By M. Muskat

A theory has been developed describing the behavior of wells and reservoirs producing by the action of bottom water drives. It is assumed that the pressures are maintained above the bubble point, and that the permeability to viscosity ratio of the water in the flooded zone is the same as for the oil in the oil-saturated pay. Accordingly, the treatment is based on the homogeneous fluid potential theory. The effect of the difference in density between the oil and water is neglected. .4fter deriving the proper potential distrihutions, the nature of the rise of the water-oil interface below the producing wells is calculated. The primary clean-oil-production phase is expressed in terms of the displacement efficiency, defined as the fraction of the pay flooded out by the rising water table at tlle time of first water entry. The variation of this displacement efficiency is calculated as a function of the well spacing, pay thickness, the ratio of the horizontal to vertical permeability, and the well penetration. The important parameter, other than the well penetration, is found to be the ratio of the well separation to the thickness of the oil pay multiplied by the square root of the ratio of vertical to horizontal permeability. It was found that the displacement efficiency continually decreases as this parameter increases, and for values of the latter >3.5, the efficiency varies inversely as the square of the parameter. It also increases with decreasing well penetration. Perhaps the most striking result of this phase of the analysis is the conclusion that in order to explain the delay in entry of water in wells producing by bottom water drives for periods longer than a few days normal production, with drawdowns large compared with the differential density head between the oil and water, it is necessary to assume that the vertical permeability is a very low fraction of the horizontal permeability. An analysis is also given of the production history after the water has broken through, on the assumption that the production mechanism and details of the flow distribution continue to be the same as during the phase of clean-oil production. As is to be expected, it is found that the water cut will increase at an accelerated rate as production proceeds. However, the initial differences between systems of different well penetrations or well spacings with respect to the total clean-oil production gradually decrease in terms of the variation of the water-oil ratio with cumulative production. In particular, by the time the water-oil ratio has reached values of the order of 5 or greater the cumulative recoveries will generally differ much less among various producing systems than their corresponding clean-oil recoveries. Introduction On the basis of elementary geological principles, one may classify effective water-drive fields in two groups. In the first, the entry of water into the oil-producing formation may be characterized as an edge-water encroachment. This term is used to suggest that the motion of the water proceeds largely in a direction parallel to the planes of stratification. This type of water intrusion occurs usually in thin producing zones and in strata lying along structural flanks of appreciable dip. In the second group—"bottom water-drive" fields—the water-oil interface lies in a plane of zero or slight inclination to the

Jan 1, 1947

By M. Muskat

A theory has been developed describing the behavior of wells and reservoirs producing by the action of bottom water drives. It is assumed that the pressures are maintained above the bubble point, and that the permeability to viscosity ratio of the water in the flooded zone is the same as for the oil in the oil-saturated pay. Accordingly, the treatment is based on the homogeneous fluid potential theory. The effect of the difference in density between the oil and water is neglected. .4fter deriving the proper potential distrihutions, the nature of the rise of the water-oil interface below the producing wells is calculated. The primary clean-oil-production phase is expressed in terms of the displacement efficiency, defined as the fraction of the pay flooded out by the rising water table at tlle time of first water entry. The variation of this displacement efficiency is calculated as a function of the well spacing, pay thickness, the ratio of the horizontal to vertical permeability, and the well penetration. The important parameter, other than the well penetration, is found to be the ratio of the well separation to the thickness of the oil pay multiplied by the square root of the ratio of vertical to horizontal permeability. It was found that the displacement efficiency continually decreases as this parameter increases, and for values of the latter >3.5, the efficiency varies inversely as the square of the parameter. It also increases with decreasing well penetration. Perhaps the most striking result of this phase of the analysis is the conclusion that in order to explain the delay in entry of water in wells producing by bottom water drives for periods longer than a few days normal production, with drawdowns large compared with the differential density head between the oil and water, it is necessary to assume that the vertical permeability is a very low fraction of the horizontal permeability. An analysis is also given of the production history after the water has broken through, on the assumption that the production mechanism and details of the flow distribution continue to be the same as during the phase of clean-oil production. As is to be expected, it is found that the water cut will increase at an accelerated rate as production proceeds. However, the initial differences between systems of different well penetrations or well spacings with respect to the total clean-oil production gradually decrease in terms of the variation of the water-oil ratio with cumulative production. In particular, by the time the water-oil ratio has reached values of the order of 5 or greater the cumulative recoveries will generally differ much less among various producing systems than their corresponding clean-oil recoveries. Introduction On the basis of elementary geological principles, one may classify effective water-drive fields in two groups. In the first, the entry of water into the oil-producing formation may be characterized as an edge-water encroachment. This term is used to suggest that the motion of the water proceeds largely in a direction parallel to the planes of stratification. This type of water intrusion occurs usually in thin producing zones and in strata lying along structural flanks of appreciable dip. In the second group—"bottom water-drive" fields—the water-oil interface lies in a plane of zero or slight inclination to the

Jan 1, 1947

By E. A. Anderson, P. W. Ramsey, E. J. Boyle

Only a few zinc-rich alloys are in commercial use today, and these depend largely upon solid solution effects for their desirable properties. Typical examples are rolled alloys containing about 1 Per cent of copper, with Or without additions of elements such as magnesium, and die-casting alloys containing about 4 Per cent of aluminum with small amounts of magnesium and sometimes copper." A number of elements are capable of forming alloys with zinc, Which do not enter into solid solution except in limited degree. The Present Paper considers One such system, zinc-titanium, in which alloys having potentially useful properties in the rolled form were found. Zinc-titanium System The zinc-rich portion of the zinc-titanium diagram, as determined by standard methods in this laboratory,3 is shown in Fig. I. The portion of the diagram of significance in the present work extends from 0 to about 0.5 per cent titanium. Gebhardt4 places the eutectic at 0.45 per cent, but the evidence in favor 01 the composition given in Fig. I is considerable. The solid solubility of titanium in zinc is very low indeed and possibly places these alloys in a somewhat different category from the commercial alloys previously mentioned. Alloy Preparation All of the alloys used in this work were prepared with titanium metal of 98.9 per cent purity. In most cases high-purity zinc (99.99 per cent) was used but sufficient work was done later to show that zinc of about high-grade composition would yield approximately equal results. Best practice in alloy manufacture seemed to be to prepare a zinc-titanium hardener by adding about 4 per cent of titanium metal to molten zinc and holding under a boric acid cover, with frequent stirrings, at 750°C, until the titanium had dissolved. The desired titanium content could readily be obtained in the final alloy by adding the calculated amount 01 this hardener. The alloys proved to be quite stable in composition, unless overheated, and, with reasonable temperature control, required no cover or flux to prevent loss of titanium content by oxidatioll, Hot-rollig Tests Three alloys containing, by analysis, 0.05, 0.12, and 0.23 per cent titanium were selected for preliminary study. Slab cross sections a a marked grain refinement* (Fig. 2) in the two alloys of highest titanium content. Cast unalloyed zinc has a columnar grain structure similar to that shown for the alloy of lowest titanium content but without the scatter of small equiaxed grains at the center.

Jan 1, 1944

By P. W. Ramsey, E. J. Boyle, E. A. Anderson

Only a few zinc-rich alloys are in commercial use today, and these depend largely upon solid solution effects for their desirable properties. Typical examples are rolled alloys containing about 1 Per cent of copper, with Or without additions of elements such as magnesium, and die-casting alloys containing about 4 Per cent of aluminum with small amounts of magnesium and sometimes copper." A number of elements are capable of forming alloys with zinc, Which do not enter into solid solution except in limited degree. The Present Paper considers One such system, zinc-titanium, in which alloys having potentially useful properties in the rolled form were found. Zinc-titanium System The zinc-rich portion of the zinc-titanium diagram, as determined by standard methods in this laboratory,3 is shown in Fig. I. The portion of the diagram of significance in the present work extends from 0 to about 0.5 per cent titanium. Gebhardt4 places the eutectic at 0.45 per cent, but the evidence in favor 01 the composition given in Fig. I is considerable. The solid solubility of titanium in zinc is very low indeed and possibly places these alloys in a somewhat different category from the commercial alloys previously mentioned. Alloy Preparation All of the alloys used in this work were prepared with titanium metal of 98.9 per cent purity. In most cases high-purity zinc (99.99 per cent) was used but sufficient work was done later to show that zinc of about high-grade composition would yield approximately equal results. Best practice in alloy manufacture seemed to be to prepare a zinc-titanium hardener by adding about 4 per cent of titanium metal to molten zinc and holding under a boric acid cover, with frequent stirrings, at 750°C, until the titanium had dissolved. The desired titanium content could readily be obtained in the final alloy by adding the calculated amount 01 this hardener. The alloys proved to be quite stable in composition, unless overheated, and, with reasonable temperature control, required no cover or flux to prevent loss of titanium content by oxidatioll, Hot-rollig Tests Three alloys containing, by analysis, 0.05, 0.12, and 0.23 per cent titanium were selected for preliminary study. Slab cross sections a a marked grain refinement* (Fig. 2) in the two alloys of highest titanium content. Cast unalloyed zinc has a columnar grain structure similar to that shown for the alloy of lowest titanium content but without the scatter of small equiaxed grains at the center.

Jan 1, 1944

By G. Das, S. V. Radcliffe

The substructural features developed in tungsten as a function of annealing temperature (up to 2200°C) and type of material [undoped and doped powder metallurgy (PM) tungsten and electron beam melted tungsten] have been investigated by transmission electron microscopy. For doped PM tungsten wires, characteristic "par-ticulate" substructural features developed rapidly with increase in annealing temperature above 700°C. The features consisted of parallel rows of elongated or circular shapes (500 to 1000A diam) lying along the direction of the wire axis and were identified as internal voids by diffraction contrast experiments. In recrystallized doped PM rod, larger voids were observed and were identified by precision dark field analysis to be cubic in shape and bounded by (100) planes. In marked contrast with both the doped PM materials, recrystallized undoped PM rod exhibited only very occasional and randomly arranged voids. Furthermore, no voids were observed in either material after electron beam melting. The high concentration of voids in the doped PM materials is attributed primarily to vaporization of doping additions or their pvoducts situated at the original grain boundaries , whereas the few voids in undoped material are considered to be traces of microporosity which were not eliminated during sintering. A tentative mechanism is suggested for the dezlelopment of the voids in relation to the processing sequences (sintering and working) and to the subsequent annealing. In recent years, a characteristic substructural feature consisting of rows of small elongated or circular regions of light contrast lying along the direction of working has been seen in thin foil electron microscopy studies of annealed sheet, wire, and rod tungsten. These features were present in the published micrographs of sheet by Weissmann et al.1 and of wire by Meieran and Thomas2, although the authors did not draw attention to them. Wronski and Fourdeux3 observed similar features in sintered rod tungsten (it was not specified whether or not the material was doped*) and interpreted them on the basis of their ap- particles, based on extraction replica evidence from the fracture surface of the initial hot-rolled slab material from which the sheet was prepared. No diffraction contrast experiments on the features were reported in any of these studies. The present investigation was undertaken with the primary objectives of: a) identifying the nature of these substructural features in tungsten by electron diffraction contrast experiments, since the contrast for voids can be expected to differ from that for crystalline or glassy particles, and b) elucidating the origin of the features and their development. For the latter purpose, doped and undoped powder metallurgy tungsten was obtained as rod and wire to represent different stages of reduction during final processing. These materials were examined both in the as-processed condition and after annealing to successively higher temperatures. In addition, the same doped and undoped materials were examined after vacuum melting in rod form. I) MATERIALS AND PROCEDURE Doped powder metallurgy (PM) tungsten wire (commercial purity 99.9 pct W) was obtained in the as-drawn and surface ground condition (0.030 in. diam "ground seal rod"). Doped and undoped tungsten rod (0.075 in. diam) representing an earlier stage of final processing was obtained from the same commercial source (Refractory Metals Division, General Electric Co.). Lengths of both the doped and undoped rod materials were single-pass melted in an electron-beam zone refiner to examine the effect of vacuum melting on the substructure. Annealing was carried out in a tungsten crucible in a tantalum strip resistance furnace under a vacuum of l0-15 mm Hg. Longitudinal sections of the wire and rod materials were examined by light and electron microscopy. The preparation of thin foils suitable for electron transmission from 0.030 in. diam tungsten wire and the rod specimens was carried out by means of a high-precision microjet technique developed to provide lack of jet stability and precise control of the area thinned. The method is described in detail elsewhere.' The foils were examined in a JEM 6A electron microscope using a goniometer stage (±20 deg tilt, 360 deg rotation) and operated at 100 kV. To minimize contamination problems a 200 µ condenser aperture was used in conjunction with a useful beam current of 50 µA. II) RESULTS AND DISCUSSION A) Diffraction Contrast Analysis. In order to determine the optimum conditions for the development of the substructural feature, a series of isochronal 30 min annealing experiments were carried out on specimens of the doped PM tungsten wire. The transmission electron microscopy analysis showed that the as-drawn wire, Fig. 1(a), consists of 'fibers' whose long axis is closely parallel to the wire axis of (110). The fiber width averages some 0.5 µ. Dense disloca-

Jan 1, 1969

By John G. Tate, George W. Nicolson, James L. Bruce

For more than 25 years modern mining has been carried on in the Island of Cyprus, Mediterranean Sea, by the Cyprus Mines Corp. of Los Angeles, Calif. The general features of these operations have been described.' From 1935 to June 30, 1940, top slicing in the Mavrovouni mine produced in excess of 2,000,000 long tons. The rate for the last part of this period was approximately 50,000 tons per month. Description of Ore Bodies The shape Of the Ore body now being top sliced in the Mavrovouni mine is an inclined irregular pyritic pipe or chimney of large dimensions) extending from unknown depths below the bottom level at elevation 250 ft below sea level) to the highest level at elevation 400 ft above sea level. The present surface above the ore body lies between 550 and 650 ft elevation. Undoubtedly the Ore body extended to surface and was Mined by the ancients by opencast and underground methods. The old pits were gradually filled up by erosion until now they show as slight depressions in the topography. The largest area of the Ore body is at elevation 170 ft below sea level, where the horizontal section is almost elliptical, with a width of 600 ft and a length of 1000 ft. Below this elevation the shape of the ore body continues to be elliptical but with reduced dimensions. Above this elevation it rises flatly towards the south with a substantial depression in the upper-side of the chimney and irregular ridges or wings rising on each side. It gradually grows smaller as it rises. The ore body is a pyritic replacement of andesitic extrusives which occur as flows and pillow lavas. With the exception of the upper portions of one or two small offshoots rising from the main ore body, all ore is completely surrounded by andesite. Most of the andesite lying above the ore body is covered by marl and Clay sedimentaries of Miocene and later age, The Miocene is presumed to be older than the ore mineralization. That portion of the andesites which lies between the sedimentaries and the ore body has been broken by slumpage, and weathered, and iron-Stained by the descending meteoric waters, It is a mass of crushed material that caves and follows downward readily as the top-slice stopes retreat. The main ore body is a heavy cupreous pyrites mass assaying on the average about 4.0 pet Cu; 48.0, S; and 42.0, Fe. In places the copper drops below 1.0 pet. on the borders of this heavy sulphide ore body lie disseminated cupreous pyrites ore deposits of large dimensions. some portions of these appear to be closely related to the heavy sulphide ore, as the ratio of copper to pyrite is about the same. The greater part of the disseminated ore, most of which lies immediately to the east of the main Ore body, contains less than 0.10 pct Cu and about 25.0 to 30.0 pct S. 'This probably can

Jan 1, 1949

By A. Keil

TO measure the absolute conductivity of metallic specimens it is generally necessary to have exact geometrical shapes and good electrical contact with the test-piece. To overcome limitations of the standard methods, an electronic conductivity-meter* Trade name, Sigmatest; model Dr. F. Forster; Reutlingen, Ger-many. has been developed, which works on the principle of inducing high frequency eddy-currents in the specimens and measuring the reaction of these curients on a measuring coil.',' To attach the instrument to the test specimen, a flat area of about 10 mm diam is all that is necessary. The reading is taken off a scale calibrated in pet of International Annealed Copper Standard. The induced eddy-currents are propagated in a circular motion parallel to the surface. Thickness of the layer included in a measurement depends on the frequency used. With a frequency of 60 kc per sec, the penetration of the currents was 0.8 mm at the upper limit of the scale, and 2 mm at the lower limit. The method is limited to nonferrous metals and other applications have been described elsewhere." The object of the present investigation was to detect the formation and growth of surface layers of differing conductivity, and to determine the depth to which these changes could be observed. A well known phenomenon which illustrates the problem is the internal oxidation of certain silver alloys containing base metal solutes, such as copper or cadmium, when they are annealed in an oxidizing atmosphere.4, 5 Until now, the only methods available for following these phenomenon have been metallo-graphic examination and hardness tests.0, 7 Changes in mechanical properties of copper alloys by internal oxidation were recently discussed in a more general way by Martin and Smith." When measuring these conductivity changes it must be remembered that the only absolute values of conductivity are those of 1) the nontreated homogeneous specimen, and 2) the final values obtained with a surface layer of depth comparable to the penetration of the eddy-currents. All intermediate values refer to the mixed conductivities of the transformed surface layer and the untransformed alloy, and are thus readings of relative value only. Experimental Results Specimens were annealed for 1/2 hr at 800°C in hydrogen, and the internal oxidation was carried out by thermal treatment in air at 800°C. Fig. 1 shows the results of the first series of experiments. With internal oxidation of a solid solution of 8 pet Cd in silver, the conductivity rises continuously until the surface layer formed has become thick enough to be the deciding factor (about 400µ). Precipitates of CdO are mainly in the form of points, Fig. 2, and, as a result, the electric contact between the silver crystals is not distorted by them. Brine11 tests were run with a 1.25 mm ball and a 7.812 kg load. The specimen annealed in hydrogen and oxidized to a depth of 400µ had a hardness of 40 Bhn,

Jan 1, 1959

By G. S. Cole, G. F. Bolling

ThIS note accompanies a study of grain structure changes in metal ingots produced by the alteration of fluid motion.1 Although the Prandtl Number of aqueous solutions is much higher than that for metals, it is quite instructive to see the simulation of freezing, as pointed out by Jackson and coworkers.2-4 Accordingly we have observed the effects of natural thermal convection, the changes induced by a steady-state rotation in one direction, and the changes under oscillation.' Temperature measurements were made under duplicate conditions whenever the visual observations appeared interesting. A solution of 15 pct NH4C1 in water was chosen. In each case the solution was preheated to 90°C in a 4-in.-diam Pyrex beaker filled to a level of about 5-in. depth and covered to prevent convective air cooling. The beaker was then placed in a container of iced brine, suitably arranged on a rotating table for movement about its cylindrical axis. Upon immersion in the brine under static conditions, fluid flow was observed near the wall of the beaker before the onset of crystallization, which generally commenced only after the temperature fell to 51.5"C. The region of flow extended about 1 mm from the wall and could not be observed elsewhere. The measured radial temperature increased sharply within 1 cm from the wall and thus over a distance considerably greater than that observed for the flow. However, we note that this difference of approximately one order of magnitude between hydrodynamic and thermal boundary layers should be expected for aqueous solutions, in contrast to metallic liquids. Beyond this layer the temperature was isothermal at a given height and in general nearly 10°C warmer than at the wall. The overall visual observation was therefore supported quite well by temperature measurement. There was also a vertical temperature gradient of nearly 2°C per cm throughout the liquid increasing from the colder bottom; this of course could not be observed visually. Eventually crystals precipitated from solution. (It

Jan 1, 1968

By J. W. Lacey, F. H. Brinkman, J. E. Faris

This paper presents an analysis of the high-pressure, gas-driven LPG-slug process, based on fluid flow tests in areal models. Two types of tests were made. One series was made in low-pressure models which permitted observation of fluid movement. Three completely misci-ble analog fluids were used. A second series of tests was made in high-pressure models using methane, propane and a light refined oil saturated with methane at room temperature and 1,550 psig. Under the test conditions of room temperature and a pressure level of 1,550 psig, the phase diagram for the fluids used is similar to those for many of the field systems where the process is considered for use. A method for using these laboratory data to calculate field performance of the process is outlined. As a result of this work, it is concluded that small banks of LPG (5 per cent HV or less) are not effective in increasing oil recovery in horizontal reservoirs. Znstead, where small banks are used, the driving gas quickly penetrates the LPG bank because of fingering and channeling; and from this point on, the process behaves essentially as an immiscible gas-injection project. The validity of this conclusion was substantiated by: (1) laboratory studies of the effect of rate, model size and mobility ratio on miscible displacement in areal models; and (2) calculation of field recovery, which compared closely with actual field recovery. INTRODUCTION Field applications and pilot tests of the gas-driven, LPG-bank, oil-recovery process are on the increase. Most of these tests are employing small banks (2% to 5 per cent hydrocarbon volume) of LPG, which is miscible with both the driving gas and the oil in place, in an effort to attain an effective yet economical miscible displacement of oil by gas. The expectation of miscible displacement with small banks is based on the concepts that: (1) lengths of solvent-oil mixed zones, measured during miscible displacements in long slim cores, are representative of those that will occur in the field; and (2) areal sweep efficiencies5 measured in electrolytic model studies are applicable to miscible displacement in reservoirs. Our experimental evidence indicates that the mixed-zone lengths and sweep efficiencies mentioned are not applicable to miscible displacement in reservoirs. In this paper we present an evaluation of the gas-driven, LPG-bank oil-recovery process based on fluid flow experiments in areal models. These results are used to predict the performance of a field pilot test of this process, and the results are compared with the actual test results. THE EFFECTIVENESS OF LPG BANKS The effectiveness of LPG banks of various sizes in accomplishing miscible displacement of oil by gas was determined by displacement tests in a model representing one-quarter of a confined five-spot pattern. The model, 12 X 12 X 1/4 in. in size, was packed uniformly with glass beads. It was operated at a pressure of 1,550 psig and at room temperature; the fluids used were methane, propane and refined oil saturated with methane at 1,550 psig. The saturated oil had a viscosity of 1.2 cp at room temperature. The results of these tests are shown in Fig. 1, where recovery is plotted as a function of the volume of fluid injected for: (1) an immiscible-gas drive with an oil-to-gas viscosity ratio of 85; (2) three sizes of LPG banks; and (3) two completely miscible displacements with mobility ratios of 85:1 and 10:1. (The miscible displacement data plotted are the averages of several tests.) The results show that a 2½ per cent bank of LPG does not increase oil recovery over that obtained by immiscible-gas drive. The 7 and 17 per cent banks are, respectively, about 30 and 50 per cent effective (with reference to the M = 85 miscible-displacement curve) in increasing oil recovery at the point where 2½ hydrocarbon volumes (HV) of fluid have been injected. The percentage effectiveness of the banks at a given volume of fluid injected is defined as Recovery by Bank — Recovery by Gas Drive Recovery by Miscible Recovery by Flooding Gas Drive We conclude from these results that banks of LPG smaller than about 5 per cent HV in an individual stratum will cause from little to no increase in oil recovery. This finding was substantiated by work in low-pressure models, which permitted visual observation of fluid movements. In these tests, three completely miscible fluids having the same viscosity ratios as those used in

By J. K. Kerver, J. S. Osoba, J. G. Richardson, J. A. Hafford

A detailed study of a number of methods of relative permea-abilitv measurement has been made in a search for the tech-niqrle most suited to routine analysis of cores taken from reservoir rock. It has been found from tests run on the same samples of core material by a number of techniques that the Penn State, Hassler, Hafford, and dispersed feed techniques all yield results which are felt to be reliable. Conditions under which the faster single core dynamic technique may be used are described. Further work on the calculation of relative permeabilities to oil from data obtained by the gas drive method is needed before this latter rapid method can be utilized. Correlations between theoretical studies and experimental results have been obtained in studies of the boundary effect. pressure distribution in two-phase flow, and gas expansion effects. Previous conclusions that the effects of the outflow boundary could be made negligibly small have been substantiated. Results of experimentally determined oil and gas pressure distributions along a core sample during flow are presented. Further studies of the effects of rate of flow in the measurement of relative permeability-saturation relations have shown that results are independent of the rate of flow as long as the flow rate is below the point where inertial effects commence. An analysis of the effects of a severalfold expansion of gas along the flow path indicates that while saturation gradients are induced in the test sample, the errors caused by this phenomenon in relative permeability measurements are small. INTRODUCTION Many pages of literature have been devoted to pointing out the need for relative permeability-saturation relations in reservoir engineering. One of the most attractive ways of obtaining this information is by the analysis of samples of core material taken from the formation in question, and again literature has described man); methods for obtaining these data. It is the purpose of this paper to present the work that has been done in the study of some of these published methods together with some other methods that have been recently developed in this laboratory. Also, a study of some of the factors that influence the laburatory determination of relative permeability-saturation relations is presented. FACTORS WHICH AFFECT LABORATORY STUDY OF FLUID FLOW THROUGH RESERVOIR ROCK To determine relative permeability-saturation relations of samples of reservoir rock in the laboratory, it is important to know what factors affect these measurements in order that the magnitude of these effects can be ascertained and steps then can be taken to eliminate or, in some cases, to minimize them. The factors that have been investigated are the boundary effect, the effect of gas expansion. and the rate effect. Boundary Effect In laboratory experiments in which two immiscible fluids are flowed through a porous medium, there exists a discontinuity of capillary properties at the outflow face. This discontinuity exists became the fluids pass from a region of finite capillary pressure in the sample to a region of zero capillary pressure in an open receiving vessel. The capillary forces existing in the core caupe the rock to tend to retain

Jan 1, 1952

J. L. CHRISTIE, Chairman T. S. FULLER, Past-chairman W. M. PEIRCE, Vice-chairman W. A. SCHEUCH, Vice-chairman E. M. WISE, Secretary International Nickel Co., Bayonne, N. J. W. M. CORSE, Treasurer Executive Committee H. A. BEDWORTH G. O. HIERS D. K. CRAMPTON R. H. LEACH E. H. DIX, JR. R. F. MEHL J. A. GANN J. WALTER SCOTT' JEROME STRAUSS Finance Committee T. S. FULLER, Chairman W. M. CORSE H. S. RAWDON C. H. MATHEWSON SAM TOUR

Jan 1, 1934

ROBERT H. LEACH, Chairman ROBERT F. MEHL, Past-Chairman D. K. CRAMPTON, Vice-Chairman E. M. WISE. Vice-Chairman W. M. CORSE, Treasurer LOUIS JORDAN, Secretary 29 West' 39th St., New York, N. Y. Executive Committee 1940 1941 ARTHUR PHILLIPS W. P. SYKES L. E. SCHUMACHER E. A. ANDERSON CARL E. SWARTZ D. L. COLWELL 1942

Jan 1, 1939

By Joseph E Pogue

Over a period of years the writer has presented a number of studies1 on various aspects of proration, in a progressive attempt to analyze critically and constructively the economic complexities of this interesting institution, which in a decade has revolutionized the economics of oil production in the United States. In the course of the investigations leading to these papers, the changing nature of proration and the principles underlying its evolution have gradually become clear, so that it is now possible to depart from the analytical method and to construct a synthesis of the steps that, if furthered by the industry, should carry proration past the economic hazards that still surround it to the goal of maximizing the value of the petroleum resource to the industry and the public alike. Nature of Proration Proration literally means the allocation of demand among competing producers on a pro rata basis, but the term now carries a much broader significance for it is employed to describe the entire process by which the production of crude oil in the United States is regulated. There is naturally much confusion of thought on the subject, for proration is an evolving system of control based upon principles of conservation and equity and embracing a body of practices that are tending to adjust themselves to the needs of the situation but are subjected to varying and divergent influences in the process. As it is now constituted, proration is a planned production measure designed to prevent waste, insure ratable takings, and balance supply and demand. The procedure is administered by State regulatory bodies through use of the police power of the States under authority of State conservation laws; the practice is supported by a considerable degree of voluntary conformance on the part of operators; and the Federal Government has accorded its cooperation by providing advisory quotas, circumscribing imports, checking movements of hot

Jan 1, 1939

By Joseph E. Pogue

Over a period of years the writer has presented a number of studies1 on various aspects of proration, in a progressive attempt to analyze critically and constructively the economic complexities of this interesting institution, which in a decade has revolutionized the economics of oil production in the United States. In the course of the investigations leading to these papers, the changing nature of proration and the principles underlying its evolution have gradually become clear, so that it is now possible to depart from the analytical method and to construct a synthesis of the steps that, if furthered by the industry, should carry proration past the economic hazards that still surround it to the goal of maximizing the value of the petroleum resource to the industry and the public alike. Nature of Proration Proration literally means the allocation of demand among competing producers on a pro rata basis, but the term now carries a much broader significance for it is employed to describe the entire process by which the production of crude oil in the United States is regulated. There is naturally much confusion of thought on the subject, for proration is an evolving system of control based upon principles of conservation and equity and embracing a body of practices that are tending to adjust themselves to the needs of the situation but are subjected to varying and divergent influences in the process. As it is now constituted, proration is a planned production measure designed to prevent waste, insure ratable takings, and balance supply and demand. The procedure is administered by State regulatory bodies through use of the police power of the States under authority of State conservation laws; the practice is supported by a considerable degree of voluntary conformance on the part of operators; and the Federal Government has accorded its cooperation by providing advisory quotas, circumscribing imports, checking movements of hot

Jan 1, 1939

By A. U. Seybolt

The pressure-temperature relations required to maintain the existence of Si3N4 in silicon-iron of 0.44-11.7 pet Si have been partially explored. The critical data obtained have allowed the calculation of some thermodynamic quantities, and have shown evidence of an order-disorder two-phase field extending at 800°C from about l pet to 5.5 pet Si. THE presence of silicon nitride in electrical sheet, nominally about 3 1/4 pet silicon, balance iron, has been described by several authors'" but there has been some discrepancy among them regarding the identity of the nitride. Also, little has been reported on the quantitative thermodynamic prop- erties. In the work to be reported here, the nitride has been found to be more stable than described by Corney and Turkdogan." Several silicon nitrides have been described in the past, including SiN, Si3N4 and Si2N4 (see, for example, Abegg6 and Pascal7). However, the literature on nitrides other than Si,N, is all very old. No recent investigators using the more powerful tools available today have reported the presence of any nitride other than S3,N4. W. B. Hicke and L. R. Brantley8 in 1930 determined the dissociation pressure of Si3N4 which they made by reacting nitrogen

Jan 1, 1959

CARL E. SWARTZ, Chairman D. K. CRAMPTON, Past-Chairman CYRIL S. SMITH, Vice-Chairman ARTHUR PHILLIPS, Vice-Chairman FRANK T. SISCO, Secretary 29 West 39th Street, New York, N. Y. H. A. MALONEY, Treasurer Executive Committee 1943 1944 ERIC R. JETTE WILLIAM C. ELLIS LOUIS W. KEMPF ALAN MORRIS GEORGE SACHS KENT R. VAN HORN

Jan 1, 1942

By F. Peter

I. GENERAL INTRODUCTION. TECHNICAL progress takes place in two directions: the improvement of methods, affecting the quality of the product; and increase in the economy of operations, affecting its cost. In the iron-industry, practice is pretty well settled, and. revolutionary changes of method are, for the present, not to be expected. Hence, in this industry, the principal endeavor is to reduce costs by the use of labor-saving inventions, such as the machines brought into use during the last decade. But it is not alone necessary to reduce the labor-cost; complete economy requires also a saving in raw material. Under this head we may rank the coal employed as metallurgical fuel; and it follows that progress includes the economic use of fuel, so managed as not to injure quality of product. In the present paper it will be shown how, by suitable utilization of the heat from the furnace, a large portion of it may be made available for other purposes. Such utilization of waste-gases is important in all industries which employ furnaces (especially heating- and smelting-furnaces); and in the first rank of these stand the iron-, glass-, and porcelain-manufactures. The following pages are devoted chiefly to the waste-gases of smelting-works, and especially to those reverberatory-furnace gases which are not combustible.'

Jan 12, 1913

By R. P. Smith

The diffusivity of carbon in iron, cobalt, and alloys of 89.7 and 79.3 wt pct Co has been determined by a decarburization method for the temperature range 850° to 1100°C. The Plots of log D us 1/T for the two Fe-Co alloys are linear through the region of the Curie temperature, showing that, unlike some cases of substitutional diffusion, carbon diffusion in these alloys is not affected by electron spin order. RECENT investigations1-' have shown that for substitutional diffusion in iron the change in diffusivity with temperature does not follow an Arrhenius equation, at temperatures near the Curie temperature. Data on the diffusivity of carbon in a iron5"9 indicate that this anomaly does not exist for interstitial diffusion; however, this has not been definitely established. Since cobalt and Fe-Co alloys, 80 to 100 pct Co, have Curie temperatures in a temperature range convenient for carbon-diffusion measurements they are suitable systems for studying the relation of interstitial diffusion and the Curie temperature. EXPERIMENTAL The carbon diffusivity, D, was determined by a decarburization method. The diffusion cylinders, made from small vacuum melts of electrolytic cobalt and plastiron, were about 0.76 cm diam and 6.3 cm long. A small amount of carbon was added to each melt to keep the oxygen content as low as possible. The cylinders were first treated with a hydrogen-3 pct water vapor mixture at 1100°C to constant weight, then carburized to the desired initial carbon content with a suitable CO-C02 gas mix-

Jan 1, 1964

By F. H. Kihlstedt

The Larap iron deposits, 125 miles east of Manila, are the biggest high-grade iron deposits in the Philippines, and have in seven years produced nearly 4 million tons of 60 per cent ore. Magnetic surveying followed by churn and diamond drilling cheaply developed a score of million tons. The ore zone is a wedge of metamorphic rocks in fresh, Miocene sediments overlain by agglomerates, which seem to have filled a river valley eroded in the sediments. A mild overthrust of the competent agglomerates crumbled the shale in front. Solutions gradually turned it into more competent hornfels and deposited pyrite, then magnetite and pyrite in the pores. As the temperature rose large bodies of magnetite with some pyrite were deposited by replacement and in open cavities in tensional areas of overthrust shears. At still higher temperature magnetite and calcium-magnesium silicates formed other bodies in similar cavities, and finally the thrust zone was invaded by syenite porphyry, causing high-temperature alteration products. Possibly, as temperature abated, more high-grade ore was deposited. The complicated faulting indicates dynamic, chronological and spatial changes of mineralization rather than zoning in a static system. Noncommercial copper, molybdenum and some gold accompanied the iron mineralization. In the thirties the Philippines gained a justified reputation as a country of considerable mineral wealth. Traces of Chinese workings show that these earliest travelers and traders had in a small way exploited the latent gold resources in the Islands. The Spaniards continued this for centuries, but did not succeed in establishing any steady mining industry. Modern technology was required to get it started. The rapid development in the last decade before the war got its impetus from several financial factors, the return to sugar growers of previously collected taxes, the influx of Spanish capital during the civil war in Spain, the influx of Chinese capital when the Japanese started their "China incident," and others. Directly or indirectly much of this capital reached the mining industry; in particular, gold mining. Out of the turmoil of an exceptional mining boom emerged a sufficient number of good and well managed gold properties to send the production to a level above that of any single state in the United States at the time. Other ore deposits besides those of gold also received their share, and for a country without any heavy industries at

Jan 1, 1949

By F. H. Kihlstedt

The Larap iron deposits, 125 miles east of Manila, are the biggest high-grade iron deposits in the Philippines, and have in seven years produced nearly 4 million tons of 60 per cent ore. Magnetic surveying followed by churn and diamond drilling cheaply developed a score of million tons. The ore zone is a wedge of metamorphic rocks in fresh, Miocene sediments overlain by agglomerates, which seem to have filled a river valley eroded in the sediments. A mild overthrust of the competent agglomerates crumbled the shale in front. Solutions gradually turned it into more competent hornfels and deposited pyrite, then magnetite and pyrite in the pores. As the temperature rose large bodies of magnetite with some pyrite were deposited by replacement and in open cavities in tensional areas of overthrust shears. At still higher temperature magnetite and calcium-magnesium silicates formed other bodies in similar cavities, and finally the thrust zone was invaded by syenite porphyry, causing high-temperature alteration products. Possibly, as temperature abated, more high-grade ore was deposited. The complicated faulting indicates dynamic, chronological and spatial changes of mineralization rather than zoning in a static system. Noncommercial copper, molybdenum and some gold accompanied the iron mineralization. In the thirties the Philippines gained a justified reputation as a country of considerable mineral wealth. Traces of Chinese workings show that these earliest travelers and traders had in a small way exploited the latent gold resources in the Islands. The Spaniards continued this for centuries, but did not succeed in establishing any steady mining industry. Modern technology was required to get it started. The rapid development in the last decade before the war got its impetus from several financial factors, the return to sugar growers of previously collected taxes, the influx of Spanish capital during the civil war in Spain, the influx of Chinese capital when the Japanese started their "China incident," and others. Directly or indirectly much of this capital reached the mining industry; in particular, gold mining. Out of the turmoil of an exceptional mining boom emerged a sufficient number of good and well managed gold properties to send the production to a level above that of any single state in the United States at the time. Other ore deposits besides those of gold also received their share, and for a country without any heavy industries at

Jan 1, 1949