By W. L. Hunter

The research on this report was conducted to obtain information on the feasibility of producing ferro chromium of varying silicon and carbon contents from domestic chromite. Concentrates from the Mouat deposit were chosen because they typify the chromite found in the Stillwater complex, the largest domestic reserve, and are similar in composition to other extensive North American and foreign deposits. Batch-smelting tests designed to produce high-, medium-, and low-carbon ferrochromium were made in single phase and three-phase, electric-arc, steelmaking furnaces. Agglomeration studies were made in a rotary kiln. Continuous smelting tests were made to yield data on the production of high-carbon ferro chromium and low-carbon ferrochromium-silicon. The carbon content of high-carbon ferrochromium was lowered to the medium-carbon range by oxygen injection. Mouat stockpile concentrates were nodulized in a gas-fired rotary kiln using quartz, limestone, and fluorspar additions in the proportion necessary to flux the slag. The nodules were smelted in a continuous test using coal, coal char, and mixtures of the two consecutively as reductants.

Jan 1, 1961

By R. S. McClain

The Federal Bureau of Mines investigated residues from aluminum plants, to determine if carbon could be removed by flotation while recovering fluorine and aluminum compounds for recycling to the reduction process. This publication summarizes studies on samples representing three types of plant waste products, supplied by three aluminum-producing companies. Samples of flue dust, pot skimmings, and pot linings from the various plants all responded to a simple turpentine flotation scheme to reject 90 to 97 percent of the carbon. Aluminum compound recoveries ranged from 42 to 94 percent on the flue dust, were about 95 percent on the pot skimmings, and ranged from 75 to 89 percent on the pot linings. Fluorine recoveries from the same samples ranged from 35 to 63, 92 to 95, and 77 to 86 percent, respectively. The pot linings contained soluble salts of aluminum and fluorine which were recovered by precipitation with sodium aluminate and carbon dioxide gas. Composites of residues from each plant responded to flotation much the same as the individual samples. Aluminum is produced by the electrolysis of alumina in a molten cryolite bath. The electrolytic reduction cell consists of a carbon-lined box containing a pad of molten aluminum which serves as a cathode, a carbon anode, and an electrolyte of molten cryolite in which the alumina is dissolved. Alumina is reduced to aluminum at the cathode, and carbon is oxidized at the anode.

Jan 1, 1961

By M. A. Hammer

In this study by the Federal Bureau of Mines Pennsylvania anthracite from the Eastern Middle field was oxidized by concentrated nitric acid at steam-bath temperature for 24 to 1,000 hours. The quantitative data obtained include yields of nitric-acid soluble and insoluble products and the distribution of carbon and ash in each. The acid-insoluble residues were examined for solubility in aqueous sodium hydroxide. With a sodium hydroxide concentration of at least 1 normal, a portion of the residue could be extracted in the form of a true solution. With lower alkali concentrations, peptization occurred. Alkali solubility of the residue increased with length of oxidation. However, when expressed in percentages of original coal weight, the alkali solubility remained essentially constant after 192 hours of oxidation. This suggests that the alkali-soluble products are converted to acid-soluble products at the same rate as the original coal substance is converted to alkali-soluble material. Microscopic observations of the peptization of the acid-insoluble residues revealed a gross micellar physical structure. The action of nitric acid is apparently not restricted to the surface of a coal particle. The acid penetrates the particle through the pore structure, dissolving some of the ash and altering the bonds between the coal micelles. The bond alteration, as indicated by ultimate analyses, involves the physical and chemical adsorption of the components of nitric acid. Some of the altered bonds are not thermally stable; this instability is shown by the complete loss of peptizing ability when the acid-insoluble products are heated above 200° C. This loss is accompanied by the evolution of water, oxides of nitrogen, and hydrocyanic acid.

Jan 1, 1961

By Edwin B. Cook

Studies of flame and combustion phenomena at the Bureau of Mines have been facilitated by computer evaluation of the thermodynamic properties of gases formed by constant-pressure burning.4 5 This report is the sixth of a series6-10 presenting results of such calculations; it deals also with constant-volume deuterium-air flames.

Jan 1, 1961

By R. B. Porter

Bench-scale tests were performed by the Federal Bureau of Mines on lignite and subbituminous coal at pressures to 1,000 p.s.i.g. (pounds per square inch gage) in atmospheres of hydrogen or nitrogen to obtain information concerning the influence of pressure on carbonization of normally noncaking coals. The distribution of gaseous, liquid, and solid products as a function of processing pressure was determined. Except for special experiments, the carbonization was at 940° F. In a hydrogen atmosphere above 400 p.s.i.g., agglomeration of the solid residue (especially with lignite) became noticeable and increased directly with the processing pressure. Although in some instances the solid particles fused together, the mechanical strength of the agglomerate was always low. On the basis of visual inspection, the coals agglomerated in the following order of decreasing intensity: (1) Steam-dried lignite; (2) lignite; and (3) subbituminous coal. Addition of lignite tar in quantities to 25 percent by weight of charge did not increase agglomeration or change the carbonization characteristics of the coal.

Jan 1, 1961

By F. P. Haver

The Federal Bureau of Mines developed a 10,000-ampere cell to determine the economic feasibility of producing high-purity electrolytic titanium from mill scrap or offgrade sponge. Operating variables were investigated, matetial handling procedures were established, and the cost of electrorefining titanium was determined. The prototype cell produced premium-grade metal (<100 Brinell hardness number (B.h.n.)) from very impure Kroll sponge at a processing cost of less than $0.60 per pound. Refined metal was deposited at the cathode in the form of coarse (85 percent plus 34-mesh), hexagonal crystals of a titanium when the cell was operated an 850° C. A cathode current density of 1,000 amperes per square foot and a molten sodium chloride electrolyte containing approximately 5 percent by weight of soluble titanium were used. In continuous operation, at the optimum number of ampere-hours, (40,000), the current efficiency averaged slightly less than 60 percent. It was possible to supply large enough amounts of electric current for electrolysis to maintain the temperature of the bath, thus reducing overall power consumption to less than 5 kilowatt-hours per pound of metal refined.

Jan 1, 1961

By Dorothy M. Richardson

The Bureau of Mines has participated in the American Petroleum Institute Research Project 48A (API-RP48A) program on the Separation and Identification of Sulfur Compounds in Crude Petroleum. The lack of reference compounds or infrared spectral data has made difficult the identification of individual sulfur compounds boiling above 140° C. The recent acquisition of 24 alkylthiophnnes has made possible a limited study of this important class of sulfur compounds. The infrared spectra of 2-monoalkylthiophenes and 2,5-dialkylthiophenes for the 2 to 15p range are reported. Correlations for determining the 2-alkyl and 2,5-dialkyl substituted thiophenes are derived from this information. The 2-alkylthiophenes show a unique pattern in the 5.50 to 6.54 region, while the 2,5-dialkylthiophenes show a distinctive pattern in the 5.6µ to 6.7µ region. A skeletal vibration occurs in the 9.5 to 10.0µ region for all of the thiophenes investigated. These data will aid the infrared spectroscopist in the identification of compounds of the type reported.

Jan 1, 1961

By J. L. Konchesky

In gasifying pulverized coal with steam and oxygen, the particle size of the coal fed to a gasifier should be as small as economically possible. A potential way to achieve this advantage is to reduce the particle size of the coal by passing the coal-steam mixture at high velocity through a heated tube coil before the mixture enters the gasifier. To evaluate this method the Federal Bureau of Mines flashed coal-water slurries in externally heated metallic tube coils to determine the extent of size reduction. The first of two different laboratory-scale apparatus reduced the average particle diameter of subbituminous C coal from 190 to 110 microns at an outlet velocity of 330 feet per second (f.p.s.). At the same outlet velocity, a second apparatus reduced the average particle diameter from 250 to 140 microns. An increase in velocity produced more finely divided coal, but variation in temperature and pressure had no effect except as they affected velocity. Virtually the same size reduction was noted for five ranks of coal at equal velocities. The rate of increase in particle-size reduction with increase in velocity decreased with a decrease in particle size. The pulverizing mechanism was concluded to be abrasion of the particles with each other and with the tube wall.

Jan 1, 1961

By T. A. Sullivan

The work described in this report was undertaken to evaluate and develop techniques for determining the oxygen content of titanium and titanium alloys. Early investigations of volatilization techniques involving halogenation were unsuccessful. Later efforts were concentrated on evaluating vacuum fusion and inert-gas fusion techniques. Two vacuum fusion methods and an inert-gas fusion method were found to be satisfactory in the 0.02 to 1.00 pct., oxygen range. These methods are described in detail. The coefficient of variation by any of the three methods is approximately 5 pct, While the main portion of this paper is devoted to the vacuum and inert-gas fusion methods, a resume of other suggested methods for analyzing titanium for oxygen also is given. INTRODUCTION The Federal Bureau of Nines has conducted research on titanium metal since 1938. This research included development of the Kroll process for the production of titanium (2)4, various sodium reduction processes for making titanium metal and lower valent titanium chloride-sodium chloride mixtures (17), and a fused salt electrolytic process for Me production of high-purity titanium metal and the recovery of titanium by electrorefining from off-grade materials (20).

Jan 1, 1961

By Joseph A. Sutton

This study was undertaken by the Bureau of Mines to determine whether the sulfur-oxidizing bacterium Thiobacillus thiooxidans could use sulfur compounds to produce sulfuric acid in sufficient quantities to leach valuable metals from low-grade ores. The results of extended tests indicated that the bacterium is capable of extracting appreciable amounts of copper and cobalt from ore and mineral samples when sulfur is available in a state that can be readily assimilated by the organisms. Under the conditions of these tests, this organism was not able to assimilate and oxidize the sulfur as it occurred in the ores and minerals. Ores containing copper minerals in the silicate, carbonate, and oxide forms, in the presence of elemental sulfur, were more susceptible to bacterial action than ores containing copper minerals in the sulfide form. Thiobacillus thiooxidans remained active on elemental sulfur in the presence of some of the ores which were tested, but could not tolerate others. Therefore, strains of the bacterium were progressively adjusted to increasing concentrations (0.5 to 10 grams) of the individual ores until they could remain active on 10-gram portions of all ores being tested.

Jan 1, 1961

By W. S. Sanner

Anthracite was used extensively as a fuel in iron metallurgy from 1840 to 1880. In 1874, 226 of the 680 blast furnaces in the United States were operating on anthracite and producing almost one-half of the Nation&apos;s pig iron. However, by 1890, railroad expansion, the development of western iron-ore reserves, and the growing use of coke decreased the importance of anthracite as a metallurgical fuel. As a result, the last blast furnace designed exclusively for anthracite use was built in 1891. Because of the increased energy requirements of our expanding national economy, the abnormally high demands during national emergencies, and the proximity of anthracite deposits to eastern steel-producing areas, interest has grown in again using anthracite in iron metallurgy. Estimates of anthracite reserves indicate a 300-yr. supply at a production rate of 30 million tons per year. These large reserves dictate the development of an adequate technology for the use of anthracite by the metallurgical industry.

Jan 1, 1961

By Donald W. Mitchell

Studies were made in the Bureau of Mines Experimental coal mine to evaluate the effectiveness of a few extinguishing agents and techniques for controlling a fire on a simulated mining machine. The investigation showed that water containing an alkali-metal salt or a surface-active (wetting) agent was more effective than water alone. For close attack, fog applications was the most effective technique studied; high rates of agent application controlled the fire more quickly than low rates. The ability to control the fire increased as the distance of attack decreased. Dry powders controlled the fire when applied by shovel but not when applied airborne by rock-dust distributor or by hand fire extinguishers. Dry alkali-metal salt powders (potassium and sodium bicarbonates and sodium tetraborate) quenched the fire more readily than limestone dust. In each instance the finer powder, the greater its effectiveness. In an open ventilated entry, smoke and hot gases backed against the air currents. An airspeed of 230 feet per minute was required to permit approach to within 10 feet of the fire. At lower airspeeds, approach could be made by extending the brattice across the bottom two-thirds of the entry, by pushing the smoke ahead with water sprays, or by discharging dust from a rock-dust distributor. In a dead-end entry, the fire was approached to within 30 feet by coursing fresh air along an airtight line brattice; however, it was safer, easier, and less time-consuming to attack the fire from a fresh-air base 100 feet away with a solid stream or by high-expansion foam; the latter method was more effective.

Jan 1, 1961

By J. R. Nettle

The purpose of these studies by the Federal Bureau of Mines was to determine the feasibility of refining low-grade hafnium by an inert-gas-shielded molten-salt electrorefining technique to produce a hafnium metal meeting reactor specifications. The techniques were adapted from those used success-fully for titanium electrorefining. Three electrolytes containing hafnium chlorides were developed from which deposits having a Brinell hardness of 170 or below were recovered. A KC1 + NaC1 + HfC14 electrolyte produced deposits in the hardness range of 140 to 165 Brinell. Deposits with a hardness range of from 132 to 152 Brinell were pro-duced from an electrolyte composed of KC1 + LiC1 + HfC14. A third electrolyte composed of NaC1 + K3HfC17 produced deposits with a hardness as low as 139 Brinell. In a fourth electrolyte, composed of NaC1 + K2HfF6, a measure of refining was accomplished, but under the test conditions no metal meeting specifications was recovered; none was softer than 174 Brinell. A number of metallic impurities were reduced in quantity by the electro-refining process, notably iron, which normally was reduced from 250 p.p.m. to less than 50 p.p.m. Magnesium generally was reduced from 680 p.p.m. to less than 80 p.p.m. Manganese content was also reduced by the electrorefining process. Sponge containing 90 p.p.m. Mn yielded deposits containing a maximum of 50 p.p.m.; some deposits contained only 10 p.p.m.

Jan 1, 1961

By R. J. Leary

Iron and steel scrap has accounted for 45 to 50 percent of the metallics used by the steel industry. In an electric furnace which utilizes a 100-percent cold charge consisting of about 99 percent scrap and 1 percent pig iron, sensible heat from molten pig iron is not present as it is when hot metal is charged to open hearths and converters. A study of means for more efficient utilization of iron and steel scrap in steelmaking indicated that the time and fuel requirements to melt scrap were important cost factors, particularly in arc-furnace steelmaking. A process to preheat scrap economically prior to charging into the arc furnace has been developed, utilizing efficiently the heat from combustion of fossil fuels as a substitute for electric-arc heating in the initial stage of arc-furnace steelmaking. Scrap is loaded into a portable vertical cylindrical furnace body that is open at the top and has a perforated dropout door at the bottom. In the heating operation, the furnace body containing scrap is placed upon a hollow base connected to a flue, and then the burner and combustion-chamber unit is lowered on top of the furnace body. The stream of hot-combustion products flows down through the bed of scrap imparting heat to it, and the cooled gases exhaust through the flue. After the heating operation the furnace body containing hot scrap is transported to the arc furnace for charging. Thus, the furnace body serves as a charging bucket for top-charged arc furnaces, enabling this preheating process to be integrated into existing material-handling patterns in many arc-furnace plants.

Jan 1, 1961

By H. E. Peterson

Rhenium occurs in very small quantities (12).4 In order for the Federal Bureau of Mines to conduct an investigation of rhenium sources and methods of extraction, it was necessary to devise improved techniques for detecting and measuring minute quantities of the metal. A modification of the procedure of Malouf and White (46) was developed which can be used to detect rhenium in concentrations as small as 0.1 part per million and can be used to measure quantities of 1.0 part per million. It can be used for the analysis of siliceous and calcareous ores, of molybdenite concentrates, of fumes, of flue dusts, and of other metallurgical products. Development of the method involved devising an amine extraction procedure for separating rhenium from all interfering elements except tungsten and a selective distillation procedure for separating rhenium from tungsten. Adoption of these separation procedures permits use of large samples and precise determination of rhenium by colorimetric analysis of the thiocyanate complex of rhenium by means of a spectrophotometer.

Jan 1, 1961

By Charles B. Kenaban

The possibility of using ultrasonic energy as a tool to improve the electrolytic deposition of copper and zinc from several electrolytes was investigated by the Federal Bureau of Mines. Sound with frequencies of 20, 26, 38, and 400 kilocycles per second and acoustical intensities of 0.25 to 1.5 watts per square centimeter was employed. Measurements of cell voltage, anode and cathode current efficiencies, and electrode potentials were made at various current densities. Effects of ultrasonics on the quality of the deposit and on anode corrosion also was noted. In the electrolytic recovery of copper from an acid copper sulfate solution at 50° C., adherent, well-consolidated deposits are normally obtained up to a current density of 30 amperes per square foot. As the current density is increased above this value, the deposits normally become progressively more spongy and less adherent. Ultrasonic irradiation resulted in adherent and well-consolidated deposits at current densities up to 300 amperes per square foot. Radiation also produced smaller grain size and preferred orientation of the copper crystals. In addition, radiation caused as much as 3-volt decreases in cell voltages at the higher current densities. These decreases were caused chiefly by depolarization of the anode, although small depolarization effects were also noted at the cathode. Radiation apparently did not greatly affect cathode-current efficiencies, but prevented excessive anode corrosion at the higher current densities and resulted in more uniform corrosion. Ultrasonic radiation at a frequency of 400 kilocycles per second was not as effective as radiation at the lower frequencies. Circulation of the electrolyte at rates up to 5 percent of the cell capacity per minute did not produce results comparable to those effected by ultrasonic radiation. Rapid rotation of the cathode up to 1,800 revolutions per minute gave results approaching those obtained with ultrasonics.

Jan 1, 1961

By K. K. Kershner

This report describes an investigation by the Bureau of Mines designed to provide background data for extending and improving the applications of chlorine metallurgy in extracting metals from ores. Optimum conditions are given tor chloridizing galena, sphalerite, and chalcocite by contact with chlorine gas. Petrographic and chemical analyses of the sulfides used in the experiments are listed. Graphs are furnished showing the extent of chloridization of each metal sulfide over the temperature range of the observations. In each case, the first tests were made with the reaction chamber at room temperature. This temperature was increased by regular increments in succeeding tests until the temperature was reached at which quantitative conversion of the sulfide to chloride was observed. The data are also plotted for screen-size fractions of the sulfide minerals investigated. Data show that the extent of metal chloride formation was affected by chloridization time, particle size of the sample, and usually, the temperature of the reaction chamber. At 300° to 400° C. an anomaly was noted for both galena and sphalerite. The temperature at which this anomaly was observed varied according to the particle size of the mineral. Comparisons are made between the chloridizing characteristics of the mineral sulfides and their chemically prepared counterparts.

Jan 1, 1961

By R. J. Leary

Significant improvements in surface conditions or mechanical properties of steels have been attributed by several investigators to ladle additions of small quantities of rare-earth metals or their oxides. To investigate systematically these effects in wrought and in cast plain carbon and alloy mechanical steels containing approximately 0.35 percent carbon, heats of four representative compositions were melted by the Bureau of Mines in a 4-ton open-hearth furnace. Each heat was cast into three sets of ingots to exemplify respectively, treatments with (1) rare-earth metals, (2) rare-earth metal oxides, and (3) an untreated set as a control. The development of melting, casting and rolling practices is described and discussed. Lance injection of oxygen shortly after melt raised the temperature of the metal immediately as much as 500° F., principally because mechanical agitation exposed the high-carbon metal to the flame and furnace root. An exceptional degree of superheat in the metal at the termination of the refining period was attributed to oxygen injection during the refining period. Bath temperatures higher than industrial practice were permitted by the all-basic furnace lining. Rates of carbon elimination as high as 0.036 percent carbon per minute were achieved by oxygen injections.

Jan 1, 1961

By Joseph Grumer

An instrumented spherical vessel has been used for many years to study laminar combustion waves. Concurrent measurements of flame speed and pressure-rise rates have led to evaluations of burning velocities, the pressure dependence of the burning velocity, and the expansion ratios of the gases passing through the combustion wave. For the most part, these studies have involved flames initially at atmospheric or subatmospheric pressure. The old spherical vessel used by the Bureau of Mines was not designed for use at elevated pressures. Moreover, being made of wrought iron, it was susceptible enough to corrosion to prohibit its use with many combustible mixtures that figure in industrial research. In mid-1956, under sponsorship of the Office of Naval Research, the Bureau undertook the development of a stainless steel spherical vessel capable of withstanding explosions of gaseous mixtures at initial pressures as high as 20 atm. and initial temperatures as high as 250° C. The design called for a double array (cross) of closely spaced small windows for observation of the flame as it traversed the vessel and a piezoelectric transducer to measure concurrently pressure-rise rates. Because no commercial contractor was willing to bid on the construction of such a vessel, it was built at the Bureau&apos;s Bruceton machine shop.7

Jan 1, 1961

By F. E. Brantley

Research was undertaken by the Bureau of Mines to assess the technical feasibility of smelting cement-copper precipitate in an electric furnace to produce commercial-grade copper. The blister-grade copper produced in smelting was refined by gaseous oxidation and reduction methods to rive a product equal in quality to fire-refined copper. The cement copper used in the study was typical of the material produced in commercial operations. The sample product was received in a partially oxidized state and analyzed 77.5 percent Cu, 3.4 percent Fe, 0.8 percent Pb, 0.05 percent Ni, 0.6 percent Sn, and 0.9 percent S. Smelting tests were made on the precipitate using laboratory-size induction and electric-arc furnaces. Three types of furnace linings were tested during, the investigation: Carbon, including graphite; clay-graphite; and silicon carbide. Although all proved satisfactory, either carbon or graphite was preferred because of their superior refractory properties and low permeability to molten copper. Copper recoveries in the induction and arc smelting tests averaged 92 percent in commercial-grade metal assaying 99.8 percent copper. Refining the molten copper by oxidation and gaseous reduction or by chlorine lancing increased the purity to plus 99.9 percent.

Jan 1, 1961