By I. Cadoff, J. P. Nielsen

The Ti-C phase diagram exhibits a peritectic point at 1750°C and 0.8 pct C, and a peritectoid point at 920°C and 0.48 pct C. The maximum solubility of carbon in a titanium is 0.48 pct. The 6 region containing the Tic compound (20 pct C) extends to 11 pct C at the peritectic temperature. THE interest in the Ti-C alloy system stems from the fact that carbon occurs as an impurity in titanium alloys when graphite electrodes or graphite crucibles are used in their melting. Since titanium-base alloys are still in the development stage, some virtue may be found in carbon addition to titanium. The Tic compound is currently emerging as an important powder metallurgy base constituent similar to the WC compound. Ehrlich' identified the phases and structures present in the Ti-C system. The peritectoid region of the phase diagram was investigated by Jaffee et al." A preliminary diagram based on theoretical considerations was proposed at the outset of this research." The Tic compound has been investigated extensively and has been reported on in a large number of papers. Experimental Procedure Arc-melted alloys of 24 compositions in the range 0 to 20 wt pct C were investigated using metallography, X-ray diffraction, and, for the liquidus and solidus regions, incipient and complete melting. All alloys were prepared from iodide titanium (New Jersey Zinc Co., 99.95 pct Ti minimum) and spectroscopic grade carbon (National Carbon Co.). To prevent carbon spattering during arc melting the carbon was encapsulated in titanium. For alloys containing less than 1 pct C the powder was inserted into a capsule formed by drilling a hole in the as-received rod. For higher compositions, capsules were formed from titanium sheet. Arc Melting: The charges were melted in the copper-hearth cold electrode furnace shown in Fig. 1. This furnace is similar in principle to the all-metal unit adapted for titanium melting at Battelle Memorial Institute.' The transparent pyrex walls giving unlimited visibility during operation and the multiple-

Jan 1, 1954

By R. R. Boucher, O. J. C. Runnalls

A pronounced thermal effect has been observed on heating or cooling a1wninum-rich Al-U and Al-Pu alloys. From microscopic and X-ray diffractionstudies, the effectl has been attributed to trnsfor)nations in the inlemetallic phases UAl, and PuAl , involuing rearrangement or cluslering of vacancies The transformation obsrved in Al-20 wi oct U alloys occurred near the a Al-UAl4 eutectic tem-perature of 646°C making it difjicult to detect from heating curves. When cooling, howeoer, thermal mad X-ray analyses indicnted that the high-temperati~re phase labeled p UAL, precipitated initially during euitectic solidification. As solidification continued and after an induction period o-f 5 lo 20 tnin the nu-cleatiorz and growth of the low- twmperature phase, a UAl4 produced an euolution of energy which raised the observed alloy temperature by 1° to 2°C. in Al-Pu alloys the transformation occurred at 645°C, 5 deg below the eutectic solidification temperccture. The eslimated latent heat of transformation was 25 +5 cnl per g PuAl,. The high-tetnpevcl-ture forms of UAl, and PuAl, were easily 9-etccined by chill casting Al-U and Al-Pu alloys and on reheating the alloys the trcltzsforrnation to the a phase was sluggish even above 600°C. Separated single cryslals o-f UAl4, joy example, showed no evidence Of transformalion after heating for 16 hr at 620°C. The transformation rates increased yapidly enough with increasing temperature, however, that a a spontaneous liberation of energy lens observed on occasion when bealing cast Al-20 wt pet U to neal- the RECENT phase studies on A1-Pu alloys have indicated that earlier reported equilibrium diagrams should be modified to take account of several poly- morphic transformations in the intermetallic compound PuAl,.' During the course of the latter work an unexpected heat evolution was observed while cooling a solid alloy consisting of a mixture of a aluminum and PuA1,. The evolution occurred at 645°C, y below the a A1-Pu A1, eutectic solidification temperature. Subsequent thermal-analysis experiments with A1-U alloys showed that heat was evolved there also at a temperature nearly coincident with the a A1-UA1, eutectic solidification temperature of 646°. A search of the literature revealed that similar thermal effects had been observed before for both A1-U and A1-Pu but had never been fully explained.2,3 The purpose of the present paper is to describe thermal-analysis and X-ray diffraction experiments which have led to the conclusion that the thermal effects are due to transformations which involve the rearrangement of vacancies in the intermetallic compounds UA1, and PuA1,. EXPERIMENTAL PROCEDURE The A1-U alloys were prepared by heating super-pure aluminum (99.99 pct +) obtained from the Aluminum Co. of Canada in a graphite crucible surrounded by an induction coil. At 1000°C high-purity uranium metal produced by the Eldorado Mining and Refining Co., Ltd. was dropped into the liquid aluminum and was dissolved completely within 15 min. The impurities in the uranium were A1—4 ppm, Ca-4, C-70, Cr-3, Cu-6, Fe-30, Mg-2, Mn-10, Ni-25, Si-25, and Zn-2. The A1-Pu alloys were prepared by reacting plutonium dioxide with liquid aluminum under cryolite (3 NaF . AlF,) for 10 min at 1100°C in graphite crucibles exposed to the air. The plutonium was 99.8 pct pure, containing trace impurities of Ca, Cu, Fe, Pb, Si, and Zn. The liquid alloys were usually poured into water-cooled molds to provide castings of uniform composition from which samples could be cut for heat treatment and thermal-analysis experiments.

Jan 1, 1965

By E. O. Kirkendall

The investigation reported herein was undertaken to obtain data to supplement those presented in an earlier paper,l particularly for longer times at a higher temperature. This information may further develop our knowledge of the mechanism of diffusion in substitutional solid solutions. Diffusion of solute atoms interstitially dissolved is not difficult to visualize: it can take place without much disturbance of the solvent atoms. The mechanism of diffusion of solute atoms substitutionally dissolved is not so easily understood. Many theories have been advanced. Rosen-hain,2,3 Frenkel,4 Smekal,5 Langmuir,3,6 Steigman, Shockley and Nix,' and Johnson8 all proposed theories to explain diffusion. Langmuir's proposed mechanism consisted of a simple cyclic interchange of atoms involving an interchange in lattice positions of four or more atoms. This mechanism, accepted by the author at the time of his previous publication,1 and apparently quite generally accepted, required a net exchange in positions of both solute and solvent atoms in equal numbers. In other words, the rate of diffusion of the solvent and solute atoms would be the same. That this cyclic interchange in lattice positions of solute and solvent atoms in equal numbers is the only true mechanism of diffusion is denied by the evidence presented in this paper. Experimental Procedure This modification of similar procedure1 will be outlined briefly. The method consisted of the following steps: I. A pure Muntz metal (60.6 per cent Cu, 0.1 per cent total impurities) that was almost all beta brass at 780°C. was chosen. 2. The brass was turned between centers in a lathe to a diameter of 0.5965 inches. 3. After the brass was cleaned, it was electroplated with pure copper to a diameter of about one inch. 4. The sample was heated slowly to 400°C. under reduced pressure and held at that temperature for 4 hr. to remove occluded gases. It was then cooled to room temperature. 5. The sample was heated to 780°C. ± 3°C. and held at that temperature for different lengths of time; then quenched. Samples were cut off each time after quenching. Metallographic samples 1/4 in. thick were removed at I hr., 6 hr., 24 hr., 96 hr. and 701 hr. After 96 and 701 hr. samples of about I in. were removed for X-ray analysis. 6. The metallographic samples were polished on the cross section and photomicrographs were taken. 7. The I-in. samples were polished and etched on both ends. With the aid of a microscope each was carefully mounted in a four-jaw chuck in a lathe, so that they could be accurately bored for an arbor. 8. Turnings were taken for each X-ray sample. After each set of turnings, the sample was heated in an oil bath for about 1/2 hr. at 300°C. It was then etched in 25

Jan 1, 1942

By E. O. Kirkendall

The investigation reported herein was undertaken to obtain data to supplement those presented in an earlier paper,l particularly for longer times at a higher temperature. This information may further develop our knowledge of the mechanism of diffusion in substitutional solid solutions. Diffusion of solute atoms interstitially dissolved is not difficult to visualize: it can take place without much disturbance of the solvent atoms. The mechanism of diffusion of solute atoms substitutionally dissolved is not so easily understood. Many theories have been advanced. Rosen-hain,2,3 Frenkel,4 Smekal,5 Langmuir,3,6 Steigman, Shockley and Nix,' and Johnson8 all proposed theories to explain diffusion. Langmuir's proposed mechanism consisted of a simple cyclic interchange of atoms involving an interchange in lattice positions of four or more atoms. This mechanism, accepted by the author at the time of his previous publication,1 and apparently quite generally accepted, required a net exchange in positions of both solute and solvent atoms in equal numbers. In other words, the rate of diffusion of the solvent and solute atoms would be the same. That this cyclic interchange in lattice positions of solute and solvent atoms in equal numbers is the only true mechanism of diffusion is denied by the evidence presented in this paper. Experimental Procedure This modification of similar procedure1 will be outlined briefly. The method consisted of the following steps: I. A pure Muntz metal (60.6 per cent Cu, 0.1 per cent total impurities) that was almost all beta brass at 780°C. was chosen. 2. The brass was turned between centers in a lathe to a diameter of 0.5965 inches. 3. After the brass was cleaned, it was electroplated with pure copper to a diameter of about one inch. 4. The sample was heated slowly to 400°C. under reduced pressure and held at that temperature for 4 hr. to remove occluded gases. It was then cooled to room temperature. 5. The sample was heated to 780°C. ± 3°C. and held at that temperature for different lengths of time; then quenched. Samples were cut off each time after quenching. Metallographic samples 1/4 in. thick were removed at I hr., 6 hr., 24 hr., 96 hr. and 701 hr. After 96 and 701 hr. samples of about I in. were removed for X-ray analysis. 6. The metallographic samples were polished on the cross section and photomicrographs were taken. 7. The I-in. samples were polished and etched on both ends. With the aid of a microscope each was carefully mounted in a four-jaw chuck in a lathe, so that they could be accurately bored for an arbor. 8. Turnings were taken for each X-ray sample. After each set of turnings, the sample was heated in an oil bath for about 1/2 hr. at 300°C. It was then etched in 25

Jan 1, 1942

By B. R. Palmer, G. Gutierrez B., M. C. Fuerstenau

Flotation responses of chrysocolla and rhodonite are correlated with electrophoretic mobility and infrared spectroscopy measurements. Flotation is effected in the pH ranges in which hydrolysis of the metal ions comprising the mineral occurs. The roles of mineral solubility and precipitate formation are suggested.

Jan 1, 1976

By B. Ball, C. H. Cox, S. N. Yap

Electrokinetic measurements on cassiterite were made in the presence of sodium di-hydrogen phosphate, mono-hydrogen arsenate, bisulfite, and sulfate. Flotation studies were also conducted using sodium dodecyl sulfonate in the presence of these salts. It was found that the anions specifically adsorb on cassiterite in the order H2AsO-4 H2PO4 HSO3 SO4 and consequently cause flotation depression. The adsorption mechanisms of the various inorganic anions are discussed in detail.

Jan 1, 1980

Jan 1, 1935

By T. S. Liu, E. A. Peretti

A LITERATURE survey of the In-Sb system, which was made before a study of the binary diagram was undertaken, revealed that the intermediate phase InSb existed and that its crystal structure is face-centered cubic of the zinc blend type. In 1929 Goldschmidt' determined the lattice constant for InSb and obtained a value of 6.452A. A more recent value, 6.461A was reported by Iandelli2 in 1941. The purity of the indium used was not very high, however. The indium used by Iandelli contained 2 pct Ge. In view of this fact it was decided to remeasure the lattice parameter using high-purity indium (99.97+ pct In) and spectrographically standardized antimony of the highest purity available (99.91 pct Sb). Specimens corresponding to the InSb composition were made by carefully weighing the ingredients on an analytical balance and heating them in vacuo in a quartz tube at 700°C. As melting losses were negligible, the alloys were not analyzed chemically, but the intended analysis was taken as being accu- rate. Powder samples were prepared by either filing or crushing of the brittle alloy, followed by screening at 325 mesh. The powders were then annealed at 400°C in evacuated capsules for about an hour. X-ray photograms were taken with a Debye and a back-reflection focusing camera, using characteristic cobalt K. radiation. Lattice parameters were calculated by Cohen's³ method. The results of a Debye pattern and of a back-reflection pattern at 25°C are given in Tables I and 11. The lattice parameter at 25 °C is 6.47602A.

Jan 1, 1952

By John D. Ridge, Robert C. Barwick

In contrast to international trade in lead, a much larger percentage of zinc shipped from one country to another is shipped in concentrate form. In 1952 international commerce in zinc concentrates accounted for 37 pct of world zinc mine production, and of the total zinc which traveled from one country to another, slightly more than 65 pct was in concentrates. The comparable figures for lead, given in Part VI, were 16 and 27 pct. Of the zinc mined in the world in 1952, 56.6 pct entered international trade; the analogous figure for lead was 57.4. This similarity in proportion of production traded is paralleled by a similarity in sources of exports. The three leading exporters of zinc in all forms in 1952 were Canada, Mexico, and Australia, in that order; the three largest exporters of lead were Mexico, Australia, and Canada. In contrast to the 86 pct theoretical maximum in lead concentrates, the maximum for zinc concentrate is only 67 pct. On this basis alone, it would be reasonable to expect that more zinc would be traded as zinc metal than lead as lead metal. Actually, the reverse is true. Less than 28 pct of the lead in international commerce moves as lead in concentrates, while 65 pct of the zinc so traded is as concentrates. Mexico, a country which has attempted to retain as much metal processing activity as possible within its own borders, has negligible exports of lead in concentrates.

Nov 1, 1955

Jan 1, 1944

By THOMAS J. CLIFFORD

IN 1926, finer grinding began to be a feature of the milling practice of the Southeast Missouri lead district. Nothing since the adoption of flotation has caused greater changes and greater improvement in results. The trend toward finer grinding, with the consequent discarding of tailing at finer sizes, and consequent lower assays in lead, continued to progress until 1931, when the abnormally low price of lead brought a halt: that is, the better metallurgical results obtained would not offset the increased costs due to higher power and necessary maintenance. Since 1931 a slight tendency toward the discard of coarser tailing has taken place. , In 1926, larger rod mills i.12 ft. 1 in. by 6 ft. 6 in.) than any previously used in the district were installed in cue plant, and a new primary crushing plant, of greater capacity was built. This combination demonstrated immediately the better metallurgical results obtainable by finer grinding and all the mills now running have adopted the practice.

Jan 1, 1934

By W Lindlief, Cyril Stanley Smith

Several investigators, mainly concerned with the mechanical properties of the alloys, have studied the so-called aluminum bronzes after various quenching and reheating treatments. Of these works, perhaps the most complete is that of Bouldoires, who studied changes of length, electrical conductivity, thermoelectric force, hardness and micro-structure on tempering quenched alloys containing 5 to 20 per cent of aluminum, although the work of Carpenter and Edwards,² Curry13 Greenwood,4 Braesco,5 Matsuda,67 Grard8 and others has added much to our knowledge of the changes occurring during tempering. The so-called acicular ß decomposes on tempering at temperatures between 350" C. and the eutectoid, giving rise to a Widmanstätten structure of a needles in a matrix of 6 or fine a + 6, associated with an increase in hardness and almost complete loss of ductility. Matsuda studied the eutectoid transformation by means of dilatation and electrical conductivity measurements during cooling at different rates. He found that on cooling at the rate of 10" C. per minute there was a decrease in electrical resistance and in length instead of the usual increase which occurred with slow rates of cooling. On tempering the rapidly cooled samples, the increase commenced at about 400" C. and at 520" C. the resistance and length had reached the equilibrium values. These peculiarities he accounted for as being due to a transitional phase ß' being formed, ß' having an electrical resistance and volume less than either ß or a + 6. Obinata9 published some electrical conductivity curves for copper-aluminum alloys showing a double break at the eutectoid temperature,

Jan 1, 1933

By F. Habashi

Conclusive evidence is given showing that the dissolution of gold in cyanide solution follows mainly the over-all equation A similar equation can also be written for the dissolution of silver. Theoretical derivation of the velocity equation for this reaction has been obtained, which describes quantitatively the experimental facts. The equation is as follows: where [CN-] and [O2] = the concentrations (in moles/ml) of cyanide and dissolved oxygen, respectively. DcN- and Do2 = the diffusion coefficients of cyanide and dissolved oxygen; 1.83 x 10-5 and 2.76 x 10-5 cm2 sec-1, respectively. A = the surface area of the metal in contact with the aqueous phase, in cm S = the thickness of the boundary layer; varies between 2 and 9 x 10-3 cm, depending on the speed and method of agitation. Rate being expressed in g. equiv. sec-1. INTRODUCTION During recent years a number of papers have been published on the kinetics of dissolution of gold and silver in cyanide solution.1,6 The authors agree that the rate of dissolution is diffusion-controlled, but disagree regarding the mechanism of the reaction. Some authors'-3 support the Bodlander equations: The apparently conflicting results, when critically reviewed, are concordant and lead to the conclusion that the proper equation for the dissolution reaction should be only Eq. 1. This conclusion is based on the following facts: 1) For every 2.2 equivalents of metal dissolved one mole O2 was consumed. 2) For every 1 equivalent of metal dissolved, 2 moles of cyanide were consumed.' 3) Hydrogen peroxide is formed during the dissolution of gold or silver, and for every 2.2 equivalents of metal dissolved, one mole H2O2 was produced.1,2 The fact that Kudryk and Kellogg4 did not detect H2O2 during the dissolution of gold should not throw doubt on the many affirmative reports of other investigators. Lund2 has shown that depending on the crystalline nature of the silver surface, (e.g. method of etching the sample) H2O2 may undergo catalytic decomposition heterogeneously according to: Further Kudryk and Kellogg4 carried out their experiments in the presence of 0.5% KC1 to achieve a greater electrolytic conductivity, and Matsudaira7 has shown that H2O2 is catalytically decomposed (homogeneously) in the presence of C1- ion in alkaline solution. 4) Experiments carried out by Boonstra8 and Lund2 showed that the dissolution of gold and silver respectively in KCN + H2O2 in the absence of oxygen was a slow process. Thus the reaction takes place to a minor extent only. Further kinetic studies showed that: 1) The rate of dissolution depends on the surface area of the metal in contact with the liquid phase, thus indicating that the process of dissolution is a heterogeneous process. 2) The rate of dissolution depends on the speed of stirring,5,6 thus indicating that the process is controlled by a physical phenomenon.

Jan 1, 1967

By B. H. Caudle, W. J. Bernard

Factors which influence the success or failure of a waterflood can seldom be determined in the laboratory. For this reason pilot waterfloods are initiated in a repreventative portion of the oil reservoir in question. For a pilot flood to predict quantitatively the recovery to be expected in a field-wide waterflood operation, the pilot area must behave as though it were confined (surrounded by similar areas). In this study, laboratory fluid-flow models were used to determine the simplest pilot pattern, for particular conditions of mobility ratio and initial gas saturation, that would behave as though it were confined. Pilot patterns studied ranged in complexity from a single inverted five-spot to a grouping of nine regular five-spots. Only the innermost producing well in each pattern was studied. Model results showed that the optimum number of wells in the pattern depends upon the oil-water mobility ratio and the expected oil-bank size. Unfavorable mobility ratios will, in general, require more wells in the pilot pattern than will favorable mobility ratios. Pilot patterns in reservoirs which contain a dispersed, flowable, free gas saturation will require fewer wells than for the under-saturated case. The single inverted five-spot pattern was found to be unsatisfactory for predicting behavior of fully developed waterfloods. In particular, it is possible that, in reservoirs which contain a flowable, dispersed gas phase, the oil bank will never be observed at the producers due to the large amounts of free gas which continue to be produced with the oil. INTRODUCTION One method which has been used to predict the performance of a waterflood is the pilot flood. The pilot waterflood is a flood which involves only a small cluster of the reservoir wells and is located in a small, representative portion of the reservoir. The object is that oil produced from the pilot can, in some way, be related to the oil recovery to be expected from a field-wide expansion of the waterflood. However, these field pilot waterfloods have often been unreliable in the prediction of oil recovery in a fully developed waterflood. This unreliability has also been demonstrated in several laboratory studies of pilot floods. Some of the investigators have shown that there are situations in which the pilot flood oil production is far too optimistic with respect to the oil recovery in the fully de- veloped flood. Others4-G have shown that the pilot results can also be pessimistic, especially if the pilot waterflood is initiated in an oil reservoir which has been depleted by primary recovery and is at very low pressure. The major reason for this unreliability of pilot water-floods is the migration of fluids into or out of the pilot area. By the well-known method of images, if straight lines can be drawn to represent vertical planes of symmetry in a porous medium which contains pressure sources and sinks (injectors and producers), then these lines are invariant streamlines, or lines across which there is no potential gradient, and therefore no flow. In an actual reservoir, these lines of symmetry can never be established exactly because of reservoir inhomogeneities and irregular reservoir boundaries. However, if the reservoir is relatively large and contains wells in repetitive patterns, these lines of symmetry are commonly assumed to exist for the pattern units sufficiently far removed from the reservoir boundary. Lines of symmetry for the five-spot injection pattern are shown in Fig. 1. Each five-spot unit in this figure can be considered confined with respect to flow across its boundary. In pilot floods this is not the case. The lines of symmetry for the pilot patterns investigated in this study are shown in Fig. 2. It is obvious that the fluid within these pilots is not confined and is therefore able to migrate into or out of the pilot area. Intuitively, one can see that, if more wells are added to the pilot, the innermost unit tends to behave more and more like the confined pattern. However, there is a practical limit to the number of wells which should be placed in the pilot. This limit is usually determined by economic factors. It was the purpose of this study to use laboratory fluid-flow models to determine which of the previously mentioned pilot patterns will force the innermost producing well to behave as it would in a fully developed waterflood. Since fluid migration is influenced by initial saturation conditions and the mobility ratio, these factors were included in the study. The ultimate objective of this study was to develop data which would allow the operator to choose a pilot pattern and operating conditions that will yield a production history which can be applied directly as an estimate of the performance of each production well of the fully developed waterflood. BASIS FOR THE STUDY The basic problem of field pilot floods is the migration of the reservoir fluids into or out of the pilot area. This problem has been the subject of previously reported model studies on pilot floods. These studies have been concerned mainly with the development of arbitrary "correction factors" to be applied to the simple, unconfined pilot systems such as the single five-spot. The correction factors were intended to adjust the production history of the un-

By C. L. T. Edwards

IN the preparation of this paper, the author has drawn upon experience with the operation of a blast furnace on 100 per cent scrap burden, which he believes was the first operation of its kind in the country. It is the writer's further belief that much of the controversy attending discussions of this subject may be obviated by the presentation of a group of facts that should be known by blast-furnace men and open-hearth men alike. The following question has been raised: "Is iron made with scrap in the blast-furnace charge as good iron as that made without scrap-made with straight ore?" This question may be answered in part by the fact that the open-hearth men of the Bethlehem Steel Co. who used pig iron from a blast furnace that operated on 100 per cent steel scrap found no difficulty in the processing of such iron other than that to be expected from the known analysis. OPERATION WITH 100 PER CENT STEEL SCRAP During World War I, there was accumulated at the Bethlehem plant of the Bethlehem Steel Co. some 22,000 tons of alloy-steel turnings and borings. This scrap material was highly corroded and, like alloy-steel turnings of that period, were as a drug on the market. There was also a small tonnage of scale, rich in valuable metal. If this scrap could be worked up into pig iron, it would become readily available for use in the open hearth. In order that the pig iron should contain the maximum percentage of nickel, permission was obtained from the Management to try a 100 per cent scrap operation. Accordingly, a blast furnace was swung over on July 25, 1919; the percentage of steel scrap increased more or less irregularly until July 29, when l00 per cent steel turnings were charged. Except for occasional charges of nickel scale as an "extra," the operation continued uninterruptedly until Aug. 27, when the furnace was swung back to the regular ore-ore and scrap-operation. During this period, the furnace production ranged from a low of 568.60 tons to a maximum of 766.07 tons. At the swing-over from i00 per cent scrap to the regular burden, the charge hung up rather severely. While the latter condition has nothing to do with the object of the paper, a brief discussion of the experience will appear later because of the interest it may have for blast-furnace operators. In Table I, results of the first and last days of the ore charge are shown, July 25 and July 29. The last column shows a summary for the period of maximum scrap charge. The furnace employed had a hearth 16 ft. 0 in., bosh 22 ft. 0 in., stock line 15 ft. 6 in., bell 11 ft. 6 in., batter ¾ in., bosh angle 73° 27' and a Baker-Neuman top, with gas-engine blowers. Analyses Range of Material Charged Gravel: Si02, 64.40 to .7o.54 per cent; A1203,3-52 to 4.58; CaO, 7.27 to 9.49; M90, 5.09 to 6.14; FeO, 1.67 to 3.34, ignition loss, 9.50 to 13.83.

Jan 1, 1941

By Charles S. Barrett, F. W. Steadman

DEFORMATION bands of surprising regularity are found in large-grained polycrystalline copper after cold-rolling (Fig. I). Individual bands frequently are large enough to permit a determination of their orientation by means of etch pits and an optical goniometer. Measurements have been made on 21 areas in seven different grains, and these, combined with X-ray studies of nine single crystals that had been cold-rolled after mounting in a polycrystal-line block, have contributed to a better understanding of the preferred orientations in rolled copper just as similar studies have for rolled iron' and brass.2.3 Particular attention was given to determining orientations that are stable during rolling and to the manner of fragmentation and rotation of unstable grains. The possible role of twinning was also carefully investigated. The texture of polycrystalline copper after cold-rolling is well established by the pole figures that have been plotted by Schmid and Staffelbach,4 Iweronowa and Schdanow,5 and Brick and Williamson,3 all of which are in substantial agreement. There has been some divergence in the list of individual "ideal" orientations that have been used to describe the texture by these observers and others,6 although the orientation (110) [112]-that is, (110) parallel to the rolling plane and [112] parallel to the rolling direction-is generally recognized as the most prominent orientation and (I12) [111] one of the lesser orientations. Other orientations have been given by some observers as (236) [533], (100) [001], and (I 10) [001]. The texture of copper has also been described as (135) [533].6.1 The sum of these orientations provides a reasonable approximation to the complete pole figure, but it does not follow that these specific orientations are necessarily of fundamental significance, for the choice of indices is arbitrary, within limits. Furthermore, a detailed investigation of the ideal orientations in cold-rolled iron discloses continuous ranges of equally favored positions rather than definite positions of high stability,1 and similarly Brick's observations in a single crystal of a brass2 suggest that all orientations in the range between (110) [113] and (110) [117] are about equally stable. MATERIALS AND METHODS The material used was vacuum-cast electrolytic copper kindly supplied by L. L. Wyman, of the General Electric Co.* Slices 1/2 in. thick and 2 1/2 in. square, cut from the ingot, were rolled with 50 per cent reduction per pass to final thicknesses between 0.02 and 0.04 in., and etched to develop cube-face etch pits suitable for goniometric work.8 The etch was light on some strips and deep in others.

Jan 1, 1942

By C. G. Brehm

The anthracite-producing region is in the northeastern section of Pennsylvania, and has an area of approximately 484 square miles. It is divided geographically into three separate fields, known as the Northern, Middle and Southern. The Northern field, with Wilkes-Barre approximately at its center, is a basin about 60 miles long and almost 6 miles wide at its greatest distance across. Generally speaking, it may be said that the coal measures in this field lie horizontally, or on slight pitches, and consist of from 11 to 19 veins of coal, varying in thickness from several inches to several feet. The intervening strata between veins may be composed of slate, clay, rock or shale, or a combination of several, and are sometimes very thin. This condition often causes a treacherous roof, therefore roof support and the attending hazard of mining are problems of concern. The Middle field is made up of a number of small basins of not very great depth, and the measures, which are in like number to those of the Northern field, are varying inclinations running from nearly flat to steep pitches. The Lower, or Southern field, is made up of basins of great depth, some being 4000 ft. deep, and its measures are mostly on very steep pitches. In certain sections this Southern field is being mined at an elevation of 1300 ft. below sea level, on a pitch ranging from 50' to practically vertical, and because of the tremendous pressure and the inherent gas in the seams, outbursts of coal frequently occur at the face, locally known as "bumps." These outbursts are accompanied by a rumbling noise, after which gas is usually found. This condition makes mining a difficult and extremely hazardous undertaking, and unusual skill is required on the part of the miner to drive and maintain openings necessary to the production of coal. Miners working in such seams on the heavy pitch must carry face batteries (Fig. 1) to afford proper protection while working at the face, because of the outbursts and free running coal. To drive haulageways or gangways in this field it is

Jan 1, 1940

By C. G. Brehm

The anthracite-producing region is in the northeastern section of Pennsylvania, and has an area of approximately 484 square miles. It is divided geographically into three separate fields, known as the Northern, Middle and Southern. The Northern field, with Wilkes-Barre approximately at its center, is a basin about 60 miles long and almost 6 miles wide at its greatest distance across. Generally speaking, it may be said that the coal measures in this field lie horizontally, or on slight pitches, and consist of from 11 to 19 veins of coal, varying in thickness from several inches to several feet. The intervening strata between veins may be composed of slate, clay, rock or shale, or a combination of several, and are sometimes very thin. This condition often causes a treacherous roof, therefore roof support and the attending hazard of mining are problems of concern. The Middle field is made up of a number of small basins of not very great depth, and the measures, which are in like number to those of the Northern field, are varying inclinations running from nearly flat to steep pitches. The Lower, or Southern field, is made up of basins of great depth, some being 4000 ft. deep, and its measures are mostly on very steep pitches. In certain sections this Southern field is being mined at an elevation of 1300 ft. below sea level, on a pitch ranging from 50' to practically vertical, and because of the tremendous pressure and the inherent gas in the seams, outbursts of coal frequently occur at the face, locally known as "bumps." These outbursts are accompanied by a rumbling noise, after which gas is usually found. This condition makes mining a difficult and extremely hazardous undertaking, and unusual skill is required on the part of the miner to drive and maintain openings necessary to the production of coal. Miners working in such seams on the heavy pitch must carry face batteries (Fig. 1) to afford proper protection while working at the face, because of the outbursts and free running coal. To drive haulageways or gangways in this field it is

Jan 1, 1940

By P. de Vitry, Oliver Bowles

THE conventional wire saw, introduced in the slate district of Pennsylvania by the Bureau of Mines in 1927, and used thereafter with remarkable success, consists of a three-strand steel cable having a diameter of 3/1 6 or 1/4 in. The equipment, methods used, and accomplishments have been described in previous reports.1-7 Similar wire saws have been used extensively in Europe, in quarries and in shaping blocks and slabs. During the period 1932-1937, competition in European marble quarries was keen, prices were declining, and orders were not abundant. When orders were received, there was generally an urgent call for speedy delivery. Because of the diversification of demands, it was impossible. to maintain in stock marbles of the color, size, and thickness called for,, therefore the material generally had to be fabricated after the order was received. The wire saw enabled stone mills to fill. such, orders promptly. With skillful handling, 7/8-in. slabs could be cut accurately and rapidly with this equipment. It was found, however, that, as the three-strand wire became worn, the cutting speed dropped rapidly and the cut became less accurate. To overcome these difficulties the junior author of this paper, after much experimentation, developed a new type of wire consisting of a single ribbon-shaped strand, twisted as shown in Fig. I. To ensure straight sawing, the twist of the ribbon is reversed from right to left and vice versa every 25 ft. The reversal of the [ ] twist is shown in Fig. 2. This is not a new feature; it has been used to advantage with the three-strand wire both in Europe and America for several years. However, some difficulties arise in splicing the three-strand reverse-twist wire, and the claim is made that cutting is less accurate as the wire becomes worn. To make an endless belt, the ends of the single-strand wire are brazed together with

Jan 1, 1941

By Henry J. Miller, Marcella Lindeman

DURING some experiments made by Henry J. Miller, partly in Germany and partly in the United States, in which it was found necessary to melt metals in quantities up to 60 kg. in a vacuum or under low pressures of hydrogen, molybdenum was tried as the resistor in the electric melting furnaces. Molybdenum ribbons 16 by 0.55 mm. and 18 by 0.45 mm. were used as resistors. The furnaces were of the type shown in Fig. 1. [ ] About the heating tube, Y, are wound parallel resistors of molybdenum ribbon from the water-cooled electrodes, E1, E2. The whole is within a copper container having outlets for the removal or introduction of gases and a window, W, for observation, the space about the heating tube and electrodes being filled with insulating material. The life of the molybdenum used as the resistor was found to depend very much on the manner of using it, its failure being due in some cases to thinning by evaporation or chemical reaction and in others to hardening, which prevented it from following the expansions and shrink¬ing of the heating tubing without cracking. As such failures are often rather expensive in commercial work, it was thought worth while to determine the causes. The factors influencing the behavior of molybdenum resistors used in this manner may be briefly stated as follows:

Jan 1, 1928