By George Mah, Charles Wert

Internal-friction peaks caused by diffusion of oxygen and nitrogen have been observed in ytterbium. They are thought to be caused by the redistribution, under stress, of strain dipoles around an interstitial oxygen or nitrogen and a neighboring substitutional impurity. With the use of a simple geometrical model, diffusion coefficients for oxygen and nitrogen between special interstitial sites have been calculated. a) APPLICATION OF INTERNAL FRICTION TO MEASUREMENT OF DIFFUSION RATES IN DISSOLVED INTERSTITIAL ATOMS In bcc metals, the interstitial atoms occupy the centers of cube faces (0, 1/2, 1/2), or their equivalents, the center of the cube edges (0, 0, 1/2). An interstitial atom in this position causes an aniso-tropic distortion in the lattice. When stress is applied, mechanical relaxation can take place by the movements of the interstitial atoms. This relaxation has been used to obtain information concerning the movements of the interstitial atoms in the bcc metals. Data for these alloys have been compiled by Stanley and Wert. Other researchers have extended the investigation of interstitial diffusion to the close-packed metals. Gupta and weinig2 found an oxygen peak in a titanium, the height of which is linearly dependent on the oxygen concentration. They assumed, therefore, that they were dealing with movement of atomic ally dispersed oxygen in titanium. KG and wang3 determined that the diffusion coefficients of carbon in fcc steels and in nickel obtained by internal-friction methods were consistent with those obtained by macrodiffusion methods at much higher temperatures. Bisogni found oxygen and nitrogen peaks in hafnium by use of which he deduced the diffusion coefficient of these gases in hafnium. He observed further that the half-widths of these peaks corresponded almost exactly with those of a single-relaxation process; he assumed it to be caused by movement of atomically dispersed oxygen and nitrogen. From these studies, the deduction can be drawn that, in general, diffusion data can also be obtained for the interstitial diffusion in close-packed metals (or more precisely, in slightly impure close-packed metals). One group of such metals for which little data exist for the diffusion of dissolved oxygen and nitrogen is the rare earths. They have great affinity for gases, which enter solution interstitially. In this investigation results were obtained for the Yb-O and Yb-N interstitial solid solutions with traces of substitutional impurities; these solid solutions are of fcc structure. b) MECHANISM OF THE RELAXATION IN FCC CRYSTALS In the fcc structure, an interstitial gas atom is usually situated in the octahedral position (1/2, 1/2,

Jan 1, 1964

By A. G. Guy

Zinc vapor from a reservoir of liquid zinc maintained at lower temperatures was diffused into sets of copper-zinc alloys at 759° and 870° C and into sets of silver-zinc alloys at 650° and 700° C. Each set of ,four copper-zinc alloys consisted of pure copper and 90/10, 80/20, and 70/30 brass. Similarly the set of silver-base alloys consisted of specimens containing 0, 7, 15, and 20 pct Zn. Natural markers at the initial surfaces of the specimens ware "trapped" under a thin electroplate and their depth of burying was measured after diffusion. The ratio of diffusivities of the two components determined from these data and the chemical diffusion coefficient calculated by the Matano method agreed with previously reported results. The line of markers was irregular and was often discontinuous when a grain boundary was crossed. TECHNIQUES involving the vapor phase have been widely employed in studying diffusion phenomena in metals. Many investigators have evaporated the more volatile component from an alloy, but it is generally believed that the porosity created under these conditions interferes with adequate interpretation of the experimental results. The extensive work of Gertsriken6 has been criticized on this score. Accary1 found that the diffusion coefficient for de-zincification of brass is larger by a factor of five than that for zincification, although he attributed the difference to a higher vacancy concentration under conditions of dezincification. Balluffi and siegle2 thoroughly investigated the technique of adding a more volatile component to a less volatile base metal as a means for studying diffusion. They verified that no porosity forms in a brass under these conditions and that the diffusivities of the two components can be determined from observations of the motion of markers originally placed on the surface of the specimen. The mathematical analysis that they developed for treating the experimental data was modified in a later note, but essentially it involved using the graphical Boltzmann-Matano method that is customarily applied to solid-solid diffusion couples. The experimental method used in the present research was similar to that employed by Balluffi and Siegle except for two modifications. Balluffi and Siegle used alloy chips as the source of metal vapor. This procedure has the disadvantage that the concentration of solute at the surface of the specimen changes during the diffusion experiment as the alloy content of the chips is gradually decreased. This disadvantage was overcome by employing liquid zinc as the source of zinc vapor in a manner similar to that described by Herasymenko.9 There was then no limitation on the amount of solute usefully available, and several relatively large specimens could be diffused in a given experiment. The second modification was the use of natural markers on the surface of the specimen rather than larger, artificial markers, such as the alumina powder employed by Balluffi and Siegle. It was expected that the fine, natural markers would permit more precise measurement of the buried interface as in the case of ordinary sandwich specimens.10 EXPERIMENTAL The experiments were designed so that zinc from the vapor phase would maintain a constant zinc content at the surface of pure copper (or silver) and

Jan 1, 1960

By T. S. Lundy, J. I. Federer

Chemically purified Zr95and Cb95 have been used in determining self-diffusion coefficients in the bcc phase of iodide zirconium over the temperature range of 900o to 1750°C. The temperature dependence of the diffusion coefficients could not be described by the usual Arrhenius-type equation over the entire temperature range. Values of the apparent frequency factors (D0)a and activation energies (Q)A for ZR95 varied from 4.8 x 10-6 to 2.5 x 10-2 sq cm per sec and 20,700 to 46,900 cal per mole, respectively, between 900°and 1750°C. Similarly, for Cb95, values of (Do) a and (Q)A varied from about 2.4 x 10'5 to 0.25 sq cm per sec and 26,500 to 56,800 cal per mole, respectively. The data may be described in terms of the a to ß transition temperature of 1136 °K and the absolute temperature of the diffusion anneals by the following eauations: SEVERAL studies on the diffusion of Zr95 in zirconium have been reported.1"5 The values of the constants contained in the usual Arrhenius-type equation for describing the temperature dependence of the diffusion coefficient, D = Do exp [- Q/(RT)], are summarized in Table I. The reported values of Do, the frequency factor, and Q, the activation energy, are seen to vary by factors of about 60 and 1.6, respectively. Examination of the data from any one study indicated reasonable consistency of measurements. The large discrepancies of over-all results, therefore, cannot be explained on the basis of experimental scatter. One possible explanation for the differences in results could be a varying impurity content of the zirconium. Another possibility is that the radioactive daughter, Cb95, influenced the values of some of the determined diffusion coefficients. Therefore, the first of the three purposes of this study was to reconcile the large differences in diffusion results that have been obtained. Several empirical relations have been proposed to relate the diffusion coefficients in solids with physical properties, such as the absolute melting point, the heat of fusion, and the heat of sublimation.

Jan 1, 1963

By Hsun Hu

Direct observations were made on the recrystalli-zntion of a cold-rolled (110) [001] crystal of 3 pct Si-Fe by annealing thin sections of the specimen inside the electron microscope during examination. Subgrain formation, presumably by polygonization, occurs rapidly, followed by a slow increase in the subgrain size before recrystallization can be detected. No migration of the subgrain boundaries was observed, and the formation of recrystallization nuclei by coalescence of subgrains is suggested. Re-c~ystallization characteristics of various texture components were individually examined. AS reported in a previous paper: orientations of the various deformation texture components in a 70 pct cold-rolled (110) [0011 crystal of 3 pct Si-Fe were completely confirmed by transmission electron diffraction patterns taken at various areas of the specimen. These orientations can be summarized as follows: Over most areas of the deformed crystal (111) planes are parallel to the surface. These areas correspond to either $- the two main defor: mation textures, the (111) [112] or the (111) [112].2-5 Within a few areas, (100) planes parallel to the surface are frequently found. These areas represent the minor deformation texture component, the (100) [Oll] type, which is derived from rotated Neumann bands.2'4'5 Only in very rare instances are (110) planes found parallel to the surface. This orientation corresponds to the very weak texture component of the (110) [001] type. In a pole figure, this (110) [0011 orientation is located within the orientation spread between the two main (111) [1121 type textures. Usually the electron diffraction patterns taken at various areas of the specimen are very simple ones, i.e., for any one area the pattern consists only of sharply defined spots of a single orientation. In some areas, however, more or less continuous rings of weaker intensities are superimposed on a simple pattern, indicating the presence of a wide range of additional orientations. In order to understand in detail the recrystallization of this cold-worked crystal, the recrywtallization characteristics of each of the various deformation texture components must be examined. This can best be done by using a high-temperature stage and transmission electron microscopy techniques, whereby small areas corresponding to the various texture components can be selected individually for examination. The present paper presents results obtained by this method. MATERIAL AND METHOD Specimens were prepared from a previously studied1 single crystal of a commercial grade 3 pct Si-Fe alloy with an initial orientation (110) [00l], cold-rolled 70 pct from 0.014 in. to 0.004 in. in thickness. Thin foils were prepared by electrolytic polishing as described in the earlier paper.' Specimens of this thin foil were then mounted in a high temperature stage similar to the one designed by Whelan.6 A direct current was used as the heating source. The temperature of the heating grid was calibrated by means of a Pt vs Pt-10 pct Rh thermocouple in a vacuum chamber (0.01 to 0.02µHg). Maximum variation within the temperature range of 250o to 000°C was about ± 25°C. After the desired areas were selected for examination, the specimen was heated to a low temperature for some time while the selected area was constantly watched. When no further change in structure and orientation could be observed, a higher temperature was applied. Photomicrographs and diffraction patterns were taken from time to time during examination, with the heater temporarily turned off* while the photographs were

Jan 1, 1962

By A. R. Troiano, E. A. Steigerwald, F. W. Schaller

The kinetics of crack propagation in a hydrogenated high-strength steel at subzero temperatures indicated that cracking progressed in a discontinuous fashion. The delayed failure process thus involves a series of crack initiations rather than the continuous growth of a single crack. The incubation time required for the initiation of delayed failure was controlled by the diffusion of hydrogen. The activation energy for the process was 9120 cal per g-alom. As the test temperature was lowered the incubation time constituted a greater percentage of the total tinze to fracture, and al -50°F the incubation and fracture times were essentially coincident resulting in instantaneous, catastroplzic fracture. A unique feature of hydrogen embrittlement is the delayed failure process in which the material fails under the action of a sustained load even though it is capable of supporting a higher load for a finite period of time.')' Delayed failure of steel and titanium is characterized by an incubation time, preceding the initiation of a crack in a highly localized region, and the subsequent growth of the crack to ultimate failure.3-5 The kinetics of crack growth in hydro-genated high-strength steels have been studied through the use of resistance measurements and have an important bearing on the mechanism of delayed failure. Delayed failure is believed to be merely a facet of hydrogen embrittlement in which sufficient time is allowed during a test for hydrogen diffusion. The current theories employed to explain hydrogen em-brittlement can be grouped into two types. one6-8 explains the embrittlement on the basis of the pressure exerted by molecular hdrogen in lattice voids or defects while the other9-10 attributes the embrittlement to the influence of hydrogen in the lattice. The mechanism used to explain the nature of the crack kinetics in delayed failure is based on the stress-induced diffusion of hydrogen to the area of maximum triaxiality.3 When the hydrogen concentration in this region reaches a critical value, a crack is nucleated. This initial crack propagates instantaneously until stopped by the higher fracture stress of the adjacent material of lower hydrogen content. The continuation of cracking must then await the further diffusion of hydrogen to the new region of triaxiality near the base of the crack where another initiation will occur. From this mechanism it follows that crack propagation is nothing more or less than a series of initiations with limited fracture. The purpose of this investigation was to examine the kinetics of crack growth in an effort to determine whether or not the process was discontinuous. Studies of crack propagation were conducted at low temperatures to retard the diffusion of hydrogen which is presumed to be the rate controlling process in delayed failure. MATERIALS AND PROCEDURE Specimen Preparation—A commercial heat of air-craft quality SAE-AISI 4340 steel, designated as Heat G, was furnished by the Republic Steel Co. in the form of %-in. hot-rolled bars. The material had the following chemical analysis: Composition of 4340 Steel—G Heat C Mn Si Ni Cr Mo 0,395pct 0.82pct 0.29pct 1.76pct 0.85pct 0.25pct Notched tensile specimens with less than a 0.001 in. radius, Fig. 1, were used throughout the investigation. The specimens were heat treated to a 230,000 psi strength level according to the following sequence: a) Normalize bar stock at 1650°F for 1 hr, b) Stress relieve at 1200°F for 4 hr and furnace cool,

Jan 1, 1960

By James C. M. Li, J. Weertman

James C. M. Li (United States Steel Covp.)—The author has discovered a single analytical relation between the minimum, or the steady-state, creep rate and the applied stress confirming a statement made earlier by orn" that such relation should exist and should reduce to the power law at low-stress levels and to the exponential law at high-stress levels. However, as pointed out by the author, all the available theories of creep are not adequate to explain such a single relation. Inspired by such a statement, I have made a suggestion concerning a possible explanation13 of the new relation. This is based on the concept that the rate-controlling step is the cooperative motion of a short dislocation segment. The nature of and the reason for the cooperation have been discussed13 as well as the reason why the motion of the dislocation could be controlled by the mobility of the short segments. A natural short segment has been proposed13 to be the node formed at the intersection of two dislocations. The reason why the node may contain only a few atoms has not been discussed and the application of the proposed model to all the metals and alloys reported in this paper has not been attempted. It seems appropriate to include these in this discussion. The model was partly inspired by the substructure recently observed in the electron microscope on creep specimens. One such example is shown in Fig. 48 in Darken's Campbell Memorial Lecture. The substructure is a collection of dislocation intersections and irregular networks. No pileups have ever been observed in such specimens. A closer look at the network indicates that one set of dislocations is more straight than the other set sug- gesting that the other set may be mobile in the plane of the net. Since, for the network to survive the creep deformation, some dislocation reaction has to take place at the intersection of the two sets of dislocations, the mobile dislocation, even if it can slip in the plane of the net, will have difficulty in moving at these intersections. To illustrate, an idealized network is shown in Fig. 9. The thin lines represent the set of dislocations which are mobile and can slip in the plane of the net except at the nodes which are formed at the intersection of the two sets of dislocations. The other set of dislocations, represented by the thick lines, may have a Burgers vector which is not parallel to the plane of the net, and therefore may be immobile. Because of this nonparallel Burgers vector, the Burgers vector of the node, which is avectorial sum of the Burgers vectors of the two sets of dislocations, will also be nonparallel to the plane of the net. Therefore, the node cannot slip in the plane of the net and the set of mobile dislocations will have to drag the node along as indicated in Fig. 9. Now the problem is how many atoms could be involved in the nodes. Exact calculation of the length of the node is a difficult task especially since the length should be a steady-state length and not an equilibrium length. An estimate of the equilibrium length can be made by balancing the line tension of all the dislocations. The results would be a small fraction of the length 1 between nodes as shown in Fig. 10. In some instances such a calculation shows that the node will not be formed. But, since the calculation is only approximate, it does not rule out the possibility of the formation of a short node. In other instances the equilibrium length of the node is an appreciable fraction of I. Such a node would

Jan 1, 1963

By T. H. Alden

T. H. Alden (General Electric Research Laboratory)—This paper as well as earlier ones of Dr. Wood represent an important contribution to the experimental description of fatigue fracture. The mechanism of fracture proposed by the authors, however, is not established by this data nor supported by other data existing in the literature. Although taper section metallography provides a rather detailed picture of fatigue crack geometry, photographs so obtained must be interpreted with care. The narrow bands revealed by etching, frequently associated with surface notches, are labeled by the authors "fissures". Measurement shows, taking into account the 20 to 1 taper magnification, that the depth of these structures is at most 2 to 3 times the width. This distinction is important in the conception of a mechanism of crack formation. It is difficult, for example, to imagine a deep, narrow fissure arising from a "ratchet slip" model. A surface notch, on the other hand, may form easily by this mechanism. The notches observed in the present work are the subsurface evidence of the surface slip bands or striations in which fatigue cracks are known to originate.4-6 It is clear that an understanding of the structure of these slip bands is of key importance in understanding the mechanism of fracture. The evidence presented shows that these regions etch preferentially, possibly because they contain a high density of lattice defects, or as the authors state equivalently, because they are "abnormally distorted." However, it is not possible to conclude that the distortion consists of a high density of vacant lattice sites. The fact of a high total shear strain in itself does not assure a predominance of point defects as opposed to other defects, for example, dislocations. Other evidence in the literature which suggests unusual densities of point defects formed by fatigue7-' refers not to the striations or fissures, but to the material between fissures (the "matrix"). If a choice must be made, the preferential etching would seem to be evidence for a high dislocation density, since dislocations are known to encourage chemical attack in copper;g no such effect is known for the case of point defects. A third alternative is that the slip bands are actually cracked, but that near its tip the crack is too narrow to be detected by the authors' metal-lographic technique. In this case the rapid etching can be readily understood in terms of the increased chemical activity of surface atoms. Unless a vacancy mechanism is operative, the motion of dislocations to-and-fro on single slip planes will not lead to crack growth. Point defect or dislocation loop generation are the principal non-reversible effects predicted by this model. In any case, the nonuniform roughening of the surface in a slip band6 requires a flexibility of dislocation motion which is not a part of the to-and-fro fine slip idea. The same is probably true of crack growth by a shear mechanism. Either some dislocations must change their slip planes near the end of the band and return on different planes,'0 or dislocations of opposite sign annihilate." The mechanism by which these processes occur in copper at room temperature or below is that of cross slip. Thus cross slip appears to be essential to fatigue crack growth.6'10"12 The fact that a tensile stress opens the slip bands into broad cracks does not indicate the structure of the bands or the mechanism by which cracks form. The charactersitic concentration of slip into bands during fatigue shows a low resistance to shear strain in these regions. (This fact in itself may be inconsistent with a high concentration of vacancies.) The authors contend also that continuing shear produces an additional mechanical weakening so that the bands fracture easily (are pulled apart) under the influence of the superimposed tensile stress. It is equally possible that the only weakness is a weakness in shear, that the crack propagates by a shear mechanism, and that subsequently the tensile stress pulls the crack apart. Even the direct observation of bands opened by a tensile stress would not be conclusive since, as argued above, they may be fine cracks. The same argument applies to internal cracks, their existence in the presence of a tensile stress not indicating the mechanism of formation. Internal cracks originating in regions of heavy shear have also been seen following tensile deformation of OFHC copper,13 so that this mode of fracture is not unique to combined tensile and fatigue straining. The authors point out in their companion report14 that 90 pct of the cracks formed during pure tor-sional strain were within 8 deg of the normal to the specimen axis. If the tensile stress were an important factor in crack propagation, it is surprising that the cracks cluster about the plane in which the normal stress vanishes. Similarly, a study of zinc single crystals showed that for various orientations the life correlated well with the resolved shear stress on the basal plane,'= and was not dependent on the normal stress across this plane. W. A. Wood and H. M. Bendler (Authors' reply) -Dr. Alden's discussion emphasizes the essential point in the relation of slip band structure to

Jan 1, 1963

By R. C. Gifkins, A. Gittins

A. Gittins and R. C. Gifkins (University of Mel-houvne)— Evidence from somewhat similar experiments to those described in this paper has led us to the conclusion that possibility 2) of the four listed on p. 319 is a description of what happens in grain boundary sliding. That is, sliding is limited by accommodation deformation, it being necessary to the Continuance of sliding that this accommodation should take place. An example of such accommodation, though probably not the most important, is fold formation at triple points. The evidence and arguments for this point of view are set out in Refs. 14 to 16. In particular, an experiment with a lead bicrys-tall5 seems to support point 2) rather than 3). In creep of this specimen it was found that at least 90 pct of the extension of a zone 0.3 mm wide at the boundary was supplied by sliding at the boundary. The sliding was localized in a region at the boundary very much smaller than 0.3 mm, in fact, in a region too narrow to resolve optically. In poly crystalline Specimens&apos; there appears to be a surface effect, as found by Rachinger," but it appears that this may not manifest itself at low strains. "Low strains" means <10 pct for a Pb-TI alloy, <2.5 pct for magnesium or "Magnox" A12 alloy, or <40 pct for a 0 brass. Up to this extension the sliding, measured by the mean vertical step at boundaries, is proportional to extension. We are able to say this with some confidence, since the error bars on our points are statistically derived. Our results would lead us to think that the error bars on other work, including that of Mullendore and Grant, are much too large at low strains to show this

Jan 1, 1963

By G. N. Maniar

G. W. Healy (union Carbide Metals Co.)-The author&apos;s paper is a useful contribution to the store of maps of chemical activities of oxides in multi-component slag systems. It is also a good example of the utility of the Gibbs-Schuhmann technique for calculating activities in a system where that of one of the components has been measured. This paper Koh and Caugherty. This plot is reproduced by alor in X-ray Metallography. Because of this nonlinearity, preparation cf suitable standards and/or correction for absorption and enhancement are essential in microanalysis. However, our objection is not the conclusion that Dr. Aaronson has arrived at nor the technique he has used; but only to the foot-note credited to V. Macres. The level of chromium that he was concerned with (less than 3 pet) is so low that the deviation of uncorrected Cr-curve will be negligible. Besides Dr. Aaronson has used chromium intensity from martensite and set it equal the bulk chromium content of the alloy. Using this chromium-intensity as a reference, he has calculated the amount of chromium in the ferrite. This amounts to the same as using an internal standard. Since the chromium content in austenite and ferrite are almost the same, enhancement due to iron in both will be the same and therefore does not need to be corrected. together with the author&apos;s recently published one1 on the CaO-FeO-Fezo3 system will be most helpful to others learning to apply Schuhmann&apos;s method, which merits a far wider application than it has received to date and should greatly aid our understanding of equilibria between metal and oxide phases. As shown by okcen" its use may even be extended to sections of systems with any number of oxides. I have some questions as to the selection of equilibrium constants made by Dr. Turkdogan. He has chosen one for the formation of Fe2O3 from FeO and oxygen which gives Fea3 activities 50 pct higher

Jan 1, 1963

By D. K. Deardorff, Haruo Kato

D. K. Deardorff and Haruo Kato (U. S. Bureau of Mines)—We wish to refute the 1875" 20°C value that Giessen, et al., report as the transformation temperature of hafnium. Although these authors state that their work along this line will be reported later, we can&apos;t leave their value undiscussed, for we believe it to be 125°C too high. Our value of 1750° 20°C, which the authors mention, has been substantiated in our laboratories by the use of three other methods. The first method of substantiation was by heating and cooling curves using a hafnium/tungsten thermocouple, the couple having first been calibrated against a t/Pt-10 pct Rh couple. The second method was by quenching and metallography of dilute Hf-Ta alloys. The third cussion, it may be pointed out that the observations of Rogers referred to large unidirectional strains where the internal cracks or voids appeared only after a strain of 32 pct or more. On the contrary the internal fissures observed, as a result of fatigue cycling, occurred for a total extension of some 5 pct and furthermore followed the directions of the slip zones. Finally, it is not our contention, as implied in Dr. Alden&apos;s last paragraph, that the tensile stress is an important factor in crack propagation. Indeed, in connection with the reference to the companion report, special note is made of the fact that "Deformation was apparently concentrated in grains which have a slip plane nearly perpendicular to the specimen axis and thus near the plane of maximum applied shear." This dependence of the growth of fissures on the orientation of the slip planes with respect to the direction of maximum applied shear is clearly shown in work on the torsional cycling of single crystals which has been submitted for publication. method was by heating and cooling curves with W/W-26 pct Re thermocouple. Counting the original resistometric method, four different methods have yielded 1750" 20°C as the transformation temperature of hafnium. All our work on determination of the hafnium transformation temperature has shown that the specimen under test must be quickly heated to and through the transformation temperature if the lowest possible transformation value is to be determined; otherwise a higher value not representative of pure hafnium will result. Speed was emphasized in all methods. In our resistometric work the corresponding voltage, amperage, and temperature readings were taken quickly and the transformation temperature was usually reached within 5 min total heating time. In the thermal analysis work involving Hf/W or W/W-26 pct Re thermocouples the transformation temperature was attained within three minutes total heating time, this time being less because the two variables were

Jan 1, 1963

By W. C. Leslie

W. C. Leslie (Edgar C. Bain Laboratory for Funda mental Research)—This investigation, with its com bination of high-purity metal, calorimetry, and metallography, will serve as a model for annealing studies for a long time to come. The evidence for a competition between recovery and recrystalliza-tion is particularly convincing. The demonstration of edge-nucleated recrystallization was so clear that it may obscure the necessity for other types of "nucleation" sites; otherwise, single crystals of aluminum could not be recrystallized after cold work. At least three types of sites have been found to operate in iron: 1) high-angle boundaries, probably in the same manner as in aluminum, 2) matrix sites, 3) inclusions or second-phase particles. In each instance, the cells developed during cold work and perfected during recovery are the "nucle for recrystallization. Observations by ourselves and others of the dislocation structure of cold-worked metals and of the structural changes that occur during annealing have led us to doubt the validity of the basic assumption of the Lucke-Detert theory, and of the modification developed by Gordon and Vandermeer, that during recrystallization of a metal containing foreign elements in solid solution a high-angle boundary is ad vancing into a cold-worked matrix having a random distribution of solute atoms. We contend that an es sential part of the cold-working and annealing of solid solution alloys is the trapping of solute atoms by the low-energy "wells" afforded by individual dislocations and by dislocation arrays. If cells are formed during cold work, the cell walls are stabilized by this concentration of solute atoms. Thus, solutes inhibit recrystallization not only by decreas-ing the rate of high-angle boundary migration, but also by preventing the formation of high-angle boundaries by subgrain growth or coalescence, i.e., solutes can inhibit both "nucleation" and growth. In addition to stabilizing the dislocation Structure, the solute-dislocation interactions may produce clusters of solute atoms which are not as readily assimilated into the recrystallized grains as are individual solute atoms. There is an additional complication. The dislocation structure formed upon cold working a dilute solid solution may not be the same as that formed during cold working of the pure solvent metal. The solute can either enhance or minimize the formation of cells during cold working. Both effects have been observed in binary alloys of iron. The annealing process is inextricably connected with the mechanisms of strain hardening and solid solution hardening. Although the correlation between experimental boundary migration rates and the predictions made from the theoretical equations are impressive, it should be mentioned that in at least four other instances (Pb-Ag and pb-Au,15, Fe-Mn,16, Fe-Mo)17 the agreement was rather poor. In brief, while it is probable that the migration of high-angle boundaries is held back by solutes in the manner described, this is only a partial explanation of the total effect of solutes upon recrystallization of cold-worked alloys. Paul Gordon and R. A. Vandermeer (author&apos;s reply)— The authors first wish to thank Dr. Leslie for his compliments of this work. It is perhaps worth pointing out that some of Dr. Leslie&apos;s remarks are directed toward subject matter covered in two earlier papers in our work.18,19 We agree with Dr. Leslie&apos;s main contention that the exact nature of the metal structure in the vicinity of a boundary should have an effect on the boundary migration. The theory of Lucke and Detert does not take such detail into account, nor does it account for orientation effects on the migration rates. We assume that since our data checks the theory so well, the effects of detailed structure are statistically averaged out by the polycrystalline techniques used just as are the effects of orientation factors.

Jan 1, 1963

By E. A. Steigerwald

E. A. Steigerwald (Thompson Ramo Wooldridge, Inc.1— he authors&apos; results clearly indicate that cracking can be produced by the hydrogen pressure developed during a charging operation. This type of cracking or blistering has also been observed in polycrystalline materials24"28 when the charging conditions are sufficiently severe and is often referred to as irreversible embrittlement since it cannot be removed by a baking treatment. There are additional data, however, which must be considered before a pressure theory can be generally employed to account for all failures which occur as a result of hydrogen. In many cases, hydrogen embrittlement in a tensile test or in delayed failures under static loads is a reversible phenomena which cannot be simply explained on the basis of preexisting cracks generated by the charging operation. It is this aspect of the problem which has prompted many investigators to seek mechanisms other than hydrogen pressure to explain their results.24&apos;n728 Fig. 15 indicates an example where, under specific experimental circumstances, hydrogen embrittlement can occur at liquid nitrogen temperatures. In this case, which has been previously decribed,&apos;&apos; specimens were charged with varying quantities of hydrogen, immediately quenched, and tested in liquid nitrogen (-320°F). A companion set of identical specimens were charged, aged at 300°F to remove the hydrogen, and also tested at -320°F. When the current density was greater than lo-&apos; amp per sq in., embrittlekent occurred in both sets of specimens, indicating that cracking had occurred during charging and the embrittlement, as in the case of Fe-Si single crystals, was irreversible. At current densities between approximately 103 and lo-&apos; amp per sq in, the embrittlement was present only for those specimens which contained hydrogen during the testing sequence. The embrittlement was therefore reversible with respect to the aging and charging operations. Since extensive hydrogen movement would not be expected at -320°F, it is difficult to reconcile these data with a mechanism which requires pressure and pressure dependent growth of preexisting cracks. There are other features of hydrogen embrittlement such as the reversibility of the incubation time for delayed failure with respect to applied stressg0 and the influence of prestraining31 which are also difficult to explain using a pressure model. Any general mechanism of hydrogen embrittlement will have to consider the reversible aspects of the embrittlement data as well as the irreversible portion which has been clearly presented for the Fe-Si crystals and which is consistent with a pressure model. A. S. Tetelman and W. D. Robertson (authors&apos; reply)—he authors agree with Dr. Steigerwald that a general mechanism of hydrogen embrittlement must be applicable in all cases where embrittlement occurs. Dr. Steigerwald&apos;s experiments were performed on an iron alloy which has an extremely complex microstructure, and therefore does not lend itself to the direct and detailed observations that can be made in Fe-Si. The change in the characteristics of cracks as a consequence of annealing at 300°F is not really known in detail but it is probable that stress-relaxation (blunting) occurs, dislocations produced near the crack tips will be pinned by carbon atoms, and hydrogen will be lost to the atmosphere. Any, or all of these effects of annealing will alter the ease with which a crack subsequently propagates under applied stress. A quantitative treatment of the problem must take these effects into account. Since diffusional processes are presumably eliminated at -320°F, the general mechanism proposed by Dr. Steigerwald&apos;s colleagues cannot be operative at this temperature. A detailed discussion of the general&apos; inapplicability of this mechanism has been presented elsewhere. However, the data presented by Dr. Steigerwald in his discussion can be explained in terms of a pressure model. Crack propagation under internal pressure P and applied stress occurs when where is the total energy expended in creating new surface area and by plastic work at the crack tip. The total crack length increases with increasing current density, since we have shown that it systematically increases with hydrogen concentration and Dr. Steigerwald has shown that hydrogen concentration increases with current density. For large L (high current density) Eq. [I] can be satisfied even if P = 0 and the embrittlement process does not require the presence of hydrogen. Specimens charged at a lower current density will con-

Jan 1, 1963

By Kenneth A. Moon

Kenneth A. Moon (U.S. Army Materials Research Agency)—The authors are to be congratulated for a very interesting and valuable paper. Their discussion of the structural implications of the results shown in their Fig. 5, however, requires a small correction. The model of Speiser and Spretnak with 0 = 1 and z&apos; = 2 is perfectly reasonable for the Ti-O a phase, but Eq. [3] is valid only for solutions sufficiently dilute that the number of empty sites excluded by more than one filled site is negligible. The composition at which intrinsic saturation occurs therefore cannot be deduced from Eq. [3], but but must be decided by consideration of the structural details of the phase in question. In this case, intrinsic saturation is expected not at the composition Ti3O but at Ti2O, because Ti2O has the anti-Cd structurel4 for which each filled octahedral site has two nearby empty sites, one in the hexagonal plane immediately above it, and one in the similar plane below it. The other two models, with ?=1/3 and 1/2, imply a distinction between octahedral sites in pure titanium which is not easy to justify. The problem of extending Speiser&apos;s and Spretnak&apos;s treatment in a general way to more concentrated solutions will be the subject of a forthcoming publication by the writer. M. T. Hepworth and R. Schuhmann, Jr. (authors&apos; reply)—The authors wish to thank Dr. Moon for calling to their attention the paper by Holmberg which presents the results of X-ray studies of Ti-O solutions ranging from 0 to 33 at. pct 0 and quenched from various annealing temperatures between 400" and 1800°C. Within these ranges, Holmberg found three types of phases: 1) At high oxygen contents (above 25 at. pct) and low annealing temperatures, he found the anti-Cd(OH)2 structure referred to by Dr. Moon. In this structure each titanium atom is in contact with 3 oxygens and each oxygen is in contact with 6 titaniums, the "available" oxygen sites corresponding to every other layer of octahedral sites in the titanium matrix. The limiting composition is Ti2O. However, this anti-Cd(OH)2 structure was not observed for samples containing 25 at. pct 0 or less. 2) For the specimen containing 25 at. pct 0 annealed at 400°C an ordered Ti3O structure was observed. This structure is related to the anti-Cd(OH)2 structure but differs from it by providing only two oxygens adjacent to each titanium atom and thus is consistent with the model represented by Eq. [5] in our paper, with 6 = 1/3, z&apos; = 0. 3) For dilute solutions and for more concentrated solutions annealed at higher temperatures, the structure corresponds to that of the metal with random distribution of oxygens among all the octahedral sites. Thus, it is interesting to observe that the thermo-dynamic indications of ordering in the vicinity of Ti3O can now be supported qualitatively at least by Holmberg&apos;s X-ray evidence of the existence of an ordered phase of the composition Ti3O. That is, for solutions with oxygen contents close to that of Ti3O, both the thermodynamic data and the X-ray data are more consistent with models based on the ordered structure of Ti3O than they are with the model which Dr. Moon suggests corresponding to "intrinsic saturation" at Ti2O.

Jan 1, 1963

By T. S. Lundy, J. Askill

J. Askill and T. S. Lundy (Oak Ridge National Laboratory)—Moore has proposed a simple correlation between the activation energy for solute diffusion in fee metals and the atomic volume of the diffusing species using both tracer and chemical-diffusion data. The first point we wish to make is that it is wrong to attempt such correlations without separating the two types of data. Activation energies obtained using tracer techniques cannot, in general, be directly compared with those obtained from chemical-diffusion experiments. A knowledge of the variations of chemical potentials with composition is necessary and chemical-diffusion data must be corrected for such variations, even for dilute alloys, before a comparison is possible. Secondly, for nickel, iron, aluminum, and lead, Moore neglected a number of recently published works, e.g., Al26 and Mn54 in aluminum,46 cr51 in nickel,47 and Fe55 in iron.48 These and others should have been used. If one considers only the tracer diffusion data, there is left no simple correlation of the type proposed by Moore. For example, in the case of solute diffusion in aluminum the only reliable tracer data listed by Moore are for zinc and aluminum. The nickel, cobalt, and iron data of Agarwala49 are representative of near-surface diffusion-not bulk diffusion. In conclusion we suggest that for tracer diffusion data in these fee metals there is no justification for proposing any simple correlation of activation energy with atomic volume using the limited data that are presently available. R. H. Moore (author&apos;s reply)—The writer has proposed a simple correlation which is useful in estimating the internal consistency of diffusion data. The accuracy of the correlation is, of course, a function of the number of data available. Lundy and Askill take issue with the writer&apos;s decision to include data for the systems: nickel, iron, aluminum, and lead, taking the view that the data are insufficient to establish the correlation. The writer agrees that the data are insufficient and has cau- tioned the reader that the correlation is tentative in these instances. Inclusion of these systems is justified by the interesting trends the correlation reveals. For example, the distinction between interstitial and substitutional diffusion may be clearly established, Figs. 4 and 6, and the behavior of transition elements and nontransition elements is indicated to parallel the behavior illustrated by the silver and copper systems. Lundy and Askill have singled out the aluminum system for special criticism. The writer chose to discuss the data for diffusion of iron, nickel, and cobalt in aluminum in the terms used by the original authors9 and has included the comments of Balluffi.l0 The writer did not intend the reader to conclude that data for these elements should correlate with data for the nontransition elements as Lundy and Askill have evidently assumed. Iron, nickel, and cobalt form intermetallic compounds with aluminum, so the activity coefficients of these elements may be expected to deviate markedly from unity. This may account for the low frequency factors observed by Hirano.9 The nontransition elements, on the other hand, yield relatively simple phase diagrams with no evidence for intermetallic compound formation as in the case of iron, nickel, and cobalt. In dilute solution, Henry&apos;s law should be closely obeyed, the activity coefficients should not deviate markedly from unity, and the effect on the activation energy should not be large. The accuracy of the correlation applied to these systems will improve as the data is extended. It does not seem unreasonable to conclude that its extension should be encouraged.

Jan 1, 1965

By I. R. Kramer

I. R. Kramer (Martin Co.)—In a recent paper Nakada and Chalmers24 reported some observations of effects of surface conditions on the stress-strain curves of aluminum and gold single crystals. It is of interest to compare these observations with the results published previously in this journal and to comment on their general conclusions. In brief, Nakada and Chalmers concluded that the removal of the surface layer of a prestrained specimen lowered the stress-strain curve for aluminum but not that for gold. Further, they concluded that the surface work hardening of aluminum is confined to a depth not more than l0-3 cm. In our results25 published previously, it was pointed out that when prestrained specimens of aluminum and gold were polished to reduce the thickness upon reloading the initial flow stress decreased markedly. Further if a sufficient amount of metal was removed, the yield point failed to appear. With continued application of the load the stress-strain curve became coincident with that of the virgin crystal. We have found this behavior in some 100 determinations to hold consistently for gold, aluminum, and copper in both single and poly-crystalline specimens. The amount of strain required before the curves coincided depends upon the amount of metal removed but it is usually less than 0.01. This type of behavior is the same as that reported for metarecovery by other investigators.29 For aluminum specimens which have been prestrained and then heated to temperatures above 50°C we have consistently found that the stress-strain curve was typical of the orthorecovery28 type. In this case the stress-strain curve always lies below that of the virgin specimen. With respect to Ref. 24 the curves for aluminum are always below that of the virgin curves, while those for gold become coincident. This observation indicates at least for aluminum that the specimens must have been heated to a temperature high enough to cause recovery by an alteration of the internal dislocations. In addition, a recovery would be expected because of the removal of the surface work-hardened layer. Nakada27 had reported that, with his particular apparatus in which a perchloric acid polishing solution was used, the temperature of the specimen increased 65°C. The curves presented in Ref. 24 for gold do not permit one to detect the initial flow stress upon reloading after the surface-removal treatment. In fact, contrary to the method used by Nakada and Chalmers, the change in the stress-strain curve produced by a surface-removal treatment cannot be described in terms of a decrease in stress at strains much higher than that at the initial flow stress because of the coincidence of the curves at the higher strain values. With regard to the depth of the work-hardened surface layer, our data show for aluminum single crystals (7.5 by 0.3 by 0.3 cm) that the initial flow stress remained constant after 12 x 10-3 cm had been removed from the thickness. This depth was independent of the prior strain. For gold crystals this depth is somewhere between 10 x 10-3 and 20 x 10-3 cm. Y. Nakada (author&apos;s reply)— Kramer states,28 "for aluminum specimens which have been prestrained and then heated to temperatures above 50°C, we have consistently found that the stress-strain curve was typical of the orthorecovery28 type. In this case the stress-strain curve always lies below that of the virgin specimen." However, Cherian et a1.26 discovered that aluminum polycrystals annealed at 32" and 100°C showed the metarecovery behavior. They showed that the orthorecovery behavior did not appear until the crystals were annealed at 150°C. Kramer suggests28 that the drop in the flow stress of aluminum crystals after the surface removal by electropolishing24 may be due to the recovery caused by the temperature rise which may occur during the electropolishing.27 However, as indirectly stated in Ref. 24, the current density used in these electro -polishing experiments was 0.15 amp per sq cm. According to ref. 27, this current density should cause a temperature rise of only 40°C. This may cause the metarecovery but not the orthorecovery. Furthermore, as stated explicitly in Ref. 24, the surface removal was accomplished by chemical etching as well as by electropolishing. The results were the same for both electropolishing and etching. During the etching, the specimen temperature did not rise above 35°C. Some aluminum crystals were placed in water at 35° C for 30 min. These crystals did not show the decrease in flow stress. Therefore, it is quite clear that the flow-stress drop after the surface removal is not caused by a high-temperature recovery. However, as Kramer points out,28 it is quite possible that the internal dislocation structure may have been altered because of the removal of the highly work-hardened surface layer. However, how much this rearrangement contributes toward the flow-stress decrease is not known at present.

Jan 1, 1965

By R. J. Stokes

S. Floreen (international Nickel Co.)— One fairly simple way to differentiate between em brittle me nt due to surface microcracks or due to a dislocation barrier effect might be to load a brittle rock salt crystal in tension to some stress just below the fracture stress and then immerse the loaded crystal in water. If a surface film is retarding plastic flow then one should observe some plastic deformation of the rock salt as

Jan 1, 1962

By J. Richter, D. Schulze

J. Richter and D. Schulze (Deutschen Akademie der Wissenschafte zu Berlin)—Introduction. In a recent paper R. G. Garlick and H. B. Probst reported on experimental results of investigations of room-temperature slip in zone-melted tungsten single crystals.17 In the paper it was pointed out that slip lines could be detected with an optical microscope only after about 10 pet plastic strain of the crystal. In our investigations we could observe slip lines in tungsten single crystals of defined orientations already with an elongation of 0.02 to 0.03 pet.18"9 Experimental Technique and Results. The tungsten single crystals were produced from 4 to 5 mm sintered rods* as starting material by electron- beam zone melting. With single-zone-pass melting a speed of 0.5 mm per min was used, while three-pass melting could be handled at a speed of 3 mm per min. Crystal axis orientations were located in the shaded area of the stereographic triangle, see Fig. 6. Orientation 1 is located at about 18 deg and orientation 2 at about 5 deg on the great circle from [011] to [ill]. This corresponds approximately to the orientations P and M referred to by Garlick and Probst. Our single crystals had a length of about 70 mm and were profiled solely by electrolytic means, leaving grip ends at both ends of the crystals. Between the latter, a cylindrical crystal of 45 to 50 mm length and about 2.4 mm diam was obtained. The crystals were deformed at room temperature in a commercial tensile-testing machine to obtain a strain of 0.02 to 5 pet. The average strain rate e = eP/t for all tensile tests amounted to approximately 10 -6 to 10-5 per sec, with ep representing plastic strain and t the duration of applied stress. In Fig. 7 a crystal is shown elongated by 0.03 pet. The picture was obtained by means of an optical microscope. Figs. 8 and 9 give electron-microscopic pictures of slip lines of crystals elongated by 0.07 and 1.1 pet, respectively. For crystals with the orientation 1, see Fig. 6, only the two main slip systems (101)[111] and (110)[111] were found. With the crystals of group 2 the two main slip systems are again evident, with

Jan 1, 1965

By A. Boltax

H. Herman and M. E. Fine (Northzcesteriz University)—The author is to be complimented on the quality and completeness of his work. Of special interest to us was the exponent of time in the exponential rate equation, n = 0.28 ± 0.03, since it is consistent with results for the early stage of quench-aging in A1-2 at. pct Cu, n = 1/3, first determined in this laboratory."&apos; In that work we attributed the early kinetics to attraction of vacancy - solute atom complexes to the plate-shaped zone due to the strain field about the zone and the lowering in free energy. To our knowledge, Hirano et 1.&apos; were the first to

Jan 1, 1962

By A. R. Troiano, E. A. Steigerwald, F. W. Schaller

D. N. Williams(BatteZle Memorial Institute)-The authors have presented an extensive collection of arguments pertaining to the role of stress in hydrogen embrittlement. The basic assumption of these arguments is that stress is essential as a driving force for diffusion of hydrogen. However, in view of the rapid diffusion rate of hydrogen in steel at low temperatures as evidenced by the ability to alloy with hydrogen by electrolytic charging, it seems unlikely to me that stress acts in this manner. Instead, I would like to suggest that stress may be essential for the nucleation of hydrogen in steel. I believe that such an assumption would equally well satisfy the experimental data presented by the authors. I should also like to comment on the interpretation of the data presented in Figs. 5 and 6. Fig. 5 shows the effect of hydrogen content on ductility in a rupture test. The curve as drawn by the authors indicates an abrupt transition from ductile to brittle behavior at about 0.001 amp per sq in. (5 ppm). The data points would equally well support a gradual transition from ductile to brittle behavior extending over the range from 0.0008 to 0.02 amp per sq in. (4 to 8 ppm). A gradual transition would be the ex-

Jan 1, 1962

By Joachim J. Hauser

William F. Hosford, Jr. (Massachusetts Institute of Technology)—Dr. Hauser has used a very interesting method to study the interaction of dislocations on different slip systems, but it should be pointed out that the analysis of the experiments is subject to a serious criticism. He states that "the effect of the compression can be adequately described by one slip system." The effect of frictional constraint during the compression makes this quite unlikely. When a block of metal is compressed its lateral expansion requires a sliding of the metal over the compression platens. The role of friction in the interface between the deforming metal and the platens is to increase the normal force required for the compression. Analyses1213 have shown that, in general, the additional force, p, required for the compression is a function of l/h where is the coefficient of friction, I is the length of the speci- men in contact with the platens. For a constant COefficient of friction, isho&apos; shows that P should increase exponentially with pl/h for both plane strain and axially symmetric compression. For a compression specimen, Fig. 7, whose cross section perpendicular to the compression axis is a rectangle whith one dimension L, much larger than the other W, a much larger force would be required for appreciable flow parallel to L than for flow parallel to U7. Therefore lateral strain in the W direction, EW, should be much greater than the lateral strain in the L direction EL. Since L/H = 14.5 for Dr. Hauser&apos;s crystals, and since no lubrication was used, it seems questionable that appreciable lengthening of the crystals could occur. Because the theories of frictional constraint have been derived for isotropic polycrystalline materials, it was decided to make experimental measurements on a single crystal. A section 3.590 in. long was sawed from an aluminum single crystal with a square section of 0.249 in., so that L/W= 14.4. This crystal was tested in compression between dry ground steel platens. Fig. 8 shows the orientation of the crystal and the axis of compression. The face for compression was chosen so that the operation of the single-slip system which would be predicted in the absence of friction would lead to a larger strain in the length direction than in the width direction. The dimensional changes of the width and length as well as the height were measured frequently during the compression with micrometers. Width strains were calculated from the average of readings near each end and at the center. A plot of the length strain, EL, against the width strain E w is given in Fig. 9. The slope indicates that the EL amounted to only 2.5 pct of cw. Other compression tests on similar crystals with shorter lengths also showed severely limited elongation. Even for a crystal with L/W = A.0, EL was only about 26 pct of cw. Because of the frequent interruptions of the tests for dimensional measurements should have decreased the frictional constraint by allowing a reseating of the platens, even smaller elongations under continuous testing seem probable. These tests on long narrow crystals show that essentially plane strain conditions prevailed. We may assume that Dr. Hauser&apos;s crystals deformed similarly. That the compression can be described by the

Jan 1, 1962