By George Stern

THE purpose of this investigation has been to study one method for making ordinary carbon steel by the powder metallurgy technique. This method con- [ ] sists of pressing and subsequently sintering an intimate mixture of iron powder and graphite in a suitable atmosphere to produce a steel. Two types of iron powder have been studied, electrolytic and reduced. The sintering of mixtures of loose carbonyl iron and carbon black for several hours at 1000° to 1100°C. (1830° to 2010°F.), followed by forging of the resultant ingots to bars, has been studied by Offermann.1 Trail' has reported on the properties of hydrogen-reduced and electrolytic iron powders, both containing 0.5 per cent carbon. Methods for making steel bodies by powder metallurgy have also been sug- [ ] gested by Goetzel,3 who recommends the addition of steel powder of well-defined carbon content to pure iron powder, and Volterra,4 who suggests compaction and subsequent sintering of a mixture of steel powder, iron oxide and iron powder. Additional methods for making steel bodies by powder metallurgy have been reported in the literature by Koehring,5 Allen,6 Balke,7 Wulff,8 Boegehold,9 and others. 10,11,12 It is felt that the method of pressing iron powder and graphite, as described herein, lends itself best to production because of the lubricating action of the

Jan 1, 1946

By Louis Huber

THE Liberty tunnels extend through a very steep hill in Pittsburgh (locally called Mount Washington) for a distance of slightly over a mile. The two tunnels parallel each other and are 59 ft. apart, center to center (Fig. 1). They are for vehicular traffic, and in each there is ample space for two lines of vehicles. Northbound traffic, towards downtown Pitts- FIG. I.-NORTH PORTAL OF LIBERTY TUNNELS. NOTE THE WINDBREAK AT END OFEAST TUNNEL. burgh, is confined to the east tunnel and southbound traffic to the west tunnel. The South Hills residential district is separated from downtown Pittsburgh by Mount Washington, a steeply rising escarpment south of and adjacent to the Monongahela River. The Mount Washington district immediately south of the Monongahela River has been reached, for many

Jan 1, 1927

By E. A. Gulbransen, K. F. Andrew

The vacuum-microbalance method was used to study the oxidation behavior of Zircaloy-2 and -3A over the temperature range of 300 to 850°C and at 0.1 atm pressure. The results fit in well with the authors' earlier studies on zirconium. Tin was found to increase the rate of oxidation and also the temperature at which the metal burns. Both the cubic-rate law and the parabolic-rate law gave imperfect fits to the rate data. Since the parabolic-rate law has been derived from accepted physical principles, this rate law was used to interpret the rate data. A heat of activation of 28,600 cal per mole was calculated. The transition phenomenon previously observed in hot-water and steam-corrosion processes was studied systematically for oxygen atmospheres. Observations on the rate of oxidation, color and properties of the oxide films show that the transition phenomenon was associated with a failure in the adherence of the oxide to the alloy. ZIRCALOY-2 and -3A have found important uses in the field of reactor metals due to their low neutron adsorption, good strength and good resistance to corrosion. One feature of the corrosion reaction in steam or hot water is the sharp transition in the rate of corrosion to a higher value after a certain amount of reaction has occurred. This paper presents a study of the reaction of Zircaloy-2 and -3A with oxygen including a study of the transition phenomenon which has been found to occur also in oxygen atmospheres. A comparison will be made between the oxidation behavior of these alloys and the pure metal. It was hoped that a study of the details of the oxygen reaction would lead to a better understanding of the reactions occurring in hot-water and steam atmospheres. Literature Kinetics-—The reaction of Zircaloy-2 and -3A with hot-water and steam atmospheres has been studied by Thomas.' Goldman and Thomas,' Thomas and Forscher," and Thomas and Kass.' Empirical equations for the kinetics of the reaction have been given by Thomas and Forscher." The change from the initial slow rate of reaction to the final rapid rate of reaction has been termed transition with the post-transition corrosion kinetics following a simple linear equation in time. The corrosion behavior in high-temperature steam was similar in many features to the corrosion in high-temperature water. Goldman and Thomas' and Pray and Peoples' have shown that the addition of tin, while increasing the rate of corrosion, counteracts the deleterious effect of nitrogen. The beneficial effect of iron, nickel and chromium was to improve the adhesion of the oxide to the metal as well as to counteract the deleterious effect of nitrogen. Mallet and Albrecht" have studied the oxidation of two zirconium-tin alloys. The cubic-rate law was found to fit the oxidation data for the 1.5 pct tin alloy while the parabolic-rate law was found to fit the data for the 2.5 pct alloy. Kendall' in a recent paper has studied the oxidation of Zircaloy-2 containing 1.5 pct tin in air atmospheres. Transition Phenomenon—In steam atmospheres Thomas' has observed fora 1.8 pct tin alloy containing small amounts of iron, nickel and chromium that transition to a more rapid rate of corrosion at 400°C

Jan 1, 1959

By Attilio Ligasacchi

The production of magnetite in copper smelting has been the subject of wide investigation in the past.1-9 It is accepted that most of the magnetite is produced in the converters and returned to the re-verberatory furnace with the converter slag. Part of this magnetite is circulated back to the converters in the matte. As a result, if proper fluxing practice is not followed, and temperatures in the converting process are not strictly controlled, an undesirable circulating load of magnetite may occur. This might ultimately lead to saturation in the reverberatory bath with consequent settling of the magnetite at the furnace bottom. This paper contains the cumulative results of a series of investigations on the formation and control of magnetite presently being conducted by the metallurgical department of the Chino Mines Division of Kennecott Copper Corp. THE METHOD USED FOR THE DETERMINATION OF MAGNETITE AND OTHER MAGNETIC MATERIALS Conventional wet chemical magnetite analyses are neither reproducible nor theoretically sound. These analyses are sensitive to time, temperature, and heating rate-all factors which tend to decrease their accuracy and reproducibility. To overcome the unreliability of the above method, H. W. Mossman1 developed an inductance bridge magnetite "meter" which completely replaces the wet chemical analysis with the advantage of quicker and reproducible results. Fig. 1 is a schematic diagram of the meter in use in the Chino metallurgical laboratory. When a pulverized specimen with magnetic properties is placed in coil A of the inductance bridge circuit, the permeability of the core is increased, causing a voltage drop across the coil. The unbalance is amplified to operate the balancing motor which adjusts the movable iron core in coils C and D to bring the bridge back to balance. An indicator arm connected to the movable iron core indicates directly the percent, or weight, of the magnetic material in the specimen. Coil B acts as a reference coil and a zero adjustment. The meter is standardized with a set of various amounts of -100 mesh pure magnetite crystals (99.8 pet Fe3O4) thoroughly mixed in a test tube with -100 mesh quartz sand. These mixtures are combined with inert transoptic powder and heated to 140° to 160°C (melting point of the powder) and subsequently cooled to room temperature, solidifying the whole mixture, in this manner eliminating any possible preferential orientation of the magnetite grains. In order to determine the effect of the particle size" of the magnetite and other magnetic materials on the meter determinations, five size fractions were obtained by wet screening of the 99.8 pet pure magnetite and several reverberatory matte and slag samples. The following size fractions were investigated: -80 + 100; -100 + 150; -150 + 180; -200 + 250; -250 + 300 and -100 mesh. The deviation of the meter readings for the various sizes of each sample never exceeded ±0.3 pet. This deviation is considered well within the accuracy needed for common smelter operation procedures. Further investigation proved also that grinding slag and matte samples in our laboratory disc grinder normally produced a powder constituted of 95 pet -200 + 300 mesh. For practical purposes a - 100 mesh size was used as standard for our studies. It was also found that for rapid determinations tamping of the sample in the test tube was sufficient and gave comparable results with those samples solidified with transoptic powder. For the purpose of this study we define the magnetite content in copper smelter slags and matte as the equilibrium amount of crystalline Fe3O4 existent in the specimen at a given reference temperature, excluding any secondary magnetite precipitated in the specimen during nonequilibrium conditions. MAGNETITE DETERMINATION IN SLAGS Since it is impossible to ascertain the status of equilibrium of a conventional slag sample, due to

Jan 1, 1965

By R. G. Hawthorne

This report is concerned with fluid displacement in porous media, in those cases where viscous and gravitational forces control the displacement. Such a system would usually be found in a sand body of large physical dimensions such as an oil reservoir, although it is possible to create such a system in the laboratory. It is shown that the position of the fluid interface can be predicted by numerical calculations using a basic idea presented by Dietz. Fluid flow is considered in a vertical plane in a homogeneous, porous medium of sufficient thickness that the capillary transition zone is small in comparison with the total reservoir. A theory developed by Dietz' is used to make numerical calculations of the position of the fluid interface. The results for several conditions are compared with scaled model experiments. The results show that, for gas drive in a reservoir of steep dip, a relatively low flow rate can displace large volumes of oil before gas breakthrough. On the other hand, water injection at favorable mobility ratio and low dip may show best performance at high rates. Water tends to underride the oil and, given sufficient rime, will break through without much oil displacement. For certain conditions, which include relatively low flow rate, the interface is a straight line and its behavior is simple to calculate. At higher flow rates, the interface is unstable, and a numerical solution was programed for an automatic computer. In general, good agreement is shown between the fluid model and the computed results so long as gravitational forces have control. For a water drive at very unfavorable mobility ratio, many small water fingers appear. These viscous fingers are not controlled by the relatively small gravitational forces. When viscous fingering becomes the controlling factor, the mathematical model is oversimplified, and results do not check the fluid flow model. INTRODUCTION Present methods of reservoir analysis depend upon certain simplifying assumptions to obtain mathematical descriptions of practical use. Material-balance methods (Muskat2 or Tarner2) assume uniform fluid saturations in the entire reservoir, or in a few subdivisions of the reservoir. An unsteady-state flow calculation by West, er at considered pressure and saturation changes in flow to a well during solution gas drive, and neglected gravity effects. Results showed only a 4 per cent difference for ultimate oil recovery by the Muskat method, even though the case chosen for study was one in which unsteady-state effects should be high. The Buckley-Leverett5 method commonly assumes a one-dimensional flow system. It is applicable at high flow rates where viscous forces predominate over gravity forces. Simultaneous, parallel flow of the two fluids is assumed, and the concept of a fluid interface is not introduced. Permeabilities to each fluid for a given saturation must be known. The method is not applicable for a two-dimensional system where cross flow becomes possible. Less well known is the displacement equation derived by Dietz. This method is designed for two-dimensional flow systems and assumes a definable fluid interface within the porous medium. Dietz showed that, for a range of low flow rates, the interface would be stable. straight and at an angle of inclination which could be simply calculated. At a certain critical flow rate, the calculated interface tilt would equal the formation dip. For higher flow rates, a finger of displacing fluid would invade the displaced fluid. Dietz indicated that his method applied only to macroscopic reservoir behavior, while the Buckley-Leverett method applied to the small transition zone at the fluid interface. The examples worked out in this report are based on the fluid-displacement theory of Dietz. It is shown that the Dietz theory may be used to derive equations analogous to the Buckley-Leverett equations. In contrast to the Buckley-Leverett method, flow is considered in a plane rather than being limited to a line. Rather than a frontal advance, the movement of a fluid interface is followed. For flow rates substantially exceeding the critical rate and for high viscosity ratio, many fingers of invading fluid occur-—rather than the single finger assumed by Dietz. On the other hand, so long as some gravitational influence remains, the flow is not entirely parallel to the bedding planes as assumed by Buckley and Leverett; therefore, both methods fail to give an adequate descrip-

By C. S. Smith, W. M. Williams

THE quantitative study of grain shape in three dimensions has been a difficult one from the practical standpoint. Experiments on grain shape have usually been based on indirect observations of two-dimensional metallographic samples or on grains separated by intergranular corrosion or fracture. The latter method was used in particular by Deschl in 1919 in observing the shapes of ß-brass grains which had been separated with mercury. The similarity in detail of shape and packing that exists between bubbles in a soap froth and metal grains was noted by Desch who remarks that: "Surface tension has an. important share in determining the form of the crystal grains in a solidifying metal and such grains have a tendency to assume the shape of foam cells." More recently the relation between grain shape and grain growth has been studied by Harker and Parker.' The importance of surface tension forces in determining microstructure has been discussed by Smith," and an analysis of the topologi-cal rules that apply to such structures has been made by the same author.' Biologists have made valuable contributions to the general problem of shape and form in an assembly of space-filling cells subject to surface tension forces. Particular mention must be made of the extensive researches of Lewis5,8 on botanical and anatomical tissues, and Matzke and Nestler,7,8 who have made painstaking studies of bubble shapes in different kinds of foam. The present paper introduces a new method of studying individual grains in particular alloys—a method which may well find use in other metallurgical researches, and which seems also to be applicable in biological problems. Metal Grains in Three Dimensions The individual grains in a piece of metal or the bubbles in a soap froth must satisfy two conditions —they must be in juxtaposition so as to fill space and their interfaces must conform to the laws of surface tension. If a further restriction is imposed, namely, that only one type of polyhedron be used, then the sole possibility is an assembly of "minimal" tetrakaidecahedra," each polyhedron having eight doubly-curved hexagonal faces and six plane quadrilateral faces, the angles between adjacent faces being 120". Such cells could be stacked on a body-centered cubic lattice and would be quite stable. For many years it was believed that soap bubbles actually possessed the shape of this ideal body, and the hypothesis was the starting point for several investigations on the shapes of soap bubbles, biological cells, and metal grains. These investigations have shown, what might have been obvious in the beginning, that if the condition of symmetry is relaxed the tetrakaidecahedron is almost never found. If we retain only the rule that all contacts should be in local surface tension equilibrium and that the assembly should fill space, metal grains may then take a nearly infinite variety of shapes and no single one may be regarded as an archetype. These two conditions, which are fully discussed in one of the previously mentioned papers,' lead us to think of a typical grain in an annealed metal as having the following characteristics: 1—A grain may have any number of faces, but usually between nine and eighteen. The faces (each of which is, of course, shared by two grains in the assembly) may have any number of edges, but usually between four and six. Pentagons are by far the most frequent. 2—In the assembly of grains each edge is shared by three faces and by three grains. Each vertex is a point shared by four grains, six faces, and four

Jan 1, 1953

By Kenneth P. Katen

INTRODUCTION Though the use of continuous mining machines consolidated the operations of cutting, drilling, blasting, and loading in one machine that would theoretically provide uninterrupted production, it was soon realized that the face haulage and roof support operations remained as major impediments to continuous production. The ability to provide not only continuous cutting and loading, but also continuous haulage and roof support (see Fig. I), was the basis for the introduction of mechanized longwall systems in this country from Europe in 1951. The early systems employed friction props for roof support, but were to become obsolete shortly after introduction of the first hydraulically powered, self-advancing supports in 1960. Since then, use of the longwall technique has grown to the point where it is currently providing more than 5% of the annual output of underground coal mines in the United States. The shortwall system had its origin in Australia, but was first introduced into this country in 1962 following the development of powered roof supports. It, too, provides for continuous cutting, loading, and roof support (see Fig. 2), but has not experienced the widespread popularity of longwall due to its inherent inability to easily provide for continuous haulage. While there are in the neighborhood of 100 longwall systems currently in operation in this country, there are only a handful of short- wall operations providing production of slightly more than 907 184.7 t/a (1,000,000 stpy) Both of these systems provide uninterrupted roof support for face operations by means of hydraulically powered steel roof supports. In each case, the coal removal consists of open-end cuts made from the narrow end of a large rectangular pillar (panel) which has been blocked out by continuous miners developing entries around its perimeter. However, this is the extent of the similarities between the two systems. It is hoped

Jan 1, 1981

By William Alden

A GREAT landslide occurred on June 23, 1925, in the valley of Gros Ventre River, about 35 miles south of Yellowstone National Park (Fig. 1). The relations of the north-easterly dipping rock formations of the slide scarp and of the dam formed by the slide are shown in the diagrammatic cross-section of the valley (Fig. 2). This generalized section is based on unpublished maps and notes by Eliot Blackwelder, in the files of the U. S. Geological Survey. FIG. 1.-MAP SHOWING SCARP AND DAM (LARGE DOTS) AND LAKE (CROSS-LINED) FORMED BY LANDSLIDE BLOCKING GROS VENTRE RIVER. (Scale 1, in. = 1 mile; contour interval 100 ft. From Grand Teton and Mt. Leidy topographic maps). Heavy rains and melting snow in the Gros Ventre Mountains had saturated clay layers in the Carboniferous strata, which dip toward the valley at angles of 18° to 21°, consequently an enormous mass of rock at the end of the north spur of Sheep Mountain became loosened and, on the afternoon of June 23, slid suddenly down into the valley. Within a few minutes this mass of debris-estimated as 50,000,000 cu. yd.-carrying

Jan 1, 1928

By L. W. McKeehan, W. C. Elmore

The magnetic powder method, long used for roughly mapping magnetic fields, has recently been refined1, "or investigating the microscopic variations in the surface magnetization of ferromagnetic crystals. Bitter2 first discovered regular powder patterns connected with the crystal structure of such specimens. Several other investigators:' have used Bitter's original technique, with slight modifications, to study the variation of the patterns with variations in the magnetizing field applied parallel to the surface, and their dependence upon the state of strain, of polish and of crystal cut. All of the explanations of these patterns on metallic ferromagnetics have been couched in general terms. In a preliminary report we have described an improvement ill the powder technique which led us to the discovery of a new effect throwing considerable light on the magnetic secondary structure of alpha iron4 and of nickel5 single crystals. We now report additional evidence confirming the existence and stability of a magnetic block secondary structure. Specimens The following list describes the specimens used in the present investigation. Designation Description A1 Silicon ferrite furnished to us by Dr. W. E. Ruder, of the General Electric Co., for which lie gave the following typical analysis: C, 0.05; P, 0.038; S, 0.026; Mn, 0.15; Si, 3.24. Disk, 0.60 cm. diameter, about 0.05 cm. thick. By X-ray analysis angles between disk normal and [100] 75o, [0101 76" [00l] 21o. A2 Same as A1 except: diameter 0.75 cm. A, Same as A1 except: diameter 0.68 cm.

Jan 1, 1936

By L. A. Rapoport, W. J. Leas

As a preliminary, consicleration is given to the conventional definition of relative permeability and to the conditions governing the simultaneous flow of oil and gas through porous media. For the conditions of flow prevailing throughout most of a gas drive reservoir, the oil and gas can reasonably be supposed to be in capillary equilibrium with each other. Under these conditions, and these conditions only, the relative permeability to liquid can be expressed as a function of saturation. The relative permeability to liquid in that case is dependent upon the distribution of fluids which itself is shown to be related to the capillary pressure, and, in turn, to the saturation. As a consequence, relative permeability to liquid can be expressed in terms of the volume and surface area of a network of liquid channels bounded by the rock and the gas phase. While the volume of this network can be evaluated accurately, the surface area cannot. However, for any such volume, maximum and minimum values of the corresponding surface area can be calculated from capillary pressure data. It is then possible to establish for any saturation the limits within which the value of the relative permeability to liquid must lie. As a consequence of the theoretical development, the validity of an experimental method for measuring relative permeability to liquid which utilizes a stationary gas phase is demonstrated. In this method capillary barriers are cemented to the ends of the core sample to permit the maintenance of capillary equilibrium between the two phases. At the same time, this procedure eliminates undesirable secondary phenomena such as end effects, fissure effects, etc., the presence of which adversely affect the results of other laboratory methods. The results obtained by theoretical calculations, and experimentally, are discussed. In view of the overall precision that can presently be obtained in reservoir calculations, the agreement between the calculated and measured relative permeability to liquid data can be considered satisfactory. In conclusion, for reasons of economy and simplicity, the procedure of calculating limiting relative permeability to liquid curves from capillary pressure data is indicated for general engineering purposes. It is shown that the above procedure can easily be extended to the cases where connate water is present. Its use for reservoir studies is particularly recommended in conjunction with the method for measuring relative permeability to gas' which simultaneously yields the capillary pressure data necessary for the calculations. THEORETICAL Definition of Relative Permeabilities — Basic Equations for Heterogeneous Flow The equations by which the relative permeability concept is defined and upon which the formulation of all of the gas-oil flow problems rests at the present time are expressed as: V, = — Grad PL = — Grad PL ....(la) PL µL, k k KG VG = —K - Grad PG k- Grad Pc .... (lb) Mo where ,. and G refer to liquid and gas; V is the volumetric rate of flow per unit gross area. µ the viscosity, Grad P the potential gradient. and k the specific permeability of the porous medium.* (For horizontal flow, Grad P becomes the pressure gradient; otherwise, gravity must be included.) According to these expressions, each of the constituent phases is considered similar to a homogeneous system where the volumetric rate of flow is proportional to the pressure gradient, and for each of which the constants of proportionality, k, and kG, are termed effective permeabilities. by analogy to the specific permeability as defined by Darcy's law in its original form. In order to obtain a convenient basis of comparison, the effective permeabilities are referred to the specific permeability, k, of the considered porous medium, with the help of the relations: k1. = KI. k kQ = Kn k..........(2) K,. and Kr. are defined as the relative permeabilities to the liquid and to the gas phase respectively, and frequently expressed in per cent of specific permeability. It may be seen that Equations (1); which appear to be a direct generalization of Darcy's law, correspond to the assignment at any given time of a set of "local" permeabilities to each point of the porous medium, and represent in a differential form the two fluid flow system as a simple superposition of the individual single flow systems. The above interpretation implies that the effective or relative permeabilities are independent of pressure or rate of flow,

Jan 1, 1951

By Anson Hayes, John Chipman

The quality of sheet and strip products made of rimming steel is closely related to the structure and chemistry of the ingots. The variation in composition throughout the ingot, as affected by segregation, is of great importance, as are also the form and distribution of the voids that result from the gases evolved. It is because of this importance that the considerable literature in this field has accumulated. No attempt is made in the present paper to compile a bibliography of the excellent work that has already been done, as this has been adequately covered in the many excellent reports on the heterogeneity of steel ingots prepared by a joint committee and published by the Iron and Steel Institute.' From time to time, in any field of investigation new tools and new technique are developed, which make further progress possible. In the field with which this paper is concerned, this is true. The development of the vacuum-fusion method as a means of following oxygen segregation, and a technique for obtaining the volume and composition of the gases evolved during solidification, have opened the way to obtaining data by means of which some considerable progress has been realized in developing more of the detailed mechanisms of solidification and segregation in rimming-steel ingots. General Theory of Segregation The basic cause of segregation lies in the fact that the impurities are less soluble in solid than in liquid iron. The solid that forms from the impure liquid is more nearly pure than the liquid itself. If solidification proceeds slowly enough, or if the liquid and solid phases are maintained in contact with one another for a sufficient time, a condition of equilibrium is set up, which may be represented by a phase diagram. Portions of the

Jan 1, 1939

By Elmars Ence, Harold Margolin

The titanium-aluminum system has been investigated in the composition region 0 to 34 pct Al in the temperature range 800" to 1450°C. The phases encountered in this region were: a,ß, TiAl3, The reactions observed are as follows: 13 ; L - 6T. A1, 0 (15 pct Al) + 6 (18 pct Al) - yTi Al (16.5 pct Al) at -1170°C andP (7 pctpct Al) + y (9.2 pet Al) - ah(9 pct Al) at - 1060°C. A eutectoid reaction: y — a +d belm 700°C is postulated. THE Ti-A1 system has been the sub.ect of a number of investigations. Several of these1-3 have indicated extensive solubility of A1 in both a and ß titanium. Ence and Margolin, as a result of work on the Ti-A1-0 system:'5 have shown that the a solubility ofalumi-num is considerably restricted, and found that a compound, Ti2A1 existed in the region formerly designated as Q a This structure was identified as hexagonal with c/a = 0.803. Pietrokowsky confirmed the existence of this phase7 and pointed out that the structure was isomorphous with Ti3Sn.8 Although the existence of Ti,A1 has been confirmed by others,9-12 there has been considerable disagreement regarding the composition and mode of formation. A detailed reinvestigation of the Ti-A1 system has been published by Sagel et al.13 The tentative diagram indicated two phases, a, and e, occurring in the former all a region. The a, phase has the same structure as Ti2A1 and was indicated as having a broad region of solubility. Epsilon, a tetragonal phase, was shown to form within the a, solubility region. AS a result of unpublished work,14 Ence and Mugy3 olin disagreed with the interpretation of Sage1 et al., although some common features existed. The present study was conducted in an attempt to clarify prevailing uncertainties. EXPERIMENTAL PROCEDURE Alloy Preparation—Alloys were prepared from iodide titanium (99.9 pct Ti with less than 0.01 pct Zr) or Bureau of Mines electrolytic titanium (BHN-73) and high purity aluminum (99.99 pct). Alloys were arc-melted in argon or helium atmosphere as 15-g buttons in the composition range up to 34 pct Al. Depending on need, alloys were made in increments varying from 0.25 to 2 pct Al. Up to five 15-g buttons of some compositions were made. Weight losses during melting did not exceed about 1 pct of the charge and chemical analysis revealed that both titanium and aluminum were evaporated. In general, nominal and analyzed compositions agreed within 0.5 pct and therefore nominal compositions were used in plotting the data. Unavoidably, some overlap of composition occurred, particularly where small increments of A1 were used. The small increments were primarily used to obtain alloys which would fall into the narrow a -, r region and this purpose was achieved. In general, the data obtained from Bureau of Mines base titanium and iodide titanium alloys were in agreement. Forging—Both as-cast and forged samples were employed. Samples were heated for hand forging by an oxygen-hydrogen torch to the region 1200" to 1300°C. A titanium anvil and cover plate were used to prevent any iron pick-up and consequent formation of a low melting point compound. Frequent reheating kept the temperature in the desired range. Under these conditions, alloys containing up to 15.5 pct could be successfully forged. To check on the depth of contamination, forged alloys were heated slightlybelow the ß transformation temperature. Metal was removed to a depth below the contaminated surface so revealed, and the subsequent results obtained from these samples agreed closely with those secured from as-cast material. Heat Treatment—Prior to heat treatment, all alloys were vacuum annealed to remove hydrogen. Samples

Jan 1, 1962

By Norman B. Braly

The following is not offered as an extended paper on the subject of shaft sinking, but more as a description of the present practice of shaft sinking in the Butte district. The Anaconda company is sinking at present the following shafts: Badger State, Moose, Mountain Consolidated, Mountain View, Pennsylvania and Tropic. At the High Ore and Leonard mines the shafts are being deepened by sinking two compartments and will subsequently be enlarged to the full working size by raising alongside the compartments which are now being sunk. The following other companies are also sinking shafts: Butte-Alex Scott, Butte and Zenith City, Boston and Corbin, North Butte Mining Co. (at the Granite Mountain shaft), East Butte Co. (at the Pittsmont shaft), and the Rainbow Lode Development Co. Shaft Timbering. The shafts of the Butte district, generally speaking, are of three compartments arranged in a straight line, and the pump compartment is usually arranged for the use of an auxiliary hoisting cage, as well as for carrying pipe lines and electric wires. The Rainbow shaft is practically square, and of three compartments. The length of the shafts outside of timber will vary from 17 to 22 ft., and the width from 6 ft. 6 in. to 7 ft. Fir timber is used in all shaft work. This may be obtained from the Coast, when it is known as Coast fir, or from Idaho or Montana, when it is known as native fir. The native fir seems to be the tougher wood, but it is hard to obtain clear lumber in the lengths and sizes necessary for shaft work. Some of the shaft timber of the Anaconda company has been treated with creosote as a preservative, but this practice has not come into general use, as the ground of the camp is so heavy that the timbers usually crush before they rot. The size of timber most used for shaft work is 12 by 12 in., while 10 by 12 in., 10 by 14 in. and 12 by 14 in. are used for some of the special pieces around the shaft. The new Leonard shaft is timbered with 14 by 14 in. wall plates throughout.

Jan 1, 1914

By H. C. Rogers

A phenomenological study of the failure of polycry stalline ductile metals at room temperature was carried out using light and electron microscopy. Tensile fractures as well as sections of partially fractured bars of OFHC copper in particular were examined. The initiation and growth of the central crack in the neck of a tensile specimen occurs by void formation. After the formation of the central crack the f'racture may be completed in either of two ways: by further void formation or by an "allernating slip" mechanism. The first leads to a "cup-cone" failure; the second, to a "double-cup" failure. In the past decade or decade and a half there has been a great deal of emphasis on the solution of the problem of the brittle fracture of metals, particularly those which normally exhibit considerable ductility such as steel. Since the problem of the fracture of metals after large plastic strains has less immediate commercial or defense significance, there has been considerably less effort expended in describing the details of the phenomenology and determining the mechanism of this type of fracture. The present research was undertaken to increase our knowledge in this area. The problem of ductile fracture has not been neglected completely, however. Ludwik1 first found by sectioning a necked but unbroken tensile specimen of aluminum that fracture began with a large internal crack which appeared to have started in the center of the neck. Examination of the fracture indicated that the crack had propagated radially with increasing deformation until a point was reached at which the path of the fracture suddenly left this transverse plane and proceeded at approximately 45 deg to the stress axis until the surface was reached. This gives rise to the commonly observed cup-cone tensile fracture. When MacGregor2 was attempting to demonstrate the linearity of the true stress-true strain curve from necking until fracture, he found that copper was anomalous in that the stress dropped off markedly from the straight line value before fracture occurred. Radiography indicated that in the copper an internal crack was formed long before the final fracture, the stress decreasing during the growth of this crack. One of the most significant advances in the understanding of ductile fracture was the result of work by Parker, Flanigan, and Davis.3 By the use of etch-pit orientations they were able to demonstrate conclusively that the fracture surface at the bottom of the cup, although on a gross scale normal to the tensile axis, did not consist of cleavage facets as had been previously supposed by many investigators. Recently, Forscher4 has shown evidence of porosity near the tensile fracture of hydrogenated zirconium which he attributes to hydride decomposition. The workers at the Titanium Metallurgical Laboratory5 have also shown evidence of porosity in a number of the commonly used metals after heavy deformation. Many metals have relatively low ductility during creep tests at high temperature. The fractures are intercrystalline, resulting from the nucleation and growth of grain boundary voids. The work in this area has been recently reviewed by Davies and Dennison.6 It is possible that some of the observations and conclusions may have a bearing on the present study? especially since at least two studies7,' have been extended down to room temperature and below using magnesium alloys. However, since magnesium does exhibit low-temperature cleavage, these results may not be pertinent to the present one. The use of the electron microscope as an aid to the study of fractures has been extensively exploited by Crussard and coworkers.9 The examination of direct carbon replicas of the fractures of a large number of metals and alloys showed that the bulk of the fracture surface was covered with cup-like indentations of the order of 1 to 2 µ in size. These frequently had a directionality by which Crussard claims to be able to tell the direction of the crack propagation. With this rather disconnected background of information, this investigation was undertaken in the hope of presenting a unified picture of the initiation and propagation of a fracture in a ductile metal. To this end all of the techniques previously used were employed simultaneously so that there might be a good correlation of the data obtained by different techniques. EXPERIMENTAL PROCEDURE The metal which was chosen as the starting material for this investigation was OFHC copper. Of the dozen or so materials considered, it best fulfilled the requirements of commercial availability in large sizes, good ductility, relatively high melting point compared with room temperature and

Jan 1, 1961

By W. J. Maraman, D. R. Harbur, J. W. Anderson

A device for rapidly quenching liquid metals into thin platelets has been developed at the Los Alamos Scientific Laboratory. This rapid quenching equipment is built around the technique of catching a molten drop of metal between a rapidly closing plate and a stationary plate. The design and operation of this unit are described. The closing speed of the smasher plate at impact is 12.6 ft per sec. The quenching rate for this device is controlled by the interface resistance between the plates and the platelet, and is dependent upon the heat content and density of the material being quenched. The initial quenching rate down to the freezing point of the platelet material is lo5º to 106ºC per sec. After an isothermal delay, which is poportional to the heat of fusion of the platelet material, the final cooling rate down to the temperature of the smaslier plates is l04ºto 105cº per sec. RAPID heating of metals by capacitor discharge and other methods has provided the metallurgist with a useful tool for probing into the kinetics of phase changes and the many nonequilibrium phenomena which occur during rapid temperature changes. Equally interesting studies can also be made on metals and alloys which are rapidly cooled from the liquid state.' Studies in this field have been limited, however, because the rates at which metals could be cooled were many orders of magnitude slower than the rates possible for heating. In recent years many new laboratory methods have been developed to rapidly cool metals from the liquid state to ambient temperature and below.2"4 All of these methods involve spreading a liquid drop of metal into a thin foil in a very short time. The methods developed have varied from ejecting a drop of molten metal at the inside surface of a rotating cylinder or stationary curved plate to catching a falling drop of molten metal between rapidly closing plates. The equipment which has been developed at the Los Alamos Scientific Laboratory for rapidly cooling molten materials uses the latter of these two approaches. The basic design, operation, and initial results of this rapid quenching device are given in this report. APPARATUS The drop smasher, which is now being used to obtain rapidly cooled metal foils, is shown in Fig. 1. Basically the device consists of a smasher plate which is driven by a solenoid into a stationary plate. The solenoid is activated by a drop passing through the photoelectric cell and is powered by discharging an adjustable 350-v capacitor bank with a 66-amp peak current into it. This power supply is designed so that the solenoid is powered for 2 m-sec after plate closure to minimize the rebound effect. There is an adjustable time-delay mechanism between the photoelectric cell and the solenoid. Both smasher plates have changeable inserts so that a variety of materials can be used to smash the molten drop. The shaft of the moving plate is guided in an adjustable housing which has ball-bearing walls. The cabinet shown to the left of the drop smasher in Fig. 1 contains the power supply and receiver for the photoelectric cell, the time delay mechanism, and the capacitor bank. The drop smasher can be placed inside a vacuum chamber, for use with radioactive materials, with the upper plate forming the lid, as shown in Fig. 2. On top of the vacuum lid is an induction coil, powered by an Ajax induction generator, which is used to melt drops from the end of the rod extending through the vacuum seal on top the quartz tube. OPERATION The drop smasher shown in Fig. 2 is operated in the following manner. The smasher plates are separated and the unit is lowered into the vacuum chamber using a pressurized cylinder. The induction coil, quartz tube, and lid with sliding vacuum seal are then assembled on top the vacuum chamber. A rod of the material for rapid quenching studies is connected to the rod extending through the sliding vacuum seal. The vacuum chamber is then evacuated and the desired atmosphere established. The photoelectric cell is turned on, and the capacitor bank is charged and armed. Power is supplied to the induction coil, and the rod of material for rapid quenching studies is lowered into the induction field. A molten drop forms on the end of the rod, drops off, falls through the light beam of the photoelectric cell, and is then caught between the smasher plates. .

Jan 1, 1970

By Edmund M. Warner

Any city dweller who has walked alone along a remote mine passageway has to be impressed by the eerie silence-the total absence of noise except for one's own breathing and scuffing of boots on the bottom. An underpound mine can have tremendous contrasts, from complete silence to the ear piercing clatter of percussion drills working in the mine roof. Noise in underground mining machines is both useful and detrimental. Without characteristic noises that are recognizable to miners, operators would have a more difficult job operating their machines. Noise serves as a warning of approaching machinery, and changes in noise give indication that breakdowns may occur. But excessive noise is a health hazard. In recognition of this fact, our congress included noise exposure as a part of the "Coal Mine Health and Safety Act of 1969." As [Fig. 1] indicates, allowable noise exposure is established by specifying a time duration permitted at different noise levels. This is the well known "Walsh-Healey" criteria which govern noise exposure in many industries. In most industries noise exposure is not a constant value. Noise emitted from coal mining machinery varies widely, and therefore interpretation of compliance is not a simple matter. Time, environment, instrumentation and machine productivity, as well as the designed machine characteristics affect the results. It is the purpose of this paper to present the underground coal face machinery noise problem from a manufacturer's point of view. Manufacturers are very much aware of their responsibility to alleviate the noise problem. Not infrequently, orders are received from coal operators that a given new machine must comply with "The Coal Mine Health & Safety Act" noise regulations. Such a request is indicative of the misunderstanding which exists with machine users, while indicating their desire to comply with the law. Obviously, if all machinery could be designed and used at some arbitrary low noise level, it would be possible to simplify the regulations. However, there still remains the pervasive problem of existing machines. Extensive investigation to create practical retrofit kits for existing machines, to substantially reduce noise have been only marginally successful. Certain machine mechanisms are inherent noise makers. The only really good solution is to substitute a quieter mechanism. Such overall new designs have been undertaken, and several examples are mentioned later in this paper. Before describing machine noise problems, it is necessary to define noise values. Noise levels are measured in decibels. The designation "DBA" is decibels measured on the "A" scale, or one in which the frequency sensitivity of the instrumentation is about the same as the human ear. The numbers are often misinterpreted because it is a logarithmic, rather than an arithmetic scale. In comprehending the numbers, it should be remembered that any increase of 3 dB doubles the sound power. In practical terms this means that two noises of equal power at the same distance away increases a dB reading by three. Consider [Fig. 2] showing a simplified case of a worker on a machine subject to

Jan 1, 1980

By Robert F. Mehl

THE solid solutions which aluminum forms with copper, and with magnesium and silicon, are not extensive, and accordingly could not be expected to form Widmanstätten figures profusely nor with great ease. A study of the Widmanstätten figures in these systems seemed desirable, however, because of the interest which these alloys bear towards age-hardening theories resulting from the necessary relationship between the age-hardening phenomena and the atomic processes leading to the formation of Widmanstätten figures.1 ALLOYS OF ALUMINUM WITH COPPER The most accurate determination f the solid solubility, of copper in aluminum seems to be that by Dix and Richardson,2 whose results are represented in Fig. 1. According to this work, aluminum dissolves 5.6 weight per cent of copper at 548°, and less than one per cent at room temperature. Judging from the constitutional diagram, this solid solution on cooling tends to precipitate the compound CuAl2, and this conclusion has been confirmed experimentally by Schmid and Wassermann .3

Jan 1, 1932

By L. R. Shoenberger

Boron has been used to produce nonaging low-carbon sheet steel. Retention of the necessary minimum amount of about 0.006 pet partially killed the steel. Amounts exceeding about 0.012 pet increased the degree of deoxidotion, piping tendencies, and possibility of hot tearing in primary rolling. Semikilled practice resulted in good ingot yields and satisfactory surface quality. Aluminum added with the boron provided a protective de-oxidizer. Good drawobility was indicated by performances of the steel in a limited number of deep-drawing trials. Some problems with hot-tearing and boron-analysis procedures were overcome. Metal lographically, the boron semikilled steels revealed some structures not usually found in plain low-carbon steels. IN 1943 Low and Gensamer1 reported that strain aging, which hardens and embrittles ordinary low-carbon rimmed steel, was due to nitrogen and carbon, and that oxygen played a relatively unimportant role. Since then, many investigators have substantiated their findings and indicated that nitrogen is particularly potent. Commercially, today's most widely produced non-aging sheet steels for deep drawing are either aluminum killed or vanadium rimmed types. The difference in deoxidation practice, alone, is evidence that oxygen is apparently not an important consideration in control of strain aging. The fact that nitrogen is important is apparent in the consideration that has been given, knowingly or unknowingly, to the amount combined with aluminum and vanadium. Patents were granted to Hayes and Griffis2 for the processing of aluminum-killed steel, and to Epstein" for the manufacture of vanadium rimmed material. Certain prescribed steps in producing these steels can be correlated with the formation of the respective nitrides within certain temperature ranges below the usual hot-finishing temperatures. The potential nonaging properties of either type can be reduced or suppressed by cooling too rapidly to permit the aluminum or vanadium to combine with nitrogen. Subsequent suberitical annealing of the cold-rolled strip, however, normally forms the nitrides and produces the resistance to strain aging. Titanium-killed nonaging steel, described by Comstock,1 forms a nitride in the molten state and is essentially nonaging throughout its processing. Zirconium-killed steel, which was investigated briefly by the author,* appeared to have similar nitride- forming characteristics. It is known" that chromium can produce nonaging rimmed steel, but relatively little is known of the potentialities of some of the other nitride-forming elements such as boron, silicon, columbium, and cerium. In attempting to develop a new nonaging cold-rolled sheet steel with good drawability, the following factors were considered pertinent. Such a steel would necessarily have a low carbon content and therefore have a relatively high degree of oxidation when made in a basic open-hearth furnace. If the denitriding element were also a deoxidizer, a part of the addition would be lost as oxide. The degree of deoxidation would determine whether the steel is rimmed, semikilled or killed, and also could be expected to have an important bearing on ingot yields and ultimate surface quality. Assuming that the pattern for the production of cold-rolled sheets would not be changed to any great extent, the nitride must form in the molten steel, in hot rolling, in subsequent cooling, or in annealing. The nitride, once formed, should resist dissociation and be stable in the final product. Usually an excess of the nitride-forming element is required to combine with sufficient nitrogen. If the element used is a strong ferrite strengthener, a small excess may markedly decrease drawability. With aluminum and vanadium, about 0.03 to 0.05 pct in the steel is preferred. Epstein has said" that about 0.30 pct chromium is required. Titanium nonaging steels are hard unless a sufficient amount (about 0.30 pct) is added also to combine with the carbon. The cost of the necessary amounts of these latter two elements discourages commercial acceptance. Silicon was considered as a possible nitride former, but since amounts up to 0.10 pct in rimmed and semikilled steels do not induce marked resistance to strain aging, larger amounts are apparently required, which would tend to harden and strengthen the ferrite. Of the other elements mentioned, all but boron are expensive heavy-metal elements. Stoichi-ometrically, almost an equal weight of boron would be required to combine with the nitrogen—-ordinarily about 0.003 to 0.006 pct in scrap-practice open-hearth steels. Boron is a slightly stronger deoxidizer than carbon but is less powerful than zirconium, aluminum, or titanium. Thus a rimmed-steel practice might be possible. There is much in the technical literature concerning the hardenability effects of minute amounts of boron in killed steels but very little about its behavior in low-carbon material—particularly as a ferrite strengthener. The available data indicated a need for better information concerning the effects of boron in low-carbon strip steels. Experimental Work Development of a Boron-Treated Nonaging Strip Steel—Initial attempts to produce a boron-rimmed strip steel employed 3-ton basic open-hearth heats which could be teemed into molds large enough to sustain a normal rimming action. Boron as ferro-boron was added to the ladle in small amounts because of the reported hot-short character of aluminum-killed heat-treating grades containing more than about 0.005 pct boron. Actually, the amounts used, i.e., 1/8 and 1/4 lb per ton, would be large for

Jan 1, 1959

By O. A. E. Jackson

Pebble milling has been practiced in the reduction works of South Africa gold mines for well over 50 years. Originally flint pebbles were imported from Denmark to grind stamp-mill amalgamation-process tailing, which contained a good deal of extractable gold, but local operators soon found that large pieces of ore could be used for the same purpose. The ore is a hard, tough conglomerate in which quartz pebbles are cemented together by a matrix of redeposited silica interspersed with pyrite crystals. The gold, rarely visible, occurs as fine particles mostly segregated at the interface of the pebble and matrix, although a small fraction occurs within the pyrite crystals. There is seldom any gold in the pebbles themselves. Following the usual South African practice in pebble milling, Union Corp. grinds the ore wet in two or three milling stages incorporating classification. The sized broken ore used as grinding media is separated from the main ore stream in the crushing section that prepares the ore for milling. Where the ore channel, or reef, is narrow there is a shortage of large pebbles. In this case primary grinding may be done in ball mills or, more recently, in rod mills, which cost less per ton to operate. The trend, however, is to prepare finer feed for the milling section. This makes it possible to use smaller primary pebbles and eliminates the need for steel. REDUCTION WORKS OF UNION CORP. LTD. Union Corp. Ltd. exercises financial and technical control over a group of seven gold mines in the Transvaal and Orange Free State. In the Transvaal, with one exception. the mines lie 20 to 40 miles east of Johannesburg, in flat or gently rolling countryside. Winkelhaak, the first of several new mines that will be developed by Union Corp., is located in similar terrain in an entirely new gold mining district about 80 miles east of Johannesburg. Table I gives details of milling units for six of the Union Corp. mines, together with the tonnage milled in 1957. Winkelhaak Mines Ltd. is not included, as it did not begin milling until 1958. This reduction plant has no crushing section; ore is ground directly from the mine (autogenously) in 12x16-ft mills. Because these operations are still in development, they are not described in this article. It will be noted that certain reduction works have mills of more than one size in the same milling stage. This came about when plant extensions in- corporated larger units. In the case of Geduld Propty. Mines Ltd., which began milling operations 50 years ago, the primary stage is stamp milling. The reduction works follow a uniform pattern and are usually joined to the main ore shaft. Ore from other shafts is brought by standard-gage railway and dumped into a common transfer bin. The trend is to increase surface storage capacity to enable the crushing and milling sections to operate at a steady rate, independent of fluctuating ore deliveries from mine. Milling and cyanide extraction divisions of new mines are always designed to allow for extensions as mine production increases. The conveying, washing, and screening system of the crushing section is usually laid out in final form, with additional space for more crushing equipment. The crushing sections operate on one shift during early years of mine production; a second shift is introduced when the mining rate warrants it. Ample surge capacity is provided. Crushing and milling is done only on weekdays, as the law does not allow these operations to take place on Sunday in any plants constructed since 1911. The cyanide extraction sections, however, operate continuously seven days a week, drawing on mill pulp gradually built up in the thickeners during the week. Construction and equipment of milling plants follow standard practice. Dilution water is drawn from a large, high-level tank to obtain constant pressure, but gland service water for the pulp pumps is reticulated from high-pressure, two-stage pumps. The mills are equipped with the most up-to-date machinery and are designed to save labor. They compare favorably with milling plants in countries where native labor does not exist, and automatic controls are being installed wherever feasible. Hydrocyclone classifiers have replaced mechanical classifiers in modern milling plants, chiefly because of the saving in capital outlay, maintenance, and building space. The hydroclones are fed from steady head boxes rather than directly from pumps, and dilution water is introduced into these boxes. Tests have shown that in steadiness of operation and separating efficiency cyclones are comparable to mechanical classifiers. but protective stationarv screens are needed to keep the spigots clear. Rubber-lined pumps are used for pulp of about 3 mesh or finer and metal-lined pumps for coarser material. None of the Union Corp. milling plants practices gravity concentration of coarse gold by amalgamation or the use of corduroy blankets. Studies have proved that no economic case can be made for these methods, which complicate the milling process and demand extra precautions against theft.

Jan 1, 1960

By Franklin G. Pardee

WARTIME depletion of the reserves of iron ore in the Lake Superior region of the grade and character now being shipped down the Lakes was serious. The time has come to take stock of the resources that remain in order to plan our future program of supply for our blast furnaces and protect, as far as possible. the tremendous investment made in the Lake Superior iron mining industry. Hugh M. Roberts and William H. Crago have estimated the reserves of the Lake Superior region in the United States at two billion long tons. These reserve figures are of direct-shipping ore and those concentrates produced by methods now in commercial use or those methods that may be expected in the near future. In their estimate they have assigned 392 million long tons to the Michigan ranges (all reserves in long tons) : 112 million tons for the Gogebic. 140 million tons for the Menominee, and 140 million tons for the Marquette.

Jan 1, 1948