By David A. Thomas, John F. Peck

Fibrous microstructures and their development have been studied by metallography and by hardness and quantitative metallographic measurements. Thin, curved grains were observed in transverse sections of commercial tungsten wire and were developed in laboratory-drawn iron wire at reductions greater than about 70 pct. The unusual grain shapes are attributed to the nonuniform mode of deformation of the grains associated with the characteristic [I101 preferred orientation that develops in bcc metals during drawing. Transverse sections of heavily swaged iron wire showed a ospiral nebulao structure that appears to result from the elliptical shape of the cross section of the swaging dies and their rotary motion. Hardness and quantitative metallographic results show unusual trends that parallel the changes in microstructure. Other phenomena are considwed in light of the results, including the strength of fine wires of bcc metals, ocylindricalo textures, and the ductility of fibrous tungsten. 1 HE microstructure of tungsten wire in a longitudinal section shows grains highly elongated in the working direction, giving the appearance of a bundle of parallel fibers, Fig. l(a). Wires of tungsten and other bcc metals show a pronounced preferred orientation in which a [I101 direction is parallel to the wire axis.l The microstructure and texture of tungsten develop during warm working (working above room temperature but below the recrystallization temperature) into wire by swaging and drawing. Fibrous tungsten so produced has limited but useful room-temperature ductility, whereas annealed tungsten is brittle at room temperature. During an investigation of the effect of recovery annealing on the substructure of commerical 0.030 in. diam tungsten wire, it was found that transverse sections of the as-received material showed thin, curved grains, Fig. 1(b), instead of the expected equiaxed grains. The fact that Figs. l(a) and (b) show different sections of the same material at the same magnification is at first disconcerting, because the long dimension of the curved grains in the transverse section is several times the average fiber width in the longitudinal section. However, a longitudinal section cuts most of the curved grains across their narrow dimension, giving the appearance of a multitude of narrow fibers. On the other hand, the plane of a longitudinal section occasionally includes a long dimension of a curved grain, resulting in a broad ofibero, such as A in Fig. l(a). EXPERIMENTS AND RESULTS To investigate the origin of fibrous microstructures and particularly the unusual transverse-section structure of tungsten, rods of iron (also bcc) were drawn and swaged in the laboratory. One rod of annealed Ferrovac E was drawn in six steps to a total reduction in area of 87 pct (0.10 to 0.036 in. diam), and a second rod was swaged to the same reduction, using approximately the same reduction steps. Longitudinal and transverse sections of the swaged and drawn iron wires are shown in Fig. 2, for reductions in area of 39, 73, and 87 pct. A fibrous microstructure in longitudinal section is first evident at 73 pct reduction, and it is further developed at 87 pct reduction. The grains in transverse section remain equiaxed until about 73 pct reduction, when they become somewhat elongated and curved. At 87 pct reduction, the drawn wire shows thin, curved grains in the transverse section, similar to those observed in tungsten. The transverse sections of the iron wires swaged 83 and 87 pct reduction in area show the striking ospiral nebulao structure in Fig. 2(d). This struc-

Jan 1, 1962

By M. von Heimendahl, G. Thomas

The microstructure of TD-Ni has been examined by transmission electron microscopy in the extruded, annealed. and deformed states. The tensile properties hove been correlated with the observed microstructures and the results ore com-pared with those obtained from pure nickel. The important conclusions are that the thorin particles in TD-Ni act as strong burriers to dislocntion motion during both deformation (slip) and annealing (climb). During deformation. the dislocations tangle around the particles and a cell structure is devleloped after 10 pct or more strain. The cell size appears to be determined by the spacing of the largest particles and is about five times smaller than that in pure nickel for the same strain. The higher work-hardening rate in TD-Ni compared to nickel is probably due to the more rapid rate of dislocation multiplication in the alloy as a result of dislocation-particle interactions. The Th0,particles inhibit recrystallization and twin growh so that some strengthening may arise from the high density of small annealing twins. THE strengthening of materials due to the presence of a dispersed second phase has been the subject of considerable experimental and theoretical investigation in recent years. One of the newest dispersion-strengthened alloys to be developed is TD-Ni,1 a system of approximately 2 vol pct thoria (ThO2) dispersed in a matrix of commercially pure nickel. This material is fabricated by powder-metallurgical techniques and offers high-temperature stability and useful mechanical properties virtually to the melting point of the base metal. While the mechanical properties of this system have been investigated,2,3 there have been no reports in the literature concerning the microstruc-ture of TD-Ni and its correlation to mechanical properties. This paper describes a transmission electron microscopy investigation of the micro-structure of TD-Ni together with its mechanical properties. The results are compared with the structure and properties of pure nickel.

Jan 1, 1964

By J. J. Pye, J. B. Drew

The surface-diffusion coefficients of Ni63 diffusing on low-index planes of nickel single crystals have been measured over the temperature range from 400° to 1000°C using a precision autoradio-gvaphic technique. The activation energy for sur -face diffusion appears to he the same on the {111}, {110), and (100) planes and amounts to -0.60 ev. This is in good agreement with the value (-0.62 ev) reported for (111) planes obtained by mass-transport techniques. In an earlier paper, the authors have reported self surface-diffusion coefficients on silver.' In that work, a deviation of the diffusion coefficients from linearity in the Arrhenius plot was observed at high temperatures. This effect was attributed to a loss of tracer atoms into the bulk by volume diffusion. The purpose of the present work was to extend the technique developed to the nickel surface-diffusion system up to the point where volume diffusion would come into play. The nickel system especially lends itself to this technique due to the high efficiency of the isotope in darkening the film and the large absorption of the weak radiation (0.063 mev /3- particle of the trapped tracer atoms. The diffusion coefficients and ictivation energy for different orientations on nickel can also be compared with a report published by Blakely and Mykura 2 where a mass-transfer technique was used. This paper reports the self surface diffusion of nickel on the low-index planes over a wide temperature range using a precision autoradiographic technique. EXPERIMENTAL PROCEDURE The experiment is similar to that described in the earlier publication consisting of a radioactive needle as a source resting on a flat, smooth, chemically polished surface annealed in a dynamic dry-hydrogen atmosphere. The needle is held snugly on the surface by a holder fabricated from commercially pure nickel. The point source is made by grinding down a small-diameter nickel rod until a tip of approximately 0.1 mm radius is formed. It is then etched and the needle tip plated with the radioactive isotope Ni63. Nickel single crystals were used whose main impurities were spectrographically determined as Co 0.05, Fe 0.007, C 0.005, and S 0.003 pct. The surfaces, oriented to within 1/2 deg of the low-index planes, were carefully mechanically polished and etched in a 50-30-10-10 hot solution of acetic, nitric, sulfuric, and phosphoric acids giving a smooth polished surface. The crystals were then washed in distilled water and alcohol. Annealing temperatures ranged from 400° to 1000°C with a furnace arrangement in which the crystals could be brought up to temperature in times short compared to diffusing times. The temperature was maintained constant to ±10°C. In the temperature range investigated, the ratio of the surface-diffusion coefficient to the volume-diffusion coefficient (Ds/Du) was 105 or more and the mean bulk-penetration values, calculated from literature values of volume-diffusion coefficients,3 were on the order of 10-5 cm. After the diffusion anneal, the sintered needle is removed, and both the radius of the needle point and spot left on the crystal face are measured. The crystal is then placed on photographic film. Diffusion profiles are obtained by scanning the film with a recording microdensitometer which has a slit width of 10µ. DISCUSSION AND RESULTS The experimental conditions are such that the source strength and needle radius are essentially constant and the time is adjusted such that the mean bulk penetration is small. An exactly analogous heat-flow problem has been considered by Carslaw and Jaeger4 and the solution can be written in integral form as:

Jan 1, 1964

By R. W. Kraft

A back- reflection precession-type X-yay camera for determining the crystallographic orientation of the crystallites of both phases in small areas of thick specimens of polyphase alloys is described ad the geometry, advantages, and limitations of the apparatus are discussed. Metallographic obseg-vations of interfacial angles (or habit planes or growth direction are made on the same specimen so that the crystallographic and metallographzc orientation data call be directly correlated. An example of the application of tile technique to a unidi-~~ectionally solidified CuA12-A1 eutectic specimen is presented. The interfacial planes ad growth directions of each phase were established, and the orientation relationship between the phases was observed and found to be approximately intermediate between two previously reported relationships. The crystallographic interfacial relationship between two solid phases is an important parameter in a variety of metallurgical phenomena because of the energy associated with the interface and because this energy is at least partly associated with the way in which the two space lattices are in contact along the interface. In order to describe the interfacial planes in the crystallites of both phases it is necessary to determine the crystallographic orientation of each phase in a specimen relative to each other, and to directly correlate these data with met-allographic measurements from which the interfacial planes can be determined on the same specimen. The back-reflection Laue technique is the easiest way to determine the orientation of thick single crystals or large grains and the method can be combined with metallographic techniques to provide the necessary data, provided the reflections from each phase can be distinguished from one another. However, if the crystallites are small or of varying orientation or if one or both phases has a unit cell with less than the maximum symmetry, many overlapping and complex Laue patterns are recorded simultaneously and it becomes impractical if not impossible to interpret the photographs. All of these complexities were present in a unidirectionally so- lidified A1-CuA12 eutectic alloy1 for which a crystallographic analysis was desired. Consequently the method described here was developed since no known X-ray or electron diffraction technique had all of the following attributes which were required. 1) Method should yield data from which the crys-tallographic orientation of every crystallite or diffracting unit in the irradiated area can be determined. 2) Method should be adaptable to the study of small areas. Depending upon the degree of preferred orientation in the specimens, it should be possible to obtain reliable data in a reasonable length of time on irradiated areas as small as 1.0 or even 0.1 mm in diam. 3) Method should permit direct correlation of crystallographic data with microscopic orientation data pertaining to crystallite axes, habit, morphology, and growth directions as determined by optical microscopy. 4) method should be such that selected areas of large specimens can be easily studied. Trepanning of a small specimen (such as an electron microscope specimen) from larger specimens was undesirable since it would greatly increase the problem of correlating the crystallographic and microscopic directional data. Requirements 3 and 4 dictated that an X-ray back-reflection pinhole technique should be used on large samples, such as metallographic specimens which had previously been examined and analyzed for their microscopic characteristics. Similarly, requirement 2 could be satisfied by choosing a collimator of appropriately small diameter. Exposure times would not be excessive provided the detector were close enough to the specimen. Because of space limitations film was chosen in preference to a Geiger counter. Requirement 1 was fulfilled by using monochromatic radiation and providing enough additional degrees of freedom in specimen rotation to compensate for Bragg law restrictions on diffracted beams. DESCRIPTION OF APPARATUS The apparatus shown in Fig. 1 consists of a pin-hole collimator, (a), projecting through a rotatable circular film in a holder, (b), which records X-ray reflections in the back-reflection region. The specimen, (c), is mounted on the end of a shaft, (d), which is provided with an adjustment, (e), so that the specimen surface can be placed accurately on

Jan 1, 1962

By J. W. Rutter, K. T. Aust

The temperature dependence of the rate of grain boundary migration was measured in bicrystals of zone-refined lead containing from 20 to less than 1 ppm by wezght of tin. The apparent activation energy in the temperature range from 320" to 200oC is markedly dependent upon the solute tin concentration and upon the orientation relationship of the grains adjacent to the grain boundavy. The quantitative experimental observat~ons are compared with the predictions of various theories of grain boundary migration. In previous work.&apos;?&apos; the mobility of individual grain boundaries was studied as a function of impurity concentration and type of boundary. Grain boundary migration occurred at the expense of dislocation arrays which were introduced into the specimen during solidification. Boundary mobility in zone-refined lead at 300°C was markedly decreased by small additions of tin. 0.004 wt pct being sufficient to decrease the rate of grain boundary migration by a factor of 1000. The mobility of grain boundaries having polar orientation relationships near 38 and 22 deg about <Ill>, and 28 deg about <100>, was much less sensitive to tin concentration in the range studied. As a result, these boundaries have relatively high mobilities. The present paper is a continuation of the above study. Data are now presented on the temperature dependence of the motion of individual grain boundaries in zone-refined lead as a function of solute tin concentration and orientation relationship of adjacent grains at the grain boundary. The experimental observations are compared with the predictions of a number of theories of grain boundary migration3-8 which, prior to the present experimental investigation, could not be critically evaluated. EXPERIMENTAL PROCEDURE The striation or lineage structure of melt-grown single crystals of zone-refined lead, containing various additions of tin, was utilized to provide a driving force for grain boundary migration, as previously described.1,2 Each grain boundary under study separated the striated single crystal from another grain which was introduced by localized plastic deformation and recrystallization of a small region of the sample. The speed of migration of grain boundaries in dilute alloys of tin in zone-refined lead was investigated as a function of 1) tin concentration from < 0.0001 to 0.002 wt pct, 2) temperature in the range of 200" to 320°C, and 3) orientation relationship of the adjacent grains at the grain boundary. The substructure driving energy available for grain boundary migration was estimated to be about 4000 ergs per cu cm, within a factor of two, from specimen to specimen.&apos; The specimen dimensions, and growth and alloying procedures for the preparation of striated single crystals of lead of known tin composition, were as described previously.&apos; Each bicrystal was carefully wrapped in aluminum foil, and annealed in a well-stirred salt bath consisting of 50 pct NaNO2 and 50 pct KNO3, for known periods of time at a series of constant temperatures (*2°C). The grain boundary positions, before and after each anneal, were determined by etching lightly in a solution of 5 pct nitric acid in methyl alcohol, in order to follow the motion of the boundary and determine its rate of migration. Thus, the rate of motion of the grain boundary in a single specimen was measured at various temperatures. The above procedure was carried out for each grain boundary in seventeen different bicrystal specimens.

Jan 1, 1960

By J. H. Westbrook

UNTIL very recently the development of high temperature alloys has been strictly empirical. It is, in fact, a great tribute to the intuition, perseverance, and industry of the practicing metallurgists of this country and abroad that the amazing increases in gas turbine service temperature over the past 15 years have been achieved with so little fundamental knowledge. The result of this development has been the realization of successful but highly complex alloys possessing five, six, or more alloying elements and correspondingly complex microstructures. Within the last few years, considerable effort has been devoted to the identification of the secondary phases in these alloys and to the correlation of the presence or absence of such phases with alloy properties. Little attention, however, has been given the problem of identification of the mechanism (s) by which such phases enhance the properties of the alloy and especially to the assessment of the particular properties of the secondary phase (either in- trinsic or relative to the matrix phase) which are basically responsible for the improvement. Conceivable mechanisms which might apply include dispersion hardening and precipitation hardening. In both cases geometrical factors—particle size, dispersion, volume fraction, etc.—and agglomeration re-

Jan 1, 1958

By R. A. Bosch, F. V. Lenel, G. S. Ansell

RECENTLY, Ansell and aenel&apos; proposed a dislocation model to account for the yielding behavior of dispersion-strengthened alloys. The criterion for yielding used in this model was that yielding occurs when the shear stress due to arrays of piled-up dislocations fractures or plastically deforms the dispersed second-phase particles. Calculations based on this model predict that the yield strength, uysof a dispersion-strengthened alloy containing particles whose geometry permits them to be considered as straight, i.e. not curved, barriers to dislocations follows the relation where and are the shear moduli of the matrix and dispersed phase respectively, b is the Burger vector of a dislocation in the matrix, A is the mean free path between dispersed phase particles and C is a constant. This yield stress, ys, is closely approximated in polycrystalline alloys by the proportional limit. The offset yield stress, uoy, is the yield stress, uys, plus the increase of stress due to strain hardening in the offset strain increment. Previous investigation1 has shown that Eq. [I] describes the yielding behavior of several different dispersion-strengthened alloys as a function of the mean free path between dispersed phase particles at a constant temperature. The purpose of this investigation was to investigate the temperature dependence of the yielding behavior of dispersion-strengthened alloys. The alloys studied, MD2100 and MD5100, are SAP-type alloys containing flake shaped aluminum oxide particles dispersed in a matrix of commercial purity aluminum. The proportional limit and 0.2 pct offset stress of both of these alloys were determined as a function of temperature over the temperature range from -190" to 500 C. All tests were conducted on an Instron tensile testing machine. Stress was measured by means of the Instron load cell. Strain was measured by means of SR-4 strain gages attached to the tensile specimens. Stress sensitivity was 80 psi. Strain sensitivity was 2 x 10F Fig. 1 shows the values received for the proportional limit and 0.2 pct offset yield stress plotted as a function of homologous temperature for both the MD2100 and MD5100 alloys. Inspection of Eq. [I] shows that of the terms which determine the theoretically predicted yield stress, uy,, only the shear moduli have an appreciable temperature dependence. From Eq. [I] the yield stress at any temperature T, UT, may be predicted from the yield stress at any arbitrary reference temperature, in this case 25 OC, u25, by the relation where the subscripts T and 25 refer to the values of the property at test temperature and at 25"C, respectively. The temperature dependence of the yield stress predicted by Eq. 121, based on the observed value for the proportional limit at 25OC, is also shown in Fig. 1. In evaluating Eq. [2] the following data was used. The values for the shear modulus of

Jan 1, 1962

By W. G. Pfann

Under certain conditions, a molten zone can be made to move through a solid by impressing a stationary temperature gradient across the solid. This phenomenon can be utilized in fabricating semiconductive devices, growing single crystals, joining, boring fine holes in solids, measuring diffusivities in liquids, small scale alloying, and purification. Fundamentals and exemplary applications are outlined. ANEW aspect of the travel of a molten zone through a solid is considered in this paper. Whereas, in previously described zone melting techniques,&apos;-&apos; zones were usually caused to move by changing the position or temperature of a heat source, in the present technique a zone is made to move by impressing a temperature gradient across it. For example, a thin layer of molten A1-Si alloy, sandwiched between two silicon slabs having a temperature gradient normal to the layer, will travel through the hotter slab. One feature of temperature gradient zone melting, as this technique will be called here, is that zones of unusually small dimensions can be maintained. This leads to such diverse uses as have been listed in the abstract. In this paper fundamentals of the movement of a molten zone in a temperature gradient, and some practical applications thereof, are outlined. Assumptions The movement of a molten zone through a solid body of solvent substance in which a temperature gradient exists will be discussed. The length of the zone will be its dimension in the direction of motion. The direction of the temperature gradient will be toward the region of higher temperature. To be considered is a binary or higher order solute-solvent system in which the concentration of solute in the molten zone is sufficient to produce a lowering of the freezing temperature of the solvent which is at least of the order of the temperature range impressed on the charge. While we discuss primarily molten zones in a solid matrix, the principles are applicable to solid or vaporous zones in a solid matrix, a requirement being that the diffusivity in the zone be substantially greater than in the matrix. Diffusion of solute into the surrounding solid will be assumed negligible. In general, its presence will not basically alter the conclusions to be drawn. For illustration, a system represented by the partial constitutional diagram of Fig. la will be discussed, in which k, the distribution coefficient defined in the figure, is constant and less than unity. However, the technique is applicable to any solute- solvent system in which one component lowers the melting point of another component. Movement of a Molten Zone in a Temperature Gradient Consider, in the system AB of Fig. 1, where B is designated the solute and A the solvent, the effect of sandwiching a thin layer of solid B between blocks of solid A and placing the whole in a temperature gradient such that the temperature of the layer is above the lowest melting temperature of the system. Surrounded by an excess of A, the layer will dissolve A, becoming molten, and expand in length." As so- lution of A continues, at both interfaces, the mean solute concentration in the zone will move to the right in Fig. la, until at temperature T, the liquid at the cooler interface reaches the liquidus concentration C,. Solution of A thereupon ceases because the liquid T1 is saturated with A. The liquid at the hotter end of the zone, being at temperature T2, is not saturated with A at concentration C1. Hence solution of A continues there and concentration C2 is approached. A concentration gradient therefore is set up in the zone, causing A to diffuse toward the cool end and B toward the hot end. As a result, the liquid at the cool interface becomes supersaturated and a layer of crystalline A containing concentration kc, of B in solid solution freezes. Since a source of A

Jan 1, 1956

By John Nunes, Frank R. Larson

Temperature-dependent functions of various ten-sile flour stress and fracture parameters were investigated on iron and low composition alloys of Fe-C, Fe-Cr, Fe-Mn, and Fe-Ni. Data were obtained over a range of test temperatures from 200" to -196"C at an initial strain rate of 0.01 min". It was found that the strain-hardening exponent, n, for the Fe-Ni alloys increased significantly at very low testing temperatures with increased alloy addition. Also, the stress and strain at fracture followed a predictable transitional type of behavior. The flour stress-temperature dependence was evaluated employing the relation: M where it is shown that composition can strongly influence the constant M. An empirical formula describing this effect is as follows: M = MI (equivalent at. pct Ni)-&apos;" Some preliminay, tests were run on several commercial steels to test the generality of this relationship. One of the phenomenological explanations of the ductile-to-brittle transition encountered in bcc metals is based upon the difference in the temperature dependence of the flow and fracture stresses.&apos; It states simply that the fracture stress is relatively insensitive to temperature and that the yield or flow stress rises rapidly with decreasing temperature so that, when the flow stress reaches the fracture stress, brittle fracture occurs without appreciable plastic deformation. This behavior is illustrated schematically in Fig. 1 where the ductile-to-brittle transition is shown to occur at two possible temperatures. The lowest temperature, TB, represents essentially completely brittle behavior while the higher temperature, TN, represents "notch" brittle behavior. Support for this theory is obtained when it is observed that fcc metals, which do not commonly have a ductile-to-brittle transition, also do not commonly exhibit any strong temperature de- pendence of the yield stress. This relationship of yield or flow stress behavior with the ductile-to-brittle transition has been generally observed for most metals representative of these two crystallo-graphic structures. One exception to this generalization appears in the case of tantalum where no apparent ductile-to-brittle transition has been observed. However, this may simply be an indication that this type of behavior is not directly related to the flow stress and that some other mechanism such as twinning must also be operative. A comparison of the typical temperature dependence of the yield stress of some representative metals is shown in Fig. 2. In the study of the temperature dependence of the strength of metallic materials, considerable ef-

Jan 1, 1963

By R. L. Smith, J. L. Rutherford

ALTHOUGH considerable effort has been devoted toward the determination of the mechanical properties of pure metals, it is extremely difficult to compare the results of such work. This is because of differences in method and type of test, grain size, heat treatment, and purity of material. There is very little information on the properties of most of the high melting point reactive metals with purities greater than 99.9 pct. Previous evidence concerning the tensile properties of unalloyed metals show that: body-centered-cubic metals are brittle at low temperatures; face-centered-cubic metals remain ductile; some hexagonal metals remain ductile, others become brittle. It may be that traces of impurities decrease the low temperature ductility of the body-centered-cubic lattice. This would suppose that a body-centered-cubic lattice free from impurities would exhibit nearly the same ductility as a face-centered-cubic structure. The present investigation has been an evaluation of the tensile properties of zone refined iron in order to determine whether higher purity material than that previously evaluated behaves differently. Experimental Procedure In this investigation, high purity iron was zone purified using the floating zone method.&apos; The starting stock was obtained from two sources. The first,

Jan 1, 1958

By S. R. Goodman, Hsun Hu

The rolling texture transition in copper as a function of deformation temperature is found to be quite similar to that in high-purity silver. The ordinary copper type texture changes gradually to the brass type, accompanied by an increase in the stacking fault frequency, as the temperature of deformation decreases. The rolling textures obtained at low temperatures and the corresponding annealing textures compare remarkably well with the ordinary rolling and annealing textures of low-zinc brasses. Furthermore, it is also found that the observed stacking fault energies of copper specimens deformed at low temperatures correspond closely with those of low-zinc brasses, as deduced from measurements of the dislocation nodes. These results are consistent with the idea that texture transition may be significantly dependent on the stacking fault energy. It was shown in a series of previous publications1"3 that the rolling texture of high-purity silver changes gradually from the common silver type (or the brass type) to the copper type* with increasing temperature *The silver or brass type rolling textures are commonly described as (110)[112],4,5 whereas the copper type rolling textures are mainly (123) [a121 and (146)[211].5 Other ideal orientations have been used by various investigators for the copper type rolling textures, but the actual difference among these ideal orientations is rather small. of deformation, and that such texture transition can be correlated with the change in stacking fault frequency as a function of rolling temperature. Furthermore, it was shown that the formation of annealing textures in high-purity silver from the various rolling textures obtained during the course of texture transition depends entirely upon the deformation texture. From a common silver type or brass type rolling texture (such as produced by rolling at 0" or at 50° C) the recrystallization texture is mainly (120)[211], which is quite different from the recrystallization texture of brass.* However, for both ma- terials the orientation relationship between the rolling texture and the recrystallization texture can be expressed in terms of similar rotations around [Ill.] axes of approximately 30 or 35 deg. They differ in that the [Ill] rotational axes are different. In the case of high-purity silver, the axes of rotation are the two (111) poles near the plane normal of the deformed specimen with a (11l)[112] type rolling texture, whereas in brass, they are the (111) poles near the direction of rolling. For high-purity silver with a predominantly copper type rolling texture (such as produced by rolling at 150° or 200°C) the recrystallization texture is mainly (100)[001], or the cube texture, plus its twin orientations. It was shown previously6 that such reorientation observed in copper or aluminum can be described as [Ill] rotations of 30 to 40 deg. For intermediate cases, i.e., when the rolling textures are composed of a

Jan 1, 1963

By A. R. Kaufman, P. Gordon

THE large-scale manufacture and use of uranium in conjunction with the atomic energy development during the war led to a need for knowing the equilibrium diagrams of uranium with various other metals. The alloys of uranium with aluminum and with iron were among the first that were studied for this purpose. Much of the work was done in the manner of a survey since it was necessary to determine the important features of the phase diagrams rather than to obtain completely detailed results. For this reason no attempt was made to locate exactly such features as liquidus lines, solid solubility limits and compound and eutectic compositions. It is believed, however, that there are no great inaccuracies in the diagrams reported here and that no important points were overlooked. Earlier work on alloys of uranium with aluminum and iron is almost nonexistent and in each case is considered to have been of little value by M. Hansen. It is interesting to note, however, that the compound UAl3 was first reported in 1902 by L. Guillet. Experimental Procedure Materials: The uranium used for making most of the aluminum alloys was obtained from material prepared by Metal Hydrides, Inc., and melted in vacuum at M.I.T. Because of the lack of an adequate supply of metal, it was necessary to use material from several different batches and hence it is impossible to state an exact analysis. However, a few results indicated about 0.01 to 0.03 pct iron and probably about 0.03 to 0.05 pct carbon. Toward the end of the work a small amount of metal was obtained from Brown University and from Iowa State College and this was used in determining the transformations in pure metal and in some dilute alloys. All of the aluminum used in this investigation came from a supply of high purity metal (greater than 99.9 pct aluminum) which was obtained through the courtesy of Dr. Mehl of the Carnegie Institute of Technology. The uranium used for making the alloys with iron was produced by the bomb reduction process which has been described by J. Chipman.² This metal, after vacuum melting, contained about 99.9 pct uranium by weight with carbon and iron as the chief impurities. Electrolytic iron containing about 0.012 pct carbon, 0.020 pct nickel and 0.009 pct copper was used in making the melts. Melting Equipment: The melting of the alloys went through a stage of development which culminated in the use of beryllia or beryllia-lined crucibles and in the use of high frequency heating in either vacuum or in an atmosphere of argon. It was found that uranium at a few hundred degrees above its melting point would pick up aluminum and to a lesser extent silicon from an alundum thimble while aluminum above 1000°C would extract silicon from the impure alundum. No reaction of either metal with beryllia was noted at temperatures as high as 1800°C. The distillation of aluminum from the aluminum-rich alloys was quite troublesome at temperatures above about 1300°C and was only partially avoided by the use of argon instead of vacuum. Melting in resistance furnaces,

Jan 1, 1951

By Nicholas J. Grant, William H. Ferguson, Bill C. Giessen

Ta-lr alloys have been examined over the complete range of compositions using metallographic and X-ray techniques. The terminal solid-solubility limits, solidus temperatures, and intermediate phases were determined. There are four inter-mediate phases: o, tetragonal, analogous to a (Fe-Cr); 0,. orthorhombic; az, tetragonal; and a TaZr,, cubic, AuCu, structure. Of these, o and a, melt peritecticaLly, a, decomposes peritectoidally, and a TaIrs has a congruent melting point. Three peri-tectic and one eutectic reactions occur. 1 HE Ta-Ir phase diagram has not been treated in the literature. Intermetallic phases and terminal solid solubilities have been described and estimated.&apos;-4 The previous findings have been confirmed in this work. A complete diagram with additional phases and solidus curves is presented. EXPERIMENTAL METHODS Starting materials were tantalum powder of 99.8 pct purity, supplied by the National Research Corp., Cambridge, Mass., and iridium powder of 99.9 pct purity, supplied by the Bishop Co., Malvern, Pa. Both powders were -200 mesh. Table I lists the analyses as given by the suppliers. A standard procedure was employed in making the alloy buttons, which was described in detail in Refs. 5 and 6, and which included repeated arc-melting of powder compacts and determination of the composition by the weight-balance method. This is especially justifiable due to the similar vapor pressures of tantalum and iridium. In the critical parts of the diagram, a spacing of 1/2 at. pct was used, based on premelted master alloy material. The observed structures and X-ray spectra were consistent with the composition sequence of the alloys. Table II lists the final alloy atomic percentages with the calculated percent error of composition. Cross sections representative in grain size and composition were selected for the study, as described in Ref. 5. Based on prior experience, no contamination from the tungsten electrode was considered. Temperature measurements were obtained using a Leeds and Northrup optical pyrometer and have been described extensively in Refs. 5 and 6. All heat treatments were made in the high-vacuum tantalum tube furnace mentioned in Ref. 5. Samples annealed in tantalum containers cooled from 1800" to 1000"~ in 5 sec; those annealed in ceramic crucibles cooled over the same range in 15 to 30 sec. The thermal treatments are listed in Table 111. All specimens were homogenized at 1735°C for 24 hr. Tantalum-rich compositions were treated in tantalum buckets. Iridium-rich compositions were annealed in tantalum buckets below the eutectic temperature of 1950°C; up to 2200°C, tungsten-lined tantalum baskets were used; and above 2200°C thoria crucibles were used. It was found that refractory oxides (in early stages of the investigation alumina crucibles were used up to 1800°C and thoria crucibles were used to 2400"~) give off minute amounts of oxygen and thereby influence the microstructure considerably, or react directly with the alloys.

Jan 1, 1963

By E. J. Rapperport, M. F. Smith

A presentation of the W-Ru constitution diagram is given. Techniques utilized in the determination of phase boundary values include electron micro-probe analysis of two-phased alloys and diffusion couples, as well as normal metallographic and X-ray methods. The primary features of the diagram are: 1) a terminal solid solution of ruthenium in tungsten with a maximum solubility of 23 at. pct Ru at 2300°C; 2) a terminal solid solution of tungsten in ruthenium with a maximum solubility of 48 at. pct W at 2205°C; 3) a o phase of maximum breadth about 6 at. pct based on the composition W3Ru2 which forms peritectically from the melt at 2300°C, and which decomposes eutectoidally at 1667 °C to form a twigs ten and 0 ruthenium; 4) a eutectic at 45 at. pct Ru and 2205°C with the products being o plus ß ruthenium. THE W-Ru diagram has previously been studied only in a cursory fashion. Raub and alter&apos; obtained a 1400°C isotherm in which they observed no intermediate phases, and on which they established the limits of solubility as 36.5 at. pct W in ruthenium and about 1.5 at. pct Ru in tungsten. In addition, Obrowski2 found a o phase forming peritectically from the melt and existing only above 1650°C. Below this temperature the phase was presumed to decompose eutectoidally. The present work finds the diagram as given in Fig. 1. I) EXPERIMENTAL PROCEDURE The materials used for alloy preparation in determining the W-Ru constitution diagram were 99.9 pct pure ruthenium powder supplied by Baker Chemical Co., and 99.9 pct pure tungsten powder from General Electric Co. Typical analyses of these elements are given in Table I. Initial alloys at 10 at. pct intervals were prepared from the metal powders by the following method. Powders sufficient for 25 g of the alloys were weighed out with an accuracy of 0.1 mg and blended mechanically. After blending, the powders were compacted, in a steel die, at approximately 30,000 psi. The compacts were sintered in an electric vacuum furnace in order to remove adsorbed gases and to achieve partial densification prior to arc-melting. Vacua of 10-4 mm Hg or less were maintained in sintering as the furnace temperature was raised to approximately 2000°C. Sintering times ranged from 10 to 20 hr. The sintered compacts were arc-melted under a protective atmosphere of purified helium. Melting was conducted on a water-cooled copper hearth, utilizing a nonconsumable tungsten electrode. In the melting process, each alloy was turned over and re-melted on opposite sides from four to six times to ensure complete melting and to eliminate gross in-homogeneities. The arc-melter used had a vacuum capability of 5 X 10-6 mm Hg, and a leak rate of about 20 -liters per hr. Chemical analysis techniques for refractory metal-platinum group metal combinations are not well-established; therefore, composition control and determination depended principally upon weight-loss observations and calculations. This consisted in weighing each alloy after sintering and after arc-melting, and calculating the maximum and minimum composition values, assuming the total weight losses to be first all tungsten, and then all ruthenium. Since composition uncertainty was directly related to weight loss, care was taken to minimize losses in handling, compacting, and melting. Prior to homogenization and equilibration the as-arc-melted alloys were analyzed in several

Jan 1, 1964

By J. W. H. Clare

An equilibrium isotherm at 550°C is given for ternary alloys rich in aluminum containing 0 to 15 wt pct Cr and 0 to 20 wt pct Mn. Phases encountered are: aluminum solid solution; stable temary compound G; and MnAl8,. In addition, a limited number of alloys were annealed at 450°C to check for differences from the 550°C isotherm. These experiments limited the composition of the G phase at 550°C and further experiments established that the G Dhase is not stable above 590 ± 1 °C. RAYNOR and Little1 established several equilibrium isotherms using aluminum-rich alloys containing up to 5 pct of the elements chromium and manganese. These isotherms showed that, in addition to an a solid solution and the two binary intermediate compounds 8 and MnAl6, a stable ternary compound ex-isted in the system. This phase was called the G phase because of its ghostly appearance in micro-sections. Little, Raynor, and Hume-Rothery2 found a similar phase in binary aluminum-manganese alloys and, as a result of their experiments, concluded that the G phase was a metastable phase existing in the aluminum-manganese system. This phase was stabilized by the addition of chromium. The constitutional work of Raynor and Little,&apos; although showing the existence of the G phase in the aluminum-chromium-manganese system, did not establish precisely the composition limits of the phase or the temperature above which the phase became unstable and disappeared from the system. The work described in this paper was undertaken to provide this information. An examination of the previous work&apos; showed that an isotherm at 550°C would provide the required data regarding composition in the shortest possible time, as the (a + G) phase field narrows considerably at higher temperatures. The same work showed that the G phase ceased to exist between 580° and 595°C. A more precise estimate of the transformation temperature would therefore be obtained by annealing selected alloys at successively higher temperatures beginning at 580°C. EXPERIMENTAL PROCEDURE 1) Materials Used—The experimental alloys were prepared from four master alloys containing 15.00 w pct Cr, 15.28 wt pct Cr, 19.80 wt pct Mn, and 19.38 wt pct Mn which were made from super-purity aluminum, electrolytic chromium, and electrolytic manganese. The aluminum was of 99.996 pct purity, the principal impurities being copper, iron, and silicon. The chromium and manganese were 99.9 pct pure, the principal impurities being antimony, calcium, and magnesium. 2) Preparation of the Experimental Alloys—The alloys were prepared in 20-g quantities by melting together the requisite amounts of master alloy and aluminum in an alumina-lined crucible and, after thorough stirring with an alumina rod, cast into a cold copper mold to give ingots 1/4 in. in diam and 3 in. in length.

Jan 1, 1960

By A. A. Bauer, M. S. Farkas, F. A. Rough

An investigation of the d-phase relationships between the uranium-zirconium and uranium-molybdenum systems was conducted. A ternary cut joining U-31.5 at. pct Mo to U-74 at. pct Zr is presented on the basis of differential thermal analysis, metallographic and X-ray diffraction data. HyDothetical isothermal ternary sections, inferred from the determined d-phase relationships, are presented for the uraniztm-zirconium-molybdenum system. A ternary eutectoid, at 454ºC, was found in zirconium-rich alloys. Its composition, based on metallography and electron-beam micro-analysis, is estimated as U-61.7 at. pct Zr-7.1 at. pct Mo. URANIUM binary systems have been studied extensively in the past to supply basic information needed in reactor-fuel development. Alloys of uranium with zirconium, molybdenum, and titanium are of particular interest because, in these binaries, extensive or complete solid solubility between the body-centered-cubic forms of these elements and y uranium exists. In addition, an intermediate phase of limited solid solubility forms in each of these systems by transformation of the high-temperature ?-uranium phase. Previous investigation of the phase relationships existing between the intermediate 6 phases in the uranium-zirconium-titanium and the uranium-molyb- denum-titanium ternaries have already been reported.1,2 The results of an investigation of the phase relationships existing between the 6 phases in the uranium-zirconium-molybdenum system is reported here. The phase equilibria that occur in the solid-state portions of the pertinent binary systems are shown in Fig. 1. Phase nomenclature appearing throughout the report is as shown in these diagrams. The crystal structure of the phases in this system are given in Table I. EXPERIMENTAL PROCEDURES Alloys were cast and fabricated to 1/4-in.-diam rod. Specimens were heat treated and examined by metallographic and X-ray techniques. Thermal-analysis data were obtained.

Jan 1, 1960

By D. Harker, E. Epremian

The constitution of the nickel-tungsten system has been studied by a number of investigators, the most recent of which are Ellinger and Sykes.1 On the basis of metallography, electrical resistivity and hardness measurements and some X ray diffraction work, they constructed a consitution diagram (Fig 1). Ellinger and Sykes report a0 for the alpha face-centered cubic phase (nickel saturated with tungsten) as 3.66?.‡ The gamma phase (tungsten saturated with nickel) is given as body-centered cubic, but no value of a. is recorded. At 43 pct tungsten by weight (approximately 20 at. pct) a beta phase is reported, but structure and lattice parameter are not known. Primarily on the basis of metallographic evidence, they conclude that beta is a new phase and rule out the possibility of formation of a superlattice since they- observe a new phase in the microstructure. Grube and Schlecht2 report an ordering reaction in a system similar to the Ni-W (Ni-Mo) and Harker3 has shown that NirMo forms a superlattice upon the pre-existing face-centered cubic lattice of the alpha phase. Elliniger arid Sykes observed a change in the diffraction pattern of a 4.3 pct W alloy upon aging and attributed it to the formation of a new phase. Thus, there appears to be some question as to the character of the beta phase reported by Ellinger and Sykes. The purpose of the present work is to determine precisely the structure and nature of the beta phase in the Ni-w system of X ray diffraction methods. Experimental Procedure One inch diameter ingots of 43.66 pct, 40.15 pct and 34.06 pct .tungsten by weight (19.8, 17.6 and 14.1 at. pct respectively) were melted and cast under vacuum from electrolytic nickel and pure wire filament grade tungsten. The ingots were soaked for 16 hr at 1300°C in a hydrogen atmosphere furnace, then swaged at this temperature and finally drawn to 0.020 in. diam wire. Some of the bar stock was retained in 1/2 in. diam rod for hardness and metallographic studies. Wire samples for diffraction work were sealed in evacuated quartz tubes and subjected to the various solution and aging heat treatments in a hydrogen furnace. X ray photograms were taken in a Debeye-Slierrer camera using copper K radiation filtered by nickel foil. Results X RAY DIFFRACTION The lattice parameters of the alpha and gamma phases at saturation were determined by an X ray photogram of the 19.8 at. pct W alloy after solution heat treatment at a temperature well within the alpha-gamma range above the peritectoid temperature (17 hr at 1150°C—oil quenched). The alpha phase was found to be face-centeted cubic with a. of 3.594 ± 0.001?, while the gamma phase was determined as body-centered cubic with a. of 3.158 ± 0.001?. Exactly the same phases and parameters were ohtained with the 17.6 at. pct W alloy for the same solution heat treatment. Thorough analysis was made of an X ray photogram of a 19.8 at. pct alloy sample in the quenched and aged condition (solution treated 1T hr at

Jan 1, 1950

By R. E. Morgan, D. L. Douglass

The determination of phase relationships and solid-solubility limits can be performed by quantitative metallography in addition to the usual X-ray and metallographic techniques. For example, Beck and smith1 redetermined the ß/ß + ?, ß + ?/?, a/a + ß and a + ß/ß boundaries in the Cu-Zn system by measuring the volume fraction of second phase of several alloys and extrapolating the volume fraction-composition curves to 0 and 100 pct. A modification of this technique is suggested for certain alloy systems, in which it is not necessary to use several alloy compositions but merely one. A single two-phase alloy may be used to determine terminal solubilities in the following manner. The method consists of equilibrating samples of the alloy in a two-phase region adjacent to the desired solid solution, at three or more temperatures, quenching, measuring the volume fraction of second phase present, and applying an analytical treatment to calculate the unknown solid solution. However, two restrictions are inherent in this technique. They are: 1) only certain types of alloy systems are amenable to it, and 2) the general features of the system must be known. The first drawback to the new technique, i.e., that only certain types of systems may be studied, necessitates that the composition at one end of the tieline must either be constant with temperature or well established as a function of temperature. Either a pure metal or some intermetallic compounds fulfill the former. If it is assumed that the volume per gram-atom of a dilute solution is unchanged by the addition of element B to element A, the composition of the solid solution in equilibrium with the second phase may be determined by a material balance and is given by where X, = volume fraction of B in a solid solution Xc = volume fraction of B in compound c X = volume fraction of B in alloy f = volume fraction of second phase The composition by weight may then be determined by the use of tables in the Metals Handbook2 when the density ratio of the solid solution constituents is known. A possible alternative treatment involving the use of the lever rule is less precise than the above tech- nique. This may be used when the density of the solid solution is either known or may be calculated from X-ray data for several compositions. The following analysis is then made. The ratio of compound to solid solution (by weight) may be expressed as follows: x0 - x wc = xr-x = x0 - x r2i Xc -X where Wc = weight of compound w = weight of solid solution x, - alloy composition, weight percent x = unknown composition Xe = compound composition but where V, = volume of compound VA = volume of solid solution pc = density of compound p, = density of solid solution fc = volume fraction of compound fB = volume fraction of solid solution and fs = l -fc then If pc and xc are known, and f, is measured, then pB is the only unknown on the right side of Eq. [4]. The known densities of the solid solution can be plotted for various compositions and can then be expressed mathematically as a function of composition. The use of an expression of pB = f(x)reduces the equation to one unknown—the desired solubility. In the event that the densities are unknown, they may be calculated for various compositions from Vegard&apos;s law. The calculated values are then plotted and expressed analytically. The most accurate results are obtained for Eq. [4] when fc<< 1, i.c., when (x, -x,) - 0, &/l-f, - m; but as fc/l -fc - 0, (xl-x,)- (x, - x), and x - x,,. However, the accuracy with which fc can be measured decreases as f, decreases.3 Alloys for investigation must be selected by a compromise, which is based upon an error analysis of Eq. [4] and knowledge of the accuracy of volume fraction measurements. An examination of phase diagrams in the literature showed many which were amenable to the technique described here. The zirconium-copper system was selected in order to determine the solubility of copper in beta zirconium. Pieces of an alloy which was arc-melted three times were wrapped in tantalum foil and sealed under an argon atmosphere in Vycor tubes. The sealed samples were equilibrated at temperatures from 850" to 960°C for 3 weeks and quenched to room temperature by smashing the capsule in water. Several planes of polish were examined, and

Jan 1, 1960

By E. G. Schempp, W. A. Morgan

The influence of modifications in the molybdenum, vanadium and, to a limited degree, carbon and boron content to a basic composition of 5 pct Cr, 0.75 pct Mo, 1 pct V hot-work tool steel composition, was studied in respect to hardenability, grpain- coarsening temperature, and tempering charactevistics. Tensile, impact, and fatigue pvoperties were studied for the most promising compositions. An alloy with a typical composition of 0.43 pct C, 4.97 pct CI-, 0.33 pct Si, 2.25 pct Mo, and 1.00 pct V uas found to offer the most favorable combination of properties in respect to high-strength applicntions when tempered at 1100°F. MANY 5 pct Cr high-strength steels are at present being manufactured in North America which fit well into the classification of the AISI-SAE system. Much interest has been shown in these materials as ultra-high-strength steels for use at elevated temperatures. The limiting temperature of use lies at the point where the steels begin to soften rapidly. Although a great deal of information has been made available in the past two years on the properties of selected alloys in this series, little information exists on the effect of systematically varying the ccntent of one or more elements in the 5 pct Cr-base alloy. This paper presents the results of an investigation of the effect of variations of the carbon, molybdenum, vanadium, and, to a limited extent, the silicon, manganese, boron, and niobium content of a 5 pct Cr steel to the AISI H-13 base analysis. EXPERIMENTAL PROCEDURE All experimental heats were melted in a 50-lb. induction furnace. The melting stock consisted of

Jan 1, 1962

By H. E. Biber

DURING the production of tin plate a thin layer of FeSn2, is formed at the interface between the steel sheet and the protective tin coating. Because excessive amounts of this alloy layer are undesirable, the kinetics of its formation is a subject of interest in the tin-plate industry. A recent study of this subject at our laboratory uncovered a relationship which should be of general interest to anyone studying kinetics of reactions in metallic systems. It had been previously concluded that, at any given temperature in the range 175" to 330°C, the Fe-Sn alloy layer would have a parabolic growth rate.1,2 However, our studies showed that this rule apparently holds only when the tin plate is heated very slowly to the "reaction" temperature; when the tin plate is rapidly heated, considerably different growth rates occur. An example of this effect of heating rate on growth behavior is contained in the accompanying results of alloy-layer growth measurements at 240°C in oil baths stirred at 10,500, 1800, and 0 rpm. The heating curves for these three conditions are given in Fig. 1, and the growth data are presented in Fig. 2. With the rapid heating rate, provided by the stirring at 10,500 rpm, the alloy layer had three distinct stages of growth. In the initial stage, which persisted well beyond the time required to heat the tin plate to bath temperature, the alloy layer formed very rapidly. The growth followed a rate law of the form w = ktn where n > 1. This initial stage was followed by a growth-retardation stage of about 50-sec duration in which little additional alloy was formed. In the third stage the growth again followed a rate law of the form w = ktn, but here « =0.3. With the intermediate heating rate provided by stirring at 1800 rpm, the three-stage nature was less pronounced and the slope of the third stage increased (i.e., n > 0.3). With the slow heating rate provided by the unstirred oil bath, the alloy layer grew in two stages. The initial rapid-growth stage persisted only until the specimen was heated to bath temperature, no growth retardation was observed, and the slope of the main portion of the plotted data was greater than in the stirred baths, having a value of almost 0.5. Similar results were obtained for other bath temperatures in the range 200" to 300°C. This effect of heating rate on growth behavior may be due to changes in the rate of nucleation of FeSn, crystallites. The iron and tin are in contact from the onset of heating. Thus the initial formation of FeSn, occurs not at the "reaction" temperature but rather while the tin plate is being heated to that temperature. Because nucleation is in general temperature-dependent, different heating rates could cause different over-all nucleation rates, which in turn could cause different growth behaviors. A more detailed discussion of the growth of Fe-Sn alloy layer and the effect of heating rate will be published shortly.

Jan 1, 1965