Search Documents

By K. L. Moazed, G. M. Pound

An investigation was made of the deposition of silver from a thermal beam onto tungsten field-emitter tips at 300°K. "Island"-type nuclei were observed to form and grow. The nucleation of silver crystals occurs preferentially on non-close -packed planes of a tungsten tip at a critical volume free-energy change of about —2900 cal per cc. The adatom population which is critical for appreciable nucleation rate of silver crystals is about 0.2 of a monolayer and is essentially independent of beam flux, time, and source temperature. This result is strong evidence that a metastable equilibrium exists between adatoms and critical nuclei, as assumed in the present theory. SOME of the more significant studies of nucleation in deposition of metals from vapor beams have been conducted by measuring the thermal beam flux which is critical for appreciable rate of nucleation on a substrate surface held at a given temperature.'2 The observed critical supersaturations may be described in terms of Eq. [7] which was derived3'3a on the model of an adsorption, surface migration, and statistical fluctuation mechanism. However there usually made with a low-power optical microscope, a fairly insensitive method of detection. The object of the present study was to overcome some of these difficulties by measuring the critical supersaturation for condensation of a thermal beam of silver onto a tungsten field-emitter tip. Such a tip may be cleaned by electrically heating it to a high temperature in situ, and the high vacuum obtainable in a field-emission tube (10-10 torr) precludes adsorption of residual gases for convenient periods of time. Furthermore, the degree of cleanliness, the orientation, and the state of imperfection of the tip may be ascertained from the field-emission pattern. Detailed explanations of theoretical considerations and experimental procedures relating to the field-emission microscope may be found in a number of excellent review articles12'13 and thus only a brief description will be given here. The electronic work function of a metal is defined as the energy that an electron needs to escape from the potential field of the solid. By applying a large field between the surface of the solid and a suitable collector, it is possible to free the electrons by the tunnel effect. Fields of approximately 30 million v per cm are needed to produce this effect, and such fields are obtained in practice by using microscopic surfaces of high curvature (tips). Because the work function of a metal is a function of surface orientation, the emission from the various planes is different, and thus it is possible to obtain a representation of the surface in the emission microscope. In general, the work function is higher for the more densely packed planes. Fig. 1 shows a pattern for "clean" tungsten in which the central dark region represents the (110)

Jan 1, 1964

By R. M. Rose, D. P. Ferriss, J. Wulff

Single crystals of tantalum, tungsten, and the binary alloys thereof were grown by electron-beam zone melting and tested in tension between 77° and 373°K. The ductile-to-brittle transition temperature increased sharply with solute concentration, for both tungsten-rich and tantalum-rich alloys; apparently, the maximum transition temperature exists near the 50 pet concentration. Twinning was observed to be a consequence of cleavage-crack propagation. Cleavage occurred on(100)planes, and extensive tearing and "river markings" were present. The onset of brittleness could not be associated with any change in deformation mode, the yield point phenomenon, or the large rise in yield stress with decreasing temperature. Cleavage was observed to initiate at either the specimen surface, or subgrain boundaries. The observation was made that the grain boundaries of Polycrystalline materials are probably even better as nucleation sites for fracture, and are responsible for brittleness at high temperatures and lower solute concentrations than those of the corresponding single crystals. TUNGSTEN and tantalum, the two high-melting neighbors in the third transition period of the periodic table, present striking contrasts. Although both are bee, tungsten has far higher elastic moduli, and the highest ductile-to-brittle transition (DBT) of all the pure metals.' Tantalum, however, is ductile at liquid helium temperatures. Large strain aging and yield point phenomena are observed in tantalum,2,3 but only to a lesser extent in tungsten.4 Tungsten work-hardens at a high rate,5 whereas this effect is negligible in tantalum.' Since the mutual solid solubility of these two metals is complete,7 and no ordering has yet been reported in the binary system, the possibility of depressing tungsten's DBT by tantalum additions was considered. Also, tungsten additions to tantalum could produce hard, high-melting alloys which might be ductile at room temperature. Such alloys offered excellent bases for complex alloy development, particularly with regard to the effect of rhenium on Group VI metals.8"10 In addition, there was the opportunity to examine flow and fracture modes in the vicinity of the DBT, with particular emphasis on the correlation between brittleness and fundamental deformation mechanisms. Myers11 has reported that recrystallized alloys with up to 10 pet W in tantalum are ductile at room temperature, but alloys with 20 pct W could not be swaged at temperatures as high as 500°C. The whole spectrum of Ta-W alloys has been surveyed by Braun, Sedlatschek, and Kiefferl2 using sintered powder compacts. In addition to some physical properties they reported a maximum hardness at about 50 at. pet W, dropping to much lower hardness levels for the pure components. They were able to cold work tantalum-base alloys with as much as 30 pet W and to warm work tungsten-base alloys with up to 20 pet Ta by procedures similar to those used for pure tungsten. EXPERIMENTAL In order to study deformation modes and to keep the impurity concentrations at a minimum, electron-beam zone melting was used to prepare single crystals of high purity. The electron-beam zone melting apparatus is similar to that described by Calverley, Davis, and ever" and incorporates a grid control rectifier to maintain control of emission current. Pure metals were refined by making three zone passes at 4 mm per min up the rod. Alloys were prepared by melting together wire of one constituent on a previously melted rod of the major constituent. Subsequently, two zone passes were made in opposite directions to level the composition after the manner suggested by pfann.14 Purification of the starting materials was accomplished by evaporation of the several impurities, and the degree to which this was accomplished is indicated in the chemical analyses of Table I. The uniformity of composition along a zone levelled rod was within the i 1 pet accuracy of the fluorescent X-ray technique used to determine composition. Crystallographic orientation of the

Jan 1, 1962

By W. A. Tiller, W. C. Johnston

The solute distribution ahead of an advancing solid-liquid interface is controlled by varying the momentum boundary layer thickness in the liquid adjacent to the interface. Single pass zone-melting experiments on Pb-Sn alloys are described in which the liquid is caused to rotate in the plane of the solid-liquid interface due to the influence of a magnetic .field rotating in this plane. The variation of the diffusion boundary layer thickness with field strength is determined. DURING the freezing of an alloy a partitioning of solute occurs at the solid-liquid interface, the magnitude depending upon the difference in the solid and liquid solubilities at the interface temperature. Because the diffusion coefficient is so small in the liquid relative to normal freezing rates, either a pileup or a depletion of solute occurs at the interface when the partition coefficient, kO, is either less than or greater than unity, respectively. This solute distribution is completely characterized by i) the solute concentration in the liquid far from the interface, C) the ratio of freezing velocityf, to diffusion coefficient, D, iii) the partition coefficient, ko, and iv) the thickness of the diffusion boundary layer, 6,, at the interface (this assumes that an electric field is not applied across the interface). For a particular system, C ko and D are fixed so that the character of the solute distribution can be changed only by a variation of either f or 6c. As is well known, the freezing velocity can be changed by varying the thermal environment of the alloy. Whereas, the thickness of the solute rich layer can be changed by varying the fluid flow conditions in the liquid. It is the purpose of this paper to describe a technique for controlling the fluid flow conditions in the liquid. During most solidification experiments the driving force for fluid flow arises from either mechanical mixing, thermal convection or electromagnetic mixing. The momentum boundary layer thickness, 6m at the solid-liquid interface, within which negligible movement of the liquid occurs, has been calculated for the special case of mechanical mixing where crystals are solidified by the Czochralski technique.l,2 The calculation of 6m for the case of thermal convection has also been made.3 In some calculations it has been assumed that the momentum boundary layer thickness, 6,, may be equated to the thickness of the diffusion boundary layer 6c, at the interface. However, as may be seen from Appendix I this is only true in very special cases and in general where a is a constant of magnitude determined by the particular liquid alloy. Neither calculations nor experimental data exist for the dependence of upon electromagnetic mixing. In this paper experiments are described in which the liquid is caused to rotate in the plane of the interface due to the torque developed on it by a magnetic field, H, rotating in this plane. The variation of is controlled by the variation of H. A magnetic field rotating in a plane perpendicular to the interface has been used for the purification of aluminum. Experimentally, we determined the variation of 5C with H by using the zone-melting technique of pfann5and a theoretical relationship of Burton et a1.2 pfann5 has shown that, after the passage of one molten zone through a long cylindrical charge of uniform concentration, CO, the solute distribution, C,, in the solid is as shown in Fig. 1. The equation describing this distribution is

Jan 1, 1962

By H. L. Gilbert, H. A. Johansen, R. G. Nelson

High purity electrolytic chromium plate has been hydrogen-reduced and arc-melted under inert atmosphere to give sound ingots. These ingots may be hot forged to break the as-cast structure and then worked at 500°C to finished form. An intermediate and final high temperature anneal gives best ductility and grain refinement. HE increasing interest in refractory metals for I use in high temperature gas turbines, jets, and rockets has led to great efforts in exploiting the fifth and sixth groups of transition elements. Much of the interest has centered upon production of metals that can be worked and fabricated by normal means to produce various engine parts or components having the high temperature characteristics of oxidation resistance and high creep strength required for such uses. If these pure elements do not exhibit all of the desired characteristics, it may be possible to obtain a high purity alloy that will. Since, in all cases, development of these transition elements has depended to a large extent upon removal of oxygen and nitrogen as a means for producing ductile metal, the hypothesis has been accepted that oxygen is the normal embrittling material in a high grade electrolytic chromium metal. Various methods have been employed in an effort to remove this oxygen by direct or indirect attack.' Many workers have endeavored to produce pure chromium through reduction of the oxide by carbon or active metals, while others have recommended fusion electrolysis of chromium salts or reduction of these salts by active metals, such as sodium or calcium. Hydrogen reduction of the oxide or chloride and thermal dissociation of the iodide have been reported to give high purity metal. Experimental Work The U. S. Bureau of Mines, Northwest Electro-development Laboratory, has systematically re-examined the more promising methods and developed two which produce metal having ductility at temperatures lower than heretofore described. It has been found' that oxide-free chromium chlorides in a NaCl-KCl carrier salt may be mag- nesium-reduced and the byproduct salts distilled off in vacuo to give a high purity chromium sponge. Fusion analysis conducted under the supervision of W. W. Horton of Knolls Atomic Power Laboratory showed the oxygen and nitrogen both to be below 10 parts per million on a selected sample. A small amount of carbon is carried over in the final metal from the chlorination and reduction steps which are carried out in graphite crucibles. This trace of carbon is not detrimental to hot ductility. A more practical method for producing ductile metal is through hydrogen reduction of high purity electrolytic chromium. Normal electrolytic chromium will, if "developed" for a few minutes at 1100°C in high vacuum, be found by the method of Adcock:; to contain about 1 pct chromium sesquioxide (Cr2O3). This small amount of oxygen may be effectively reduced by hydrogen.2, 4 The method employed was to crush electrolytic chromium plate in a gyratory crusher to pass 60-mesh; finer crushing appears to offer no advantage. A nitric acid leach removed the iron picked up during crushing. The leached powder was rinsed until neutral with distilled water and vacuum-dried.

Jan 1, 1954

By S. A. Bradford

Internal-oxide precipitates in decarburized a iron alloys were studied by microscopic and X-ray methods. Diffusion of oxygen is primarily trans-granular, although large amounts of manganese or PhosPhorus cause preferred grain boundary dimsion at temperatures below 1450OF. Transgvanular internal oxidation follows the parabolic rate law with an apparent activation energy of 60 kcal per g-atom for decarburized rimmed steel and around 50 kcal per g-atom for higher alloy contents. The internal oxide is (Fe,Mn)0. Evidence was found for a miscibility gap in the FeO-MnO system. UNTIL very recently, the internal oxidation of metals was studied primarily as a scientific curiosity or, in a few cases, as a means of strengthening alloys by precipitation hardening. However, with the recent development of low-carbon enameling sheet steel, internal oxidation has become a problem of practical importance to the steel industry. For example, in 1961 it was reported1 that internal oxidation of steel can occur during decar-burization by open-coil annealing and will reduce the notch ductility of the sheet unless the process is carefully controlled. The present study was therefore undertaken to learn more about the rates and mechanism of oxygen diffusion and oxide formation in iron alloys. BACKGROUND The process of internal oxidation has been well-defined in the literature:',' oxygen dissolves in an alloy, diffuses inward from the surface of the metal, and reacts to form a precipitate with the alloying element that will provide the most stable oxide. he growth of the finely divided so-called subscale, i.e., the internal-oxidation zone, depends on the diffusion rates of both the oxygen and the reactive element.4 Investigators have generally found that increasing the temperature increases the size of the oxide particles, the rate of subscale growth, and the tendency to transgranular diffusion. With very few exceptions, the square of the thickness of the internal oxide layer is directly proportional to the reaction time. Given two conditions easily satisfied for iron systems— a) an oxygen solubility much less than the concentration of the alloying metal and b) an oxygen-diffusion rate to the oxide boundary much faster than that of the alloying element—then the general expression developed by Rhines and co-workers5 for the parabolic growth rate of the internal-oxide zone can be simplified to the following form: where Co and CM are, respectively, the solubility of oxygen and the concentration of the alloying element, DO is the diffusion coefficient of oxygen, O/M is the weight ratio of oxygen to metal in the precipitated oxide, and x is the thickness of the internal-oxide zone after an annealing time t. Both the oxygen solubility and diffusion coefficient can be approximately expressed as functions of temperature by Arrhenius-type equations: in which H and Q are, respectively, the heat of solution and the activation energy of diffusion. Consequently, the apparent activation energies calculated from Arrhenius plots are the sum of the heat of solution of oxygen in iron and the activation energy for diffusion of oxygen. The data, if not the interpretation, of Schenck et al.8 bear out the fact that oxygen diffuses in the atomic form. The general rate law for atomic diffusion is: the reaction rate being proportional to the square root of the pressure at low pressures. Benard and Moreau8 studied both the surface oxidation of Fe-Ni alloys and the gradual penetration of oxygen into the metal. They observed that oxide particles first form along grain boundaries and then grow to form continuous films that eventually envelop the grains. The parabolic rate law does not usually apply in these cases, especially at the higher temperatures. The oxide formed is wustite which gradually transforms into Fe3O4 and finally into Kennedy and coauthors8 examined Fe-Ni alloys with 26, 75, and 84 pct Ni oxidized at 800°C and

Jan 1, 1964

By Hsun Hu, R. S. Cline

The formation of annealing textures during the course of recrystallization in 2 pct Al-Fe crystals rolled in the (111) [112], (112) [111], and (112) [Till orientations has hem studied in detail. When the rolling texture is composed of both (111) [121] and (001)[110] components, the annealing texture consists of mainly (110) [001] and (113) [332] components. As the (001) [110] component diminishes from the surface to the interior of the rolled crystal, the relative concentration of the (113) [332] component in the annealing texture decreases accordingly, whereas that of the (110)[001] component increases with the (111)[112] component in the rolling texture. Such dependence of the annealing texture on the composition of the rolling texture is in accmdance with the oriented growth mechanism. Grain-growth characteristics during recrystallization, hence the annealing texture, can he considerablv different in (112) [111]-type crystals depending sensitively on the initial orientation of the crystal. In a previous publication,' the formation of rolling textures in 2 pct A1-Fe single crystals with initial orientations of approximately (1ll)[112], (112)[111], and (112)[111] was studied in detail. The deformation texture of these crystals consisted of either a single (111)[112] or a combination of (111)[112] and (001)[110] components in various concentrations. For the (lll)[112] crystal, the deformation texture was a single (lll)[112] up to 70 pct rolling reduction, but it became (lll)[112] plus (001)[110] after -90 pct reduction. For the (112)[113.]-type crystals, the relative concentration of the (111)[ 112] and (001)[110] components varied with the depth below the surface of the crystal, as well as with the amount of deformation. These series of specimens, having deformation textures with a range of concentration of the (111)[112] and (001)[110] components, could therefore be used for a thorough investigation of the effect of deformation-texture components on the formation of annealing textures. In a study of rolling and annealing textures in Si-Fe crystals, Dunn and Koh3 noted that the addition of a (001)[110] component to the (111)[112]-type deformation texture had practically no effect on the recrystallization texture.* According to the ori- ented growth mechanism for the formation of annealing textures, nuclei related to the deformation texture by approximately 30-deg rotation around a common [110] axis have the highest rate of growth and the resulting annealing textures generally have such an orientation relationship with respect to the deformation textures.314 It was reasoned by Dunn and Koh3 that if the oriented growth mechanism operated the recrystallization texture developed from a deformation texture containing both (111)[112] and (001)[110] components should be strongly centered around (113)[332], because (113)[332] is approximately midway between the (111)[112] and (001)[110], and is related to both of these two orientations by [110] rotations of 25 to 30 deg. Hence, nuclei of (113)[332] orientation should have a high rate of growth in the deformed matrix. However, their results were not in accord with this prediction. It was felt by the writers that a detailed study was needed to clarify the effect of deformation-texture components on annealing-texture formation. For this reason, the present investigation was conducted. EXPERIMENTAL PROCEDURE Specimens used for the present investigation were taken from the crystals rolled previously for deformation-texture studies.' In order to follow the progress of annealing-texture formation during the course of recrystallization, a single specimen was taken from each rolled crystal and its textural changes examined after successive anneals until recrystallization was complete. The specimen was carefully cut from the rolled strip with a jeweler's saw. Prior to annealing, the sawed edges were etched to remove distorted metal, while both faces of the specimen were protected from the etching solution by acid-proof plastic tape. After annealing, the specimen was etched from the "bottom" face only (the reference or "top" face of the specimen was protected by plastic tape) to one half of its original thickness, so that the texture at the surface and at the central section of the strip could be determined by the reflection technique. The

Jan 1, 1965

By D. J. Schmatz

DISCUSSION OF RESULTS The qualitative correlation between low-temperature ductility and prior high-temperature creep strain in nickel obtained in this investigation confirms the result obtained on high-purity brass by Chen and Machlin. However, the quantitative effect is much smaller in nickel. Comparison can be made on the basis of a prior high-temperature strain that is a certain percentage of the total high-temperature elongation to rupture. In the research of Chen and machlin, the prior high-temperature strain of 1/2 pct equaled 8.5 pct of the total high-temperature elongation at rupture. For nickel, in our experiments, 8.5 pct of 21.2 pct equals 1.8 pct. For eh = 1.8 pct, the loss in ductility in percent equals x 100 = b.5 pct. That is, for equivalent bo Formation of Beta Manganese-Type Structure in Iron-Aluminum-Manganese Alloys D. J. Schmatz IRON-aluminum alloys have gained much interest in the past few years for use as a base material for elevated-temperature alloys because of their excel- high-temperature strain the loss in low-temperature ductility is 8.5 pct for nickel as compared to 60 pct for pure a, brass. It is also interesting to note the observation that in nickel the low-temperature fractures, even at the most extreme high-temperature pre-strain, were partly trans crystalline and partly intercrystalline. In the case of a brass, these fractures were completely intercrystalline. According to the data on the percent of the grain boundary area that is cracked, at 22 pct high-temperature elongation, about 12.5 pct of the grain boundary area does not carry load. Thus, the inter-crack areas are carrying a stress that is about 11 pct higher than the nominal stress. A simple model predicts that the overall elongation, which is primarily the elongation in the bulk of the specimen, will correspond to the nominal stress when the stress in the intercrack area equals the tensile strength. Quantitatively this model predicts the equation The form of this equation will agree with that found if the strain-hardening exponent, n, equals unity. Actually this model is too gross an approximation to yield good quantitative results. The question naturally arises as to whether in ordinary hot-working, such as hot-rolling, intercrys-talline cracks are introduced that affect the low-temperature properties. It appears that the answer is that such a possibility cannot be overlooked, if the hot-working induces tensile stresses at temperatures above the equicohesive temperature and if the material tends to be notch sensitive at low temperature. ACKNOWLEDGMENT This research was supported by the Aeronautical Research Laboratory, Directorate of Research, Wright Air Development Center, United States Air Force. REFERENCES lC. Zener: Fracturing of Metals, 1948, Cleveland, ASM. 'H. C. Chang and N. J. Grant: Mechanism of Intercrystalline Fracture. AIME Trans., 1956, voL 8, p. 544; lownal of Metals, May, 1956. 'E. S. Machlin. CreepRupt ure by Vacancy Condensation, AIME Trans., 1956, vol. 8, p. 106; lownd of Metals, February, 1956 'C. Chen and E. S. Machlin: On a Mechanism of High-Temper at ure Inter-crystalline Cracking, lownd of Metals, July. 1957. p. 829. Alloys lent oxidation resistance. Binary alloys of aluminum in iron are ferritic and consequently have poor hot strength. Alloys of iron-aluminum-manganese were made in an attempt to produce an austenitic alloy containing sufficient aluminum to retain the oxidation resistance of binary alloys of iron-alumi-

Jan 1, 1960

By P. Lelong, P. Lacombe, J. Herenguel

IN previous studies on the effect of orientation on the rate of anodic oxidation of A1-3 pct Mg mono-crystals of high purity, certain anomalies were observed on the cold-worked metal. These anomalies were shown to correspond to regions of changed orientation within the grains resulting from plastic deformation.' In fact, they are deformation bands revealed by differences in rate of oxidation and produced by more or less continuous bending of the lattice about a [Ill] axis common to the original crystal and the band.2,3 Preliminary observations made after relatively large degrees of cold working revealed an approximate twin relationship between the bands and the surrounding crystal. Fig. 1 shows the etch figures formed on such a band and on the original monocrystal after a 67 pct rolling reduction. It is evidently not a true twinning, since there is a broad transition zone between the two systems, however the two extreme orientations are nearly in a twin relationship. It was decided to investigate these preliminary observations by progressive rolling-reductions on monocrystals of varied initial orientation. From these studies, which form the subject of the present article, it became apparent that the initial observation of an approximate twin relation between the bands and the monocrystal was simply a special case. Our experiments show that deformation in rolling proceeds by a mechanism analogous to those which have already been observed in the simpler cases of tension and compression. Micrography—in particular, the formation of etch figures—has been applied to the quantitative study of these orientations. In addition, observations have been made of slip lines, of thin oxide films yielding interference colors, of thick films in polarized light, and of etchants giving "engraving." These micrographic methods for studying orientation have established the orientation relationship without any ambiguity, whereas X-ray methods would have given only a statistical result because we were often dealing with thin bands (2 to 100 microns) and even narrower connecting zones covering a maximum of 20 microns. Specimen Preparation and Methods The Al-3 pct Mg alloy was prepared from 99.95 pct A1 and is of the type used industrially in France for brilliant anodized finishes under the name of Brillalumag. This material combines the normal commercial properties with an enduring brilliance due to the protection of a thick, but perfectly transparent, film of alumina.' The monocrystals were prepared by the method of critical deformation followed by prolonged annealing. Great care was taken to insure perfect homogeneity of composition, to eliminate included crystals,6,7 and to avoid the formation of undulations during oxidation. The critical deformation for this alloy is about 1.2 pct (1-l0/10x100) and the subsequent annealing was for one week at 500 °C after gradual increase of temperature (35°C per hr). The crystals thus prepared had a section of 10x5 mm and a length of 20 to 40 mm. Each of these crystals was polished electrolytically and etched for the formation of etch-figures with the classical reagent.' The orientation was then calculated from their angles, as measured with a goniometer microscope.

Jan 1, 1954

By H. Conrad, E. Stofel

The fracture behavior of 60-deg-oriented sapphire crystals was investigated for both tension and compression. Plastic flow on the basal plane was found to be a factor in reducing the tensile stress required to produce fracture in the temperature RECENT experiments1-' have shown that single crystals of a alumina (sapphire) can deform plastically, particularly at temperatures greater than 1000°C. The effect of this plastic flow on the fracture behavior of sapphire was not established, but range 1100º to 1500ºC. Mechanical twins, both (0001) and (0111) types, were produced by compression in the temperature range 1100" to 1300°C. Cracks propagated more readily along the twin boundaries than in the nontwinned crystal. experiments with other ceramic crystals4'5 have shown that plastic flow can initiate cracks that lead to catastrophic failure. This suggests by analogy that plastic flow might also be an important factor in the fracture of sapphire crystals. A recent experimental investigationS undertaken to determine the mechanism of plastic flow in sapphire provided an opportunity to study the type of fracture produced after various amounts of plastic shear strain. The results of this study of fracture are reported in the present paper. During the course of

Jan 1, 1963

By R. W. Hertzberg, R. W. Kraft

A study of the fracture behavior of unidirectwn-ally solidified Cu-Cr eutectic alloy was performed. Fractured whiskers, grain boundaries, and the interface between proeutectic Cr dendrites and the Cu matrix were the predominant failure initiation sites where grain size was larger. Strain induced void formation was restricted at lower solidification rates. This was attributed to a lack of adequate plastic constraint and a probable preferred orientation. A modification of the Crussard et al. model is presented to explain the appearance of "elongated dimples" on the shear fracture surface. A Cu-Cr alloy containing about 1.8 at. pct Cr solidifies by a eutectic reaction forming filamentary crystals of chromium within a continuous copper solid solution matrix.' Webb and Forgeng2 have shown by bend tests that the extracted chromium filaments, which are ordinarily curved and branched (due to random solidification), have the high strengths associated with whiskers. If an ingot of the eutectic alloy is unidirectionally solidified and appropriate control exercised over the thermal gradient, growth rate, and impurity level, the chromium fibers can be forced to solidify as fibers which are substantially parallel to the growth direction, Fig. 1. Uniaxial tensile tests on these straight chromium fibers extracted from controlled ingots3 have confirmed the earlier bend test results on curved fibers. Combining the facts that the strength and modulus of the chromium filaments are higher than the more ductile copper matrix and assuming that a "good bond" exists between the two phases, the Cu-Cr controlled eutectic system fulfills the requirements for effective fiber reinforcement of ductile matrices as established by studies on fiber glass reinforced plastics and other two-phase systems.4 Therefore, it was decided to study the fracture characteristics of morphologically simple specimens of chromium fiber reinforced copper (i.e., specimens of the controlled eutectic with substantially parallel reinforcing fibers) with the objective of establishing the dominant aspects of fracture. PREVIOUS WORK Comparatively little work has been done to understand the manner in which ductile alloys fail be- cause of the limited demand for this kind of information. Ordinarily ductility is specified for safety or similar reasons and when a part deforms plastically its useful life is terminated. In recent years, however, a number of investigators have begun to

Jan 1, 1963

By Robert T. Ault

The nature of fracture in unnotched tensile and notched tensile sheet and round specimens and V -notched and precracked Charpy-type sheet specimens of both wrought stress -relieved and re-crystallized molybdenum was investigated over the temperature range of -78° to 300°C. The sharp rise in fracture stress, for unnotched tensile samples, as the temperature is increased above the brittleness transition temperature (Tb), is found to be a result of an increase in flow stress due to plastic constraint and an increased strain rate which results from the onset of necking at Tb . Quasi-brittle fracture in notched tensile samples is found to occur when the tensile stress at the elastic-plastic interface, beneath the root of the notch, reaches a maximum critical value, which is independent of test temperature over the range from —78° to 25°C, but dependent on microstructure. In the temperature range between 150° and 300°C, unnotched tensile and notched tensile samples alike are found to fracture by a ductile fibrous tearing process which is discontinuous in nature, as a result of the competition between the processes of tearing, through continued plastic flow, and local work hardening. Results from the V-notched and fatigue-cracked Charpy-type impact tests demonstrate that crack initiation is the governing factor in the low-temperature (-78° to 25°C) fracture process for molybdenum. In recent years, there has been considerable interest, and a commensurate number of investigations, concerning the duc tile-to-brittle transition in refractory metals. There has not developed, however, a satisfactory explanation for the uniaxial tensile fracture-stress transition which accompanies the well-known ductility transition. This matter therefore warranted investigation. In a similar manner, the increased importance of notched tensile strength values in evaluating materials and in design criteria requires a better understanding of the factors which control the fracture behavior of notched tensile samples. In a previous investigation1 of the nature of initial yielding and fracture in notched sheet molybdenum at room temperature, it was suggested that plastic constraint was the controlling factor in governing the fracture behavior of notched samples. The final portion of this investigation was concerned with the fracture toughness of molybdenum. Of particular interest was the comparison of effective surface energies for fracture in V-notched samples with fatigue-cracked, Charpy-type samples in order to ascertain the relative importance of the initiation and propagation phases of the fracture process. MATERIALS AND TEST PROCEDURE Sheet tensile, notched tensile, and V-notched Charpy specimens were prepared from 50-mil, stress-relieved molybdenum sheet.* Half of these specimens were vacuum-annealed for 1 hr at 1200°C and 7.5 x l0-5 Torr and furnace-cooled to produce a relatively uniform grain size of 0.30 mm diameter. Round notched and unnotched tensile specimens were prepared from warm-rolled and swaged 5/8-in.-diam bar.* These specimens were vacuum-annealed for 1 hr at 1350°C and 5 x lom5 Torr and furnace-cooled to produce a grain diameter of 0.11 mm. Material analyses in ppm were: C N O H Sheet 290 10 4 1 Bar 50 30 30 2 The unnotched tensile sheet specimens had a 1/4-in. gage width and a 1-in. gage length. The unnotched tensile round specimens had a 9/32-in. gage diameter and a 1-1/4-in. gage length. The sheet and round notch tensile specimens are shown in Fig. 1. All of the notched tensile specimens tested were tandem-notched in order to study the location and mode of fracture initiation. The tandem-notched specimens were carefully machined so that the largest variation in notch depth on a single specimen was 0.001 in. Thus, when fracture occurs, the extent of plastic deformation that exists in the un-fractured notch section is that which exists just prior to fracture. All of the tandem-notched sheet specimens were electrolytic ally polished and chemically etched prior to testing. The V-notched Charpy-type specimens machined from the 50-mil sheet material had the standard dimensions of 2.125 in. long, 0.394 in. deep, and a 0.010-in. root radius. The unnotched tensile and notched tensile tests were conducted over the temperature range of -78° to 300°C, in a 10,000-lb Instron Universal Testing Machine, at a constant crosshead speed of 0.020 in. per min. The V-notched Charpy-type

Jan 1, 1964

By C. J. Beevers

Tlze influence of zirconium hydride precipitate mprphology on the fructure of Zr-H alloys tested at strain rates of 10- sec at 20° and - 196°C and at strain rates of -500 sec.-1 at 20°C has been inves-tigated. The critical stage in the embrittlement of these alloys was the fracture of the zirconium hyhide precipitates to form large interval cracks at a stress of 25,000 10 137,000 psi. In specimens con-temping up to 100 ppm H the preciptates existed as isolafed platelets in the zirconium matrix and their fracture as enhanced by low temperature (—196°C) and high strain rate (-500 set-f) loading. These resl~lts lead to the conclusion that the rate of strain hardening of the zirconium metal controls the frac-tzrm of the hydride platelets. Increased hydrogen contents of 500 to 2000 ppm resulted in an increase in the 1)volume fraction and size of precipitates and crlso led to crack propogation in the hydride at both 20 and —196C at the low strain rates (10'* sec-'). Quenching led to refinerment of hydride precipitate size and reduced the degree of embrittlement at — 196°C; this effect is attributed to the absence of fracture of the fine precipitates. The formation of zirconium hydride precipitates has been shown to be the cause of hydrogen embrittlement of zirconium.' Several investigators'-" have studied the problem in broad outline, demonstrating that impact-loading conditions, testing temperatures below room temperature, and increasing hydrogen content produce increased brittleness. For example, Muehlenkamp and schwope2 showed that the transition temperature for notched impact tests was raised from 150" to 350°C on increasing the hydrogen content from 45 to 490 ppm. The degree of embrittlement is also controlled by the morphology of the zirconium hydride precipitates. The solubility of hydrogen in zirconium decreases from 600 ppm at 550°C to 10 ppm at 20"C,~ so that the form of the zirconium hydride precipitates (ZrH2) can be modified by varying the cooling rate through the Zr-aZr + ZrH2 phase boundary.= Forscher showed that quenching a specimen containing 35 ppm H from above 315°C resulted in a reduction in area of 70 pct at -196"C, whereas slowly cooling from above 315°C resulted in a ductility of half this value. The role of the hydride precipitate in the fracture process has been examined by Young and schwartz6 and more recently by westlake.' From metallo-graphic observations on slowly cooled Zr-H alloys they have suggested that cracks are nucleated in the hydride precipitates by the interactions of twins in the zirconium metal with the hydride. The experiments reported in this paper show that crack propagation in the zirconium hydride precipitates is the critical stage in the embrittlement of Zr-H alloys. The factors influencing fracture of the hydride precipitates and crack propagation in the zirconium metal will be related to the problem of embrittlement. EXPERIMENTAL TECHNIQUES The zirconium used in these experiments was produced from an ingot of vacuum arc-melted iodide zirconium forged down to 1 in. diameter at 800' to 850°C. The 1-in.-diameter bar was surface-machined and cold-swaged to 0.375 in. diameter. After a vacuum anneal at 800°C for 1 hr the hardness was 60 to 70 Vdh. The total impurity content was approxi-

Jan 1, 1965

By G. C. Gould

The nature of freckle segregation is determined by chemical analyses, microradiograplzy, and electron microprobe. In addition, the influence of chemistry variation on freckle formation is studied in laboratory experiments. It is demonstrated that controlled laboratory solidification can produce freckle segregation. "FRECKLE" segregation is a discontinuous, rod-like segregation observed in vacuum consumable -electrode ingots. Figs. 1 and 2 show this segregation as pencil-like, dark etching areas of segregation found in longitudinally and transversely sectioned consumable-electrode ingots. In most cases the segregation is perpendicular with respect to gravity and parallel to the longitudinal axis of the ingot. The segregation is most often encountered at or around midradius in large vacuum consumable-electrode ingots. The austenitic alloys, A-286* and 718, † have shown particular susceptibility to this mode of segregation. The origin of these rodlike pockets of segregation is not well-understood. It has been suggested that the segregation is a result of a portion of the electrode dropping off and passing through the arc un-melted. On the other hand, smeltzer1 has demonstrated the freckle segregation in A-286 to be comprised of low-melting constituents relative to the matrix melting point. The discontinuous nature of the segregation is the most perplexing facet of the freckle-segregation problem. It was to gain some insight into this part of the problem that this work was undertaken. I) PROCEDURE At the outset of the work identification of the phases present and the elements concentrated in the freckle areas was undertaken. The electron micro-probe was used to determine general enrichment as well as -specific phase chemistry. Microradiography using cobalt and chromium radiation was also used on the freckle areas again to determine the elements involved in the segregation. X-ray diffraction patterns were made from portions of these same foil specimens. Optical microscopy and Knoop hardness measurements were also used

Jan 1, 1965

By R. W. Gurry, L. S. Darken

The solubility of cementite in austenite is computed by thermodynamic methods from the observed solubility of graphite. It is found that the solubility of cementite is greater than that of graphite in the entire austenite temperature range. Thus the prior discrepancy between this portion of the phase diagram and the observed metastability of cementite is partially resolved. FOR several years it has been apparent that a serious discrepancy exists in certain observations pertaining to the Fe-C system. Direct experimental data indicate: 1-That the curve representing the solubility of graphite in austenite'" crosses that for cementite4 at about 945°C as shown in Fig. 1. 2— That graphite and austenite saturated therewith are stable1 relative to cementite at all temperatures between the eutectoid, about 723°C, and the eutectic, about 1153°C. These observations are mutually incompatible in view of a well-known consequence of the second law of thermodynamics, namely, that the stable phase (presumably graphite at all temperatures) has a lower solubility than the metastable phase (presumably cementite). Hence either 1 or 2 above must be in error; either the measured solubility of graphite or of cementite, or the observation as to the stability of graphite, is in error. Our present purposes are: 1—To collate the available data on cementite and prepare a table of HO — HO° and of (Fa— HO°)/T. This tabular method seems the best and most convenient way to represent the heat and free energy of formation. 2—To determine whether the measured solubilities of cementite and graphite in austenite are in accord with the above table and the measured thermodynamic properties of austenite, in order to resolve, if possible, the existing paradox of these two solubilities. Enthalpy of Cementite The enthalpy of cementite at 273 °K, H279 — HOcem, was computed by integration of the low temperature heat capacity as measured by Seltz, McDonald, and Wells" 68" to 298 °K) and as given by the Debye functions recommended by them (0" to 68°K); the result is included in Table I. At higher temperature HCem — H,,"" is given by Kelley who used the data of Naeser7 (298" to 1037°K) and of Umino8,9 (273° to 1923°K). We have recalculated Hcem — H273 cem from the data of UminoO in the following way. In the equilibrated alloy at temperature the weight fraction of cementite Pct c -Pct cr is PctC -PctCr designated f(C), and the

Jan 1, 1952

By R. H. Tien

Temperature distribution as well as position of the solidified front is solved by means of "heat balance integral", for the case of freezing a slab with time-dependent surface temperature. Numerical solutions for the cases of linear variation and exponential decay for surface temperature are given. Application also includes solidification of casting. An increased interest in the heat-transfer problem involving a change of phase has been developed in recent years. Practical problems include solidification of a casting, freezing and thawing of soil, ice formation, and others. Despite the importance of the topic, a literature search reveals relatively few solutions which may be extended to practical problems. Due to mathematical complexity, which comes from the nonlinearity of governing differential equations, exact analytical solutions which have been published are limited to a few cases with simple boundary conditions. Although numerical solutions of these problems have become available after highspeed digital computers were introduced, lack of simple and general methods of programming for computation makes this approach impractical. The case of the semi-infinite slab with constant surface temperature was solved in the 19th century. In honor of Neumann, who first found an analytical solution, this kind of problem is generally referred to as the Neumann solution. As has been shown in Fig. 1, the problem to be analyzed is the freezing of a semi-infinite region (x > 0) which is initially liquid at the melting temperature with the surface (x = 0) maintained at time-dependent temperature. This analysis can be applied to the study of many casting processes where most of the heat removal is essentially unidirectional. "Heat balance integral" which has been used by Goodman1 is employed in this analysis. The concept of "heat balance integral" is to define a quantity, d(t), called the thermal layer. Beyond this thermal layer, for all practical purposes, there is no heat transfer, and the region is at the equilibrium temperature. "Heat balance integral" is obtained by integrating the conduction equation with respect to the space variable over this thermal layer d(t). Choosing some plausible temperature distribution, usually a polynomial or a finite trigonometric series in the space variable, this integral equation becomes an ordinary differential equation, with time as the independent variable, which can be solved by classical methods. The thermal layer and "heat balance integral" are equivalent, respectively, to the boundary-layer thickness and the momentum integral in hydrodynamics. A modern account of Prandtl's concept of the boundary layer and von Karman's momentum integral may be found in Ref. 2. Although the problem considered here has been limited initially to uniform melting temperature, the present method is equally applicable to the case with arbitrary temperature distribution in the liquid. STATEMENT OF THE PROBLEM The physical situation and coordinate system used in the problem to be analyzed are shown in Fig. 1. Notations used are listed in the table of nomenclature. Let us assume a semi-infinite region extending over positive x, initially at the uniform melting temperature. At the surface x = 0, a time-dependent temperature, which has a numerical value

Jan 1, 1965

By P. A. Fisher, J. B. Wilson, D. J. Whitehead, C. J. P. Ball, A. C. Jessup

The properties of a new magnesium alloy ZT1 containing 3.0 pct Th, 2.5 pct Zn, 0.7 pct Zr are described. The alloy possesses good creep and fatigue resistance up to 650°F, is free from microporosity, and is readily sand-cast. ZT1 is shown to be superior to zinc-free Mg-Th-Zr alloys. THE advent of the jet engine created a demand for a light sand-casting alloy capable of being cast into large complex shapes and capable of resisting creep at temperatures up to 500°F. This demand has been largely met by alloys of the magnesium-cerium mischmetal-zirconium types, containing about 3 pct Ce mischmetal and 0.7 pct Zr, typified by Elektron magnesium alloys MCZ and ZREI, the latter alloy also having a zinc addition of 2.5 pct. These alloys utilize the valuable properties at elevated temperatures conferred by the addition of rare earth metals to magnesium, a fact which has been known for many years and discussed by several investigators.1-1 Murphy and Payne8 showed that the addition of the powerful grain-refining element zirconium to Mg-Ce mischmetal alloys produced alloys with attractive room temperature properties combined with good creep properties and castability. With the increasing power of modern jet engines the temperatures to which some of the magnesium parts are subject are likely to exceed the safe working range of the cerium-mischmetal-containing alloys, and at the beginning of the research considerable interest had been shown by aeroplane engine designers in a magnesium sand-casting alloy suitable for service at higher temperatures, e.g., 600°F and above. At an early stage in the development of this type of alloy a check on the fatigue properties at elevated temperatures indicated that, since the fatigue limit even at 108 eversals was appreciably higher than any permissible creep stress, the main emphasis of the research could be concentrated on creep behavior. The primary aim in developing the new alloy has therefore been to attain maximum creep resistance; but due consideration has also been given to other important properties such as castability, tensile strength, and cost. It is by now well established that it is not possible to correlate creep strength with other short time mechanical properties such as are obtained in tensile

Jan 1, 1954

By Chester T. Sims, Robert I. Jaffee

The thermoelectric behavior of the Pt—Pt-Re thermocouple and the resistance of rhenium to attack by certain molten metals is discussed. In addition, data are presented on the stress-rupture behavior of drawn wire, the tensile characteristics of rolled sheet, the variation of Young's modulus with temperature, and the effect of specimen size and fabrication method on the work harden ability. Mechanical properties of thoriated rhenium are discussed. This includes data on the effect of thoria in rhenium on tensile properties, ductility, work hardening, and recrystallization. RECENT work by the authors', has described methods of fabrication and some of the physical and mechanical properties of rhenium. Rhenium was established as a high melting, dense, refractory-type metal with favorable mechanical properties. In addition, Todd and co-workers' and others" have studied such properties of rhenium as the work function, specific heat, and the resistance of rhenium to the water cycle. Revelation of these and other properties has led to serious consideration for application as electrical contacts, high temperature thermocouples, and wear resistant materials. chanical properties reported previously,' several additional examinations have been conducted. The stress-rupture behavior and the Young's modulus of rhenium have been investigated at elevated temperatures. Tensile data have been obtained for rolled sheet, and a study of the relative work hardening characteristics of rod, wire, and sheet has been conducted. Variation of Modulus of Elasticity With Temperature—The Young's modulus of a % in. diam annealed rhenium rod was determined from room temperature to 880"C (1620OF). The rod, approximately 6 in. in length, was activated in a transverse vibration apparatus suspended in a furnace. The resonance frequencies of the rod were measured and used to calculate the moduli values. The driven frequency was 569 cycles per sec, and a protective helium atmosphere was used. The data, plotted in Fig. 1, show that the modulus decreases in an approximately linear manner with temperature over the range tested.

Jan 1, 1957

By R. L. Smith, I. G. Greenfield

The binary system Ga-Sb has been investigated by thermal, X-ray, and metallo-graphic methods. 'The intermetallic compound GaSb melts at 705.9OC and forms a eutectic with antimony at 11.8 atomic pct Ga. This eutectic melts at 589.8OC. A eutectic appears to be formed at 29.8°C but is too close to the composition of pure gallium to be detected. IN the course of an investigation of the semiconducting properties of the intermetallic compound, GaSb, the phase equilibrium between gallium and antimony has been investigated. Recently, the phase diagram of similar systems, such as In-Sb,' In-AS,' and Bi-As3 have been determined. These diagrams have the same general appearance in that an intermetallic compound is formed at 50 atomic pct and a eutectic is formed on both sides of the intermetallic compound. Jenny,& who has been investigating the semiconducting properties of intermetallic compounds, has concluded from thermal data of several alloys that the phase diagram of the Ga-Sb system resembles those mentioned previously. This paper represents a more detailed study of the Ga-Sb equilibrium. Experimental Procedure The gallium that was used to prepare the alloys was obtained from A. D. Mackay Inc. and the Aluminum Co. of America; the latter reported the purity as 99.95 pct. The antimony was obtained from Bradley Mining Corp. who specified a purity of 99.997 pct. Since the intermetallic compound of GaSb was prepared primarily to be used for further studies of the semiconducting properties, additional purification by a standard zone-melting technique under an atmosphere of hydrogen was performed. Hall-effect measurements on this material indicated an impurity content of less than 3 ppm.5 The antimony also was purified by zone melting and used in conjunction with the compound GaSb to make the necessary alloys for the determinations of the antimony-rich side of the phase diagram. The antimony-rich alloys were chill cast in Vycor tubes which were evacuated to a pressure of less than one micron. Since these alloys expand on freezing, precautions were taken to prevent oxidation of the ingot in the event the tube fractured. To insure homogeneity, the brittle alloys were ground and then placed in the furnace for the thermal-arrest determinations. Since the cost of gallium is high, the experimental procedure was complicated somewhat because of the necessarily limited sizes of the melts. In order to economize, the gallium-rich side of the diagram was determined by using a 35 g ingot of pure gallium initially and adding increasing amounts of antimony in order to obtain additional alloys. The furnace used in the determination of the cooling curves is illustrated in Fig. 1. A 2¼ in. quartz tube, sealed at one end, was fitted with a brass flange which was attached with DeKhotinsky cement. The brass collar was water cooled to prevent the cement from softening. An "0" ring was used to provide a seal between the brass collar and the furnace cover. Nichrome ribbon was wound around a 2 ½ in. asbestos-covered copper core which was used to reduce the thermal gradient in the furnace. The insulation consisted of alternate layers of asbestos and aluminum foil surrounded by sil-o-cel refractory and

Jan 1, 1956

By Gordon G. Bentle, W. P. Fishel

GREINER, Marsh, and Stoughton1 have reviewed the literature in a monograph on the iron-silicon system. The lack of agreement among the various studies may be due to the difference in the purity of materials in some cases. The results of the X-ray method indicate only a general rather than a specific limit of the y loop. The iron-titanium system was investigated by Roe and Fishel,' whose results are used in determining the iron-silicon-titanium y loop. The literature indicates that no study has been made thus far of the iron-silicon-titanium system in the y loop region. Experimental Procedure The alloys were made from Armco iron, 99.86 pct Si, and 98.5 pct Ti. The titanium contains 1.07 pct Fe. The Armco iron contains 0.01 pct C, 0.005 pct Si, 0.02 pct Mn, 0.006 pct P, 0.01 pct S, and 0.04 pct Cu. A dilatation sample of Armco iron was prepared in the same manner as were the other samples. Several dilatation runs indicated that Ac3 begins at 905°C and ends at 910°C, which compares favorably with the study of Wells, Ackley, and Mehl' employing specially purified iron. All alloys were melted in an induction furnace in Alundum crucibles and were top poured into baked core sand molds. The ingots weighed about 600 g as cast. Dilatation samples of 4 in. by % in. diam were taken from the bottom end of the ingot, from which turnings for analysis were taken. Turnings from each end of two of the samples indicated that the alloys possessed uniform silicon content. A hole was drilled halfway through each end of a 4 in, dilatation sample. A chromel-alumel thermocouple was inserted in each hole and the surrounding metal peened in to hold the thermocouple in place. Fig. 1 represents the dilatation apparatus. The heating unit is an Alundum tube wound with resistance wire; the dilatation tube is a McDanel combustion tube; the push rod is zircon; the dial gage is graduated in 0.0001 in. and was vibrated to prevent sticking. A blank run over the temperature range of interest gave no significant dilatation. The thermocouples were attached to a multiple recording micromax which indicated the temperature at each end of the sample at 35 sec intervals. A Lindberg control unit governed the rate of heating of the furnace, and lowering or raising the

Jan 1, 1957

By J. J. Hauser, H. C. Theuerer

A cathode sputtering technique is described which elin7inates the need for ultrahigh vacuum in preparing thin films of materials sensitive to gaseous impurities. This technique uses a fraction of the atoms sputtering within an anode container to getter actice gases, such as HzO, Oz, and Nz. The gases alzd gettering metal are deposited on the container walls, thus shielding the coating zone of the system from contamination. The use of the method for preparing superconducting-normal metal couples such as Ph-Cu and Ph-Pt is described, and the properties of the individual and composite films are given and discussed. GETTER sputtering is a method which greatly simplifies the preparation of thin films in cases where composition control is critical. A major difficulty with conventional sputtering and other vacuum-deposition techniques is the contamination of the forming film caused by residual gases, such as H20, CO, Oz, and Nz, in the coating equipment. The difficulty arises from the fact that even when the residual pressure in the system is as low as 1 x 10"6 Torr, with a deposition rate of 10A per sec, there are as many contaminating gas collisions with the substrate as there are with film-forming metallic atoms. It is not surprising, therefore, that with reactive metals, such as tantalum and niobium or with semiconductors, such as silicon and germanium, films with properties far different from the starting materials are obtained. In the case of niobium and tantalum, deposited either by sputtering or vacuum evaporation in systems with reactive gases at pressures of the order of 1 x l0-' Torr, the loss of superconductivity is traceable to interstial oxygen or nitrogen. On the other hand, working in vacuum of the order of 1 x l0-" Torr, Marchand and enema' have shown that superconducting films of tantalum with properties approaching those of bulk material are possible. At this level of gaseous impurities -lo6 metallic atoms arrive at the substrate before a contaminating collision occurs again assuming a deposition rate of 10A per sec. It is evident from the above that any successful vacuum technique requires the elimination of reactive gases from the region of the system where coating is occurring. Getter sputtering accomplishes this using conventional vacuum equipment with residual pressures in the 106 Torr range. In fact? vacuum systems with residual pressures of lo-" Torr are adequate for most purposes. With this method, sputtering is confined within an anode can and, by geometric design, sputtering itself is used to purify the argon at the lower and upper parts of the system by the gettering action of the reactive metal. In consequence, the central region of the system where coating occurs is shielded from gaseous contamination. Getter sputtering is particularly useful for the preparation of alloy and compound films. With this method, if a cathode of homogeneous composition is bombarded with high-energy argon ions, transfer of material to the substrate having the same composition as the cathode will occur. This is true after an initial equilibration time, even though the constituents of the cathode may have different sputtering rates. During equilibration, the surface of the cathode changes composition due to differences in sputtering rate, but mass conservation demands a steady-state condition such that the atoms sputtered from the surface have the same composition as the cathode material from which the surface is generated. GETTER-SPUTTERING APPARATUS The original form2 of the getter-sputtering apparatus is shown in Fig. 1. It consists of a closed nickel or stainless-steel can 4 in. tall and 2-3/8 in. in diameter. Mounted symmetrically from each end

Jan 1, 1965