By C. Chiou, D. P. Seraphim

The effect of clustering on the superconducting properties of Al-Zn alloys has been studied by the ballistic induction techniques. The superconducting critical temperature, T,, changes when zinc-rich clusters are formed. The change in T, depends on the concentration and may be positive or negative, but always correlates with an effective decrease in the solute concentration of the alloy. Reversion after clustering effectively returns a 5 at. pct Zn alloy to the quenched state. These methods might be use&lly extended to the Al-Mg system, where X-ray data are difficult to obtain. In very dilute Al-Zn alloys, as in other tin,' indium, aluminum,2 or tantalums base solid solutions, there is a decrease in the superconducting critical temperature, Tc, roughly proportional to the temperature independent resistivity, i.e., -0.2°K per pS2cm. With increasing solute concentration, the T, generally reaches a minimum and then increases4 to a value well above that for the pure solvent. The change of T, with solute concentration follows an empirical formulation involving two constants which correlate with the scattering cross section of the impurities. As will be shown below, the Al-Zn alloys more concentrated than 1or2at. pct do not follow the empiricism, probably because they are unstable even when rapidly quenched.5 However, it seems possible to study at least the later stages of solute clustering by precise measurements of the 1', following various thermal treatments. A few experiments on quenched alloys, aged alloys, and tests on reversion are reported here. The heat treatments selected for obtaining the quenched and aged states were mainly deduced from the work of Dash and Fine.6 For the quenched state, specimens were homogenized at 480°C, quenched to -160°C, and immediately transferred and mounted in liquid nitrogen. Measurements on the superconducting properties and residual resistivities were then made at helium temperatures, after which the specimens were aged at room temperature for 3 to 5 hr, i.e., much longer than the time required for clustering to be essentially completed. The superconducting properties and residual resistivities were once again examined. To reach the reverted state of the A1-5at. pct Zn alloy, the aged specimen was heated for 5 min at 200°C and then tested as above.

Jan 1, 1963

By B. H. Kear

Clustering of slip bands in different systems has been observed in both ordered and disordered Cu3Au crystals compressed in the <110> orientation. Certain features of the slip band patterns are explained in terms of reactions between dislocations with Burgers vectors at 120 deg; in a few rare cases, the slip band evidence suggests that the Products of such reactions form diffuse tilt boundaries between the differently slipped regions of the crystal, similar to the known behavior of ionic crystals, but not nearly so well defined. WHEN crystals with orientations favorable for multiple slip undergo plastic deformation, slip may occur in different systems in localized regions, so that clusters of slip bands are developed. This phenomenon has been observed in fee1-4 metals and also in ionic crystals having the sodium chloride structure.5-8 In the ionic crystals, the boundaries formed between the differently slipped regions of the crystal assume characteristic orientations and are associated with macroscopic tilts that are plainly visible on the sides of the crystal. Recently, this interesting feature was explained in terms of the formation of diffuse low-angle boundaries as a result of interactions between families of glide dislocations in the different systems meeting in the boundaries.9 This paper describes an attempt to obtain similar evidence for boundary formation in an fee crystal. The alloy Cu3Au was chosen for the present study simply because this material is currently being used in a general study of differences in deformation behavior of the ordered and disordered phases of this alloy, which will be described elsewhere. EXPERIMENTAL PROCEDURE The two specially oriented compression specimens used in the present study were prepared from a melt-grown single crystal by careful cutting, grinding and polishing. The finished specimens were about 6 mm by 2 mm in cross section by 6 mm tall, with their ends parallel to (101) and sides parallel to (111) and (121); the broad faces of the specimens were made parallel to (711). Both specimens were annealed in an evacuated quartz tube at 850oC for several hours, slowly cooled to 500°c, and then quenched into water in order to obtain the disordered state for the alloy. One of the specimens was partially ordered (with S- 0.8) by reannealing at 350oC for 100 hr. After these annealing treatments, both of the specimens were electropolished. 10 Finally, the specimens were compressed in the [loll orientation and their stress-strain curves were recorded. The deformation was carried out in increments of a few percent strain. At each stage in the deformation the specimens were unloaded, removed from the compression jig, and examined optically for slip bands. Before reloading, the specimens were repolished, so that the observed slip band patterns were characteristic of a particular stage in the deformation. EXPERIMENTAL RESULTS Fig. 1 show!; the stress-strain curves for the ordered and disordered specimens and also indicates the stages 1, 2, and 3 where the deformation was interrupted for examination of slip bands. The curves show marked differences in flow stress and in work hardening rate in the two specimens, as observed by previous workers.11,12 Also, it was found, in agreemement with the observations of Taoka and Sakata,&apos;3 that the plastically deformed disordered alloy showed the characteristic coarse slip bands of alloys, whereas the ordered alloy exhibited a fine slip band structure similar to that of pure metals. Slip Band Observations. In what follows, the description of the slip band patterns, with accom-

Jan 1, 1962

By R. B. Russell

The expansion coefficients of hexagonal (a) zirconium have been calculated from the lattice expansionparameters of both coefficientsofhexagonallow and high hafnium alloys in the range 0° to 600°C. It is found parametersofboththat the coefficients are straight-line functions of the temperature and that the effect of hafnium is to depress the mean coefficients by about 1 pct at room thattemperature and 9 pct at 600°C. The cubic (ß) form was stabilized so that its coefficient could be determined from 400&apos; to 900°C. COEFFICIENTS of thermal expansion for hexagonal-close-packed (a) zirconium were determined up to 600°C (1112°F), without any interference from the effects of preferred orientation, by measurement of the lattice parameters obtained from a symmetrical back-reflection focusing X-ray camera. This paper combines the results for a 1.2 atomic pct hafnium alloy from an earlier report&apos; with those for hafnium-free zirconium. The problem confronting the investigator is essentially that of getting sharp, high-angle diffraction lines which represent the material at a known constanl. temperature and chemical composition. In order to do this, it was necessary to use the proper X-ray emission wave length (Co K was chosen) and to have a fine-grained metal whose atomic spacings would be free from effects of cold work (the specimen was annealed) and to prevent a changing composition owing to gas absorption during the heating of the metal to temperature (the sample was heated in a vacuum). A summary of the effect of temperature on properties is listed in Table I which gives data for ordinary zirconium, as well as new values for the low hafnium metal. The coefficients of the linear thermal expansion that have been reported are given in Table 11. The discrepancies shown may be explained perhaps by the effect of preferred orientation, and McGeary and Lustman2 have done this successfully for sheet metal. The differences in texture cannot explain all the differences in expansion coefficient shown in Table II. liesults by the author agree most closely with those of Kroll.3 Chemical analysis of the high hafnium metal pre- viously reported1 showed that it was 98.22 atomic pct (97.40 wt pct) pure. The low hafnium metal was dehydrogenated Westinghouse crystal bar, designated SMZ-137A. Its analysis was as given in Table 111 (chemical analyses 5377, 5431, and 5432).

Jan 1, 1955

By M. G. Nicholas

The influence of deformation, relative movement and surface cleanliness on the strength of room -temperature "interparticle" bonds between copper surfaces has been studied. No bonding resulted when clean surfaces were merely pressed together, even under pressures of 50,000 psi. Bonding resulted, however, when clean surfaces were simultaneously pressed and moved relative to each other, some bonding occurring no matter how small the pressure or relative movement. Exposure of the clean surfaces to various chemicals inhibited bonding, none at all being produced by small relative movements. The size of the movements which first produce bonding between exposed surfaces depends on the nature of the chemical, being less than 0.002 in. for cleansing reagents and greater than 0.004 in. for lubricants, water and hydrogen sulfide. It is concluded from the experimental data that the prime requirement for bonding is the dispersal of surface films such as oxides and adsorbed contaminants. THE formation of interparticle bonds during the room-temperature compaction of powder metallurgy components greatly increases the ease of handling in subsequent production operations prior to sintering. The strength of unsintered compacts follows the same general trends as their density and hardness, but quantitative data are extremely Scarce. Quantitative correlation of the data on the overall strength of a compact with that of the individual interparticle bonds is virtually impossible due to the extremely complex geometry of powder compacts. Qualitatively, however, the strengths of unsintered compacts can be correlated with variations in parameters known to influence the extent of cold bonding, and hence interparticle bonding, such as surface cleanliness, relative movement, and deformation of the mating surfaces. Kuzmic and seelig4 found that contamination of powder particle surfaces with lubricants reduced the strength of unsintered iron and copper compacts. Interparticle shear has been shown to promote bonding by Train and Hersey7 while Gregory has shown that die rotation is beneficial. Eilender and schwalbe6 concluded that most bonding occurred during the early stages of pressing iron powder compacts when interparticle shear is one of the principal processes occurring. mile there can be little doubt that these and other factors, such as particle size and shape, affect the extent of interparticle bonding produced by compaction, evaluation of the influence of individual factors is not easy. Particle deformation and relative movement, for example, occur simultaneously during compaction, making any precise measurement of their relative influences difficult. Because of these and other difficulties encountered in studying interparticle bonding in actual powder compacts, the approach adopted in this study was to

Jan 1, 1963

By R. O. Williams

A recent article by Chernock, Singer, Mueller, and Beck 1 which supports the use of the integral of I sin $ d$ for comparing fiber texture data does not settle what happens to I sin ø as ø approaches zero, where I is the diffraction intensity for poles oriented 0 deg from the fiber axis. They indicate that they believe that it should approach some constant value (that is, I increases without bound) and the fact that in reality it does not was a result of the diffraction

Jan 1, 1960

By J. Gurland

The effect of four different second-phase additions on the strength of composite alloys with a common matrix was investigated. The four compositions each consisted of 85 pct by volume of silver with additions of 15 pct of either tungsten, molybdenum, tungsten carbide, or nickel. These particular additives were chosen because of their low mutual solid solubilities with silver at room temperature, the alloys consisting essentially of a dispersion strengthened silver matrix in which the second phase is distributed randomly. Test specimens were prepared by a powder metallurgy procedure consisting of ball milling the mixed powders, compacting, and sintering at 920°C for 1 hr in hydrogen. The constituent powders were of CP quality and of particle size between 2 and 10 ?. The compacts were subsequently hot pressed at 1000 psi and 1400° in an Inconel die, coined at room temperature at 60,000 psi and finally annealed and outgassed in vacuum at 800°F. The microstructures of the alloys are shown in Fig. 1, and the microscopically observed porosity grade was A-2 or better as evaluated by ASTM Recommended Practice B 276-54. The properties of the sintered compacts are listed in Table I, and the load-deformation curves in bending are shown in Fig. 2. The samples, of rectangular cross section, were loaded at the center of 58 in. span, and the reported stress was calculated on the basis of linearly elastic behavior in order to allow the comparison of specimens of slightly different dimensions. It is apparent that the tungsten, molybdenum, and tungsten carbide alloys exhibit very similar deformation curves. The moduli of elasticity were determined from the slopes of the stress-deflection curves at small loads. The measured values agree quite well with those calculated by the strength of materials approximation proposed by Paul1 for the elastic constants of mixtures, the calculated values being 15.0, 15.0, 17.4, and 13.4 million psi, respectively, for the tungsten, molybdenum, tungsten carbide, and nickel combinations with silver. The strength of the Ag-Ni composition is appreciably lower than that of the other three alloys. The discrepancy between the two groups is accounted for by the following characteristics of deformation and failure which were observed microscopically during the tests: A) The deformation of the W, Mo, and WC alloys did not involve the second phase particles to any appreciable extent. Slip and fracture took place in the silver-rich matrix alone, although the fracture path generally skirted the particles by favoring the phase boundaries. The deformation proceeded according to the following sequence: 1) formation of small, discontinuous microcracks in areas of the matrix adjacent to a particle, 2) general slip in the matrix and extension of cracks, 3) failure of specimens by propagation of cracks through matrix. The near coincidence of the 3 load-deflection curves suggests that the nature of the second phase particles does not decisively influence the plastic behavior of composite alloys of this composition as long as the particles do not undergo any considerable deformation themselves. B) A markedly different behavior was exhibited by the Ag-Ni composition where the relatively low flow strength is associated with the low yield strength of the nickel grains. Slip in the nickel grains was first observed at a stress of approximately 10,000 psi, although failure, at a later stage, took place by the propagation of cracks through the matrix. The ductility of this aggregate, in which both components deform plastically, is appreciably greater than that of the elastic-plastic composites. In summary: 1) The measured values of the moduli of elasticity of the composite alloys under discussion are in good agreement with the "strength of materials" approximation proposed by Paul.&apos; 2) The overall plastic behavior of these particle-strengthened alloys is unaffected by the nature of the second phase particles, if the latter remain elastic. This work was supported by the Office of Naval Research. The experimental results are presented

Jan 1, 1962

By W. A. Wood, W. H. Reimann, K. R. Sargant

A study is made of the microstructural changes produced in armco and pure iron subjected to alternating torsion at amplitudes above and below the knee of the S/N curve. The aim was to identify the basic mechanisms of fatigue and to find why they should give rise to a sharp S/N knee in contrast to the type of S/N curve shown by fcc metals. It is found that the basic structural change above the knee in the iron is a pronounced cell formation in the grains, which determines irregular micro-cracks, and below the knee a dispersion of fine slip that determines a dispersed pore formation in the grains. Comparison of these changes with those in fcc metals similarly tested shows that they do not include an intermediate structural change, a concentrating of slip in narrow bands with associated slip-band cracking, that characterizes the fcc metals and accounts for their different type of S/N curve. RECENT conferences on basic mechanisms of fatigue emphasize that fatigue damage takes many forms: for example, cracking in slip bands (Thompson1), at grain boundaries and inclusions (Hempel&apos;), at precipitation zones in alloys (Han-stock, Forsythe), or at surface notch-peak effects, both hypothetical (Mott, cottrel16) and observed (Wood). Evidently it is not easy to see in this diversity a basic mechanism. At the same time the contributions suggest that some reconciliation may be possible if distinctions are drawn between three phases of the fatigue process: initiation of damage at nuclei, distribution of these nuclei, and the final macroscopic crack system. In initiation, the relevant features appear to be that nuclei may appear early, at least by 1/100th to 1/1000th of the life of a test specimen; that they may do so at many independent centers, appearing according to some observationsa as pores or voids; and that they are not necessarily self-propagating, damage spreading rather by their multiplication. In distribution, the relevant feature appears to be that they form preferentially in zones where the microstructure becomes abnormally strained (as defined more closely below). Now in these two phases the basic fatigue process should be systematic. But, at the same time, the "abnormal strains" in particular set the stage for considerable diversity in the final phase of macroscopic cracking, for where zones of abnormal strain develop will depend on what kind of fatigue deformation is applied and what kind of prior processing the test material has had. On this view it seems desirable to know what in

Jan 1, 1964

By F. E. Jaumot, R. L. Smith

Self-diffusion in zinc has been used as an instrument for comparison of the absorption and sectioning techniques as a means of studying diffusion. Single crystal as well as poly-crystal samples were used asanda the temperature range of diffusion extended from 200° to 415°C. For temperatures above 200°C, the data indicate that the results obtained from the absorption technique agree with those obtained from the sectioning technique. The effect on the values of the diffusion coefficient of electroplating vs evaporation as a means of applying the tracer was investigated and no significant difference observed. It was found that an excess or deficiency of tracer did not materially affect the results obtained from the sectioning technique, but invariably caused errors with the absorption technique. NEARLY all self-diffusion experiments and many alloy diffusion experiments have employed radioisotopes as the instrument for following the diffusion. Of the various techniques in which radioisotopes are applicable, the two most widely used are the sectioning and absorption techniques. In the former, the diffusion coefficient is obtained from a curve of log concentration vs the square of the mean penetration depth. In the latter, the diffusion coefficient is calculated from a knowledge of the decrease in activity at the surface after diffusion. In spite of the importance of knowing the reliability of the diffusion data and the widespread use of these two techniques, they had not been directly compared experimentally on the same samples. Thus, such a comparison was worthwhile. The specific system chosen for this comparison was the self-diffusion of zinc, since the metal was readily obtainable in high purity, single crystals were easily grown, and the anisotropic features of the diffusion added an additional factor of interest to the comparison. Self-diffusion in both single and polycrystals was investigated, since the possibility existed that grain boundaries and grain boundary diffusion might produce different effects for the different techniques. Also, the effects of electroplating vs evaporation as a means of applying the radioactive tracer, and the effects of applying an excess or deficiency of tracer material were studied. The general experimental procedures and the mathematical analyses of both techniques have been described previously in some detail, and only those points essential to an understanding of the present work will be discussed here. The mathematical analysis of the sectioning data requires only a knowledge of the solution of Fick&apos;s equation. where C,, is the initial concentration, C is the concentration at depth x, D is the diffusion coefficient, and p is the absorption coefficient of the solvent metal for the radiation from the solute. Having obtained F from the experiment, the value of z can be read from a plot of F vs In z, and D can then be calculated if is known. The necessity of knowing the absorption coefficient causes most of the criticism of the absorption technique. It is very difficult to measure accurately under the conditions existing in the diffusion experiment, but it is absolutely necessary, as will be indicated briefly later. Portions of this problem have been discussed in detail elsewhere." The difficulties involved in the measurement of the absorption coefficient arise from three principle factors: the physical characteristics of the absorber, the geometry, and complex radiation spectra. The first two are heavily dependent upon the third. If

Jan 1, 1957

By A. G. Rozner

TRANSVERSE rupture tests have been commonly used in mechanical investigations of brittle materials. The specimens are simple, easy to prepare, and loading presents no difficulty. Owing to the complexity of stress distribution in bending1 one can determine stresses rigorously only for the elastic range. The bend-test results, however, are at times converted into tensile-strength data, determined as maximum fiber stress. The assumption is made that for small plastic deformations the linear stress-strain relation applies. This problem was experimentally investigated by Bach3 who tested cast iron in bending and in tension and found that the maximum fiber strength obtained in bending exceeded the experimental tensile strength by a factor depending on the geometry of the tested piece. The factor varied from 1.57 for a rectangular cross section to 2.12 for a circular cross section of the tested beam. Since this work was carried out 60 years ago, the cast iron used could be expected to have been highly brittle, thus the extent of plastic deformation prior to fracture very small. We have therefore carried out a number of tests on magnesium-modified cast iron with an average elongation of -5 pct. It was hoped that the data obtained from the tests would serve as a guideline for comparing data obtained in tension and bending for brittle materials. Mechanical properties were measured at room temperature on an Instron tensile machine at a crosshead speed of 0.05 in. per min. The three-point bend test employed cylindrical bars 0.20 in. in diameter with a 1.0-in. span. For the tensile test, cylindrical tensile specimens with a gage length of 0.85 in. and a diameter of 0.160 in. were used. Results are summarized in Table I. From Table I one can see that fracture strength

Jan 1, 1965

By J. F. Enrietto

It is shown that one cannot approximate the broad internal friction Peaks observed in the Fe-Mn-N system as the sum of a number of subsidiary Peaks and still vetain the concept of a single relaxation time. Furthermore, the approximation of manganese affectirg only nearest neighbor interstitial sites is shown to be incompatible with the experimental results. The results of this experiment show that the influence of manganese in the ferrite lattice extends over 3 to 4 atomic distances. NUMEROUS experiments have shown that the presence of relatively small amounts of substitutional alloying elements can profoundly affect the profile of the damping spectrum in the vicinity of the Snoek peak in bee metals.1-7 Dijkstra and Sladekl observed this phenomenon in Fe-Mn-N alloys where it appeared as a broadening and shifting of the Snoek peak to higher temperatures. The authors interpreted this as being the result of a superposition of two damping maxima—the normal Snoek peak, located at its usual position and having a normal half-width, and an interaction peak having a normal half-width, but occurring at a somewhat higher temperature. They prclposed that the interaction peak was caused by nitrogen atoms jumping from Fe-Mn sites to Fe-Fe sites, the Fe-Mn interstitial sites having one manganese and one iron atom as nearest neighbors, and the Fe-Fe sites having two iron atoms as nearest neighbors. They further suggested that the Fe-Mn sites had a lower energy than the normal Fe-Fe sites because of the presence of the adjacent manganese atoms. From the relative heights of the two postulated damping peaks, the dif-

Jan 1, 1962

By R. W. Gurry

In a series of charts this paper presents the composition of all gas mixtures, composed of the elements carbon, hydrogen, oxygen and nitrogen, which at temperatures from 1000° to 1800°F are in equilibrium with (1) austenite of various carbon contents, (2) iron and iron carbide, (3) graphite, (4) iron and its oxide. THIS paper presents the results of calculations made to determine the proportions of CO, CO2, CH4, H2, H2O and N2 in gas mixtures which, at temperatures from 1000" to 1800°F, satisfy, individually, the following conditions: (1) equilibrium with carbon steel of specified carbon content throughout the stable 7 iron region; (2) equilibrium with iron and iron carbide, both above and below the eutectoid temperature; (3) equilibrium with graphite; (4) equilibrium with iron and its oxide. From these data a new type of chart has been prepared which permits one to determine, from a room-temperature analysis of the furnace gas in question, the effect of the gas upon the steel at furnace temperature. Thus a guide is provided as to the carbon content which will result and as to the possibility of oxidation or sooting. All of the atmospheres commonly used in the commercial heat treatment of steel are composed of some or all of the simple constituents CO, CO2, CH4, H2, H2O and N2, and also in some cases oxygen or higher hydrocarbons. As the gas mixture is heated certain alterations in the proportions of the constituents take place, and at the temperature of the furnace the composition is, in general, not at all that of the entering gas. If equilibrium in the gas phase is presumed a calculation involving the use of certain fundamental data predicts for a certain temperature the carburizing, decarburizing, or sooting characteristics of a given atmosphere, and, upon the additional assumption of equilibrium between gas and metal, also the oxidizing ability of the gas and the ultimate carbon content of the steel. The extent to which these predictions are fulfilled will depend upon how closely the assumptions of equilibrium are realized in any particular case. Although at lower temperatures equilibrium is often not reached, there is considerable evidence indicating that above about 1000°F the approach to equilibrium in the gas phase is generally substantially complete, particularly in the vicinity of the steel which acts as a powerful catalyst in promoting reactions in the gas phase. The extent of the gas-metal reactions is commonly affected essentially by the sojourn at temperature; equilibrium with respect to carbon, for example, is accomplished simply by continuing the treatment long enough. However close the approximation of equilibrium may be in any instance, the above mentioned calculation indicates the condition of the steel at equilibrium, and at the present time this is the only basis of control of a furnace atmosphere. The effect at elevated temperature of a gas of a certain composition at room temperature upon a given steel has customarily been judged by first calculating from gas equilibrium constants the proportions of the gas constituents at the temperature of the steel, then comparing certain of these with the proportions known to be in carbon or oxygen equilibrium. This process is tedious and time-consuming, in particular because the calculation generally involves a series of successive approximations; and since some knowledge and familiarity with this type of computation are required, not everyone needing the information has been, in the past, in a position to obtain it. By making a series of equilibrium calculations, combining with fundamental data for gas-metal reactions, and plotting the results in a special way, a chart has been prepared which enables anyone

Jan 1, 1951

By B. Ramaswami, Y. Nakada, U. F. Kocks

Compression tests were performed on single crystals of aluminum, silver, gold, and a Ag-10 pet Au alloy, with height-to-width ratios from 8:1 to 1:1. As this ratio decreased, so did the amount of easy glide until, for cubic specimens of all the pure materials, it was entirely absent. Heterogeneity of deformation is proposed to he a major contribution to the explanation of easy glide in slender specimens. For comparison, one single-crystal cube of zinc was tested and showed a behavior very similar to that in tension. Beyond easy glide, tension and compression curves are very similar. It is concluded that, in this range, neither grip effects nor orientation change influence the work-hardening characteristics to any significant extent. (121) and (100) crystals of all materials had similar stress-strain curves in tension and compression, except that the stress level of the flat portion of aluminum (109 crystals at high strains mas somewhat higher in compression. These results are at variance with previously proposed mechanisms of orientation dependence by both Hosford and Kocks. The compression tests themselves are described in detail and it is shown that they are essentially frictionless and produce single slip when the crystal is suitably oriented. DEFORMATION in uniaxial compression does not necessarily give the same result as deformation in uniaxial tension, essentially because the boundary conditions chosen are practically always different. 1) The shape and size of the specimens are usually different, and any genuine effect of size on work hardening should thus influence the result. 2) The grip constraints are usually different and can vary substantially for different kinds of tests. If the compression specimen is a thin plate and the friction on the platen is large, the grip contraints are more serious than in tension and lead, in the extreme, to uniaxial strain rather than uniaxial stress. If the specimen is roughly cubical and the friction is low, the specimen is less constrained than in tension inasmuch as displacements in the contact face are allowed. 3) The orientation change of single crystals is of opposite sign in tension and in compression; it is furthermore different in detail, because the relevant orientation in a squat specimen is the normal to the contact face, whereas that in a slender specimen is the generator of the side faces.&apos; The considerable dependence of work hardening on the initial orientation in tension would suggest that the orientation change should also be very important. 4) Finally, localized deformation instabilities found in tension tests, such as necking and Lüders band propagation, are not possible in squat specimens. This is, for some investigations, a favorable consequence of the large grip influence. Even if one is not interested in any of the effects mentioned above, compression tests are often desirable just because the specimens needed are so much smaller and sturdier. For example, they have been very helpful in the investigation of latent hardening by means of alternate longitudinal and lateral compression of cubes,* and for testing

Jan 1, 1964

By Luke L. Y. Chang, Bert Phillips

A number of molybdenum oxides have been synthesized and their crystal structures have been described.&apos; No data have been published on the stabilities of these oxides nor on the phase relations in the system Mo-0. It is probable that the tendency toward oxidation of both the metal and the oxides with low oxygen content in addition to the high volatilization rate of the oxides with high oxygen content have precluded accumulation of reliable data for establishing phase relations. These problems make experimentation difficult, but a modifi-

Jan 1, 1965

By G. Sachs, E. P. Klier, W. Beck

HYDROGEN embrittlement of steels has recently attracted much attention because it is asso- ciated with a variety of failures, especially those of aircraft structural components.&apos; For instance, one of the undesirable properties of the ultra-high strength steels used for landing gears is their pronounced susceptibility to hydrogen embrittlement during plating. The presence of hydrogen in these steels becomes particularly apparent through delayed or sustained load failures of parts which have been subjected to low loads for an extended time. A number of variables are involved in causing a reduction of strength and ductility through hydrogen

Jan 1, 1957

By R. I. Jaffee, C. M. Craighead, G. A. Lenning

Hydrogen forms a beta-stabilized system with titanium, with a beta eutectoid at about 300°C and 44 atomic pct H2. &apos;The solid solubility of hydrogen in alpha decreases from about 8 to about 0.1 atomic pct from 300°C to room temperature. Hydrogen has little effect on tensile properties, but decreases notch-bar toughness to a large degree. This latter effect appears to be the result of increased notch sensitivity. PRIOR to this investigation, only a small amount of information was available on the effect of hydrogen on the mechanical properties of titanium. The effects of the other interstitially soluble elements, carbon, oxygen, and nitrogen, had received detailed study. Jaffee and Campbell1 indicated that hydrogen up to 1 atomic pct did not affect tensile properties deleteriously. Pitler&apos; indicated that 1 atomic pct H, in titanium reduced the impact strength appreciably, but his alloys contained appreciable amounts of oxygen, and it was difficult to attribute the embrittlement entirely to hydrogen. The high temperature portion of the equilibrium diagram for the Ti-H system was established by McQuillan," and his data generally corresponded with the results of Kirschfeld and Sieverts," Gibb and Kruschwitz," Bevington, Martin, and Mathews," and other investigators. The lower concentration limit of the hydride phase varied considerably among investigators, and Gibb and Kruschwitz9 ad shown that small amounts of contaminants in either titanium or hydrogen caused considerable variation in this lower limit. In view of this pronounced effect of contaminants, the extrapolated value of McQuillan&apos;s, about 48 atomic pct at the 325°C eutectoid, appeared the most reasonable. McQuillan&apos;s lowest experimental value was 54 atomic pct at a temperature of 450 °C. The density of titanium had been shown to decrease with increasing hydrogen content, but discrepancies were noted among the various investigations. The best values indicated that the density was decreased from 4.56 grams per cc at 0.27 atomic pctl to 3.84 grams per cc at 61.3 atomic pct? This investigation was conducted to determine the effects of hydrogen on a titanium, both in high purity and commercially pure metals, and on high purity a titanium alloys. Material and Fabrication The literature indicated that impurities in either the hydrogen or the titanium must be kept to a minimum. For this reason, the initial studies were made with high purity iodide-refined titanium. The vendor&apos;s analysis of the iodide titanium and the hydrogen content of the as-fabricated Y4 in. diameter rods are shown in Table I. Two 1 lb ingots were prepared by arc melting under argon in a water-cooled crucible, using a water,cooled tungsten electrode. This equipment has been described.&apos; As-cast Brine11 hardness numbers of 88 and 58 for these ingots were low enough to insure that the high purity of the metal was maintained during arc melting. The ingots were hot forged to % in. diameter rods at 800°C, cleaned by grit blasting, and then cold swaged to Yz in. diameter rods. The rod was then air annealed at 725 "C, ground to remove scale, and cold swaged to Y4 in. diameter (75 pct reduction in area). The material was then annealed for 1 hr in argon at 800°C to develop an equiaxed a grain size of about 0.05 mm. Micro tensile specimens and microimpact specimens were machined from this rod prior to treatment in the Sieverts-type absorption apparatus. Two lots of commercially pure RC-55 titanium were also used in this investigation to determine the effects of hydrogen and the normal impurities on mechanical properties. The commercially pure RC-55 alloy was obtained in the form of % in. diameter rod. The analysis of this material is also given in Table I. The % in. diameter rods were hot swaged

Jan 1, 1955

By F. H. Wilson, E. W. Palmer

The solid solubility of iron in 2 to 10 pct cupro-nickels increases with temperature and nickel content. Property changes accompanying various heat treatments indicate typical precipitation hardening behavior. Iron content also affects softening temperature and sub-scale formation. These factors, as well as impingement corrosion resistance, influence the optimum iron content of commercial alloys. FOR many years Cu-Ni alloys have been used extensively in the form of tubes, pipes, and plates for the construction of salt-water lines and surface condensers on shipboard and in tidewater power stations. The 30 pct Ni alloy has been considered more resistant to rapidly flowing sea water than alloys of lower nickel content, and has been standard on ships of the U. S. Navy. Some ten years ago, the still better corrosion resistance obtained by modifying the 30 pct Ni alloy with approximately 0.5 pct Fe was recognized, and the iron-bearing alloy rapidly superseded the plain alloy as the standard material for severe service. In 1945, Tracy and Hungerford1 published a study of the effect of iron on the corrosion of various cupro-nickels in sea-salt solutions, and their data indicated that the 10 pct Ni alloy containing about 0.75 pct Fe was equivalent to the 30 pct Ni alloy containing 0.5 pct Fe. This was confirmed by LaQue in discussion of the above paper, and by results in an experimental condenser set up at the Kure Beach marine test station of The International Nickel Co., reported by Freeman and Tracy.&apos; The 10 pct Ni iron-bearing alloy is now being very widely used in applications where the 30 pct Ni iron-bearing alloy was formerly considered standard. While this "substitution" has undoubtedly been stimulated by the present extreme shortage of nickel, it must be emphasized that it involves no loss of service performance, and would have occurred anyway in the course of time, for economic reasons. In view of the increasing use of the 10 pct alloy, it seems desirable to make generally available the results of several investigations of Cu-Ni-Fe alloys carried out in the Metallurgical Research Laboratory of The American Brass Co. in recent years. The present paper, deals with the constitution of these alloys in the copper-rich corner of the system, and with the variations in hardness and tensile properties resulting from the heat treatment of alloys containing various amounts of iron. Most of this work is concerned with alloys containing 10 pct Ni. With over about 0.75 pct fe, the 10 pct Ni alloy is suscep- Alloys Several series of cupro-nickel alloys containing iron were used in these investigations. Most of them were prepared in the laboratory, but two samples of commercially fabricated alloys were included. Series A—Nominally 2 and 5 pct Ni, each with 0 to 1.5 pct Fe. Series B—Nominally 10 pct Ni with 0.1 to 0.4 pct Fe. Series C—Nominally 1.0 pct Ni with 0 to 2 pct Fe. Series D—Nominally 10 pct Ni with 3 to 5 pct Fe. Series E—Nominally 10 pct Ni with 1 and 1.5 pct Fe.

Jan 1, 1953

By A. Taylor

NICKEL-RICH alloys hardened with small additions of titanium and aluminum and centered around that region of face-centered-cubic primary solid solution, 7, where the atomic ratio of nickel chromium is about 3 to 1, form an important series of high temperature materials because of their resistance to oxidation, high temperature strength, and excellent creep characteristics at elevated temperatures.&apos; With suitable heat treatment it is possible to precipitate a phase based on the ordered face-centered-cubic y&apos; phase, Ni,,Al, from the randomly ordered nickel-rich y face-centered-cubic primary solid solution. By adjusting the ratio of aluminum to titanium the precipitation of needles of the hexagonal intermetallic compound n-NiaTi may be effected. In the present investigation, the main interest was focused on the interrelationships among the y, y, and 7 phases. By using alloying elements of high purity and a suitable melting technique the presence of carbides and nitrides could be completely obviated, although it is realized that their presence is probably essential in alloys of commercial importance. As a preliminary to the study of the Ni-Cr-Ti-A1 system, it was necessary to establish the constitutional diagrams of the three contiguous systems, Ni-Cr-Al, Ni-Ti-Al, and Ni-Cr-Ti, which together form the nickel-rich corner of the Ni-Cr-Ti-A1 quaternary tetrahedron. Accounts of this work on the ternary systems have already been published by the author. A preliminary disclosure of the author&apos;s investigations on the ternary and quaternary systems has been made by Hignett2 and has since stimulated work in the same field by Nordheim and Grant." Before the detailed account of the quaternary system, a brief description will be given of the three contiguous ternary diagrams on which it is ultimately founded. Ni-Cr-Ti System The 750° and 1000°C temperature isothermals of the Ni-Cr-Ti system as determined by Taylor and Floyd&apos; are shown in Figs. 1 and 2. The single phase fields of greatest interest are occupied by the extensive face-centered-cubic y primary solid solution of chromium and titanium in nickel, and the close-packed-hexagonal Daltonide, n-Ni3Ti, from which tie-lines radiate across the very wide y+n two-phase field. The chromium-rich primary solid solution is represented by a. As may be seen from the diagrams, the extent of the y phase field increases quite appreciably as the temperature is raised from 750" to 1000°C. Isoparametric lines for the y phase are shown in Fig. 1. They are interesting in that they are almost parallel to the y/r+n boundary. Thus the determination of the tie-line directions is entirely dependent on the exact stoichiometry of composition of the 7 phase. Ni-Ti-Al System The 750°C isothermal section of the nickel-rich portion of the system Ni-Ti-A1 as determined by Taylor and Floyd is shown in Fig. 3.&apos; The regions of greatest interest are the extensive y primary solid solution of titanium and aluminum in nickel, the y&apos; Berthollide phase field based on the ordered face-centered-cubic structure of Ni3Al, and the hexagonal Daltonide phase, n-Ni3Ti. As may be seen from Figs. 3 and 4 the area occupied by the y phase is substantially the same at 750°C as at 1000°C, but the area of the 7 phase is considerably greater at the higher temperature. The tie-lines radiate from n-Ni3Ti across the y+v and y&apos; + v two-phase fields and are evenly distributed

Jan 1, 1957

By I. W. L. Finlay, H. R. Ogden, R. Jaffee, D. J. Maykuth

Aluminum has been found to be soluble in a titanium to about 26 pct, and to raise the temperature range of transformation from a to 8. Two intermediate phoses exist in the system, a new face-centered tetragonal phase, designated as 7, which occurs between 34 and 46 pct Al, and TiAI Metallographic and X-ray diffraction data were used to determine the diagram. ALUMINUM is one of the useful alloying additions for titanium-base alloys. It is an important constituent in two commercial alloys released in 1950, one containing 4 pct A1 and 4 pct Mn, and the other containing 3 pct A1 and 5 pct Cr as the metallic alloy content. It is probable that, in the future, other titanium alloys containing aluminum will be released. In the course of alloy development work, some of the features of the constitution of titanium-rich Ti-A1 alloys have been developed. These are described in the present paper. The only available information on the Ti-A1 system concerns the aluminum-rich end of the diagram. In summarizing the early work, Hansen&apos; indicated that there is little solubility of titanium in aluminum, and that a two-phase region exists up to the intermediate compound, TiA1a (37.2 wt pct Ti), which has a congruent melting point at 1355°C. Fink&apos; has reported that a peritectic reaction occurs at 665°C between the melt and TiA1³ to form the terminal solid solution of titanium in aluminum. The solubility of titanium in aluminum has been established at 0.24 pct at 510°C and is estimated to be between 1 and 1.5 pct at the peritectic temperature. No information has been published on the diagram above TiAl,, other than a statement- hat aluminum raises the a to ß transformation temperature of titanium. Materials and Preparation of Alloys Iodide-type titanium and high-purity aluminum were used in this investigation. Typical analyses of these materials are given in Table 1. Alloys were prepared by arc melting on a water-cooled copper hearth, using the techniques described previously for contamination-free melting.&apos; Weight losses during melting were very low, ranging from 0 to 0.02 g in a 10 to 15 g charge, indicating that little or no loss of aluminum occurred during melting. This permitted the use of nominal compositions for these alloys. Alloy ingots containing from 0 to 7.5 pct A1 were rolled in air at 850°C to 0.040 in. sheet. Alloys containing from 7.5 to 16 pct A1 could only be rolled about 25 pct reduction at temperatures up to and including 1200°C. Alloys containing above 16 pct A1

Jan 1, 1952

By J. L. Taylor, P. Duwez

The phase boundaries in the ternary system Ti-Cr-Al have been established at 1800° and 1400°F for alloys containing more than 60 pct Ti. The martensite transformation temperature has been measured for the titanium-rich alloys. THE studies of binary alloys of titanium with the transition elements which have been published so far1-0 ndicate clearly that the solubility of these elements is always much greater in the high temperature body-centered cubic form of titanium (ß phase) than in the low temperature hexagonal form. In this category of alloying elements are iron, nickel, chromium, manganese, vanadium, molybdenum, tungsten, columbium, and tantalum. Although studies of the nontransition elements have been rather limited, early work on titanium binary alloys&apos;" has shown that most of them were not very soluble in the a form, with the exception of aluminum, for which the solubility in a is about 25 pct.13, 12 In addition to this large solubility in a, aluminum is also soluble in ß titanium to the extent of about 35 pct and the transformation temperature from ß to a is raised with aluminum content. This effect is also typical of aluminum, in contrast with that found for the transition elements which lower the ß to a transformation temperature. Therefore, it may be anticipated that tprnarv titanium alloys with aluminum and any one of the transition elements will constitute a class of ternary alloys having characteristic features absent in alloys involving two transition elements. Chromium was chosen as a typical transition element for the present study because ternary alloys of Ti-Al-Cr commercially produced have been found to possess very interesting physical properties (MST-3 pct A1-5 pct Cr of Mallory-Sharon).&apos;" Binary Systems The binary systems Ti-A1 and Ti-Cr have been established recently by several investigators. The data used in this investigation were taken from the complete diagram of Bumps, Kessler, and Hansen." This diagram agrees quite well with earlier investigations." For the Ti-Cr system, the phase boundaries at 1800" and 1400°F were taken from refs. 6 and 7. The binary system Cr-A1 has been studied recently by Bradley." This system is rather complex and contains not less than seven intermediate phases. The present study was limited to the titanium corner of the ternary system (less than a total of 40 pct Cr plus Al) and none of the phases present in the Cr-A1 binary alloys were found in the ternary alloys investigated. Experimental Technique Microscopic observation and X-ray diffraction measurements were used to identify phases and de-

Jan 1, 1954

By W. Chubb

By measuring the hardness of metals at temperatures just above and just below their allotropic change point, it has been established that crystal structure has a real effect upon the strength of metals. The DPH of cobalt, iron, titanium, uranium, and zirconium have been measured at temperatures up to 1000°C. It was found that the body-centered-cubic crystal structure is always the softer structure when it is involved in an allotropic transformation. The close-packed and more complex structures are inherently harder, and may be expected, therefore, to be better base materials for high strength alloys. IT has been observed that for metals with nearly the same melting point (i.e., tin and lead, magnesium and aluminum) the metal with the more complex crystal structure has a higher tensile strength and hardness. It might be asked whether this effect is really caused by the difference in crystal structure; and, if so, just what is the contribution of crystal structure to the strength of these metals. A qualitative answer to these questions can be obtained by measuring the change in hardness produced by the change in structure in metals exhibiting allotropic forms. The evidence for changes in mechanical properties during allotropic transformations is rather meager. In 1909, Rosenhain and Humfrey&apos; observed that "ß" iron showed much less deformation at the transformation temperature than a iron. By means of a torsion test, Lee found that iron bars were "critically plastic" at the a-7 transformation temperature. Sauerwald and Knehans have shown that the dynamic hardness of iron increases between 900" and 1000°C. In 1930, Albert Sauveur&apos; presented data on the hardness, tensile strength, and torsional strength of pui-e iron up to 1000°C. He concluded, "At 900°C, the a iron transforms into y iron, and this is accompanied by increased strength and stiffness and decreased ductility." The same year, Schischokin" obtained data on the hardness of thallium at temperatures above and below its transformation temperature. His data are replotted on semilogarithmic coordinates as Fig. 1. The fact that his data fall on straight lines in this type of plot is believed to attest to the purity of his metal and the accuracy of his results. In 1941, Nadai and Manjoine" obtained tensile data on pure iron with an indicated increase in strength at about 900°C. These experiments make it quite evident that changes in mechanical properties occur when a metal transforms from one crystal structure to another; but, except for Schischokin&apos;s data on thallium, none of the measurements seem accurate enough to determine the relative magnitude of the mechanical property change. Materials The metals that have been examined for changes in hardness during transformation include l—as- deposited commercial electrolytic cobalt about 99.7 pct pure, 2—Armco ingot iron, 3—are-melted iodide titanium of a purity in excess of 99.8 pct, 4—uranium of a purity in excess of 99.5 pct, 5—are-melted iodide zirconium of a purity in excess of 99.8 pct, 6—annealed, 0.08 pct C, rimmed steel, and 7—commercially pure RC55 titanium. While the purity of the first five of these materials leaves something to be desired, it will be noted that the observed hardness discontinuities occurred at the accepted transformation temperatures. (These temperatures are indicated by vertical arrows in Figs. 1 and 3 through 7.) The last two materials are commercial alloys introduced to show the effect of minor alloying elements upon the hot hardness curve. Apparatus Hardnesses at elevated temperatures were determined by means of a vacuum hot hardness machine. A diagram showing the basic features of this machine appears as Fig. 2. This machine is essentially a deadweight hardness .machine in a furnace within a vacuum chamber. The sapphire-tipped indentor

Jan 1, 1956