By K. L. Komarek

Based on theoretical and experimental evidence a discussion follows of the behavior of phosphorus -bearing iron ores in the R-N Direct Reduction Process and suggestions are made of methods of reducing the amount of phosphorus in the metallic end product. In ferrous metallurgy a direct reduction process is one in which iron ores are reduced to metallic iron with gaseous or solid reductants without the appearance of a liquid phase. A number of attractive features have induced several companies and government agencies to invest in the development of direct reduction processes. A summary of all direct reduction processes up to 1954 has been given by Barrett,' and Wiberg,2 and Willems3 have reviewed the most recent developments in this rapidly expanding field. Many difficulties have been encountered in direct reduction processes and the nature of these difficulties has varied from process to process. One problem common to almost all of them is the removal of phosphorus which is one of the reasons for the rather pessimistic outlook given by some government publications4'5 to direct reduction processes. In this paper an attempt is made to give a theoretical explanation of the variations in phosphorus removal observed in the R-NY Direct Reduction Process. However, many conclusions are general enough to be applicable to other processes. Most iron ores treated by the R-N process yield products lower in phosphorus than the original ore. A qualitative account of the factors has been given by Stewart, Reed, and Herasymenkoe but the erratic removal of phosphorus from some ores and the general importance of this problem make a more careful analysis of the theoretical aspects desirable. In the R-N process mixed ore or balled fines, ex-

Jan 1, 1963

By P. T. Carter, A. B. Murad, H. B. Bell

N. A. Gokcen (Michigan College of Mining and Technology, Houghton, Mich.)—The activities of silica, represented in Fig. 5 for the systems MnO-SiO2 and CaO-SiO2, are in disagreement with the established binary phase diagrams. At Ns102 = 0.50 in MnO-SiO2, and at Ns102, = 0.65 in CaO-SiO2, each binary system is saturated with respect to silica at 1550°C, and therefore as102, is unity in each case. The curves for as102 (FeO-SiO2) and as102, (MnO-SiO,) should nearly co-

Jan 1, 1953

By S. K. Tarby, W. O. Philbrook

Limited experimental data and a critical review of the literature are given to indicate that the true equilibrium distribution of manganese between carbon-saturated iron and blast-furnace type slags has not yet been satisfactorily established as a function of the composition, temperature, and pressure of the system. THE distribution of manganese between carbon-saturated iron and blast-furnace type slags has been studied by a number of investigators.1-7 Generalization of the results of these works indicates that the weight percent distribution ratio, (%Mno)/[%Mn], decreases with increasing temperature and slag basicity, in accord with thermodynamic data and practical observation. However, where comparisons among these studies can be made for similar slag compositions and temperatures, the reported values of the manganese distribution ratio are discordant. The variations are attributed to failure of the experimenters to bring their systems completely to equilibrium with graphite and CO at 1 atm, as judged by departures from silicon equilibrium. Even in the most recent work,5-7 this problem was recognized but the authors made the questionable assumption that equilibrium could prevail for manganese distribution even though other reactions were still in progress. Manganese equilibrium values for three particular slag compositions were required incidental to a kinetic study8 and were determined experimentally. Special pains were taken to approach concurrent equilibrium with respect to silicon. Although the results were not completely definitive, they indicate that the true manganese equilibrium distribution ratios are lower than have heretofore been reported. The data are presented together with a brief commentary on the literature to suggest the need for further work in this area. EXPERIMENTAL METHOD Equilibrium runs were carried out in a stationary, induction-heated graphite crucible closed by a graphite lid and flushed continuously by a slow flow of carbon monoxide at 1 atm pressure. Temperature was controlled manually within ±3 deg C with the aid of immersed thermocouples in mullite tubes protected against slag attack by graphite sleeves. The desired temperature was established by a calibrated Pt vs Pt-10 pct Rh thermocouple and control was then maintained using a more stable W-Mo couple. Runs were made at 1500º and 1575ºC for durations of 7.5 to 10.5 hr. The charges were calculated to yield 400 g of metal and 100 g of slag. The primary slag compositions and designation numbers were as follows:

Jan 1, 1963

By Avnulf Muan, P. V. Riboud

The effect of Cr2O3 on melting relations of iron oxide at oxygen pressures slightly above those prevailing in contact with metallic iron has been determined. Liquidus and solidus temperatures of wüstite are raised by the addition of Cr2O3, from 1385°C for pure iron oxide to 1420°C at the peri-ledie point where wüstite, iron chromite, liquid, and gas coexist in equilibrium under the atmospheric conditions used in the present investigation (CO2/H2 = 1). It has been shown in a previous investigation1 that the liquidus and solidus temperatures of iron oxide are drastically increased by the addition of Cr2O3 under the relatively oxidizing conditions prevailing in air. This is to be expected in view of the easy substitution of cr3+ for Fe3+ in crystalline oxide structures which are stable at high oxygen pressures, as demonstrated for instance by the completeness of the solid solution series Fe2O3-Cr2O3 at high temperatures (>1000°C). The stable phase of iron oxide at oxygen pressures approximating those prevailing when metallic iron is present is wüstite. This phase, although commonly represented by the simplified formula FeO for sake of convenience, in reality has a defect structure in which a part of the iron ions are present as Fe3+. It is to be expected that at least a limited amount of cr3 ions will substitute for Fe in this structure when Cr2O3 is added to wüstite. Depending on the ease of this substitution in comparison with that of cr3 substitution for Fe in iron oxide-Cr2O3 liquids under the same atmos- pheric conditions, the liquidus and solidus temperatures of wüstite may increase or decrease upon addition of Cr2O3. The methods of establishing these melting relations and the results obtained are presented in the following. I) EXPERIMENTAL METHOD 1) General Procedure. The quenching technique was used in this study. Oxide mixtures were heated at chosen constant temperatures in an atmosphere consisting of equal parts of CO2 and H2 until equilibrium was established among gas and condensed phases. The samples were then quenched in mercury to room temperature, and the phases present were determined by microscopic and X-ray investigation. 2) Preparation of the Mixtures. Starting mixtures were prepared by weighing and thoroughly mixing Fe2O3 and Cr2O3, or wüstite and Cr2O3. The Fe2O3 and Cr2O3 used were "Baker Analyzed" reagent grades, whereas wüstite of composition was synthesized by reducing Fe203 at 1325°C in an atmosphere consisting of equal parts of CG andHz. In order to avoid contact with crucibles, the equilibration runs were made with small pellets suspended from thin (-0.004-in.) platinum wires. Mixtures made from FOs and Cr203 were readily pelletized at a pressure of 500 atm in a 9.5-mm die, whereas mixtures made from wüstite and Cr203 when treated identically were too weak for handling. In order to obtain a stronger product, these pellets were sintered by heating for 2 min at -1200°C in the same atmosphere as was subsequently used for the equilibration runs (CG/H2 = 1:1). During the sintering, these pellets were wrapped in thin (0.0004-in.) platinum foil, which was stripped off before the equilibration runs. In order to reduce the time needed for equilibrium to be attained, preliminary equilibration of relatively large pellets of each mixture was carried out at -1200°C for 4 to 12 hr. Smaller pellets

Jan 1, 1964

By J. P. Morris

PREVIOUS investigations1,2 have shown that alloying elements in liquid iron influence the thermodynamic activity of sulphur and thereby affect the partition of sulphur between metal and slag in the desulphurization process. For example, the greater efficiency of desulphurization in the blast furnace as compared to the open hearth can be attributed in part to a higher level of sulphur activity in blast-furnace metal due to the higher concentration of carbon and silicon. In the present investigation, a short study was made of the influence of manganese on the activity of sulphur in liquid iron and iron-carbon alloys. In contrast to carbon and silicon, manganese was found to decrease the activity coefficient of sulphur; and in iron-carbon alloys it counteracts to some extent the influence of carbon. However, at manganese concentrations normally present in the blast furnace or open hearth, the effect of manganese is small. Since manganese sulphide has a limited solubility in iron, manganese can act, under certain conditions as a desulphurizing agent. Considerable data on the manganese-sulphur product in carbon-saturated melts were obtained in the investigation and have been included in this report. The experimental procedure was the same as that used in the earlier investigations on the effect of silicon' and carbon' on sulphur activity. Briefly, the method was as follows: The molten alloy, contained in a graphite or sintered alumina crucible, was brought to equilibrium at a constant temperature with a mixture of hydrogen and hydrogen sulphide of constant composition by bubbling the gas through the metal. Samples of' the melt were taken for analysis at regular intervals by suction through a 2 to 3 mm bore silica tube dipped into the metal. The experiments were run in a graphite spiral resistance furnace with melts weighing 50 to 60 g. The gas bubbling tubes were made of sintered alumina and were 5/16 in. OD, 1/16 in. ID, and 24 in. long. Equilibrium was assumed to have been attained when the sulphur content of the liquid metal reached a constant value. During an experiment there was a rapid loss of manganese from the melt by volatilization. To offset this loss, small additions of manganese were made periodically. The rate of manganese addition needed to maintain a constant manganese concentration was determined in preliminary tests. In all of the experiments, deposits of manganese sulphide formed above the melts in a cooler region of the furnace. Apparently, these deposits resulted from a reaction between manganese vapor and hydrogen sulphide in the gas. To prove that manganese sulphide did not volatilize from the melts to a measurable extent, an experiment was run in which helium was bubbled through liquid iron containing both manganese and sulphur. Although manganese volatilized rapidly in this test, there was no appreciable loss of sulphur. Volatilization of manganese sulphide from a melt would have led to an apparent equilibrium condition in which the sulphur content of the metal was lower than the true equilibrium value. The experimental results are shown in the first seven columns of Table I. The data in the last two columns were obtained from the previous work on the effect of carbon' and show what the results would have been in the absence of manganese but with temperature, gas composition, and carbon content of the metal remaining the same. Comparison of the last four columns show that, in the presence of manganese, the sulphur content of the metal increased at equilibrium and the activity coefficient of sulphur decreased. However, the results show that, for manganese concentrations below 3 pct, the effect of manganese is small. The values for activity coefficient of sulphur given in Table I were calculated from the following relations: S (in liquid metal) + H2 (gas) = H2S (gas) [l] K ph2s/?s X %S X phg = 0.00251 [2] where K is the equilibrium constant for the reaction, PH2S and ph2 are the partial pressures of hydrogen sulphide and hydrogen, respectively, and ?s is the activity coefficient of sulphur. The standard state for sulphur was taken to be a 1 pct solution of sulphur in pure iron. The numerical value for K at 1600°C was determined in the earlier work. For the purpose of showing graphically the results of the tests run at 1600°C, the activity coefficients of sulphur were recalculated so as to correspond to a manganese concentration in the metal of 2 pct in each case. In the calculation it was assumed that the increase in sulphur content of the metal at equilibrium caused by the presence of manganese

Jan 1, 1953

By R. H. Gautschi, F. C. Langenberg

Rare-earth additions were made to laboratory heats of Type 310 stainless to observe their effect on as-cast ingot structure, nitrogen and sulfur contents, and nonmetallic inclusions. Lanthanum had a grain-refining effect in 30-lb ingots, but results with 200-lb ingots were inconsistent. Cerium, lanthanum, and misch metal lowered the sulfur content when the sulfur exceeded 0.015 pct and the rare-earth addition was greater than 0.1 pct. The rare-eardh content in the metal dropped very rapidly within the first few minutes after the addition. The size, shape, and distribution of nonmetallic inclusions was not changed in 30-lb ingots, but changes were noticed in larger ingots. RARE-earth* additions have been made to austenitic Cr-Ni and Cr-Mn steels to improve their hot workability. The high alloy content of these steels often results in a considerable resistance to deformation and inherent hot shortness at rolling temperatures, particularly in larger ingots. Rare earths in the metallic, oxide, or halide form are usually added to the steel in the ladle after deoxidation although they can be added in the furnace prior to tap or in the molds during teeming. The literature- indicates that the effects of rare-earth treatments on these stainless steels are not consistent, and sometimes even contradictory. Since no mechanism has been presented which satisfactorily accounts for the claimed improvements, the effects of rare earths are a qualitative matter. The work described in this paper was initiated to expand the knowledge of the effects of rare-earth additions on melting variables such as ingot structure, chemical analysis, and nonmetallic inclusions. REVIEW OF LITERATURE Ingot Structure—Rare-earth additions to stainless steels have been reported to cause a change in primary ingot structure in that there are fewer coarse columnar grains. However, the results are inconsistent. While one investigation1 has shown a large reduction in coarse columnar crystals, another2 has been unable to observe this effect, particularly when small ingots were poured. Post and coworkers3 observed ingot structures for a number of years and found that the columnar type of structure is not definitely a cause of any particular trouble in rolling or hammering, provided the alloy is ductile. Knapp and Bolkcom4 found rare-earth additions to be quite effective in preventing grain coarsening in Type 310 stainless steel. Chemical Analysis—Many effects of rare-earth treatment on chemical analysis have been claimed in the literature. Russell5 observed that some sulfur is removed by rare-earth metals, and that a high initial sulfur content improved the efficiency of sulfur removal. Lillieqvist and Mickelson6 report that rare-earth treatment causes sulfur removal in basic open-hearth furnaces, but not in basic lined induction furnaces. Knapp and Bolkcom found no sulfur removal in acid open-hearth and acid electric furnaces, probably because the acid slag can not retain sul-fides. snellmann7 showed that sulfur could be lowered apprecfably with rare-earth additions; however, a sulfur reversion occurred with time. Langenberg and chipman8 studied the reaction CeS(s) = Ce(in Fe) + S(in Fe), and found the solubilit product [%Ce] [%S] equal to (1.5 + 0.5) X 10-3'at 1600°C. Results in 17 Cr-9 Ni stainless were about the same as those in iron. Beaver2 treated chromium-nickel steels with 0.3 pct misch metal and observed some reduction in the oxygen content. He also noted an inconsistent but beneficial effect of rare earths when tramp elements were present in amounts sufficient to cause difficulty in hot working. It is not known whether rare earths reduce the content of the tramp elements or change the form in which these elements appear in the final structure. No quantitative data are available concerning a possible effect of rare-earth treatment on hydrogen and nitrogen contents. However, Schwartzbart and sheehan9 stated that additions of rare earths had no effect on impact properties when the nitrogen content was low (0.006 pct), but served to counteract the adverse effects of high nitrogen content (0.030 pct) on these properties. Knapp and Bolkcom4 analyzed open-hearth heats in the treated and untreated conditions and found the nitrogen content (0.006 pct) to be unaffected. These two results lead to the speculation that rare-earth additions can reduce the nitrogen content to a certain level. Decker and coworkers10 have observed that small amounts of boron or zirconium, picked up from magnesia or zirconia crucibles, increased high-tem-

Jan 1, 1961

By D. J. Carney, C. W. Boquist, E. C. Rudolphy

Effect of variations in sinter feed composition on sinter strength, bulk density, re-ducibility, chemical composition, and microstructure were determined by sintering experimental samples on a production sintering machine. Increasing amounts of roll scale, ore fines, return fines, and blast furnace slag were most beneficial to feed permeability, sinter bulk density, and strength. Burnt lime additions improved feed permeability but were not beneficial to sinter strength or bulk density. Sinter reducibility was adversely affected by all additives. DEVELOPMENT of methods for evaluating sinter quality, which would in some way predict the behavior of the sinter during charging and smelting in the blast furnace, has been given considerable attention in recent years. In a previous investigation at South Works of the United States Steel Corp., standard sinter sampling and testing procedures were developed.1,2 By modifying the sinter sampling device, a method of sintering experimental mix sinter samples upon a production Dwight-Lloyd sintering machine was also developed. This technique afforded a rapid and controlled method of investigating the effects of the various raw materials and additives on sinter quality and was used in this present investigation. Since the beginning of the present study in 1953, the results of numerous sinter investigations have been published, most of which were concerned with production tests of iron ore sinter, both here and abroad. Three groups of investigators reported results of experimental sinter studies that were related to this investigation. Voice et al.3 studied the effects of controlled variables on sinter quality by producing and testing experimental Northants iron ore sinter using an experimental sintering unit. Mor-rissey and Powers' determined the relationship between iron ore sinter quality and the moisture and coke content using a small laboratory sintering system. Burlingame et al.5 studied the effects of "additives" upon iron ore sinter using a laboratory sintering apparatus and laboratory grade raw materials. At South Works, it was considered desirable to study the effects of sinter mix composition and additives upon the quality of a flue dust-base sinter produced on a production sintering unit. Extrapolation of controlled laboratory test data to sintering plant operation lacking such precise control is not altogether satisfactory. Therefore, the present study was conducted in a manner which approximated production conditions as closely as possible. The raw materials used were those commonly encoun- tered in the production of flue dust and flue dust ore-type sinters and these were varied within extremes encountered in this type of sinter production. Experimental Procedure The experimental sinters were produced from 100 lb mixtures of sinter feed. The principal raw materials and additives used, their particle size, and approximate chemical composition are listed in Table I. The mixing of the raw materials was accomplished by means of a miniature single shaft pug mill shown in Fig, 1. The use of the pug mill as a mixer was decidea upon after encountering difficulty in reproducing the mixing and chopping effect of the sinter plant pug mill with other types of available small mixers. The miniature pug mill was constructed, consisting of 31/2x2x1/4 in, blades spaced 3 in. apart along a 3 ft shaft. Preliminary tests were run with this small mixer to establish the proper rotation speed and the required number of passes through the pug mill to thoroughly mix and distribute all the raw materials in a manner approximating the production Pug mill- Although the effects of varying the mosture content were determined in one particular series of tests, the amount of moisture added was changed as the composition of the experimental mix was varied. The aim in making water additions was to achieve a permeability as high as possible for each particular

Jan 1, 1956

By F. R. Cattoir, R. W. Kimball, C. T. Anderson

ONE of the principal impurities in all steels is sulphur. Sulphur-bearing, manganese-free steels exhibit hot shortness. Manganese is added to steel to improve the hot-working properties. If no sulphur were present in steel, it is probable that hot shortness would be nonexistent. This paper is the first of a series to be issued by this Laboratory reporting the measurements of hot forgeability tests and the physical properties of Fe-C alloys to which additions of various alloying elements have been made. The present paper describes the results- obtained by the addition of varying amounts of sulphur to Fe-C alloys. To obtain control over residual elements in the various charges melted in the arc furnace, it was considered advantageous to use sponge iron from one source as the melting stock rather than scrap metal having an unknown history. Small amounts of unwanted alloying elements might be introduced into the charge when scrap was used, thereby influencing the results of the various heats. A sponge iron having a high silica-lime ratio was used. Ore from Sunrise, Wyo., had been reduced to sponge iron and briquetted at the Bureau of Mines sponge-iron plant at Laramie, Wyo. The briquettes were 5 in. in diam and 2 to 3 in. in thickness, and weighed about 10 lb each. The chemical analysis of the sponge iron is as follows: C, 0.67 pct; Mn, 0.10; SiO2, 4.75; CaO, 1.4; P, 0.044; S, 0.72; MgO, 0.4; A12O3, 1.1; total Fe, 87.5; Fe metallic, 79.2; and reduction, 90.5 pct. Where a reducing agent was required, crushed graphite electrodes usually were used. The charcoal available contained 0.20 pct S. An analysis of the available coke showed it to contain 0.70 pct S. Where high sulphur heats were required, elemental sulphur additions were made to the ladle. Limestone of good quality was obtained locally and had the following analysis: CaO, 53.7 pct; MgO, 0.8; ignition loss, 42.4; R2O3, 0.2; SiO2, 3.0; and P2O5, 0.014. Melting Procedure Sponge iron was melted to produce metal stock for the experimental alloys in a silica-lined, three-phase, direct-arc, size ST, Moore Rapid Lectromelt furnace with a 500 kva rating. Fig. 1 shows this furnace installation. About 25 tons of sponge iron was melted in 75 heats, averaging 927 lb of sponge iron to the heat. An addition of carbon was required to complete the reduction of a portion of the iron oxide remaining in the sponge to prevent high losses of iron oxide in the slag and a low carbon content in the resulting metal. As reducing agents in preparing the melting stock, charcoal, coke, and a carbon product resulting from the thermal decomposition of natural gas were used. The quantity varied from 20 to 60 Ib per furnace charge, with an average of 38 lb. An average analysis of the metal obtained gave 0.52 pct C, about 0.01 pct Mn, 0.070 pct P, and 0.092 pct S. The average yield of metal was 647 lb with 241 1b of slag, the sponge-iron recovery being 70 pct. The metal obtained in melting the sponge iron was cast into pigs weighing about 20 lb each to facilitate recharging into the furnace for further refining. The pouring of the pigs is shown in Fig. 2. The average power consumption for the production of the 24 tons of metal obtained was 1704 kw-hr per ton.

Jan 1, 1954

By H. A. Hancock, L. M. Pidgeon

Equilibrium carbon monoxide pressures were measured over the reaction between chromium oxide and a number of solid ferrochromium alloys in the composition range 0.4 to 4.8 pct C and 0 to 49 pct Fe. Measurements were also made for the carbides Cr23C6 and Cr7C3 which agreed well with previous investigations. Between 1050°and 1400°C the pvessures varied from 0.1 to 56 mm and increased markedly with the iron and carbon contents of the alloys. The data were used to estimate the activity of carbon in the alloys and to calculate the equilibrium conditions for the decarburization of a useful range of ferrochromium alloys. WHEN ferrochromium is produced by the reduction of chromite with carbon in an electric arc furnace it invariably contains up to 10 wt pct C. For many purposes such as the production of stainless steel, it is necessary that the carbon content be as low as from 0.02 to 0.05 pct. Thus an important part of the ferrochromium industry consists of the production of low carbon ferrochromium. The classical Bessemer steelmaking technique cannot be used to oxidize low carbon contents in chromium and ferrochromium alloys without also oxidizing the chromium. Recently a new commercial process2-4 has been introduced for oxidizing carbon from high chromium content alloys which consists of heating the solid alloy with such oxidizing agents as Cr2O3, Fe2O3, or SiO2 in a retort at reduced pressures. By maintaining the carbon monoxide pressure below the equilibrium value for the system, the carbon can be removed as carbon monoxide without oxidizing the chromium. The equilibrium conditions for the decarburization of solid chromium carbon alloys have been determined by Boericke5 who measured the carbon monoxide pressure over the reaction between the various chromium carbides and chromium oxide. A typical reaction is shown below. Cr23C6 + 2Cr2O3 =u 27Cr + 6CO [1] These values are not applicable to the decarburization of commercial ferrochromium alloys which invariably contain major amounts of iron. The present investigation was therefore undertaken to measure the change in the equilibrium carbon monoxide pressure brought about by additions of iron to the Cr-C-0 system, thus extending the work of Boericke into the region of the production of low carbon ferrochromium. MATERIALS AND METHOD Materials. Measurements were made on two carbides of chromium, Cr233C6 and Cr7C3, and fifteen Fe-Cr-C alloys. The chromium carbides were made

Jan 1, 1963

By J. Chipman, N. J. Grant, H. L. Bishop, H. N. Lander

Data of several studies on the equilibrium between molten iron and open hearth-type slags have been combined to determine some of the chemical reactions involved in steel-making. Effects of slag composition and temperature on the iron oxide activity, distribution of sulfur between slag and metal, and the carbon content of the metal are discussed. Also, an overall reaction for the equilibrium between sulfur and oxygen is presented. DURING the past 15 years, a number of significant equilibrium studies have been carried out between liquid iron and simple basic and acid slags in an effort to throw light on the chemical reactions involved in steelmaking. This paper is a summary of the experimental reports on investigations which have been conducted at the Massachusetts Institute of Technology, and of related work in other laboratories. The investigations summarized in this paper include the works of Fetters and Chipman1 and Taylor and Chipman,' which dealt with simple slags that are similar to those found in the open hearth. The sulfur determinations of the slag-metal tests of Fetters and Chipman as reported by Grant and Chip-man" are included. Also, the investigations by Win-kler and Chipman' and Grant and ChipmanQ f more complex slag systems are included in this summary. The experimental procedure is described in detail in each of these papers and will not be discussed. Since the previous reports have been somewhat independent, it is desirable to review and combine the data of the various investigations to determine, as accurately as possible, the reactions in the slag-metal systems of the open hearth. It is the object of this report to present the combined data in such a way as to enhance their utility and applicability. Oxidizing Power of Slags of the System (CaO+MgO)-Si0,-FeO in Equilibrium with Carbon-Free lron The slags selected to determine the iron oxide activity in equilibrium with pure liquid iron were those containing less than 2 pct each of P,O,, MnO, or A1,0, on a weight percentage basis. The method used to calculate activities of iron oxide in liquid slags was that developed by Taylor and Chipman.' The solubility of oxygen in molten carbon-free iron under pure iron oxide slags can be expressed by the following eauation —6320 log (pctO)-------------— + 2.734 [1] where T is the absolute temperature. The oxygen solubility values as determined from Eq. 1 were used throughout this study to calculate the iron oxide activity. The iron oxide activities of slags of various iron oxide contents are plotted in Fig. 1 as a function of the basicity, which is defined as the ratio (pct CaO + pct MgO)/pct SiO,, and are based on molecular percentage values of the components. The percent (FeO), is the total iron content in the slag calculated to FeO. Fig. 1 shows that as the basicity increases at constant mol pct (FeO),, the iron oxide activity increases rapidly and reaches a plateau which extends on the basicity scale from about 1.3 to 2.3; the iron oxide activity then decreases rapidly until a basicity of about 3.0 is reached, where it tends to level off. The solid portions of the curves represent the experimental data of Fetters and Chipman and Win-kler and Chipman. Their experimental heats were made in magnesia crucibles, and hence the slags were saturated with magnesia. The broken lines on the left represent the experimental data of Taylor and Chipman, who used a rotating crucible. In general, these slags contained less than 3 pct MgO. The absence of data for slags containing less than about 40 mol pct (FeO), and basicity ratios greater than about 2.5 made it necessary to calculate curves using ionic concepts of slags. The broken lines on the right, which disregard the solubility limits of di and tricalcium silicate and lime, were obtained by following the treatment of Flood and Grjotheim,"

Jan 1, 1957

By R. L. Hadley, G. Derge

The amounts of oxygen in liquid iron-titanium alloys up to 50 pct Ti were measured and the oxide phases in equilibrium with these alloys were determined by using TiO² crucibles. A minimum of about 0.003 pct 0 occurs at less than 1 pct Ti. The various liquid and solid oxide phases can be arranged on a ternary isotherm. THREE characteristics of titanium contribute to the interesting aspects of its reaction with oxygen in liquid iron: 1—It forms a number of stable oxides. 2—All oxides have large negative free energies of formation. 3—The pure metal exhibits high solubility for oxygen. In addition, the use of titanium as a stabilizing and strengthening element in alloys suggests a need for investigation of its reactions in amounts greater than those normally required for deoxidation. These higher compositions are also of interest because they occur during the addition of ferroalloys and produce deoxidation products before dilution is achieved. Titanium Deoxidation in the Literature While the use of titanium as an alloying element and deoxidizer has been common for several decades, the first detailed study of its deoxidizing characteristics was carried out by Wentrup and Hieber' in 1939. These authors determined the extent of deoxidation possible with titanium and identified, by microscopic examination, the products formed. They found that titanium in excess of 0.2 pct did not reduce the oxygen content of iron below 0.004 pct at 1600°C. They identified the spinel FeO-TiO² at low titanium concentrations and Ti2O³ in melts containing more than 0.2 pct Ti. A portion of the area surveyed by Wentrup and Hieber has been investigated recently by Evans and Sloman² using X-ray diffraction for inclusion identification. They concurred in general with the findings of Wentrup and Hieber, but reported the existence of Ti³O5 as a deoxidation product in the range near 0.1 pct Ti. Comstock, Urban, and Cohen³ discussed the deoxidation of iron with titanium, correlating the data of Wentrup and Hieber with free-energy data for the titanium oxides. Scatter at high titanium values was considered attributable either to the formation of an oxide exhibiting high solubility in liquid iron or to the entrainment of solid oxide particles leading to high apparent solubility. Chipman' has calculated the deoxidation curves for titanium based on free-energy data for titanium oxides. These calculations (Fig. 1) and those of Comstock, Urban, and Cohen involve assumptions as to the activity coefficients of oxygen and titanium in liquid iron, since such data have not been determined. Investigation of the deoxidizing characteristics of chromium" and vanadium0 have shown that these elements decrease the activity coefficient of oxygen in liquid iron, leading to a tendency toward relatively high oxygen values and experimental scatter in highly alloyed melts. Experimental This investigation involved two major objectives: 1—determination of the composition of the oxide phases in equilibrium with liquid Fe-Ti alloys, and 2—establishing the pattern of oxygen solubility in liquid Fe-Ti alloys at titanium concentrations in excess of that required for attainment of minimum oxygen content. Raw Materials Ingot iron was used having the following composition: 0.02 pct C, 0.017 pct Mn, 0.01 pct Si, 0.02 pct S, 0.006 pct P, and 0.03 pct 0. The titanium used

Jan 1, 1956

By F. L. Toy, C. E. Sims

PNEUMATIC processes for converting molten pig iron to steel were the major producers of steel during the latter half of the 19th Century and until shortly after the turn of the century, when these processes began losing ground to their rival—the basic open hearth process. The first pneumatic process for converting molten pig iron to steel was introduced almost simultaneously by Sir Henry Bessemer in England and by William Kelley in the United States during the decade 1850-1860, but it was Bessemer who pushed it to a successful commercial operation. The process itself is so basically simple that it has not lent itself to many extensive or revolutionary improvements since its inception. During the first 30 yr, numerous' designs of vessel and many modifications of practice were tried before the industry standardized on something resembling current practice. The evolution in construction has resulted in proportions and arrangements based more on mechanical expedience than on metallurgical requirements. Many of the early converters were stationary and had to be tapped similarly to the cupola or open hearth furnace. Such types were used for many years in Sweden and Germany, but the rotating or tilting types were favored in England and the United States. There was evident trouble with bottom tuyeres, becAuse about half of the early designs were constructed for side blowing with tuyeres submerged below the metal-bath surface. Even portable tuyeres, introduced from above, were tried. The principal advance, which made bottom blowing practical, was the invention, in 1863, by Henry Bessemer, and subsequent improvement by A. L. Holley, of a detachable bottom so that the tuyere section could be renewed. In the meantime, it was the demonstration, by Robert Mushet, of the value of manganese in overcoming hot-shortness in converter steel, that made the process metallurgically feasible. At first, only the acid practice was used, and Swedish pig iron, because of its low sulphur and phosphorus, was in great demand. The development of a suitable basic lining, by Sidney G. Thomas and Percy G. Gilchrist in 1876-1879, made the process applicable to the high-phosphorus ores of Europe. From the beginning of the use of the Thomas-Gilchrist process, trouble was experienced in obtaining sufficiently high temperatures in the blown metal, particularly in small heats. It is necessary, of course, to have the low-carbon blown metal at a considerably higher temperature for handling from vessel to ladle to molds than is needed for the molten pig iron. All of the increase in temperature in a pneumatic process must be obtained from the heat of combustion of the elements contained in the pig iron plus that from silicon when ferrosilicon is added. In bottom blowing practice, carbon is almost completely burned, but inasmuch as it cannot be oxidized to a higher state of oxidation than to CO when in contact with liquid iron, only a minor portion of the heat-producing capacity is utilized. Under such conditions, it is not considered to be an efficient source of heat. In the acid practice, therefore, silicon and manganese are the large heat producers, are quickly oxidized, and are efficient fuels. Too much manganese, however, thins the slag greatly and tends to promote excessive slopping or throwing of slag and metal from the converter during the blow. Most operators, therefore, like to keep the manganese content of the iron below 0.60 pct, and thus the main source of heat is the silicon, which must be at least 1 pct and sometimes 2 to 3 pct for small blows such as for castings. Ferrosilicon is sometimes added during the blow to obtain an adequate temperature level. In the basic (Thomas) practice, even more heat is required, because cold lime is added to flux the phosphorus after it is oxidized, and the basic slag must be maintained at a proper temperature. Silicon

Jan 1, 1951

By Takashi Katsura, Avnulf Muan

Equilibrium relations in the system FeO-Fe2O3 Cr2O3 have been determined at 1300°C at oxygen pressures ranging from that of air (0.21 atm) to 1.5 x 10-11 atm. The following oxide phases have stable equilibrium existence under these conditions : a sesquioxide solid solution with corundum-type structure (approximate composition Fe2O3-Cr2O3); a ternary solid solution with spinel-type structure (approximate composition FeO Fe2O3-FeO Cr2O3) and a ternary wüstite solid solution with periclase-type structure and compositions approaching FeO. The metal phase occurring in equilibrium with oxide phase(s) at the lowest oxygen pressures used in the present investigation is almost pure iron. The extent of solid-solution areas and the location of oxygen isobars have been determined. ThE system Fe-Cr-O has attracted a great deal of interest among metallurgists as well as ceramists and geochemists. Metallurgists have studied the system because of its importance in deoxidation equilibria, ceramists because of its importance in basic brick technology, and geochemists because of its importance for an understanding of natural chromite deposits. Chen and chipman1 investigated the Cr-O equilibrium in liquid iron at 1595°C in atmospheres of known oxygen pressures (controlled H2O/H2 ratios). The main purpose of their work was to determine the stability range of the iron-chromite phase. Hilty et al.2 studied oxide phases in equilibrium with liquid Fe-Cr alloys at 1550°, 1600°, and 1650°C. They reported the existence of two previously unknown oxide phases, one a distorted spinel with composition intermediate between FeO Cr203 and Cr3O4, the other Cr3O4 with tetragonal structure. They also sketched diagrams showing the inferred liqui-dus surface and the inferred 1600°C isothermal section for the system Fe-Cr-O. Koch et al3 studied oxide inclusions in Fe-Cr alloys and also observed the distorted spinel phase reported by Hilty et al. Richards and white4 as well as Woodhouse and White5 investigated spinel-sesquioxide equilibria in the system Fe-Cr-O in air in the temperature range of 1420" to 1650°C, and Muan and Somiya6 delineated approximate phase relations in the system in air from 1400" to 2050°C. The present study was carried out at a constant temperature of 1300° C and at oxygen pressures ranging from 0.21 atm (air) to 1.5 x 10-11 atm. The chosen temperature is high enough to permit equilibrium to be attained within a reasonable period of time within most composition areas of the system, and still low enough to permit use of experimental methods which give highly accurate and reliable results. These methods are described in detail in the following. I) EXPERIMENTAL METHODS 1) General Procedures. Two different experimental methods were used in the present investigation: quenching and thermogravimetry. In the quenching method, oxide samples were heated at chosen temperature and chosen oxygen pressure until equilibrium was attained among gas and condensed phases. The samples were then quenched rapidly to room temperature and the phases present determined by X-ray and microscopic examination. Total compositions were determined by chemical analysis after quenching. In the thermogravimetric method, pellets of oxide mixtures were suspended by a thin platinum wire from one beam of an analytical balance, and the weight changes were recorded as a function of oxygen pressure at constant temperature. The data thus obtained were used to locate oxygen isobars. The courses of the latter curves reflect changes in phase assemblages and serve to supplement the observations made by the quenching technique. 2) Materials. Analytical-grade Fe2O3 and Cr2O3 were used as starting materials. Each oxide was first heated separately in air at 1000°C for several hours. Mixtures of desired ratios of the two oxides were then prepared. Each mixture was finely ground and mixed, and heated at 1250" to 1300°C in air for 2 hr, ground and mixed again and heated at the same temperature for 5 to 24 hr, depending on the Cr2O3 content of the mixture. A homogeneous sesquioxide solid solution between the two end members resulted from this treatment. A Part of some of the sesquioxide samples thus prepared was heated for 2 to 3 hr at 1300°C and oxygen pressures of 10-7 or 1.5 x 10-11 atm. Reduced samples (either iron chromite

Jan 1, 1964

By F. B. Foley

IT is with an unusual degree of personal satisfaction that I find myself in a position to pay tribute to the memory of Henry Marion Howe. One could not have spent any length of time in the presence of Dr. Howe without profiting intellectually. I do not hesitate to say that my years of association with him were the most stimulating of all my years of metallurgical study. He always impressed one with his own eager search for knowledge. Never dependent on the written word alone he sought information from anyone whose opinion he valued. His ability to piece together bits of apparently conflicting data from various sources so as to build up a logical hypothesis was unique. A small slight man with the intellect of genius he would have gone to the top in any endeavor he undertook and it was fortunate for metallurgy that its study attracted him as it did. Howe was a modest man. I like to recall an incident which left a lasting impression with me. The lab- oratory in his home, "Green Peace," was in the basement and access was by way of stairs leading down from his secretary's room. In using these stairs my attention was attracted many times to an ordinary cardboard shoe box which reposed on the shelf above the landing. It was crudely labeled on its side in black ink "Vanity Box." My curiosity was aroused to the point that I finally asked his secretary what it was. With some amusement she took the box from its shelf on the stairway, opened it and showed me its contents—numerous letters, from the foremost men of science of every civilized country throughout the world, commending his "Metallography of Steel and Cast Iron." I recall that in reply to one who thought there was not enough of Howe's own researches in his book he wrote, "Primarily I am a writer, secondarily an investigator." Howe wrote to make his readers think. No one ever strove harder than he to be right but above all, whether his viewpoint proved ultimately to be right or wrong, he was always content if by his stand, he provoked a reader to take the next step along the path to greater knowledge. I doubt that he was ever afraid to be wrong for he was always secure in the thought that his effort was guided by a sincere search for the truth. One continually searching for truth is entitled to occasional excursions up the wrong alley. A glance backward to the metallurgical confusion of some thirty to forty years ago, or need one go back so far, provides convincing proof of what a host of companions one may have in a common acceptance of ideas which the future will prove to be wholly untenable. Well over a hundred years have passed since investigators have interested themselves in the effect of increasing the temperature of iron and steel on their mechanical properties. We are told by Charles Walrandl in "Industrial Annals" for June 11, 1822, that bend tests, conducted in a Russian steel works of Prince Demidoff, on steel bars "highly heated" and bent during cooling became brittle when bent at an iris blue color. He concluded, "That when steel is heated to a temperature between 473°F and 662°F the mettle was more brittle between these limits than at a much lower or at a much higher temperature." It was a curious bit of information recognized as true to this day and still not explained satisfactorily. In 1878 Charles Houston in Annales de Mines associated this brittleness with an increase in tensile strength at 572°F. When this relatively low temperature is exceeded it is recognized that steel becomes weaker as temperature is increased up to the melting point, where no strength of practical importance remains. It is easy to believe, in fact it goes without saying, that this weakening as the temperature of a metal is increased is the result of the motion of the atoms making up the metal, a motion which itself is evidence of the temperature increase. However, if we are considering iron or steel we find that this decrease in strength is not a steady one, for, besides the increase in strength just referred to, one comes to a temperature, the critical temperature, where results of tests indicate the metal to be extremely weak and then as temperature increases to become sensibly stronger again. This apparent anomaly was made the subject of the first Howe Memorial Lecture, delivered by Albert Sauveur in 1924. It may be of interest to review these findings of Sauveur. He used two methods of investigation. One involved the twisting of bars. The bars were heated in an

Jan 1, 1951

By C. Richards Honeycutt, Frederick C. Langenberg, Guenter Pestel

Solidification in a moving electromagnetic field was successful in altering the as-cast grain structure of steel ingots. The equipment is described and exerimental results are presented for several different alloys. Conditions for optimum grain refinement are described and an empirical design constant presented. The effect of the grain refinement on hot workability is briefly discussed. T HE grain structure of a steel ingot teemed into a metal mold can be defined by macroscopic examination in semiquantitative terms. For example, the relative volume of obviously differing structures can be estimated with the classic definitions of chill, columnar, and equiaxed zones. Experimental evidence has proven that the grain structure of an ingot is affected by changes in such factors as teeming temperature, rate of teeming, degree of turbulence, size of ingot, mold characteristics (including preheat temperature, design and coating), and composition of the metal (especially as it affects the range of solidification). Significant advances have been made in fundamental solidification studies; but the principles which have been developed are difficult to apply tothe complex and changing phenomena that occur simultaneously during ingot solidification. In particular, many attempts have been made to refine the as-cast structure of ingots, with special emphasis on the columnar grains. The formation of large columnar grains is generally considered harmful to the further fabrication of an ingot. It may also result in undesired ani-sotropic properties. However, columnar grains are not undesirable in all grades, or product applications, and caution must be exercised to determine in which grades and applications columnar grains are not desired in the ingot. Although the literature on the refinement of as-cast ingot grain structures is too vast in general to review here, it is noteworthy that such methods are additions of artificial nuclei, mold vibration, mechanical stirring or ultrasonic agitation of the molten metal, and controlled cooling and reheating during solidification have been tried with varying degrees of success. However, it is doubtful that any method of refining the as-cast ingot grain structure has been completely successful on a commercial basis. The purpose of

Jan 1, 1962

By A. R. Orban, R. B. Engdahl, J. D. Hummell

The initial phase of a research program on smoke abatement from Bessemer converters is described. In work sponsored by the American Iron and Steel Institute, a 300-lb experimental Bessemer converter was assembled to simulate blowing conditions in a commercial vessel. Measurements of smoke and dust were also made in the field on a 30-ton commercial vessel. During normal blows the dust loading from the laboratory converter averaged 0.51 lb per 1000 lb of exhaust gas. This was similar to the exhaust-gas loading of a commercial vessel. The addition of hydrogen to the blast gas of the laboratory converter caused a decided decrease in smoke density. Smoke was also reduced markedly when methane or ammonia was added instead of hydrogen. The research is continuing on a bench-scale investigation of the mechanism of smoke formation in the converter process. DURING the past 2 years, on behalf of the American Iron and Steel Institute, Battelle has been conducting a research program on the control of emissions from pneumatic steelmaking processes. The objective of the research program is to discover a practical method for reducing to an unobjectionable level the emission of smoke and dust from Bessemer converters. PRELIMINARY INVESTIGATION Although conceivably some new collecting technique may be devised which would be economically practicable for cleaning Bessemer gases, no such system based on presently known principles seems feasible because of the extremely large volume of high-temperature gases involved. Hence, the research is being directed toward prevention of smoke formation at the source. A thorough review was first made of former work to determine the present status of the cleaning of converter gases. No published work was found on work done in the United States on collecting smoke or on preventing its formation in the bottom-blown, acid-Bessemer converter. In Europe, however, a number of investigations have been made on the basic-Bessemer converter. Kosmider, Neuhaus, and Kratzenstein1 conducted tests on a 20-ton converter to obtain characteristic data for dust removal and the utilization of waste heat. They concluded that because of the submicron size of the dust, special equipment would be necessary to clean the exhaust gases. Dehne2 conducted a large number of smoke-abatement experiments at Duisburg-Huckingen in a 36-ton Thomas converter discharging into a stack. A number of wet-scrubbing and dry collectors were tried unsuccessfully. A waste-heat boiler and electrostatic collector with necessary gas precleaners was felt to be the best solution for this particular plant. Meldau and Laufhutte3 determined that the particle size was all below 1 µ in the waste gas of a bottom-blown converter. Sel'kin and zadalya4 describe the use of oxygen-water mixtures injected into a molten bath in refining open-hearth steel. They claim that with use of oxygen-water mixtures the amount of dust formed was reduced between 33.3 and 20 pct of its previous level, and emission of brown smoke almost ceased. Pepperhoff and passov5 attempted unsuccessfully to find some correlation between the optical absorption of the smoke, the flame emission, and the composition of the metal in a Thomas converter in order to determine automatically the metallurgical state in the melt. In a recent U. S. Patent (NO. 2,831,762)' issued to two Austrian inventors, Kemmetmuller and Rinesch, the inventors claim a process for treating the exhaust gases from a converter. By their method the inventors claim that the exhaust gases from the converter are cooled immediately after leaving the converter to a degree that oxidation of the metal vapors and metal particles to form Fe2O3 is inhibited in the presence of surplus oxygen. Gledhill, Carnall, and sargent7 report on cleaning the gases from oxygen lancing of pig iron in the ladle. They claim the Pease-Anthony Venturi scrubber removed 99.5 + pct of the smoke, thereby reducing the concentration to 0.1 to 0.2 grain per cu ft, which resulted in a colorless stack gas after the evaporation of water. Fischer and wahlster8 developed a small basic converter and compared the metallurgical behavior of the blow with that of a large converter. Later work by Kosmider, Neuhaus, and Hardt9 on the use of steam for reduction of smoke from an oxygen-enriched converter confirmed that the cooling effect of steam is detrimental to production. From review of all of the published information on the subject, it was concluded that a practical solution to the smoke-elimination problem had not been found. Accordingly, it was deemed desirable to investigate the feasibility of preventing the initial formation of smoke in the converter.

Jan 1, 1961

By E. T. Turkdogan, P. Grieveson, J. F. Beisler

Jan 1, 1963

By E. T. Turkdogan, P. Grieveson, J. F. Beisler

Experimental results are given for the rate of reduction of silica from silicate melts by paphite-saturated iron in the presence of carbon monoxide. It is shown that, when gas bubbles are present at the slag-metal interface, the interfacial chemical reaction is the rate-controlling process in the transfer of silicon from slag to metal. From the silicon-concentration profiles in the metal sample, the diffusivity of silicon in paphite-saturated iron is found to be (5.4 * 0.4) x 10 sq cm per sec at 1600°C. Some consideration is given to the transport of oxygen from the slug-metal interface to the walls of the gvaphite metal container as becoming the rate-controlling process in the absence of gas bubbles at the slag-metal interface. ATTEMPTS were made by Fulton and chipman1 to investigate the kinetics of reduction of silica from calcium alumino-silicate melts by graphite-saturated iron in an atmosphere of carbon monoxide. In these experiments with 400 to 500 g of metal and slag, both phases were stirred in such a manner that the interface was essentially undisturbed. Initially, the graphite-saturated iron contained about 15 pct Si and, after about 8 or 10 hr of reaction time at 1600°C, the silicon content of the metal in- creased by about 0.2 pct. In a written discussion on this paper of Fulton and Chipman, schuhmann2 pointed out the possibility that this observed slowness of the reduction of silica could be due to the transport of oxygen across the liquid metal boundary layer at the slag-metal interface. Although this explanation of Schuhmann is quite feasible for the experimental data of Fulton and Chipman on silica reduction, such a reasoning should not be extended to other rate data on slag-metal reactions unless sufficient evidence is available satisfying the boundary conditions for such a transport process. The hydrodynamics of stirred liquids are very complex and even for a simple method of stirring there is no exact mathematical solution which will predict the mass transfer coefficient accurately. The best available solution of this problem is that given by Lewis' and later modified by mayers~ for a two-liquid system where liquids are stirred by counter-rotating stirrer blades without disturbing the interface. In such a system the mass transfer coefficient is estimated from an empirical relationship using the data on viscosity and density of the two liquids, rate of revolution, the length of stirrer blades, and the diffusivity of the element which is transferred from one phase to the other. It was found in these investigations' that the estimated and observed mass transfer coefficients, in systems containing two immiscible aqueous solutions, agreed within *40 pct. Although this is not considered to be an unreasonable error for the study of industrial processes, uncertainties of this magnitude cannot be tolerated in any theoretical study of reaction kinetics. In view of the complexity of the

Jan 1, 1963

By R. D. Pehlke, P. D. Goodell, R. W. Dunlap

The rate of dissolution of steel bars in molten pig iron has been measured experimentally in the temperature range 2300° to 2650° F. The rate of solution is shown to be a .function of bath composition, temperature, and stirring. A kinetic model based on carbon diffusion in the liquid phase has been derived to fit the experimental results. THE rate of scrap melting has long been an important variable in steelmaking operations. With the advent of the oxygen steelmaking process and the accompanying shorter heat times, the rate of scrap melting has now become one of the rate-limiting factors in steel production. As observed in commercial practice, the solution rate is influenced by the compositions of liquid and solid, the temperature, agitation, and time. However, no definitive work has been done on the Fe-C system, and there is very little information in the literature regarding the relative effects of these variables in steelmaking systems. A number of questions have been raised in regard to scrap utilization in basic oxygen steelmaking operations. Consideration has been given to the optimum size and shape of scrap, and to the use of preheated scrap as a means for decreasing the pig-iron requirement in oxygen blowing. The determination of an optimum scrap practice for a specific installation depends to a large extent upon the economics of the scrap market and also upon the behavior of scrap in the vessel. The present research was undertaken as a preliminary study in evaluating the behavior of steel in a pig-iron bath under various conditions of temperature, composition, and agitation, as might be encountered in oxygen converter operations or in any steelmaking operation where scrap behavior is an important process variable. Related studies have been carried out on non-ferrous systems. The solution rate of solid aluminum in a molten A1-Si alloy has been studied.' Furthermore, the increasing use of liquid metals has created considerable interest in studies related to dissolution of a solid in a liquid, or mass transfer taking place between a solid interface and a liquid metallic phase.2-10 In an effort to clarify the relative importance of factors influencing the dissolution of scrap in Fe-C alloys, this paper presents the results of a study of the rate of dissolution of a low-carbon steel cylinder in a molten Fe-C bath at various bath compositions, temperatures, and conditions of agitation. An attempt has been made to determine the mechanism of solution, and a model has been derived to fit the experimental results. The rate of heat transfer between the molten pig-iron bath and the solid-steel cylinder has also been studied. EXPERIMENTAL PROCEDURE A molten bath of pig iron (nominal composition 4.2 pct C, 0.5 pct Mn, 0.8 pct Si)* was held in a 200- *In view of the fact that the composition of the pig-iron bath was slowly changing with time because of steel dissolution and reaction with the surrounding atmosphere, intermittent samples of the liquid bath were taken throughout each experiment, Table 1. lb induction melting unit. The internal diameter of the furnace was 8-1/2 in. and the bath depth approximately 14 in. Cold-finished 1020 steel cylinders of 1/2-, 3/4-, 1-, 1-1/2-, and 2-in. diameters were cut into 1 -ft lengths for use as test specimens. One end of each bar was machined to fit a hand-driven, mechanical stirring device which rested on top of the furnace. This fixture permitted 7 to 8 in. of the bar to be immersed in the melt. The steel cylinders were cleaned to free the surface of grease and oxide. The rods, at ambient temperature, were immersed into the molten pig-iron bath. The melt temperatures studied in this investigation were 2300°, 2500°, and 2650°F. Different agitation conditions were achieved by operating with a) the power to the furnace, giving induction stirring; b) induction stirring plus mechanical stirring, using hand rotation with a chain and sprocket assembly at approximately 200 rpm; c) mechanical stirring alone with the power off; and d) the power off and no mechanical stirring resulting in minimum agitation, i.e., only that caused by natural convection currents in the bath. The samples were immersed in the melt for prescribed times ranging from 30 sec up to 6 min. Immersion times were measured with a stopwatch and temperature control of the melt was achieved by power adjustment following temperature measurement with an optical pyrometer. The measurements with the calibrated pyrometer were checked out to within less than 10°F with simultaneous thermocouple measurements. Following immersion, the bars were water-quenched and the diameters were measured with a micrometer at several positions on the reduced area, and by volumetric displacement. The dissolution rates calculated from the

Jan 1, 1965

By Renato G. Bautista, Theodore D. Tiemann

A kinetic study of the hydrogen reduction of taconite from the Wisconsin Gogebic range was made over the temperature range from 500° to 1000°C on eleven size fractions from 4 to 150 mesh. Two stages of reduction were observed, a rapid initial reaction followed by a slower reaction presumably taking place at an internal receding FexO-Fe interface. Calculated mean activation energies for the two reactions were 7800 and 14,600 cal per mole respectively. In recent years there has been an increased interest in the direct reduction of iron oxide ores to metallic iron by means of gaseous reducing agents such as hydrogen and carbon monoxide.1,2 These investigations have been motivated by the desire to develop a process that will by-pass the blast furnace in the production of steel. The majority of these processes have been developed to produce metallic iron by direct reduction from high-grade iron oxide ores.3"5 Very little work has been done on the low-grade siliceous iron oxide ores.6"8 The work reported here is directed principally towards the fundamental aspect of the reduction reactions of siliceous iron oxide ores, since the practical aspects of the gaseous reductant process were discussed previously. The ore used in the investigation was obtained originally from the United States Bureau of Mines10 trench sample of the Yale member of the Wisconsin Gogebic range iron formation. The Yale taconite has an average analysis of 28.2 pct Fe and approximately 50 pct SiO2. Chemically, these nonmagnetic taconites contain on the average about 53 pct silica and 30 pct Fe. An average analysis calculated fron the USBM10 figures for a composite of the five members (Norrie, Plymouth, Pence, Pabst, and ale) of the iron formation is given in Table I. Mineralogically, based on previous X-ray diffraction and other studies, the principal minerals are hematite (Fe2O3), geothite (Fe2O3.H2O), and quartz (SiO2). Minor amounts of iron containing silicates, siderite (FeCO3) and magnetite (FeO. Fe2O3) are present.10,11 The iron minerals and the quartz are finely disseminated requiring extremely fine grinding for liberation. For the experimental work, the ore sample was screened into a number of size fractions, the analyses and densities of which are given in Table II. EXPERIMENTAL PROCEDURE The reduction experiments were carried out in a 24 in. by 2 in. ID nichrome-wound vertical-tube furnace mounted on a stand. A 1 1/2 in. OD zirconium-oxide combustion tube was used inside the furnace to contain the atmosphere. To the top of this combustion tube was joined a pyrex ground-glass joint to which was attached a glass bulb with a small (1.0 mm) opening at the center, and with two outlets controlled with a stopcock on each side. A pyrex-glass joint with connections to three stopcock joints for introducing hydrogen, nitrogen, and mixtures of hydrogen and nitrogen gas was joined to the tapered bottom of the combustion tube. The sized ore fractions were contained in a 1 in. diameter by 1 1/2 in. 150-mesh nickel screen basket. The basket was suspended in the furnace from a balance by means of a supporting nickel wire which hung freely inside the combustion tube. The furnace temperature was controlled by a Leeds and Northrup Speedomax Type G controller, connected to a chromel-alumel thermocouple placed

Jan 1, 1962