By E. W. Johnson, M. L. Hill

The dijfusiuity D was determined at 25° to 780°C- from hyd?-ogen evolution rates. Anomalous evolution from air-melted iron was att~zbztted to residual hydrogen, which is interpreted as a hydrogen compound that decomposes at a strongly temperature-(Ieperzdent rate above 500°C. Above 200°C, D = 0.0014 cm2sec-1 exp (-3200 cal per g atom/RT). Below, 200°C the diffusivity is anomalously low and represented by D = 0.12 cm2sec-l exp (-7820 cal per g atom/RT). It is postulated that at low temperatures the hydrogen in the metal is "trapped" with an energy 4.8 kcaL per g atom below- that of the interstitial hydrogen. 1 HE purpose of the present experimental study was to determine the diffusivity of hydrogen in a-Fe over an extended temperature range. As certain anomalies were encountered, attempts were made to understand the anomalies themselves. This research was in progress both before and after a determination of the diffusivity of hydrogen in nicke1.l The latter system was found to exhibit none of the anomalies of hydrogen in iron, and its description was far simpler. The experiments on nickel also

Jan 1, 1961

By I. L. Barker

ALTHOUGH valuable information has been pub-lished on the important problems of slag losses with which every copper metallurgist has to contend, a great deal of money is still being wasted in copper smelters all over the world, through metal being irretrievably lost in reverberatory slags. When smelting a relatively low-grade pyritic concentrate together with a proportion of direct-smelting oxi- dized ore, as is done in Oroya, slag volumes are of necessity high, and even a relatively clean slag, say of 0.5 pct Cu, means a loss of almost 4 pct of all the copper charged, or over $1,000,000 annually at present output and prices. While it is known that such losses can often be reduced by allowing the slag time to settle, with or without addition of a reducing agent such as coal or pyrite, the facilities for such treatment are not always available in a plant of old design working to capacity under severe space limitations. Nor is it easy under such conditions to run large scale tests which may endanger the smooth flow of production for considerable periods without yielding

Jan 1, 1958

By V. C. Rogers

ALTHOUGH surveying at mining properties is fundamentally the same regardless of the method of mining, at Climax, due to the nature of the ground, the policy of advance development work, and extremes in climatic conditions, surveying practice has had to be revised to meet the specialized conditions of this particular type of mining operation. The company's mine is one of the largest underground properties in the United States. It has proved ore reserves of 275,000,000 tons, 60,000,000 tons of which have been broken. To date, 109,000 ft. of development drifting have been driven, as well as 40,926 ft. of development raising, 10,000 ft. of ventilation drifting and raising, 16,000 ft. of exploration drifting, and 206,000 ft. of diamond drilling. Normal production varies between 1.2,000 and 15,000 tons daily. Development work proceeds at a rate of 11/2 tons developed for every ton milled and with a development of 18,000 to 20,000 tons per day, the following crew is required to take care of mine and surface engineering

Jan 1, 1946

By Yu A. Chernegov

Building up the USSR's economic strength was the result of all the achievements and successes of our economy. The Soviet Union was the first to begin planned guidance of the economy. The mining industry of the USSR, which holds the first place in the world output of mining production, has always been considered as the main raw materials basis of the country's economy. High and stable development rates are a feature of planned economic management, based on the social ownership of the means of production. During the past ten years from 1965 to 1875 the national income used for consumption and accumulation increased practically by 1.9 times. There has been no inflation, no unemployment in the Soviet Union for about forty years already. High and stable growth rates of the production of mining industries and that of the branches, which are their direct consumers are characterized by the data in table I. The achievements and successes of the economy's development are to a great extent determined by the three planning components, which are as follows:

Jan 1, 1977

By Robert Stefanko

Roof bolting in coal mines has progressed very rapidly in the last decade, and today this method of support is in general use. There are many theories concerning the functions of roof bolts, but the importance of beam building is indisputable. Proper tension in the bolts minimizes shearing along bedding planes and creates a thick, competent beam from individually weak layers. Bolting must be accomplished immediately upon exposure of the roof, and bolt tension must be maintained if roof failure is to be prevented. Seams are being mined today with roof bolt support where conventional timbering was not effective1. The widespread use of continuous mining equipment was made possible by roof bolts which permit long supported spans free of obstructions.2 Since adequate anchorage is the key to successful bolting, better methods for determining the efficiency of anchorage are continually being sought. Attempts have been made to measure bolt loads, thus assessing anchorage efficiency by employing sensing devices between the bolt head and roof. 3,4,5 None of the techniques appears to be very accurate, and all have at least one serious deficiency.

Jan 5, 1962

By JESSE L. MAURY

ONE OF the most hopeful features of the current depression is the discussion which it has en- gendered of ways and means to counteract similar recurrences in the future. 1t is widely recognized that fruitful attack will be directed toward the steady employment of labor, through which the purchasing power of this preponderant class in society will be maintained. S. A, Lewisohn's article' has presented the major factors to be considered; the physical suffering and mental torture endured by those who are deprived of income through no fault of their own, the direct economic losses' sustained in the degradation of 'great, numbers of our population and the disintegration of efficient working forces, and the prime responsibility of owners and managers.

Jan 1, 1931

By D. A. Elgillani, S. Atak, D. A. Rice, M. C. Fuerstenau, R. B. Bhappu

Quartz and feldspar cannot be floated with sulfonate at any pH; spodumene floats over a narrow acid pH range, while beryl responds moderately over a broad pH range. After wet-grinding in a steel mill, beryl, quartz, and spodumene float well with sulfonate below about pH 7, whereas the improvement in the response of feldspar is not so marked. A mechanism by which iron can be adsorbed on these minerals is presented. Also, the responses of leached, natural, and wet-ground beryl to amine, sulfonate, and oleate flotation are shown and related to the measured zero-points-of-charge of these materials. Earlier work with leached beryl showed that good flotation could be obtained with alkyl aryl sulfonate over a rather wide pH range using a Fagergren flotation cell.' When a similar response was observed with leached quartz, it was decided that unintentional activation was being obtained from the metallic components of the Fagergren cell. To obviate this difficulty, a microflotation cell was designed, and an experimental technique was devised. These have been described elsewhere. Experiments conducted with the small cell showed that leached quartz could not be floated at any pH with any sulfonate addition,3 which is in agreement with the observations of Kraeber and Boppel.4 Similarly, it was also found that leached beryl responded to sulfonate flotation only over a narrow pH range rather than the broad range reported earlier.1 This early work,1 however, revealed the important effect that wet-grinding in a steel mill has on the flotation response of certain silicates. That is, it was found that quartz and especially beryl floated well over an unusually wide pH range after wet-grinding in a steel mill. Microcline, however, floated poorly below pH 4, even though wet-ground under the same conditions. The work of Eigeles6 on adsorption of oleic acid on leached quartz and iron-contaminated quartz at constant pH is in agreement with these flotation data. Other research has shown that ferric iron, added as a salt to the system, functions as an activator in the narrow pH range in which Fe +++ iron hydrolyzes to its hydroxy complexes.3,5 These phenomena indicate that iron functions differently in flotation systems depending on its method of introduction. The object of this paper is to determine the mechanism by which iron is adsorbed on certain minerals, the mechanism of collector adsorption after iron abstraction, and the role that Fe++ and Fe+++ assume in the selective separation of these minerals. EXPERIMENTAL MATERIALS AND METHODS Sodium alkyl aryl sulfonate, mol wt 450,7 pure potassium oleate, and pure dodecylamine were used as collectors. All other chemicals were reagent grade in quality, i.e., n-amyl alcohol as frother; HC1, H2SO4, and KOH for pH adjustment; and ferric chloride as activator. Conductivity water, made by passing distilled water through an ion exchange column, was used in the experimental work. All minerals used in the investigation were hand-picked specimens. Sample Preparation: Each of the minerals was crushed through 8 mesh, and the product was divided into two groups, one to be ground dry and the other wet. Dry grinding was accomplished with an alumina mortar and pestle. The product was dry-screened to 48 x 150 mesh, cleaned magnetically, deslimed in conductivity water, and dried. Preparation of the samples by wet-grinding involved grinding a 200-g charge of the mineral (-8 mesh) at 60% solids with natural water in a mild steel rod mill for four minutes. This charge was then wet-screened immediately with natural water to 48 x 150 mesh, dried, and cleaned magnetically. Some experiments were also conducted with leached beryl and quartz. These products were prepared by leaching the sized sample (48 x 150 mesh) with concentrated HC1 with a percolation technique until no iron could be detected in the leach liquor. Following this step, the sample was rinsed with conductivity

Jan 1, 1967

By D. M. Schuster, E. Scala

The elastic effects occurring in the matrix of a composite reinforced by discontinuous fibers were studied by means of photoelastic techniques. A hirefringent plastic was employed as the matrix material with high-strength a Al2O3 whiskers as the reinforcing fibers. It was found that for whiskers aligned parallel to the tensile load direction: (I) Matrix reinforcement occurred along the length of the whisker to within about 5 diameters of the whisker tip for a length to diameter ratio, L/D, of 40. (2) Significant stress concentrations were created in regions immediately surrounding the tips; the fine as-formed tapered ends exhibited the minimum stress concentration whereas the square-ended whisker produced relatively high values, K r 2.5 for L/D = 40. (3) The axial and radial stress distributions could he determined quantitatively; the stress distribution at the whisker-matrix interface was in general agreement with theoretical calculations. (4) The highest source of stress concentration occurred at points of fracture in whiskers which had ruptured after incorporation into the composite. Whiskers aligned perpendicular to the load direction neither reinforced nor caused appreciahle stress concentrations in the matrix. ThE properties of composites have generally been formulated empirically on the basis of macroscopic tests. There are still many questions concerning the mechanical and chemical interactions occurring at the interface between the reinforcing fiber and its matrix. Continuously reinforced plastics and dispersion-hardened metals represent the two extremes of composite reinforcement. Whether artificially produced or formed in situ, the whisker composite falls between these two extremes and is an example of discontinuous fiber reinforcement. The effect of fiber shape, size, surface condition, and end configuration on the stress distribution in the matrix is important since the presence of stress concentrations, especially in any high-strength, thin-wall structure, could become the cause of catastrophic failure. DOW,' in his theoretical discussion of discontinuous fiber reinforcement, has pointed out that appreciable stress concentrations occur at the tips or ends of the reinforcing fibers. It is the purpose of this study to examine directly, by means of the photoelastic technique, the stresses which occur in the vicinity of a discontinuity or whisker tip and to measure qualitatively and quantitatively the effects of whisker geometry when embedded in a birefringent matrix material. The use of sapphire (a A1,O3) whiskers was decided upon as the reinforcing agent because of their high elastic modulus (E- 60 X 106 psi) and in some cases strengths in excess of one and a half million psi. Sapphire whiskers are of further practical interest since they retain large fractions of their strength up to temperatures approaching the melting point (3720oF).2 The whiskers were grown, by the vapor-phase reaction commonly employed,3 as part of this study to insure a physically uniform supply. Tensile and bend tests were performed to verify that the whiskers were of the expected ultra-high strength. The high-strength whiskers can be identified and selected from the combustion boats by surface perfection, shape, and size; otherwise, strength values can vary by a factor of ten or more. Macroscopic defects are quite common on the surface of large bladed whiskers and the principal experiments were conducted with hexagonal whiskers of about 0.002 in. diameter and lengths ranging from 0.1 to 0.4 in. Upon completion of these two phases of the experiment, several birefringent resins were evaluated. A plastic, developed by Zandman,4 which is supplied by the Budd Co., was found most suitable and was used as the matrix material for the whisker composite throughout the study. It has a sensitivity of 60.5 lb per in. order, calibrated in tension and cures without introducing residual stresses. Young's modulus for this matrix material is 430,000 psi in the fully cured condition. Since good wetting and bonding between the sapphire and the matrix material is essential to the interpretation of the results, a wettability test was performed. The contact angle was measured to be 168 deg where perfect wetting is defined as 180 deg; therefore, the Budd Plastic wets the sapphire

Jan 1, 1964

By W. F. Hosford, E. W. Kelley

Deformation studies have been conducted at room temperature on single crystals of magnesium and magnesium alloys with thorium and with lithium. Single crystals oriented to suppress shear on the easily activated basal slip systems were deformed by plane-strain compression. Compression along the C axis was accommodated by {1011} banding. Compression perpendicular to the unconstrained c axis activated {1012} twinning, and, after virtually complete twinning, deformation continued by {1011) banding in the twinned material. Compression perpendicular to the constrained c axis was accommodated by the simultaneous operation of (1012) twinning against the constraint and (1011 ) banding. Although this orientation was favorable for {1010)(1210) prism and {1011}(1~10) pyramidal slip, these modes were not observed in pure magnesium or in Mg-0.5 pct Th. However, {10i0)(1~10) prism slip was observed in crystals of Mg-4 pct Li during compression perpendicular to the constrained c axis. Fracture in all materials occurred parallel to (1124) or {l~il) depending on the orientation and composition of the specimen. THE mechanical behavior of the hcp metals is strongly anisotropic. Although several slip systems have been reported the slip is cpmmonly in the directions of closest packing, the (1210),' and this does not produce strains parallel to the c axis. Hence the inherent anisotropy. The deformation mode most easily activated in magnesium at room temperature is (0001)(1210)- basal slip. Also {1010}(1~10) prism slip and {1011)(1210) pyramidal slip have been reported, primarily at elevated temperatures.2"4 However, at room temperature the shear stresses to activate the prism and pyramidal modes are roughly a hundredfold greater than that required for basal slip.'j4 Thus prism and pyramidal slip may be expected only under special conditions of loading. Strains normal to the basal plane can be produced by twinning, however. Many twinning modes have been reported for magnesium,' with (1012) twinning the most common and relatively easy to activate. Magnesium can deform by (1012) twinning when stressed along the c axis jn tension, but not in compression. In contrast, (1011) twinning is activated by compression along the c axis and not by tension. In addition to primary twinning, secondary twinning or slip can occur within the reoriented material of primary twins.' In general at least five independent shear systems must be active to bring about an arbitrary shape change such as that in the individual grains of a deforming polycrystalline material.' Because basal slip can_ provide only two independent shear systems and (1012) twinning can only accommodate an extension of the c axis, other deformation modes must be active in magnesium for an arbitrary shape change to occur. The purpose of this investigation has therefore been to study the various deformation modes in magnesium at room temperature, with special emphasis on those modes that are less easily activated. The effect of the alloying elements, thorium and lithium, has also been investigated. In polycrystalline aggregates, unambiguous identification of deformation modes is extremely difficult and the direct evaluation of the resolved shear stresses to activate them is not feasible. On the other hand, uni-axial tension and compression experiments on single crystals may not activate some of the- deformation modes because basal slip and/or {1012) twinning cannot be suppressed in most orientations. However, it should be possible to activate all possible deformation modes using oriented single crystals and plane-strain compression. Identification of active deformation systems and evaluation of the resolved shear stresses required to activate them should be facilitated. Wonsiewicz and Backofen have recently completed an investigation of the plasticity of pure magnesium crystals at various temperatures utilizing plane-strain compression and selected crystal orientations. This technique has also been used in the present work. The seven orientations selected for study are indicated in Table I. Plane-strain compression along the c axis (orientations A and B) should activate some deformation mode _other than basal, prism, or pyramidal slip, or (1012) twinning. In orientations C and D, prism or pyramidal slip would be expected to take place. When the compressive load is applied perpendicular to an unconstrained c axis (orientations E and F) the three slip modes should be suppressed but not (10i2) twinning. In orientation G, basal slip should occur.

Jan 1, 1969

By David L. Holt

The contribution of grain boundary shear to total elongation, CS/E&apos;, has been measured in an Al-Zn eu-tectoid alloy that was quenched from above the invariant temperature, then annealed at 250° C to a grain size of&apos; 1.8 p. At 250°C, ks/E&apos; is low at both high and low strain rates, but reaches a maximum, estimated as 60 pct at an intermediate rate of 5 X 10 per rnin. Rate sensitivity, as measured by the index m = a log a/a log E&apos;, follows the same trend, and furthermore the maximum values of m and -cur at approximately the same strain rate. This result, combined with the metallographic observation that boundary migration enhances boundary shearing, is interpreted as supporting a previous suggestion that the high rate sensitivity characterizing super-plasticity is the result of combined boundary shearing and migration. It is suggested that the latter event relieves stress concentrations at triple points, and smoothes boundaries so that stress is governed largely by a viscous boundary shear. GrAIN boundary shear has been considered in relation to superplasticity in several recent papers.&apos; The problem has been to explain the high strain rate sensitivity of flow stress, and the variation of rate sensitivity with strain rate (E&apos;) and grain size (L). The requirements for superplasticity, small L and high T, suggest the reasonableness of an approach to high rate sensitivity involving grain boundary shear. Further support came from experiments on the A1-Cu eutectic alloy,&apos; where it was found that strain rate sensitivity of cast material annealed to produce an equiaxed, micron-size grain is always low; taking as an index of rate sensitivity m = a log a/a log <, m < 0.3. However, m in hot-worked alloy of comparable grain size can be as high as 0.7. In the cast and annealed material, each phase is a single crystal, the only boundaries are interphase boundaries, and it is, consequently, geometrically impossible for boundary shear to contribute to deformation in any major way. Other observations (for hot-worked material) were a-L at constant (low) strain rates and indications that the rate of recrystallization was enhanced as strain rate increased. As a result of this work, it was proposed that high rate sensitivity arises from a deformation mode of boundary shear associated with boundary migration. Migration serves to relieve stress concentrations at triple points, and smoothes boundaries so that they assume properties of fluid films. On the other hand, the low rate sensitivity observed at high and low strain rates reflects deformation of bulk material. Measurement of the variation of grain boundary shear with strain rate and m have not yet been made. Such measurements are important, especially in view of a proposal, differing in detail from the above, that high m arises merely from a transition between a grain boundary shear mode of deformation at low rates to a transgranular mode at high rates.2&apos;4 In the present work, the contribution of boundary shear to total deformation is measured and in addition metallographic observations are made on surfaces of deformed specimens to look at the interaction between boundary shear and migration. The Al-Zn eutectoid alloy was chosen for its homogeneous, fine-grained structure, which is obtained readily without hot-working. It has also been the subject of a previous phenom-enologically directed study. EXPERIMENTAL Material. Compression specimens, cross section 4 by + in., length \ in., were machined from a sand-cast ingot of composition 77.5 wt pct Zn, 22.5 wt pct Al. (The melt was prepared from 99.9 pct Zn and 99.99 pct Al.) After homogenization at 375°C for 50 hr, the specimens were quenched in brine and removed before the heat evolution that accompanies de -composition of the high-temperature phase.5&apos;6 The resulting microstructure, see Fig. l(a), was too fine for grain boundary sliding to be easily studied; coarser structures were obtained by annealing for various times at 2 50°C. Annealing was terminated by a brine quench. Final average intercept lengths between all grain boundaries (both interphase and those lying in a phase), L, were: 0.5 p [annealed for 15 min, Fig. (a)], 0.8, 1.1, and 1.8 p [Fig. l(b)l. Testing Procedure. An Instron machine was used for most of the compressive deformation. Tests were of two types: those in which crosshead velocity was changed in steps to measure m as a function of strain rate15 and tests at constant velocity to a fixed (engineering) strain of -0.2 (20 pct). Stress reached a steady-state value (a) which was plotted, on a logarithmic scale, against log strain rate (E&apos;). An alternate and equivalent evaluation of m was to take the slope of the log o vs log 6 curve. Time at temperature before testing was 15 min. Strain rates covered by the Instron (4 x lo-&apos; to 4 x 10&apos; per min) were insufficient; at a higher rate of 5 x lo2 per min a gas-operated testing machine was used, the gas driving a piston to compress the specimen at a controlled velocity.&apos; To obtain points on the log a vs log E&apos; curve at low rates, specimens were compressed by a dead weight. strain rate was an average value computed by dividing strain at the end of test by loading time. In some tests strain was measured at fractions of the loading time; creep rate was found to be reasonably constant.

Jan 1, 1969

By D. W. White

The kinetics of isothermal transformation of ß-to-u uranium have been studied over a broad temperature range in alloys containing from 0.3 to 4.0 atomic pct Cr. Two modes of transformation are indicated by the existence of two C-curves in the TTT diagram. The upper temperature mode is regarded as a nucleation and growth mechanism, whose rate is controlled by diffusion of chromium in the ß phase matrix. The lower temperature mode is martensitic in nature. The M, temperature increases with decreasing chromium content, suggesting that the two transformation processes become synonymous in unalloyed uranium. URANIUM metal undergoes two allotropic transformations in the solid state. The a phase, orthorhombic in crystal structure,&apos; is stable from room temperature up to about 665°C. The ß phase, characterized by a complex tetragonal structure,&apos; prevails from 665" to about 770°C. The y phase is body-centered-cubic3 and is the stable modification from 770°C up to the melting point (about 1130"). In uranium of reasonable purity, neither of the two high temperature phases can be retained by quenching. However, the addition of certain alloying elements to uranium makes it possible to retain either the y-uranium phase or the ß-uranium phase at room temperature. Chromium alloyed in small amounts with uranium will permit retention of the ß-uranium phase in a metastable state at room temperature upon quenching from a ß-phase temperature.&apos; From available information&apos; on the equilibrium phase diagram for the U-Cr alloy system (Fig. I), it is to be expected that, however sluggish in its rate, the ß phase in such alloys should decompose eutectoidally to a phase and elemental chromium. It was the aim of this investigation to measure the rate and study the nature of this decomposition as a function of temperature and of chromium content. The investigation was reported in classified literature about five years ago and has recently been declassified for publication. In the meantime, there have appeared the papers of Holden,5 Mott and Haines,".&apos; and Butcher and Rowe8 ealing with the metallography and the crystallography of the ß-to-a transformation in U-Cr alloys. These investigators have confirmed several of the phenomenological observations that will be described in the present paper and have examined in considerable detail certain aspects of the transformation and its mechanism. Although all of these investigations have concerned themselves experimentally with U-Cr alloys for the most part, an important consequence has been a clearer understanding of the nature of the ß-to-a transformation in uranium metal itself. Experimental Procedure This investigation dealt with a series of uranium alloys varying in chromium content from 0.3 to 4.0 atomic pct (0.066 to 0.90 weight pct). On five of the alloys, rates of isothermal transformation from the ß to the a phase were measured over a wide temperature range, leading to the development of TTT (time-temperature-transformation) diagrams. Transformation rates were measured over certain narrow temperature ranges on additional alloys. The alloys were prepared by vacuum melting and casting, using zircon or magnesia crucibles and graphite molds. Electrolytic chromium was used as the alloying addition, and the uranium was Mallin-ckrodt biscuit metal that had been vacuum remelted and cropped to remove many of the nonmetallic impurities that had floated to the top of the ingot. The ingots, 3/4 or 1 in. diam, were reduced in size by swaging. Alloys containing less than about 2 atomic pct Cr were swaged at 250° to 275°C, with initial and intermediate anneals at 550°C after every 75 pct reduction in area. Alloys with higher amounts of chromium were swaged at 550" to 600°C, although at the smaller sizes some of them were reduced by the procedure used on the more dilute alloys. Before use as test specimens, the swaged rods were annealed at 700" to 720°C for several hours, followed by slow furnace-cooling. The purpose of the anneal was to achieve the maximum amount of solution of the available chromium into the ß phase, as well as to remove extensive preferred orientation. The isothermal transformation rates were measured dilatometrically, using a quenching dilatometer and an experimental technique similar to those employed by Davenport and Bain in their original work on the transformation kinetics of austenite in

Jan 1, 1956

By Nathaniel Arbiter, Arthur F. Taggart

THE fact that the floatability of minerals with fatty-acid collectors changes as the pH of a pulp varies was utilized in the early days of flotation, when sulphuric acid was used with oleic acid to float sphalerite and galena from gangues which themselves float with fatty acids in alkaline pulps. Gaudin1 showed that this difference in floatability is a regular function of the extent of the change in pH. The present paper offers an explanation of the phenomenon, and on the basis thereof sets up recommendations for control of soap-flotation operations. EXPERIMENTAL Parallelism between floatability of a mineral in a given environment and its contact angle in that environment is so well established,&apos; and the contact angle is so readily and rapidly measurable, that contact angles have been used throughout the experimental work to indicate relative floatability. Experiments comprised contact-angle measurements on a number of representative minerals and metals, and a variety of subsidiary tests designed to check and to amplify the contact-angle indications. Contact-angle measurements were made by the method described in detail by del Giudice.3 Sequence of procedure for determination of the points of Fig. I was: 1. Polish specimen. Most specimens yielded zero contact angle after polishing; a few showed a slight "cling." Cling is characteristic of specimens that pit on polishing; it is due to a residue of organic contamination, originally on the particle surface, which persists in the pits. The cling did not change total contact angle after conditioning, and is not, therefore, additive in the upper part of the curves of Fig. I. It may have broadened the bases of the curves for the affected minerals slightly. 2. The specimen was next conditioned in soap solution for 5 minutes. 3. The conditioned particle was transferred, under conditions that precluded surface drying, to an aqueous solution of the pH desired and contact angle determined. 4. The particle was thereupon transferred, again without surface drying, to water. The confirmatory tests will be described at the places pertinent in the argument. DISCUSSION OF RESULTS Gaudin and Vincent4 have shown that contact angles with heptoic acid as a collector decrease for a given specimen when the concentration of collector present falls below a certain value. A similar reduction in angle occurs with collector-conditioned particles that are visibly slime-coated, and varies roughly with the extent of coating. Since in the last case the reduction in angle is certainly due to reduction in the proportion of total conditioned mineral surface presented to the bubble, the authors believe that the same condition prevails in the first case cited, and that similar reduction in angle and floatability will occur whenever starvation quantities of collector are present, whether

Jan 1, 1943

The Bougainville ore body was discovered in 1964 by a partnership of Conzinc Rio Tinto of Australia and New Broken Hill Consolidated Limited. The ore body is a porphyry copper in a fine-grained quartz diorite, which intrudes andesite volcanics and is located at an elevation of about 2, 000 ft in the Crown Prince Range of Bougainville in the Solomon Islands. Mineralization is predominantly chalcopyrite with some bornite and some gold and silver present. Rainfall in the area amounts to 200 in. (5. 08 m) per year. An active volcano is situated only 24 miles (38.4 km) from the mine, and all structures were designed to resist seismic shocks. An interesting and unique feature of the Bougainville operation was that the overburden was stripped with hydraulic monitors. Bougainville Copper, at 90,000 tpd, is the largest copper concentrator to be designed and constructed at one time; and besides the twin 54 in. by 74 in. Allis-Chalmers gyratories, it features seven 7 ft (2. 13 m) standard and fourteen 7 ft shorthead crushers, in addition to nine 18 ft diameter by 21 ft long (5. 5 m by 6. 4 m), 4250 hp, single -stage ball mills. During the design stage of the Bougainville primary crushing plant, several alternates were studied because the ore was expected to break with the production of large amounts of small-sized particles but with a minimum of fines. These alternates included two 54 in. by 74 in. gyratories with grizzlies, two 60 in. by 89 in. gyratories, and one 72 in. by 96 in. gyratory, the latter two installations without grizzlies. The two 54 in. units with grizzlies were finally selected as giving good reliability and the ability to handle the large amounts of small material in the feed. As originally installed, grizzly bars were set at 8 in. (203 mm); but, in an effort to perform more interparticle crushing in the primary and less rock-on-steel crushing in the secondaries and tertiaries, a test is underway (1976) to determine the effect of using 6 in. (152 mm) grizzly spacings (see write -up on Anaconda&apos;s crusher at Butte). The Bougainville ore is mined with 17 cu yd (13 cu m) shovels and hauled in 105, 170, and 210 st trucks to the crushers, which are equipped for two-side dumping. Up to 40% of the ore passes the grizzlies, which are equipped with splitters; and additional horizontal splitter bars are located directly above the spider caps. Because of the grizzlies, the crushers are supported by unique U-shaped enclosures, which are in turn supported by the end and center walls of the installation.

Jan 1, 1978

By John E. Conley

THE slate industry of the United States has shown a marked decline in value of products made annually since the peak year 1925, although there has been moderate improvement over the lean years 1932 to 1934. In 1940, the value of all slate products sold was approximately 5 ¾ million dollars for a total output of 473,450 short tons. The quantity sold was a little less and the value a great deal lower than the annual averages for the past two decades. Enormous quantities of waste materials result from the quarrying, splitting and milling of slate. Obviously, utilization of such waste material is desirable, not only from the viewpoint of economical operation but also for the purpose of conserving natural resources. One possible use is to produce expanded or puffed lightweight aggregate for use in concretes. Such concretes are strong enough for specific uses, and the advantage of lightness could be obtained in such structures as the walls and roofs of buildings, suspension-bridge roadways and various other applications where weight is a factor. Conceivably, these uses could consume an appreciable annual tonnage. USE OF WASTE SLATES FOR MAKING AGGREGATES The lightweight-aggregate industry has been discussed elsewhere4.5 and need not be covered in detail in this paper. The materials commonly utilized are naturally occurring aggregates such as volcanic cinder, tuff and pumice; by-product materials, such as ordinary cinders and air-cooled slags; and the specially manufactured products, including Haydite, Pottsco, Gravelite, Cel-seal, Superock and Waylite. Slates, however, have not been given the consideration they merit, especially in the United States. In the British Isles, some work has been done3 on certain Welsh slates by the Building Research Station to stimulate the use of these wastes. REQUIREMENTS FOR RAW MATERIALS As pointed out by Hughes,4 the light-weight-aggregate industry is segregated in regions adjacent to large cities in order to localize the market and avoid the necessity of long freight haulage. Waste slate from the deposits of eastern Pennsylvania, northern Maryland, and Virginia would meet the basic requirement of any low-priced structural raw material. One apparent advantage is attained when slate waste, normally discarded, is utilized in the manufacture of a by-product. Mining or quarrying costs usually have been assessed against the main product. Some additional grinding might be desirable, but this operation would be relatively cheap, as most slates grind easily. It is believed that virtually all slates, when properly heated, will expand to some degree. However, types that will expand from 3 to 7 times their original volume are preferred. Fig. I illustrates the expansion of a Pennsylvania slate. The cube originally

Jan 1, 1942

By John E. Conley

The slate industry of the United States has shown a marked decline in value of products made annually since the peak year 1925, although there has been moderate improvement over the lean years 1932 to 1934. In 1940, the value of all slate products sold was approximately 5¾ million dollars for a total output of 473,450 short tons. The quantity sold was a little less and the value a great deal lower than the annual averages for the past two decades. Enormous quantities of waste materials result from the quarrying, splitting and milling of slate. Obviously, utilization of such waste material is desirable, not only from the viewpoint of economical operation but also for the purpose of conserving natural resources. One possible use is to produce expanded or puffed lightweight aggregate for use in concretes. Such concretes are strong enough for specific uses, and the advantage of lightness could be obtained in such structures as the walls and roofs of buildings, suspension-bridge roadways and various other applications where weight is a factor. Conceivably, these uses could consume an appreciable annual tonnage. Use of Waste Slates for Making Aggregates The lightweight-aggregate industry has been discussed elsewhere4,5 and need not be covered in detail in this paper. The materials commonly utilized are naturally occurring aggregates such as volcanic cinder, tuff and pumice; by-product materials, such as ordinary cinders and air-cooled slags; and the specially manufactured products, including Haydite, Pottsco, Gravelite, Cel-seal, Superock and Waylite. Slates, however, have not been given the consideration they merit, especially in the United States. In the British Isles, some work has been done3 on certain Welsh slates by the Building Research Station to stimulate the use of these wastes. Requirements for Raw Materials As pointed out by Hughes,4 the lightweight-aggregate industry is segregated in regions adjacent to large cities in order to localize the market and avoid the necessity of long freight haulage. Waste slate from the deposits of eastern Pennsylvania, northern Maryland, and Virginia would meet the basic requirement of ally low-priced structural raw material. One apparent advantage is attained when slate waste, normally discarded, is utilized in the manufacture of a by-product. Mining or quarrying costs usually have been assessed against the main product. Some additional grinding might be desirable, but this operation would be relatively cheap, as most slates grind easily. It is believed that virtually all slates, when properly heated, will expand to some degree. However, types that will expand from 3 to 7 times their original volume are preferred. Fig, I illustratcs the expansion of a Pennsylvania slate. The cube originally

Jan 1, 1942

By John E. Conley

The slate industry of the United States has shown a marked decline in value of products made annually since the peak year 1925, although there has been moderate improvement over the lean years 1932 to 1934. In 1940, the value of all slate products sold was approximately 5¾ million dollars for a total output of 473,450 short tons. The quantity sold was a little less and the value a great deal lower than the annual averages for the past two decades. Enormous quantities of waste materials result from the quarrying, splitting and milling of slate. Obviously, utilization of such waste material is desirable, not only from the viewpoint of economical operation but also for the purpose of conserving natural resources. One possible use is to produce expanded or puffed lightweight aggregate for use in concretes. Such concretes are strong enough for specific uses, and the advantage of lightness could be obtained in such structures as the walls and roofs of buildings, suspension-bridge roadways and various other applications where weight is a factor. Conceivably, these uses could consume an appreciable annual tonnage. Use of Waste Slates for Making Aggregates The lightweight-aggregate industry has been discussed elsewhere4,5 and need not be covered in detail in this paper. The materials commonly utilized are naturally occurring aggregates such as volcanic cinder, tuff and pumice; by-product materials, such as ordinary cinders and air-cooled slags; and the specially manufactured products, including Haydite, Pottsco, Gravelite, Cel-seal, Superock and Waylite. Slates, however, have not been given the consideration they merit, especially in the United States. In the British Isles, some work has been done3 on certain Welsh slates by the Building Research Station to stimulate the use of these wastes. Requirements for Raw Materials As pointed out by Hughes,4 the lightweight-aggregate industry is segregated in regions adjacent to large cities in order to localize the market and avoid the necessity of long freight haulage. Waste slate from the deposits of eastern Pennsylvania, northern Maryland, and Virginia would meet the basic requirement of ally low-priced structural raw material. One apparent advantage is attained when slate waste, normally discarded, is utilized in the manufacture of a by-product. Mining or quarrying costs usually have been assessed against the main product. Some additional grinding might be desirable, but this operation would be relatively cheap, as most slates grind easily. It is believed that virtually all slates, when properly heated, will expand to some degree. However, types that will expand from 3 to 7 times their original volume are preferred. Fig, I illustratcs the expansion of a Pennsylvania slate. The cube originally

Jan 1, 1942

By Arthur F. Taggart, Nathaniel Arbiter

The fact that the floatability of minerals with fatty-acid collectors changes as the pH of a pulp varies was utilized in the early days of flotation, when sulphuric acid was used with oleic acid to float sphalerite and galena. from gangues which themselves float with fatty acids in alkaline pulps. Gaudin1 showed that this difference in floatability is a regular function of the extent of the change in pH. The present paper offers an explanation of the phenomenon, and on the basis thereof sets up recommendations for control of soap-flotation operations. Experimental Parallelism between floatability of a mineral in a given environment and its contact angle in that environment is so well established,2 and the contact angle is so readily and rapidly measurable, that contact angles have been used throughout the experimental work to indicate relative floatability. Experiments comprised contact-angle measurements on a number of representative minerals and metals, and a variety of subsidiary tests designed to check and to amplify the contact-angle indications. Contact-angle measurements were made by the method described in detail by del Giudice.3 Sequence of procedure for determination of the points of Fig. I was: I. Polish specimen. Most specimens yielded zero contact angle after polishing; a few showed a slight "cling." Cling is characteristic of specimens that pit on polishing; it is due to a residue of organic contamination, originally on the particle surface, which persists in the pits. The cling did not change total contact angle after conditioning, and is not, therefore, additive in the upper part of the curves of Fig. I. It may have broadened the bases of the curves for the affected minerals slightly. 2. The specimen was next conditioned in soap solution for 5 minutes. 3. The conditioned particle was transferred, under conditions that precluded surface drying, to an aqueous solution of the pH desired and contact angle determined. 4. The particle was thereupon transferred, again without surface drying, to water. The confirmatory tests will be described at the places pertinent in the argument. Discussion of Results Gaudin and Vincent4 have shown that contact angles with heptoic acid as a collector decrease for a given specimen when the concentration of collector present falls below a certain value. A similar reduction in angle occurs with collector-conditioned particles that are visibly slime-coated, and varies roughly with the extent of coating. Since in the last case the reduction in angle is certainly due to reduction in the proportion of total conditioned mineral surface presented to the bubble, the authors believe that the same condition prevails in the first case cited, and that similar reduction in angle and floatability will occur whenever starvation quantities of collector are present, whether by design or by reason of excessive consumption.

Jan 1, 1943

By J. Chipman, N. J. Grant, R. Rocca

D. E. Babcock (Republic Steel Corp., Youngstown, Ohio)—With reference to eqs 7 and 8, at what temperature do they apply John Chipman (authors&apos; reply)—That was 1600°C. Dr. Babcock—You have l x 10-4 as the component for the lime and 1 or 4x10-. Now, is it by dividing one into the other you get the 400? That is assuming equivalent activity on the part of oxygen, sulphur, and magnesia. Dr. Chipman—Yes, they are calculated for 1600. Now, the first one for CaO was calculated before we had a glimpse of Dr. Rosenqvist&apos;s paper." If you take his calculation you get 14,000 cal which is very good agreement, but our calculation would be superseded by Dr. Rosenqvist&apos;s new data. Dr. Babcock—The state you assume those to be in is the liquid state, as near as you can measure? Dr. Chipman—Naturally it is based on the solid CaS, but if you add the effect of fusion on both sides it just about balances out, so the ratio would be about the same. B. M. Larsen (U. S. Steel Co., Kearny, N. J.)—If we knew the activity of sulphur in the slag instead of merely the percentage, we might be able to find some conflicting factors that balance one another out, and find that the FeO or oxygen pressure effect is really present over the whole range. Dr. Chipman—I am fairly sure we would. The activity of sulphur in the slag and the activity of CaO in the slag, if we just knew those quantities, would enable us to save a lot of this computation and assumption and all the approximations we are doing now. Mr. Larsen—Two other points perhaps should be included: 1—an independent effect of manganese in helping the desulphurization; and 2—the number of mols of constituents or number of mols of ions or whatever there is in the slag could vary with these compositions in such a way that you get dilution effects. Dr. Chipman—You can figure all that in if you want to and it might improve the degree of approximation a little bit. Maybe enough to justify the labor of calculation, inaybe not, but we did not do it. L. S. Darken (U. S. Steel Co., Kearny, N. J.)—The authors have tackled a very complicated problem in trying to tie together in one picture the desulphurizing problem over the wide range of basicity and oxidation level from that of the open hearth to that of the blast furnace. At the present state of our knowledge of slags such an ambitious undertaking necessarily involves the adoption of numerous hypotheses. Their formulation (eq 11) for the higher FeO range

Jan 1, 1952

By E. F. Johnson, F. H. Brinkman, H. J. Welge, A. L. Hicks

A method is presented for predicting the character of gas or water displacement in a radial system, which can be either horizontal or inclined. The latter case would comprise cone-shaped or dome-shaped symmetry. The method conriders the one dimension of radial distance, taken parallel to the bedding planes. Approximate allowance can be made for segregation of the two fluids perpendicular to the bedding planes. A complete saturation history can be obtained in about a day&apos;s time with the use of a desk calculator. Results of an example calculation agree well with the performance of simulated gas drive in a large model representing a section of a cone. This pie-shaped, sand-packed model was 8-ft long and 4-in. thick. The method of solution is useful in handling other partial differential equations of first order and first degree. INTRODUCTION A new analytical method has been developed for predicting the performance of gas or water drive in a reservoir having radial or cone-shaped symmetry (see Fig. 1). In addition, this new development offers a general method of handling partial differential equations of first order and first degree. This work extends those methods developed previously&apos;- "or predicting the displacement of oil by gas or water in linear systems. The method of calculating oil recovery in a radial system involves two major parts. The first part is a calculation of the distribution of saturations at various times of depletion. The second part is the calculation of oil recovery and producing gas-oil or water-oil ratios through volumetric balance on the saturation distributions obtained in the first part. This second part differs only slightly in principle from similar calculations made with linear systems, for instance. The basic assumptions used in the calculations are as follows. 1. One-dimensional radial flow. An approach is explained later for approximating a second vertical dimension. (With- drawals of oil, and of the driving fluid after breakthrough, are assumed uniform around the periphery of the dome.) 2. Constant-volume fluid flow. Thus, in a gas drive there is no change in gas solubility, or in oil or gas volume due to viscous and gravity pressure drops. 3. Capillary forces are negligible. 4. Constant rate of injection. A program has been written for carrying out the calculations needed on a digital computer. However, a prediction can also be arrived at using a desk calculator; this latter method of work requires about a day&apos;s time for each prediction made. CALCULATION OF SATURATION DISTRIBUTION For definiteness, we describe the development of our method for the case of gas drive from the crest of the structure. The reader will note, however, that the method is just as applicable to an advancing radial water drive. The equation describing gas flow over an infinitesimal

By Nathaniel Arbiter, Arthur F. Taggart

The fact that the floatability of minerals with fatty-acid collectors changes as the pH of a pulp varies was utilized in the early days of flotation, when sulphuric acid was used with oleic acid to float sphalerite and galena. from gangues which themselves float with fatty acids in alkaline pulps. Gaudin1 showed that this difference in floatability is a regular function of the extent of the change in pH. The present paper offers an explanation of the phenomenon, and on the basis thereof sets up recommendations for control of soap-flotation operations. Experimental Parallelism between floatability of a mineral in a given environment and its contact angle in that environment is so well established,2 and the contact angle is so readily and rapidly measurable, that contact angles have been used throughout the experimental work to indicate relative floatability. Experiments comprised contact-angle measurements on a number of representative minerals and metals, and a variety of subsidiary tests designed to check and to amplify the contact-angle indications. Contact-angle measurements were made by the method described in detail by del Giudice.3 Sequence of procedure for determination of the points of Fig. I was: I. Polish specimen. Most specimens yielded zero contact angle after polishing; a few showed a slight "cling." Cling is characteristic of specimens that pit on polishing; it is due to a residue of organic contamination, originally on the particle surface, which persists in the pits. The cling did not change total contact angle after conditioning, and is not, therefore, additive in the upper part of the curves of Fig. I. It may have broadened the bases of the curves for the affected minerals slightly. 2. The specimen was next conditioned in soap solution for 5 minutes. 3. The conditioned particle was transferred, under conditions that precluded surface drying, to an aqueous solution of the pH desired and contact angle determined. 4. The particle was thereupon transferred, again without surface drying, to water. The confirmatory tests will be described at the places pertinent in the argument. Discussion of Results Gaudin and Vincent4 have shown that contact angles with heptoic acid as a collector decrease for a given specimen when the concentration of collector present falls below a certain value. A similar reduction in angle occurs with collector-conditioned particles that are visibly slime-coated, and varies roughly with the extent of coating. Since in the last case the reduction in angle is certainly due to reduction in the proportion of total conditioned mineral surface presented to the bubble, the authors believe that the same condition prevails in the first case cited, and that similar reduction in angle and floatability will occur whenever starvation quantities of collector are present, whether by design or by reason of excessive consumption.

Jan 1, 1943