By W. Bradley, R. G. Hall

This paper will attempt to show how a metallurgical problem at one California quicksilver mine was solved, and how the solution was applied successfully at another mine. The pronouns "we" and "our," as used below, refer '0 the Bradley 'lining Co. of San Francisco. The term "concurrent firing" for the purpose of this paper can be defined as feeding and firing a a kiln at the same end—that is, of course, the upper end' This is as opposed to "countercurrent firing," the orthodox method, in which a kiln is fed at the upper and fired at the lower end. The terms "quicksilver" and "mercury" are used interchangeably. Early References The earliest work on nonferrous metallurgy, we believe, was The Pirotechnia of Vannocio Biringuccio,l its first edition having been printed in Italy in 1540. Quoting from its chapter entitled "Concerning Quicksilver and Its Ore": Quicksilver ... is one of the gods and has divine strength in itself, and also, to the annoyance of the alchemists, it is winged. Hence, when it sees that it is in gravest danger, it loosens itself from . . . every bond . . . and fies away into the heavens, escaping from the hands of those who crucify it. Almost laughing, it leaves all its adversaries mocked and scorned, with their phials and filters empty . . . How thorough a job, under certain conditions, it can do of mocking its adversaries and leaving their phials and filters empty, was found out four centuries later at the Sulphur Bank mine, on the east shore of Clear Lake, in Lake county, California, The other mine mentioned in the title is the Reed, in Yolo County, California, 35 miles by road southeast of Sulphur Bank, Reed and Sulphur Bank ranked respectively Nth and seventh in U. S. production in 1943. The earliest direct reference we can find to furnacing troubles at these mines was by Thomas Egleston in 1890.2 Speaking of Sulphur Bank, Egleston says: of there is more sulphur than cinnabar in the ore, which is a detriment to both . . . making the sulphur impure, and rendering the cinnabar difficult to work on account of the soot. In some of the early . . . furnaces the accumulation of soot from the excess of sulphur has been known to penetrate as far as the fan blower at the end of the . . . condensers, and completely prevent its revolution. In order to get rid of the inconvenience of this accumulation . . . , as well as to get a commercial value from the sulphur, it (the sulphur) is now separated by steam and sold. It is claimed that the sulphur alone pays all the expenses of ... the mine. The mine was first worked for sulphur, and the cinnabar it contained was considered to be an inconvenience, and was carefully picked out and thrown away, as its richness and value were not

Jan 1, 1949

By Leslie F. Tedsen, John E. Dorn, Alan E. Flanigan

It is necessary occasionally to use aluminum-alloy sheet where moderately elevated temperatures are encountered. Considerable attention has been directed toward determining the influence of "artificial aging" on the room-temperature properties of the precipitation-hardenable alloys, as testified by numerous company reports and by references I to 4. Investigations on the properties at elevated temperatures are few, however, and have not always covered the range of times and temperatures of greatest interest. The present investigation was instituted to overcome this deficiency. The work was done for the Office of Production Research and Development of the War Production Board, under the supervision of the War Metallurgy Committee, as a part of the "restricted" Project NRC-548. It has been released for publication by the Office of Production Research and Development. AS is well known, the high-strength aluminum alloys achieve their remarkable properties as a result of precipitation-hardening. In production they are subjected to a solution heat-treatment followed by quenching, to retain the supersaturated solid solution. The solution treatment is followed by "aging" (precipitation-hard- ening) either at room temperature or at a suitable elevated temperature. A considerable increase in tensile and compressive yield stresses results from precipitation at room temperature ("natural aging"). Through the elevated-temperature process ("artificial aging") it is possible to obtain values of yield stress considerably higher than those attainable by natural aging. The increase in yield stress is accompanied by a smaller gain in ultimate tensile stress and by a decrease in elongation. During the first stages of artificial aging the yield stress increases steadily until it reaches a maximum value. In this condition the material is said to be "fully aged." Further exposure results in "averaging," attended by a steady decrease in yield stress. In the production of the artificially aged materials, temperatures and times are selected to achieve full aging. The following important characteristics are associated with the process: 1. The higher the temperature, the more rapidly is the fully aged condition attained. :7

Jan 1, 1946

By Leslie F. Tedsen, Alan E. Flanigan, John E. Dorn

It is necessary occasionally to use aluminum-alloy sheet where moderately elevated temperatures are encountered. Considerable attention has been directed toward determining the influence of "artificial aging" on the room-temperature properties of the precipitation-hardenable alloys, as testified by numerous company reports and by references I to 4. Investigations on the properties at elevated temperatures are few, however, and have not always covered the range of times and temperatures of greatest interest. The present investigation was instituted to overcome this deficiency. The work was done for the Office of Production Research and Development of the War Production Board, under the supervision of the War Metallurgy Committee, as a part of the "restricted" Project NRC-548. It has been released for publication by the Office of Production Research and Development. AS is well known, the high-strength aluminum alloys achieve their remarkable properties as a result of precipitation-hardening. In production they are subjected to a solution heat-treatment followed by quenching, to retain the supersaturated solid solution. The solution treatment is followed by "aging" (precipitation-hard- ening) either at room temperature or at a suitable elevated temperature. A considerable increase in tensile and compressive yield stresses results from precipitation at room temperature ("natural aging"). Through the elevated-temperature process ("artificial aging") it is possible to obtain values of yield stress considerably higher than those attainable by natural aging. The increase in yield stress is accompanied by a smaller gain in ultimate tensile stress and by a decrease in elongation. During the first stages of artificial aging the yield stress increases steadily until it reaches a maximum value. In this condition the material is said to be "fully aged." Further exposure results in "averaging," attended by a steady decrease in yield stress. In the production of the artificially aged materials, temperatures and times are selected to achieve full aging. The following important characteristics are associated with the process: 1. The higher the temperature, the more rapidly is the fully aged condition attained. :7

Jan 1, 1946

By C. Dirksen

This study investigates whether oxygen consumption during segregated forward combustion may be affected by natural convection. Linear theory indicates that thermal instability occurs in a horizontal porous medium when the modified Rayleigh number N 'Ra exceeds a critical value of about 40. Most experimental results, including those described here, indicate this value to be about an order of magnitude smaller. N ', is derived from "differential similarity" and the proper time scale factor is also obtained. The critical value of N'ra for a horizontal, water-saturated porous medium at atmospheric pressure subjected to a uertical temperature gradient was found to be about 3.0. The ambiguity in the value of N'R, arising when fluid properties cannot be assumed constant is indicated. Natural convection was observed for oblique systems below N 'Ra , while simultaneous horizontal flow did not affect N Racrit. The expected range of values for the various parameters pertaining to segregated forward combustion is indicated and the corresponding values of N 'Ra calculated. Only under very favorable conditions, such as high permeability, high pressure and low top temperature, can the critical value of N 'R, be exceeded. Thickness of the convection layer should not become too large, since the time required to obtain significant mixing is proportional to the square of the thickness. For an oblique combustion frant the conditions for significant mixing may be less strenuous. LNTRODUCTION Laboratory1,2 and field314 experiments have shown that a markedly upgraded oil can be produced by in situ forward combustion. Under certain conditions injected air may move through a high permeability, gas-saturated channel over the oil-saturated layer, while combustion takes place, exclusively, at the horizontal interface (Fig. 1). Such a channel may be a natural gas cap, or it may result from a forward combustion process in which injected air and combustion gases fingered through the top of the formation, causing a premature breakthrough at the production well. In this particular case of segregated forward combustion, the air stream moves parallel to the combustion front. Molecular diffusion and transverse mechanical dispersion will be insufficient to cause all the oxygen in the air stream to reach the combustion front. When the oxygen in the air stream is not completely consumed in the combustion process, it will reach the production well and create a serious fire hazard. In addition, the reduced efficiency may make the process economically unprofitable while also serious corrosion problems may be experienced in the production we11.3 This undesirable situation should, therefore, be prevented. However, in a situation as depicted in Fig. 1, an unstable temperature gradient exists in the gas phase. The combustion is taking place at the lower boundary at a nearly constant temperature that may be anywhere from 600 to 1,200F, depending on the conditions. The upper boundary of the gas phase is overlying, impermeable rock; its temperature might be around 100F, but may increase to 300F or higher due to conduction and convection as the combustion process continues. This represents a steep temperature gradient and it is conceivable that under those conditions free or natural convection will take place in the gas

Jan 1, 1967

By B. S. Hickman

Using primarily quantitative single crystal X-ray techniques studies have been made of the precipitation of the metastable w phase in alloys of titanium with Mo, Mn, Fe, Cr, and Nb. It is shown that, in agreement with earlier work on the Ti-V system, the composition of the w phase during aging approaches a constant; the value varies from one system to another in a systematic manner with the electron concentmtion. Results relevant to the mechanism of w precipitation during quenching and during aging are presented and discussed. Results are presented to confirm that the w phase is coherent and the nzorphology of the Necipitates is described and discussed. PRECIPITATION of the metastable w phase in alloys of titanium is of interest because of its severe embrittling effect and also because of the enhancement of the superconducting properties which accompanies precipitation.1 The general features of w phase precipitation have been discussed by cuillan and by Bagaratskii et d3 The work described in this paper forms part of a general study of w phase precipitation which was undertaken to elucidate various unknown or controversial features of the process, namely: i) What is the mechanism of formation of the phase ii) How does its composition, morphology, volume fraction, and particle size vary with the type and content of the alloying element and with the heat treatment conditions? iii) What is the relation between the w phase and the equilibrium a phase? In a previous paper4 the results of a detailed study of w phase in Ti-V alloys were presented. It was shown that: U During aging the composition of the w phase approached a saturation value of 13.5 to 14.0 at. pct V. ii) w precipitated as cube shaped particles and once precipitation was complete, particle coarsening did not occur. iii) a phase formed initially by direct conversion of w-phase precipitates. In this paper similar measurements are reported on Ti-Mo alloys and some more limited data given on the Ti-Cr, Ti-Fe, Ti-Mn, and Ti-Nb systems. The results i.1 the six systems are then compared. It has been shown previously by electron microscopy that the w precipitates as ellipsoids in both the Ti-Nb system,&apos; and in i-o.&apos; Blackburn and williamsz3 have reported the precipitates in Ti-Fe, Ti-Cr, and Ti-Mn are cubic, i.e., similar to the Ti-V system.476 EXPERIMENTAL METHODS 1) Specimen Preparation. Samples of the compositions shown in Table I were prepared by arc melting. High purity electron beam zone refined titanium (Materials Research Corporation Grade I—total impurity content =250 ppm) was used; the other source materials are given in the table. A commercial Ti-8 wt pct Mn alloy was used for studies of this system. After homogenization the materials were rolled or cut into strip approximately 1/4 in. by 2 in.; the strip was then heated at temperatures of 1200" to 1300°C for several hours by passage of a direct current through the strip in an ultra high vacuum system (<10-torr) and then quenched by admitting high purity helium and switching off the current. This treatment resulted in crystals up to 2 in. by 2 in. by A in., almost all of which had a [100] direction nearly perpendicular to the plane of the strip. The crystals were cut from the strip by spark machining and their composition checked by lattice parameter measurements supported by chemical analysis. 2) X-Ray Diffraction Methods. Lattice parameter measurements were made using a modification of the single crystal spectrometer described by ond. In this technique the crystal angles for reflection on either side of a highly collimated primary beam are measured. Generally the 400 CuK, or the 400 CuKp reflections of the bcc lattice were used. In the as-quenched crystals a precision of 1 in 105 was obtained, but due to line broadening the parameters in aged materials could only be measured to 1 in lo4. This accuracy was, however, quite adequate for the purposes of these experiments and enabled the composition of the p phase to be obtained to 10.1 pct in all systems except Ti-Nb where the lattice parameter change with composition is very small. The precipitation and growth of the w phase was examined using a single crystal goniometer attached to a Phillips diffractometer. The relative intensities and line shapes of b-phase and w-phase reflections

Jan 1, 1970

By William G. Kegel

Apart from a usable product and good mining conditions, the greatest asset for a profitable coal mining organization is an effective mine maintenance program. The first step in achieving this is to have good mechanics-or men who want to be mechanics and are interested in knowing, more about the design and control of the machines in their charge. A good mechanic&apos;s knowledge and ability result from ambition, curiosity, and determination. Starting with these qualities, the aspiring mechanic can launch his career by learning all he can about mechanics, electricity, and hydraulics. Though the path is rough, the end result is rewarding. Mining machinery probably receives as much, if not more, abuse as any other heavy equipment in use today. Considering the conditions under which much of the repair work must be done, it is essential that the mine operator has the best men and tools to perform the work. Mining machines, from their inception, have utilized the electric motor; and down through the years of mechanization, this power source has undergone many changes to better adapt it to the job. The first motors used were direct-current (d-c) motors since d-c power was the most economical power source for mining at the time of early mechanization. These motors were large open-type machines which are seldom used in modern mining. Because of the mine environment, the d-c motor has been reduced in size to better suit the application in mining machines and is now manufactured with dust-tight or explosion-proof enclosures. The d-c motor is constructed with either (or both) series and shunt fields located on the stationary part of the motor (stator) and an armature coil wound on the rotating part of the motor (rotor). Power is supplied to the armature by brushes which are held stationary and make sliding contact with the armature. The brushes requires regular and careful maintenance because worn or defective brushes will cause heat or arcing which can destroy the motor. D-c motors can be used as d-c generators when mechanical power is supplied to them by the rotating

Jan 1, 1981

By AIME AIME

AMONG the European nations Germany is the center of interest economically as well as politically, and of prime importance for Europe as a whole is Germany&apos;s capacity to produce mineral products for armament and for export in exchange for the import of the essential supplies to maintain its industries. So far as minerals are concerned, Germany is worse off than any other great power except Italy, and deficiencies are being met by attempts to increase output from local deposits and by greater use of substitutes derived from domestic raw materials to replace imported metals, petroleum products, and other minerals.

Jan 1, 1939

By R. D. Pehlke, P. D. Goodell, R. W. Dunlap

The rate of dissolution of steel bars in molten pig iron has been measured experimentally in the temperature range 2300° to 2650° F. The rate of solution is shown to be a .function of bath composition, temperature, and stirring. A kinetic model based on carbon diffusion in the liquid phase has been derived to fit the experimental results. THE rate of scrap melting has long been an important variable in steelmaking operations. With the advent of the oxygen steelmaking process and the accompanying shorter heat times, the rate of scrap melting has now become one of the rate-limiting factors in steel production. As observed in commercial practice, the solution rate is influenced by the compositions of liquid and solid, the temperature, agitation, and time. However, no definitive work has been done on the Fe-C system, and there is very little information in the literature regarding the relative effects of these variables in steelmaking systems. A number of questions have been raised in regard to scrap utilization in basic oxygen steelmaking operations. Consideration has been given to the optimum size and shape of scrap, and to the use of preheated scrap as a means for decreasing the pig-iron requirement in oxygen blowing. The determination of an optimum scrap practice for a specific installation depends to a large extent upon the economics of the scrap market and also upon the behavior of scrap in the vessel. The present research was undertaken as a preliminary study in evaluating the behavior of steel in a pig-iron bath under various conditions of temperature, composition, and agitation, as might be encountered in oxygen converter operations or in any steelmaking operation where scrap behavior is an important process variable. Related studies have been carried out on non-ferrous systems. The solution rate of solid aluminum in a molten A1-Si alloy has been studied.&apos; Furthermore, the increasing use of liquid metals has created considerable interest in studies related to dissolution of a solid in a liquid, or mass transfer taking place between a solid interface and a liquid metallic phase.2-10 In an effort to clarify the relative importance of factors influencing the dissolution of scrap in Fe-C alloys, this paper presents the results of a study of the rate of dissolution of a low-carbon steel cylinder in a molten Fe-C bath at various bath compositions, temperatures, and conditions of agitation. An attempt has been made to determine the mechanism of solution, and a model has been derived to fit the experimental results. The rate of heat transfer between the molten pig-iron bath and the solid-steel cylinder has also been studied. EXPERIMENTAL PROCEDURE A molten bath of pig iron (nominal composition 4.2 pct C, 0.5 pct Mn, 0.8 pct Si)* was held in a 200- *In view of the fact that the composition of the pig-iron bath was slowly changing with time because of steel dissolution and reaction with the surrounding atmosphere, intermittent samples of the liquid bath were taken throughout each experiment, Table 1. lb induction melting unit. The internal diameter of the furnace was 8-1/2 in. and the bath depth approximately 14 in. Cold-finished 1020 steel cylinders of 1/2-, 3/4-, 1-, 1-1/2-, and 2-in. diameters were cut into 1 -ft lengths for use as test specimens. One end of each bar was machined to fit a hand-driven, mechanical stirring device which rested on top of the furnace. This fixture permitted 7 to 8 in. of the bar to be immersed in the melt. The steel cylinders were cleaned to free the surface of grease and oxide. The rods, at ambient temperature, were immersed into the molten pig-iron bath. The melt temperatures studied in this investigation were 2300°, 2500°, and 2650°F. Different agitation conditions were achieved by operating with a) the power to the furnace, giving induction stirring; b) induction stirring plus mechanical stirring, using hand rotation with a chain and sprocket assembly at approximately 200 rpm; c) mechanical stirring alone with the power off; and d) the power off and no mechanical stirring resulting in minimum agitation, i.e., only that caused by natural convection currents in the bath. The samples were immersed in the melt for prescribed times ranging from 30 sec up to 6 min. Immersion times were measured with a stopwatch and temperature control of the melt was achieved by power adjustment following temperature measurement with an optical pyrometer. The measurements with the calibrated pyrometer were checked out to within less than 10°F with simultaneous thermocouple measurements. Following immersion, the bars were water-quenched and the diameters were measured with a micrometer at several positions on the reduced area, and by volumetric displacement. The dissolution rates calculated from the

Jan 1, 1965

FRIENDS of the late Charles F. Rand presented in 1930 a sum of money from which the income is available to support various phases of the work of the Institute in which Mr. Rand was so deeply interested. At present the fund amounts to $10,400. The specific terms of the deed of gift are as follows: "The fund collected to establish a memorial to the late Charles F. Rand shall be placed in the custody of the Board of Directors of the American Institute of Mining and Metallurgical Engineers, to be set up as a trust to be known as the `Charles F. Rand Foundation,&apos; the income of which shall each year be applied to a distinct purpose to be decided upon in that year by vote of the Board of Directors. This purpose shall be such as to promote the general welfare of the Institute and to constitute a permanent memorial of the usefulness of Mr. Rand, who for many years gave unstintingly of his time and talents in its service. "It shall be within the discretion of the Board of Directors to establish a medal to be known as the Charles F. Rand Memorial Medal to be awarded at such a time and under such rules as may be determined by the Board of Directors, for Distinguished Achievement in Mining Administration." The establishment of this medal was announced at the annual meeting in February, 1932, the term "mining" being defined in its broad sense to include metallurgy and petroleum. Robert Linton is chairman of the Charles F. Rand Foundation Award Committee.

Jan 1, 1943

By T. D. Yensen

It is safe to say that of all the different materials that go to make up electrical machinery, iron is the most important. Upon its magnetic and electrical quality depends not only the efficiency of the machine but, to a very large extent, the cost. Aside from the mechanical strength, there are three characteristics of iron that are of importance in this connection, viz., magnetic hysteresis, electrical resistance, and magnetic permeability. In the homopolar machine, where the magnetic flux is unidirectional, permeability is the only important factor, but in all other machines the flux is reversed in one or more parts and causes losses due to hysteresis and eddy currents. The eddy-current loss depends largely upon the electrical resistance of the iron; the higher the resistance the lower the loss, under otherwise identical conditions. These hysteresis and eddy-current losses cause heating of the machine, and as they depend upon the magnetic density in the iron, this density must be regulated so that the heating shall not be excessive. If the hysteresis and eddy-current losses and the permeability of the magnetic circuit will permit an increase in the magnetic density, or, in other words, a decrease in the amount of iron, this in turn will mean a decrease in the amount of copper needed, with a consequent decrease in the copper loss. It is thus seen that, indirectly as well as directly, the above characteristics have an important bearing on both the efficiency and the cost of electrical machinery. In general, it may be said that iron for electrical machinery should have the following characteristics: (1) low hysteresis loss, (2) high electrical resistance, and (3) high permeability. These are the characteristics that investigators have been striving to attain since electrical machinery first came into use. Until the beginning of the present century, Swedish charcoal iron was regarded as the best grade of iron for magnetic purposes, and even now it ranks high among the various grades used. About that time Sir Robert Hadfield1 produced a number of iron alloys that revolution-

Jan 1, 1916

By Strathmore R. B. Cooke, Thomas E. Bam

The paper discusses the mineralogy, structure, and strength of magnetite pellets fired in air and in a neutral atmosphere at various temperatures. The information obtained from this investigation is used to explain the origin of the structures occurring in pellets produced by pilot-plant operation. MUCH experimental work has been performed on i-VL the mechanism of agglomeration and pelletiz-ing of moist ore and concentrates and on the process of firing agglomerates, but except for the work of Tigerschiold and Ilmonil much of the published information is empirical, and the literature contains no information concerning the structure of fired pellets. Results of a preliminary study of the micro-structures occurring in pellets produced both in the laboratory and on a pilot-plant scale are presented in this paper. Most of the results were obtained from pellets prepared from Mesabi magnetic taconite, but through the courtesy of the staffs of the Minnesota Mines Experiment Station and the Bethlehem Steel Co., fired pellets produced from limonite and hematite ores and from Lebanon magnetite have also been examined. The work has been restricted almost entirely to pellets produced without additives, the exceptions being those in which coal was added to the filter cake before rolling. Schwartz has described the microstructures occurring in ore sinters produced under reducing conditions.&apos; Many of the structures and constituents he describes are common to fired pellets, but the constituents normally occur in markedly different proportions. His statement that "in all satisfactory sinter the amount of hematite is small, perhaps not over 2 or 3 per cent" is inapplicable to pellets produced by pilot plant operation or by any process in which air is not deliberately excluded. Pilot plant pellets contain over 90 pct by weight of hematite, and those produced in the smaller furnaces of the Minnesota Mines Experiment Station contain more than 80 pct of that constituent. Preparation of Specimens It is difficult to examine unfired pellets microscopically because of their insufficient coherency to withstand sectioning and polishing. Fired pellets sometimes lack coherency and frequently contain holes which are troublesome during polishing. Impregnation of both air-dried and fired pellets is readily accomplished by the use of methyl metha-crylate monomer." The dry pellets are covered in a test tube with excess monomer, to which a small amount of accelerator has been added. When the test tube is placed in a cooling bath and evacuated with an aspirator, most of the entrapped air is removed, and disruption of weak pellets by boiling of the monomer is reduced to a minimum. Polymerization is then effected by immersion of the test tube in a water-bath at about 45"C, this temperature being held for 4 or 5 days. The test tube may then be broken away from the solidified mass and the pellets sectioned by a carborundum wheel or a diamond saw. Where time is important, impregnation is carried out at a higher temperature by Meyer&apos;s method.&apos; Air-dried pellets must be impregnated with especial care; otherwise swelling occurs and the solids are displaced. It is more important to be certain that the monomer forms a reasonably complete network throughout the specimen than that all entrained air is removed, and for this reason the vacuum technique may be omitted. Impregnated agglomerated products and pellets are extremely coherent, section well, and may be polished either by hand or by machine. Hand polishing is not satisfactory for the examination of conditions existing at the boundaries of grains, and for this machine polishing must be used. The Graton-Vanderwilt machine gives excellent results, provided that pressure on the specimen is considerably in excess of that recommended by the manufacturer. Mineralogy of Fired Pellets Only two opaque iron minerals, magnetite and hematite, have been recognized in pellets. The complete identity of, these artificial minerals with their corresponding natural counterparts is shown by their mineralographic characteristics and their X-ray structures. Wiistite has not been found. Slag is the most common transparent constituent of fired pellets. Occasionally conditions have been appropriate for the crystallization of fayalite from the slag, and at other times another crystalline sil-

Jan 1, 1953

By Strathmore R. B. Cooke, Thomas E. Bam

The paper discusses the mineralogy, structure, and strength of magnetite pellets fired in air and in a neutral atmosphere at various temperatures. The information obtained from this investigation is used to explain the origin of the structures occurring in pellets produced by pilot-plant operation. MUCH experimental work has been performed on i-VL the mechanism of agglomeration and pelletiz-ing of moist ore and concentrates and on the process of firing agglomerates, but except for the work of Tigerschiold and Ilmonil much of the published information is empirical, and the literature contains no information concerning the structure of fired pellets. Results of a preliminary study of the micro-structures occurring in pellets produced both in the laboratory and on a pilot-plant scale are presented in this paper. Most of the results were obtained from pellets prepared from Mesabi magnetic taconite, but through the courtesy of the staffs of the Minnesota Mines Experiment Station and the Bethlehem Steel Co., fired pellets produced from limonite and hematite ores and from Lebanon magnetite have also been examined. The work has been restricted almost entirely to pellets produced without additives, the exceptions being those in which coal was added to the filter cake before rolling. Schwartz has described the microstructures occurring in ore sinters produced under reducing conditions.&apos; Many of the structures and constituents he describes are common to fired pellets, but the constituents normally occur in markedly different proportions. His statement that "in all satisfactory sinter the amount of hematite is small, perhaps not over 2 or 3 per cent" is inapplicable to pellets produced by pilot plant operation or by any process in which air is not deliberately excluded. Pilot plant pellets contain over 90 pct by weight of hematite, and those produced in the smaller furnaces of the Minnesota Mines Experiment Station contain more than 80 pct of that constituent. Preparation of Specimens It is difficult to examine unfired pellets microscopically because of their insufficient coherency to withstand sectioning and polishing. Fired pellets sometimes lack coherency and frequently contain holes which are troublesome during polishing. Impregnation of both air-dried and fired pellets is readily accomplished by the use of methyl metha-crylate monomer." The dry pellets are covered in a test tube with excess monomer, to which a small amount of accelerator has been added. When the test tube is placed in a cooling bath and evacuated with an aspirator, most of the entrapped air is removed, and disruption of weak pellets by boiling of the monomer is reduced to a minimum. Polymerization is then effected by immersion of the test tube in a water-bath at about 45"C, this temperature being held for 4 or 5 days. The test tube may then be broken away from the solidified mass and the pellets sectioned by a carborundum wheel or a diamond saw. Where time is important, impregnation is carried out at a higher temperature by Meyer&apos;s method.&apos; Air-dried pellets must be impregnated with especial care; otherwise swelling occurs and the solids are displaced. It is more important to be certain that the monomer forms a reasonably complete network throughout the specimen than that all entrained air is removed, and for this reason the vacuum technique may be omitted. Impregnated agglomerated products and pellets are extremely coherent, section well, and may be polished either by hand or by machine. Hand polishing is not satisfactory for the examination of conditions existing at the boundaries of grains, and for this machine polishing must be used. The Graton-Vanderwilt machine gives excellent results, provided that pressure on the specimen is considerably in excess of that recommended by the manufacturer. Mineralogy of Fired Pellets Only two opaque iron minerals, magnetite and hematite, have been recognized in pellets. The complete identity of, these artificial minerals with their corresponding natural counterparts is shown by their mineralographic characteristics and their X-ray structures. Wiistite has not been found. Slag is the most common transparent constituent of fired pellets. Occasionally conditions have been appropriate for the crystallization of fayalite from the slag, and at other times another crystalline sil-

Jan 1, 1953

By E. F. Kingsbury

ONE of the well-known and important uses of the noble or precious metals has been for electrical contacts. In fact, the elements of this group, comprising gold, silver and. the six platinum metals, have been called "noble" because of their ability to resist heat and corrosion, properties which. were early found to be of importance in good contacts. Of these, platinum and its iridium alloys, palladium, and silver, have been extensively used. In recent years the electrical industry has been responsible for about one-eighth of the total consumption of the platinum metals in the United States. Information is not available as to what part of this one-eighth has been used for contacts but it is certainly an important one. SUBSTITUTES FOR PLATINUM During the past 20 years a considerable number of contact alloys have been proposed in the patent literature largely with the aim of more or less replacing platinum by gold or silver, and some of these alloys are finding increasingly widespread application as the reliability of their performance becomes established. From even the partial data at hand it appears that this substitution by the less precious metals has replaced at least one-half of the amount of platinum that the entire electrical industry would otherwise be consuming at the present time. While the subject is of considerable interest to the metallurgist it is even more so to the electrical engineer and it is surprising that the literature records no systematic and&apos; comprehensive investigation along these lines. Practically all the scattered work on noble metal contacts has centered around platinum as a standard and has had two more or less distinct aims. One of these has been the replacement of platinum by cheaper materials, and the other, the development of materials of superior electrical performance. The merit, of a contact metal has been assumed to be dependent on its infusibility, and since the more precious metals have the higher melting points there has naturally been an association of the two qualities in the sense that the more precious were

Jan 1, 1928

On the following pages are abstracts of papers published by the Institute during the year 1934 as TECHNICAL PWLICATIONB, CONTRIBUTIONS, m bound volumes and in MINING AND METALLURGY. For abstracts of papers that appear In bound volumes in 1934 but that were published as TECHNICAL PWLICATIONS m 1932 or 1933, see the TRANSACTIONS for 1932 and the YEAR BOOK dated January, 1934. Many of the TECHNICAL PWLICATIONS have been reprinted In bound volumes Information regarding this disposition, and number of pages in each paper, may be found m the list beginning on page 92 Volume numbers are given as listed at the beginning of the index, page 99 The abstracts are grouped as follows:

Jan 1, 1935

Prof. H. S. Munroe, New York City : In his reference to cop per-dressing at Lake Superior, p. 325, Mr. Douglas says that " the .. concentration .. . has been carried out with greatest financial economy,... I do not say with the greatest economy of min eral." And again, on p. 344, referring to the same, " it would not pay to reduce the quantity treated, and increase hand-labor, in order to save a few hundredths of one per cent. of copper." Mr. Douglas probably has in mind the fact that the copper lost is all included copper, locked op in grains of sand. To save this, the rock must be crushed finer. If the mesh of the stamp-screens be reduced, the stamps will crush less; and thus we shall have to reduce the quantity treated in the mill per day, while the labor re mains the same per day, or is increased per ton, as he says. Submitting to the loss of copper, however, is not the only solution of the difficulty. A large quantity of rich sand is now collected by the jigs, and it would be easy to save so much of this material that the escaping sands would be quite poor. What is wanted at Lake Superior, and at many dressing-works in this country, is an efficient crushing-machine to treat the sands thus collected. Abroad, we have the Heberle machine and the Schranz mill for this purpose, the latter being the more successful. The Heberle grinder was tried at the Calumet and Hecla mill for crush ing these rich sands, with what success I do not know. I should like to ask Mr. Douglas if we have no American crushing-machine that will reduce jig-sands to a fine state of division

Jan 1, 1894

By M. A. Grossman

The harden ability of most steels can be predicted within 10 to I5 per cent provided the complete chemical composition is known, including "incidental" elements; and provided the as-quenched grain size is known; and provided, finally, that the composition and heating temperatures for hardening are such as to result in austenite free from carbide particles. In the method proposed herein, the steel is considered as having a base hardenability due to its carbon content alone (the hardenability of a "pure steel" of the given carbon content, without any other elements), and this base hardenability is multiplied by a multiplying factor for each chemical element present. After multiplying all these together, the final product is the hardenability. Grain size may be taken into account either in the base hardenability or after the multiplication. Hardenability is stated in terms of "ideal critical diameter", namely, the diameter of bar, in inches, that will just harden all the way through (absence of un-hardened core) in an "ideal" quench, and the calculation may also be related to the Jominy test The data bring out certain features rather clearly. For example: i. It is quite useless to attempt to predict hardenability unless all elements, including "incidentals,,) are known; thus an "incidental,, chromium content of 0.20 per cent increases the hardenability by about 50 per cent. 2. The relative effectiveness of different alloys is sometimes unexpected; thus molybdenum when calculated in this way appears to be of the same order of effectiveness as manganese, rather than much more powerful, as would appear to be common experience; observe that an increase from no manaanese to 0.20 per cent Mn provides a multiplying factor of 1.67, and an increase from no molybdenum to 0.20 per cent Mo provides a factor of 1.63, an increase of over 60 per cent in each case. However, if to a steel containing 0.50 per cent Mn there is added "20 points of manganese," the factor is raised from 2.65 (for 0.50 per cent Mn) to 3.35 (for 0.70 per cent Mn), or an increase of only 26 per cent. Thus the fist small addition of an element has a much more powerful percentage effect than an equal further addition when some is already present, and in most cases the effect of molybdenum is considered in relation to a steel in which molybdenum is absent. 3. If two elements are equally effective, a greater hardenability will be obtained by using, for example, 0.5 per cent of each than by using I.o per cent of either of them alone. 4. A knowledge of the as-quenched grain size is essential for precise work, since a difference of only one grain size number (say No. 7 instead of No. 6) makes a difference of almost 10 per cent in hardenability (in these units); this, however, does not apply to certain It should be emphasized that in chromium steels (over 0.30 per cent Cr) and chrome-molybdenum and chrome-vanadium steels, un-dissolved carbides are likely to be present in the steel as quenched, and that in such cases the charts can indicate only a maximum Passible hardenability, whereas the extent of hardening actually obtained may be much less. Thus tests on a number of chrome-molybdenum steels have indicated a degree of hardening amounting to only 50 to 65 per cent of the maximum possible, and in chromium steels from full hardening (100 per cent) down to as low as 70 per cent. On the other hand, when the amount of such elements is small (Cr under 0.30 per cent, Mo up to 0.25 per cent in the

Jan 1, 1942

By M. A. Grossman

The harden ability of most steels can be predicted within 10 to I5 per cent provided the complete chemical composition is known, including "incidental" elements; and provided the as-quenched grain size is known; and provided, finally, that the composition and heating temperatures for hardening are such as to result in austenite free from carbide particles. In the method proposed herein, the steel is considered as having a base hardenability due to its carbon content alone (the hardenability of a "pure steel" of the given carbon content, without any other elements), and this base hardenability is multiplied by a multiplying factor for each chemical element present. After multiplying all these together, the final product is the hardenability. Grain size may be taken into account either in the base hardenability or after the multiplication. Hardenability is stated in terms of "ideal critical diameter", namely, the diameter of bar, in inches, that will just harden all the way through (absence of un-hardened core) in an "ideal" quench, and the calculation may also be related to the Jominy test The data bring out certain features rather clearly. For example: i. It is quite useless to attempt to predict hardenability unless all elements, including "incidentals,,) are known; thus an "incidental,, chromium content of 0.20 per cent increases the hardenability by about 50 per cent. 2. The relative effectiveness of different alloys is sometimes unexpected; thus molybdenum when calculated in this way appears to be of the same order of effectiveness as manganese, rather than much more powerful, as would appear to be common experience; observe that an increase from no manaanese to 0.20 per cent Mn provides a multiplying factor of 1.67, and an increase from no molybdenum to 0.20 per cent Mo provides a factor of 1.63, an increase of over 60 per cent in each case. However, if to a steel containing 0.50 per cent Mn there is added "20 points of manganese," the factor is raised from 2.65 (for 0.50 per cent Mn) to 3.35 (for 0.70 per cent Mn), or an increase of only 26 per cent. Thus the fist small addition of an element has a much more powerful percentage effect than an equal further addition when some is already present, and in most cases the effect of molybdenum is considered in relation to a steel in which molybdenum is absent. 3. If two elements are equally effective, a greater hardenability will be obtained by using, for example, 0.5 per cent of each than by using I.o per cent of either of them alone. 4. A knowledge of the as-quenched grain size is essential for precise work, since a difference of only one grain size number (say No. 7 instead of No. 6) makes a difference of almost 10 per cent in hardenability (in these units); this, however, does not apply to certain It should be emphasized that in chromium steels (over 0.30 per cent Cr) and chrome-molybdenum and chrome-vanadium steels, un-dissolved carbides are likely to be present in the steel as quenched, and that in such cases the charts can indicate only a maximum Passible hardenability, whereas the extent of hardening actually obtained may be much less. Thus tests on a number of chrome-molybdenum steels have indicated a degree of hardening amounting to only 50 to 65 per cent of the maximum possible, and in chromium steels from full hardening (100 per cent) down to as low as 70 per cent. On the other hand, when the amount of such elements is small (Cr under 0.30 per cent, Mo up to 0.25 per cent in the

Jan 1, 1942

By G. Sandoz, D. A. Meyn

The fracture surfaces of specimens of titanium a1loys which exhibited susceptibility to subcritical crack growth in a wide variety of environments, including aqueous solutions, alcohols, hydrocarbon gases, carbm tetrachloride, and dry air, were examined. The dominant and characteristic fracture mode was cleavage. which became mixed with an increasing porportion of ductile fracture modes (dimples. and so forth) as the applied KI was increased. The cleavage plane in all the alloys was oriented at 15 deg from (0001) of the a phase. No indices could be assigned to the 15 deg cleavage Plane because of uncertainty as to which zone it belonged to. SLOW crack growth and delayed fracture take place in certain titanium alloys at stress intensity (KI) lower than the critical values for complete fracture (KIc) found in short-time tests for plane strain fracture toughness.&apos; Such crack growth may take place in very dry air on sustained loading if the alloy contains a sufficient amount of hydrogen and if the stress intensity factor is higher than a threshold value designated KIH.2 Similarly, a number of environments such as water, alcohols, and hydrocarbons may cause slow crack growth provided the stress intensity factor exceeds the threshold value KISCC. In this paper it is intended to examine some fracto-graphic and crystallographic details of this subcritical crack propagation process as related to alloy composition, environment, and stress intensity. It has been previously reported that subcritical crack growth takes place in titanium alloys in aqueous environments by cleavage.2"6 The observations to be described here indicate that in the alloys investigated the mode of subcritical crack propagation is more dependent on the stress intensity during cracking than on the environment. The fracture mode is illustrated with photographs of the fracture surfaces at a wide range of magnifications. The crystallographic character of the cleavage mode is also presented and the results discussed. EXPERIMENTAL APPROACH The studies were made on four titanium alloys— Ti-8A1-1Mo-lV, Ti-5A1-2.5Sn, Ti-7Al-1Mo-lV, and Ti-0.350. Of these four alloys the first two were mill annealed and fine grained. The latter two were noncommercial and coarse grained, having been prepared for other experimental purposes. The crystallographic studies required a large-grain size. Consequently the fine-grained alloys were an- nealed in a vacuum at 1950°F and furnace cooled to produce samples for these studies. This treatment did not alter the microstructure significantly except for grain size. All the aluminum-containing alloys showed primary a with a network of ß-phase particles within the a grains; Figs. 1 and 2 show this microstructure for the specific case of fine-grained Ti-8A1-1Mo-1V. The cracks in the figures will be discussed later. Fractographic studies were made on all the alloys, but the electron fractographs displayed herein are from the Ti-8A1-1Mo-1V alloy in the fine-grained condition. Emphasis was placed on this commercial alloy because considerable information was available on the stress-corrosion cracking characteristics in a variety of environments. Sufficient supplementary studies of the alloy after the anneal to produce large grains were conducted to establish that the stress-corrosion cracking susceptibility and fractographic characteristics were not changed significantly. Thus it could be inferred that the crystallographic data obtained exclusively on large-grained specimens would apply also to fine-grained specimens. Fracture surfaces for study were obtained using precracked cantilever beam specimens loaded as described by Brown. The precracked section of a specimen was immersed in the environment of interest. Values of initial stress intensity factor Kli were chosen slightly higher than KISCC in order to obtain a fairly extensive region of slow crack growth. Fracture surfaces representative of a variety of stress intensity levels could then be examined because in the cantilever beam test KI increases as the crack propagates.

Jan 1, 1970

By H. I. Smith

THE recently developed potash industry in southeastern New Mexico, though based on a relatively new discovery, marks the latest and perhaps culminating phase of the effort to obtain a domestic source of potash that began with the leaching of wood ashes more than 300 years ago. In the search for mineral potash in America, the Geological Survey has played a conspicuous part and has paved the way for much of the private activity that now bids fair to free the nation of foreign domina¬tion in supplying the nation&apos;s potash requirements. HISTORICAL REVIEW A pamphlet published by Thomas Stephen in 1758 pictures the industry in its early struggling condition.1 Just before the Civil War, a deposit of mineral potash had been found in Germany and its value as a fertilizer had been discovered. On this account and because the supply of wood ashes had decreased, the Ameri-can potash industry gradually lost its importance. During the next 50 years, with European potash available with little effort and with satisfactory substitutes on the market for the manufacture of soap, the interest of the American people in American potash declined. In 1910 this interest was suddenly revived by the abrogation of American potash contracts in Europe. Congress passed an act, approved by President Taft March 4, 1911, providing for "researches with a view to determining geological conditions favorable to the presence of deposits of potash salts." Appropriations were made to the Geological Survey and the Bureau of Soils to carry out the provisions of this act. The work of the Survey was directed toward the finding of commercial bodies of natural soluble potash salts; the Bureau of Soils was more concerned with the processes of extracting potash from industrial wastes and organic sources. Private agencies also became interested in the program. The Geological Survey has continued its search throughout the ensuing period of more than 20 years and has studied many types of deposits in many parts of the country.

Jan 1, 1933

By E. W. Davis

If the tonnage of merchantable iron ore remaining in the Lake Superior district is divided by the average of the annual shipments for the past 20 years, it will be found that this ore supply will be exhausted in approximately 35 years. This computed exhaustion period would be an indication of the future activities of the iron-mining industry if it were not for the fact that merchantable ore is being manufactured from low-grade ore, of which there is an almost inexhaustible supply in the Lake Superior district. It is true that at present only the simplest of these low-grade ores are being concentrated to any considerable extent, but progress is being made with the treatment of the more complex ores, and now, in addition to 20 washing plants on the Mesabi Range, three plants are equipped with jigs for the treatment of ore that cannot be concentrated simply by washing. The latest addition to the ore-treating plants of the Mesabi Range is a magnetic roasting and concentration plant at Cooley, Minn., in which ore that cannot be concentrated either by washing or by jigging is roasted to the magnetic state and concentrated on magnetic separators. This plant is beginning its third season of operation, and while it is too soon to make definite predictions, there are strong indications that this new process may make commercially possible the manufacture of high-grade, merchantable iron ore from large quantities of low-grade ore now considered worthless. After the iron oxide contained in an ore has been converted to magnetite, almost any desired grade of concentrate can be produced, using magnetic-concentration equipment of the types now in general use for the concentration of the natural magnetites of New York, New Jersey and Pennsylvania. The conversion of hematite (Fe203) to magnetite (Fe3O4) is easily accomplished by heating the ore to a dull red temperature in a reducing atmosphere. The reaction is slightly endothermic, and while it requires 200 B.t.u. to heat to 900&apos; F. one pound of hematite ore containing 45 per cent Fe, it requires only 100 B.t.u. to convert the oxide into magnetite. In the laboratory, using small quantities of ore, this conversion is very simple, but large furnaces suitable for commercial

Jan 1, 1939