By George H. Gilman

THE campaign now being waged to improve the quality of the rock-drill bit is the natural outcome f the scientific development of the drilling machine during the past twenty years. In this development there has been a great increase of power output per unit of weight of machine. But the development of the rock drilling engine has been seriously hampered by the need of a drill bit that would withstand, without undue wear or breakage, the heavy rapid blows of the improved pneumatic hammer. This problem was difficult to solve because an increase in the weight or section of the drill-steel bar resulted in decreased cutting speed and higher operating costs of both the bit and its actuating engine. The solution, therefore, is to make the bit of steel that, for a given weight or section, will be more shock and wear resisting. In the attempt to meet these requirements, many of the drill-steel manufacturers alloyed the steel with vanadium, chromium, nickel, etc., on the assumption that such elements would improve the rock-drill bit but due to the sensitiveness of such steel to forging and heat treatment, higher cost, and lack f continuity of effort on the part of the steel manufacturer to perfect this product, but little progress has been made in the adoption of these steels and the so-called straight carbon steel is today recognized as the standard material for all rock-drill bits. The first step in improving drill-bit efficiency is the determination f the cause of breakage and wear. For this reason, in 1917, certain rock-drill manufacturers, in conjunction with some of the larger mining interests, conducted exhaustive tests in both the field and laboratory. It was then found that, in the main, the cause of drill-steel troubles is not attributable to the duty imposed upon it by the normal operation of the drilling engine, but to improper forging and heat treating of the bit and to the subjecting of the bit to improper use. The fact that it is possible to minimize the troubles attributable to improper heat treatment of the drill steel has been demonstrated and it is recommended that such knowledge be made available by teaching those interested in the production, use, and up-keep of drill bits the principles on which success in this direction may be achieved.

Jan 6, 1921

By H. W. Ahrenholz

Seven weeks of 1971 were devoted to a nationwide coal walkout resulting in lost production of some 70 million tons and leaving 1971 coal production at about 550 million tons. Compounding the problem, consumption of coal in 1971 by electric utilities rose by about 5% to 336 million tons. In the mean- time, numerous contracts were awarded for coal R&D including $24.8 million given by the Office of Coal Research to Bituminous Coal Research for the construction of a coal-to-gas pilot plant using the BIGAS process. Exports declined mainly due to Japan's decrease in steel production and to that country's increase in coal imports from Canada and Australia. The advances in equipment design and mining procedures made 1971 a noteworthy year. Introduction of the variable pitch I dipper, the trend toward wheeled vehicles, the greater use of scrapers in reclamation and battery-operated vehicles and oscil-mining, and the increased activity in the areas of ventilation and dust control were given widespread approval. There were also strides made in computerization, longwall mining, roof bolting, rock dusting, mine haulage and methane detection.

Jan 2, 1972

By William H. Kobbé

The word recovery as used in this paper is applied in its broader sense and not limited to wells producing from horizons of unconsolidated sands. Certain problems connected with the winning of petroleum from such horizons present themselves while drilling is in progress and should be considered before drilling is commenced wherever unconsolidated sands are expected. Maximum recovery depends not alone. upon efficient pumping methods but also upon the selection of a proper drilling system and the completion of a well especially adapted to the extraction of these oil-bearing sands. 11. DRILLING Determining Factors in Selection of Method The selection of a drilling method for the development of a region in which the oil reservoir consists of unconsolidated sands is based on the following considerations: (1) Character of the formations overlying the reservoir; (2) thickness of the oil-bearing stratum or strata; (3) thickness and character of water or gas sands; (4) gas pressure to be encountered or expected; (5) total depth of well. 1. Character of the Formations Overlying the Reservoir The strata overlying the reservoir may consist of beds of shales, clays, sands and other soft materials, or they may be slates, limestones and sandstones consolidated to all degrees of hardness. Very often the overlying strata are predominantly of soft materials but interbedded with harder formations. Likewise, soft strata are encountered at different horizons in an overburden consisting almost entirely of the harder sedimentaries. The physical character of this overburden is frequently

Jan 1, 1917

By JAMES J. DOUGHERTY

THIS paper is a general discussion of developments in our reverberatory smelting practice during the past five years. It deals briefly kith changes in furnace types ; changes in furnace feed ; de- crease in the amount of slag produced; relation of slag assays to copper loss in the slag; increase in the grade of matte and furnace capacities. The reverberatory is but one unit in the copper plant ancl 'any discussion of it must be considered with reference to the other units and to the plant as a whole. A change in the grade of concentrates at the concentrator puts an entirely new aspect on reverberatory smelting and, likewise, a change in the grade of matte at the reverberatory affects the rate and cost of converting. The introduction of differential flotation in 1927 had a very marked influence on all smelting operations and its effect will be noted

Jan 1, 1930

By David W. Brunton

Mine-drainage and the ever-increasing demand for water on the plains have within the past few years necessitated the driving of a great number of adits and tunnels, including many of considerable size and great length. In most instances, existing conditions have called for extreme rapidity of execution; and this necessity, coupled with the high altitudes at which most of the work has been carried on, excessive freight-rates, and difficulty of access, has involved many complex and interesting problems. One of the most rapidly executed undertakings of this class is the Laramie tunnel, recently completed for the Laramie-Poudre Reservoirs & Irrigation Co. This tunnel is driven through Green ridge, a spur of the Continental Divide, which separates the Laramie river from the Cache-la-Poudre in Laramie county, Colo. Green ridge is extremely persistent, and further northward in Wyoming is known as Sherman hill, the highest point on the Union Pacific railway. At the point where the tunnel is driven, two opposing bends bring these streams within 2.5 miles of each other, with a difference in elevation of 500 ft. The rock exposed on the banks of the two rivers does not differ materially in hardness; and, without a geological study of the conditions involved, it would appear that the difference in the depth of erosion of the two streams is due principally to the greater volume of water at this point in the Cache-la-Poudre, which has a drainage-area above the tunnel-portal of 110 sq. miles, as against 30 sq. miles of natural drainage for the Laramie. To increase the water-supply at the tunnel, however, this latter amount has been augmented by two side collection-canals, which bring the available drainage-area up to 84 square miles. The nearest railroad shipping-point to the eastern portal is

Jan 1, 1913

By A. J. Bowie

Jan 1, 1879

By Philip D. Pearson

CALAND Ore Co.'s dredging program has reached the halfway mark. The goal is to remove more than 160 million cu yd of lake bottom material overlying the iron orebody in Falls Bay of Steep Rock Lake, Ont. Two large dredges were constructed to remove this overburden, a layer of soil about 90 pct varved clay some 400 ft thick. Moisture content of the clay is high-approximately at the liquid limit of the soil. A few years ago, searching for additional reserves of ore, Inland Steel Co. looked toward Canada and the newly developed Steep Rock iron range. To this end an option agreement was signed Dec. 30, 1949, between Steep Rock Mines Ltd. and Caland Ore Co. Ltd., a wholly owned subsidiary of Inland Steel. Several drilling programs were conducted between this date and Jan. 1, 1953, when a 99-year lease was signed covering an area of 1249 acres. This lease calls for ore production to begin in 1960, with full production of 3 million tons per year by 1969.

Jan 8, 1957

By H. S. Jerabek, Charles S. Barrett, Robert F. Mehl

The precipitation of the nitride Fe4N from the solid solution of nitrogen in a Fe and of the phosphide Fe3P from the solid solution of phosphorus in a Fe both lead to the formation of structures that may be easily identified as Widmanstatten figures, within the meaning of the term as used in this series of papers. A complete solution has been obtained for the figure formed by Fe4N. The structure of Fe3P, however, is not fully known and a complete solution of this figure thus cannot be obtained; nevertheless, a study of this figure has furnished some new information. Precipitation of Fe4N from Alpha Solid Solution of N in Alpha Fe Constitution of System Iron-nitrogen A knowledge of the constitution of the whole of the Fe-N system is unnecessary for this work, though the recent studies by Eisenhut and Kauppl and by Lehrerz have clarified most of the moot points; it is sufficient for our purpose to state that a Fe of high purity dissolves 0.42 per cent of nitrogen in solid solution at the eutectoid temperature, 591' C., and that this solubility decreases at first rapidly and then more slowly until at room temperature the solid solubility amounts to approximately 0.1 per cent nitrogen.3

Jan 1, 1934

By P. T. Chiang

Chemical etching methods for the simultaneous revealing of the tellurium or selenium Phase and the chalcogenide grain boundaries of the alloy systems are given. A tellurium eutectic was found Present in zone-melted ingots. Similarly, a selenium monotectic was present in ingots. In general, the second phase (tellurium or seleniumn) occubies three different sites; viz., along the chalcogenide grain boundaries, as inclusions within the chalcogenide grain, and on the undersurface of the ingot. The detection limit for the tellurium phase is about 1 u in width. THERMOELECTRIC materials based on Group V (bismuth, antimony) and Group VI (selenium, tellurium) elements have aroused considerable interest in recent years in the practical application of thermoelectric cooling. In many cases, a small amount of excess tellurium (or selenium) was added to the material to optimize its thermoelectric properties. Then the question immediately arises as to the number of phases present in the resultant alloy. In the binary systems of Bi-Te, Sb-Te, and Bi-Se, the congruent melting compositions have been reported to be non-stoichiometric and are represented by Bi~Te respectively. It is to beexpected and known that Bi2Te3 and SbzTe3 crystallize from the melt with an excess of bismuth and antimony in the lattice and that tellurium forms a eutectic.~' The same could be assumed to take place in the pseudo binary systems of (Bi,Sb)zTe3 and Bi2(Se,Te)3 as well as in the system studiedby puotinen5 and other workers. Likewise, BiaSe3 crystallizes from the melt with an excess of bismuth in the lattice and selenium forms a monotectic.~ Therefore, in practice, alloys solidified from the melt often contain a second phase (tellurium or selenium) in one region or another of the solid mass even without the addition of excess tellurium (or selenium). ~u~~recht' studied the thermoelectric properties of (Bi,Sb)2Te3 alloys with excess tellurium and simultaneous additions of selenium. He mentioned that the materials show two phases because of the considerable excess of tellurium or selenium. However, he did not report as to how the tellurium or selenium phase was identified. It is generally believed that the presence of an excessive amount of tellurium or selenium phase in the alloy would adversely affect its thermoelectric properties and its uniformity. Consequently, there is a need for a simple method for the identification of the tellurium and selenium phase. The quantity of the second phase present is usually too small to be detected either by chemical analysis or by normal X-ray techniques. This investigation was therefore carried out, first, to devise a simple metallographic method for the identification of the tellurium or selenium phase coexisting with the chalcogenides and, second, to determine the distribution and specific location of the tellurium or selenium phase in the ingots. EXPERIMENTAL PROCEDURE The starting materials used for the alloy preparations were 99.999 pct pure bismuth, antimony, and tellurium and 99.997 pct pure selenium. The bismuth and antimony were obtained from Consolidated Mining and Smelting Co. of Canada Ltd., while the selenium and tellurium were obtained from Canadian Copper Refiners Ltd. The tellurium was purified further in the laboratory by zone refining. The elements were pulverized in a stainless-steel pestle and mortar. The amounts for the desired composition were weighed out each time on an analytical balance to make up a 100-g sample. Then the sample was introduced into a Vycor ampule (19 by 150 mm), pumped down to a vacuum of 10"5 Torr for 15 min, and sealed off. The ampule was then heated in a horizontal resistance furnace at 800" to 900°C for about 20 hr. During this period the assembly was rocked back and forth several times to ensure good mixing. At the end of the heating period, the ampule was quenched in cold water and then transferred to the zone-melting apparatus described in a previous publications to grow large-size aligned polycrystals. The background and ring-heater temperatures were adjusted to make the freezing solid-liquid interface slightly convex to the liquid. The recorded temperature gradient in the vicinity of the freezing solid-liquid interface was around 15°C per cm. The ampule was moved horizontally at a speed varying from 0.4 to 2 cm per hr so that the ring heater would cover the whole ingot length from end to end. A single zone-melting pass was used for the Bi-Te, Sb-Te, and Bi-Sb-Te ingots. Two passes in the forward and reverse directions were carried out for the Bi-Se and Bi-Se-Te ingots. Six passes in the forward and reverse directions were performed for the Bi-Sb-Se-Te ingot. The zone-melted ingots were found to contain several large crystals, with their basal planes (0001) approximately parallel to the growth axis. Samples of bismuth and antimony tellurides coated with a layer of tellurium, and bismuth selenide coated with a layer of selenium, were prepared for comparison in phase identification. These coatings were made by dropping a piece of the zone-melted ingot into some molten tellurium or selenium under argon atmosphere and allowing them to cool slowly to room temperature. The metallographic specimens were prepared by

Jan 1, 1969

HE purpose of this chapter is to present a general outline of the basic open-hearth process for the benefit of students, practicing open-hearth operators, and metallurgists who wish to review the subject. The discussion is limited to a description of the sequence and purpose of the operations, illustrated by data and examples. Subsequent chapters deal with more detailed and fundamental studies of the subject. The function of the basic open-hearth furnace is to convert various types of ferrous material into finished steel of given composition and quality. In comparison with other steelmaking methods, the basic open-hearth process is one of the most versa- tile, both from the standpoint of the raw materials that can be used and the types of steel that can be produced. The process can be considered as a sequence involving melting, refining, and deoxidation. With some types of liquid-metal charges, the melting stage is not present, but refining and deoxidation in varying degrees are fundamental features of the process. GENERAL DISCUSSION OF BASIC OPEN-HEARTH PROCESS The first consideration in open-hearth practice is the type of charge on which the operation is based. This consists of three components-fluxing, oxidizing, and metallic materials. Fluxes. In the basic process the fluxing material is primarily lime, added in the form of either limestone (CaC03) or burnt lime (CaO). This is supplemented by magnesia (MgO) and lime from the furnace bottom and banks. The function of these fluxes is to form a slag with the silica (SiO2) , manganese oxide (MnO), iron oxides (FeO and Fe2O3), and phosphorus oxide (P2O5) that are produced by the oxidation of varying amounts of the silicon, manganese, iron, and phosphorus in the charge during melting and refining. The slag, composed of the basic fluxes and the neutral and acid oxides, floats on top of the steel bath when the charge is melted. The composition of this slag depends on the amount of each slag-forming element present in the charge and on the extent of oxidation of these elements during the course

Jan 1, 1951

By L. W. Kempf, R. S. Archer

The binary aluminum-silicon alloys have certain characteristic advantages which are now well known, and these alloys have come into considerable use during the past several years.' Their field of application has been limited to a certain extent, however, by their low yield point and hardness, low endurance limit, and relatively poor machining characteristics. These properties are improved by the addition of copper, and the ternary aluminum-silicon-copper alloys constitute an important class. The addition of copper decreases the corrosion resistance of the aluminum-silicon alloys and increases specific gravity. Magnesium is a hardening addition which seems to have relatively little effect on corrosion resistance, and which, of course, reduces specific gravity. The object of the work described in this paper was the development of alloys and heat treatments for the production of sand castings and permanent-mold castings having substantially all the advantages of the binary aluminum-silicon alloys together with mechanical properties improved to a degree permitting wider application. Constitution of Alloys Magnesium and silicon combine in aluminum alloys as the compound Mg2Si, which forms a binary system with aluminum. In alloys containing an excess of silicon over that required to form the compound, solidification ends with the freezing at 1022' F. (550' C.) of a ternary eutectic of aluminum, Mg²Si, and silicon. Judging from the horizontal projection of the liquidus surface as given by Hanson and Gayler,² this ternary eut,ectic contains about 13 per cent. silicon and 6 per cent. magnesium. All of the alloys discussed here contain excess silicon, so it

Jan 1, 1931

By O. W. Simmons, L. W. Eastwood, C. M. Craighead

The results of a preliminary study of 113 ternary titanium-base alloys are described. The compositions investigated were as follows: 1. Ternary titanium-carbon alloys containing copper, silicon, vanadium, chromium, manganese, iron, or cobalt. 2. Ternary titanium-nitrogen alloys containing chromium. 3. Ternary titanium-chromium alloys containing additions of vanadium, molybdenum, tungsten, cobalt, or nickel. 4. Ternary titanium-manganese alloys containing additions of silicon, chromium, tungsten, or iron. Tensile properties, minimum bend radii, hardnesses, response to heat treatment and aging treatment, and phase relationships for these alloys were determined. THIS is the second in a series of papers describing some of the results of the exploratory work on titanium alloys being conducted at Battelle Memorial Institute for the Wright-Patterson Air Force Base. The work with the binary alloy systems has been described in a previous publication.' This paper describes ternary titanium-base alloys as follows: 1. Ternary titanium-carbon alloys containing copper, silicon, vanadium, chromium, manganese, iron, or cobalt. 2. Ternary titanium-nitrogen alloys containing chromium. 3. Ternary titanium-chromium alloys containing additions of vanadium, molybdenum, tungsten, cobalt, or nickel. 4. Ternary titanium-manganese alloys containing additions of silicon, chromium, tungsten, or iron. As the preparation and fabrication of the 0.5-Ib experimental titanium alloy ingots to 14-ga sheet, as well as the methods of testing used in this work, have been described in the first paper of this series, Titanium Binary Alloys, no further discussion of these techniques will be given. Ternary Alloys Containing Carbon The following alloys of titanium, containing carbon and one other metal, were investigated: 1. 0.25 pct carbon; 1, 2.5, and 5 pct copper. 2. 0.25 pct carbon; 1, 2, and 3 pct silicon. 3. 0.25 pct carbon; 1, 2.5, and 5 pct vanadium. 4. 0.25 pct carbon; 2.5, 3.5, 5, 10, and 15 pct chromium. 5. 0.5 pct carbon; 2.5, 3.5, and 5 pct chromium. 6. 0.25 pct carbon; 1, 1.75, 2.5, 3.5, 5, 7.5, and 10 pct manganese. 7. 0.5 pct carbon; 1.75, 2.5, 3.5, 5, 7.5, and 10 pct manganese. 8. 0.25 pct carbon; 0.25, 0.5, 1, and 2 pct iron. 9. 0.25 pct carbon; 1, 2, and 3 pct cobalt.

Jan 1, 1951

By Lynn B. Hales

The software systems which support the Pinto Valley Supervisory Control System are divided into three general categories. These are defined as the real-time operating system; a process data acquisition, reduction, and communication system; and a set of process-oriented systems which interface the operators and engineering staff to the process. The role of each of these three classes is reviewed. The software systems which provide reports, status displays, and trend graphs are discussed.

Jan 1, 1978

By G. E. Goodspeed

THE Cornucopia gold quartz veins form a parallel vein system traversing meta-morphic and granodioritic rocks. Field and petrographic evidence suggests that metasomatism has played an important role both in the emplacement of the grano-diorite and in the formation of the veins. Structurally the veins appear to be related to the major tectonic features of the Wallowa Mountains and to be narrow shear zones rather than filled fissures. Petrographic studies indicate a complex history of formation starting from initial alteration along fractures or joints followed by recurrent fracturing and a quartz-forming stage,-and closing with continued shearing and microbrecciation, which permitted the upward percolation of the later ore-forming solutions. The precipitation of ore minerals from these solutions formed ore shoots. Postmineral effects include the injection of Tertiary basaltic dikes, a slight amount of cross faulting, and some movement along the planes of the veins as well as oxidation. INTRODUCTION Cornucopia is in the southeastern part of the rugged Wallowa Moun-tains of northeastern Oregon. It was founded over 50 years ago following the discovery of its system of gold quartz veins. The major veins are roughly parallel and dip into the western side of Pine Valley, which drains the southern slope of the range. Previous operations had cut the upper portion of four major veins with two tunnels over 1000 ft. apart, when the present operating company drove a third tunnel, called the Coulter, at the level of the valley over 1000 ft. lower to intersect the most easterly major vein at over 6200 ft. from the portal.

Jan 1, 1939

By R. G. Wayland

SINCE the installation at Kropfmuehl, Bavaria, of a modern flotation concentrator in 1938, the flake and fine graphite from the Passau area can now be delivered in about any normal specified carbon content of any size range up to a flake averaging about 0.7 mm. The graphite finds a wide German and export market for crucible manufacture, pencil leads, dry cells and other uses. A controversy over the origin of the graphite deposits is being resolved in favor of syngenesis rather than epigenesis. The syngenetic theory is newly supported by the yet unpublished work of Hartmann of the Bavarian Geological Survey. Development work and exploration for graphite in the area may be changed in direction as the syngenetic theory is accepted. Crystalline graphite is produced in the area east of Passau near the junction of Germany, Austria and Czechoslovakia, as shown in Fig. 1. This is the only graphite area of importance in Germany, and Gra-phitwerk Kropfmuehl AG is the only operating firm in the area. The plant and mine are located at Kropfmuehl near Hauzenberg, Kreis Wegscheid, about 10 miles east of Passau. A narrow gage railway from the mine connects with the German Railway at Schaibing Bahnhof. The Pfaffenreuth mines date from about 1730. Until the early 20th century mining operations were carried out in a haphazard fashion. During World War I graphite mining and milling was increased, since it had to cover almost all of the crucible needs of the Central Powers. Between the wars some 11 mines were operated by two large and several small companies, but under the Nazis these were consolidated by 1938 into the Kropfmuehl enterprise. Kropfmuehl built a modern flotation mill to treat its own ores and small amounts of custom ores and tailings from the area. Since Graphitwerk Kropfmuehl AG was an I.G. Farbenindustry subsidiary, it has been under Military Government Property Control and probably will be sold to private German capital. Geology The country rock of the graphite area is part of the "kristallines Grundgebirge," the series of old gneissic and schistose rocks that constitutes the bed rock of most of the Bohemian basin and rims the Sudeten-land. The gneissic rocks of the graphite area are considered to have been metamorphosed during the Carboniferous period. They are bordered on the north by granite stocks and penetrated by numerous smaller granite and pegmatitic intrusive rocks, as shown in Fig. 1. The gneiss is classed as a micaceous, coarse-grained cordierite gneiss by most investigators. It is much metamorphosed by the granite, particularly in the north near the larger granite bodies. Interbedded in the gneiss are the graphite seams and lenses, and also beds and lenses of crystalline limestone containing disseminated graphite in noncommercial quantities. The gneiss, together with the included graphite and limestone seams and lenses, is cut and displaced by a number of granite sills of medium to fine grain and by a large number of diorite lamprophyre dikes and a few syenite-pegmatite dikes. The lamprophyre dikes are of various mineral compositions and textures, but many are banded and richly impregnated with pyrite; while the syenite-pegmatite dikes are coarse-grained with good crystals of titanite, pyroxene, uralite and other green amphiboles. Most investigators and the miners speak only of diorite and granite dikes cutting the graphite seams. The diorite dikes are later than the granite and some of the faulting, as is evident from Figs. 1 and 2. Individual graphite seams and lenses may be mined for thicknesses of several feet up to several scores of feet, and for distances of several hundred feet. The aggregate thickness of a series of some 20 seams of graphite, limestone and interbedded gneiss at Kropfmuehl is stratigraphically about 450 ft. Laterally, the graphite in a seam may pinch out or grade into crystalline limestone. Graphite crystals also are found disseminated in the gneiss itself, although in unmineable concentrations. The faults that cut the graphite seams carry graphite for some feet or tens of feet away from the seams, apparently mechanically. Similarily, the graphite lenses themselves often contain mechanically introduced inclusions of wall rock, probably from flowage during folding. Graphite crystals make up 10 to 30 pct of the fresh, mineable graphite lenses at Kropfmuehl, averaging about 20 to 25 pct after hand-sorting by the miners. In weathered lenses, the graphite concentration is said to be as high as 50 pct. The associated primary and hydrothermal minerals are dom-inantly feldspar and calcite, plus quartz, pyrrhotite, pyrite, biotite and occasional garnet, hornblende, sphalerite and galena. Associated secondary minerals include kaolin, nontronite, mangano-oxide-silicates (mog), adularia and chlorite. The superimposed suite of siliceous cementation minerals present consist largely of opal, chloropal, chalcedony, jasper, and hyalite. The kaolin is of special interest since it too was mined as early as 1730 and was used in the well-known Nymphenburg porcelain from 1756 on. The kaolin is derived from the gneiss and the syenite pegmatites. The crystals of graphite vary in size within a given seam, but in seams more than a mile away from the granite on the north the average crystal-linity is less coarse, lowering the commercial value. The lenses in the Kropfmuehl-Pfaffenreuth area are the most developed, and are the only ones with deep workings now accessible. Other similar crystalline graphite lenses are known from older workings at Habersdorf, Oberoetzdorf, Ficht, Diendorf, and

Jan 1, 1952

By J. J. Rutledge

I. Description of the Clinton Ores and Associated Rocks. The Clinton rocks in Stone valley comprise (1) thick layers of deep-red shale, (2) layers of reddish-gray shale interspersed with beds of sandstone and thin beds of extremely fossiliferous limestone, and (3) yellowish-gray shales alternating with thin layers of olive-colored shales. These layers of shale are all very thin and are at no point massive.' A bed of gray-white sandstone varying in thickness from 12 to 30 ft. occurs in the upper portions of the Clinton shales. This is called the ore sandstone, a name given to it by Rogers and adopted also by the Second Pennsylvania Geological Survey. It is the surest guide to the presence of the iron-ore bed, which lies below its lower edges at distances varying from 10 to 20 ft. This ore sandstone, in the valley, lies generally at very low inclinations, but often is locally subjected to considerable changes in dip. At its outcrop this ore sandstone weathers very easily and yields a rather sparse crop of stone, composed of dirty, iron-stained boulders. Upon the roads these boulders are quite well rounded, and bear fragments of crinoid stems and other fossil forms. The ore sandstone exhibits at many points evidences of former movements in this very great thickness of the shales, and as it is the only stratum in this series competent to transmit and record stresses due to structural movements, its evidence is of considerable importance in determining the occurrence of movements in times past.

Jan 1, 1910

By R. I. Jaffee, J. G. Dunleavy, W. Hodge, H. R. Ogden

IN a search for an improved conductor for use in field wire for the L. S. Army Signal Corps, an alloy of copper and silver was developed from which it was possible to obtain 29 B & S ga. strands with tensile strengths in excess of 160,000 psi combined with an electrical conductivity of over 70 pct IACS. Such a favorable combination of strength and electrical conductivity has not been reported previously in the rather extensive literature covering this subject. The properties obtained from various binary alloys of copper and silver, together with the method of fabrication of these alloys which has been developed to obtain the properties desired in fine wire strands, are discussed in this paper. LITERATURE The effect on the electrical conductivity of copper of the various elements in solid solution is shown in Fig I, taken from published data by J. O. Linde and others.' It will be noted that silver in solid solution depresses the electrical conductivity to a lesser extent than any other element for which data are given, and is followed rather closely by cadmium, and then by chromium. Zinc, which lies between cadmium and chromium, has so high a solid solubility in copper that the data for zinc are scarcely comparable to the data for the other two in the range covered. Not many data are available on the strain hardening of copper-rich Cu-Ag alloys. Corson2 reports a 3 pct Ag alloy properly cold worked and annealed to have 100,000 psi tensile strength and 90 pct IACS conductivity. On straight cold working, Hessenbruch3 reports 101.000 psi for a 5 pct Ag, 0.3 pct Be alloy, and 129,000 psi for a 30 pct Ag, 0.5 pct Be alloy. Here it would he expected that much of the strain hardening came from the silver content of the alloys. The copper-rich side of the Cu-Ag diagram, according to Stockdale,4 is shown in the upper part of Fig 2. The electrical conductivities for copper-silver alloys annealed at 750 and 350°C, taken from the work of Johansson and Linde,5 are shown in the lower part of Fig 2. The sloping line corresponds to the conductivity of solid solutions of silver in copper, and the horizontal offshoots correspond to the conductivity of the two-phase alloys in equilibrium at the two temperatures shown. The electrical conductivities are very high, even for the 750°C anneal. The potentiality for age hardening from supersaturated alpha copper solutions appears to be excellent from the solubility line, but Smith and Lindlief6 have shown that the response to age hardening of solution-annealed alpha alloys is not good. They found that the tensile strength of a 5 pct Ag alloy aged at various temperatures was not as great as in the quenched condition, even though, anomalously, the hardness increased from RB68 to RB78 by annealing for 4 hr at 400°C after a 750°C quench. Weist7 also found that the alloys increased in hardness

Jan 1, 1948

By L. H. Robinson

Triaxial compression tests have been performed to determine the strength characteristics of limestone, sand-stone and shale rocks subjected to controlled stress conditions. This control tuns exercised by varying the liquid pressures within and around a plastic-encased rock specimen. The pressure in the pores of the rock was varied throughout the range from atmospheric to 15,000 psig; the external pressure was changed over the same range with various positive pressure differences between is and the intertnal pressure. The data show that the rock strength increased and the mode of failure changed as the pressuire. surrounding the rock became greater than the pressure in the pores of the rock. These observations and the resu1ts of microbit drilling experiments indicate that the increased rock strength under pressure may bc an important effect in reducing drilling rare, but that other factors are probably of even greater importance. INTRODUCTION A large part of the research conductcd to reducc thc cost of drilling is directed toward improving present drilling technology and dcveloping new drilling methods. In spite of the fact that drilling is essentiaIly the act of making rocks fail, many details of the mechanism of failure are not known. It seems probable, therefore, that continuing studies of the fundamentals of rock failure can lay a foundation for future improvements in drilling technology. One of the factors which affects rock failure is the stress applied to the rock. This effect has been known for many years.'.'.; As an example, stress studics have been published by engineers' concerned with the strength characteristics of concrete in large dams. More recently, a number of investigators4-12 have explored the effects of stress on the strength of geologic formations and the geologic implications of their findings. During the last few years some research'" on rock strengths has also been conductcd in an attempt to gain additional insight into the factors which affeet rock drillability. In detcrmining the strength characteristics of rocks under different stress conditions, investigators have conventionally used triaxial compression equipment. wherein a jacketed rock cylinder is uniformly loaded from all directions and then compressed longitudinally. The results of this work have demonstrated that the mode of failure (brittle or malleable) is dependent upon the loading pressure, and that the strength of the rock increases as the loading pressure increases. These results clearly manifest that the stress, which is determined by the loading pressure, affects rock strength, and this implies that rocks under stress should be stronger and hence harder to drill. During the drilling of a porous rock the stress conditions are determined not only by the pressure surrounding the portion of the rock undergoing failure (confining pressure) but also by the pressure of the interstitial fluids within the rock (pore pressure). The importancc of both these pressures on the drilling rate of rocks has already been demonstrated by a number of investigators. Murray and Cunningham" found in microbit drilling expcriments that at constant pore pressures the drilling ratc decreased as the hydrostatic pressure surrounding an unjacketed, impermeable rock increased. Later Eckel" found that for jacketed Iimestone specimens the differcnce between hydrostatic (wellbore) pressure and formation (pore) pressure had an important effect on drilling rate. These observations of the effect of pressure on drilling rate emphasize that for drilling studies triaxial compression tests should be conducted under conditions of confining and pore pressure which simulate conditions underground. In the past, triaxial tests have been made under conditions which do not reproduce those underground. In particular, most of the tests on porous materials have keen made at varying confining pressures but with atmospheric pore pressures. In only one group of tests' was any data on the effect of pore pressurc reported, and these few data were on materials not representiltive of those encountered in drilling earth formations. The research described herein was initiated to deter-mine the importance of both internal pore pressure and confining pressure on failure characteristics of limestone. sandstone and shales. Triaxial loading equipment was used to obtain strength data at pressures up to 15,000 psig. An additional objective of this research was to apply these results to drilling rate studies by comparing them with the previously published drilling data of Murray and Cunningham" and of Eckel12. The work reported here is but one step in determining and evaluating the fundamental mechanisms which control drilling rate. Additional research is needed to clarify other aspects of the drilling process. The better

By Frederick Vickery

THE discovery of oil on the Goleta anticline has extended the petroliferous areas of California 18 miles west of the previous limit at Summerland and 35 miles south of the fields at Santa Maria. In each of these localities the oil is found in the Miocene-Pliocene strata, but as the oil at Goleta is found in the Sespe formation, which is generally considered as Oligocene or lowermost Miocene, the Goleta field extends the production of that horizon 52 miles west of South Mountain, the previous western outpost. Two horizons of high-gravity, paraffin-base oil have been found at shallow depths, and the exploratory well, Goleta No. 1, is now being drilled to test the productivity of an expected horizon in the Meganos formation. The Goleta structure is 12 miles west of the city of Santa Barbara and 2 miles north of the coast. Although it is within part of the old Spanish Rancho, Los Pueblos, it corresponds to T. 4 N., R. 29 W., S. B. B. and M., Santa Barbara county, California. The discovery well, Goleta No. 1 was drilled by the Miley Petroleum Ex-ploration Co. on the Tecolote ranch in the part of the Spanish grant corresponding to the sw. 1/4 of the nw. 1/4 of Section 3. Despite the apparent isolated position of the Goleta field, it is within the Ventura basin. The idea that the Ventura basin terminates at the ocean beach near the city of Ventura is neither sup-ported by the geologic structures nor the sequence of strata west of that city. This basin at the present time is known on the land as the Santa Clara valley and beneath the sea as the Santa Barbara channel. It extends westward to Point Concepcion. The Ventura basin, before the Miocene and Pliocene epochs of deformation, was much broader than at the present time. It is bounded by two lines of uplift, the Santa Ynez range on the north and the Santa Monica mountains with their extension, the Channel islands, on the south. Both of these ranges trend east and west. The Ventura basin and the mountains that bound it are part of a remark-able east-west orogenic unit, which interrupts the pre-vailingly northwest ranges along the Pacific Coast.

Jan 10, 1927

By R. Sporcic, P. J. Mudra

During the past year personnel of the Roof Control Research Group of the Bureau of Mines designed and developed encapsulated hydraulic cells for measuring pressure changes in coal in situ. Preliminary results from feasibility tests in progress in the laboratory and field indicate that the cells respond favorably to changes in pressures associated with a coal-mining environment. The ultimate objective is to use these cells to obtain engineering information relating to coal bump or coal outburst phenomena. Mining research has experienced a remarkable growth during the past decade and from all indications should surge forward at even a greater pace in the future. This increased interest in mining research has been brought about by the ever-multiplying number of technical problems being encountered by the mining industry in its effort to produce pay-dirt tonnages safely and economically from greater underground and surface pit depths. Among the various divisions in the field of mining research, the study of ground stress has received a large part of the overall attention. Numerous technical papers have been written with regard to ground stress conditions around mine openings and yet the total usable knowledge concerning this subject is extremely limited. Research teams around the world are endeavoring to bridge the gap between theoretical and laboratory approaches and the solution to design problems in the field. The problem of ground stress is not a new one for the coal mining industry. Operators in both eastern and western coal fields of the United States as well as in many foreign countries have long been plagued with a number of ground stress problems, one of which is commonly referred to as the coal-mine bump. This term or phenomenon has been aptly defined by earlier investigators as the violent and sudden failure of coal and adjacent rock. Direct results of such failures have been the loss of human lives and thou- sands upon thousands of dollars of sustained mine damages. In an effort to alleviate the magnitude and frequency of these failures, mine operators have employed and are presently employing various corrective techniques. These include: Inducing failure in heavily stressed areas by augering large-diameter holes into stressed pillars, using extensively yield-able steel arches in both long-term haulage and short-term face entries, backfilling unused or abandoned entries with mine waste to gain additional support, and using systematic pillar coal panel extraction techniques including mechanized longwall mining. The Health and Safety Activity of the Bureau of Mines has for a number of years contributed considerable time, funds, and talent in an effort to define better the ground stress problems associated with coal-mine bumps. As a part of this investigative program, in situ ground pressures are presently being studied in coal mines located in West Virginia and Utah. The description and development of the device being used to measure these pressures is the specific topic of this paper. CHOICE OF INSTRUMENTATION After consideration and evaluation of the various instruments and techniques that are being used by researchers in the field of rock mechanics to detetmine in situ stresses, a simple hydraulic system was selected for detailed investigation. Aside from simplicity, a hydraulic system is relatively inexpensive and also eliminates the need for electricity in its installation and operation. The hydraulic device referred to is, in essence, a simple unidirectional pressure-measuring cell. Hydraulic cells, which had been used for measurement of pressures in hard rock, were investigated but found not entirely suitable for use in coal, particularly since they involved (1) preparation and emplacement of cement grout at the test site, and (2) a waiting period before the cells became operational. At the outset, it was decided that certain design parameters be established. The cell should be simple and inexpensive, constructed of materials readily obtainable and easily built in the laboratory or field by unskilled labor. It was further decided that it was desirable to encapsulate the cell in a suitable mate-

Jan 1, 1963