By M. Mirzazadeh

Air cooled crackable and conventional forged steel specimens were tested under reversed push-pull conditions to examine the effect of shot-peening on their high cycle fatigue behaviour (-106 cycles). The steels were tested in the normalized as well as shot-peened conditions. The results showed that shot-peening smooth specimens had little effect on the fatigue limit of the air cooled forged steels and the detrimental effect of the rougher peened surface was not apparent. Microhardness profiles indicated that the shot peening produced a gradient of compressive residual stresses that was greater than that of the loading stresses, suppressing the anticipated beneficial effect on fatigue life. Crack initiation was more likely to occur below the surface. The results indicate that the surface roughness was not a significant factor in controlling the fatigue lives, since they were essentially the same for the non shot-peened and shot-peened steels.

Jan 1, 2010

By M. Pawlik, E. Arinaitwe, V. Ferrera

A series of flocculation tests were performed on dilute quartz suspensions with the use of five polyacrylamide-based flocculants of similar molecular weights but of different degrees of anionicity. The tests were performed as a function of ionic strength and pH. The macromolecular conformation of flocculants in solution was assessed through intrinsic viscosity measurements under the same physicochemical conditions as those of the flocculation tests. It was generally found that the flocculating efficiency of the polyacrylamides correlated with their ability to coil or stretch in solution. Polyacrylamides with the degrees of anionicity on the order of 10-18% showed the highest flocculating efficiency in terms of the settling rates of the flocculated solids and the residual turbidity of the resulting supernatant. At the same time, these most effective flocculants were also found to exhibit the greatest tendency to coil and stretch in solution. This result suggests that the flocculating power of a flocculant is determined not only by its ability to adsorb onto (and bridge) fine particles but also on its ability to conform to the size of the resulting floes.

Jan 1, 2009

By Steve Scott

Outline of Talk Seafloor Massive Sulfides (SMS) and Seafloor Sedimentary Sulfides (SSS) Ocean mining of SMS (Nautilus Minerals) Environmental issues Summary

May 1, 2013

By G. M. Card, K. D. Card, B. V. Sanford

The Canadian Shield and its extensions are traversed by an orthogonal system of north-west and northeast trending arch-style uplifts. These basement arches were formed by repeated vertical movements along pre-existing structures during compressional and extensional tectonism connected with events in surrounding Proterozoic and Phanerozoic orogens and ocean basins. The arches in?uenced patterns of sedimentation and tectonism in the intervening epicratonic basins andmarginal platforms throughout the Proterozoic and Phanerozoic. Movements on the arch structuresalso triggered minor magmatism and controlled the location and timing of alkalic rock-carbonatite, kimberlite, and related intrusions in the Canadian Shield, the Western Canada Sedimentary Basin, and West Greenland.

Jan 1, 1997

By G. M. Card, K. D. Card, B. V. Sanford

Abstract-The Canadian Shield and its extensions are traversed by an orthogonal system of northwest and northeast trending arch-style uplifts. These basement arches were formed by repeated vertical movements along pre-existing structures during compressional and extensional tectonism connected with events in surrounding Proterozoic and Phanerozoic orogens and ocean basins. The arches influenced patterns of sedimentation and tectonism in the intervening epicratonic basins and marginal platforms throughout the Proterozoic and Phanerozoic. Movements on the arch structures also triggered minor magmatism and controlled the location and timing of alkalic rock-carbonatite, kimberlite, and related intrusions in the Canadian Shield, the Western Canada Sedimentary Basin, and West Greenland.

Jan 1, 1997

By Michael Cullen

The Quinsam Coal Mine is in the process of extracting a panel beneath the mine access road. To prevent damage to the road, and adjacent powerline, it was necessary to establish a ?protection zone? within which the extent of mining would be limited. The protection zone is analogous to the setback limit. For economic reasons it was desirable to make the protective zone as small as possible, and with the greatest extraction ratio possible. The size of the protective zone was established by determining the angle of critical deformation using the numerical model FLAC, coupled with field data on subsidence from the Mine. The angle of critical deformation (defined as the angle, measured from the vertical, at which intolerable damage is sustained by a structure) was determined to be between 0 and 5 degrees. The allowable extraction ratio in the protection zone was established using the ARMPS method of pillar design coupled with field data on pillar stability from the Mine. Excavations spans to prevent caving were determined by historical experience and field data on span stability from the Mine, coupled with numerical modeling. The minimum pillar size was determined to be 7.5m. The maximum pillar height was established at 2.5m. The maximum allowable excavation span was determined to be 8.5m. With these criteria, extraction ratios between 54 and 73% (measured in plan view) were determined to be appropriate for the protection zone.

May 1, 2001

By W. Dietzel

Fracture mechanics based techniques are used to gain insight into the phenomenon of stress corrosion cracking (SCC) and to develop guidance for avoiding or controlling SCC. From constant extension rate experiments under rising load or rising displacement conditions the susceptibility of high strength steels, aluminum, magnesium and titanium alloys to SCC and hydrogen embrittlement can be assessed. Such tests on pre-cracked specimens are also well suited for studying the mechanisms leading to SCC by employing appropriate models for the degradation of metallic materials which take into account the uptake of atomic hydrogen from the corrosive environment. Measurements of crack growth resistance curves using the crack tip opening displacement as fracture parameter can be compared with simulated R-curves obtained from modeling of the mechanism of hydrogen embrittlement. The materials investigated are a high strength steel and a magnesium alloy both exposed to environmental conditions which fostered the uptake of hydrogen.

Jan 1, 2010

By G. S. Hume

Dr. K. A. Clark: No one will doubt the statement of fact that, during drilling operations through the bituminous sand beds in the Mildred-Ruth Lakes area, the core-barrel was found to contain bitumen with minor amounts of sand instead of bituminous sand. But many will doubt the interpretation of this fact as meaning that beds of bitumen occur interstratified with the bituminous sand beds. They will prefer to hold faith in the laws of physics, which deny that sand will float on oil or that fluid under pressure will not flow away through a permeable medium, until it is proved that the appearance of the oil in the core-barrel was not due to circumstances surrounding the drilling of the bituminous sand beds. The implication of the interpretation that sand is floating on oil is clear and it is unacceptable. Bituminous sand is unconsolidated sand more' or less saturated with a viscous oil. It is as difficult to conceive of bituminous sand lying on top of a body of the viscous oil as it is to conceive of unconsolidated sand more or less saturated with water lying on top of a body of water. The only difference between the two concepts is that the oil is viscous whereas the water is fluid. Oil-soaked sand placed on viscous oil would, when released, sink through the oil slowly, whereas water-soaked sand would sink through the water quickly.

Jan 1, 1947

By L. Szecowka, M. Poskart, Siwka M. . J.

Oxides of nitrogen, created during combustion, are the most hazardous components of atmospheric pollution. However, it is possible to limit the negative influence of hazardous components on the natural environment. An experimental appartatus was built to determine the influence of the following "primary methods" on the reduction in concentration of NOx: air staging, reburning and flue gas recirculation. The influence of the simultaneous usage of the primary methods on reduction in NOx emissions was also examined. A significant increase in the efficiency of NOx reduction was achieved in two cases.

Jan 1, 2004

By A. J. Paul Laprairie

"ADVANCE planning of mining methods, from the first development openings to stope layout and pillar recovery, has long been accepted as a normal method of operating a mine. Recently, mine managers have become increasingly aware that advance planning of cost and accounting controls can also be considered a normal method of operation. The use of such controls is wide-spread in manufacturing industries. In mining, the gold mines of South Africa have pioneered, with marked success, in this field and have been closely associated with most of the research and field work in accounting control. Canadian mine managers are also beginning to realize the advantages of using planned costs. The control procedures which subsequently have been introduced at various mines have come to be known by such names as ""Responsibility Costing"" or Budgetary Control"".Budgetary control, the term used in this paper, is based on the concept of decentralized authority with centralized control. ;The control is achieved by measuring results against yardsticks which are in the form of budgets or standards. Bud-gets are made for the future activities of each possible operation as planned by the department head, and attention is directed to variations from this plan. Furthermore, the control process charges to each operation only those costs which are incurred directly for that operation, and which can be controlled by the person in charge. Thus, budgetary control relates results to the officials responsible for those results. Expenditures are analyzed according to the organizational structure of the mine and the people who run it, and not according to production processes."

Jan 1, 1960

By E. C. Goodhue, R. D. Coleman, I. E. Puddington, A. F. Sirianni

Iron ore samples containing apatite are fractionated to acceptable products by spherical agglomeration methods. The phosphorus is upgraded by a factor of 10 at an elevated pH. High-grade iron products are obtained in good yields from the tailings in a second step of the operation. The grade of the phosphorus separated appears to reach a maximum at about pH = 10; recovery of iron decreases below about pH = 4. Both the recovery and grade of iron are found to be reduced sharply above about pH = 8.

Jan 1, 1968

By Osamu Inoue, Takashi Yamashita, Takashi Ikemoto

The expansion project in Naoshima smelter and refinery to meet enhancing recycling business of E-scrap was successfully completed in 2016 to have a capacity of 110,000 tpa of E-scrap treatment. Increasing treatment of E-scrap has raised the Ni content of copper anode to 4000 ppm on average, which is double the level of 10 years ago, and to 6000 ppm or more occasionally. The tank house has refined such copper anode to copper cathode with starter sheets. Since most Ni in Copper anode dissolves in copper electrolyte, the Ni content of the electrolyte has increased to 27 g/L and more. Ni accumulated in the electrolyte has increased power consumption during the electrolytic refining of copper, although cathode quality has been controlled satisfactory so far. In order to ensure sustainable operation while growing E- scrap business, the NiSO4 process has been expanded recently so as to recover Ni in the electrolyte more and the pressurized-leaching technology will be introduced to the slime leaching process so as to enhance the capacity of slime treatment and to improve Ni recovery in the near future. INTRODUCTION In recent years, the treatment amount of E-scrap at Naoshima smelter and refinery has increased according to the growth of its recycling business as shown in Figure 1, while impurities from E-scrap have concentrated in copper anode as well. Especially, Ni content in anode has been increasing remarkably since 2012, causing to raise Ni content in the electrolyte as shown in Figure 2. The increment of Ni content in copper anode and electrolyte has adversely affected the electrorefining process, slime leaching process, and NiSO4 crystallization process at the tank house. Such severe conditions provided opportunities to redesign the tank house to establish a robust process to which more Ni is acceptable.

Jan 1, 2019

By R. F. Neider, W. R. Bain

"Expanding upon one aspect of a recent paper on ""Fluid Column Roasting at Sherbrooke Metallurgical Co. Ltd.,"" the present paper deals with the operation of the fluid column process to achieve substantial elimination of cadmium and lead during the roasting of pelletized zinc concentrates. Designed to meet the need for additional feed for Matthiessen and Regeler Zinc Company's vertical retort zinc smelter in West Virginia, without recourse to a sintering operation, the plant is capable of simultaneously attaining very low lead and cadmium levels on demand, through operation in the manner described. Fluidizing air admitted via the wind box is supplemented by natural gas admitted via a tuyere bank 15 ins. above the hearth, in quantities adjusted to maintain a reducing atmosphere within the interstices of the bed. In addition, careful attention is paid to bed temperatures, which run from 1,080° to 1,100°C. Under these reducing conditions, 90 per cent of the cadmium and 92 per cent of the lead in the feed are eliminated, the sulphate sulphur content is decreased by 0.5 per cent, sulphide sulphur is held at 0.6 to 0.08 per cent, and the zinc content correspondingly in-creases. The fuel value of the natural gas is recovered as extra steam, which carries a credit. There are some added difficulties with fume accretions, gas conditioning and gas -cleaning, some of which have yet to be overcome."

Jan 1, 1967

By J. Fellowes, V. Landais, J. Robson, J. Carr

"Aerospace Al-Zn-Mg-Cu (7xxx) alloys are known to be susceptible to environmentally assisted cracking (EAC). This phenomenon has been studied intensively for many decades, leading to empirically adopted methods to mitigate this problem through overaging and composition design. In parallel, many theories have been developed to explain EAC in 7xxx, but none is yet universally accepted. Today, a number of emerging techniques offer potential to shed new light on EAC in 7xxx. The purpose of the present paper is to demonstrate how X-ray tomography (XCT) combined with electron microscopy can be used to identify the true crack path in 3-dimensions, and hence identify material for site specific electron microscopy analysis. Composition mapping over large areas to high accuracy has been performed using a modern electron microprobe analysis system. This has been combined with transmission electron microscopy to investigate local composition in matrix and precipitates at high resolution. This combination of techniques across length scales offers the potential to provide new insights into the links between local composition, microstructure, and EAC resistance.INTRODUCTION Environmentally-assisted cracking (EAC) is a phenomenon which dramatically decreases the performance of metals and can cause premature failure of large structures. Observed in situations where components were not subjected to critical loads and no widespread corrosion was involved, this type of brittle failure is extremely difficult to predict. The EAC designation covers a number of phenomena, e.g. stress corrosion cracking (SCC), hydrogen embrittlement (HE), corrosion fatigue (CF), etc. Initially identified in steels, EAC can also affect other metals such as high-performance aerospace aluminium alloys, and this phenomenon has been a concern for industries for decades. Extensive research has been conducted on the effects of various environments (moist air, saline water, dry hydrogen gas, etc.) on microstructures and crack propagation, however no consensus has been reached and the exact nature of the mechanisms that control EAC is still being debated (Birnbaum & Sofronis, 1994; Gangloff, 2007; Holroyd & Scamans, 2013; Lynch, 2012; Oriani, 1972; Scamans, Alani & Swann, 1976, Young & Scully, 2002)."

Jan 1, 2018

MR. J. F. MYERS, Consulting J3eneficiation Engineer, Greenwich, Conn.: In the written discussion contributed by Mr. F. C. Bond in item ( 2) (page 515), speaiking about the significance of the ratio of mill diameter to the make-up ball diameter, he states: "When this ratio exceeds 100 the power and capacity of the mill are de-creased"; and the paragraph ends with a reference to the 30 per cent ball volume "with some de-crease in mill capacity". I believe this broad statement is incorrect. When we are dealing with a non-cataracting mill, pre-ceded by a good rod mill, there is a slight increase in capacity, but the power does drop. The second point that I consider needs consideration is Mr. Bond's item (8), Proper Mill Speed (page 516). This paragraph should be qualified to cover single-stage mills only. It does not apply where a rod mill is followed by a non-cataracting ball mill. The statement as is, with no qualification, gives an erroneous idea of proper mill speeds.

Jan 1, 1957

By D. H. Schwarz

The performance of proton exchange membrane (PEM) fuel cells depends on catalyst layer composition and structure. Experimental observations reveal that state-of-the-art catalyst layers consist of microporous agglomerates of carbon-supported catalyst sites bound together by polymer electrolyte. In between the agglomerates are macropores which provide pathways for the transport of gaseous reactants. In this work, three-dimensional, multicomponent and multiphase transport computations are performed using a computational fluid dynamics (CFD) code (FLUENTTM) with a new PEM fuel cell module, which has been further improved by taking into account the detailed composition and structure of the catalyst layers using a multiple thin-film agglomerate model. In this model, it is assumed that thin films of polymer electrolyte and liquid water surround the catalyst sites. The results of CFD computations show that transport limitations associated with the thin film of polymer electrolyte and the presence of liquid water in the catalyst and gas diffusion layers have substantial negative effects on PEM fuel cell performance. Also, the results of computations with variable distributions for a given precious metal loading show that, in general, uniform catalyst loading provides the best fuel cell performance.

Jan 1, 2005

By J. Tuzo Wilson

Abstract A division of part of the Canadian Shield into provinces believed to represent former mountain belts is attempted, special emphasis- being laid upon radioactive age determinations, the relation of Archaean to Proterozoic rocks, and the structure of the Grenville province. Original data on the distribution of radioactivity within several batholiths and their connection with ore deposits are' presented. The possible growth of continents and a theory which explains the shape and distribution of the world's younger mountain and island areas are discussed and applied to the Canadian Shield in an attempt to explain how the growth and present structure came about. The relation of the major mining camps of northeastern Ontario to fault zones is discussed in the light of this theory. Introduction The valuable symposium issued by this Institute to celebrate its jubilees emphasizes the important role of major faults in determining the location of many ore deposits in the Canadian Shield. Many of these faults are known to extend for long distances. It is therefore widely appreciated that it would be of great value if the pattern, ages, and causes of these faults were better understood. This would be particularly useful if the relations of the major fault systems to petrological and metallogenic provinces and to former mountain belts could be established. Each year the volume of available data, and hence the chance of reaching a fuller solution of this problem, increases. This article is a review of the present situation. It is accordingly based almost wholly upon the work and ideas of others, which are gratefully acknowledged. Naturally, responsibility for the selection and marshalling of the data is the writer's.

Jan 1, 1949

By N. Erarslan, M. Ghamgosar

The size of rock fragments depends on the nature of the loading applied the strength of the minerals and the texture of the rock. Research in the literature demonstrates that there is a distinct difference in the rock fracturing process for static and cyclic loading. The tensile strength of brittle rocks is also one of the most significant parameters influencing the rock fracturing process and the propagation of micro-fractures on the crushing, blasting and cutting of rock. The Brazilian indirect tensile test, one of the methods approved by the International Society for Rock Mechanics (ISRM), has been used to determine rock fracture behaviour under different cyclic loading modes. In this study, the dimensions of Brisbane Tuff specimens have been selected according to the method outlined by the ISRM. The main aim of this study is to evaluate the effect of cyclic loading amplitude and frequency on the Fracture Process Zone (FPZ) at the micro-, meso- and macro-scales. The post-failure behaviour of the Brisbane Tuff specimens was obtained under cyclic loading with frequencies varied from 1 to 10 Hz. The amplitude was varied from 10% of Ultimate Tensile Strength (UTS) up to 80% UTS. Laboratory investigations of rock fragment size revealed that different loading frequencies and amplitudes produce different FPZ dimensions. Multivariate Analysis of Variance (MANOVA) results demonstrated that the FPZ dimension is relatively sensitive to the frequency change. Fragment size analysis showed that the FPZ is a consequence of the initiation, propagation and coalescence of micro-fractures and depends on the nature of the loading. Laboratory evidence showed that the FPZ dimension, for the cyclic tests performed on Brisbane tuff, is ranged from 0.07 to 20 mm. The achievement of this study highlights a key finding in the understanding of fracture patterns and propagation models in the FPZ under cyclic loading, which is the dominate mechanical action in the oscillator disc cutter (ODC).

Jan 1, 2015

By W. D. Fogwill, P. J. Clarke

"The Dawn Lake uranium deposits are located 340 km north of La Ronge, Saskatchewan, in the Athabasca Basin between the Midwest Lake and Rabbit Lake deposits. Four zones of uranium mineralization, called the ""11, 14, 11A and 11B Zones,"" lie within the Athabasca Sandstone, at the sub-Athabasca unconformity and in the basement.At Dawn Lake, approximately 100 metres of Helikian Athabasca Group clastic sediments overlie Aphebian Wollaston Group pelitic and calcareous metasediments and pegmatites. Uranium with some nickel, cobalt and copper, occurs near the sheared stratigraphic contact between calc-silicate gneiss and graphitic, pyritic pelite. The mineralization lies in an area of low magnetic susceptibility which is thought to represent a rock sequence lying stratigraphically high within the Wollaston Group. There is no obvious vertical displacement of the unconformity by faulting, despite considerable brecciation, shearing and slickensides seen in the basement rocks. This suggests horizontal displacement on steeply dipping wrench faults as the main tectonic control along the 11, 11A and 11B trend.Below the Athabasca unconformity, the Wollaston Group rocks are altered to fine-grained mixtures of clays, chlorite and silica commonly called regolith. Along the mineralized trend post-Athabasca fracturing and (or) compaction have occurred through this clay-rich alteration zone, causing the steeply-dipping primary foliation to become contorted. This ""crenulated"" horizon can reach depths of 35 metres below the unconformity and is thickest along fault zones in the calc-silicate rocks. The ""crenulite"" is a distinctive unit which at Dawn Lake is commonly found above pods of ore located deep below the unconformity.Much of the mineralization in the 11A and 11B Zones occurs above, beside and below the thickest part of the crenulated zone, although the crenulated rock itself contains negligible amounts of carbonate, pyrite and uranium. Intense vuggy alteration and collapse breccias are found in calc-silicate rocks deeper and to the west of the 11A and 11B mineralization. There are at least two ages of uranium deposition in the basement zones, shown by small bright cubes of ""pitchblende /"" overgrown and replaced by duller botryoidal ""pitchblende II. ""Sooty pitchblende and yellow secondary minerals are the result of still younger reworking.The geological setting of mineralization, along the contact between carbonate-rich calc-silicate rock and pyritic pelite, suggests that the uranium was concentrated at a pH/Eh boundary located between deeply weathered, carbonate-rich and sulphide-rich basement rocks."

Jan 1, 1986

"Shales play a major role in the stability of slopes, both natural and engineered. This paper attempts to provide a review of the state-of-the-art in shale slope stability. The complexities of shale terminology and classification are first reviewed followed by a brief discussion of the important physical and mechanical properties of relevance to shale slope stability. The varied mechanisms of shale slope stability are outlined and their importance highlighted by reference to international shale slope failures. Stability analysis and modelling of anisotropic rock slope masses are briefly discussed and the potential role of brittle rock fracture and damage highlighted. A short review of shale slopes in open pits is presented.INTRODUCTIONShales have been stated to form approximately 58% of sedimentary rock so it is not surprising that they are frequently encountered in both natural and engineered slopes. They represent challenging environments for slope stability due to the wide variation in their engineering properties, their changing behaviour with time due to geomorphic processes and the variation in the failure mechanisms as a function of both stratigraphy and tectonics. An extensive body of literature exists on the terminology and classification relevant to shales; it is not possible in the scope and length of the current paper to review these works in detail and the reader is referred to Farrokhrouz and Asef (2013), Bell (2000) and Goodman (1993) for detailed discussions. It is arguably the case that no universally accepted classification of shales exists today and depending on the field of application the terminology varies widely. Shales in slope stability, for the purpose of this keynote paper, are taken to include material varying in properties from weak rocks to soils and therein lies one of the most challenging aspects in shale slope characterisation for engineering purposes. They have been classified as “rock-like” or “soil-like’, (Underwood 1967) or compacted and cemented, Table 1, Yagiz (2001). Classifications have considered numerous factors including composition, cementation and a wide range of engineering properties.The propensity of shales to degrade with time due to geomorphic processes has resulted in an important aspect in their classification, that is, the attempts to incorporate slaking, durability and swelling and softening behavior through purpose developed testing methods (Gamble 1971, Morgenstern and Eigenbrod, 1974). Figures 1 and 2 show examples of terminology used to describe argillaceous materials and some proposed engineering classification schemes (Grainger 1984 and Bott 1986). Corominas (2014) provides a recent classification of argillaceous rocks and their durability relating five stages of slope deterioration to the texture of the rock on Ternary diagrams. No attempt will be made here to discuss the merits of the proposed terminology and classifications, suffice it to say, that the controversy and flux surrounding these issues is a strong indicator of the complexities in the behavior of these materials. In this paper the author will consider slope stability in the materials indicated in Table 1, Figures 1 and 2 without undue focus on terminology. At the lower strength limit of shales the engineer must design slopes using the principles of soil mechanics which may vary from the simple Mohr Coulomb plasticity constitutive criterion to modified critical state models, some even attempting to incorporate softening behaviour in the weaker clay shale materials. Given the transitional nature of shale materials several workers have treated overconsolidated clays and clay shales using concepts such as peak and residual shear strength, brittleness index and softening. Martin and Stacey (2013) provide a useful review of the importance of weak rocks in open pit mining, with mudrocks as a specific member, and note the importance of delayed failure, progressive failure and loosening in the stability of"

Jan 1, 2015