By Horace Mann

A FEW years ago, it was generally thought that from 15 to 18 per, cent. of zinc oxide was the upper limit of a workable lead blast-furnace slag. With slags above this zinc-oxide content, the furnaces gave so much trouble because of hearth, wall, and crucible accretions that the campaign was very short. The time lost in cleaning out the frozen furnaces, for it was seldom possible to blow them out, and blowing in was so great that it was considered uneconomical to attempt the running of high-zinc slags, even if this were metallurgically possible. It is true that there are, references to one or two slags much higher in zinc than the foregoing,1 but the average smelterman regarded these, as freaks and not to be considered for regular furnace work. One or two plants, notably the plant of the United States Smelting Co, at Canyon City, Colo., ran charges, higher in zinc. At this plant, the zinc-oxide content of the charge was frequently 20 per cent. and higher but the slags from these furnace's seldom ran over 10 to 12 per. cent. zinc oxide. The furnaces were run with a large volume of air under a relatively low pressure, a low smelting column, and a very hot top; as a result, a large amount of zinc was volatilized. Even with the low smelting column and hot top, accretions caused much trouble and barring, down was a daily occurrence. At the time most of the theories on lead blast-furnace work were promulgated or worked out, it was necessary to run a furnace with a cold top in order to avoid an excessive loss due to fines and fume. At the same time, the smelting conditions had to be such that the lead and silver would be reduced and would enter the bullion. The slag had to be liquid but the charge must not give excessive accretions either in the hearth or on the walls of the furnace. This forced the operators to run the furnaces with a comparatively low blast, which, in turn, caused a small fuel consumption per unit of time with the accompanying result of a low working temperature.

Jan 8, 1925

By Oliver Smalley

EXCEPT for the work of Guillet, who conducted a systematic investigation on the zinc-replacing value of nickel in brass, and extended his investigation with a view to developing commercial high zinc content nickel brasses, the author does not know of any systematic research on the subject. The most promising commercial alloys and their physical properties obtained by Guillet are given below: Maximum Elonga- Reduction Copper Zinc Nickel Stress, tion, of Area, Brinell Tons Per Per Cent. Per Cent. Sq. In. 55.0 41.0 5.0 24.4 46.5 94 Sand cast. 22.6 27.0 90 Chill cast. 56.7 39.74 3.35 30.0 43.0 51.7 97 Casting annealed 2 hr. at 750° C. 33.9 33.0 50.7 144 Cold-drawn bar. 55.15 42.3 2.24 29.8 33.0 116 Casting annealed 2 hr. at 750° C. 32.3 29.0 151 Cold-drawn bar. These test results scarcely justify the use of such quantities of so expensive a metal, and could have been obtained from ordinary commercial brass. For purposes of comparison, the physical properties of ordinary brasses, ranging from 70 per cent. to 50.1 per cent. Cu in both the cast and normalized1 conditions are included in Table 1. These incidentally furnish a useful standard of the properties of castings and of rolled, extruded and forged brass when correctly annealed. A close study of some of the well-known special brasses containing nickel reveals a series of alloys which bewilder by their complexity, and one can only hazard a guess at the function and commercial value of each of the many elements used.

Jan 10, 1925

By A. I. Krynitzky, Henry S. Rawdon

The most commonly used material for terminals in spark plugs is commercial nickel wire, because of its relatively high temperature of melting, excellent heat conductivity, and slow rate at which the metal is oxidized, even upon continued heating at high temperatures. The grade commonly used for this purpose averages 97 per cent. nickel, the remainder being manganese, cobalt, iron, copper, with traces of other impurities always found in commercial nickel. A peculiar and interesting type of deterioration that occurs in these nickel terminals during the service life of the spark plug was recently brought to the attention of the Bureau of Standards. Commercial spark plugs vary greatly in their size and shape and the terminals differ considerably as to their relative size, shape, number, and arrangement with respect to one another. Although this defect was studied in detail in only one form of spark plug, the deterioration is a characteristic of the material, i.e., of nickel wire, rather than of the particular type of spark plug in which it was noted and studied. The mechanical features of the plugs, however, have a considerable bearing on the time required for the deterioration to become serious. The results of this study of the deterioration of nickel terminals in service should be of value to the makers of all types of spark plugs in which the terminals are made of this metal. CharacteR of Deterioration of WIres During Service Macroscopic Appearance and Properties of Changed Wire.—The nickel terminals in which the deterioration was studied were taken from spark plugs having a central terminal with the ground or side terminals attached firmly at both ends to the shell of the plug. In some of the plugs, two side terminals were used, one on each side of the central one. Although both terminals were found to have deteriorated to some extent, the attack of the central one was quite negligible compared to that of the side ones. These latter wires had developed, in service, transverse cracks that, in many cases, were as sharp and definite as a knife-cut. After a separation occurred, the breach widened by loss of material from the

Jan 1, 1921

By J. A. Cahill, A. D. Kirshenbaum

Using an alumina or zirconia crucible with an alumina sinker or a molybdenum sinker coated with zirconium dioxide, the density of liquid iron was determined by the immersed-sinker method over the temperature range of 1800" to 2500°K. The density, with respect to temperature, is ex-Dressed by the equation Dg/cm = 8.523 - 8.358 X 10 T'K The molar Volumes and thermal coefficients of expansion were calculated. Iron, upon me1ting, was found to expand 3.5 pct. A basic knowledge of the physical properties of materials at high temperatures is becoming increasingly important. A check of the literature shows, that in spite of the importance of iron, very few measurements have been made of its physical properties in the liquid state. Density measurements have been made by Benedicks and his collaborators1g using the method of balanced columns, by Desch and smith4 using the immersed sinker method with an alumina sinker, by Lucas using the maximum bubble method5 and by Stott and endall' who used an alumina pyknometer. In the method of balanced columns, the difference in level of molten iron in two arms of a U-tube, together with the corresponding difference of pressure had to be measured. The formation of gas bubbles in one or both arms was a great source of error. These values are very erratic. They vary from 6.83 to 7.45 g per cm3 at the melting point (1805"~) and from 6.45 to 7.15 g per cm3 at 1890°K. Stott and Rendall determined the density at 1837"K, with a reproducibility of *0.2 pct. They used an alumina pyknometer fired to 1973°K. The vessel was filled in a vacuum furnace by immersion in the liquid metal. When thermal equilibrium was attained, the pyknometer was withdrawn, cooled, the ingot removed and then weighed. The chief disadvantage of the method was the difficulty of inserting the pyknometer without cracking it. The authors have been able to determine the density of liquid iron from its melting point up to 2500°K, by using the immersed-sinker method, with A1203 or ZrOz crucibles and A1203 or molybdenum sinkers coated with Zr02, Fig. 1. EXPERIMENTAL Apparatus. In these studies the source of heat was the carbon tube resistance furnace with an argon atmosphere described previously.7 Experimental runs were made using either Ala3 or ZrOz crucibles. The sinkers used were 1) pure A1a3 and 2) molybdenum coated with ZrOz. The crucible, 2 1/8 in. in diam and 3 in. high, was centered in the furnace on an Ala3 of Zr02 pedestal. The sinker, 1/2 in. in diam and 1 1/2 in. long, together with a counter weight, was suspended from an analytical balance into the melt by a molybdenum wire. Procedure. The procedure, as described previously,' consisted in measuring the weight loss of the sinker in the liquid iron while determining simultaneously the liquid iron temperature by means

Jan 1, 1962

By C. K. Stoddard, R. G. Knickerbocker, E. T. Leidigh, R. R. Lloyd, K. L. Mattingly

DURING July 1941, a study was initiated at the Boulder City Experiment Station of the Bureau of Mines on proposed methods for the production of magnesium metal. The major emphasis was placed upon development of a process that required minimum reliance upon the sale or utilization of by-products to meet economic competition from processes already in operation. It was felt that only through the development of such a process could the nation's vast resources of dolomite and low-grade magnesite that are contiguous to large blocks of firm power be properly utilized. During the course of exploratory tests on electrolytic and electrothermic processes, it was noted that fused magnesium chloride would dissolve appreciable quantities of magnesium oxide in the presence of small amounts of boric oxide. The use of such a solution in an electrolytic cell employing a graphite anode and a steel cathode caused the deposition of magnesium at the cathode and the evolution of carbon oxides at the anode with minimal amounts of chlorine The original results were sufficiently encouraging to justify further investigation on an enlarged scale, since the process seemed to present advantages over other proposed processes 1.2 for the direct use of magnesium oxide in a fused chloride electrolyte. When work on a larger scale was initiated it was found that the addition of boric oxide to the electrolyte resulted in dispersion of metal and constantly decreasing current efficiency. However, by this time solubility studies had shown that magnesium oxide was sufficiently soluble in magnesium chloride melts containing no boric oxide to effect the same anode reactions, and development work was continued. Over two years of development work have been carried out, and considerable work remains to be done. It is desired to emphasize the fact that many of the difficulties met require a long period of continuous operation before they become serious enough to affect operation of the cell. ACKNOWLEDGMENTS This paper is one of many reporting on various aspects of the Bureau of Mines' program initiated in August 1939 by passage of the Strategic Minerals Act the scope of which was greatly expanded by subsequent legislation. Some of these papers are published as war minerals reports. others as bulletins, technical papers, reports of investigations

Jan 1, 1945

By W. F. Chiao, R. B. Gordon

Tile sharp-yield point found in magnesium crystals in the solulion-treated and aged condition is studied by dislocation internal-friction experiments. The results show that the sharp yield is not file to the sudden release of pinned dislocations hut is movc likely due to the rapid multiplication of an initially small number of dislocations. Recovery or the dislocation internal friction after deformation is also studied. This yecovery results from the re-pinning of dislocations by a solute, presumably nitrogen, which moves with a relatively small activation energy. SHARP-yield points, when they occur, are a striking feature of the stress-strain curve generated during a tensile test. Although commonly associated with steel, sharp yielding has been found in a variety of metallic and nonmetallic crystalline materials. In particular, sharp-yield points have been found in zinc"' and cadmium3 containing nitrogen. With this background, Geiselman and Guy4 investigated the tensile properties of magnesium single crystals containing nitrogen to see if sharp yielding also occurs in this system. They found that sharp yields did indeed occur in solution-treated and aged specimens tested at elevated temperature but were not able to give conclusive proof that the sharp yield was caused by nitrogen, a yield drop being observed even in their purest crystals. Sharp-yield points have also been found in various polycrystalline magnesium alloys.7'8 In the study of the sharp-yield phenomenon it is desired to observe the behavior of dislocations in the earliest stages of the deformation process. Internal-friction experiments are useful for this purpose because dislocation damping is sensitive to the mobility of free-dislocation segments. At low strain amplitudes the damping, A, due to the the forced vibration of dislocation segments of average length L is ? =KAL4 [1] where A is the dislocation density and K, if the applied frequency is well below the resonant frequency of the dislocation segments? is a constant for the sample under observation.5 Dislocation damping, because of the fourth-power dependence on L, is particularly sensitive to the creation of free-dislocation segments during deformation. Since sharp yielding is associated with the sudden release of pinned-dislocation segments, marked changes in the dislocation damping are expected at the yield point.6 The use of the dislocation-damping observations to help elucidate the incompletely understood mechanism of yielding in magnesium is the primary objective of the experiments reported here. PROCEDURE Many investigations have shown that very marked and rapid changes occur in the dislocation damping of of a deformed material as soon as the straining is stopped.5 It was quite essential, then, for the purpose of this investigation, to make the damping measurements during the deformation of the samples. This can only be accomplished through the use of the ultrasonic-pulse method. In this method traveling sound-wave pulses are used and, in contrast to resonating-bar methods, only the sample ends are set in vibration. Thus, the sample can be gripped along its sides in the tensile-test machine without disturbing the damping measurements. In the pulse method, the decrease in the amplitude of a sound pulse is measured as it travels back and forth through the sample. If A is the amplitude after traversing a distance x and A. is the initial amplitude, A=Aoe-ax [2] and a is called the attenuation. It is commonly measured either in units of cm-I or as db per µ sec. The observed attenuation in a metal sample is due to a number of causes. These include scattering by grain boundaries and impurity particles, thermo-elastic damping, diffraction effects, stress-induced ordering of solute atoms, and dislocation damping. The total observed attenuation in a given sample usually cannot be resolved into these various components, but changes in a due solely to changes in dislocation damping can be accurately determined, provided the experiment is arranged so that all other sources of damping are held constant. It is desired to reduce the extraneous sources of attenuation to a minimum and for this reason the experiments are done on single crystals of high purity. Magnesium crystals offer the further advantage that, when properly oriented, only a single set of slip planes is active during deformation. Crystal Preparation. The method of sample preparation is similar to that of Geiselman and Guy.4 The starting material was high-purity, sublimed magnesium rod supplied by the Dow Chemical Co. Melting under Dow 310 flux was used to reduce the nitrogen content of the starting material: the fluxing was done under an argon atmosphere and the

Jan 1, 1965

By Ralph H. Sweetser

Carbon in pig iron is not only essential but, ordinarily, it is the most abundant metalloid present; iron without carbon could not be pig iron. Carbon in pig iron has been accepted, but seldom specified. How it gets into the pig iron as it is being smelted in the blast furnace, and why just about so much of it enters into the pig iron in certain blast furnaces, and more of it,; or less of it, enters the pig iron in other blast furnaces, or in the same blast furnace under varying conditions, are problems that have not yet been satisfactorily solved. During my own practical blast-furnace experience, I collected analyses of pig iron, including the graphitic and combined carbon, and recorded them in reference to the percentage of silicon present, having in mind the generally accepted explanation that "silicon drove out the carbon." To this actual experience, I have added some analyses given to me by J. B. Rogers, who was superintendent of the blast furnaces of the Ashland Iron & Mining Co., Ashland, Ky., and was making "silvery iron" at the time. These analyses are shown in Table 1. The analyses do not tell the whole story, but they show that with Pocahontas beehive coke, the total carbon was generally high. The data relating to the composition of the slag are lacking but my own customary practice was to have a rather basic slag. During my experience in making pig iron for the Bessemer and open-hearth departments, there were times when the steel men would complain about some mysterious quality in the pig iron that caused bad steel, in spite of the fact that the percentages of silicon, sulfur, phosphorus and manganese were within the specifications. Many reasons were advanced for this undetermined "poison" in the pig iron, but the favorite one offered by the steel men was that the blast-furnace man had "oxidized" the pig iron at the tuyeres in his eagerness to get big production and low cost. To these complaints of the users of steel-making pig irons were added those of the gray iron-foundry men and the malleable iron men. These groups are unaninlous in their conclusions that the trouble lies with the blast-furnace men; but there is not yet any harmonious conclusion as to the exact cause and remedy.

Jan 1, 1927

By H. l. Burghoff, J. S. Porter

This paper presents the results of an investigation of the effect of cold-working and annealing treatments upon the occurrence of preferred orientation in annealed brass wire. The subject has received less consideration than has the same phenomenon in annealed brass sheet or strip, and perhaps very properly so in view of the obvious and undesired results obtained in the forming or drawing of strip having preferred orientation, which results are in contrast with the lack of any spectacular visual evidence in wire. The factors of cold-working and annealing that control preferredness in strip are naturally expected to function similarly in wire. Indeed, one might expect the condition to be commoner in annealed wire, because the severity of the cold-working between anneals in commercial Practice is usually much greater for wire than for strip. For example, a wire that is to be finished in the annealed condition on a diameter of 0.040 in. is commonly subjected to a final reduction of 90 per cent between the last two anneals, the large reduction being accomplished in the successive drafts of a multiple-die machine. Wire for rivets, for instance, on 0.125-in. diameter, although given a slight reduction of about Io per cent after the final anneal, may have been given a prior reduction of 75 to 80 per cent. Barrettl states the fiber axis of annealed 70-30 brass wire to be [111], with some indication of [IOO] as a secondary fiber axis. Croft and Sachs2 have reported briefly on some differences in brass wire with random and with preferred orientations. They showed statistical plots of the twin-band angles with respect to the wire axis or direction of drawing as observed on an axial plane. They also pointed out that the resistance of the wire to corrosion-cracking when externally stressed and exposed to a mercurous nitrate solution decreased as the degree of the preferred orientation increased. Material and PRocedure All the wire for the investigation was processed from one portion as cut for extrusion from a cast billet of the following analysis: 70.13 per cent copper; 0.01 lead; 0.01 iron; 0.02, nickel; 29.83 zinc (by difference). The billet section, 8 in, in diameter, was extruded hot to 3/4-in. diameter, after which it was processed by alternate cold-drawing and annealing treatments as indicated in Fig. I. The earliest anneals in process were at about 1100°F. and the next to the last reductions by drawing were 58 per cent. The diameter of the finally annealed wire was 0.132 in. Semifinal anneals were at 800°F., 950°F. and 1100°F. and reductions of 47.5, 74, 83.5 and 89.5 per cent were employed in drawing to 0.132 in. The final anneals were at 87s°F., 1050°F. and 1250°F. and were

Jan 1, 1944

By H. l. Burghoff, J. S. Porter

This paper presents the results of an investigation of the effect of cold-working and annealing treatments upon the occurrence of preferred orientation in annealed brass wire. The subject has received less consideration than has the same phenomenon in annealed brass sheet or strip, and perhaps very properly so in view of the obvious and undesired results obtained in the forming or drawing of strip having preferred orientation, which results are in contrast with the lack of any spectacular visual evidence in wire. The factors of cold-working and annealing that control preferredness in strip are naturally expected to function similarly in wire. Indeed, one might expect the condition to be commoner in annealed wire, because the severity of the cold-working between anneals in commercial Practice is usually much greater for wire than for strip. For example, a wire that is to be finished in the annealed condition on a diameter of 0.040 in. is commonly subjected to a final reduction of 90 per cent between the last two anneals, the large reduction being accomplished in the successive drafts of a multiple-die machine. Wire for rivets, for instance, on 0.125-in. diameter, although given a slight reduction of about Io per cent after the final anneal, may have been given a prior reduction of 75 to 80 per cent. Barrettl states the fiber axis of annealed 70-30 brass wire to be [111], with some indication of [IOO] as a secondary fiber axis. Croft and Sachs2 have reported briefly on some differences in brass wire with random and with preferred orientations. They showed statistical plots of the twin-band angles with respect to the wire axis or direction of drawing as observed on an axial plane. They also pointed out that the resistance of the wire to corrosion-cracking when externally stressed and exposed to a mercurous nitrate solution decreased as the degree of the preferred orientation increased. Material and PRocedure All the wire for the investigation was processed from one portion as cut for extrusion from a cast billet of the following analysis: 70.13 per cent copper; 0.01 lead; 0.01 iron; 0.02, nickel; 29.83 zinc (by difference). The billet section, 8 in, in diameter, was extruded hot to 3/4-in. diameter, after which it was processed by alternate cold-drawing and annealing treatments as indicated in Fig. I. The earliest anneals in process were at about 1100°F. and the next to the last reductions by drawing were 58 per cent. The diameter of the finally annealed wire was 0.132 in. Semifinal anneals were at 800°F., 950°F. and 1100°F. and reductions of 47.5, 74, 83.5 and 89.5 per cent were employed in drawing to 0.132 in. The final anneals were at 87s°F., 1050°F. and 1250°F. and were

Jan 1, 1944

By Henry Rawdon

ONE of the most vital problems in the manufacture of steel at present is the occurrence of the defects that have been popularly termed "snow flakes," "flakes," or "scabs." Particularly is this the problem of many manufacturers who during the past 2 yr. have undertaken large-scale production for the first time. A study of the microstructure of such defective material throws considerable light upon the nature of these defects and is essential before measures may be taken for the elimination of the defects. Flakes do not appear to be found in the plain carbon steels; they have been found, however, in abundance in some of the simple alloy steels that are being used in such vast quantities; viz., nickel steel of the approximate composition, 0.40 carbon and 3.5 per cent. nickel, and in the chrome-nickel type. The present article summarizes the characteristic features of defective steel of the flaky type as they have been found by laboratory study of numerous specimens, and it aims to show the conditions within the metal that are favorable to the occurrence of this type of defect without entering into the details of mill practice (size of ingot, design of molds, rate of cooling, distribution of cooling stresses, etc.), all of which conditions appear to play a role in the production of these defects.

Jan 2, 1919

By B. H. Sage, W. N. Lacey

The results of an extensive experimental program relating to the effectiveness of gravel screens have been correlated. The factors considered in some detail include gravel size and condition of packing, sand size and size distribution, fluid velocity, fluid viscosity, and thickness and arrangement of grave! screens. Good agreement between calculated values based upon probability considerations and experimental results relating to the influence of the thickness of the gravel screen was obtained. All of these factors are treated in the correlation in order that their influence may be taken into account in ascertaining the characteristics of an effective gravel screen for a particular set of conditions. The details of the experimental program are not given in the present paper but a description of generalized behavior and typical experimental results are recorded in graphic form. Introduction Gravel screens have been placed in water and oil wells for a number of yearsl,2,3 with the dual objective of increasing the productivity and decreasing the entrance of sand into the well bore. An understanding of the factors controlling the effectiveness of gravel screens in this connection is of industrial interest because it will lead to the proper selection of gravel. Some of the fundamental considerations involved in the migration of sand through a coarser body of porous materials were investigated by Coberly and Wagner4 and further experimental work has been carried out by Gumpertz.5 Apparently the pertinent phenomena are somewhat complex and are influenced by many variables. The present paper deals with the prediction of the behavior of gravel screens under the conditions encountered in practice but does not attempt to discuss the experimental methods or results that were obtained as a background and upon which the prediction is based. Influence OF Gravel Screens upon Productivity The use of a gravel screen may increase the productivity of a well by increasing its effective diameter, and this constitutes one of the objectives of its use. The permeability of most gravels and coarse sands that are employed in practice is so large compared to that of the sand in place that relatively little loss in production rate will arise from the use of material fine enough to cause the desired resistance to sand migration. For example, in Fig. I is depicted the approximate variation in the permeability of closely sized spherical gravels under the conditions of packing likely to be encountered in screens. The dotted lines indicate the variation that might be found because of differences in packing. It should be realized that the permeability is not a single-valued function of the average grain diameter but is related to a large number of factors, including the size, the size distribution and the shapes of the particles. However, Fig. I does permit a rough estimation of the permeability of closely sized spherical gravels and shows that the permeability with even the smaller particles is very large compared to that of most petroleum production horizons.

Jan 1, 1942

By W. N. Lacey, B. H. Sage

The results of an extensive experimental program relating to the effectiveness of gravel screens have been correlated. The factors considered in some detail include gravel size and condition of packing, sand size and size distribution, fluid velocity, fluid viscosity, and thickness and arrangement of grave! screens. Good agreement between calculated values based upon probability considerations and experimental results relating to the influence of the thickness of the gravel screen was obtained. All of these factors are treated in the correlation in order that their influence may be taken into account in ascertaining the characteristics of an effective gravel screen for a particular set of conditions. The details of the experimental program are not given in the present paper but a description of generalized behavior and typical experimental results are recorded in graphic form. Introduction Gravel screens have been placed in water and oil wells for a number of yearsl,2,3 with the dual objective of increasing the productivity and decreasing the entrance of sand into the well bore. An understanding of the factors controlling the effectiveness of gravel screens in this connection is of industrial interest because it will lead to the proper selection of gravel. Some of the fundamental considerations involved in the migration of sand through a coarser body of porous materials were investigated by Coberly and Wagner4 and further experimental work has been carried out by Gumpertz.5 Apparently the pertinent phenomena are somewhat complex and are influenced by many variables. The present paper deals with the prediction of the behavior of gravel screens under the conditions encountered in practice but does not attempt to discuss the experimental methods or results that were obtained as a background and upon which the prediction is based. Influence OF Gravel Screens upon Productivity The use of a gravel screen may increase the productivity of a well by increasing its effective diameter, and this constitutes one of the objectives of its use. The permeability of most gravels and coarse sands that are employed in practice is so large compared to that of the sand in place that relatively little loss in production rate will arise from the use of material fine enough to cause the desired resistance to sand migration. For example, in Fig. I is depicted the approximate variation in the permeability of closely sized spherical gravels under the conditions of packing likely to be encountered in screens. The dotted lines indicate the variation that might be found because of differences in packing. It should be realized that the permeability is not a single-valued function of the average grain diameter but is related to a large number of factors, including the size, the size distribution and the shapes of the particles. However, Fig. I does permit a rough estimation of the permeability of closely sized spherical gravels and shows that the permeability with even the smaller particles is very large compared to that of most petroleum production horizons.

Jan 1, 1942

By J. D. Sullivan, Chester R. Austin, J. L. Nunes

IT is characteristic of most shales and surface clays that a bloated or vesicular structure is produced by burning to a sufficiently high temperature, usually about 150° to 200°F. above the normal maturing temperature used when making common brick of the same material. Early investigators recognized this phenomenon and attributed it to the release or expansion of gases in the vitrified piece. A number of theories have been advanced on the source of the gas and the manner in which it is evolved, but none has been proved conclusively. T. E. Jackson's1 early theory that bloating was due to oxygen evolved by ferric oxide in forming ferrous oxide or ferrous silicate was never substantiated by experimental work. Orton2 thought this explanation unlikely, as all clays should bloat at the same temperature, if this were true. He found that clays bloated in the range from 1100° to 1706°C. Also, many clays containing iron did not bloat at all, but fused. Orton also stated that oxidation of different types of carbon was a source of gas during burning of clay and should be expelled before vitrification was reached. Seger3 said that he had dissolved ferric oxide in glass with no apparent evolution of gas. Matson4 came to the conclusion that ferruginous days burned to vitrification in an oxidizing atmosphere did not have the iron in a ferrous form. According to Wilson,5 the gases responsible for bloating might be entrapped air, water, sulphur dioxide, carbon monoxide, oxygen, and hydrocarbons. He spoke of two causes of bloating: (I) incomplete oxidation below the vitrification temperature, and (2) decomposition of compounds and evolution of gases above the vitrification temperature. Decomposition of calcium sulphate was given as the principal example of the latter. Bleininger and Montgomery6 stated that if any time after vitrification began the evolution of gaseous matter was rapid enough so that pressure was produced within the day, bloating was certain to take place, and a vesicular structure would be formed. They recognized that initial structure, rate of heating, kiln atmosphere, and many other variables affected bloating. Work done by the Emergency Fleet Corporation7 indicated that clays suitable for bloating should be high in compounds of metallic oxides, carbon, sulphur, sodium, potassium, or other equivalent compounds, which either act as a flux or give off gas. Orton2 studied the chemical status of the carbon, iron, and sulphur in clays during various stages of burning, using a Huron shale that bloated under oxidizing or reducing conditions. He found that only a small amount of sulphur remained in the clay and that it could be detected only by dissolving the clay in hydrofluoric acid; i.e., the sulphur was in combination with the silica. Orton said that this sulphur was probably in the form of iron sulphide dissolved in the glass phase. The iron sulphide was not broken down by heating, but was dissolved in the basic slag or glass,

Jan 1, 1942

By H. R. Hanley

ONE of the most important contributions to the art of electrolytic zinc production-has been the aluminum cathode. This has been used in all major production: since its commercial development in 1916. The literature is replete with important contributions, some of which may have been replaced by better ones, but thus far there appears no other metal to take the place of aluminum as cathode material. Credit for this innovation goes to Sherard Cowper Coles, of England. When experi-menting on the extraction of-zinc from Broken Hill ore at Hayle, Cornwall, in 1893, he introduced the aluminum cathode, and in 1895 obtained British Patent-No. 20073. The reason for this dominant position of aluminum as cathode mate-rial in zinc sulphate electrolytes is its unique surface, to which electro-deposited metals usually do not tightly adhere. The metal must be of high purity for best results. It is possible to develop a starting-sheet method by which thin electro-deposited sheets of cathode zinc are made and stripped from a smooth aluminum plate. Such thin sheets of cathode zinc may be used as arc tine copper sheets in standard electrolytic copper-refinery practice. However, complications arise because of extreme warping of the zinc starting sheet after a .few hours of deposition, and thus special arrangements must be made to compensate for this abnormality.

Jan 1, 1938

By Ian William Wark, Keith Leonard Sutherland

MERCAPTOBENZTHIAZOLE and its sodium salt are marketed under the trade names Flotagen and Flotagen S respectively, for use as collectors for cerussite and other minerals. The structural formulas for sodium mercaptobenzthiazole and for sodium ethyl xanthate are: [ ] Chemically there is a resemblance between the two compounds, though the free acid (mercaptobenzthiazole itself) is much more stable than xanthic acid. Both are readily oxidized, e.g., by iodine to disulphides, and can be estimated by iodometric titration. Qualitatively they are similar as collectors in flotation, although there are quantitative differences between them that may be important in practice. It is deduced that the influence of the nitrogen atom is subordinated to that of the sulphur atoms, and that the dominant group of these compounds is the mercapto group -SH or -SNa. The general method of investigation has been based on contact tests. Two temperatures, 10º and 35º C., have been chosen, and with a standard concentration of 20 mg. per liter of mercaptobenzthiazole (i.e., of the free acid) the influence of alkali, cyanide and copper sulphate on contact at sulphide mineral surfaces has been studied. This standard concentration corresponds to about 19 mg. per liter potassium ethyl xanthate; it brings out the differences between the minerals better than a higher concentra-

Jan 1, 1939

By Keith Leonard Sutherland, Ian William Wark

Mercaptobenzthiazole and its sodium salt are marketed under the trade names Flotagen and Flotagen S respectively, for use as collectors for cerussite and other minerals. The structural formulas for sodium rnercaptobenzthiazole and for sodium ethyl xanthate are: Chemically there is a resemblance between the two compounds, though the free acid (mercaptobenzthiazole itself) is much more stable than xanthic acid. Both are readily oxidized, e.g., by iodine to disulphides, and can be estimated by iodometric titration. Qualitatively they are similar as collectors in flotation, although there are quantitative differences between them that may be important in practice. It is deduced that the influence of the nitrogen atom is subordinated to that of the sulphur atoms, and that the dominant group of these compounds is the mercapto group —SH or —5Na. The general method of investigation has been based on contact tests. Two temperatures, 10" and 35" C., have been chosen, and with a standard concentration of 20 mg. per liter of mercaptobenzthiazole (i.e., of the free acid) the influence of alkali, cyanide and copper sulphate on contact at sulphide mineral surfaces has been studied. This standard concentration corresponds to about 19 mg. per liter potassium ethyl xanthate; it brings out the differences between the minerals better than a higher concentra-

Jan 1, 1939

By Ian William Wark, Keith Leonard Sutherland

Mercaptobenzthiazole and its sodium salt are marketed under the trade names Flotagen and Flotagen S respectively, for use as collectors for cerussite and other minerals. The structural formulas for sodium rnercaptobenzthiazole and for sodium ethyl xanthate are: Chemically there is a resemblance between the two compounds, though the free acid (mercaptobenzthiazole itself) is much more stable than xanthic acid. Both are readily oxidized, e.g., by iodine to disulphides, and can be estimated by iodometric titration. Qualitatively they are similar as collectors in flotation, although there are quantitative differences between them that may be important in practice. It is deduced that the influence of the nitrogen atom is subordinated to that of the sulphur atoms, and that the dominant group of these compounds is the mercapto group —SH or —5Na. The general method of investigation has been based on contact tests. Two temperatures, 10" and 35" C., have been chosen, and with a standard concentration of 20 mg. per liter of mercaptobenzthiazole (i.e., of the free acid) the influence of alkali, cyanide and copper sulphate on contact at sulphide mineral surfaces has been studied. This standard concentration corresponds to about 19 mg. per liter potassium ethyl xanthate; it brings out the differences between the minerals better than a higher concentra-

Jan 1, 1939

By Charles Fulton

EXPERIMENTAL work on the process was begun on a laboratory scale at Cleveland, Ohio, in 1914, and transferred to East St. Louis, Ill. in 1916, where a commercial sized furnace was in technical operation until January, 1918. The essential steps of the process are as follows: Oxidized zinc ore or roasted zinc concentrate is mixed with crushed coke and coal-tar pitch and formed into briquets 9.25 in. (23.5 cm.) in diameter and 21 in. (53 cm.) long in a manner similar to that used in the manufacture of graphite or carbon electrodes, except that much less care and time are required. The composition varies with the nature of the ore; in one case, the composition was 100 parts ore, 70 parts coke, and 18 to 20 parts pitch. These briquets maintain their form and volume during and after the distillation of the zinc. This object is gained by using coke as the matrix and coal-tar pitch as the binder; this pitch becomes coke on heating and unites the ore particle and the original coke particle into a continuous mass. The briquet is an electrical conductor but only to such, a degree that it can be used as a resistor. The size of the ore, as in the present practice of zinc metallurgy, ranges from fine material, such as flotation concentrate, to coarse table and fine jig concentrate. The process is not restricted to any particular kind of ore, but is applicable to pure high-grade ores, ores high in iron, and complex zinc lead ores, since the residue from the distillation is held immovably in place within the briquet. In the case of complex zinc-lead ores, the distillation is conducted with a carefully regulated temperature so that a high percentage of lead is retained in the distilled briquet, which may then be smelted for its lead content. In present zinc smelting practice, the reduction fuel is from 40 to 50 per cent. of the weight of the ore. In the briquet, it is from 60 to 85 per cent. of the ore; but unless the ore is exceptionally high in residue, the distilled briquet

Jan 9, 1919

H. G. Haemers (Ghent University, Belgium)—The authors claimed "the results of their work indicate that the metals can be arranged in a sulfation series similar in its application for selective sulfation tot the electromotive series for displacement of metals from solution". The series as stated in decreasing order for tendency of SO3 give up, is the same as that stated by free energy diagrams. Indeed, the degree of stability of a sulfate is measured by the free energy of sulfate formation out of the corresponding metal oxide and SO3. The more negative the value of the free energy (-DG) the greater the stability of the sulfate. As a second consequence this statement results in a relative aptitude for capture of SO3 by each metal oxide when brought in contact with the sulfate of other metals. Let M1 and M1 be the two metals, and — DG1 and — DG2 their free energy values at temperature T. Both sulfates are stable at temperature T if - DG1 < O and — DG2 < O. In case where — DG1 < — DG2 the stability of M1SO4 is greater than that of M2SO4, and when M1O (oxide of

Jan 1, 1958

By Ian Wark

MERCAPTOBENZTHIAZOLE and its sodium salt are marketed under the trade names Flotagen and Flotagen S respectively, for use as collectors for cerussite and other minerals. The structural formulas for sodium mercaptobenzthiazole and for sodium ethyl xanthate are: Chemically there is a resemblance between the two compounds, though the free acid (mercaptobenzthiazole itself) is much more stable than xanthic acid. Both are readily oxidized, e.g., by iodine to disulphides, and can be estimated by iodometric titration. Qualitatively they are similar as collectors in flotation, although there are quantitative differences between them that may be important in practice. It is deduced that the influence of the nitrogen atom is subordinated to that of the sulphur atoms, and that the dominant group of these compounds is the mercapto group -SH or -SNa. The general method of investigation has been based on contact tests. Two temperatures, 10° and 35° C., have been chosen, and with a standard concentration of 20 mg. per liter of mercaptobenzthiazole (i.e., of the free acid) the influence of alkali, cyanide and copper sulphate on contact at sulphide mineral surfaces has been studied. This standard concentration corresponds to about 19 mg. per liter potassium ethyl xanthate; it brings out the differences between the minerals better than a higher concentra-

Jan 1, 1939