Reconnaissance Studies In discussion of the results of determinations made in these two studies the values of thermo-electric potential in millivolts will be used. It will be noted that in some of the diagrams the determinations are recorded in terms of pyrite geothermometer temperatures. Fig. 1 is a calibration chart relating pyrite geothermometer temperatures and thermoelectric potentials. A full discussion of the technique is given in the original paper by F. G. Smith.&apos; Briefly, the determinations are made by placing two stainless steel probes, one hot and the other cold, against the surface of the pyrite crystal being tested. The thermoelectric potential that is developed is read with a null-point potentiometer that is calibrated in what

Jan 1, 1953

By G. C. Wallick, W. R. Foster, J. G. Savins

A comprehensive review of the salient features of the differentiation method of rheological analysis in Poiseuille flow from its inception circa 1928 is presented. Here no initial assumptions regarding the nature of the function relating rheological parameters to observed kinematical and dynamical parameters are required in the data-analysis process. In contrast, the integration method involves interpreting flow properties in terms of a particular ideal model. It is shown that, although both methods represent modes of solution of the same integral equation, being relatively bias-free, the differentiation method offers a more discriminating procedure for rheological analysis. The application to problems involving plane Poiseuille flow is also described. INTRODUCTION In most instances, the approach to the problem of interpreting the rheological properties of various compositions as they are affected by changes in chemical or physical environment, assaying the characteristics of a particular constituent of a suspension, analyzing flow behavior in terms of interactions between components in a system, to cite but a few examples, has been in terms of what Hersey1 terms the integration method. Briefly, it consists of interpreting flow properties in terms of a particular ideal model. The usual practice of the integration method is to choose a model with a minimum number of parameters because, other things being equal, it is desirable to use the simplest model which will describe the behavior of a real material and yet be mathematically tractable for the requirements of data analysis. This expression is then substituted into an equation which relates observed kinematical and dynamical quantities, such as volume flux Q and pressure gradient ], and angular velocity and torque T, in a capillary and concentric cylinder apparatus, respectively. The rheological parameters appear on integrating, in an expression relating the pairs of observable quantities such as those just given. In many instances a particular model provides a good representation of rheological behavior over a reasonable range of compositional and environmental changes. Just as often, however, it is obvious that the interpretation of rheological changes by the integration method is not providing realistic information about changes in flow behavior. A more general method of interpreting rheological data for a given material is to make no initial assumptions regarding the nature of the function relating rheological parameters to observed kinematical and dynamical quantities, e.g., flow rate and pressure drop in capillary flow or angular velocity and torque in a rotational viscometer. This general method Hersey1 terms the differentia-ation method. Instead of integrating, one differentiates the integral equation with respect to one of the limits, i.e., one of the boundary conditions; the resulting expression contains the same observable quantities just given, their derivatives, and the rheological function evaluated at that boundary. By obtaining these derivatives from experimental data, graphically or by a computer routine, they can be substituted into the differential equation and a graphical form of the function derived. THEORY OF THE DIFFERENTIATION METHOD FOR POISEUILLE-TYPE FLOWS In this introductory paper, two flow cases which are important in viscometry are considered (one for the first time) from the differentiation method of analysis, flow in a cylindrical tube and flow between fixed parallel surfaces of infinite extent, the basic integral equations being formulated in a manner analogous to the way they originally appeared in the literature. In addition, the following ideal conditions will be assumed: (1) an absence of anomalous wall effects, (2) isotropic behavior everywhere, and (3) steady laminar flow conditions. Before proceeding it would seem appropriate to preface the analysis of these flow geometries with the comment that the basic philosophy of the differentiation method could be said to stem directly from the efforts of Herzog and weissenberg2 to indicate systematically the various ways of using

By Goldye Leeds, Marian Balicki

A SURVEY of literature reveals the scarcity of experimental evidence relating to work hardening and reannealing of silver.&apos;-&apos;" With the exception of the well-known X-ray investigation of silver and other metals by W. A. Wood? the effect of progressive cold working has not been studied. The determination of thermal stability of silver in the work-hardened state by means of isochronal or isothermal annealing has been confined apparently to very high reductions only. In the survey made, no study was encountered which endeavored to produce a complete picture of the changes in various properties due to cold working and subsequent reannealing. To fill these gaps and to assemble data that could be used for the determination of activation energies and of frequency coefficients of primary recrystallization, a systematic experimental approach, which was developed by one of the authors, has been applied to pure silver. Material and Processing The silver used was Handy and Harman fine silver, with a spectroscopic analysis at the testing stage of Cu, 0.0001 to 0.001 pct; Te, 0.0001; Pb, Si, Ca, Mg, and Mn, traces. The material was supplied in the form of a rod 0.406 in. diam and was converted into test samples according to the procedure condensed in Table I. It should be mentioned that air annealing was adopted to simulate industrial practice, though it was realized that annealing in a neutral gas or in a vacuum would be preferred. The usual precautions have been taken to eliminate any structural changes and property changes resulting from the storage of the samples prior to annealing or testing. Thus the wires were kept at the fully annealed stage, and the final wire drawing, which produced the desired degree of work hardening, was done just prior to the final annealing or testing. During the short waiting period, the samples were kept in a thermosflask filled with ice. Even with these precautions some strain-age-hardening or self-annealing could occur. To test such a possibility, wires of different reductions were prepared in the manner adopted and portions of them were immediately tested. The remaining portions were similiarly tested after different periods of storage, both at room and melting-ice temperature. Within experimental error, all samples obtained from a wire of a given percentage of reduction yielded identical values. This result qualified the material for further tests and interpretations, because it showed that either strain-age-hardening and self-annealing were absent, or that these effects fully balanced each other. The final annealing was carried out in an electric resistance furnace automatically controlled to within a 10°F. It was realized that the temperature fluctuations were greater than desired for this type of work. TO diminish the errors due to fluctuations of temperature, the hot junction of the thermocouple was placed as close to the samples as possible; the time of soaking was reduced to 15 min; and the number of samples annealed at different temperatures was increased. It will be seen from Table I that some tests were performed on the same material at rising temperature. These will be discussed elsewhere. Room temperature testing was limited to the determination of some of the mechanical properties that are known to be additive in a degree sufficient to be used for indirect study of the kinetics of the reannealing process, Tensile tests, carried out on a manually operated J. Camillon machine, accurate to within permitted the determination of the ultimate stress (U.S.1 and of the 2 in. elongation, (A,). The proof stress (d,e) has been determined from a series of bend tests carried out on a Tinius Olsen Stiffness Tester by using the offset method. This involved accurate determination for each sample of load-angular deflection curves, finding a

Jan 1, 1952

By J. R. Lucas, H. E. Rutherford

The primary objective of this research was to evaluate the feasibility of ultrasonic testing for the purpose of analyzing the structure and properties of rock material. A secondary objective of this study was to determine experimentally the elastic wnstants of various rock specimens with the use of ultrasonic equipment. Elastic constants can definitely be determined quickly and accurately by ultrasonic investigation. With proper equipment there are indications that ultrasonic waves could be utilized in the detection of flaws, such as fractures and planes of weakness, measurement of thickness, and the study of structure of rock material. Ultrasonic principles have been applied in many industries for the purpose of determining the structural characteristics of various materials. The principal applications of interest here are detecting flaws, measuring thicknesses, and determining elastic constants. The main advantage of ultrasonic analysis is that it is nondestructive. It also has extreme sensitivity, high penetrability, good accuracy, rapid response, and the necessity to have access to only one side of the specimen. These various applications and advantages lead one to think that ultrasonic principles might be applied to rock material in situ for purposes of analyzing its structural characteristics. Therefore, the primary objective of this research was to evaluate the feasibility of ultrasonic testing for the purpose of analyzing the structure and properties of rock material. A secondary objective of this research was to determine experimentally the elastic constants of various rock specimens with the use of ultrasonic equipment. The term ultrasonics is given to that branch of acoustics dealing with periodic sounds whose fre- quencies are above the audible range or above approximately 15,.000 to 20,000 cps. The first practical production of this high frequency sound was made possible after World War I due to developments of electronically controlled sound wave sources. At the present, the maximum practically attainable ultrasonic frequency is approximately 1000 megacycles per sec. Sound waves of sufficiently high frequency can be made to travel in a beam with little spreading. Therefore, such a beam can explore a material and detect nonhomogeneities in it by reflection. This is the principle of the ultrasonic reflectoscope invented by F. A. Firestone&apos; in 1942. An ultrasonic beam, on pulse-penetratink a solid material medium, produces an echo when it strikes a flaw which has different acoustical properties than the surrounding medium. This echo can be detected by the same transducer which sends out the original pulse. This principle is the basis of the important industrial techniques of nondestructive ultrasonic testing of metals and other solid material. Later developments in the field of ultrasonic testing of solid material have been mostly improvements in equipment and instrumentation. To date, most of the industrial applications of ultrasonic analysis of solid bodies have been in the aircraft, electrical, and nuclear energy fields on the nondestructive testing of metal. The one solid material similar somewhat to rock material, upon which some work has been done to apply ultrasonic testing techniques to study structural integrity, is concrete. Jones and Gatfield3 briefly summarize this work on concrete. Their basic conclusion was that the strength of concrete was a function of the change of the longitudinal sound wave velocity in the concrete. Only recently has any extensive study been made to apply ultrasonic testing techniques to rock material. Lutsch studied rock material by an ultrasonic pulse method to determine the extent and degree of fracture of rock faces. Lutsch states that the number of observed reflections is a measure of the degree of fracture and that only ultrasonic waves are able to detect fractured zones subjected to high pressure. Suzuki, Sasaki, and Siohara5 studied the characteristics of the sonic wave in rock for propagation over a wide range of wave lengths. They indicated that, in rock, the propagation constant and attenuation of the

Jan 1, 1962

By Euclid P. Worden

In 1977, an article in World Mining1 reported a total of 2726 rotary blasthole drills in service. This figure included only those machines produced by three of the manufacturers building drills of this type. The total, therefore, is much higher. Rotary drilling in the mining industry is big business to the manufacturers and suppliers involved, and a significant cost item to mine operators. The time has come to take a hard look at rotary drilling technology with an eye to reducing costs by increasing drilling efficiency. The efficiency of any rotary drilling operation is best measured in terms of the rate of penetration achieved by the bit. In blast hole drilling, there are five factors which affect the rate of penetration. They are: (1) bit selection, (2) weight on the bit, (3) rotary speed, (4) hole cleaning, and (5) formation properties. Of these factors, all but one may be controlled by the operator. Looking at any one in detail may reveal possible improvements in the system. One of these factors -- proper hole cleaning - will be discussed in this paper. In order for a bit to perform at its maximum capability, each tooth or insert should strike fresh clean rock as it falls into its drilling position. If the tooth or insert lands on previously drilled cuttings, a major portion of the energy delivered to the bit is absorbed in redrilling this broken material. A major portion of the interest, therefore, should be directed to the proper cleaning of the bottom of the hole. In an in-depth study of the cleaning of large diameter holes, Allen2 reports that horizontal air velocities of 38.10 m/s are necessary to prevent the saltation of drilled cuttings on the bottom of the hole. The exact flow pattern on the bottom of the hole, however, is not generally known. The air leaves the bit through the jet nozzles and the mouths of the cones, but where it goes from there is uncertain. This problem should be investigated by the bit manufacturers because they can best utilize the results of such an investigation to provide a more effective product. Some work has been initiated in this area and competition will probably increase its intensity. Bailing velocity is the best criteria to measure the cleaning of the hole, including the bottom, and is the factor on which efforts toward improvement must be concentrated. The first consideration is "What should the bailing velocity really be?" In drilling deep holes for oil and gas, 15.24 m/s is the generally accepted figure. In blasthole drilling, the figures of 25.40 m/s for average rock to 35.56 m/s for iron ore were first mentioned by Capp3 in 1962. The recommendations are the same to this day. A number of questions could be asked in regard to the apparent disparity between these two sets of figures. Various investigators have derived formulas which support one or another of these criteria. A thesis on the subject was written by Alexander4 who derived a formula based on research which resulted in velocities in the lower end of the ranges quoted previously. He set out to compare this figure to laboratory tests and his tests indicated that the velocities given by the derived formula appeared to be high.1 Perhaps the best reason that the 25.40 to 35.56 m/s range has been used, is that these velocities seem to work. Below the accepted figures, low bit life and slow penetration rates occur. Above these figures, increasing amounts of abrasive wear on the drill pipe and stabilizers seem to appear. There is a fallacy to this entire approach, however. The entire velocity calculation is made using nominal bit and pipe sizes and compressor deliveries with no compensation made for losses in the system. Perhaps an examination of some of the things that are not presently considered could lead to some practical improvements in the operation.

Jan 1, 1980

By Leon H. Nelson

Several factors which affect the segregation and solidification of killed hot-topped steel ingots are: (1) pouring temperature, (2) volume in the hot top, (3) taper in the ingot, (4) pouring rate by varying the nozzle size, (5) segregation of several elements, (6) moving ingots before completely solidified. In most of this discussion, segregation will be measured in terms of carbon variation only. All the data given are results on S.A.E. 1040 analysis of fully killed steel direct-poured in hot-topped molds giving 20-in, square ingots. Thus the variables of analysis and ingot size and contour are eliminated. Segregation results are all on the rolled-bloom size, not on the ingot itself. They are results from plant-control work and not results of special research on ingot segregation. Pouring Temperature The temperature (or, more correctly, the amount of superheat above the liquidus-solidus) of the steel entering the ingot is, of course, one of the most important factors influencing segregation and solidification. Table 1 gives the average segregation of a number of heats of S.A.E. 1040 steel with normal pouring temperatures of 2775" to 2825" F. The table also gives some data on segregation in hot heats (pouring temperature 2840" to 2870" F.) and in cold heats with some skull (poured at 2725" to 2760" F.). The results in Table 1 are on steel ingots with 20-in. square cross section and 60 in. long to the hot top. The ingot weighs 7100 lb. and the hot top contains 14.3 per cent of the total ingot volume and 11.2 per cent of the total ingot weight. The results are from drillings after rolling the ingots to bloom size. Segregation results obtained on the bloom are probably not as great as they would be in the ingot itself, since heating the ingots for rolling can perhaps cause some migration of carbon from regions of high and low carbon to those of average carbon content.

Jan 1, 1937

By C. W. Wark, Fred Wise

The Getchell mine, a comparatively recent gold discovery, is in the old Potosi mining district, Humboldt County, Nevada. All ore is mined from open pits using Diesel shovels and gasoline trucks. Two types of ore are mined, oxide and sulphide. Oxide ores are siliceous or shaly; sulphide ores either gougy, siliceous or shaly. In mining, the sulphide ore is segregated into hard and gougy ore, because the gouge must be dried before it can be crushed. The oxide ore is not segregated. General Metallurgy The oxide ore is the leached outcrop that overlies the sulphide ore body. All of the iron and arsenic sulphides found in the sulphide ores have been thoroughly oxidized. The sulphur and arsenic have been leached out while the iron is present as hematite and limonite. The oxide ore is amenable to direct cyanidation, and although no visible free gold is present it is released at a comparatively coarse grind. The sulphide ore is more refractory, since the gold is all of micron size and some of it is locked in fine sulphides. It has been established microscopically that the free gold is coated with an impervious shell, which is probably some form of iron compound. The sulphide ores contain from 1.5 to 2 per cent of arsenic, which is present as orpiment and realgar with minor amounts of arsenopyrite. The orpiment and realgar are of a later mineralization than the gold and are barren. Roasting and washing of the sulphide ore prior to cyanidation is necessary to eliminate , the arsenic, to alter the gold coating from an insoluble form to a soluble form, and to release the gold associated with the fine sulphides. Washing the ground calcine in weak sulphuric acid, trona, or hot water are beneficial in the order named, but to date the water is the best from an economic standpoint. Metallurgical tests as well as plant practice indicate that a certain amount of gold cannot be recovered even by going beyond economic practices. On this basis metallurgical results are viewed in the light of an optimum tailing rather than a percentage of extraction. Milling Practice Crushing (Fig. I).—There are three primary ore bins, one each for oxide ore, gougy sulphide ore, and hard sulphide ore. In front of each bin a substantial yard is maintained, which makes it possible to Stockpile 2500 tons of oxidized ore, 1000 tons of hard sulphide ore, and 1000 tons of gougy sulphide ore. The bins are fed by a 60-hp. caterpillar bulldozer from the stockpiles. Fig. I shows the method and

Jan 1, 1943

By B. M. Larsen, T. E. Brower

THIS discussion is based on statistical manipulation and evaluation of operating data from several commercial blast furnaces which include rather wide variations in practice. We are concerned here mainly with the effect of manganese on sulphur elimination under operating conditions in commercial blast furnaces, but this effect can be outlined more clearly by including certain other variables such as silicon in iron and slag basicity, which are all in part interrelated. Real progress in understanding all of the smelting-zone reactions in this process requires more laboratory studies of slag-metal melts similar to those in the blast furnace, with careful control of oxygen pressure. Such experimental work is very difficult, however, and in the meantime, with the present scarcity of more fundamental data, such statistical trends and correlations as can be obtained from commercial furnace operating records may help in choosing laboratory test conditions as well as adding to our knowledge of operating procedures. We do not know just why the furnace data are apparently so irregular that statistical treatment of large numbers is needed to obtain accurate trends. It is partly caused, no doubt, by the many simultaneous variables present, but there are perhaps also such factors as: (I) the con- tinual swings up and down so characteristic of the process; (2) difficulty of accurate sampling of co-existing phases, as well as (3) the presence of both equilibrium and rate factors as a result of the fast driving of the process. In desulphurization, for example, the flow of thin layers of slag and metal over solid coke surfaces, plus the contact between droplets of iron falling through the slag layer in the hearth, would lead one to expect a close approach to equilibrium. On the other hand, most of the critical part of sulphur removal may occur in a short time and distance below the tuyeres with perhaps an accompanying decrease in oxygen pressure and the concurrent reduction of much of the silicon and manganese, so its degree of approach to equilibrium may be quite variable. Probable Chemistry of Desulphurization Since there is little evidence that sulphur atoms in the iron solution are aasociated to any appreciable extent in molecules such as MnS, the transfer from slag to metal and back again can be written:* (FeS) ? [FeS], [I] hence the following reactions seem most probable in the slag phase, (FeS) + (CaO) ? (CaS) + (FeO), [2] and, (FeS) + (MnO) ? (MnS) + (FeO). 131

Jan 1, 1949

By Joseph M. Jacisin

Fatigue tests were conducted on 2017-T4 alumium in alloy in an u1lrcthig.h vacuum of 2 x 10-lo Torr and in air. The vatio of vacuum-to-air faligue life for this ~malerial varied Jrom 3.5:1 at a strain of 2.5 X 1O-3 ill. pegr in. to 8:l at a strum of 3.3 x X ill. per 171. Sotlze pvelivtlinary data were also obtained on the faligue life of the alumirnum alloy in a dvy-nitrogen atmosphere. A dark deposit observed on the fracture surfaces of the aiv-tested specimens was identified as oxides of tr~angarzese and magnesium This observalion, and the close correlalion betaveen results obtained in vaCuum and dry-nitrogen environtments, tend to confirm that air stvongly influences the fatigue mechanism by a covrosion process. THE fatigue life of certain metals is known to increase when the atmospheric pressure is reduced. Gough and Sopwith1-2 postulated that this is due to a joint chemical and mechanical process operating in air at the surface of the metal with oxygen and water vapor playing significant roles. Wadsworth and Hutchings3 observed that aluminum is mainly affected by the presence of water vapor. Very little information is available on the fatigue properties of structural aluminum alloys in a vacuum environment. This report describes work performed on 2017-T4 aluminum alloy in an ultrahigh vacuum (2 x 10-loTorr) and in air. Some preliminary data are also presented on the fatigue life of the alloy in a dry-nitrogen environment. 1) EXPERIMENT 1.1) Test Material. The material tested was commerciaT 2017-T4 aluminum alloy which, in addition to aluminum, has an approximate composition of 4 pct Cu, 1 pct Fe, 0.8 pct Si, 0.5 pct Mg, 0.5 pct Mn, plus smaller amounts of other elements.* Some typical naturally age to a substantially stable condition. Specimens were then machined from these rods and ground to a No. 8 microfinish. In order to minimize variation in material characteristics, specimens were made from rods procured from the same lot. 1.2) Apparatus. The apparatus and test specimen used in the fatigue tests are shown in Fig. 1. The device utilized a single-cantilever beam with rotating-bending loading. Bending stress was applied to the fatigue test specimen by placing a spacer beneath the bearing support, thereby providing a constant deflec-

Jan 1, 1968

By B. M. Larsen, T. E. Brower

THIS discussion is based on statistical manipulation and evaluation of operating data from several commercial blast furnaces which include rather wide variations in practice. We are concerned here mainly with the effect of manganese on sulphur elimination under operating conditions in commercial blast furnaces, but this effect can be outlined more clearly by including certain other variables such as silicon in iron and slag basicity, which are all in part interrelated. Real progress in understanding all of the smelting-zone reactions in this process requires more laboratory studies of slag-metal melts similar to those in the blast furnace, with careful control of oxygen pressure. Such experimental work is very difficult, however, and in the meantime, with the present scarcity of more fundamental data, such statistical trends and correlations as can be obtained from commercial furnace operating records may help in choosing laboratory test conditions as well as adding to our knowledge of operating procedures. We do not know just why the furnace data are apparently so irregular that statistical treatment of large numbers is needed to obtain accurate trends. It is partly caused, no doubt, by the many simultaneous variables present, but there are perhaps also such factors as: (I) the con- tinual swings up and down so characteristic of the process; (2) difficulty of accurate sampling of co-existing phases, as well as (3) the presence of both equilibrium and rate factors as a result of the fast driving of the process. In desulphurization, for example, the flow of thin layers of slag and metal over solid coke surfaces, plus the contact between droplets of iron falling through the slag layer in the hearth, would lead one to expect a close approach to equilibrium. On the other hand, most of the critical part of sulphur removal may occur in a short time and distance below the tuyeres with perhaps an accompanying decrease in oxygen pressure and the concurrent reduction of much of the silicon and manganese, so its degree of approach to equilibrium may be quite variable. Probable Chemistry of Desulphurization Since there is little evidence that sulphur atoms in the iron solution are aasociated to any appreciable extent in molecules such as MnS, the transfer from slag to metal and back again can be written:* (FeS) ? [FeS], [I] hence the following reactions seem most probable in the slag phase, (FeS) + (CaO) ? (CaS) + (FeO), [2] and, (FeS) + (MnO) ? (MnS) + (FeO). 131

Jan 1, 1949

By John L. Boardman

BECAUSE of the attention that has recently been given to the health and safety of miners by various organizations such as the A.I.M.E., The American Congress, Mining Section, National Safety Council, as well as the Bureau of Mines and various state mining departments, your committee on health and safety deemed it best to call attention this year to the mine-accident cause that is by far the most important; namely, injuries due to falls of ground, rock, roof and coal. Each of several members of the committee contributed a brief outline of the importance of this accident cause in his district. While these papers were brief, it would require too much time and space to give them in full, therefore we present an outline of each and summation of all. REPORT OF M. D. COOPER, HILLMAN COAL AND COKE CO. M. D. Cooper, Division superintendent, Hillman Coal and Coke Co., Pittsburgh, Pa., contributed the following: During the period from 1930 to 1939. accidents from falls of roof in bituminous mines average 54.3 per cent of all accidents. In mechanized mining, there is a tendency toward reduction in this class of accidents because the operator of the machine is usually at a distance of 10 to 20 ft. from the face, whereas in hand loading the miner is close to the face during most of the shift. No doubt the use of aluminum and light steel beams supported at regular intervals by jacks, a common practice in mechanical mining, has contributed to the favorable record so far developed. REPORT OF M. H. FIES, DE BARDELEBEN COAL CORPORATION Milton H. Fies, Vice-President, DeBardeleben Coal Corporation, Birmingham, Ala., says: With reference to the types of mining, it is suggested that a clear understanding be had as to the character and thickness of the directly overlying strata, with especial consideration to the strength and in some cases an analysis of it. In coal mining, generally speaking, overlying strata higher in silica than others is stronger. In changing from narrow to wide places, the procedure should be experimental, both as to the width and depth of places and as to the nature of the necessary timbering. Since most of the accidents in coal mining particularly are due to falls of roof and coal, this phase of mining should be attacked with vigor There is no substitute for discipline and, in this connection, under present conditions it is important that cooperation by the labor organizations be sought and that a spirit of fairness prevail. Frequent and thorough inspection of all active working places should be made.

Jan 1, 1941

By Fred Wise, C. W. Wark

The Getchell mine, a comparatively recent gold discovery, is in the old Potosi mining district, Humboldt County, Nevada. All ore is mined from open pits using Diesel shovels and gasoline trucks. Two types of ore are mined, oxide and sulphide. Oxide ores are siliceous or shaly; sulphide ores either gougy, siliceous or shaly. In mining, the sulphide ore is segregated into hard and gougy ore, because the gouge must be dried before it can be crushed. The oxide ore is not segregated. General Metallurgy The oxide ore is the leached outcrop that overlies the sulphide ore body. All of the iron and arsenic sulphides found in the sulphide ores have been thoroughly oxidized. The sulphur and arsenic have been leached out while the iron is present as hematite and limonite. The oxide ore is amenable to direct cyanidation, and although no visible free gold is present it is released at a comparatively coarse grind. The sulphide ore is more refractory, since the gold is all of micron size and some of it is locked in fine sulphides. It has been established microscopically that the free gold is coated with an impervious shell, which is probably some form of iron compound. The sulphide ores contain from 1.5 to 2 per cent of arsenic, which is present as orpiment and realgar with minor amounts of arsenopyrite. The orpiment and realgar are of a later mineralization than the gold and are barren. Roasting and washing of the sulphide ore prior to cyanidation is necessary to eliminate , the arsenic, to alter the gold coating from an insoluble form to a soluble form, and to release the gold associated with the fine sulphides. Washing the ground calcine in weak sulphuric acid, trona, or hot water are beneficial in the order named, but to date the water is the best from an economic standpoint. Metallurgical tests as well as plant practice indicate that a certain amount of gold cannot be recovered even by going beyond economic practices. On this basis metallurgical results are viewed in the light of an optimum tailing rather than a percentage of extraction. Milling Practice Crushing (Fig. I).—There are three primary ore bins, one each for oxide ore, gougy sulphide ore, and hard sulphide ore. In front of each bin a substantial yard is maintained, which makes it possible to Stockpile 2500 tons of oxidized ore, 1000 tons of hard sulphide ore, and 1000 tons of gougy sulphide ore. The bins are fed by a 60-hp. caterpillar bulldozer from the stockpiles. Fig. I shows the method and

Jan 1, 1943

I. PRESIDING OFFICER. At all business meetings of the Institute the President, or, in his absence, the First Vice-President, or, in the absence of both of them, any other Vice-President or Director, chosen by the meeting, shall preside. At all other meetings of the Institute the President, or, in his absence, one of the Vice-presidents, shall preside. If none of these be present the meeting shall elect a Chairman. The President shall do and perform such other duties as may from time to time be assigned to him by resolution of the Board of Directors of the Institute. II. ORDER OF BUSINESS. At each business meeting of the Institute the order of business shall be as follows: 1. Reading of minutes of preceding meeting. 2. Report of the President. 3. Report of the Treasurer. 4. Report of the Secretary. 5. Election of Directors. 6. Reports of Standing Committees. 7. Reports of Special Committees. 8. Special Orders. 9. Miscellaneous business. This order of business may be changed at any meeting, by a vote of a majority of the Members and Associates present. At all sessions of the Institute, other than business meetings, the order of proceedings and the time of adjournment shall rest in the discretion of the presiding officer. III. SECRETARY OF THE INSTITUTE. The Secretary shall keep a record of the proceedings of all the meetings of the Institute. He shall be custodian of the corporate seal, of the minute books and of all the legal documents belonging to the Institute. He shall have charge on behalf of the Institute of all correspondence. He shall notify all Officers and Directors and all members of committees of their election and appointment; shall issue notices of all meetings of the Board, and of the annual and other business meetings of the Institute; and shall, in calling special meetings of the Directors, specify the objects of such meetings. He shall act as clerk at all the meetings of the Board of Directors and at all meetings of the Institute. The Secretary shall be custodian of all technical or scientific papers submitted to the Institute for its consideration and shall have general charge and supervision of the editing and proof-reading of all material published by the Institute, and of the distribution thereof. The Secretary shall be the custodian of all back numbers of the Transactions and other publications of the Institute. There shall be kept under his direction an account

Jan 1, 1925

There is plenty of sulphur available but not at the price currently being paid for brimstone. Immediate shortages may be felt before the market adjusts, making marginal sources and by-product sulphur and acid available. (See P. 403) Government aid for mineral exploration is available and regulations governing applications are available from The Defense Minerals Administration, Dept. of Interior. lust ask for M0-5 and also for the contract form which is MP-103.

Jan 5, 1951

By E. F. Ketterer, D. B. Collyer, A. B. Wilder

The microstructural stability of 59 carbon and low alloy steels after 34,000 hr exposure at 900&apos; and 1050°F, including the weld heat-affected zone, is discussed. The tensile and creep rupture properties of the parent metal of many of the steels before and after 10,000 hr exposure are presented. SEAMLESS pipe has been used for many years at elevated temperatures. When seamless first began to be used, operating temperatures and pressures were relatively low and the steel produced adequately met the existing requirements. The need for knowledge of creep properties and graphitiza-tion was nonexistent. Today the requirements for tubular products have changed considerably. Operating temperatures and pressures are increasing continually and corrosion, particularly at high temperatures, presents a problem. Carbon steels have, under these conditions, certain economic advantages particularly in oil refinery use. However, the use of low alloy steels in the generation of steam power has increased appreciably due to the influence of molybdenum on creep strength and the control of graphitization with chromium. The behavior of carbon and certain low alloy steels after long periods of exposure at 900° and 1050°F (480° and 565°C) has been investigated. The steels were examined before and after 10,000 to 34,000 hr exposure. Results obtained with material exposed at 1200°F (650°C) are not presented due to the severe oxidation and resulting decarburiza-tion after long periods of exposure. The graphitization characteristics of carbon and low alloy steels are of fundamental concern to the users of these materials. This is particularly true where welded joints are employed. In order to evaluate properly the behavior of steels at elevated temperatures, it is desirable to employ not only long periods of exposure under controlled conditions, but to use material with known properties and steelmaking practices. The purpose of this investigation has been to study the microstructure of the weld and the tensile and creep rupture properties of the parent metal after long periods of exposure at elevated temperatures. In the report&apos;.&apos; of a previous investigation data were presented on the microstructure, impact strength, hardness, and oxidation characteristics after 10,000 hr exposure at elevated temperatures. When this investigation was planned, methods for controlling the graphitization characteristics of steel were not established and, therefore, a number of special alloy steels were included in the study. During the exposure of these steels, the influence of aluminum in accelerating the rate of graphitization and the inhibiting power of chromium were established by various investigators. Also, the vanadium-bearing steels, because of their outstanding creep properties, received attention. As a result of these developments, considerable progress has been made in the field of high temperature tubular products, and the necessity for special alloys to prevent graph-itization has been restricted largely to the use of chromium. Material Chemical analysis, deoxidation treatment, and austenitic grain size of the 59 steels discussed in this paper are shown in Table I. The steels were forged to 1x1 in. bars with the exception of steels 12B, 12DX, 12DY, 12DZ, 70, 70A, 72 to 78, 82, and 83 which were machined from heavy wall pipe. All bars were surface ground before exposure. Heat treatment before exposure is shown in Table 11. The majority of the steels included were melted in either a basic open hearth or basic electric furnace; how-

Jan 1, 1955