By John J. Gilman

BECAUSE of their layerlike structure, zinc crystals exhibit strong anisotropies for almost all physical and chemical properties. This should, and indeed does, greatly influence the plasticity of zinc for various crystal orientations. At low temperatures, the investigator of this plastic anisotropy is plagued by the great variety of deformation modes that operate. However, at high temperatures (250° to 419°C) only two deformation modes predominate: basal (0001) and prismatic (1010) glide. Furthermore, since strain hardening is virtually absent at high temperatures, the plasticity for these two modes of deformation can be very simply described by means of two equations of state. It is the purpose of this paper to describe the experimental behavior of basal and prismatic glide in zinc crystals, and to interpret this behavior in terms of other physical properties (in particular, the thermal expansion coefficients and the elastic constants) using the theory of dislocations. Fig. 1 defines the two planes of the zinc structure that will be discussed. Glide occurs very readily on the basal planes at all temperatures, and there is a very large literature on this subject. Much of the literature has been reviewed by Schmid and Boas;' it will not be reviewed here. Kolesnikovl was the first to show that if basal glide is circumvented by stressing a zinc crystal parallel to the basal planes (giving zero shear-stress on the basal planes) then, at temperatures above about 320°C, glide on the first-order prism planes occurs. His results have recently been confirmed by Cahn, Bear, and Bell." These previous workers have established the existence and crystallographic elements of prismatic glide; the present paper is concerned with the stress, strain rate, and temperature relations of prismatic glide as contrasted with basal glide. Experimental Methods The crystals were square ones, 6x6 mm, that had been grown in precision Pyrex tubes by a method that is described in detail elsewhere.' Most of the crystals were 99.999+ pct Zn (New Jersey Zinc Co. CP grade). Some were alloyed with 0.1 -+-0.005 atomic pct Cd, and chemical analysis showed that almost all of the added cadmium persisted through the crystal-growing process. For measurements of nonbasal glide, crystals were oriented with their basal planes parallel to both the rod axis and one of the flat faces of the square cross section. However, the orientation of the close-packed directions [1210] with respect to the rod-axis was variable. For basal glide measurements, the angle between the basal plane and the specimen axis was 35". The orientations were measured by the Gren-inger back-reflection X-ray method. The problem of finding a suitable method of gripping the crystals was the most serious experimental obstacle that arose. Because of the large plastic anisotropy of zinc, the usual gripping methods were unsatisfactory. Some methods that were tried were: high melting-point solder, making heads on the ends by locally melting a crystal, and electroplating nickel on the ends to form enlarged portions. For all these methods, the regions of the grips were weaker than the crystals themselves. Finally, two methods were decided upon: bend tests and direct machining of tensile specimens. In the bend tests, specimens were loaded as simple beams so that gripping was not a problem. The beams were 1 in. long and the axis of bending was parallel to the hexagonal axis of the crystals. For the crystals that were machined into tensile specimens, brass bars with slots in them were used to support the crystals, and thereby minimize the distortions due to machining. The crystals were glued into the brass bars with plastic cement which was later dissolved away with acetone. See Fig. 2, left. No clamps were used near the crystals and the machining was done using a milling machine with a fly-cutter. The tool bit was very sharply pointed to minimize burnishing. The feed was less than 1 mil per cut. The depth of cut was 2 mil for roughing cuts, and % mil for the finishing cuts. This machining method produced surface layers of tiny recrys-tallized grains only 2 to 3 mil deep, and the bodies of the crystals were not measurably disturbed. After the crystals had been machined and removed from the brass holders, they were chemically polished until about 5 mil had been removed from all their surfaces. The polishing reagent consisted of equal parts of concentrated HNO,, 30 pct H3O and ethyl alcohol; it is described in detail elsewhere." A typical crystal is shown in Fig. 2, right. The I-shaped faces are normal to the hexagonal axis of the crystal; otherwise the projections at the ends would simply shear off when the crystal was loaded. The cross section in the 2?-in. gage length is 0.215x0.115 in. It was found that the polished

Jan 1, 1957

By Henry R. Piehler

Continuous seven- and nine teen -filament close-packed silver-steel filamentary composites mere tested in tension. For purposes of comparison, the tensile behavior of the composite was predicted from the measured properties of the individual com-ponents. It was assumed that the axial strain is the same in both components and that the contribution of each component to the composite flow stress is proportional to its volume fraction. Good agreetnent was obtained between the observed and predicted tensile behavior. However, the composite elongation at fracture was about twice that observed when the individual steel wires were tested alone. Composites in which the filaments were widely spaced failed by the consecutive fracture of the filaments. In composites with closely spaced filaments, a composite instability preceded frachcre. These effects are explained in terms of a lateral restraint to the necking of the filaments which develops in the deforming composite. TWO-COMPONENT or composite materials are increasingly being developed and used as structural materials. Of all the composite geometries used, the filamentary configuration has proved to be the most successful. Polymer-bonded fiber-glas, the most common of the filamentary composites, has been investigated most extensively to date. One explanation of the behavior of fiberglas1 suggests that the load transfer between the glass fibers and the polymer matrix occurs primarily through friction. Bond separation between the fibers and the matrix is presumed to occur at very low stresses. Subsequently, only frictional bonding can provide for the transfer of load from the matrix to the fibers. The force normal to the fiber-matrix interface which gives rise to this friction is assumed to arise from the matrix shrinkage which occurs during solidification. The behavior of metallic filamentary-composite materials would be expected to differ from that of fiberglas in several significant aspects. Residual stresses resulting from differences in thermal contraction can be kept to a minimum by proper heat treatment. A strong wetted bond is formed between the two phases. In brazed joints,2 for example, the interphase bond is sufficiently strong that the weaker material will fail before separation occurs at the interface. Most metal filaments can undergo appreciable amounts of plastic deformation before failure. Failure by plastic instability or necking frequently occurs in metallic filaments, but not in glass fibers tested at room temperature. Differences between the behavior of fiberglas-polymer and metallic filamentary composites have indeed been observed in composites containing various types of metallic filaments in a silver matrix.3,4 At strains of the order of 10-2 pct, all the deformation was accommodated by the silver matrix. Hence, the strength of the composite depended only on the fiber concentration and not on the nature of the fiber. At higher strains, the strength of the composite increased when filaments with higher work-hardening rates were used. Surface slip line observations on a silver-mild steel composite that had been stretched 4 pct showed that an appreciable amount of deformation occurred in the filaments. Work on tungsten-copper filamentary composites5 has shown that the ultimate tensile strength for varying filament fractions followed a linear mixture rule. Assuming that the axial strains in both filaments and the matrix are equal, this linear mixture rule can be expressed as: The subscripts c, f, and m refer to the composite, filaments, and matrix, respectively. A and V are the area and volume fractions of each component. sc and of are the ultimate tensile strengths of the composite and the filaments. sm is the flow stress of matrix at a strain equal to the elongation at failure of the filaments. However, the tungsten filaments can undergo only a limited elongation before they fracture without an appreciable reduction in area. A composite containing more ductile filaments might indeed deviate from this linear mixture rule for the ultimate tensile strength, since filament failure by necking might be arrested by the matrix. SPECIMEN PREPARATION Specimens were prepared from 0.8 pct carbon steel piano wires of 0.015 in. initial diameter. The wires were given a thin nickel flash and a silver plate varying in thickness from 0.015 to 0.007 in., depending on the filament fraction desired. In order

Jan 1, 1965

By R. H. Richman

Coarse-grained Fe-Ni-C martensites formed at subzero temperatures were strained in compression at room temperature and the plastic deformation modes examined as a funclion of carbon content. At very low carbon levels, defovmation occurs hy wavy slip; commencing at about 0.05 pct C, mechanical twinning accounts for an increasing proportion of the plastic flow. Beyond approximately 0.4 pct C the deformation appears to be entirely by mechanical twinning. The habit planes of the operative twin modes were determined to be (113), (0131, and "(089)" in decreasing frequency of occurrence. Some of the implicaticms of Ihe o6served deformation modes upon the structure and properties of ferrous martensites are discussed. METALLURGISTS have long sought to explain the mechanical properties of ferrous martensites, particularly the extraordinary hardness and strength of the high-carbon varieties. Until recently the lack of precise knowledge of the structure of martensite crystals was the most serious barrier to understanding; however, the advent of thin-foil techniques for transmission electron microscopy has removed much of the mystery from martensite structure. Observations by Kelly and Nutting,"' and many others since, indicate that Fe-C based martensite crystals are internally twinned to a degree dependent upon the carbon content, and that a martensite plate containing 0.8 wt pct C or more consists of a stack of twin-related lamellae with each lamella on the order of l00A thick. Such a structure would be expected to influence greatly all aspects of metallurgical behavior, and many of the properties of Fe-C based martensites have been rationalized accordingly. Recent independent experiments led Winchell and cohen3 to conclude that the strength of ferrous martensite is derived primarily from solid solution hardening of the iron lattice by interstitial carbon atoms. Strength contributions from precipitation, dislocation-atmosphere interactions, clustering, short-range order, crystallite size, and so forth, were considered to be of secondary importance. In the view of Winchell and Cohen, the twinned structure of martensite serves mainly to limit the effective length of dislocation lines in the lattice, and thereby confers an added measure of hardening. Few properties of metallic crystals are as sensitive to metallurgical structure as are deformation mechanisms. It is somewhat surprising therefore, that, except for metallographic evidence of mechanical twins in strained martensite,4 no systematic examination of plastic deformation

Jan 1, 1963

By C. Elbaum

Specimens consisting of several crystals, each with a prescribed geometry and a controlled orientation with respect to both the extermally intposed stress and the highboring crystals, werer deformed in tension at room temperature. It is shown that the influence of a grain boundary on the plastic defolrmation of a mullicrystal depends on the extent to which the presence of the grain boundary, contributes to the necessity 01. multiple slip in the component crystals. MANY investigations were carried out in the past on the plastic deformation of aluminum single crystals, bicrystals, and polycrystals. The various studies of bicrystals aimed primarily at elucidating the influence of grain boundaries on the mechanisms of plastic deformation. In the earlier studies the emphasis was placed primarily on finding the "strength" contributed by a grain boundary. In more recent investigations it became apparent that the grain boundary does not contribute any strength per se but rather acts by influencing the mechanism of plastic deformation in the adjoining grains. The concept thus emerged of the plastic properties of a bi-crystal, and by extension of a polycrystal. depending solely on the mechanism of deformation prevailing in each grain. The contribution of the grain boundaries thus becomes limited to the type of restrictions imposed on each grain by its neighbors. The present investigation of the behavior of specimens consisting of more than two crystals was designed for the purpose of studying the influence of the grain boundary in simple aggregates. The findings of this study further support the concept that the restriction imposed on a deforming crystal by its neighbor constitutes the predominant factor in the plastic deformation of polycrystals. The term "multicrystal", in contrast with single and polycrystals, is used to describe specimens consisting of several crystals. Each one of the component crystals has a prescribed geometry and a controlled orientation with respect to both the externally imposed stress and the neighboring crystals. Two groups of multicrystals were prepared. All the component crystals of both groups of multicrystals had the axial orientation (isoaxial multicrystals) shown in Fig. 2, with the primary slip plane and slip direction both at 45 deg to the specimen axis. In the first group (hereafter referred to as group I) the component crystals were symmetrically oriented with respect to the plane of the grain boundary; the primary slip plane and slip direction were respectively at an angle of 60 and 30 deg to this plane. For the second group (group 11) the axial orientation remained the same and the relative positions of the primary slip plane and slip direction are shown in Fig. 3. EXPERIMENTAL METHODS The material used was aluminum 99.993 pct pure, according to the manufacturer. The specimens were produced by growth from the melt in a horizontal graphite container. In order to maintain the prescribed geometry of the individual crystals of a multicrystal, a technique described elsewhere was used.' The specimens were grown under a small, positive pressure of helium at a rate of approximately 1 mm per min. annealed in air for 24 hr at 640°C and cooled over a period of several hours to room temperature. All the multi-crystals were rectangular in cross-section, 6 by 18 mm (see Fig. 1) and from 150 to 170 mm long. In each group bicrystals, tricrystals and quadru-crystals were prepared as shown in Figs. 1 and 4.

Jan 1, 1961

By E. S. Greiner

Germanium and silicon have been plastically deformed in torsion at elevated temperatures. Slip took place on the four {Ill} planes. Dislocations, revealed by etch pits on a (111) face, occurred in rows that were traces of operative slip planes. THE plastic deformation of germanium and silicon by bending and tension at elevated temperatures has been reported by Gallagher.&apos; Transla-tional slip during plastic flow in these materials, according to Gallagher&apos; and Treuting,&apos; occurs on (111) planes. Recent work by Treuting&apos; indicates the direction of slip to be <1l0>. The present paper describes the plastic flow characteristics of germanium and silicon deformed by torsion. Torsional deformation was accomplished by twisting 1/4x1/4x2 in. specimens held in molybdenum grips and contained in an atmosphere of helium in a transparent quartz tube and heated by an external resistance furnace. The angular displacements were measured on a graduated circle with a pointer attached to the movable grip. Temperatures were measured with a chromel-alumel couple; the hot junction was within the quartz tube and in close proximity to the specimen. Photographs of samples of germanium and silicon twisted at 850" and 1180°C, respectively, are shown in Fig. 1. The germanium was twisted 230" per in. and the silicon 80" per in. These deformations are larger than those used in experiments to be described later and are presented only to emphasize the extensive plasticity of these materials. Germanium A single crystal specimen of germanium (n-type, 7 ohm-cm resistivity) with a (111) plane normal within 3" of the torsion axis, Fig. 2, was chemically polished with CP-4 solution" and then twisted 9" during the twisting of these specimens of germanium, the slip lines from the (lli) plane should have appeared in the four lateral faces instead of in only two. Perhaps the absence of rotational slip is brought about by the square cross-section. A cylindrical specimen would have a more uniform stress distribution in torsion than one with a square cross-section, and may deform by rotational slip. A specimen of germanium (n-type, 5 ohm-cm resistivity) twisted less than 8" per in. at 550°C, was cut to expose the (111) face 19" 28&apos; from the torsion axis, Fig. 4a. This face, after metallographic

Jan 1, 1956

By D. F. Gibbons

THIS investigation was undertaken in order to gain further information on the mechanism of plastic deformation of iron at temperatures between room temperature and 77.2°K, and also to contribute to our understanding of the low temperature brittleness phenomenon that occurs in both the tensile and impact tests. It was decided to study as pure an iron as possible and to use the tensile test in order to simplify the problem as much as possible. Two series of iron were used throughout the investigation: iron A, obtained from the National Research Corp. and supplied as gas-free, high purity iron; and iron B, obtained from Fast&apos; and produced by melting iron under purified hydrogen. Typical analyses of samples of both irons, after fabrication, are given in Table I. The main difference in composition of these irons is in their nickel and oxygen contents. Nickel has a very large solid solubility in iron. However, oxygen has an extremely small solid solubility. An attempt was made to reduce the oxygen content still further by remelting under purified hydrogen. This was successful in reducing the oxygen content to -0.0006 pct. However, no results on tests of this iron are included, since difficulty was encountered in fabricating the ingot. Wire specimens 1 mm in diameter were used for the investigation. The wires were produced from the ingots, as supplied, by cold rolling and swaging, with intermediate vacuum anneals at 700°C. Care was taken to reduce preferred orientation in the wires to a minimum by keeping the percentage of reduction in area between anneals of 30 to 40 pct. X-ray transmission photographs showed no indication of preferred orientation. The final grain size of iron A was 20 to 24 grains per linear mm and of iron B, 16 to 18 grains per linear mm. All specimens were tested in the decarburized and denitrided condition unless otherwise stated. The procedure was to pass hydrogen, saturated with water vapor at 26oC, over the specimens at 730°C for 2 hr. The specimens were quenched in iced water and then annealed in a vacuum of - 5x10-6 mm Hg for one day at 560°C to remove hydrogen. Higher temperatures were used for the vacuum anneal but this temperature was found to be quite satisfactory in removing hydrogen. The specimens were slow-cooled after the vacuum anneal. Where it is stated that the specimens were carburized, the specimens were given an identical decarburizing treatment and then carburized by passing hydrogen, saturated with pure n-heptane vapor at 0°C, over the specimens at 730°C. The specimens were then homogenized at 730°C for 2 hr in dry hydrogen. After the carburizing treatment the specimens were given the same vacuum anneal as for the decarburized specimens. The carbon content was determined from the maximum value of the internal friction carbon peak.2 Apparatus Fig. 1 shows a diagram of the tensile apparatus, with half the cooling coil removed. The cooling coil enabled temperatures from 200" to 77.2oK to be obtained. The apparatus was designed to fit a standard Tinius Olsen Universal tensile machine. The apparatus consisted of the rigid plate A which carried two carefully machined hooks H. These hooks attached the plate firmly to the moving crosshead of the tensile machine. The lower grip B was rigidly suspended from the plate A by three stainless steel rods. The upper grip C was joined to the upper grip of the tensile machine by the stainless steel rod E. The lower part of the apparatus was surrounded by a Dewar vessel, which was made a sliding fit inside the brass collar D. The specimen was held in a clamp which fitted into the grip, forming a ball and socket joint (see inset a). This was to attain as nearly pure

Jan 1, 1954

By E. C. Burke, W. R. Hibbard

Plastic deformation in magnesium single crystals was studied by tensile tests at room temperature utilizing an improved preparation and testing technique. Consistent critical resolved shear stress values for basal slip were obtained. The advent of pyramidal slip at room temperature was rationalized upon the basis of grip constraints. A bend-twinning hypothesis was advanced as an explanation of mechanical twinning which occurs as a complex stress-relief mechanism. INVESTIGATIONS of the plastic deformation of magnesium have been limited to the determination of the fundamental kinetics which may be summarized as follows: 1—Twinning on the {102).l 2— Slip on the (001) plane in the [loo] direction at room temperature.&apos; 3—Slip on the {101) or {102) plane in the [loo] direction above 225°C." 4—Critical resolved shear stresses for basal slip in tension at room temperature of 83 g per sq mm with a variation from 57 to 127 g per sq mm." Bakarian&apos; studied the compression of thin wafers of magnesium single crystals and classified the components of the deformation mechanisms as follows: 1—The Basal field: (001) at an angle of less than 20" to the compression surface. Fracture along {101} or slip on (001) followed by {101} fracture. 2—The prism field: (001) at an angle greater than 60" to the compression surface. Twinning on the {102) generally occurring during the early stages of loading, basal slip in the areas of original orientation and (001) slip within twins. 3—The central field: (001) at angles greater than 20" but less than 60" to the compression surface. Slip on the (001). 4—The critical resolved shearing stress for {101} slip above 225°C was 400 g per sq mm. Observations of mechanical twins in hexagonal close-packed metals have been summarized by numerous investigatorsb-&apos; emphasizing a lateral or rotational atomic adjustment, in addition to the pure twinning shear, and the importance of reorienting the basal plane to a position more favorable for continued slip, rather than the resulting small dimensional changes. Criterion for the operative twinning planes has not been clearly established. Schmid and Boas hurmised that an energy condition related to the atom movements is the determining factor. MillerQ bserved that twinning stresses in zinc crystals decreased as the amount of prior deformation increased. Preparation of Specimens Magnesium single crystals % in. in diam x 8 in. long were grown from the melt under an argon atmosphere in a gradient furnace similar to that described by Jillson." Magnesium containing 0.018

Jan 1, 1953

By R. C. de Lange

An improved replica technique is developed for a nondestructive study of the nucleation and growth of fatigue cracks. Three different growth stages of a fatigue crack were observed. An initial stage of high growth rate is followed by a long period of very slow growth, until finally a third period of high growth rate leads to fracture. THE metal-fatigue process is of a very complex nature. The experimental approach towards fatigue is susceptible to many minor influences which, together with the unavoidable scatter in testing results, makes the interpretation a matter of extreme care. The generally accepted fact that, in a homogeneous material, the fatigue cracks start at a free surface indicates that surface studies may contri-but in an essential way to a better understanding of the fatigue mechanisms. Indeed metallographic observations of the fatigue phenomena have been very fruitful in the last decade. The study of extrusions, intrusions, and persistent slip bands has contributed much to the present knowledge of the early processes in fatigue.&apos; The drawback of the current metallographic techniques lies in the fact, however, that either observations of fatigue phenomena had to be made in a destructive way after an only partly executed test or a sequence of observations on the same test bar was only possible on notched specimens.2 4 In both cases an uncertainty exists as to the nucleation and growth of the fatigue crack in an unnotched test bar, where the crack can start at any place of a large area and develops in a test bar, which is macroscopically

Jan 1, 1964

By R. A. Wood, R. I. Jaffee, H. R. Ogden, D. N. Williams

Strain-induced porosity has been found to occur in titanium and other materials at tensile strains greater than the uniform elongation of the material. Porosity in titanium increases with increasing strain and temperature, being most severe at 300° to 800°F. Strain-induced porosity is believed to be a normal part of the mechanism of deformation in ductile materials. DURING the past few years there have been numerous references to the occurrence of voids in laboratory test specimens of metals subjected to strain.l-7 These voids have been referred to as intercrystalline cracking, strain-induced porosity, intergranular cav-itation, voids, and porosity. They appear to occur at grain boundaries or interfaces, and are generally associated with large amounts of strain and have been found mostly in creep specimens and to a lesser extent in tensile specimens. Because the phenomenon does not occur unless the material has been strained,

Jan 1, 1960

By A Guinier

RECIPITATION in alloys is undoubtedly one of the most essential phase transformations in metallurgy and, besides, it is a phenomenon of great interest to physicists. It seems then that it can be chosen as a topic for an Annual IMD Lecture. Of course, the subject is a very wide one and I shall discuss here only a very restricted part of it. I should like to show why it is now considered that there is, at the beginning of the process, a stage distinct from the real precipitation, which is the pre-precipitation. We shall be chiefly interested in the atomic structure of the metal in this preprecipi-tation stage. Numerous reviews on this subject have been published recently.&apos;, &apos; The latest was given by H. K. Hardyh t the last meeting of the Institute of Metals in London. One of the most complete articles has been written by the late Dr. Geisler." I should like, at the beginning of this lecture, to pay a tribute to the memory of our friend Arthur Geisler. Some of the ideas which will be developed here are different from those advocated by him. But everybody knows the considerable progress in experiment and in theory which we owe to him and, personally, I deeply feel how fruitful have been the long discussions which we have had during many years. Experimental Basis of the Precipitation Problems Let us recall the essential facts pertaining to the problem of the precipitation. The starting point and the final one are well known. The initial stage is the supersaturated solid solution before quenching. The dissolved atoms replace some of the atoms of the solvent at the points of a definite lattice. It is generally considered that the distribution of the atoms is completely random, and that the lattice distortions are relatively weak. These assumptions are only an approximation. It has now beenproven", that, in some cases, the dissolved atoms have a tendency to segregate to form very small nuclei. These fluctuations of composition are greater than the normal statistical fluctuations in a purely random alloy. We shall see the role played by these nuclei later. The final state is obtained by a very long annealing at such a temperature that an equilibrium is reached in a reasonable time. The alloy is then composed of a matrix which is a saturated solid solution, much poorer than the initial one. Imbedded

Jan 1, 1957

By A. Boltax

Precipitation processes occurring during both furnace cooling and aging of copper-iron albys were studied by means of electrical and magnetic measurements. On furnace cooling, two distinct stages in the precipitation process were detected; one occurring above and the other below 850° C. The kinetics of precipitation from quenched alloys were studied between 200° and 700°C. The reaction appears to be consistent with the concept of tmcleation of precipitate particles at dislocation loops formed by the clustering of quenched-in vacancies. A study Of in copper-iron alloys is particularly interesting because the combination of magnetic and electrical properties in these allovs provides a quantitative means of following the course of the precipitation reaction. (The details of precip-

Jan 1, 1961

By S. E. Bronisz, R. E. Tate

s-plutonium samples possessing a strong growth texture have been produced by allowing them to transform under pressure from p to a. A fiber texture with [010] parallel to the pressure axis results. The textured samples are expected to be useful in determining the effects of crystallographic orientation on the physical properties of a plutonium, and initial results of measurements of resistivity and mechanical properties are described. THE crystal structure of a plutonium1 is mono-clinic, P21/m, and many of the metal&apos;s properties should reflect the crystallographic anisotropy. Unfortunately, it has not yet been possible to grow useful sizes of single crystals of a plutonium. Therefore, few of plutonium&apos;s orientation-sensitive properties have been determined as a function of crystallographic orientation. One way to gain information about at least some of the orientation-dependent properties is to study a highly textured sample. Such samples have been produced by cold rolling a plutonium,2 but they are necessarily very small in one dimension. We have now successfully used two other techniques to produce highly textured samples, not limited to small thicknesses. METHODS OF PRODUCING PREFERRED ORIENTATION The texture is produced by causing the plutonium to transform from ß to a while under pressure. It was observed by Gardner3 that applying a compres-sive load during the transformation resulted in the formation of columnar grains of a plutonium, and Cramer4 observed a similar structure in some diffusion couples rolled in the P phase. Neither of these workers, however, investigated the subject beyond these observations. The more flexible of the two methods developed is that of compressive loading. The technique is to enclose a sample of plutonium in a die assembly before applying the load. It is possible, of course, to dispense with the die and simply press the sample between two platens. In this case, however, the unrestrained sample deforms during the pressing, making it difficult to maintain the load and to control the final sample thickness. This compressive loading technique has been used on specimens ranging from 1/4 to 3 in. diameter, with height-to-diameter ratios ranging from 5 : l to 1:6. The procedure begins with loading the sample, a right cylinder of a plutonium, into the pressing die. Plastic deformation of the sample while it is being pressed is minimized by machining the sample so that its diameter is nearly the same as that of the die barrel. Then the loaded die assembly is placed in a vacuum pressing can that fits on a hydraulic press. After a vacuum is achieved the die assembly is heated to 180°C and equilibrated. The load is then applied and the specimen and die are allowed to cool to about 40° to 50°C before the pressure is removed. The resulting sample is composed of rod-shaped a -plutonium grains, the rod axes being parallel to the cylinder axis and the pressing direction. Photomicrographs of the oriented structure are shown in Fig. 1. Although most of the specimen is composed of grains whose rod axes are parallel to the cylinder axis, a thin, peripheral layer consists of rod-shaped grains whose rod axes are perpendicular to the cylinder axis. Presumably, the highly plastic nature of p plutonium leads to approximately hydrostatic conditions during the initial stages of the P — a transformation under pressure. At this time, the grains in the peripheral layer would have grown parallel to the local force direction. During the latter stages of the transformation, the accompanying volume contraction would have eliminated the radial forces, leaving only the axial force and resulting in the growth of the observed structure. The growth texture did not form without the application of pressure. Attempts were made to produce the texture by repeating the standard temperature cycle without

Jan 1, 1965

By C. S. Barrett, A. Smigelskas

There have been no publications of the deformation and recrystallization orientations of the metal beryllium, yet pronounced textures would certainly be anticipated since it is close-packed hexagonal in structure. Having an axial ratio approximately that of magnesium, beryllium probably deforms by nearly the same slip and twinning mechanisms that operate in magnesium, and the textures are likely to be similar or but slightly different from the magnesium textures. In the tests reported below this is found to be the case; the textures are found to differ from those of magnesium only in the details of the scatter from the average orientation. This report covers not only samples rolled at room temperature, but some rolled at elevated temperatures. Since magnesium has been suspected by some investigators of altering its crystallo-graphic deformation mechanism at elevated temperatures, it was considered possible that beryllium might do so and alter its textures accordingly. No pronounced alterations were found, however. Unfortunately, the theory of deformation textures is not in a state of development that permits one to deduce the deformation mechanism from a knowledge of the textures, which means that the similarity of textures at different rolling temperatures, reported here, cannot be taken as definite evidence that the deformation mechanism is actually the same at all temperatures. The general similarity of the deformation textures of magnesium and beryllium also extend to the recrystallization textures of the two metals, judging by the pole figures for recrystallized sheet presented in this report. Samples were prepared in the form of composite sheets made up of small pieces stacked in a pile. Each piece was trimmed with scissors so that an edge was parallel to the rolling direction, dipped in paraffin, and assembled into the pack by aligning it under the cross hair of a microscope. As the desired orientation was obtained on each piece it was secured in place by touching with a hot wire to melt the paraffin. A stack of ten or fifteen pieces was built up in this way, then trimmed to the shape of a T; the portion to be X rayed was then etched to the shape of a wire about 0.045 in. diam with 6N HCl. This method of shaping the sample is a modification of that used by Bakarian on magnesium.&apos; The absorption of the rays in the sample was so slight that it caused no difficulty in interpreting the films. Exposures were made with a 0.030 in. diam pinhole, using molybdenum radiation (40 kv, 25 ma, Type A film at 5 cm, 2 to 3 hr exposures). With the recrystallized specimens it was found necessary to oscillate the specimen so as to reduce the spottiness of the lines. A range of oscillation of 5" was SUB- cient to produce reasonably satisfactory patterns, though the quality was somewhat inferior to that of the deformation texture patterns, and only two degrees of intensity were read from the arcs on the films. Typical photo-grams for each of the deformation textures and the recrystallization texture are assembled in Fig 1. The pole figures were plotted in the usual way with the intensity of the various portions of the diffraction rings estimated by eye. Seven to nine films were made of each sample and each was carefully read in plotting the pole figures. Typical series included exposures with the beam normal to the rolling direction and at 11, 26, 41, 56 and 71" to the cross direction, plus two exposures with the beam normal to the cross direction, and at 11 and 79" respectively to the rolling direction. The rolling was in each case considered sufficient to develop the final texture: the reduction by cold rolling was 84 pct (from 0.0045 to 0.0007 in. thickness), following prior hot rolling in longitudinal and transverse directions and recrystallization; the reduction by hot rolling at 800°C was 90 pct (0.010 to 0.001 in.), following similar prior treatment; the reduction by rolling at 350°C was 88 pct (from 0.005 to 0.0006 in.) after similar prior treatment. The recrystallization texture was determined on a sample rolled at 350" to a reduction of 88 pct (0.0165 to 0.002 in.) after similar prior treatment, then mounted between steel strips to keep it flat and annealed at 700" in an atmosphere of argon. Discussion of Results The results of the X ray determinations are assembled in the pole figures of Fig 2, 3, 4 and 5 for rolling at

Jan 1, 1950

By S. L. Lopata, E. B. Kula

A variation of yield and tensile strength with direction has been noted in heat-treated 4340 steel which had been warn-worked by rolling in the austenitic condition prior to quenching. Measurements by X-rays showed a preferred orientation of martensite crystals. Various ideal preferred orientations of martensite were calculated by assuming a preferred orientation for austenite and transforming this to martensite by the Kurdjumov -Sachs and Nishiyama relationships. Comparison with the measured preferred orientation showed that the ideal rolling texture for austenite in 4340 steel could be expressed as a (112) [111] texture with a component of (110) [112]. No evidence was found for any fiber axis in the rolling direction, or fop- a (123) [412] texture. The observed martensite pole figures can be adequately accounted for by these ideal austenite textures and by the Kurdjumou-Sachs or Nishiyama transformation relationships between austenite and martensite. ALTHOUGH preferred orientations are found in cold-rolled steel sheet and in many nonferrous metals, they are not generally encountered in wrought, heat-treated high-strength steels, since such steels are generally not cold worked sufficiently to develop a strong texture, and any texture that is present is removed during heat treatment by the phase transformations taking place. This report gives details on a preferred orientation found in warm-rolled and hardened 4340 steel. In a recent study, a special combination heat-treating and working technique was used in which 4340 steel was deformed in the austenitic condition, and before re crystallization of the austenite could occur, quenched to form martensite.&apos; Since the austenite was unrecrystallized, it was cold worked and hence could have contained a preferred orientation which could be transmitted to the martensite on quenching, and this in turn could be manifested as a directionality of mechanical properties. Such a directionality of properties was found as a result of working, and this prompted an X-ray study of the preferred orientation. Literature Survey— Rolling Texture in Face-Cen-tered-Cubic Austenite—M a preferred orientation is found in a rolled and hardened steel, it is first appropriate to consider what texture existed in the austenite as a result of the rolling but prior to the transformation to martensite. The changes taking place as a result of the austenite-martensite transformation are then considered. In view of the instability of austenite in 4340 steel at low temperatures, no direct determination of the austenite texture was made. However, an estimate of the texture for austenite in 4340 steel may be made by considering the textures found for other face-centered-cubic metals. Barrett&apos; has reviewed the rolling textures for many materials. The most common orientation in face-centered-cubic metals has the (110) planes parallel to the rolling plane and the [112] directions parallel to the rolling direction, or (110) [112]. Other orientations found are (112) [111], as well as (100) [001], (110) [001], and others. Beck and his co-workers, using quantitative pole figures, report that (123) [121],3 later corrected to (123) [412],4 better describes the ideal orientation. smallman5 reported that the ideal preferred orientation for high-purity face-centered-cubic metals is (123) [121], but that there is a transition to (110) [112] as solid solution elements are added. The latter texture tends to occur more readily at lower temperatures. This transition between the two textures was explained by differences in the slip characteristics with concentration or temperature. More recently, Jones and Fell6 concluded that the (123) [412] texture for face-centered-cubic metals could equally well be represented by a mixture of (110) [112] and (112) [111] textures, and hence it had no physical reality. From the above results it can be seen that there is no agreement on the "ideal" texture for fcc metals and, hence, no firm basis for assuming a texture for austenite in 4340 steel. Therefore, the orientations (110) [112], (123) [412], and (112) [111] have been considered in the following.* *The (123) [4121 is identical to the (123) [121] rotated 90 deg. Orientation Relationship between Austenite and Martensite—When martensite forms from austenite, certain crystallographic planes of the martensite are parallel to planes in the austenite. This orientation relationship was first determined by Kurdjumov and

Jan 1, 1960

By M. Semchyshen, G. A. Timmons

The predominant orientation in both straight-rolled and cross-rolled molybdenum is the {100} [110] texture. Upon complete recrystallization, this same texture predominates, but there is less spread about the ideal orientation. A secondary orientation about the [111] direction as the axis develops in cross-rolled sheet. Compression-rolled sheet exhibits random orientation in the plane of the sheet. Some mechanical properties were measured at varying angles to the rolling direction to determine the effect of preferred orientation on anisotropy in molybdenum sheet which had been straight, cross, or compression rolled. THE development of the arc-cast process has made available large ingots of molybdenum from which it is possible to roll sheet of considerable size. It is anticipated that such sheet will be further fabricated by spinning, drawing, stamping, or forming. Anisotropy of physical properties caused by the preferred orientation developed in the sheet during rolling may be expected to affect the behavior of the metal when subjected to these fabricating operations. To produce a sheet which will be most amenable to the fabrication of a given shape by a particular operation, consideration should be given to the directions and magnitudes of plastic deformations produced in the operation. When possible, the rolling schedule should be controlled to develop a texture which favors the required deformation. The existence of preferred orientations in rolled molybdenum sheet has been reported by Jeffries,&apos; Konobejewsky,&apos; Fujiwara," Goss,&apos; and Ransley and Rooksby." None of these investigators obtained sufficient X-ray data to permit the construction of pole figures; instead, they based their conclusions upon Debye-Scherrer patterns of a limited number of positions. Ransley and Rooksby devoted some attention to transcrystalline cleavage at 45" to the rolling direction, indicating that it is appreciable in polycrystalline material only when the crystals are in the ideally preferred condition, and that this condition is only approached if the metal has been rolled successively in two perpendicular directions. In a recent paper, Custers and Riemersmao introduced the first pole figures to describe the textures of straight-rolled and cross-rolled molybdenum sheet. To increase the knowledge concerning the generation and effects of preferred orientations in molybdenum sheet, an investigation was undertaken to determine the effects of variations in rolling schedule and annealing treatments on preferred orientation, and to correlate preferred orientations with some mechanical properties. The orientations of straight-rolled, cross-rolled, and compression-rolled sheet have been determined by X-ray analysis, both as-rolled and after recrystallization. Pole figures have been constructed to describe the textures produced by these various rolling procedures. Texture of Cast Molybdenum Ingots In the arc-cast process, molybdenum powder is pressed into a vertical column which is sintered to increase its strength as it proceeds downward into a water-cooled mold, where the metal is melted in an alternating-current arc established between the end of the formed powder electrode and the metal bath at the top of the growing ingot. Since the solid-liquid interface moves continuously upward in the mold, the crystal axes are not normal to the cold surface of the mold but have the curvature shown in Fig. la. X-ray analysis reveals that the cube axis is the fiber axis and that it is normal to the cold surface of the mold; that is, the [loo] direction is parallel to the longitudinal axis of the ingot. This substantiates recent work by

Jan 1, 1953

By A. H. Geisler, J. H. Keeler

Preferred orientations in rolled and annealed titanium sheets were determined by the Geiger counter spectrometer X-ray diffraction technique. Five annealing textures dependent upon the temperature range of annealing were found, and in order of increasing annealing temperature pendent upon the temperature range are: 1—a deformation like texture, 2—a rotated inorder a-recrystallization temperature texture, 3-a retained u-recrysraIlization texture, on annealing at lower temperatures of the ß-region, 4—a transformation texture based on recrystallized a and predicted by the Burgers&apos; relationship, and 5—a ,ß-cube texture. These results are examined in terms of current theories of recrystallization textures. UMEROUS investigators have described the tex- ture obtained by cold rolling the hexagonal metals, titanium, zirconium, and beryllium, which have c/a ratios less than that of ideal packing, 1.633. The basal planes are rotated out of the rolling plane, about the rolling direction, so that the basal poles are tilted toward the transverse direction as shown schematically in Fig. la. In all instances but one,&apos; it was also reported that the [1010] direction was parallel to the rolling direction (see Fig. lb). Hot rolling has been reported as causing a similar tilt of the basal poles in the transverse direction (see Fig. la) and causing the [1010] direction also to be parallel to the rolling direction as shown schematically in Fig. lb. Annealing after deformation does not appreciably change the tilt of the basal poles in the transverse direction." Beryllium2-7 continues to have the [1010] direction in the rolling direction after annealing, and similar observations for titanium and zirconium&apos; . have been reported for annealing at fairly low temperatures, again as in Fig. lb. At higher annealing temperatures, however, the recrystallized grains of titanium" and zirconium have an orientation such that the [1120] direction is approximately in the rolling direction, although the basal poles are still inclined in the transverse direction. Figs. la and lc show the resulting orientations schematically. This change in orientation has been described as a nominally ±30° rotation of the hexagonal crystallites about the basal poles of the cold rolled texture and is apparent from the results which are summarized in Table I for investigations with the X-ray diffraction technique employing film. The angles y, , and ß are indicated in Fig. 2 which represents the stereographic projection of (1070) poles for the mean orientation of a pole figure. Texture determinations for titanium using the Geiger counter spectrometer have provided similar results except that in some instances additional components of the texture were proposed, as shown by the summary of data in the upper half of Table 11. On the other hand, the spectrometer technique, when applied to zirconium,* has revealed a splitting Recently completed studies of the textures of annealed zirconium", show zirconium to possess textures very similar to those reported here for titanium. Therefore, much of this discussion will include zirconium by virtue of its close similarity to titanium in pref erred orientations. of the intense areas of the pole figure for samples annealed at 600°C. This splitting could be described by a 7" rotation of the tilt axis about the normal to the rolling plane. Such a splitting for the annealed texture relative to the cold rolled texture was not observed in other determinations for either zirconium or titanium using the less sensitive film X-ray methoe and makes the relationship between the two types of texture more complex than the simple rotation about the (0001) pole based on film work. The more precise investigations on zirconium permit the descriptions in the lower part of Table 11, which show that the texture depends quantitatively on the temperature of annealing. When zirconium is annealed at temperatures up to 400°C, the texture is similar to the cold rolled texture, while annealing in the range 500" to 900°C produces a texture which is only approximately described as [11%] in the rolling direction. More precisely described results for zirconium show that the two types of splitting ( 1—about an axis in the rolling plane through an angle given in the second column in Table II and 2—about the normal to the rolling plane through an angle given in the third column of Table 11) depend on annealing temperature. The [1120 is the rolling direction only when the annealing temperature is in the vicinity of 900°C

Jan 1, 1957

By Jack L. Taylor

WITH the exception of the work of Vogel,&apos; and Rolla and Iandelli, very little information has appeared in the literature on titanium binary systems with the rare earth elements. Rare-earth additions to titanium alloys may possibly parallel the beneficial effects on the physical properties of certain steels. Having this in mind, some knowledge of solubility limits and intermediate phases, if any, would be useful. An investigation of the titanium-rich Ti-Ce system was started. Alloy Preparation The iodide titanium from the New Jersey Zinc Co. and the cerium metal from the Institute for Atomic Research Ames Laboratory used in this work were supplied with the typical analysis shown —iodide titanium: 0.0065 pct Mn, 0.0022 pct Fe, 0.0015 pct Cu, and 0.0042 pct Pb; cerium metal: <0.01 pct Fe, <0.03 pct Si, <0.05 pct Ta, <0.02 pct Pr, <0.03 pct Ca, <0.02 pct Mg, with no trace of Nd, La, or Th. The cerium metal, stored in oil, was washed and scraped just before weighing into capped cups machined from iodide titanium. The cold hearth helium-arc furnace described by Schramm et al3 was used for melting. The alloy buttons from the arc-melted cup were cut in two, mounted, and examined. Homogeneous alloys were demounted and rolled to approximately 1/4-in.sq bars. Sections l/8 in. thick were cut from the bar to provide samples. The Ti-Ce alloy buttons analyzed for cerium were of the following composition: 0.19, 0.36, 0.48, 0.61, 1.15, 2.52, 3.06, 3.70, 4.30, 9.20, 14.26, and 18.50 wt pct. Nominal

Jan 1, 1958

By G. W. Cullen

Niobium-tin has been prepared on insulating suhstrates hby simultaneous hydrogen reduction of gaseous niobium and tin halides. Stoichiometric material is greater than 98.8pct theoretical density, appears to he single-phase, and has a total impirity level less than 0.3 at. pct. Transition temperatures and lattice constants may he related to composition. Typical current densities in various fields and orientations are given. IT is known that Nb3Sn carries large current densities in high fields, 1 and exhibits an unusually high transition temperature2 and critical field.3 For these reasons high-field solenoids have been constructed of this material.4 Because of the emphasis on solenoid fabrication, much of the materials research has been directed toward development of wire geometries wherein the brittle Nb3Sn is supported by a more malleable metal or alloy. There are, however, basic studies and applications that can be carried out only on Nb3Sn supported by an insulator. Insulating substrates are desirable for a number of reasons: the substrate does not interact with applied or induced currents and fields; diffusion of metallic species into the de- posit is avoided, both during the preparation and during subsequent heat treatment; irradiated samples are not more active than the deposit itself. Unsupported Nb3Sn geometries may also be prepared by preferential chemical dissolution of the insulating substrate. This report describes the preparation and properties of Nb3Sn deposits on ceramic substrates. Experiments currently utilizing material prepared in the manner described in this report include the following: dependence of current-carrying properties on field strength and orientation 5,6 radiation damage,7,8 tunneling,9 thermal conductivity (substrate removed),1° microwave surface impedance," tube magnetization,6,12 resistivity as a function of temperature,13 and current density and transition temperature as a function of annealing.14 Possible practical applications include magnetic shielding, superconductor generators, and frictionless bearings. PREPARATION Methods for the deposition of elemental niobium and tin by hydrogen reduction of the gaseous metal halides have been known for some time,15,18 but only recently a procedure was developed in this laboratory17 for the codeposition of these two metals on a hotwire as the intermetallic compound, Nb3Sn. This method of simultaneous hydrogen reduction of the gaseous niobium and tin chlorides is used for the preparation of Nb3Sn On ceramic substrates. The procedure differs from that employed on a hot wire in that insulating substrates cannot conveniently be heated to temperatures greater than their surround-

Jan 1, 1964

By T. J. Koppenaal

The surface slip line structure has been investigated by optical microscopy during the easy glide deformation of Cu-A1 single crystals as a function of composition, testing temperature and prior thermal treatment. The slip line structure in alloys of 2.5 or less at. pct Al is similar to pure copper, while alloys of 5 or more at. pct Al show slip tracings typical of a brass. Cross slip is observed in the "a-brass type" crystals and the amount of this type of slip increases rapidly with aluminum content. The cross slip tendency in 14 at. pct Al crystals is signicantly higher when tested at 150°C as compared to 4.2" and 77°K. In addition, cross slip is more pronounced in this alloy in the furnace cooled condition than when quenched from 450°C. The cross slip behavior is analyzed in terms of existing models for this type of deformation. In two previous investigations, reports of yield points1 and solid solution strengthening2 in Cu-A1 single crystals have been given. This paper enlarges upon the brief description of the slip line structure discussed in these reports. Since the easy glide slip line pattern of copper changes markedly with the addition of -30 pct Zn (-brass),3 a study of slip lines as a function of solute additions in Cu solid solutions should help to explain some of these differences. In addition to composition variables, slip lines have also been studied as a function of testing temperature and prior thermal treatment. PROCEDURE The slip line observations were made on single crystals of 0.5 to 14 at. pct Al using a light microscope. Details concerning the preparation and basic testing procedure are given elsewhere.&apos; Prior to testing, each crystal was homogenized at 900°C for 24 hrs, furnace cooled, and electrolytically polished in a 60 pct phosphoric acid solution. The strain rate was-5 X 10 sec-I in each case. Unless otherwise stated, all observations reported upon here were made during the early stages of easy glide. RESULTS AND DISCUSSION The maximum magnification generally used was 1000X, and slip lines could be resolved down to about 105 cm (1000A). This resolution is appreciably less than obtainable with electron microscopy replica techniques where the replication can resolve slip lines down to about 40 A. Thus, while many qualitative features could be studied, the type of quantitative data obtainable with an electron microscopy replica study could not be made. Crystals containing 0.5 and 2.5 at. pct Al deform much like pure copper exhibiting a high density of fine slip lines that cover the entire gage length of the specimens. Fig. 1 shows the surface slip line pattern in a 2.5 at. pct A1 extended 0.01 shear strain at room temperature. Crystals having 5 to 14 at. pct A1 showed appreciably coarser slip lines that were generally concentrated at one end of the gage length. During easy glide these coarse slip lines propagate along the gage length in a manner similar to that observed in a-brass single crystals by Piercy, Cahn, and cottrel14 and refered to by them as a Lüders band propagation. Fig. 2 shows a typical area of these coarse slips in a 14 at. pct A1 crystal after a room temperature shear strain of 0.01. Two slip systems were apparently active. Using a method described by Cullity, the angles, between the specimen axis and the normals of the primary and secondary slip planes were determined to be 50 and 84 deg, respectively. &apos;From the Laue photograph, was 52, 81, 66, and 30 deg for the primary, cross, conjugate, and fourth slip planes, respectively. The secondary active plane in Fig. 2 is thus established as the cross slip plane, and the operative slip system is evidently the cross slip system, e.g., slip

Jan 1, 1963

By C. G. Dunn, P. K. Koh

The primary recrystallization textures of 11 single crystals cold rolled 70 pct were determined. The effect of crystal orientation on recrystallization behavior was investigated also and found to be large. An exception was found to the relationship that strong components of the recrystolliza-tion texture are rotated from the cold rolled texture by 30° about <110> axes, but generally this relationship was found to hold quite well. Evidence supporting oriented nucleotion was found and discussed in terms of probable active slip systems and <110> edge dislocations. THE present paper is one of a series&apos;.&apos; on recrys-tallization phenomena in cold rolled 31/4 Si-Fe single crystals and is mainly concerned with the textures produced on recrystallizing from stable end orientations. Data for the cold rolled textures of the crystals used have been reported by Koh and Dunn." Their results showed that the sharpness of the cold rolled textures varied throughout the range of stable end orientations and that the tendency to re-crystallize was related to the sharpness of the cold rolled texture, wherein the rate of recrystallization increased and the size of recrystallization grains decreased with decreasing sharpness of the cold rolled texture. In the project under consideration the cold rolled crystals involved a range of initial orientations that, together with those studied earlier,&apos; provide information on several points. The first point is whether the recrystallization texture from a (111) [112] cold rolled texture, a stable end orientation that can be approached from different directions, correlates in any way with the initial orientation before cold rolling, or whether the recrystallization texture is entirely determined by the observable features of the cold rolled texture. The second point involves a preliminary study to see if the main components of the recrystallization textures correlate with the most probable active slip systems. The third point is to determine what effect departure from slip on one slip system has on the tendency to recrystallize. Experimental Procedure Nine specimens from a previous investigation and two additional ones from thicker stock (lot D) but of similar composition to the others were used in the present work. The latter two crystals, like the nine, were cold rolled to a reduction in thickness of 70 pct and the amount of widening was determined. Depending on their primary recrystallization behavior, the cold rolled crystals were given short or long anneals at temperatures of 980°C or higher. Table I summarizes the data on initial orientations, the textures obtained by cold rolling, and the anneals given to provide samples for the present work. Fine grained specimens were thinned to 0.002 in. thickness and placed in an integrating specimen holder. Chart recordings using a transmission X-ray method and MoKa radiation were obtained for diffraction from (110) planes. This method,&apos;,3 which gives data for all of the pole figure except a central region of 30" radius, proved sufficient to give generally five, and sometimes six, of the six possible pole concentration areas of any one component of the texture. These data, therefore, were generally adequate for a positive identification of each component present. The first texture obtained for specimen B-2 was poorly defined because of too coarse a grain structure and therefore too few crystals in each component for satisfactory X-ray reflections. The same

Jan 1, 1957