Jan 1, 1968

By Y. C. Liu, G. A. Alers

The anisotropy of Young's modules has been measured in a series of Cu-Zn alloys containing from 1 to 28 wt pct Zn and cold-rolled to 97.5 pct reduction in thickness. These modulus data show a transition in texture as a function of zinc content. In alloys containing 3 pct Zn or less, the texture is essentially that of copper. A transition is clearly seen to develop in 5 and 8 pct Zn alloys, and to have been completed in a 12 pct Zn alloy. Increasing the proportion of zinc to 28 pct does not produce any further changes in texture. The ease and clarity with which this texture transition can be seen in the modulus data is in great contrast with the inccertainty in the visual detertiination of the range of texture transition from a series of pole figures. It is also shown that the rolling texture of the high zinc content alloys cannot be a one-COIIIponenl texture, characterized by the (110)(112) ideal orientations, as usually assumed. A second, quite important component must also be present. Furthermore, the present data are inconsistent with matrix orientations on which the "oriented growth" hypothesis of the Formation of recrystallization textures is based. THE rolling textures of binary fcc alloy systems have generally been considered to lie between two terminal textures. One of these terminal textures is the copper type and the other is the 70:30 brass type. Alloys of intermediate solute content exhibit a texture which is said to be a transition between the two terminal textures. On the basis of efforts to correlate rolling and recrystallization textures, two concepts have been advanced in the literature on the nature of these transition textures. One school1 suggests that the addition of alloying elements, e.g., zinc, causes a gradual rotation about one of the (111) poles from the (358)( 523) ideal orientation of the copper-type rolling texture to the terminal {1 10)( 112) ideal orientation used to describe the rolling texture of 70:30 brass. This concept is depicted in Fig. 1 with the angle of rotation corresponding approximately to the zinc content and is designated here as the "rotational concept", since the ideal orientation of the transition textures varies continuously with alloy content. The other concept,' the "mixture concept", suggests that the copper-type rolling texture is a two-component texture. {358) (523) and {110)(112). The addition of alloying elements affects only quantitatively the relative amounts of these two components—a decrease in the amount of material in the {385}(523) orientation and an increase of that in the {110)(112) orientation with increasing solute content. An experimental distinction between these two concepts is essential to a better understanding of both the mechanism of formation of rolling textures and the subsequent formation of recrystailization textures in fcc metals. Because of the lack of resolution inherent in pole figures, it has not been possible to differentiate between the two concepts on the basis of this data. Both concepts, in fact, make use of the same set of pole figures but interpret them in a manner acco-rding to the view held.'" Experimental results obtained from inverse pole figures or selected-area electron diffraction3j4 simply -yield more refined pole figures but do not eliminate the ambiguity of interpretation. Quantitative measurement of an entirely different, orientation-dependent property must thus be considered

Jan 1, 1967

By H. Morgolin, M. A. Greenfield, P. A. Farrar

In attempts to correlate mechanical properties with microstructure, it is desirable to determine the effect of ß grain size. Determination of 6 grain size is not a problem where a has precipitated at ß grain boundaries. However, in alloys which have been processed to produce an equiaxed a +ß structure the ß grain size is difficult to determine because ß grain boundaries do not etch. The ß grain size can sometimes be laboriously determined by searching for grains which have some a! outlining the 6 grains. This difficulty of ß grain size determination in equiaxed a + ß alloys can be overcome by heating below the ß transus temperature for a short time and water quenching. Fig. 1 shows the starting equiaxed a + ß structure of the Ti-5.25A1-5.5V-0.9Fe-0.5Cu alloy used in this investigation, and Fig. 2 shows the microstructure of the same sample water-quenched after heating 1 min at 1675"F, which is 25°F below the 0 transus. The heavily etched microstructure consists of some equiaxed a! in a structure showing considerable amounts of transformed ß. The ß grain

Jan 1, 1969

By D. Webster

It has been found that cold work and annealing treatments greatly retard subsequent grain growth and re-crystallization in thoria-dispersed nickel and NiCr. It is suggested that this is due to cavities which form at the particle-matrix interface durilzg cold work. Some of' the cavities formed are stable at elevated temperatures and prevent the mouement of large-angle grain boundaries. The movement of these boundaries at elevated temperatures is known to start recrystal-lization and when they are pinned by voids recrystal-lization is made more difficult. TD Nichro,me had a maximun resistance to recrystallization when the initial structure was coarse-grained and had a low dislocation density. A precipitation reaction occurred between 700° and 1200° F in cold-worked TD Nichrome. It has been shown by Grant and his coworkers1-3 that a large part of the strength of dispersion-hardened materials is a result of the cold-worked structure produced during fabrication. In a comparison of the strength of cold-worked copper with and without an oxide dispersion, Grant4 has demonstrated that there is little difference in strength at room temperature. The function of the dispersion is essentially to maintain the cold-worked structure at higher temperatures than is possible in the base material. The dispersion accomplishes this by making recrystallization more difficult. The mechanism by which this is achieved is discussed in this paper. The fabrication history of the material has been found to greatly influence recrystallization behavior and this aspect is discussed in some detail. I) MATERIAL Three different thoria-dispersed materials were examined. 1) DuPont 2 pet thoria-dispersed nickel (TDNi) in 0.050-in. seeet. Thoria particle size is in the range 100 to 2500A. 2) DuPont 2 pct thoria-dispersed nichrome (20 pet Cr, 80 pct Ni) (TDNiC) in 0.125-, 0.060-, and 0.040-in. sheet. In the as-received condition these sheets have

Jan 1, 1969

By W. G. Davenport, M. Paneni

Experiments in sheets of mercury and water have confirmed that the dynamics of bubble rise are simi-lur in Liquid metal and aqueous systems. RECOGNITION that bubble/metal interactions are important in pyrometallurgical refining processes (e.g., steelmaking, vacuum degassing, deoxidation of copper) has led to a number of investigations into the dynamic behavior of bubbles rising in liquid metals. Terminal velocities of bubbles rising in mercury (20°C)' and silver (1000" to 1050"c)1,2 have been measured. Good agreement between aqueous and liquid metal systems has been obtained. Shapes of air bubbles rising in mercury have been determined experimentally by Davenport, Bradshaw, and Richardsonl who used a system of electric probes to measure maximum horizontal and vertical dimensions, Fig. 5. In the present work the motion and shape of nitrogen bubbles rising in a thin sheet of mercury (i.e., a "two-dimensional" environment) have been studied with the view of confirming dynamic similarity between aqueous and metallic systems. The use of thin sheets of liquid permitted direct visual and photographic comparisons of bubble behavior in clear liquids and in mercury. EXPERIMENTAL METHOD The thin sheets of mercury or water were held in a clear acrylic plastic container, Fig. 1. The sheets of liquid were 80 cm high by 30 cm wide and 0.47 cm thick. Single bubbles were formed by injecting the desired volume of nitrogen into an inverted semicircular cup (stainless steel). The cup was then rotated into the upright position using an external handle thus releasing a single bubble of measured volume. Nitrogen was injected into the cup from a nitrogen cylinder through the external handle and a hollow rotating axle. The volume of a bubble (volume range 0.01 to 10 cu cm) at any instant was obtained by connecting a soap film meter to a small gas space above the liquid. By this technique any change in the volume of a gas bubble in the liquid (i.e., during cup filling or during rise) produces an equivalent displacement from gas space A into the buret B. This displacement is determined by measuring the movement of a horizontal soap film in the buret. Bubble shapes were determined using single-frame photography. Rising velocities were determined by cinephotography with a 1/100-sec stopwatch in the field of view. In both cases dimensions were referenced to a rule attached to the container surface, also in the field of view. Linear dimensions were measured on projections of the single-frame negatives. Rising velocities were calculated from measured heights of rise (10 to 20 cm) and times of rise. The effects of disturbances caused by cup rotation and by bubble release were minimized by photographing bubbles at a point not less than 25 cm above the cup. MATERIALS Mercury: Technical-grade purified: minimum 99 pct Hg; Johnson Matthey and Mallory Limited, Toronto. Nitrogen: Technical-grade purified nitrogen: 99.99 pct Nz, 0.01 pct 02, trace argon; Air Liquide Canada Limitee, Montreal.

Jan 1, 1970

By Pervez Patel, Martin G. Frohberg, Demetrios Papamantellos

Model experiments were carried out on the mass transfer of iodine between n-hexane and a 4 2 X 10-3 M aqueous sodium hydroxide solution. The influence of mechanical stirring by means of small gas bubbles (ca. 0.01 ml in volume) on mass transfer was examined in independent experiments. The results were described with the help of the penetration theory and in the case of bubble stirring with the help of a mathematical model based on this theory. S LAG-METAL reactions, especially those in steel-making processes, often occur under conditions where gas is evolved in the form of bubbles that break through the slag-metal interface. It is known that stirring by means of bubbles increases the mass transfer coefficient, but there has been very little quantitative work done in this field. Because of the difficulties that attach to experimental work at high temperatures this study was confined to model experiments at room temperature. EXPERIMENTAL APPARATUS The transport of iodine from an n-hexane layer into a weak sodium hydroxide solution was studied a) with stirring by means of bubbles and b) with mechanical stirring. The apparatus for the experiments with bubbles consisted of the cell, two Dreschel bottles filled with hexane in order to saturate the nitrogen flow, one flow meter, and a nitrogen gas cylinder fitted with a fine-regulating valve. Fig. 1 shows the cell consisting of a glass cylinder 33 cm in height with an overall diameter of 7.5 cm embedded in a copper flange. The flange is connected to a Plexiglas plate and to the gas inlet. The Plexiglas plate has holes of 0.2 mm diam bored into it which are spaced 1 cm from each other. For the experiments with mechanical stirring the bottom of the cell was sealed off by a Plexiglas plate. The upper layer was stirred by means of a glass stir-rer and the bottom layer with the help of a magnetic stirrer in a counter rotatory direction. Both stirrer speeds could be varied continuously. EXPERIMENTAL PROCEDURE Iodine dissolves in n-hexane producing a stable violet color thus enabling the iodine concentration in

Jan 1, 1970

By J. Grosso, D. J. Nagel

In many metallurgical studies, it is necessary to reveal the composition and structural properties of materials. Usually this is done by etching, but some substances do not etch well or easily. Anodizing is known to provide an alternate treatment in many cases. In general, this technique is simple, often more sensitive to composition differences than etching, has excellent resolution, and provides variable contrast in those elements and alloys which anodize. Here we report the use of anodizing in diffusion studies in the TiCb system. Fig. 1 shows a cross section of the diffusion zone in a TiCb couple. The anodizing has clearly revealed both composition and crystallographic features. The maximum bulk penetration of the titanium into the columbium is marked by a sharp line because of the steep concentration gradient. The titanium grain size and orientation differences are also evident. Variation in the grain size reflects the gradually decreasing columbium concentration.

Jan 1, 1967

By P. Niessen, W. C. Winegard, C. J. Beingessner

DURING the last 10 years, several grain-growth studies have been made using zone-refined metals with controlled amounts of solute to elucidate the interaction of solute with moving boundaries. In all these studies, it was more or less implicitly assumed that the alloys used were, after recrystallization and grain growth, homogeneous within the grains with respect to solute and lattice defects. This note deals with observations made on microstructures originating from solidification of dilute alloys and from grain growth. Briefly, the experimental procedure used in these studies was the following: zone-refined cadmium and master alloys were melted and cast in Pyrex under vacuum to produce bars 14 mm in diam and about 150 mm long. These bars were cut into 8-mm-thick slices which were mechanically and chemically polished. The specimens were then deformed 30 pct in compression and given a 1-week anneal at 260°C in argon. After this anneal, a second deformation produced completely recrystallized samples 4 mm thick. The time-temperature controlled anneals were carried out in a bath of silicone oil. After the grain-growth anneal, the specimens were polished in Gil-man's' solution (33 g CrOs, 6 g NazSO, in 100 ml of water). Several etches were used depending on the alloy investigated, but mostly a mixture of concentrated HC1 and HNOj (98:2 vol) was employed. In all the alloys examined, the ease with which substructures could be revealed depended strongly on the crystallographic orientation of the surfaces of the grains. However, very frequently the microstructures to be discussed here etched up over broad areas comprising several grains. Fig. 1 is a micrograph of a Cd-0.05 at. pct Mg alloy annealed for 100 sec at 270°C. Different substructures are seen in this photograph. A denotes the now existing grain boundaries. The well-defined lines and points marked B are the remains of a solidification substructure. The lines are boundaries between cell colonies, and the points are nodes located on regular two-dimensional cells. This cellular structure has the same appearance as that found by weinberg2 for rapidly quenched Zn-Au alloys. The "ghost boundaries", marked C, are very similar in appearance to a grain boundary array in a polycrystalline sample. Repeated polishing and etching showed that all the substructures observed were three-dimensional. To date, the ghost boundaries have been clearly observed in all samples containing 0.005, 0.01, 0.05, and 1 at. pct Mg, and in samples containing 0.01 at. pct Zn. Attempts to outline these ghost boundaries in cadmium alloys containing 0.01 at. pct Ag and Au were only partially successful. In these alloys, parallel lines, having a resemblance to the ghost boundaries in the Cd-Mg and Cd-Zn alloys, were observed, but it was not possible to obtain complete arrays of ghost boundaries which extended over several grains. It is possible that a different etch than that presently employed would reveal the ghost boundaries in the Cd-Au and Cd-Ag alloys as clearly as in the Cd-Zn and Cd-Mg alloys. A close examination of the ghost structure showed that it consisted of linear etch-pit arrays, Fig. 2. The ghost boundaries were resolvable even in grains which showed over-all faceting due to the etching, as seen in the corner of Fig. 2. The general appearance of the ghost structure suggests that it originated during grain growth. This is supported by the observation that the mesh width in the ghost-boundary array generally increased with increasing final grain size. To test whether the ghost structure was formed during the long homogenizing anneal or during the grain-growth anneal, some as-cast samples were deformed and given a grain-growth anneal. This anneal was terminated by air cooling or

Jan 1, 1967

By A. H. Larson, L. G. Twidwell

DURING the roasting of zinc sulfide concentrates and by-product recovery from flue dusts, the zinc sul-fate phase may occur in various stages of the processes. In addition to zinc sulfide, other sulfide phases are usually present such as CdS, PbS, CuzS, and FeS. Consequently, the effect of these sulfides on the thermal decomposition of ZnS04 was investigated. Merck high-purity, anhydrous zinc sulfate was used as the starting material. The sulfate was heated under an argon atmosphere, at a rate of 10°C per min. With the first slight indication of decomposition as determined by gas analysis, the sample was removed from the furnace and allowed to cool. X-ray patterns showed no other phase present. It is estimated that less than 0.05 pct of the ZnS04 decomposed. The metal sulfides were also heated under an argon atmosphere to drive off any adsorbed water. The materials were then sized (-200 to +270 mesh), mixed in predetermined mole ratios, and pressed into pellets. The experimental measurement of the reaction rate consisted of purifying the argon carrier gas, continuous flushing of the heated reacting mixture with argon, and collection and analysis of the SOn product gas. The reaction system was heated to 600°C and al-

Jan 1, 1967

By Fred H. Perfect

The thermite process, now approximately 80 years old, has heretofore been practiced in ceramic vessels. This paper outlines the successful production of several million pounds of alloy produced in zuater-cooled copper vessels. THE high temperatures necessary to produce fluid high-alumina slags have probably discouraged earlier workers from attempting to utilize water-cooled vessels. The following is a report of the successful application of this method, together with a report of the physical and chemical problems which had to be solved to make the process practical. About 1955, when Reading Alloys was more concerned with the production of ferrotungsten than with most other types of alloys, it was found to be exceedingly difficult to predict the reaction rate that one would experience from one tungsten ore to another . This difficulty was increased for two reasons: the physical state of the ore as received was seldom uniform, and the size of the mass to be reduced is a very important factor in developing the proper mix for the final reaction rate and temperature. For example, the reduction of ferric oxide with aluminum would theoretically produce temperatures of about 2600°C, and, in spite of the losses due to radiation, the energy is quite sufficient to produce a very fluid slag and iron effecting a very clean separation. On the other hand, the reduction of ferrous oxide with aluminum, while it is not as energetic as the first reaction, nevertheless should give temperatures above 2000"C, which should cause separation of alumina and iron, but, in practice, this is not the case and good fluid slag is not obtained. The heat of reaction, calculated from the thermo-dynamic heats of formation of the constituents of the reaction, offers a convenient guide to the feasibility of a thermite reaction. Thus, the values listed in Table I can be used as an approximate guide for estimating the results which may be expected in the reduction of various oxides and combinations of oxides using aluminum as the reducing agent. As a generalization, those reactions releasing approximately 600 cal per g of total mass represent the lower limit at which to expect separation of slag and metal. On the other hand, those reactions which release 1100 to 1200 cal per g are too violent to be used successfully without the addition of considerable inert material, such as lime, fluorspar, and so forth. Reaction rate is also a very important factor. This, of course, is governed very largely by the sizing and intermingling of the oxidant and reductant and by the starting temperature of the reactants. This is why those figures shown in Table I can only be a general guide. Further, it must be understood, that by adding powerful oxidizing agents, such as nitrates, chlorates or metallic oxides, such as molybdenum trioxide or chromium trioxide, certain problems respecting low temperatures are not necessarily solved. This is true in the addition of oxidants, such as sodium chlorate. By adding too high a concentration of sodium chlorate as a booster for a particular reduction, explosions are generated. Generally, they are of an intermittent type so as to give a Roman Candle effect to the reduction itself; with each surge resulting from a minor explosion more and more material is thrown

Jan 1, 1968

By E. T. Turkdogan, M. T. Hepworth, R. P. Smith

The permeability of oxygen in 0 iron in the tempera-ture range 700" to 900 C and in 6 iron at 1450°C was determined by the rate of internal oxidation of iron, containing -0.1 pct Al. The solubility of oxygen in zone-refined iron was determined by equilibration with hydrogen-water vapor gas mixtures at 1450" and 1510°C; oxygen solubilities , for iron in equi1ibriu.rn with molten oxide, are found to be 66 and 83 ppm for these two temperatures, respectively. The diffusivity of oxygen in iron at 14500C3 as calculated from the permeability and solubility data, is (4.1 * 0.6) x 10 "B sq cm per sec. OXYGEN is one of the most common impurities present in iron or steel, mainly in the form of oxide inclusions. In the study of many metallurgical problems concerning solid iron, it is often desirable to know with a reasonable accuracy the solubility and diffusivity of oxygen over a wide temperature range. The solubility of oxygen in solid iron has been the subject of numerous studies yielding highly discordant results as seen for example from the literature surveys made by Meijering &apos; and Schenck et a1.&apos; As shown by Kitchener et aL3 and by Sifferlen, the high oxygen solubilities reported by many investigators are the result of oxidizable impurities which are often present in iron. In addition, there have been experimental problems associated with icaccuracy of oxygen analysis of iron containing less than 100 ppm 0. A number of studies have been made on the permeability of oxygen in a and y iron using Fe-Si, Fe-Mn, and Fe-A1 alloys in the internal-oxidation experiments.1&apos;2&apos;5&apos;6 However, no direct measurements have been made of the diffusivity of oxygen in iron. In the present work two sets of experimental measurements were made: permeability and solubility studies at 1450" and 1510°C and permeability studies only in the range 700 to 900°C. In both sets of permeability measurements slab-shaped specimens containing small predetermined amounts of aluminum in solution were exposed at constant temperature to gas mixtures of hydrogen, water vapor, and argon for varying times. These specimens were quenched, sectioned, and examined for oxygen penetration by metallographic observation of aluminum oxide particles which formed. From these data, it is possible to calculate the ratio of the diffusivity of oxygen in iron, D, to the equilibrium constant K for the reaction Hz(g) * O (dissolved in iron) = H,O(g). EXPERIMENTAL Permeability Measurements at 1450°C. An ingot of vacuum-carbon deoxidized iron containing 0.086 pct A1 was prepared, using commercial "Type lO4A Plas-tiron"; after hot rolling, specimens were machined into slabs a by 2 by 2 in. The impurity contents were: S, P < 0.002 pct; C, Mn < 0.01 pct; each of all other Usual impurities < 0.004 pet. The amount of oxide inclusions in this material, determined by a bromine-methyl acetate extraction, corresponded to about 20 ppm 0 in the iron which agreed well with the results of vacuum-fusion analysis. Each specimen was annealed at 1450°C for 1 hr in purified hydrogen, polished to a smooth surface, and then introduced into a controlled oxidizing atmosphere in a recrystallized alumina tube at 1450°C. The constant temperature zone (*3"C) was about 3 in. in length. The gas composition was controlled by mixing argon with hydrogen (using calibrated constant-head flow meters) and passing the mixture through a column of a mixture of oxalic acid dihydrate and 10 pct anhydrous oxalic acid, to establish a required water-vapor content in the gas mixture. The temperature of the oxalic acid dihydrate column was controlled by a thermostat. The total gas flow was in the range 800 to 1000 cu cm per min. The exit gas from the reaction tube was passed through a weighing bottle containing a desiccant, to cross-check the degree of water-vapor saturation, which for all experiments was about 97 pct of those derived from the data of Baxter and Lansing.1 For a typical experiment, a specimen was introduced into the furnace in a stream of dry argon and hydrogen. The specimen was then rapidly raised by a Pt-Rh alloy wire into the hot zone and allowed to reach the reaction temperature, at which time the oxidizing gas mixture was introduced. The oxygen potentials employed were sufficient to oxidize aluminum but not to cause liquid iron oxide to form. After a specified time, the experiment was ended by dropping the specimen onto a water-cooled copper block at the bottom of the reaction tube. The depth of the internally oxidized zone, hereafter called the "case", was determined by sectioning the specimen at right angles to the long direction. The section was then examined under a microscope equipped with a micrometer stage. In general, the oxide particles were fairly uniform in size and distribution, forming a reasonably well-defined interface between the oxidized and unoxidized region. A typical cross section as observed at X30 is shown in Fig. 1. A thermal macroetch was used in one selected specimen to delineate the case. A cross section of a previously oxidized slab was polished and reheated at 1450°C in a hydrogen atmosphere for about 10 min. Upon quenching, the surface relief shown in Fig. 2 was produced; causes of this effect are unknown. Permeability Measurements Below 900°C. A slightly

Jan 1, 1967

Jan 1, 1967

Jan 1, 1968

By Harry C. Gatos, Frank J. Bachner

It was shown through high-pressure experiments that tin loss by volatilizatim is necessary for the degrada-tion of the superconducting transition temperature of Nb,Sn associated with high-temperature annealing. Crystallochemical analysis of the degraded Nb3Sn showed that it constitutes a new phase with ordered niobium-site vacancies, created by the migration of niobium atoms to vaccnt tin sites. This new phase was found to form when 4 pct Nb-site vacancies were present. It has a transition temperature of 6&apos;K and a lattice parameter of 5.283A. A similar degradation effect was observed in Nb,Al. Its superconducting transition temperature dropped from 16.5" to 8" K following a high-temperature annealing. The superconducting temperature degradation in these 0-tungsten structure compounds is attributed to the disruption of the interchain d bonding by the periodic interruption of the niobium atom chains. By annealing the degraded Nb, Sn at 1000 C in nitrogen its normal superconducting behavior is restored most likely due to the incorporation of nitrogen atoms causing the elimination of the ordered vacancies. HANAK et al.&apos; have observed low superconducting transition-temperature values (T, - 9"K) in some NbsSn samples deposited from the vapor phase. They attributed such low T, values to disorder in the 0-tung-sten structure. Much lower T values (down to 5.6"K) were reported by Reed et al.zC for NbsSn samples annealed at high temperatures. These authors also attributed this degradation effect to disorder (random occupation of the A and B sites by niobium and tin) but pointed out that such disorder could be brought about (by high-temperature treatment) only in samples containing niobium in excess of the stoichiometric composition NbsSn. Both groups reported that the normal superconductivity behavior could be rever-sibly restored by appropriate heat treatment. Courtney et al., also found that degradation in NbsSn requires excess niobium brought about by the loss of tin during the treatment. However, these investigators proposed that the degradation is due to niobium-site vacancies resulting from the migration of the niobium atoms to the vacated tin atom sites. They did not consider the reversibility of the effect. The present study attempts to establish the nature of the above degradation phenomenon. EXPERIMENTAL PROCEDURES All compounds prepared for this investigation were made from the powders or filings of the elements which were intimately mixed, cold-pressed into a cylindrical pellet at approximately 50,000 lb per sq in., and then submitted to the desired heat treatment. The samples annealed under high pressure were placed in a MgO sample container which was mounted in a pyrophyllite tetrahedron designed for a tetra-hedral-anvil press. Details of the experimental arrangement are given elsewhere. This setup allowed heating at 1800°C or above under pressures in excess of 30kbars for 3 hr. The samples annealed in a vacuum were prepared in a high-temperature vacuum furnace which could reach temperatures up to 2400°C under a pressure of 2 x lo-&apos; Torr. For annealing in a reactive atmosphere, a quartz tube was placed in a clamshell furnace and the desired gas ambient passed through the tube. Lattice parameters were determined using a Debye-Scherer 114.6-mm camera. Cohen&apos;s method, programmed for the IBM 7094 computer, was used to calculate the lattice parameter from the measured d spacings. X-ray integrated intensity measurements were made on several samples. These samples were ground to -400 mesh and the powder mixed with a solution of collodion in amyl acetate. The mixture was poured into a depression milled in a bakelite disc. When the mixture dried, the surface of the disc was ground flat leaving a diffraction surface defined by the face of the disc. The disc was mounted in a Philips rotating specimen holder which allowed the rotation of the sample in the plane of the diffraction surface and the integrated intensity measured using a scintillation counter and a pulse-height analysis sys-tem. The superconducting transition temperatures were determined by means of self-inductance techniques.&apos; EXPERIMENTAL RESULTS AND DISCUSSION The Role of Tin Loss in the Degradation of Super-conductivity. The loss of tin during high-temperature annealing can be effectively suppressed by annealing under high hydrostatic pressures. Accordingly, a series of experiments were performed under pressures of approximately 30kbars. This pressure was the minimum under which high-temperature experiments could be safely performed in the particular pressure apparatus employed. Experiments were also designed to test high-pressure effects on the superconductivity behavior of NbJSn. The results of the high-pressure annealing experi-ments are summarized in Table I. All samples were prepared as described earlier. They were reacted and homogenized at 1000°C for 24 hr under argon at-

Jan 1, 1967

By N. A. Gjostein

The formal descnption of the decay of an isolated scratch can be written in terms of an appropriate Fourier integral. With the application of certain approximations, this description leads to the second-moment analysis developed by King and Mullins. It is shown that the second-moment analysis does not adequately describe the behavior of a decaying, isolated scratch, and that it is difficult to obtain internally consistent values of the surface self-diffusion coefficient, D,,from this analysis. This inconsistency arises from contributions of higher-order moments to the decay process. Two new analytical methods, based on the Fourier integval representation of a scratch profile, have been developed for determining values of D, from the decay kinetics of isolated scratches. In the profile-matching method, a given initial profile is resolved into its Fourier components, the components are allowed to decay exponentially over an annealing time interval, At, and finally they are synthesized to form a decayed profile. The predicted profile is adjusted to fit the experimental profile by varying only the parameter, D,At; the contribution from volume diffusion is directly taken into account and the integrals involved in the Fourier analysis are evaluated by numerical integration on an electronic computer. In the kinetic method, the widths, W, of a series of predicted profiles are determined for various volume-diffusion contributions, and the results are plotted in the form W vs DSAt. For a fixed ratio of surface to volume diffusivities, R, these plots are linear; the slope of the lines increases as R decreases. A simi-lar analysis can be performed on the depths of the predicted profiles. In this case, plots of (l/df3 vs D,At are found to be nonlinear. The proper value of Ds is found by superimposing the data for the experimental widths and depths on Plots of this kind and adjusting Ds until a fit is obtained with the line having the appropriate value oj R. An analysis of the slopes of these plots for R —= (surface diffusion only) reveals that they do not give the correct value, 2276, for width tf second-moment standard profile. This finding allows one to modify the second-moment analysis in such a way as to obtain internally consistent values of Ds. ThERE are several processes, involving a flow of matter along a surface, due to gradients in curvature of the surface, that may be used to determine the surface self-diffusion coefficient, Ds. These processes are commonly known as 1) thermal grooving, 2) single and 3) multiple scratch decay, 4) blunting of field-emitter tips, and 5) sintering. In this series of papers, the first three of these processes are examined in detail in an attempt to subject the phenomenological theories governing these processes to a critical test and, furthermore, to make a critical comparison of the values of D, obtained from these techniques. Although the thermal grooving technique has been established&apos;&apos; as a reliable method for determining D, , this has not been the case for the process of scratch flattening. Mullins and coworkers374 have proposed phenomenological laws governing the growth of the width and the decay of the amplitude of an isolated scratch, but only in one study5 has the width-growth law been supported by experimental evidence. In paper I of this series detailed experimental evidence is presented that points up the deficiencies of the second-moment analysis; the origins of these deficiencies are also discussed. Following this development, some new analytical procedures, based on representing the scratch profile by Fourier integrals, are presented as a means of obtaining reliable values of D, from the kinetics of the scratch-flattening process. Further applications of the Fourier integral approach are reported in papers 11&apos; and 111,~ where the method has been useful in interpreting the anisotropy of flattening rates of isolated scratches (paper 11) and in describing the multiple scratch decay process (paper 111). THEORY OF SCRATCH DECAY Following ~ullins" approach we consider an arbitrarily shaped scratch profile, Fig. 6, at some time, t. The profile is designated by a function z(x,t) which can be expressed in terms of a Fourier integral as follows:

Jan 1, 1967

By A. U. Seybolt

Experiments on both suljidation and hot corrosion have been carried out using ternary Ni-Cr-X alloys and commercial nickel-base superalloys. It has been shown that lhere are certain micro structural similarities between sulfidation using H,S/H2 mixtures and hot corvosion using Na,S04 in "crucible" experiments or hot corrosion tests using a flame tunnel apparatus. It is proposed that two key processes in the hot cowosion process are: 1) formation of chromium sulfides which deplete the alloy matrix, and 2) oxidation which can be accelerated because of chromium depletion. Other processes play an important role in the hot corrosion process, such as accelerated oxidation attack due to the presence of a N& S04 or N&SO,- NaC2 film which inhibits the formation of a protective external oxide scale. However, this latter phenomenon was not studied in this work. THE term hot corrosion has come to mean a combination of sulfur and oxygen attack on nickel-base or cobalt-base superalloys used as gas turbine blades or partitions. This attack can be initiated by any combustion process in air involving fuel containing sulfur if the sulfur level is sufficiently high. Levels of 5 pet SO2l for example, in the combusting gas have been observed to produce hot corrosion attack on nickel-base alloys. The important immediate corroding medium in aircraft gas turbines, however, has been established to be Na2S04, formed from reaction between NaCl from sea air and sulfur in the fuel.&apos; The Na2S04 concentrates the sulfur sufficiently so that superalloy parts heated in the range 1400" to 1900°F can become sulfided by reducing the Na2S04 film which forms on the parts, and this reaction allows sulfur to gain access to the alloy. The sulfur thus released diffuses into the superalloy and forms primarily chromium sulfides of various compositions, but frequently Cr2S, has been identified. Figs. 1 and 2 show the morphology typical of hot corrosion of a cobalt-base superalloy X-45 (25 Cr, 10 Ni, 7.5 W, 0.25 C) and a nickel-base alloy, Udimet 500 (19 Cr, 19 Co, 4 Mo, 3 Ti, 2.9 Al, 0.07 C). Both alloy samples were subjected to the same hot corrosion conditions: 616 hr at 1600°F in a combusted 2.9 pct S distillate oil containing 125 ppm Na as NaC1. It will be noted at once that the nickel-base alloy is much more severely attacked. The depth of corrosion is much greater and the number and size of the sulfides present are much greater. Both alloys show a duplex oxide scale, which is more noticeable in the X-45 alloy. The external scale is probably a spinel in both cases, with CrQ3 lying next to the alloy. Many investigators1 -"ve been concerned with hot corrosion phenomena, but there has been a lack of unanimity of opinion as to the details of the hot corrosion mechanism. More than one definition of hot corrosion is possible. Some investigators con- sider as a measure of hot corrosion only the weight gain due to an accelerated oxidation. However another point of view is that the total depth of affected alloy may be used as a measure. While it is recognized that surface oxidation attack is greatly accelerated by the presence of salts like Na2S04 or Na2S04-NaC1 mixtures, sulfur penetration into the alloy also undoubtedly produces very important effects. The region of sul-fide penetration which is so prominent in Fig. 2 is one of the outstanding characteristics of hot corrosion. For highly stressed parts, such as first-stage buckets, this sulfur-penetrated region can be more significant in mechanical property loss than the reduction of cross section produced by the formation of the massive external scale. In addition, evidence will be presented that this sulfided region can be less resistant to subsequent oxidation attack. Since it appears that the sulfided region below the surface oxide scale plays an important role in the overall corrosion process,

Jan 1, 1969

By R. D. Nelson, S. D. Dahlgren

The conditions of temperature, strain rate, and total strain favoring deformation by grain boundary sliding, slip, or deformation with concurrent recrystallization were evaluated for alpha plutonium. Grain boundary sliding and slip were studied by examining structures formed on polished surfaces with 4.5 pct compressive deformation. The conditions required for recrystallization were determined from compressive deformation us time curves. At 110" C and at a strain rate of 10&apos;per min, deformation was almost exclusively by grain boundary sliding whereas slip was the predominant deformation mode at -10°C and lo-&apos; per min. Defarmation at intermediate tenzperatures and strain rates produced structures showing mixtures of grain boundary sliding and slip. Recrystallization occurred concurrently with deformation only after a critical strain was reached. About 14, 6, and 3 pct strain was required at 105", llO°, and lZO°C, respectively, before recrystallization started, irrespective of the strain rate in the range of lo-&apos;1 to 10&apos;4 per nzin. L HE temperature and strain-rate dependency of the modes of plastic deformation were evaluated for high-purity as-cast alpha plutonium. The techniques used to study slip and grain boundary sliding were similar to those employed previously for alpha plutonium by Bronisz and Gorum,&apos; and spriet.&apos; Recrystallization was investigated using the methods reported by Nelson.3 Bronisz and Gorum&apos; found that slip occurred on more than one slip system at room temperature, and suggested that grain boundary sliding also contributed to the deformation. spriet2 found that deformation was predominantly by slip at room temperature, and observed one to three orientations of slip traces in individual grains. In addition, he deformed polished samples at 10O° C, but concluded that the deformation character of alpha plutonium at 100° C and at room temperature were not essentially different. Several investigators reported that twinning was only occasionally observed.1&apos;2&apos;4 Nelson3 recently found in creep tests that high-purity alpha plutonium would recrystallize concurrently with compressive deformation at temperatures between 25" and 115°C. EXPERIMENTAL PROCEDURE Electrorefined plutonium having less than 300 ppm total impurities was received from Los Alamos Scientific Laboratory in the form of +-in. diarn cast rods. Major impurities were americium, <I00 ppm, and tungsten, (60 ppm. Less than 25 ppm each of other impurities were present. The rods were cut into right half-cylinders 0.35 in. long and 0.25 in. in diam, and the flat faces along the cylinder axes were metal-lographically polished. To avoid loss of the metallo-graphic polish by oxidation, the polished samples were deformed in a silicone fluid heat treating medium contained in a chamber evacuated to a pressure of lo-&apos; torr. Deadweight loading was used to compress the samples between 4.5 and 20 pct at strain rates between 10"4 and lo- &apos; min-&apos;. Strain rates were determined by dividing the total deformation by the elapsed time of the test, even though the strain rate was not constant during deformation. Curves of strain vs time for samples deformed with a constant compressive stress3 show that the strain rate changes by less than a factor of four during the testing of a given sample, which is small compared to the three orders of magnitude change in strain rate investigated. Two samples were loaded into an ordinary metallographic mounting mold and impacted by striking the mold piston with one blow of a 2-lb hammer. Deformation temperatures for the two impact samples were 25" and 90°C. The samples, following deformation, were washed in carbon tetrachloride and their polished and deformed surfaces were immediately inspected metallographi-cally. Subsequently, the deformation structures were replicated with acetate replicating tape for later electron microscope examination, and the samples were then repolished and etched to reveal the microstruc-tures of the deformed metal. Second-stage carbon replicas were prepared from decontaminated acetate replicas using the procedure developed by Miller, Bierlein, and astel.&apos; Additional samples, which were 0.35 in. long by 0.25 in. in diam, were used to obtain constant load deformation vs time curves. These samples were deformed 10 to 20 pct with loads of 15 and 20,000 psi at 120°C; 30, 45, and 55,000 psi at 110°C; and 20 and 30,000 psi at 105°C. Samples were polished and etched to determine whether or not recrystallization or twinning had occurred during deformation. RESULTS AND DISCUSSION The experiments showed that alpha plutonium deforms by grain boundary sliding, slip, and deformation with concurrent recrystallization. Deformation by twinning was insignificant. Metallographic examination of polished and deformed surfaces revealed grain boundary sliding and slip. The start of recrystallization was ascertained from constant load deformation vs time curves. Deformed surface structures of samples compressed 4.5 pct under four different conditions of temperature and strain rate, Fig. 1, show how the deformation mode changes from predominantly grain boundary sliding to predominantly slip with increasing strain rate and decreasing temperature. Deformation at 110°C and 10" 4 min-&apos;, Fig. l(a), was predominantly by grain boundary sliding. Only a few slip traces can be seen in Fig. l(a).

Jan 1, 1969

By Hansheinz Portisch, Harold Margolin

A surface expansion was found to occur sometime after etching in Ti-A1 alloys containing 9.5 to 12.5 wt pct Al. The structure formed, grew, and disappeared with tzrrze. The surface expansion was followed by microscope observations and interferometric and lattice parameter measurements. Activation energy measurements for the growth of the "expansion structure" and chemical analysis indicated that the phenomenon occurred as a result of hydrogen pzckup during etching. It is proposed that hydrogen initially enters octahedral sites of Ti3Al coherent with a Ti and later shifts to the tetrahedral sites. It is postulated that expansion occurs when hydrogen enters the tetrahedral sites. The expansion structure disappeared, it is proposed, because of diffusion of hydrogen from the surface into the body of the alloy and because of loss of coherency of Ti3Al. In examining Ti-A1 alloys, Ence and arolinl observed markings on the surface of specimens. These markings did not appear after electropolishing only, but rather appeared only after etching. The markings appeared to grow as a function of time after etching and later seemed to disappear. Although the markings had some similarity to precipitates, showing, frequently, a Widmanstatten type of arrangement, the observation that other microstructural markings continue to be seen within the new structure suggested that it was actually not a precipitate. The source of this structure was unknown and an attempt was made in the present investigation to develop some understanding of its nature. It has been labeled expansion structure. 1) EXPERIMENTAL PROCEDURE A) Alloys. Alloys in the range 6.5 to 14.5 wt. pct A1 were studied. Bars, 4 in. sq, forged from Bureau of Mines (73 Bhn) titanium consumably arc-melted 4-lb ingots,&apos; as well as 50-g arc-melted buttons of desired aluminum contents were used. The 50-g buttons also used Bureau of Mines titanium (73 Bhn) and aluminum of 99.99 pct purity. Buttons containing up to 8.5 wt pct A1 were hot-rolled from a furnace at 900&apos; . Those with higher aluminum contents were hand-forged on a titanium anvil, and heated with an oxygen-hydrogen torch in the region of 1200" to 1300°c. Frequent reheating kept the samples at the desired temperature range. After a reduction of about 30 pct, the samples were water-quenched. To eliminate any contamination picked up either during hot rolling or forging, at least 1 mil of the surface of the sample was taken off. B) Heat Treatment. Prior to heat treatment all alloys were vacuum-annealed to remove hydrogen. Samples were annealed at 900&apos; until a vacuum of 10&apos;5 mm Hg was established. After this treatment, the samples were wrapped in molybdenum sheet and heat-treated in argon-filled quartz capsules, which were broken under water or iced brine at the conclusion of the heat treatment. All heat treatments under dynamic vacuum were performed in a rapid-quench furnace. This consisted of a molybdenum-lined quartz tube attached to a vacuum system and through a stopcock to a beaker of water. At the completion of the heat treatment the vacuum stopcock was closed, the furnace shut off, and dropped below the quartz tube. Then immediately the inlet stopcock was opened and water admitted until the tube was filled. The steam formed was allowed to escape through the inlet stopcock. This method was used in heat treatments up to llOO°C. C) Metallography. Specimens for metallographic examination were ground, then electropolished using a Disa Electropol machine with a perchloric acid electr01te. Specimens were etched with R-etch.3 A standard etching time of 3 min was used, with the specimen being agitated during immersion. D) Sample Preparation for X-ray Analysis. Samples 0.2 to 0.5 mm in diam were produced from heat-treated rods which were turned to 2 mm diam on a lathe and then rotation-etched. An etchant consisting of 1 pt HF, 7 pt HN03, and 12 pt HzO was satisfactory. With the rod rotating in a vertical position at 50 to 100 rpm, a needle with uniform dimensions could be obtained. Care had to be taken to insure that the rod was at the center of rotation, otherwise cavitation developed. If a small unevenness developed, it was possible to grind it off with a fine emery paper. E) X-ray Diffraction. All X-ray work was done on a North American Phillips X-ray diffraction apparatus and a Jarrell Ash microfocus X-ray unit. The Phillips unit was used with a copper target and nickel filter. The Jarrell Ash unit was fitted with a cobalt target and iron filter. For the Phillips unit 35 kva and 20 ma were used, whereas for the microfocus unit with the 100-p fixed-focus gun 40 kv and 1.5 ma were used. It was found that alignment of cameras on the Jarre11 Ash unit was very critical. The X-ray beam contains an intense area which is not the beam center. The cameras were aligned with the intense region by monitoring the beam coming out of the camera with a Geiger counter. Adjustments were made until a maximum intensity was obtained. A Phillips diffractometer with a Brown chart recorder furnished some of the lattice parameter data. The divergence slit up to 80 deg 28 was I deg; above 80 deg, a 4-deg opening was used, while the scatter slit was1 deg and the receiving slit had a 0.003-in. opening. The general scanning rate was 1 deg per min, while peaks of special interest were rescanned at -j deg per min. For elevated-temperature X-ray diffraction a Uni-cam High Temperature Camera with a film diameter

Jan 1, 1969

By J. Brett, L. Seigle, L. Castleman, T. Montelbano

Impurity-induced low-temperature recrystallization of cold-worked tungsten was inuestigated with emphasis on the influence of nickel on the reaction. Palladium, nickel, aluminum, manganese, platinum, and iron greatly lower the recrystallization temperature of doped tungsten, which zs normally very high, but the recrystallization temperature of electron-be am zone-refined tungsten wzre is slightly raised by conlacl with nickel. Recrystallization can be induced at low temperature by the presence of solid nickel on the surface of doped tungsten wire, but apparently not by exposure to nickel vapors alone. Approximately 200 ppm of Ni dijjused into 10-mil wires at 1200 from a deposit of nickel on the surface produced total recrystallization, whereas more than 600 ppm of Ni could be absorbed frotn a vapor source without altering the fibrous structure of cold-worked tungsten. Once initiated, nickel-induced recrystallization required a continued source of&apos; nickel for propagation of the recrystallization front. The solubility of nickel in fibrous 10-mil W wire was approximalely 500 ppm at 1150&apos; C, and the activation energy for penetration of the recrystallization front was 52 kcal per mole. In many applications the usefulness of tungsten depends on critical control of its structure. Cold-worked tungsten with the fibrous structure developed by suitable thermo-mechanical treatment has a low, but technologically significant, ductility. It has long been known1 that traces of nickel, and perhaps other metals, are profoundly deleterious in doped tungsten, because they induce recrystallization at low temperature, which produces a brittle, equiaxed grain structure. This effect appears to be an exception to the general observation that recrystallization is impeded and the recrystallization temperature raised by the presence of impurities.2"9 Previous studies7-&apos;&apos; of the annealing and recrystallization of tungsten wire have divided the phenomenon into prior recovery stages, primary recrystallization and secondary recrystallization. The present investigation is concerned principally with primary recrystallization which is defined here as the replacement of the fibrous structure of deformed tungsten by equiaxed grains. The objective of this study was to explore the nickel-induced recrystallization reaction in tungsten and attempt to elucidate its mechanism. As well, an effort to define which other elements give rise to low-temperature-induced recrystallization was carried out. EXPERIMENTAL PROCEDURE The procedure adopted for these experiments was essentially to bring nickel and other elements into diffusive contact with cold-worked tungsten wires. The process of recrystallization was followed as a function of time and temperature by light and electron microscopic observations. First the influence of nickel on the recrystallization temperature of arc-melted, zone-refined, and variously doped tungsten wire was determined by electroplating a deposit of nickel on the surface of the wire and annealing at a variety of temperatures for 3 hr. The chemical analyses of the tungsten wires used in this investigation are given in Table I. The surface of the tungsten wire was etched with Murakami&apos;s slution&apos; and approximately 0.005 in, of Ni was deposited from a Watts-type low pH bath14 for the conditions of these experiments. Variations in plating thickness from about 0.001 to 0.005 in. had no discernible influence on the resulting structures. The wires were then annealed in an atmosphere of dry hydrogen to establish the recrystallization temperature. Concurrently, un-plated specimens were annealed to establish the recrystallization characteristics of nickel-free wire. The criterion of recrystallization was that the fibrous structure be completely replaced by equiaxed grains after a 3-hr treatment of temperature. This provided more reproducible results than use of the first recrystallized grain or a fixed proportion of re-crystallized structure as the critical observation. The structures encountered in longitudinal and transverse sections were examined by both light and electron microscopy at magnifications up to X32,000 using parlo-dion-carbon replicas shadowed with platinum for the latter method. Second, the influence of a variety of metals on the recrystallization temperature of 0.010 in. D alumina-silica doped tungsten wire, AW136-64, was determined. The elements were applied by electroplating whenever possible. Alternatively, they were vapor-plated on the tungsten wire and a greater thickness built up by coating with a dispersion of metal powder in nitrocellulose lacquer. Elements not amenable to either of these procedures were merely slurry coated on the tungsten. The recrystallization temperature was determined as above. Third, the nickel-induced recrystallization process in doped wire was studied more closely by electroplating 8 mils of Ni on 65-mil alumina-silica doped tungsten wire, AW153-NS10, and exposing the wire to temperatures of llOO°, 1200°, or 1300°C for various times in a hydrogen atmosphere. A circular recrystallization front, &apos;Onsisting of equiaxed grains, developed at the periphery Of the coated tungsten wire, and the advance of this front into the fibrous interior was studied. These experiments employed relatively coarse 0.065 in. D wire because the 0.010 in. D wire recrystallized too quickly to permit observation of the pene-

Jan 1, 1969

By J. D. Hunt, R. J. McDonald

It is proposed that extensive fluid motion occurs between the dendrites of a Partially solid casting and it is suggested the A segregates in steel castings are a direct result of this motion. The fluid flow arises because of density differences between liquid ahead of the dendrites and the interdendritic liquid. Experiments are described on a model system investigating this fluid motion. The importance of interdendritic fluid flow is discussed with reference to longitudinal segregation. SERIOUS macro segregation is often found in large killed steel ingots. Among the most common segregates are those known as A and V, Fig. 1. The A segregates are arranged over the surface of cones, the wide parts being at the base of the ingot. The A segregates are pencil like in shape and extend from the columnar into the equiaxed region. The V segregates are distributed over inverted cones but have a less well defined shape. They occur at the center of the ingot. Because of the commercial importance of macro inhomogenities these segregates have attracted wide-scale attention. The segregates contain alloying elements and impurities which depress the freezing temperature and are thus the last liquid to freeze. A number of explanations have been proposed to explain their presence. It has been suggested1&apos;&apos; that the segregates are the result of the equiaxed zone growing towards the columnar region together with the interaction of convection within the bulk liquid. It has also been proposed that the segregates are the result of nucleation and rapid growth ahead of the dendritic front.3 Neither of these explanations is completely satisfactory because A segregates are pencil shaped and are not found as continuous cones. In this paper an alternative mechanism is proposed, and experiments are described on a model system to determine whether the mechanism occurs in practice. It is thought that A and V segregates are not peculiar to steels but should occur in many other large castings. Fluid motion within the bulk liquid region of a casting has been extensively discussed. Little attention has been paid to fluid motion within the partially solid regions. The work415 that has been done has been mainly concerned with the fluid motion which results from the volume contraction on freezing. The volume contraction is used to explain various types of macro segregation. The present authors suggest that in many cases the fluid flow resulting from volume contraction will be small compared with that due to other causes. When the columnar region is growing, the liquid still remaining between the dendrites has a much lower temperature near the ingot walls than at the dendrite tips. The composition of the liquid in contact with solid will vary with temperature. The density of the liquid will thus vary both because of changes in temperature and composition. The layers of different density liquid will give rise to a slow but steady liquid flow through the interdendritic regions. If there is no density change with composition, the temperature gradient within the dendritic region should give rise to a downward flow between the dendrites, shown schematically in Fig. 2. When the liquid density changes appreciably with alloy concentration this motion could either be en-

Jan 1, 1970