Search Documents

By L. D. Hall, D. R. Mash

The paper presents the results of experiments on the anelastic. behavior of gold, as manifested by grain boundary relaxation. Two grain boundary internal friction peaks are found for 99.9998 pct Au. It is found that the peaks are associated with primary and secondary recrystallization. However, the existence of two discrete peaks cannot be explained on the basis of grain size and shape alone. It is suggested that grain boundary stability, as determined by orientation, plays a role in the observed effects. EVIDENCE for the viscous behavior of grain boundaries in metals has been presented in recent years by several investigators, based upon studies of various anelastic effects, especially internal friction. KG1 has contributed greatly to this field, having put forward a coherent body of evidence for stress relaxation by the viscous intercrystalline flow mechanism. In this connection, he has made extensive use of pure aluminum (99.991 pct) as the test material, although he has also studied other metals and alloys, including pure iron (Puron).² Rotherham, Smith, and Greenough³ have studied the internal friction of pure tin, interpreting their results in a manner similar to that of KG. In view of the importance of such studies in shedding light upon the fundamental structure and behavior of the grain boundaries in pure metals, it appears that the use of a very pure test material which is inert to its environment should provide useful information on anelastic properties and the source of such behavior in pure metals. The present work was carried out on spectrograph-ically pure, 99.9998 pct Au, free of all impurities except for a trace of silver, estimated to be present to the extent of about 0.0002 pct. The term "pure gold" will hereafter refer to this very pure material. Gold of commercial purity, 99.98 pct, was also studied to observe the effects of small amounts of impurities. A pure gold "single crystal" specimen was also tested for comparison. The variation of the internal friction and rigidity modulus as a function of temperature was determined by means of a torsion pendulum apparatus employing extremely low stress amplitudes and a frequency of vibration of the order of 1 cycle per sec. A 12 in. length of 0.031 in. (20 gage) gold wire formed the suspension element. The apparatus was similar to that described by Ke.l The test procedure and the basic requirements to be met for obtaining useful experimental data by this method have been given elsewhere.1,2 It should be made clear that in all of the experiments to be described, the internal friction and rigidity were independent of the amplitude of torsional vibration. The semilog plot of amplitude of vibration vs ordinal number of vibration was a straight line. This was carefully verified for each internal friction measurement. The linear variation shows that the internal friction was independent of stress; i.e., that the specimens were not being cold-worked during testing. The reproducibility of the internal friction curves, which were obtained by cyclic heating and cooling, indicates that the gold was unaffected by its environment during the tests. The measure of internal friction adopted in the present study is the conventional "logarithmic decrement," defined as follows: log. dec. = l/n In A0/An [I] where n is the number of cycles or vibrations; A,, the initial amplitude of vibration; and An, the amplitude after the nth cycle. When the logarithmic decrement is small, the shear modulus, G, of the wire is proportional to the square of the frequency of vibration provided the length and radius of the wire are kept constant. A plot of frequency squared vs temperature gives the following ratio:' This expresses the fraction of the stress which has not been relaxed at a given temperature. Gr and Gv are the relaxed and unrelaxed moduli, respectively. The frequency of vibration in the polycrys-talline specimen is fp, and the frequency of vibration of a single crystal is f8. This latter quantity is obtained simply by extrapolating the linear, low temperature portion of the curve of frequency squared vs temperature for the polycrystalline specimens. The theory of viscous grain boundary stress relaxation as demonstrated by the anelastic behavior of metals has been discussed in detail by Zener4 and need not be reproduced here. Experimental Results Initial measurements of the internal friction of pure gold were carried out on specimens which had been drawn with no intermediate annealing, resulting in a material which had undergone approximately 99 pct reduction of area in final processing. Annealing was then carried out at successively higher temperatures starting at 400°F for 1 hr and proceeding in this manner to as high as 1600°F in 100°F intervals. After each annealing treatment an internal friction and rigidity vs temperature curve was obtained over the range from room temperature to the particular annealing temperature. The resulting internal friction curves did not exhibit well defined maxima (peaks), but rather several fairly flat

Jan 1, 1954

By P. W. Bakarian, John C. McDonald

Three magnesium alloys were processed in various ways to exhibit a wide variation in the ratios of yield strength and tensile strength in the rolling direction compared to the cross-rolling direction. Basal-plane pole figures were prepared from several specimens. A fair correlation was observed between the property ratios and the ratio of percent of poles oriented in the cross-direction quadrants compared to the percent oriented in the rolling-direction quadrants of the pole figures. THE modes by which magnesium crystals deform are such as to lead to marked preferred orientations in all forms of wrought products. The effect of the active modes at room temperature, coupled with these orientations, is often to produce a lower compressive yield stress compared to the tensile yield stress. The phenomenon is due to easy twinning in compression, and has been well-related to the preferred orientations as described by basal-plane pole figures of the hcp magnesium single crystal. The literature contains some information on the variation with test direction of the tensile properties of sheet, but no quantitative relationship to the observed pole figures has been established. These effects have been reviewed in the few com- prehensive treatises in English which have been written on magnesium technology and metallurgy.1°3 Roberts presents several pole figures, but no tensile-property data in the plane of the sheet. Raynor has no pole figures, but quotes Frommer's4 results. The information in Beck's compendium more or less parallels the results of Jones and powell.5 In both a Mg + 1.5 Mn alloy and a Mg + 4.6 A1 alloy, cold rolling was found not to change the general situation of higher properties in the cross-rolling direction,* than in the rolling direction. Thomas'6 X-ray studies of Jones and Powell's specimens did not permit correlation of properties and preferred orientation. Ansel and Betterton7 report tensile and compressive properties on three other alloys as a function of degree of cold rolling, plus a recrystallizing anneal. As rolled, there was a change in anisotropy with degree of reduction, but all alloys were reasonably isotropic in tension when annealed. X-ray diffraction photograms illustrated the kinds of orientations present, but were not correlated with the properties. Bakarian8 has described a method of determining quantitatively a preferred orientation, and illustrated the method by applying it to pure magnesium and two of its alloys. This method was used in the present work as a basis for correlating the strength properties with the texture.

Jan 1, 1965

By R. L. Grunes, F. K. Kies, C. D&apos, Antonio

THE several studies concerned with the annealing of thin nickel films have largely been restricted to films of a single thickness.1-4 It is well-known, however, that both physical and mechanical properties depend upon film thickness.5, 6 The strength-thickness relations found in vapor-deposited nickel films in the annealed and as-deposited states, as an example, are at least partially due to the density and arrangement of imperfections within the films.7, 8 For these reasons, the annealing characteristics of thin nickel films as a function of thickness were investigated. Electrical resistance was chosen to monitor annealing behavior since resistance changes are partially dependent upon defect structure. In addition, the equations predicting film resistivity as a function of thickness are already available.9, 10 Further advantages afforded by electrical-resistance measurements are its adaption to continuous readings during annealing and its relative simplicity. Nickel films were vapor-deposited, at average rates of 60Å per sec, on Vycor substrates held at room temperature in vacuums of about 10-5 torr. Afterwards, deposition-thickness measurements were made using a multiple-beam interferometric technique. A more detailed description of deposition procedures and the interferometer appear elsewhere.7, 8 The four-probe method was employed in measuring electrical resistance since this technique measures film resistance without contributions from lead wires and contacts. Resistance measurements were made before, during, and after annealing to temperatures of 700°C under vacuums of approximately 10-4 torr. Measurements were made every 25°C or more often when necessitated by unusual resistance changes. Cooling and heating rates were maintained at approximately 5°C per min. Typical resistivity vs temperature curves are shown in Figs. 1 through 4. It is apparent from these

Jan 1, 1965

By S. R. Goodman, Hsun Hu

A study has hem made of the formation of annealing textures in an 18-8 austenitic stainless steel (Type 304L) from various deformation textures obtained by rolling at different temperatures. When the deformation texture is a mixture of the ferritic type and the brass type owing to the pres -ence of both martensitic ferrite and retained aus-tenite in the specimen, recrystallization takes place by the growth of the existing austenite phase. In a previous report,' it was shown that the rolling texture of austenitic stainless steel (Type 304L) changed gradually from the brass type to the copper type with increasing temperature of deformation above 200°C. These changes are similar to those in high-purity silver2,3 and electrolytic copper;4 a brass-type texture is favored at low rolling temperatures, whereas a copper-type texture is favored During the course of rolling -texture transition from the brass type to the copper type, the subsequent recrystallization textures change accordingly. The orientation relationship between the annealing textures and the various rolling textures, being consistent with previous observations on various fcc metals, can be described as [Ill] rotations of approximately 25 to 40 deg. Carhide precipitation may influence the annealing textures. at high rolling temperatures. Furthermore, the annealing textures in high-purity silver5 and electrolytic copper4 were found to depend entirely on the prior deformation texture. From a copper-type rolling texture a strong cube texture will form upon recrystallization, whereas from a brass-type rolling texture the annealing texture will be quite different from the cube orientation. In an earlier comm~nication,6 the formation of a strong cube texture in 18-8 austenite stainless steels (Types 304 and 304L) was reported briefly by the authors. The present paper constitutes the results of a complete study of the annealing textures obtained from a

Jan 1, 1965

By K. T. Aust

The occurrence of annealing twins in high-purity aluminum resulted in the formation of grain boundaries having orientation relationships which correspond to a high density of coincidence sites. The results provide support for the coincidence site model and indicate that large-angle coincidence boundaries have lower free energies than large-angle noncoincidence boundaries. Observations are presented concerning the coherent structure of twin interfaces in aluminum and the importance of inter-facial energy in preferred orientation. RECENT experiments1 have shown that when an annealing twin is formed during grain boundary migration in zone-refined lead, a large-angle random boundary is replaced at the growth front by a large-angle coincidence site boundary. The coincidence site orientation relationships obtained by twinning were of the type considered by Kronberg and Wilson,2 Frank,3 and Dunn.4 On the basis of the theory of annealing twins advanced by Fullman and Fisher,5 these observations indicate that the energy of a coincidence site boundary is less than the energy of a random boundary by an amount which exceeds the energy of the coherent twin boundary. This energy difference between the coincidence and random boundaries must be at least about 5 pct since the ratio of twin boundary energy to grain boundary energy in zone-refined lead is 0.05 * .014.6 Fullman7 has found that the twin boundary energy in aluminum is about 21 i 5 pct that of a large-angle grain boundary. A twin boundary energy as large as this would be expected to exclude the formation of many coincidence site grain boundaries, especially those which have a relatively low density of coin- cidence sites. Therefore, if the coincidence site model is a useful interpretation of certain large-angle boundaries, then it would be predicted that only coincidence boundaries which separate adjacent crystals with a relatively high density of coincidence sites may be obtained as a result of twinning in aluminum. The present experiments provided a means of testing this prediction since annealing twins occurred during the growth of recrystallized grains into striated, melt-grown single crystals of zone-refined aluminum. EXPERJMENTAL PROCEDURE A striated single crystal of zone-refined aluminum, about 1 cm sq and 37 cm in length, was obtained during zone melting of aluminum of 99.996 wt pct starting purity in a graphite boat under helium atmosphere.8 A molten zone of 2 to 3 cm in length, which was maintained by induction heating. was passed along the length of the bar for eleven passes at a rate of 0.9 mm per min. An additional final pass was given at a rate of 0.2 mm per min. The center portion of the zone-melted bar was characterized by an electrical resistivity ratio between room temperature and 4.2° K of 8000 to 9000. Single crystals of 1 to 2 cm in length were removed from the center section of the zone-refined bar and electrolytic ally polished in a 2:l solution of methyl alcohol and concentrated nitric acid. The specimens were then chemically polished in Alcoa R-5 solution. X-ray analysis of the single crystals indicated the presence of striations or lineage substructure having misorientations as high as 2 deg. New, recrystallized grains were introduced into each striated crystal by the technique of artificial nucleation and growth, previously described.9 During the growth of the recrystallized grains at 300' to 600°C in argon, it was sometimes found that a

Jan 1, 1962

By G. M. Ault, G. C. Deutsch

The paper reviews the efforts made to utilize powder metallurgy to solve problems encountered when using alloys at high temperatures. The following subjects are discussed: comparison of wrought and sintered super alloys, sintered aluminum powder, porous materials for transpiration cooling, molybdenum, and cermets. TODAY, powder-metallurgy techniques are be-JL coming increasingly important, producing materials which at the present time cannot be made by any other method. Among these materials are high melting-point metals such as tantalum and tungsten, porous metals for filters and lubricant-containing bearings, electrical contacts and electrodes (i.e., tungsten-copper), cutting tools of the cemented carbides, and magnet alloys. In addition, the powder-metallurgy industry has grown because, through the application of its methods, shaped parts, such as gears, can be produced at tremendous rates with a low scrap loss in comparison with manufacture by casting or forging and machining. In the past few years, by utilizing powder metallurgy, several approaches to the problem of high temperature materials have been investigated. In this paper the authors will review some of the studies on application of materials having properties above 1350°F. Since their experience lies in the aeronautical field, possible uses of powder-metallurgy techniques in the production of aircraft en- gines will be emphasized. A large portion of the work is classified, but such a restriction has not eliminated any field from discussion, although limiting the amount of detail it is possible to present. The development of high temperature alloys from powders and porous metals for cooling will be discussed as well as research done on molybdenum and molybdenum alloys, cermets, and intermetallics. Some studies on the utilization of cermets will be considered along with special problems that have been revealed through these investigations. Special interest in certain factors of sintered aluminum powder (SAP) makes it desirable to discuss this material although its use temperature is below the 1350°F limitation set for this paper. High Temperature Alloys from Powders In general, components made from powders for room-temperature application have been investigated with the primary purpose of taking advantage of the high production rates and economies made possible by powder metallurgy. From the standpoint of properties, the ojective of the powder metallurgist has been to obtain a product comparable to the cast or wrought product that is to be replaced. Comparisons of the properties of alloys made by powder-metallurgy methods with those of similar compositions made by casting and forging are reported in the literature.12 In many cases equivalent

Jan 1, 1955

By R. G. Treuting, W. C. Ellis

D. Whitwham, M. Mouflard, and P. Lacombe (British Council Research Fellow, Labratoire du Professor Chaudron, Vitry-sur-Seine; Inqenieur de Recherches, Labratoire de Vitry; and Maitre de Recherches, Labratoire de Vitry, Professeur Adjoint de Metallurgie, Ecole des Mines, Paris)—The authors' work is of great interest in bringing out the geometrical relations existing between twinned lattices, and for the notion of a coincidence super lattice developed from this. We should like to point out that a similar idea was put forward by Friedel8 in his book on the subject of lattice merohedrism "merihedrie réticulaire:"—When two crystals A and B are twinned with respect to a mirror plane, there exists a common superlattice, "réseau periode," which is independent of the contact surface between the two crystals. The volume V of this superlattice is a simple multiple of the volume v of the lattice of crystals A, or B, (Fig. 5). This "multiple cell" is defined by the twin plane (p q r) and a row of atoms [h k l] normal to this plane, the base being taken as the smallest unit (two-dimensional) of this plane. Two cases must be considered. First when the multiple cell, as defined, has no atom site at its center nor at the center of its faces other than (p q r), v the twinning index is defined by —. In the second v case, when one of the two above conditions does not v apply, then the twinning index is V 2v A more intuitive definition of the twinning index would be the proportion of atoms of C, which would coincide with those of C1 when the C, lattice is imagined to extend on the other side of the contact surface. In the case of cubic crystals, the twinning index

Jan 1, 1952

By O. P. Arora, M. Metzger

Single-phase aluminum containing 1 to 600ppm copper was studied in 7 to 26 pct HCl. The corrosion rate in the autocatalytic stage was resolved into a constant intrinsic component and an acdelerating autocatalytic component, and attention was focused on the part of this stage where the corrosion rate could be described by a simple empirical relation. Autocatalytic corrosion in this period was localized and its rate increased rapidly with copper content and with the strength and chlaride content of the acid. The effects of adding cupric ion to 16 pct HCI were functionally and quantitatively inconsistent with the autocatalytic rates observed. A theory of these rates was given based on the deposition in nzetallic contact with the aluminum of part of the copper introduced by corrosion. It has long been known in a general way that aluminum containing sufficient copper suffers in hydrochloric acid an autocatalytic acceleration of corrosion resulting from the introduction into the acid of copper ions and their reduction on the specimen as elemental copper, which provides cathodes of low hydrogen overvoltage.'-3 In a previous paper, this phenomenon was identified in single-phase high-purity material at copper levels as low as 20 ppm and an empirical equation describing autocatalytic corrosion rates in 16 and 20 pct HC1 was presented. In the present work the range of acid strength and chemistry studied was extended, a more accurate empirical equation for the autocatalytic rate was determined, and a theory of this rate was formulated. A major source of interest in this system is the intergranular corrosion, which is also strongly influenced by copper content,= and an objective of the present work on general corrosion was to provide a basis for studying the role of copper content in intergranular corrosion, which is experimentally much less accessible.

Jan 1, 1963

By R. J. Wasilewski

THERMAL expansion of rhenium data have been reported by Agte et al.,&apos; and Medoff and cadoff,&apos; respectively, while the linear expansion coefficient was determined by Sims et Al.3 Denoting expansion coefficients parallel and at right angle to c axis by all and Al respectively, their weighted mean should be equal to dilatometric linear coefficient of a random polycrystalline specimen. The values reported for these coefficients are tabulated below: Since these values are in poor agreement, and because of anomalous expansion behavior observed in titanium 4 and chromium, a rede termination of the axial expansion was carried out. A Unicam 19-cm-diam high-temperature camera was used, with unfiltered CuK radiation. Camera calibration was carried out using at Pt wire standarde at temperatures up to 1100oC, the variation between indicated and true temperature being within the experimental error (estimated at <3oC) above 750o C. Rhenium Johnson Matthey spectrographic standard) was vacuum annealed at 1000 oC prior to X-ray diffraction experiments. Lattice parameters were obtained by least-squares solution using the reflec- tions (1232), (1015), (2024), and (3030) for all the patterns, and the additional reflection (2133) for higher temperature (400°C and above) patterns. The relative expansion data obtained are shown in Fig. 1, lengths of the vertical bars indicating the spread in the parameter values obtained by using various combinations of three spacings from the four or five measured. The data calculated from the equation of Ref. 2 are included for comparison purposes. Several specimens were used to obtain the above data, neither of them showing a significant parameter change after completion of the high temperature runs. Some parameter data and the corresponding expansion coefficients between 25 oC and the measurement temperature are tabulated below. The comparison of the present data with those previously reported shows reasonable agreement with the results of Medoff and cadoff2 within the temperature range covered by them (up to 1000 oC). The a values are appreciably higher throughout most of the investigated temperature range. The basal expansion is—in agreement with their findings—appreciably higher than that in the direction of hexagonal axis. The expansion coefficient, al, however, decreases rather more slowly with temperature than previously reported. The expansion along the c axis up to nearly 1000°C appears in excellent agreement. However, at higher temperatures there is a marked deviation towards higher expansion, reproducible between different specimens. Furthermore, there seems to be some irregularity in the variation of all with temperature, the apparent local minimum and maximum values at 510o and 1024o C, Table II, being well outside the experimental error limits. It must be stressed that the apparent discontinuity in the c parameter expansion is still insufficient to account for the expansion value reported by Agte et al.&apos; since a total expansion of close to 2 pct would

Jan 1, 1962

By W. F. Hosford

A series of aluminum single crystals was subjected to axially symmetric flow by drawing through dies. The orientation dependence of the drawing stress, which indicates the resistance to this type of flow, compares reasonably with predictions of Taylor and of Bishop and Hill. Measured lattice rotations likewise are generally consistent with theory. The most successful analyses of the plastic behavior of polycrystalline metal and its relationship to single crystal behavior are those of Taylor1-3 and of Bishop and Hill.4-6 The purpose of this paper is to provide a critical test of some of the basic assumptions involved in these theories. Both treatments apply to fcc metals and assume the shape change of each grain in a polycrystal to be the same as that of the polycrystal as a whole. Thus for a randomly oriented polycrystal extended under uni-axial tension each grain is assumed to undergo axially symmetric flow. dey = dez = -1/2dex, deyZ = dezx = dexy = 0 [l] where x, y, and z are a set of orthogonal axes, x being the tensile axis. Although [011.] oriented grains in bcc and fcc metals may depart markedly from this ideal behavior,7,8 the assumption is probably quite reasonable for most grains. Under a uniaxial tensile stress, ox, the work dW per unit volume expended in producing an increment of axial strain dex is, dW=oxdex [21 Since this work is expended in slip, dw =STi dyi 131 where Ti and yi are the shear stress and shear strain on the active slip systems. In both analyses Ti is taken to be the same on all slip systems, and dependent only on the total prior shear strain on all systems, so dw = Tdy [41 where t is the shear stress required for slip and y is the sum of the shear strain yi on all slip systems. Combining 121 and [4] and defining M = oX/T The ratio M is a generalized Schmid factor. It relates the tensile stress required for axially symmetric flow, ox, to the basic shear stress, 7, and it also expresses the ratio of crystallographic strain, y, to the tensile strain, Ex It depends only on the orientation of the crystal. Taylor evaluated M for various orientations by finding the least value of dy/dEx which could satisfy the shape change. Bishop and Hill, on the other hand, found M by considering the relative work (1/T)dW/dEx expended by stress states which could activate enough slip systems to produce the shape changes. The results of both methods appear to be equivalent, although certain omissions were made in Taylor&apos;s original work. The orientation dependence of M, calculated by the second method,9 is shown in Fig. 1. Taylor used the average 2= 3.06 for all possible orientations to predict the tensile stress-strain curve (oxvs Ex) for a random polycrystal from the shear stress-strain curve (t vs y) of a single crystal. Changes in M from lattice rotation were neglected so points on the ox vs ex curve were simply taken at ox = 3.06t and e = y/3.06 from corresponding points on the t vs y curve. Recent extension of the analyses of Taylor and of Bishop and Hill to crystallographically textured metals has been used to relate plastic anisotropy to textures, and to predict the potential texture hardening that could result from texture control.9 Unfortunately there have been relatively few experimental tests of the underlying theory. Taylor found that the tensile stress-strain curve of polycrystalline aluminum did agree reasonably well with that predicted from a single-crystal T-y curve. Had the single crystal undergone easy glide, how-

Jan 1, 1965

By Jack L. Taylor

As expected from similar crystal structures and favorable atomic size factors, titanium, vanadium, and molybdenum are completely soluble in one another above the transformation temperature of titanium. The fl phase parameters of the continuous solid solution are shown graphically. Limiting compositions for retained fl phase have been determined. VANADIUM and molybdenum both have body-centered-cubic structures at all temperatures and, from the atomic diameter comparison factor, 3.9 pct, would be expected to form a complete series of solid solutions. The existence of complete solubility has been confirmed by work&apos; at the Jet Propulsion Laboratory. Furthermore, vanadium and molybdenum have favorable atomic size factors to form complete binary solid solutions with the B phase, high temperature form of titanium, which also has body-centered-cubic structure. Pietro-kowsky and Duwez&apos; and Hansen et al." have established the existence of the complete series of solutions in these binary systems. It would be logical, therefore, to expect that p-titanium, vanadium, and molybdenum would be completely soluble in one

Jan 1, 1957

By J. H. O’Dette

BLISTER formation on wrought aluminum products has been a matter of concern to aluminum fabricators for many years. The fact that blisters make their appearance during the final stages of fabrication means that much time and effort have been expended before it is evident that the material must be scrapped. This and the loss of production are ample reasons for embarking on a research program to find out more about blistering and possible methods of control. Many excellent papers on this subject have appeared in the technical literature in the last few years. In one of the more recent papers, Kostronl gives a fairly complete review of the problem of gas in aluminum and blistering in general. From the work of the various investigators, a general mechanism for the formation of blisters has evolved and may be summarized briefly as follows: Hydrogen gas is usually present in the cast ingot, in the atomic or ionic state, in excess of the solid solubility. At room temperature the gas atoms are relatively immobile, but at elevated temperatures they become mobile and diffuse to free surfaces where they associate to form molecules. If these free surfaces are discontinuities within the ingot then the associated gas molecules collect and build up considerable pressure until equilibrium is reached with the dissolved gas around the discontinuity. Since the solubility of the gas is proportional to the square root of the partial pressure it is evident that large pressures may be built up at the discontinuities. When the metal is rolled to sheet the pressure of the gas in these, discontinuities is sufficient to deform the surface of the sheet and form a blister, particularly when the strength of the material is reduced during the annealing. Although the mechanism of the formation of blisters was fairly well known, the actual impor- tance of the individual roles played by the gas and the discontinuities was not so well established that positive methods for control of blistering were at hand. It was the object of the investigation to learn more about the nature of the discontinuities giving rise to blistering and to develop methods of control. The investigation was carried out in three stages as follows: a) A study of the more commonly used methods of removing hydrogen from aluminum, such as fluxing and holding, and their effects on blistering. b) Location of the discontinuities giving rise to blistering. c) A study, by indirect methods, of the movement of gas in the metal and its effect on blistering, and the development of methods of blister control during fabrication. Removing Gas and Reducing Blistering by Fluxing or Holding-—The work of removing gas and reducing blistering by fluxing or holding was carried out on metal of Alcan 2s (1100) composition with an artificially high gas content. The high gas content was obtained by introducing water into the melt prior to casting; the water reacted with the aluminum forming A12O3 and hydrogen. The procedure was to raise the gas content by introducing water into an aluminum melt and using half the melt to cast one ingot immediately. The remaining metal was treated again with water to make up for the reduction in gas content during holding, while the first ingot was being cast, and then given a fluxing or holding treatment and cast into an ingot. Samples for gas determination were cast from the molten metal before and after the gassing operation; before, after, and during fluxing, and while casting. Samples were also cut from sections of the ingots. Gas determinations were made on these samples using the well known vacuum fusion technique. All ingots were hot rolled at 500°C to 0.250-in. slab which, in turn, was cold rolled to 0.040 in. sheet. The sheet was coiled and annealed for 2 hr at 500 °C and then cut into 5-in. squares which were inspected for

Jan 1, 1958

By J. W. Clark, C. T. Sims

Wrought chromium-base alloys containing yttrium, cubic monocarbides of the Ti(Zr)C type, and similay alloys containing manganese and rhenium have been melted and fabricated. Strength has been studied by hot hardness and elevated-temperature tensile and rupture measurements, low-temperature ductility by tensile testing, and surface stability by oxidation testing. In additiod, studies have been conducted of the carbide stability, and of aging behavior. The carbide dispersion generates effective elevated-temperature strength, which is further enhanced hv strain-induced precipitation. The dispersion exhibits classical dissolution and aging response. The ductile-to-brittle transition temperature of these alloys is above room temperature. The alloys reported show fairly good oxidation resistance, but nitrogen contamination can cause fortnation of a hard Cr2N layer under the oxide scale. Manganese does not appear to be a promising alloying element in chromium. In the years 1945 to 1950, the metal chromium was considered as a possible base for alloy systems due to its considerably higher melting point than superalloys, its low density, its high thermal conductivity, and its apparent capacity for strengthening. However, this interest in chromium was short-lived. It was found difficult to melt and cast, to be exceptionally sensitive to the effect of minor imperfections, to have a lack of ductility at both room and elevated temperatures, and to be subject to a deleterious effect of alloying elements upon the ductile-to-brittle transition temperature.&apos; Since then, chromium, as a practical alloy base, has remained virtually unstudied. Further, purposeful ignoring of chromium has been promoted by statements that its bcc structure would not allow it to be strengthened to useful values, when compared to the "austenitic" alloys.2 Recently, a new look has been taken at chromium-base alloy systems. Study of the literature will show that chromium, providing some of its disadvantages could be eliminated or minimized, actually has a rather attractive potential as an alloy-system base. Analysis of rather scattered data suggests that chromium is quite capable of being strengthened to high levels. Also, significant strengthening of its two sister elements in Group VI-A, molybdenum and tungsten, has been demonstrated in a number of commercial and exploratory alloys. Chromium should be similar. Since chromium does not readily form a volatile oxide like tungsten or molybdenum, it offers a much higher probability of giving birth to alloy systems with useful oxidation resistance. Concerns about possible high elemental vapor pressure have been mitigated by recent data.3 In addition, the physical properties exhibited by chromium are attractive for application as a high-temperature structural material. For instance, its thermal conductivity varies from 49 to 36 Btu-ft/hr-sq ft-°F over its range of usefulness (which is two to four times higher than most superalloys), its density is about 7.2 g per cc (20 pct less than most nickel-base alloys), its coefficient of thermal expansion varies from 4 to 8 x 10-6 per OF, and it has a relatively high modulus of elasticity, approximately 42 x 10&apos; psi.4 Alloying studies on a chromium base in the past have usually encompassed rather sweeping solid-solution alloy additions for strengthening. This is not consistent with contemporary alloying practice in Group VI-A. For instance, molybdenum, also in Group VI-A, is primarily alloyed for strength improvement by use of heat-treatable carbide dispersions.5 Chromium and molybdenum are similar in their chemical activity and other properties. Thus, strengthening of chromium by carbide dispersions was studied. Chromium-base alloys are plagued with room-temperature brittleness, although high-purity unal-loyed chromium can be made ductile.4,8 Use of yttrium as a scavenger has done much to improve ductility and resistance to nitrogen embrittlement in chromium systems,7 so it was utilized in this program. It has also recently been found8 that small rhenium additions (1 to 5 pct) create improvement in the ductility of Type 218 tungsten wire. This is apparently related to the remarkable effect of rhenium additions near its terminal solid solubility in all Group VI-A metals.9&apos;10 Investigation to establish if dilute concentrations of rhenium would also be effective in chromium appeared to be logical for this program. Since rhenium is too expensive to be practical in alloys for application as structural components, ductility improvements through solid-solution alloying were also sought by substitution of manganese for rhenium; manganese, like rhenium, exists in Group VII of the periodic system. The optimum amount of carbide dispersion for chromium-base alloys was obtained by analogy with molybdenum. Strengthening in molybdenum is achieved by use of Ti-Zr carbide dispersions. A

Jan 1, 1964

By J. L. Lamon, W. Crafts

P. Coheur and L. Habraken—We read this paper with great interest and are glad to congratulate the authors for their valuable work, supplying an important contribution to the mechanism of tempering on the carbides in vanadium steels. We are in a good position to appreciate this work since we have been studying, for more than a year, Cr-Mo steels of a composition similar, but less highly alloyed (namely 0.1 pct C, 3 pct Cr, 1 pct Mo). Our results are quite in concordance with the authors&apos;, however, we wish to point out that it is very interesting to use equally the electron microscope in order to observe the variations of microstructure in steels. We have studied simultaneouslv the evolution of the carbides in situ with the electron microscope, and, after extraction, again with the electron microscope, and then with X-rays. The first results which we have obtained have been communicated at the Congress of Delft (July 1949) and at the "Journbes de la Metallurgie" in Paris (October 1949). These may be summarized as follows: After tempering with varying either the tempering temperatures or the tempering times, the carbides show two evolutions. The first one is connected to the carbides existing in the steels, principally in the boundaries of the grains. For some groups of steels these carbides may coalesce and for other groups they may

Jan 1, 1951

By G. W. P. Rengstorff, R. B. Fischer

A study was made of the effect of impurities on the bend ductility of cast molybdenum. High purity molybdenum was repared by re-melting under high vacuum. The ductility of "transverse-grain" specimens indicated that intergranular brittleness decreased with an increase in purity of the metal. THE production of as-cast molybdenum with high ductility at room temperature would make working of the metal easier and increase the usefulness of the as-cast metal. Furthermore, a .knowledge of the factors that influence the ductility of as-cast molybdenum might be applied to the problem of making fusion weldments having satisfactory room-temperature ductility. Individual grains of commercial as-cast molybdenum are slightly ductile at room temperature. However, the presence of carbides at the grain boundaries may cause the metal to fracture in a brittle manner. This behavior has been discussed.&apos; The amount and distribution of the impurities in as-cast molybdenum would be expected, from previous research on the metal, to have considerable influence on its ductility. Some effects of oxygen and carbon on the mechanical behavior of the metal were discussed by Parke and Ham,2 Woodside,3 and Zappfe. Landgraf, and Worden.4 Parke and Ham2 found that, if a sufficient number of molybdenum oxide particles were present at the grain boundaries, the intergranular cohesion was reduced to the extent that arc-melted molybdenum would rupture intergranularly during hot forging. They also found that if the oxygen content was less than 0.003 pct, the cast molybdenum was hot forgeable. It is suspected, however, that forgeable molybdenum may contain a small amount of oxide that could reduce the ductility of the as-cast metal at room temperature. Also, there is the possibility of the unfavorable distribution of other impurities having a detrimental effect on the ductility of cast molybdenum. The results of a study of the influence of purity on the room-temperature ductility of cast molybdenum are presented here. Vacuum Arc-Melting to Produce High Purity Mo One way of determining the effect of impurities on the ductility of molybdenum is to prepare and test metal as free of all impurities as possible. Accordingly, the present investigation was undertaken with this in view. Arc melting in high vacuum (less than 0.1 micron of mercury) was chosen as the method for reducing the impurities below the concentrations occurring in commercial molybdenum. Commercial arc melting of molybdenum is carried out at about 50 microns pressure. During the arc melting, carbon and oxygen in the metal react to form carbon monoxide. By virtue of the vacuum process, the partial pressure of carbon monoxide is maintained at such a low value that the reaction greatly lowers oxygen and carbon contents. An excess of at least 0.03 pct C is used in commercial arc melting to insure that the oxygen content will be below 0.003 pct. The excess carbon remaining after the deoxidation step forms carbides on freezing. Some of the carbides precipitate at the grain boundaries and, as will be shown, have an unfavorable effect on the room-temperature ductility. In the present work, only the small amount of carbon (0.003 pct) contained in the commercial powder-metallurgy molybdenum used for melting stock was present. Partial removal of oxygen from the melt probably occurred as the result of the volatilization of molybdenum oxides, or by distillation of oxygen at the high melting tem-

Jan 1, 1953

By A. E. Gorum, J. Washburn, E. R. Parker

Experimental evidence was obtained in support of the idea that cleavage fracture can be initiated by dislocation pile-up. The high ductility of MgO crystals when tested in bending comPared to their relative brittleness in tension was explained on the basis that large pile-ups are more likely in a tension specimen. CLEAVAGE fractures have been a problem of major concern for many years. A number of large steel structures have failed in a brittle manner, usually suddenly and without warning; often the failures occurred for no obvious reason and at nominal stress levels well within the generally accepted range. A great deal of data have been collected about factors that contribute to failures,1 but the physics of the fracture process has never been revealed. cottrel12 has recently developed a theory of brittle fracture in ductile materials which was based upon the concept that dislocations moving on two intersecting planes can unite to form a crack nucleus. This theory accounts for the known effect of grain size and for the effect of testing temperature. There has, as yet, been no experimental evidence published that would substantiate this or the earlier theories based on stress concentrations due to piled-up dislocations. The study reported herein was conducted to obtain information that would either substantiate or disprove the

Jan 1, 1960

By V. Damiano, M. Herman

CELLULAR substructure observed in metal crystals grown from the melt. has been studied extensively&apos;-&apos; and is attributed to the existence of a constitutionally supercooled zone in the liquid ahead of the solidifying interface. The mathematical description of this process has been given in terms of the concentration of solute in the liquid phase, the rate of solidification, and the temperature gradien.t in the liquid as the only variables.5 This technical note presents some evidence of 1) the effect of crystal orientation on some aspects of cellular growth, and 2:) the degeneracy of these cells into dislocation arrays. The zinc single crystals used in these studies were alloyed with cadmium sufficient to produce the constitutional supercooled cellular substructure. Crystals containing 0.05 pct Cd exhibited substructure formation for a growth rate of 10 cm per hr and a temperature gradient of 15°C per cm in accord with the theory. The growing liquid-solid interface was examined after we liquid had been decanted away in a fashion similar to that described by Rutter and Chamers.&apos; The cellular substructure was also observed after polishing and etching the surface directly behind the decanted interface with a solution of HNO, and water. Fig. 1 is a photomicrograph of a typical polished and etched surface revealing substructure, the cleavage plane, and twins. The crystal has been grown with its basal plane parallel to the direction of growth and the plane of the micrograph is per-

Jan 1, 1960

By M. N. Shetty, A. C. D. Chaklader

RECENTLY, it has been demonstrated that a considerable densification and interparticle bonding can be achieved if a pressure is applied to a powder compact while the material of the compact is undergoing either a decomposition reaction&apos; or a polymorphic transformation.&apos; The term "reactive hot pressing" has been coined to identify this process in which a phase change is combined with pressure to achieve interparticle bonding. This process is based on a principle which postulates that there is an enhanced reactivity and mobility of the molecular species at the phase-transformation temperature and this effect is utilized for interparticle bonding in powder compacts. This note summarizes the results obtained in an attempt to utilize this technique to produce ceramic-metal composites. In this case, a decomposition reaction of a compound (which after decomposition yielded an oxide) was used to achieve interparticle bonding in ceramic-metal composites. The reactive hot pressing was carried out in a Phillips induction heating unit, using either a graphite or a high-temperature steel die which functioned as both the susceptor and the hot-pressing component. The die was heated to the desired temperature in a helium atmosphere. All cermets produced by this technique were based on alumina as the ceramic phase. Different metal phases such as iron, copper, and chromium were used to study the effect of varying the metal phase on the properties of the composite. a Mono-hydrate (Boehmite) was mixed with different proportions of metal powders (-325 mesh) in dry condition in a mortar and pestle. No special precautions were taken for proper mixing. The mixtures were then compacted into a cylindrical form having an approximate dimension of 1 cm in diameter and 1 cm in height. For this compaction an ordinary

Jan 1, 1965

By L. S. Birks

The bainite transformation in a 3.5 pct Ni-1.25 pct Cr steel was studied under various conditions of cooling and stress. Several characteristics may be specified: 1) transformation in the bainite region (925° to 575°F) is very little affected by the manner of cooling from the austenitizing temperature at 1600°F to 575°F)tothe upper limit of bainite transformation at 925°F; 2) starting time for the bainite transformation is the same order of magnitude for either isothermal transformation or continuous cooling, but the rate of transformation is somewhat greater for isothermal transformation; 3) tensile stress accelerates both isothermal and continuous cooling transformation, and 32,000 psi stress changes the form of the isothermal transformation diagram to correspond in appearance to the continuous cooling diagram; 4) transformation for nonlinear, continuous cooling may not be determined directly from the linear, continuous cooling transformation diagram, but may be predicted by assuming first that the fractional amount of austenite transformed in a given small temperature interval depends on the approximate linear cooling rate during that temperature interval and then by summing stepwise over the whole temperature range. IN a previous publication&apos; an X-ray spectrometer was described with which the X-ray diffraction from a specimen could be observed continuously under controlled temperature and tensile stress. This instrument has now been applied to a study of the austenite-bainite transformation in a Ni-Cr steel for both isothermal and continuous cooling conditions, with and without stress. Certain characteristics of the transformation lead to a method of predicting the amount of transformation to be expected at a given temperature for any type of cooling curve. Material and Specimen Preparation The steel chosen for the investigation was a Ni-Cr steel having the composition in the following percentages: 0.30 C, 0.27 Mn, 0.019 P and S, 3.50 Ni, and 1.25 Cr. In order to fabricate specimens suitable for the X-ray spectrometer, a 1/4 in. plate was ground down to 0.060 in. and then cold rolled to about 0.035 in. Next it was heat treated by quenching in oil from 1650°F and tempering at 1200°F for 1 hr. Then it was etched in dilute nitric acid to reduce its thickness to 0.014 in. and cut into blanks in the shape of flat tensile specimens 3 1/4 Vi in. long, 7/16 in. wide, with a notch % in. long and 7/32 in. wide; see Fig. 1. X-Ray Technique Since the X-ray spectrometer has been described in detail elsewhere,&apos; only a brief outline of the principles will be repeated here. A focusing, pow- der-diffraction arrangement&apos; was used, as shown schematically in Fig. 1, and the specimen was mounted vertically in a vacuum furnace (not shown in the figure). The X-rays, moving in a horizontal plane, enter and leave the furnace through beryllium windows. As shown in the figure, X-rays diverging from the line source A are diffracted by the specimen B and converge at the detector slit C. The detector D and the slit C may be set at the proper angle in the horizontal plane to receive X-rays diffracted by either the face-centered phase (austenite) or the body-centered form (ferrite, bainite, martensite). The specimen is heated by electrical conduction between connectors E, and E,, and a Pt—Pt-10 pct Rh thermocouple spot-welded to the center of the notched region on the side away from the X-ray beam indicates the temperature continuously on a Brown recorder. Temperature control is exercised manually with a variable transformer on the input to E,-E,. Any desired time-temperature relationship is easily obtained by first drawing the desired curve on the temperature recorder chart and then adjusting the variable transformer during the run so that the thermocouple

Jan 1, 1957

By J. J. Gilman

Examination showed that characteristic cleavage step patterns are observed on the cleavage surfaces of undeformed, slipped, bent, twinned, compressed, and indented zinc crystals; and the effect of temperature is discussed. Dimples were seen to produce cleavage steps in a treelike pattern in otherwise undeformed crystals. The steps seem to originate when cracks intersect screw dislocations. IT has been known for a long time that the path of fracture in polycrystals may be discontinuous (see Jaffe, Reed, and Mannl for review). Recently, Kies, Sullivan, and Irwin2 have proposed, and given evidence, that crack propagation is discontinuous within individual crystals as well. Other evidence has been given by Low.&apos; When discontinuous cracks within a crystal join together to make a macrocrack, the lamellae between each set of two cracks are torn somewhere, forming small cliffs. These cliffs appear as lines when the cleavage surface is observed microscopically.4,5 The lines have been called vein, tree, and riverlike markings by various authors, and they have sometimes been mistaken for fissures. The descriptive term cleavage steps is used in this paper. Cleavage steps vary in height over a wide range of values, from molecular dimensionsG to lor. and larger. Kies, Sullivan, and Irwin,2 as well as George,&apos; have shown that the gross cleavage step patterns for plastics, polycrystalline metals, and for mono-crystals are sometimes similar. Thus, they depend mostly on the mechanical variables that prevail during cleavage and are relatively insensitive to the structure of the material. For example, parabolic markings2,7,8 sometimes result when cracks open up ahead of, and not coplanar with, the main crack front. If the advance crack has the same velocity as the main crack, their intersection line is a parabola, otherwise it is a hyperbola or an ellipse. The patterns are strongly affected by differences in crack velocities. This results in chevron patterns which point to the place of origin of the main crack. It is the purpose of this paper to demonstrate the existence of a mechanism of cleavage step formation which is a continuous rather than a discontinuous process. Also, certain characteristic step patterns are described, and the strong effect of temperature is shown. The specimens were zinc monocrystals (grown from 99.999+ pct pure metal). These were cleaved at room temperature and at — 196°C. Results and Discussion Cleavage step patterns are highly variable from point to point on a given specimen, as well as from one specimen to another. Although the patterns shown in the photographs are typical, they have been selected for graphic illustration. Figs. la and lb compare undeformed crystals that were cleaved at —196 °C and room temperature, respectively. Cleavage at room temperature (Fig. lb) resulted in a higher density of high steps (dark black lines) and enhanced the visibility of the fine background markings. Deformation by simple slip caused no marked change in the step patterns until the glide strain reached about 1.0. But, as Fig. lc shows, the density of high cleavage steps was greatly increased by large glide strains. Corrugations lying perpendicular to the slip direction may also be seen in Fig. lc. These are caused by deformation bands. The cleavage resistance of the crystal of Fig. lc was very high compared to undeformed crystals (estimated by the force on a needle required for cleavage). Striking and varied cleavage step patterns were observed on bent crystals. Two characteristic patterns that were observed on crystals bent at 25°C, and cleaved by reverse bending at —196°C, are shown in Figs. 2a and 2b. The first, Fig. 2a, consists of V-shaped lines similar to the parabolas of other materials2,7 Fig. 2b shows a pattern that is the equivalent of Fig. la, consisting of faint background lines with a few higher step markings. Cleavage of bent crystals at room temperature resulted in Figs. 2c and 2d. Now, the cleavage step lines show a strong tendency to follow one of two perpendicular paths. In Fig. 2c (bent once), many of the cleavage step components that lie parallel to the bend axis are assembled into irregular lines. In Fig. 2d (bent twice), the cleavage steps again tend to consist of two perpendicular components, but neither of the components is assembled into lines. Also, the step density is higher.

Jan 1, 1956