By R. D. Barer, M. B. Bever

Age hardening alloys are quenched from the solution treatment to room temperature in order to retain a supersaturated solid solution. Some alloys age "naturally" in this condition but in most alloys aging is induced "artificially" by heating to intermediate temperatures. Cold working of the supersaturated solid solution accelerates the aging process and quenching strains have the same effect. The investigation reported here is a study of the progress of aging in specimens quenched directly from the solution treatment to various aging temperatures. This procedure reduces the temperature interval of quenching and the resulting quenching stresses. It also eliminates any changes which would take place in the undercooled sample at room temperature prior to aging at an elevated temperature. Isothermal aging is thus approached and its kinetics may be studied. An aluminum-copper and an aluminum-silicon alloy were chosen for this investigation. The aging mechanism of aluminum-copper alloys is complex while the aging of aluminum-silicon alloys is nearly ideal. As standards of comparison for the samples directly quenched to the aging temperature, specimens were also age hardened by the usual procedure in which solution treated samples are first quenched to room temperature and then reheated to the aging temperature. Review of Previous Work The mechanism of age hardening has been the subject of a controversy which has ranged from the theory of outright precipitation of an equilibrium phase to theories based on subtle changes occurring in the matrix prior to precipitation. A detailed critical review of the literature up to 1939 is available1 and contributions to the general theory of age hardening continue to be made.2,3 Age hardening, whatever its mechanism, involves the nucleation of a second phase within a supersaturated solid solution. Theoretical considerations4,5 indicate that the rate of nucleation reaches a maximum at an intermediate temperature below the temperature at which supersaturation sets in. Studies of precipitation at various subcritical temperatures have demonstrated that the largest property changes in a given time occur at such intermediate temperatures.6,7,8 The precipitation of a phase from supersaturated solid solution is accelerated by strains which may result from quenching or cold work. Phillips and Brick9 established that quenching strains are an essential condition for the age hardening of aluminum-copper alloys at room temperature, at least for aging periods of less than 30 days. They also found that on aging at 300°C the hardness increased faster and reached a higher maximum after quenching into water than after quenching directly to the aging temperatures. Fink and Smith10 observed preferential precipitation on slip bands and grain boundaries in aluminum-

Jan 1, 1950

By W. C. Winegard, A. Galibois, C. J. Beingessner

The effects of solutes on the distribution of two-dimensional configurations of grains in zone-refined tin have been studied. When solutes with partition coefficients (ko) greater than unity are added, three-sided pains become more prevalent and the growth law changes. It is shown by electron-Probe micro-analysis that a solute buildup occurs ahead of a moving grain boundary when ko > 1. It has been found recently1, 2 that solutes with partition coefficients greater than unity have a larger retarding effect on grain growth than solutes with k, less than unity. ko is defined as the ratio of the concentration of solute in the solid to the concentration of solute in the liquid with which the solid is in equilibrium. Niessen and winegard2 have suggested that this effect is probably due to the complex shape changes which occur during the process of grain growth and that no theory based on single boundary motion3-5 can explain the results. They suggested that the dissociation of the unstable fourfold junction was delayed in alloys where ko was greater than 1 because the boundaries at the junction had to move into a region of high solute concentration. If indeed this mechanism were correct, it was felt that not only would the dissociation of fourfold junctions be affected by the solute buildup ahead of the boundaries, but the collapse of three-sided grains would be impaired. These combined effects would naturally lead to a modification in the distribution of the number of sides per grain seen on a two-dimensional section. The present investigation was undertaken to test these hypotheses by examining the grain-growth process in detail. EXPERIMENTS The Distribution of Grain Configurations in Zone-Refined Tin as Seen on a Two-Dimensional Section. Following the method of Bolling and Winegard,6 zone-refined tin was cast into button-shaped specimens and, subsequently, plastically deformed under a drop hammer at room temperature. The resulting flat coin-shaped samples were annealed at 200°C, some for 50 sec and others for 100 sec. The specimens were then examined to determine the distribution of the number of sides per grain, i.e., the num- ber of crystals adjacent to any particular grain in the section. For simplicity, the grains were classified as three-sided, four-sided, and so forth; this concept is schematically illustrated in Fig. 1. As indicated by smith,' it was necessary to examine every grain within an enclosed area to obtain a proper distribution of the relative frequency of each type. The distributions for the two annealing times are illustrated in Fig. 2. The total number of grains examined is also indicated on the figure. It is evi-

Jan 1, 1965

By J. O. Nelson, C. J. Altstetter

Single crystals of hcp cobalt, 3 mm in diameter and up to 35 cm long, were grown using an electron-beam, zone-melting technique. The martensitic-phase transformation was studied in single-crystalline and polycrystalline specimens by making length-change measurements as a function of temperature under various elastic compressive stresses. Upon thermal cycling, single-crystalline or polycrystalline specimens repeatedly transformed almost entirely on the same variant of close-packed plane provided the maximum temperature did not exceed 600°C. Cycling to 1000°C resulted in transformation on more than one {111} variant. This behavior is termed multivariance. The multivariant transformation occurred very rapidly at an M, temperature 2° to 6°C lower than the M, of a transformation which would result in a single-crystal product. Elastic compressive stresses (up to 253 g per sq mm) tended to lower the A, and raise the M, temperatures, decreasing the width of the temperature vs dilatation hysteresis loop. The transformation habit plane and transformation shear direction of an as-grown single crystal were not grossly affected by elastic compressi?ie stress. This was evidenced by similar dilatations on the temperature us dilatation loops joy specimens with and without compressive stress. A dislocation mechanism is proposed to explain the observed results. IT has been shown that, on heating, cobalt transforms martensitically from the hcp to the fcc phase.' The transformation habit plane is (0001)hcp || (lll)fcc and the transformation shear direction is (1010)hcp || (112)fcc. The transformation involves a shear of 1g°28', which may be achieved by a shearing of a/6(112) of every two planes with respect to the plane beneath, thus changing the ABABAB stacking of hcp to the ABCABC stacking of fcc. Associated with the phase change is a 0.3 x 10"3 contraction in the habit plane and a 4.2 X 10"3 expansion perpendicular to the habit plane resulting in a 3.6 x X volume increase on heating.' On cooling, an identical volume decrease takes place. The temperature at which the fcc phase begins to form on heating (A,) is reported as 430°C, and the temperature at which the hcp phase begins to form on cooling from an elevated temperature (A&) is reported as 390oC1,3 Consequently, temperature vs dilatation plots have the form of a hysteresis loop. If heating or cooling is reversed during a transformation, a smaller hysteresis loop results. Upon heating, the transformation is always complete; whereas, fcc is often retained at room temperature as a metastable phase entrapped in the polycrystal-line hexagonal matrix.1,4,5 Two obstacles in the theory of the allotropic-phase transformation of cobalt have been: 1) a detailed knowledge of the product nucleus, and 2) a plausible method of propagation of the transformation. Bilby,8 christian, 7 and seeger 8,9 have suggested a "pole mechanism" as a means of propagation of partiai dislocations from plane to plane. A pole dislocation and a Shockley partial come together at a node. The a/6(112) Shockley partial rotates about the pole dislocation effecting the transformation shear. The pole dislocation must have a 2a/3(111) screw component which causes extension of the transformed region by two atomic planes with each full rotation of the Shockley partial. Bollmannl0 suggested, on the other hand, that transformation propagation occurs due to the stress fields of intersecting (111)-type stacking faults. As faults intersect, a stress distribution is set up about their intersection which is in turn reduced by the emergence of another fault on the second nearest plane. This process continues with the final result of a complete phase transformation. In view of the similarities between deformation and transformation in cobalt, the effect of stress on the transformation would, hopefully, yield valuable information concerning nucleation and propagation. In the present work single-crystalline and polycrystalline specimen length changes were measured as a function of temperature at various compressive loads. PROCEDURE Several orientations of single crystals of hcp cobalt in lengths up to 25 cm were grown by electron-beam floating zone melting from 99.95 and 99.999 pct, 3-mm-diam cobalt rod as supplied by Johnson

Jan 1, 1964

By G. B. Craig, J. Rezek

The critical resolved shear stress of zone-refined zinc single crystals deformed in tension is found to increase with increasing amount of striation substructure. The increase in strength with numbers of striations can be accounted for by a dislocation pile-up mechanism. A somewhat different means of plotting stress-strain data is introduced which allows a more unambiguous choice of yield stress to be made. FEW systematic studies of the role played by mac-romosaic or striation-type substructure in the de- formation of high-purity metal single crystals grown from the melt have been reported. McGrath and Craig' found that striations increased the critical resolved shear stress of zone-refined aluminum crystals, postulating a dislocation blockage by the striations as the strengthening mechanism. Lauri-ente and Pond2 found that, as the etch pit density increased in aluminum crystals grown from the melt, the critical resolved shear stress also increased. Fleischer and Chalmers3 also found changes in the critical resolved shear stress of aluminum crystals grown from the melt at varying rates, but could not be certain whether an increase of strength with rate was due to a higher concentration of impurity in the gage length or to an increase in the number of small-angled boundaries. An early work by Hibbard4 indicated that copper crystals containing lineage boundaries were stronger than those free from this type of imperfection.

Jan 1, 1962

By J. T. McGrath, G. B. Craig

Tensile tests on aluminum single crystals, grown from the melt, revealed that the yield stress of these crystals was raised as the amount of striation substructure was increased. The number of striation-type boundaries was varied by changing the rate of growth of the crystals. The results are interpreted in terns of a blockage of dislocation movement by striation boundaries. IMPERFECTIONS are known to have a large effect on the mechanical properties of metals. Teghtsoonian and Chalmers 1 studied a block or striation-type substructure in tin and found that the formation of the striations depended upon rate of crystal growth and orientation. They found that the angular misorienta-tion between neighboring striations varied between 15 min and 5 deg. Atwater and chalmers2 investigated striations in tin and lead, and found that purity was another factor which influenced their formation. There was a limiting purity above which the striations were straight and regular. There is little information in the literature concerning how substructures in melt-grown crystals affect strength. washburn3 introduced small-angle boundaries into zinc by a shear process and found a subsequent increase in yield stress which he attributed to the presence of these boundaries. Lauriente and pond4 found the critical resolved shear stress in aluminium crystals grown from the melt, to increase with etch pit density. The etch pits were used as an indication of growth imperfections. In Hibbard's5 work on lineage structure in copper crystals grown from the melt, he tested one crystal containing interlineage boundaries, and found a 50 pct increase in the critical resolved shear stress. Fleischer and Chalmers6, in a recent paper, mention briefly that, in the production of aluminium crystals from the melt when the growth rate was raised from 1.2 to 18 cm per hr, the yield stress increased 50 pct. They felt that the increase in yield stress with rate of growth might be attributed to a higher concentration of impurities in the gage length and also might be affected by the increased number of small-angle boundaries (striations). The present investigation was undertaken to determine the effect of the striation substructure on the strength of aluminum single crystals. EXPERIMENTAL PROCEDURE Aluminum single crystals of 99.9992 purity were grown from the melt using a technique described by Chalmers.7 The growth rate was varied from 0.6 to 20 mm per min, thus producing crystals with varying numbers of striation boundaries. To avoid prior deformation, the crystals were chemically cut to the desired length with a saturated solution of cupric chloride. They were then annealed at 580°C for 24 hr and allowed to cool slowly in the furnace. Finally, the specimens were electropolished using an electrolyte of 5 parts ethyl alcohol and 1 part perchloric acid. Each specimen was approximately 5 in. in length and 0.125 sq in. in cross section. The average orientations of the 5 series of crystals studied are shown on the stereographic projection of Fig. 1. The crystals were strained approximately 2 pct in a soft tensile machine. The strain sensitivity was 3.6 x 10-4 cm over a 5-cm gage length.

Jan 1, 1960

By I. R. Kramer, L. J. Demer

Aluminum single crystals were pulled in an electrolytic cell allowing surface removal during the deformation. The extent of Stages I and 11 of the stress-st-aitz curve was increased and the slope decreased as the rate of metal removed from the surface was increased. An increase of the strain rate caused a decrease in the effectiveness of the metal removal. The data indicate that the work-hardening coefficient in Stage I is determined primarily by the conditions which exist on the surface of the crystal. In Stages 11 and 111, both surface effects and internal barriers are important. ALTHOUGH numerous investigations have been conducted on the plastic flow characteristics of metals in an attempt to explain the mechanism of work-hardening, relatively few studies have taken into account the influence of the surface. In all current theories of work-hardening it is assumed that the impediments to the movement of dislocations are within the crystal. The barriers due to the surface and the existence of solid and liquid films have been neglected even though it has been demonstrated that the surface exerts a large effect. A number of investigators1-l8 have shown that solid films on the surface of single crystals markedly affect their mechanical behavior. In general, the presence of a solid film tends to increase the yield stress and increase the work-hardening rate. Often, on single crystals, Stage I and, at times, Stage II regions are completely suppressed. Various mechanisms have been offered for the effects of oxide and metal films as well as the influence of electrolytes. Of these, concepts concerned with the locking of surface dislocation sources and the blocking of dislocations at the surface resulting in pileups appear to be actively considered at present. Barrett,11 Takamura,6 Gilman,19 Lipsett and King,20 Shapiro and Read,10 and Weiner and Gensamer21 are among those who have interpreted their results in terms of piled-up dislocations at the surface, while Adams.22 and Chalmers and Davis23 have explained their experimental observations in terms of locking of surface dislocation sources. In general, the change in plastic flow properties due to electrolytes has been explained in terms of the unblocking or unlocking of dislocations by the removal of the oxide films. In considering the two proposed mechanisms, it appears that the locking of sources of surface dislocations by a solid film should exert a primary influence only on the critical resolved shear stress for flow and not on the slopes of Stages I and 11. However, the blocking at the surface of dislocations from internal sources may also affect the critical resolved stress and furthermore exert an influence throughout the whole plastic range. In certain cases it does not seem feasible to explain the results of experimental observations in terms of locking of surface dislocation sources. The abnormal aftereffects found by Barrettll,12 by removing the oxide by an acid treatment are excellent evidence of the blocking of dislocations at the surface. Additional evidence in favor of a blocking due to a pileup of dislocations at the surface may be found from the observations that the critical resolved shear strength continues to increase with the thickness of the oxide layer until very heavy oxide layers are formed. If the locking of surface dislocations sources were the dominant factor, the critical resolved shear stress would not be expected to increase after all of the surface sources were locked by the formation of the oxide. This may be expected to happen after a few atomic layers of the oxide are formed. In spite of the above evidence on the strong influence of the surface on the plastic flow characteristic, this has been ignored in current theories of work-hardening. Seeger24,25 suggested that most of the dislocations may slip out of the crystal only when the specimen axis is within certain areas of the orientation triangle. In other areas the resolved shear stress in other glide systems is large enough to generate dislocations which can form Lomer-Cottrell locks, thereby decreasing the average slip distance in some directions and causing a larger hardening rate. Friede126 assumed that at the beginning of Stage 11, a large number of Lomer-Cottrell dislocations are formed by a catastrophic process which used up all the Frank-Read sources on the secondary slip-planes. In this manner a fixed number of Lomer-Cottrell locks is formed which act as barriers against which the dislocations can pile up. In Stage 111, Seeger24 and Diehl, Mader, and Seeger25 proposed that Lomer-Cottrell barriers are circumvented by the cross slip of extended screw dislocations. Cottrell and Stokes,27 Friedel,26 Cottrell,26 and stroh29 suggest that the Lomer-Cottrell dislocations collapse under the stress field of the dislocation pileup. It is the purpose of this paper to report the changes in Stages I, II,and III of the deformation process in

Jan 1, 1962

By I. R. Kramer, L. J. Demer

T. H. Alden and R. L. Fleischer (General Electric Research Laboratory)— The authors' results indicate clearly and, we believe, significantly that during tensile deformation the surface layers of an aluminum crystal are hardened more severely than the interior of the crystal. A probable explanation of this effect, as the authors indicate, is that dislocations in the primary slip system may be obstructed at the surface or, it should be added, near the surface. The intent of this discussion is to show that the oxide film on aluminum is not likely to be responsible for this effect, but that the results can be understood if it is assumed the secondary slip is more active in the surface layers than in the interior. Prior study has shown that the principal mechanical effect of an oxide film on a single crystal is to raise the yield stress while leaving the rate of strain hardening during the initial deformation relatively unaffected.33 Since the yield stress is unchanged during polishing in the present case, we conclude that continual removal of the oxide film exerts a small effect on the plastic hardening.* It appears that the hardening interactions are occurring not only at the immediate surface, but to an appreciable depth below it, although with decreasing severity. For example, Kramer and Demer found that with removal of 0.004 in. from a specimen, the easy glide region was extended somewhat; but the yield stress did not decrease. The initial yield stress was recovered only after 0.041 in. was removed. Since a very brief polish would permit dislocations trapped behind a surface film to run out,34 extra dislocations must, instead, be trapped to a considerable depth below the surface. The same conclusion is drawn from the observation of decreasing hardening slope with increasing surface removal rates. If the hardening interactions were only at the immediate surface, a full softening effect would be observed at some small removal rate. The view is taken here that strain hardening is principally caused by small amounts of secondary slip.35 The secondary dislocations will interact in various ways with the primaries, interfering with their motion and causing them to accumulate in the crystal. Prior studies of easy glide have shown Diehl's model of hardening to be qualitatively consistent with the effects of impurities,36 of temperature,36 and of crystal size.37 On this basis the enhanced hardening of the surface layers in aluminum arises from increased secondary slip at and to some depth below the surface. Selective removal of this hardened layer is expected to decrease the measurable "bulk" hardening, the effect increasing with the removal rate and decreasing with the applied strain rate. We suggest that the stress on secondary systems is raised by the bending moments arising from interactions with the grips during the deformation. This stress from the grips has been shown to be a maximum37 near the surface, and hence, increased secondary slip should result. Prior investigations of grip effect:; indicate that as the grip stresses are raised by changing the crystal shape, the easy glide slope increases while the extent of easy glide decreases.38-40 It has been shown also that bending moments superimposed during tensile testing may either decrease easy glide, when supporting the moments caused by gripping, or increase it, when cancelling the gripping moments.38 This interpretation of the authors' results, emphasizing the special importance of secondary slip near the surface, is also consistent with the earlier results of Rosi.41 Copper crystals alloyed with silver in the surface layer show greatly increased easy glide compared with pure copper. In addition, the easy glide slope is reduced. The effect of bulk alloying in extending easy glide has been well established and has been interpreted as indicating the relative difficulty of secondary slip in alloy crystals. Since non-basal glide is difficult in zinc crystals, the effects of surface removal during deformation may be less important. Experiments to test this idea are in progress. I. R. Kramer and L. J. Demer (authors' reply)—The authors wish to thank Dr. Alden and Dr. Fleischer for their discussion. Our interpretation of the data in the paper is that dislocation motion is obstructed by "debris" which starts to form at the surface and extends towards the interior of the crystal with further plastic deformation. The fact that we did not find a reversion from Stage II to Stage I by surface removal shows that in Stage II the "debris" fills the entire cross-section of the specimen. Drs. Alden and Fleischer take the view that bending stresses due to the grips are responsible for the

Jan 1, 1962

By I. R. Kramer

Studies of the effect of size of the specimen on the change of slopes of Stages I and 11 by surface removal showed that the change of Stage I was independent of size with respect to the polishing rate; however, the change in the slope of Stage 11 with polishing rate increased directly in proportion to the surface area. The removal of the surface during the test affected the plastic deformation characteristics of gold, aluminum, and zinc single crystals and polycrystalline aluminum. The apparent activation energy of aluminum was found to be decreased markedly by removing the surface during the deformation process. In previous papers1-3 it was shown that the surface played an important role in the plastic deformation of metals. By removing the surface layers of a crystal of aluminum by electrolytic polishing during tensile deformation, it was found that the slopes of Stages I, II, and III were decreased and the extents of Stages I and II were increased when the rate of metal removal was increased. By removing a sufficient amount of the surface layer after a specimen had been deformed into the Stage I region, upon reloading, the flow stress was the same as the original critical resolved shear stress and the extent of Stage I was the same as if the specimen had not been deformed previously. The slope of Stage I was decreased 50 pct and that of Stage 11 decreased 25 pct when the rate of metal removal was 50 X 10"5 ipm. These data show that in Stage I the work hardening is controlled almost entirely by the surface conditions, while in Stages 11 and III both surface conditions and internal obstacles to dislocation motion are important. It appears that during the egress of dislocations from the crystal, a fraction of them becomes stuck or trapped in the surface regions and a layer of a high dislocation concentration is formed. This layer would not only impede the motion of dislocations, but would provide a barrier against which dislocations may pile up. In this case, there will be a stress, opposite to that of the applied stress, imposed on the dislocation source and dislocations moving in the region beyond this layer. It has been found convenient to refer to this layer as a "debris" layer. The "debris" layer may be similar to the dislocation tangle observed by thin-film electron microscope techniques.4 Reported in this paper are the results of studies on the effects of removing the surface during plastic deformation on aluminum crystals of various sizes. The effects of the surface on the yield point behavior of gold and high-purity aluminum crystals as well as the creep behavior were also determined. The effects of surface removal on polycrystalline aluminum (1100-0 and 7075-T6) are also reported. EXPERIMENTAL PROCEDURE For those portions of the investigation involving creep and tensile specimens, single crystals, having a 3-in. gage length and a nominal 1/8-in. sq cross section, were prepared by a modified Bridgman technique using a multiple-cavity graphite mold. The single crystals were prepared from materials which had initial purities of 99.997, 99.999, 99.999, and 99.999 pct for Al, Cu, Zn, and Au, respectively. The aluminum specimens for the size effect studies were prepared through the use of a three-tier mold in which crystals having a cross section of 1/8, 1/4, and 1/2 in. were grown from a common seed. The mold design was arranged so that one 1/2-in. crystal, two 1/4-in. crystals, and four 1/8-in, crystals of the same orientation could be cast. With this technique, it was possible to obtain only one set of crystals with the same orientation. Because of this limitation, it was not possible to determine both the changes of extent and slope of the various stages since a large number of crystals of the same orientation would have been required. Instead, only the change of slope as a function of the rate of metal removal was studied by abruptly altering the current density of the electrolytic polishing bath at various strains within the regions of Stages I and 11. The experimental techniques used for the tensile studies were essentially the same as those used previously.1,3 The specimens were deformed in a 200-lb Instron tensile machine, usually at a rate of 10-5 sec-5. A methyl alcohol-nitric acid solution was used as the polishing bath for aluminum. The temperature was maintained constant within ±0.l°C by means of a water bath. The tensile machine was

Jan 1, 1963

By C. Feng, I. R. Kramer

A study was conducted to determine the influence of the surface on the yield point of fcc metals and high-purity iron. For the high-purity fcc metals, the yield Point produced by restraining a specimen may be eliminated by removing a sufficient amount of the layer. A yield point similar to that in fcc metals was found when iron specimens were pre-strained after a prior deformation. This yield point is not due to an aging effect but is associated with the surface layer. The yield points in age-hardenable aluminum alloy and those connected with "work softening" are not affected by a surface-removal treatment and are, therefore, caused by bulk-type dislocation reactions. The yield point which appears in previously strained fcc metals has been the subject of numerous studies. Several theories have been advanced to explain this "unloading-reloading" yield point. Cottrell and stokes,' from their study on the effect of temperature on plastic properties of high-purity aluminum, considered that it was the result of an avalanche "breakdown" of Lomer-Cottrell sessile dislocations. Haasen and Kelly2 extended this concept of dislocation-dislocation interaction to account for the yield point when unloading and reloading was carried out at the same temperature. On the other hand, strain aging was found to be responsible for the yield point in A1-Mg alloy by Westwood and Broom,3 and in aluminum alloys containing various amounts of alloying elements by Smallman, Williamson, and Ardley.4 In these cases, the yield point is considered to be associated with the locking of dislocations by impurity atoms. Birn-baum and filer5,6 and Takamura and muira7 reported that, when a high-purity copper specimen was prestrained, then held at a lower stress, and finally reloaded at the prestrain temperature, a larger yield point was observed. Such an increase was attributed to the locking of dislocations by point defects. In addition, Bolling8 suggested that both mechanisms, i.e., dislocation-dislocation interaction and strain aging, are responsible for the yield phenomenon, at least in a brass. Thus, there appears to be experimental evidence for both the strain aging and dislocation-dislocation interaction theories to explain the yield point in the fcc metals and alloys. In a previous article,9 one of the authors observed that, if sufficient amounts of metal were electrolti-cally removed after deformation of a high-purity aluminum single crystal, the yield point did not appear upon reloading. Continued pursuit in this area revealed that the effect of the surface on the yield-point phenomenon is not limited to one metal but affects a variety of metals of different lattice structures. Nor is the effect limited to the yield points produced by simple unloading-reloading at constant temperature; the surface exerts an important role on the yield point even when the temperature is changed at some stage during the test. It is the intent of the present article to give additional information regarding the effect of the surface on the yield-point phenomenon and to show the association between the yield point in both fcc and bcc metals and the existence of a heavy concentration of dislocation in the region near the surface of a deformed specimen.10 EXPERIMENTAL Materials. The single crystals used in this study had a nominal cross section of 0.125 by 0.125 in. and a 3-in. gage length and were prepared by a modified Bridgman technique. The initial purity for the metals was 99.997, 99.999, and 99.999 pct for aluminum, copper, and gold, respectively. Bar stock of these same materials was used in the preparation of the polycrystalline specimens of aluminum and copper. The iron specimens were machined from rods of "ferrovac", reported to have a purity of 99.98 pct. In addition, a precipitation-hardening aluminum alloy, containing 1.5 pct Cu, 2.5 pct Mg, and 5.5 pct Zn, was used. The polycrystalline specimens of iron, copper, and the aluminum alloy had a diameter of 0.17 in. and a gage length of 2 in. while the high-purity aluminum specimen had a nominal rec-

Jan 1, 1965

By H. G. Sell, G. W. King

An investigation was made of the lensile proper-ties of recrystallized high-purity tungsten and a W-1 pel ThO2 dispersed-phase alloy over the temperature region of 800° to 2400°C. The thoria addition resulted in a modest strengthening effect over the entire temperature region. A decrease in ductility of both materials occurred above 0.5 Tm which was caused by void formation. Current theories of IT has long been recognized that a second phase of hard particles has a strengthening effect on a pure metal. At low or intermediate temperatures (<0.5 Tm), the strengthening effect is thought to arise mainly from the interaction of dislocations with dispersed particles. Above 0.5 Tm, dynamic recovery processes greatly alter the deformation mechanisms from those simply involving glide, and grain bound- strengthening by a dispersed second phase do not adequately explain the tensile results. Melallographic examination suggests that the improved strength of tire alloy results from the effect of thoria on the mierostructure. Stress-dependent thermally activated processes were found to occur high temperatures. aries may act as sources of weakness rather than strength because of grain boundary sliding. Grain boundary sliding at high temperatures has been postulated to be the primary factor giving rise to the formation of voids or cavities at grain boundaries1-3 which in turn cause premature failure and poor ductility.4 Voids, once formed, can grow by the condensation of vacancies from the equilibrium concentration&apos; or from the excess vacancies produced by the deformation.4,5 The high-temperature tensile properties of unalloyed tungsten have previously been investigated by Sikora and Ha116 and also by Taylor and Boone.7 The purpose of the present work was to investigate

Jan 1, 1965

By J. Szekely

The paper discusses simultaneous heat conduction and diffusion. These problems may arise in slag-metal kinetics and in connection with rapid heating or cooling of specimens. A mathematical formulation is given and it is shown that the transients due to either the variability of the diffusion coefficient with temperature, or thermal diffusion, are unlikely to be important for molten or solid metals and slags. The negligibility of these effects is due to the large values of the ratio thermal diffu-sivity/molecular diffusivity. In many problems relating to transport-controlled metallurgical kinetics the diffusion process is accompanied by the transfer of heat; large-scale metal refining or metal reduction may be quoted as examples. It has been shown that due to turbulent mixing in these systems the relevant transport phe- nomena are best described in terms of "surface renewal models" which require the solution of the unsteady-state diffusion equation.1-1 Problems involving simultaneous diffusion and heat conduction are also encountered in the laboratory in connection with rapid heating or cooling of specimens. The effect of variable temperature on diffusion may be twofold: a) in the absence of "cross effects" the problem, due to variable temperature, is that of diffusion with a variable diffusion coefficient; b) if the Soret Effect is nonzero, thermal diffusion must also be taken into account in the formulation. Although information is available on thermal-diffusion transients in a steady-temperature gradient,4&apos;5 little work has been done on the effect of unsteady temperatures on either the diffusion coefficient or on thermal diffusion.&apos; In the following a formulation is given and solutions presented with a view of examining the areas where these effects may be important.

Jan 1, 1965

By B. Ramaswami, Y. Nakada, R. Schaefer

EARLY investigations1 of the tensile properties of fcc single crystals did not reveal the easy glide region of crystals with axial orientations inside the standard stereographic triangle. With the production of high-purity metal, a region of easy glide became known1 Consequently, modern work of fcc single crystals ordinarily uses high-purity metal. In order to determine whether further purification of aluminum beyond 99.992 pct purity would result in significant alteration of the tensile properties of single-crystal specimens, metal was zone-refined and crystals grown from the purified material were compared to crystals grown from the original material. Some similar studies were made of gold and silver crystals. Aluminum. The material to be zone-refined was cast into bars 1/4 by 1/2 by 8 in. A zone, approximately 1-1/2 in. in length, was passed over each bar eighteen times at a rate of 6 in. per hr. Melting and stirring were carried out by an induction heater under a vacuum of approximately 10"5 mm Hg, the metal being held in a graphite container. he last 3 in. of each processed bar were then cut off and discarded. No quantitative determination of purity was made, but the effectiveness of the zone refining was tested by a method first suggested by Walton, Tiller, Rutter, and winegard3 depending on the relation between cell structure and impurity content. Rutter and Chalmers4 have shown that a cellular substructure is associated with the presence of impurities during solidificatibn, and have shown how solute rejection at the freezing interface can lead to such an association. Thus the observation of cells gives evidence of impurities being present. To look for cells, the last quarter of a zone-refined bar was cut off, remelted, and grown rapidly into a single crystal. It was then heavily electropolished and thermally etched.~ Cells were revealed by the presence of many parallel rows of etch pits. The same process was carried out with material from the first half of the bar, but no cells were detected. These observations give evidence that a significant amount of impurity material was moved to the "dirty" end of the zone-refined bars. Further indication of purification was obtained from recrystallization experiments. It was found that, after cold rolling to a 97 pct reduction in thickness, the material from the pure end of the bar re-crystallized at room temperature, but the material from the "dirty" end did not. Other investigators6 have previously reported that zone-refined aluminum recrystallized at room temperature. The purified material was cast into 1/4 by 1/4 in. bars, and seeded crystals were grown in a (100) orientation and in a single slip orientation where the Schmid factor is m =2. The crystals were then cut to the desired length, annealed for 24 hr at 610°C, furnace-cooled, and etched in Tucker&apos;s etch. The crystals were tested in a floor-model Instron machine, using a gage length of 4 in. and a strain rate of 1/2 pct per min. The resulting curves are shown in Fig. 1. It is seen that the differences between the curves for zone-refined and original-purity materials are small. These differences are within the scatter observed for crystals of the original purity. In particular, the zone refining does not significantly affect the onset of the different "stages" of the curves.

Jan 1, 1964

By D. I. Bardos, A. M. Bardos, Paul A. Beck

The approximate effective silicon radii in ternary Laves phase alloys with transition elements and silicon were found to range between 1.16 and 1.21A, i.e., considerably smaller than the atomic radius calculated for elemental silicon. The atomic radii were found to increase with the size of the transition element atoms in the structure. It has been noted by Aronsson1 that silicon in solid solution in iron, cobalt, and nickel has an effective CN 12 atomic radius of approximately 1.20Å, a value very much smaller than the CN 12 radius of 1.34Å derived from the interatomic distances in elemental silicon.7 The unusually short metal-silicon interatomic distances in transition element monosilicides and disilicides have been also pointed out by various investigators.1 A similar tendency was observed by Nevitt in Cr3O type silicides.2 Recent work on Laves phases in ternary systems of silicon with transition elements4"8 suggested that extensive Laves phase fields may occur in such systems.8 It has been pointed out by Laves7 that the MgCu2 and MgZn2 type structures lend themselves particularly well for the determination of the effective radii of the component atoms. In these AB2 phases the B atoms are arranged in close packed straight lines, and their distances are related in a simple manner to the lattice parameters.8 The present work was undertaken in order to find out whether or not the B transition element in such AB2 Laves phases can be replaced to an appreciable extent by silicon. In cases where extensive substitution proves to be possible, the "average atomic radius for the B site" at various silicon contents was to be determined, and the effective atomic radius of silicon calculated by extrapolation to complete replacement of the B component by silicon. The following ternary systems were studied: Ti-Mn-Si, Ti-Fe-Si, V-Co-Si, V-Ni-Si, Nb-Fe-Si, Nb-Co-Si, Ta-Fe-Si, Ta-Co-Si, and Mo-Fe-Si. In all of these alloy systems, the Laves phase solid solutions were found to extend over a considerable range of silicon content. As previously reported,4"8 in the V-Co-Si, V-Ni-Si, and Mo-Fe-Si ternary systems Laves phases do occur, even though there are no corresponding binary Laves phases. In stabilizing the Laves phase, silicon acts as if it were decreasing the effective electron concentration of the alloy.8 A more detailed study of the boundaries of the Laves phases in the V-Co-Si and V-Ni-Si systems has been made and will be published elsewhere. In both cases, the elongated Laves phase fields extend parallel to the B-Si side of the composition triangle, clearly showing that silicon is substituting for cobalt, respectively, nickel over a wide range of compositions. The binary Laves phases NbCo2 and TaCo2 have the cubic MgCu2-type structure. It was found that, in both ternary systems with silicon, again the MgZn2-type hexagonal Laves phase is stabilized and that this phase extends to high-silicon contents. In each ternary system at least three Laves phase alloys of the composition A(B1_xSix)2 were used, x here denoting the fractional substitution of the B-transition element atoms by silicon. The alloys, listed in Table I, were prepared by arc melting in argon. Each specimen was water quenched after a homogenizing anneal of 3 days at 110(FC, except for the Mo-Fe-Si alloys, which were annealed at 1200°C. Metallographic examination showed that most of the homogenized alloys consisted of a single phase, although some had minor amounts of a second phase, as shown in Table I. X-ray diffraction patterns were prepared using an asymmetrical focusing camera of large resolution and Fe Ka radiation. The patterns were indexed, and the lattice parameters of the hexagonal Laves phases were determined from the available diffraction lines of highest indices: (213), (205), and (313). The lat-

Jan 1, 1963

By J. B. Coher, M. B. Bever

COLD work destroys long-range order, as was first observed by Dehlinger and Graf.1 Dahl2 showed that the mechanical disordering caused by cold work produces changes in those properties that are affected by long-range order. The existence of order has a marked effect on tile manner in which an alloy deforms and therefore on its mechanical properties.L&apos; The relation between order and deformation behavior however, is only beginning to be understood. Seemann and G1ander4 suggested that cold work reduces an ordered alloy to a kind of gruel of antiphase domains. According to Cottrell,5 superdis-locations and pairs of dislocations in a slip plane connected by a strip of anti-phase domain boundary provide deformation mechanisms which do not change the state of order. In general, however, slip may be expected to produce new domain boundaries and destroy order if dislocations move on intersecting planes or cut through existing domain boundaries. The yield strength of an ordered alloy may pass through a maximum with decreasing domain size.5"7 The reduction of domain size resulting from cold work may, therefore, lead to a maximum in strength properties. Flinn8 suggests that dislocations can climb by short-range diffusion during deformation and thus can generate domain boundaries not only on slip planes, but also on other planes which will be those with the lowest domain-boundary energy. It has long been known that the rate of strain hardening of an alloy in the ordered state is larger than in the disordered state.3&apos;9 Also the slip bands in ordered CU3, AU10 and Ni3Mn" are finer than in the disordered alloys. The stress which causes initial yielding in Cu,Au passes through a maximum with decreasing domain size.6&apos;12 A maximum has also been observed in the hardness of ordered Ni3Mn as a function of strain.&apos; These observations suggest, but do not prove, that domain size reduction occurs during deformation. According to Fisher13 slip destroys short-range order and thus the strength of an alloy is related to the degree of short-range order present. Rudman and Averbach14 and Averbach et a1.,15 demonstrated that cold work reduces short-range order in copper-gold and gold-silver alloys. Destruction of long-range and short-range order by cold work implies slip on an appreciable fraction of planes. Yielding of an alloy in which short-range order exists or antiphase domain boundaries are present should be discontinuous because the first dislocations moving across the slip plane meet with the largest resistance.5 Such discontinuous yielding has been observed in CU3AU6,16 and Cuzn.l7 This phenomenon, however, can also be explained by mechanisms not involving order.b The published investigations of the effects of cold work on alloys with long-range or short-range order have not been covered thoroughly in reviews of order-disorder phenomena. These investigations, therefore, will be listed here. They have been concerned with strength properties> 2,3,6,8,9,12,16-21 electrical resistivity,2,4,18,19,21-26: thermoelectric power, magnetic properties,2,18,21,26 and X-ray strain&apos;1,2,14,15,27,28 The slip systems and the appearance of the microstructure after deformation in ordered and disordered alloys have also been investigated. 6.10.ll,l7,23,29,30 The alloys used in these investigations were copper-gold. 1-4,6,9,10,14,16,18 23-26,28,29 copper-zinc. L7. 19. 20,30 nickel-manganese,2 11,21 iron-aluminum. iron-nickel,&apos; copper palladium,4,18,22 gold-silver.4,18,22 and palladium-silver-copper.4 In the work reported here. the changes in properties of polycrystalline Cu3Au were investigated as functions of strain in wire drawing and rolling. Specimens were heat treated before deformation

Jan 1, 1961

By Harry A. Lipsitt, Douglas Y. Wang

A fatigue study in completely reversed axial tension-compression has been perforried on high-purity titanium and on three high-purity alloys of titanium. The alloys each contain approxi7nately 0.75 at. pct of a single interstitial element; carbon, nitrogen, and oxygen, respectivley. The results corroborate a previously published theory which proposed that strain aging under alternating stress was responsible for the fatigue limit behavior of certain alloys. The present data indicate that in these alloys an increasing strain-talline aging effect under alternating stress is provided by oxygen, carbon, and nitrogen, respectively. CURRENT research on the nature of the fatigue limit in metals suggests that the presence of a fatigue limit in metallic materials is a manifestation of strain aging that occurs under alternating stress.lm5 A comprehensive theoretical model based on the above hypothesis has been developed to explain the existence of a fatigue limit.&apos; This model also provides increased insight into several other fatigue phenomena as under stressing, overstressing, and coaxing effects. The theory, as well, provides equal understanding for those cases where no real fatigue limit is observed. Briefly, this theory assumes that the S-N curve for a pure metal is a smooth function of the applied stress, and the effect of adding an element that is soluble (or forms a precipitate) in the pure metal is simply to shift the S-N curve to the right. If the added element confers the power to strain age, the result is a further shift of the S-N curve, this time upward and to the right. Since strain aging is not expected to be a strong function of stress, and since damage per cycle is known to be quite stress dependent, it is to be expected that there will be some limiting lower stress at which the strengthening due to strain aging will balance the damage due to crack propagation. This stress is the fatigue limit. The position of the fatigue-limit knee was thought to be a function of the magnitude of the strain-aging effect on both the finite and infinite life portions of the S-N curve. Although the strain aging hypothesis seems to be reasonably valid for bcc materials,2&apos;6 it needed to be tested for both fcc and cph metals. This report is the first of a series concerning the fatigue-limit behavior of titanium with varying amounts of the interstitial solutes (C, N,, and 4) that are known to cause static strain aging in titanium. Yield-point effects have been reported for polycrys-talline high-purity titanium alloys containing either carbon, nitrogen, or oxygen.7&apos;9 These effects were observed at testing temperatures in the range 100 to 300&apos;. In addition yield-point and strain-aging effects have been reported for single crystals of titanium containing 0.1 wt pct C plus N.&apos; These yield points were observed over a wide temperature range, but no room-temperature aging occurred. Aging at 180&apos; was required to cause the return of the yield point. The magnitude of the yield phenomena in titanium containing interstitials is not expected to be as large as is observed in bcc metals because of several factors. Titanium has a very high chemical affinity for oxygen and nitrogen. The thermodynamic stability of solutions of oxygen or nitrogen in titanium is recognized. Lattice parameter measurements of titanium containing arbon, oxygen,1° or nitrogen" show that the "c" parameter is expanded more than the "a" parameter, but that up to about 2 wt pct this results in an insignificant change of the axial ratio &apos;c/a." Ehrlich" has shown that the sites occupied by interstitial atoms in titanium are spherically symmetrical and therefore a lattice expansion, at a constant c/a ratio, results in a simple dilation of the interstitial site. Such a dilation involving no shear has been shown to react only with edge components of dislocations.13 This causes only a weak pinning action. Shear stresses would be anticipated locally when only one of the two interstitial positions was occupied. The carbon atom will cause a symmetrical distortion of the lattice whereas the oxygen and nitrogen atoms have, in addition, the previously mentioned chemical affinity of titanium for these elements. These factors will result in a considerably smaller reduction of free energy upon the association of interstitial atoms with dislocations, and therefore a much weaker pinning than has been observed for the bcc metals. These considerations would lead to the hypothesis that of the interstitial elements considered here carbon would cause the strongest pinning effect in titanium where the amount of interstitial in solution is constant. This hypothesis will be borne out in the analysis of the present results.

Jan 1, 1962

By F. Seitz

STAFF: Editor, Gerhard Derge Carnegie Institute of Technology Schenley Park Pittsburgh 13, Pa. Editorial Assistant, M. A. Redmerski Managing Editor, James J. Burke THE METALLURGICAL SOCIETY: John Chipman, President; W. R. Hibbard, Jr., Post-President; C. C. Long, Vice-President; T. D. Jones, Treasurer; R. W. Shearman, Secretary. PUBLICATIONS COMMITTEE OF THE METALLURGICAL SOCIETY: R. Maddin, Chairman; Dennis Carney, J. C. Fulton, J. H. Hollomon, T. B. King, C. C. Long, W. 0. Philbrook, J. D. Sullivan, David Swan, and F.L. Vogel. Review and selection of manuscripts is under the supervisian of the following Publications Committees: Extractive Metallurgy D ivis ion: T. 0. King, Chairman; S. J. Dick inson, R. P. Hermsdorf, R. Schuhmann, Jr., and H. H. Kel logg. Institute of Metals Division: F. L. Vogel, Choirmon; R. L. Smith, Vice Chairman; R.W. Balluffi, J. H. Bachtold, A Servi, C.D.Graham, Jr., C. G. Goetzel, F. E. Joumot, Jr., G. E. Pellissier, Paul Gordon, Jock Washburn, Harold Margol in, A. U. Seybolt, I. R. Kromer, R. A. Meussner, R. W. Guard, M. Harmon, J. N. Hobstetter, Dean Starr, P. Shewmon, R. Gordon, J. 0. Betterton, and E. Morgan. Iron and Steel Division: W. 0. Philbrook, Chairman; F. C. Langenberg, C. W. Sherman, J. Wagstaff, and E. J. Whittenberger. Published bimonthly by the American lnstitute of Mining, Metallurgical, and Petroleum Engineers, Inc., 29 West 39th Street, New York 18, N. Y. Telephone: PEnnsylvania 6-9220. Subscription $20 per year for non-AIME members in United States and North, South, and Central America; $25, foreign; $5 for AlME members. Single copies, $4.00, single copies foreign, $5.00. The AlME is not responsible for any statement made or opinion expressed in its publications . . . Copyright 1959 by the Americon Institute of Mining, Metallurgical, and Petroleum Engineers, Inc. . . . Registered cable address, AlME New York ... Indexed in Engineering Index, Industrial Arts Index, and Chemical Abstracts . . .Second class postage paid at New York, N. Y. , ond Ann Arbor, Mich. Volume 215, Number 3

Jan 1, 1960

By J. W. Cunningham, M. J. Stultzman

THE demand for improved materials for high-temperature service has increased during the last few years. Iron,- nickel,- and cobalt-base alloys have been investigated extensively and many alloys with outs&apos;tanding high-temperature strength have been developed. Considerable research has been directed toward improved methods of processing these alloys. The vacuum furnace as a tool for the purification and improved control of high-temperature alloys has been studied extensively and production units are in operation. The research covered by this paper studied the effects of casting in air, vacuum, or argon upon the elevated-temperature properties of two nickel- and two cobalt-base alloys. The alloys investigated were Stellite 31, He 1049, Udimet 500, and Guy Alloy. MELTING AND CASTING PROCEDURES Two heats of each of the four alloys under investigation were melted and investment cast under the following conditions: 1) Stellite 31 was melted and investment cast in air and in vacuum, with an argon atmosphere for pouring. 2) He 1049 was melted and investment cast in air and in vacuum, with an argon atmosphere for pouring. 3) Udimet 500 was melted and investment cast in vacuum with and without additions of zirconium and boron. 4) Guy Alloy was melted and investment cast in vacuum and in argon. The heats were all melted in induction furnaces equipped with preformed magnesia crucibles of 50-lb capacity. The air-melting furnace was powered by a spark-gap converter of 40 kw capacity. The vacuum-melting furnace was powered by a motor-generator set of 100 kw capacity. The argon heat of Guy alloy was melted in the vacuum melting furnace under an argon atmosphere. Virgin materials were used for preparing all heats except the air heats of Stellite 31 and He 1049. The charge for the air heat of Stellite 31 was a commercial blend of shot. The charge for the air heat of He 1049 was Stellite 6 shot plus those virgin materials necessary to give the desired composition. All of the materials used were of the same grade used com-

Jan 1, 1960

By L. S. Richardson, N. J. Grant

Iodide-grade titanium, two oxygen alloys, and two aluminum alloys were studied by means of creep-rupture tests from 1000° to 2000°F. From the test information an evaluation was made of, 1) the relative creep-rupture strengths of the u (hexagonal-close-packed) and 0 (body-centered-cubic) forms of titanium and some of its alloys; 2) the effects of solid-solution strengthening by oxygen and aluminum on the u and 0 structures; and 3) the extent and effect of atmospheric oxygen alloying on rupture life in tests above about 1000°F. THE use of titanium alloys at temperatures above 1000° F has been considered unlikely by most investigators because of low creep strength (based on a requirement for room-temperature ductility, formability, and weldability) and low oxidation resistance. The results of this testing program do not entirely uphold this pessimism in terms of strength and oxidation resistance. The observations described below are based entirely on stress-rupture results, although some creep tests were also carried out on these alloys. Three items of primary importance are covered: 1) Stress-rupture data in the form of the Larson-Miller parameter curves for several titanium alloys at temperatures up to 2000°F; 2) The relative strengths of the hexagonal-close-packed a structure and the body-centered-cubic 0 structure; 3) The effects of solid-solution alloying on the creep-rupture properties of titaniu&apos;m at elevated temperatures. Only two investigatons have reported the creep- rupture properties of titanium at temperatures above 1000° F. Lunsford and rant&apos; tested iodide titanium; their values are also utilized in the paper. EXPERIMENTAL PROCEDURE After a few tests had been made in a conventional creep-rupture test machine, it became clear that some sort of atmospheric protection would be necessary for short-time tests conducted at temperatures above 1600°F, or for times greater than 100 hr at 1200°F or above. Several furnace units and test machines were constructed, the most successful of which is shown in Fig. 1. Certain experimental difficulties peculiar to titanium were encountered; for example, the use of molybdenum holders was dictated because titanium forms low melting-point eutectics with conventional high-temperature alloys containing appreciable amounts of iron, nickel, or cobalt. This same difficulty made the use of chrome l-alumel thermocouples in direct contact with a test specimen impossible, above about 1500" F. The high-temperature high-vacuum furnace shown in Fig. 1 was capable of maintaining a vacuum of better than 10"5 mm of mercury at 2000°F (pressure measured in cold part of system) and 5 X lo-&apos; mm at room temperature. Most of the tests eonducted in vacuum were at temperatures

Jan 1, 1960

By R. H. Frazier, J. M. Hodge, F. W. Boulger

This paper reports the results of studies of the impact properties of quenched and tempered alloy-steel plates as a function of sulfur content. It was found that the impact energy levels decreased continuously as the sulfur content increased and that there was a straight-line relationship between impact energy and sulfur content when plotted on logarithmic coordinates. Cross rolling raised the level of these Lines for transverse tests and lowered the level for logitudinal tests proportionately to the amount of cross rolling. ALTHOUGH it has been generally recognized that, for applications in which notch toughness is critical, the sulfur content of the steels used should be held to a low value, quantitative information on the effect of sulfur on notch toughness has not been available. For such applications, it is a common practice to specify minimum impact values, and in order that these may be met consistently it is important that the steel producer know quantitatively the effect of sulfur on notch toughness so that realistic sulfur content limits can be applied to the steels they produce. In many instances, particularly in flat-rolled products, impact properties are specified in the direction transverse to the principal rolling direction, so that the factors affecting the anisotropy or directionality of impact properties are also of concern to the steel producer. For some applications, furthermore, it is a common practice to increase the sulfur content of steels in order to improve their machinability, and, in such instances, the effect of this practice on notch toughness may often be of concern. This paper reports on an investigation, carried out at Battelle Memorial Institute, designed to furnish this quantitative information on the effect of sulfur on notch toughness and also to furnish further information on the factors affecting the anisotropy of impact properties in wrought heat-treated alloy steels. MATERIALS AND EXPERIMENTAL PROCEDURE The experimental steels were of intended base analysis: 0.30 pct C, 0.80 pct Mn, 0.25 pct Si, 2.5 pct Ni, 0.80 pct Cr, and 0.45 pct Mo. Steels were made with sulfur contents varying from 0.005 to 0.179 pct. The steels were prepared from 600-lb induction-furnace melts. Steels containing 0.020 pct or more sulfur (at meltdown) were melted from a charge of ingot iron (except for one heat): lower-sulfur steels were made from electrolytic iron. The charge consisted of ingot or electrolytic iron, ferrosilicon to give 0.10 pct Si, and ferromanganese to give 0.05 pct Mn. At meltdown, electrolytic nickel, ferromolybdenum, iron phosphide, and pyrite were added followed in sequence by ferrochromium, sili-comanganese, ferrosilicon, and ferromanganese. The slag was then removed and graphite added to give the desired carbon content. Bath temperature was adjusted to 2850°F and, when no other additions were to follow, 2 lb per ton of aluminum was added, immediately before tapping. Compositions of the experimental steels appear in Table I. Analyses are from single determinations, except sulfur which was analyzed in duplicate. A test sample (3 in. in diam by 6 in. long) and a 575-1b ingot were poured from each heat. The test sample was poured in a sand mold; the cooling rates of the test sample and the large ingot were approximately the same. Chemical analysis chips and metal lographic specimens were taken from the test samples. The ingot was 8 in. sq at the base and 9 in. sq at the top. A 5 X 5 X 6-in. sand mold hot top was completely filled in teeming the ingot. After solidification, the mold was stripped from the ingot which cooled to room temperature. Ingots were reheated to 2250"F and rolled to 1.9-in. slabs on a commercial mill. The slabs were box-cooled to room temperature. Sections of the 1.9-in. slabs were heated to 2250°F and rolled on a Battelle laboratory mill according to one of three schedules: 1) rolled straightaway to 0.5-in. plate; 2) rolled straightaway to 1.3-in. thickness, then cross rolled to 0.5-in. plate (29 pct cross rolling); or 3) cross rolled from 1.9-in. to 0.5-in.-thick plate (46 pct cross rolling). The 0.5-in.-straight- or cross-rolled plates were normalized at 1700°F for 1 hr and then water quenched from 1600°F. Plates were then tempered 2 hr at 1240°, 1170°, 1080°, or 860°F to obtain Rockwell C hardness of 25, 30, 35, and 40, respectively. Tempering was followed by quenching to room temperature to avoid temper embrittlement. Slack-quenched plates were isothermally transformed for 26 min at 800°F, quenched, and tempered 2 hr at 1170°F. Pearlitic microstructures were obtained by holding 168 hr at 1200° F, followed by quenching. Charpy V-notch specimens were taken both transverse and longitudinal to the main rolling direction, notched perpendicular to the plate surface, and tested. Slabs and plates which were to be homogenized

Jan 1, 1960

By L. W. Davies

A problem often encountered is the provision of materials which have impurity contents below a certain specified level. This problem is in some cases solved by making use of the segregation of the impurity with respect to the liquid and solid states of the material: an ingot of the material is subjected to directional solidification and the ends of the ingot. which are richer in solutes which respectively raise and lower the melting point of the solvent, are removed. An important extension of this process is the zone-refining process invented by Pfann,&apos; in which molten zones are passed successively along the length of an ingot and displace solutes towards the ends. Pfann&apos;s process is particularly appropriate in cases for which the segregation coefficient k does not differ greatly from unity, or when the impurity content must be kept extremely low (=10-6 atom fraction); it is widely used, particularly in the purification of materials for use in semiconductor electronic devices. It is the purpose of this paper to investigate theoretically the efficiency of the above refining processes; that is! we determine the most economic method of attaining a given yield of solvent of specified purity, taking into account the variables of the process. One variable of interest is the effective value of the segregation coefficient. which depends on the rate of movement of the liquid-solid interface and on the degree of stirring in the liquid; in addition to this, in the zone-refining process we are also interested in the choice of zone length for most efficient operation. A mathematical determination is made here of the lengths of successive molten zones which give, for an initially uniform distribution, the most efficient removal of a solute of arbitrary distribution coefficient. In order to be able to give a quantitative treatment of efficiency, we first define figures of merit applicable to a given distribution of solute. FIGURE OF MERIT Let an ingot of length L contain a distribution y(x) of solute: we confine our discussion to mono-tonic distributions, in order to avoid inconsistencies in the subsequent analysis. The first moments of the distribution about the origin and x = L are respectively L F = hy{x)dx [I] G = f(L -x)y(x)dx = YoL2-F, [21 where yoL is the total amount of solute present. We shall see that the quantities F and G are useful figures of merit for a discussion of the efficiency of zone-refining processes. In the first place, it is

Jan 1, 1960