By C. H. Ma, J. S. Makris

This paper describes a modified X-ray diffraction microscope wzethod based on the general principles of Berg-Bawett's Method, Lang's Method, and Woosters1 Technique. This new method may be used for stationary or oscillatory photomacrographs, with both reflection and transmission techniques. In the stationary technique, a small point-source of a divergent X-ray beam of white radiation is used; in the oscillatory technique, a monochromatic divergent beam is employed. The chief advantages of the method described herein are that only approximate alignment of the Bragg angle -of-interest is needed during exposure, and that a large portion of a crystal-specimen surface can he irradiated. In recent years, the study of dislocations through X-ray diffraction microscope techniques has received considerable attention as concerns the per,fection of single crystals. Very promising results have appeared in the literature.'-' These techniques are very useful when the dislocation density of a crystal is near 105 per sq cm or lower. The principle of X-ray diffraction microscopy is based on the differential effect of X-ray primary extinction between the distorted parts and the perfect parts of a crystal. When an X-ray beam impinges on a set of planes of a crystal at the correct Bragg angle, diffraction of X-rays will occur with a 90-deg phase shift of the diffracted beam. This once-diffracted beam still forms the correct Bragg angle with the planes ahead of it, if the planes are not distorted. Thus, part of the strength of the once-diffracted beam is rediffracted and the beam continues to travel in the direction of the primary X-ray beam. This twice-diffracted beam not only takes away part of the strength of the once-diffracted beam, but also causes destructive interference with the primary beam because it now is exactly 180 deg out of phase with the primary beam. As the primary beam goes farther and farther into the crystal, its intensity is continuously weakened. Asa result, the ultimate X-ray diffraction power of a set of undistorted planes is largely extinguished. This phenomenon is called primary extinction.1,2'4 If the set of planes ahead of it is distorted, the once-diffracted beam will have less chance to be rediffracted, because it could not meet the exactly correct Bragg angle for rediffraction. If a part of the beam does rediffract, this twice-diffracted beam is not exactly 180 deg out of phase with the primary beam, and thus it causes less destructive interference. As a result, the registered X-ray diffraction power of the distorted part of a crystal appears stronger than that of the perfect part. Thus, point-by-point contrast of a diffraction image is theoretically possible from a crystal containing dislocations. Two most popular X-ray diffraction microscope techniques today are Berg-Barrett's Method and Lang's Method. Both of these techniques require a

Jan 1, 1964

By N. A. Tiner, Saara Asunmaa

The early stages of nucleation of vacuunz-deposited gold coatings on electropolished surfaces of pure nickel and binary alloys of Ni-A1 and Ni-Ti have been studied, employing carefully controlled temperature and vacuum conditions. The preferential nucleation of gold on slip-plane edges on the crystal surfaces gave rise to a very pronounced decoration effect which was used in studying the morphology of the pain boundaries, etch pits, and slip planes on crystal faces. Characteristic surface patterns were observed with local dimensional variations. Most pronounced geometric patterns were ohserved in the pain boundaries of nickel and on the crystal faces of Ni-A1 alloy. The nucleation behauior of gold indicates contamination on the Ni-T1 alloy and the getter properties of titanium are presented as a tentative interpretation for the detected contamination. The markings and imperfections on cleavage surfaces of crystals have long been observed by optical microscopy.1,2 Surface-replica techniques are also used to detect the smallest steps and structural details on crystal surfaces by electron microscopy. Recently, Bassett3-5 and Sella, Conjeaud, and Trillat 6 have shown that, when gold is deposited onto a rocksalt cleavage surface, there is preferential nucleation at steps and slip-plane edges on the crystal surface. This gives rise to a very pronounced decoration effect which is invaluable for revealing the lattice steps on a cleavage surface. According to Bassett,3 gold atoms arriving during vacuum evaporation at the crystal surface have a certain mobility on the surface after arrival, particularly at elevated temperature. If a significant

Jan 1, 1964

By D. Kuhlmann-Wilsdorf

A new theory of work hardening is developed which rests on only a few simple principles and is applicable to a wide variety of materials and dislocation structures. It explains, qualitatively, the general characteristics of the three-stage shear stress-shear strain curve of fcc metals, as well as the most important features connected with easy glide. The value of, the work-hardening coefficient in stage 11, is derived quantitatively, from first principles, and is shown to be insensitive to many changes in detailed dislocation behavior. The low rate at which energy is stored during mechanical working in stage 11, the dependence of slip line length on stress, and the so-called Cottrell-Stokes law are explained. Although the theory is primarily developed for fcc metals and alloys, it is largely applicable also to some other materiuls, and in particular apparently to poly crystalline simple steels in theh linear range of hardening. FOR pure fcc metals and alloys, after many different pretreatments and under a great variety of testing conditions, the well-known three-stage work-hardening curve is commonly observed. Moreover, the work-hardening coefficient in stage 11, 011, bears an almost constant relationship to G, the modulus of rigidity, such that K = G/Brr" = 300, within a factor of about 2 either way. The very fact that the three-stage curve and the value of K are so very persistent, can hardly be understood except on the assumption that some quite simple phenomena are responsible. In this light all available theories of work hardening must be judged unsatisfactory: Each of them is based on some quite specific dislocation model, while it is known that metals with similar values of K may have widely different dislocation structures, for example, dislocation tangles in the case of pure fcc metals, and piled-up groups of dislocations in a-brasstype alloys. Thus, while a particular theory might conceivably represent a special case with a reasonable degree of accuracy, it cannot possibly have illuminated the underlying principle. Another severe criticism applying to the presently most widely discussed theories is that they employ empirical or even quite unexplained parameters in order to arrive at a numerical value of K. This indicates that some vital aspect of the work-hardening process has remained unexplained. In the present paper, a new theory of work-hardening is developed which does not suffer from the above shortcomings. It is derived from first principles, and is founded on the realization that the underlying causes for the three-stage work-harden- ing curve and for the persistence of the numerical value of O,, must be few and simple. As a first step it is shown herein that the experimental oklservations on "easy glide" can be explained on the assumption that in this stage dislocations multiply, beginning in a number of restricted area:;, and from there penetrate into crystal regions still substantially free of glide dislocations until a quasi-uniform dislocation distribution has been established. During "easy glide", the resistance to the movement of the foremost dislocations, advancing into still largely a dislocation-free regions, is believed to control the flow stress. This resistance is determined by various factors, among them the reaction of the dislocations against bowing-out into loops, which is due to their line tension. Without such bowing-out no dislocation multiplication would occur, but the corresponding contribution to the flow stress stays practically constant all through stage I. According to the present theory, stage TI begins as soon as there are no more areas left into which newly formed dislocations have not yet penetrated, i.e., as soon :is a quasi-uniform dislocation density has been attaned. Regardless of how, in detail, the dislocations should happen to be arranged at the end of "easy glide", whether in pileups or tangles, on one glide system or on several, the stress necessary to overcome the line tension of the segments must now increase, because the dislocation density increiises while the average free dislocation length decreases. It is argued that all other contributions to the flow stress stay at about the same level as in stage I, and that the said increase in the stress necessary to bow out dislocation segments into loops is responsible for the major part of work hardening in stage 11. Stage TII of the stress-strain curve is explained by largely follouing the ideas of Seeger and his co-workers; however, it is pointed out that the start of stage m may on occasion indicate the onset of "conservative climb" instead of cross slip. Indirect evidence indicates that linear work hardening persists even under the profuse action of cross slip, but at a lower rate. Only when, in addition to cross slip, climb operates extensively, does the work-hardening rat,. drop sharply, ultimately down to zero. BRIEF SURVEY OF EXPERIMENTAL EVIDENCE The stress-strain curve of crystals of many different substances are qualitatively similar. No significant permanent plastic deformation takes place below the so-called "critical resolved shear stress". As the applied stress is raised beyond this level. yielding occurs with little or no work hardening and

Jan 1, 1962

By H. H. Hausner, H. S. Kalish

IN recent years zirconium and beryllium have become of great interest because of their special properties. Zirconium is known for its remarkable ability to absorb the gases oxygen, nitrogen and hydrogen, has extensive use as a getter in electron tubes and has indeed become the primary metal in the manufacture of photoflash bulbs. Beryllium is of interest because it is light metal and as such could supplement aluminum and magnesium in light metal applications. The late development of zirconium ductile at room temperature produced by both the iodide and calcium reduction methods has stimulated frequent articles on this metal in the recent literature. Beryllium is so closely akin to zirconium crystall-ographically that some investigators are of the opinion that beryllium should be ductile at room temperature if it were pure enough. The crystallographic relationship of beryllium and zirconium, the interest created in Be-Zr alloys where the zirconium is believed to function as a remover of solid solution gas in beryllium and thus increase the ductility of the beryllium rich alloy, and the amenability of these metals to powder metallurgy methods stimulated this approach to an investigation of the system Be-Zr. Preliminary work showed that a zirconium compact melted when pressed in contact with a beryllium compact and sintered at 1250°C, without any apparent final bond between the two. A search of the literature revealed nothing pertinent about the Zr-Be system or about any zirconium - beryllium alloys. In 1936 Misch³ vaguely identified the compound ZrBe2 and reported that it has a deformed cubic structure. Two patents," , were issued to Mach-lett Laboratories in 1943 and in 1946 regarding the addition of small amounts of zirconium to beryllium in order to improve the ductility of beryllium so that it may better be used for X ray windows. In considering the alloy formation of beryllium with other metals Raynor thought it unlikely that zirconium would have any solid solubility in beryllium. From this indefinite information nothing could be ascertained about the possible use of Zr-Be alloys or the use of these metals intimately. A brief preliminary study of the system Zr-Be by powder metallurgy methods was undertaken to provide regions for more intense studies of Zr-Be alloys and as a guide to a formal phase diagram determination. The investigation described in the following pages was completed in less than three weeks. The usefulness of this rapid method to facilitate phase diagram studies and new alloy investigations will be shown. Materials and Procedure Zirconium powder was produced from crystal bar stock of high purity supplied by Foote Mineral Co. The crystal bar was converted to hydride at 730°C, crushed, and the hydride decomposed in purified argon at 850°C. 60 pct of the powder passed through a 325 mesh screen, 40 pct of the powder was —140 mesh, +325 mesh and the average particle size of the total was 8 to 12 microns. The beryllium powder was used as re-

Jan 1, 1951

By N. Brown

From the theories of flow and fracture it is shown that the difference in reciprocals of the transition temperatures (OK) is a quantitative measure of temper ernbrittlement. Experimental data are given which support this conclusion. STUDIES of temper embrittlement have been made with various viewpoints; some involved a study of the kinetics of the reaction,',2'" others were concerned with changes in the mechanical properties," . and still others investigated the structural differences between the embrittled and unembrittled states by means of the microscope," -ray ,' measurements of electrode potential," and electrical resistivity." In all these studies, the difference in impact properties was the criterion for distinguishing between the embrittled and unembrittled states. By common agreement the difference in transition temperatures is now taken as a measure of the degree of embrittlement, and this measure is used as the quantitative measure upon which studies of the phenomenon are based. Vidal and Jolivet"' suggested that the degree of embrittlement was the same whether measured by impact or by a slow bend test. Their conclusion was based on tests at constant temperature. Jaffe and Buffum" using the impact and slow bend test showed that, for a given degree of embrittlement, the difference in transition temperatures varied with the method of testing. Hultgren and Chang" showed that the difference in transition temperature produced by the V-notched Charpy impact test was not the same as the value produced by the keyhole-notched impact test. This is a very fundamental point because there can be no true measure of temper embrittlement unless it is invariant with respect to the test method. Theory The purpose of this analysis is to show how the transition temperature depends on the stress distribution and the state of the material. The criterion for fracture may be stated as follws: where iF is some function of the principle stresses and F is a critical condition depending on the state of the metal. Similarly yielding occurs when Where is another function of the prin-ciple stresses and Y is a critical value depending on the state of the material. There is some controversy as to the exact form of the function f,.(u,, u,, us) but most experimental data give the following criterion:= where 8, and 6, = 21 or 0. Combinations of 6, and 8, give the various criteria such as the normal stress, the hydrostatic tension, and the maximum shear stress laws. Agreement is general that the octahedral shear stress law adequately describes the yield condition. where the bracketed factor will be called the design factor and depends on the stress distribution. Whether the metal decides to yield or fracture is given by the condition that The effect of temperature and strain rate upon Y has been studied by various investigators, It has been shown by MacGregor and Fisher" that

Jan 1, 1955

By R. E. Ogilvie, J. I. Goldstein

The a and y solubility limits in the Fe-Ni phase diagram have been redetermined at temperatures above 500°C. Both a diffusion-couple and a quench and anneal technique were used. The solubility limits were measured with an electron-probe micro-analyzer. The nickel concentration at the phase boundary is increased below 700°C and the a solid-solubility range is much larger than had been previously measured. The solubility limits are also extrapolated to 300°C. It is suggested that the solubility of nickel in a FeNi reaches a maximum in the temperature interval 400o to 500°C. THE equilibrium diagram has been of great use in the field of meteoritics, where the phase relations between kamacite (a) and taenite (?) in metallic meteorites can be described by means of the Fe-Ni diagram. The study of metallic meteorites by electron-probe microanalysis has cast some doubt on the accuracy of the presently available Fe-Ni diagrams.1, 2 Recent thermodynamic studies of the Fe-Ni system also suggest that the diagram may be in error.3 For these reasons the high-temperature (800o to 500°C) part of the diagram was redetermined. INTRODUCTION The currently accepted Fe-Ni diagram is that of Owen and Liu.4 Above 910°C, there is a region of complete solid solubility, ? (fee). Below 910°C, the a (bee) phase is stable in pure iron. The effect of increasing amounts of nickel is to stabilize the y phase. The phases that form when Fe-Ni alloys are heated or cooled bear little relation to the equilibrium diagram. If an alloy is cooled from the y state and held at a temperature within the a + y field, no evidence has been found for the occurrence of the y - a transformation.5 If the alloy is cooled to low enough temperatures the y phase breaks down into a supersaturated bee phase called a2. In fact, in alloys over 27 pet Ni the y phase is retained at room temperature.6 The a, phase has the same composition as the original y. The temperature at which a2 forms, the M, temperature, has been determined experimentally.' A state of equilibrium can be approached by cooling below M, to form a2 and then reheating the alloy into the two-phase region of the diagram. The y phase will then begin to precipitate out of the a2 phase and grow. The growth of the phase, however, is quite slow. Using the interdiffusion coefficients -Da of Goldstein et al.,8 it is estimated that it takes about 1 year to grow a 10-µ-wide region of ? at 700°C in a 5 pet Ni alloy. Owen and Liu4 used the technique just described to form the equilibrium phases. The phases present were determined by means of X-ray analysis. The accuracy of their diagram depends on the number of alloys available near the phase boundary at a given temperature. In this study two different techniques were used to determine the a/a + ? and ?/a + ? solubility limits. The inherent accuracy of both techniques was greatly improved over that used by previous investigators because the phase-boundary compositions were measured with an electron-probe microanalyzer. PROCEDURE The two methods used to determine the Fe-Ni diagram are the diffusion couple (D.C.) and the quench-and-anneal (Q.+A.) techniques. In the first method, diffusion couples whose diffusion path goes through a two-phase region of the phase diagram were used. A description of the technique used for making the diffusion couples has been described in a previous paper.' After the diffusion treatment a discontinuity in the resultant concentration vs distance profile was measured. The nickel concentrations in the a and ? phases at the interface of the discontinuity are the solubility limits of the a and ? phases in the phase diagram at the diffusion temperature. If the interface com-

Jan 1, 1965

By J. H. Brophy, A. L. Prill, H. W. Hayden

An error lzas been found in the conventional way of determining the time exponent of linear shrinkage for the solution-precipitation stage of liquid-phase sintering. Large amounts of shrinkage due to initial rearrangenzent result in erroneously low exponents and tni si dentification of the rate-controlling process. Two alternative, mathematically correct, methods of calculation are applied to existing data on Fe-Cu, WC-Co, and Tic-Ni-Mo. This results in reidentifi-cation of the rate-controlling process and somewhat better agreement with related data. In each case the solution-precipitation process is solution-controlled and not diffusion-controlled. THE liquid-phase sintering process has been the object of a considerable amount of research for many years. Linear shrinkage vs time data at various sintering temperatures have been used recently in an attempt to identify the prevailing mass-transport processes in a number of metallic and nonmetallic systems. There is an analytical error inherent in the methods previously used for handling data during the "solution-precipitation" stage of shrinkage which must be recognized before the correct rate-controlling processes can be determined. It is the purpose of this paper to show how the error has affected previous conclusions and to suggest corrections. A number of mechanisms have been proposed to explain experimental observations during sintering in the presence of a liquid phase. The earliest of these is due to Price, Smithells, and williamsl who attributed the observed growth of the solid phase to the simultaneous solution of smaller particles and growth of larger particles. From the work of Lenel et al.2,3 and Gurland and Norton4 has come the suggestion that the liquid-phase sintering process may be divided for analysis into three steps: 1) rearrangement upon formation of the liquid phase; 2) solution and reprecipitation of the solid phase in the liquid; and 3) "coalescence" or a final stage of sintering, characteristically slower than the solution-precipitation process. The sequence of steps is shown schematically in Fig. 1. Kingery5 presented a thermodynamic and kinetic analysis of the first two "stages" of the liquid-phase sintering process in which the functional dependence of lineal shrink- age on time at temperature was used to identify the rate-controlling mass-transport process. Table I summarizes the time dependences and processes considered by Kingery.5 This method of data presentation has been employed by Kingery and coworkers for Fe-CU,6 WC-Co, and a number of nonmetallic systems," and bv Whalen and Humenik for Tic-Ni-Mo and Fe-cu.8 In each of these studies, the rate-controlling step during the "solution-precipitation" stage was identified from the slope of the curve in that stage on a logarithmic plot such as Fig. 1. However, in all of the previous studies, at a certain composition, relatively large amounts of shrinkage due to rearrangement preceded the solution-precipitation stage. Under these conditions, the larger the amount of rearrangement shrinkage the

Jan 1, 1965

By C. E. Birchenall, J. R. Stubbles

ThE equilibrium between lead, lead sulfide (PbS), and atmospheres of H2 and H2S has been determined previously by Jellinek and Deubel,' and SudO.' Blbem and Kroger3,4 used Jellinek's data to calculate the sulfur dissociation pressures of PbS crystals (of

Jan 1, 1960

By J. E. Hilliard, H. E. Cook

It is shown that for systems having a miscibility gap the spinodal composition (c,) in the vicinity of the critical temperature (Tc) is related to the equilibrium composition (c,) by where cc is the critical composition. This expression is exart for the limit T — Tc and is a good approximation down to (T/Tc) - 0.9. If the miscibility gap meets the composition of the pure components THE recent theoretical treatment by cahn1,2 on spinodal decomposition of solid solutions has revived interest in methods of estimating the chemical spinodal, * i.e., the locus on a binary phase By use of the appropriate expression, the spinodal can be drawn on the Phase diagram almost by inspection with an accuracy comparable to that of lengthy calculations in which a free-energy function is fitted to the phase diagram. Satisfactory agveemenf is also obtained with spinodals comPuted from experimental free-energy curves. where G is the Gibbs free energy of the homogeneous solution and c the atomic fraction of component 2, the derivative being evaluated at constant temperature (T) and pressure (P). (These subscripts will hereafter be omitted from the partial derivatives.) If experimental measurements of G as a function of c and T are available in a single-phase region above the spinodal, then these can be extrapolated to obtain a series of metastable free-energy isotherms in the two-phase region, and from these isotherms a series of spinodal compositions can be calculated. Because the value of is very sensitive to experimental errors, an elaborate analytic procedure is required for

Jan 1, 1965

By L. F. Mondolfo

An investigation of the relationship between properties of the elements and type of binary diagram formed was conducted. It was found that, for each type of equilibrium diagram, the factors for the size, valence, electronegativity, period, melting point, entropies of fusion, and sublimation calculated for each pair of elements cover a range of values. However, these factors show sufficient relationship to the equilibrium diagram so that the correlation of several of them can be used to predict the type of diagram formed, or at least limit the choice to only a few types. ThE goal of the metallurgist concerned with alloy development has always been to find a method that predicts the properties that can be obtained when a certain metal is added to another one. In most cases a qualitative predictiton of properties can be made if the equilibrium diagram is known. However, this means that for new metals the alloy development has to start with the experimental determination of the equilibrium diagrams. Because this determination is at least as complicated and time-consuming as the determination of the properties themselves, most alloy development has taken place by trial and error, and the study of the equilibrium diagrams has followed rather than preceded the creation of new alloys. Alloy structures and properties depend on the interaction between electrons and a complete knowledge of these interactions would permit prediction of structure and properties of alloys. Unfortunately direct measurement of these interactions is extremely difficult and somewhat doubtful and only properties that depend on them can be measured easily and with certainty. Study of the relationship between properties of the elements and equilibrium diagrams is not new. Besides the well known Hume-Rothery rule of the necessity of an atomic diameter fit within 15 pct for extensive miscibility in the solid, and the wide knowledge of the effect of such factors as size, electronegativity, electron-atom ratio on solid state features,"' work relating to liquid state and liquid-solid reactions can be found in the literature. Of particular interest is the work by Axon,3 who investigated the effect of size and melting point on a selected number of eutectic and monotectic dia-

Jan 1, 1962

By David A. Thomas, John F. Peck

Sam Leber (General Electric Refractory Metals Laboratory)—I think that the authors should differentiate between the curved grains obtained by swaging and the crumpled grains produced by drawing. This can be seen most easily in the transverse sections of Fig. 2d, and is also apparent in Fig. 2c. This difference in structure indicates that the mode of deformation shou1d affect the texture, since the cylindrical texture should be maintained or even increased by the curved grains developed by swaging. Drawing, on the other hand, crumples the grains. This should convert the cylindrical texture into a normal fiber texture. This has been substantiated by a comparison of tungsten wires fabricated by similar drawing and swaging schedules. Although cylindrical textures have been detected in drawn iron wires, they were weak in comparison to tungsten wires which included swaging as part of the fabrication process. It should also be noted that large curved surfaces developed by swaging are concentric with the surface. The postulated (100) surface of these crystals would be confirmed by a (100) cylindrical texture, as was observed in tungsten. The preservalion of the (100) cylindrical texture by swaging would maintain the <100> direction in the radial position required for easy flow. This might provide a partial explanation for the decreased rate of work hardening observed in the swaged wire. J. F. Peck and D. A. Thomas (authors&apos; reply) — The authors appreciate Dr. Leber&apos;s comments on the differences in textures, microstructures, and properties of swaged and drawn wires. The evidence of the prominence and persistence of the cylindrical texture in swaged bee wires seems quite consistent with our microstructural observations and interpretations. We are presently engaged in further work to correlate the development of texture and micro-structure in drawn bee metals.

Jan 1, 1962

By T. J. Whalen and Michael

The grain shape of the carbide in nickel-bowled ad cobalt-bonded titanium carbides was studied by microgiaphic examination, and the influcence of sintering atmosphere, sintering substl-after, ami the amount of metal binder on the grain shape was determined. If was found that the Carbide grain cross sections in the nickel and cobalt cermets ranged from round to angular, depending on the sintering conditions. The spheroidization of the carbides in both cobalt-bonded and nickel-bonded titanium carbides may be attribicted to oxygen. In the course of studies on titanium-carbide base cermets, various investigators have reported on the shape of the carbide grains, and it was noticed that grain shapes were obtained which were either spheroids, or polygons with rounded or square edges. It was also noted that the shapes of the carbide grains changed with time or composition. skolnickl showed that the titanium-carbide grains. after infiltration in vacuum with nickel tended to spheroi- dize with time. The titanium-carbide skeleton was located on a beryllia plate during infiltration. Gur-land,&apos; who studied the microstructure of titanium carbide-cobalt compacts, showed that the carbide grains are round after 1 hr at 1450oC in a hydrogen atmosphere and angular after 7 hr at the same temperature. Goetzel3 has found that the carbide grains in compacts with a high binder content. 40 to 60 pet. tend to be spheroidized. whereas Blumenthal and silverman4 pointed out that the higher binder contents could yield either round or rectangular grains with rounded edges. depending on the nature of the binder. It is the purpose of this paper to present experi-

Jan 1, 1961

By D. S. Tomalin, D. F. Stein

The effect of reducing oxygen to low concentrations on the fracture of high-purity iron single crystals has been examined at 78° and 20°K. It is found that iron single crystals grown by the strain-anneal method usually contain a few occluded grain boundaries which may become embittled in the presence of oxygen, thereby nucleating cleavage fractures. High purity with respect to interstitial elements was found to inhibit twinning and evidence is presented for an orientation dependence of the resolved yield stress. Deformation occurred by slip rather than twinning at both temperatures of testing with elongations of as much as 9 pct at 20°K. THE fracture properties of iron single crystals have been observedl-3 to be a function of temperature, orientation, and purity. Allen, Hopkins, and McLennan1 demonstrated that at 78°K iron single crystals became increasingly brittle as the tensile axis approached the (001) pole of the stereographic unit triangle. Iron crystals with the tension axis near a (001) pole were completely brittle and orientations near the (011)-(111) boundary were very ductile, achieving a 100 pct reduction in area prior to fracture. Later work of Biggs and pratt2 and of Edmondson3 demonstrated that by reducing the carbon content of the single crystals the transition between brittle and ductile failure at 78°K could be shifted to orientations nearer the (001) pole. Ed-mondson went further and pointed out that any mechanism which tended to increase the yield strength of the iron (i.e., carbon addition, pre-strain) also increased the tendency for brittle behavior at 78°K. Thus by a reduction of carbon content Biggs and Pratt were able to obtain ductile behavior to within 20 deg of the (001) pole, and Ed-mondson was able to obtain ductile behavior to within 26 deg of the (001) pole. Edmondson&apos;s material had a total interstitial content (carbon, oxygen, and nitrogen) of approximately 60 ppm and, although Biggs and Pratt reported no analysis, indications were that their iron contained comparable impurities. Stein, Low, and seybolt4 purified iron single crystals to a total carbon, oxygen, and nitrogen content of approximately 20 ppm. They observed a lowering of the yield stress with this increased purity, and thus one might have expected an observation of increased ductility. Although they tested specimens of orientations which the previous workers had indicated should be ductile, the crystals failed at a 78°K in a brittle manner with little elongation. Stein noted,&apos; however, that about 90 pet of the failures could be traced in origin to occluded grains. Allen et al.1 and Edmondson3 do not report examination of their cleavage surfaces, but Biggs and pratt2 reported that microscopic examination of the cleavage surfaces of many of their specimens revealed the presence of small occluded grains. Honda and cohen6 and Keh7 have also observed the initiation of fracture at occluded grains in iron single crystals. Therefore, the additional complication of occluded grains must be considered in studying the properties of iron single crystals and the origin of fractures determined if the ductility exhibited by the crystals is to be considered meaningful. Various investigators8-12 have studied the effects of impurities on grain boundaries in high-purity polycrystalline iron. Rees and Hopkins10 showed that the addition of oxygen to low-carbon (0.002 pet) iron weakened the grain boundaries, causing a shift from transcrystalline to intercrystalline fracture and a progressive decrease on the brittle-fracture stress with increasing oxygen content. In addition, it has been shown by Low and Feustel11 that the addition of carbon to polycrystalline iron containing oxygen eliminated grain boundary brittleness. Thus, oxygen can embrittle grain boundaries in high-purity polycrystalline iron, but the addition of an appropriate amount of carbon can eliminate the oxygen-induced brittleness. The oxygen content (19 ppm) of the iron "single crystals" employed by Stein el al. was large enough to suspect impurity effects at the occluded grain boundaries. Allen et al.1 Biggs and pratt,2 and Edmondson3 may have masked any occluded grain problem in their specimens considering the relatively high carbon levels they employed. stein13 demonstrated that the addition of as little as 0.9 ppm C to previously purified (less than 5 x 10-3 ppm C) "single crystals" would increase the elongation from a few percent to more than 20 pet at 78°K and the fracture was not associated with grade boundary initiation.

Jan 1, 1965

By B. R. Banerjee

MATERIAL used throughout this investigation was high-purity aluminum (99.998 pct). The 1/2-in. cubes were cut out of a cold-rolled slab and annealed at 550°C for 1 hr before deformation. The single crystal specimen was 1 in. in diam x 0.33 in. thick, cut from a cylindrical crystal produced by cooling at about 55°C per hr in a furnace which had a convenient gradient of about 10°C in every 4.5 in. vertical crucible length. Specific data on the ten specimens studied are summarized in table I. Three types of deformation were employed: (I) compression in a hand-operated hydraulic press; (2) impact with a 7-lb sledge hammer; and (3) rolling, using a wedge-shaped specimen&apos; to obtain a gradient of deformations varying from 0 to 50 pct along the length of the wedge. Specimens were either deformed at room temperature, or first cooled in a freezing mixture of dry ice and ether at a temperature of —72°C and then deformed between steel blocks cooled with dry ice. The specimens deformed at the low temperature were ground and polished through 000 emery paper and wheels impregnated with alundum and alumina No. 1. During this entire procedure the specimens were dipped frequently in the freezing mixture of dry ice and ether in order to maintain constantly a frosty surface as insurance against overheating. All specimens were given a final electrolytic polish, using two different electrolytes* to insure that the surface effects observed were not char- acteristic of the polishing technique. With both electrolytes, the annealed specimens gave even surfaces with good polish. Several standard etchants were tried without success. The best results were obtained with an immersion etchant, developed in this connection, containing: hydrofluoric acid, 4 parts; nitric acid, 1 part; glycerine, 3 parts. Discussion of Results Typical strain markings have been observed within deformation bands, as shown in figs. 1, 2, and 4. By stereographic plotting of metallographic measurements, the strain markings within a deformation band in a single crystal of aluminum deformed by compression were found to be traces of (111) planes within a maximum scatter of 6". The edges of the deformation band were found to be traces of the (100) planes also within the maximum scatter of 6" (in agreement with previous workers). At 30 pct deformation, this scatter was considered quite normal because of the fragmentation and rotation of the crystal. This solution, based on the traces on one plane of observation is not unique, but as the planes were observed to be those normally and logically to be expected, further work in this regard was not felt to be necessary. The study of strain markings in a wedge-shaped specimen, rolled to obtain a gradient of deformation from 0 to 50 pct, revealed prominent strain markings at 25 pct reduction in thickness (fig.5). Faint and weak strain markings were visually observable up to a minimum reduction in thickness of about 12 pct. Since strain markings have been observed in other face-centered cubic metals after much smaller deformations;1, 2 and since the rate of recovery in aluminum is high, it is believed that, at lower deformations, self-recovery removes the localized strains at the slip interfaces, thus removing the source of the etching effects that give rise to strain markings. At high magnifications, strain markings sometimes seem to appear as very thin, light-banded re-gions bounded by a pair of dark edges. This so-

Jan 1, 1951

By W. D. Robertson, Raymond C. Boettner

A study was made of the change in density during the first (transient) and second (linear) stages of the creep curve of polycrystalline copper as a function of 1) stress, 2) temperature, 3) plastic strain, 4) impurity and atmosphere effects, and 5) structure, including single crystals. Voids were not observed in single crystals strained 15 pct at 500°C, or in a polycrystal-line aggregate produced by recrystallizing a single crystal, within the limit of sensitivity, Ae/e = 1 x 10-4. It appears that voids are heterogeneously nucleated at grain boundaries by an insoluble phase, or phases, which can be removed by directional solidification. The principal controlling mechanism of void growth appears to be condensation of vacancies at grain boundaries. Vacancies are transported to a boundary and condense as a consequence of the tensile stress component across the boundary, which depends on the orientation and configuration of the boundary plane and on boundary shear across ledges and other irregularities. The ultimate source of vacancies is the free surface and diffusional transport is by way of the boundary plane. PREVIOUS investigations have dealt with the nucle-ation of voids at grain boundaries under creep condition~&apos;-~ and with the connection between grain boundary voids and subsequent brittle fracture.5-7 Growth of voids during the creep process, particularly in the transient and linear stages of creep, has not been studied with the same intensity. Therefore, it seems pertinent to investigate the process of void growth with respect to the related creep curve, and the morphology of growing voids with respect to the structure.

Jan 1, 1962

By J. W. Pugh, J. D. Nisbet

THIS study of the ternary has been made as one phase of a metallurgical investigation which began nearly four years ago in the General Electric Company&apos;s Research Laboratory in Schenectady, N. Y. The objective of this program is the discovery of new metallurgical information which will lead to the development of better high-temperature materials. Combinations of the four pure base elements—iron, chromium, nickel, and cobalt—are being studied at the present time. It is essential in an investigation such as this to know as much as possible about the constitutional diagrams involved. The study of the iron-chromium-nickel system has been made to this end. Preliminary Explanation of Experimental Procedure: In all, fifty-five alloys at steps of 10 at. pct were made for the investigation of this ternary. Several ternary alloys in the chromium rich corner had to be omitted because their extreme brittleness made testing impractical. All alloys were vacuum melted with hydrogen reduction and centrifugally cast. The apparatus and technique of this process has been described in detail by Nisbet.1,2 The purity of the alloys prepared in this way is considered to be quite good. Impurities are listed as follows: Pct Carbon.............................0.02 Oxygen................................0.02 Nitrogen.........................0.005 Magnesium..................0.03-0.05 Sulphur...........................trace Hydrogen....................trace Phosphorous..................trace Silicon........................ trace After casting, all samples were given a homo-genization treatment which consisted of holding them for 15 hr at 1150°C (2100°F) and water quenching. Testing was begun with the samples in this condition. The tests employed in the study of this system were (1) dilatometer, (2) hardness versus aging temperature, (3) tensile strength and elongation versus temperature, (4) microstructure analysis, and (5) electrical resistance versus temperature. Dilatometer tests were made at the rather rapid heating rate of 1093°C (2000°F) in one hour on a Bristol-Rockwell type instrument. Hardness data were taken on specimens cooled from 204", 427", 649°, 760°, 871°, 982°, and 1093°C under conditions which are thought sufficient to bring the specimens to equilibrium in all but the cases of the very sluggish transformations. Electrical resistance data for several specimens were taken for both heating and cooling conditions in a vacuum furnace especially designed for this work by D. W. Bainbridge, formerly of this laboratory. Provisions were made for heating and cooling standard specimens at a constant rate, while autographic records of resistance and temperature were made simultaneously. Micrographs of all the alloys were made in the quenched condition. Some question may exist as to how such physical values as hardness, tensile strength, and elongation were interpreted to indicate a change in phase. Original data were recorded on physical property versus temperature graphs, each of which was made from the data of a single alloy (fig. la). From these, another series of graphs were plotted with the physical property as a function of composition for constant temperatures (fig. 1b). Sharp deviations in the slope of these composition versus hardness curves often indicate a change in phase. The example of fig. 1 will serve to describe this experimental technique. The plotting of a single point from graph "a" to graph "b," and finally to the phase diagram "c," is illustrated. The location of the point on graph "b" is indicated as point (1). If all the alloys of the A-B binary system were solid solutions at temperature X, the hardness in this curve would be expected to rise at a fairly even rate as A is diluted with B to a maximum at some intermediate value between A and B, as

Jan 1, 1951

By J. W. Pugh, J. D. Nisbet

F. B. Foley—The use of data published by Wever and Jellinghaus in 1931 to fix boundaries of the sigma phase in the Fe-Cr system, in the face of the author&apos;s own references to the suggestions of Bradley and Goldschmidt, Aborn and Bain, and Hougardy that the phase is much more extensive, and the very much more accurate work, which weighs heavily in favor of these suggestions, of Cook and Jones, published in 1943 and evidently disregarded by the authors, makes their derived ternary diagram, especially fig. 15 for 400°C, quite inaccurate on the Fe-Cr side and affects the extent of phase boundaries in the most controversial and important part of this ternary system. In commercial Fe-Ni-Cr alloys the occurrence of sigma has been observed time and time again at lower chromium contents than that of the 24 pct Cr, 16 pct Ni, 60 pct Fe alloy which is the lowest permitted by fig. 15 of practically carbonless metal. Newel1 reports sigma in 27 pct Cr-Fe even with some carbon present to be one of the greatest detriments to its extensive application, whereas Pugh and Nisbet set a low limit of 36 pct Cr for sigma in the binary Fe-Cr system. J. J. Heger—The diagrams presented by the authors do not agree with observations made on commercial Fe-Cr and Fe-Cr-Ni alloys, nor do they agree with two recent investigations made on the Fe-Cr and the Fe-Cr-Fe systems. I refer first to the investigation made by Cook and Jones1&apos; on the sigma region of the Fe-Cr system. On the basis of their results which were published in 1943, Cook and Jones established new boundary limits for the sigma and the alpha plus sigma regions. These new limits have been accepted and are incorporated in the Fe-Cr diagram that appears in the 1948 edition of the Metals Handbook. This diagram is shown here as fig. 34. As will be noted, the boundary limits of the alpha plus sigma region in this diagram extend to much lower chromium contents than do those in the diagram presented by the authors in fig. 2. These new limits indicate that sigma phase should form in an Fe-Cr alloy containing 26 pct Cr, and experience with commercial alloys confirms this finding. Indeed, recent studies on a commercial Fe-Cr alloy containing 17 pct Cr have shown sigma phase to be stable in this alloy at 550°C. I recognize that the authors&apos; work did not include studies on the sigma region; however, I believe this is a serious omission because sigma phase may profoundly affect the physical properties of these alloys and should be evaluated in any investigation which attempts to relate physical properties to the equilibrium diagram. The second investigation to which I refer is that made on the Fe-Cr-Ni system by Rees, Burns, and Cook,&apos;&apos; who used pure alloys and employed heating 17 W. P. Rees, B. D. Burns, and A. 3. Cook: Journal Iron and Steel Institute. (July 1949) 162, Part 3. p. 325. times that extend to 200 days. These investigators published their results in July 1949 and from these results constructed isothermal sections at 800" and 650°C. The isothermal section at 650°C is shown here as fig. 35. This diagram indicates sigma phase should form in a pure 18 pct Cr-8 pct Ni alloy. Although sigma phase has not been observed after 10,000 hr at 1200°F in commercial 18-8 alloys containing carbon and nitrogen, it has been observed under the same conditions in 18-8 alloys modified with titanium and columbium, both of which serve to reduce the effect of carbon and nitrogen. This section and the one at 800°C suggest that the constant iron sections which are presented by the authors, should be considerably altered, if they are to represent an accurate picture of the system. A few of the suggested alterations are as follows: In fig. 9, the section at 50 pct Fe, the gamma plus sigma region should be widened, not narrowed at 800" and 650°C. In fig. 10, the section at 60 pct Fe, the gamma plus sigma region should be widened at 800° and 650°C. In fig. 11, the section at 70 pct Fe, an alpha plus sigma, an alpha plus gamma plus sigma, and a gamma plus sigma region should be added. In fig. 12, the section at 80 pct Fe, the alpha plus gamma region should be widened at 800°C. In fig. 13, the section at 90 pct Fe, the alpha plus gamma region should be widened at 650° and 800°C. Undoubtedly, the chief reason for the discrepancies between the authors&apos; data and those of Rees, Burns, and Cook is that the authors did not employ long enough heating times to allow for transformation. In this connection, I wish to warn that transformations in these alloys, particularly transformations at temperatures below 800°C, are extremely sluggish and may require a year or more to approach completion. Therefore, unless extremely long heating times are employed or steps are taken to accelerate these transformations by such means as mechanical working, the results will not yield an accurate picture of the alloy system. Certainly, an accurate picture is needed for the development of better high-temperature materials. E. J. Dulis-The purpose of this work is not clear. If an improvement of the ternary equilibrium diagram of the Fe-Cr-Ni system was wanted, it seems logical that testing techniques superior to those previously used would be a prime requirement. To approach equilibrium in this system, long holding times are needed; a fact established long ago but apparently ignored by the present authors, who used the continuous heating and cooling tests in equilibrium studies. A publication on the same system by Bradley and Goldschmidt6 was criticized by Monypenny in a

Jan 1, 1951

By R. Silverman, H. Blumenthal

It was found that despite the similarity of chemical analyses of different titanium carbides used as base materials for cermets, the physical properties, especially transverse-rupture strengths, of test bars were different. Hence this metallographic study attempts to link physical properties to micro-structures. It is shown that microstructure, grain shape, and grain growth are functions of three interrelated factors: 1—powder production procedure, 2—surface conditioning of the particles, and 3—impurities either contained in the original powder or acquired during ball milling. An explanation is offered for the "coring effect," long observed, but heretofore of unknown origin. The explanation is based on assumption of an oxide film and on chemical analyses which substantiate these findings. TITANIUM carbide has become in recent years a material of great interest in the high temperature field. Consequently, many manufacturers in the United States and Europe are producing titanium carbide for cermet applications as well as for additions to the well known tungsten carbide tools. All present commercial processes of titanium carbide production utilize the chemical reaction of titanium dioxide and carbon to form as nearly as possible stoichiometric Tic. This reaction is carried out in three ways: 1—in a menstruum of molten metal,&apos; 2—in the solid state, either in a protective atmosphere2 or in vacuum;" or 3—in an are-melting operation. In spite of the fact that the pure carbides obtained in these operations are almost identical chemically, the physical properties vary considerably when they are combined with a binder (Ni, Co) to form cermets. This fact led the authors to examine metal-lographically nickel-bonded titanium carbide in order to find the possible reasons for this behavior. Materials and Methods Five different titanium carbides were used in this investigation. They are identified in Table I. The first four materials were used in the as-received condition. Material E, received in lumps, was crushed to —100 mesh and carried through a flotation process in order to bring its graphite content in line with the other products. A Galagher flotation cell was used with pine oil as frothing agent. The chemical analyses of the investigated materials are given in Table 11. The binder used was carbonyl nickel of 9 to 14 microns particle size, supplied by A. D. Mackay. The materials were ball milled at a ball to charge ratio of 6:1 using procedures described under "Experiments and Results." All particle sizes mentioned are averages determined with a Fisher Sub-sieve Sizer. Test bars (lx0.40x0.16 in.) were prepared by 1—hot pressing to 85 to 95 pct of theoretical density at pressures between 1 and 1½ tsi and temperatures from 1600" to 1800°C, 2-—-cold presssing after 3 pct camphor had been added, or 3—wet pressing, both 2 and 3 at pressures between 5 and 10 tsi. All pressed bars were sintered in a vacuum of 105 to 10-6 mm Hg for 2 hr at 1350 °C. Transverse-rupture strengths were determined by breaking on a Baldwin Universal Testing Machine over a 9/16 in. span. Densities were measured by water displacement. The preparation of the specimens for micrographs was done according to Silverman and Doshna Luscz." All magnifications are at X1000. A sodium picrate electrolytic etch was used. Experiments and Results The influence of ball-milling procedure, ball-milling medium, pressing procedure, and sintering procedure on the microstructure of 80/20 — TiC/Ni were investigated. Ball Milling of Materials A, B, and C in a Steel Mill: Figs. 1 and 2 show microstructures of hot-pressed and vacuum-sintered test bars of materials A and B after the respective materials had been ball milled to 2.1 microns particle size in a steel mill and mixed with 20 pct Ni binder. Material A (Fig. 1) shows considerable grain growth. Also evident is a tendency of the carbide grains to coalesce. The density is 98 pct and the low transverse-rupture strength of 111,000 psi is probably caused by many large grains and an unfavorable packing factor. Almost all grains show a slight indication of "coring." Material B (Fig. 2), although showing grain growth, still has many small particles and a better distribution of binder and carbide due to the relative absence of the coalescing tendency. "Coring" can be observed in almost all grains. The high transverse-rupture strength of 179,000 psi and the density of 100 pct are believed to be due to the many small grains completely surrounded by the binder phase. There is also a preference to form spherical grains with material A, while most grains of material B preserve their angular shapes. Material C, of which no picture is given, stays between A and B in every respect. Rounding of some grains can be observed as well as coring, but the latter to a lesser degree than with material B. Its densification is good and the transverse-rupture strength obtained is 142,000 psi. Ball Milling of Materials A, B, C, and E in a WC Mill: When the Tic powders were ball milled to 2 microns particle size in a we mill, then ball-mill mixed with 20 pct Ni binder, hot pressed, and vacuum

Jan 1, 1956

By D. J. Mack, R. E. Reiswig

Six examples of the peritectoid transformation were selected from the literature and studied by the method of isothermal transformation. The kinetics and mechanisms of five of the examples are presented as TTT diagrams and photomicrographs. The exist-enc- of a peritectoid in the sixth case is doubtful. ALTHOUGH the peritectoid transformation per se has been known for many years, no precise published data exist concerning the kinetics or mechanisms involved in transformations of this type, except for the brief treatment by Rhines, et al. 1,10 Bearing in mind the fact that investigations of recent years are uncovering more and more peritectoids and suspected peritectoids, a thorough study of the well-established peritectoids appeared to be in order. It was for this reason that a study of the kinetics and morphological mechanisms of six binary peritectoids was undertaken. The six peritectoids selected from the literature for study were those reported at 7.02 wt pct Al-Ag, 26.0 wt pct Sb-Cu, 30.5 wt pct Sb-Cu, 32.3 wt pct Sn-Cu, 8.35 wt pct Si-Cu, and 21.2 wt pct Al-Cu. These selections were based on availability and purity of components, ease of preparation and heat-treatment, and estimated reliability of the available equilibrium diagrams in the regions of interest. EXPERIMENTAL PROCEDURE The alloys used in this investigation were induction melted in electrode-grade graphite and chill-cast in cast-iron split molds. In all cases, the alloys were so brittle that they could easily be broken into samples weighing 1 or 2 g. Chemical analyses showed that the alloys used were close to the respective peritectoid compositions reported in the literature and that the impurity levels were low in all cases. Metallographic examination showed uniform distributions of phases in all samples, indicating uniformity of composition in the samples studied. Isothermal transformation studies were carried out in fused-salt media, using the familiar inter-rupted-quench method. Uniformity of temperature in the salt baths was maintained by continuous stirring with a stainless-steel agitator. On the basis of actual observations of the temperature fluctuations, the estimated temperature control was + 10C for the Ag-Al and Cu-Sb alloys and ±30C for the Cu-Sn, Cu-Si, and Cu-Al alloys. The accuracy of all temperature measurements was estimated to be ±1°C. It was found necessary to mount metallographic specimens of the Ag-Al alloy in cold-curing methyl methacrylate, since the temperatures encountered in mounting in bakelite or lucite caused an appreciable degree of transformation to the ß phase. For the other alloys, wood-flour-filled bakelite mounts were used to avoid extraneous X-ray diffraction lines during the later examination of the metallographic specimens on a Norelco Geiger-counter d if f r ac tomete r. In the X-ray diffraction procedure, agreement between the published diffraction patterns and those obtained in this study was good. This was particularly important for phase identification, since the literature contained little in the way of micrograph description in some cases. Etching of the silver-aluminum alloy for metallographic examination was done by swabbing with either of the following reagents: 1) 10 g CrO3, 1 g (NH4), SO2, 0.5 g NH4NO3, 100 ml H2O, or 2) 10 ml NH4OH, 1 ml 20 pct KOH, 4 ml 3 pct H2O2, 5 ml H2O. The other alloys were etched with the usual bichromate etchant: 2 g K2Cr2O7, 1.5 g NaC1, 8 ml conc. H2SO4, 100 ml H20 (swabbed vigorously). EXPERIMENTAL RESULTS A) The Ag-Al peritectoid at 7.02 wt pct Al— The phase equilibrium involved in this peritectoid is shown in Fig. I.2 The phase boundaries in the vicinity of the peritectoid were most comprehensively established by Hume-Rothery, et al,3 who placed the equilibrium temperature at 448 °C and the equilibrium compositions of the a ß&apos; and y phases at 6.11, 7.02, and 7.24 wt pct Al, respective The alloy used in this study analyzed4 6.95 wt pct A making it slightly hypoperitectoid according to the accepted equilibrium diagram. The rate of the transformation a+ y — ß&apos; varies rapidly with degree of undercooling below the equilibrium temperature, passing through a maximum in the vicinity of 350°C. Thus the TTT dia-

Jan 1, 1960

By F. D. Rosi, C. H. Mathews

THE plastic properties of face-centered cubic metals below room temperature present a field of investigation which has not been extensively ex-plored. The work by Schmid and Boas1 has demonstrated the importance of temperature upon such properties as strain hardening and critical resolved shear stress. The work by Yamaguchi2 upon the shear stress as related to the number of slip bands accentuates the necessity for further experiments of a similar nature. The approach to a mechanical equation of state from the standpoint of thermal fluctuations and activation energies by Becker3 and more recently by Kauzmann4 further emphasizes the need for a quantitative and more comprehensive analysis of the dependence of fundamental plastic properties on temperature. The purpose of the present work was to investigate specifically: (1) The gross shape of the stress-strain curves at several temperatures, (2) the change in the critical shear stress as a function of temperature, and (3) the number and appearance of slip bands as a function of strain and temperature. Preparation of Specimens Single-crystal specimens of 99.996+ pct alumi-num, 1/2 in. in diam and 5 to 6 in. in length, were made by the Bridgman method of gradual solidification from the liquid state. The crystallographic orientation of the single crystals was determined from back-reflection, Laue X-ray photograms ac-cording to the method described by Greninger.6 In most specimens the Laue photograms showed double diffraction spots indicative of the lineage structure type of imperfection, discussed in great detail by Buerger.7 The angular spread of these spots was never observed to exceed 2". Most of the crystals were radiographed to insure against microporosity. In preparing the metal surface for optical microscopy, the following sequence of operations gave good results: The as-cast crystals were turned down in a lathe, 0.001 in. per cut, to obtain a 2.5 in. gauge length. The cold-worked layer resulting from this operation was removed chemically by etching with Tucker&apos;s reagent. Then the specimen was polished mechanically through 2/0 metallographic emery paper, after which it was etched again to remove the cold-worked layer resulting from the mechanical treatment. A 48-hr anneal at 580°C ±10°C followed so as to insure an essentially stress-free single crystal. After the annealing treatment, the specimen was electrolytically polished in a 2:l solution of methyl alcohol and concentrated nitric acid. With a current density of 10 amp per sq dm (decimeter) the time required to obtain a satisfactory surface varied from 10 to 12 min. The polish-ing was carried out for short periods of 2 min to avoid rapid deterioration of the solution as well as to enable the rotation of the specimen 180" for uniformity of polish. It was necessary to place the solution in a bath of dry ice in view of its explosive nature at room temperature. Etching of the electrolytically polished surface was accomplished by using the fuming etch-pit method recommended by Lacombe and Beaujard8 for high-purity aluminum. Method for Tensile Testing A modification of the loading equipment devised by Miller9 was used. In this apparatus, the specimen was suspended from a chain and gimbal arrangement (for axial loading) in a heavy steel framework connected at the bottom to a balanced 6:1 lever and bucket system. Loading of the specimen was accomplished by allowing sand to flow from a reservoir into the bucket suspended from the longer end of the lever-arm at a rate of approximately 3 lb per min. Strain measurements were made using the Baldwin SR-4, bonded, resistance-wire, strain gauge and an SR-4 portable strain indicator (type K), which permits a reading accuracy of 2 microinches per inch. For low-temperature study, the gauge was calibrated by measuring the elastic modulus of an annealed stainless steel rod, which is known to be independent of temperature."

Jan 1, 1951