Search Documents

By A. J. McEvily, R. C. Boettner, C. Laird

The processes leading to fatigue failure in the low-cycle range were studied to obtain an understanding of the basis of Coffin's law. Particular attention was paid to the manner of mack nucleation and to the determination of the portion of the total lifetime spent in crack propagation. It was observed that cracks are nucleated at surface notches meated during reversed plastic deformation, Principally at grain boundaries, and that crack growth occupies greater than 75 pct of the fatigue life. When inclusions are present, they are often the primary sites of crack initiation. From consideration of the incremental distances advanced by a crack in each cycle and of the lifetimes of different materials, it appears that the universality of Coffin's law arises from the similarity of crack-tip strain for a given applied strain amplitude, irrespecti7:e of material. STUDIES of low-cycle fatigue have been particularly rewarding in that a simple correlation between fatigue lifetime and plastic-strain range has been shown to exist. This empirical relationship takes the forml,2 Nner=C [1] where N is the number of cycles to failure, Er is the plastic-strain range defined as the total plastic strain per cycle (the sum of the tensile plastic strain plus the compressive plastic strain), n, the exponent, is a constant independent of the material to a first-order approximation and often has a value of about 0.5, and C is a constant which for a number of ductile and metallurgically stable materials is approximately 0.65 for fully reversed strain.3 This relationship has been shown to be valid for a wide variety of metals and alloys and is often referred to as Coffin's law. However, it is yet not clear why so many different metals and alloys exhibit the same over-all behavior in the low-cycle range. Less is known about the mechanisms of fatigue failure in the low-cycle range than in the high-cycle range, but it is expected that the processes would have much in common. For example, an important characteristic common to both high-and low-cycle ranges is that fatigue crack propagation can occupy a considerable portion of the total lifetime. This has been shown by Laird and smith4 by a count of the number of ripples present on the fracture surface of copper specimens, each ripple corresponding to one cycle of load. On the other hand, some marked differences have been noted. For example, in copper,5 nickel, and aluminum4 there is a greater tendency for grain boundary cracking to occur as the strain amplitude is increased. The purpose of the present work was to study further the processes leading to fatigue failure in the low-cycle range and to obtain an understanding of the basis for the validity of Coffin's law. Particular attention has been paid to the manner of crack initiation and to the determination of the portion of total lifetime spent in crack propagation. MATERIALS A number of metals and alloys were tested, although more attention was focused on a particular few, once general trends had become apparent. Alloys were selected so as to investigate the effects of crystal structure, number of phases, stacking-fault energy, and impurity content. The materials in this grouping were: high-purity copper OFHC copper 1100 aluminum (commercially pure) 70-30 brass (Cu-30 wt pct Zn)

Jan 1, 1965

By B. A. Wilcox, A. H. Clauer

DURING the course of an investigation on the high-temperature creep behavior of TD Nickel* (Ni + 2) vol pct ThO2), it was observed that the creep fractures were similar in appearance to low-temperature ductile fibrous fractures and creep ruptures by cavitation. Microfractographs of fibrous ruptures are typically characterized by a dimpled appearance, with second-phase particles frequently found near the bottom of the dimples.'-4 These somewhat resemble creep ruptures by cavitation, in that fracture occurs by void formation, with the subsequent growth and final merging of the voids to form a complete fracture.' It is the purpose of this communication to describe the creep fracture of TD nickel and suggest a mechanism for the rupturing process. The discussion is relevant to material crept to fracture in vacuo at a constant stress of 18,000 psi, over the temperature range 900" to ll00°C. The material used in this investigation was 1/2-in.-diam bar stock supplied by Du Pont, contain- ing 2.3 vol pct Tho2. The final fabrication treatment consisted of -95 pct reduction by swaging followed by a 1-hr anneal at 1000°C. Transmission and replica electron microscopy revealed that the material had a fibered structure with a transverse grain size of -1 µ and a longitudinal grain size of 10 to 15 µ. Selected-area diffraction indicated that the fiber axis was parallel to (00l), in agreement with the results of Inman et a1.6 The thoria particle size varied from 80 to 1000Å, with an average size of 400Å, and the mean particle spacing was about 1200Å. The remarkable structural stability7 was confirmed by annealing for 6 hr at 1300°C (about ' 0.9 the absolute melting point). Transmission electron microscopy revealed that the only structural change was a slight decrease in dislocation density. Furthermore, recrystallization or grain growth during creep has not been observed. All specimens were annealed in vacuo at 1300°C for 3 hr prior to creep testing. The following times to rupture were obtained for vacuum creep tests at a constant stress of 18,000 psi: 900°C, 854 hr; 930°C,

Jan 1, 1965

By G. S. Ansell, J. Weertman

The creep behavior of an aluminum alloy hardened with a finely dispersed phase of aluminum oxide was investigated. The as-extruded alloy shows an approximate steady-state creep in which the creed rate depends exponentially on the applied stress. The activation energy of creeb is abbroximately 150,000 cal per mole. The recrystallized alloy shows no steady-state creep. ONE method of improving the creep resistance of a metal is to introduce a finely dispersed second phase into the metal matrix. The improvement of the creep resistance has been qualitatively explained by assuming that the dispersed second-phase particles act as obstacles to dislocation motion. If the main effect of second-phase particles is simply to hinder dislocation motion then it is possible to derive a high-temperature creep equation for a dispersion-hardened alloy in a straightforward manner. In the Appendix of this paper such an equation is derived from a creep model which works very well for pure metals. Recently, F. V. Lenel has fabricated, for the first time, powder extrusions of aluminum-aluminum oxide in a large-grained recrystallized form. This alloy, designated as MD 2100, consists of a fine dispersion of aluminum oxide plates in a matrix of commercial purity aluminum. A considerable amount of investigation has been carried out concerning the microstructure and physical properties of this alloy.&apos; ) The aluminum oxide is present in the form of flakes 130A units thick and 0.3 u on edge. They are dispersed in the aluminum matrix with an average spacing of approximately 0.5 jx. The spacing varies in the range of 0.05 to 1.5 µ. The alloy structure is extremely stable at high temperatures. For this reason the alloy offers a unique opportunity for a fundamental study of creep of a very finely dispersed two-phase alloy. Lenel supplied specimens in both the unrecrystallized and recrystallized condition. This paper reports high-temperature creep experiments carried out on these specimens. The results obtained were rather unexpected. No steady-state creep was observed in the recrys-tallized material. In fact, after some transient creep which takes place upon loading, the creep rate is essentially zero ( < 10-8per min). If the second-phase particles acted solely as obstacles to the motion of dislocations, measurable steady-state creep would be expected. Since none is observed it appears that the main effect of the fine dispersion in the recrystallized material is to inactivate the dislocation sources themselves, rather than hinder the motion of dislocation loops created at these sources. EXPERIMENTAL DETAILS Specimens were tested in wire form, 0.087 in. in diam for the as-extruded alloy, and 0.035 in. in diam for the recrystallized alloy. These samples were held in friction-type wire grips; a gage length of 2.5 cm was used for all the creep tests. The specimens were held at 600°C in the test apparatus for at least 15 hr prior to each test. The tests were run under the condition of constant loading and, since the creep strains were small, can be considered as constant stress tests. The temperature of testing was held constant within 3°C. Elongations were measured with an optical cathetometer which was capable of measuring strains as smaIl as 0.00012. This allowed the measurement of strain rates as low as l0-8&apos;per rnin. In addition to the creep tests optical micrographs were made in order to determine both the grain size and microstructure of these materials. RESULTS Fig. 1 shows a few typical creep curves obtained from the as-extruded material. The elongations were somewhat erratic, but each curve shows a region of quasi-steady-state creep from which an approximate steady-state creep rate can be obtained. In general the higher the stress at a given temperature, the greater the total elongation before fracture. The lower the applied stress, the longer is the region where the creep rate is almost constant. Summary data from the creep tests of the as-extruded material are listed in Table I. The steady-state creep data of the as-extruded material for a range of stresses at a constant temperature follow a creep equation of the type creep rate = K&apos; = A exp (&) [11 where A and B are constants, k is Boltzmann&apos;s constant, T is the absolute temperature, and a the stress. The standard error of estimate of the data received is less than one order of magnitude. As shown in Fig. 2, if one compensates the creep-rate data for the effect of temperature over the range of test temperature, the steady-state creep data roughly follow a creep equation of the type Temperature compensated creep rate = K* = A exp

Jan 1, 1960

By L. Guttman, C. S. Barrett, J. S. Bowles

THE transformation from the face-centered cubic (Al) to the face-centered tetragonal (A6) structure in certain alloys of the indium-thallium system reported in the preceding paper1 exhibits many interesting crystallographic and metallo-graphic features, most of which presumably are similar to those of other cubic to tetragonal transformation such as, for example, the one which occurs in the chromium-manganese system,2 the one which, judging by microstructures and X-ray pat-terns,3 probably occurs in the copper-manganese system, the ones accompanying ordering in FePt,4 Copt,&apos; and AuCu,5 and the transformation near 115°C in barium titanate.6,7,8 If, as mentioned in ref. 1, the transformation is second order, the phases in equilibrium do not differ in composition, and it is both possible and likely that the mechanism is a diffusionless one. The present paper reports the results of a detailed study of the indium-thallium transformation and presents a theory for the atomic movements of the transformation which accounts for the observations. Experimental Crystallography of Transformation Markings The transformation from cubic to tetragonal in the indium-thallium alloys produces microstruc-tures of the type illustrated in fig. 1. These structures are observable either as relief effects produced on a smooth surface by the transformation, or after polishing and etching. These microstruc-tures are markedly similar to those found in copper-manganese alloys: iron-platinum alloys," and barium titanate,7,8 where it has been demonstrated that the lamellae are parallel to the (101) planes of the original cubic crystal. That the observed lamellae in indium-thallium alloys are also parallel to the (101) planes was proved by the following analyses performed on single grains in polycrystal-line samples containing 20.75 atomic pct T1. A study of the microstructures of a number of specimens revealed the fact that in many specimens the transformation markings continued unchanged in direction across the (111) interfaces of annealing twins. This at once demonstrates that the lamellae are parallel to a plane that is common to both parent and twin orientations, i.e., a plane in the zone <112>. This conclusion is compatible with the lamellae being parallel to (101) planes. To make a more complete determination of the habit plane of the lamellae, two grains were selected in which annealing twins ({Ill) twins) had been present in the high-temperature modification (cubic). The traces of the annealing twins, and of the transformation markings in both parent and twin crystals, were plotted together in stereographic projection, and a parent-twin pair of orientations was found that accounted for all lamellae as (101) planes. The projection of one of these twinned grains is reproduced in fig. 2. In view of these results the probability of there being another solution for the habit plane remote from (101) is very small, but to explore the possibility that the habit plane deviates slightly from (101), a more precise analysis was undertaken. In this, the orientation of a grain in the cubic modification was determined from a Laue back-reflection photograph taken with the sample at 90°C. The traces of the lamellae that formed in this grain on cooling were plotted in the stereographic projection

Jan 1, 1951

By T. V. Philip, Paul A. Beck

IN a previous note1 it was pointed out that the available information suggests a distinct correlation between the occurrence of the CsCl-type ordered structures formed in equi-atomic binary alloys of transition elements and the location of the components in the periodic table. A definite increase in the bond strength between unlike atoms, as compared with that between like atoms, is indicated when, in binary alloys of iron group elements, the other component is changed from chromium to vanadium or tantalum, to titanium. Laves and Wallbaum,2 eported a CsCl-type ordered structure for the stable intermediate phase at the equi-atomic composition in the Ti-Fe system (and also in the Ti-Ru and Ti-Os systems). On the other hand, Tagaya, Nenno, and Nishiyama8 found no ordering of this kind in the body-centered-cubic solid solutions in the Cr-Fe system. It was concluded&apos; that the occurrence of a CsC1-type ordered phase of intermediate stability may be expected in the V-Fe system. Preliminary results were described: suggesting that at least some degree of order does exist in the equi-atomic alloy VFe, annealed at 1200° C and quenched in cold water. Using CrK radiation, at least one weak superlattice line was found in the X-ray diffraction pattern which could be indexed as (100). and which disappeared, as expected, when FeK radiation was used. It was found more recently that the impurity phase (presumably VN), previously giving rise to additional X-ray diffraction lines and thus preventing definite indentification of the (111) superlattice line,&apos; can be eliminated by preparing the alloy by arc melting in a helium atmosphere. The alloy specimen melted in this manner had clean surfaces and showed very littte, if any, nitride phase in the microstructure after annealing in vacuum at 1250°C and quenching. The relative intensity of the (100). superlattice line with CrK radiation was greatly increased and, in addition, a fairly strong (Ill) , superlattice line and even a detectable (210) , super- lattice line was obtained, when the powder produced by filing from the 1250°C annealed and quenched specimen was reannealed in vacuum at 625°C for 1 hr. By using a cellulose acetate film as a filter in front of the photographic film in order to absorb the soft radiation resulting from air fluorescence, the background intensity could be reduced considerably in relation to the intensity of the diffraction lines. All three superlattice lines, (100),, (111)., and (210)a, disappeared, as expected, when a radiation other than CrK, was used.1 For the powder reannealed at 625ºC, the strongest lines of the s pattern also appeared weakly, indicating that during an: nealing at 625°C a small amount of transformation took place from the body-centered-cubic to the u phase. However, since all superlattice lines to be expected in the 0 angle range used were actually very clearly present, it was evident that the high temperature body-centered-cubic phase had transformed into a CsCl-type ordered structure before much s phase could form. Reannealing filings for 1 hr at 700°C resulted in complete transformation into the u phase. After 1 hr at 650°C the transformation into IT was not quite complete, the strongest body-centered-cubic diffraction lines were still present, although fairly weak, and only the (100), super-lattice line was detectable (extremely weak). These findings not only confirm the previous conclusionsL as to the existence of a CsCl-type ordered structure in the Fe-V system, but they also indicate that this metastable ordered structure forms at about 600°C preceding the formation of the stable s phase, while at 1250°C the disordered body-centered-cubic phase is stable. The faint (loo) , super-lattice line previously observed in specimens quenched from 1200°C was probably due to the fact that the quenching of the powder in an evacuated fuse:! quartz capsule was not fast enough to prevent completely the ordering reaction on cooling. The present results conform with the suggestion that the A-B bond, in relation to the A-A and B-B bonds, increases in strength from CrFe to VFe to TiFc. It is, therefore, of interest to compare the measured values of the average atomic diameter for these three alloys with the corresponding average atomic diameters calculated from the atomic radii of the elements concerned. ASSUming A-B contacts

Jan 1, 1958

By N. S. Stoloff, M. Gensamer

The effects of temperature, grain size, and magnesium content on the strength and ductility of cadmium were studied in the range -269° to 23 °C. A sharp drop in ductility between -140° and -190°C marked a transition in fracture mode from ductile shear to inter gvanular fracture. The addition of up to 15.35 wt pct Mg in solid solution raised the transition temperature, and for two compositions produced basal cleavages. The relatively high ductility of unalloyed cadmium at cryogenic temperatures is attributed to temperature independence of the yield stress and the absence of dislocation locking. ALTHOUGH numerous studies have been made of the mechanical properties of cadmium single crystals,1-5 no comprehensive investigation of deformation and fracture in polycrystalline cadmium has been carried out. This investigation was initiated to determine the mechanisms of deformation and fracture in polycrystalline cadmium, and to attempt to correlate these mechanisms with the behavior of other metals of hexagonal close-packed structure. A second objective of this work was to determine whether the slip systems and mode of fracture of polycrystalline cadmium could be altered by reduction of the axial ratio, which is 1.886, through alloying. Dorn and co-workers&apos; have been able to induce prismatic slip in magnesium through alloying to reduce the axial ratio. Single crystals of cadmium are so highly ductile that glide strains of 400 pct are observed at room temperature, and 80 pct at -269°c.l Failure in every reported case is by necking down and shearing off of the crystal. Cleavage in cadmium single crystals has never been observed. Magnusson and aldwin reported a ductile to brittle transition for polycrystalline cadmium at about —160 C for specimens tested at a strain rate of 0.05 in. per in. per min in tension. However, even at -196° substantial ductility was retained. The transition temperature was strain rate dependent, impact loading at 19,000 in. per in. per min raising the transition temperature to about -85°C while leaving the low temperature ductility unchanged. No information was given on microstructures or fracture mode, nor were stress-strain characteristics reported. In the present investigation, tensile tests were carried out on polycrystalline cadmium and solid solution Cd-Mg alloys to determine flow stresses, work-hardening behavior, fracture strength, and fracture ductility. Variables employed included temperature, alloy content (and c/a ratio), and grain size.Some compression data also have been obtained for comparison purposes. I) EXPERIMENTAL PROCEDURES A) Polycrystalline Cadmium. Two purities of cadmium were employed in this investigation. Cadmium of 99.95 pct purity was supplied by Belmont Smelting and Refining Co. Cadmium of 99.99+ pct purity was supplied by American Smelting and Refining Co. Threaded cylindrical tensile specimens were machined to give approximately a 1/2 in. long straight gage section with a reduced diameter of about 0.110 in. Specimens were heat treated in evacuated pyrex capsules in the range 140" to 290°C to produce desired grain sizes. All specimens were polished in a solution containing 320 g Cr03 and 20 g NaS04 in 1000 cc of H20. Occasionally this solution caused staining of the specimen, in which case a further polish with a solution of one part HN03 and two parts H202 in two parts ethyl alcohol was employed.&apos; Tensile testing was carried out on a screw-driven Instron machine, at a constant rate of crosshead movement, which for most tests was 0.01 in. per in. per min. Load vs time, and therefore load vs total strain, were recorded. Temperatures from -196" to -40°C were obtained by passing nitrogen gas through a copper coil immersed in liquid nitrogen, and then feeding the gas into a jacket around the specimen. Tests at -269°C were carried out in a helium cryostat, at a crosshead rate of 0.1 in. per in. per min, with specimens of 1 in. gage length. Compression specimens were tested in a jig similar to one designed by ilman. The jig was mounted on the under side of the Instron crosshead. Load was transmitted by means of a rod connected to a movable part of the jig at one end, and the load cell at the other end. A downward movement of the crosshead applied a compressive load to the specimen.

Jan 1, 1963

By M. N. Shetty

LARGE copper whiskers (-100 p) of 11111 orientation were tested in a floor-model Instron testing machine, at liquid nitrogen temperature. (Testing methods will appear elsewhere.) Whiskers deformed by twinning after some initial deformation. A load-elongation curve at the onset of twinning is reproduced in Fig. 1. Twinning was confirmed by taking a back-reflection Laue picture, using a slit colli-mator, which showed distinct splitting of reflections. The tensile stress reached just before twinning is about 1.4 x 107 g per sq cm (-7.0 x106 g per sq cm—resolved shear stress) which drops to 1.2 x107 g per sq cm (-6 x 106 g per sq cm—resolved). This twinning stress is about five to ten times larger than the value for bulk single crystals of copper deformed at 77°K (-106 g per sq cm—resolved). Twinning models based on Cottrell-Bilby&apos;s pole mechanism are discussed in detail by Venables.&apos; In the present work a mechanism based on the idea of failure of a Lomer-Cottrell barrier by recombination will be proposed. An L-C barrier may fail either by recombination or by dissociation.3 Fig. 2 provides the necessary information. It shows that the stress necessary to break such a barrier is about 1.8 x 107 g per sq cm by recombination and 4 x 107 g per sq cm by dissociation at 77°K. The twinning stress reached by whiskers is comparable to the stress level required for failure of an L-C barrier by recombination. (Stroh himself points out that his calculations should not be taken too literally.) We consider a segment of the L-C dislocation which has recombined (AB in Fig. 3) over a length to form the total dislocation which then glides in the

Jan 1, 1965

By Barbara A. Thompson

A previously reported high-resolution method for the location of boron-rich areas in metallurgical and biological specimens was been adapted for general use on a routine basis. The rnetlzod utilizes neutron activation and autoradiograpizy. Alpha-particles emitted by boron nuclei upon neutron capture are recorded on a photographic emulsion. The resulting a-particle tracks show the location of boron-rich areas. Experimental techniques, interferences, and limitations of the method are discussed in detail. The method is most useful where there is marked segregation of boron. In this type of sample, the segregation can be observed when the nominal boron concentration is as low as 0.0006 pct. THE positive identification and location of boron-rich areas in metals is frequently of great interest in metallurgical work. Unequivocal identification is often difficult to make by conventional metallo-graphic methods. Recently, a method has been described which accomplishes this objective by neutron activation and autoradiography.l-3 The method can be described briefly as follows. Upon neutron capture, a -particles are emitted by boron nuclei according to the following reaction: ,Blo + n - ,a4 + 3Li7 + 2.4 mev The energy is dissipated as kinetic energy of the products. By irradiating a boron-containing sample in contact with a photographic emulsion and subsequently developing this emulsion, a-particle tracks are obtained whose location corresponds to the location of boron-rich areas in the sample. Two factors combine to make the reaction extremely specific for boron. The first is the unusually high (755 barns) cross section of boron for thermal neutron capture. The second is the higher neutron energy required to produce (n, a ) reactions in essentially all other nuclei except lithium. These two factors make the method specific for boron by six to seven orders of magnitude when a predominantly thermal neutron source such as the Brookhaven reactor is used. The reported limit of detection of this method is of the order of 0.01 pct B., The present work was originally undertaken to determine whether this limit could be lowered by use of a thinner emulsion. However, initial experiments showed that in order to use the method at all, it was necessary to reestablish the optimum experimental conditions in terms of the available irradiation facilities. It is the purpose of this paper to describe these experimental conditions in detail, to discuss the factors influencing sensitivity, and to evaluate several techniques for increasing sensitivity. EXPERIMENTAL A) Preliminary Experiments—The first measure-ments were made using samples of crystal oriented silicon steel containing various concentrations of boron. In the later experiments, samples of various high-temperature alloys such as M-252, hcoloy 901, Nichrome V, and so forth, were used. Faraggi, et al.,2 reported that the lower limit of sensitivity in this type of sample was about 0.01 pct B using nuclear emulsions of 50- u thickness. but that it should be possible to extend this limit by the use of thinner emulsions. Accordingly, we first used Kodak Auto-radiographic Stripping Film (Permeable Base) which has an emulsion thickness of only 5 µ. This was mounted on the metallographic specimens according to the technique described by Boyd.4 The emulsion remained in contact with the metal surface throughout exposure and development. Since the emulsion is transparent after development, the autoradiograph and metal surface can be viewed simultaneously and any correlation between film blackening and structure of the metal can be made directly with no problems of realignment. Because the silicon steel is readily attacked by moisture alone, it was necessary to apply a protective coating to the metal surfaces before mounting the emulsion. The coating was made extremely thin in order to absorb as few a-particles as possible. Boyd4 and Gomberg5 have discussed various plastics used for this purpose; however, none was sufficiently impermeable to prevent chemical attack of the steel during the developing process. This attack resulted in the production of gross chemical artifacts in the emulsion. It was, therefore, necessary to use the method of Wolfsberg and John6 as follows. A very thin (approximately 1 µ) coating of Plexiglas II was applied by dipping the sample in a 2 pct solution of Plexiglas II in dichloroethylene. Then, because the emulsion will not adhere to Plexiglas 11, a thin coating of Parlodion was applied in a similar manner using 2 pct Parlodion in iso-amyl acetate. No protective coating was necessary with the high-tem-

Jan 1, 1961

By Cyril Wells, Paul E. Busby, Donald P. Hart

EARLY workers in the field have established that the diffusion of nitrogen follows normal diffusion laws. Concentration-penetration data from layer analyses of reasonably pure iron specimens nitrided in an atmosphere of CO-NH, are given in the literature,&apos; and were utilized to calculate diffusion constants for nitrogen. The diffusion of nitrogen in y-iron may be represented approximately by the equation D - 1.07x10-&apos; e-:".&apos;m&apos;"&apos;r The diflusion coefficients, D, given by this relation represent mean values, since carburization occurred simultaneously with nitriding. The rate of diffusion in a-iron has been determined from calculations based on data obtained by measuring the internal friction of samples at each of several frequencies and temperatures.&apos; The expression for the diffusion of nitrogen in a-iron derived from these experiments is D= 1.4x10-1 e-it tudent Increasing carbon content decreases the diffusion of nitrogen in a-iron.3 Oxygen, either dissolved or combined, has been shown&apos; to exert a marked influence on the diffusion of nitrogen from a nitriding atmosphere. D values increase rapidly with increasing amount of dissolved oxide in the metal, but diffusion is completely inhibited if preliminary oxidation has produced the slightest trace of iron oxide on the surface. Diffusion coefficients have also been calculated from permeability and solubility data,&apos; but these values are of questionable accuracy since the boundary conditions assumed may not actually exist. Experimental Method The method selected for determining the diffusion coefficient of nitrogen in a-iron in the present investigation was the so-called fractional saturation method. This method consists of heating the specimen in an atmosphere of H2-NH8 mixtures of known composition for a predetermined time. Following this treatment, the specimen is analyzed for nitrogen; and the diffusion coefficient is calculated from a known relationship of the fractional saturation, time of diffusion, and dimensions of the specimen. This relation is based on a solution of Fick&apos;s second law and assumes that the surface of the specimen immediately reaches a given concentration which remains constant during the diffusion anneal. Tabular solutions are available4-5 and provide the relationship between fractional saturation and the quantity \/Dt /a, where D is the diffusion coefficient in cm2 per sec, t is the time of the diffusion anneal in seconds, and a, in the present experiments, is the half-thickness of the slab specimen in cm. The method is adequately discussed elsewhere.9-10 Material The material for this study consisted of 3/32 in. thick (0.24 cm) carbonyl iron plate. The major impurities in this iron are oxygen and carbon, which are readily removed by long time high temperature treatment in an atmosphere of purified hydrogen. In order to reduce the diffusion anneal time for saturation runs, some of this material was rolled to a thickness of 0.015 in. (0.038 cm) prior to the hydrogen treatment. Hydrogen treatments were carried out in a hydrogen-purified Armco iron tube heated in a global

Jan 1, 1957

By A. R. Troiano, E. A. Steigerwald, F. W. Schaller

The kinetics of crack propagation in a hydrogenated high-strength steel at subzero temperatures indicated that cracking progressed in a discontinuous fashion. The delayed failure process thus involves a series of crack initiations rather than the continuous growth of a single crack. The incubation time required for the initiation of delayed failure was controlled by the diffusion of hydrogen. The activation energy for the process was 9120 cal per g-alom. As the test temperature was lowered the incubation time constituted a greater percentage of the total tinze to fracture, and al -50°F the incubation and fracture times were essentially coincident resulting in instantaneous, catastroplzic fracture. A unique feature of hydrogen embrittlement is the delayed failure process in which the material fails under the action of a sustained load even though it is capable of supporting a higher load for a finite period of time.&apos;)&apos; Delayed failure of steel and titanium is characterized by an incubation time, preceding the initiation of a crack in a highly localized region, and the subsequent growth of the crack to ultimate failure.3-5 The kinetics of crack growth in hydro-genated high-strength steels have been studied through the use of resistance measurements and have an important bearing on the mechanism of delayed failure. Delayed failure is believed to be merely a facet of hydrogen embrittlement in which sufficient time is allowed during a test for hydrogen diffusion. The current theories employed to explain hydrogen em-brittlement can be grouped into two types. one6-8 explains the embrittlement on the basis of the pressure exerted by molecular hdrogen in lattice voids or defects while the other9-10 attributes the embrittlement to the influence of hydrogen in the lattice. The mechanism used to explain the nature of the crack kinetics in delayed failure is based on the stress-induced diffusion of hydrogen to the area of maximum triaxiality.3 When the hydrogen concentration in this region reaches a critical value, a crack is nucleated. This initial crack propagates instantaneously until stopped by the higher fracture stress of the adjacent material of lower hydrogen content. The continuation of cracking must then await the further diffusion of hydrogen to the new region of triaxiality near the base of the crack where another initiation will occur. From this mechanism it follows that crack propagation is nothing more or less than a series of initiations with limited fracture. The purpose of this investigation was to examine the kinetics of crack growth in an effort to determine whether or not the process was discontinuous. Studies of crack propagation were conducted at low temperatures to retard the diffusion of hydrogen which is presumed to be the rate controlling process in delayed failure. MATERIALS AND PROCEDURE Specimen Preparation—A commercial heat of air-craft quality SAE-AISI 4340 steel, designated as Heat G, was furnished by the Republic Steel Co. in the form of %-in. hot-rolled bars. The material had the following chemical analysis: Composition of 4340 Steel—G Heat C Mn Si Ni Cr Mo 0,395pct 0.82pct 0.29pct 1.76pct 0.85pct 0.25pct Notched tensile specimens with less than a 0.001 in. radius, Fig. 1, were used throughout the investigation. The specimens were heat treated to a 230,000 psi strength level according to the following sequence: a) Normalize bar stock at 1650°F for 1 hr, b) Stress relieve at 1200°F for 4 hr and furnace cool,

Jan 1, 1960

By James C. M. Li, J. Weertman

James C. M. Li (United States Steel Covp.)—The author has discovered a single analytical relation between the minimum, or the steady-state, creep rate and the applied stress confirming a statement made earlier by orn" that such relation should exist and should reduce to the power law at low-stress levels and to the exponential law at high-stress levels. However, as pointed out by the author, all the available theories of creep are not adequate to explain such a single relation. Inspired by such a statement, I have made a suggestion concerning a possible explanation13 of the new relation. This is based on the concept that the rate-controlling step is the cooperative motion of a short dislocation segment. The nature of and the reason for the cooperation have been discussed13 as well as the reason why the motion of the dislocation could be controlled by the mobility of the short segments. A natural short segment has been proposed13 to be the node formed at the intersection of two dislocations. The reason why the node may contain only a few atoms has not been discussed and the application of the proposed model to all the metals and alloys reported in this paper has not been attempted. It seems appropriate to include these in this discussion. The model was partly inspired by the substructure recently observed in the electron microscope on creep specimens. One such example is shown in Fig. 48 in Darken&apos;s Campbell Memorial Lecture. The substructure is a collection of dislocation intersections and irregular networks. No pileups have ever been observed in such specimens. A closer look at the network indicates that one set of dislocations is more straight than the other set sug- gesting that the other set may be mobile in the plane of the net. Since, for the network to survive the creep deformation, some dislocation reaction has to take place at the intersection of the two sets of dislocations, the mobile dislocation, even if it can slip in the plane of the net, will have difficulty in moving at these intersections. To illustrate, an idealized network is shown in Fig. 9. The thin lines represent the set of dislocations which are mobile and can slip in the plane of the net except at the nodes which are formed at the intersection of the two sets of dislocations. The other set of dislocations, represented by the thick lines, may have a Burgers vector which is not parallel to the plane of the net, and therefore may be immobile. Because of this nonparallel Burgers vector, the Burgers vector of the node, which is avectorial sum of the Burgers vectors of the two sets of dislocations, will also be nonparallel to the plane of the net. Therefore, the node cannot slip in the plane of the net and the set of mobile dislocations will have to drag the node along as indicated in Fig. 9. Now the problem is how many atoms could be involved in the nodes. Exact calculation of the length of the node is a difficult task especially since the length should be a steady-state length and not an equilibrium length. An estimate of the equilibrium length can be made by balancing the line tension of all the dislocations. The results would be a small fraction of the length 1 between nodes as shown in Fig. 10. In some instances such a calculation shows that the node will not be formed. But, since the calculation is only approximate, it does not rule out the possibility of the formation of a short node. In other instances the equilibrium length of the node is an appreciable fraction of I. Such a node would

Jan 1, 1963

By R. C. Gifkins, A. Gittins

A. Gittins and R. C. Gifkins (University of Mel-houvne)— Evidence from somewhat similar experiments to those described in this paper has led us to the conclusion that possibility 2) of the four listed on p. 319 is a description of what happens in grain boundary sliding. That is, sliding is limited by accommodation deformation, it being necessary to the Continuance of sliding that this accommodation should take place. An example of such accommodation, though probably not the most important, is fold formation at triple points. The evidence and arguments for this point of view are set out in Refs. 14 to 16. In particular, an experiment with a lead bicrys-tall5 seems to support point 2) rather than 3). In creep of this specimen it was found that at least 90 pct of the extension of a zone 0.3 mm wide at the boundary was supplied by sliding at the boundary. The sliding was localized in a region at the boundary very much smaller than 0.3 mm, in fact, in a region too narrow to resolve optically. In poly crystalline Specimens&apos; there appears to be a surface effect, as found by Rachinger," but it appears that this may not manifest itself at low strains. "Low strains" means <10 pct for a Pb-TI alloy, <2.5 pct for magnesium or "Magnox" A12 alloy, or <40 pct for a 0 brass. Up to this extension the sliding, measured by the mean vertical step at boundaries, is proportional to extension. We are able to say this with some confidence, since the error bars on our points are statistically derived. Our results would lead us to think that the error bars on other work, including that of Mullendore and Grant, are much too large at low strains to show this

Jan 1, 1963

By R. J. Stokes

S. Floreen (international Nickel Co.)— One fairly simple way to differentiate between em brittle me nt due to surface microcracks or due to a dislocation barrier effect might be to load a brittle rock salt crystal in tension to some stress just below the fracture stress and then immerse the loaded crystal in water. If a surface film is retarding plastic flow then one should observe some plastic deformation of the rock salt as

Jan 1, 1962

By J. Richter, D. Schulze

J. Richter and D. Schulze (Deutschen Akademie der Wissenschafte zu Berlin)—Introduction. In a recent paper R. G. Garlick and H. B. Probst reported on experimental results of investigations of room-temperature slip in zone-melted tungsten single crystals.17 In the paper it was pointed out that slip lines could be detected with an optical microscope only after about 10 pet plastic strain of the crystal. In our investigations we could observe slip lines in tungsten single crystals of defined orientations already with an elongation of 0.02 to 0.03 pet.18"9 Experimental Technique and Results. The tungsten single crystals were produced from 4 to 5 mm sintered rods* as starting material by electron- beam zone melting. With single-zone-pass melting a speed of 0.5 mm per min was used, while three-pass melting could be handled at a speed of 3 mm per min. Crystal axis orientations were located in the shaded area of the stereographic triangle, see Fig. 6. Orientation 1 is located at about 18 deg and orientation 2 at about 5 deg on the great circle from [011] to [ill]. This corresponds approximately to the orientations P and M referred to by Garlick and Probst. Our single crystals had a length of about 70 mm and were profiled solely by electrolytic means, leaving grip ends at both ends of the crystals. Between the latter, a cylindrical crystal of 45 to 50 mm length and about 2.4 mm diam was obtained. The crystals were deformed at room temperature in a commercial tensile-testing machine to obtain a strain of 0.02 to 5 pet. The average strain rate e = eP/t for all tensile tests amounted to approximately 10 -6 to 10-5 per sec, with ep representing plastic strain and t the duration of applied stress. In Fig. 7 a crystal is shown elongated by 0.03 pet. The picture was obtained by means of an optical microscope. Figs. 8 and 9 give electron-microscopic pictures of slip lines of crystals elongated by 0.07 and 1.1 pet, respectively. For crystals with the orientation 1, see Fig. 6, only the two main slip systems (101)[111] and (110)[111] were found. With the crystals of group 2 the two main slip systems are again evident, with

Jan 1, 1965

By I. R. Kramer

A delay time for yielding in cold-worked face-centered-cubic metals was found. Slip on (123) planes was observed. Glide on these planes occurred during the delay-time period before slip starts on the (111) planes. AN important approach to the study of the anchoring and blocking of dislocations is available through the delayed-yield phenomenon which has been observed in body-centered and hexagonal close-packed metal by several investigators. Clark and his associate1-5 showed that a delay time for yielding is present in mild steels and fine-grain molybdenum. Type 302 stainless, SAE 4130 normalized, SAE 4130 quenched and tempered, and 24s-T aluminum aid not have a delay time. Kramer and Maddin6 studied the delay-yield effect. in metal single crystals. While they found a delay time in body-centered-cubic metals none could be found in the face-centered-cubic metals. Later7 a delay time was found in hexagonal close-packed metals. cottrell8 has proposed an explanation for the difference in the yield phenomena of b.c.c. and f.c.c. metals based upon the anchoring of edge dislocations by the proper types of impurity atoms (C and N). In the body-centered-cubic lattice the interstitial atoms are near a cube edge and can interact with an edge dislocation, while in a face-centered-cubic lattice the distortion around an interstitial atom is of spherical symmetry and cannot anchor a screw dislocation which has practically no hydrostatic component. Cottrell&apos;s theory seems to account rather well for the behavior of body-centered-cubic . metals. EXPERIMENTAL PROCEDURE The apparatus used in these experiments is essentially of the same design as described previously.&apos; Single crystals 1 in. long and having a diameter of % in. were placed in a pendulum which consisted of a bar 8 ft long designed with a crystal holder to accommodate the specimen at low temperatures. This portion of the apparatus was supported on fine molybdenum wires. A bar of the same diameter and length comprised the other portion of the apparatus. This bar was supported on a set of roller bearings arranged around the periphery of the bar to allow accurate alignment. This bar was propelled by means of a spring-loaded gun and allowed to strike the lead bar in front of the single-crystal specimen. SR-4 type A-8 resistance strain gages were cemented to the specimen and the strain measurements were obtained by amplifying the strain-gage output by means of a high-gain preamplifier. A tektronix 545 oscilloscope was used together with a polaroid camera to record the strain and time sweep. An Ellis Associate Bridge was used to calibrate the strain gages and calibration readings were obtained before each test. The sweep of the time signal was initiated by means of a miniature thyraton which was fired when the two bars came into contact. The single-crystal specimens were cut from single-crystal bars about 12 in. long, grown by a modified Bridgman technique. The aluminum crystals were made with material of 99.99 pct purity while the purity of the copper was 99.999 pct. A cut-off wheel was used to prepare the specimens which were then machined to the desired length. The two opposite faces of the specimen were parallel to each other and perpendicular to the axis of the specimen. The specimens were compressed 1 pct. No machining followed thereafter. In some cases prestraining was carried out in liquid nitrogen by impacting the specimens directly in the apparatus so that subsequent observations could be made without allowing the specimen to warm up to room temperature. The single crystals were compressed 1 pct at room temperature in a hand press without much control of the rate of deformation. In some cases specimens were recompressed to obtain the desired length change. As far as could be determined in these experiments this factor did not seem to influence the results. The SR-4 strain gages were glued with a cellulose type cement onto the specimen surface and baked at 45°C for 12 hr. As a check on the baking treatment gages were allowed to dry at room temperature. All delay time tests in this paper were conducted in a liquid nitrogen bath at -195°C. A schematic delay time oscilloscope trace is shown in Fig. 1. At point B the elastic stress wave caused by the impact reaches the strain gage on the specimen. The portion BC is the elastic strain. In this investigation the strain at point C was used to calculate the critical resolved shear stress by multiplying by the proper modulus depending upon the orientation of the single-crystal specimen. The time between C and D is the delay time portion of the curve. This portion of the curve is fairly flat but does have a definite microstrain associated with it. After the point D is reached the specimen deforms rapidly and the strain reaches a maximum at E. Following this, depending upon the length of the bar behind the specimen, the strain remains constant for a period and then decreases when the reflected elastic wave returns from the end of the pendulum bar. A permanent plastic strain is recorded on the oscilloscope trace and also measured by a strain-measuring bridge. The strain, E p,

Jan 1, 1960

By Nicholas J. Grant, Oliver Preston

PUBLICATION of data by Irmann&apos; indicating outstanding thermal stability and elevated-temperature strength properties in a sintered aluminum powder product (SAP) stimulated interest in the strengthening of metals by means of a highly dispersed oxide phase. This material was produced by compacting, sintering and extruding a fine flake aluminum powder, resulting in a dense product containing 10 to 16 volume pct alumina, which arises from the thin oxide film on the starting powder, highly dispersed in a matrix of pure aluminum. The method of producing SAP, and the stable high-temperature properties obtained from it, introduced the possibility of developing superior materials for high-temperature service by powder metallurgy methods. The composition of the materials of this type which are presently under consideration is predominantly metallic, containing from less than 1 pct up to about 20 volume pct of the oxide. As a result, other properties of these materials, such as electrical and thermal conductivity, thermal shock resistance, and to a certain extent ductility, notch sensitivity, machinability and hot working properties, are also predominantly metallic. These alloys do not constitute, therefore, a completely new class of materials as do the cermets, but rather present a new means of modifying the properties of a metallic matrix. In this sense, SAP type alloys are more closely analogous to the alloy aging systems. While the strength properties realized in the oxide-pure metal systems at the lower temperatures are substantially less than the best attainable in the aging systems, the thermal instabilities in the latter make them of less value for use at temperature much above their optimum aging temperatures, as indicated in Fig. 1. While the means of obtaining an oxide dispersion are more difficult and costly than conventional aging processes, in the light of the as yet limited understanding of such systems there is considerable promise of improved high temperature properties arising from the thermal stability of these structures. Since the development of SAP in 1946, its properties and the properties of a series of similarAl,O,-A1 products containing from about 1 to 20 pct aluminum oxide have been fairly extensively studied and reported.&apos;- "articular attention has been given to

Jan 1, 1958

By Erhard Hornbogen

Twins were propagated into large, well-annealed crystals of a, iron-phosphorous and a, iron-molybdenum solid solutions. Strain fields caused by interaction of these twins were made visible by precipitation. These strain fields can be explained by assuming that transmitted and reflected plastic waves are created when a twin strikes an obstacle with high velocity. The twin front itself can be regarded as a shear wave that may be able to develop a one-dimensional shock front. The occurrence of {WO} fracture by the reflected stress is also discussed. The described effects were not found when twins propagated at lout velocity into disturbed crystals, for example, into crystals previously deformed by slip. DEFORMATION twinning leads to shearing of a crystal lattice under external load. The shear appears to be homogeneous over a large number of crystal layers. In a iron, shear occurs on the (112) planes and in the <1ll> directions. The formation of a twin proceeds by the movement of partial dislocations that change the stacking at the twinning plane.l, In the bcc lattice, this partial dislocation can be created by dissociation of a sessile a/2[111] dislocation that lies in the (112) plane: Cottrell and Bilby&apos;s spiral mechanism can explain the homogeneous shear, but has not been proven experimentally. Nevertheless, this mechanism can explain the possible high velocity of formation of a twin. In Cottrell and Bilby&apos;s model, as in other models of twinning or phase transformation, a much higher energy is required to spread the first stacking fault than to add new layers by further movement of the partial dislocations. The dislocations will therefore become accelerated proportional to the difference between the stress, tN, to nucleate and tp to propagate the twin. It has been assumed3,4 that tn is the stress required to make two partial dislocations of apposite sign pass for the first time. After the first layer of new stacking has been formed, the maximum stress is TN=Gb/4pd where G is the shear modulus, b is the Burgers vector of the partial dislocation, and d is their perpendicular spacing so that the amount of shear is S = b/d. From this formula, a value of 25 kg per mm2 has been estimated for twinning in Zn3. The measured values are smaller, but local internal stresses may help to provide the necessary stress. For a iron, a higher value can be expected, mainly due to the higher value of G. That agrees with the observation that "burst" twinning occurs if the yield strength is in-

Jan 1, 1962

By H. Conrad

The strain hardening associated with the creep of magnesium single crystals at room temperatu.Je was investigated by shear tests in which the direction of stressing was reversed a number of times after creep in a <100> direction. The strain hardening was strongly anisotropic; the largest amount occurring in the direction of flow and the least 180 deg to this. The time law for creep changed from a parabolic type to logarithmic for the first and subsequent reversals of stress. For a given stress the creep strain decreased significantly for the first and second reversals and then only slightly for subsequent reversals. The logarithmic creep constant a changed in a similar manner. A linear relationship was observed between the creep strain for a given reversal and the stress. The slope for the third reversal yielded a strain hardening coefficient 12 to 16 times greater than that observed for unidirectional flow. Al-though no recovery was observed upon resting at room temperature, the hardening resulting from stress reversals could be completely removed by heating to 450" C. PREVIOUS work1.&apos; indicated that the creep rate of magnesium single crystals tested in the temperature range of 78" to 364°K decreased with time. This was attributed to an increase in internal stress resulting from an accumulation of dislocations at internal obstacles. The object of the present investigation was to further evaluate the nature of this hardening by conducting tests in which the direction of stressing is changed after previous creep in shear in a given slip direction. Previous to 1950 three investigations indicated that a Bauschinger effect3 occurred for single crystals as well as polycrystals brass in tension compression,

Jan 1, 1960

By B. Wilshire, P. W. Davis

It has been shown that grain-boundary migration during high-temperature creep can reduce or even prevent the formation of intercrystalline voids, giving a considerable increase in ductility.&apos; A similar observation has been made in a recent investigation of the creep properties of various grades of nickel and nickel alloys. The results can be illustrated by the observations made on: a) Pure vacuum-cast nickel (99.993 pct Ni) b) Impure vacuum-cast nickel (99.97 pct Ni) c) Pure nickel containing internal voids (produced by a process of intering). d) A substitutional solid solution alloy of pure nickel containing 1.16 pct Sn. All the materials were given a high-temperature anneal (>850°C) to produce a stable grain size of 7 to 10 grains per linear mm. The apparatus and techniques used to obtain the present results have been described elsewhere.&apos; In this series, grain growth was observed only in the highest-purity, vacuum-cast metal. Thus we may consider that in the other materials grain-boundary migration was prevented by either preexisting voids or solute atoms. The effect of migration on the creep ductility of the above materials can be seen from Fig. 1, which

Jan 1, 1962

By Hsun Hu, R. S. Cline

The effect of rate of deformation on texture formatiotz has been studied with cube-oriented single crystals of 3 pct Si-Fe, compressed 80 pct at two widely different rates. Compression at a low rate (crosshead speed, 0.1 ipm) produces large orienta-tional changes and coarse deformation bands, whereas little change in orientation is observed, particularly at the surface of the crystal, when compressed at a high rate (impact velocity, -500 ips). Thin plates of mechanical twins are produced at the high rate, but their contribution to the deformation texture is practically negligible. The crystal deformed at a high rate has a lower hardness and a more uniform dislocation structure and is morc resistant to recrystallization. There is also a dilference in the recrystallization texture between the slowly and rapidly compressed crystals. These results indicate that plastic flow is less "turbulent" at high strain rates than at low strain ratcs. THE behavior of metals under high-speed deformation has been the subject of wide study in the past decade. Most of these works were concerned with mechanical properties during testing at high rates of loading, the resulting structures, and the theoretical aspects of the observed phenomena. The present status of knowledge and research activities in this field has been documented in recent publications.17&apos; There is, however, very little information available in the literature concerning the effect of high-speed deformation on the texture formation in metals. The possibility of an effect of rate of deformation on texture is suggested by the microstructural differences observed between normally and very rapidly deformed samples. Aside from the strong tendency for twinning (and phase transformation in certain metals) in high-speed deformation, the slip-line patterns and the dislocation configurations show marked differences as a result of large differences in the strain rates. For instance, in mild steel in static and dynamic compression, Campbell and co-worker3,4 observed that coarse slip occurred on several systems in specimens deformed at normal strain rates, whereas specimens deformed rapidly showed only fine slip on fewer systems, the slip-line pattern being very similar to that in specimens deformed at low temperatures and at normal strain rates. The absence of multiple slip was also noticed by Dieter5 in shock-loaded nickel. The dislocation configuration in an iron shock loaded at 70 kbar pressure was shown by Leslie et al.6 to be similar to that produced by light rolling at low temperature—the dislocation lines were mostly straight and uniformly distributed. These observations suggest that the mode of deformation at high strain rates is notably different from that at low strain rates. Consequently, the nature and the extent of lattice reori-entation during deformation should also be different. This investigation was undertaken to test this idea. MATERIAL AND METHOD The remaining part of a single-crystal ingot of a 3 pct Si-Fe alloy,* prepared for an earlier investi- gation,1 was used in the present studies. Specimens 9/16 in. square and 0.365 in. thick were cut from this ingot with (001) planes parallel to the square surfaces, and the [loo] and 1010] directions parallel to the edges of the specimen, within ±1 deg. These machined crystals were etched to remove distorted metal, and annealed at 1300°C for 24 hr in a purified helium atmosphere. The annealed crystals had a hardness of 161 Dph. The crystal orientation was rechecked with X-ray back-reflection techniques. In high-strain rate experiments the crystal was compressed in a Dynapak machine to approximately 80 pct reduction in thickness (from 0.360 to 0.070 in. with an impact velocity of -500 ips). Thus, the duration of loading was approximately 6x 10-4 sec, and the average strain rate was about 103 sec-1. As a result of this rapid, severe deformation, the specimen became a roughly circular thin disc. The original shape of the crystal, however, could still be recognized by a diffusely outlined square area in the center of the disc. For compression at a low speed, the crystal was deformed in a universal testing machine at a rate of crosshead movement of 0.1 ipm. Compared with

Jan 1, 1965