Search Documents

By Valentine A. Chanturiya

A model for development of electric discharges between particles of sulfide minerals (pyrite) under the action of high-voltage nanosecond pulses is proposed. It is shown that through discharges in a layer of pyrite particles lead to energy concentration in small contact regions between particles; the concentrated energy is sufficiently high for local disintegration of mineral complexes.

Jan 1, 2009

By David E. Hardt

"One of the critical variables to be controlled during arc welding is the size or geometry of the weld pool. The measurement of pool geometry has become an increasingly important problem with the advance of welding automation and control, and this paper addresses that problem. The basic concept of pool size estimation via measurement of pool dynamics is presented. The theory underlying this concept is discussed and is followed by a review of the current work in this area. It is concluded that pool dynamics can be characterized by natural frequencies of oscillation, for stationary welds, and that these can be measured by appropriate signal processing performed on the arc voltage. However, it appears that only full penetration welds show a strong correlation between weld size and natural frequency. Also, the extension of these results to the realistic case of moving welds has yet to be considered in detail. Nonetheless, this method of in-process measurement for real-time weld process control is still quite attractive where applicable since it can be accomplished simply by modifying the arc current schedule and by signal processing of the arc voltage.INTRODUCTUIONThe study of welding process control has been dominated by research into methods of in processing sensing of the weld pool geometry. While it has been shown feasible to measure the topside pool geometry using video methods [1,2], the penetration or backside bead width have remained elusive quantities. This is particularly true if a topside sensor location is required.The concept of using weld pool motion as a pool geometry sensing method was proposed by Hardt et al. [3] and later demonstrated by Hardt and Zacksenhouse [5] and Richardson and Renwick [6]. The concept is based on the fluid dynamics of a pool constrained by a solid container and by significant surface tension forces (i.e. a small shallow pool, not a ""pond"" or ""lake""). Such a pool, if subjected to external forces, will exhibit a surface motion is a function of that force, the properties of the fluid, the surface tension, and the shape of the container. Thus, if this motion can be excited and measured, and the relationship to the pool geometry determined, a means of sensing pool shape will exist."

Jan 1, 1986

By M. Suzuki, M. Dobashi, M. Kahata, T. Yoshida

Almost 30% of steel in Japan is produced by electric arc furnace (EAF) treatment of iron scrap. EAF dust includes approximately 20 wt % of Zn and 3- 5 wt % of CI and is treated by the pyrometallurgical processes to recover Zn as Zn oxide. Direct hydrometallurgical processing is one of the most effective methods to recover high purity Zn. In this case, CI in the EAF dust is dissolved in the liquid phase by leaching, and the CI anion in electrolyte attacks anodes which are commonly made of a lead base alloy. Several processes have been proposed to remove CI anions from acidic sulfate solution. In this study, an electrolytic process was examined to eliminate CI anions from Zn sulfate electrolyte. From our study it can be said that the elimination rate of CI anion depends on the anode material ( i.e., the elimination rate is Pb-Ag alloy == Pb > DSE== Pt). In industrial Zn electrowinning process, the electrolyte contains Mn, which means the influence of Mn should be considered in the elimination of Cl. Mn dioxide deposition on an anode plate reduces the efficiency of CI removal. A periodical reverse current electrolytic system was examined to prevent this efficiency decrease, and deposited Mn dioxide could be removed very rapidly when the current is reversed. More than 95% of CI anion could be removed by this method in a shorter period than direct current method.

Jan 1, 1997

By Chikabumi Yamauchi, Mitsuru Tanahashi, Jutaro Miura, Takaharu Iwadachi, Toshiharu Fujisawa

"Tue oxidation behavior of molten Cu-Be alloys was investigated by exposing· the molten Cu-Be alloys to various Ar-O2 atmospheres to control the oxygen partial pressure, PO2 = 10 ~105 Pa at 1423 K. The following results were obtained:• The oxygen · partial pressure in gas phase affects the morphology of the oxide formed on the surface of the alloy and · the oxidation rate of beryllium.• At lower oxygen partial pressure, a molten Cu-Be alloy is covered with a homogeneous and compact internal layer of BeO. Thus, the beryllium oxidation rate can be minimized.• By adding a small amount of calcium or zirconium into the molten Cu-0.5 mass% Be alloy, a protective BeO layer is formed even at higher oxygen partial pressure. Thus, the beryllium oxidation rate can be reduced.IntroductionCopper-beryllium (Cu-Be) alloys are well recognized for their unique properties, such as high electrical conductivity, high strength, high fatigue strength, excellent properties at elevated temperatures, good formability and good corrosion resistance. .This extraordinary collection of properties are the reasons why Cu-Be alloys are expected to be ""Key-materials"", which are necessary to further advance science and technology and to be applied in.various fields such as electronic devices, machine parts, repeater housings of undersea optical fiber communication cables, etc.However, a large amount of beryllium is oxidized to BeO in melting stage of the current Cu-Be alloy production process, because beryllium is a highly reactive element. This is one of the ·main factors that negatively affect the production yield and th_e product quality."

Jan 1, 2000

By Andreas Dietrich

Laser off-gas measurement of CO, O2 and temperature has been carried online in EAFs. A visualization screen shows the values of CO and Oxygen and temperature for the entire heat, and includes the status of furnace equipment. The historical data of the heats are stored such that the furnace performance can be evaluated and optimized. A short comparison between laser based and conventional systems has been carried out related to speed, influence of dust, water, pressure, protection for bag house explosions. A high water and/or dust content in the sample does not represent a problem for this type of system. The measurement method works without interruption even under worst conditions such as dirty scrap, carbon injection etc. The installation was developed in conjunction with Marienhuette, Graz. They are 100% scrap based with a tap to tap time of ca. 46 min. Keywords: Laser Measurement, Off Gas, CO, O2, Temperature

Jan 1, 2003

By John A. Mavrogenes

The Texaco gasification system developed at the Monte Bello pilot plant efficiently bums petroleum-coke thereby producing syn-gas and electricity. This system produces more electricity than conventional burners, yet the only by-products are pharmaceutical grade sulfur and V -rich slag. Vanadium is known to exist in multiple valence states in compounds which possess a wide range of melting points and physical properties. Consequently, it becomes important to carefully regulate oxygen fugacity throughout the system in order to control vanadium valence state. Vanadium phase equilibria is presently poorly understood, in large part because of the multiple oxidation states of vanadium (-I, 0, +2, +3, +4, and +5) and the difficulty of unequivocally identifying the valence state(s) in many compounds. The operation of these gasifiers at approximately 1400°C is well above the melting point of V20S but considerably below the melting temperature of V02 and V 203. If J02 can be regulated to keep the burner within the V 205 field, slag material would more likely remain molten and more easily flow out of the bottom of the burner. In pure V oxides. the oxidation state is readily determined by microprobe analysis. where V20S (V+5) is 56% V, V02 (V+4) is 61.4% V, and V203 (V+3) is 68% V. However, V valence in multi-element phases (especially phases containing other elements of variable valence) cannot be resolved by microprobe analysis alone. Petroleum-coke gasification slags collected from within the gasifier under different oxidation conditions were studied by electron microprobe analysis (EMPA). X-ray diffraction (XRD). X-ray photoelectron spectroscopy (XPS) and Raman spectroscopy. Raman spectrometry in conjunction with microprobe analysis was found to resolve the valence of vanadium in the phases of these slags. Raman spectra collected from homogeneous single phase V-oxide standards in vacuum at low temperatures (-150°C) yielded peaks characteristic to each valence state. Gasifier slag samples are, however, much more complicated. Oxidized samples contain: fine grained (Ca. Mg, Fe. V) oxide matrix of variable composition, (Fe. V, Ni) spinel. (Fe, AI, V, Ni, Mg) spinel, V205laths, AI-Si glass blebs and Ni sulfides. Reduced samples contain: crystalline Ca-siIicate matrix, subhedral to euhedral (V, Fe, Mg, AI) spinel, subhedral V02, Fe and Fe-Ni sulfides, Fe-Ni alloys, and complex Ca-oxide matrix. The different spinel assemblages, the characteristic V-oxides and the distinctly different character of the matrices makes the oxidized and reduced slags readily discernible.

Jan 1, 1995

By C. B. Solnordal, R. N. Taylor

"The heat transfer conditions on the outer side of a Sirosmelt lance have been determined using experimental measurements in combination with a mathematical model. By measuring the temperature distribution along the wall of an operating Sirosmelt lance, as well as the thickness of the slag layer on it, it was possible to use the model to determine both the heat transfer coefficient between the vessel contents and the lance, as well as the effective thermal conductivity of the slag layer. The effective thermal conductivity of the slag layer was found to be within the range 0.7-1.3 W.m-1. ºCl, which was in good agreement with measured values for magnetite. The outside heat transfer coefficient varied from 80 to ISO W.m-2. ºC1, which was smaller than quoted in the literature for metal/slag systems. The discrepancy was attributed to the high thermal resistance experienced between the lance wall and the slag layer, as well as the large quantities of combustion gases that envelop the lance tip and reduce convection and conduction from the melt to the lance. INTRODUCTIONThe Sirosmelt submerged combustion smelting process [1] utilizes top injection lances to deliver fuel and air into a metallurgical melt. To help prevent lance failure from attack by liquid slag, helical vane swirlers are used within the annular lance to impart swirl to the flowing air and enhance the heat transfer from the lance wall to the air. The swirlers thus cool the wall, and enable a frozen layer of slag to form on its outer surface. This solid layer ensures liquid slag cannot reach the lance surface, and the lance is protected.A mathematical model of the heat transfer processes associated with the lance has been developed, which combines heat balance equations with engineering correlations to predict the wall and cooling air temperature of the lance, as well as the air pressure distribution. An account of the model was given by Rankin et al. [2]. To further enhance the model and enable it to predict the thickness of slag accumulating on the lance, a detailed analysis of the heat flow through the slag layer commenced in 1992. By far the most complex aspect of the model, the flow of heat from the vessel contents to the outside of the lance was dependent on many factors, including:-"

Jan 1, 1996

By Y. Ide, K. Kishitake

It is expected that an Al-Cr-N composite nitride film may have a higher resistance to oxidation at elevated temperatures than the well-known Ti-Al-N films. The formation conditions of Al-Cr-N films by a de reactive sputtering method and their properties were studied in this study. The films characterized with respect to their high temperature properties such as chemical composition, crystal structure, microhardness, wear and· friction. The crystal structure of the Al-Cr-N films changed from hexagonal phase to cubic phase with an increase in Cr content in the films. The resistivity to thermal oxidation of the Al-Cr-N films is superior to that of usual TI-Al-N films. A half of the friction coefficient in the Al-Cr-N film was obtained comparing with that in the ordinary TI-Al-N film at room temperature and the wear rate of Al-Cr-N film was 2 order smaller than that of TI-Al-N film. The Al-Cr-N films show a small friction coefficient at 500°C and then they are recognized to have good tribological characteristics.

Jan 1, 2000

By Pedro A. Netto, Sergio N. Monteiro, Foluke S. de Assis, Rômulo L. Loiola, Frederico M. Margem

Banana fibers are among the lignocellulosic with great potential for use in polymer composites, such as the variety from the Musaceae family, due to its low density and good mechanical properties. In this work, epoxy matrix composites incorporated with continuous and aligned banana fibers were tested for their flexural behavior. Specimens with up to 30% in volume of fibers were bend-tested until rupture. The results showed an increase in both the composite mechanical strength and the stiffness with incorporation of these fibers. A fractographic analysis by SEM examinations a moderate adhesion mechanism between the banana fiber and the epoxy matrix. This mechanism is apparently responsible for the improved performance of the composites.

Jan 1, 2015

By Kazuteru Tozcwa

The oxidation of several sulfide minerals in aqueous ammoniacal solution is discussed thermodynamically. The region in which Cu(NH3)2 4+ is stable has been estimated as a function of pH and concentration of total ammonia, {[NH3) + [NH4)}. In ammonia leaching when copper in sulfides is assumed to be extracted in the form of Cu(NH3)2 which will be rapidly converted to cupric ammine, thermodynamic data predict that such minerals are oxidized readily in the following order, CuS, Cu2S, CuFeS2, ZnS, NiS, Ag2S. This agrees with investigations on ammonia leaching of sulfide minerals, reported previously. The leaching of copper sulfide concentrate has been examined experimentally. Copper in a copper sulfide concentrate, in which the main constituents were chalcopyrite and pyrite, was effective¬ly extracted. The copper extraction was affected by factors such as (1) agitation intensity, (2) oxygen partial pressure, (3) NH3/Cu molar ratio, (4) leaching temperature and (5) addition of ammonium sulfate. From the results obtained in this work, it is concluded that mass transfer of oxygen plays the most important role in ammonia leaching of copper sulfide minerals.

Jan 1, 1976

By A. F. Sidorov

A method of improving mineral recoveries from ores by modifying the physical and chemical properties of minerals using radioisotope radiation was tested. It was observed that irradiation modifies mineral cell sizes, changes the crystal structure of some minerals, reduces the sulfur content 1 to 1.5 % in sulfides, changes the zeta potential, alters the surface properties of mineral grains I and produces other changes. Preliminary tests indicate that accelerated electron treatment of ores in connection with mineral processing has a potential for improving mineral recoveries by flotation and by magnetic separations.

Jan 1, 1989

By Guo Xueyi

The electrochemical couple behavior of manganese dioxide with ferrous/ferric ions in acidic chloride medium was investigated, It was proven that the dissolution of Mn01 is due to the electrochemical couple reaction between MnO2/Mn2+ and Fe2+/lFe3+ in the solution, The driving force for the process originates from the rest potential difference of the two couples. The reduction of Mn02 is controlled by clectrochemical kinetics, whereas the conversion of F e2+ to Fe3+ is limited by diffusion, The factors such as the Mn2+, Fe2+, Fe3+, Cl concentration, pH of the solution and the temperature, have much influence on the kinetics of the couple process, This study will be useful to elucidate the mechanism for the leaching of manganese nodule from the deep ocean as well as manganese dioxide ores in land,

Jan 1, 2003

By C. Dresen

This paper discussed the reaction kinetics of the reduction of industrial phosphate pellets for P4 production. In the reduction process of various phosphate ores, the following parameters were investigated: Diffusion of the phosphorus oxide and other gaseous products from the reaction mixture after having been reduced on the reductant (coke) surface. Influence of silica on reaction kinetics. Temperature influence. Influence of mineralogy and morphology (different ores). Particle size influence of silica and coke. Experiments were carried out in a vertical tube furnace with 2 ores, 2 types of silica and one type of coke. Selected experimental conditions simulated furnace conditions. The following conclusions could be made: Reaction rate increases with the addition of SiO2 into the pellet. The reaction rate increases above 1350°C (melting temperature of the slag). Mixing different ore types in the pellets leads to differences in reduction kinetics. Particle size of the coke particles influence reduction kinetics. The amount of slag formation is influenced by silica addition, coke size and temperature.

Jan 1, 2002

By William Petruk

A mineralogical and image analysis study was conducted on samples of U tailings from pilot-plant runs on Midwest ore in Northern Saskatchewan. The tailings had been subjected to simulated weathering for the equivalent of 10 years in a tailings facility (lysimeter). The pH varied from 7.0 at the beginning of the test to 5.9 at the end. The results show that during the simulated weathering sane of the gersdorffite, uraninite, galena and pyrite had oxidized, with gersdorffite being the most reactive and pyrite the least. Reaction was evident at the top of the lysilleter , but was most intense at the seepage discharge. sane of the released ions precipitated as Ni, Pb, and U arsenates, sulfarsenates, sulfates and oxides on particles of all minerals. Green crystals of Ni sulfate and white crystals of ca sulfate had precipitated at the surface of the lysilleter. Clay minerals and chlorite had washed from the top of the lysirneter towards the seepage discharge.

Jan 1, 1989

By J. K. Brimacombe, I. V. Samarasekera, B. G. Thomas

"Mathematical models have been developed for the processing of static cast steel ingots and are app1ied to investigate the mechanisms for the formation of panel cracks. Panel cracking is an intermittent but persistent defect that causes affected steel ingots to be scrapped. A two-dimensional, finite-element, heat-transfer model was formulated and employed to calculate the temperature distribution in both large and small steel ingots during the various processing stages from initial casting to the start of rolling, including solidification, cooling in the mold and in air, reheating in the soaking pit, and subsequent air cooling. The stress state in the ingot arising from the calculated temperature variations was then determined. This involved the development of a transient, elasto-visco-plastic, finite element, thermal stress model, including the effects of phase transformation volume changes and kinetics creep, and temperature-dependent, mechanical properties. The results of the mathematical model predictions of temperature and stress were then used to determine the mechanisms and to suggest solutions for two different types of panel crack formation. Mid-face panel cracks apparently form during air cooling when the mid-face surface temperature is between the Arl and 500~C. Off-corner panel cracks appear to initiate internally during the early stages of reheating but do not propagate to the surface until much later. IntroductionPanel crack formation in static-cast steel ingots is a defect that has been plaguing the steel industry for several decades. Although the problem is intermittent, it is also serious since affected ingots must be scrapped. Panel cracks are manifested as two distinct types of cracking problems. ""Mid-face"" panel cracks are found exclusively in small, 2 to 6 ton, medium carbon steel (0.3 to 0.7% C) ingots and usually exhibit a single, continuous, longitudinal crack down the center of one of the ingot faces as shown in Fig. l (l). ""Off-corner"" panel cracks often form roughly oval, discontinuous crack patterns on the wide faces of large, 20 to 30 ton ingots as seen in Fig. 2 (2). They affect only low carbon steels (0. l to 0.2% C) with high manganese content. Both defects affect only aluminum-treated steels and are caused by a combination of intermediate temperature ductility loss involving aluminum-nitride precipitation and thermal stress generation. The ductility problem has received a good deal of attention which was the subject of a recent review (3). The present study was undertaken to investigate the thermal stress aspects of the problem through the development of mathematical models of heat transfer and stress generation in static-cast steel ingots. The ultimate objective was to elucidate the mechanisms of formation for both types of panel crack and to evaluate possible solutions to the problem."

Jan 1, 1986

By W. G. Davenport

Chapter 11 determined the combinations of industrial oxygen, oil and blast preheat that will steadily produce 65% Cu matte from pure chalcopyrite concentrate. It showed that the . combinations are described by a flat plane. It also showed that the minimum energy requirement for making 65% Cu matte occurs with maximum oxygen enrichment, zero oil and zero blast preheat. This chapter examines the, effect of matte grade on industrial oxygen, oil and preheat requirements.

Jan 1, 2001

By Bogidar Mihaylov

A laboratory study was conducted on continuous precipitation of copper, cadmium, mercury and arsenic using thiourea, thioacetamide, sodium sulfide and ammonium sulfide as precipitating agents. Depending on the experimental conditions the metals precipitate with the sulfide donors at different orders and rates. These differences were employed as a basis of several techniques for continuous separation of copper and arsenic, cadmium and arsenic, mercury and copper, and copper, mercury and arsenic. The separation of the metals from industrial waste solutions was also studied. The precipitates obtained were inspected using x-ray diffraction, scanning electron microscope, atomic absorption spectrometer and plasma particle counter.

Jan 1, 1992

By M. Yoshida, S. Hanada, T. Takasugi

"A study has been conducted to examine the effect of ternary alloying elements on high temperature deformation of the C15 NbCr2 based intermetallics in Nb-Cr-X (X=V, Mo and W) alloy systems, which have attractive properties as high temperature structural materials. The high temperature deformation of the C15 NbCr2 intermetallics can be improved by two alloying methods. One method is based on geometrical consideration for site occupation and atomic size factor of component elements and additive elements in the single phase C15 lattice; addition of Mo and V can promote dislocation movement without introducing significant hardening. The other method is based on microstructural modification through ternary alloying; moderate addition of these elements results in a variety of duplex microstructure consisting of the C15 phase and bee solid solution without forming any intermediate phases, and can enhance the high temperature deformability. Particularly, alloys with duplex microstructure equilibrating with Cr-rich bee solid solution is shown to exhibit superior deform ability. Also, lattice property of the additive atoms in the C15 structure and phase relation between the C15 structure and the bee solid solution are investigated by OM, XRD, TEM and ALCHEMI observations and then discussed in association with observed mechanical behavior.IntroductionLaves intermetallics with AB2 stoichiometry belong to the largest group in a large number of intermetallics with various kind of crystal structures, and have a variation of the cubic CIS, the hexagonal C14 and the dihexagonal C36 structures, depending on stacking sequence of XYZ type, each of which consists of four interpenetrating atomic layers (1-3). Some of the Laves intermetallics have good functional properties and therefore are considered to be used as, for instance, magnetic materials, magneto-optical materials, hydrogen storage materials and superconducting materials (2). Also, the Laves intermetallics are considered to be good candidate as high temperature structural materials operating at high temperatures and in severe environment because they have high melting point, low density, and potential resistance to corrosion and oxidation. However, the Laves intermetallics are very brittle at low temperatures because they consist of complex crystal structures similar to many other intermetallics."

Jan 1, 1996

TiO2 and Ti/TiO2 thin films were deposited on a quartz substrate by laser ablation of Ti02 and Ti targets using Nd:YAG pulsed laser. After sulfurization of the Ti02 film in H2S or CS2 gas at 1273 K for 1 hour, the surface atomic structure was changed. Furthermore, the Ti/TiO2 film was successfully prepared by the subsequent ablation of Ti and TiO2 targets. The morphology and structure of the films were characterized by XRD, XPS and AFM analyses.

Jan 1, 2003

By T. Nakamura

TiO2 and Ti/TiO2 thin films were deposited on a quartz substrate by laser ablation of TiO2 and Ti targets using Nd:YAG pulsed laser. After sulfurization of the TiO2 film in H2S or CS2 gas at 1273 K for I hour, the surface atomic structure was changed. Furthermore, the Tirri02 film was successfully prepared by the subsequent ablation of Ti and Ti02 targets. The morphology and structure of the films were characterized by XRD, XPS and AFM analyses.

Jan 1, 2003