Search Documents

By R. I. Jaffee, F. C. Holden, H. R. Ogden

The mechanical properties of Ti-C and Ti-C-0 alloys can be altered by heat treatments to dissolve or reject carbon from solid solutions. The maximum strength is obtained by annealing just below the peritectoid temperature. Quenching from the ß-carbide field results in softening. Impact behavior is influenced by the extent of solution of interstitials CARBON is not as important in titanium alloys as it was in earlier years when graphite induction melting was more prevalent. With induction melting, carbon pickup is about 0.5 to 0.8 pct. Cold-mold arc melting with graphite electrodes, which is among the more current methods, results in carbon pickup of 0.1 to 0.2 pct. The titanium-sponge melting stock itself contains about 0.02 to 0.07 pct C, picked up from the magnesium used in the reduction process. Thus, carbon is still one of the more important contaminants in titanium and needs careful study and evaluation in order to understand titanium and titanium alloys. Moreover, it is equally proper to consider carbon as an alloying addition because, in controlled amounts in titanium alloys, it may serve a most useful function. This is particularly the case where the ultimate in toughness is not required. The addition of carbon to titanium results in a peritectoid-type system as illustrated in Fig. 1. The solubility of carbon is seen to be higher in the a phase than in the ß phase in the temperature range of interest. Below the peritectoid temperature, the solubility of carbon in a titanium decreases with decreasing temperature. This type of system permits many microstructural and heat-treatment variations which may influence the properties of the alloys. The study of how the microstructure variations affect mechanical properties is described in this paper. Experimental Procedures The experimental techniques and testing methods used in this work were the same as those described in detail in a previous paper.' No further descriptions will be given except where changes have been made. High purity iodide titanium, produced by the New Jersey Zinc Co., was used in all of the alloys. Carbon additions were made using high purity spectro-graphic carbon electrodes in order to obtain the highest purity carbon available. The alloys were prepared by double arc melting to reduce the possibility of segregation. The alloys were forged at 875°C to ¾ in. round, descaled, vacuum annealed for 5 hr at 900°C to remove the residual hydrogen, and swaged to ¼ in. round at 750°C. All heat treatments were made on material in this initial condition. Two of the early Ti-C ingots were found to have been contaminated in melting. Vacuum-fusion analyses showed that the two contaminated alloys had picked up oxygen, so the test results on these two alloys permitted an evaluation of ternary Ti-C-0 alloys. A list of the alloys and their compositions are given in Table I. Properties of Ti-C Alloys In a peritectoid-type system, such as the Ti-C system, the chief microstructural variable which influences the properties is solid-solution strengthening. For a given composition, it is possible to control the disposition of carbon, either in solid solution or as the compound Tic, by suitable heat treatments. When in solid solution, the carbon present in the alloy makes a definite contribution to the strength of the alloy. However, when present as Tic, it has very little effect on the strength. Other microstructural variables considered in this investigation were transformation structures and grain size. As discussed in subsequent sections, these variables have only a minor effect on properties as compared to the solid-solution effect. Solid-Solution Strengthening: The principal strengthening mechanism for Ti-C alloys has been found to be solid-solution strengthening. Carbon in interstitial solid solution strengthens titanium, but has very little strengthening effect if present as the compound. Since carbon has a higher solubility in

Jan 1, 1956

By Robert Bakish, William D. Robertson

AFTER more than fifty years of investigation and continuing failure in service, a satisfactory mechanism to explain stress corrosion cracking in homogeneous alloys is still lacking. The relative chemical activity of grain boundaries and adjacent grains, inferred from the boundary structure, has been used to explain intergranular cracking in a brass.' This concept is probably correct as a general hypothesis, but it requires much more extensive development in order to explain satisfactorily the observed phenomena. For example, the specific function of the solute in an alloy must be considered, because intergranular failure does not occur in pure metals,' which are structurally similar to homogeneous alloys. Also, in this connection, an inter crystalline fracture path in binary copper alloys can be changed to a transcrystalline path by relatively small ternary additions.' The fracture path in ß brass is predominantly transcrystalline,' in contrast with an inter crystalline path in a brass. Whether the two different fracture paths are the result of a difference in composition, crystal structure, or the state of long range order is unknown and cannot be determined with ß brass, because only the ordered state can be obtained at room temperature. The study of chemical activity at structural sites in the Cu-Zn system is restricted by the formation of opaque films in an ammonia environment in which stress corrosion cracking is generally observed. Furthermore, both components of the alloy are chemically active and the interpretation of observations is therefore relatively complicated. The Cu-Au system is a better choice for the purpose of studying structural factors. In particular, CuAu is very susceptible to cracking in ferric chloride and opaque films are not formed in this solution; it may be obtained in different states of long and short range order; and, finally, only copper is oxidized in dilute ferric chloride, which considerably simplifies the chemical problem. To provide information necessary for a more general explanation of stress corrosion cracking in homogeneous solid solutions, the following structural factors have been investigated in a Cu-Au alloy having a composition corresponding to Cu,Au: 1) the effect of long and short range order; 2) the structural sites from which copper is removed from the annealed and cold worked polycrystalline alloy; and 3) the effect of annealing time and temperature on structural reactions in the cold worked alloy. Experimental Procedure A Cu-Au alloy of nominal Cu3Au composition was cast from cathode copper and high purity gold and fabricated into sheet and wire. Chemical analysis for copper and gold indicated 48.92 wt pct Cu and 51.01 pct Au. Quantitative spectrographic analysis indicated 0.01 pct Ag, 0.002 pct Pd, 0.001 pct Pb, and 0.002 pct Fe, with traces of magnesium, silicon, and zinc. Presumably most of the remaining 0.055 pct corresponds to the limits of analytical precision. Heat treatments of wire and sheet were conducted in argon or vacuum. Wire specimens, 0.064 in. diam, were heated for 1 hr at 850 °C to establish a definite

Jan 1, 1957

By A. E. Austin, J. R. Doig

Ti-Cr alloys age harden after B-quenching by formation of an W-phase. The structure and orientation of this transition phase have been determined. The hardness ap-pears to be caused by strain in the B-matrix produced by concurrent enrichment of alloy content in the W-phase. EARLY studies of age hardening in B-stabilized titanium alloys revealed the formation of a transition phase named o' This phase was detected by X-ray diffraction in binary alloys of Ti-Fe, Ti-Cr,

Jan 1, 1958

By Kichizo Niwa, Toshio Yokokawa, Mitsuo Shimoji, Yoshihiko Watanabe, Satoshi Kado

A LTHOUGH a systematic research on diffusion in liquid metals has not been carried out, partial studies have been developed by various workers in several systems. A few recent papers among them have shown that this line of approach is quite useful for understanding the structure of the liquid state. Furthermore, it has been found in kinetic

Jan 1, 1958

By David A. Thomas, John F. Peck

Fibrous microstructures and their development have been studied by metallography and by hardness and quantitative metallographic measurements. Thin, curved grains were observed in transverse sections of commercial tungsten wire and were developed in laboratory-drawn iron wire at reductions greater than about 70 pct. The unusual grain shapes are attributed to the nonuniform mode of deformation of the grains associated with the characteristic [I101 preferred orientation that develops in bcc metals during drawing. Transverse sections of heavily swaged iron wire showed a ospiral nebulao structure that appears to result from the elliptical shape of the cross section of the swaging dies and their rotary motion. Hardness and quantitative metallographic results show unusual trends that parallel the changes in microstructure. Other phenomena are considwed in light of the results, including the strength of fine wires of bcc metals, ocylindricalo textures, and the ductility of fibrous tungsten. 1 HE microstructure of tungsten wire in a longitudinal section shows grains highly elongated in the working direction, giving the appearance of a bundle of parallel fibers, Fig. l(a). Wires of tungsten and other bcc metals show a pronounced preferred orientation in which a [I101 direction is parallel to the wire axis.l The microstructure and texture of tungsten develop during warm working (working above room temperature but below the recrystallization temperature) into wire by swaging and drawing. Fibrous tungsten so produced has limited but useful room-temperature ductility, whereas annealed tungsten is brittle at room temperature. During an investigation of the effect of recovery annealing on the substructure of commerical 0.030 in. diam tungsten wire, it was found that transverse sections of the as-received material showed thin, curved grains, Fig. 1(b), instead of the expected equiaxed grains. The fact that Figs. l(a) and (b) show different sections of the same material at the same magnification is at first disconcerting, because the long dimension of the curved grains in the transverse section is several times the average fiber width in the longitudinal section. However, a longitudinal section cuts most of the curved grains across their narrow dimension, giving the appearance of a multitude of narrow fibers. On the other hand, the plane of a longitudinal section occasionally includes a long dimension of a curved grain, resulting in a broad ofibero, such as A in Fig. l(a). EXPERIMENTS AND RESULTS To investigate the origin of fibrous microstructures and particularly the unusual transverse-section structure of tungsten, rods of iron (also bcc) were drawn and swaged in the laboratory. One rod of annealed Ferrovac E was drawn in six steps to a total reduction in area of 87 pct (0.10 to 0.036 in. diam), and a second rod was swaged to the same reduction, using approximately the same reduction steps. Longitudinal and transverse sections of the swaged and drawn iron wires are shown in Fig. 2, for reductions in area of 39, 73, and 87 pct. A fibrous microstructure in longitudinal section is first evident at 73 pct reduction, and it is further developed at 87 pct reduction. The grains in transverse section remain equiaxed until about 73 pct reduction, when they become somewhat elongated and curved. At 87 pct reduction, the drawn wire shows thin, curved grains in the transverse section, similar to those observed in tungsten. The transverse sections of the iron wires swaged 83 and 87 pct reduction in area show the striking ospiral nebulao structure in Fig. 2(d). This struc-

Jan 1, 1962

By G. K. Manning, A. R. Elsea, C. R. Simcoe

Boron increases the hardenability of hypoeutectoid steels by decreasing the nucleation rate of ferrite and bainite. It is postulated that concentrations of lattice imperfections, such as exist at the grain boundaries, furnish the necessary energy for nucleus formation. Boron, because of its atomic diameter, will concentrate at lattice imperfections where sites of suitable size are present. Boron will decrease the energy of these local areas by occupying these sites. This mechanism accounts for the large increase in hardenability observed with small amounts of boron. The loss of the boron hardenability effect and the boron precipitate formation are explained on the basis of increased concentration of boron at the grain boundaries either with increasing boron content of the material or with increasing temperature. COMMON alloying elements affect both the nucleation and growth rates of the austenite decomposition reactions.' This effect is largely a result of the slow diffusion rates of these elements. Although a small addition of boron markedly increases the hardenability of steel, the diffusion rate of boron, which is of the same order of magnitude as that of carbon, can hardly account for this effect. An addition of boron in the range of 0.001 to 0.003 pct is about as effective as an addition of 0.30 pct Mo, 0.40 pct Cr, or 1.25 pct Ni in increasing the hardenability of a 0.40 pct C steel;' however, increasing the carbon content of the steel decreases the effectiveness of the boron addition."' The difficulty in understanding why so small an addition of boron can replace much larger quantities of the more strategic alloys, together with the erratic behavior sometimes encountered in boron-treated steels, has interfered with their general acceptance by industry. In the belief that an understanding of the mechanism by which boron increases the hardenability of steel should lead to a more general acceptance of boron-treated steels, a research investigation to determine this mechanism was undertaken at Battelle Memorial Institute under sponsorship of Wright Air Development Center. Experimental Work In order to study the effect of boron on the transformation of austenite to ferrite and bainite, a group of steels was made with a basic composition similar to that of the SAE 8600 series. This base composition was chosen because it has sufficient hardenability to permit accurate measurement of the times required for transformation to start at various temperatures. The chemical analyses of the steels used in the first part of this investigation are listed in Table I. These steels were made as 200 lb heats in an induction furnace. The furnace charge was Armco ingot iron with the alloying elements added as ferroalloys. After the alloy additions were made, the heat was deoxidized with 0.125 pct Al. A 100 lb ingot was cast and an addition of 0.003 pct B, as ferroboron, was made to the metal remaining in the furnace. This metal was cast into a second 100 lb ingot. The ingots were forged to 11/4 in. diam bar stock from which end-quench hardenability specimens were obtained. Part of this material was further reduced by hot rolling to lx¼ in. bar stock from which specimens were obtained for isothermal transformation studies. Studies of Nucleation and Growth: End-quench hardenability tests were performed on these steels, using an austenitizing temperature of 1600°F. The hardenability curves, shown in Fig. 1, indicate that boron treatment resulted in considerable increase in hardenability of the steels. Any such change in hardenability must result from a change in the transformation rate of the austenite, and these rate changes can be established readily by isothermal transformation studies. Isothermal transformation studies were conducted on these steels as follows: specimens were austeni-tized at 1600°F for 15 min, transferred to a lead bath operating at a constant subcritical or intercritical temperature, held for various lengths of time, and water quenched. The specimens were sectioned for metallographic examination to determine the amount and the type of transformation products present. In order to determine the effect of boron on the formation rate of ferrite, isothermal transformation tests were made on the 0.20 pct C steel in both the boron-treated and boron-free condition at an intercritical temperature of 1375°F where ferrite is the only decomposition product of this low carbon austenite. The results of these tests are shown in Fig. 2, where the percentage of ferrite formed is plotted as a function of time at temperature. It is apparent that boron markedly decreased the transformation rate of austenite to ferrite at this temperature.

Jan 1, 1956

By R. H. Atkinson

With the object of improving the melting, casting, and working of palladium and 95.5 pct Pd-4.5 pct Ru, the effects of different melting atmospheres (reducing, oxidizing, and neutral), crucible linings, and annealing atmospheres have been studied. Some interesting observations are included about the solubility and diffusion of gases in palladium. THE object of the present work was to ascertain the effect of oxidizing, inert, and reducing ambient atmospheres on the melting and casting of palladium and a Pd-Ru alloy commonly used for jewelry. The need for such a study was indicated during World War I1 when jewelers experienced difficulty in their attempts to make small castings of the torch-melted Pd-Ru alloy by the lost-wax process. When the metal was melted under oxidizing conditions similar to those used for platinum, the castings were gassy; on the other hand, if the melting atmosphere was reducing, the castings were hot-torn and brittle. General Experimental Procedure Pure palladium sponge (99.9 pct Pd) and pure ruthenium powder (99.8 pct Ru) were used for making small ingots (50 g) of palladium and 95.5 pct Pd-4.5 pct Ru by induction melting. The coil, 3 in. high by 2 in. ID with 16 turns, was energized by a 20 kva Ajax high frequency converter. The melting crucibles, so-called sand crucibles, which were made of a highly refractory fireclay, were lined with different materials, including proprietary magnesia, alundum, zircon, and zirconia

Jan 1, 1957

By M. von Heimendahl, G. Thomas

The microstructure of TD-Ni has been examined by transmission electron microscopy in the extruded, annealed. and deformed states. The tensile properties hove been correlated with the observed microstructures and the results ore com-pared with those obtained from pure nickel. The important conclusions are that the thorin particles in TD-Ni act as strong burriers to dislocntion motion during both deformation (slip) and annealing (climb). During deformation. the dislocations tangle around the particles and a cell structure is devleloped after 10 pct or more strain. The cell size appears to be determined by the spacing of the largest particles and is about five times smaller than that in pure nickel for the same strain. The higher work-hardening rate in TD-Ni compared to nickel is probably due to the more rapid rate of dislocation multiplication in the alloy as a result of dislocation-particle interactions. The Th0,particles inhibit recrystallization and twin growh so that some strengthening may arise from the high density of small annealing twins. THE strengthening of materials due to the presence of a dispersed second phase has been the subject of considerable experimental and theoretical investigation in recent years. One of the newest dispersion-strengthened alloys to be developed is TD-Ni,1 a system of approximately 2 vol pct thoria (ThO2) dispersed in a matrix of commercially pure nickel. This material is fabricated by powder-metallurgical techniques and offers high-temperature stability and useful mechanical properties virtually to the melting point of the base metal. While the mechanical properties of this system have been investigated,2,3 there have been no reports in the literature concerning the microstruc-ture of TD-Ni and its correlation to mechanical properties. This paper describes a transmission electron microscopy investigation of the micro-structure of TD-Ni together with its mechanical properties. The results are compared with the structure and properties of pure nickel.

Jan 1, 1964

By Craig R. Barrett, Jack L. Lytton, Oleg D. Sherby

The types of substructures developed during high-temperature creep of (110)[001]-oriented polycrys-talline Fe-3.1 pct Si were examined by electroetching of dislocation sites. Edge dislocations were observed to accumulate adjacent to grain boundaries and poly-gonize perpendicular to their glide planes to form a "Pile-up" of nearly parallel tilt boundaries. The dislocation density developed within the grains during steady-state creep was found to increase with increasing stress. The formation of periodically spaced groups of edge dislocations along grain boundaries was observed, and it was proposed that these formed to relive bending stresses at grain boundary shear .faults. Grain boundary serrations developed at these faults, and it was suggested that this was a result of localized grain boundary migration at the polygonized groups. THE authors have conducted a series of high-temperature creep tests on (110)[001]-oriented poly-crystalline Fe-3.1 pct Si sheet. The creep specimens were examined at various stages of creep by means of electrolytic etching of dislocation sites using the chrome-acetic acid solution developed by Morris.' Hibbard and Dunn2 have demonstrated that the etch pits produced with this technique correspond to single dislocations. It is the purpose of this paper to present and discuss the dislocation substructures which were formed during high-temperature creep at constant stress. EXPERIMENTAL PROCEDURES The polycrystalline Fe-3.1 pct Si sheet employed in this study contained a (110)[001] texture. This texture was quite strong, and the elastic properties of the sheet closely approached those of a single crystal of iron.3,4 A typical analysis in weight percent for this material is 3.1 Si, 0.1 Mn, 0.003 C,

Jan 1, 1965

By R. W. Guard, M. E. Fine

By treating the dislocation like a surface and ap-plying the usual thermodynamic treatment to the adsorption process a Gibbs adsorption equation for dislocations was derived. For extended dislocations in binary solutions the adsorbed concentration on the fault, X2a, may be computed from (jo/da2b) where a2b is the activity of the solute in the bulk material and s is the stacking-fault energy. Using the data of Howie and Swann for s the adsorption concentration goes through a maximum at 2 at. pct Al in Ag-Al, 10 at. pct Zn in Cu-Zn, and 8 at. pct A1 in Cu-Al. The pinning stress calculated from this concentration difference goes Ihrough a maximum at the same concentration us the peak in X2 a. The computed pinning stress thus does not vary with composition in the manner predicted by Suzuki, as was also pointed out by Hendrickson. The results are compared with the stress increment which can be attributed to Suzuki locking in Cu-Zn and Cu-Al stress-strain curves. They both agree in magnitude and in the location of the maximum. The predicted and observed maximum values for the Cu-Zn system (where activity data are available) are 700 g per sq mm (predicted) and 1000 g per sq mm (measured, laking into account the orientation factor of 2.2 to convert poly-crystalline to single-crystal data). CERTAIN simple internal surfaces may be regarded as dislocation grids. This fact suggested that it might be profitable to consider certain phenomena related to segregation of solute atoms at dislocations from the point of view of the thermodynamics of surfaces and surface adsorption. A general treatment of this type is given and then the results are applied to Suzuki segregation and pinning. Confirmation of the results is obtained from comparison of stress-strain behavior for copper and copper-base alloys. Two kinds of dislocations need be treated: perfect and extended dislocations. In either case the line tension of a dislocation, ?. the work which must be done to increase the length of dislocation by a unit length, is analogous to the surface tension. For an undissociated dislocation ? is the self-energy of a unit length of dislocation; for an extended dislocation where is the self-energy per unit length of a pair of partials far enough apart so that there is no interaction energy, is the interaction energy per unit length, is the stacking fault energy per unit area, and w is the equilibrium separation of the paired partials. In the absence of an applied stress the force pushing the dislocation partials apart in a close-packed structure is Gb2/12p where G is the shear modulus, b is the Burgers' vector of the complete dislocation, and is the separation of the partials. At the equilibrium separation, w this force equals s. Thus

Jan 1, 1965

By J. J. Pye, J. B. Drew

The surface-diffusion coefficients of Ni63 diffusing on low-index planes of nickel single crystals have been measured over the temperature range from 400° to 1000°C using a precision autoradio-gvaphic technique. The activation energy for sur -face diffusion appears to he the same on the {111}, {110), and (100) planes and amounts to -0.60 ev. This is in good agreement with the value (-0.62 ev) reported for (111) planes obtained by mass-transport techniques. In an earlier paper, the authors have reported self surface-diffusion coefficients on silver.' In that work, a deviation of the diffusion coefficients from linearity in the Arrhenius plot was observed at high temperatures. This effect was attributed to a loss of tracer atoms into the bulk by volume diffusion. The purpose of the present work was to extend the technique developed to the nickel surface-diffusion system up to the point where volume diffusion would come into play. The nickel system especially lends itself to this technique due to the high efficiency of the isotope in darkening the film and the large absorption of the weak radiation (0.063 mev /3- particle of the trapped tracer atoms. The diffusion coefficients and ictivation energy for different orientations on nickel can also be compared with a report published by Blakely and Mykura 2 where a mass-transfer technique was used. This paper reports the self surface diffusion of nickel on the low-index planes over a wide temperature range using a precision autoradiographic technique. EXPERIMENTAL PROCEDURE The experiment is similar to that described in the earlier publication consisting of a radioactive needle as a source resting on a flat, smooth, chemically polished surface annealed in a dynamic dry-hydrogen atmosphere. The needle is held snugly on the surface by a holder fabricated from commercially pure nickel. The point source is made by grinding down a small-diameter nickel rod until a tip of approximately 0.1 mm radius is formed. It is then etched and the needle tip plated with the radioactive isotope Ni63. Nickel single crystals were used whose main impurities were spectrographically determined as Co 0.05, Fe 0.007, C 0.005, and S 0.003 pct. The surfaces, oriented to within 1/2 deg of the low-index planes, were carefully mechanically polished and etched in a 50-30-10-10 hot solution of acetic, nitric, sulfuric, and phosphoric acids giving a smooth polished surface. The crystals were then washed in distilled water and alcohol. Annealing temperatures ranged from 400° to 1000°C with a furnace arrangement in which the crystals could be brought up to temperature in times short compared to diffusing times. The temperature was maintained constant to ±10°C. In the temperature range investigated, the ratio of the surface-diffusion coefficient to the volume-diffusion coefficient (Ds/Du) was 105 or more and the mean bulk-penetration values, calculated from literature values of volume-diffusion coefficients,3 were on the order of 10-5 cm. After the diffusion anneal, the sintered needle is removed, and both the radius of the needle point and spot left on the crystal face are measured. The crystal is then placed on photographic film. Diffusion profiles are obtained by scanning the film with a recording microdensitometer which has a slit width of 10µ. DISCUSSION AND RESULTS The experimental conditions are such that the source strength and needle radius are essentially constant and the time is adjusted such that the mean bulk penetration is small. An exactly analogous heat-flow problem has been considered by Carslaw and Jaeger4 and the solution can be written in integral form as:

Jan 1, 1964

By W. Rostoker, R. P. Elliott, B. W. Levincer

Phase equilibria in the Ti-Cr-Mo system have been investigated for alloys containing 100 to 40 pct Ti in the temperature range 550° to 1300°C. Five experimental isothermal sections and a surface of incipient melting are presented in addition to a summary projection of the space. Seven vertical sections have been constructed from the isothermal sections. A STUDY of the system Ti-Cr-Mo was undertaken as part of a program sponsored by Watertown Arsenal toward the development of titanium-base phase equilibrium diagrams of potential technical importance to alloy development. The scope of the investigation included the composition range contained by the titanium corner and the line of 64 pct Ti (all compositions are by weight) and the temperature range 550" to 1100°C. A surface of incipient melting was constructed from measurements on a large number of alloys. The system Ti-Cr has been established.&apos;-? The phase diagram is characterized by a wide miscibility field of the solid solution at elevated temperatures and a eutectoid reaction of the type: (15 pct Cr) + TiCr, (685C). The a solid solution has a very limited capacity for solution of chromium (< 0.5 pct Cr). The intermediate phase TiCr2 has at best a very narrow composition range. It has been shown that two allotropic modifications of this phase exist. However, this behavior does not appear to be perceptibly reflected in the form of phase boundaries of the type + TiCr,. In the system Ti-Mo,9-10 the phase is stabilized to successively lower temperatures with increasing molybdenum content. There are no known intermediate phases. The a solid solution is limited to less than 0.5 pct Mo. Because of the very extensive range of the phase, the ternary system was ideally suited to the determination of the phase boundaries by the parametric method of Andersen and Jette." A parametric surface was constructed to provide the necessary basis for the application of this method. Preparation and Treatment of Alloys More than 60 alloy compositions were prepared for the study of this system. Alloy buttons of 10 grams were arc-melted in a nonconsumable electrode furnace using inert atmosphere protection and a water-cooled copper crucible. The construction and operation of this type of melting unit have been adequately described elsewhere.&apos;&apos; To insure complete solution of alloy additions, the buttons were remelted alternately on top or bottom as many as five times. This was accomplished by a suitable mechanism for "flipping" over the ingots. Iodide titanium (99.97 pct Ti) was used as the alloy base. An especially high quality chromium (99.9 pct Cr) was obtained from the National Research Corp. Molybdenum sheet (0.005 in.) of 99.9 pct purity was used.

Jan 1, 1954

By R. F. Domagala, M. Hansen, D. J. McPherson

Iodide zirconium was combined with calculated amounts of nitrided zirconium sponge and arc melted to prepare alloys in the 0 to 6 wt pct N region. Annealing treatments were carried out at 21 temperature levels. Metallographic examination of the heat-treated specimens permitted construction of the binary phase diagram from 0 to 6 pct N. Features of the diagram include the peritectic formation of both a and ß solid solutions. The maximum solubility of nitrogen is 0.8 pct in 8 zirconium and 4.8 pct in a zirconium. An X-ray study of nitrided materials was made in the range 6 to 13 wt pct N region because serious nitrogen losses were experienced when attempts were made to arc melt these high nitrogen alloys. PHASE relationships in the Zr-N system have been determined. Due to the inability to retain nitrogen in nitrogen-rich alloys subjected to arc melting, definitive work was possible only in the range 0 to 6 wt pct (0 to 30 atomic pct) N. Sufficient complementary X-ray work was done to permit construction of the binary phase diagram up to 13.3 wt pct (50 atomic pct) N (ZrN). Small ingots were prepared by arc melting master alloys with enough zirconium to produce an alloy of the desired composition. Following pretreatment, alloys were annealed at temperature levels between 600" and 2020°C. Determination of the phase boundaries was then accomplished by metallographic evaluation of specimens quenched from the various temperatures. Incipient melting techniques were used to corroborate solidus curves, and X-ray diffraction was employed to study the nitrogen-rich region of the a + ZrN phase field. Materials Westinghouse Grade 1 iodide zirconium crystal bar served as the base material for this investigation. The as-received bars were lightly sandblasted, pickled in a 20 pct HN0-5 pct HF aqueous solution, rinsed in water and acetone, and dried. They were rolled to about 1/32 in. strip and acid-pickled, followed by water and then acetone rinses. The material was sheared to approximately 1/4 in. squares, cleaned with acetone, and stored for use. Pure zirconium nitride is not commercially available, according to correspondence with possible suppliers. A literature survey indicated that nitrogen may be introduced into zirconium metal by passing nitrogen or ammonia gas over zirconium at an elevated temperature. After considerable experimentation, a train was devised whereby high quality nitrogen was passed through a series of bubblers to remove the last traces of oxygen, through an H,SO, bubbler and a cold trap to remove moisture, and finally over zirconium within a resistance furnace. Hand-picked Bureau of Mines magnesium-reduced zirconium sponge proved more amenable to nitriding than the crystal bar. The nitrogen used was extra pure gas purchased from Linde Air Products Co. The first two bubblers through which the gas was passed contained a solution suggested by L. F. Fieser" as being ideal for removing the last traces of oxygen from nitrogen. The solution contains 20 g KOH, 2 g sodium-anthraquinone ,9-sulphonate, and 15 g NaHSO, dissolved in 100 ml water. It is blood-red and turns brown when contaminated with oxygen. A saturated lead acetate solution, next in the series of bubblers, removed any H2S which might have formed in the 0, removal stage. An H,SO, bubbler and cold trap removed moisture before the nitrogen was passed over the zirconium. The zirconium was contained in a stainless steel screen within a Vycor or quartz tube in a resistance furnace. Unreacted nitrogen passed out of the system through a mercury bubbler. A nitriding run was performed in the following manner: Zirconium was placed in the screen within the furnace tube. The unit was assembled, suitably clamped off, and evacuated to remove the air and moisture within the tube and that trapped by the zirconium sponge. The unit was flushed with nitrogen and evacuated twice. After nitrogen was allowed to pass over the zirconium for about 30 min, the furnace was turned on; several hours were required to reach temperature. The reaction was allowed to continue at temperature for about 4 hr and the screen was then withdrawn from the hot zone of the furnace by means of a Nichrome or Kanthal rod. The screen and its contents were allowed to cool at the end of the tube and were then removed. At 800°C no more than about 5 pct N could be introduced into the sponge zirconium. This material was designated M-1 (master alloy No. 1) and reserved for the preparation of alloys in the dilute nitrogen region. A second set of experiments was conducted at 1000°C; no more than 7.2 pct N could be introduced into the zirconium at this temperature. Enough material (M-2) of this nitrogen content was prepared to produce a second set of alloys to complement the first and to provide alloys in the 0 to 6 wt pct N range. It was hoped that a diffusion anneal plus a re-nitriding might yield a material of higher nitrogen content. The material containing about 7 pct N was therefore given a homogenization treatment at 1000°C for 6 hr under an argon atmosphere. It was

Jan 1, 1957

By R. F. Domagala, D. J. McPherson

Iodide zirconium was combined with calculated amounts of ZrO2 or master alloys and arc-melted. Annealing treatments were carried out at 21 temperature levels. Metallographic examination of the heat treated specimens permitted construction of the binary phase diagram from zirconium to ZrO2. Oxygen additions to zirconium raise the transformation temperature as well as the melting point. Features of the diagram include the peritectic formation of beta, the formation of alpha directly from the melt, an intermediate phase ZrOB with a&apos; range of homogeneity, and a eutectic between alpha and Zr02. PHASE relationships in the Zr-0 system were determined in the range 0 to 66. 7 atomic pct 0 (ZrO,). Arc-melted alloys were annealed at temperature levels between 600" and 2000°C. Determination of the phase boundaries was accomplished by metallographic evaluation of specimens quenched from the various temperatures. Incipient melting techniques were used to determine solidus curves, and X-ray diffraction work was employed to study the lattice parameters of the a solid solution and the phase ZrO,. Experimental Procedures Westinghouse "Grade 1" iodide zirconium crystal bar (approximately 99.8 pct pure) was employed for the investigation. This material is substantially free of the impurity inclusions characteristic of most zirconium metal. Previous work has shown it to be the most satisfactory grade for phase diagram studies. The zirconium crystal bar, as-received, was coated with corrosion product from autoclave tests by which its grade designation is determined. The bars were sand blasted lightly, pickled for 1 min in a 20 pct HN0,-5 pct HF aqueous solution, rinsed in water and acetone, and dried. The bars were rolled to about 1/32 in. strip, cut into 10 in. lengths, and pickled again. The material was sheared to approximately Y4 in. squares, cleaned with acetone, and stored for use. Two pounds of specially prepared "chemically pure," and 100 grams of spectrographic grade ZrO, were obtained for the preparation of alloys. The "Specpure" ZrO, was obtained from Johnson, Mat-they Co.. Ltd.. and Titanium Alloy Manufacturing Div. of National Lead Co. supplied the other grade of oxide. The "chemically pure" material (henceforth referred to as C.P. ZrO,) was used for the preparation of all alloys employed in the determination of phase relationships. A limited number of alloys were prepared with the "Specpure" oxide to recheck certain phase boundaries. Analyses of the two grades of oxide are given in Table I. The C.P. ZrOI was received in powder form, not suitable for arc melting. Therefore, this material was compressed to wafers 1 in. in diameter and about Vn in. thick. These were segmented and stored for use. The "Specpure" material, in the form of small granules, was suitable for use in the as-received condition. A nonconsumable electrode arc-melting furnace was used to prepare alloys. A water-cooled copper crucible and tungsten-tipped electrode were employed. The material was placed in the crucible and rapidly melted under a protective atmosphere of helium gas by striking the arc on a tungsten stud and directing it upon the charge material. Details of operation, including drawings of this type furnace, have been published.&apos;

Jan 1, 1955

By C. E. Lundin, M. Hansen, D. J. McPherson

PRIOR work on the Zr-Cu phase diagram by Alli-bone and Sykes,&apos; Pogodin, Shumova, and KUGU cheva,&apos; and Raub and EngeL3 as confined largely to copper-rich alloys. The investigations of Raub and Engel were the most recent and seemingly the most complete of these. Alloys from 0 to 68.3 pct Zr were studied principally by thermal analysis and microscopic examination. These authors reported an inter metallic compound ZrCu, (1116°C melting point) and two eutectics, one at 86.3 pct Cu (977°C mp) and the other at 49 pct Cu (877°C mp). The solubility of zirconium in copper was reported to be less than 0.1 pct at 940°C. The zirconium melting stock consisted of Westing-house "Grade 3" iodide crystal bar (nominally 99.8 pct pure). It was treated by sand blasting and pickling (HF-HNO, solution) to remove the surface film of corrosion product, resulting from grade designation tests. The crystal bar was cold rolled to strip, lightly pickled again, and cut into pieces approximately 1/32 in. thick and 1/4 in. square. These were cleaned in acetone, dried, and stored for charging. The high-purity copper (spectrographic grade) was supplied by the American Smelting and Refining Co. with a nominal purity of 99.99 pct. These copper rods were rolled to strip, cut into squares the same size as the zirconium platelets, cleaned in acetone, dried, and stored. Equipment and Procedures The equipment used for melting and annealing the zirconium binary alloys and for the determination of solidus curves has been described in connection with previous work on the Ti-Si system&apos; and in recent papers in this series describing the studies on eight binary zirconium systems.5-&apos; Techniques employed for preparing and processing the alloys were also similar to those used in the above references. Ingots of 20 g were melted under a protective atmosphere of helium on water-cooled copper blocks in a nonconsumable electrode (tungsten) arc furnace. The ingots were homogenized and cold-worked prior to isothermal annealing to aid in the attainment of equilibrium. The specimens were heat-treated in Vycor bulbs sealed in vacuo or under argon, depending on the temperature of the anneal. Quenching was accomplished by breaking the Vycor bulbs under cold water. Temperature control was within ±3OC of reported temperatures. Thermal analysis was primarily relied on to determine eutectic levels, peritectic levels, and compound melting points. The induction furnace incipient melting technique was also used but did not provide the accuracy obtained by thermal analysis in this system, which involves much lower solidus temperatures than the other zirconium systems. A special technique for the determination of characteristic temperatures was employed in the case of several intermediate phases and their eutectics which displayed very small differences in melting temperatures. Specimens were sealed in Vycor bulbs and annealed at a series of very accurately controlled temperatures. Metallographic examination was then employed to reveal incipient melting. Furnaces and techniques in general were described previously.&apos; The echant used was 20 pct HF plus 20 pct HNO3 in glycerine unless otherwise stated. Results and Discussion The chemical analyses of the majority of alloys prepared for the determination of phase relationships in this system are given in Table I and a brief summary of the equilibrium anneals employed is given in Table 11. In a preliminary program, alloys containing 1, 4, and 7 pct Cu were annealed for three different times at each of the temperatures 700°, 800°, and 900°C. No change in the relative amounts of phases present was detected after 350, 150, and 75 hr at the above temperatures, respectively. The times listed in Table II were accordingly chosen as a result of these preliminary tests. Zirconium-rich alloys containing from 0.1 to 10 pct CU were reduced by cold pressing from 58 to 8 pct, depending upon thk alloy content, homogenized for 7 hr at 900°C, and then reduced 80 to 13 pct by cold rolling, again depending upon copper content. Other alloys were studied in the cast, or cast and annealed conditions. The contracted scope of investigation for this system included the range 0 to 50 atomic pct Cu. This approximate region is shown in Fig. 1. Due to evidence of phase relationships departing considerably from those proposed by Raub and Engel" in the 50 to 100 atomic pct range, the investigation was extended to cover this composition area rather thoroughly also. Fig. 2 is a drawing of the entire diagram. The labeling of some phase fields was omitted in Fig. 2 for the sake of clarity. An expanded view of the zirconium-rich region, with the experimental points necessary for its construction, is given in Fig. 3. The generally accepted value of Vogel and Tonn8 or the allotropic transformation a + 862&apos; ±5OC, was employed in the construction of these diagrams. A careful study revealed that the "Grade 3" crystal bar used in this investigation actually transforms over the approximate range 850" to 870°C, due to impurities. It must be expected that this two-phase field in unalloyed zirconium will cause some departures from binary ideality in the very dilute alloys. Zirconium-rich Alloys: The a + ß transformation temperature is decreased from 862" to about 822°C by increasing amounts of copper. Thus, a eutectoid reaction, fi ß a+ Zr,Cu, occurs at a composition of about 1.6 pct Cu. The eutectoid level was determined to lie between the alloy series annealed at 815" and 830°C. The placement of this eutectoid temperature

Jan 1, 1954

By R. F. Domagala, M. Hansen, D. J. McPherson

On the basis of metallographic analysis, incipient melting data, thermal analysis work, and X-ray diffraction, phase relationships in the 0 to 50 atomic pct alloy content were carefully resolved. Phase relationships in the higher alloy content regions were outlined. A single intermediate phase, peritectically formed, of the form ZrX2 was established in each system. A eutectic and a eutectoid were found in the zirconium-rich region of both systems. Appreciable solubility of molybdenum and wolfram was found in ß zirconium, but only a slight solubility in a zirconium. PREVIOUS work on these systems was limited to X-ray investigations of the intermediate phases1, 2 and preliminary surveys of the zirconium-rich alloys." The diagrams presented were determined principally by metallographic, thermal analysis, and incipient melting techniques. In accordance with the Atomic Energy Commission contract requirements, phase relationships up to 50 atomic pct molybdenum or wolfram were carefully resolved, while only a limited amount of work was done to outline the 50 to 100 atomic pct alloy region. A description and analysis of the metals used in the preparation of alloys for this study are included in Table I. A "low-hafnium" zirconium crystal bar, produced by the decomposition of a volatile iodide onto a hot filament, was employed for these studies. Westinghouse "Grade 3" crystal bar was used for all alloys. The zirconium, as received, was coated with corrosion product from a standard autoclave test by which its grade designation is determined. This was removed by a sand-blasting and HF-HNO, pickling technique developed by the Atomic Energy Commission. The bars were cold rolled to approximately 1/32 in. sheet, pickled for iron removal, sheared to 1/4 in. squares, washed with acetone, and stored for furnace charge. Molybdenum sheet. 0.003 in. thick, 0.001 to 0.005 in. wolfram wire, and M in. wolfram rod crushed to granular form, from Fansteel Metallurgical Corp., were used as alloying stock. Melting Procedure A nonconsumable electrode arc furnace identical to that described in detail by Hansen et al.4 was used. The source of power for melting Zr-Mo alloys was a 400 amp dc welding generator, while a 900 amp dc generator was used for preparing Zr-W alloys. Electrode tips of the same material as the alloy addition were employed in both systems, i.e., molybdenum tips were used for Zr-Mo alloys, and wolfram tips for Zr-W alloys. This precluded any possible electrode contamination during arc melting. Ingots of 20 to 30 g of Zr-Mo alloys were melted under high purity helium in the cavity of a copper block insert in a spun copper crucible. Homogeneity was insured by remelting all ingots four to six times without opening the furnace. Due to the large difference between the melting points of wolfram and zirconium, direct melting of the charged metals as above generally yielded ingots containing unmelted wolfram particles. This was overcome, after many variations in technique, by melting a pure wolfram charge at high power levels (700 to 900 amp) and slowly adding zirconium to form a master alloy. Such master alloys were sectioned and remelted several times, then crushed to serve as melting stock for alloys of lower wolfram content. Master alloys containing 26, 50, 52, 70, and

Jan 1, 1954

By R. W. Kraft

A back- reflection precession-type X-yay camera for determining the crystallographic orientation of the crystallites of both phases in small areas of thick specimens of polyphase alloys is described ad the geometry, advantages, and limitations of the apparatus are discussed. Metallographic obseg-vations of interfacial angles (or habit planes or growth direction are made on the same specimen so that the crystallographic and metallographzc orientation data call be directly correlated. An example of the application of tile technique to a unidi-~~ectionally solidified CuA12-A1 eutectic specimen is presented. The interfacial planes ad growth directions of each phase were established, and the orientation relationship between the phases was observed and found to be approximately intermediate between two previously reported relationships. The crystallographic interfacial relationship between two solid phases is an important parameter in a variety of metallurgical phenomena because of the energy associated with the interface and because this energy is at least partly associated with the way in which the two space lattices are in contact along the interface. In order to describe the interfacial planes in the crystallites of both phases it is necessary to determine the crystallographic orientation of each phase in a specimen relative to each other, and to directly correlate these data with met-allographic measurements from which the interfacial planes can be determined on the same specimen. The back-reflection Laue technique is the easiest way to determine the orientation of thick single crystals or large grains and the method can be combined with metallographic techniques to provide the necessary data, provided the reflections from each phase can be distinguished from one another. However, if the crystallites are small or of varying orientation or if one or both phases has a unit cell with less than the maximum symmetry, many overlapping and complex Laue patterns are recorded simultaneously and it becomes impractical if not impossible to interpret the photographs. All of these complexities were present in a unidirectionally so- lidified A1-CuA12 eutectic alloy1 for which a crystallographic analysis was desired. Consequently the method described here was developed since no known X-ray or electron diffraction technique had all of the following attributes which were required. 1) Method should yield data from which the crys-tallographic orientation of every crystallite or diffracting unit in the irradiated area can be determined. 2) Method should be adaptable to the study of small areas. Depending upon the degree of preferred orientation in the specimens, it should be possible to obtain reliable data in a reasonable length of time on irradiated areas as small as 1.0 or even 0.1 mm in diam. 3) Method should permit direct correlation of crystallographic data with microscopic orientation data pertaining to crystallite axes, habit, morphology, and growth directions as determined by optical microscopy. 4) method should be such that selected areas of large specimens can be easily studied. Trepanning of a small specimen (such as an electron microscope specimen) from larger specimens was undesirable since it would greatly increase the problem of correlating the crystallographic and microscopic directional data. Requirements 3 and 4 dictated that an X-ray back-reflection pinhole technique should be used on large samples, such as metallographic specimens which had previously been examined and analyzed for their microscopic characteristics. Similarly, requirement 2 could be satisfied by choosing a collimator of appropriately small diameter. Exposure times would not be excessive provided the detector were close enough to the specimen. Because of space limitations film was chosen in preference to a Geiger counter. Requirement 1 was fulfilled by using monochromatic radiation and providing enough additional degrees of freedom in specimen rotation to compensate for Bragg law restrictions on diffracted beams. DESCRIPTION OF APPARATUS The apparatus shown in Fig. 1 consists of a pin-hole collimator, (a), projecting through a rotatable circular film in a holder, (b), which records X-ray reflections in the back-reflection region. The specimen, (c), is mounted on the end of a shaft, (d), which is provided with an adjustment, (e), so that the specimen surface can be placed accurately on

Jan 1, 1962

By J. W. Rutter, K. T. Aust

The temperature dependence of the rate of grain boundary migration was measured in bicrystals of zone-refined lead containing from 20 to less than 1 ppm by wezght of tin. The apparent activation energy in the temperature range from 320" to 200oC is markedly dependent upon the solute tin concentration and upon the orientation relationship of the grains adjacent to the grain boundavy. The quantitative experimental observat~ons are compared with the predictions of various theories of grain boundary migration. In previous work.&apos;?&apos; the mobility of individual grain boundaries was studied as a function of impurity concentration and type of boundary. Grain boundary migration occurred at the expense of dislocation arrays which were introduced into the specimen during solidification. Boundary mobility in zone-refined lead at 300°C was markedly decreased by small additions of tin. 0.004 wt pct being sufficient to decrease the rate of grain boundary migration by a factor of 1000. The mobility of grain boundaries having polar orientation relationships near 38 and 22 deg about <Ill>, and 28 deg about <100>, was much less sensitive to tin concentration in the range studied. As a result, these boundaries have relatively high mobilities. The present paper is a continuation of the above study. Data are now presented on the temperature dependence of the motion of individual grain boundaries in zone-refined lead as a function of solute tin concentration and orientation relationship of adjacent grains at the grain boundary. The experimental observations are compared with the predictions of a number of theories of grain boundary migration3-8 which, prior to the present experimental investigation, could not be critically evaluated. EXPERIMENTAL PROCEDURE The striation or lineage structure of melt-grown single crystals of zone-refined lead, containing various additions of tin, was utilized to provide a driving force for grain boundary migration, as previously described.1,2 Each grain boundary under study separated the striated single crystal from another grain which was introduced by localized plastic deformation and recrystallization of a small region of the sample. The speed of migration of grain boundaries in dilute alloys of tin in zone-refined lead was investigated as a function of 1) tin concentration from < 0.0001 to 0.002 wt pct, 2) temperature in the range of 200" to 320°C, and 3) orientation relationship of the adjacent grains at the grain boundary. The substructure driving energy available for grain boundary migration was estimated to be about 4000 ergs per cu cm, within a factor of two, from specimen to specimen.&apos; The specimen dimensions, and growth and alloying procedures for the preparation of striated single crystals of lead of known tin composition, were as described previously.&apos; Each bicrystal was carefully wrapped in aluminum foil, and annealed in a well-stirred salt bath consisting of 50 pct NaNO2 and 50 pct KNO3, for known periods of time at a series of constant temperatures (*2°C). The grain boundary positions, before and after each anneal, were determined by etching lightly in a solution of 5 pct nitric acid in methyl alcohol, in order to follow the motion of the boundary and determine its rate of migration. Thus, the rate of motion of the grain boundary in a single specimen was measured at various temperatures. The above procedure was carried out for each grain boundary in seventeen different bicrystal specimens.

Jan 1, 1960

By J. H. Westbrook

UNTIL very recently the development of high temperature alloys has been strictly empirical. It is, in fact, a great tribute to the intuition, perseverance, and industry of the practicing metallurgists of this country and abroad that the amazing increases in gas turbine service temperature over the past 15 years have been achieved with so little fundamental knowledge. The result of this development has been the realization of successful but highly complex alloys possessing five, six, or more alloying elements and correspondingly complex microstructures. Within the last few years, considerable effort has been devoted to the identification of the secondary phases in these alloys and to the correlation of the presence or absence of such phases with alloy properties. Little attention, however, has been given the problem of identification of the mechanism (s) by which such phases enhance the properties of the alloy and especially to the assessment of the particular properties of the secondary phase (either in- trinsic or relative to the matrix phase) which are basically responsible for the improvement. Conceivable mechanisms which might apply include dispersion hardening and precipitation hardening. In both cases geometrical factors—particle size, dispersion, volume fraction, etc.—and agglomeration re-

Jan 1, 1958

By R. A. Bosch, F. V. Lenel, G. S. Ansell

RECENTLY, Ansell and aenel&apos; proposed a dislocation model to account for the yielding behavior of dispersion-strengthened alloys. The criterion for yielding used in this model was that yielding occurs when the shear stress due to arrays of piled-up dislocations fractures or plastically deforms the dispersed second-phase particles. Calculations based on this model predict that the yield strength, uysof a dispersion-strengthened alloy containing particles whose geometry permits them to be considered as straight, i.e. not curved, barriers to dislocations follows the relation where and are the shear moduli of the matrix and dispersed phase respectively, b is the Burger vector of a dislocation in the matrix, A is the mean free path between dispersed phase particles and C is a constant. This yield stress, ys, is closely approximated in polycrystalline alloys by the proportional limit. The offset yield stress, uoy, is the yield stress, uys, plus the increase of stress due to strain hardening in the offset strain increment. Previous investigation1 has shown that Eq. [I] describes the yielding behavior of several different dispersion-strengthened alloys as a function of the mean free path between dispersed phase particles at a constant temperature. The purpose of this investigation was to investigate the temperature dependence of the yielding behavior of dispersion-strengthened alloys. The alloys studied, MD2100 and MD5100, are SAP-type alloys containing flake shaped aluminum oxide particles dispersed in a matrix of commercial purity aluminum. The proportional limit and 0.2 pct offset stress of both of these alloys were determined as a function of temperature over the temperature range from -190" to 500 C. All tests were conducted on an Instron tensile testing machine. Stress was measured by means of the Instron load cell. Strain was measured by means of SR-4 strain gages attached to the tensile specimens. Stress sensitivity was 80 psi. Strain sensitivity was 2 x 10F Fig. 1 shows the values received for the proportional limit and 0.2 pct offset yield stress plotted as a function of homologous temperature for both the MD2100 and MD5100 alloys. Inspection of Eq. [I] shows that of the terms which determine the theoretically predicted yield stress, uy,, only the shear moduli have an appreciable temperature dependence. From Eq. [I] the yield stress at any temperature T, UT, may be predicted from the yield stress at any arbitrary reference temperature, in this case 25 OC, u25, by the relation where the subscripts T and 25 refer to the values of the property at test temperature and at 25"C, respectively. The temperature dependence of the yield stress predicted by Eq. 121, based on the observed value for the proportional limit at 25OC, is also shown in Fig. 1. In evaluating Eq. [2] the following data was used. The values for the shear modulus of

Jan 1, 1962