By W. R. Atkins

The Negaunee mine is at the east end of the Marquette Range, in the city of Negaunee, on the Upper Peninsula of Michigan. Iron ore was first discovered on this property in 1883 by diamond drilling. A shaft was sunk soon afterward. and the mine has been worked continuously ever since. The total shipments from 1887 to Jan. I, 1945, were 20,417,587 long tons. The mine was taken over by the present operators, The Cleveland-Cliffs Iron Co., in 1903. During the past four years, 1941 to 1944 inclusive, the property has produced an average of nearly a million tons a year, and has employed more than 400 men. Geology The ore body at the Negaunee mine lies in a large syncline dipping about 15° to the west, the ore coming to ledge at the east end of the trough. The ore occurs in the Negaunee formation of the middle Huronian age, which consists of ferruginous cherts and slates through which intrusions of diorite have occurred. Although these intrusions of diorite have an important bearing on the formation of ore on the range, they are not important in this ore body. Some faulting has taken place along the diorite intrusions, or dikes as they are called locally, and also other faults are known to exist across the formation. These faults do not complicate either mining or development of the ore body. The footwall consists of jasper underlain with Siamo slate; the hanging wall is jasper and ferruginous chert. Fig. I shows a typical cross section of the ore body. The ore body is quite regular, about 120 ft. thick in the middle of the syncline and thinning out toward both sides of the fold. Its width ranges from 400 to 800 ft., the average being about 600 ft. The footwall is uniform in dip and strike, but irregular lenses of ore often extend 50 to 75 ft. up into the overlying jasper capping. Method of Mining Ore in the Negaunee mine has been mined by top slicing almost exclusively since 1903 This method of mining has been employed because it is especially adapted to the size and shape of the Negaunee ore body, and to the soft, sticky nature of the ore as well as the generally soft, broken jasper capping. Development The ore body has been developed from six different levels with intervals varying between loo and 125 ft. On the average, the dip causes a horizontal offset of 350 ft. per level, and under these circumstances it has been necessary to carry on considerable development in rock to make available the ore lying along the north and east footwalls. This is not as disadvantageous as might be supposed, because of reduced pressure and the accompanying saving in maintenance costs. The development of the

Jan 1, 1949

By T. H. Dunn, P. L. Menaul

This paper discusses the results of an investigation made to develop a method of combatting corrosion of subsurface oil-well equipment caused by brines containing hydrogen sulphide. Carbon monoxide, aldehydes, and certain cyanide compounds were found by laboratory tests to effectively inhibit corrosion of steel by sulphide brines. Experiments were made for one year in eight wells in West Texas fields using formaldehyde as an inhibitor. It was found that the inhibitor treatment successfully prevented the severe corrosion previously experienced in these wells, and effected important net savings in operating costs. Introduction Corrosion of oil-field equipment has long been a problem in areas producing sour crudes. These areas include the major fields of Arkansas, Western Kansas, West Texas and New Mexico. Corrosion in these fields is caused primarily by the chemical action of hydrogen sulphide in the presence of water and by electric currents entering the wells through flow lines. Hydrogen sulphide is noncorrosive to iron or steel in the absence of water but under the usual conditions prevailing in oil wells where more or less water is present, hydrogen sulphide is very corrosive. This type of corrosion occurs over the pH range below 9, which includes all natural oil-field brines. If air is present in addition to hydrogen sulphide and water, corrosion proceeds at an extremely rapid rate. It was reported several years ago that a string of oil-well tubing was literally dissolved within 50 days where an air lift was used on a well producing considerable water and hydrogen sulphide. Air is generally absent in wells producing sour crude. After hydrogen sulphide corrosion starts, it proceeds with increasing severity and its correction becomes progressively more difficult. This characteristic of sulphide corrosion has been attributed to the formation of galvanic couples between the iron and steel equipment on one hand and the products of corrosion on the other.' Severe corrosion of subsurface oil-well equipment leads to a multitude of troubles. In addition to destruction of costly equipment, producing sands often are damaged by flooding with water leaking through corroded casing; bad mechanical conditions may develop in a well due to obstructions caused by corroded equipment lost in the hole, or partly collapsed casing; pumping operations are interfered with, and severe emulsification problems may result from the homogenizing action of corroded balls and seats.% A typical case of severe corrosion caused by hydrogen sulphide was reported in Howard County, Texas, where it was necessary to pull tubing once a week to repair leaks after the tubing had been in use for only one year. On one well in this area a string of tubing was pulled 11 times in 8 months; 11 joints of tubing being replaced because of leaks. In Ector

Jan 1, 1946

By David B. Scott

When mining operations were first instituted in the mines of the Miami Copper Co., at Miami, Ariz., the relatively hard character of the ground in the western section of the property made it seem advisable to use a wide shrinkage stope and pillar system. The system as finally evolved was applied to the mining of 2,300,000 tons of ore by the use of stopes and pillars each 50 ft. in width. Development, mining and extraction of this reserve has been continuously in progress since 1910, and the final stages of extraction are now reached. A complete survey of all phases of this system can therefore be made. Modification in working methods was obviously necessary, and the system to be described is believed to be typical of the best features. Development The preliminary work had three main objectives: The opening of a haulage level, the construction of a drawing-off level, and the driving of sublevels for use in stoping. In addition to these, some extra sublevel drifting was necessary to determine exactly the boundaries of the orebody, the general outline having been determined by churn drilling. This development was based on the requirements of stopes 50 ft. wide, with pillars 50 ft. wide between each stope. The length of these units varied from 200 to 500 ft.. Haulage Level The tramming level was 50 ft. below the floor of the stopes, and the tramming lines were run parallel with the long axis of the stopes. These lines were also beneath the middle of the stopes and pillars. Each line therefore served one stope or one pillar, this arrangement making it possible to load along an entire stope without switching or uncoupling. This advantage is apparent principally during the process of stoping when rapid drawing of excess broken ore is desirable. Furthermore, the arrangement of the drawing-off level chutes at 25-ft. intervals, as shown

Jan 1, 1917

By W. S. Keyes

The State of Nevada, known par excellence as " the Silver State," occupies the major portion of the wide plateau, or so-called Great Basin, lying between the Sierra Nevada range on the west and the Wahsatch range of the Rocky Mountains on the east. It extends from the 114th degree to the 120th degree of longitude, west of Greenwich. It is limited, on the north, by the 42d degree of latitude, and on the extreme south by the 35th degree of latitude. Its general shape is that of an irregular parallelogram, from which the lower or southwestern portion has been cut off by a diagonal southeasterly line; the missing portion forms a part of the State of California on the west. The Great Basin is made up of a succession of low hills, or minor mountain ranges, running very nearly north and south, with long valleys between them. All of these mountains are more or less metalliferous. On the westcrn rim, marking the eastern flank or foothills of the Sierra, we find granites, porphyries, and propylites. Here we note the great Comstock lode, with its free-milling gold and silver ores, and still further south the once prominent and the now reviving gold and silver-bearing districts of Esmeralda County, Nevada, and of Morro County, California. Next, at some distance to the east, we find the mining districts at and near Unionville, in Humboldt County. Still further to the east we find the Battle Mountain copper-silver district, north from the railroad, and southerly therefrom the Austin or Reese Ever, Belmont, and other districts. Still further east and north of the railroad, we find the Tuscarora, a new district of very

Jan 1, 1879

By H. E. Stamm, H. H. Spain, R. C. Rumble

This paper presents a reservoir analyzer study of the performance of the Woodbine formation in the East Texas basin. The study was made possible by the compilation of available information on the configuration. thickness and the pressure drawdown of the formation. The investigation was made of the pressure variations in the basin incident to production from the several Woodbine reservoirs. In addition, the apparent compressibility of Woodbine water was evaluated so that the potential water yield of the formation could be determined. The distribution of permeability of the Woodbine sand and the interference between producing areas were also investigated. In conjunction with this basic study of the Woodbine sand, an acceptable match of the production-pressure relationship in the East Texas Field was established on the analyzer. INTRODUCTION When production is taken from a reservoir contiguous to an aquifer, the resultant pressure gradient causes a water influx into the reservoir. For some years it has been the practice to predict the performance of water drive reservoirs with mathematical equations that relate the water influx into reservoirs to their pressure behavior. A rigorous solution of these equations is quite complex: hence, the conventional method requires the simplifying assumptions that the formation have constant thickness, permeability and poiosity, and that it have a known and regular shape. It is necessary to use performance records of the reservoir in question to determine the equation constants that make the results of the mathematical calculations duplicate the reservoir history. The values of the constants determined in this manner sometimes differ so greatly from theoretical or measured values that the constants appear unreasonable. The equation constants comprise such factors as the thickness, porosity and permeability of the formation, and the viscosity and compressibility of water. Usually the thickness, porosity and viscosity are known within a reasonable degree of certainty. whereas the formation permeability and the water compressibility are known with considerably less certainty. Hence. permeability and compressibility values are arbitrarily selected that will make the mathematical equations duplicate the reservoir behavior. In many reservoir studies the value of the compressibility of water thus selected has exceeded the reported value by a factor of from severalfold to manyfold. Whether this excessive value results from the inadequacy of the mathematical approach to take into account the shape irregularities and the heterogeneities of the aquifer, or is due to some type of formation compaction and decrease of porosity has not been established. Because of the significance of the potential water yield of formations with reference not only to oil reservoirs but to water resources as well, it is very important that a representative value for the effective water compressibility be determined. One of the best known examples of a field for which it has been possible in the past to predict the future reservoir pressure is the East Texas Field. Until about 1943 it was possible by means of mathematical equations to duplicate past pressure behavior and to predict with a high degree of accuracy the reservoir pressure of the field. Since 1943, however, the calculated pressures have deviated progressively from the observed pressures to such a degree that in recent years, it has

Jan 1, 1951

By H. H. Spain, R. C. Rumble, H. E. Stamm

This paper presents a reservoir analyzer study of the performance of the Woodbine formation in the East Texas basin. The study was made possible by the compilation of available information on the configuration. thickness and the pressure drawdown of the formation. The investigation was made of the pressure variations in the basin incident to production from the several Woodbine reservoirs. In addition, the apparent compressibility of Woodbine water was evaluated so that the potential water yield of the formation could be determined. The distribution of permeability of the Woodbine sand and the interference between producing areas were also investigated. In conjunction with this basic study of the Woodbine sand, an acceptable match of the production-pressure relationship in the East Texas Field was established on the analyzer. INTRODUCTION When production is taken from a reservoir contiguous to an aquifer, the resultant pressure gradient causes a water influx into the reservoir. For some years it has been the practice to predict the performance of water drive reservoirs with mathematical equations that relate the water influx into reservoirs to their pressure behavior. A rigorous solution of these equations is quite complex: hence, the conventional method requires the simplifying assumptions that the formation have constant thickness, permeability and poiosity, and that it have a known and regular shape. It is necessary to use performance records of the reservoir in question to determine the equation constants that make the results of the mathematical calculations duplicate the reservoir history. The values of the constants determined in this manner sometimes differ so greatly from theoretical or measured values that the constants appear unreasonable. The equation constants comprise such factors as the thickness, porosity and permeability of the formation, and the viscosity and compressibility of water. Usually the thickness, porosity and viscosity are known within a reasonable degree of certainty. whereas the formation permeability and the water compressibility are known with considerably less certainty. Hence. permeability and compressibility values are arbitrarily selected that will make the mathematical equations duplicate the reservoir behavior. In many reservoir studies the value of the compressibility of water thus selected has exceeded the reported value by a factor of from severalfold to manyfold. Whether this excessive value results from the inadequacy of the mathematical approach to take into account the shape irregularities and the heterogeneities of the aquifer, or is due to some type of formation compaction and decrease of porosity has not been established. Because of the significance of the potential water yield of formations with reference not only to oil reservoirs but to water resources as well, it is very important that a representative value for the effective water compressibility be determined. One of the best known examples of a field for which it has been possible in the past to predict the future reservoir pressure is the East Texas Field. Until about 1943 it was possible by means of mathematical equations to duplicate past pressure behavior and to predict with a high degree of accuracy the reservoir pressure of the field. Since 1943, however, the calculated pressures have deviated progressively from the observed pressures to such a degree that in recent years, it has

Jan 1, 1951

By Bailey Willis

It is proposed to present some of the results of observation of the geologists of the Appalachian division during the past seven years, and of experimental study during the past three years, on the subject of structural geology in the Appalachian Province. The article must be brief, even at the risk of obscurity; but a more complete and fully illustrated paper will appear in the Thirteenth Annual Report of the United States Geological Survey. Certain Facts. The following facts are first to be taken account of: From the Cambrian age to the Carboniferous there existed a conti nent stretching southeast from the present range of the Blue Ridge, covering what is now eastern Pennsylvania, New Jersey, eastern Vir ginia, North and South Carolina and eastern Georgia, with some un known part of the present Atlantic ocean-bed. Northwest from this continent lay a sea, reaching to the west and north of the Mississippi. Sedimentary deposits derived from the land accumulated with or ganic remains, in the sea; the greater part fell in a narrow zone along the shore, the remainder spread in a comparatively thin sheet over the bottom of the Mediterranean of North America. The resulting strata measure, near Mauch Chunk, Pa., 30,000 feet; over much of Pennsylvania, 20,000 to 25,000 feet; over eastern Tennessee, Georgia and Alabama, but 10,000 to 15,000 feet. The stratified mass, considered with reference to its broad physical char acters, consists of three members: A base of shale and sandstone ; a middle of limestone, 2500 to 6000 feet thick—a stratum probably not equalled in the world for uniformity of character and massive ness; and a top of shale and sandstone, 5000 to 23,000 feet thick. This mass has been folded. In a zone 900 miles long and 50 to 125 miles wide, the strata exhibit such attitudes and relations as could result only from a force of compression acting from north west or from southeast, or from both directions. Our problem is :

Jan 1, 1893

By E. S. Grumell

THE correct sampling of coal and coke is becoming important to an ever increasing number of producers and consumers. This, therefore, may be an opportune moment to examine where we stand with regard to existing and proposed methods. In this paper an attempt will be made to review, as briefly as possible, some of the considerable amount of painstaking research which has been done in the last 10 years, and which has unquestionably led to a much better understanding of the subject. In so doing we shall try, on the one hand, to make clear where substantial progress has been made, and on the other hand, to draw attention to points that require further investigation. The paper is divided into sections in order to emphasize the major divisions of the subject; further, in order to retain this emphasis, detailed consideration of some of the points has been relegated to appendixes. No attempt has been made to give a complete survey of the literature, as this has already been done by L. A. Bushell.2 The following abbrevia-tions will be used: A.E., average error; P.E., probable error; S.W.R., size-weight ratio; B.S.I., British Standards Institution.

Jan 1, 1939

INTRODUCTION This chapter summarizes characteristics of porphyry copper deposits within the Cordilleran orogen east of the Coast Range plutonic complex of the Yukon and British Columbia and south to the Columbia River plateau and the Idaho batholith. Porphyry copper deposits in this area reflect a geologic environment different from that found for mineralized intrusions elsewhere in the Cordilleran orogen, both to the south in the United States and Mexico and to the west in Alaska. A section on the Tertiary Cascade porphyry copper province is included herein. The Cascade province is considered separately because its deposits display a unique mineralogy and age of mineralization. That portion of the Cordilleran orogen described in this chapter is shown in Fig. 32, with the Cascades shown in Fig. 39 (see p. 114). The regional geology of this area has been described by Monger, et al. (1972), Hollister (1974), Wolfhard and Ney (1974), Field, et al. (1974), and Stacey (1974). Each offer slightly differing views on the post-Mississippian evolution of the geology in this porphyry copper province. The descriptive geology in this chapter has benefited from many discussions with J. E. Armstrong and J. W. H. Monger. Two separate petrologic models have been used popularly to categorize porphyry copper deposits in this area, a diorite and a quartz monzonite model. The diorite model, which involves a mineralized quartz-free pluton, has also been called the alkalic type (CZM Special Volume 15, 1976, and Soregaroli, 1975) and the syenite suite (Sutherland Brown, et al., 1971). The quartz monzonite model has also been named the calcalkalic type (CZM Special Volume 15, 1976) and includes mineralized quartz-bearing plutons compositionally ranging from quartz diorite to granite, with the igneous phase closest to ore in time and space commonly being quartz monzonite.

Jan 1, 1978

Readers of recent Bulletins have doubtless observed that the problem of improving both material and moral condition of employees is receiving close attention from influential members of the Institute. This will lend interest to certain developments and investigations that have been reported elsewhere.

Jan 5, 1918

By R. W. Waterfill

MANY existing ore deposits of valuable metals have been worked out in their upper surface levels and the continued productivity of these mines is dependent on their extension to greater depths in the earth. The maximum depths at present reached are about 6000 to 8000 ft. below the surface, with no evidence of an impoverished ore vein. These mines are widely distributed; some of the best known are in South Africa, Brazil, India and in the western sections of the United States. Among the factors which increase the difficulty of working these mines at increasing depths are hoisting, rock pressure and temperature. The manner and effectiveness with which these problems arc met will, no doubt, determine in a large measure the ultimate depths to which any mine can be profitably worked. The most critical of these three factors at present is the increase in temperature with depth. The high temperature and humidity in many of these mines at present are severely detrimental to the health of the workers and greatly hamper their efficiency. Some have almost reached a condition in which the human system cannot survive. The problems involved in the cooling and ventilation of mines have all been ably analyzed and presented in previous articles. For this reason, only a résumé of conditions affecting the cooling and conditioning of deep and hot mines will be given in this paper before attention is directed to possible methods of improving atmospheric conditions in the working levels. Physiological Effects of Temperature, Humidity and Air Motion Many data on the physiological effects of different atmospheric conditions on the human system have been compiled and published through the combined efforts of the American Society of Heating and Ventilating Engineers, the U. S. Bureau of Mines and U. S. Public Health Service. These data were not primarily developed around the conditions existing in deep mines, but the upper temperature limits of the investigations extend into, and are applicable to, mine atmospheric conditions. While the exact values of the standard comfort conditions, established for persons of such habits as those employed in detecting the different degrees of comfort, might not produce identical effects upon persons inured to

Jan 1, 1929

By M. Yokoi, K. Yoshida, T. Ishihara

The solubility of aluminum in cryolite melts has been determined by measuring the weight loss of aluminum submerged in melts contained in closed silicon nitride crucibles. The solubility in pure cryolite has also been checked with radioactive isotopes. The solubility decreases with increasing A1203 concentration, decreasing temperature, and decreasing cryolite ratio. The change of aluminum solubility in pure cryolite with the activity controlled by using Al-Ag and A2-Cu alloys supported the assumption that aluminum would dissolve in the form of monovalent ions according to the reaction 2AI + A1' —3 A1'. DURING the electrolytic production of aluminum, the electrodeposited metal redissolves in the bath in some form and is subsequently oxidized back to the former ionic state. This dissolution is believed to cause a decrease in current efficiency. Reported data on the solubility of aluminum in cryolite melts are scattered. The mechanism of the dissolution has not yet been determined, although certain tentative interpretations have been proposed. Many previous studies were performed under different test conditions. Studies were performed in open Systems and closed systems,'o and some were apparently not given sufficient time to Saturate." The solubility can be determined either analytically or gravimetrically. The analytical determination involves measurement of hydrogen gas evolved when frozen cryolite bath saturated with aluminum is treated with sodium hydroxide or hydrochloric acid. The gravimetric determination, adopted by many investigators,'-37'3>14 involves measurement of weight loss of the metal after equilibration with a known amount of salt. It appears that the former technique yields much smaller values of solubility than the latter technique. This large difference in results strongly suggests that the dissolved metal in the cryolite melt is no longer in the metallic state. In the present study, the solubility was determined by the gravimetric technique at various activities of aluminum using A1-Ag and Al-Cu alloys. An attempt was also made to determine the ionic (or atomic) state of the dissolved metal from the solubility data. 1) EXPERIMENTAL Apparatus. Preliminary tests demonstrated that silicon nitride was suitable as a container material since it is compatible to both the fluoride melts and molten aluminum. Crucibles were made from silicon powder nitrided with Nz gas at 1600°C. The good compatibility between crucible and melts is due to the near perfect nitrogenation of silicon. Only small amounts of silicon were found in the aluminum metal after the experiments. The crucible dimensions were 90 mm inside height, 38 mm ID, 105 mm outside height, and 50 mm OD. Close-fitting lids made of silicon nitride were also prepared. The crucible was placed in a close-fitting graphite crucible heated by a vertical Kanthal furnace, Fig. l. The lid and crucible are fastened tightly together by the condensation of vaporized bath in the narrow gap between them. The temperature was measured in the wall of the graphite crucible and controlled within * 5°C. The temperature difference between the measuring point and the interior of the melts was initially determined. Materials. The materials used were: Greenland cryolite (impurities CaF,, 0.5 pct; AlzO3, 0.2 pct; high-purity aluminum metal (purity 99.99 pct); A1203 and AlF, (provided by Nippon Light Metal Co., Ltd); reagent-grade NaF and CaF2; and 99.9+ pct Ag and Cu. Powdered reagents were carefully dried before use. A1-Ag and A1-Cu alloys were prepared before the experiments; their composition was checked by analysis

Jan 1, 1969

By K. K. Kershner, W. A. Calhoun, C. W. Funk

Future resources of aluminum may require the utilization of low grade ores to provide a more permanent protection for the nation. Aluminum minerals such as cloy, shale, and high iron laterites may become important sources. An evaluation of reserves is given. New laboratory results are reported on the Vereinigte desilication process. THIS report on future resources of aluminum metal emphasizes the necessity for investigating utilization of low grade potential ores to provide more permanent protection for the nation. Partial or complete interruption of the importation of high grade aluminum ores must be given consideration. Ultimately, aluminum minerals such as clay, shale, and high iron laterites may become the principal sources of aluminum. The development of extractive processes for treating these low grade materials is a step in long-range national preparedness that should receive more attention. In formulating such processes, the application of beneficiation methods for the purpose of classifying the several types of minerals before subjecting each type to the more expensive extractive procedures should be considered, and a careful survey of the basic factors of power sources, transportation facilities, and sources of raw material should be made. Domestic Bauxite Resources Of the domestic supply of current, treatable-grade bauxite, 95 pct comes from Arkansas. The present reserve of Arkansas bauxite suitable for metal production, including abrasive-grade, Bayer-grade, and modified Bayer-grade ores, is 34,000,000 tons. The total reserve of bauxite of all grades is approximately 75,000,000 tons. Reserves are estimated on a mined and dried basis. Data available to the Bureau of Mines in 1948 to 1949 were used in preparing Table I, which shows a breakdown by grades of bauxite for about a half of the reserves of the state. The modified Bayer ore, 10,555,500 long dry tons, is based on a cutoff of 8 to 15 pct silica. The sub- marginal 10,074,700 long dry tons is assumed to contain more than 40 pct gibbsite, more than 15 pct silica, and less than 32 pct available alumina. A considerable amount of this low grade material was consumed in 1949 and 1950. Additional tonnages of bauxitic and kaolinitic clays are indicated by the Bureau of Mines drilling project.' Applying a 50 pct factor to arrive at long tons mined and dried, the results of this project are approximately 31,500,000 tons kaolinitic clay at +35 pct Al²O3 and 11,800,000 tons kaolinitic clay at 20 to 35 pct A1,0,. Total reserves of kaolinitic clays are probably quite extensive—several times the reserves shown in the Bureau's work. Total reserves of bauxitic and high iron clays from the drilling program and previously established figures are 63,980,000 tons. The mineral dressing methods,' the lime-sinter process, he lime-sinter modification of the Pederson process," the lime-soda sinter process,"-' and the Alcoa combination processa. have been described in the literature and will not be elaborated upon here. The less familiar Vereinigte Aluminium-Werke process used by the Germans during World War 11 may require some amplification. It was used to bene-ficiate boehmite ores containing 12 to 18 pct silica for a feed to the European Bayer process. Ore was

Jan 1, 1952

By P. H. Delano, Will H. Coghill, G. D. Coe

Data concerning the actual net energy required for pulverizing coal are lacking from the literature on coal pulverization. Power data given in the literature concern gross power and frequently include the power expended on the air blast or product-conveyor system, as well as power lost through friction in the pulverizer itself. Consequently, such data supply no information regarding the net energy consumed in pulverizing or the relative grinding resistance of various coals. In the study of coal pulverizing much work has been done on what is known as " grindability-index numbers," but grind-ability tests have seldom considered the energy input (that is, the "cause" part of the system "cause and effect"). There are many records of the effect, but even these have questionable value because the "grindability" tests did not make a pull'erized product by a method comparabLe with- commercial pulverizers. In many of the tests, only a selected part of the coal was ground, and the remainder continued to be an unknown factor. Furthermore, none of the grindability tests provide the balanced circulating load common to all modern commercial pulverizing. In order to obtain better understanding of the fundamental principles of coal pulvcrizing, the Bureau of Mines is investigating the "cause" phase; that is, the net energy input or net power excluding friction between the moving parts of the machine. As a first step in the investigation,it was necessary to design and construct a laboratory machine in which no friction-loss corrections are involved, which could grind and finish a minus-¾-inch feed, which could be emptied rapidly and completely, which could operate with a continuous feed and finish in an air separator; and, most essential of all, which would be equipped with a measuring device for recording only that portion of the total power consumed in actual pulverizing, hereafter referred to as "net energy input" or "net horsepower-hours." The channel-roller pulverizer hereinafter described is believed to meet these requirements. History oF the Machine The, work started when Ralph W. smith, engineer, St. Genevieve Lime Co., St. Cenevieve, Mo., was appointed one of the consultants of the Bureau of Mines, United States Department of the Interior, in cooperation with the University of Alabama, to develop a machine for testing the abrasiveness of coal. Smith had already developed a machine for testing the abrasive-ness of dentifrices,1 and it was thought the same principles might be applied to coal, Smith's machine had a revolving disk with an annular channel in which the sample was placed. Riding in the channel was a small block or runner of selected soft metal held

Jan 1, 1942

By Will H. Coghill, P. H. Delano, G. D. Coe

Data concerning the actual net energy required for pulverizing coal are lacking from the literature on coal pulverization. Power data given in the literature concern gross power and frequently include the power expended on the air blast or product-conveyor system, as well as power lost through friction in the pulverizer itself. Consequently, such data supply no information regarding the net energy consumed in pulverizing or the relative grinding resistance of various coals. In the study of coal pulverizing much work has been done on what is known as " grindability-index numbers," but grind-ability tests have seldom considered the energy input (that is, the "cause" part of the system "cause and effect"). There are many records of the effect, but even these have questionable value because the "grindability" tests did not make a pull'erized product by a method comparabLe with- commercial pulverizers. In many of the tests, only a selected part of the coal was ground, and the remainder continued to be an unknown factor. Furthermore, none of the grindability tests provide the balanced circulating load common to all modern commercial pulverizing. In order to obtain better understanding of the fundamental principles of coal pulvcrizing, the Bureau of Mines is investigating the "cause" phase; that is, the net energy input or net power excluding friction between the moving parts of the machine. As a first step in the investigation,it was necessary to design and construct a laboratory machine in which no friction-loss corrections are involved, which could grind and finish a minus-¾-inch feed, which could be emptied rapidly and completely, which could operate with a continuous feed and finish in an air separator; and, most essential of all, which would be equipped with a measuring device for recording only that portion of the total power consumed in actual pulverizing, hereafter referred to as "net energy input" or "net horsepower-hours." The channel-roller pulverizer hereinafter described is believed to meet these requirements. History oF the Machine The, work started when Ralph W. smith, engineer, St. Genevieve Lime Co., St. Cenevieve, Mo., was appointed one of the consultants of the Bureau of Mines, United States Department of the Interior, in cooperation with the University of Alabama, to develop a machine for testing the abrasiveness of coal. Smith had already developed a machine for testing the abrasive-ness of dentifrices,1 and it was thought the same principles might be applied to coal, Smith's machine had a revolving disk with an annular channel in which the sample was placed. Riding in the channel was a small block or runner of selected soft metal held

Jan 1, 1942

By Eugene McAuliffe

SINCE 1917, the bituminous coal industry has surged, violently at times, across the nation's social, industrial and economic foreground. To-day a silent, yet more active, force is working within the industry, and the movement now taking place, if allowed to continue, will cause serious consequences when coal is again wanted at the rate of 550,000,000 tons annually instead of at the rate of 400,000,000 tons, the apparent requirement for 1921. I refer to the shift of tonnage from the highly unionized fields of Pennsylvania, Ohio, Indiana and Illinois to the non-union fields of Pennsylvania, West Virginia, Alabama and certain western states, and to the so-called union fields in Kentucky and Colorado, on which the union saddle rests lightly. This movement, in the absence of the usual winter transportation shortage, is taking place rapidly and will be accentuated if, as is probable, work is suspended in the union mines on March 31 next. This drift of tonnage has been made possible by the unit wage reductions in the non-union fields and by the modification of the so-called conditions that have been saddled on all mines wherever the United Mine Workers have gained a foothold; these changes permitted the first reduction in mine cost, which made possible the securance of contracts; better running time assisted in making further reductions, and the transfer of ton-nage served to increase the unit cost in the field from which it was transferred. This situation not only opposes the highly unionized operation but brings about a transfer of traffic from the roads serving such mines to those that serve in a primary or secondary manner the more favored localities. The net result is evidenced in (a) the migration of union labor to the non-union mines; (b) the deteriora-tion and decadence of union properties; (c) the neces-sary curtailment in the purchase of new equipment and in the maintenance of existing equipment and track facilities on the part of the carriers serving the union fields. This, in turn, when business is restored to normal or to the point above normal that invariably follows an adverse swing of-the business pendulum, will cause (d) a shortage of coal and coal transportation facilities; (e) an era of coal speculative debauchery with exorbitant prices and serious deflection in the matter of quality; (f) a period of labor unrest followed by de-mands for increased wage rates supplemented by a marked loss in individual efficiency, with, resultant strikes, business unrest, and the pressure of new eco-nomic theories. In 1918, the labor status with respect to relative tonnage produced was approximately as follows: pro-duced in highly organized fields, 62 per cent.; produced in partly organized fields, 21 per cent.; produced in unorganized fields, 17 per cent. During the strike of November and December, 1919, the mines that remained at work attained 35 per cento of the nominal production of soft coal, a situation made possible by the migration of union labor to non-union mines and the concentration of the nation's coal trans-portation facilities on the rails of the carriers serving the non-union fields. The history of the efforts made by the carriers to untangle the car scrambling which took place during this period and which sent the self clearing battleship type of car into western territory where it could not be readily unloaded, and the western gondola type of car to New England and the seaboard, is yet painfully recalled. -This confusion proved a serious factor in the coal car shortage that continued throughout the following year. We are drifting toward a similar situation now, propelled by economic forces rather than by a sudden strike.

Jan 1, 1922

By M. Hansen, C. C. Wang

THE 6 phase of the Cu-Sn system (Cu,Sn, = 32.53 pct Sn) was considered to be stable down to room temperature until Owen and Iball showed by X-ray analysis that it undergoes a eutectoid decomposition into the a and e phases at a temperature near 300°C. Their findings have been confirmed by other investigators,2-5 a11 of whom used X-ray diffraction studies of powdered specimens. The transformation temperature has been reported by various authors as lying between 300" and 380°C. To our knowledge, no microscopic evidence of the eutectoid reaction has been published, as yet. It was in connection with other work that longtime annealings at 300°C were conducted with alloys containing 22, 32.6, and 35 pct Sn (nominal compositions) prepared from electrolytic copper and electrolytic tin and cast in a small iron mold. The specimens were first annealed at 700°C for 5½ hr and quenched from 400 °C after cooling to, and annealing at, that temperature for 9½ hr. After this treatment the sample with 22 pct Sn was cold worked for 15 pct reduction in thickness; the 32.6 and 35 pct alloys were too brittle to be cold worked. The final anneal at 300°C was done in a sealed pyrex glass bulb for 63 days. Fig. 1 represents the microstructure of the annealed alloy with 22 pct Sn. It shows primary a solid-solution crystals in a matrix of the (a + 8)-eutectoid formed at 520 °C. The a crystals contain 8 inclusions which precipitated from a due to the decrease in the solubility of tin in copper with fall in temperature. The decomposition of the 8 phase into a (light) and E (dark) can clearly be seen in some areas of the (a + 8)-eutectoid matrix. However, the decomposition is far from being completed, even after the long-time anneal used. Figs. 2 and 3 depict the microstructures of the annealed 32.6 pct alloy, which was intended to consist entirely of 6 phase. Due to some loss in copper on melting, the composition is slightly higher in tin. Accordingly, the sample after quenching from 400 "C consisted of grains of the 8 phase with the e phase arranged along the grain boundaries and as a Wid-manstatten precipitate within the 6 grains. After an annealing time of 63 days, the eutectoid decomposition, 6 + a + e, is still in its early, initial state. The pearlitic type of eutectoid is nucleated at the c crystals, preferably those surrounding the grain boundaries of the 8 phase. The appearance of the (a + €)-eutectoid in the 35 pct Sn alloy was very similar to that shown in Figs. 2 and 3. Again, the eutectoid decomposition nucleated at the 6 phase and proceeded from there into the 8 areas. As is evident from Fig. 2, the rate of decomposition of the 6 phase at 300°C is extremely sluggish: In the representative area shown only about 5 pct of the 8 phase has undergone the eutectoid trans- formation after annealing for 63 days. On the other hand, Owen and Williams2 have reported that X-ray photographs of powdered samples with between 17.5 and 34 pct Sn did not show 8 lines after annealing for only five to seven days at 300°C. This is in accordance with the fact that the rate of reaction in powdered samples is higher than in massive specimens, as a result of the excess free energy of the powder (due to its greater surface area). The authors wish to express their thanks to C. A. Johnson for preparation of the micrographs.

Jan 1, 1952

By Kehsin Kuo

DIE steel with 1.47 pct C, 0.42 pct Mn, and 8.22 pct W contains Fe,C and WC in the annealed state and WC embedded in a martensitic matrix in the hardened state (quenched from 800°C). The presence of a large amount of undissolved angular WC carbide particles makes this steel extremely wear-resistant. However, the WC carbide begins to dissolve in the austenite when the heating temperature is raised above 1000°C, but this solution process is still not complete at 1250°C although partial melting has already taken place at the austenite grain boundaries. At 1325 C, this steel contains austenite and liquid metal but no WC carbide, Fig. 1. On quenching into brine, the liquid metal solidifies into a constituent which etches differently from the austenite-martensite matrix. This constituent appears lighter than the matrix at the 1250°C stage when etched with 2 pct nital but darker in Fig. 1 when etched with Murakami's reagent. Such a constituent has also been found in burnt tungsten high speed steels. This constituent has been isolated from the matrix by anodic dissolution in a 5 pct HC1 electrolyte and was found by the X-ray powder method to be iso-morphous with &manganese, Table I. The agreement in line intensity between these two phases indicates that there is no ordering in this new phase. The calculated cube edge of this phase is 6.395A, somewhat larger than that of ß-manganese (6.30A). Besides this phase, the anodic residue also contains free carbon from the matrix and amorphous WO,, although the X-ray powder pattern of the residue shows the presence of only this phase. This makes it impossible to determine directly the composition of this phase from the residue. Attempts to prepare an alloy containing only this phase have hitherto been fruitless. The following experiments serve to show that this phase can only be obtained by drastic quenching from the liquid state and that its tungsten and carbon contents must be lower than those in the Fe,W,C carbide. On air cooling from 1325oC, the liquid metal solidifies into a eutectic consisting of austenite and the Fe3W3C carbide. The nature of this dark-etching Fe3W3C has also been ascertained by X-rays. This eutectic becomes coarser on furnace cooling. The solidification of a specimen cooled for 5 min from 1325" to 1200°C and water quenched is still not complete and the fine eutectic is formed during the quenching. Since this new phase can be replaced by a eutectic of austenite and the Fe,W,C carbide, its composition must lie somewhere between the latter two phases. The special features of this phase are: 1—it can only form directly from the liquid state by drastic quenching and 2—it is a ternary phase of iron, tungsten, and carbon. The ß-manganese structure of this phase is also interesting. In the Periodic Table, iron and tungsten lie on opposite sides of manganese; a certain combination of these two elements, in the presence of carbon, may have average properties similar to those of manganese. It has already been established that the x phase, a ternary one of iron, chromium, and molybdenum, has the a-manganese structure."' A similar phase has also been found in the ternary system Fe-Cr-W and in the following binary systems: Re-Cb, Re-Ta, Re-Mo, and Re-W.6 References 1 G. D. Preston: Philosovhical Magazine 11928) 5. 7th Series, p. 1207. - K. W. Andres: Nature (1949) 164, p. 1015. 35. G. McMullin, S. F. Reiter, and D. G. Eberling: Trans. ASM 11954) 46, p. 799. ' J. S. Kasuer: Acta Metallurgica (19541 2, p. 456. • H. J. Goldschmidt: Trans. ASM (19541 46, p. 807. P. Greenfield and P. A. Beck: Private communication.

Jan 1, 1957

By D. B. Smith, John Chipman

THIS investigation was undertaken as a prerequisite to the study of sulphur activities in the liquid system Fe-Cu-Ni, a continuation of the work of Sherman, Elvander, and Chipman,¹ using the same equipment and the same experimental technique. Temperature measurements are made with a disappearing filament optical pyrometer, sighting through a prism onto the surface of the melt which is heated by induction. To obtain true temperatures by this means, a calibration is necessary, since, in the absence of true black-body conditions, the observed temperature is always lower than the true temperature. This calibration is actually an emissivity correction, since the emissivity is a function of both temperature and melt composition. The original furnace was used with a deeper metal bath to provide sufficient depth of immersion for the thermocouple which was inserted through the sampling hole. The atmosphere was a 50-50 mixture or argon and hydrogen passing through the furnace at a rate of 1000 ml per min, and preheated by means of a molybdenum resistance coil. It was assumed that the rapid gas flow effectively eliminated any error which might have resulted from the presence of metallic vapor. The charge in each case consisted of about 300 g of metal, contained in a high purity, dense alumina crucible. At each melt composition, readings of the optical pyrometer and of a thermocouple immersed in the molten metal were taken simultaneously. Calibration curves of optical vs. true temperature were then made for each melt composition investigated. Thermocouples were made of 0.010 in. platinum and platinum-10 pct rhodium. They were checked against the melting point of chemically pure copper. Silica protection tubes with an outer diameter of approximately 1/8 in. were used. The depth of immersion of the tip in the molten metal was approximately 1 14 in. The life of these small thermocouples was relatively short, varying from approximately 1 min at 1550°C to 10 min or longer at 1300°C. Melts containing iron corroded the protection tubes more than those without iron present. Measurements taken while heating checked those taken while cooling, indicating the absence of a temperature gradient between the molten metal and the thermocouple. Results The temperature range of the. measurements on copper-free metals extended from the melting point to 1600°C. For copper the upper limit was 1380°C, and the data were extrapolated linearly for comparison with observations on the other metals and alloys at 1535°C. Examples of typical calibration curves for various melt compositions are shown in Fig. 1. These curves, besides providing a calibration system for the given experimental conditions, also give a basis for the calculation of true emissivities at the effective wavelength of the pyrometer, 0.65 micron. The starting point of the calculations is the value of the emissivity of iron at its melting point. Taking the melting point of electrolytic iron under hydrogen as 1535°C, and using the corresponding emissivity value of 0.43, as determined by Dastur and Gokcen,² the emissivities can be determined as functions of composition (and temperature, if desired). The relationship used is the Wien equation: ln(Ea)=C2/?(1/T1-1/Ta where E is the emissivity; a, the transmissivity of the optical system; C,, the fundamental constant, 14,380 micron-degrees; A, the wave length of light used (0.65 micron); Tt, the true temperature, OK; and T., the apparent temperature, OK. At the melting point of iron the observed temperature was 1358"; this gives 0.62 for the transmissivity, which compares with 0.65 in the similar system used by Dastur and Gokcen. The emissivities of all the compositions investigated were determined at 1535°C, after obtaining from each calibration curve the corresponding temperature. These results

Jan 1, 1953

By Claus G. Goetzel

Pressing of powdered metal parts is best done in the direction of the shortest extension of the piece, to avoid too great a loss of pressing force through internal iriction. As long as curved surfaces, re-cessej, or offsets occur only parallel to this shortest axis of pressure, no special difficulties arise: the cross sections, perpendicular to the pressure, do not vary, nor does the shape of the parts change during compression except for a gradually reduced thickness (Fig. IA). The problem becomes more dificult, however, when the curved surfaces or recesses are perpendicular to the shortest axis of the part (Fig. IB) Two processes for molding uniformly dense parts with complicated shapes from powdered metals are described in detail in this paper. Both can be employed successfully by those trained in the art. The first refers to curved parts; the second is especially adapted to parts having one or more recesses or steps. Both methods, as set forth here, are applied under the condition that presents the more difficult problem. For clarity, before description of the two practical methods, the variable factors in molding powdered metal parts will be reviewed, then an idealized procedure will be considered briefly. Variable Factors in Molding Powdered Metal Parts Compression Ratio Compression ratio is defined as the proportion of the final relative density of the compact to the apparent density of the powder. For iron powder of an apparent density of 3.0, for example, a compression ratio of 2 1/2:1 would be required to produce a compressed compact of 7.5 density; whereas for another iron powder having an apparent density of only 1.5, a compression ratio of 5:1 would be required to produce the same density. The lower the powder's apparent density, the greater must be the compression ratio for pressing compacts of high density.

Jan 1, 1946