Search Documents

By N. Kanari

The thermal decomposition studies of two zinc basic carbonate samples were carried out up to 400 "C by thermogravimetric analysis, boat experiments and differential scanning calorimetry measurements 'DSC'. The initial samples and the solid decomposition products were analyzed by scanning electron microscopy, x-ray diffraction and laser particle size analyzer. The thermal decomposition of both samples started at about 150 "C and the rate of decomposition became significant at temperatures higher than 200 "C. The apparent activation energies 'Ea' in the temperature range 150-240 "C for sample decomposition were between 132 and 153 kJ1mole depending on the sample origin. The XRD analyses of the intermediately decomposed samples and the DSC results up to 400 "C suggest that the decomposition reaction probably occur in a single step.

Jan 1, 2002

By Chonghe Li, Xionggang Lu, Wei Xiao, Xingli Zou, Weizhong Ding

The reduction degree and rate of the initial ilmenite concentrate and pre-oxidation samples by hydrogen were investigated by using thermogravimetric analysis system. H2-TPR was used to detected reduction properties of the pre-oxidation products which were oxidized at different temperatures. The phase transformations and micromorphology changes during pre-oxidation and hydrogen reduction were identified by XRD and SEM. The FeTiO3 was decomposed into TiO2 and Fe2O3 at the temperature below 900 oC. With the temperature rising, Fe2TiO5 was the only stable phase in high temperatures. The reduction of pre-oxidation ilmenite concentrate was faster than the natural sample, which was attributed to the micropores generated on the surface of ilmenite concentrate during oxidation. The main phases of the reduction product were metallic iron, ferrous pseuodbrookite.

Jan 1, 2014

By Stephanie Trant

Montana Tech has been engaged in fundamental research on the processing of critical materials for more than a decade. Efforts include examining novel reagents for the flotation of Rare Earth Minerals (REMs). For this paper, research results on a collector, salicyl hydroxamic acid (SHA), are presented. Various REMs were examined and include the rare earth oxides (REOs), carbonates (RECs), and phosphates (REPs) of a suite of Rare Earth Elements (REEs). Differences are attributed to solution and surface chemistry, coordination number, and ionic diameter. SHA adsorption follows an ion-exchange process that leads to chemisorbed and surface-precipitated states, depending mostly on pH. Many effects are directly attributed to lanthanide contraction. Results should also be applicable to other REM/collector systems and further suggest that REM flotation should consider dual collectors.

By Emmanuel N. Zevgolis

In the present work, a reduction roasting experimental study of Greek nickeliferous laterite samples with a gaseous reducing mixture ? CO:N2- is presented. The effect of parameters such as temperature, ore grain size, and composition of the reducing mixture were examined. It is deduced that the reducibility of intermediate type laterite sample, where iron appears mainly in the form of goethite (a-FeOOH), is considerably higher than that of limonitic type laterite samples, where hematite (a-Fe2O3) is the predominant iron mineral phase. The degree of reduction of the limonitic type laterite samples does not exceed 50%, while it reaches 95% in the case of the intermediate-type laterite sample under the same experimental conditions. Increasing the temperature in the range 750-900°C does not considerably favor the reduction of the limonitic type laterites, whereas decrease of ore grain size of the limonitic-type ore samples and more intense reducing conditions increase the reduction. The considerably higher specific surface area values of the intermediate laterite samples, diminishes the effect of the ore grain size and this can be regarded as the critical parameter leading to the higher reducibility of this ore.

Jan 1, 2009

By Mansoor Barati, Leili Tafaghodi Khajavi

"This study involves employing solvent refining as a purification process in which silicon recrystallization takes place from an iron-silicon melt. It is believed that iron will act as the impurity “getter” and purified silicon crystals will grow from the alloy melt, while the impurities are segregated to the liquid alloy. Phosphorous is a problematic impurity to remove since its segregation coefficient in pure silicon is relatively large. To assess the feasibility and efficiency of phosphorous removal through solvent refining, it is critical to study its equilibrium distribution between solid Si and the Fe–Si alloy phase.The distribution of phosphorous between solid silicon and iron-silicon melt at 1210-1310 °C was measured to evaluate the impurity removal potential of each alloy. Interaction parameter between phosphorous and iron was calculated by varying the concentration of phosphorous in silicon.IntroductionAmong various semiconductor materials for manufacture of solar cells, silicon accounts for over 90 percent of today's PV materials [1, 2].The major challenge in producing solar silicon that operates efficiently is to meet purity level requirement through a cost efficient route. Silicon solar cells can play a significant role in answering the world's need for energy if cost reductions can be achieved through manufacturing process. Considerable effort has been made to replace the expensive, complex vapor-phase purification by a simpler and less costly process. One of the refining approaches that have attracted wide research interests is producing low-cost solar grade silicon by purification of metallurgical grade silicon. Since metallurgical processes are selective in removing impurities, a combination of various purification processes can be used to reduce the impurity level in silicon. Considering different thermodynamic characteristics of impurities, each refining step is responsible for lowering specific impurities."

Jan 1, 2012

By S. Mondon

Hibi Smelter which is a Copper Smelter lining a blast furnace, produces 2,700 metric tons of anode copper per month. Generally, in a copper refinery, arsenic and antimony are considerably troublesome impurities. With regard to the elimination of antimony, Hibi Smelter has two handicaps described as follows. (1) Smelting under the slightly oxidizing atmosphere in the blast furnace. (2) Recycling the converter slag to the blast furnace after cooling. Therefore antimony and arsenic, mainly antimony, elimination tests, in which the alkaline flux was injected through the two tuyeres in the blowing stage, were carried out in the rotary anode furnace. Antimony and arsenic were respectively removed more than 90 96 from the molten copper, and their high eliminations are discussed by application of the transitory and permanent reaction model with the flux injection, which was presented by T. Lehner.

Jan 1, 1983

By Run-boWang, Fan-yi Meng, Jian-Liang Zhang, ZheWang

To elucidate the influence of high Al2O3 content on sinter softening and melting behavior, heating-up reduction test under load was carried out. In addition, microstructure study of sinter bed structure change at a different temperature was also made and the mechanism that the effect of Al2O3 content on sinter softening and melting property was discovered. SEM results showed that the increase of Al2O3 content favored the formation of Al2O3-rich slag phase, such as the eutectic (2CaO·SiO2-2CaO·Al2O3·SiO2-FeO) and gehlenite (2CaO·Al2O3·SiO2), resulting in the decrease of sinter Ts temperature. Further, high Al2O3 content improved the concentration of metallic iron and lowered the dripping temperature due to the decrease of slag liquidus temperature and viscosity. At a fixed basicity, it was indicated that there was a relationship between Al2O3 content and sinter softening-melting property. Based on the results, counter strategies to cope with the adverse effect of high Al2O3 content on the cohesive zone property were also proposed. It could provide guidance for the blast furnace operation of sinter with high Al2O3 content.

Jan 1, 2015

By V. M. Lsoitko

Statistical methods of technological mineralogy are used to model processing flowsheets in order to improve ore dressing efficiencies. The procedure involves determining geological and mineralogical characteristics of ores, classifying ore types and metallurgical procedures, and developing computer programs to interpret essential mineralogical parameters from on-stream analysis data. The on-stream analysis data include magnetism, radioactivity, luminescence and assays. The data are interpreted by computer and appropriate adjustments are made automatically in the plant.

Jan 1, 1989

By Jay R. Hitchings

A technique that enables excellent color photograph production from black and white negatives of electron microprobe x-ray images is described in this paper. The photographs are made by superimposing one, two or three negatives of black and white x-ray images individually through assigned primary color filters directly onto color print paper. When used to examine metallurgical or geological microstructures, the resulting color photograph provides detailed, qualitative information about spatial arrangements, elemental associations and relative concentrations of at least three elements. The technique is simple and straightforward, requiring only standard darkroom equipment. The use of color to display or present complicated microprobe data also allows a non-technical reader or audience to better understand the data.

Jan 1, 1981

By den Bulck A. Van

In Europe, 50% of the copper originates from recycling. High-Cu containing scraps are regularly rich in impurities like Fe, Ni, Sn and Pb. Many high-Cu containing scraps are fed directly into anode-furnace casting installations or furnaces with limited refining capability. The impurities levels of the anodes produced in these processes should however remain acceptable for further electro-refining. The distribution of Sn between copper and slag has been investigated for conditions relevant to copper converting. Unlike previous studies, this work focuses on the behavior of Sn relevant to fire refining conditions, which are essential for anode refineries.In this study, liquid Cu–1Sn and CuOx–FeOy–SiO2 slag, with CaO additions, were equilibrated at 1300 °C in vacuum sealed SiO2 ampoules. After metal–slag equilibration, the samples were quenched in water. The composition of the slag and Cu metal was investigated with Electron Probe X-ray Microanalysis. The distribution coefficients of Sn between slag and Cu metal were determined as a function of slag composition.

By Carlos Maurício Fontes Vieira, Sergio Neves Monteiro, Diogo Neves Henriques

"This work evaluates the effect of incorporation of an ornamental rock waste into an industrial clayey body used for roofing tiles fabrication. Formulations with 0, 10, 20 and 30 wt.% of waste were prepared by replacing the sand in the industrial clayey body. The plasticity of the formulations was determined by the Atterberg limits. Specimens were fabricated by 18 MPa press-molding and then fired from 850 to 1100oC. The specimens were tested to determine the water absorption, linear shrinkage and three points bending flexural strength. The results indicated that the waste improves the extrusion performance of the clayey body by decreasing its plasticity. The use of the waste was beneficial to the water absorption and mechanical strength of the fired clayey ceramic at temperatures above 1000 ° C.IntroductionOrnamental rock is a natural resource available in the municipal area of Santo Antônio de Pádua and located 150 km from the city of Campos dos Goytacazes, northe of state of Rio de Janeiro, Brazil. Intense industrial activity related to ornamental stones, especially gneisses, is traditionally occurring in the region. After mining, the flagstone is submitted to sawing to obtain blocks and then, after a manual operation, the final products are small flagstones [1,2]. During the sawing operation, a sludge composed of water and fine particles of rock is generated. A monthly production of 1000 tons of ornamental rock waste is estimated to be produced at Santo Antônio de Pádua. The final disposal of this waste has brought serious environmental problems. Since most industries do not have an adequate sludge treatment, the waste is contaminating the soil and underground waters as well as obstructing rivers and lakes.Ceramic bodies industrially fabricated in the municipal area of Campos dos Goytacazes, 280 km from the city of Rio de Janeiro, are still empirically elaborated using a mixture of local clays. These clays are predominantly kaolinitic mineral, associated with high plasticity. Due to the excessive plasticity of the ceramic bodies, it is common to have dimensional defects in the final products after the drying and firing processes. Moreover, the kaolinitic structure and the presence of aluminum hydroxide confer a refractory behavior to the local clays. This impairs sintering during the firing operation. In the case of clay ceramics for civil construction, this results in greater porosity associated with elevated values of water absorption and low mechanical strength [3,4]. To avoid these problems, it is necessary to reformulate the ceramic body composition. The addition of both non-plastic materials to reduce plasticity and fluxes to condition the refractoriness is a possible alternative."

Jan 1, 2008

By Mariane Costalonga de Aguiar, Carlos Mauricio Fontes Vieira, Sergio Neves Monteiro

"This work evaluates the effect of incorporation of an ornamental rock waste into an industrial clayey body used for roofing tiles fabrication. Formulations with 0, 10, 20 and 30 wt.% of waste were prepared by replacing the sand in the industrial clayey body. The plasticity of the formulations was determined by the Atterberg limits. Specimens were fabricated by 18 MPa press-molding and then fired from 850, 950 and 1050°C. The specimens were tested to determine the water absorption, linear shrinkage and three points bending flexural strength. The results indicated that the waste improves the extrusion performance of the clayey body by decreasing its plasticity. The use of the waste was beneficial to the water absorption and mechanical strength of the fired clayey ceramic at 1050°C.IntroductionOrnamental rock is a natural resource available in the municipal area of Santo Antonio de Padua and located 150 km from the city of Campos dos Goytacazes, northe of state of Rio de Janeiro, Brazil. Intense industrial activity related to ornamental stones, especially gneisses, is traditionally occurring in the region. After mining, the flagstone is submitted to sawing to obtain blocks and then, after a manual operation, the final products are small flagstones [1,2]. During the sawing operation, a sludge composed of water and fine particles of rock is generated. A monthly production of 1000 tons of ornamental rock waste is estimated to be produced at Santo Antonio de Padua. The final disposal of this waste has brought serious environmental problems. Since most industries do not have an adequate sludge treatment, the waste is contaminating the soil and underground waters as well as obstructing rivers and lakes.Ceramic bodies industrially fabricated in the municipal area of Campos dos Goytacazes, 280 km from the city of Rio de Janeiro, are still empirically elaborated using a mixture of local clays. These clays are predominantly kaolinitic mineral, associated with high plasticity. Due to the excessive plasticity of the ceramic bodies, it is common to have dimensional defects in the final products after the drying and firing processes. Moreover, the kaolinitic structure and the presence of aluminum hydroxide confer a refractory behavior to the local clays. This impairs sintering during the firing operation. In the case of clay ceramics for civil construction, this results in greater porosity associated with elevated values of water absorption [3,4]. To avoid this problem, it is necessary to reformulate the ceramic body composition. The addition of both non-plastic materials to reduce plasticity and fluxes to condition the refractoriness is a possible alternative."

Jan 1, 2011

By Yang Xianwan, Zhu Xiaoyun, Guo Zhongcheng, Zheng Yanping, Zhai Dacheng

"Corrosion resistance of RE-Ni-W-P-SiC composite coating and 3 l6L stainless steel in corrosion media of H2SO4, HCl, H3PO4 and FeC13 solutions at different concentrations by means of immersion methods and anodic polarization curves obtained by DHZ-1 electrochemical synthetic tester and HDV-7 transistor constant potentiometer. Immersion experiment results show that corrosion rate of RE-Ni-W-P-SiC composite coating as-deposited in HCl solutions increases with the rise of HCl concentrations, on the contrary, the corrosion rate of the composite coating after heat treatment decreases with increasing the HCl concentrations the corrosion rates of the coatings as-deposited and after heat treatment in H2SO4 and H3PO4 solutions respectively decrease with the rise.of H2SO4 and H3PO4 concentrations the corrosion rate of the deposit as-deposited in FeC13 solutions decreases with increasing FeC13 concentrations, while the rate of the composite coating after heat treatment increases .with the rise of FeC13 concentrations.In addition, the corrosion rate of 3 l 6L stainless steel in the corrosion media of H2SO4, HCl, H3PO4 and FeC13 solutions at different concentrations increases with rising of concentrations. Furthermore, the corrosion rate of 316L stainless steel in the corrosion media of H2SO4, HCl, H3PO4 and FeC13 solutions respectively is much greater than that of the RE-Ni-W-P-SiC composite coating as-deposited and after heat treatment in the same corrosion media.1. IntroductionAll the materials and their products, when processed, stored and used, it is inevitable that the corrosion, wear, fatigue and crack occur owing to the actions of surroundings. Those early failure and abrasion, through all kinds of departments and profession that corrosion consumes one percent of tens of the steel products of the whole world; and two or four percent of the GDP is lost because of the corrosion."

Jan 1, 2000

By J. L. Holman

The Bureau of Mines is investigating recovery of Ni, Co, Cr, and other metals from mixed contaminated supera110y scrap. The scrap is melt-refined and cast into anodes for electrodeposition of recyclable Ni-Co alloy. Melt oxidation using roasted superalloy grinding sludge as oxygen source can divert the Cr to the slag but with excessive Ni-Co loss. Melt oxidation-carburization or direct melt carburization retains -95 pct of the Ni-Co in the anode alloy. With direct carburization, -90 pct or more of the Cr and other refractory metals report to the anode alloy, largely as carbide phases insoluble in electrolysis. Electrorefining data relate parameters such as controlled cathode potential, Fe and Cr impurities, pH, and compartmented cell use, to current efficiency and Ni-Co deposit quality. Recovery of -90 pct of the Ni-Co in the scrap can be achieved. Preliminary experiments to recover Cr, W, and other metals from the anode sludge and other byproducts are discussed. 347

Jan 1, 1987

By M. Nilmani, H. Pham

"A mathematical model was developed for the dissolution of particles in gas-stirred liquid baths, linking the hydrodynamic flow field of the bath, the average particle trajectory and liquid-side mass transfer controlled dissolution kinetics. The model was validated by comparison with experimental data for the dissolution rates of urea particles in gas-stirred aqueous CaCl2 solutions measured during this study. The dissolution rates of urea. particles were measured using an image analysis system.The effects of operating conditions on the dissolution rates of urea particles were investigated. It was found that the key operating parameters influencing the utilisation efficiency of particles were the gas flowrate, particle diameter and lance submergence. An optimisation of the operating conditions for the model urea-aqueous CaCl2 system indicated that the utilisation efficiency increased with decreasing gas flowrate and decreasing particle size for a given lance submergence.IntroductionThe utilisation solid reagents in molten baths varies from one process to another, depending upon the rates and mechanisms of the reactions between the particles and melts, as well as the trajectory and residence time of the particles in the melts. Previous studies have not attempted to predict the utilisation efficiency of injected solids by coupling the motion of the particle with its dissolution rate. Instead, the particles have usually been assumed to remain suspended in the bath until completely dissolved, and the mass transfer coefficients were based on the average specific mechanical energy dissipation rates in the bath. Investigations of this nature relevant to the present study have been undertaken by Apelian et al. [1], Brucato et al. [2] and Langberg and Nilmani[3]. The objective of the present study was to develop a mathematical model, incorporating both the reaction kinetics between the particles and liquid and the particle motion simultaneously, to predict the dissolution rates and times of the particles. The mathematical model was validated by comparison with experimental dissolution rates of a cold model analogue system measured using an image analysis technique, and then applied to optimise the operating conditions in the model system."

Jan 1, 1996

By Shengli Wu, Laixin Wang, Minyin Kou, Xinliang Liu, Weidong Zhuang, Yujue Wang

COREX process has obvious advantages in environment protection but still has some disadvantages, for example, it has a higher sulfur content of hot metal than blast furnace. In this paper, the thermodynamics and dynamics of desulfurization have been investigated to obtain the main operation parameters related to the mass fraction of sulfur in the hot metal. In addition, statistical analyses have been carried out to study the relationship between operating parameters and sulfur content of COREX hot metal based on actual plant data. It has been found that the mass fraction of sulfur in hot metal is significantly influenced by the C content in hot metal, MgO/Al2O3 in slag, the concentration of MgO in slag, the temperature of hot metal and binary basicity (R2).A linear model has been developed and subsequently used for reducing the mass fraction of sulfur in hot metal, improve the quality of hot metal and contribute to low carbon ironmaking.

Jan 1, 2016

By Fabiola Alvarez, Ana E. Bote, Daniel Pasquevich

"The oxidation of aluminum and its alloys was extensively studied for improving the corrosion resistance in structural materials having high specific strengths. But this reaction involves the formation of a very thin barrier layer on the metallic pieces. Furthermore, the ·recent development of the directed melt oxidation process for producing metal-ceramic; composites has renewed the interest in the study of interaction between gases and metals. Oxidation experiments in the presence of different chlorine partial pressures and at different temperatures were performed in ·a thermogravimetric balance, and microstructures were analyzed by electronic microscopy and X-ray diffraction. The oxy-chlorination kinetics was determined and the oxide formed W(IS amorphous at temperatures below 600 °C and crystalline .at higher temperatures. The appropriate experimental conditions for the fastest completed oxidation was further determined.IntroductionThe use of fine powders for the manufacture of ceramic components has significant advantages. They include excellent sinterability; low sintering temperature and better microstructure leading to improved mechanical properties. The conventional method of producing fine oxide powders involves controlled precipitation and pirolysis of suitable salts. The main limitation of the high temperature decomposition route is the evolution of environmentally unacceptable and corrosive gases. Controlled precipitation of hydroxides from solutions of salts, followed by thermal treatment involves large volumes of solutions and the calcination step that can induce grain growth (1).Direct oxidation of aluminum metal for producing alumina powder requires high temperatures for the direct oxidation of molten Al alloys by a vapor phase oxidant process (2, 3) or high technological process like thermal plasma reactor ( 4).Oxidation of high purity aluminum (5, 6) below the melting temperature· is initially characterized by a nearly linear reaction rate, followed by a rate which decreases rapidly with further weight gain. However, the oxidation rate of an aluminummagnesium alloy is much faster and it does not conform to any common oxidation law, but it is nearly parabolic at temperatures between 200 and 400 °C, an nearly linear· above 400 °C."

Jan 1, 2000

By Tetsuro Ohashi, Tooru Matsumiya, Yoshio Abe

"The three-dimensional deformation of a continuously cast slab was modeled into two-dimensional deformation by developing the solidified shell of the slab. The developed solidified shell was divided into rectangular elements. The thermal strain produced as the slab is wi thdrawn over one roll spacing in the casting direction was calculated from the temperature change during that time and the increment of the geometrical unbending strain during the time was calculated from the change in the radius of curvature of the slab by assuming that the neutral axis of bending is located at the mid-thickness of the slab and that the transverse section of the slab is kept in a plane during unbending. These strains were imparted to each element as initial strains. The interaction between the elements and the overall deformation of the solidified shell were analyzed by the finite element method.The analysis was performed on a slab being cast on a machine of the circular arc type with progressive unbending. The following findings were obtained as a result. The effect of unbending is spread in the upstream and downstream directions of the slab by the shear deformation of the narrow and wide faces. As the shear deformation increases, the strain in the unbending zone decreases and the strain outside of the unbending zone increases. The effects of secondary cooling conditions, slab size, radius of caster circular arc section, compression casting, etc., were also analyzed. IntroductionTo develop a method for preventing the internal cracking of continuously cast slabs, it is important to acurately analyze the deformation of the slab and this subject has been extensively investigated. Many researchers, including the present authors, have analyzed slab bulging. (1)- (11) Analysis has also been made of thermal deformation that assumes importance in continuous casting of small-section blooms.(12)-(18) However, unbending deformation, an extremely important subject for continuous casters of the circular arc type, has not been fully analyzed."

Jan 1, 1986

By Jillian Spindura

This work investigates the carbothermic reduction of the complex sulphide mineral, pentlandite, in the presence of lime. The effects of change in temperature and the use of different carbon sources are studied and the role of these variables on the reducibility of pentlandite mineral is discussed. The microstructures of the heat-treated pellets are examined using X-ray diffraction and scanning electron microscopic techniques. The latter analytical method also allows any variation in the morphology and composition of the metallic phases formed, with temperature, to be considered. The kinetics of the reduction process is studied and the magnitude of the overall activation energy is determined from the plots of percentage reduction versus time.

Jan 1, 1996

By H. Soto, J. Jara, F. Nava

A method has been developed to recover cyanide and copper from solutions containing copper complexes and thiocyanate. Copper is precipitated as copper thiocyanate or as copper cyanide depending on pH and the concentrations of thiocyanate and cyanide in the effluent. The copper precipitate assays over 50% copper and presents good dewatering characteristics. After settling it can be separated from the effluent by filtration. The solution containing the bulk of the cyanide is then oxidized with ozone to transform the remaining thiocyanate into cyanide. This results in a regenerated solution rich in free cyanide that can be recycled to the cyanidation process. Careful control of the pH of the solution is required. First, pH of the effluent is lowered to optimize the precipitation and oxidation stages, then the pH is restored to an alkaline value to regenerate the cyanide solution. Recoveries of over 96% copper and cyanide were obtained in laboratory tests using industrial solutions. With this procedure, cyanocidic gold/copper ores could be treated economically by heap leaching, since the cyanide consumed by the copper impurities could be regenerated at very low cost (most of the cost of cyanide regeneration would be compensated by the copper credits). In order to achieve this, a bleed of the barren solution could be treated by the proposed method, and then recycled to the leaching step. The volume of solution to be treated should be large enough to keep a cyanide/copper molar ratio higher than 3:1. This would assure that copper does not cause undue interferences in the leaching or the carbon adsorption stages. If the thiocyanate content is low, the oxidation stage can be avoided, and the solution can be recycled to the leaching stage directly after the solid-liquid separation stage.

Jan 1, 1997