By Huimin Lu, Liyuan Zhao, Zhijiang Gao

The aluminum matrix composite reinforced by graphene was successfully fabricated using high pressure torsion (HPT). With only 0.5wt% graphene, the grain size was reduced to 100nm while that of pure Al was about 500nm. The hardness of the composite increased from the center (64HV) to the edge (120HV) of the sample. Moreover, the tensile strength of this composite reached 197MPa, while that of pure Al was 157MPa. The enhancement in mechanical properties was induced by grain refinement, load transfer from the matrix to the reinforcement and dislocations piled up at the grain boundaries.

Jan 1, 2015

By Antoine Allanore, Guillaume Lambotte, Bradley R. Nakanishi

Current industrial methods used for rare earth element (REE) extraction involve: 1) ore enrichment, 2) separation of rare earth oxides (REOs), 3) chlorination or hydrofluorination, and 4) individual electrowinning of REEs from a molten halide electrolyte. The complexity of REE extraction is inherited from their electronic configuration. Recently, molten oxide electrolysis (MOE) has been used to produce reactive metals directly from their oxides, e.g. titanium. As a single-step alternative to processes 3) and 4), or laboratory has investigated rare earth extraction by MOE. A key challenge is to find a molten electrolyte more stable than REOs. One possibility is to use binaries of REOs directly as a solvent. We have, therefore, developed two experimental approaches for studying molten REOs at temperatures exceeding 2200oC. The present work reports the most recent experimental results obtained with La2O3-Y2O3. Those promising results demonstrate potential for operating with molten REOs and refine the underlying materials challenge for electrodes to enable metal recovery.

Jan 1, 2015

By Pinakin C. Chaubal

Today?s steel industry is in a vibrant and resurgent mode. This transformation has been in the making for some time now. Over the last few decades, the industry was steadily transforming itself into becoming a high tech industry. New technology was adopted, efficiencies were enhanced, lean manufacturing concepts were brought in and a strong customer focus was developed. Today?s mills employ sophisticated instrumentation, computerized monitoring, on-line smart systems etc. driving processes that are producing at rates of many tons/minute. All this is not possible without judiciously using the latest available technologies in various fields and developing a more sophisticated work force. Prof. Sohn has been a pioneer in driving the concept of process engineering in process metallurgy. In this paper the focus is on some aspects of process engineering ? primarily process modeling - as applied to iron and steelmaking processes. Examples are shown to demonstrate how problems have been addressed. Some thoughts on future directions are presented.

Jan 1, 2006

By Roberto Parra

The selective reduction smelting of Cu2O in Cu2O-FeOx-SiO2 melts has been studied at laboratory level, using as a feed a dead roasted calcine from a copper concentrate. The purpose of the study was to evaluate the kinetic and mechanisms of the indirect reduction with CO and the direct reduction with graphite from 1260°C to 1350°C. The reduction rate by CO was found to be 10-2 to 10-1 mole Cu2O m-2s-1. The graphite reduction macrokinetics for FeO and. Fe2O3 containing melts, was found to be a first order reaction with respect to the Cu2O concentration, with a kinetic constant of 104 to 10-3 s-1. The reduction rate was not sensitive to temperature nor to stirring, in the range studied. The measured reduction rate is almost one order of magnitude larger than the observed rate for the direct reduction of FeO.

Jan 1, 1999

By Stefan Mutl

By the term sorting one understands the separation of a material mixture into two or several products according to different material characteristics in the preparation technology. The oldest sorting procedure, the handpicking, is less and less used to separate different material mixtures because of the considerable personnel expenditure and the strict hygienic regulations at the workplaces in Europe. In general, the manual assortment is able to solve separation tasks, which could not be solved by machines so far. The picking is one of the most selective processing methods. However, the progress in the computer and sensor engineering today makes the creation of automatic picking devices possible, whose efficiency goes far beyond the possibilities of handpicking. Therefore in the future automatic picking will not only be applied to already common applications like the waste glass assortment by colour, but also to the assortment of complex composed material mixtures e.g. old shreddered cars. Thus, the automatic picking, supported by high performance computer systems and new sensor technology, gains more and more significance within many applications of waste processing. However, in order to apply automatic sorting procedures for different material streams within recycling processes, a substantial research and development need still is existing. The desire of the users is to sort more extensively in order to achieve products with bigger material varieties, In addition, the requirement of the accuracy of recognizing and sorting out of single grains rises, This lecture illustrates the procedure of the hand picking before it was employed in waste processing. Thus, a renaissance of a long forgotten method is happening in terms of today's state of the art procedure "automatic picking". Possible technologies, fields of application and future potentials of this technology are pointed out.

Jan 1, 2003

By Ailton S. Ferreira, Rubén J. Sanchez Rodriguez, Sergio N. Monteiro, Felipe Perissé D. Lopes, Teresa E. Castillo

"Polyester composites reinforced with natural lignocellulosic fibers have, in recent times, been gaining attention in engineering areas as lighter and cheaper alternatives for traditional composites such as the ""fiberglass"". One of the strongest, the curaua fiber, is today being considered as reinforcement of composites for automobile interior parts. In fact, several research works are currently being dedicated to curaua fiber composites since physical and mechanical properties are required for practical uses. In this work, the thermal behavior of polyester composites reinforced with up to 30 % in volume of curaua fibers was investigated by differential scanning calorimetry, DSC. The results showed endothermic and exothermic events associated with water release and possible molecular chain amorphous transformation. Comparison with similar composites permitted to propose mechanism that explains this DSC thermal behavior.IntroductionThe modem composite materials, especially those reinforced with synthetic fibers such as glass and carbon, have been used since last century to attend the demands required by most technological fields, from home appliances to aerospace [1]. In fact, fiber composites offer significant advantages over monolitic materials, such as common metallic alloys, plastic and ceramics. One of the most important is the ratio between the ultimate stress and the density, known as the specific strength. For example, in common glass fiber polymer composites, the so called ""fiberglass'', the specific strength of around 400 MPa.cm3/g is higher than any conventional monolitic material. However, drawbacks exist. The energy required to fabricate ""fiberglass"" generates large emissions of C02, which are responsible for global warming. Moreover, ""fiberglass"" is not recyclable and cannot be incinerated [2]. As a result, most synthetic fiber composites end up in landfills or contribute to rivers and oceans pollution."

Jan 1, 2011

By Isabela Leao Amaral da Silva, Felipe Perisse Duarte Lopes, Alice Barreto Bevitori, Sergio Neves Monteiro, Ruben Sanchez Rodriguez

"The fibers extracted from the stem of the ramie plant are among the strongest natural lignocellulosic fibers with a potential to be used as reinforcement of polymer matrix composites. Characterization of the ramie fiber has recently been conducted for its physical and mechanical properties. However, the effect of increasing temperature on the ramie fiber behavior has not yet been fully investigated. Therefore, the objective of this work was to perform a thermal analysis on ramie fibers with different diameters within the naturally found range of practical interest. The analysis was conducted by thermo-gravimetric, TGA and DTG, as well as differential scanning calorimetric, DSC, techniques. It was found that the ramie fibers present thermal stability up to 200°C and then suffer a sharp deterioration between 300 and 500°C, resulting in characteristic peaks.IntroductionSince the middle of last century, polymer composites have substituted many conventional monolithic materials in applications ranging from aerospace to sport [l]. The main advantages of these composites are the low density and flexible properties specially using fiber as reinforcement to suit the mechanical performance requirements [2]. These are usually high strength and stiffness requirements that could be reached with synthetic fibers such as glass, carbon and aramid fibers. In recent years, however, the use of synthetic fibers is being questioned in terms of problems caused to the environment. In fact, as non degradable material, synthetic fibers are associated with long term pollution when discarded. Moreover, the expended energy for fabrication and processing can be related to relatively large amounts of C02 emissions and represents a contribution to global warming [3]. Glass fiber, in addition, is toxic and cannot be incinerated as a waste in thermal power plants [ 4]. Possible substitutes for glass fiber are the natural fibers. Many natural fibers are today being considered as viable alternatives to replace glass fiber as reinforcement of polymer composites. In particular, some natural lignocellulosic fiber extracted from plants present a real potential for this replacement [2-8]. Their comparative advantages are lower density and reduced cost as well as renewability, biodegradability, recyclability and neutrality with respect to C02 emission [3]."

Jan 1, 2011

By Guanghui Li

Nickel pig iron (NPI), used as a substitute for electrolytic nickel, is able to reduce the production cost of stainless steel greatly. Aiming for preparing NPI from nickeliferous laterite ore, a pilot-plant scale test of coal-based rotary kiln direct reduction of laterite ore was performed and reported in this study. In this process, the ground laterite sample (18.85% TFe and 1.52% Ni) mixed with additives, pulverized coal and binder was briquetted into briquettes with the size of 40mm×40mm×31mm, laterite ore briquettes and reducing coal were charged into a rotary kiln with the diameter of 1.6 m and the length of 16 m, for a retention period of 6~7 hours, in which reduction section temperature was ranging from 950~1050 oC. The reduced briquettes were water quenched, ball mill ground and beneficated via low intensity magnetic separation. A magnetic concentrate, Ferronickel powder, with 86.9% TFe and 8.0% Ni was obtained, and the corresponding magnetic recovery of iron and nickel are 75% and 96.3%, respectively.

Jan 1, 2014

By Harovel G. Wheat

It has been shown that the incorporation of fly ash into concrete as a replacement for part of the cement can be beneficial. In some cases, the strength of the concrete can be increased and the permeability can be decreased. This latter property can lead to a reduction in the migration and/or penetration of aggressive species into reinforced concrete. Some of these species, such as chlorides from deicing salts or marine environments, can subsequently result in accelerated corrosion of the steel reinforcement, a loss of the protection provided by the passive film on steel, and a loss of structural integrity of the concrete. Care has to be taken so that the appropriate compositions of the components of the fly ash are utilized in order to ensure maximum benefit to the concrete structures. This will be discussed as it relates to fly ash generation and treatment.

Jan 1, 2002

By P. A. Treasure

The EMEW® cell has been developed to overcome a number of inherent limitations in conventional electrowinning technology, particularly the high cost and restricted process windows characteristic of conventional hardware. The technology has been widely demonstrated to achieve high performance for various metals under chemical conditions well outside the limits required for efficient operation of conventional cells. This process flexibility offers significant opportunities for cost savings. in recovery of zinc from primary and secondary sources. The EMEW® technology is now available on a fully engineered basis, as a versatile commercial alternative to conventional electrowinning hardware. Application of the EMEW® cell for recovery of secondary zinc material offers significant advantages to the recycling industry. For example, a selective caustic leach can be used where there are high levels of iron or other contaminants in the target material. The reagent requirement is minimal as most of the caustic is regenerated in the bell and zinc dust that may be required for electrolyte purification is produced in the cell. A high purity zinc powder or cathode is produced in the cell. In the case of acidic zinc electrolytes, the cell is capable of operating over a much wider range of operating conditions than a conventional cell.

Jan 1, 2000

By Baozhong Ma, Qian Li, Yonggang Wei, Shiwei Zhou, Bo Li, Chengyan Wang, Hua Wang

The magnesium-rich nickel oxide ore (w (Ni) =1.09 %, w (MgO)=29.08 %) mixed with 6 % and 8 % anthracite were roasted at different temperatures. XRD and SEM/EDS techniques were utilized to characterize the phase and microstructure transformation of the ores. The results show that lizardite and chrysotile of raw ore were converted into forsterite and enstatite during reduction roasting process. Simultaneously, iron and nickel oxide were reduced and migrated from the initial magnesium silicate. Fe3Si were formed when the roasting temperature went up to 1300 ℃ and 1350 ℃, and a small amount of Ni was observed in it. Temperatures got too high were not benefit to the polymerization of ferronickel.

Jan 1, 2015

By Lijun Lu, Honghui Fang

This article carried out the experimental study on using desulfurization ash in steel slag composite material. This was done by investigating the desulfurization ash content in formula one and formula two samples on the influence of setting time and strength of mortar. Through this study the following conclusions were reached for formula one: (1) a setting time of more than 10 hours is required, (2) a dosage of desulfurization ash of 1 ~ 2% is optimal, where flexural strength is reduced by 10% ~ 23% and compressive strength reduced by 5.7% ~ 16.4%. The conclusions of formula two were: (1) when the dosage of desulfurization ash is within 5%, the setting time is within 10 hours; (2) when the dosage of desulfurization ash is 1 ~ 2%, the flexural strength is increased by 5 ~ 7% and the compressive strength is reduced by 1 ~ 2%. The results show that the formula two is better.

Jan 1, 2015

By Shengfan Zhou, XUEWEN WANG, Bianfang Chen, Mingyu Wang

Vanadium was leached from roasted stone coal by NaOH solution, and the effect of leaching temperature, leaching time, addition of NaOH, liquid to solid ratio, the grinding fineness of stone coal, and stirring speed on the vanadium leaching rate was studied. The kinetics analysis for the process is presented by the shrinking core model. The results show that the vanadium leaching ratio of roasted stone coal can be beyond 75% at the 6% NaOH addition, leaching temperature of 95°C, leaching time of 7h, liquid to solid ratio of 1.2mL/g, and grinding fineness of 0.111mm. The leaching process is controlled by interfacial reaction kinetics and the apparent activation energy was 59.36kJ/mol.

Jan 1, 2016

By Larry G. Twidwell, Jannette L. Chorney, Bryce D. Ruffier, Katelyn M. Lyons, Daniel W. Gaede, Ryan J. Foy, Jerome P. Downey

The Metallurgical and Materials Engineering Department at Montana Tech is investigating various methods of extracting and refining rare earth elements from mineral ores and concentrates. As part of this research, an elevated temperature “roasting” process has been evaluated as a means of converting the rare earth elements contained in various matrices to bromides as a pretreatment step in preparation for downstream rare earth element extraction and recovery operations. Laboratory and bench-scale experiments have been performed to assess the effects of varying temperature (150 to 400° C), time (1 to 4 h), and the ammonium bromide to rare earth oxide molar ratio (6 to 24) in the roaster charge. The results show that nearly complete bromination of the rare earth oxide is achievable when the roast is performed under optimum conditions.

Jan 1, 2015

By Shengfan Zhou, XUEWEN WANG, Changjun Jiang, Mingyu Wang

In the process of extracting vanadium from stone coal by sulfuric acid leaching - P204 solvent extraction, Fe(III) can accumulate in the organic phase which reduces the extraction of vanadium. In order to eliminate the effects of the accumulation of iron, oxalic acid was used as the stripping agent to strip the Fe(III). The effects of oxalic acid concentration, phase ratio O/A, stripping time and shake velocity on the stripping of Fe(III) were studied. The results showed that the Fe(III) stripping rate can reach beyond 96% at the room temperature with 70g/L oxalic acid using an O/A of 2 at 160 rpm shake velocity for 20min. After 2-stage stripping, the concentration of Fe(III) in organic phase was 0.008g/L.

Jan 1, 2016

By Guangliang Wu, Dong-chang Huang, Xin-bin Liu

High temperature mechanical properties of 50Cr5MoV roll steel was investigated by Gleeble 1500 thermal simulator testing machine The morphology, composition and microstructure of fracture surface were observed and analyzed by OM, SEM and EDS The results are indicative of that, there are two brittle temperature zones of 50Cr5MoV roll steel at the temperature of 600°C~950°C and 1300°C~1450°C, respectively. The section shrinkage rate is less than 60% The fracture mode changes from mixed ones dominated by intergranular to toughness transgranular one with the increase of temperature at the range of 650°C~1300°C. The fracture is along the solid--liquid phase at the range of 1300°C~ melting point It is crucial to formulate the 50Cr5MoV casting technology, to prevent the cracks and improve the quality of 50Cr5MoV roll steel.

Jan 1, 2016

By Jaeheon Lee

Gold-copper alloys are shown to form during the cementation of gold on copper in a solution containing 0.25M [S2O32-] at 25oC. The alloy composition is strongly dependent on the initial Cu:Au ratio in solution and ranges from Au3Cu to AuCu3. XPS results for Au, Cu, S, and O are reported as a function of depth through an entire deposited film with an initial solution containing 20 ppm [Au] and 30 ppm [Cu]. The deposit contained about 20 atomic % gold and was predominantly Cu3Au. Underpotential deposition (UPD) theory is discussed as a mechanism for explaining the formation of these alloys. Several other systems that produce alloys during contact reduction/cementation are also discussed.

Jan 1, 2003

By Hee Dong Jang

Crystalline metal oxide nanoparticles such as lithium cobalt oxide (LiCoO2) and indium tin oxide (ITO) were synthesized from sprayed droplets of aqueous precursor solution by flame spray pyrolysis. Complete thermal decomposition of the aerosol precursors was obtained at high flame temperature. Molar concentrations of the precursor solution, and the flow rate of combustion gas such as hydrogen, oxygen and air were varied to control particle size, size distribution and crystal structure. The crystalline nanoparticles synthesized were nearly spherical, and their average primary particle diameters ranged from 11 to 35 nm for LiCoO2 and from 8 to 15 nm for ITO.

Jan 1, 2006

By Motoyasu Sato

Highly pure pig irons were produced in a multimode microwave reactor from powdered iron ores with carbon as a reducing agent in the nitrogen atmosphere. The grains in compacted powder absorb microwave energy selectively. Microwave-matter interaction creates thermal non-equilibrium state microscopically and enhances chemical reactions and the phase mixing at the grain boundaries very rapidly. The visible light spectroscopic techniques was used to monitor the progress of the reactions. Up to 650°C, the heated powders radiate the continuous spectrum of blackbody emission. The small non-equilibrium hot spots rise, move and finally burst in to brighter light emitting from all over the surface at 650°C. CN molecules and Fe (I) atoms were identified in the recorded spectrum. These bursts are similar to the ?ignition propagation? normally observed in chemical reactions. The line spectra originated from CO molecules have not been detected yet. The solid-solid reaction could be expected between the iron oxides and carbon to produce CO2 directly. A loss in the sample weight was accelerated during the excess-emission. These are the clear evidence that microwaves cause thermally non-equilibrium state and accelerate reduction process. The reduction of iron ore is completed at 1380°C and relatively very pure pig iron was produced. It should be noted that the impurity level of Mg, S, Si, P and Ti is only 5-10% of what is found in the pig irons produced by modern conventional blast furnaces in the steel industries. The necessary amount of carbon needed was 1/2 compared to conventional blast furnace to produce the unit weight of steel, if we applied renewable energy or nuclear power for the microwave excitations.

Jan 1, 2006

The standard procedure of fire refining consists of sulphur removal via air injected through tuyeres, arsenic slagging via soda-lime flux and oxygen reduction by air or oxygen deficient air or a steam fuel mixtures. The use of porous plugs to stir with an inert gas has been mainly considered as a surface renewing agent that increases the product quality and shorten the refining cycle. In the present study the effect of the bottom stirring by nitrogen gas injection through porous plugs for the treatment of the crude copper in the range of 400-150 ppm sulphur, 3,000-2,000 ppm arsenic and 14,000-7,000 ppm oxygen content was investigated. The combined effect stirring-reducing, by the use of air or a steam fuel mixtures through tuyeres for oxygen removal, follows a kinetics of first order where the constant, K, can be represented by the following polynomial expression: K = A * R2 + B * R + C Where A, Band C are constants that depend on the nitrogen flow rate and R is the air-fuel ratio or the steam-fuel used in the reducing step. Depending on the optimization of the flow of nitrogen and the air-fuel or steam-fuel mixture and only if just the oxidation, complexing and reducing steps are considered, the process cycle might be shortened by 45%.

Jan 1, 2003