This study investigated leaching kinetics by alternative lixiviants for copper leaching from chalcopyrite (CuFeS2), the most abundant copper resource in the world. As a refractory sulfide mineral, chalcopyrite shows low copper extraction due to passivation on chalcopyrite surface. Also, decrease of copper grade with high portion chalcopyrite requires the alternative leaching procedure to increase copper recovery. Therefore, alternative lixiviants such as sulfurous acid and methanesulfonic acid (MSA) were tested for both concentrate and low grade ore to enhance copper extraction. Also, an oxidant, hydrogen peroxide, was compared to ferric to find out the improvement of leaching kinetic. In concentrate leaching tests, 30 g/L MSA showed the highest copper extraction (47%), compared to other lixiviants at 75 °C. Periodical H2O2 addition enhanced copper extraction, and above 90% of copper extraction was observed within 96 h by periodical addition of 0.6% H2O2 at 75 °C. The activation energy of chalcopyrite leaching by MSA and H2O2 achieved 40 kJ/mol, which is chemical reaction control. The results of low grade ore leaching tests indicates that no significant difference among lixiviants (H2SO4, H2SO3 and MSA) with ferric was observed, all of which achieved around 37% within 24 h at room temperature. However, significant increase of copper extraction (>80%) was observed at both 20 g/L MSA and 10 g/L H2SO4 conditions by the addition of 10% H2O2.

By Ivo André

Sorption of copper ions from aqueous solutions by dried biomass of the aquatic plant Potamogeton luscens was studied at laboratory scale. The aquatic plant was collected in water resources in Brazil, washed, dried at 60°C and ground in a bladed mixer. Sorption experiments were conducted in agitated flasks and in a packed bed column. Maximum copper removal was obtained between pH 5.0 and 6.6 when copper was present in the ionic form Cu'. Sorption followed the Langmuir isotherm with saturation attained at 35 mg/g. Free energy of sorption was found, to be of the order of -25 kJ/mol. Sorption kinetics data were better described by a second order reaction and rate constants were calculated in 0.030 1/(min.mg) for - 4.0 mm particles and 0.081 1/(min.mg) for - 0.59 mm particles. Removal of metal ions in a packed bed column showed that Potamogeton luscens biomass can be used in several sorption/dessorption cycles. After sorbent saturation, copper ions can be recovered from the loaded biomass by elution-with H2SO4, solution. Main mechanism responsible for heavy metal uptake was found to be ion exchange. Results are discussed in terms of the surface properties of the biomaterial, solution chemistry of copper ions and thermodynamics parameters.

Jan 1, 1995

By C. P. Snyman

Three independent methods of coal classification can be distinguished, namely on the basis of grade, type and rank. The latter two can be determined accurately and unambiguously only by means of microscopical techniques. These three independent variables affect all the coal properties and therefore also the technological behaviour of a particular coal. The influence of the inorganic constituents of coal on the fusibility of the ash and on the length of the slag, and also on fouling and slagging, is discussed. The fractionation of the ash-forming constituents during combustion and gasification of pulverised coal shows that fouling and slagging are not related directly to the fusibility and composition of ash of the coal as a whole. The results of combustion experiments using a drop furnace technique indicate that the ignition temperatures of the light volatiles in the coal, and of the formed char, as well as the burn-out time of the char are more dependent on the rank than on the type or grade of the original coal. High-ash coals, however, apparently ignite at lower temperatures and are more reactive than low-ash coals of similar type and rank. The surface properties of coal, which are important in froth flotation and oil agglomeration, correlate well with the inherent moisture content (and by inference with the heat of wetting and the calorific value) and therefore with the type and rank of the coal. In coal exploration, variations of rank offer the possibility of predicting the presence of an intrusion near the seam, thus contributing to more effective exploration and mine planning.

Jan 1, 1991

By F. San Martin, Y. Lefevre, F. Tamargo

The San Juan de Nieva smelter was commissioned in 1960 with an electrolytic zinc capacity of 15,000 t/y. After a number of minor expansions, the capacity was increased to 320,000 t/y in 1991 and will reach 440,000 t/y by August 2001. The expansion involves the construction of a 900 t/day Lurgi roaster and a new acid plant. The leaching will be fully revamped and modernised, including the construction of a new building for residue treatment and for j arosite precipitation with a separate circuit for silver-containing concentrates. The project also includes the construction of a fully automated 137,000 t/y zinc cathode tankhouse fitted with 3.4 m2 cathodes designed by Asturiana de Zinc, and based on the existing tankhouse and introducing some improvements. New melting and casting facilities, also designed by Asturiana, will be constructed.

Jan 1, 2000

By Jafar Safarian

Bauxite is the main raw material used for the production of alumina (Al2O3) through the well-known commercial Bayer process. This process has significant challenges such as limitation in using low-grade bauxites as they contain significant amounts of impurities such as Fe, Si, Ti. The Bayer process residue, which is known as red mud, is also a global environmental challenge due to huge amount of this low value residue production. An alternative sustainable process with high potential to solve these problems and produce valuable and consumable by-products is a pyrometallurgical-hydrometallurgical process in which the low-grade bauxite ore is treated through a smelting-reduction process, yielding iron alloys and a calcium-aluminate slag. Alumina is then produced from the slag by hydrometallurgical treatment. In the present work, the reduction of pellets produced from different bauxite ores by hydrogen is studied and it is shown that complete iron oxides reduction is possible. Further smelting and smelting-aluminothermic reduction of the reduced pellets show that iron and silicon ferroalloys can be produced, in addition to a proper slag for alumina extraction.

By L. Xia

Sodium silicate(s), also known as “water glass”, are one of the oldest and most widely used industrial chemicals. Its first use in Canadian operations can be traced back to around 1925, which coincided with early use of xanthates in mineral flotation. Silicate functions as a sulphide and non-sulphide gangue mineral dispersant, depressant and modifying reagent in grinding and flotation operations. It is believed that soluble sodium silicate promotes selectivity of value added sulphides against gangue minerals, resulting in both grade and recovery improvement. This paper seeks to link improved grade/recovery to the interaction characteristics of minerals and the sodium silicate. A systematic study was performed with individual mineral species, an artificially designed model ore and the feed ore from a copper flotation operation. The function of sodium silicate was evaluated in the context of colloidal chemistry and linked to mineral surface chemistry. Measurement of pulp rheology and mineral zeta potential identified that sodium silicate works as a dispersant. The dispersion is accomplished by increasing a mineral’s net surface charge, resulting in a change in slurry viscosity. Bench scale laboratory flotation tests suggest that better dispersion leads to a diminished interaction of chalcopyrite with gangue. The improved Cu grade and recovery then are likely in response to an increased accessibility to collector along with a linked increase in particle bubble attachment resulting in better separation efficiency. ToF-SIMS surface chemical analysis of the flotation samples found a higher proportion of sodium silicate on minerals from the flotation tailings relative to the concentrates. Moreover, attachment of sodium silicate appears to be mineral specific; the data indicates that sodium silicate favours the surface of gangue phases over the value sulphides.

By Zhang Yongzhu

Sulfoxides are one kind of extractants for precious metals. The structure, the coordination reaction, the extraction behaviour and the precious metals complexes of sulfoxides are summarized. The differences between sulfides, sulfoxides and sulphones are also discussed.

Jan 1, 1992

By L. A. André Santos

Atmospheric processing of nickel lateritic ores with low costs has been encouraged. In this work the kinetic of atmospheric acid leaching of a northern- Brazilian ore with 1.63% Ni and large amount of fine particles (d50 ≈ 0.075 mm and 40% below 0.038 mm) is presented. Chemical analysis showed a trend of Ni and Fe concentration in finer fraction (−0.075 mm) and Si and Mg in the coarsest one (−0.500 + 0.150 mm) associated to distinct mineral phases. Nickel is widespread in the mineral matrix. Distinct behaviors were observed as a function of particle size associated to the distribution of silicates and iron oxides in the ore. The kinetic modeling indicated that leaching is controlled by porous layer diffusion at 65 °C, but at 95 °C exhibits a mixed control by porous layer diffusion in initial minutes (60 min) and by chemical reaction or diffusion through the pore layer in final minutes (60–240 min) depends on metal evaluated.

By Donghai Li, Cheng Pan, Xuewei Lv, Mei Liu, Enguang Guo

"Phosphorite is the main raw material for the production of phosphorus in chemical industry. More attentions have been drawn to the phosphorite concentrate beneficiated from low-grade phosphorite due to the decrease of high-grade phosphorite. For another, the agglomeration process is necessary for the phosphorite concentrate after beneficiation process. The mineralogy and sintering process of the phosphorite from Leshan, China were studied in this work. The result shows that the main phases in the phosphorite are fluorapatite (Ca3(P04)3F), hydroxylapatite (Cas(P04)3(0H)), quartz (Si02) and dolomite (CaMg(C03)2). The yield of the sinter increases with increasing the carbon dosage to 7%, and then decreases when it continuously increases. Similar regularities were found for the strength and the content of P20s of the sinter. The best strength of the sinter as well as its P205 content were discovered when the carbon dosage is 7%. Fluorapatite ((Ca5(P04)3)F) is the main phase in the sinter while fuggerite (Ca2MgSiz01) is the main binder phase.IntroductionPhosphorus is an important foundation industrial raw material of national defense industry, food industry and chemical industry, where it is used to produce red phosphorus, phosphonium hydroxide, phosphorus pentasulfide and phosphoric anhydride[l-2]."

Jan 1, 2013

By John R. FitzPatrick

The separation and purification of uranium from either nitric acid or hydrochloric acid media tan be accomplished by using either solvent extraction or ion-exchange. Over the past two years at Los Alamos, emerging programs are focused on recapturing the expertise required to do limited, small-quantity processing of enriched uranium. During this period of time, we have been investigating ion-exchange as a method for extraction/purification of uranium from acidic media. In addition, waste stream polishing is associated with this effort in order to achieve more complete removal of the uranium prior to recycle of the acid. Extraction chromatography has been demonstrated' to further polish the uranium from both nitric and hydrochloric acid media thus allowing for a more complete recovery of the actinide material and creation of less waste during the processing steps. We will discuss contact experiments for evaluation of eleven different resins for uranium removal from nitric acid, the evaluation (again by contact experiments) of uranium elution from the ion-exchange media by various chemicals, and small-scale experiments for the removal of 235U from nitric acid. Larger-scale (100-gram) flow experiments using depleted uranium, were done after the small-scale evaluation Of the selected resin. A discussion is also included concerning the shortcomings of the contact experiments and how the flow experiments were modified in order to overcome these problems. We will also discuss the application of ion-exchange for some specific process needs at Los Alamos Contact experiments were used to evaluate some commercially available solvent-impregnated resins in addition to evaluation of several resins of this type synthesized in our laboratory. These experiments' involved both nitric and hydrochloric acid media. The data from these experiments will be used to determine the column size and' amount of resin required to polish the waste stream produced by the ion-exchange process described above. Small-scale flow experiments will be described and data given on the mass balances achieved using this two step process. Future work for evaluation of new ion-exchange and solvent-impregnated resins as well as the search for new eluants will be discussed. Other future experiments for both processes, including large-scale experiments, will be discussed in detail.

Jan 1, 1996

By Ailton S. Ferreira, Rubén J. Sanchez Rodriguez, Sergio N. Monteiro, Felipe Perissé D. Lopes, Teresa E. Castillo

"Polyester composites reinforced with natural lignocellulosic fibers have, in recent times, been gaining attention in engineering areas as lighter and cheaper alternatives for traditional composites such as the ""fiberglass"". One of the strongest, the curaua fiber, is today being considered as reinforcement of composites for automobile interior parts. In fact, several research works are currently being dedicated to curaua fiber composites since physical and mechanical properties are required for practical uses. In this work, the thermal behavior of polyester composites reinforced with up to 30 % in volume of curaua fibers was investigated by differential scanning calorimetry, DSC. The results showed endothermic and exothermic events associated with water release and possible molecular chain amorphous transformation. Comparison with similar composites permitted to propose mechanism that explains this DSC thermal behavior.IntroductionThe modem composite materials, especially those reinforced with synthetic fibers such as glass and carbon, have been used since last century to attend the demands required by most technological fields, from home appliances to aerospace [1]. In fact, fiber composites offer significant advantages over monolitic materials, such as common metallic alloys, plastic and ceramics. One of the most important is the ratio between the ultimate stress and the density, known as the specific strength. For example, in common glass fiber polymer composites, the so called ""fiberglass'', the specific strength of around 400 MPa.cm3/g is higher than any conventional monolitic material. However, drawbacks exist. The energy required to fabricate ""fiberglass"" generates large emissions of C02, which are responsible for global warming. Moreover, ""fiberglass"" is not recyclable and cannot be incinerated [2]. As a result, most synthetic fiber composites end up in landfills or contribute to rivers and oceans pollution."

Jan 1, 2011

By J. J. Talja

An investigation of oxidation of various nickel concentrates was carried out using differential scanning calorimetry (DSC). The aim of this study was to determine the ignition temperature and investigate other oxidation behavior of various sulfide-based nickel concentrates. Variables in the experiments were mineralogy, particle size and partial pressure of oxygen with temperature increasing linearly at 25 K/min from 323 to 1023 K (50-750 °C). The igni¬tion temperature was determined to represent the starting point of rapid oxidation. The reac¬tion enthalpies of the concentrates were determined and the amount of heat generated up to various time were used to calculate the extent of reaction. Mineralogical changes at various stages of oxidation were also investigated. For this purpose a second set of DSC-experiments were carried out in which each experiment was interrupted at a desired temperature between 673-873 K. From these tests the weight loss of samples were determined and changes in the individual constituent of sulfide minerals were analyzed. For pentlandite-based Ni-concentrates the ignition temperature was 705-710 K (approximately 435 °C). Pyrite was the first sulfide to oxidize. Reactivity of the violarite-based concentrate was greater than those of the pentlandite-based concentrates. The stoi-chiometry of pentlandite changed before ignition because of preferential oxidation of iron. Rapid oxidation of the pentlandite mineral occurred at about 823 K (550 °C). By 900 K about 90 % of the iron in pentlandite was converted to hematite, and NiS containing some iron was formed.

Jan 1, 1994

By Minjun Tang, Jianfeng Zhou, Feng Chen, Linjiang Qing, Xiaolei Song, Yufeng Guo, Tao Jiang

"Reduction swellability index (Rsn and low temperature reduction disintegration index (RDI) of vanadium-titanium magnetite oxidized pellets are harmful to the processing of ironmaking, for example, causing serious gas permeability, decreased yield, higher coke ratio and more furnace dust. Thus, the improvements of RSI and RDI of vanadium-titanium magnetite oxidized pellets were investigated in this paper, including the pretreatment of raw material, additives of dolomite or boric acid, pellets treated in chloride solution and so on. The results showed that damp milling as pretreatment and boric acid added in pelletizing were conducive to the RSI which decreased 5% and 7% respectively, while they were not efficient enough in improving RDI. Dolomite was efficient in improving RSI, but had negative effect on RDI. There was no evidence to show that RSI and RDI would be improved when pellets were treated in chloride solution. Pursuing this further, the mechanism of those improvements were investigated.IntroductionIn the world, vanadium-titanium magnetite utilization is investigated around how to recover iron, titanium, vanadium, and divided into blast-furnace method and non-blast-furnace method according to respective characteristics. Blast furnace method [1, 2] can recover iron and vanadium effectively, but Ti02 cannot be recycled. Non-blast-furnace methods include rotary kiln-electric furnace method, pre-reduction electric furnace method, reduction- grinding method and sodium vanadium-rotary kiln-electric furnace method and so on. [3-7]Comparing to the Non-blast-furnace method, the method of blast furnace smelting has been put into industrial applications. And it has the following advantages: First of all, effective recycling iron and vanadium; Second, technical problems of high titanium slag in blast furnace smelting; Third, it has mature technology in blast furnace smelting."

Jan 1, 2013

By William Petruk

A fully automatic image analysis system that consists of a microprobe, an energy dispersive x-ray analyzer, and an image analyzer was developed at CANME:I' to determine mineral behaviour that affects beneficiation. The interlacing between the instruments permits automatic identification and characterization of minerals in samples of unbroken ore pieces and of mill products. Different types of information are obtained for minerals in samples of unbroken ore pieces than in samples of mill products, and are used differently. For unbroken ore pieces size distributions are determined for discrete mineral grains to predict a grind at which they might be liberated, and other measurements are Irade to predict the percentage of mineral that occurs as nonrecoverable grains. For mill products the minerals are analysed to determine percentages that (1) are free, (2) are likely to be recovered in concentrates, (3) are likely to be lost to tailings, and (4) could be liberated with regrinding. The image analysis data for mill products are processed by a mineral-metals balance program to determine the distributions of free and unliberated mineral grains at each point in a concentrator, pilot plant or bench test. For samples containing trace minerals, such as gold, an automatic search technique is used to scan the entire area of the polished section for the trace mineral grains. The identified trace mineral grains are characterized with regard to size, liberation, and other properties.

Jan 1, 1988

Lead blast furnace water-jacket stability was investigated by examining samples from the Port Pirie Lead Smelter. The compositions of the phases formed in the samples were analysed using Scanning Electron Microscopy (SEM) and Electron Probe X-ray Microanalyser (EPMA). Phase equilibria analysis and thermodynamic modelling was undertaken using FactSage with latest thermodynamic database for the slag/matte/metal/speiss/solids multi-component Cu2O–PbO–ZnO– Al2O3–CaO–MgO–FeO–Fe2O3–SiO2–S major and As–Bi–Sb–Sn–Ag–Au minor elements system. Results indicated that the stability of the water-jacket steel wall without freeze-lining is influenced by formation of the complex Fe-rich speiss phase at critical As concentrations. The integrity of the furnace walls with freeze-lining is critically dependent of the stability of the oxide-based freeze-lining which is dependent on various factors including most critical one—the proportion of solids determined by the slag chemistry and fluxing. Thermodynamic modelling of the lead blast furnace operation indicated limiting thermochemical conditions for the water-jacket stability. Factors and controls critical to the water-jackets integrity are discussed.

By G. Granata

In this work, we studied the recovery of copper from AMD by cementation with iron powder. To control the size of copper particles within the nanoscale range, we tested the use of the anionic surfactant sodium dodecyl sulfate (SDS). We tested three concentration levels (0.2, 0.4 and 0.6 M) and temperatures (25, 50 and 75 °C). The activation energy of cementation was also assessed by fitting the experimental data with the Arrhenius equation. Under all investigated conditions, the cementation reaction was found to be a diffusion-controlled process. Without surfactant, the activation energy was 19.9 kJ/mol. In the presence of SDS the activation energy increased up to about 35 kJ/mol. With or without SDS, the particle size of the copper product was strongly affected by the cementation temperature. Without SDS, the cemented product aggregated into micro-sized clusters of about 15 μm at 25 °C, 2–3 μm at 50 °C and 1 μm at 75 °C. The addition of SDS resulted in a dramatic decrease of copper particle size up down to the nanoscale range. Under the best operating conditions, the particle size of copper was <100 nm.

By Xiangwen Wang

Electrochemical measurements associated with the electrowinning of lead metal from concentrated brine (NaCI) - lead chloride (PbCI,) electrolytes at temperatures in the range 328 to 353°K (55 - 80°C) were conducted. The electrodeposition of lead metal onto a lead rotating-disk electrode may be described by the electrodic reaction: {PbCl 4 2 + 2e- = Pb° + 4Cl-} The deposition-overpotential requirements are low (approximately 41mV per decade of current density - Am+), with a corresponding high exchange current (approximately 0.018 A.cm2). The diffusion coefficient of the electroactive PbC142- species in a 3.5 NaCl electrolyte at 353°K was insensitive to the total PbCI, concentration (0.01 to 0.1M), and its value was found to be (1.21*0.1)~10-5 cm2Is with a temperature-sensitivity coefficient (E,/R) of approximately 1.98x103K-1 (328OK(T<353OK).

Jan 1, 1993

By Shengli Tao, Hongxu Li, Hao Bai, Yu Chen, Daqiang Cang

"China is the world's largest steel producer, in order to give environment load comprehensive analysis of steel and iron industry in china using LCA method, the life cycle inventory was compiled and assessment model based on Gabi software was also established. Environmental impact of two different routes ofBF-BOF and the EAF were analyzed respectively and intercompared. The results show that the modem EAF route is superior to the traditional BFBOF route on almost all the environmental impact indexes, which including acidification potential, eutrification potential, global warming potential, ozone depletion potential, etc. In the whole life cycle ofBF-BOF route in China, the transporting process ranks the biggest contribution part to the overall global warming potential, which can be explained by the fossil fuel burning of transporting vehicles during the long distance from Australia to China as the iron ore used are mainly imported from Australia. Apart from transporting process, Coking, blast furnace and iron mining processes could induce great environmental problems, while for the EAF route, the electricity consumption is considerable, which causing large amount ofC02 emission indirectly. Based on the analysis, several further countermeasures were proposed. Key words: Iron and steel industry, LCA, Gabi software, C02 emissionIntroductionCrude steel of china which reached 101.24 million tons in 1999 ranked the first column in the world since1999, So far has been to keep the world's largest steel output. At the year of2009, China crude steel output of 568 million tons, accounting for 46.6% of the global crude steel production, more than the total sum of crude steel production produced by 20 countries ranked behind. In 2011, China's crude steel production which is expected to be or close to 700 million tons, an increase of 12% than last year, will account for half of the global steel production.The steel industry, however, is intensive resources industry with huge consumptions of energy and water together with mineral resources. Energy consumption of the iron and steel industry has been about 10% of the total energy consumption since 1980. Coal dominants, power next and other energies share least in the energy consumption structure, for example coal accounts for 72.19%, power 23.52% and other total sums less than 5% in the steel energy consumption at year of 2002[2,3]. The consumption of coal discharges much emission of CO2, yet emissions of C02 in China steel industry, secondary only to the power and cement industry, ranked the third, and the coal dominant energy structure and its process have a close relationship. The aim of this research is to target steel production of typical blast furnace-converter (BFBOF) and electric furnace, using GABI software to evaluate and analyze resources and environment influence of LCA, directing at the existing problems in the development of China steel as well as finding the possible way to improve ability of reducing pollution and energy consumption in order to realize the sustainable development of the steel industry [ 4-7]."

Jan 1, 2012

By V. I. Lakshmanan, R. Roy

"TiO2 is used in paints, plastics, rubber, paper, inks, textiles and other miscellaneous applications. The demand for the pigment grade Ti02 is growing at 3.0%/year on average and this invites the development of innovative and cost effective processes. The current processes are not designed to recycle the reagents and thereby discharge the effluents into the environment, causing an environmental concern.During this study, synthesis of TiO2 from an ilmenite concentrate was investigated using an innovative atmospheric mixed-chloride leach process. The solution purification was carried out using solvent extraction in two stages. In the first stage iron removal was carried out and in the second stage titanium was extracted. The strip solution obtained from the second stage solvent extraction contained the purified titanium and from this stream pigment grade Ti02 was recovered. The barren solution was used for reagent recovery and the regenerated leach liquor was recycled."

Jan 1, 2011

By Jinliang Zhang, Jian Pan, Deqing Zhu

"Limestone and burnt magnesite were added to vary MgO content and basicity (CaO/SiO2 ratio) of pellets for investigating their influences on the properties of specularite pellets. At fixed MgO content, the addition of limestone does not affect on the properties of green balls significantly. The addition of burnt magnesite has obvious influence on the quality of green balls, especially on the thermal shock temperature. Without burnt magnesite, the thermal shock temperatures are about 400°C, and, the thermal shock temperature increases to 600~630°C by adding burnt magnesite. For preheated pellets, when the burnt magnesite is added, the compressive strength will be decreased. For roasted pellets without burnt magnesite, the calcium additives can form binding phase of calcium-ferrite, and suitable liquid phase will improve recrystallization of hematite, but excessive liquid will destroy the structure of pellets, so the compressive strength of pellet increases firstly and then decreases. When adding burnt magnesite, the compressive strength will increase as the basicity increases. When the basicity is more than 0.2, the compressive strength of the pellets various MgO content and basicity is above 2500N/pellet and then MgO-bearing fluxes can be added to prepare pellets with good high temperature properties.IntroductionWith the rapid development of the steel industry in China, oxidized pellets, possessing good mechanical and metallurgical properties, are becoming indispensable burdens for blast furnace ironmaking [1-3]. However, this has resulted in the shortage of domestic iron concentrates, so many Chinese steel plants begin to use imported hematite concentrate to prepare pellets. Compared with magnetite pellets, the hematite pellets require high roasting temperature and narrow roasting temperature range (1300–1350°C) and possess low compressive strength [4,5].1"

Jan 1, 2012