By F. Keller, E. H. Dix, L. A. Willey

The consideration of alloying elements for aluminum has led to a series of investigations of the equilibrium relations between aluminum and those alloying elements. Therefore, the aluminum end of the aluminum-antimony diagram has been studied. The general form of the aluminum-antimony equilibrium diagram has been worked out by Campbell and Mathewsi and by Tammann.2 Canlpbell and mathews described principally the beginning of solidification. They found the curve of beginning of solidification rising gradually from the melting point of pure alunlinum to a maximum at about 67 per cent. aluminum. After a slight lowering of the curve at a little greater antimony concentration the curve again rises to a maximum at 18.4 per cent. aluminum, which corresponds to the compound AISb. The curve then drops to the melting point of pure antimony. Tamrriarln explained the maximum occurring at about 67 per cent. aluminum as the result of the slow formation of the single compound AISb. The space lattice of the compound AISb, according to Owen and Preaton,³ is face-centered cubic, the antimony atoms being intermeshed with an identical aluminum lattice. Very little, if any, work has been done on aluminum alloys containing small amounts of antimony. The Present Investigation It has been the purpose of this investigation to determine the solid solubility of antimony in aluminum and also to investigate the eutectic temperature and concentration. The experimental work has been carried out in a manner similar to that described in a previous paper4 from this laboratory.

Jan 1, 1931

By Ingvar Janelid

DURING the last ten years, in the effort to save manpower and costs, methods of drilling and blasting in Sweden have changed and developed in a revolutionary manner. These developments have been accompanied by extensive alterations in methods of tunneling and in mining technique. Since the end of the 1940's there has been a 100 pct change-over in Sweden to the use of tungsten carbide tipped drill steel. Both investigations and practical results have shown clearly that a tungsten carbide chisel bit fastened directly on the drill steel is the most economical for Swedish conditions. This applies to drill steel up to the longest size it is practical to handle. In terms of drilling footage, durability of the drill steel and the tungsten carbide bit is generally the same. In this respect, therefore, a detachable bit offers no advantage over integral steel. Transportation of integral steel to the grinding plant, instead of detachable bits only, involves heavier work, but this is counteracted by placing grinding plants closer together or by grinding at the working place itself. The drilling rate with integral steel is higher, the trouble of changing bits is avoided, and the difficulties which always arise with joints are eliminated. At present steel dimensions are usually 7/8 in. with a shank 41/4 in. long, whereas the international standard shank was formerly 31/4 in. The longer shank renders possible a better guide control of the steel and consequently longer life for the rotation chuck and the water-flushing pipe. After extensive experiments and investigations, agreement has been reached in Sweden on certain series of standards, shown in Table I. Other steel dimensions are, of course, available for special purposes. The standard drill-steel set begins with a 34-mm diam and has a length interval of 2 2/3 ft. On the other hand, for ordinary drifting it has been proved more economical to use greater length intervals on the steel, so only one steel change is required for a 61/2-ft round. Moreover, owing to the relatively close hole spacing necessary in a drift round, it has been possible to reduce the diameters of the tungsten carbide bits. This results in faster and cheaper drilling. As shown by the table, the lengths of drill steels for normal drifting are 33/4 ft and 71/2 ft, with 29 and 28-mm diam bits. During the last few years operators have begun to use 3/4-in. drill steel in place of the 7/8-in. drill steel chiefly employed earlier. This is a valuable development in drilling technique, particularly in view of

Jan 1, 1955

By William E. Ford, Edward Salisbury Dana

Secondary Twinning. - When there is reason to believe that the twinning has been produced subsequently to the original formation of the crystal, or crystalline mass, as, for example, by pressure, it is said to be secondary. Thus the calcite grains of a crystalline limestone often show such secondary twinning lamella?. The same are occasionally observed (Ilc, 001) in pyroxene crystals. Further, the polysynthetic twinning of the triclinic feldspars is often secondary in origin. This subject is further discussed on a later page, where it is also explained that in certain cases twinning may be produced artificially in a crystal individual - e.g., in calcite (see Art. 282).

Jan 1, 1922

By Charles Jones

IN the winter of 1902, while occupying the position of mining and examining engineer for the Mountain Copper Co., Ltd., of Keswick, Cal., I had occasion to discuss with the General Manager, among other things, the question of the enormous waste of sulphur in smelting cupriferous, pyrite ore, and to cast about for means to utilize this waste or to render the fumes innocuous to vegetation. The decreasing rate of production of California farms, the consequent need of fertilizers, and the opportunity thus offered to utilize large quantities of sulphuric acid in the manufacture of superphosphates naturally brought the subject to the practical and commercial side of phosphates. I was informed that the company had made efforts to find phosphates in the West, without success. I advised as a start placing inquiries for phosphate deposits on the Pacific coast in the current mining ,journals. This was done, with the result that in January, 1903, from an advertisement in the Mining and Scientific Press we got track of a deposit in Rich county, Utah, through T.J . Wilson, of the Southern Pacific railroad in San Francisco. As soon as snow in the mountains would permit, in May, 1903, I undertook an examination of the property, with the result of recognizing the importance of the find, in spite of its lack of facilities for transportation at a commercial figure. On June 15, 1903, I concluded my report by saying, "This may be one of the world's deposits of phosphates." On Nov. 17, 1903, I concluded my report for the season in the following words : " I have now no hesitation in saying that I believe the Carboniferous formation so largely developed in the Wasatch mountains of Utah and the mountains of the Great Basin will prove to be one of the greatest storehouses of phosphoric acid in the world."

Jan 10, 1913

Discussion of the paper of GEORGE S. RICE and H. H. CLARK, presented at the Pittsburgh meeting, October, 1914, and printed in Bulletin No. 94, October, 1914, pp. 2563 to 2571. NORMAN V. BRETH,* Pittsburgh, Pa.-It was my privilege to visit in the last two months on behalf of the U. S. Bureau of Mines 10 mines where electric shot-firing systems controlled from outside the mine are installed. I will describe briefly what I saw in some of these mines, which are located in Utah, New. Mexico, Oklahoma, Alabama, and Kansas. At a mine in Utah, 230-volt alternating current is used to fire the shots, which is taken from a small transformer in the substation. The shot-iring circuit is independent of all other wires and is tested for grounds every day. There are no lightning arresters on the firing circuit. Porcelain insulators are used inside of the mine, and glass outside. The switches are situated as follows: One in the substation, one in, the shot-firer's cabin, two at each cross entry; where the shot-firing circuit crosses the trolley wire a switch is placed on either side of the entry in series with the shot-firing circuit. The miners are checked in and out of the mine. The coal is undercut and is shot down with permissible explosive, the shots being connected in multiple. There are 75 to 110 shots fired each day. A great many times there are no missed shots. If not more than two or three are missed they are left until next day. The fan is kept running at full speed when the shots are fired. The shot-firing switch is closed only once and the whole mine is shot at once. At another mine in Utah, power wires are used for shot-firing circuits; 500-volt, direct current is used to fire the shots. The only sizes of wire used outside of the power wires are Nos. 8 and 14 B. & S. gauge. The return is connected to the pipe lines and track. Porcelain insulators are. used inside of the mine.

Jan 4, 1915

By J. B. Gayle

PRESENT flotation processes depend almost entirely on the buoyant properties of air bubbles to effect separations of mineral and gangue, but there is no convenient method for measuring aeration in flotation cells. Consequently the relation between aeration and cell performance has not been definitely established. In connection with a comparative study of kerosene and froth flotation processes, a modification of the displacement method' was developed in which air escaping from the cell surface is measured with a wet-test meter. The arrangement shown in Fig. 1 is satisfactory for use with a number of cells and is not critical, except that care must be taken to use connections and tubing large enough to avoid excessive back pressures. Attempts to use smaller tubing resulted in back pressures that caused displacement of the liquid level in the receiver, so that some air was lost around the sides, an occurrence readily visible when measurements were taken with only water passing through the cell. With the arrangement shown, the manometer indicated an average reading of about 1/2-in. water pressure. No loss of air was evident. Fig. 2 presents typical data for a standard Denver sub-A 24x24-in. unit cell operated at impeller speeds from 0 to 710 rpm. Each plotted point represents the average for five readings distributed over the entire cell surface. Readings were taken with only water passing through the cell. Results of this type have been used in a study of the influence of operating variables on cell performance and in detecting inherent differences in the operating characteristics of cells of various kinds. Although the information presented in Fig. 2 resulted only with water passing through the cell, the apparatus is suitable for use during flotation of coal when various reagents are present. Possible modi- fications that might prove convenient under special circumstances include varying the size and shape of the receiver and substituting a calibrated, inverted, water-filled carboy or other gas-measuring device for the wet-test meter. If such modifications result in excessive back pressures, some form of draft should be applied at the discharge end of the measuring system.

Jan 1, 1959

By Enrique Touceda

FOR a number of years prior to the world war, the firm of Geo. H. Thacher & Co., of Albany, N. Y., was engaged in the manufacture of marine and other gray-iron castings. At -the outbreak of the war the firm decided to specialize in the manufacture f propeller wheels. It attacked the problem, therefore, from a foundry point of view, seeking to produce a casting that would be so accurate that no subsequent machining would be required on the blades, also from the point of view of the ship builder. There were two general methods f manufacture, the shortcomings of which have been freely acknowledged. In the sweep method, the nowel, or bottom half-mold, for each blade is swept up by a spindle beam and pitch race, while the top half-mold for each blade is built up individually. In the pattern method one individual blade, with the hub or hub portion, is mounted on a spindle and the individual -blade mold formed, the pattern is then rotated on the spindle to the position- for the next blade, etc. In rare cases wheels were made from a solid pattern. Owing to the cost of the pattern, its failure in many instances to be correctly made, and (when made of wood) its early and sure distortion the disadvantage of this practice is obvious, while metal patterns in most instances were prohibitive in cost. In these methods both green-sand and loam molding was practiced. The casting produced by either method can be considered only as a blank from which the propeller must be machined. The back surface f each blade must be chipped too the templet and through this procedure chipped to such accuracy, as will be required for a static balance. Inasmuch as the' work done by the machine tool is confined to the driving face of the blades, not only is perfection most difficult, but corrosion will be greater because of the removal of the dense skin f the casting and the local strains set up by the pneumatic tool in chipping. To produce a finished 9-ft. propeller for a Navy destroyer required from 8 to 21 days f foundry work and about the same length of, time for the machining. Through the use f the Thacher process, only as many hours are required, besides it is possible to produce a finished casting in perfect conformity, with any particular propeller-wheel design,

Jan 4, 1921

By C. A. Allen

For over three years we have been endeavoring to reduce the number of fatalitics and minor accidents in Utah. The physical condition of the FIG: 1.—Number kiLlEd per million short tons of coal produced in ColoraI)o, New Mexico, utah, Wyoming, and bituminous mines of the United States 1014 to 1920. mines, concentrators, and smelters is good, yet the number of accidents,

Jan 1, 1923

By C. A. Allen

For over three years we have been endeavoring to reduce the number of fatalitics and minor accidents in Utah. The physical condition of the FIG: 1.—Number kiLlEd per million short tons of coal produced in ColoraI)o, New Mexico, utah, Wyoming, and bituminous mines of the United States 1014 to 1920. mines, concentrators, and smelters is good, yet the number of accidents,

Jan 1, 1923

By E. J. Bonet, P. B. Crawford

It is fairly common practice to reinject water into the aquifer near the oil-water interface in water-drive reservoirs. There have been many studies of aquifer behavior without reinjection,l-5 but apparently no analytical studies have been made to indicate performance when injection wells are present in the aquifer. The diffusivity equation may be used to describe the pressure behavior in an aquifer. When sources are present it can be written as A general solution of Eq. 1 may be obtained as the sum of two solutions. One is a general solution of the homogeneous equation, obtained by dropping the source term in Eq. 1 and still satisfying the required boundary conditions. Another is a general solution of Eq. 1 satisfying homogeneous boundary conditions.1° The first solution, which corresponds to the aquifer without reinjection, has been given quantitative and qualitative treatment in the literature.l-5,8,9 The latter solution will be treated here. Solutions with variable injection rates are obtained by superimposing solutions with constant rates, so we have considered only the latter. Five cases have been treated here: 1. A linear aquifer of finite width and extent. Water is injected into the aquifer at point xo, yo at constant rate. The pressure along the line x = 0 is maintained at zero pressure. (See Fig. 1.) Equations showing the pressure distribution, rates, velocity and cumulative influx have been developed. Certain numerical results are shown. 2. A linear aquifer of finite width and extent. Water is injected into the aquifer at point xo, yo at constant rate. The rate of production along the oil-water water contact is maintained constant. Equations showing the pressure distribution inside the aquifer are presented. 3. A linear aquifer of finite width and extent. Constant pressures are maintained at opposite ends of the aquifer. Water is injected at constant rates at point xo, yo. Equations showing the pressure distribution are shown. 4. A linear aquifer of finite width and infinite extent. The pressure is maintained constant at the oil-water contact. Water is injected at a constant rate at point xo, YO. 5. A linear aquifer of finite width and finite extent. The pressure at the oil-water contact is maintained constant. Water is injected at constant rate per unit length along a line x,. The Linear Aquifer The linear closed aquifer, performing at constant terminal pressure was selected as the first case to be analyzed. The development of the equations is based on uniform injection per unit of thickness, and gravity effects are neglected. In practical application this condition is probably most closely achieved when the

Jan 1, 1970

By Michel L. Bilodeau

The objective of delineation drilling is to provide a data base for the tonnage and grade estimates required to evaluate the economics of mine development. As drilling information is accumulated, geological risk is reduced and more reliable estimates of tonnage and grade are obtained. Investment in drilling is justified by the benefits which result from improving the reliability of the economic criteria evaluated. These benefits are subject to diminishing returns, i.e. as drilling information is accumulated the reliability of the economic criteria evaluated is improved but at a decreasing rate. At the same time, costs are incurred -- the direct investment cost associated with additional drilling and the time cost of delaying possible production revenues. The economic sampling limit is de- fined by the point at which the marginal benefits from drilling investment just balance the marginal costs. The paper describes the formulation of an economic model to optimize investment in delineation drilling. The model is applied to a simulated mineral deposit to illustrate the economic effects of a sequential drilling program.

Jan 1, 1977

By E. A. Gulbransen, J. W. Hickman

DURING the past two decades considerable progress has been made in the art of manufacturing heater alloys. The conventional iron-chromium-nickel alloys have been improved by the addition of small quantities of other elements. Up to the present time, to our knowledge, there has not appeared a systematic study of these alloys where the newer tools of investigation have been brought to bear on the problem. It is not yet clear what roles the additional elements play in increasing life time in usage. As a first approximation one might guess that elements such as manganese, silicon, zirconium, calcium and aluminum would aid in the formation of a protective film on the alloy surface, thus retarding the oxidation rate and increasing lifetime. If these additional elements do form protective oxides in the outer surface of the oxide film, it may be possible to identify them by means of reflection electron diffraction. It is also possible that the additional elements may not diffuse to the surface but may remain at the interface between the oxide and the metal. Then, too, the major elements in the alloys undoubtedly form oxides which are stratified on the surface. If the minor elements concentrate in a layer in contact with the substrate where they undergo oxidation and if this oxide film offers resistance to the diffusion of iron, chromium and nickel ions, then the lifetime of the heater element might be expected to increase. It is also possible that preferential reduction in the diffusion rates of the several ions may Occur to such a degree that oxides may form in the body Of the film and On the outer surface which are different from those that would normally form if the additional elements were not present. The use Of transmisson electron diffraction may aid us in jnterpreting these phenomena. UP to the Present time all Of the factors which influence the lifetime of a given heater element are not definitely known. Among these are: (I) The rate of oxidation of the alloy. This may be dependent upon the composition and the physica1 state of the "alloy. (2) The stability of the structure of the coating which forms. Transitions from one structure to another or solid phase reactions resulting in a change of composition may occur. The tendency of the film to adhere to the substrate when heated and cooled successively will be important. (3) The evaporation of various constituents from the alloy such as the remova1 of carbon by Oxygen in a decar-burization reaction. With these possibilities in view, an electron diffraction study of the oxides occurring on six different nickel-chromium alloys was undertaken with the hope that the results of this study could be correlated with oxidation rate studies as determined by means of the vacuum microbalance method1 and with lifetime tests carried

Jan 1, 1949

Jan 1, 1971

By Earl L. H. Sackett

Barite, although not a glamour mineral and probably little known to many of those in the mining business, is produced in the US. in very respectable quantities and is an important factor in the mineral economy of this country. The scope of the various uses of this mineral is perhaps one of the most misunderstood things about it, for it is surprising how many of those with a casual knowledge of the subject speak of its primary utilization in terms of paint pigments and barium chemicals. The life blood of barite utilization, however, is the petroleum industry by virtue of its dependence on this high specific gravity, inert mineral as the weighting material in its drilling fluids. From 80 to 85% of barite usage in the U. S. is accounted for in this manner-in fact, its role in oil well drilling is the only excuse for some of the large-scale barite production facilities which have been developed. Other uses are important and widely varied, but comparatively they are of small scale. They include fine crushed barite of low iron content as a component in glass manufacture, barite as a source material for manufacture of barium chemicals, finely divided barite as a component of some rubbers and ground, bleached barite in pigments. The formerly substantial use of barite in lithopone, however, has declined markedly because of replacement of lithopone by titanium pigments

Jan 5, 1962

By J. M. Uys, T. B. King

WalSH, Chipman, King, and rant' have measured the water content (as hydrogen) of actual steel-making slags. An average water content of 290 ppm was found for basic open-hearth tapping slags and 114 ppm for acid open-hearth slags. Upon equilibration of these slags at 1550°C with a 25 pct H20-75 pct Nz atmosphere, the water content increased to about 410 and 300 ppm for the basic and acid slags, respectively. Walsh et al. concluded that an acid slag was thus relatively far removed from equilibrium, and that basic slags showed a closer approach to equilibrium, with the water vapor in the furnace atmosphere. Herasymenko2 contended that these conclusions were unjustified, as the oxygen pressure used in the equilibration experiments, ;bout 5 x X atm, was quite different from that found in the furnace. Consequently, during the experiments the slag composition would have changed due to oxidation of ferrous iron. As an extension of Walsh's work and to attempt to clarify this matter, the solubility of water in a basic open-hearth slag was measured as a function of oxygen pressure. Similar measurements were also made on synthetic silicates in the "Fe0"-Fe203-SiO, system. The experimental technique has been described previously by Walsh et a1.l and Uys and King.3 Samples of the basic open-hearth finishing slag, contained in 10-cc platinum crucibles, were equilibrated at 1550°C with atmospheres of different oxygen pressure but constant water-vapor pressure, Ph~o = 0.192 atm. Calculations, as well as measurements, indicate that this figure approximates the water pressure of the combustion gases in a steam-atomized, oil-fired open hearth. Oxygen pressures in the open hearth can vary from 10"2 atm in the combustion gases to between l0-' and 10" atm in the steel bath. The former figure depends on the combustion practice and the latter on the carbon content and temperature of the bath. The oxygen pressure of the slag should lie somewhere between these extremes and is expected to be closer to that of the steel bath than that of the combustion gases. Oxygen pressures were therefore varied between 10" and 6 x l0 atm. At the lowest pressure the slag "puffed up" when quenched (indicating possible loss of water) so experiments were not conducted at lower oxygen pressures. The results are shown in Fig. 1, which includes the water content of the slag "as sampled". The results show that the water content of the slag increased appreciably on equilibration with water vapor at 0.192 atm pressure and that the water solubility apparently decreases with increased oxygen pressure. The solubilities found are comparable to those of the Li20-Ca0-Si02 system.3 Work with synthetic slags in the "Fe0"-Fe203-SiOz system was performed at 1500" C, with Ph20 = 0.192 atrn and for oxygen pressures varying between 10"2 and 10-lo atm. Samples for chemical analysis were prepared as described by Larson.4 The results are shown in Fig. 2. Some low-silica melts tested at low oxygen pressures "puffed up" when quenched and analyzed less than 100 ppm water; these results are not included in Fig. 2. The melts containing 40 mol pct silica also showed a tendency to "puff up" during the quench, when they were tested at the lowest oxygen pressure. These results indicate that, at constant silica content, the solubility of water decreases somewhat with increased oxygen pressure. The effect is, however, small considering the wide range of oxygen pressures studied. Also, at constant oxygen pressure (above about lom5 atm) the solubility increases

Jan 1, 1963

By A. H. Larson, L. G. Twidwell

DURING the roasting of zinc sulfide concentrates and by-product recovery from flue dusts, the zinc sul-fate phase may occur in various stages of the processes. In addition to zinc sulfide, other sulfide phases are usually present such as CdS, PbS, CuzS, and FeS. Consequently, the effect of these sulfides on the thermal decomposition of ZnS04 was investigated. Merck high-purity, anhydrous zinc sulfate was used as the starting material. The sulfate was heated under an argon atmosphere, at a rate of 10°C per min. With the first slight indication of decomposition as determined by gas analysis, the sample was removed from the furnace and allowed to cool. X-ray patterns showed no other phase present. It is estimated that less than 0.05 pct of the ZnS04 decomposed. The metal sulfides were also heated under an argon atmosphere to drive off any adsorbed water. The materials were then sized (-200 to +270 mesh), mixed in predetermined mole ratios, and pressed into pellets. The experimental measurement of the reaction rate consisted of purifying the argon carrier gas, continuous flushing of the heated reacting mixture with argon, and collection and analysis of the SOn product gas. The reaction system was heated to 600°C and al-

Jan 1, 1967

By F. W. Maclennan

The following is a list of members who died in 1929. It is compiled from reports to the Secretary's office. Biographical sketches published in Mining and Metallurgy are indicated in the last two columns. Issue Containing Year of Date of Biography Election Name Death 1929 Page 1922 Adams, Waldo Peck................................ June 2 September 435 1903 Argall, Joseph.................................... Nov. 1 1894 Austin, Leonard S................................. Oct. 30 December 580 1905 Bailed, Melbourne.........................Dec. 12 May* 280 1890 Barringer, Daniel M.............................. Nov. 30 February* 119 1895 Batchelleb, HENRr R.............................. Jan. 15 March 167 BINGHAM Charles E............................. 1923 Bibkett, E. H..................................... Apr. 23 August 394 1913 Bibbell, Robert W................................. Jan. 18 April 214 1926 Blackmar, Don C.................................. June 4 March* 189 1920 Bosworth, T. O.................................... Jan. 18 April 214 1894 Boucher, Arthur S..........................Jan. 6 May 257 1927 Brandenthaler, R. R.............................. Dec. 14 January* 64 1889 Bretherton, S. E............................... Oct. 4 December 581 1911 Brunton, F. K................ .. Aug. 17 1924 Brush, Charles F................................. June 15 September 436 1925 Cameron, Frank N........................May 16 July 349 1891 Chambers, Robert E.............................. May July 348 1908 Clark, J. Murray................................. Dec. 3 August* 407 1883 Clymer, edward T............................. Oct. 13 December 579 1914 Cofpey, George T................................. May 8 July 349 1901 Cooke, L. H....................................... Aug. 23 November 537 1915 Cousins, George W........................ June 30 February* 118 1886 Cowles, A. H...................................... Aug. 13 September 436 1892 Crane, Theron I............................. Nov. 2 December 579 1921 Crowell, Samuel B................................ Dec. 9 January* 64 1907 Curtis, Bracey.................................... Jan. 31 April 215 1895 de Batz, Rene........ ............... January March* 189 1928 Dines, Tyson S.................................... March May 257 1909 Dufourco, R. G............................. January November 537 1920 Ericsson, Eric A.................................. Apr. 4 April* 231 1920 Erlenborn, Willi....................... Nov. 10 March* 189 1888 Farish, John B.................................... Nov. 14 December 580 1891 Ferguson, Vincent........................... Mar. 8 May 257 1917 Finucane, T. R.................................... Mar. 22 February* 118 1921 Foch, Ferdinand................................... Mar. 20 1885 Foucar, Edouard I....................... Jan. 3 March 167 1880 Francklyn, Charles G............................. Jan. 11 April 214 1925 Friedl, Arthur J.............................. July 9 September 435 1894 Fuller, James W. Jr............................... April 4 1876 . Goodale, Charles W.............................. April 11 May 258 1912 Graybill, John..........................Dec. 11 June* 320 1887 Gritzner, F. A.................................. Mar. 26 July 394 1906 Gunther, C. Godfrey.............................. Deo. 26 February* 118 1900 Haggen, Edward A.............................. Apr. 22 October 488 1895 Hall, Benjamin M........................Nov. 19 March* 189 1913 Harper, Walter S................................. Feb. 15 August 394 1921 Hawley, William S................................ Apr. 20 June 298 1920 Herd, Walter ... . . . ..... Aug. 23 September 435 1889 Holt, Marmadtjke B............................... Dec. 26 February* 118 1928 Husk, Albert D .... ................June 9 December 580 1920 Hutchinson, S. Pemberton......................... Feb. 16 April 214 1926 Ivanoff, Constantine L............................ Mar. 7 June 298 1914 Jaeger, Frederick..... .............July 28 October 488 1891 Jennings, Robert E.......................Oct. 30 December 580 1922 Johnson, Homar L................................. Sept. 17 October 483 1927 Johnson, Homer H................................. Mar. 21 May 257 1918 Jones, Jesse L ..... ...............Jan. 22 April 214 1892 Jones, Thomas J................................... June 18 October 488 1883 JoOet, Cavalier H................................. Mar. 29 May 258 1881 Kennedy, John S . . . . ... ..........Apr. 22 August 394 1881 Kennedy,- Hugh.................................... May 23 September 435 1895 Kebvin, James H................................... September October 488 1926 Kkom, L. J........................................ Dec. 24 January* 64 1905 La Follette, Harvey M........................... Sept. 19 November 538 1920 MacDonald, Alexander............................ May August 394 1904 Marengo, Paolo................................... May 257 1925 Maxwell, Allison R............................... May 7 November 538

Jan 1, 1930

By J. B. Dyess

TARNISH films on some of the common metals (particularly on copper and silver) have been of much scientific and commercial concern for a long time, but before the development of the electrical method1 of measuring film thicknesses there was no satisfactory quantitative approach by which to study the separate parts of these complex films. This method has been adapted to the measurement of duplex (cuprous-cupric) oxide films on copper .2 In the present work it has been used to measure tarnish films on copper when they were mixtures of cuprous oxide and cuprous sulphide, and also when they contained cuprous oxide, cupric oxide and cuprous sulphide, each component part being measured at a different potential value. Oxide-coated copper specimens, prepared by heating copper in air at chosen temperatures for given periods, were exposed to moist hydrogen. sulphide in air to form the various oxide-sulphide films studied. The comparative resistances afforded by (1) different thicknesses of oxide films, and also (2) equal thicknesses of oxide and sulphide films, against severe attacks of hydrogen sulphide were measured. The electrical method requires that the time be observed for the cathodic reduction of each part of the film substance, and these respective time values multiplied by the constant current give the corresponding quantities of electricity expended. Then each millicoulomb per square centimeter represents a film thickness of T= MX10 8 2D X 96,494 X 103 (a) where M is weight of oxide (or sulphide) giving one gram-atom of oxygen (or sulphur) for cathodic reduction, D is density of the oxide (or sulphide) and t is the thickness in Angström units per millicoulomb per square centimeter. The value of t for cuprous sulphide (cubical) is 14.27, and is obtained by substituting 5.78 for D and 159.20 for M in equation a. Previous values2 of t for cuprous and cupric oxides (12.36 and 6.39, respectively) were used in the present work.

Jan 1, 1939

A New Ingersoll-Rand Turbo Blower The Ingersoll-Rand Co. has added to its Turbo Compressors and Blowers a low-pressure machine t o handle volumes from 3,000 to 35,000 cu. ft. per minute at from 1-2 ½ lb. These are particularly adapted to such service as foundry cupola blowing, atomizing oil for oil burners, supplying blast to heating and annealing furnaces of various kinds, blowing air for water-gas generators, pneumatic conveying and ventilating. They are of the single stage, double flow type and are furnished either electric motor, steam turbine or water wheel driven.

Jan 6, 1916

By R. L. Grunes, F. K. Kies, C. D&apos, Antonio

THE several studies concerned with the annealing of thin nickel films have largely been restricted to films of a single thickness.1-4 It is well-known, however, that both physical and mechanical properties depend upon film thickness.5, 6 The strength-thickness relations found in vapor-deposited nickel films in the annealed and as-deposited states, as an example, are at least partially due to the density and arrangement of imperfections within the films.7, 8 For these reasons, the annealing characteristics of thin nickel films as a function of thickness were investigated. Electrical resistance was chosen to monitor annealing behavior since resistance changes are partially dependent upon defect structure. In addition, the equations predicting film resistivity as a function of thickness are already available.9, 10 Further advantages afforded by electrical-resistance measurements are its adaption to continuous readings during annealing and its relative simplicity. Nickel films were vapor-deposited, at average rates of 60Å per sec, on Vycor substrates held at room temperature in vacuums of about 10-5 torr. Afterwards, deposition-thickness measurements were made using a multiple-beam interferometric technique. A more detailed description of deposition procedures and the interferometer appear elsewhere.7, 8 The four-probe method was employed in measuring electrical resistance since this technique measures film resistance without contributions from lead wires and contacts. Resistance measurements were made before, during, and after annealing to temperatures of 700°C under vacuums of approximately 10-4 torr. Measurements were made every 25°C or more often when necessitated by unusual resistance changes. Cooling and heating rates were maintained at approximately 5°C per min. Typical resistivity vs temperature curves are shown in Figs. 1 through 4. It is apparent from these

Jan 1, 1965