Search Documents

By G. S. Scott, G. W. Jones

ECONOMIC waste caused by mine fires may become considerable,15 especially if a fire is allowed to spread or temporarily to get beyond control. It is important, therefore, to act promptly whenever a fire is suspected and to make every action count. To contribute toward its extinction effectively it is necessary to know at the earliest possible moment, and continuously thereafter, what is happening at the seat of the fire, which may be in a remote or inaccessible area, and also to recognize what may be expected as a result of any proposed combative measure. In combatting a fire the mining engineer and the chemist should cooperate, first deciding upon the course of action to be taken and then drawing upon the mining engineer's intimate knowledge of the physical structure of the fire area, the cost and time required to carry out proposed operations, and the probable efficiency with which these operations could be performed, and upon the chemist's knowledge for the results to be expected therefrom. After the initial steps to be taken have been decided, it devolves upon the mining engineer to see that they are carried out and upon the chemist to evaluate the results and to keep the mining engineer continuously informed in regard to a variety of matters-such as the composition and toxic or asphyxiating properties of the atmosphere in which the men may be working, whether the fire is increasing or decreasing in intensity and its probable temperature, the quantity of air leakage and the explosion hazards of the fire area. The purpose of this paper is to discuss what the chemist can and cannot contribute as a member of the fire-fighting personnel. The technical literature contains several hundred papers relating directly and indirectly to mine fires, and this fact alone is testimony to the complex nature of the phenomena involved in the birth, life, and final demise of a fire. A fire may be stopped (I) by preventing oxygen from reaching the coal or (2) by removing the conditions necessary for the rapid reaction of coal with oxygen; i.e., decreasing the temperature. All methods of prevention or control. necessarily must be based upon one or the other, or both, of these two principles. . The chemistry of a fire may be understood readily if the low-temperature oxidation of coal is considered as a starting point; then oxidation at higher temperatures (or combustion) ; and with these, the composition of the solid and gaseous products resulting from the oxidation or from the effects of the heat liberated. This discussion refers particularly to Pennsylvania anthracite, although much of the material applies equally well to coals of lower rank. OXIDATION OF COAL Oxidation of coal fundamentally is confined to the surface; that is, the rate at which oxygen penetrates into the interior of a solid block of coal is so slow that it may be ignored.6,16 Oxidation starts when a fresh surface is exposed, and the rate is

Jan 1, 1942

By A. L. Titchener, M. B. Bever

The stored energy of cold work was investigated in drawn gold-silver wires by tin-solution calorimetry as a function of strain, strain rate, initial grain size, and temperature of defornation. The energy expended in the deformation process was measured. Hardness was also measured and was correlated with the stored energy as a function of strain and strain rate. Mechanisms of energy storage are discussed. THE variables which determine the amount of energy stored in a metal during cold work are of two kinds: those involving the metal and its condition and those involving the process of deformation. For example, the stored energy differs between one metal and another and between different degrees of purity of a single metal. It also depends on the nature of the deformation process and particularly the extent, rate, and temperature of deformation. Most investigators have reported the stored energy as a function of strain (or some similar geometric parameter) or of the energy expended during deformation. In general the stored energy increases with strain, rapidly at first, but more slowly at large strains until a saturation level is reached. Information about the effects of other variables, however, is limited. Some data are available on the dependence of the stored energy on the purity of a metal1 and on the composition of

Jan 1, 1960

By Richard E. Gray, Robert W. Bruhn

INTRODUCTION Underground coal mining has been practiced in the United States for over 200 years. Much early mining was not as efficient as today and unrecovered coal pillars, often of variable size and spacing, remain to support the overlying strata after mining has ceased. These conditions constitute a potential subsidence problem since the pillars will eventually fail. The possibility of subsidence above an abandoned mine must be anticipated except when total extraction has been achieved, permitting subsidence concurrent with mining, or when large coal pillars which have an adequate factor of safety for long-term support remain in the mine. Coal is found in 37 states and is mined under- ground in 22 states (HRB Singer, Inc. 1980). Underground mining produced 40 percent of the 7.5 x 10" kg. (830,000,000 tons) of U. S. coal mined in 1980 (Keystone, 1981). There are approximately 70,000 abandoned or inactive underground coal mines in the United States and approximately 2000 active underground coal mines (NAS/NAE, 1975). Underground coal mining in the United States will eventually extend beneath 162 x 109m2 (40 million acres). Thirty-two billion m2 (8 million acres) are already undermined (HRB Singer, 1977). Subsidence due to mining has affected more than 8 x 109m2 (2 million acres) in 30 states, 7.7 x 10 9m2 (1.9 million acres) from bituminous coal mining and the remainder primarily from anthracite mining (Johnson and Hiller, 1979). Subsidence from all other underground mines has affected only 6.9 x 10 7m2 (17,000 acres) (Johnson and Miller, 1979). Subsidence appears to be particularly widespread in two states, Pennsylvania and Illinois, although serious subsidence is found in localized areas of numerous other states (HRB- Singer, Inc. 1977). Host underground coal mining has occurred in the eastern United States, where the U. S. Bureau of Mines estimates 1.6 x 109m2 (398,600 acres) in urban areas in 18 states (out of a total 1.7 x 109m2 1418,400 acres]) are threatened by subsidence (Table 1) (Johnson and Miller, 1979). Pennsylvania and West Virginia contain 57 percent of the total threatened areas. The U.S. Bureau of Mines estimates the total cost to stabilize the estimated 1.7 x lo9m2 (418,400 acres) of subsidence prone urban land located above abandoned mines is over $12.5 billion (1978 costs).

Jan 1, 1982

By F. H. Kihlstedt

THE Larap iron deposits, 125 miles east of Manila, are the biggest high-grade iron deposits in the Philippines, and have in seven years produced nearly 4 million tons of 6o per cent ore. Magnetic surveying followed by churn and diamond drilling cheaply developed a score of million tons. The ore zone is a wedge of metamorphic rocks in fresh, Miocene sediments overlain by agglomerates, which seem to have filled a river valley eroded in the sediments. A mild overthrust of the competent agglomerates crumbled the shale in front. Solutions gradually turned it into more competent hornfels and deposited pyrite, then magnetite and pyrite in the pores. As the temperature rose large bodies of magnetite with some pyrite were deposited by replacement and in open cavities in tensional areas of overthrust shears. At still higher temperature magnetite and calcium-magnesium silicates formed other bodies in similar cavities, and finally the thrust zone was invaded by syenite porphyry, causing high-temperature alteration products. Possibly, as temperature abated, more high-grade ore was deposited. The complicated faulting indicates dynamic, chronological and spatial changes of mineralization rather than zoning in a static system. Noncommercial copper, molybdenum and some gold accompanied the iron mineralization. In the thirties the Philippines gained a justified reputation as a country of considerable mineral wealth. Traces of Chinese workings show that these earliest travelers and traders had in a small way exploited the latent gold resources in the Islands. The Spaniards continued this for centuries, but did not succeed in establishing any steady mining industry. Modern technology was required to get it started. The rapid development in the last decade before the war got its impetus from several financial factors, the return to sugar growers of previously collected taxes, the influx of Spanish capital during the civil war in [ ] Spain, the influx of Chinese capital when the Japanese started their "China incident," and others. Directly or indirectly much of this capital reached the mining industry; in particular, gold mining. Out of the turmoil of an exceptional mining boom emerged a sufficient number of good and well managed gold properties to send the production to a level above that of any single state in the United States at the time. Other ore deposits besides those of gold also received their share, and for a country without any heavy industries at

Jan 1, 1946

By Charles Burrows

THE burden a man can endure depends on its magnitude and the number of tunes it is applied, as well as on many other factors. The resisting power of steel likewise is dependent on many factors. The maximum load it can support indefinitely is much less than its possible momentary burden. A light load straining the metal far within its elastic limit, if repeated indefinitely, ruptures the metal. The magnitude f the stresses that may be alternately applied and removed without rupturing the material depends on the number of repetitions of the cycle; the intervening periods of rest; the thermal, electric, and magnetic conditions, as well as the presence of secondary stresses. While we are unable to formulate the law between the magnitude f repeated stresses necessary to produce rupture and the length of time during which these alternating stress may be applied before rupture, my experience is that the time increases as the magnitude of the force decreases, according to a law which, to a first approximation, is exponential. In other words, F = Ce-t where F = magnitude f alternating stresses; = time for which stresses are continued; C = constant, which' depends on the conditions under which the operations are carried out. It is quite probable that the same type of law holds for the magnitude of a continuous force and its duration. When a rod of steel is subjected to the blows of a drilling hammer several things happen. First, one end is struck by the hammer and the other end is driven into the rock, thus causing a bodily displacement of the entire material of the steel drill. The greatest stresses involved in this bodily displacement are located at the two ends of the steel and manifest themselves by the distortion of these parts. Second, after the blow has been delivered the steel drill, due partly to its own resiliency and partly to the resiliency of the rock, experiences a vibratory motion as a whole, this motion is quite similar to the bouncing of a rubber ball thrown violently upon a smooth pavement. Third, the free vibration of the drill is determined only by its own natural period of vibration. This motion involves all the characteristics f any vibrating body emitting sound. Certain elements of the rod will experience alternations of condensation and rarefaction and, in these regions, the individual steel

Jan 6, 1921

By J. N. Breston, R. V. Hughes

Conclusions drawn by previous research workers with reSPect to the relation between Pressure gradients and/or velocity and oil recovery obtained by laboratory water flood tests have been in disagreement probably due to variable procedures and unnatural conditions and materials. The Bradford Laboratory of the Pennsylvania Grade Crude Oil Association as part of its secondary recovery research program has conducted nineteen water floods on two long cores of widely differing characteristics in an attempt to clarify this relationship and make it an aid in predicting flooding pressures in the field. Unlike previous research procedures the present experiments were conducted with the aim of duplicating field conditions as closely as possible by using long unextracted consolidated cores, a live crude, and natural brines for both flooding and, connate water content. Also, the pressure gradients and flooding velocities were representative of field conditions where similar sands were being flooded. Eleven floods on one core and eight floods on the other core showed increased recoveries and lower residual oil saturation with increased flood pressure gradients and flood velocities. A marked decrease in recovery was obtained from both cores at very low flood velocities. This pressure versus recovery relationship is shown to hold up to the point of water breakthrough and also up to the 100 and 1 produced water to oil ratio point. INTRODUCTION The possibility of water flooding oil sands was suggested by Carl1 of the Pennsylvania Geological Survey in 1880. It is not known when the practice was tried intentionally for the first time, but its beneficial effects were noted in the annual production rate of the Bradford field as early as 1907. The practice was illegal in Pennsylvania until 1921. Early water floods in the Bradford field usually consisted of shooting or splitting the casing secretly to permit subsurface waters to enter the producing sands under hydrostatic head. As it was noted that the benefits of water flooding seemed to be proportional to the quantity of water dumped into the well many also began to utilize surface sources after the practice became legal. It was probably during the middle 20's before many producers realized that the pressurehead of the water upon the producing sand determined the rate and quantity of water that would enter the sand. Hence, rate and quantity of production appeared to be a direct function of input pressures. By 1927 a few producers had ventured the installation of pressure pumps in order to increase water-input rates and production through the combination of hydrostatic and hydraulic pressures. The adoption of pressure flooding and the "five-spot" drilling pattern in the Bradford field were essentially simultaneous. Water-input pressures in 1930 seldom exceeded 300 p.s.i. at the well head or 1100 p.s.i. at the sand face. Since that time, water-flood producers in the Bradford-Allegany fields have gone to higher and higher pressure until today 600 p.s.i. at the well heads is called a low pressure flood. Many high pressure floods now operate at 1300-1400 p.s.i. at the well head. The limiting and advisable pressure at the sand face has been pronounced as that pressure just under what is required to lift the overburden or to cause formation parting: According to this rule any water flood operation utilizing well-head pressures nearly equal in pounds per sq. in. to 1.1 times the average depth in feet to the top of the producing sand would be considered as a high-pressure flood. Despite the higher pressure trends in the Bradford-Allegany field operations and the results of early laboratory water flooding research, the desirability and benefits of high input pressures are still questioned by many operators, particularly in midwestern water flood operations. The present paper recounts a series of 19 laboratory water floods using two long, consolidated cores of widely differing characteristics saturated with live crude and flooded with oil field brines in an effort to simulate field conditions under • various pressure gradients and flooding velocities. For both cores, higher recoveries and lower residual oil saturations were obtained at higher pressure gradients and flood velocities. This relationship is shown to hold up to the water breakthrough point and also up to the 100 to 1 produced water to oil ratio point.

Jan 1, 1949

By R. V. Hughes, J. N. Breston

Conclusions drawn by previous research workers with reSPect to the relation between Pressure gradients and/or velocity and oil recovery obtained by laboratory water flood tests have been in disagreement probably due to variable procedures and unnatural conditions and materials. The Bradford Laboratory of the Pennsylvania Grade Crude Oil Association as part of its secondary recovery research program has conducted nineteen water floods on two long cores of widely differing characteristics in an attempt to clarify this relationship and make it an aid in predicting flooding pressures in the field. Unlike previous research procedures the present experiments were conducted with the aim of duplicating field conditions as closely as possible by using long unextracted consolidated cores, a live crude, and natural brines for both flooding and, connate water content. Also, the pressure gradients and flooding velocities were representative of field conditions where similar sands were being flooded. Eleven floods on one core and eight floods on the other core showed increased recoveries and lower residual oil saturation with increased flood pressure gradients and flood velocities. A marked decrease in recovery was obtained from both cores at very low flood velocities. This pressure versus recovery relationship is shown to hold up to the point of water breakthrough and also up to the 100 and 1 produced water to oil ratio point. INTRODUCTION The possibility of water flooding oil sands was suggested by Carl1 of the Pennsylvania Geological Survey in 1880. It is not known when the practice was tried intentionally for the first time, but its beneficial effects were noted in the annual production rate of the Bradford field as early as 1907. The practice was illegal in Pennsylvania until 1921. Early water floods in the Bradford field usually consisted of shooting or splitting the casing secretly to permit subsurface waters to enter the producing sands under hydrostatic head. As it was noted that the benefits of water flooding seemed to be proportional to the quantity of water dumped into the well many also began to utilize surface sources after the practice became legal. It was probably during the middle 20's before many producers realized that the pressurehead of the water upon the producing sand determined the rate and quantity of water that would enter the sand. Hence, rate and quantity of production appeared to be a direct function of input pressures. By 1927 a few producers had ventured the installation of pressure pumps in order to increase water-input rates and production through the combination of hydrostatic and hydraulic pressures. The adoption of pressure flooding and the "five-spot" drilling pattern in the Bradford field were essentially simultaneous. Water-input pressures in 1930 seldom exceeded 300 p.s.i. at the well head or 1100 p.s.i. at the sand face. Since that time, water-flood producers in the Bradford-Allegany fields have gone to higher and higher pressure until today 600 p.s.i. at the well heads is called a low pressure flood. Many high pressure floods now operate at 1300-1400 p.s.i. at the well head. The limiting and advisable pressure at the sand face has been pronounced as that pressure just under what is required to lift the overburden or to cause formation parting: According to this rule any water flood operation utilizing well-head pressures nearly equal in pounds per sq. in. to 1.1 times the average depth in feet to the top of the producing sand would be considered as a high-pressure flood. Despite the higher pressure trends in the Bradford-Allegany field operations and the results of early laboratory water flooding research, the desirability and benefits of high input pressures are still questioned by many operators, particularly in midwestern water flood operations. The present paper recounts a series of 19 laboratory water floods using two long, consolidated cores of widely differing characteristics saturated with live crude and flooded with oil field brines in an effort to simulate field conditions under • various pressure gradients and flooding velocities. For both cores, higher recoveries and lower residual oil saturations were obtained at higher pressure gradients and flood velocities. This relationship is shown to hold up to the water breakthrough point and also up to the 100 to 1 produced water to oil ratio point.

Jan 1, 1949

By R. Casting, J. Philibert, and C. Crussard

APPARATUS described in this paper uses the properties of X-radiation, emitted by substances under electron bombardment, as a means of rapid chemical point analysis. The method is based upon the principles of emission X-ray spectrography pioneered by Moseley in 1913. A very finely focused beam of electrons—the electron probe—is projected on the surface of a sample, which has a very large area compared with the beam diameter, at the point where it is desired to know the chemical composition. The minute volume of the sample which is thus irradiated emits a complex X-ray spectrum consisting principally of the characteristic radiations of the elements present in the volume. Measurement of the wavelength and intensity of each component of this spectrum thus affords a simple method of determining the chemical identity and concentration of these elements. The volume of sample which is analyzed at each position of the beam is limited by the diffusion of electrons in the sample. For an accelerating potential of the electron beam of about 30 kv, which is a convenient value for producing the characteristic radiation, this diffusion extends over a diameter of about 1 µ normal to the beam, and about 2 µ in the direction of the beam. Thus a beam of 1 µ in diameter leads to a volume of about 2 µ in diameter being irradiated. The limits of the analyzed region are thus considerably smaller than those obtained by using spark or arc emission spectrometry, which must extend to about 50 µ at right angles to the beam, and those obtained in X-ray fluorescence analysis, where the penetration of the specimen is considerably greater. The apparatus itself consists of three main parts: an electron optical system. an X-ray spectrograph and an optical microscope. The electron opticai system consists of a tungsten cathode emitting the electrow and a pair of magnetic lenses which focus the electron beam on the specimen to be analyzed. The specimen is prepared in the usual way, as in optical micrography. The X-radiation, emitted at the focal spot where the electrons strike the sample, is analyzed with a curved crystal, Geiger-Müller counter, vacuum spectrograph. The light microscope, designed to observe the surface of the sample in the region to be analyzed, is provided with a reflecting objective placed on the axis of the second magnetic lens. Its magnification is X450. The quantitative determination of an element A in the analyzed region is made by measuring the intensity I, of a strong characteristic line of the element, as emitted from the sample, and then the intensity I (A) of this same line as emitted from a

Jan 1, 1958

By R. T. Webber, R. B. Owen

The vapor phase deposition of molybdenum and tungsten from the hexacar-bonyls has been thoroughly investigated by Lander and Germerl, and shown to yield well-bonded coatings on a variety of hot metallic surfaces. They also demonstrated that chromium coatings2'3 could be similarly deposited, but did not investigate this metal extensively. Recently, conditions have been described by which this compound can be prepared in quantities sufficient for laboratory scale plating experiments, and it is the purpose of the present communication to outline the results of preliminary experiments upon the plating of chromium from its carbonyl. Apparatus and Technique The apparatus used in these experiments is shown in Fig I. At one end, connected by a short length of rubber tubing, is a Cenco Hypervac 20 pumping continuously. At the opposite end is a needle valve which allows a small stream of purified hydrogen to flow through the apparatus. Connected in series are a trap T1, maintained at the temperature of dry ice and acetone, the plating chamber, and two traps T² and T3 containing crystals of the carbonyl. T² is kept in a constant temperature bath (not shown), while T³ is at room temperature. Stopcock S6 allows the hydrogen flow to by-pass the carbonyl traps. A McLeod gauge is connected so that it can measure the pressure at the pump through Se, or the pressure at the plating chamber through S9 and S6. The standard (12 liter) volume connected by Sb is used to determine the volume included by S4, S6, SB, Slot the needle valve and the McLeod gauge. Knowledge of this volume allows calibration of the flow of hydrogen. The apparatus* is built entirely of pyrex, except for the needle valve, the rubber connection to the Hypervac, and the cover of the plating chamber. The plating chamber is water-jacketed, with a large brass top allowing insertion of the specimen to be plated. Set into the brass top is a ground glass stopper through which thermocouple leads are sealed. The thermocouple wires (pure Pt, and 87 pct Pt-13 pct Rh) serve the double purpose of measuring the specimen temperature and suspending it in the chamber. Surrounding the chamber is the coil of an induction heater, H. The apparatus is designed to allow variation of the following conditions: (I) the specimen temperature, from room temperature to about 1000°C, (2) the carbonyl vapor pressure, from 40 to 220 microns, and (3) the hydrogen flow. In several runs, 0.8 to 1.8 PCt of hydrogen sulfide was introuced through a needle valve that replaced S4. The vapor pressure of the carbonyl is

Jan 1, 1949

By W. A. Anderson, F. N. Rhines, W. A. Johnson

THE rate of the high-temperature oxidation of pure copper has been measured repeatedly by numerous investigators. It appears to be generally agreed: (I) that at constant temperature, after the initial stages of oxidation have been passed and the scale has attained a substantial depth, the film thickness increases in proportion to the square root of the time of oxidation; and (2) that for any given period of oxidation the logarithm of the square of the film thickness is proportional to the reciprocal of the absolute temperature of oxidation.' These relationships are explained upon the basis that the rate of diffusion of copper to the external surface of the film is the controlling factor in establishing the rate of growth. Extensive studies have been devoted also to the mechanism and rates of the early stages of oxidation. There is thus available a reasonably well established theory of the oxidation of pure copper upon which to construct an explanation of the more complex oxidation of copper alloys. Few general principles have as yet emerged from the chaos of observations that have been reported in the field of the oxidation of alloys.2 It is evident, however, that the copper alloys may be divided into two main groups, whose oxidation characteristics are distinguish able. The first group, composed of the alloys with the noble metals, forms substantially pure copper oxide scales; the alloying element is concentrated within the residual metal, and sometimes particles of almost pure noble metal are found in the scales completely surrounded by copper oxide. In the second group, composed of the alloys of copper with the baser metals, the alloying element appears as an oxide in the scale, often in greater concentration than in the alloy itself and sometimes to the exclusion of copper oxide. The oxide scales of the latter class have been found to be made up of one, two, and sometimes more distinguishable layers of which the innermost is often metallic in character, composed of particles of the oxide of the alloying element embedded in essentially pure copper and known as the subscale or zone of internal oxidation. The need for a thorough quantitative study of these modes of oxidation is evident. Since it is apparent that several mechanisms must be cooperating to produce the complex oxide scales found on copper alloys, the analysis of the process into its several simple operations should prove instructive. Fortunately, it is possible experimentally to produce internal oxidation in the absence of an external scale; this permits the isolation and intensive study of one of the steps in the oxidation process. In the present research the rates of internal oxidation of an extensive series of dilute solid solution alloys of copper have been measured and a theory has been developed to predict the observed

Jan 1, 1941

By Donald W. Scott, Adam Wesner

This paper describes the study of 23 nonmagnetic iron-formation samples from the Mesabi Range and shows the significance of their chemical, mineral, and physical properties in terms of their concentration. Data presented here resulted from a research project carried out from 1942 to 1952 by 10 major producers of iron ore, working in conjunction with Battelle Memorial Institute. THE inevitable depletion of Mesabi direct-shipping iron ores, hastened by recent wars, has increased the importance of developing methods to concentrate iron-formation materials. Many mining companies, independent research organizations, chemical companies, and equipment manufacturers are devoting attention to this important work. It is only natural that magnetic iron-formation materials have received major emphasis, since magnetic recovery methods apply and reserves of Mesabi magnetic taconites are large. However, the nonmagnetic* iron-formation materials are likewise believed to represent a large reserve and their study has not been neglected. tions over the years have shown that in addition to the unenriched taconite, which is dense and hard, and the direct-shipping ore, there are transition taconites grading into the friable wash, or intermediate ores. The transition taconites are less massive than the unaltered taconites and usually coarser-grained. This variation, coupled with the fact that there were no extensive drillings in the unaltered taconite, posed a most difficult problem of obtaining samples that would be representative of large tonnages of the fresh rock. The problem was increased by the tremendous extension of the nonmagnetic formation materials on the Mesabi and by the question of their accessibility to mining. A drilling program was evolved that would surmount these difficulties. Selection of samples was made by a committee representing producers in the area. The samples were procured from 1—taconite walls near bodies of stripping burden or wash ore and 2—from shafts in the process of being sunk through taconite for drainage or mining operations. Most of the samples were obtained from the cherty horizons because it became obvious early in the program that the slaty horizons represented an exceedingly difficult concentration problem, owing to the character of the gangue minerals and the fine grind required for liberation of the valuable minerals. More samples were procured from the lower cherty horizon than from the upper cherty because it was more accessible to mining. It is not known how well the samples selected represent the nonmagnetic iron-formation material. However, they were chosen by people Well acquainted with the geology of the Mesabi range and the mining problems involved. It is believed that they represent a fair cross-section of the types of materials that will be encountered. Table I gives data on the origin of the 23 samples and the horizon footages from which they were obtained. Samples 1 through 10, and 15 and 16

Jan 1, 1955

By R. E. Miner, J. K. Jackson, T. L. Wilson

THE nature of the decomposition reactions producing hardening in aluminum-rich A1-Ag alloys is now fairly well understood. The silver is not uniformly dispersed even at temperatures above the solvus line: rather, it is clustered into zones and associated with dislocations.' During quenching, nearly all of the silver segregates into zones' and some is attracted to dislocations, producing stacking faults. Growth of these faults produces the semicoherent y precipitate.1 During aging, the larger zones and the y precipitates grow at the expense of the smaller zones. The large zones persist up to about 350°C; where they redissolve in favor of the y' and y precipitates.' The equilibrium hcp y precipitate occurs both by a cellular reaction at the grain boundaries1 and by growth of the Y' plates to a critical size where incoherency results. Damask and Nowick 4 observed an internal friction peak in an A1-6 at. pct Ag alloy at about 140°C (0.25 cps). The peak was found to exhibit a systematic instability. After aging at successively higher temperatures between 155' and 23Z°C, the peak first migrated to higher temperatures while increasing in height, then returned to lower temperatures and decreased in height. After aging at temperatures above about 200°C, the peak position remained constant while the height decreased very slowly. In quenched specimens, elastic after-effect measurements inhcated a rapid initial transient in peak position from low temperatures up to 155°C. The authors concluded that a stress induced growth and resolution of the clusters and the 7' was the most reasonable mechanism to account for the behavior. It would seem, however, very unlikely that both the clusters and the y' precipitate would provide damping contributions whose relaxation time and activation energies were identical, which is required for them to produce the same internal friction peak. The present investigation was motivated by this apparent anomaly and the development of a very low thermal inertia torsion pendulum5 capable of monitoring transient behavior. Low frequency internal friction measurements were made on four binary A1-Ag alloys nominally containing 5, 10: 15, and 20 at. pct Ag. The results of measurements made on a 10 at. pct Ag alloy in the quenched condition are shown in Fig. 1. There are two peaks apparent in the spectrum, one centered at about 160°C, the second at about 210°C. The two peak spectrum was observed in each alloy, but it was best resolved in the 10 pct Ag specimens. Because of the instability in the internal friction, 4 it seemed possible that the second peak was not a peak at all, but simply a manifestation of a single, sharply transient, peak. This effect has been observed in Au-Ni alloys.6 The existence of the higher tempera-

Jan 1, 1970

By Y. Dardel

Since the first determination of Dumas1 in 1880, many authors have tried to measure the solubility of hydrogen in solid aluminum, or at least the amount of dissolved gas in it. However, the interpretation of the results which have been obtained is still difficult. Sieverts? then Baukloh and Oesterlen,a during their gassing experiments could not determine any solubility of hydrogen in solid aluminum. On the other hand, Portevin, Chaudron and Moreq4 leaving the determination of the hydrogen solubility beyond the scope of their experiments, measured only the amount of gas that they could extract by high voltage positive ion bombardment and found up to 151 cm3 of gas per I00 g of metal. Winterhager,6 by repeated vacuum extraction during severe cold rolling, extracted up to 161 cm3 per 100 g. In both series of experiments, the extracted gas contained chiefly hydrogen with a small amount of nitrogen, carbon monoxide, carbon dioxide and methan. Later, Schmidt and von Schweinitze as well as Chaudron and Moreau7 showed the importance of the adsorbed layer of hydrogen, the extracted quantities being proportional to the surface and not to the weight of the sample, when its cleaning was not perfect. In earlier experiments, Steinhausers extracted from more massive samples nothing but a little amount (< 0. 5 cm3 per I00 g) of hydrogen, carbon monoxide and methane. Thus, according to these experiments the quantity of dissolved gas is probably very small and the effect of the surface could falsify the results of the extraction. However, owing to the care taken by Chaudron and his coworkers, it was clear that all the hydrogen extracted could not come from the superficial layer, or that the links which bound hydrogen to the surface were so strong that the usual method of cleaning could not destroy them. After the main parts of the experiments reported here had already been carried out, Eborall and Ransley9 published the results which they obtained with an analysor having an accuracy of 0.03 cm3 per I00 g, while that of the usual apparatus was only about 0.2 cm3 per I00 g. During all their experiments the adsorbed layer would have been a difficulty, for the value of the adsorbed hydrogen was approximately equal to that of the dissolved amount. Table i—Amount of Adsorbed and Dissolved Hydrogen (After Eborall and Ransley) Extraction Hz Adsorbed „ h2 dissolved Temperature Calculated Extraction OCcma 500 0.057 0.050 600 0.062 o.096 Since always keeping the same adsorbed layer is very difficult, an error in the correction for the adsorption can be made when using the apparatus of. Eborall and Ransley, as well as the earlier apparatus.

Jan 1, 1949

By A. H. Daane, B. J. Beaudry

The Sc-Ti system was studied by thermal, metal-lographic, and X-ray methods. Scandium was found to transform at 1334 °C from a (hexagonal) to ß which was concluded to be bee since a continuous series of solid solutions is formed between ß scandium and ß titanium at elevated temperatures. There is a minimum in the solidus at 51 wt pet Ti and 1300°C, a monotectoid at 1050°C and 49 wt pet Ti, and a eutectoid at 875°C and 91.5 wt pet Ti. The maximum solubility of titanium in a scandium is 13.5 wt pet at the monotectoid temperature, while the maximum solubility of scandium in a titanium is 6.5 wt pet at 875°C. SCANDIUM, a member of Group 111 A of the periodic table, and now called a rare-earth metal,&apos; has become of interest recently due to its low density (2.99 g per cc) and relatively high melting point (1539°C).Spedding,&apos; et al. have described a method of preparation of pure scandium metal and have made a study of its basic properties. Since scandium is approximately 10 to 12 pet smaller in at. diam than the other rare earths while its electronegativity and valence are the same, a knowledge of its alloying behavior in contrast to these elements should be very helpful to fundamental alloy theory. Since scandium is quite scarce and difficult to prepare in pure form, its use as a structural material by itself seems quite unlikely. However, its use in special cases as an alloying addi- tive to other low-density materials is a possible application; the Sc-Ti system was chosen for this reason and for others of fundamental interest. Scandium was suspected of having a high temperature bee form as do some of the other rare-earth metals.3&apos;4 Since titanium has a high-temperature bee form, a continuous series of solid solutions at elevated temperatures between ß scandium and ß titanium would prove the existence and structure of the high-temperature form of scandium. The existence of a continuous series of hexagonal solid solutions at room temperature was predicted by Burkhanov and Savitskiy,5 but Hias shown to be incorrect in early X-ray studies. EXPERIMENTAL METHODS Materials. The metals employed in this investigation were crystal bar titanium and distilled scandium prepared by the method described by Spedding,2 et al. The major impurities are listed in Table I in PPm. Alloy Preparation. All the alloys examined were initially formed in a nonconsumable electrode are-melting furnace under an atmosphere of purified helium or argon. A curve based on the observed weight loss of 0.6 pet* when titanium was melted

Jan 1, 1962

F. WEIMER,* Washington, D. C. (written discussiont).-For electrical measuring instruments, especially those types that involve the Wheat-stone bridge or potentiometer principle and standards of electrical resist-ance, there has been, for a considerable time, a need for better resistance materials. For a satisfactory resistance material, much depends on the purposes for which it is to be used. For potentiometers and Wheatstone bridges, such as are in more or less general use, and the more common forms of resistance standards, a good quality of manganin answers fairly well. However, it should not be presumed that manganin is considered ideal for the purpose, for in measuring instruments and resistance stand-ards, there is still much to be desired. An experience of more than 10 years in the study of the resistance standards and resistance apparatus shows that manganin resistances change with time in a way that is very annoying and the maintenance of the unit of resistance to the desired accuracy requires an excessive amount of work or may be said to be prac-tically impossible. The changes in resistance are generally most rapid and erratic in resistances of very low and very high values. In resist-ances of low value, the resistance material is often in the form of thin sheets so that the surface is large and usually more or less unprotected from the atmosphere, or the oil in. the case of oil-immersed standards. In resistances of high value, the resistance material is in the form of fine wire and, therefore, the surface is large compared with the cross-section. In resistances of medium value, the surface is less, compared with the cross-section, or better protected, usually by a silk wrapping impregnated with shellac. This suggests that one of the difficulties with manganin is slow surface action or oxidation, even when an effort has been made to protect the surface from such action However, the changes observed cannot all be accounted for on this basis. There are, presumably, also some internal changes in the resistance material even when it has been annealed. Further; the changes in manganin resistances seem to be more or less independent of its electrical properties. In other respects, too, manganin is not ideal.

Jan 11, 1919

By G. A. Moore, D. W. Williams, C. E. Sims

During the past several years, the steel casting industry has made studies of heavy castings in which the test bar has been taken from heavy sections rather than from attached or separately cast coupons. It has been noted that the ductility properties of these heavy sections are often lower than those normally expected. Such lowered ductility is usually accompanied by a spotty test bar fracture, and the ductility values can often be greatly improved if a low-temperature aging treatment is given to the casting. A loss of ductility of this type is considered "abnormal," since it is not accompanied by an increase of tensile strength or hardness, and "temporary" when the ductility can be restored by aging. The cure of such an abnormal condition represents a real improvement in the quality of the steel. Several types of abnormal loss of duetility can be distinguished, of which those caused by excessive amounts of inclusions of undesirable type and those caused by unsuitable grain size and inget structure are well known. The particular type of abnormal lowered ductility currently under consideration may be distinguished by the fact that the low-temperature aging treatment necessary for its relief is insufficient to cause any visible change in the micro-structure as ordinarily observed. As this aging will in fact eventually occur at room temperature, the phenomenon of present interest may be given the symptomatic definition, &apos;&apos;Temporary Abnormal Low Ductility." Some hundreds of previous investigations, largely qualitative in nature, have established, beyond reasonable doubt, that hydrogen is normally present in newly manufactured steel and that this gas, in small amounts, can cause a temporary abnormal loss of ductility. The commonly observed association of high gas content and low ductility has given strong evidence for the presumption that hydrogen, possibly assisted by other gases, is the primary cause of the low ductility observed. Accordingly, The Steel Founders&apos; Society of America has, since Nov. 1, 1944, sponsored investigations at Battelle Memorial Institute whose primary objective is to obtain quantitative information on the relation of the amount of hydrogen and nitrogen in steel, together with associated methods of steelmaking and treatment, to low-duetility effects and porosity. The interest of this investigation thus extends to permanent abnormal losses of ductility, such as are caused by the inclusions which sometimes result from special deoxidizing practices and possibly from metallic nitrides, but as these can he distinguished from the temporary effect of hydrogen, they have been excluded from the work reported here except when they

Jan 1, 1949

By John Wulff, Robert Kamm, Steinberg Morris

In powder metallurgy it has often been observed that shrinkage may occur in one direction and growth in another during sintering. Even in long-time sintering experiments the rate of shrinkage may be different in different parts of the compact. In the fabrication of some parts requiring a constant permeability it is even questionable in some cases whether pressing from one direction should be attempted. These observations require for their interpretation a more detailed study of green or pressed density than has heretofore been available. Usually average density measurements of the whole compact are made and in some cases carefully cut sections are measured. A different approach to the problem was first mentioned by Rakowskil and also used by Balshin.2 Balshin&apos;s diagram is reproduced in Fig I and schematically shows the result of pressing three layers of metal powder with fine intervening layers of graphite. The retarding effect of the die walls and a qualitative example of the density distribution is evident. More quantitative information about the distribution of density within a cold-pressed powder compact would be useful in showing the variation in density in as as influenced by the type of poKder, shape of die, lubricatioll during the process, and other variables. Furthermore, information about the cracking of cold-pressed compacts may be obtained from an analysis of the stress distribution within a, powder compact, and some information about the stress distribution can be obtained in turn from the derlsity and strain distributions. A more detailed report on some of the present experiments appears in reference 3. Present Investigation In order to ascertain the density gradients in cold-pressed metal powders, a deformable lead grid within the powder was employed. After pressing in cylindrical di" the ejected compact was radiographed, giving a pattern of the deformed grid. From the radiograph density and deformation from point to point is readily measured. From the radiograph strain distribution and stress trajectories were also determined. The latter also permits the determination of the coefficient of friction at the die wall. This technique indicates that the densest Part of a compact pressed from one side is at the top outer circumference and the least dense region at the bottom circumfercnce near the stationary plunger. For Some heights of compacts the density at the axis is such that the lower density is at the top rather than at the bottom. SO irregular a density distribution is due primarily to die-wall friction. As the ratio - diameter to height of compact is increased the die walls play a correspondingly smaller role. More uniform density

Jan 1, 1947

By John Wulff, Steinberg Morris, Robert Kamm

In powder metallurgy it has often been observed that shrinkage may occur in one direction and growth in another during sintering. Even in long-time sintering experiments the rate of shrinkage may be different in different parts of the compact. In the fabrication of some parts requiring a constant permeability it is even questionable in some cases whether pressing from one direction should be attempted. These observations require for their interpretation a more detailed study of green or pressed density than has heretofore been available. Usually average density measurements of the whole compact are made and in some cases carefully cut sections are measured. A different approach to the problem was first mentioned by Rakowskil and also used by Balshin.2 Balshin&apos;s diagram is reproduced in Fig I and schematically shows the result of pressing three layers of metal powder with fine intervening layers of graphite. The retarding effect of the die walls and a qualitative example of the density distribution is evident. More quantitative information about the distribution of density within a cold-pressed powder compact would be useful in showing the variation in density in as as influenced by the type of poKder, shape of die, lubricatioll during the process, and other variables. Furthermore, information about the cracking of cold-pressed compacts may be obtained from an analysis of the stress distribution within a, powder compact, and some information about the stress distribution can be obtained in turn from the derlsity and strain distributions. A more detailed report on some of the present experiments appears in reference 3. Present Investigation In order to ascertain the density gradients in cold-pressed metal powders, a deformable lead grid within the powder was employed. After pressing in cylindrical di" the ejected compact was radiographed, giving a pattern of the deformed grid. From the radiograph density and deformation from point to point is readily measured. From the radiograph strain distribution and stress trajectories were also determined. The latter also permits the determination of the coefficient of friction at the die wall. This technique indicates that the densest Part of a compact pressed from one side is at the top outer circumference and the least dense region at the bottom circumfercnce near the stationary plunger. For Some heights of compacts the density at the axis is such that the lower density is at the top rather than at the bottom. SO irregular a density distribution is due primarily to die-wall friction. As the ratio - diameter to height of compact is increased the die walls play a correspondingly smaller role. More uniform density

Jan 1, 1947

By Enid C. Plante, K. L. Sutherland

PRACTICAL metallurgists are unanimous in stating that oxidation of mined sulphide ore adversely affects separation of the constituent minerals under standard conditions in a mill. Frequently, the need for different operating conditions in different plants is attributed either to the extent of oxidation of the mineral surfaces or to soluble oxidation products. The investigations reported in this paper study the effect of oxidation on the primary condition necessary for flotation, namely that of adhesion of an air bubble to the mineral. OXIDATION PRODUCTS FROM SULPHIDE MINERALS Weinig and Carpenter1 state that the relative rates of oxidation of some sulphides are: FeAsS > FeS2 > CuFeS2 > ZnS >PbS > Cu2S tetrahedrite. They also show that oxidation is rapid at first, that sulphides of older geological formations are more stable than those of recent date and that mixtures oxidize more rapidly than any one mineral alone. The more rapid oxidation of mixtures is borne out by results of Gottschalk and Buehler2 who found that PbS, ZnS and CuS oxidized 8 to 20 times faster when pyrite was present. Only the end products of oxidation, sulphate and the metal ion, were identified in these tests. Gaudin3 states that pyrite is difficult to oxidize in the laboratory. Winchell,4 using pyrite containing 99.98 pct FeS2, allowed water to percolate through a bed of this ground material. At the end of three months only a trace of Fe +++and S04- were found. Even after 10 months the quantity of Fe+++ was only 7.8 mg and S04- 25.5 mg per liter of percolating solution. Carmichael5 confirmed Winchell&apos;s results on the slow oxidation of pyrite. Usually the oxidation of sulphide surfaces has been conducted in neutral or acid solutions, the acidity being caused by the oxidation products. Eliseev and Nagirnyak6 found that treatment of pure pyrite with lime gave only thiosulphate, but considered it possible that thiosulphate was obtained not by oxidation of the pyrite itself, but by oxidation of calcium disulphide. Mitrofanov7 suggested that thiosulphate was formed by the following process: oxidation of sulphide to give free sulphur (this frequently happens with marcasite), followed by oxidation of the sulphur to sulphur dioxide and reaction of the sulphur dioxide with sulphur to give thiosulphate. Ferric and ferrous hydroxides, or similar compounds, were shown to be present. The Research Staff of the United Verde Copper Co.8 treated ore from the United Verde mine with lime. Thiosulphate, sulphide and polysulphides were stated to be

Jan 1, 1947

By C. E. Sims, G. A. Moore, D. W. Williams

During the past several years, the steel casting industry has made studies of heavy castings in which the test bar has been taken from heavy sections rather than from attached or separately cast coupons. It has been noted that the ductility properties of these heavy sections are often lower than those normally expected. Such lowered ductility is usually accompanied by a spotty test bar fracture, and the ductility values can often be greatly improved if a low-temperature aging treatment is given to the casting. A loss of ductility of this type is considered "abnormal," since it is not accompanied by an increase of tensile strength or hardness, and "temporary" when the ductility can be restored by aging. The cure of such an abnormal condition represents a real improvement in the quality of the steel. Several types of abnormal loss of duetility can be distinguished, of which those caused by excessive amounts of inclusions of undesirable type and those caused by unsuitable grain size and inget structure are well known. The particular type of abnormal lowered ductility currently under consideration may be distinguished by the fact that the low-temperature aging treatment necessary for its relief is insufficient to cause any visible change in the micro-structure as ordinarily observed. As this aging will in fact eventually occur at room temperature, the phenomenon of present interest may be given the symptomatic definition, &apos;&apos;Temporary Abnormal Low Ductility." Some hundreds of previous investigations, largely qualitative in nature, have established, beyond reasonable doubt, that hydrogen is normally present in newly manufactured steel and that this gas, in small amounts, can cause a temporary abnormal loss of ductility. The commonly observed association of high gas content and low ductility has given strong evidence for the presumption that hydrogen, possibly assisted by other gases, is the primary cause of the low ductility observed. Accordingly, The Steel Founders&apos; Society of America has, since Nov. 1, 1944, sponsored investigations at Battelle Memorial Institute whose primary objective is to obtain quantitative information on the relation of the amount of hydrogen and nitrogen in steel, together with associated methods of steelmaking and treatment, to low-duetility effects and porosity. The interest of this investigation thus extends to permanent abnormal losses of ductility, such as are caused by the inclusions which sometimes result from special deoxidizing practices and possibly from metallic nitrides, but as these can he distinguished from the temporary effect of hydrogen, they have been excluded from the work reported here except when they

Jan 1, 1949