By Hiroshi Tabuchi, Akihiko Takahashi

"High strength aluminum matrix composites were prepared and studied using as reinforcement newly developed nearly mono-dispersed a-alumina single crystal particles each of which has a regular polyhedral shape. The composites were formed by centrifugal casting using aluminum casting alloys (Al-Si and Al-Cu-Mg) as the matrices, followed by heat treatment. The volume fraction of the alumina particles was as high as 60%. The same matrix composites reinforced by conventional crushed fused alumina particles were similarly prepared as the reference. The bending strength and tensile strength of the Al-Cu-Mg matrix composites reinforced by the novel alumina particles of 10 µm in average diameter are as high as 1020 MPa and 560 MPa, respectively, which are higher than those of the conventional alumina composites. Furthermore, the bending strength of the novel alumina composites degraded less than that of the conventional alumina composites after thermal fatigue tests. The number of cracks in the matrix seemed to influence the thermal fatigue property because many cracks were observed in the conventional alumina composites, whereas only a few cracks were observed in the novel alumina composites. This was confirmed by SEM observation of the sample composites before and after the thermal fatigue tests.IntroductionAluminum matrix composites strengthened by dispersed reinforcements are of interest for various applications due to their improved properties, such as high specific strength and stiffness, wear resistance, etc .. A large number of investigations have been made concerning fabrication processes and properties of these composites. With regard to the fabrication processes, powder metallurgy has been well-known as a solid phase process, and recently many liquid phase processes such as a compocasting, a squeeze casting, the Lanxide process, and the Osprey process have been studied and developed.(1)"

Jan 1, 1998

By C. S. Ek

Tests have been performed to recover silver and lead from residues produced after a super-hot leaching in a zinc hydrometallurgical plant operating with jarosite precipitation. When this residue is leached in ammoniaammonium sulfate or in diethylenetriamine solutions, lead dissolution is not complete and its recovery from the aqueous solutions is either difficult, due to the operating conditions, either expensive due to the amount of added reagents. In both cases, silver is partly dissolved, partly left in a new residue still containing lead and baryum sulfates. The best treatment seems to include a selective flotation producing first a silver concentrate assaying about I % Ag, then a 50 % lead concentrate collecting the baryum salts, and a final quartz-gypsum tailing. Metal recoveries can reach 50 % and 80 %, respectively.

Jan 1, 1989

By Patrick M. Eduafo, Brajendra Mishra, Mark L. Strauss

Direct acid leaching of rare earth metals (REMs) from waste lamp phosphors is non-selective, leading to co-dissolution of impurities mainly calcium, phosphorus, silicon, iron and zinc. Calcining the phosphor powder at different temperatures followed by leaching with HCl isn’t efficient for the extraction of all the chief rare earths especially cerium (Ce), lanthanum (La) and terbium (Tb). Therefore, multi-stage leaching operations are required for the separation of the REMs in phosphor dust. This paper will outline a new process for extracting Ce, La, Tb, Eu and Y from waste fluorescent lamps using a three-stage leaching and separation process. A flowsheet has been developed which shows this process is selective and efficient.

Jan 1, 2015

By Petrus Christiaan Pistorius, Farzin Fatollahi-Fard

The production of synthetic rutile—a common starting material for most titanium production processes—from iron-rich titanium minerals such as pseudorutile and ilmenite is described. The process for “upgrading” the mineral to synthetic rutile is by carbothermal reduction of the mineral while immersed in a molten salt at high temperature, followed by magnetic separation of the reduced iron. A variety of factors are also investigated, such as particle size of the mineral, the type of mineral, and the molten salt used. The solubility of iron(III) oxide in different molten salts is also experimentally determined.

Jan 1, 2016

By Peter Sylvén, Darwin Morales

Despite being crucial for the smelting process, furnace tapping using oxygen lances has not been considered an operation that brings value. Therefore, these important tools have not seen a significant change in over 100 years. Problems related to the use of oxygen lances include: • Inaccurate tool: causing damages shortening the life of the taphole refractories. • Safety: extended exposure to the operator in an unsafe area of the furnace. • Cost: high oxygen consumption & high lance consumption. • Time consuming and frustrating to connect one lance to another. This paper will suggest a very good solution; new concept thermal lances. We will show how these provide an outstanding performance for a more efficient, faster and cost-effective furnace tapping operation. These new lances are very accurate tools that enable the operator to perform a more controlled operation; resulting in longer taphole life, fewer repairs and less down-time.

Jan 1, 2016

By Peng ZANG, Qihang Liu

Experimental work was conducted to determine the relationships of coal char conversion with temperature and heat absorption. The results show that at an earlier stage of the coke forming process, lump coal would absorb large amounts of heat but the increase of high temperature strength of lump coal was not significant. Contrarily, the lump coal’s high temperature strength was greatly improved at later stage of coke forming process. A number of residual coal was found in most tuyere coke samples illustrating that the lump coals added in the melter gasifier were not completely transformed into coke when they arrived at the tuyere region. The results indicate that the improvement of lump coal’s high temperature performance is limited in the melting gasifier by the low coke forming rate which could become the core factor of fines generation of lump coal in the melting gasifier.

Jan 1, 2016

By Yuzhe Zhang, Xiaodi Huang, Xinli Wang, Bowen Li, Matthew Andriese, Jiann-Yang Hwang, Zhiwei Peng

The recycling of waste tires has been a big environmental problem. About 280 million waste tires are produced annually in the United States and more than 2 billion tires are stockpiled, which cause fire hazards and health issues. Tire rubbers are insoluble elastic high polymer materials. They are not biodegradable and may take hundreds of years to decompose in the natural environment. Microwave irradiation can be a thermal processing method for the decomposition of tire rubbers. In this study, the microwave absorption properties of waste tire at various temperatures are characterized to determine the conditions favorable for the microwave heating of waste tires.

Jan 1, 2015

By Marie-Aline Van Ende, In-ho Jung

A thermodynamic database for the oxyfluoride system CaO-MgO-Al2O3-SiO2-Na2O-K2O-Li2OMnO- FeO-F has been developed based on the critical evaluation and optimization of all available experimental thermodynamic and phase diagram data. The developed database can be used for phase diagram and equilibrium solidification calculations for multicomponent systems and for understanding the solidification behavior of mold fluxes. Based on this thermodynamic database, a simple kinetic model was developed to simulate the interactions between the mold flux and molten steel using effective equilibrium reaction volumes combined with the thermodynamic database.

Jan 1, 2014

By Björn Lindquist

Boliden has developed a number of specialised technologies for smelter gas handling and effluent treatment. These technologies will be described. Special attention will be given to the high-pressure venturi, Editube wet electrostatic precipitator, mercury removal processes, and two-stage effluent treatment.

Jan 1, 2002

By José Luiz Rodrigues Bravo

The production of electrolytic copper with assured quality corresponding to international standards, in a conventional electrorefkery of a custom smelter, is a hard and cautious task, if no advanced technologies for selective control of electrolyte impurities are available. The improper control of the amount of As , Sb and Bi in the anode that enter the tankhouse , attributable either to a bad schedule of concentrate input or to the unavailability of clean concentrates in the international market , as well as the lack of means to maintain the suitable level of these elements in the electrolyte together with other operational circumstances, can result in off-grade copper, as well as affect the starting sheet chemically and physically. This paper presents in a practical way the relationship between the operational conditions and the cathode and starting sheet quality produced at CMSA, covering the period of the last five years of operation, discusses the technologies available in the market for antimony and bismuth removal and compare the results of testwork, achieved in the laboratories of CMSA, using two resins not associated with patented technologies.

Jan 1, 1997

By Dariusz Kopyci ski, Józef Dorula

The study proves that by introducing the iron powder and disintegrated steel scrap to low-sulphur cast iron still before the inoculation carried out with a conventional graphitising inoculant, the mechanical properties similar to those obtained during the inoculation treatment carried out on cast iron with the recommended high sulphur content are achieved. The said operation increases the number of crystallisation nuclei for dendrites of the primary austenite. In this case, the iron particles act as substrates for the nucleation of primary austenite, due to a similar crystallographic behaviour of the regular face centred cubic lattice The more numerous are the dendrites of primary austenite, the less free space is available in the interdendritic spaces for the formation of graphite eutectic grains, which makes the structure more refined (more eutectic grains) and the mechanical properties higher.

Jan 1, 2016

By Xu Zhang, Xuewei Lv, Guibao Qiu

Slag foaming phenomenon is of vital importance to the mass and energy transfer in metallurgical processes. A considerable extensively studies carried out via out-gas in the past cannot simulate well the foaming phenomenon formed in the blast furnace where high TiO2 iron ore is used. A gas reaction was designed in the water-glycerol system to simulate the inner-gas system. This study investigated the influences of solution viscosity, particle concentration and particle size on foaming caused by endogenetic gas. The results show that the foaming height decreases with the increase of solution viscosity, which means reduced foaming ability, more difficult foaming elimination process and prolonged time for natural defoaming. With increasing the solid particle content, the foam height presents a trend which increases firstly and then decreases. Under a certain solid particle content, foaming height decreases with the increase of solid particle size, indicating a weak foaming ability.

Jan 1, 2015

By Cui Wang, Bing Dai, Haibin Zuo, Jianliang Zhang

The damage mechanism of ductile cast iron cooling stave applied to No.4 blast furnace of Guofeng steel was analyzed through damage investigation in details, the damage causes: hightemperature gas flow erosion, wear of burden, high-temperature ablation, carburizing damage, improper operation on blast furnace, etc. were given out both in macroscopic and microscopic views. It can be obtained from metallographic diagrams that the diameter of graphite nodules increases, the number per unit area reduces, and roundness declines, successively, from cold to hot surface, which are not conducive to stave longevity. In summary, the material for staves manufacture should be better in comprehensive mechanical properties to prolong the service life, thus making blast furnace long campaign.

Jan 1, 2015

By Jiangtao Li, Zhongwei Zhao, Xingyu Chen, Xuheng Liu

In tungsten ion-exchange process, excessive sodium impurity enters into ammonium tungstate solution. However, the Na content of the final ammonium paratungstate (APT) product must be strictly controlled. Consequently, it is necessary to remove Na from the ammonium tungstate solution during processing in order to obtain the required purity of APT. In this study, porous Na specific absorbent, Na1+xAlxTi2−x(PO4)3, is used to remove Na from the ammonium tungstate solution. Through experiments, the effect of reagent concentration of Na1+xAlxTi2−x(PO4)3, reaction time, reaction temperature and Na concentration on the Na removal were investigated. The results showed that under optimal reaction conditions of reagent amount of NATP 1.0 times of theoretical amount, reaction temperature 25 °C and reaction time 15 min, the Na removal from commercial (NH4)2WO4 solution can reach 98%. Na1+xAlxTi2−x(PO4)3 has a good applicability to different Na+ concentrations. The obtained APT product reaches the national standard purity of zero level.

Jan 1, 2014

By Jianguo Yin, Wenqiang Yang, Xiaoli Yuan, Juan An, Wentang Xia

Low grade iron ore with phosphorus (LGIOWP), a raw and wasted industrial solid material was used as an adsorbent to remove Pb(II) from wastewater. The effects of initial pH value, adsorptive time, initial Pb(II) concentration, adsorptive temperature and LGIOWP dosage on the Pb(II) removal efficiency were studied. The results show that the Pb(II) removal efficiencies exceed 99.4% and Pb(II) concentrations are less than 0.30 mg/L under the conditions of pH value 7.0, adsorptive temperature 50 oC, adsorptive time 30 min, initial Pb(II) concentration 100 mg/L, particle size <0.25 mm, adsorbent dosage 5 g/L and stirring speed 260 r/min. After Pb(II) removal reaction, the Pb(II) concentrations of wastewater completely accord with the requirement of national discharge standards of pollutants from lead and zinc industries (GB 25466-2010) (TPb= 0.5 mg/L) in China. Therefore, it can be concluded that LGIOWP is a new low-cost adsorbent which is suitable for the adsorption of Pb(II) from wastewater.

Jan 1, 2015

By Noritaka Horii, Katsuyoshi Kakinuma, Hiroshi Yamamura

"ZrO2 and Y2O 3-doped ZrO2 gel film were obtained by spin coating of sol from Zr-n-propoxide, n-propanol, acetylacetone, nitric acid, and water on a silica glass as a substrate. ·Dried gel films crystallized to monoclinic, tetragonal, cubic and their mixed phases, depending on the chemical composition of sol, .firing temperature, and coating cycles. ZrO2 films with highly preferential orientation were successfully obtained from a solution containing a large amount of n-propanol. The highly oriented ZrO2 film was found to have high transparency compared with non-oriented 'films. Electrical conductivity of 8 mol% Y2O 3 doped ZrO2 film was also measured.Introduction3 mol% Y2O 3 doped ZrO2, which has a tetragonal symmetry is ·well known to have a strong mechanical property and a high toughness. (1) On the other hand, 8 mol % Y 2O 3-doped ZrO2 is high oxide-ion conducting material and is applied to oxygen sensor, oxygen pump, and solid oxide fuel cell (SOFC). (2) Sol-gel methods using metallic alkoxide are widely applied for synthesizing ceramics such as high-purity fine particles, thin film, and fiber. (3) For ceramics films, many reports have been made on SiO2, (4) TiO2, (5) and PZT. (6) Several case studies have been done on zirconia film based on the sol-gel method, (7) - (11) but very few on preferentially oriented film and on systematic Y zO3 doping. Almost zirconia ceramic· films reported were prepared by means of dip-coating. Kamiya et al. (12) and Ganguli et al (13) converted zirconia into fiber. Sol from Zr alkoxide is usually very unstable, and a stabilizing agent such as glycol or ß-keton is used beforehand (7) (14)."

Jan 1, 2000

By Carlos Ortiz

The Huelva Flash Smelting Furnace was commissioned in September 1975. The Smelter and the Acid Plant were expanded in 1995 to their present capacity of 300,000 tpa new copper equivalent and one million tonnes of concentrate per year. During these years of operational experience, most of the initial practices have been reviewed, process control has drastically improved and main process equipment has been modernised. The fourth Flash Furnace campaign lasted 9 years (1995-2004) during which 8 million tonnes of concentrate were smelted. Increasing sulphur content in concentrates and new environmental requirements imply new challenges for smelters to keep production and operation costs down. This paper is an overview of the modifications and improvements carried out in the 2007 general shutdown in Smelter and Acid Plants. Al

Jan 1, 2008

By Jin Yu, Fang-Qiu Zu, Yun Xi, Li-Na Mao

"According to the behaviors of resistivity-temperature of Cu-Sb70 melt, which suggests a partly reversible temperature-induced liquid structure transitions (LST) could occur in this alloy, in this paper, we investigated the dependence of solidification on the liquid state. Both resistivity and temperature were measured to track solidification process. The results show that the nucleating undercooling of the melt which experienced the LST increased and the solidified time decreased. Meanwhile, the solidified microstructures refined evidently, with the microscopic pattern of primary phase changes from disordered pillarlike dendrites into homotaxic ones. Moreover, it is verified that the microstructures would be different if the reversible part of the LST was restrained. The new phenomena and results reflected in this paper suggest that grasping the rules of melt structure change with temperature before material processing will give help for controlling the solidification more effectively and finally resulting in more ideal microstructures.IntroductionThe structure and quality of liquid alloys have a direct and important influence on the structure, performance and quality of the solidified ones. In recent years with in-depth study of liquid structure, researchers have found that some liquid structure transitions (LST) could occur on dependence of the temperature or pressure [1-5]. And the article [6] reported that a pressure-induced reversible LST was found in liquid triphenyl phosphite, which further confirmed the authenticity of the existence of the LST. Furthermore, in our earlier studies of Sn-based melts using resistivity method, some abnormal structure changes induced by temperature have been found at hundreds of degrees above liqiudus, and these LSTs are partly reversible[7]. This phenomenon has been discussed and it is suggested that the reversible LST in Sn-based melts are related to the short-range ordering (SRO) structures of Sn, which are tetrahedron structure with covalent bonding. However, does this reversible LST exist in other melts too?"

Jan 1, 2012

By R. P. King

The linear intercept distributions provide unambiguous and accurate characterizations of the texture of mineralogical materials. The relation between the measured linear intercept distributions and the spatial correlation function is shown to be given by: in the Laplace Transform domain. The linear intercept distributions of the two phases in a low- grade chromite-serpentinite ore were measured. and the spatial correlation functions for both phases were evaluated using the above relation. The correlation functions are the primary relations for integral geometric models of mineralogical texture and this work demonstrates the relation between the 10 stereological model and the 3D integral geometry model for mineral liberation.

Jan 1, 1991

By Mikko Loponen

Outotec has developed an operator training simulator (OTS) platformsuitable for various hydrometallurgical processes. The complete solution is run in the cloud, where virtual client instances can be managed on-demand. The aim is to build a generalizable model that produces coherent results even when operating outside of ideal parameters, allowing the operator to train in unsteady state conditions such as start-up and shutdown. Complex software products are commonly associated with significant development time and cost. Utilizing modular software architecture, only the control system and processmodel are tailored for theOTS,whereas modules such as user administration and cloud-based client machine spawning can be imported, shortening development time. A generic acidic pressure oxidation process (POX) operator training simulation consisting of feed preparation, autoclave, dual-stage flash evaporation and off-gas scrubbing is described. Process is simulated using Outotec HSC Sim 9 process simulator and controlled by Siemens Simatic PCS7 control system.