By F. X. Spiegel, D. Bardos, Paul A. Beck

Ti6NileSi7)G is known to be cubic, with 116 atoms in the unit cell. In the present work four new G sili-cides were found with other transition elements and five G germanides. The titanium-group elements are very efficient in forming G phases. The vanadium -group elements are somewhat less efficient, and the chromium-group elements do not form any. Cobalt can replace nickel in most cases, but it is somewhat less efficient. Iron was not found to form any G phases. Germanium is somewhat less efficient than silicon. The (TiNiSi)E phase has been previously identified by Westbrook. However, its crystal structure has not been determined. In the present work the E phase was found to have an orthorhombic unit cell with lattice parameters a. = 7.02, bo = 5.18, co = 11.11A. A large number of other E phases were found at the same stoicheometric ratio in ternary systems of silicon and germanium with transition elements. Lattice parameters similar to those for TiNiSi were measured. The number of atoms per unit cell is estimated at 30 to 36. The vanadium-group elements are somewhat more efficient in forming the E phase than the titanium-group elements. Chromium-group elements were not found to form any E phases. Cobalt is somewhat less efficient than nickel, and iron is less efficient than cobalt. Germanium is not as efficient as silicon. ThE ternary silicide designated as G-phase was first identified by Beattie and versnyder1 and by Beattie and Hagel2 at the approximate composition TiNi2Si. Westbrook et al.' gave the composition as Ti2Ni7Sis. This phase was found to be fcc with a. = 11.201A and 116 atoms per unit cell. Beattie4 and more recently independently Hladishevskii, Kripyakevich, Kuzma, and Teslyuk5 were able to show that this structure is isotypic with MgeSi7CuLe and Th6Mn23. The latter structures had been determined by Florio, Rundle, and snow,' Nagorsen and Witte,7 and Bergman and Waugh.8 According to the crystal structure, Ti8Ni6Si7 may be considered as the ideal composition. The Russian investigators5 identified six additional ternary phases isotypic with Ti6Ni6Si7, in which titanium is replaced by Mn, V, Nb, Ta, Zr, and Hf, and one, namely MneNil6Ge7, in which germanium replaces silicon. They also found that Cr6Ni6Si7, which does not occur as a ternary phase, can be stabilized by replacing 1 at. pct of the Cr by V, Mn, or Ta. Another ternary silicide was found by Westbrook et al.3 at the composition TiNiSi, and it was designated by them as the E phase. The crystal structure of this phase has not been deter-

Jan 1, 1963

By R. D. Daniels, T. G. Oakwood

A study was made of the effects of small quantities of hydrogen on the mechanical properties of colum-bium. Tensile specimens, hydrogenated to concentrations of 20 to 200 ppm, were tested at temperatures of 300°, 191°, and 77°K. Although hydrogen was found to have little effect on the strength of columbium, the ductility of Cb-H alloys was found to be quite sensitive to both hydrogen concentration and temperature. At 300°K, an abrupt loss in ductility occurred at a critical hydrogen concentration, although some ductility was observed beyond the tolerance limit. A similar result was found at a lower hydrogen concentration at 191°K. At 77°K, however, a more gradual loss in ductility with increasing hydrogen concentration was observed. Hydrogenated columbium was thus observed to undergo a ductile-brittle-ductile transition. Metallographic examination of fractured specimens revealed extensive porosity at both 77° and300°K which was a distinct function of hydrogen content. At 191°K, although some secondary cracking was noted, the amount of observed porosity was minimal. These observations are interpreted in terms of hydrogen solubility and mobility as a function of temperature and in the role of hydrogen in promoting growth of microcracks. lHE effect of hydrogen on the mechanical properties of the refractory metals is not, at present, completely understood. A number of studies have shown these materials to be susceptible to hydrogen embrittlement. Roberts and Rogers1 have found that vanadium can be embrittled by hydrogen. It was further demonstrated that fracture undergoes a ductile-brittle-ductile transition as the temperature is lowered from 150° to -196°C; i.e., there is a ductility minimum observed at a certain temperature. The ductility is increased by either raising or lowering the temperature from this point. A more complete study by Eustice and Carlson2 on vanadium containing 10 to 800 ppm placed the ductility minimum at about -100°C with variations reportedly due to hydrogen content and strain rate. Ductility minima have also been found at certain temperatures for tantalum containing 7 ppm H3 and 140 ppm H.4 At hydrogen concentrations above 270 ppm, however, the ductility return at low temperatures was considerably reduced.4 In the case of columbium, some disagreement exists in the literature. Eustice and Carlson,5 Wilcox et al.,6 and Imgram et al.4 failed to find a ductility minimum although a composition-dependent ductile-brittle transition was observed. Hydrogen concentrations in these investigations were 20 ppm,5 1 to 30 ppm,6 and 200 to 390 ppm.4 However, Wood and Daniels7 observed a rather pronounced ductility minimum at hydrogen contents ranging from 19 to 252 ppm. Those theories of hydrogen embrittlement involving the precipitation of diatomic hydrogen which have been applies to ferrous metals8-12 do not seem to be applicable to the case of columbium and other exothermic occluders. Such theories propose that extensive crack formation and propagation occurs by the precipitation and expansion of diatomic hydrogen at internal voids and microcracks. However, photomicrographs of hydrogenated columbium do not show any evidence of damage introduced by the sorption and precipitation of diatomic hydrogen; rather, at high hydrogen concentrations, a hydrogen-rich second phase is precipitated.13'14 In addition, a number of these theories require the development of high hydrogen pressures at voids in the structure.8'10'12 This does not appear to be feasible in the concentration ranges discussed in the aforementioned paragraphs. The possible interaction of atomic hydrogen with microcracks resulting from dislocation pile-ups15,16 remains in doubt since pile-ups have not been observed in bcc metals17 including columbium.18 Wood and Daniels7 have put forth the possibility that a hydride precipitation could be responsible for crack nucleation in columbium. Work by Longson19 has shown that hydrogen embrittlement of columbium parallels the bulk solubility limit; i.e., as the solubility increases, for instance with temperature, the amount of hydrogen necessary to cause embrittlement also increases. Although a hydride precipitation appears attractive as a means of nucleating microcracks in columbium, what require more intensive study are the low-temperature anomalies which have been observed, i.e., the ductile-brittle-d'ictile transition characteristics. Also, the hydrogen concentrations where embrittlement occurs are often below the bulk solubility limits determined by Albrecht et al.13,14 and Walter and Chandler.20 This work is an attempt to determine more definitively the effects of concentration and temperature on the mechanical properties of dilute Cb-H alloys. EXPERIMENTAL PROCEDURE Ultrahigh-purity columbium rods, obtained from the Wah Chang Corp., were cold-reduced by rotary swaging. A chemical analysis is given in Table I. The material was cut into cylindrical blanks 1.50 ±0.005 in. long. Individual specimens were either given a stress relief anneal at 750°C or recrystal-lized at 1200°C. Resulting microstructures were either a "bamboo" structure characteristic of a wrought material or a recrystallized structure with a grain diameter of approximately 100 n. All heat treatments were carried out in a vacuum of 10-5 Torr or less.

Jan 1, 1969

By K. Osseo-Asare

The DIAGRAM computer program has been used to develop stability diagrams such as Eh-pH, log [CNI-pH, and log [Me]-pH for the systems Me-CN-H 0 where Me = Au, Ag, Fe, Zn, Cu, Ni, Co. More complex 2 diagrams involving sulfur- and arsenic-containing species are also presented. With the aid of these diagrams, a discussion is presented of the solution conditions (e.g. pH, [CN], [CNS], Eh) vhich influence gold and silver extraction in cyanide solutions. Special emphasis is given to the effects of ore minerals or calcination products, such as pyrrhotite, pyrite, arsenopyrite and hematite on gold-silver dissolution. Application of the stability diagrams to solution treatment operations such as cementation is also indicated.

Jan 1, 1984

THE Nominating Committee appointed at the Division meeting in October and consisting of Frank A. Herald, A. W. Peake, C. R. McCollom, Joseph Jensen, H. W. Camp, C. P. Watson, F. Julius Fohs, George Otis Smith, J. B. Umpleby, J. M. Lovejoy and A. W. Ambrose, have presented the following ticket for the year 1929: Chairman, Joseph B. Umpleby; associate chairman, A. C. Rubel; secretary-treasurer, R. Van A. Mills; vice-chairman for Economics, Warren A.. Sinshein~er; vice-chairman for Engineering Education, H. C. George; vice-chairman for Engineering Research, Harry H. Hill; vice-chairman for Production, C. P. Watson;vice-chairman for Refinery Engineering, A. D. David. For Production Engineering Charles V. Millikan. is named vicechairman, with ,Charles E. Beecher, Glenn D. Robertson and W. W. Scott as associate vice-chairmen. The Executive Committee named is to consist of Joseph B. Umpleby, chairman with A. W. Ambrose, Charles E. Beecher, A. D. David, Glenn D. Robertson, H. C. George, Harry H. Hill, John M. Lovejoy, Charles V. Millikan, R. Van A. Mills, Earl Oliver, A. W. Peake, A. C. Rubel, W. W. Scott, Warren A. Sinsheimer and .C. P. Watson, members. Ballots will be mailed to members of the Division.

Jan 1, 1928

By Walter Lawson

THE first plans were made in 1930 for the mining by open-pit methods of the low-grade disseminated ore body now known as the Morenci open pit. It was not until 1937, however, that final plans were completed and the decision reached to go ahead with the actual development. Many advances were made in open-pit mining equipment during that period of seven years, therefore the ways and means of attack actually used were very different from those originally contemplated. Diesel-operated bulldozers, big trucks, full-revolving electric shovels and electric churn drills constitute the major equipment finally purchased for this modern stripping operation. Neither the bulldozers nor the big trucks were considered in the early operating plans, for at that time bulldozers had not, been used in mining operations and the trucks as yet were undesigned. The full-revolving shovel and the churn drills were not new developments in open-pit equipment, but both had undergone remarkable manufacturing transition, emerging far more efficient and far more dependable than their predecessors. Even the ordinary drilling steel had been fundamentally changed. It was now threaded so that the dulled cutting bits could be detached and replaced, thus eliminating the costly transportation of long bars to the drill shop for resharpening. The decision to use trucks in the preliminary stripping operations was based on the desirability of this type of transportation to economi-cally prepare the pit for rail haulage, coupled with the success that the contractors had had with them on other big excavation jobs. There are at present no plans for the use of trucks beyond the preliminary work, inasmuch as rail haulage will give lower costs after roadbeds and benches are once established.

Jan 1, 1938

By W. Shockley

THIS lecture can best begin with a statement of the chief conclusion: The metallurgical industry will find profit in supporting fundamental research on dislocations. This support should be done both in their own laboratories and in universities. My lecture consists of an exposition of the basis for this conclusion. The experience on which I base it is drawn largely from two fields in solid state physics—one field is transistor electronics and the other is dislocation theory. At present the relationship of solid state physics to technology is different in these two fields. In electronics without question, the physics has led the technology. In metallurgy, on the other hand, the technology in the form of metallurgical art is far ahead of the fundamental science. In transistor electronics, physics has suggested and can still suggest previously unachieved combinations of matter that will have new and useful properties; that is, the physicist can make specific predictions. The physicist can also have some confidence that the predicted devices will actually come into existence in a matter of months or years and that they will live up to the predictions. In metallurgy, the physicist cannot to a comparable degree make predictions and have the same hope that they will lead to something new and valuable. There are a number of reasons for this difference. The first is simply historical. Transistor physics is young. It may be regarded as dating from the announcement of the transistor, in which case it is about four years old, or from the first real control of semiconductors as materials (this was accomplished largely by metallurgists, by the way) in which case it is about ten years old. Metallurgical art, on the other hand, is thousands of years old. There is no doubt that the advance of this art has been and will be hastened by a good fundamental understanding of the quantum theory of atomic phenomena. It, is too much to expect, however, that theory will soon catch up with the lead that practice has gained in a thousand years, and that theory will then point out specific pathways to better materials. It seems more probable that modern atomic theory will serve to interpret and organize information much as thermodynamics has done through phase diagrams. In this lecture, I shall emphasize an important feature common to both solid state electronics and to metallurgy. This common feature is the harmonizing principle that justifies discussing electronics and metallurgy as related topics in solid state physics. In both cases the important properties of the materials arise from imperfections. By imper- fections I mean deviations of the materials from perfect single crystals. The imperfections may be of many forms. From the point of view of utility they may be either good or bad, and a given type may be good or bad depending on circumstances. The technical material of my lecture will be divided into two parts. The first will be chiefly concerned with four types of imperfections in germanium crystals. The control of these imperfections makes possible the fabrication of useful electronic devices. A good example of such control is the junction transistor, which I shall discuss from this viewpoint later. The junction transistor, as some of you may have heard, can be used as an amplifier of electrical signals and in a number of respects surpasses what has hitherto been achieved with vacuum tubes. The second part of my technical material will be concerned with dislocations. For about fifteen years the theoretical physicist has had dislocations in mind as the most important kind of imperfection in metals. He has, however, until recently had experimental material of a highly speculative nature to back up his assertions. I am fortunate in the timing of this lecture to be able to describe some recent results that put dislocations on a far more definite basis than has been the case in the past. In fact there are now some experiments which reveal the characteristic properties of dislocations almost as clearly as experiments in transistor physics reveal the properties of holes and electrons, properties that I shall soon describe. It is this advance in the status of dislocations that emboldened me to make my initial assertion that the metallurgical industry will profit from supporting fundamental research on dislocations. Transistor Electronics In order to discuss imperfections in semiconductors, it is necessary to visualize a reference condition that may be regarded as perfect. In the cases of silicon and germanium, which find application in transistor electronics,' the perfect structure is the diamond structure shown in Fig. I. In this structure, each atom is surrounded by four neighbors with which it forms four covalent or electron-pair bonds. These bonds use all of the four valence electrons possessed by each of the silicon or germanium atoms. The electronic structure of the crystal is thus complete and perfect. A crystal of silicon or germanium with a perfect electron-pair bond structure would be an insulator, In order for electrical conduction to occur, it is necessary for imperfections to arise in the electronic structure. In this lecture, I shall discuss four possible imperfections whose symbols and relationships are indicated in Table I. We shall consider first, as an example, a crystal of silicon containing an arsenic atom as an impurity.

Jan 1, 1953

By S. C. Sun

Most previous work on sedimentation of coal 1 and mineral 2-3 suspensions has been conducted in graduated 1-liter glass cylinders of 6-cm diam. With this type of large container it is often difficult to see through the suspension and tedious to perform a large number of tests. Furthermore, the heavy glass walls and the graduation lines of glass cylinders cause internal and stray reflections, respectively. To obviate these difficulties, an Atlab Emulsion Viewer from Arthur H. Thomas Co. was adopted as an alternative apparatus. Equipment: The viewer," shown in Fig. 1, consists of: 1) a stainless steel frame rack holding 21 flat-bottom Nessler tubes or an ungraduated replica 1.64 cm ID and 1.80 cm OD, 2) a movable masked 150-w lumaline lamp behind the tubes, and 3) a scaled glass panel with 100 vertical divisions in front of the tubes. The tubes are snugly held by springs in slots formed by spacer bars, which also serve as shields to eliminate stray light. The lumaline lamp is mounted behind a slit in a movable housing so that it can be positioned behind the suspension to be examined. The lowest or 100-divi-sion line on the front glass plate is leveled with the upper side of the bottom of all tubes. The scaled portion of each tube, roughly 19 cm high and 40 ml in volume, is used to study coal and mineral suspensions. Procedure: The following procedure was used in many tests. A 1.6-gm sample of dry coal was mixed with 16 ml of distilled water in an ordinary test tube and allowed to stand for three days, with occasional shaking to insure thorough wetting of all particles. The slurry was transferred to a Nessler tube and diluted to 32 ml. The pH regulator and flocculating reagent were added, and the slurry was diluted to reach the uppermost or zero-division line. The tube was immediately stoppered and inverted downward and up again ten times during a period of 35 to 40 sec. The lumaline lamp was turned on during the inversion period. After inversion the tube was quickly returned to the viewer rack. The time elapsed for each 10-division drop of the demarcation line between solid and liquid was recorded by stopwatch until the 80-division line was reached in the zone of compression. Additional readings were taken at 15, 30, and 60 min after settling began. The clarity of the supernatent liquid was observed also. As the settling rate became considerably slower at the 75-division line, it was convenient at this time to start the next test in a separate Nessler tube. This was continued until the suspensions in any number of the 21 tubes were tested. An attempt was made to correlate the experimental results between the Nessler tube and a 1-liter glass cylinder. Table I shows that coal particles settle much faster in the cylinder than in the tube, which has a large wall effect.' The correction factor for the tube impedance is 1.662 2 0.145 at the 40-division line in the hindered settling zone, and 1.614 & 0.139 at the 75-division line in the compression zone. This rough correlation was established by dividing the pulp height of each container into 100 divisions and comparing the settling rates of the two containers at the same divisions. Tests were also performed to determine the accuracy of the viewer. The results, not presented, showed that error was within 10 pct.

Jan 1, 1960

NEW MEMBERS The following list comprises the names of those persons who became members during the period Oct. 10 to Nov. 10, 1914: Members ADDAMS, CHARLES EDWARD, Asst. Supt.. . Ray Consolidated Copper Co., Ray, Ariz. ALEXANDER, HARRY H., Asst. Mgr. and Mgr., American Smelting & Refining Co., Maurer, N. J. ALLING, MARK,N., Min Engr Downieville, Sierra Co., Cal. ANDERSON, LESLIE DOUGLASS, Supt U. S. Smelting Co., Midvale, Utah. ATKINS, WILLIAM, JR., Sec'y Kingwood Coal Co., Howesville, W. Va. BLAKE, TRUE WALTER, Min. Engr Rombauer Coal Co., Novinger, Mo. BRACKETT, GEORGE SYLVESTER, Supt... Pittsvein Coal Co., Flemington, W. Va. BRAINERD, HOWARD STANFORD, Met Ingersoll-Rand Co., Phillipsburg, N. J. BROWN, THOMAS J., Genl. Supt., Nova Scotia Steel & Coal Co., Sydney Mines, N. S., Canada.

Jan 12, 1914

By A. H. Geisler, F. Keller

Some of the important changes that take lace in the structure of aluminum alloys are largely submicroscopic in character. This is especially true of the changes that accompany age-hardening and recrys-tallization. Although improved metal-lographic practices have been helpful in indicating some of these changes indirectly, results are limited by the resolving power of optical microscope lenses. The electron microscope, however, provides a new and important means for investigating the fine structure of metals in a range not possible heretofore. It is anticipated that this microscope will yield new and useful information to metallurgists when suitable techniques are developed to utilize its very high resolving power. Several unique methods have been devised to permit the examination of the structure of opaque samples by the electron microscope. These are all based 011 the principle of producing a very thin film that represents the prepared surface of the opaque metal sample, which can be examined in the transmission microscope; however, the available methods fall into three categories, depending on the manner in which the film is obtained. With the oxide-film method developed by Mah13-l7 a very thin surface layer of the metallographic sample is converted into oxide by a thermal, chcmical or anodic treatment. .After removal from the metal sample by one of the special techniques described by Evans,l9 this oxide film is examined in the electron microscope, and is found to portray the structure of the original metal surface. Films formed on aluminum,8,l7 nicke1,7 iron3,8,9 and a nickel-beryllium alloyl1 by heating; films formed on iron8,9 by chemical action; and films formed on aluminum3-'" by anodic oxidation, have been examined. The other two are more recent methods developed principally in this country; they consist in making the thin film in the form of a mold or replica of the surface contour of an etched sample. With the negative replica method the thin film is made directly on the sample; with the positive replica method it is made on a negative reproduction of the sample. With both methods, variations in the contour of the metal sample, caused mainly by etching, produce variations in the thickness of the surface replica. Because of the direct dependence of the amount of scattering of the illuminating electrons upon the thickness of the film penetrated, only the variations in thickness of the replica are responsible for tones in the electron image. Negative replicas are made by forming a thin film of some suitable material directly on the polished and etched metal sample, and derive their name from the fact that after removal from the sample they have the high and low points in the sample reversed, as shown in Fig. I. Nega-

Jan 1, 1944

By F. Keller, A. H. Geisler

Some of the important changes that take lace in the structure of aluminum alloys are largely submicroscopic in character. This is especially true of the changes that accompany age-hardening and recrys-tallization. Although improved metal-lographic practices have been helpful in indicating some of these changes indirectly, results are limited by the resolving power of optical microscope lenses. The electron microscope, however, provides a new and important means for investigating the fine structure of metals in a range not possible heretofore. It is anticipated that this microscope will yield new and useful information to metallurgists when suitable techniques are developed to utilize its very high resolving power. Several unique methods have been devised to permit the examination of the structure of opaque samples by the electron microscope. These are all based 011 the principle of producing a very thin film that represents the prepared surface of the opaque metal sample, which can be examined in the transmission microscope; however, the available methods fall into three categories, depending on the manner in which the film is obtained. With the oxide-film method developed by Mah13-l7 a very thin surface layer of the metallographic sample is converted into oxide by a thermal, chcmical or anodic treatment. .After removal from the metal sample by one of the special techniques described by Evans,l9 this oxide film is examined in the electron microscope, and is found to portray the structure of the original metal surface. Films formed on aluminum,8,l7 nicke1,7 iron3,8,9 and a nickel-beryllium alloyl1 by heating; films formed on iron8,9 by chemical action; and films formed on aluminum3-'" by anodic oxidation, have been examined. The other two are more recent methods developed principally in this country; they consist in making the thin film in the form of a mold or replica of the surface contour of an etched sample. With the negative replica method the thin film is made directly on the sample; with the positive replica method it is made on a negative reproduction of the sample. With both methods, variations in the contour of the metal sample, caused mainly by etching, produce variations in the thickness of the surface replica. Because of the direct dependence of the amount of scattering of the illuminating electrons upon the thickness of the film penetrated, only the variations in thickness of the replica are responsible for tones in the electron image. Negative replicas are made by forming a thin film of some suitable material directly on the polished and etched metal sample, and derive their name from the fact that after removal from the sample they have the high and low points in the sample reversed, as shown in Fig. I. Nega-

Jan 1, 1944

By Carl H. Schmuck

The terms "cable bolting," "extended ground support," and "grouted cable" are synonymous, and they have been popping up with much more regularity in the mining engineer s vocabulary. In simplest terms, lengths of u itensioned cable up to 18.3 m (60 ft) are grouted in drill holes prior to mining. This permits radical departures from mining practices that rely on conventional rock reinforcement. For example, by placing a pattern of cable bolts in the back of an open stope, ore can be mined in successive slices. After each slice is taken the protruding cable; are simply cut off and mining proceeds. When about 4.6 m (15 ft) of reinforced back remains, a crew places a new par tern of cable bolts in the ore.

Jan 12, 1979

THE decision of the lower court (United States District Court for the Southern District of New York) in the suit of the Dwight & Lloyd Sintering Co., vs. John E. Greenawalt has been affirmed by the United States Circuit Court of Appeals for the Second Circuit. In the original suit, infringement of seven patents was alleged, these covering the process of producing a sinter .out of finely pulverized metalliferous ores as practised in shallow pans operating intermittently in distinction to the Dwight 6: Lloyd continuous machine. The court found that the long delay in bringing suit precluded any recovery of profits from the defendant under the basic down-draft sintering patent, although Dwight & Lloyd are recognized as the inventors of this' contribution to the art and its .importance is acknowledged.

Jan 1, 1928

By Charles H. Thurman

THE data given herein were first included in a paper read before San Francisco Section, A.I.M.E., in October 1940, and are applicable to conditions existing until the gold-dredging industry was temporarily suspended by Order L-208 of the War Production Board in the fall of 1942. There is no doubt that gold dredging will be resumed at some future time, and on a scale equivalent to that of the recent past, but the cost data given herein will be affected to some extent by conditions existing at that time, and by labor rates and prices for materials then prevailing. DRAGLINE VS. BUCKET-LINE Dragline dredges should not be considered for mining large areas of low-grade placer gravel. In such deposits a dragline operator with a 5-cu. yd. dragline would be doing well to maintain an operating cost of 6¢ per cu. yd., while a bucket-line dredge with buckets no smaller than 7 cu. ft. each could be operated for less than 4¢ per cu. yd. By operating costs, I mean only field charges such as direct operating and overhead, which includes pay roll, power or fuel, repairs and maintenance, insurance, land clearing and general expenses, but not including such items as prospecting, depletion, depreciation of equipment, State Franchise Tax, or Federal Income Tax. It is not to be inferred that a dragline dredge cannot make a profit in small low-grade deposits, where the extent of a given property is too small to justify the use of the more costly bucket-line dredge. Consider small deposits of 10¢ gravel. It is obvious that a deposit of 5,000,000 cu. yd. of such gravel could not be mined profitably with a new, 7-cu. ft. bucket-line dredge, costing upward of $250,000, and with operation costs at 4¢ per cu. yd., paying for land or royalties out of earnings; nor could a new combination 5-cu. yd. dragline and washing plant, worth upward of $125,000 and working at 6¢ per cu. yd., make a profit. These comparisons are made because the hourly capacity of both types of dredges is nearly the same. The bucket-line dredge averages 93 per cent operating time in 24 hr., as against about 80 per cent or less for the dragline dredge. These percentages of operating time are important factors in making a comparison of this kind. The bucket-line dredge has greater efficiency in cleaning soft bedrock, usually characteristic of dredging deposits, and a 7-cu. ft. bucket-line dredge can be efficient to a total digging depth of 80 ft. (65 ft. below water, 15 ft. above). A 5-cu. yd. dragline dredge is limited to about 30 ft. of efficient digging depth, 5 ft. of which could be above water. In small areas of gravel not over 30 ft. deep, a 5-cu. yd. dragline dredge could make a profit where a bucket-line dredge could not do so. As an example: compare the dredging of 3,000,000 cu. yd. of 10¢ gravel 28 ft. deep with bucket line, costing 4¢ per cu. yd., and with a 5-cu. yd. dragline dredge operating at 6¢ per cu. yd. Because of small yardage, new equipment is not warranted, therefore we can assume that the dredges of both types are used equipment, fully depreciated. Dismantling, mov-

Jan 1, 1945

By Charles H. Thurman

The data given herein were first included in a paper read before San Francisco Section, A.I.M.E., in October 1940, and are applicable to conditions existing until the gold-dredging industry was temporarily suspended by Order L-208 of the War Production Board in the fall of 1942. There is no doubt that gold dredging will be resumed at some future time, and on a scale equivalent to that of the recent past, but the cost data given herein will be affected to some extent by conditions existing at that time, and by labor rates and prices for materials then prevailing. Dragline vs. Bucket-line Dragline dredges should not be considered for mining large areas of low-grade placer gravel. In such deposits a dragline operator with a 5-cu. yd. dragline would be doing well to maintain an operating cost of 6¢ per cu. yd., while a bucket-line dredge with buckets no smaller than 7 cu. ft. each could be operated for less than 4¢ per cu. yd. By operating costs, I mean only field charges such as direct operating and overhead, which includes pay roll, power or fuel, repairs and maintenance, insurance, land clearing and general expenses, but not including such items as prospecting, depletion, depreciation of equipment, State Franchise Tax, or Federal Income Tax. It is not to be inferred that a dragline dredge cannot make a profit in small low-grade deposits, where the extent of a given property is too small to justify the use of the more costly bucket-line dredge. Consider small deposits of 106 gravel. It is obvious that a deposit of 5,000,000 cu. yd. of such gravel could not be mined profitably with a new 7-cu. ft, bucket-line dredge, costing upward of $250,000, and in operation costs at 4¢ per cu. yd., paying for land or royalties out of earnings; nor could a new combination 5-cu. yd. dragline and washing plant, worth upward of $125,000 and working at 6¢ Per cu. yd., make a profit. These comparisons are made because the hourly capacity of both types of dredges is nearly the same. The bucket-line dredge averages 93 per cent operating time in 24 hr., as against about 80 per cent or less for the dragline dredge. These Percentages of operating time are important factors in making a comparison of this kind- The bucket-line dredge has greater efficiency in cleaning soft bedrock, usually characteristic of dredging deposits, and a 7-cu. ft. bucket-line dredge can be efficient to a total digging depth of 80 ft- (65 ft. below water, 15 ft. above). A 5-cu. Yd. dragline dredge is limited to about 30 ft. of efficient digging depth, 5 ft. of which could be above water. In small areas of gravel not over 30 ft. deep, a 5-cu. yd. dragline dredge could make a profit where a bucket-line dredge could not do so. As an example: compare the dredging of 3,000,000 cu. yd. of 10 gravel 28 ft. deep with bucket line, costin 4¢ Per cu. yd., and with a 5-cu. yd. dragline dredge operating at 6¢ Per cu. yd. Because of small yardage, new equipment is not warranted, therefore we can assume that the dredges of both types are used equip-ment, fully depreciated. Dismantling, mov-

Jan 1, 1946

By C. A. Hartnagel, D. H. Newland

Most of the petroleum produced in New York State is obtained by flooding; that is, water drive. No important oil fields have been developed during the past 30 years, nor does there seem much hope that the productive oil areas will be substantially enlarged in the future. There is some prospect that additional supplies may be obtained by deeper drilling, but deep tests for gas to the Oriskany sandstone in some of the oil-producing areas have been without results so far as any discoveries of oil are concerned. Although the flooding method had been made legal in 1919, and some floods had been in operation previous to 1921, that year marks the beginning of a rapid increase in oil production by the new method. The flush production of oil in New York was in 1882, shortly after the discovery of the Richburg pool in Allegany County. The oil production in that year amounted to 6,685,000 bbl. The 1937 production of 5,478,000 bbl. was the largest since the flush production of 55 years ago. The effectiveness of water-flooding for increasing oil production from the old New York fields is shown in Table 1. Table 1.—Production of Oil in New York since 1921 Year Barrels Year Barrela 1921 988,000 1929 3,377,000 1922 1,000,000 1930 3,647,000 1923 1,250,000 1931 3,363,000 1924 1,440,000 1932 3,508,000 1925 1,695,000 1933 3,181,000 1926 2,242,000 1934 3,804,000 1927 2,603,000 1935 4,236,000 1928 3,377,000 1936 4,633,000 1937 5,478,000 The area of the New York oil fields is about 60,000 acres. It has been estimated that not over one-fourth of the area is being flooded. Very little of flooded territory has ceased to produce. Some leases flooded by the early, less scientific methods are being again subjected to the water

Jan 1, 1938

By Boris J. Kochanowsky

In a mobile crushing unit system trucks are replaced by a conveyor, which results in a continuous, almost fully automated operation with all its attendant advantages. Because of new designs for large mobile crushing units that have been placed on the market, the use of these plants has increased significantly during the last three years. Gains in productivity and reductions in costs are vital to every mine operator, and the shovel-crusher-conveyor system is a powerful tool with which to achieve this goal. New Designs Increase Throughput While Reducing Size The basic concept of the shovel-crusher-conveyor scheme of operations is simple and sound, with the result that domestic operators are showing a growing interest in its application. A number of operators have been using small mobile crushing plants for several years, but large operators, in spite of considerable interest, have not been able to use this system because no mobile crusher capable of crushing 1000-2000 tph of rock loaded by a large shovel (6-12 cu yd) has been available. A suitable crusher must accept rock of the size handled by these large shovels, be simple in design, easily maneuverable, remotely controllable, and have price and maintenance costs not much higher than those for stationary crusher installations.

Jan 9, 1968

By T. L. Joseph

IN connection with its investigations of the blast'-furnace process, the Bureau of Mines, in coöperation with the Minnesota School of Mines Experiment Station, developed a 6-ton experimental furnace. Such a furnace was needed to determine the feasibility of producing ferromanganese from Minnesota manganiferous iron ores, a problem of national importance because of the present need for manganese in the steel industry and our small reserves of ferro-grade ores. Furnace operators are reluctant to use new or untried raw materials or to make decided innovations in practice on account of the financial hazard of experimenting with full-scale equipment. A small furnace which can be operated at a relatively low cost is particularly adapted for testing new, raw materials and for determining the feasibility of decided innovations in practice. Laboratory experiments, plus whatever information may be available, are valuable but often do not indicate the net result of changes in an operation involving a large number of interrelated variables. From time to time the coöperation of the Bureau of Mines is solicited in connection with problems involving departures from normal procedure. Under these circumstances some sort of a practical demonstration is a desirable forerunner to full-scale operations which appear feasible after small-scale tests.

Jan 1, 1928

By Georges Fleming

The new burden preparation plant of ARBED Luxembourg, Belval- Works, which comprises 2 large sinter strands, is equipped with a process computer connected to a comprehensive process control system. The main jobs done by the computer are the control of the raw mix composition, and thus the monitoring of the stacking of the piles at the bed-blending plant, and the optimization of the sintering process. Among the optimization criteria, quality is considered as the most important. The sinter quality, characterized by the mechanical strength and the state of oxidation, is controlled automatically. The control system which we have dev loped is highly reliable; as a result, the standard deviation of Fe++, for the control of bivalent iron, has been narrowed to 0,5 % and the standard deviation of the IS0 + 6, 3 mm index, for the control of the mechanical strength, has been kept within 1 %. Thanks to these results, the combined savings in fuel consumption at the sinter plant and at the blast furnaces have covered the total costs of the optimization project in 2 years. By applying automatic control, the optimum driving range of the sinter plant has been defined and these new guidelines are used for monitoring the sinter production.

Jan 1, 1977

By O. N. Carlson, D. G. Alexander

THE hardness anisotropy of metals and alloys has been of increasing interest in recent years but silicon ferrite,1 niobium,2 and tungsten3,4 are the only bcc metals about which this type of information has been reported. This investigation was carried out on vanadium and chromium single crystals in an effort to determine to what degree the hardness variations observed in these metals are due to orientation effects and to compare their behavior with other bcc metals. In earlier work the authors had observed a small angular dependence in the Diamond Pyramid Hardness of single crystalline vanadium on the (100) plane but no anisotropic effects were noted on either the (110) or (111) planes. At the suggestion of R. G. wheeler5 it was decided to investigate this effect in greater detail using the more asymmetric Knoop indentor. The vanadium metal used in the study was prepared by the aluminothermic reduction of V2O5 followed by electron beam melting.6 The principal analyzed impurities were 230 ppm C, 230 ppm O, 65 ppm N, 90 pprn Al, Cr not detected, 50 ppm Fe, 60 ppm Ni, and 200 ppm Si. The chromium was an iodide-refined product obtained from the Chromalloy Corporation. Analysis of this material showed the following amounts of impurities present: 10 ppm C, 9 ppm O, 2 ppm N, 0.4 ppm H, 3 ppm Al, 2 ppm Ca, 2 ppm Cu, 20 ppm Fe, 1 ppm Mg, 0.3 ppm Mn, 1 ppm Mo, 3 ppm Ni, 10 ppm Si, and 1 ppm V. Single crystals of both metals about 1 cm in diam and 10 cm in length were grown by an arc-zone melt- ing technique.7 The chromium crystal was annealed at 1600°C for 6 hr in a purified argon atmosphere to remove any strains or inhomogeneities, but the vanadium was tested in the as-grown condition. The crystals were oriented by the Laue back-reflection method and then sectioned with a spark cutter into individual specimens with a (loo), (110), or (111) plane parallel to the crystal surface. They were mounted in Lucite and carefully ground to a flat surface. The vanadium specimens were then electropolished in a 6 pct perchloric acid-methanol mixture while the chromium specimens were mechanically polished on a Syntron vibratory polisher using an alumina abrasive. The orientation of each crystal was then rechecked by the back-reflection X-ray method. All of them were found to lie within 2 deg of the desired orientation with the exception of the (110)-Oriented chromium crystal which was within 4 deg. Microhardness impressions were taken at 10 deg intervals from the common (110) direction by rotating the crystal in the plane of the crystal surface. A Knoop indentor was used with a 400-g load on the vanadium crystals and an 800-g load on the chromium. The hardness values are averages of 6 impressions and standard deviations were calculated for each set of data. The values reported for the (111) plane of vanadium are based on from 10 to 15 measurements for each point. The microhardness results for vanadium and chromium are plotted as a function of the angular rotation of the long axis of a Knoop indentor from the (110)

Jan 1, 1970

By AIME

BORN in 1899, in Bridgeport, Conn., E. A. Anderson grew up in a center of the nonferrous metal industry. Perhaps that had something to do with his selection of mining as a career while an undergraduate in Yale. After securing his Ph.B. in mining he worked for a year at Handy & Harman. By this time physical metallurgy had supplanted his interest in mining and he entered the Yale graduate school where he secured his M.S. degree in metallography under C. H. Mathewson. After completing his graduate work he entered the employ of The New Jersey Zinc Co. in their research division where he has remained ever since. The transition from graduate study to industry involved no disruption of technical interests. Academic research relating to the zinc-aluminum alloys, then coming into use for die-casting, was followed by extensive and productive industrial research in the perfection and commercialization of these alloys. Research on rolled zinc and rolled zinc alloys, corrosion and stress corrosion, dry cells, electroplating on zinc, and electrodeposition of zinc followed in overlapping succession as time passed.

Jan 1, 1947