By Hai-Peng Guo, Lu Jiang, Xiao-Man Yan, Bing Xie, Hong-Yi Li

Traditional, calcium compounds cannot be used in vanadium extraction processing due to the limitation of sodium roasting technology, which results in unsatisfied dephosphorization for vanadium-containing hot metal in converter and thus increasing the dephosphorization burden for subsequent steelmaking. The calcium roasting technology is an alternative for vanadium extraction and allows adding lime into vanadium slag in converter. In the present study, vanadium was leached by soda from roasted vanadium slag with high calcium content. Effects of roasting temperature and time, leaching temperature, Na2CO3 concentration andliquid to solid ratio on vanadium leaching rate were studied. The results show that 94% of vanadium was extracted by roasting the vanadium slag at 950℃ for 2.5h and then leaching in 160g/L Na2CO3 liquid at 95℃ for 1h with liquid to solid ratio of 10:1 ml/g. Impurities of Si and P reacted with calcium and formed insoluble Ca2SiO4 and Ca3(PO4)2 respectively.

Jan 1, 2015

By Zhenyang Wang, Yiran LIU, Xiangdong Xing, Jianliang Zhang, Zhengjian Liu

Basic characteristics of marine placer were systematically studied by chemical analyze, scanning electron microscope and X-ray diffraction in this paper. It could be found that the marine placer mainly consists of titanomagnetite and titanohematite. A series of experiments were performed to investigate reduction-magnetic separation for Fe and Ti from the marine placer. Effects of reduction temperature, reduction time, carbon ratio, magnetic density, and grinding fineness on the reduction-magnetic separation process were investigated. And the optimal process parameters were obtained as follows: the reduction temperature 1300, the reduction time 30 min, the carbon ratio 1.1, the magnetic density 50mT, and the grinding fineness of 0.074μm 86.34%. Under such conditions, the metallization rate, iron grade of magnetic substance and iron recovery reached to 94.23%, 97.19% and 90.28% respectively, and the titanium grade in non-magnetic substance and recovery of was 57.94% and 87.22% respectively. The effective separation of iron and titanium could be achieved in reduction-magnetic separation process.

Jan 1, 2015

By Jingyuan Wang, Hengyi Zhang, Peng Lan, Ruitian Zhang, Jiaquan Zhang, Yang Li

"For the determination of mould taper and wall thickness, a 3-D numerical model of ingot-mould-hot top system has been made to evaluate the related ingot solidification process and the final soundness. The effect of mould wall thickness and the taper of its hot faces on the thermal history and the as cast structure of steel ingot has been revealed through the numerical simulation. It is shown that the ingot soundness can be improved remarkably by increasing the mould wall thickness, which is possibly beneficial to the mould life as well owning to an improved mould thermal state. The mould taper is vital to the ingot soundness but much less coherent to the mould temperature profiles. Under given casting situations, a larger mould taper can lead to a less intensity of the shrinkage porosities at the top part of ingot.IntroductionIngot casting is still one of important processes for steel production, which is adopted especially for the supply of large-sized semi-products of high quality special steels. The understanding to the solidification process is vital to both the yield improvement of casting production and the quality control of steel ingots, such as their soundness and homogeneity.The ingot processing and service performance are closely related to its defects, such as porosities and pipes[1,2], which are the most common but serious defects during ingots casting. In the late 1960s, Mahadevan and Murthy et al.[3], Irani and Kondic[4] began to analyze criteria for the prediction of shrinkage porosities in light metal casting. In 1980s, Niyama and Uchida[5], Hansen and Sahm[6,7] et al have successfully presented some related porosities and pipes criteria for steel casting. At the same time, numerical solidification simulation was well developed and applied to ingot quality studies[8-10]. However, due to the quick development of continuous casting, less emphasis has been given to the further study on ingot casting process. There leaves much work to be made for the comprehensive understanding to ingot quality improvement and the mould design by the aid of modern solidification technology[11, 12]. In this paper, the effects of mould taper and wall thickness on its thermal history, ingot solidification and the final soundness are numerically studied through solidification simulation, which has been adopted in mould design and industrial production of both the mould and its steel ingot."

Jan 1, 2012

By K. R. Robilliard

Ausmelt Technology has been developed to process copper concentrates containing significant levels of lead, arsenic and antimony. A process was developed aimed at smelting these concentrate materials to remove the contaminants to fume and produce a clean copper product. The production of clean copper and the potential economic benefits of this process step over the sale of impure concentrates is discussed.

Jan 1, 1995

By Nicole de Jager, Michael J. Nicol

"In order to liberate gold from refractory gold ores and concentrates it is generally necessary to oxidise the surrounding sulphide minerals, typically pyrite and arsenopyrite. Traditional methods of oxidation include pressure leaching, roasting and bacterial oxidation. In recent years, bacterial and pressure oxidation have found increasing favour, although these methods are by no means completely satisfactory and each is subject to particular disadvantages.A novel process has been developed as an alternative to the traditional methods whereby electro-generated ferrate(VI) ions in alkaline solution are used to oxidise a pyrite concentrate. This process has been observed to proceed fairly rapidly and could prove to be a more economically viable process, as well as being more environmentally acceptable. As an added benefit, operating in an alkaline environment is advantageous for downstream cyanidation processes.Ferrate(VI) is a relatively unknown species, due mainly to its instability in acidic solutions. However, in alkaline solution it has been observed to be sufficiently stable for use as an oxidant when used under favourable conditions. Ferrate(VI) is most conveniently manufactured electrolytically via the dissolution of high-carbon anodes in strongly alkaline solutions. Some literature has been published on the electrolytic generation of ferrate(VI) and relatively high efficiencies have been observed by both the authors and other researchers.This study utilises both electrochemical techniques and leaching experiments to examine the kinetics of the oxidation of pyrite by ferrate(VI), which is produced electrolytically. Cyclic voltammetry, rotating disk voltammetry and potential step experiments have been used to investigate the kinetics and mechanism of the oxidation process."

Jan 1, 1997

By T. T. Lin, N. H. Madsen, K. Groom, B. A. Chin

"The objective of this research is to investigate the feasibility of using infrared sensors to monitor the welding process. Data were gathered using an infrared camera which was trained on the molten metal pool during the welding operation. Several types of process perturbations which result in weld defects were then intentionally induced and the resulting thermal images monitored. Gas tungsten arc using AC and DC currents and gas metal arc welding processes were investigated using steel, aluminum and stainless steel plate materials. The thermal images obtained in the three materials and different welding processes revealed nearly identical patterns for the same induced process perturbation. Based upon these results, infrared thermography is a method which may be very applicable to automation of the welding process.IntroductionAutomatic welding is commonplace in industry today. However, most, if not all, involves preprogramming for performance of a repetitive task. These systems are incapable of correcting for perturbations which arise during the welding process. Control of the welding process requires the identification and monitoring of perturbations in a wide variety of parameters. The varied nature of these parameters and the large number of variables involved have thwarted previous attempts at closed loop control of the welding process. The sensor(s) employed by a control system need to meet rather strenuous requirements. First and foremost of these is that such a sensor must be able to identify and discriminate between perturbations that might affect the quality of the weld, including such geometrical perturbations as a change of direction in the seam between the parts being welded, gaps in the seam or a misalignment of the parts being welded. The sensor should also be able to locate and identify contaminants and impurities in the weld puddle and ahead of it while monitoring the extent of the heat-affected zone and the cooling rate of the metal. The sensor(s) should, additionally, be able to perform these tasks in a time frame that is consistent with automatic control of the welding process. This paper presents results that could aid in the assembly of such a controlled welding system."

Jan 1, 1986

By L. A. André Santos

Atmospheric processing of nickel lateritic ores with low costs has been encouraged. In this work the kinetic of atmospheric acid leaching of a northern- Brazilian ore with 1.63% Ni and large amount of fine particles (d50 ≈ 0.075 mm and 40% below 0.038 mm) is presented. Chemical analysis showed a trend of Ni and Fe concentration in finer fraction (−0.075 mm) and Si and Mg in the coarsest one (−0.500 + 0.150 mm) associated to distinct mineral phases. Nickel is widespread in the mineral matrix. Distinct behaviors were observed as a function of particle size associated to the distribution of silicates and iron oxides in the ore. The kinetic modeling indicated that leaching is controlled by porous layer diffusion at 65 °C, but at 95 °C exhibits a mixed control by porous layer diffusion in initial minutes (60 min) and by chemical reaction or diffusion through the pore layer in final minutes (60–240 min) depends on metal evaluated.

By Dirk Bergmann

During the spray forming process, a continuous molten metal stream is atomized by impinging high speed inert gas jets. In the generated spray cone, the resulting metal droplets are rapidly cooled by the huge temperature difference to the surrounding gas phase and thereby partly solidified during flight. After a certain flight and residence time inside the spray cone, the droplets impinge onto the solid substrate and form the product (deposit) by compaction. Material properties of this preform strongly depend on several process parameters and especially on the thermal and kinetic state of the deposited droplets at the point of impingement. Smaller droplets may cool very fast due to their low mass and impinge onto the product in a completely solidified state as solid metal powder particles. Larger droplets with big mass contain a higher amount of thermal energy and impact during the state of phase change or still as completely liquid. It is obvious, that a certain amount of liquid content in the droplets is needed for forming a homogeneous deposit. Therefore, the thermal history of metal droplets during flight in the spray cone is of great importance for overall process modelling and control. Modelling the effects of the impinging droplet mass on the formation and heat balance of the deposit, the thermal conditions of the droplet stream need to be temporary and spatially averaged at different locations. Averaging may be achieved in different ways, giving alternative results. A first method is averaging over the droplets total enthalpy which consists of the thermal content and the remaining latent heat of fusion within the droplets. A second method may yield the average over the heat content and the solid fraction separately. Results of these two methods depend on the application and the kind of information which one wants to achieve and show some deviations, which will be discussed in terms of consolidation and energy conservation of the deposit.

Jan 1, 1999

By Reza Rahimi, M. Nili Ahmadabadi

"Because of high cost and shortage of primary resources of Ni-base superalloys, revert alloys can be used as a part of charging materials for production of superalloys ingots. The current study is based on recycling of IN738LC, a Ni-base superalloy, using 30% and 50% reverted alloy and balanced amount of virgin raw materials. Therefore, it has been attempted to cast an alloy with references to standard chemical composition and mechanical properties. After charging and casting in vacuum melting furnaces, chemical composition verification and non-destructive tests (i.e. Penetration and Radiography Tests), quality of samples were evaluated at elevated temperature by stress-rupture test. Results acquired from chemical composition and mechanical test indicate that cast ingots using 30% and 50% reverted alloy is reliable and consistent with the quality control requirements.IntroductionIn recent years, there have been many fluctuations in cost and availability of raw materials which are extremely determining in Ni-base superalloys production. Accessibility to the high purity metals such as Cobalt, Molybdenum, Tantalum, Niobium and etc. have been problematical during the past decades. Therefore, shortages of critical raw materials beside the economical considerations motivated the alloy suppliers and investigators to study and find alternate sources such as reclamation and recycling of scraps [1].There are a lot of reasons for the necessity of recycling; perhaps the most justifiable one is that consumers themselves produce scraps. For example, the weight of a finished superalloy product could be less than one-third of the cast alloy weight and in the case of complicated machined parts; this portion may reach to one-tenth [2]. High values of constituents, reduction of energy consumption and environmental concerns have all strengthened the obligation of recycling in Ni-base superalloys.Because of the high degree of risk in usage of improper materials for production of turbine blades, a delicately controlled program for recycling is needed. Depending on the type of scraps, this program can define the recycling procedure, required instruments, allowable percentage of scrap for usage and finally confidence level of the process."

Jan 1, 2012

By R. H. Hanewald

INMETCO, a subsidiary of Inco Limited, is the only facility in North America that provides High Temperature Metals Recovery for nickel-, chromium-, and iron-bearing wastes. Since 1978, this process has prevented more than 775,000 tons of materials from becoming part of the nation's waste stream. The paper describes Inco's experience in metals recovery, traces the development and explains the operation of the High Temperature Metals Recovery Process, and examines the procedures and criteria used to determine whether spent catalysts meet process feed specifications. An overview of the current requirements for transporting spent catalysts is provided. The paper concludes with brief case histories of catalysts users employing High Temperature Recovery to manage spent catalyst.

Jan 1, 1995

By Yongqi Sun, Zuotai Zhang

Our study investigated the influence of P2O5 and B2O3 on the viscosity and crystallization behavior of Ti-bearing blast furnace (Ti-BF) slags for the purpose of Ti extraction. The investigation of the crystallization behaviors were carried out using a single hot thermocouple technique (SHTT) and the viscosity was obtained by rotating cylinder method. For the viscosity, the results showed that P2O5 substantially increased the slag viscosity. P2O5 is a network-forming oxide, which increased the degree of polymerization of slags and accordingly increased the slag viscosity. However, both of slag viscosity and apparent activation energy for viscous flow remarkably decreased with B2O3 addition. As a typical network forming oxide, B2O3 was introduced into the network and existed dominantly as 2-D structure, BO3 triangular, which caused a simpler structure and a decreasing slag viscosity. As for the crystallization behaviors of Ti-BF slags, both P2O5 and B2O3 enhanced the crystallization trend of rod-shape rutile and suppressed the crystallization trend of dendrite CaTiO3. Therefore the added P2O5 and B2O3 caused the primary phase change from CaTiO3 to rutile. Additionally, it was found that the rod-shape rutile showed a 1-D growth, whereas the dendrite CaTiO3 showed a 3-D growth style.

Jan 1, 2015

By Thomas Brynjulfsen, Merete Tangstad, Eli Ringdalen

Manganese ore fines cannot be added to the submerged arc furnace directly as they will prevent even gas flow through the burden. Low gas permeability in the burden will lower the degree of pre-reduction of ore subsequently increase the carbon and energy consumption of the process. In order to utilize manganese ore fines in the furnace, they are typically agglomerated into sinter. In this work, the melting and reduction properties of Gabonese sinter and Gabonese ore have been investigated in pilot scale experiments. Two experiments were conducted, one with 100% sinter as manganese source and one with 50/50 sinter and ore. Lime was used to achieve a charge basicity of 0.72 in both experiments. The composition of slag samples from the excavation of the furnace was established using EPMA(WDS), and the composition of the tapped slag and metal was found using XRF. It was found that while the coke-bed size would determine the tapped slag composition, the melting behavior of the Mn source would determine the mixing with lime.

Jan 1, 2014

By John C. Taylor

With growing emphasis on energy conservation and increased concern over the presence of heavy metals in the environment, it is fortunate that most metals are readily recycled. In this respect, metals have a significant advantage over plastics and similar materials used as metal substitutes. For many years a secondary industry has processed scrap copper, nickel, lead and zinc to produce refined metal which has, to varying degrees, influenced the price and displaced the production of primary metal. This paper reviews some of the challenges the industry will face and the changes in process technology which will be required as pressure mounts to increase the amount of metal recycled. In the case of most base metals, this will have an impact on primary metal production; as the tonnage of metal recycled increases, the requirement for primary production, or new metal, will depend more and more on the growth in consumption.

Jan 1, 1993

By F. L. Marley

Small and medium-sized flotation plants with no assaying instrumentation still depend much upon the art of the operator to produce acceptable and consistent results. Improved performance can be accomplished by the use of the simple microscope set up as a control device. The visual recognition of products in the circuit does much to eliminate uncertain shift operating decisions and is an easy technique to acquire. Mineral staining methods further assist in the determination of components within the mill products. Simple mounting upon scotch tape and other adhesives is rapid and convenient. The microscope also has a practical role for the plant metallurgist or laboratory technician when evaluating middling products, and their routing within the circuit. Examples are reviewed where the microscope has been used for operational control in both sulfide and nonmetallic mineral flotation plants.

Jan 1, 1981

By Toshiaki Nakai, Kunihiko Takeda, Kimio Imaizumi, Hiroaki Shirasaka

"The new type of nano-porous silica particle was considered to be constructed by the spinodal decomposition-type process which was found to have narrower pores than those of conventional porous silica prepared from boron silicate or ""Shirasu"" balloon. Nano-porous silica particles were fabricated by the calcination of silica gel mixed with well-dispersed complex salts composed of phosphorous and molybdenum compounds. Both silica and inorganic salts were not perfectly dissolved in the suspension solution. After removing of the water, the silica-inorganic salts complex was volatized and successively calcinated at a temperature ranging from 650 °C to 800 °C. Then, the inorganic salts were removed by dissolving in hot water. Other inorganic salts such as potassium halides were also found to be effective as a pore-size controller.IntroductionControl of structure has an important role in the field of industry as well as in the separation and purification technology for metals and organic syntheses. Many studies on the control of material structures have been reported regarding porous materials with pores ranging from nanometer to micrometer scale. 1 ) One example is zeolite as a naturally yielded porous inorganic material. Various types of synthetic zeolites have been studied as ""molecular sieve"" materials with ordinary pore-size of less than one nanometer. In 1992, crystalline meso-porous material with a large surface area named MCM-41 was synthesized through the use of template synthesis. 2) In direct relation to our study, amorphous borate glass having 4 to 100 nm of fine pores known as Corning glass 3l or SiO2-Al2OrB2O 3-CaO porous glass having large pore dispersity ranging from 4 to 10,000 nm have been reported. 4 ) S) 6 ) Some examples of several reported studies are as follows: phase-separated porous glass consisting of B2OrAl2O3-ZrO2-RO-R2O complex oxide 7 ) glass with finer pore induced from hydrolysis of silane alkoxide, porous material attained by condensation polymerization through the use of sol-gel process 8), alumina meso-porous material 9 ) 10), silica-zirconia material 11), carbon porous material 12), etc.."

Jan 1, 2000

By Andy Judge

"In traditional Permanent Magnet Machines, such as electric motors and generators, power is transmitted by magnetic flux passing through an air gap, which has a very low magnetic permeability, limiting performance. However, reducing the air gap through traditional means carries risks in manufacturing, with tight tolerances and associated costs, and reliability, with thermal and dynamic effects requiring adequate clearance. Using a magnetically permeable, high thermal conductivity material has the potential to improve magnetic performance, while at the same time offering performance advantages in heat transfer.Ferrofluids can be used to improve permeability in the rotor I stator gap. However, there are several tradeoffs in this approach. Fluid immersion comes with an increase in fluid friction loss compared to the windage losses of a traditional system. Isolating the rotating components from the ferrofluid can offset this effect. Also, while the magnetic effect can be positive for gap permeability, leakage flux can increase, and saturation can limit gains. These effects must be taken into account for a system optimized for ferrofluid immersion.IntroductionPermanent Magnet Machines (PMM's) convert electrical energy to mechanical energy in motor applications, or, for generator applications, convert mechanical energy to electrical energy through means of passing alternately polarized magnets past electrical coils. Looking at a simplified version of a PMM, where Rx is magnetic reluctance and <l>x is magnetic flux, we have the circuit shown in Figure 1."

Jan 1, 2013

By Patricio Barrios

In February 1996, ATLANTIC, COPPER completed the construction of a Project for Expansion and Environmental Improvements in its Smelter and Electrolytic Refinery located in Huelva. Following the expansion, the new operating concept is based on the simultaneous blowing of two converters, while increasing throughput in the Flash Furnace up to the level required to deliver matte to both converters. While the production level planned with the Project.(270,000 MTPY of copper from concentrates) was reached the following June, work since then has been carried out to optimize the new equipment .and to develop a new operating shedule. This paper describes operational experiences from the start up of the Expansion Project, difficulties encountered and operating improvements introduced, which have allow an increase of production levels up to 300,000 MTPY of copper.

Jan 1, 1998

By R. M. Westcott

A two-electrode, direct current, slag resistance furnace (SRF) has been constructed and operated to selectively reduce the zinc and lead contents of non-ferrous slags. The experimental SRF is equipped with multiple methods of gas/solids injection for both mixing and reaction. A computer is used to position the electrodes and for data acquisition. A geometric factor correlation was previously developed at Columbia University for calculating the electrical resistance on the basis of furnace geometry and slag conductivity. The experimental SRF was used to test this correlation.

Jan 1, 1994

By N. J. Tannyan

Laboratory bath smelting tests were conducted to determine the feasibility of smelting nickel- copper concentrate directly to a low iron matte in one step. Concentrate, air/oxygen and a silica flux were fed to a matte-slag bath kept in MgO crucibles at I 300°C. Various oxygen enrichments and smelting rates were used to maintain 0.5 to 2 wt% iron in the product matte. The slag losses are comparable to those obtained under similar industrial conditions. Due to the highly oxidizing conditions required to produce mattes with low iron contents, it is not recommended to target iron contents below about 2% in the matte. The specific bath smelting rates were equal to or higher than those in various industrial bath smelting processes.

Jan 1, 2003

By Gabriel Plascencia

Copper was oxidized in the temperature range from 300 to 1000 °C under different pressures of oxygen, In the range from 300 to 500 °C, copper oxidizes following the logarithmic rate law; while in the range from 600 to 1000°C oxidation follows the parabolic rate law. Transition from logarithmic to parabolic growth occurs at about 525°C. X-ray diffraction was performed on oxide scales to account for the CuO/Cu2O ratio at different temperatures. Activation energies found in this work are in good agreement with reported values.

Jan 1, 2003